ISO代号 | 化學成分(質量分數)a / % | 對應的緊固件組别b | |||||||||||
C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | Nb | Ti | ||
奧氏體不鏽鋼 | |||||||||||||
4305-303-00-I | 0.120 | 1.00 | 2.00 | 0.060 | ≥0.15 | 17.0~19.0 | / | 8.0~10.0 | 1.0 | 0.10 | / | / | A1 |
4301-304-00-I | 0.070 | 1.00 | 2.00 | 0.045 | 0.030 | 17.5~19.5 | / | 8.0~10.5 | / | 0.10 | / | / | A2 |
4307-304-03-I | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 17.5~19.5 | / | 8.0~10.5 | / | 0.10 | / | / | A2L |
4311-304-53-I | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 17.5~19.5 | / | 8.0~11.0 | / | 0.12~0.22 | / | / | A2L |
4567-304-98-X | 0.080 | 1.00 | 2.00 | 0.045 | 0.030 | 17.0~19.0 | / | 8.0~10.5 | 1.0~3.0 | / | / | / | A2 |
4567-304-30-I | 0.040 | 1.00 | 2.00 | 0.045 | 0.030 | 17.0~19.0 | / | 8.0~10.5 | 3.0~4.0 | 0.10 | / | / | A3 |
4541-321-00-I | 0.080 | 1.00 | 2.00 | 0.045 | 0.030 | 17.0~19.0 | / | 9.0~12.0 | / | / | / | 5×C~0.70 | A3 |
4550-347-00-I | 0.080 | 1.00 | 2.00 | 0.045 | 0.030 | 17.0~19.0 | / | 9.0~12.0 | / | / | 10×C~1.00 | / | A3 |
4401-316-00-I | 0.080 | 1.00 | 2.00 | 0.045 | 0.030 | 16.0~18.0 | 2.00~3.00 | 10.0~13.0 | / | 0.10 | / | / | A4 |
4404-316-03-I | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 16.5~18.5 | 2.00~3.00 | 10.0~13.0 | / | 0.10 | / | / | A4L |
4406-316-53-I | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 16.5~18.5 | 2.00~3.00 | 10.0~12.5 | / | 0.12~0.22 | / | / | A4L |
4578-316-76-E | 0.040 | 1.00 | 2.00 | 0.045 | 0.015 | 16.5~17.5 | 2.00~2.50 | 10.0~11.0 | 3.0~3.5 | 0.10 | / | / | A4 |
4571-316-35-I | 0.080 | 1.00 | 2.00 | 0.045 | 0.030 | 16.5~18.5 | 2.00~2.50 | 10.5~13.5 | / | / | / | 5×C~0.70 | A5 |
4529-089-26-I | 0.020 | 0.75 | 2.00 | 0.035 | 0.015 | 19.0~21.0 | 6.0~7.0 | 24.0~26.0 | 0.5~1.5 | 0.15~0.25 | / | / | A8 |
4547-312-54-I | 0.020 | 0.70 | 1.00 | 0.035 | 0.015 | 19.5~20.5 | 6.0~7.0 | 17.5~18.5 | 0.50~1.00 | 0.18~0.25 | / | / | A8 |
4478-083-67-U | 0.030 | 1.00 | 2.00 | 0.040 | 0.030 | 20.0~22.0 | 6.0~7.0 | 23.5~25.5 | 0.75 | 0.18~0.25 | / | / | A8 |
注:表中所列成分除标明範圍或最小值外,其餘均為最大值。 | |||||||||||||
a 未經買方同意,不宜将未規定的元素加入鋼材中,除非為了完成冶煉。應采取一切合理的預防措施,以防止從制造中使用的廢料或其他材料中添加影響淬透性、機械性能和适用性的元素。 b 鋼的組别與GB/T 3098.6和GB/T 3098.15規定的成分範圍最接近,但是,本表中包含的不一定完全符合。 |
ISO代号 | 化學成分(質量分數)a / % | 對應的緊固件組别b | |||||||||||
C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | Nb | Ti | ||
馬氏體不鏽鋼 | |||||||||||||
4006-410-00-I | 0.08~0.15 | 1.00 | 1.5 | 0.040 | 0.030 | 11.5~13.5 | / | 0.75 | / | / | / | / | C1 |
4021-420-00-I | 0.16~0.25 | 1.00 | 1.50 | 0.040 | 0.030 | 12.0~14.0 | / | / | / | / | / | / | C1 |
4028-420-00-I | 0.26~0.35 | 1.00 | 1.50 | 0.040 | 0.030 | 12.0~14.0 | / | / | / | / | / | / | C1 |
4057-431-00-X | 0.12~0.22 | 1.00 | 1.50 | 0.040 | 0.030 | 15.0~17.0 | / | 1.50~2.50 | / | / | / | / | C3 |
4005-416-00-I | 0.08~0.15 | 1.00 | 1.50 | 0.040 | ≥0.15 | 12.0~14.0 | 0.60 | / | / | / | / | / | C4 |
鐵素體不鏽鋼 | |||||||||||||
4016-430-00-I | 0.08 | 1.00 | 1.00 | 0.040 | 0.030 | 16.0~18.0 | / | / | / | / | / | / | F1 |
雙相不鏽鋼 | |||||||||||||
4482-320-01-X | 0.030 | 1.00 | 4.0~6.0 | 0.035 | 0.030 | 19.5~21.5 | 0.10~0.60 | 1.50~3.50 | 1.0 | 0.05~0.20 | / | / | D2d |
4362-323-04-I | 0.030 | 1.00 | 2.00 | 0.035 | 0.015 | 22.0~24.5 | 0.10~0.60 | 3.5~5.5 | 0.10~0.60 | 0.05~0.20 | / | / | D2d |
4062-322-02-U | 0.030 | 1.00 | 2.00 | 0.040 | 0.010 | 21.5~24.0 | 0.45 | 1.00~2.90 | / | 0.16~0.28 | / | / | D4 |
4162-321-01-E | 0.040 | 1.00 | 4.0~6.0 | 0.040 | 0.015 | 21.0~22.0 | 0.10~0.80 | 1.35~1.90 | 0.10~0.80 | 0.20~0.25 | / | / | D4 |
4662-824-41-X | 0.030 | 0.70 | 2.50~4.0 | 0.035 | 0.005 | 23.0~25.0 | 1.00~2.00 | 3.0~4.5 | 0.10~0.80 | 0.20~0.30 | / | / | D4 |
4462-318-03-I | 0.030 | 1.00 | 2.00 | 0.035 | 0.015 | 21.0~23.0 | 2.5~3.5 | 4.5~6.5 | / | 0.10~0.22 | / | / | D6 |
4481-312-60-J | 0.030 | 1.00 | 1.50 | 0.040 | 0.030 | 24.0~26.0 | 2.5~3.5 | 5.5~7.5 | / | 0.08~0.30 | / | / | D6 |
4410-327-50-E | 0.030 | 1.00 | 2.00 | 0.035 | 0.015 | 24.0~26.0 | 3.0~4.5 | 6.0~8.0 | / | 0.24~0.35 | / | / | D8 |
4501-327-60-I c | 0.030 | 1.00 | 1.00 | 0.030 | 0.010 | 24.0~26.0 | 3.0~4.0 | 6.0~8.0 | 0.5~1.0 | 0.20~0.30 | / | / | D8 |
4507-325-20-I | 0.030 | 0.70 | 2.00 | 0.035 | 0.015 | 24.0~26.0 | 3.0~4.0 | 6.0~8.0 | 1.0~2.5 | 0.20~0.30 | / | / | D8 |
注:表中所列成分除标明範圍或最小值外,其餘均為最大值。 | |||||||||||||
a 未經買方同意,不宜将未規定的元素加入鋼材中,除非為了完成冶煉。應采取一切合理的預防措施,以防止從制造中使用的廢料或其他材料中添加影響淬透性、機械性能和适用性的元素。 b 鋼的組别與GB/T 3098.6和GB/T 3098.15規定的成分範圍最接近,但是,本表中包含的不一定完全符合。 c 鎢的含量應為0.5%~1.0%。 d 當wCr+3.3wMo+16wN>24和符合GB/T 3098不鏽鋼系列标準時,可被認同為D4。 |
ISO代号 | 化學成分(質量分數)a / % | 對應的緊固件組别b | |||||||||||
C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | Nb | Ti | ||
馬氏體不鏽鋼 | |||||||||||||
4021-420-00-I | 0.16~0.25 | 1.00 | 1.50 | 0.040 | 0.030 | 12.0~14.0 | / | / | / | / | / | / | CH0 |
4028-420-00-I | 0.26~0.35 | 1.00 | 1.50 | 0.040 | 0.030 | 12.0~14.0 | / | / | / | / | / | / | CH1 |
4057-431-00-X | 0.12~0.22 | 1.00 | 1.50 | 0.040 | 0.030 | 15.0~17.0 | / | 1.50~2.5 | / | / | / | / | CH2 |
4923-422-77-Ec | 0.18~0.24 | 0.50 | 0.40~0.90 | 0.025 | 0.015 | 11.0~12.5 | 0.8~1.2 | 0.30~0.80 | / | / | / | / | V或VH |
1.4913d | 0.17~0.23 | 0.50 | 0.40~0.90 | 0.025 | 0.015 | 10.0~11.5 | 0.50~0.80 | 0.20~0.60 | / | 0.05~0.10 | 0.25~0.55 | / | VW |
奧氏體沉澱硬化不鏽鋼和鎳合金 | |||||||||||||
4980-662-86-Xc | 0.08 | 1.00 | 2.00 | 0.040 | 0.030 | 13.5~16.0 | 1.0~1.5 | 24.0~27.0 | / | / | / | 1.90~2.35 | SD |
2.4952f | 0.04~0.10 | 1.00 | 1.00 | 0.020 | 0.015 | 18.0~21.0 | / | ≥65 | 0.20 | / | / | 1.80~2.70 | SB |
2.4668g | 0.02~0.08 | 0.035 | 0.035 | 0.015 | 0.015 | 17.0~21.0 | 2.80~3.30 | 50.00~55.00 | 0.30 | / | / | 0.60~1.20 | 718 |
注:表中所列成分除标明範圍或最小值外,其餘均為最大值。 | |||||||||||||
a 未經買方同意,不宜将未規定的元素加入鋼材中,除非為了完成冶煉。應采取一切合理的預防措施,以防止從制造中使用的廢料或其他材料中添加影響淬透性、機械性能和适用性的元素。 b 鋼的組别與GB/T 3098.6和GB/T 3098.15規定的成分範圍最接近,但是,本表中包含的不一定完全符合。 c 此外,釩的含量應為0.25%~0.35%。 d 化學成分與EN 10269一緻;此外,鋁含量應≤0.020%,釩含量應為0.10%~0.30%,硼含量≤0.0015%。 e 此外,鋁含量應≤0.35%,釩含量應為0.10%~0.50%,硼含量0.001%~0.010%。 f 化學成分與EN 10269一緻;此外鋁含量應為1.00%~1.80%,钴含量應≤1.00%,鐵含量≤1.50%,硼含量≤0.008%。 g 化學成分與EN 10269一緻;此外鋁含量應為0.30%~0.70%,钴含量應≤1.00%,硼含量0.002%~0.006%,铌含量應為4.7%~5.50%(其餘為鐵)。 |