| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Pressure loss (Unit Pa) | 压力损失（单位Pa） |
The loss in stagnation pressure in internal flow due to wall friction and minor losses in fittings. 壁面摩擦引起的内部流动停滞压力损失和配件的微小损失。 |
| Wrought iron | 锻铁 |
A highly ductile (but anisotropic) type of iron containing elongated slag fibres that resulted from the method of manufacture in which excess carbon in pig iron was burnt and worked out. The yield strength is some 200 MPa, tensile strength 320 MPa, and reduction of area on a 50-mm gauge length up to 35%. Now replaced by steel. 一种高韧性（但各向异性）的铁，含有细长的矿渣纤维，由生铁中多余的碳燃烧和加工的制造方法产生。屈服强度约为200MPa，抗拉强度为320MPa，50mm标距上的面积缩减率高达35%。现在被钢所取代。 |
| Hardenability | 淬透性 |
Defined as the ability of a ferrous material to acquire hardness after austenitization and quenching. The relative ability of a ferrous alloy to form martensite when quenched from a temperature above the upper critical temperature. Hardenability is commonly measured as the distance below a quenched surface where the metal exhibits a specific hardness (50 HRC, for example) or a specific percentage of martensite in the microstructure. 定义为黑色金属材料在奥氏体化和淬火后获得硬度的能力。铁合金从高于上临界温度的温度淬火时形成马氏体的相对能力。淬透性通常以淬火表面下方的距离来测量，金属在淬火表面处表现出特定硬度（例如50HRC）或微观结构中马氏体的特定百分比。 |
| Ablation cooling | 烧蚀冷却 |
The cooling of a surface exposed to very high external gas temperature which causes the surface material to sublime, melt or decompose. The chemical process absorbs heat while the mass flow of material away from the surface blocks the heat flux from the hot gas. 冷却暴露于非常高的外部气体温度的表面，导致表面材料升华、熔化或分解。化学过程吸收热量，而远离表面的物质的质量流阻挡了来自热气体的热通量。 |
| Carburizing | 渗碳 |
Absorption and diffusion of carbon into solid ferrous alloys by heating, to a temperature usually above Ac3, in contact with a suitable carbonaceous material. A form of case hardening that produces a carbon gradient extending inward from the surface, enabling the surface layer to be hardened either by quenching directly from the carburizing temperature or by cooling to room temperature, then reaustenitizing and quenching. 通过与合适的含碳材料接触加热至通常高于Ac3的温度，将碳吸收和扩散到固体铁合金中。一种表面硬化形式，产生从表面向内延伸的碳梯度，通过直接从渗碳温度淬火或冷却至室温，然后重新奥氏体化和淬火，使表层硬化。 |
| Total combustion air (Unit kg/s) | 总燃烧空气（单位：kg/s） |
1. The combination of the stoichiometric flow of air required for combustion together with any excess air. 2. The flow of fresh air into a boiler plus any flue gas recirculated. 1.燃烧所需的化学计量空气流与任何过量空气的组合。2.进入锅炉的新鲜空气流加上再循环的任何烟气。 |
| Acid rain | 酸雨 |
Any form of precipitation, including rain, snow, sleet, fog, dew, and particulates, which contains higher than normal levels of sulfuric and nitric acids. These acids result from natural and man-made emissions of sulfur dioxide and oxides of nitrogen, respectively. Acid soot consists of unburned carbon particles, typically larger than 10 μm, in the atmosphere contaminated with sulfuric acid. The particles result from poor combustion of fossil fuels. 任何形式的降水，包括雨、雪、雨夹雪、雾、露水和颗粒物，其中含有高于正常水平的硫酸和硝酸。这些酸分别来自二氧化硫和氮氧化物的自然排放和人为排放。酸烟灰由未燃烧的碳颗粒组成，通常大于10微米，在被硫酸污染的大气中。这些颗粒是化石燃料燃烧不良造成的。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Waste-heat recovery | 废热回收 |
The recovery of thermal energy from flue and exhaust gases, or from liquids heated in industrial processes. Recovery devices include pre-heaters, recuperators, regenerators, and waste-heat boilers. 从烟道和废气中或从工业过程中加热的液体中回收热能。回收装置包括预热器、回热器、再生器和余热锅炉。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Gauge pressure (Unit Pa) | 表压（单位Pa） |
The level of static pressure above the ambient pressure. 高于环境压力的静压水平。 |
| Inch (in) | 英寸（in） |
A non-SI unit of length now defined as 25.4 mm. The conversion to SI is 1 in = 2.54 × 10−2 m. 现在定义为25.4毫米的非SI长度单位。转换为SI为1in=2.54×10-2m。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Actual cubic feet per minute | 实际立方英尺每分钟 |
(acfm) An obsolete (i.e. non-SI) measure of volumetric flow rate; the volume of a gas flowing per minute at actual operating pressure and temperature, as opposed to the corresponding volume flow rate at STP. （acfm）已被淘汰的（即非SI）体积流量测量；在实际工作压力和温度下每分钟流动的气体体积，与STP下的相应体积流量相反。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Span (Unit m) | 跨度（单位：m） |
A dimension measured between the extremities of a body or structure, such as between the tips of a wing or the supports of a bridge. 在身体或结构的末端之间测量的尺寸，如机翼尖端或桥梁支架之间。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Nano machining | 纳米加工 |
The machining of silicon chips typically less than 1 nm thick. 硅芯片的加工通常小于1nm厚。 |
| Mass flow meter | 质量流量计 |
An instrument, such as a Coriolis flow meter, which measures the mass flow rate of a fluid flowing through a pipe or other duct, rather than its volume flow rate. 一种仪器，例如科里奥利流量计，一种测量流经管道或其他管道的流体的质量流率而不是其体积流率的仪器。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Piston pump | 活塞泵 |
A positive-displacement pump in the basic configuration of which a piston reciprocates in a cylinder. On the suction stroke, fluid is drawn into a chamber through the inlet valve, which is then open while the outlet valve is closed. On the delivery stroke the fluid is forced out of the chamber through the outlet valve, which then opens while the inlet valve is closed. Both axial and radial configurations are common. 活塞在气缸中往复运动的一种容积泵。在吸入冲程，流体通过入口阀吸入腔室，然后在出口阀关闭时打开。在输送冲程中，流体通过出口阀被迫流出腔室，然后出口阀打开，同时入口阀关闭。轴向和径向配置都很常见。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Transgranular fracture | 穿晶断裂 |
Fracture in crystalline materials where the path of cracking is predominantly across grains. 晶体材料中的断裂，其中裂纹路径主要跨越晶粒。 |
| Thermochemical treatment | 热化学处理 |
Heat treatment carried out in a medium suitably chosen to produce a change in the chemical composition of the object by exchange with the medium. 在适当选择的介质中进行热处理，以通过与介质交换产生物体化学成分的变化。 |
| Sample variance (s²) | 样本方差（s²） |
The sum of the squares of the differences between each observed value and the sample average divided by the sample size minus one. It is a point estimate of the population variance. 每个观测值与样本平均值之差的平方和除以样本大小减1。它是总体方差的点估计。 |
| Blue annealing | 蓝色退火 |
Heating hot-rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental. 在开放式炉中将热轧铁板加热到转变范围内的温度，然后在空气中冷却，以软化金属。在表面上形成蓝色氧化物是偶然的。 |
| Annealing twin | 退火孪晶 |
A twin form in a crystal during recrystallization. 重结晶过程中晶体中的孪晶形式。 |
| Imperial system | 英制单位体系 |
The units of measurement developed in the UK. Formerly known as the fps system, which is an abbreviation for the ‘foot-pound-second system of units. 英国开发的计量单位。以前称为fps系统，是“英尺-磅-秒（foot-pound-second）单位制”的缩写。 |
| Twist | 扭转 |
The helix produced in a cylindrical component, such as a shaft, wire, tensioned cable, or rope, when one end is rotated relative to the other. Measured either as the number of turns per unit length, or by the helix angle (twist angle). 当一端相对于另一端旋转时，在圆柱形部件（如轴、钢丝、张紧电缆或绳索）中产生的螺旋。以每单位长度的圈数或螺旋角（扭曲角）测量。 |
| Scale effect | 规模效应 |
The change in behaviour with size of a material, component, or structure. For example, cube-square scaling where one element changes with volume and another with area, as in the range of a projectile or ship, droplet formation, and fracture mechanics. 性能随材料、部件或结构尺寸的变化。例如，立方体平方比例，其中一个元素随体积变化，另一个元素因面积变化，如在射弹或飞船的射程、液滴形成和断裂力学中。 |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Apparent area of contact | 表观接触面积 |
In tribology, the area of contact between two solid surfaces defined by the boundaries of their macroscopic interface. 在摩擦学中，两个固体表面之间的接触区域由其宏观界面的边界定义。 |
| Dynamic load rating (Unit N) | 额定动载荷（单位N） |
The allowable load on a component or structure when the loading is not static. 当负载不是静态时，组件或结构上的允许负载。 |
| Linear-elastic fracture mechanics | 线弹性断裂力学 |
A method of fracture analysis that can determine the stress (or load) required to induce fracture instability in a structure containing a cracklike flaw of known size and shape. 一种断裂分析方法，可确定在含有已知尺寸和形状裂纹状缺陷的结构中引起断裂不稳定性所需的应力（或载荷）。 |
| Rotary valve (rotating valve) | 旋转阀 |
A cylindrical or conical plug in which there is a transverse hole through which fluid can flow when the hole is aligned with the adjacent piping. 一种圆柱形或锥形塞，其中有一个横向孔，当该孔与相邻管道对齐时，流体可通过该孔流动。 |
| Standardization | 标准化 |
1. National and international agreements for design, manufacture, materials, performance, practices, requirements, strength, etc. which ensure common results wherever an item is made and wherever used. 2. The manufacture of components so that interchangeability of parts during assembly of new, or repair of old, items is possible without ‘fitting’. 1.关于设计、制造、材料、性能、惯例、要求、强度等的国家和国际协议，确保在任何地方制造和使用物品都能产生共同结果。2.部件的制造，以便在装配新部件或维修旧部件时，无需“装配”即可实现部件的互换性。 |
| Shear strain rate(Unit 1/s) | 剪切应变率（单位1/s） |
In the deformation of solids, the rate at which shear strain is applied in a test or changes with time in a loaded component or structure. 在固体变形中，在试验中施加剪切应变的速率，或在加载部件或结构中随时间变化的速率。 |
| Brake fluid | 制动液 |
The hydraulic fluid used to transmit force to the pistons in disc brakes or the wheel cylinders in drum brakes. Requirements include a high boiling point and low hygroscopy. 用于将力传递到盘式制动器中的活塞或鼓式制动器中的轮缸的液压油。要求包括高沸点和低吸湿性。 |
| Thermal analysis | 热分析 |
A method for determining transformations in a metal by noting the temperatures at which thermal arrests occur. These arrests are manifested by changes in slope of the plotted or mechanically traced heating and cooling curves. When such data are secured under nearly equilibrium conditions of heating and cooling, the method is commonly used for determining certain critical temperatures required for the construction of equilibrium diagrams. 一种通过记录发生热阻的温度来确定金属转变的方法。这些阻力表现为绘制或机械追踪的加热和冷却曲线斜率的变化。当这些数据在加热和冷却的近似平衡条件下得到保证时，该方法通常用于确定构建平衡图所需的某些临界温度。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Total elongation | 总伸长率 |
A total amount of permanent extension of a test piece broken in a tensile test. 拉伸试验中断裂试样的永久延伸总量。 |
| Horsepower | 马力 |
Unit indicating the rate at which work is done. The electrical equivalent of one horsepower is 746 watts. 单位表示完成工作的速率。一马力的电当量为746瓦。 |
| Slug | 猛击 |
1. A starting workpiece for forging and similar operations, such as a length of wire or rod to make a bolt blank on which a thread can be rolled or cut. 2. (geepound) An obsolete imperial (non-SI) unit of mass, being the mass which under an acceleration of one foot per second squared gives a force of one pound-force. The conversion to SI is 1 slug = 14.593 902 94 kg. 3. A large-scale flow structure which occurs in the transition from laminar to turbulent flow in a pipe. 1.一种用于锻造和类似操作的起始工件，如用于制造螺栓毛坯的一段线材或棒材，在该毛坯上可以轧制或切割螺纹。2.（吉磅）一种已被淘汰的英制（非国际单位制）质量单位，在一英尺/秒平方加速度下产生一磅力的质量。转化为SI国际单位制的转化率为1slug=14.59390294kg。3.一种大规模流动结构，其发生在管道中从层流到湍流的过渡中。 |
| Eyebolt (eyescrew) | 吊环螺栓（眼螺丝） |
A bolt threaded at one end and bent to a loop at the other end. A bolt or screw with a closed loop in place of a head. 一端有螺纹，另一端弯曲成环的螺栓。带有闭合环代替头部的螺栓或螺钉。 |
| Oil-cooled | 油冷却 |
A term for a machine that uses circulating oil to remove heat. 使用循环油散热的机器的术语。 |
| Fluid mechanics | 流体力学 |
The study of fluids in motion (fluid dynamics) or fluid statics where there is no relative motion between fluid particles. Fluid statics concerns primarily the variation of pressure with altitude or depth; it includes aerostatics and hydrostatics. Fluid dynamics includes the topics of aerodynamics, gas dynamics, hydraulics, hydrodynamics and many aspects of acoustics, chemical engineering, flight, lubrication, meteorology, non-Newtonian fluid flow, oceanography, power-plant technology, propulsion, and turbomachinery. 研究运动中的流体（流体动力学）或流体静力学，其中流体粒子之间没有相对运动。流体静力学主要关注压力随高度或深度的变化；它包括空气静力学和流体静力学。流体动力学包括空气动力学、气体动力学、水力学、流体动力学以及声学、化学工程、飞行、润滑、气象学、非牛顿流体流动、海洋学、发电厂技术、推进和涡轮机械的许多方面。 |
| Charles law/Charles' law | 查尔斯定律 |
(Gay–Lussac law) The volume of a fixed mass of gas at constant pressure is proportional to its absolute temperature. The volume of a gas at constant pressure is directly proportional to its absolute temperature. （盖-吕萨克定律）在恒定压力下，固定质量气体的体积与其绝对温度成正比。恒压下气体的体积与其绝对温度成正比。 |
| Crest of screw thread | 螺纹牙顶 |
The top surface joining the two sides of flanks of a thread. 连接螺纹牙侧两侧的顶面。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Creep–time relations | 蠕变时间关系 |
Algebraic or numerical relations between creep strain and time at constant stress. 恒定应力下蠕变应变与时间之间的代数或数值关系。 |
| Acoustic pyrometer | 声学高温计 |
A non-intrusive pyrometer based on the principle that the sound speed in a gas is proportional to the square root of its absolute temperature. 一种非侵入式高温计，其原理是气体中的声速与其绝对温度的平方根成正比。 |
| Hot quenching | 热淬火 |
An imprecise term used to cover a variety of quenching procedures in which a quenching medium is maintained at a prescribed temperature above 70 °C (160 °F) 一个不精确的术语，用于涵盖各种淬火程序，其中淬火介质规定温度保持在70°C（160°F）以上。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Hot-wire test | 热线测试 |
Method used to test heat extraction rates of various quenchants. Faster heat-extracting quenchants will permit more electric current to pass through a standard wire because it is cooled more quickly. Compare with hot-wire analyzer. 用于测试各种淬火剂的热提取率的方法。与热线分析仪相比，更快的热提取淬火剂将允许更多电流通过标准导线，因为标准导线冷却更快。 |
| Screw | 螺钉 |
Threaded fastener designed to be used in a tapped or untapped (e.g., wood screw) hole, but not with a nut. A fastener with a screw thread cut or rolled into its cylindrical or conical shank, intended either to cut its own thread (as in a wood screw) or engage in a threaded hole. A self-tapping screw (sheet-metal screw, tapping screw) has a sufficiently hard thread that it cuts an internal thread in thin sheet or a component made of soft material when driven into a hole in the sheet or component. The screw head is the part of a screw used to apply torque to the screw. Common screw-head designs are circular in cross section with a diametral slot or cross, or hexagonal and recessed with a cross or hexagon. A screw thread is one or more continuous helical grooves of uniform section along either the exterior surface (male thread) or the interior surface (female thread) of a cylindrical or conical body. The three-dimensional shape that results when the thread cross section is rotated and axially advanced along an axis is called a helicoid, the angle that the thread makes when projected on to the axis being called the angle of inclination. Threads are employed in fasteners such as bolts, nuts, and screws; location and measuring instruments; in power drives; in some electrical fittings (Edison thread); and on the ends of crankshafts to suppress oil leakage (thrower thread). Parallel threads are formed on cylinders; tapered threads on cones, typically with a taper rate of 1:16. A screw with a righthanded thread appears to move away from the observer when turned clockwise. All standard screws, bolts and nuts have right-hand threads, but left-handed threads are sometimes employed. The axial distance between corresponding points on adjacent threads is called the screw pitch or screw rate and, for a single continuous helical groove (a single-start thread), is the same as the change in axial distance (the lead) between a nut and the head of a bolt during one revolution, the number of thread forms per mm then being the reciprocal of the pitch. For the same screw diameter, coarse threads have fewer threads per mm than fine threads. A multiple-start screw thread (usually coarse, see later) consists of two or more identical threads running simultaneously along its axis so as to provide greater bearing area and greater velocity ratio. The starts are separated by 180° (double start), 120° (triple start), 90° (quadruple start) etc., depending upon the number of threads. Thus, in double-start threads, the lead is twice the pitch; and so on. The axial distance between corresponding points on two adjacent threads in a multiple start thread is called the divided pitch. The position on a screw thread where there is equal distance between the flanks on the solid part of the thread and in the space between the threads is the pitch point, the associated diameter of which is termed the pitch diameter. The basic nomenclature for threads, some of which is common with that for toothed gearing, is shown in the diagrams. A helix formed or cut on a cylindrical surface which may advance along the axis to the right or left. The helix may be single or multiple. 一种螺纹紧固件，设计用于攻丝或未攻丝（如木螺钉）孔，但不与螺母配合使用。其螺纹被切割或卷成圆柱形或锥形柄，用于切割自身螺纹（如木螺钉）或嵌入螺纹孔。自攻螺钉（钣金螺钉、自攻螺钉）具有足够硬的螺纹，当打入薄板或部件中的孔时，它会在薄板或软材料部件中切割内螺纹。螺钉头是螺钉的一部分，用于向螺钉施加扭矩。常见的螺钉头设计为横截面为圆形，带有直径槽或十字，或为六边形，并带有十字或六边形凹槽。螺纹是沿圆柱形或锥形体的外表面（外螺纹）或内表面（内螺纹）具有均匀截面的一个或多个连续螺旋槽。当螺纹横截面旋转并沿轴轴向前进时产生的三维形状称为螺旋面，螺纹投影到轴上时形成的角度称为倾角。螺纹用于紧固件，如螺栓、螺母和螺钉；定位和测量仪器；在动力驱动中；在一些电气配件中（爱迪生螺纹）；并安装在曲轴端部，以抑制漏油（抛掷器螺纹）。在圆柱体上形成平行螺纹；圆锥上的锥形螺纹，通常具有1:16的锥形率。当顺时针旋转时，具有右手螺纹的螺钉似乎会远离观察者。所有标准螺钉、螺栓和螺母都有右手螺纹，但有时使用左手螺纹。相邻螺纹上对应点之间的轴向距离称为螺距或螺纹率，对于单个连续螺旋槽（单个起始螺纹），与螺母和螺栓头之间的轴向间距（导程）在一周内的变化相同，每mm的螺纹形式数为螺距的倒数。对于相同的螺钉直径，粗螺纹的每毫米螺纹数少于细螺纹。多头螺纹（通常为粗螺纹，见下文）由两个或多个沿其轴线同时延伸的相同螺纹组成，以提供更大的承载面积和更大的速比。根据螺纹的数量，起点之间的间隔为180°（双起点）、120°（三起点）、90°（四起点）等。因此，在双起始螺纹中，导程是螺距的两倍；多起点螺纹中两个相邻螺纹上对应点之间的轴向距离称为分割螺距。螺纹上的位置，即螺纹实体部分的侧面和螺纹之间的空间之间的距离相等，即节点，其相关直径称为节径。图中显示了螺纹的基本术语，其中一些与齿轮传动的基本术语相同。在圆柱面上形成或切割的螺旋线，可沿轴线向右或向左前进。螺旋可以是单个或多个。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Crossed threads | 交叉螺纹 |
When the axis of a nut offered up to a bolt is not aligned with the axis of a bolt (or a screw to a threaded member), it may be possible for the threads to engage incorrectly and even for the nut or screw to advance a turn or more, but ultimately the misaligned threads become locked together. Forcing the nut in such circumstances may irretrievably damage the threads on both. 当提供给螺栓的螺母的轴线与螺栓（或螺纹构件的螺钉）的轴线不对齐时，螺纹可能会错误接合，甚至螺母或螺钉会提前一圈或更多，但最终未对齐的螺纹会锁定在一起。在这种情况下强行拧入螺母可能会对两侧的螺纹造成无法修复的损坏。 |
| Semiguided bend | 半导弯曲 |
The bend obtained by applying a force directly to the specimen in the portion that is to be bent. The specimen is either held at one end and forced around a pin or rounded edge, or is supported near the ends and bent by a force applied on the side of the specimen opposite the supports and midway between them. In some instances, the bend is started in this manner and finished in the manner of a free bend. 通过将力直接施加于待弯曲部分中的试样而获得的弯曲。将试样固定在一端，并围绕销或圆边施力，或者在靠近端部的位置支撑试样，并通过施加在试样与支撑件相对的一侧以及两者中间的力进行弯曲。在某些情况下，折弯以此方式开始，然后以自由折弯的方式结束。 |
| Fracture toughness | 断裂韧性 |
A generic term for measures of resistance to extension of a crack. The term is sometimes restricted to results of fracture mechanics tests, which are directly applicable in fracture control. However, the term commonly includes results from simple tests of notched or precracked specimens not based on fracture mechanics analysis. Results from tests of the latter type are often useful for fracture control, based on either service experience or empirical correlations with fracture mechanics tests. 裂纹扩展阻力测量的通用术语。该术语有时仅限于断裂力学试验的结果，这些结果直接适用于断裂控制。该术语通常包括非基于断裂力学分析的切口或预裂纹试样的简单试验结果。基于使用经验或与断裂力学试验的经验相关性，后一类试验的结果通常有助于断裂控制。 |
| Angle of torsion | 扭转角 |
(angle of twist) (Unit ° or rad) The angle relative to a chosen section, normal to the axis of twist, through which another part of a component rotates when subjected to a torque. （扭转角）（单位°或弧度）相对于选定截面的角度，垂直于扭转轴，部件的另一部分在受到扭矩时通过该角度旋转。 |
| Taper | 变尖 |
A gradual, often linear, reduction in cross section or shape. A shaft or hole that gets gradually smaller toward one end. 横截面或形状的逐渐减小，通常是线性的。一端逐渐变小的轴或孔。 |
| Surface tension (σ, γ) (Unit N/m) | 表面张力（σ，γ）（单位：N/m） |
At the interface between a liquid and a gas or two immiscible liquids, unbalanced cohesive forces acting on the liquid molecules at the interface lead to the property surface tension which causes tensile forces to develop as if it were a skin or membrane. 液体和气体或两种不混溶液体之间的界面处，作用在界面处的液体分子上的不平衡内聚力导致表面张力的性质，从而导致张力的发展，就像皮肤或薄膜一样。 |
| Salt-velocity meter | 盐速计 |
A volume flow meter based on detecting the transit time for a small quantity of salt or radioactive isotope in a flow by measuring electrical conductivity or radiation level. 一种体积流量计，通过测量电导率或辐射水平来检测流量中少量盐或放射性同位素的渡越时间。 |
| Thermal energy (heat energy) (Unit J) | 热能（单位：J） |
The sensible and latent forms of internal energy. 内能的感知和潜在形式。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Plowing | 犁 |
In tribology, the formation of grooves by plastic deformation of the softer of two surfaces in relative motion. 在摩擦学中，通过相对运动的两个表面中较软的表面的塑性变形形成凹槽。 |
| Athermal transformation | 非热变化 |
A reaction that proceeds without benefit of thermal fluctuations; that is, thermal activation is not required. In contrast, a reaction that occurs at constant temperature is an isothermal transformation; thermal activation is necessary in this case and the reaction proceeds as a function of time. 在没有热波动的情况下进行的反应；也就是说，不需要热激活。相反，在恒温下发生的反应是等温转变。在这种情况下，热活化是必要的，并且反应作为时间的函数进行。 |
| V-block | V型块 |
A block having a 90° V-shaped recess; used in a workshop to hold round workpieces. 具有90°V形凹槽的块体；在车间里用来装圆形工件。 |
| Supercooling | 过冷 |
Cooling below the temperature at which an equilibrium phase transformation can take place, without actually obtaining the transformation. 在没有实际获得相变的情况下，冷却到可以发生平衡相变的温度以下。 |
| Acoustic separation | 声学分离 |
(Unit m) The separation of particles in a fluid using standing acoustic waves, typically ultrasound, to drive them to nodal points (acoustic particle concentration). （单位m）使用驻声波（通常是超声波）将流体中的粒子分离，以将它们驱动到节点（声学粒子浓度）。 |
| Centrifuge | 离心机 |
A machine incorporating a rapidly spinning drum in which liquids and suspended particles of different densities are separated by centrifugal action. 一种装有快速旋转滚筒的机器，在该滚筒中，不同密度的液体和悬浮颗粒通过离心作用分离。 |
| Differential heating | 差动加热 |
Heating that intentionally produces a temperature gradient within an object such that, after cooling, a desired stress distribution or variation in properties is present within the object. 加热有意在物体内产生温度梯度，从而在冷却后，在物体内出现所需的应力分布或特性变化。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Creep fatigue | 蠕变疲劳 |
The effects of combined creep and fatigue at high homologous temperatures in metals, and in other materials such as polymers having time-dependent behaviour. 金属和其他材料（例如具有时间相关行为的聚合物）在高同源温度下的组合蠕变和疲劳的影响。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Sliding-vane compressor | 滑片压缩机 |
(rotary-vane compressor, vane compressor) A rotary compressor in which gas is compressed as the spaces between spring-loaded sliding vanes held in an offset rotor reduce as the rotor revolves within a cylindrical housing. （旋转叶片压缩机，叶片压缩机）一种旋转式压缩机，当转子在圆柱形外壳内旋转时，偏置转子中的弹簧加载滑动叶片之间的空间减小，从而压缩气体。 |
| Ferralium | 铁素体钢 |
Ferralium is a type of Super Duplex Stainless Steel which is optimised for use within fasteners. 一种超级双相不锈钢，经过优化用于紧固件。 |
| Sample standard deviation (s) | 样本标准偏差（s） |
The square root of the sample variance. It is a point estimate of the population standard deviation, a measure of the “spread”of the frequency distribution of a population. This value of sprovides a statistic that is used in computing interval estimates and several test statistics. For small sample sizes, s underestimates the population standard deviation. 样本方差的平方根。它是总体标准偏差的点估计，是总体频率分布“扩散”的度量。SPR的这个值提供了一个用于计算区间估计和若干测试统计量的统计量。对于小样本，s低估了总体标准偏差。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| Compression failure | 压缩失败 |
The reduction or removal of a component’s load-bearing capacity in compression, caused by buckling, fracture, crease formation in fibre composites, etc. 由纤维复合材料中的屈曲、断裂、折痕形成等引起的部件在压缩中的承载能力的降低或消除。 |
| Ion carburizing | 离子渗碳 |
A method of surface hardening in which carbon ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma carburizing or glowdischarge carburizing. 一种表面硬化方法，利用高压电能将碳离子在真空中扩散到工件中。与等离子渗碳或辉光放电渗碳同义。 |
| Plane-stress fracture toughness (Kc) | 平面应力断裂韧性（Kc） |
In linear-elastic fracture mechanics, the value of the crack-extension resistance at the instability condition determined from the tangency between the R-curve and the critical crack-extension force curve of the specimen. 在线弹性断裂力学中，由试样的R曲线和临界裂纹扩展力曲线之间的切线确定的不稳定条件下裂纹扩展阻力的值。 |
| Threshold stress for stress-corrosion cracking (σth) | 应力腐蚀开裂阈值应力（σth） |
An experimentally determined critical gross-section stress below which stress-corrosion cracking will not occur under specified test conditions. 实验确定的临界总截面应力，低于该应力，在规定的试验条件下不会发生应力腐蚀开裂。 |
| Composite material | 复合材料 |
(composite structure) A general term used of two or more materials or structures acting in combination (e.g. concrete, reinforced concrete, filamentreinforced polymers, laminated materials, particulate-reinforced materials, flitched beams), resulting in values of strength, stiffness, or toughness greater than the base matrix material alone. （复合结构）用于组合作用的两种或多种材料或结构的通用术语（例如混凝土、钢筋混凝土、纤维增强聚合物、层压材料、颗粒增强材料、切割梁），从而产生强度、刚度或韧性值大于单独的基体材料。 |
| Size dimension (Unit m) | 尺寸范围（单位：米） |
The specified value of a diameter, length, width, etc. of a feature required to specify the finished form of a component or assembly. 指定部件或组件的成品形状所需的特征的直径、长度、宽度等的指定值。 |
| Engine | 引擎 |
A machine that converts energy, including the chemical energy in a fuel and electrical energy, into mechanical energy, usually to produce power delivered through a rotating shaft or thrust. Examples include internal-combustion engines, gas and steam turbines, rocket engines, electric, hydraulic and pneumatic motors. 一种将能量（包括燃料中的化学能和电能）转换为机械能的机器，通常通过旋转轴或推力产生动力。例子包括内燃机、燃气轮机和蒸汽轮机、火箭发动机、电动、液压和气动马达。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Ferrite | 铁素体 |
A solid solution of one or more elements in body-centered cubic iron. Unless otherwise designated (for instance, as chromium ferrite), the solute is generally assumed to be carbon. On some equilibrium diagrams, there are two ferrite regions separated by an austenite area. The lower area is alpha ferrite; the upper, delta ferrite. If there is no designation, alpha ferrite is assumed. 一种或多种元素在体心立方铁中的固溶体。除非另有说明（例如，铁酸铬），否则通常假定溶质为碳。在一些平衡图上，有两个铁素体区域被一个奥氏体区域隔开。下部区域为α铁素体；上部，δ铁氧体。如果没有指定，则假定为 α 铁氧体。 |
| Spalling | 剥落 |
The separation of macroscopic particles from a surface in the form of flakes or chips. 以薄片或碎片形式从表面分离宏观颗粒。 |
| Refractory materials | 耐火材料 |
Metals or ceramics that do not melt when exposed to temperature above about 1 500°C or deteriorate rapidly in a continuous temperature above about 550°C. 当暴露于高于约1500°C的温度时不熔化或在高于约550°C的连续温度下快速劣化的金属或陶瓷。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Pitch diameter | 中径 |
For screw threads, the diameter of an imaginary cylinder, the surface of which would pass through the threads at such points that would make the width of the groove and width of the land equal to one half the pitch. 对于螺纹，指一个假想圆柱体的直径，其表面将在使凹槽宽度和焊盘宽度等于螺距一半的点穿过螺纹。 |
| Sizing | 颗粒化 |
1. A finishing operation to ensure the specified dimensions and tolerances for a component are met. 2. (size classification) Separating an aggregate of mixed particles into groups according to size using a series of screens. 1.精加工操作，以确保满足部件的规定尺寸和公差。2.（粒度分类）使用一系列筛网根据粒度将混合颗粒的聚集体分成组。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Working load (Unit N) | 工作负荷（单位：N） |
The tension in a bolt in use; tension produced by a combination of Residual preload and a portion (usually) of any External load. The Joint diagram is usually used to predict the approximate working load a fastener will see in service. The load under which a component or structure is designed to operate under normal conditions. 螺栓在使用中的张力；残余预载荷和部分（通常）任何外部载荷的组合产生的张力。连接图通常用于预测紧固件在使用中的近似工作载荷。部件或结构设计为在正常条件下运行的荷载。 |
| Bolt stress (Unit Pa) | 螺栓应力（单位Pa） |
The axial tensile stress induced in a bolt by tightening. 通过拧紧在螺栓中产生的轴向拉应力。 |
| Mean value | 平均值 |
The average value of a number of data points. Computed by dividing the sum of all data by the number of data points. 多个数据点的平均值。通过将所有数据的总和除以数据点的数量来计算。 |
| Shrink ring | 预紧环 |
A ring, which is expanded by heating, is placed around an assembly of parts, and then contracts upon cooling to hold the assembly in place. 通过加热膨胀的环被放置在零件组件周围，然后在冷却时收缩以将组件固定到位。 |
| Finish annealing | 精制退火 |
A subcritical annealing treatment applied to cold-worked low- or medium-carbon steel. Finish annealing, which is a compromise treatment, lowers residual stresses, thereby minimizing the risk of distortion in machining while retaining most of the benefits to machinability contributed by cold working. Compare with final annealing. 适用于冷加工低碳钢或中碳钢的亚临界退火处理。与最终退火相比，精加工退火是一种折衷处理，可降低残余应力，从而最大限度地降低加工中的变形风险，同时保留冷加工对可加工性的大部分好处。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Artificial aging | 人工时效 |
Aging above room temperature. 在室温以上的时效。 |
| Combined carbon | 复合碳 |
The part of the total carbon in steel or cast iron that is present as other than free carbon. 钢或铸铁中总碳中除游离碳外的部分。 |
| Final annealing | 最终退火 |
An imprecise term used to denote the last anneal given to a nonferrous alloy prior to shipment. 一个不精确的术语，用于表示有色金属合金在装运前的最后一次退火。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Columnar structure | 柱状结构 |
A coarse structure of parallel elongated grains formed by unidirectional growth, most often observed in castings, but sometimes in structures resulting from diffusional growth accompanied by a solid-state transformation. 由单向生长形成的平行细长晶粒的粗略结构，最常见于铸件中，但有时也出现在伴随固态转变的扩散生长产生的结构中。 |
| Valve spring | 气门弹簧 |
The spring that restores a valve to its closed position after having been opened, and is also intended to prevent valve bounce. 在阀门打开后将其恢复到关闭位置的弹簧，也用于防止阀门反弹。 |
| Nut | 螺母 |
A metal fastener of square, hexagon or other shape, having an internal thread which screws onto a bolt, stud or arbor. An internally-threaded fastener used with externally-threaded bolts. Usually hexagonal in shape but there is a multitude of other geometries, such as square, for special purposes and different gripping tools. 一种方形、六角形或其他形状的金属紧固件，具有内螺纹，可拧在螺栓、螺柱或心轴上。与外螺纹螺栓一起使用的内螺纹紧固件。通常为六边形，但也有许多其他几何形状，如方形，用于特殊用途和不同的夹持工具。 |
| Nut thickness | 螺母厚度 |
The nut thickness shall be the overall distance measured parallel to the axis of nut, from the top of the nut to the bearing surface, and shall include the thickness of the washer face where provided. 螺母厚度应为平行于螺母轴线测量的从螺母顶部到轴承表面的总距离，还应包括垫圈表面的厚度。 |
| Offset yield strength | 条件屈服强度 |
The stress at which the strain exceeds by a specified amount (the offset) an extension of the initial proportional portion of the stress-strain curve. Expressed in force per unit area. 应变超过应力-应变曲线初始比例部分延伸规定量（偏移）的应力。以每单位面积的力表示。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Monotron hardness test | 摩诺硬度试验 |
An obsolete method of determining indentation hardnessby measuring the load required to force a spherical penetrator into a metal to a specified depth. 一种已被淘汰的方法，通过测量将球形侵彻体压入金属至规定深度所需的载荷来确定压痕硬度。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Nipple | 喷嘴 |
A device containing a non-return valve screwed into a lubrication point through which grease may be introduced, for example into a bearing. 一种包含止回阀的装置，该止回阀拧入润滑点，通过该润滑点可以将润滑脂引入，例如轴承中。 |
| Rosette | 玫瑰形的结 |
Strain gages arranged to indicate, at a single position, strain in three different directions. 应变计布置成在单个位置指示三个不同方向的应变。 |
| Centrifugal fan | 离心风机 |
A machine with a rotor consisting of a number of blades mounted around a hub and used for moving air or other gases. The gas enters the rotor axially and is discharged radially at increased pressure. 一种带有转子的机器，转子由安装在轮毂周围的许多叶片组成，用于移动空气或其他气体。气体轴向进入转子并在增加的压力下径向排出。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Quench hardening | 淬火硬化 |
(1) Hardening suitable alpha-beta alloys (most often certain copper to titanium alloys) by solution treating and quenching to develop a martensitic-like structure. (2) In ferrous alloys, hardening by austenitizing and then cooling at a rate such that a substantial amount of austenite transforms to martensite. （1）通过固溶处理和淬火硬化合适的α-β合金（通常是某些铜-钛合金），以形成类似马氏体的结构。（2）在铁合金中，通过奥氏体化硬化，然后以一定速度冷却，使大量奥氏体转变为马氏体。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Gage length | 标距 |
The original length of the portion of a specimen over which strain, change of length, or other characteristics are determined. 确定应变、长度变化或其他特性的试样部分的原始长度。 |
| Fog quenching | 雾淬 |
Quenching in a fine vapor or mist. 在细蒸汽或薄雾中淬火。 |
| Bolt gage | 螺栓量规 |
An ultrasonic instrument used to measure the stress or strain in bolts. 用于测量螺栓应力或应变的超声波仪器。 |
| Boyle’s law | 波义耳定律 |
The product of the pressure of a gas p and its volume is constant at a given absolute temperature T. Together with Charles law, it yields the ideal gas equation p = Mrt where m is the mass of gas and R is the specific gas constant. The volume of a gas at constant temperature is inversely proportional to the pressure. This means that as pressure increases, the volume of a gas decreases. 在给定的绝对温度T下，气体的压力p与其体积的乘积是恒定的。与查尔斯定律一起，它产生了理想的气体方程p=Mrt，其中m是气体的质量，R是特定的气体常数。恒温下气体的体积与压力成反比。这意味着随着压力的增加，气体的体积会减少。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Radial flow | 径向流 |
radial flow Fluid flow for which the principal direction of flow is either radially inward or radially outward relative to an axial direction. 径向流动流体流动的主要方向是径向向内或径向向外流动。 |
| Atomic volume | 原子体积 |
Volume of unit cell per atom. 每个原子的晶胞体积。 |
| Radiation pressure (Unit μPa) | 辐射压力（单位：μPa） |
The pressure exerted on a surface exposed to any form of electromagnetic radiation. If the radiation is absorbed, it is equal to the power-flux density divided by the speed of light. 施加在暴露于任何形式电磁辐射的表面上的压力。如果辐射被吸收，它等于功率通量密度除以光速。 |
| Yield stress | 屈服应力 |
The stress level of highly ductile materials, such as structural steels, at which large strains take place without further increase in stress. 高韧性材料（如结构钢）的应力水平，在该应力水平下发生大应变而不会进一步增加。 |
| Mechanical energy (Unit J) | 机械能（单位J） |
The sum of kinetic energy and potential energy for an object or a mechanical system, including the energy stored in springs, etc. 物体或机械系统的动能和势能之和，包括储存在弹簧等中的能量。 |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Transmissibility | 传递率 |
The ratio of the transmitted force to the disturbing force for a system subjected to a vibratory disturbance. The ratio may also be defined in terms of displacements, velocities, or accelerations. 受到振动干扰的系统的传递力与干扰力之比。该比率也可以用位移、速度或加速度来定义。 |
| High-tensile bolt | 高强度螺栓 |
(high-tension bolt) A bolt manufactured from an alloy steel that has a high tensile strength of about 1 GPa. （高压螺栓）由合金钢制成的螺栓，具有约1GPa的高抗拉强度。 |
| Tolerances | 公差 |
A fractional allowance for variation from the specifications. In mass production, using automatic machines, parts are intended to be completely or partially interchangeable, and in batch production parts should ideally fit without the need for selection. In practice it is impossible for mass-produced parts to have exactly the same size, owing to tool wear, variations in raw materials, thermal effects, etc. In consequence, variations from exactness, termed tolerances, are assigned to what is permissible on the basic size. 与规范不同的部分公差。在大规模生产中，使用自动机器时，零件应完全或部分可互换，在批量生产中，零件应理想匹配，无需选择。在实践中，由于刀具磨损、原材料变化、热效应等原因，批量生产的零件不可能具有完全相同的尺寸。因此，将精度偏差（称为公差）指定给基本尺寸上允许的尺寸。 |
| Oxygen probe | 定氧测头 |
An atmosphere-monitoring device that electronically measures the difference between the partial pressure of oxygen in a furnace or furnace supply atmosphere and the external air. 一种大气监测装置，以电子方式测量熔炉或熔炉供应大气中的氧分压与外部空气之间的差值。 |
| Torque arm | 扭力臂 |
A bar fixed at one end used to resist torque applied at the other, for example by an electric drill. 固定在一端的杆，用于抵抗施加在另一端的扭矩，如电钻。 |
| Contact strength (Unit N) | 接触强度（单位N） |
The maximum allowable load between contacting bodies converted into a stress. 换算成应力的接触体之间的最大允许载荷。 |
| Chafing fatigue | 磨损疲劳 |
Fatigue damage initiated in a surface damaged by rubbing against another body. 因与另一个物体摩擦而损坏的表面引起的疲劳损坏。 |
| Guided-bend test | 导向弯曲试验 |
A test in which the specimen is bent to a definite shape by means of a punch (mandrel) and a bottom block. 用冲头（心轴）和底块将试样弯曲成一定形状的试验。 |
| Celsius | 摄氏度 |
The temperature scale based on the freezing point of water (0ºC) and the boiling point of water (100ºC). The interval between these points is divided into 100 degrees. The scale was devised by Anders Celsius. 基于水的冰点（0ºC）和水的沸点（100ºC）的温标。这些点之间的间隔被划分为100度。这个比例是由安德斯·摄氏设计的。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Crushing strain | 压应变 |
The supposed single strain that results in comminution of a brittle material. The corresponding stress is termed the crushing strength. Neither quantity can be a material constant as they must obey the laws of fracture mechanics and will depend on the type of testpiece, method of loading etc. 导致脆性材料粉碎的假定单应变。相应的应力称为抗压强度。这两个量都不能是材料常数，因为它们必须遵守断裂力学定律，并取决于试件类型、加载方法等。 |
| Nanoparticles | 纳米颗粒 |
Particles with dimensions of order 1 nm which have either been introduced into microstructures for reinforcement or are present as impurities. 尺寸为1nm级的颗粒，其已被引入微结构中用于增强或作为杂质存在。 |
| Rotary piston flow meter | 旋转活塞流量计 |
A rotary liquid flow meter in which a cylindrical rotor, eccentrically mounted within a cylindrical casing, the axes of the two cylinders being parallel, is caused to rotate by the liquid flow. The flow rate is determined from the number of rotations of the rotor in a given time. 一种旋转式液体流量计，其中偏心安装在圆柱形外壳内的圆柱形转子，两个圆柱体的轴线平行，由液体流引起旋转。流量由转子在给定时间内的转数确定。 |
| Hard temper | 硬化回火 |
Same as full hard temper. 和全硬化回火一样。 |
| Turning angle (θ) | 转向角（θ） |
The change in direction experienced by a gas flow passing through an oblique shock wave or Prandtl–Meyer expansion fan. 气流通过斜激波或Prandtl–Meyer膨胀风机时所经历的方向变化。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Austempered steels | 等温钢 |
Medium to high carbon steels with improved mechanical properties as a result of austempering. After heating to between 800° and 900°C to form the austenite phase, they are quenched to, and held at, just above the martensite transformation range (between 260° and 370°C) to form bainite, before cooling further. Austempering of ductile cast irons results in a microstructure of bainite and spheroidal graphite. Austempered ductile irons have excellent toughness and wear properties. 由于等温淬火，机械性能得到改善的中高碳钢。在加热到800°和900°C之间形成奥氏体相后，将它们淬火并保持在略高于马氏体转变范围（260°和370°C之间）以形成贝氏体，然后进一步冷却。球墨铸铁的等温淬火导致贝氏体和球状石墨的微观结构。等温淬火球墨铸铁具有优异的韧性和耐磨性。 |
| Bypass flow meter | 旁通流量计 |
(shunt flow meter) A flow meter installed in a pipework bypass which may itself be part of the flow meter. An orifice plate is used to ensure a fraction of the main flow passes through the bypass. （分流流量计）安装在管道旁路中的流量计，它本身可能是流量计的一部分。孔板用于确保一部分主流通过旁路。 |
| Machine screw | 机械螺丝 |
A countersunk, slotted screw with machined threads such as are found on bolts. A relatively small screw, usually less than 20 mm in diameter, with the thread running along the whole length up to the head, intended to be screwed into threaded holes. If inserted through plain holes in assembled parts and held together by a nut, an undesirable contact surface of threads bearing against the surface of a hole results. 带有机加工螺纹的沉头开槽螺钉，如螺栓上的螺纹。一种相对较小的螺钉，直径通常小于20毫米，螺纹沿整个长度一直延伸到头部，用于拧入螺纹孔中。如果通过装配零件上的平孔插入并用螺母固定在一起，则会导致螺纹与孔表面接触不良。 |
| Tension | 拉伸 |
The force or load that produces elongation. 1. The condition in a bar, belt, cable, spring, string, wire, etc. that is being pulled from either end. 2. (tensile force) (unit N) The force associated with tension as in (1). It is measured by a tension meter. 伸长力产生伸长的力或载荷。1.从两端拉出的杆、带、电缆、弹簧、线、线等的状态。2.（张力）（单位N）与张力相关的力。 |
| Tap | 旋塞 |
1. A threaded hard metal plug for cutting screw threads in holes. It has longitudinal grooves for the clearance of chips while cutting. Progressive cutting is achieved by using three taps in succession: taper, second, and plug. First and second taps have tapers to help start the thread along the axis of the hole; the plug tap has no taper and is used on the final cut in a blind hole. 2. A valve in, or at the end of, a pipeline. 1.一种用于在孔中切割螺纹的螺纹硬金属塞。它具有纵向凹槽，用于在切割时清除切屑。渐进式切割通过连续使用三个丝锥实现：锥度、二次和塞。第一和第二丝锥具有锥度，以帮助沿孔的轴线开始螺纹；塞式丝锥没有锥度，用于盲孔的最终切割。2.管道中或管道末端的阀门。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Gear pump | 齿轮泵 |
A positive-displacement pump in which fluid is pumped by meshing gears, one driven and the other an idler gear, on parallel axes within a closed casing. 一种容积式泵，其中流体由啮合齿轮泵送，在封闭外壳内的平行轴上一个驱动，另一个为空套齿轮。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Rivet | 铆钉 |
A short rod with a head on one end that is inserted through aligned holes in plates to be joined, after which a second head is made on the protruding shank by hammering or forming. The most common head shapes are flat, domed, and inverse conical. In an array, the rivet pitch is the distance between the centres of adjacent rivets. Failure may occur by different mechanisms or modes. A one piece fastener consisting of a head and a body and used for fastening two or more pieces together by passing the body through a hole in each piece and then forming a second head on the body end. It cannot be removed except by taking off the head. 一种一端有头的短杆，插入待连接板上对齐的孔中，然后通过锤击或成型在突出的杆身上制作第二个头。最常见的头部形状是扁平、圆顶和倒锥形。在阵列中，铆钉间距是相邻铆钉中心之间的距离。故障可能由不同的机制或模式发生。一种一体式紧固件，由头部和主体组成，用于将两个或多个部件紧固在一起，方法是将主体穿过每个部件上的孔，然后在主体端部形成第二个头部。除非取下头部，否则无法移除。 |
| Flat head | 平头 |
Flat top surface and a conical bearing surface. 平顶表面和锥形轴承表面。 |
| Thermoelectric converter | 热电转换器 |
(thermoelectric generator) A device consisting of series-connected alternate n- and p-type semiconductor elements sandwiched between two ceramic plates. Due to the Seebeck effect, electrical power is generated when a temperature difference is maintained across the plates. Due to the Peltier effect, a thermoelectric converter can act as either a thermoelectric heater or a thermoelectric cooler (thermoelectric refrigerator) by passing an electrical current through it. The thermoelectric figure of merit (Z), with unit 1/K, is a dimensional parameter on which the efficiency of a thermoelectric device is primarily dependent, defined by Z = σα2/k where α is the Seebeck coefficient, σ is the electrical conductivity, and k is the thermal conductivity. The product of Z and a temperature is non-dimensional. （热电发生器）由串联连接的交替的n型和p型半导体元件夹在两块陶瓷板之间组成的装置。由于塞贝克效应，当板之间保持温差时，就会产生电能。由于珀尔帖效应，热电转换器可以通过使电流通过而充当热电加热器或热电冷却器（热电制冷机）。热电优值（Z）和第一单元/K是一个尺寸参数，热电装置的效率主要取决于此，由Z=σα2/K定义，其中α是塞贝克系数，σ是电导率，K是热导率。Z和温度的乘积是无量纲的。 |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Tightness parameter | 密封参数 |
A dimensionless parameter which defines the mass leakage of a gasket as a functionof contained pressure and a contained fluid constant. 一种无量纲参数，将垫圈的质量泄漏定义为所含压力和所含流体常数的函数。 |
| Hot dipping | 热浸 |
(hot-dip galvanizing) A process of coating an iron, steel, or aluminium object with a thin layer of zinc by passing it through a bath of molten zinc at a temperature of about 460°C. （热浸镀锌）通过使铁、钢或铝物体通过温度约为460°C的熔融锌浴，在铁、钢或铝物体上镀上一层薄薄的锌层的工艺。 |
| Maximum stress-intensity factor (Kmax) | 最大应力强度因子（Kmax） |
The maximum value of the stress-intensity factorin a fatigue cycle. 疲劳循环中应力强度因子的最大值。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Median fatigue strength at N cycles | N次循环的中位疲劳强度 |
An estimate of the stress level at which 50% of the population would survive N cycles. The estimate is derived from a particular point of the fatigue life distribution, because there is no test procedure by which a frequency distribution of fatigue strengths at Ncycles can be directly observed. 估计50%的量在N个周期内生存的压力水平。该估计值来自疲劳寿命分布的一个特定点，因为没有试验程序可以直接观察N次循环疲劳强度的频率分布。 |
| Cap nut | 盖型螺母 |
A nut with a blind threaded hole, for example a dome nut to cover the end of a bolt. 带有盲螺纹孔的螺母，例如用于覆盖螺栓末端的圆顶螺母。 |
| Profile | 轮廓 |
The shape of a cross section of an object, such as an aerofoil or cam. 物体的横截面形状，如机翼或凸轮。 |
| Scratch hardness test | 划痕硬度测试 |
A form of hardness test in which a sharp-pointed stylus or corner of a mineral specimen is traversed along a surface so as to determine the resistance of that surface to cutting or abrasion. 硬度测试的一种形式，用尖头笔或矿物样品的一角沿一个表面移动，以确定该表面的抗切割或耐磨性。 |
| Plane strain | 平面应变 |
The stress condition in linear-elastic fracture mechanics in which there is zero strain in a direction normal to both the axis of applied tensile stress and the direction of crack growth (i.e., parallel to the crack front); most nearly achieved in loading thick plates along a direction parallel to the plate surface. Under plane-strain conditions, the plane of fracture instability is normal to the axis of the principal tensile stress. 线弹性断裂力学中的应力条件，其中在垂直于施加拉应力轴和裂纹扩展方向（即平行于裂纹前沿）的方向上存在零应变；最接近于沿平行于板表面的方向加载厚板。在平面应变条件下，断裂失稳平面垂直于主拉应力轴。 |
| Elongation measurement | 伸张率测量 |
Bolt elongation is directly proportional to axial stress when the applied stress is within the elastic range of the material. If both ends of a bolt are accessible, a micrometer measurement of bolt length made before and after the application of tension will ensure the required axial stress is applied. 当施加的应力在材料的弹性范围内时，螺栓伸长率与轴向应力成正比。如果螺栓的两端都可以接近，则在施加张力前后对螺栓长度进行测微计测量，以确保施加所需的轴向应力。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Turbine | 涡轮 |
A turbomachine in which a rotor (turbine wheel) or impeller is caused to rotate and convert flow energy into shaft power or thrust. 转子（涡轮）或叶轮旋转并将流动能量转换为轴功率或推力的涡轮机。 |
| Angularity | 角度 |
The underfaces of the nut and the bolt head should be exactly perpendicular to the thread or shank axes. If the angle between the face and the axis is, for example, 868 or 948, the fastener is said to have an angularity of 48 (sometimes called Perpendicularity). 螺母和螺栓头的底面应与螺纹或柄轴完全垂直。例如，如果面和轴之间的角度为868或948，则称紧固件的角度为48（有时称为垂直度）。 |
| Altitude | 高度 |
(Unit m) Vertical height measured relative to a specified datum such as sea level. （单位m）相对于特定基准（例如海平面）测量的垂直高度。 |
| Outside diameter (Unit m) | 外径（单位：m） |
(external diameter, OD) The diameter of a circular cylindrical tube or a sphere measured between opposite points on the external surface. （外径，OD）在外表面上的相对点之间测量的圆柱管或球体的直径。 |
| Strain rate | 应变率 |
The time rate of straining for the usual tensile test. Strain as measured directly on the specimen gage length is used for determining strain rate. Because strain is dimensionless, the units of strain rate are reciprocal time. 通常拉伸试验的应变时间速率。直接在试样标距上测量的应变用于确定应变率。因为应变是无因次的，所以应变率的单位是倒数时间。 |
| Fitted bolt | 装配螺栓 |
A bolt with a plain unthreaded portion immediately beneath the head. 一种螺栓，其头部正下方有一个普通的无螺纹部分。 |
| Calorie | 卡路里 |
(cal, gram calorie, small calorie) An obsolete (i.e. non-SI) unit of energy equal to 4.186 8 J. It is the amount of energy needed to raise the temperature of 1 gram of pure airfree water from 14.5°C to 15.5°C at standard atmospheric pressure. （卡，克热量，小热量）一种已被淘汰的（即非SI）能量单位，等于4.1868J。它是在标准大气压力下将1克纯无空气水的温度从14.5℃升高到15.5℃所需的能量。 |
| Pressure control valve | 压力控制阀 |
A valve used to set the pressure level in a pressure vessel or piping system. 用于设置压力容器或管道系统中压力水平的阀门。 |
| Congruent transformation | 全等变换 |
An isothermal or isobaric phase change in which both of the phases concerned have the same composition throughout the process. 等温或等压相变，其中相关的两个相在整个过程中具有相同的成分。 |
| Load factor (F) | 负载系数（F） |
The ratio between an increase in bolt tension and the external load which has caused the increase. Factors reflecting the probability of an increase in load in a shear joint. Used in load and resistant factor design. 螺栓张力增加与导致增加的外部载荷之间的比率。反映剪切接缝中荷载增加概率的系数。用于载荷和阻力系数设计。 |
| Cavitation-resistance inducer | 抗气蚀诱导剂 |
An axial-flow pump used upstream of a main pump in order to prevent cavitation in the latter by increasing the inlet head. 在主泵上游使用的轴流泵，通过增加进口压头防止主泵出现气穴。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Materials selection | 材料选择 |
The process of selecting the most suitable material for a particular application. In the case of solid materials, it involves assessment of candidate materials in terms of their physical properties (density, elastic moduli, fracture toughness, yield strength, hardness, fatigue resistance, coefficient of thermal expansion, thermal conductivity, resistance to thermal shock, creep resistance, corrosion resistance, radiation resistance, etc), and such factors as the function of the final product, its shape, method of manufacture, required tolerances, number to be made, ease of inspection and quality control, cost, and design methodology employed. 为特定应用选择最合适材料的过程。对于固体材料，它涉及根据其物理特性（密度、弹性模量、断裂韧性、屈服强度、硬度、抗疲劳性、热膨胀系数、导热系数、抗热冲击性、抗蠕变性、耐腐蚀性、抗辐射性等）评估候选材料，以及诸如最终产品的功能、其形状、制造方法、所需公差、制造数量、检查和质量控制的容易程度、成本和采用的设计方法等因素。 |
| Specimen | 样品 |
A test object, often of standard dimensions or configuration, that is used for destructive or nondestructive testing. One or more specimens may be cut from each unit of a sample. 用于破坏性或无损检测的测试对象，通常具有标准尺寸或配置。可以从样品的每个单位切割一个或多个样品。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Regenerative pump | 涡流泵 |
(regenerative turbine pump, peripheral pump) A pump with a double-sided impeller having a large number of radial blades. The pressure of the pumped liquid increases progressively over several revolutions of the impeller. It is particularly suited to producing large heads at small flow rates without cavitation. （再生涡轮泵，外围泵）具有具有大量径向叶片的双面叶轮的泵。泵送液体的压力在叶轮的几圈内逐渐增加。它特别适合于在小流速下产生大水头且不产生气穴。 |
| Torsion-bar suspension | 扭杆悬架 |
A type of motor-vehicle suspension in which one end of a torsion bar is rigidly fixed to the chassis while the other carries a lever to which are attached the components that carry a wheel. In a torsion-beam suspension, a beam connects the wheels on either side of the vehicle. 一种汽车悬架，其中扭力杆的一端刚性固定在底盘上，而另一端带有一个杠杆，杠杆上连接着承载车轮的部件。在扭转梁悬架中，梁连接车辆两侧的车轮。 |
| Cooling stresses | 冷却应力 |
Residual stresses resulting from nonuniform distribution of temperature during cooling. 冷却过程中温度分布不均匀导致的残余应力。 |
| Toughening mechanisms | 增韧机理 |
Various methods of increasing the resistance to crack initiation and propagation in materials. They include transformation toughening, in which the microstructure around the crack tip alters so as to slow down or arrest cracks; deflexion of cracks; various ways of de-sharpening crack tips; fibre bridging of cracks; and fibre pull-out. 增加材料中裂纹萌生和扩展阻力的各种方法。它们包括相变增韧，其中裂纹尖端周围的微观结构发生变化，以减缓或阻止裂纹；裂纹偏转；消除裂纹尖端锐化的各种方法；纤维桥接裂纹；和纤维拉出。 |
| Achme thread | Achme螺纹 |
A screw thread having an included angle of 29° and largely used for feed screws on machine tools. 一种夹角为29°的螺纹，主要用于机床上的进给丝杠。 |
| Bimetallic strip | 双金属片 |
A strip formed by welding, riveting or brazing together two metals having different coefficients of expansion, which causes the strip to curl when its temperature changes. Typical combinations are steel and copper or steel and brass. 将两种膨胀系数不同的金属焊接、铆接或钎焊在一起形成的带材，当温度变化时，带材会卷曲。典型的组合是钢和铜或钢和黄铜。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Washer | 垫圈 |
An annular disc of metal, rubber, plastic, ceramic, etc., placed between two surfaces in contact either to spread the load (for example, between a surface and a tightened nut or a bolt head), to provide a seal, or to separate or align components. 由金属、橡胶、塑料、陶瓷等制成的环形圆盘，放置在两个接触面之间，以分散载荷（例如，在一个表面和拧紧的螺母或螺栓头之间），提供密封，或分离或对齐部件。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Abrasivity | 磨蚀性 |
The extent to which a surface, particle, or collection of particles will tend to cause abrasive wear when forced against a solid surface under relative motion and under prescribed conditions. 在相对运动和规定条件下，一个表面、颗粒或颗粒集合在被迫抵靠固体表面时趋向于引起磨粒磨损的程度。 |
| Decalescence | 退色 |
A phenomenon, associated with the transformation of alpha iron to gamma iron on the heating (superheating) of iron or steel, revealed by the darkening of the metal surface owing to the sudden decrease in temperature caused by the fast absorption of the latent heat of transformation. 一种现象，与铁或钢加热（过热）时α铁向γ铁的转变有关，由于转变潜热的快速吸收导致温度突然降低，金属表面变黑。 |
| Heat (q, Q) (Unit J) | 热量（q, Q）（单位J） |
A form of energy that is transferred across the boundary of a system at one temperature to another system (or the surroundings) at a different temperature by virtue of the temperature difference between them. Heat can be identified only as it crosses the boundary. A body can never be said to contain heat which is thus a transient phenomenon. 一种能量形式，由于它们之间的温差在一个温度下通过系统边界传递到另一个温度不同的系统（或环境）。只有当热量穿过边界时才能识别。一个物体不能说永远含有热量，这是一种瞬态现象。 |
| Q-factor | 品质因素 |
(quality factor, sharpness of resonance) A non-dimensional parameter that describes, for a given resonant mode, the sharpness of the peak in the frequency response of a lightly-damped linear oscillator: Q = ωRES/Δω where ωRES is the resonance frequency and Δω is the half-power bandwidth of the resonance. It is inversely related to the damping such that a broad peak corresponds to high damping and a narrow peak to low damping. （品质因数，共振尖锐度）一个无量纲参数，用于描述给定共振模式下，轻阻尼线性振荡器频率响应峰值的尖锐度：Q=ωRES/Δω，其中ωRES是共振频率，Δω是共振的半功率带宽。它与阻尼成反比，因此宽峰值对应于高阻尼，窄峰值对应于低阻尼。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Fatigue limit | 疲劳极限 |
The maximum stress that presumably leads to fatigue fracture in a specified number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. Compare with endurance limit. 在指定数量的应力循环中可能导致疲劳断裂的最大应力。还应说明最大应力值和应力比。与耐力极限比较。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| Dynamic modulus | 动态模量 |
The ratio of stress to strain under cyclic conditions (calculated from data obtained from either free or forced vibration tests, in shear, compression, or tension). 循环条件下的应力与应变之比（根据在剪切、压缩或拉伸中的自由或强制振动测试中获得的数据计算得出）。 |
| Spray quenching | 喷雾淬火 |
A quenching process using spray nozzles to spray water or other liquids on a part. The quench rate is controlled by the velocity and volume of liquid per unit area per unit of time of impingement. 使用喷嘴将水或其他液体喷射到零件上的淬火过程。淬火速率由每单位撞击时间内每单位面积的液体速度和体积控制。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Stress area | 应力面积 |
The effective cross-sectional area of the threaded section of a fastener. Used to compute average stress levels in that section. Based on the mean of pitch and minor diameters. 紧固件螺纹部分的有效横截面积。用于计算该截面中的平均应力水平。基于节距和小直径的平均值。 |
| Dead space | 死区 |
(dead volume) (Unit m³) That volume of a gas-filled thermometer in which the gas is not at the same temperature as that being measured. （死容）（单位m³）充气温度计的体积，其中气体的温度与被测温度不同。 |
| Snap temper | 快速回火 |
A precautionary interim stress-relieving treatment applied to high-hardenability steels immediately after quenching to prevent cracking because of delay in tempering them at the prescribed higher temperature. 在淬火后立即对高淬透性钢进行预防性临时应力消除处理，以防止因在规定的更高温度下回火延迟而开裂。 |
| Ferritic decarburization | 铁素体脱碳 |
Decarburization with sufficient loss of carbon to cause a lighter shade of tempered martensite and a significantly lower hardness than that of the adjacent base metal, with the presence of ferrite grains or grain boundary network under metallographic examination. 脱碳，碳损失充分，导致回火马氏体颜色较浅，硬度明显低于相邻母材，金相检查时存在铁素体晶粒或晶界网络。 |
| Shear test | 剪切试验 |
Any of several tests to obtain shear strength of a metal. Common tests used on mill products include the double-shear test, single-shear test, the blanking shear test (also known as the punching shear test) and the torsion test. 获得金属剪切强度的几种测试中的任何一种。轧机产品上常用的试验包括双剪试验、单剪试验、落料剪切试验（也称为冲切试验）和扭转试验。 |
| Range of stress (Sr) | 应力范围（Sr） |
The algebraic difference between the maximum and minimum stress in one cycle—that is, Sr = Smax – Smin 一个循环中最大和最小应力之间的代数差，即Sr=Smax–Smin |
| Blue brittleness | 蓝色脆性 |
Anomalous loss of ductility when quenched steels are tempered in the range 250–350°C (temperatures that produce blue tints on the surface of components). Brittleness exhibited by some steels after being heated to some temperature within the range of about 205 to 370 °C (400 to 700 °F), particularly if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. 当淬火钢在250–350°C范围内回火（在部件表面产生蓝色色调的温度）时，延展性异常损失。某些钢在加热到约205至370°C（400至700°F）范围内的某个温度后表现出脆性，特别是在高温下加工钢时。镇静钢几乎没有这种脆性。 |
| Total energy (Unit J) | 总能量（单位J） |
The sum of all forms of energy associated with a system, including kinetic, potential, internal, magnetic, chemical, and electrical energy. 与系统相关的所有形式能量的总和，包括动能、势能、内能、磁能、化学能和电能。 |
| Compression crease | 压缩折痕 |
A crease formed during the compression of composites having a high volume fraction of filaments. These composites fail in compression by forming a crease at an angle to the loading axis. 在压缩具有高体积分数长丝的复合材料期间形成的折痕。这些复合材料通过形成与加载轴成一定角度的折痕而在压缩中失效。 |
| Water hammer | 水锤 |
The reflected pressure surge that occurs in a liquid flowing through a pipe, usually as a consequence of sudden closure of a valve. The surge may cause the pipe to vibrate and a hammering noise to be heard. Key factors affecting the surge amplitude are the compressibility of the liquid (especially if it contains undissolved gas) and the elasticity of the pipe wall. 在流经管道的液体中发生的反射压力波动，通常是阀门突然关闭的结果。浪涌可能导致管道振动，并听到锤击噪音。影响喘振幅度的关键因素是液体的可压缩性（特别是当其含有未溶解气体时）和管壁的弹性。 |
| Acceleration-error constant | 加速度误差常数 |
When the reference (demand) input to a control system is parabolic, the output signal will also be parabolic in steady state. The signal that is constant in this situation is the acceleration and thus for a parabolic input the steady-state error, referred to as the acceleration-error constant, is the error in the acceleration. 当控制系统的参考（需求）输入是抛物线时，输出信号在稳定状态下也将是抛物线。在这种情况下恒定的信号是加速度，因此对于抛物线输入，称为加速度误差常数的稳态误差是加速度中的误差。 |
| Impact strength | 冲击强度 |
The resiliency or toughness of a solid as measured by impact energy. 用冲击能量测量的固体的弹性或韧性。 |
| Bernoulli’s law | 伯努利定律 |
For a steadily flowing fluid (liquid or gas), the sum of the pressure, kinetic energy per unit volume and potential energy per unit volume is constant at any point in the fluid. Using this relationship, it is possible to measure the velocity of a fluid by measuring its pressure at two points, as with a manometer or Pitot tube. 对于稳定流动的流体（液体或气体），压力、每单位体积的动能和每单位体积的势能之和在流体中的任何点都是恒定的。使用这种关系，可以通过在两个点测量流体的压力来测量流体的速度，就像使用压力计或皮托管一样。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Combined dimensioning | 组合尺寸标注 |
The use of chain dimensioning and parallel dimensioning on the same engineering drawing. 在同一工程图上使用链式尺寸标注和平行标注。 |
| Grain refiner | 晶粒细化机 |
A material added to a molten metal to induce a finer-than-normal grain size in the final structure. 添加到熔融金属中以在最终结构中产生比正常晶粒尺寸更细的材料。 |
| Austenite | 奥氏体 |
A solid solution of one or more elements in face-centered cubic iron. Unless otherwise designated (such as nickel austenite), the solute is generally assumed to be carbon. Solid solution of alloying elements and/or carbon in γ-Fe. It is named after British metallurgist W. C. Roberts-Austen. 一种或多种元素在面心立方铁中的固溶体。除非另有说明（如镍奥氏体），溶质通常假定为碳。合金元素和/或碳在γ-Fe中的固溶体。它以英国冶金学家WCRoberts-Austen的名字命名。 |
| Tera (T) | 特拉（T） |
An SI unit prefix indicating a multiplier of 1012; thus terawatt (TW) is a unit of power equal to one trillion watts. 指示乘数1012的SI单位前缀；因此，太瓦（TW）是等于1万亿瓦的功率单位。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| Radiosity (J) (Unit W/m²) | 辐射度（J）（单位W/m²） |
The total radiation leaving a given surface per unit area, including emitted, reflected, and transmitted radiation. 每单位面积离开给定表面的总辐射，包括发射、反射和透射辐射。 |
| Acoustic droplet ejection | 声液滴喷射 |
The ejection of small droplets from the surface of a liquid that results from focusing high-intensity ultrasound near the surface. 由于在表面附近聚焦高强度超声波而从液体表面喷射出小液滴。 |
| Grain size | 晶粒大小 |
A measure of the areas or volumes of grains in a polycrystalline metal, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. For metals, a measure of the areas or volumes of grains in a polycrystalline material, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. Grain sizes are reported in terms of number of grains per unit area or volume, average diameter, or as a grainsize number derived from area measurements. 多晶金属中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。多晶材料中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。晶粒尺寸以每单位面积或体积的晶粒数、平均直径或从面积测量得出的晶粒尺寸数来报告。 |
| Slip joint | 滑动接头 |
A mechanical connection which allows limited endwise relative movement of two components such as pipes, rods, and ducts. 一种机械连接，允许两个部件（如管道、杆和管道）进行有限的轴向相对运动。 |
| Thumb screw | 蝶形螺钉 |
A type of screw having a winged or knurled head for turning by hand when a quick and light clamping effect is desired. 一种螺钉，具有翼形或滚花头，当需要快速、轻夹紧效果时，可手动转动。 |
| Fin | 翼 |
A thin projecting rib. 一根细长的凸肋。 |
| British Standards Institution (BSI) | 英国标准协会（BSI） |
The Institution in the UK responsible for the preparation and publication of standard specifications (British standards) for manufactured goods, their design, manufacture and testing. 负责为制成品及其设计、制造和测试制定和发布标准规范（英国标准）的英国机构。 |
| Joint space | 关节空间 |
The description of the position and orientation of a robot in terms of the rotational angles and translational positions of the joints. Kinematic analysis, normally using homogeneous transforms, allows conversion between this description and the end‐effector position and orientation in x,y,z space. 根据关节的旋转角度和平移位置描述机器人的位置和方向。通常使用齐次变换的运动学分析允许在该描述与x、y、z空间中的末端执行器位置和方向之间进行转换。 |
| Cavitation damage | 气蚀损坏 |
Erosion of a solid surface through the formation and collapse of cavities or bubbles in an adjacent liquid that contains vapor and/or gas. 通过在包含蒸汽和/或气体的相邻液体中形成空穴或气泡并破坏固体表面。 |
| Tolerance limits | 公差极限 |
The extreme values (upper and lower) that define the range of permissible variation in size or other quality characteristic of a part. 定义零件尺寸或其他质量特性允许偏差范围的极值（上限和下限）。 |
| Nominal power (Unit kW) | 公称功率（单位kW） |
1. For an internal combustion engine, the average power output of a typical production engine under normal working conditions measured according to SAE standard J 1349/ISO 1585. 2. For an electric motor, the rated equivalent mechanical power output. 1.对于内燃机，根据SAE标准J 1349/ISO 1585测量的正常工作条件下典型生产发动机的平均功率输出。2.对于电动机，额定等效机械功率输出。 |
| Thread insert | 螺纹嵌件 |
(threaded bushing) Either a thin cylinder with an internal thread (and sometimes also an external thread) or a helical coil of wire, pressed or screwed into a hole to accept a bolt or screw. Used in material too soft or a component too thin to be threaded, to change one form of thread to another or to repair a damaged thread. （螺纹衬套）一种带有内螺纹（有时也有外螺纹）的薄圆柱体或螺旋形线圈，压入或拧入孔中以接受螺栓或螺钉。用于材料太软或部件太薄而无法螺纹连接，用于将一种形式的螺纹更换为另一种形式或修复损坏的螺纹。 |
| Absolute viscosity | 绝对粘度 |
A measure of the internal shear properties of fluids, expressed as the tangential force per unit area at either of two horizontal planes separated by one unit thickness of a given fluid, one of the planes being fixed and the other moving with unit velocity. 流体内部剪切特性的量度，表示为两个水平面中的任何一个上的单位面积切向力，两个水平面被给定流体的一个单位厚度隔开，其中一个平面固定，另一个以单位速度移动。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Fretting fatigue | 微动疲劳 |
Fatigue fracture that initiate at a surface area where fretting has occurred. The progressive damage to a solid surface that arises from fretting. 在发生微动的表面区域开始的疲劳断裂。由微动引起的对固体表面的渐进性损坏。 |
| Permissible variation | 允许偏差 |
For testing machines, the maximum allowable error in the value of the quantity indicated. It is convenient to express permissible variation in terms of the percent error. 对于试验机，所示数量值的最大允许误差。用误差百分比表示允许偏差是很方便的。 |
| Translational joint | 平移铰 |
A robot joint where the controlled variable is straight line movement. 控制变量为直线运动的机器人关节。 |
| Liquation temperature | 液化温度 |
The lowest temperature at which partial melting can occur in an alloy that exhibits the greatest possible degree of segregation. 偏析程度最高的合金发生部分熔融的最低温度。 |
| Strain hardening | 应变硬化 |
An increase in hardness and strengthcaused by plastic deformation at temperatures below the recrystallization range. Also known as work hardening. (workhardening) The increase in stress above the initial yield stress required to deform a metal to greater strains in the plastic range at temperatures below the recrystallization range (cold working). Unloading after some strain or work input gives a harder and stronger material. 在低于再结晶范围的温度下，塑性变形导致硬度和强度的增加。也称为加工硬化。（加工硬化）在低于再结晶范围（冷加工）的温度下，使金属在塑性范围内变形至更大应变所需的高于初始屈服应力的应力增加。在一定的应变或功输入后卸载，会得到更硬、更强的材料。 |
| Cold working | 冷加工 |
The plastic deformation of a metal, by rolling (cold rolling), drawing, forging (cold forging), etc. at a temperature well below its recrystallization temperature, which results not only in permanent shape change but also increase in strength and loss of ductility owing to work-hardening. 金属在远低于其再结晶温度的温度下通过轧制（冷轧）、拉拔、锻造（冷锻）等方式发生塑性变形，这不仅会导致永久的形状变化，还会增加强度并降低延展性由于加工硬化。 |
| Active vibration suppression | 主动振动抑制 |
The reduction of undesirable vibration in components by feedback control. 通过反馈控制减少部件中的不良振动。 |
| Pressure recovery (Unit Pa) | 压力恢复（单位Pa） |
The progressive increase in static pressure for unseparated flow through a diverging nozzle or diffuser. 通过发散喷嘴或扩散器的未分离流的静压逐渐增加。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Temperature factor | 温度系数 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. Accounts for the effects of thermal expansion and the temperature-induced change in the velocity of sound. 用于螺栓应力或应变超声波测量的校准常数。说明了热膨胀和温度引起的声速变化的影响。 |
| Scleroscope hardness number (HSc or HSd) | 硬化镜硬度值（HSc或HSd） |
A number related to the height of rebound of a diamond-tipped hammer dropped on the material being tested. It is measured on a scale determined by dividing into 100 units the average rebound of the hammer from a quenched(to maximum hardness) and untempered AISI W5 tool steel test block. 与落在被测材料上的菱形锤的回弹高度相关的数字。通过将锤子从淬火（达到最大硬度）和未淬火的AISI W5工具钢试块上的平均回弹分为100个单位来测量。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Stabilizing treatment | 稳定化处理 |
(1) Before finishing to final dimensions, repeatedly heating a ferrous or nonferrous part to or slightly above its normal operating temperature and then cooling to room temperature to ensure dimensional stability in service. (2) Transforming retained austenite in quenched hardenable steels, usually by cold treatment. (3) Heating a solution-treated stabilized grade of austenitic stainless steel to 870 to 900 °C (1600 to 1650 °F) to precipitate all carbon as TiC, NbC, or TaC so that sensitization is avoided on subsequent exposure to elevated temperature. （1）在精加工至最终尺寸之前，反复加热含铁或非铁零件至或略高于其正常工作温度，然后冷却至室温，以确保使用中的尺寸稳定性。（2）在淬火可淬硬钢中转变残余奥氏体，通常通过冷处理。（3）将固溶处理的稳定等级奥氏体不锈钢加热至870至900°C（1600至1650°F），使所有碳沉淀为TiC、NbC或TaC，从而避免在随后暴露于高温时敏化。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Notch ductility | 缺口延展性 |
The percentage reduction in area after complete separation of the metal in a tensile test of a notched specimen. 在缺口试样的拉伸试验中，金属完全分离后的面积减少百分比。 |
| Torricellean barometer | 托里塞莱气压计 |
A vertical glass tube with its upper end sealed and the lower end submerged in a pool of mercury. The space above the mercury is under vacuum. The height to which the mercury rises up the tube is a measure of the barometric pressure. 一种垂直的玻璃管，上端密封，下端浸入汞池中。水银上方的空间处于真空状态。水银在管道中上升的高度是大气压力的量度。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| Diagonal pitch (Unit m) | 对角线间距（单位米） |
The distance, when components in an assembly are staggered, between the position of a component in one row or column and the position of the corresponding component in the next row or column. The term is applied to rivets, turbine or compressor blades in a cascade, vortex generators on the surface of a wing, etc. 当部件中的零部件交错时，一行或一列中零部件的位置与下一行或下一列中相应零部件的位置之间的距离。该术语适用于铆钉、叶栅中的涡轮或压缩机叶片、机翼表面的涡流发生器等。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Grinding stress (Unit Pa) | 磨削应力（单位Pa） |
The residual stresses left in the surface of a component after grinding, owing to non-uniform cooling from the high surface temperatures produced. 由于产生的高表面温度造成的不均匀冷却，磨削后留在部件表面的残余应力。 |
| Absolute value error | 绝对值误差 |
The magnitude of the error dlsregarding the algebraic sign, or, for a vectorial error, disregarding its function. 关于代数符号的误差幅度，或者，对于矢量误差，不考虑其函数。 |
| Transformation temperature | 相变温度 |
The temperature at which a change in phase occurs. The term is sometimes used to denote the limiting temperature of a transformation range. The following symbols are used for iron and steels. 发生相位变化的温度。该术语有时用于表示转变范围的极限温度。以下符号用于钢铁。 |
| Proof stress | 弹性极限应力 |
(1) The stress that will cause a specified small permanent set in a material. (2) A specified stress to be applied to a member or structure to indicate its ability to withstand service loads. （1）在材料中引起规定的小永久变形的应力。（2）施加在构件或结构上的规定应力，以表明其承受工作荷载的能力。 |
| Verified loading range | 验证加载范围 |
For testing machines, the range of indicated loads for which the testing machine gives results within the permissible variation specified. 对于试验机，试验机在规定允许偏差范围内给出结果的指示载荷范围。 |
| Oldham coupling | 十字联轴节 |
(double-slider coupling) A device for connecting a pair of misaligned parallel shafts, on the end of each of which are flanges having diametral tenons (tongues) that engage with matching slots spaced at 90° in an intermediate disc. As the coupling rotates, the disc compensates for shaft offset by sliding along each tenon in turn. Low-friction surfaces are requisite and the disc is often made of a polymer. An alternative arrangement has the slots in the flanges and the tenons on the disc. （双滑块联轴器）一种连接一对未对准平行轴的装置，在每个平行轴的端部有法兰，法兰具有直径榫（舌），与中间盘中间隔90°的匹配槽接合。当联轴器旋转时，圆盘通过依次沿每个榫头滑动来补偿轴偏移。低摩擦表面是必需的，阀盘通常由聚合物制成。另一种布置方式是法兰上的槽和阀盘上的榫头。 |
| Springback | 回弹 |
The extent to which metal tends to return to its original shape or contour after undergoing a forming operation. 金属在经历成形操作后趋于恢复其原始形状或轮廓的程度。 |
| Degree (°) | 度数（°） |
A measure of plane angle such that 1° is 1/360 of a complete revolution and equal to π/180 rad. 平面角度的一种度量，使得1°是一整圈的1/360，等于π/180弧度。 |
| Relaxed stress | 松弛应力 |
The initial stress minus the remaining stress at a given time during a stress-relaxation test. 在应力松弛试验期间，初始应力减去给定时间的剩余应力。 |
| Starting torque (Unit N.m) | 起动扭矩（单位：N.m） |
The torque developed by a motor at zero rotational speed in order to initiate rotation of the applied load. 电机在零转速下产生的扭矩，以启动所施加负载的旋转。 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Air cleaner | 空气净化器 |
A device, such as a filter, hydrocyclone, or electrostatic precipitator, that removes particles and aerosols from a flow of air. 一种设备，例如过滤器、水力旋流器或静电除尘器，用于从气流中去除颗粒和气溶胶。 |
| Intense quenching | 强烈淬火 |
Quenching in which the quenching medium is cooling the part at a rate at least two and a half times faster than still water. 淬火，其中淬火介质以比静水快至少两倍半的速度冷却零件。 |
| Nominal stress | 名义应力 |
The stress at a point calculated on the net cross section by simple elasticity theory without taking into account the effect on the stress produced by stress raisers such as holes, grooves, fillets, etc. 通过简单弹性理论在净截面上计算的点处的应力，不考虑孔、槽、圆角等应力提升器产生的应力影响。 |
| Transfer moulding | 转移模塑 |
(resin-transfer moulding, RTM) A method of compression moulding polymers in which the dies are closed before the operation starts. （树脂传递模塑，RTM）一种对聚合物进行压缩模塑的方法，其中模具在操作开始前关闭。 |
| Stress-strain diagram | 应力-应变图 |
A graph in which corresponding values of stress and strain are plotted against each other. Values of stress are usually plotted vertically(ordinates or y-axis) and values of strain horizontally (abscissas or xaxis). Also known as deformation curve and stress-strain curve. 对应的应力和应变值相对绘制的图表。应力值通常垂直绘制（纵坐标或y轴），应变值水平绘制（横坐标或X轴）。也称为变形曲线和应力-应变曲线。 |
| B-basis | B-基础 |
Mechanical property value above which at least 90% of the population of values is expected to fall, with a confidence of 95%. 机械性能值超过该值时，至少90%的值预计会下降，置信度为95%。 |
| Fretting corrosion | 微动腐蚀 |
(1) The accelerated deterioration at the interface between contacting surfaces as the result of corrosion and slight oscillatory movement between the two surfaces. (2) A form of fretting in which chemical reaction predominates. Fretting corrosion is often characterized by the removal of particles and subsequent formation of oxides, which are often abrasive and so increase the wear. Fretting corrosion can involve other chemical reaction products, which may not be abrasive. （1）由于两个表面之间的腐蚀和轻微振荡运动，接触表面之间的界面加速劣化。（2）一种以化学反应为主的微动磨损形式。微动腐蚀通常以颗粒的去除和随后形成的氧化物为特征，这些氧化物通常具有研磨性，因此会增加磨损。微动腐蚀可能涉及其他化学反应产物，这些化学反应产物可能不是磨料。 |
| Torsion spring | 扭簧 |
1. A spring in the form of a torsion bar. 2. A helical spring to which torque can be applied at the ends. 1.一种扭杆形式的弹簧。2.一种螺旋弹簧，其端部可施加扭矩。 |
| Starting friction | 起动摩擦 |
(limiting friction, static friction, stiction) (Unit N) The force required to initiate movement between two bodies in contact. （极限摩擦力、静摩擦力、粘滞）（单位N）在两个接触物体之间启动运动所需的力。 |
| Anode | 阳极 |
That electrode in a battery or corrosion cell which produces electrons. It is the electrode which is destroyed (corrodes). 电池或腐蚀电池中产生电子的电极。被破坏（腐蚀）的是电极。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Forge | 锻造 |
To shape metal while holt and plastic by a hammering or forcing process. Dies used in process. 通过锤击或强制过程使金属成型，同时保持塑料成型。过程会使用模具。 |
| Available resource | 可用资源 |
(total resource) (Unit J) The total annual energy theoretically available from a renewable-energy source, such as ocean waves, the wind, or the total incident solar energy. （总资源）（单位J）理论上可从可再生能源（例如海浪、风或总入射太阳能）获得的年度总能量。 |
| Wire rope | 钢丝绳 |
A type of cable formed from individual strands of wire with a helical twist. 一种线缆，由具有螺旋扭曲的单独的线股形成。 |
| Tracking problem | 跟踪问题 |
A control problem where the set point changes with time and thus the plant output must follow the changing set point. The opposite of a regulator problem. 一种控制问题，其中设定值随时间变化，因此设备输出必须遵循变化的设定值。与调节器问题相反。 |
| Weight (W) (Unit N) | 重量（W）（单位：N） |
The force of attraction on a body due to gravity. A body’s weight is the product of its mass and the gravitational field strength at that point. Mass remains constant, but weight depends on the object’s position on the Earth’s surface, decreasing with increasing altitude. If g is the acceleration due to gravity, the weight of a mass m is given by W = mg. On Earth, the acceleration due to gravity is approximately 9.81 m/s², so that the weight of a 1 kg mass is 9.81 N. More generally, the weight is the force exerted on the mass of a body when in the gravitational field of another body. 重力由于重力作用在物体上的吸引力。物体的重量是其质量和该点引力场强度的乘积。质量保持不变，但重量取决于物体在地球表面的位置，随着海拔的升高而减小。如果g是重力引起的加速度，则质量m的重量由W=mg给出。在地球上，重力引起的加速度约为9.81m/s²，因此1千克质量的重量为9.81N。更一般地说，重量是在另一个物体的重力场中施加在物体质量上的力。 |
| Available head (Unit m) | 可用水头（单位米） |
In a hydroelectric power system, the difference between the vertical height of the water level in the supply reservoir above the turbine inlet less the head loss due to friction and fittings in the duct leading to the turbine. 在水力发电系统中，水轮机入口上方供水水库中水位垂直高度之间的差减去由于通向涡轮机的管道中的摩擦和配件造成的水头损失。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Submerged-electrode furnace | 浸入式电极炉 |
A furnace used for liquid carburizing of parts by heating molten salt baths with the use of electrodes submerged in the ceramic lining. 一种通过使用浸入陶瓷衬里中的电极加热熔融盐浴对零件进行液体渗碳的炉。 |
| Centigrade heat unit | 摄氏热量单位 |
(Celsius heat unit, CHU) An obsolete (i.e. non-SI) unit equal to the energy required to increase the temperature of one pound of pure, air-free water from 14.5°C to 15.5°C at a pressure of one standard atmosphere. （摄氏热量单位，CHU）一个已被淘汰的（即非国际单位制）单位，等于在一个标准大气压的压力下将一磅纯净的无空气水的温度从14.5°C提高到15.5°C所需的能量. |
| Temper color | 回火颜色 |
A thin, tightly adhering oxide skin that forms when steel is tempered at a low temperature, or for a short time, in air or a mildly oxidizing atmosphere. The color, which ranges from straw to blue depending on the thickness of the oxide skin, varies with both tempering time and temperature. 一种薄的、紧密粘附的氧化皮，当钢在低温或短时间内在空气或轻度氧化气氛中回火时形成。颜色范围从稻草色到蓝色，取决于氧化皮的厚度，随回火时间和温度而变化。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Damage tolerance | 损伤容限 |
(defect tolerance) A design philosophy that takes into account initial imperfections, crack-growth rates and conditions at final fracture, and uses fracture mechanics to demonstrate that cracks should not grow to their critical length within the design life (or at least should be capable of ready detection). （缺陷公差）考虑初始缺陷、裂纹扩展速率和最终断裂条件的设计理念，并使用断裂力学证明裂纹不应在设计寿命内增长到其临界长度（或至少应能够随时检测）。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Bolt blank | 螺栓毛坯 |
A rod on which a head has been formed, but on which no thread has been cut, from which bolts or screws may be made as required. 一种已形成头部但未切割螺纹的杆，可根据需要从中制造螺栓或螺钉。 |
| Spring load (Unit N) | 弹簧载荷（单位：N） |
A load exerted on a component by bending, compressing, extending, or twisting an attached spring. Mechanical energy stored in the spring can be released if any constraints on the component are removed. 通过弯曲、压缩、延伸或扭转连接的弹簧而施加在部件上的载荷。如果部件上的任何约束被移除，则可以释放弹簧中存储的机械能。 |
| Slenderness ratio | 长细比 |
The effective unsupported length of a uniform column divided by the least radius of gyration of the cross-sectional area. 均匀柱的有效无支撑长度除以横截面积的最小回转半径。 |