| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Coarsening | 粗粒化 |
An increase in the grain size, usually, but not necessarily, by grain growth. 晶粒尺寸的增加，通常但不一定是晶粒变大。 |
| Core | 核心 |
In a ferrous alloy prepared for case hardening, that portion of the alloy that is not part of the case . Typically considered to be the portion that (a) appears light on an etched cross section, (b) has an essentially unaltered chemical composition, or (c) has a hardness, after hardening, less than a specified value. 在为表面硬化而制备的铁合金中，合金中不属于表面的那部分。通常被认为是（a）在蚀刻横截面上看起来很轻，（b）化学成分基本不变，或（c）硬化后硬度低于规定值的那部分。 |
| Fracture stress | 断裂应力 |
The true normal stress on the minimum cross-sectional area at the beginning of fracture. This term usually applies to tension tests of unnotched specimens. 断裂开始时最小横截面积上的真实正应力。该术语通常适用于无缺口试样的拉伸试验。 |
| Butt joint | 对接接头 |
The end-to-end joining of two plates either by welding or by overlapping plates that are bolted or riveted. 通过焊接或通过螺栓或铆接的重叠板将两块板端对端连接。 |
| Span (Unit m) | 跨度（单位：m） |
A dimension measured between the extremities of a body or structure, such as between the tips of a wing or the supports of a bridge. 在身体或结构的末端之间测量的尺寸，如机翼尖端或桥梁支架之间。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Dynamic modulus | 动态模量 |
The ratio of stress to strain under cyclic conditions (calculated from data obtained from either free or forced vibration tests, in shear, compression, or tension). 循环条件下的应力与应变之比（根据在剪切、压缩或拉伸中的自由或强制振动测试中获得的数据计算得出）。 |
| Offset yield strength | 条件屈服强度 |
The stress at which the strain exceeds by a specified amount (the offset) an extension of the initial proportional portion of the stress-strain curve. Expressed in force per unit area. 应变超过应力-应变曲线初始比例部分延伸规定量（偏移）的应力。以每单位面积的力表示。 |
| Sampling | 抽样 |
The process of measuring a series of values of a time-varying quantity. 测量一系列时变量值的过程。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Low-E coating | 低辐射涂层 |
(low-emittance coating) A thin metallic or metal-oxide coating on a glass sheet to absorb and reflect infrared radiation. The coating is applied either by a pyrolytic chemical vapour-deposition process (hard coat), or by sputtering (soft coat). （低辐射涂层）玻璃板上的薄金属或金属氧化物涂层，用于吸收和反射红外辐射。通过热解化学气相沉积工艺（硬涂层）或溅射（软涂层）施加涂层。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Recrystallization temperature | 再结晶温度 |
The approximate minimum temperature at which complete recrystallization of a cold-worked metal occurs within a specified time. 冷加工金属在规定时间内发生完全再结晶的近似最低温度。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Bioengineering | 生物工程 |
(biological engineering) The application of engineering principles to biology, medicine, agriculture, etc. （生物工程）工程原理在生物学、医学、农业等方面的应用。 |
| Heat treatment | 热处理 |
(heat treating) Alteration of the mechanical properties of materials, particularly metals, by different sequences of heating, holding at temperature, and cooling at different rates. Heating and cooling a solid metal or alloy in such a way as to obtain desired conditions or properties. Heating for the sole purpose of hot working is excluded from the meaning of this definition. （热处理）材料，特别是金属的机械性能的改变，通过不同的加热顺序、温度保持和不同速率的冷却。加热和冷却固体金属或合金，以获得所需的条件或性能。仅用于热加工的加热不属于本定义的含义。 |
| Lead screw | 丝杠 |
The master screw running along the length of the bed of a lathe from which all screws threads on that machine are cut. Master screw used for cutting a screw thread in a lathe. 沿车床床身长度方向运行的主螺钉，该机床上的所有螺钉和螺纹都从主螺钉上切割下来。用于在车床上切削螺纹的主螺钉。 |
| Hot working | 热加工 |
Plastic deformation of a metal, by rolling, drawing, forging, etc., at a temperature above its recrystallization temperature (in commercial alloys above about 40% of their melting points in kelvins) which results in permanent shape change but no increase in strength or loss of ductility. 金属通过轧制、拉拔、锻造等在高于其再结晶温度（在商业合金中高于其熔点的40%的开尔文）的温度下发生塑性变形，导致永久的形状变化，但不会增加强度或失去延展性。 |
| Laser sintering | 激光烧结 |
A manufacturing technique by which parts are built layer by layer (each typically 20 μm thick) from plastic or metal (Direct Metal Laser Sintering, DMLS) material in powder form, each layer being sintered by a scanning laser. 一种制造技术，通过这种制造技术，零件由粉末形式的塑料或金属（直接金属激光烧结，DMLS）材料逐层（每个厚度通常为 20 微米）构建，每一层都由扫描激光烧结。 |
| Circular pitch | 齿距 |
The distance from the center of one gear tooth to the center of the next gear tooth measured on the pitch line. 在节线上测量的从一个轮齿中心到下一个轮齿中心的距离。 |
| Half hard | 半硬化回火 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength about mid-way between that of dead soft and full hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于完全软回火和完全硬回火之间。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Manometer | 压力计 |
An instrument used in the measurement of a pressure difference in a fluid (manometry). 用于测量流体压力差（测压）的仪器。 |
| Preload accuracy | 预载精度 |
A measure of the precision with which a given tool or procedure creates preload in a bolt when the bolt is tightened. A common torque wrench, for example, is said to produce preload with an accuracy of +30%. The mean preload, however, may not be that which the designer intended, or may not be what he should have intended. Accuracy as used here, in other words, is synonymous with Scatter. 当螺栓拧紧时，给定工具或程序在螺栓中产生预紧力的精度度量。例如，一个普通的扭矩扳手据说可以产生精度为+30%的预载。然而，平均预载可能不是设计者预期的。这里使用的准确度是分散度的同义词。 |
| Mechanical alloying | 机械合金化 |
Production of alloys from powders by consolidation, e.g. hotpressing or extrusion, followed by hot and/or cold working and final annealing. Materials such as dispersion-strengthened alloys, high-temperature aluminium alloys, and amorphous alloys can be made in this way. 通过固结（例如热压或挤压）从粉末生产合金，然后进行热和/或冷加工和最终退火。用这种方法可以制造弥散强化合金、高温铝合金和非晶合金等材料。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Vertical engine | 立式发动机 |
A piston engine having the cylinders above the crankshaft. 气缸位于曲轴上方的活塞发动机。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Physical testing | 物理测试 |
Methods used to determine the entire range of physical properties of a material. In addition to density and thermal, electrical, and magnetic properties, physical testing methods can be used to assess simple fundamental physical properties such as color, crystalline form, and melting point. 用于确定材料整个物理特性范围的方法。除了密度和热、电、磁特性外，物理测试方法还可用于评估简单的基本物理特性，如颜色、结晶形式和熔点。 |
| Ball mill | 球磨机 |
A mill for grinding and pulverizing materials, consisting of a horizontal rotating drum containing loose steel or ceramic balls. 一种用于研磨和粉碎物料的磨机，由装有松散钢球或陶瓷球的水平旋转滚筒组成。 |
| Compound pendulum | 复摆 |
A rigid body free to swing about an axis. 可绕轴自由摆动的刚体。 |
| Shoulder joint | 轴肩关节 |
The second joint on an articulated robot, which has a horizontal axis and is analogous to the human shoulder. 关节机器人上的第二个关节，具有水平轴，类似于人的肩膀。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Coefficient of cubic expansion | 立方膨胀系数 |
The fractional increase in volume per unit temperature rise. 每单位温度升高的体积增加分数。 |
| Celsius | 摄氏度 |
The temperature scale based on the freezing point of water (0ºC) and the boiling point of water (100ºC). The interval between these points is divided into 100 degrees. The scale was devised by Anders Celsius. 基于水的冰点（0ºC）和水的沸点（100ºC）的温标。这些点之间的间隔被划分为100度。这个比例是由安德斯·摄氏设计的。 |
| Binary vapour cycle | 二元蒸气循环 |
A power cycle which combines a steam cycle at relatively low temperature (the bottoming cycle) with a higher temperature cycle (the topping cycle) in which a working fluid such as mercury, sodium or potassium is used. 一种动力循环，它将相对低温的蒸汽循环（底部循环）与高温循环（顶部循环）相结合，其中使用了诸如汞、钠或钾之类的工作流体。 |
| Imperial system of units | 英制单位 |
British imperial system of units) An obsolete system of units first defined in the British Weights and Measures Act of 1824. Its three base units were second (time), yard (length), and pound avoirdupois (mass). The imperial unit of capacity was the gallon. The many associated units introduced subsequently include cubic inch, cubic foot, cubic yard, pint, and quart for both liquid and dry measures of capacity (i.e. volume); ounce, hundredweight, short and long ton for avoirdupois mass; poundal for force; minute and hour for time; fahrenheit for temperature; and British thermal unit for energy. Closely related to the imperial system of units is the US customary system of units. Each imperial unit is now legally defined in terms of the metric (i.e. SI) equivalent. （英帝国单位制）1824年英国度量衡法首次定义的已被淘汰的单位制。其三个基本单位为秒（时间）、码（长度）和磅（质量）。容量的英制单位是加仑。随后引入的许多相关单位包括立方英寸、立方英尺、立方码、品脱和夸脱，用于液体和干燥容量测量（即体积）；盎司，百分之一百重量，短吨和长吨，以保证重量；磅达表示力；以分钟和小时表示时间；华氏温度；英国热能单位。与帝国单位制密切相关的是美国习惯单位制。现在，每个英制单位在法律上都是以公制（即SI）当量来定义的。 |
| Full size body | 全尺寸螺纹杆 |
The body of a bolt or screw which has a diameter between the minimum and maximum limits of the major diameter of the thread. 螺栓或螺钉的主体，其直径介于螺纹大径的最小和最大限制之间。 |
| Pulse | 脉冲 |
An increase or decrease in the magnitude of a physical quantity, such as pressure, voltage, or force, with a time scale short compared with other time scales in a process, after which there is a return to the original level. 物理量的大小的增加或减少，如压力、电压或力，与过程中的其他时间尺度相比，时间尺度较短，之后返回到原始水平。 |
| Remaining stress | 残留应力 |
The stress remaining at a given time during a stress-relaxation test. See also stress relaxation. 在应力松弛试验期间在给定时间内剩余的应力。参见压力松弛。 |
| Fretting corrosion | 微动腐蚀 |
(1) The accelerated deterioration at the interface between contacting surfaces as the result of corrosion and slight oscillatory movement between the two surfaces. (2) A form of fretting in which chemical reaction predominates. Fretting corrosion is often characterized by the removal of particles and subsequent formation of oxides, which are often abrasive and so increase the wear. Fretting corrosion can involve other chemical reaction products, which may not be abrasive. （1）由于两个表面之间的腐蚀和轻微振荡运动，接触表面之间的界面加速劣化。（2）一种以化学反应为主的微动磨损形式。微动腐蚀通常以颗粒的去除和随后形成的氧化物为特征，这些氧化物通常具有研磨性，因此会增加磨损。微动腐蚀可能涉及其他化学反应产物，这些化学反应产物可能不是磨料。 |
| Black oxide | 黑色氧化物 |
A black finish on a metal produced by immersing it in hot oxidizing salts or salt solutions. 通过将金属浸入热氧化盐或盐溶液中产生的黑色饰面。 |
| Gasket stress | 垫片应力 |
The contact stress exerted on the gasket by the joint members. 连接件施加在垫片上的接触应力。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Tooth lock washers | 带齿锁紧垫圈 |
These washers serve to lock fasteners, such as bolts and nuts, to the component parts of an assembly, or increase the friction between the fasteners and the assembly. They are designated in a manner similar to helical spring lock washers, and are available in carbon steel. 这些垫圈用于将紧固件（如螺栓和螺母）锁定到组件的零部件上，或增加紧固件与组件之间的摩擦力。它们的设计方式类似于螺旋弹簧锁紧垫圈，可采用碳钢。 |
| Dislocation density | 位错密度 |
The total length of dislocation lines per unit volume, or the number of dislocation lines that cut through a unit cross-sectional area. 每单位体积的位错线的总长度，或穿过单位横截面积的位错线的数量。 |
| Damage | 损伤 |
1. The deterioration of a component or structure in fault or accident conditions, reducing or preventing its ability to perform its intended function. 2. The accumulation of defects or microcracks in the microstructure of a body loaded monotonically or in fatigue, which weakens the body and can lead to crack propagation and failure. 1.部件或结构在故障或事故条件下的劣化，降低或阻止其执行预期功能的能力。2.在承受单调载荷或疲劳载荷的物体的微观结构中累积的缺陷或微裂纹，这会削弱物体，并可能导致裂纹扩展和失效。 |
| Selective quenching | 局部淬火 |
Quenching only certain portions of an object. 仅淬火工件的某些部分。 |
| Coarse threads | 粗螺纹 |
Threads with relatively large separation between corresponding points on the threads. 螺纹上相应点之间的间距相对较大的螺纹。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| System engineering | 系统工程 |
A methodology which integrates all disciplines and specialty groups into a team effort, forming a structured development process that proceeds from concept to production to operation. 一种将所有学科和专业组整合到团队工作中的方法，形成从概念到生产再到运营的结构化开发过程。 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Temperature factor | 温度系数 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. Accounts for the effects of thermal expansion and the temperature-induced change in the velocity of sound. 用于螺栓应力或应变超声波测量的校准常数。说明了热膨胀和温度引起的声速变化的影响。 |
| Elongation | 伸张率 |
A term used in mechanical testing to describe the amount of extension of a test piece when stressed. 机械测试中使用的术语，用于描述试样在受力时的延伸量。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Wheel | 轮 |
A solid disc, or a circular ring with spokes radiating from a central hub, either attached to an axle around which it revolves or which revolves with a rotating axle. 一个实心圆盘，或一个带有辐条的圆环，辐条从一个中心毂放射出来，或附在一个绕其旋转的轴上，或与一个旋转轴一起旋转。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Alloy steels | 合金钢 |
Steels that contain alloying elements such as chromium, nickel, molybdenum, manganese, silicon, tungsten, and vanadium. These are added to improve properties such as the hardenability, toughness, strength, wear resistance, and corrosion resistance compared with those of plain-carbon steel. Low-alloy steels have a total alloy content (including carbon) of less than about 8%. They are hardenable and have strength up to 30% higher than plain-carbon steels. High-alloy steels contain considerably more alloy content and are developed for specific properties such as superior corrosion and chemical resistance. 含有铬、镍、钼、锰、硅、钨和钒等合金元素的钢。添加这些是为了提高与普通碳钢相比的淬透性、韧性、强度、耐磨性和耐腐蚀性等性能。低合金钢的总合金含量（包括碳）小于约8%。它们是可硬化的，强度比普通碳钢高出30%。高合金钢含有相当多的合金含量，并针对特定性能而开发，例如卓越的耐腐蚀性和耐化学性。 |
| Absolute specific gravity | 绝对比重 |
The ratio of the weight of any volume of a substance to the weight of an equal volume of a reference substance at the same temperature, often water at 4°C, both measured in a vacuum to avoid any effect of buoyancy. 在相同温度下，任何体积的物质的重量与等体积的参考物质的重量之比，通常是4°C的水，两者都是在真空中测量的，以避免任何浮力的影响。 |
| Design stress (Unit Pa) | 设计应力（单位Pa） |
The greatest allowable stress in a component or structure that will not result in failure under normal operating conditions. 在正常操作条件下不会导致失效的部件或结构中的最大许用应力。 |
| Friction loss (Unit J) | 摩擦损失（单位J） |
The conversion of mechanical energy to heat due to friction within a machine, mechanism, linkage, etc. 由于机器、机构、连杆等内部的摩擦而将机械能转化为热能。 |
| Water hammer | 水锤 |
The reflected pressure surge that occurs in a liquid flowing through a pipe, usually as a consequence of sudden closure of a valve. The surge may cause the pipe to vibrate and a hammering noise to be heard. Key factors affecting the surge amplitude are the compressibility of the liquid (especially if it contains undissolved gas) and the elasticity of the pipe wall. 在流经管道的液体中发生的反射压力波动，通常是阀门突然关闭的结果。浪涌可能导致管道振动，并听到锤击噪音。影响喘振幅度的关键因素是液体的可压缩性（特别是当其含有未溶解气体时）和管壁的弹性。 |
| Bend test | 弯曲试验 |
A test for determining the relative ductility of metal that is to be formed (usually sheet, strip, plate, or wire) or for determining soundness and toughness of metal (after welding, for example). The specimen is usually repeatedly bent over a specified diameter through a specified angle and then unbent for a specified number of cycles. There are four general types of bend tests, named according to the manner in which the forces are applied to the specimen to make the bend: free bend, guided bend, semiguided bend, and wrap-around bend. 确定待成形金属（通常为薄板、带材、板材或线材）的相对延展性或确定金属的坚固性和韧性（例如，焊接后）的试验。试样通常在规定的直径上重复弯曲一个规定的角度，然后在规定的循环次数内弯曲。弯曲试验有四种一般类型，根据施加在试样上的力进行弯曲的方式命名：自由弯曲、引导弯曲、半引导弯曲和环绕弯曲。 |
| Conditioning heat treatment | 调质热处理 |
A preliminary heat treatment used to prepare a material for desired reaction to a subsequent heat treatment. For the term to be meaningful, the exact heat treatment must be specified. 用于制备材料的初步热处理，以便对随后的热处理进行所需的反应。为了使该术语有意义，必须指定确切的热处理。 |
| Thermocouple | 热电偶 |
A device for measuring temperature, consisting of lengths of two dissimilar metals or alloys that are electrically joined at one end and connected to a voltage-measuring instrument at the other end. When one junction is hotter than the other, a thermal electromotive force is produced that is roughly proportional to the difference in temperature between the hot and cold junctions. 一种测量温度的装置，由两种不同的金属或合金组成，一端电连接，另一端与电压测量仪相连。当一个结比另一个结更热时，产生的热电动势大致与热结和冷结之间的温差成比例。 |
| Combustion chamber | 炉膛 |
1. In a piston engine, the volume between the head of an individual cylinder and the crown of the piston in which the fuel–air mixture burns during each power stroke of the engine. 2. (combustor) In a gas-turbine engine, a ramjet, an afterburner, or a rocket motor, the component, often cylindrical or annular in shape, in which the fuel–air mixture burns in a continuous-flow process. 1.在活塞式发动机中，在发动机的每个动力冲程中，燃料-空气混合物燃烧的单个气缸盖和活塞顶之间的体积。2.（燃烧室）在燃气涡轮发动机、冲压发动机、加力燃烧室或火箭发动机中，燃料-空气混合物在连续流动过程中燃烧的部件，通常为圆柱形或环形。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Two-stage compressor | 两级压缩机 |
A machine in which gas is compressed from low pressure toan intermediate pressure in a low-pressure cylinder, and then to final pressure in a highpressure cylinder. Efficiency is improved if the two cylinders are separated by an intercooler. 一种机器，其中气体在低压气缸中从低压压缩到中压，然后在高压气缸中压缩到最终压力。如果两个气缸由中冷器分离，则效率提高。 |
| Galling | 磨损 |
An extreme form of adhesive wear, in which large chunks of one part stick to the mating part (during sliding contact). 一种极端形式的粘着磨损，其中一个零件的大块粘在配合零件上（在滑动接触期间）。 |
| Static equilibrium | 静态平衡 |
A solid body, structure, or physical system (or any subdivided part) will be in static equilibrium, either at rest or moving with constant velocity, if the resultants of all external forces and moments acting on it are zero. 如果作用在固体上的所有外力和力矩的合力为零，则固体、结构或物理系统（或任何细分部分）无论是静止还是以恒定速度移动，都是处于静态平衡。 |
| Turboblower | 涡轮鼓风机 |
A centrifugal or axial compressor or fan. 离心式或轴流式压缩机或风扇。 |
| Failure | 失效 |
The result when a body, component, or structure is incapable of performing the task for which it was designed. The term is often used without reference to what causes failure, such as fracture, buckling, excessive deformation, wear, or erosion. Failure criteria (failure theories, theories of strength) are mathematical expressions for the combinations of stress, strain, or strain energy at which materials fail, which are employed in design to dimension components. 主体、部件或结构无法执行其设计任务时的结果。该术语通常未提及导致失效的原因，如断裂、屈曲、过度变形、磨损或侵蚀。失效准则（失效理论、强度理论）是材料失效时应力、应变或应变能组合的数学表达式，用于部件尺寸设计。 |
| Acceleration due to gravity | 重力加速度 |
(acceleration of free fall, gravitational acceleration, g) (Unit m/s²) The acceleration of a freely-falling body in a vacuum, with a mean value at sea level of approximately 9.81 m/s². （自由落体加速度，重力加速度，g）（单位m/s²）自由落体在真空中的加速度，在海平面处的平均值约为9.81m/s²。 |
| Maximum allowable operating pressure (Unit Pa) | 最大允许使用压力（单位Pa） |
The highest pressure at which any pressure system may be operated, usually 10 to 20% below the maximum allowable working pressure. 任何压力系统可运行的最高压力，通常比最大允许工作压力低10%至20%。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Linear (tensile or compressive) strain | 线性（拉伸或压缩）应变 |
The change per unit length due to force in an original linear dimension. An increase in length is considered positive. 由于原始线性尺寸中的力，每单位长度的变化。长度的增加被认为是正的。 |
| Coalescence | 聚结 |
Growth of grains at the expense of the remainder by absorption or the growth of a phase or particle at the expense of the remainder by absorption or reprecipitation. 通过吸收以牺牲剩余为代价的晶粒的生长或以通过吸收或再沉淀为代价的以剩余为代价的相或颗粒的生长。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Cone pulley | 锥轮 |
A stepped pulley having several diameters which, when linked by a laterallymoveable transmission belt to a corresponding pulley, gives a series of speed ratios. 具有多种直径的阶梯式皮带轮，当通过可横向移动的传动带连接到相应的皮带轮时，会产生一系列速比。 |
| Mole number (N) | 摩尔数（N） |
The number of moles in a given mass m of a substance, equal to m divided by the molar mass of the substance. 摩尔数物质给定质量m中的摩尔数，等于m除以物质的摩尔质量。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Annealing twin | 退火孪晶 |
A twin form in a crystal during recrystallization. 重结晶过程中晶体中的孪晶形式。 |
| Steam gauge | 汽压表 |
A pressure gauge used to measure gauge pressure in a line, boiler, cylinder, or other device operating with steam. 一种压力表，用于测量管道、锅炉、汽缸或其他与蒸汽一起工作的装置中的表压。 |
| Tangent screw | 微动螺旋 |
A worm screw used to adjust measuring instruments such as sextants and vernier callipers. 用于调整六分仪和游标卡尺等测量仪器的蜗杆。 |
| Thermomechanical working | 热机械加工 |
A general term covering a variety of processes combining controlled thermal and deformation treatments to obtain specific properties. Same as thermal-mechanical treatment. 一个通用术语，涵盖结合受控热处理和变形处理以获得特定性能的各种工艺。与热机械处理相同。 |
| Absorption dynamometer | 吸收式测功机 |
A dynamometer in which input work or power is dissipated by mechanical friction, electrical resistance, hydraulic resistance, etc. 通过机械摩擦、电阻、液压阻力等耗散输入功或功率的测功机。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Turbine pump (turbopump) | 涡轮泵 |
An axial or centrifugal pump driven by a turbine. Typically used to supply fuel to the combustion chamber of a rocket engine such as on the space shuttle. 由涡轮驱动的轴向或离心泵。通常用于向火箭发动机（如航天飞机）的燃烧室供应燃料。 |
| Standard deviation (σ) | 标准偏差（σ） |
A statistical term used to quantify the Scatter in a set of data points. If the standard deviation is small, most of the data points are ‘‘nearly equal.’’ A large deviation means less agreement. The most usual measure of the dispersion of observed values or results expressed as the positive square root of the variance. The square root of variance, a measure of the spread of data about the mean value. 用于量化一组数据点中分散度的统计术语。如果标准偏差很小，则大多数数据点“几乎相等”大的偏差意味着更少的一致性。观测值或结果离散度的最常用度量，表示为方差的正平方根。方差的平方根，衡量平均值的数据分布。 |
| Nominal stress | 名义应力 |
The stress at a point calculated on the net cross section by simple elasticity theory without taking into account the effect on the stress produced by stress raisers such as holes, grooves, fillets, etc. 通过简单弹性理论在净截面上计算的点处的应力，不考虑孔、槽、圆角等应力提升器产生的应力影响。 |
| Spring temper | 弹簧回火 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about two-thirds of the way from full hard to extra spring temper. 非铁合金和一些铁合金的一种回火，其特点是抗拉强度和硬度约为全硬回火到超弹性回火的三分之二。 |
| Biodiesel | 生物柴油 |
A substitute for diesel fuel derived from the oily seeds of sunflowers, oilseed rape, soya beans, etc. 从向日葵、油菜、大豆等的油性种子中提取的柴油的替代品。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Tension | 拉伸 |
The force or load that produces elongation. 1. The condition in a bar, belt, cable, spring, string, wire, etc. that is being pulled from either end. 2. (tensile force) (unit N) The force associated with tension as in (1). It is measured by a tension meter. 伸长力产生伸长的力或载荷。1.从两端拉出的杆、带、电缆、弹簧、线、线等的状态。2.（张力）（单位N）与张力相关的力。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Residual stress (Unit Pa) | 残余应力（单位Pa） |
Stresses that remain within a body as the result of thermal or mechanical treatment or both. (internal stress) An internal-stress system found in components that have experienced elastic unloading from non-uniform plastic-strain fields during manufacture. 由于热处理或机械处理或两者兼而有之而留在物体内的应力。（内应力）在制造期间从非均匀塑性应变场经历弹性卸载的部件中发现的内应力系统。 |
| Gasket m-factor | 垫片m系数 |
For a gasketed joint of area A in which the clamping force is F, the factor m is defined by F ≥ mpA where p is the pressure that would separate the two halves of the joint and m > 1. 对于面积为A且夹紧力为F的垫片接头，系数m由F≥mpA定义，其中p是分离接头两半的压力，m>1。 |
| Acicular ferrite | 针状铁素体 |
A highly substructured non-equiaxed ferrite that forms upon continuous cooling by a mixed diffusion and shear mode of transformation that begins at a temperature slightly higher than the temperature transformation range for upper bainite. It is distinguished from bainite in that it has a limited amount of carbon available; thus, there is only a small amount of carbide present. Ferrite crystallite growing, apparently, as in the course of bainitic transformation. It has a lath-like shape and an increased dislocation 一种高度亚结构的非等轴铁素体，在连续冷却时通过混合扩散和剪切相变模式形成，其开始温度略高于上贝氏体的温度转变范围。它与贝氏体的区别在于它的碳含量有限。因此，仅存在少量碳化物。显然，铁素体微晶在贝氏体转变过程中生长。它具有板条状的形状和增加的位错。 |
| Compression member | 压缩构件 |
A structural component, the major loading on which is compressive. 一种结构部件，其上的主要载荷是压缩的。 |
| Scragging machine | 刮擦机 |
1. A machine to test springs by impulsive loading 2. A machine to increase the service life of coil springs by compressing them to their minimum solid length before use, thereby inducing favourable residual stresses. 1.一种通过冲击载荷测试弹簧的机器2.一种在使用前将螺旋弹簧压缩至其最小实心长度以提高其使用寿命的机器，从而产生有利的残余应力。 |
| Dimensional stability | 尺寸稳定性 |
Ability of a plastic part to retain the precise shape in which it was molded, fabricated, or cast. 塑料零件保持其成型、制造或铸造时的精确形状的能力。 |
| Salt bath heat treatment | 盐浴热处理 |
Heat treatment carried out in a bath of molten salt. 在熔融盐浴中进行的热处理。 |
| Frequency | 频率 |
(temporal frequency, f) (Unit Hz) The number of cycles per second in an oscillation or the repetition rate for a cyclic process. （时间频率，f）（单位Hz）振荡中每秒的周期数或循环过程的重复率。 |
| Strain rate | 应变率 |
The time rate of straining for the usual tensile test. Strain as measured directly on the specimen gage length is used for determining strain rate. Because strain is dimensionless, the units of strain rate are reciprocal time. 通常拉伸试验的应变时间速率。直接在试样标距上测量的应变用于确定应变率。因为应变是无因次的，所以应变率的单位是倒数时间。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Cavitation tunnel | 空泡试验筒 |
A closed-circuit recirculating water tunnel in which the static pressure can be reduced to sufficiently low levels for cavitation studies to be performed. 一种闭路循环水隧洞，其中静压可降至足够低的水平，以便进行气蚀研究。 |
| Impact testing | 冲击测试 |
Determination of the mechanical properties of materials under high-rate conditions. Often determined from the behaviour of a testpiece when struck by a pendulum or a weight falling from a known height, or when sandwiched between two Hopkinson bars. 在高速条件下测定材料的机械性能。通常根据测试件在被钟摆撞击或从已知高度坠落的重物或夹在两个霍普金森棒之间时的行为来确定。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Granular fracture | 粒状断裂 |
A type of irregular surface produced when metal is broken that is characterized by a rough, grainlike appearance, rather than a smooth or fibrous one. It can be subclassified as transgranular or intergranular. 金属破碎时产生的一种不规则表面，其特征是粗糙的颗粒状外观，而不是光滑或纤维状的外观。它可以细分为穿晶或晶间。 |
| Flattening test | 压扁试验 |
This term as applied to tubing refers to a method of testing a section of tubing by flattening it until the inside walls are parallel and separated by a given distanceusually equal to three times the wall thickness for seamless tubes and five times the wall thickness for lap-welded tubes. Boiler tubes subjected to this test should show no cracks or flaws. The flattening test applied to rivets, consists in flattening a rivet head while hot to a diameter equal to 21⁄2 times the diameter of the shank or body of the rivet. Good rivet steel must not crack at the edges of the flattened head. 该术语适用于管材，是指通过压扁管材直至内壁平行并隔开给定距离（通常等于无缝钢管壁厚的三倍，搭接焊管壁厚的五倍）来测试管材截面的方法。进行该试验的锅炉管应无裂纹或缺陷。适用于铆钉的压扁试验包括在热态下压扁铆钉头，使其直径等于铆钉柄或铆钉体直径的21⁄2倍。良好的铆钉钢不得在扁平头部边缘开裂。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Nut splitter | 螺母分离器 |
A tool for removing rusted-on and corroded nuts from bolts. It consists of a stiff steel ring that is placed around the nut. A screw thread passing through the ring bears diametrically on a wedged-shape tip that indents and cuts though a face of the nut. 从螺栓上去除锈蚀螺母的工具。它由一个围绕螺母放置的刚性钢环组成。穿过环的螺纹径向支撑在楔形尖端上，该尖端凹陷并穿过螺母的表面。 |
| Reduction in area (RA) | 缩小面积（RA） |
The difference between the original cross-sectional area of a tensile specimen and the smallest area at or after fracture as specified for the material undergoing testing. Also known as reduction of area. 拉伸试样的原始横截面积与试验材料断裂时或断裂后的最小面积之间的差值，也称为减少面积。 |
| Rated power (Unit kW or hp) | 额定功率（单位：千瓦或马力） |
(rated capacity, rated horsepower) The maximum power output that can be sustained continuously for any power-producing machine or system, such as an engine or a power plant. （额定容量、额定马力）任何发电机器或系统（如发动机或发电厂）可连续维持的最大功率输出。 |
| Sawing | 锯切 |
Sawing is the process of cutting a workpiece with power band saws, hacksaws, and circular saws. Each of these methods is used in cutoff operations (cutting pieces to a required length), although band sawing also provides a method of cutting contours. 锯切是用带锯、钢锯和圆锯切割工件的过程。这些方法中的每一种都用于切割操作（将工件切割到所需长度），尽管带锯也提供了一种切割轮廓的方法。 |
| Infinite life diagram | 无限疲劳寿命图 |
A simple plot experimentally derived fatigue-life data, showing the conditions required for infinite life. 一个简单的曲线图，实验得出的疲劳寿命数据，显示了无限寿命所需的条件。 |
| Oxidized surface (on steel) | 氧化表面（在钢上） |
Surface having a thin, tightly adhering, oxidized skin (from straw to blue in color), extending in from the edge of a coil or sheet. Sometimes called annealing border. 表面具有薄的、紧密粘附的氧化皮（从稻草色到蓝色），从线圈或薄片的边缘延伸。有时称为退火边界。 |
| Oxidizing agent | 氧化剂 |
A compound that causes oxidation, thereby itself becoming reduced. 一种引起氧化从而自身被还原的化合物。 |
| Die threading | 模具螺纹 |
Die threading is a machining process for cutting external threads in cylindrical or tapered surfaces by the use of solid or self-opening dies. Die threading is a slower method of producing external threads than thread rolling, but it is faster than single-point threading in a lathe. 模具螺纹加工是一种通过使用实心或自开模具在圆柱形或锥形表面上切削外螺纹的加工工艺。模具螺纹加工是一种比滚丝加工更慢的外螺纹加工方法，但它比车床中的单点螺纹加工要快。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Ideal critical diameter | 理想临界直径 |
(DI). Under an ideal quench condition, the bar diameter that has 50% martensite at the center of the bar when the surface is cooled at an infinitely rapid rate (that is, when H = ∞, where H is the quench severity factor). （DI）在理想淬火条件下，当表面以无限快的速度冷却时（即H=∞, 其中H是淬火严重度因子）。 |
| Waist | 腰部 |
The joint in a robot corresponding to the human waist, i.e. providing rotation about a vertical axis. In an articulated robot, the first joint mounted at the base frame. 机器人中的关节对应于人的腰部，即提供绕垂直轴的旋转。在关节式机器人中，第一个关节安装在基架上。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| Impact extrusion | 冲击挤压 |
The extrusion of separate components of soft metals whose properties permit the action to be performed quickly. 挤压单独的软金属组件，其特性允许快速执行操作。 |
| Caustic cracking | 苛性开裂 |
A form of stress-corrosion cracking most frequently encountered in carbon steels or iron-chromiumnickel alloys that are exposed to concentrated hydroxide solutions at temperatures of 200 to 250 °C (400 to 480 °F). Also known as caustic embrittlement. 在200至250°C（400至480°F）的温度下暴露于浓氢氧化物溶液中的碳钢或铁铬镍合金中最常遇到的一种应力腐蚀开裂形式。也称为碱脆。 |
| Thread insert | 螺纹嵌件 |
(threaded bushing) Either a thin cylinder with an internal thread (and sometimes also an external thread) or a helical coil of wire, pressed or screwed into a hole to accept a bolt or screw. Used in material too soft or a component too thin to be threaded, to change one form of thread to another or to repair a damaged thread. （螺纹衬套）一种带有内螺纹（有时也有外螺纹）的薄圆柱体或螺旋形线圈，压入或拧入孔中以接受螺栓或螺钉。用于材料太软或部件太薄而无法螺纹连接，用于将一种形式的螺纹更换为另一种形式或修复损坏的螺纹。 |
| Controlled cooling | 控制冷却 |
Cooling from an elevated temperature in a predetermined manner, to avoid hardening, cracking, or internal damage, or to produce desired microstructure or mechanical properties. 以预定方式从升高的温度冷却，以避免硬化、开裂或内部损坏，或产生所需的微观结构或机械性能。 |
| Forced-air quench | 强制空气淬火 |
A quench utilizing blasts of compressed air against relatively small parts such as a gear. 利用压缩空气冲击相对较小的零件（例如齿轮）进行的淬火。 |
| Wrinkling | 起皱 |
A wavy condition obtained in deep drawing of sheet metal, in the area of the metal between the edge of the flange and the draw radius. Wrinkling may also occur in other forming operations when unbalanced compressive forces are set up. 在金属板深冲过程中，在法兰边缘和拉深半径之间的金属区域内获得的波浪状状态。当设置不平衡压缩力时，在其他成形操作中也可能发生起皱。 |
| Wrist | 腕关节 |
The final three joints on a robot which simulate rotations provided by the human wrist and thus allow orientation of the end effector to which it is attached by the wrist socket. 机器人上的最后三个关节，模拟人类手腕提供的旋转，从而允许其通过手腕插座连接到的末端执行器的方向。 |
| Concentration ratio | 浓度比 |
For a concentrating solar collector, the ratio of the projected area of the concentrator facing the solar beam to the actual area of the receiver. 对于聚光太阳能集热器，集中器面向太阳光束的投影面积与接收器的实际面积之比。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Countersinking | 埋头孔 |
The flaring out of the rim of a drilled hole to form a truncated conical depression to receive a screw having a conical head, thus giving a flush fitting. 从钻孔的边缘向外张开以形成截锥形凹陷，以容纳具有锥形头的螺钉，从而提供齐平的配件。 |
| Ion nitriding | 离子氮化 |
A method of surface hardening in which nitrogen ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma nitriding or glowdischarge nitriding. 一种表面硬化方法，其中氮离子通过使用高压电能在真空中扩散到工件中。与等离子体氮化或辉光放电氮化同义。 |
| Ductile fracture | 韧性断裂 |
Fracture characterized by tearing of metal accompanied by appreciable gross plastic deformation and expenditure of considerable energy. A fracture of a component or structure which is preceded by extensive ductile deformation so that the broken pieces cannot be re-fitted to regain the original size and shape of the component or structure. 以金属撕裂为特征的断裂，伴随着明显的总塑性变形和相当大的能量消耗。一种部件或结构的断裂，在断裂前会发生大范围的延性变形，从而使断裂的碎片无法重新装配以恢复部件或结构原来的尺寸和形状。 |
| Stress | 应力（单位Pa） |
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression)or shear. 1. Stress ‘at a point’ (i.e. over a volume of material that is very small compared with that of the component or structure) is the load per unit area for every face of an infinitesimal cube surrounding the point. 2. In fluid flow the stress tensor σij is the sum of an isotropic part −pδij, δij being the Kronecker delta, having the same form as the stress tensor for a fluid at rest, p being the static pressure, and the non-isotropic, deviatoric stress tensor dij which is due entirely to the fluid motion. 内部分布力或力分量的强度，这些力或力的分量抵抗正在或已经受到外力的材料的体积或形状的变化。应力以单位面积的力表示，并根据试样横截面的原始尺寸计算。应力可以是直接（拉伸或压缩）或剪切。1.“在一点”的应力（即在与组件或结构相比非常小的材料体积上）是围绕该点的无限小立方体的每个面的单位面积载荷。2. 在流体流动中，应力张量σij是各向同性部分-pδij的总和，δij是Kroneckerδ，具有与静止流体的应力张量相同的形式，p是静压，非各向同性, 偏应力张量 dij 完全由流体运动引起。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Vacuum servo | 真空服务器 |
A vacuum-operated servomotor which is used in a motor vehicle to provide a brake effort greater than the capability of the driver. 一种真空操作的伺服电机，用于机动车中，以提供大于驾驶员能力的制动力。 |
| Strain aging | 应变时效 |
The changes in ductility, hardness, yield point, and tensile strength that occur when a metal or alloy that has been cold worked is stored for some time. In steel, strain aging is characterized by a loss of ductility and a corresponding increase in hardness, yield point, and tensile strength. 已冷加工的金属或合金在储存一段时间后发生的延展性、硬度、屈服点和抗拉强度的变化。在钢中，应变时效的特点是延性损失，硬度、屈服点和抗拉强度相应增加。 |
| Secondary hardening | 二次硬化 |
The process whereby some low-alloy steels, quenched to produce martensite, produce fine precipitates when tempered above 550°C, which inhibit dislocation motion and reverse the trend towards lower strength at higher tempering temperatures. 某些低合金钢经淬火产生马氏体，在550°C以上回火时产生细小沉淀的过程，这抑制了位错运动，扭转了在较高回火温度下强度降低的趋势。 |
| Mohs hardness test | 莫氏硬度测试 |
A scratch hardness test for determining comparative hardness using 10 standard minerals—from talc (the softest) to diamond (the hardest). 刮擦硬度测试，用于使用从滑石（最软）到钻石（最硬）的10种标准矿物测定比较硬度。 |
| Fracture surface | 断裂面 |
The irregular surface produced when a piece of metal is broken. 一块金属破碎时产生的不规则表面。 |
| Total head (hT) (Unit m) | 总水头（hT）（单位：m） |
Total pressure pT expressed in terms of the vertical height of a column of liquid, typically water or mercury, i.e. hT = pT/ρg where g is the acceleration due to gravity and ρ is the liquid density. 总压力pT以液体柱（通常为水或汞）的垂直高度表示，即hT=pT/ρg，其中g为重力加速度，ρ为液体密度。 |
| Degree (°) | 度数（°） |
A measure of plane angle such that 1° is 1/360 of a complete revolution and equal to π/180 rad. 平面角度的一种度量，使得1°是一整圈的1/360，等于π/180弧度。 |
| Austempered steels | 等温钢 |
Medium to high carbon steels with improved mechanical properties as a result of austempering. After heating to between 800° and 900°C to form the austenite phase, they are quenched to, and held at, just above the martensite transformation range (between 260° and 370°C) to form bainite, before cooling further. Austempering of ductile cast irons results in a microstructure of bainite and spheroidal graphite. Austempered ductile irons have excellent toughness and wear properties. 由于等温淬火，机械性能得到改善的中高碳钢。在加热到800°和900°C之间形成奥氏体相后，将它们淬火并保持在略高于马氏体转变范围（260°和370°C之间）以形成贝氏体，然后进一步冷却。球墨铸铁的等温淬火导致贝氏体和球状石墨的微观结构。等温淬火球墨铸铁具有优异的韧性和耐磨性。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Calorizing | 热化 |
Imparting resistance to oxidation to an iron or steel surface by heating in aluminum powder at 800 to 1000 °C (1470 to 1830 °F). 通过在800至1000°C（1470至1830°F）下加热铝粉，赋予铁或钢表面抗氧化性。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| GGas turbine | G燃气轮机 |
An engine in which air, compressed by a multi-stage axial compressor and/or one or more centrifugal compressors, flows into a combustion chamber (or chambers) where fuel is burned and the hot gases then drive an axial turbine which powers the compressor. 由多级轴流压缩机和/或一个或多个离心压缩机压缩的空气流入燃烧室（或多个燃烧室），在燃烧室中燃烧燃料，然后热气体驱动轴流涡轮，为压缩机提供动力。 |
| Yield strength | 屈服强度 |
That stress level which will create a permanent deformation of 0.2% or 0.5% or some other small, preselected, amount in a body. Approximately equal to the elastic and proportional limits of the material; a little higher than the proof strength of a bolt. The stress at which a material exhibits a specified deviation from proportionality of stress and strain. An offset of 0.2% is used for many metals. 该应力水平将在物体中产生0.2%或0.5%的永久变形，或其他一些小的、预先选定的量。近似等于材料的弹性和比例极限；略高于螺栓的强度。材料表现出与应力和应变比例的特定偏差的应力。许多金属使用0.2%的偏移量。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Notch strength | 缺口强度 |
The maximum load on a notched tensile-test specimen divided by the minimum cross-sectional area (the area at the root of the notch). Also known as notch tensile strength. 缺口拉伸试样上的最大载荷除以最小横截面积（缺口根部的面积）。也称为缺口抗拉强度。 |
| Edge distance ratio | 边距比 |
The ratio of the edge distance to the pin diameter in a bearing test. 轴承测试中边缘距离与销直径的比值。 |
| Stress cracking | 应力开裂 |
A family of failure modes, each of which involves high stress and chemical action. The family includes Hydrogen embrittlement, Stress corrosion cracking, stress embrittlement, and hydrogen-assisted stress corrosion. 一系列失效模式，每种模式都涉及高应力和化学作用。该系列包括氢脆、应力腐蚀开裂、应力脆化和氢辅助应力腐蚀。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Abelian group | 阿贝尔群 |
Property of a group of elements associated with a binary operation. In an Abelian group, the group elements commute under the binary operation. If a and b are any two group elements and if the (+) sign denotes the binary operation, then, for an Abelian group, 与二元运算相关的一组元素的属性。在阿贝尔群中，群元素在二元运算下交换。如果a和b是任意两个群元素并且（+）符号表示二元运算 |
| Pin expansion test | 插头膨胀试验 |
A test for determining the ability of a tube to be expanded or for revealing the presence of cracks or other longitudinal weaknesses in it, made by forcing a tapered pin into the open end of the tube, similar to flare test. 通过将锥形销压入管道开口端来确定管道膨胀能力或揭示其存在裂纹或其他纵向缺陷的试验，类似于扩口试验。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Allotropy | 同素异形体 |
A near synonym for polymorphism. Allotropy is generally restricted to describing polymorphic behavior in elements, terminal phases, and alloys whose behavior closely parallels that of the predominant constituent element. 多态性的近义词。同素异形体通常仅限于描述元素、终端相和合金中的多晶型行为，其行为与主要组成元素的行为非常相似。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Fatigue | 疲劳 |
The phenomenon leading to fracture under repeated or fluctuating stresses having a maximum value less than the ultimate tensile strength of the material. Fatigue failure generally occurs at loads that, applied statically, would produce little perceptible effect. Fatigue fractures are progressive, beginning as minute cracks that grow under the action of the fluctuating stress. A term referring, in components and structures subjected to either random or cyclic periodically-varying loads, to a progressive reduction in strength leading to failure at stresses lower than those that cause failure under monotonic loading. Variable loads arise from outof-balance machinery and other vibration sources, wind gusts, etc., and a large proportion of service failures is caused by fatigue. Fatigue results from the initiation and slow propagation of cracks. In manufactured components, crack initiation usually occurs at a point of stress concentration. After a period, often of millions of stress cycles, the crack reaches a critical length at which the next peak load causes sudden brittle or ductile fracture. Fracture surfaces resulting from fatigue display characteristic striations or progression marks emanating from the crack initiation site during the slow crack growth period, with a different surface appearance for the final fracture. 在最大值小于材料极限抗拉强度的重复或波动应力下导致断裂的现象。疲劳失效通常发生在静态施加的载荷下，不会产生明显影响。疲劳断裂是渐进性的，从在波动应力作用下生长的微小裂纹开始。在承受随机或周期性变化载荷的部件和结构中，指强度逐渐降低，导致在低于单调载荷下导致失效的应力下发生失效的术语。可变负载由失衡的机械和其他振动源、阵风等引起，大部分故障是由疲劳引起的。疲劳是裂纹萌生和缓慢扩展的结果。在制造部件中，裂纹萌生通常发生在应力集中点。在一段时间（通常是数百万次应力循环）后，裂纹达到临界长度，此时下一个峰值载荷会导致突然脆性或韧性断裂。疲劳产生的断裂表面在缓慢裂纹扩展期间显示出从裂纹萌生部位发出的特征条纹或进展标记，最终断裂的表面外观不同。 |
| Cleavage fracture | 解理断裂 |
A fracture, usually of a polycrystalline metal, in which most of the grains have failed by cleavage, resulting in bright reflecting facets. It is one type of crystalline fracture and is associated with low energy brittle fracture. Contrast with shear fracture. A fracture created by splitting (cleavage), as between layers in materials like slate or mica. In brittle metals, and brittle microconstituents in alloys, cleavage occurs along particular crystal planes. 一种通过分裂（劈裂）产生的裂缝断裂，通常是多晶金属的断裂，其中大部分晶粒因解理而失效，产生明亮的反射面。它是一种结晶性断裂，与低能脆性断裂有关。与剪切断裂相对。如板岩或云母等材料的层之间。在脆性金属和合金中的脆性微量成分中，沿特定晶面发生解理。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Secondary stresses (Unit Pa) | 二次应力（单位Pa） |
Stresses different from those induced by the major loading but nevertheless resulting from the major loads; for example, the hoop stresses that occur around the circumference of barrelled compression testpieces and forgings. 与主要荷载引起的应力不同，但主要荷载产生的应力；例如，桶装压缩试件和锻件周围产生的环向应力。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Full-size fastener | 全尺寸紧固件 |
Finished fastener with a shank diameter of ds ≈ d or ds > d, or screw threaded to the head, or fully threaded stud. 柄径为ds≈d或ds>d的紧固件，或螺纹连接到头部，或全螺纹螺柱。 |
| Brittle lacquer coating | 脆性漆涂层 |
A lacquer that, when painted on to an unloaded body, reveals the direction of maximum tension stresses from the pattern of cracking produced in the lacquer when the body is loaded. 一种漆，当涂在未加载的车身上时，从车身加载时在漆中产生的裂纹图案中显示出最大拉应力的方向。 |
| Vibration-testing machine (vibrator) | 振动试验机（振动器） |
Any machine that subjects components or systems to vibration at known amplitudes and frequencies in order to determine the response. vibratory equipment Vibrating process equipment, such as shakers, used to separate small and large particles, or feeders to supply particulate or granular material that may otherwise clog. 使部件或系统以已知振幅和频率振动以确定响应的任何机器。振动设备振动工艺设备，如用于分离小颗粒和大颗粒的振动筛，或用于供应可能堵塞的颗粒或粒状材料的给料机。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Stress relaxation | 应力松弛 |
The slow decrease in stress level within a part (e.g., a bolt) which is heavily loaded under constant deflection conditions. A ‘‘cousin’’ to creep, which is a slow change in geometry under constant stress conditions. The time-dependent decrease in stress in a solid under constant strain at constant temperature due to creep. The stress-relaxation behavior of a metal is usually shown in a stress-relaxation curve. 在恒定挠曲条件下，零件（如螺栓）内的应力水平缓慢降低，该零件承受重荷载。蠕变的“表亲”，是在恒定应力条件下几何结构的缓慢变化。在恒定温度下，由于蠕变，固体在恒定应变下的应力随时间变化的减小。金属的应力松弛行为通常显示在应力松弛曲线中。 |
| Transmissibility | 传递率 |
The ratio of the transmitted force to the disturbing force for a system subjected to a vibratory disturbance. The ratio may also be defined in terms of displacements, velocities, or accelerations. 受到振动干扰的系统的传递力与干扰力之比。该比率也可以用位移、速度或加速度来定义。 |
| Work ratio | 工作比 |
The ratio of the net work out to the actual work out for a thermodynamic cycle. 热力学循环的净功与实际功之比。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Hydraulics | 液压系统 |
The study of water flow in open channels (including canals, rivers, etc.), water-supply, drainage, and irrigation systems. 研究明渠（包括运河、河流等）、供水、排水和灌溉系统中的水流。 |
| Clevis joint | U形接头 |
A joint formed by two parallel cantilever beams pressed upon a component between the beams. 由两个平行悬臂梁压在梁之间的部件上形成的接头。 |
| Specific weight (γ) (Unit N/m³) | 比重（γ）（单位：N/m³） |
The weight per unit volume of a substance: if W is the weight of a volume of the substance, ρ is its density, and g is the acceleration due to gravity, γ = W/ = ρg. 物质单位体积的重量：W是物质体积的重量，ρ是其密度，g是重力引起的加速度，γ=W/=ρg。 |
| Compressed liquid | 压缩液体 |
A liquid subjected to a pressure greater than the saturation pressure corresponding to its temperature. 承受大于与其温度对应的饱和压力的压力的液体。 |
| Creep modulus (Unit Pa) | 蠕变模量（单位Pa） |
The ratio of stress/strain at a chosen strain level obtained from creep tests, often plotted against time to show changes in stiffness. 从蠕变测试中获得的选定应变水平下的应力/应变比，通常随时间绘制以显示刚度的变化。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Cavitation-resistance inducer | 抗气蚀诱导剂 |
An axial-flow pump used upstream of a main pump in order to prevent cavitation in the latter by increasing the inlet head. 在主泵上游使用的轴流泵，通过增加进口压头防止主泵出现气穴。 |
| Flange rotation | 法兰转角 |
Angular distortion of a flange under the influence of bolt and reaction forces. Measured with respect to the center of the cross section of the flange. 法兰在螺栓和反作用力影响下的角度变形。相对于法兰横截面的中心测量。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Torsional angle (ϕ) | 扭转角（ψ） |
(Unit ° or rad) The angular deflexion between two locations on a straight bar subjected to a torque. （单位为°或rad）受扭矩作用的直杆上两个位置之间的角偏转。 |
| Elastic interactions | 弹性相互作用 |
When a bolt is tightened it partially compresses the joint members ‘‘in its own neighborhood.’’ When nearby bolts are tightened later, they further compress the joint in this region. This allows the first bolt to relax a little (lose a little preload). Tightening bolts on the opposite side of the joint, however, might increase preload in some of the earlier bolts tightened on the near side. These shifts and changes in the elastic energy stored in individual bolts, during assembly, are called elastic interactions. 当螺栓拧紧时，它会“在其自身附近”部分压缩接头构件稍后拧紧附近的螺栓时，进一步压缩该区域的接头。这允许第一个螺栓稍微松弛（失去一点预载）。但拧紧接头另一侧的螺栓可能会增加早期在近侧拧紧的一些螺栓的预载。在装配过程中，储存在单个螺栓中的弹性能量的这些位移和变化称为弹性相互作用。 |
| Tempered martensite embrittlement | 回火马氏体脆化 |
Embrittlement of ultrahigh-strength steels caused by tempering in the temperature range of 205 to 400 °C (400 to 750 °F); also called 350 °C or 500 °F embrittlement. Tempered martensite embrittlement is thought to result from the combined effects of cementite precipitation on prioraustenite grain boundaries or interlath boundaries and the segregation of impurities at prioraustenite grain boundaries. 超高强度钢在205至400°C（400至750°F）温度范围内回火引起的脆化；也称为350°C或500°F脆化。回火马氏体脆化被认为是由于渗碳体沉淀在原奥氏体晶界或层间晶界上以及杂质在原奥氏体晶粒边界处偏析的综合影响。 |
| Absolute value error | 绝对值误差 |
The magnitude of the error dlsregarding the algebraic sign, or, for a vectorial error, disregarding its function. 关于代数符号的误差幅度，或者，对于矢量误差，不考虑其函数。 |
| Shear strength (Unit Pa) | 抗剪强度（单位Pa） |
The maximum shear stress that can be withstood by a material either (a) before plasticity occurs or (b) before rupture. 材料在（a）塑性发生之前或（b）断裂之前能够承受的最大剪切应力。 |
| Blueing | 发蓝 |
Application of blue dye (‘engineers’ blue’) to identify high spots on surfaces in contact, or for marking out. 应用蓝色染料（“工程师蓝”）来识别接触表面上的高点，或用于标记。 |
| Dead load (Unit N) | 静载（单位N） |
A load on a component or structure that is steady with time, e.g. the self-weight of a bridge. 部件或结构上随时间稳定的载荷，例如桥梁的自重。 |
| Nonlinear behavior | 非线性行为 |
A fastener or joint system is said to exhibit nonlinear behavior when the relationship between the External load on the joint and deformation of the parts is nonlinear, or when the relationship between increasing Preload and deformation is nonlinear. 当接头上的外部载荷与零件变形之间的关系是非线性的，或者当增加的预载荷与变形之间的联系是非线性的时，可以说紧固件或接头系统表现出非线性行为。 |
| Diaphragm compressor | 隔膜式压缩机 |
A machine in which compression is achieved by the reciprocating motion of a flexible membrane of metal, plastic, or elastomeric material. This arrangement is ideally suited to pumping high-purity, toxic, or explosive gases. A similar machine incorporating check valves is a self-priming positive-displacement pump (diaphragm pump, membrane pump). 通过金属、塑料或弹性材料的柔性薄膜的往复运动实现压缩的机器。这种布置非常适合泵送高纯度、有毒或爆炸性气体。装有止回阀的类似机器是自吸容积泵（隔膜泵、隔膜泵）。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Thermodynamic pressure (Unit Pa) | 热力学压力（单位Pa） |
The pressure within a fluid given by an equation of state such as p(ρ,T) where ρ is the fluid density and T is the absolute temperature of the fluid. 流体中的压力由状态方程给出，如p（ρ，T），其中ρ是流体密度，T是流体的绝对温度。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Torricellean barometer | 托里塞莱气压计 |
A vertical glass tube with its upper end sealed and the lower end submerged in a pool of mercury. The space above the mercury is under vacuum. The height to which the mercury rises up the tube is a measure of the barometric pressure. 一种垂直的玻璃管，上端密封，下端浸入汞池中。水银上方的空间处于真空状态。水银在管道中上升的高度是大气压力的量度。 |
| Twist | 扭转 |
The helix produced in a cylindrical component, such as a shaft, wire, tensioned cable, or rope, when one end is rotated relative to the other. Measured either as the number of turns per unit length, or by the helix angle (twist angle). 当一端相对于另一端旋转时，在圆柱形部件（如轴、钢丝、张紧电缆或绳索）中产生的螺旋。以每单位长度的圈数或螺旋角（扭曲角）测量。 |
| Radiation pressure (Unit μPa) | 辐射压力（单位：μPa） |
The pressure exerted on a surface exposed to any form of electromagnetic radiation. If the radiation is absorbed, it is equal to the power-flux density divided by the speed of light. 施加在暴露于任何形式电磁辐射的表面上的压力。如果辐射被吸收，它等于功率通量密度除以光速。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Fastener quality | 紧固件质量 |
A fastener’s adherence to its specification for dimensional tolerances, mechanical properties, and other requirements stated under applicable standards. 紧固件对尺寸公差、机械性能和适用标准规定的其他要求的规范的遵守情况。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Waste-heat recovery | 废热回收 |
The recovery of thermal energy from flue and exhaust gases, or from liquids heated in industrial processes. Recovery devices include pre-heaters, recuperators, regenerators, and waste-heat boilers. 从烟道和废气中或从工业过程中加热的液体中回收热能。回收装置包括预热器、回热器、再生器和余热锅炉。 |
| Graham’s laws | 格雷厄姆定律 |
The laws stating that the rates of diffusion and effusion of a gas are inversely proportional to the square root of its density. 规定气体的扩散和渗出速率与其密度的平方根成反比的定律。 |
| Carbon steels | 碳钢 |
(plain carbon steels) Steels in which carbon is the principal alloying element, and the amount of manganese does not exceed 1.65% and the copper and silicon contents are less than 0.60%. There are three main types: low-carbon steels (0.08–0.35% carbon); medium-carbon steels (0.35–0.50% carbon); and high-carbon steels (0.50–2.0% carbon). （普通碳钢）以碳为主要合金元素，锰含量不超过1.65%，铜和硅含量低于0.60%的钢。主要有三种类型：低碳钢（0.08-0.35%碳）；中碳钢（0.35–0.50%碳）；和高碳钢（0.50–2.0%碳）。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Liquid nitriding | 液体氮化 |
A method of surface hardening in which molten nitrogen-bearing, fused-salt baths containing both cyanides and cyanates are exposed to parts at subcritical temperatures. 一种表面硬化方法，其中含有氰化物和氰酸盐的熔融含氮熔盐浴在亚临界温度下暴露于零件。 |
| Available draught (Unit Pa) | 可用通风量（单位Pa） |
The reduced pressure of combustion gases in a furnace or boiler, either forced or due to the buoyancy of hot gases, which is used to draw in combustion air and remove products of combustion. 炉子或锅炉中燃烧气体的压力降低，无论是强制还是由于热气体的浮力，用于吸入燃烧空气并去除燃烧产物。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Impact wrench | 冲击扳手 |
An air- or electric-powered wrench in which multiple blows from tiny hammers are used to produce output torque to tighten fasteners. A pneumatically-or electrically-powered socket wrench used to tighten or loosen nuts through the application of torque in a rapid series of impulses. 一种气动或电动扳手，使用小锤子多次敲击来产生输出扭矩以拧紧紧固件，用于通过在一系列快速脉冲中施加扭矩来拧紧或松开螺母。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| DIN | DIN |
Deutsches Institut für Normung, the German Institute for Standardization. Deutsches Institut für Normung，德国标准化研究所。 |
| Scale effect | 规模效应 |
The change in behaviour with size of a material, component, or structure. For example, cube-square scaling where one element changes with volume and another with area, as in the range of a projectile or ship, droplet formation, and fracture mechanics. 性能随材料、部件或结构尺寸的变化。例如，立方体平方比例，其中一个元素随体积变化，另一个元素因面积变化，如在射弹或飞船的射程、液滴形成和断裂力学中。 |
| Absolute viscosity | 绝对粘度 |
A measure of the internal shear properties of fluids, expressed as the tangential force per unit area at either of two horizontal planes separated by one unit thickness of a given fluid, one of the planes being fixed and the other moving with unit velocity. 流体内部剪切特性的量度，表示为两个水平面中的任何一个上的单位面积切向力，两个水平面被给定流体的一个单位厚度隔开，其中一个平面固定，另一个以单位速度移动。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Total heat (Unit kJ) | 总热量（单位kJ） |
An alternative term for enthalpy. It is inappropriate as it suggests that it includes kinetic energy in the same way as total enthalpy, but it does not. Also, heat and enthalpy are quite different quantities, as their definitions show. 焓的另一个术语。这是不恰当的，因为它表明，它包括动能的方式与总焓相同，但它实际上并不是的。此外，热和焓是完全不同的量，正如它们的定义所示。 |
| Tare weight (Unit N) | 皮重（单位N） |
The weight of an empty container. 空容器的重量。 |
| Density | 密度 |
The mass per unit volume of a solid material. (mass density, ρ) (Unit kg/m³) The mass per unit volume of a substance that satisfies the continuum assumption. The reciprocal of specific volume. 固体材料每单位体积的质量。（质量密度，ρ）（单位kg/m³）满足连续统假设的物质每单位体积的质量。和比容相关联。 |
| Impact | 撞击 |
Sudden loading of a body or component, as in a vehicle collision or striking by a hammer. 物体或部件的突然加载，如车辆碰撞或锤击。 |
| Atmometer | 气压计 |
(atmidometer, evaporimeter) An instrument that measures the rate of evaporation of water from a surface into the atmosphere. （湿度计，蒸发计）测量水从表面蒸发到大气中的速率的仪器。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Clearance angle | 后角 |
(relief angle) (Unit °) The angle between the underneath or flank of a cutting tool and the machined surface. （后角）（单位°）切削刀具的底部或侧面与加工表面之间的角度。 |
| Hydraulic air compressor | 液压空气压缩机 |
1. A compressor powered by a hydraulic motor. 2. A device in which air is compressed as a result of being entrained in water flowing in a downcomer pipe. The compressed air is released in a chamber at the bottom of the pipe. 1. 由液压马达驱动的压缩机。2.一种装置，其中空气由于夹带在降液管中流动的水中而被压缩。压缩空气在管道底部的腔室中释放。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Failure of the bolt | 螺栓失效 |
Term implying that the bolt has broken or the threads have stripped. There can be many reasons for this. 表示螺栓断裂或螺纹脱落的术语。原因可能有很多种。 |
| Hydrodynamics | 流体力学 |
A term sometimes used to mean fluid dynamics, even when the fluid is a gas or a liquid other than water. 有时用于表示流体动力学的术语，即使流体是气体或水以外的液体。 |
| Creep–time relations | 蠕变时间关系 |
Algebraic or numerical relations between creep strain and time at constant stress. 恒定应力下蠕变应变与时间之间的代数或数值关系。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Repeatability | 重复性 |
A term used to refer to the test-result variability associated with a limited set of specifically defined sources of variability within a single laboratory. 一个术语，用于指与单个实验室内一组有限的特定变异源相关的测试结果变异性。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Freezing point | 冰点 |
The temperature at which a substance changes phase (or state) from liquid to solid. The freezing point for most substances increases as pressure increases. The reverse process, from solid to liquid, is melting; melting point is the same as freezing point. 物质从液态变为固态的温度。大多数物质的冰点随着压力的增加而增加。从固体到液体的逆过程是熔化；熔点与凝固点相同。 |
| Hypereutectoid alloy | 过共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of alloying element compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共晶的合金系统中，合金成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Piston pump | 活塞泵 |
A positive-displacement pump in the basic configuration of which a piston reciprocates in a cylinder. On the suction stroke, fluid is drawn into a chamber through the inlet valve, which is then open while the outlet valve is closed. On the delivery stroke the fluid is forced out of the chamber through the outlet valve, which then opens while the inlet valve is closed. Both axial and radial configurations are common. 活塞在气缸中往复运动的一种容积泵。在吸入冲程，流体通过入口阀吸入腔室，然后在出口阀关闭时打开。在输送冲程中，流体通过出口阀被迫流出腔室，然后出口阀打开，同时入口阀关闭。轴向和径向配置都很常见。 |
| Final annealing | 最终退火 |
An imprecise term used to denote the last anneal given to a nonferrous alloy prior to shipment. 一个不精确的术语，用于表示有色金属合金在装运前的最后一次退火。 |
| Hysteresis | 滞后 |
The phenomenon of permanently absorbed or lost energy that occurs during any cycle of loading or unloading when a material is subjected to repeated loading. 当材料经受重复加载时，在任何加载或卸载循环期间发生的永久吸收或损失能量的现象。 |
| Continuous precipitation | 连续沉淀 |
Precipitation from a supersaturated solid solution in which the precipitate particles grow by longrange diffusion without recrystallization of the matrix. Continuous precipitates grow from nuclei distributed more or less uniformly throughout the matrix. They usually are randomly oriented, but may form a Widmanstätten structure. 来自过饱和固溶体的沉淀，其中沉淀颗粒通过长程扩散生长而无需基质再结晶。连续析出物从在整个基体中或多或少均匀分布的核生长而来。它们通常是随机取向的，但可能形成魏氏结构。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Slip line | 滑移线 |
The trace of the slip plane on a viewing surface; the trace is usually observable only if the surface has been polished before deformation. The usual observation on metal crystals (under the light microscope) is of a cluster of slip lines known as a slip band. 滑动平面在观察表面上的轨迹；只有在变形前对表面进行抛光，才能观察到痕迹。通常对金属晶体的观察（在光学显微镜下）是一组称为滑移带的滑移线。 |
| Contact strength (Unit N) | 接触强度（单位N） |
The maximum allowable load between contacting bodies converted into a stress. 换算成应力的接触体之间的最大允许载荷。 |
| Sinter (sintering) | 烧结 |
A solid-state diffusion densification process for the production of objects, particularly porous objects, from raw material in powder, granular, mesh, perforatedsheet, or fibre form by heating to a temperature below the melting point until the constituents bond together. It is used for ceramic materials and metals. Applications of sintered materials include filtration, separation, flow control, fluidization, and noise reduction. The bonding of adjacent surfaces in a mass of particles by molecular or atomic attraction on heating at high temperatures below the melting temperature of any constituent in the material. Sintering strengthens a powder mass and normally produces densification and, in powdered metals, recrystallization. 一种固态扩散致密化工艺，用于从粉末、粒状、网状、穿孔片或纤维形式的原材料中生产物体，尤其是多孔物体，方法是加热至低于熔点的温度，直到成分结合在一起。它用于陶瓷材料和金属。烧结材料的应用包括过滤、分离、流量控制、流化和降噪。在低于材料中任何成分熔化温度的高温下加热时，通过分子或原子引力将大量颗粒的相邻表面结合起来。烧结增强了粉末质量，通常会产生致密化，在粉末金属中还会产生再结晶。 |
| Abrasion | 磨损 |
The removal of surface material by the scratching action of hard particles, either deliberately (abrasive papers, abrasive cleaning, abrasive machining) or as a consequence of operation (wear). 通过硬质颗粒的刮擦作用去除表面材料，可以是故意的（砂纸、研磨清洁、研磨加工），也可以是操作的结果（磨损）。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Gage length | 标距 |
The original length of the portion of a specimen over which strain, change of length, or other characteristics are determined. 确定应变、长度变化或其他特性的试样部分的原始长度。 |
| Annealing carbon | 退火碳 |
Fine, apparently amorphous carbon particles formed in white cast iron and certain steels during prolonged annealing. Also called temper carbon. 白口铸铁和某些钢在长时间退火过程中形成的细小、明显的无定形碳颗粒。也称为回火碳。 |
| Tangent modulus | 切线模量 |
The slope of the stress-strain curve at any specified stress or strain. See also modulus of elasticity. 在任何规定的应力或应变下，应力-应变曲线的斜率。另见弹性模量。 |
| Torque pack | 扭矩包 |
A geared wrench which multiplies input torque and provides a read-out of output torque. In effect, a combination of a Torque wrench and a Torque multiplier. 一种齿轮扳手，可增加输入扭矩并提供输出扭矩读数。实际上，它是扭矩扳手和扭矩倍增器的组合。 |
| Punch | 冲床 |
1. A hand tool with a sharp point, used to mark the position of a hole centre in a workpiece prior to drilling. 2. A flat-ended tool with sharp edges, used to shear out a hole in a plate that is supported underneath on a die having a slightly larger same-shaped orifice. 1.一种带有尖头的手动工具，用于在钻孔前标记工件中孔中心的位置。2.一种具有锐边的平头工具，用于剪切板上的孔，该板支撑在具有稍大相同形状孔口的模具下方。 |
| Fog quenching | 雾淬 |
Quenching in a fine vapor or mist. 在细蒸汽或薄雾中淬火。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| Air-cooled condenser | 风冷冷凝器 |
A heat exchanger, in which the cooling medium is air, used to condense the exhaust steam from a steam turbine, the condensate being returned to the boiler. 一种热交换器，其中冷却介质为空气，用于冷凝蒸汽轮机排出的蒸汽，冷凝水返回锅炉。 |
| Stability | 稳定性 |
1. A term relating to whether a body, structure, system, or flow is in a state of stable, unstable, or neutral equilibrium. 2. In numerical analysis, whether numerical errors, such as roundoff or input-data errors, are damped, propagate, or cause divergence of the solution as the numerical method proceeds. 3. A control system is often described as stable when a step change in input results in a steady output without continuing oscillation. 1.与物体、结构、系统或流是否处于稳定、不稳定或中性平衡状态有关的术语。2.在数值分析中，随着数值方法的进行，数值误差（如舍入误差或输入数据误差）是否衰减、传播或导致解发散。3.当输入的阶跃变化导致稳定输出而无持续振荡时，控制系统通常被描述为稳定的。 |
| Minimum stress (Smin) | 最小应力（Smin） |
In fatigue, the stress having the lowest algebraic value in the cycle, tensile stress being considered positive and compressive stress negative. 在疲劳中，循环中代数值最低的应力，拉应力被视为正应力，压应力为负应力。 |
| Alpha iron | 阿尔法铁 |
The body-centered cubic form of pure iron, stable below 910 °C (1670 °F). 纯铁的体心立方形式，在910°C(1670°F)以下稳定。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| International System of Units | 国际单位制 |
(SI system of units, Le Système international d’unités) The standard system of units now used almost universally in science and engineering except in the United States. The definitive reference on the SI is a booklet published by the International Bureau of Weights and Measures, often referred to as the BIPM SI Brochure. There are seven base units: metre (symbol m) for length; kilogram (kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred.(kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred. （国际单位制，Le Système international d\\\'unités）目前美国除外，在科学和工程中几乎是普遍使用的标准单位制。SI的最终参考是国际度量衡局出版的小册子，通常称为BIPM SI小册子。有七个基本单位：米（符号m）表示长度；质量为千克（kg）；物质量的摩尔（mol）；时间为秒；开尔文（K）表示温度；电流为安培（A）；而坎德拉（cd）表示发光强度。新的国际单位制定义于2019年5月20日生效，该定义基于自然界的普遍常数（也称为基本物理常数：阿伏伽德罗常数、玻尔兹曼常数和普朗克常数）。这些常数的值也进行了少量调整。除了基本单位外，还有22个相干导出单位，包括平面角的弧度（rad）、立体角的斯特拉迪安（sr）、频率的赫兹（Hz）、力的牛顿（N）、压力的帕斯卡（Pa）、能量、功和热量的焦耳（J）以及功率和辐射通量的瓦特（W）。建议的做法是避免N/mm²、MN/m²等组合。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Millimetre of mercury | 毫米汞柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of mercury 1 mm high. Approximately equal to 133.3 Pa or 1 torr. 一种非SI压力单位，等于1毫米高的垂直水银柱施加的压力。大约等于133.3Pa或1托。 |
| Anelastic | 无弹性 |
Literally ‘not elastic’, but in practice used for materials that display timedependent recovery on unloading. 字面意思是“没有弹性”，但实际上用于在卸载时显示随时间恢复的材料。 |
| Poisson’s ratio (ν) | 泊松比（ν） |
The absolute value of the ratio of transverse (lateral) strain to the corresponding axial strain resulting from uniformly distributed axial stress below the proportional limit of the material. 横向（侧向）应变与相应轴向应变之比的绝对值，该比值由低于材料比例极限的均匀分布的轴向应力产生。 |
| Accelerated testing | 加速测试 |
A type of testing, for rates of wear, fatigue, corrosion etc., in which failure times are reduced by employing greater loads, more frequent power cycling, higher vibration levels, higher humidity, higher temperatures, greater potential differences etc. than would be encountered in normal operation. 一种测试类型，用于测试磨损率、疲劳率、腐蚀率等，通过采用比正常运行中更大的负载、更频繁的功率循环、更高的振动水平、更高湿度、更高温度、更大的电位差等，减少故障时间。 |
| Pressure control valve | 压力控制阀 |
A valve used to set the pressure level in a pressure vessel or piping system. 用于设置压力容器或管道系统中压力水平的阀门。 |
| Semi-rotary pump | 半回转泵 |
A form of self-priming pump, often hand-operated, suitable for pumping water and light oils such as diesel oil and petrol. As shown in the diagram, liquid is sucked into one side of the pump through flap valves and simultaneously ejected from the other side on one stroke. The sequence is reversed on each successive stroke. 一种自吸泵，通常是手动的，适用于泵送水和轻油，如柴油和汽油。液体通过翻板阀吸入泵的一侧，同时在一个冲程中从另一侧排出。在每个连续冲程上，顺序颠倒。 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Fatigue striations | 疲劳条纹 |
Parallel lines frequently observed in electron microscope fractographs or fatigue-fracture surfaces. The lines are transverse to the direction of local crack propagation; the distance between successive lines represents the advance of the crack front during the one cycle of stress variation. 在电子显微镜断口图或疲劳断口表面中经常观察到平行线。这些线横向于局部裂纹扩展方向；连续线之间的距离表示在一个应力变化周期内裂纹前沿的前进。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Thermoelastic effect | 热弹性效应 |
The change in temperature of material under adiabatic elastic deformation, e.g. when loading is so rapid that the material is not in thermal equilibrium with its surroundings. For most materials, elastic tension lowers the temperature and compression raises it. The reverse occurs in elastomers such as rubber that exhibit entropic elasticity because stretching reduces the number of possible molecular configurations and so reduces the entropy. The thermoelastic effect gives rise to a stress–strain hysteresis loop in cyclic elastic loading and is one mechanism by which vibrational energy is dissipated internally in materials. 材料在绝热弹性变形下的温度变化，例如当加载速度如此之快，以至于材料与其周围环境不处于热平衡时。对于大多数材料，弹性张力降低温度，压缩提高温度。相反的情况发生在弹性体中，如橡胶，其表现出熵弹性，因为拉伸减少了可能的分子构型的数量，从而降低了熵。热弹性效应在循环弹性载荷中产生应力-应变迟滞回线，是振动能量在材料内部耗散的一种机制。 |
| Vacuum pump | 真空泵 |
A pump for exhausting air and non-condensable gases from a vessel to be maintained at sub-atmospheric pressure. The pirani and thermal-conductivity gauges are vacuum gauges used to measure the absolute pressure within a vacuum system (vacuum level), usually expressed in torr or Pa. 用于从容器中排出空气和不凝性气体以保持在亚大气压的泵。皮拉尼和热导率计是用于测量真空系统内绝对压力（真空水平）的真空计，通常用托或帕表示。 |
| Vernier | 游标 |
A short auxiliary scale that slides along the main instrument scale to permit more accurate fractional reading of the least main division of the main scale. 一种短辅助刻度，沿主仪表刻度滑动，以便更准确地读取主刻度的最小主刻度。 |
| Radiator | 散热器 |
A heat exchanger used to transfer thermal energy from one fluid to another for heating or cooling purposes. Despite the name, the principal mode of heat transfer is convection rather than radiation. In motor vehicles, water circulated through the engine block is cooled as it flows through the tubes of an air-cooled heat exchanger. In domestic radiators, hot water from a boiler is circulated through a heat exchanger with a large surface area which transfers heat to the surrounding air. 一种热交换器，用于将热能从一种流体传递到另一种流体，用于加热或冷却。尽管有这个名字，但热传递的主要方式是对流而不是辐射。在机动车辆中，通过发动机缸体循环的水在流经风冷热交换器的管道时被冷却。在家用散热器中，来自锅炉的热水通过具有大表面积的热交换器循环，该热交换器将热量传递给周围的空气。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Toughness (Unit J/m²) | 韧性（单位：J/m²） |
The ability of a metal to absorb energy and deform plastically before fracturing. 1. The ability of a material to resist crack initiation and propagation. 2. The ability of a material to absorb strain energy without fracturing. 金属在破裂前吸收能量和塑性变形的能力。1.材料抵抗裂纹萌生和扩展的能力。2.材料在不发生断裂的情况下吸收应变能的能力。 |
| Fillet radius | 圆角半径 |
Concave junction at two intersecting surfaces of a fastener. Often used to describe the junction between the head and the shank of a threaded fastener (under head fillet). 在紧固件的两个相交表面处的凹形接合处。通常用于描述螺纹紧固件的头部和柄部之间的连接处（头部圆角下方）。 |
| Concentrated solar power plant (CSP plant) | 聚光太阳能发电厂（CSP发电厂） |
A power plant in which solar radiation is concentrated using mirrors or lenses, typically using parabolic trough mirrors which focus solar radiation on to receiver tubes along the trough’s focal line. In an alternative arrangement molten salt, heated by solar receivers mounted on a tower, is circulated through a steam generator. 使用镜子或透镜集中太阳辐射的发电厂，通常使用抛物面槽镜，将太阳辐射沿着槽的焦线聚焦到接收管上。在另一种布置中，由安装在塔上的太阳能接收器加热的熔盐通过蒸汽发生器循环。 |
| Wrist pin | 腕销 |
A stud projecting from a crank as an attachment for a connecting rod. wrought alloys Metal alloys that are initially cast and then shaped into final form by processes such as extrusion, forging, or rolling. 从曲柄上伸出的一个螺柱，作为连接杆的附件。锻造合金最初铸造，然后通过挤压、锻造或轧制等工艺成形为最终形状的金属合金。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Newton (N) | 牛顿（N） |
The basic unit of force in the SI system, defined as the force that results in an acceleration of 1 m/s² when acting on a 1 kg mass. SI国际单位制中力的基本单位，定义为作用于1kg质量时产生1m/s²加速度的力。 |
| Mechanical properties of solid materials | 固体材料的力学性能 |
The strength and stiffness properties of solid materials such as fracture toughness, the moduli of elasticity, percent elongation, 固体材料的强度和刚度特性，例如断裂韧性、弹性模量、伸长率、 |
| Slot | 狭槽 |
A groove machined into a component, e.g. to allow for thermal expansion, or in which the tongue or tip of another component can fit or slide. 在部件上加工的凹槽，例如，允许热膨胀，或另一部件的榫舌或尖端可在其中安装或滑动。 |
| Newton’s law of gravitation | 牛顿万有引力定律 |
(Newton’s law of universal gravitation) Any two bodies exert a gravitational force of attraction F on each other directed along the line joining their centres of mass, in magnitude proportional to the product of their masses and inversely proportional to the square of the distance r between them. （牛顿万有引力定律）任何两个物体沿其质心连接线相互施加引力F，其大小与其质量乘积成正比，与它们之间距离r的平方成反比。 |
| Strain energy | 应变能 |
A measure of the energy absorption characteristics of a material determined by measuring the area under the stress-strain diagram. 通过测量应力-应变图下的面积确定的材料能量吸收特性的度量。 |
| Torsional stress | 扭转应力 |
The shear stress on a transverse cross section resulting from a twisting action. 扭转作用在横截面上产生的剪切应力。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Stainless steels | 不锈钢 |
Iron-base alloys that are highly resistant to corrosion in many environments. The predominant alloying element is chromium, which, like iron at room temperature, has BCC crystal structure. Corrosion resistance by passivation is achieved by the formation of chromium oxide on the steel surface. Nickel, which has FCC crystal structure, is another important addition for some steels. Other additions used to enhance properties include manganese, molybdenum, niobium, and titanium. There are several classes of stainless steel. 在许多环境中具有高度耐腐蚀性的铁基合金。主要的合金元素是铬，与室温下的铁一样，铬具有BCC晶体结构。钝化抗腐蚀性是通过在钢表面形成氧化铬来实现的。具有FCC晶体结构的镍是某些钢的另一种重要添加剂。其他用于增强性能的添加剂包括锰、钼、铌和钛。不锈钢的种类有好几种。 |
| Black annealing | 黑退火 |
Box annealing or pot annealing ferrous alloy sheet, strip, wire to impart a black color to the oxidized surface. 对铁合金板、带、线进行箱式退火或罐式退火，使氧化表面呈黑色。 |
| Jack | 杰克装置 |
A lifting device that exerts large forces over small displacements, achieved by mechanical gearing or hydraulics. 通过机械传动或液压装置在小位移上施加大力的提升装置。 |
| Intense quenching | 强烈淬火 |
Quenching in which the quenching medium is cooling the part at a rate at least two and a half times faster than still water. 淬火，其中淬火介质以比静水快至少两倍半的速度冷却零件。 |