牌号 X2CrNiMo18-14-3
1.4435
对应标准 NF EN 10028-7-2008
压力容器用不锈钢扁平产品
Flat products made of steels for pressure purposes - Part 7 : stainless steels
归类 奥氏体不锈钢
标签 耐腐蚀等级
X2CrNiMo18-14-3 化学元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo N
最小值 - - - - - 17 12.5 2.5 -
最大值 0.03 1 2 0.045 0.015 19 15 3 0.1
◎ 未经买方同意,不得随意向钢中添加表中未列的元素,冶炼精加工除外。采取一切必要措施以防在废钢和生产原料中带入这些元素,因为其会削弱钢的机械性能,降低钢的适用性。
X2CrNiMo18-14-3 机械性能
条件 热处理或状态
抗拉强度
σb
Mpa
屈服点
σs
Mpa
断后伸长率或延伸率
δ
%
冲击吸收能量
KV2
J
C:T ≤ 8 +AT 550~700 Rp0.2:≥240
Rp1.0:≥270
①②
T < 3mm: ≥40
T ≥ 3mm: ≥ 40
②③
20℃:
(l: ≥100;t: ≥60)
-196℃:
(t: ≥60)
H:T ≤ 13.5 +AT 550~700 Rp0.2:≥220
Rp1.0:≥260
①②
T < 3mm: ≥40
T ≥ 3mm: ≥ 40
②③
20℃:
(l: ≥100;t: ≥60)
-196℃:
(t: ≥60)
P:T ≤ 75 +AT 520~670 Rp0.2:≥220
Rp1.0:≥260
①②
T < 3mm: ≥45
T ≥ 3mm: ≥ 45
②③
20℃:
(l: ≥100;t: ≥60)
-196℃:
(t: ≥60)
◎C- 冷轧带钢; H- 热轧带钢; P- 热轧中厚板;T- 厚度;t- 横向;l-纵向。
◎+A=软化退火;+AT=固溶退火;+QT=淬火及回火;+RA=再结晶退火。
◎ 奥氏体钢有足够的韧性,不需要进行冲击试验。相比之下,奥氏体-铁素体钢必须按要求做冲击试验,以确保足够的韧性。
*抗晶间腐蚀根据EN ISO 3651-2进行测试。在交货条件下:有;在致敏状态下:有。
① 对于连续热轧产品,可在询价和订购时商定Rp0.2(即表中σs)的最小值提高20MPa,Rp1.0的最小值提高10MPa。
② 如果在轧制宽度<300mm的带材情况下,采用纵向试验件,最小值减小如下:屈服强度-15MPa,恒定标距的延伸率-5%,比例标距延伸率-2%。
③ T<3mm:该值适用于标距为80mm、宽度为20mm的试件,也可以使用标距为50mm、宽度为12.5mm的试件。T ≥3mm:该值适用于标距为5.65√S的试件。

  • 高温下的最小屈服强度

    Material designationHeat treatment
    condition
    Minimum 0.2% proof strength Rp0.2,MPa
    at a temperature (in°C) of:
    Name Number50①100150200250300350400450500550600
    X2CrNiMo18-14-31.4435+AT19916515013712711911310810310098-
    Minimum 1.0% proof strength Rp1.0,MPa
    at a temperature (in°C) of:
    50①100150200250300350400450500550600
    237200180165153145139135130128127-
    ① Determined by linear interpolation.

  • 高温下的最小抗拉强度

    Material designationMinimum tensile strength Rm,MPa
    at a temperature (in°C) of:
    Name Number50①100150200250300350400450500550600
    X2CrNiMo18-14-31.4435482420400380375370370-----
    ① Determined by linear interpolation.

  • 热处理指南

    Material designationHot formingHeat
    treatment
    symbol
     Solution anneailing
    ①②
    Post weld heat 
    treatment
    Steel with ≤ 0.03% C
    Name NumberTemperature
    Type of
    cooling
    Temperature
    ℃ ③④
    Type of
    cooling
    Temperature
    ℃ ⑥
    Type of
    cooling
    X2CrNiMo18-14-31.44351150 to 850air+AT1030 to 1110water,air ⑤960 to 1040 ⑦forced air 
    ◎ a=air; o=oil; w=water.
    ◎ Scale and annealing colours produced during hot forming, heat treatment or welding may adversely affect the corrosion resistance. They should be removed as far as possible before use, e.g. by pickling.
    ◎ The temperatures of annealing should be agreed for simulated heat treated test pieces.
    ① The solution treatment may be omitted if the conditions for hot working and subsequent cooling are such that the requirements for the mechanical properties of the product and the resistance to intergranular corrosion as defined in EN ISO 3651-2 are obtained and provided these requirements are met even after appropriate subsequent solution annealing.
    ② Re-crystallizing annealing.
    ③ If heat treatment is carried out in a continuous furnace, the upper part of the range specified is usually preferred, or even exceeded.
    ④ The lower end of the range specified for solution annealing should be aimed at for heat treatment as part of further processing,because otherwise the mechanical properties might be affected. If the temperature of hot forming does not drop below the lower temperature for solution annealing.a temperature of 980℃ is adequate as a lower limit for Mo-free steels,a temperature of 1000℃ for steels with Mo contents up to 3% and a temperature of 1020℃ for steets with Mo contents exceeding 3%.
    ⑤ cooling sufficiently rapid.

    ⑥ Minimum holding time:30min.

    ⑦ Not recommended if welded with stabilized filler medal.

X2CrNiMo18-14-3 对应不同标准
1 EN 10088-1-2005 不锈钢 第1部分:不锈钢的清单
2 EN 10296-2-2005 机械工程和一般工程用焊接圆钢管.交货技术条件.第2部分:不锈钢
3 EN 10253-4-2003 对接焊管道接头.具有特殊检验要求的锻制奥氏体和铁素体-奥氏体(二相)不锈钢
4 EN 10250-4-1999 一般工程用途的自由锻钢锻件:不锈钢
5 ISO TS 15510-2003 技术规范 不锈钢-化学成分
6 EN 10088-2-2005 不锈钢-第 2 部分: 通用耐腐蚀钢的薄钢板/钢板和带钢的技术交货条件
7 DIN 17440-1972 不锈钢质量标准
8 EN 10088-3-2005 不锈钢第3部分:一般用途的半成品,钢棒,轧制线材和型钢的交货条件
9 EN 10297(2)-2005 机械和一般工程用途-交货技术条件-第2部分:不锈钢无缝钢管
10 EN 10088-3-2014 不锈钢 - 第3部分:半成品,棒材,杆材,线材,型材和光亮产品的一般用途耐腐蚀钢的交货技术条件
11 ISO 15510-2014 技术规范 不锈钢-化学成分
12 ISO 9328-7-2018 不锈钢承压扁钢制品
13 DIN EN 10088-3-2014 不锈钢-半成品、棒材、杆材、线材、型材及光亮产品交货技术条件
14 NF EN 10088-2-2005 普通用途不锈钢板和钢带的交货技术条件
15 NF EN 10088-1-2005 不锈钢 - 第1部分:不锈钢清单
16 NF EN 10028-7-2008 压力容器用不锈钢扁平产品
17 NF EN 10296-2-2005 机械和一般工程用焊接圆钢管-交货技术条件-第2部分:不锈钢管
18 NF EN 10028-7-2000 压力容器用不锈钢扁平产品