| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Impact strength 1. (Unit Pa) | 冲击强度1.（单位Pa） |
The stress to cause failure (by yielding or fracture) under conditions of high strain rate. 2. (Unit J) A term sometimes used to describe the energy required to fracture a specimen in a Charpy or Izod impact test even though the unit is not that of strength. 在高应变率条件下导致失效（通过屈服或断裂）的应力。2.（单位J）有时用于描述在夏比或悬臂梁式冲击试验中使样品断裂所需的能量，即使单位不是强度单位。 |
| Thread insert | 螺纹嵌件 |
(threaded bushing) Either a thin cylinder with an internal thread (and sometimes also an external thread) or a helical coil of wire, pressed or screwed into a hole to accept a bolt or screw. Used in material too soft or a component too thin to be threaded, to change one form of thread to another or to repair a damaged thread. （螺纹衬套）一种带有内螺纹（有时也有外螺纹）的薄圆柱体或螺旋形线圈，压入或拧入孔中以接受螺栓或螺钉。用于材料太软或部件太薄而无法螺纹连接，用于将一种形式的螺纹更换为另一种形式或修复损坏的螺纹。 |
| Intercritical annealing | 临界退火 |
Any annealing treatment that involves heating to, and holding at, a temperature between the upper and lower critical temperatures to obtain partial austenitization, followed by either slow cooling or holding at a temperature below the lower critical temperature. 任何退火处理，包括加热至并保持在上临界温度和下临界温度之间的温度，以获得部分奥氏体化，然后缓慢冷却或保持在低于下临界温度的温度。 |
| Static fatigue | 静态疲劳 |
A term referring to a time-dependent reduction in strength with a static (noncyclic) load. The term may refer to hydrogen-induced delayed cracking or the effect of creep on the strength of plastics. Delayed fracture caused by environmental effects under dead-weight loading of materials such as glass. The name is unfortunate, as cyclic loads are not involved and glass is not susceptible to fatigue. 指静态（非循环）载荷下强度随时间变化的降低。该术语可指氢致延迟开裂或蠕变对塑料强度的影响。在玻璃等材料的自重荷载下，由环境影响引起的延迟断裂。 |
| Gasket m-factor | 垫片m系数 |
For a gasketed joint of area A in which the clamping force is F, the factor m is defined by F ≥ mpA where p is the pressure that would separate the two halves of the joint and m > 1. 对于面积为A且夹紧力为F的垫片接头，系数m由F≥mpA定义，其中p是分离接头两半的压力，m>1。 |
| Slip band | 滑带 |
A group of parallel slip lines so closely spaced as to appear as a single line when observed under an optical microscope. 一组平行滑移线，间距如此之近，以至于在光学显微镜下观察时显示为一条直线。 |
| Working section | 工作区 |
That part of a wind tunnel in which models are placed for testing, or where detailed measurements are performed. 风洞中放置模型进行测试或进行详细测量的部分。 |
| Fracture surface | 断裂面 |
The irregular surface produced when a piece of metal is broken. 一块金属破碎时产生的不规则表面。 |
| Interrupted aging | 分段时效 |
Aging at two or more temperatures, by steps, and cooling to room temperature after each step. 分为两个或两个以上的温度时效，按顺序并在每个步骤后冷却至室温。 |
| Unit | 单位 |
A numerical indication of the magnitude of a physical quantity. The basic units of mass, length, time, etc. are relative to agreed standards. 物理量大小的数字指示。质量、长度、时间等基本单位与商定的标准相对应。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Water hammer | 水锤 |
The reflected pressure surge that occurs in a liquid flowing through a pipe, usually as a consequence of sudden closure of a valve. The surge may cause the pipe to vibrate and a hammering noise to be heard. Key factors affecting the surge amplitude are the compressibility of the liquid (especially if it contains undissolved gas) and the elasticity of the pipe wall. 在流经管道的液体中发生的反射压力波动，通常是阀门突然关闭的结果。浪涌可能导致管道振动，并听到锤击噪音。影响喘振幅度的关键因素是液体的可压缩性（特别是当其含有未溶解气体时）和管壁的弹性。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Compression crease | 压缩折痕 |
A crease formed during the compression of composites having a high volume fraction of filaments. These composites fail in compression by forming a crease at an angle to the loading axis. 在压缩具有高体积分数长丝的复合材料期间形成的折痕。这些复合材料通过形成与加载轴成一定角度的折痕而在压缩中失效。 |
| Material velocity | 材料速度 |
The velocity of sound in a body (e.g., a bolt). A term used in the ultrasonic measurement of bolt stress or strain. 声音在物体（例如螺栓）中的速度。用于螺栓应力或应变的超声波测量的术语。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Atomic volume | 原子体积 |
Volume of unit cell per atom. 每个原子的晶胞体积。 |
| Flexural strength | 抗弯强度 |
The maximum stress in the outer fiber at the moment of crack or break. 断裂或断裂时刻外层纤维的最大应力。 |
| Temper | 回火 |
(1) In heat treatment, reheating hardened steel or hardened cast iron to some temperature below the eutectoid temperature for the purpose of decreasing hardness and increasing toughness. The process also is sometimes applied to normalized steel. (2) In tool steels, temper is sometimes used, but inadvisedly, to denote the carbon content. (3) In nonferrous alloys and in some ferrous alloys (steels that cannot be hardened by heat treatment), the hardness and strength produced by mechanical or thermal treatment, or both, and characterized by a certain structure, mechanical properties, or reduction in area during cold working. （1）在热处理中，将硬化钢或硬化铸铁重新加热到共析温度以下的温度，以降低硬度和增加韧性。该工艺有时也适用于正火钢。（2）在工具钢中，有时使用回火来表示碳含量，但这是不恰当的。（3）在非铁合金和一些铁合金（不能通过热处理硬化的钢）中，通过机械或热处理或两者产生的硬度和强度，其特征是在冷加工过程中具有一定的结构、机械性能或面积减小。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Pressure ratio | 压力比 |
One pressure divided by another which may be a reference pressure. In many flow and thermodynamic processes, the pressure ratio is more important than the absolute pressure levels. For example, in compressible gas flow the Mach number is determined by the ratio of the stagnation pressure to the static pressure. 一个压力除以另一个压力，该压力可以是参考压力。在许多流动和热力学过程中，压力比比绝对压力水平更重要。例如，在可压缩气流中，马赫数由停滞压力与静压之比决定。 |
| Diffusion coefficient | 扩散系数 |
A factor of proportionality representing the amount of substance diffusing across a unit area through a unit concentration gradient in unit time. 一个比例因子，表示在单位时间内通过单位浓度梯度扩散到单位面积上的物质量。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Clevis | U形夹 |
A U-shaped hook with holes at the ends through which a retaining bolt or pin (clevis pin) passes. 一种U形钩，末端有孔，固定螺栓或销（U形销）穿过这些孔。 |
| Coining | 压印 |
A forging operation, employing a closely-fitting punch and die from which no metal is allowed to escape, in which the surface pattern on the punch and die is imprinted on the blank. 一种锻造操作，采用紧密配合的凸模和模具，不允许金属逸出，其中凸模和模具上的表面图案印在坯料上。 |
| Crack | 裂缝 |
A thin fissure-like defect in a component or structure across which material continuity is lost and which reduces the strength of the body. 部件或结构中的细裂缝状缺陷，材料连续性丧失并降低了身体的强度。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Size effect | 尺寸效应 |
Effect of the dimensions of a piece of metal on its mechanical and other properties and on manufacturing variables such as forging reduction and heat treatment. In general, the mechanical properties are lower for a larger size. 金属件的尺寸对其机械和其他性能以及对制造变量（如锻造、压下和热处理）的影响。一般来说，尺寸越大，机械性能越低。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Essential conditions | 必要条件 |
Each type of failure to which bolted joints are subject is set up by three or four conditions. The conditions vary, depending on the mode of failure, but never number more than four. Eliminating any one of the essential conditions for a particular type of failure can prevent that type of failure. 螺栓连接所遭受的每种类型的故障都由三个或四个条件确定。根据故障模式的不同，情况会有所不同，但数量不得超过四个。消除特定类型故障的任何一个基本条件都可以防止该类型故障。 |
| Biodiesel | 生物柴油 |
A substitute for diesel fuel derived from the oily seeds of sunflowers, oilseed rape, soya beans, etc. 从向日葵、油菜、大豆等的油性种子中提取的柴油的替代品。 |
| Notch strength | 缺口强度 |
The maximum load on a notched tensile-test specimen divided by the minimum cross-sectional area (the area at the root of the notch). Also known as notch tensile strength. 缺口拉伸试样上的最大载荷除以最小横截面积（缺口根部的面积）。也称为缺口抗拉强度。 |
| Lüders lines | 吕德斯线 |
Elongated surface markings or depressions, often visible with the unaided eye, that form along the length of sheet metal or a tension specimen at an angle of approximately 45° to the loading axis. Caused by localized plastic deformation, they result from discontinuous (inhomogeneous) yielding. Also known as Lüders bands, Hartmann lines, Piobert lines, or stretcher strains. 拉长的表面标记或凹陷，通常肉眼可见，沿金属板或拉伸试样的长度形成，与加载轴的角度约为45°。由于局部塑性变形，它们是不连续（不均匀）屈服的结果。也被称为吕德斯带、哈特曼线、皮奥伯特线或拉伸线。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Radial wave equation | 径向波动方程 |
A differential equation describing the transmission of a wave in a system with radial symmetry. 描述波在径向对称系统中传输的微分方程。 |
| Final annealing | 最终退火 |
An imprecise term used to denote the last anneal given to a nonferrous alloy prior to shipment. 一个不精确的术语，用于表示有色金属合金在装运前的最后一次退火。 |
| Cleavage fracture | 解理断裂 |
A fracture, usually of a polycrystalline metal, in which most of the grains have failed by cleavage, resulting in bright reflecting facets. It is one type of crystalline fracture and is associated with low energy brittle fracture. Contrast with shear fracture. A fracture created by splitting (cleavage), as between layers in materials like slate or mica. In brittle metals, and brittle microconstituents in alloys, cleavage occurs along particular crystal planes. 一种通过分裂（劈裂）产生的裂缝断裂，通常是多晶金属的断裂，其中大部分晶粒因解理而失效，产生明亮的反射面。它是一种结晶性断裂，与低能脆性断裂有关。与剪切断裂相对。如板岩或云母等材料的层之间。在脆性金属和合金中的脆性微量成分中，沿特定晶面发生解理。 |
| Rockwell hardness number (HR) | 洛氏硬度值（HR） |
A number derived from the net increase in the depth of impression in a Rockwell hardness test as the load on an indenter is increased from a fixed minor load to a major load and then returned to the minor load. Rockwell hardness numbers are always quoted with a scale symbol representing the penetrator, load, and dial used. 当压头上的载荷从固定的小载荷增加到大载荷，然后返回到小载荷时，洛氏硬度试验中压痕深度的净增加值。洛氏硬度值总是用刻度符号引用，表示所用的穿透器、载荷和刻度盘。 |
| Acid rain | 酸雨 |
Any form of precipitation, including rain, snow, sleet, fog, dew, and particulates, which contains higher than normal levels of sulfuric and nitric acids. These acids result from natural and man-made emissions of sulfur dioxide and oxides of nitrogen, respectively. Acid soot consists of unburned carbon particles, typically larger than 10 μm, in the atmosphere contaminated with sulfuric acid. The particles result from poor combustion of fossil fuels. 任何形式的降水，包括雨、雪、雨夹雪、雾、露水和颗粒物，其中含有高于正常水平的硫酸和硝酸。这些酸分别来自二氧化硫和氮氧化物的自然排放和人为排放。酸烟灰由未燃烧的碳颗粒组成，通常大于10微米，在被硫酸污染的大气中。这些颗粒是化石燃料燃烧不良造成的。 |
| Vane engine (vane motor) | 叶片发动机（叶片马达） |
A rotary engine in which high-pressure hydraulic fluid in the spaces between spring-loaded sliding vanes held in an offset rotor acts on the vanes, causing the rotor to revolve within a cylinder. The design is much like a sliding-vane compressor, as is that of a vane pump, used to pump liquids. 一种旋转式发动机，其中偏置转子中装有弹簧的滑动叶片之间的高压液压流体作用在叶片上，使转子在气缸内旋转。这种设计很像滑动叶片压缩机，就像用于泵送液体的叶片泵一样。 |
| Apparent area of contact | 表观接触面积 |
In tribology, the area of contact between two solid surfaces defined by the boundaries of their macroscopic interface. 在摩擦学中，两个固体表面之间的接触区域由其宏观界面的边界定义。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Preload adjustments | 预载调整 |
Preloads may be applied directly by axial loading or indirectly by turning of the nut or bolt. When preload is applied by turning of nuts or bolts, a torsion load component is added to the desired axial bolt load. 预载荷可通过轴向载荷直接施加，或通过转动螺母或螺栓间接施加。当通过转动螺母或螺栓施加预载荷时，扭转载荷分量被添加到所需的轴向螺栓载荷中。 |
| Secant modulus | 割线模量 |
The slope of the secant drawn from the origin to any specified point on a stress-strain curve. Compare with chord modulus. 从原点到应力应变曲线上任何指定点的割线斜率。与弦模量进行比较。 |
| Freezing point | 冰点 |
The temperature at which a substance changes phase (or state) from liquid to solid. The freezing point for most substances increases as pressure increases. The reverse process, from solid to liquid, is melting; melting point is the same as freezing point. 物质从液态变为固态的温度。大多数物质的冰点随着压力的增加而增加。从固体到液体的逆过程是熔化；熔点与凝固点相同。 |
| Load and resistance factor design | 负载和阻力系数设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Assigns uncertainties in the strength of (i.e., resistance of) and in the service loads to be placed on a shear joint to estimate the probable strength of the joint. It is a recently defined alternative to the Allowable stress design procedure. 结构连接研究委员会为AISC制定的设计程序。分配剪切接头的强度（即阻力）和工作荷载的不确定性，以估计接头的可能强度。它是最近定义的容许应力设计程序的替代方案。 |
| Fatigue | 疲劳 |
The phenomenon leading to fracture under repeated or fluctuating stresses having a maximum value less than the ultimate tensile strength of the material. Fatigue failure generally occurs at loads that, applied statically, would produce little perceptible effect. Fatigue fractures are progressive, beginning as minute cracks that grow under the action of the fluctuating stress. A term referring, in components and structures subjected to either random or cyclic periodically-varying loads, to a progressive reduction in strength leading to failure at stresses lower than those that cause failure under monotonic loading. Variable loads arise from outof-balance machinery and other vibration sources, wind gusts, etc., and a large proportion of service failures is caused by fatigue. Fatigue results from the initiation and slow propagation of cracks. In manufactured components, crack initiation usually occurs at a point of stress concentration. After a period, often of millions of stress cycles, the crack reaches a critical length at which the next peak load causes sudden brittle or ductile fracture. Fracture surfaces resulting from fatigue display characteristic striations or progression marks emanating from the crack initiation site during the slow crack growth period, with a different surface appearance for the final fracture. 在最大值小于材料极限抗拉强度的重复或波动应力下导致断裂的现象。疲劳失效通常发生在静态施加的载荷下，不会产生明显影响。疲劳断裂是渐进性的，从在波动应力作用下生长的微小裂纹开始。在承受随机或周期性变化载荷的部件和结构中，指强度逐渐降低，导致在低于单调载荷下导致失效的应力下发生失效的术语。可变负载由失衡的机械和其他振动源、阵风等引起，大部分故障是由疲劳引起的。疲劳是裂纹萌生和缓慢扩展的结果。在制造部件中，裂纹萌生通常发生在应力集中点。在一段时间（通常是数百万次应力循环）后，裂纹达到临界长度，此时下一个峰值载荷会导致突然脆性或韧性断裂。疲劳产生的断裂表面在缓慢裂纹扩展期间显示出从裂纹萌生部位发出的特征条纹或进展标记，最终断裂的表面外观不同。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Centigrade heat unit | 摄氏热量单位 |
(Celsius heat unit, CHU) An obsolete (i.e. non-SI) unit equal to the energy required to increase the temperature of one pound of pure, air-free water from 14.5°C to 15.5°C at a pressure of one standard atmosphere. （摄氏热量单位，CHU）一个已被淘汰的（即非国际单位制）单位，等于在一个标准大气压的压力下将一磅纯净的无空气水的温度从14.5°C提高到15.5°C所需的能量. |
| Torque meter | 扭矩计 |
An instrument for measuring torque using spring-loaded, piezoelectric, or strain-gauged devices. 使用弹簧加载、压电或应变测量装置测量扭矩的仪器。 |
| Wave spring | 波形弹簧 |
A type of compression spring, similar to a coil spring, but made of strip shaped into waves around the circumference. 一种压缩弹簧，类似于螺旋弹簧，但由沿圆周成波浪形的条状物制成。 |
| Proportional limit | 比例极限 |
The greatest stress a material is capable of developing without a deviation from straight-line proportionality between stress and strain. 材料能够产生的最大应力不偏离应力和应变之间的直线比例。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Heat capacity (C) (Unit J/K) | 热容量（C）（单位J/K） |
The energy required to raise the temperature of a body by 1K without change of phase. Heat capacity is an extensive thermodynamic property dependent on temperature and pressure. 在不发生相变的情况下将物体的温度提高1K所需的能量。热容量是一种广泛的热力学性质，取决于温度和压力。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Diffusion coating | 扩散涂层 |
Coating on metal for corrosion- and/or oxidation-resistance. Coatings are produced by heating a metal in contact with an alloy in powder, liquid, or gaseous form at elevated temperature such that atoms of the coating diffuse into the substrate. Examples include chromium, aluminium, or silicon on substrates such as nickel-based superalloys, steels, and refractory metals. 金属上的防腐和/或抗氧化涂层。涂层是通过在高温下加热与粉末、液体或气体形式的合金接触的金属，从而使涂层的原子扩散到基体中而产生的。实例包括基底上的铬、铝或硅，如镍基高温合金、钢和耐火金属。 |
| Mechatronics | 机电一体化 |
The integration of mechanical engineering, electrical engineering, electronic engineering, and software engineering. 机械工程、电气工程、电子工程和软件工程的集成。 |
| Fretting corrosion | 微动腐蚀 |
(1) The accelerated deterioration at the interface between contacting surfaces as the result of corrosion and slight oscillatory movement between the two surfaces. (2) A form of fretting in which chemical reaction predominates. Fretting corrosion is often characterized by the removal of particles and subsequent formation of oxides, which are often abrasive and so increase the wear. Fretting corrosion can involve other chemical reaction products, which may not be abrasive. （1）由于两个表面之间的腐蚀和轻微振荡运动，接触表面之间的界面加速劣化。（2）一种以化学反应为主的微动磨损形式。微动腐蚀通常以颗粒的去除和随后形成的氧化物为特征，这些氧化物通常具有研磨性，因此会增加磨损。微动腐蚀可能涉及其他化学反应产物，这些化学反应产物可能不是磨料。 |
| Net weight (Unit N) | 净重（单位：N） |
The difference between the gross weight of any container including its contents and the tare weight of the empty container. 任何容器（包括其内容物）的毛重与空容器皮重之间的差值。 |
| Pop rivet | 拉钉 |
A hollow rivet that enables a connexion to be made from one side only of an assembly. 一种空心铆钉，使连接只能从组件的一侧进行。 |
| Monotron hardness test | 摩诺硬度试验 |
An obsolete method of determining indentation hardnessby measuring the load required to force a spherical penetrator into a metal to a specified depth. 一种已被淘汰的方法，通过测量将球形侵彻体压入金属至规定深度所需的载荷来确定压痕硬度。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Dead centre | 止点 |
The point at which, in a crank mechanism, the piston connecting rod and crank are all in line so that there can be no driving moment. 在曲柄机构中，活塞连杆和曲柄都在一条线上，因此不会有驱动力矩。 |
| Actuating system | 驱动系统 |
A system in which an electrical, pneumatic or hydraulic input supplied to an actuator produces force, torque, or displacement, usually in a controlled way. 一种系统，其中提供给执行器的电气、气动或液压输入通常以受控方式产生力、扭矩或位移。 |
| Blade compressor | 叶片式压缩机 |
An oil-free, double-acting rotary compressor in which an angled blade attached to the inner surface of a rotating housing passes through a slot in a disk rotating about an axis perpendicular to that of the housing but offset from it. Air enters through apertures in the housing and leaves through a port in the housing. 一种无油双作用旋转式压缩机，其中连接到旋转外壳内表面的倾斜叶片穿过圆盘上的槽，该槽绕垂直于外壳的轴旋转，但偏离外壳。空气通过壳体中的孔进入，并通过壳体的端口离开。 |
| Corrosion failure | 腐蚀失效 |
1. The failure of a component or structure after corrosion has reduced the load-bearing area to an unsupportable level. 2. A situation in which a mechanism cannot function owing to corrosion products preventing free movement at joints. 1、部件或结构在腐蚀后失效，使承重面积减少到无法支撑的程度。2.由于腐蚀产物阻止关节处的自由运动，导致机构无法运行的情况。 |
| Yield stress | 屈服应力 |
The stress level of highly ductile materials, such as structural steels, at which large strains take place without further increase in stress. 高韧性材料（如结构钢）的应力水平，在该应力水平下发生大应变而不会进一步增加。 |
| Specific weight (γ) (Unit N/m³) | 比重（γ）（单位：N/m³） |
The weight per unit volume of a substance: if W is the weight of a volume of the substance, ρ is its density, and g is the acceleration due to gravity, γ = W/ = ρg. 物质单位体积的重量：W是物质体积的重量，ρ是其密度，g是重力引起的加速度，γ=W/=ρg。 |
| Coefficient of cubic expansion | 立方膨胀系数 |
The fractional increase in volume per unit temperature rise. 每单位温度升高的体积增加分数。 |
| Eutectic | 共晶 |
(1) An isothermal reversible reaction in which a liquid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectic point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectic reaction. （1）一种等温可逆反应，其中液体溶液在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）一种合金，其成分由平衡图上的共晶点表示。（3）由共晶反应形成的混合固体成分的合金结构。 |
| Ductile | 延展性材料 |
(ductile material) Describes a material that can be deformed permanently to large strains without fracture. If a bolt can be stretched well past its yield point before breaking, it is said to be ductile. （延展性材料）描述一种可以永久变形到大应变而不断裂的材料。如果螺栓在断裂前可以很好地拉伸超过其屈服点，则称其具有延展性。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Biomedical engineering | 生物医学工程 |
The application of engineering principles and methodology to the medical field. Examples involving mechanical engineering include the design and construction of artificial limbs and hearts, heart-lung machines, prosthetic eyes, and orthopaedic implants such as hip joints and pins to stabilize fractured bones. 工程原理和方法在医学领域的应用。涉及机械工程的例子包括假肢和心脏、心肺机、假眼和骨科植入物（如髋关节和用于稳定骨折骨骼的销钉）的设计和建造。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Stress distribution | 应力分布 |
The manner in which tensile, compressive, and shear stresses are distributed within a loaded body, indicated by loci of constant stress. 拉应力、压应力和剪应力在受载物体内的分布方式，由恒定应力轨迹表示。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Stability | 稳定性 |
1. A term relating to whether a body, structure, system, or flow is in a state of stable, unstable, or neutral equilibrium. 2. In numerical analysis, whether numerical errors, such as roundoff or input-data errors, are damped, propagate, or cause divergence of the solution as the numerical method proceeds. 3. A control system is often described as stable when a step change in input results in a steady output without continuing oscillation. 1.与物体、结构、系统或流是否处于稳定、不稳定或中性平衡状态有关的术语。2.在数值分析中，随着数值方法的进行，数值误差（如舍入误差或输入数据误差）是否衰减、传播或导致解发散。3.当输入的阶跃变化导致稳定输出而无持续振荡时，控制系统通常被描述为稳定的。 |
| Elastic energy | 弹性能 |
The amount of energy required to deform a material within its elastic range of behavior, neglecting small heat losses due to internal friction. The energy absorbed by a specimen per unit volume of material contained within the gage length being tested. It is determined by measuring the area under the stress-strain curve up to a specified elastic strain. See also modulus of resilience and strain energy. 材料在其弹性行为范围内变形所需的能量，忽略因内耗引起的小热损失。试样在被测标距内每单位体积材料吸收的能量。它是通过测量应力-应变曲线下达到规定弹性应变的面积来确定的。另见弹性模量和应变能。 |
| Thread form | 螺纹形式 |
The cross-sectional shape of the threads, defining thread angle, root, and crest profiles, etc. Thread length Length of that portion of the fastener which contains threads cut or rolled to full depth. 螺纹的横截面形状，定义螺纹角度、齿根和齿冠轮廓等。螺纹长度：紧固件中包含全深度切割或轧制螺纹的部分的长度。 |
| Impact loads | 冲击载荷 |
Especially severe shock loads such as those caused by instantaneous arrest of a falling mass, shock meeting of two parts (in a mechanical hammer, for example), or by explosive impact, in which there can be an exceptionally rapid build-up of stress. 特别严重的冲击载荷，例如由下落质量的瞬时停止、两部分的冲击碰撞（例如在机械锤中）或爆炸性冲击引起的冲击载荷，其中可能会出现异常快速的应力积聚。 |
| Observed value | 观测值 |
The particular value of a characteristic determined as a result of a test or measurement. 作为测试或测量结果确定的特性的特定值。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Temper embrittlement | 回火脆化 |
Brittleness that results when certain steels are held within, or are cooled slowly through, a certain range of temperature below the transformation range. The brittleness is manifested as an upward shift in ductile-to-brittle transition temperature but only rarely produces a low value of reduction in area in a smooth-bar tension test of the embrittled material. The anomalous reduction in toughness of martensitic stainless steels when tempered in the range 370–600°C. Embrittlement of alloy steels caused by holding within or cooling slowly through a temperature range just below the transformation range. Embrittlement is the result of the segregation at grain boundaries of impurities such as arsenic, antimony, phosphorus, and tin; it is usually manifested as an upward shift in ductile-to-brittle transition temperature. Temper embrittlement can be reversed by retempering above the critical temperature range, then cooling rapidly. 当某些钢保持在低于转变范围的某一温度范围内或缓慢冷却时产生的脆性。脆性表现为延性到脆性转变温度的向上移动，但在脆性材料的平滑棒材拉伸试验中，很少产生较小的面积减小值。马氏体不锈钢在370–600°C范围内回火时的韧性异常降低。合金钢的脆化是由于在低于转变范围的温度范围内保持或缓慢冷却而引起的。脆化是杂质（如砷、锑、磷和锡）在晶界处偏析的结果；它通常表现为韧脆转变温度的上升。回火脆化可以通过在临界温度范围以上重新回火，然后快速冷却来逆转。 |
| Compression stroke | 压缩冲程 |
The stroke in a reciprocating compressor or engine during which the working fluid is compressed. 往复式压缩机或发动机中工作流体被压缩的冲程。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Form of thread | 螺纹形式 |
The profile of a thread in an axial plane for a length of one pitch. 一个螺距长度的螺纹在轴向平面中的轮廓。 |
| GGas turbine | G燃气轮机 |
An engine in which air, compressed by a multi-stage axial compressor and/or one or more centrifugal compressors, flows into a combustion chamber (or chambers) where fuel is burned and the hot gases then drive an axial turbine which powers the compressor. 由多级轴流压缩机和/或一个或多个离心压缩机压缩的空气流入燃烧室（或多个燃烧室），在燃烧室中燃烧燃料，然后热气体驱动轴流涡轮，为压缩机提供动力。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Coefficient of rolling friction | 滚动摩擦系数 |
The ratio of force parallel to a surface, on which an object rolls, to the normal force. Unlike sliding friction, rolling friction depends on the size of the contact patch and the radius of the rolling element, and the behaviour depends on whether the contact is elastic, viscoelastic, or plastic and on hysteresis losses. 平行于物体滚动表面的力与法向力之比。与滑动摩擦不同，滚动摩擦取决于接触片的大小和滚动元件的半径，其行为取决于接触是弹性的、粘弹性的还是塑性的以及滞后损失。 |
| Crack size (a) | 裂纹尺寸（a） |
A lineal measure of a principal planar dimension of a crack. This measure is commonly used in the calculation of quantities descriptive of the stress and displacement fields. In practice, the value of crack size is obtained from procedures for measurement of physical crack size, original crack size, or effective crack size, as appropriate to the situation under consideration. 裂纹主平面尺寸的线性度量。这种测量通常用于计算描述应力场和位移场的量。在实践中，裂纹尺寸的值是通过测量物理裂纹尺寸、原始裂纹尺寸或有效裂纹尺寸的程序获得的，视情况而定。 |
| Crack-growth rate | 裂纹增长速度 |
Rate of propagation of a crack through a material due to statically or dynamically applied load. 由于静态或动态施加的载荷，裂纹在材料中的扩展速率。 |
| Fatigue strength | 疲劳强度 |
The stress to which a metal can be subjected for a specified number of cyclic changes of stress. The maximum stress that can be sustained for a specified number of cycles without failure. The value of the maximum stress and the stress ratio also should be stated. 金属在指定数量的应力循环变化下可以承受的应力。可以在指定的循环次数内持续而不失效的最大应力。还应说明最大应力值和应力比。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Notch brittleness | 缺口脆性 |
Susceptibility of a material to brittle fractureat points of stress concentration. For example, in a notch tensile test, the material is said to be notch brittle if the notch strengthis less than the tensile strength of an unnotched specimen. Otherwise, it is said to be notch ductile. 材料在应力集中点易发生脆性断裂。例如，在缺口拉伸试验中，如果缺口强度小于无缺口试样的抗拉强度，则称材料为缺口脆性材料。否则，称其为缺口韧性。 |
| Static equilibrium | 静态平衡 |
A solid body, structure, or physical system (or any subdivided part) will be in static equilibrium, either at rest or moving with constant velocity, if the resultants of all external forces and moments acting on it are zero. 如果作用在固体上的所有外力和力矩的合力为零，则固体、结构或物理系统（或任何细分部分）无论是静止还是以恒定速度移动，都是处于静态平衡。 |
| Diffusion | 扩散 |
(1) Spreading of a constituent in a gas, liquid, or solid, tending to make the composition of all parts uniform. (2) The spontaneous movement of atoms or molecules to new sites within a material. （1） 一种成分在气体、液体或固体中的扩散，趋于使所有部分的成分均匀。（2） 原子或分子自发运动到材料内的新位置。 |
| Atom | 原子 |
The smallest unit of matter that has the properties of a chemical element. The simplest description of an atom (Bohr model) is of a compact nucleus surrounded by one or more orbiting electrons. 具有化学元素性质的最小物质单位。原子的最简单描述（玻尔模型）是由一个或多个轨道电子包围的致密原子核。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Tightness parameter | 密封参数 |
A dimensionless parameter which defines the mass leakage of a gasket as a functionof contained pressure and a contained fluid constant. 一种无量纲参数，将垫圈的质量泄漏定义为所含压力和所含流体常数的函数。 |
| Steady pin | 定位销 |
A dowel, key, or pin that prevents a pulley from turning on its shaft. 防止滑轮在其轴上转动的销钉、键或销。 |
| Sampling frequency (Unit Hz) | 采样频率（单位Hz） |
(sampling rate) The number of measurement samples per unit time taken from a continuous analogue signal to produce a discrete signal. It is the inverse of the time between successive measurements (sampling interval, sampling period, or sampling time). （采样率）从连续模拟信号中提取以产生离散信号的每单位时间的测量样本数。它是连续测量之间时间的倒数（采样间隔、采样周期或采样时间）。 |
| Crankshaft | 曲轴 |
The main shaft, of which the cranks are a part, of a reciprocating single-or multi-cylinder machine. Crankshafts may be built up in sections or forged as a single component. In an engine, the reciprocating motion of the pistons transmits power to the crankshaft and causes it to rotate, whereas in a pump the crankshaft is driven and its rotation causes the pistons to reciprocate. 曲柄是往复式单缸或多缸机器主轴的一部分。曲轴可以分段组装或作为单个部件锻造。在发动机中，活塞的往复运动将动力传递给曲轴并使其旋转，而在泵中，曲轴被驱动，其旋转使活塞往复运动。 |
| Total carbon | 总碳 |
The sum of the free and combined carbon (including carbon in solution) in a ferrous alloy. 铁合金中游离碳和结合碳（包括溶液中的碳）的总和。 |
| Thermal shock | 热冲击 |
The development of a steep temperature gradient and accompanying high stresses within a structure. 在结构内形成陡峭的温度梯度和伴随的高应力。 |
| Design heating load (Unit kW) | 设计热负荷（单位kW） |
The heating requirements based on a specified number of heating degree days, or required to maintain a building or other enclosed space at a specified temperature for a given outside temperature. 基于指定的采暖度日数的加热要求，或在给定的外部温度下将建筑物或其他封闭空间保持在指定温度下所需的加热要求。 |
| Base metal hardness | 母材硬度 |
Hardness closest to the surface (when traversing from core to outside diameter) just before an increase or decrease occurs, denoting, respectively, carburization or decarburization. 在发生增加或减少之前最接近表面的硬度（从芯部到外径时），分别表示渗碳或脱碳。 |
| Trepanning | 开孔 |
Trepanning is a machining process for producing a circular hole or groove in solid stock, or for producing a disk, cylinder, or tube from solid stock, by the action of a tool containing one or more cutters (usually single-point) revolving around a center. 开孔是一种机械加工工艺，通过包含一个或多个围绕中心旋转的刀具（通常为单点）的作用，在实心坯料中制造圆孔或凹槽，或从实心坯料生产圆盘、圆柱体或管。 |
| Fillister head | 槽头 |
Similar to a pan head but with a smaller head diameter and a taller head, with higher vertical sides. 类似于盘头，但头部直径较小，头部较高，垂直边较高。 |
| Die threading | 模具螺纹 |
Die threading is a machining process for cutting external threads in cylindrical or tapered surfaces by the use of solid or self-opening dies. Die threading is a slower method of producing external threads than thread rolling, but it is faster than single-point threading in a lathe. 模具螺纹加工是一种通过使用实心或自开模具在圆柱形或锥形表面上切削外螺纹的加工工艺。模具螺纹加工是一种比滚丝加工更慢的外螺纹加工方法，但它比车床中的单点螺纹加工要快。 |
| Transfer ratio | 传输比 |
(transfer constant) A complex variable representing the ratio between the output of a transducer and the input causing that output. （传递常数）一个复变量，表示传感器输出与产生该输出的输入之间的比率。 |
| Grip length | 夹紧长度 |
Combined thickness of all the things clamped together by the bolt and nut, including washers, gaskets, and joint members. 由螺栓和螺母夹紧在一起的所有部件的总厚度，包括垫圈、垫圈和接头构件。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Caustic cracking | 苛性开裂 |
A form of stress-corrosion cracking most frequently encountered in carbon steels or iron-chromiumnickel alloys that are exposed to concentrated hydroxide solutions at temperatures of 200 to 250 °C (400 to 480 °F). Also known as caustic embrittlement. 在200至250°C（400至480°F）的温度下暴露于浓氢氧化物溶液中的碳钢或铁铬镍合金中最常遇到的一种应力腐蚀开裂形式。也称为碱脆。 |
| Toggle (toggle clamp) | 拨动（拨动夹） |
A device consisting of two pinned levers that are almost in line between two end points in the same plane. Bringing the levers into line generates large forces between the ends. Used to obtain a large mechanical advantage or as a locking mechanism. 由两个销杆组成的装置，在同一平面的两个端点之间几乎成一条直线。将杠杆对齐会在端部之间产生较大的力。用于获得较大的机械优势或用作锁定机构。 |
| Austempering | 等温淬火 |
A heat treatment for ferrous alloys in which a part is quenched from the austenitizing temperature at a rate fast enough to avoid formation of ferrite or pearlite and then held at a temperature just above Ms until transformation to bainite is complete. Although designated as bainite in both austempered steel and austempered ductile iron (ADI), austempered steel consists of two phase mixtures containing ferrite and carbide, while austempered ductile iron consists of two phase mixtures containing ferrite and austenite. Heat treatment comprising austenitization of a steel article, cooling it to a bainitic range at a rate higher than the critical cooling rate and holding at a fixed temperature until the completion of bainitic transformation. 一种铁合金的热处理，其中零件从奥氏体化温度以足够快的速度淬火，以避免形成铁素体或珠光体，然后保持在略高于Ms的温度，直到完全转变为贝氏体。虽然在奥氏体钢和奥氏体球铁(ADI)中都被指定为贝氏体，但奥氏体钢由含有铁素体和碳化物的两相混合物组成，而奥氏体球墨铸铁由含有铁素体和奥氏体的两相混合物组成。热处理包括钢制品的奥氏体化，以高于临界冷却速率的速率将其冷却到贝氏体范围，并保持在固定温度直到贝氏体转变完成。 |
| Coefficient of friction (μ) | 摩擦系数（μ） |
(coefficient of kinetic friction, coefficient of sliding friction, friction coefficient, μ) The ratio of the frictional force F to the normal force N between two surfaces in contact, i.e. μ = F/N. Static friction is when there is no relative sliding; kinetic friction when there is. For structural components sliding on one another, the coefficient of friction is the ratio of the force causing the sliding to the force perpendicular to the sliding component surfaces. The coefficient of friction is dimensionless with values between zero and one. The number characterising the force necessary to slide or roll one material along the€surface of another. If an object has a weight N and the coefficient of friction is μ, then the force F necessary to move it without acceleration along a level surface is F = μN. The coefficient of static friction determines the force necessary to initiate movement; the coefficient of kinetic friction determines the force necessary to maintain movement. Kinetic friction is usually smaller than static friction. （动摩擦系数、滑动摩擦系数、摩擦系数，μ）两个接触表面之间摩擦力F与法向力N的比值，即μ=F/N。静摩擦是指没有相对滑动时；有摩擦时的动摩擦。对于相互滑动的结构部件，摩擦系数是引起滑动的力与垂直于滑动部件表面的力的比值。摩擦系数是无量纲的，其值介于0和1之间。代表一种材料沿另一种材料的表面滑动或滚动所需的力的数字。如果一个物体的重量为N并且摩擦系数为μ，那么在没有加速度的情况下沿水平表面移动它所需的力F为F=μN。静摩擦系数决定了启动运动所需的力；动摩擦系数决定了保持运动所需的力。动摩擦通常小于静摩擦。两个物体之间的力（F）与将这些物体压在一起的法向力（N）的无量纲比：μ（或f）=（F/N）。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Corrosion cell | 腐蚀电池 |
A natural ‘‘battery’’ formed when two metals having different electrical potentials (an Anode and a Cathode) are connected together in the presence of a liquid (the Electrolyte). 当两种具有不同电势的金属（阳极和阴极）在液体（电解质）存在下连接在一起时形成的天然“电池”。 |
| Teeth | 齿 |
The projecting elements on gears, cutting tools, etc. 齿轮、刀具等上的突出元件。 |
| Bimetallic strip | 双金属片 |
A strip formed by welding, riveting or brazing together two metals having different coefficients of expansion, which causes the strip to curl when its temperature changes. Typical combinations are steel and copper or steel and brass. 将两种膨胀系数不同的金属焊接、铆接或钎焊在一起形成的带材，当温度变化时，带材会卷曲。典型的组合是钢和铜或钢和黄铜。 |
| Breaking load (Unit N) | 断裂负荷（单位N） |
The load applied at some point to a component or structure which leads to fracture. The breaking stress (breaking strength) is the average stress at which a member breaks, given by the breaking load divided by the area over which it acts. 在某个点施加到导致断裂的部件或结构的载荷。断裂应力（断裂强度）是构件断裂时的平均应力，由断裂载荷除以其作用的面积给出。 |
| Shell hardening | 壳型硬化 |
A surface-hardening process in which a suitable steel workpiece, when heated through and quench hardened, develops a martensitic layer or shell that closely follows the contour of the piece and surrounds a core of essentially pearlitic transformation product. This result is accomplished by a proper balance among section size, steel hardenability, and severity of quench. 一种表面硬化工艺，在该工艺中，合适的钢工件在加热和淬火硬化后，会形成一层马氏体层或壳，该层或壳紧随工件的轮廓，并包围一个基本上为珠光体相变产物的核心。这一结果通过截面尺寸、钢淬透性和淬火强度之间的适当平衡来实现。 |
| Complete decarburization | 完全脱碳 |
Decarburization with sufficient carbon loss to show only clearly defined ferrite grains under metallographic examination. 脱碳，具有足够的碳损失，以在金相检查下仅显示清晰定义的铁素体晶粒。 |
| Stress raisers | 局部应力集中 |
Changes in contour or discontinuities in structure that cause local increases in stress. 导致局部应力增加的轮廓变化或结构不连续性变化。 |
| Continuous precipitation | 连续沉淀 |
Precipitation from a supersaturated solid solution in which the precipitate particles grow by longrange diffusion without recrystallization of the matrix. Continuous precipitates grow from nuclei distributed more or less uniformly throughout the matrix. They usually are randomly oriented, but may form a Widmanstätten structure. 来自过饱和固溶体的沉淀，其中沉淀颗粒通过长程扩散生长而无需基质再结晶。连续析出物从在整个基体中或多或少均匀分布的核生长而来。它们通常是随机取向的，但可能形成魏氏结构。 |
| Quimby screw pump | 昆比螺杆泵 |
A screw pump with two meshing screws, each having a righthand and a left-hand screw. Liquid enters at either end and is discharged from the middle. 带有两个啮合螺钉的螺杆泵，每个都有一个右旋螺纹和一个左旋螺纹。液体从两端进入，从中间排出。 |
| Brake lining | 制动衬片 |
The replaceable friction material that covers a brake shoe in an internally expanding brake. 在内膨胀制动器中覆盖制动的可更换摩擦材料。 |
| Least count | 最小计数 |
The smallest value that can be read from an instrument having a graduated scale. Except on instruments provided with a vernier, the least count is that fraction of the smallest division which can be conveniently and reliably estimated; this fraction is ordinarily one-fifth or one-tenth, except where the graduations are very closely spaced. 可从具有刻度尺的仪器中读取的最小值。除配备游标的仪器外，最小计数是可以方便可靠地估计的最小除法的分数；这个分数通常是五分之一或十分之一，除非刻度间隔非常近。 |
| Sliding-vane compressor | 滑片压缩机 |
(rotary-vane compressor, vane compressor) A rotary compressor in which gas is compressed as the spaces between spring-loaded sliding vanes held in an offset rotor reduce as the rotor revolves within a cylindrical housing. （旋转叶片压缩机，叶片压缩机）一种旋转式压缩机，当转子在圆柱形外壳内旋转时，偏置转子中的弹簧加载滑动叶片之间的空间减小，从而压缩气体。 |
| Active accommodation | 主动适应能力 |
The use of information from sensors, for example, in a vision system, that allows a robot to show accommodation to the environment. 使用来自传感器的信息，例如在视觉系统中，允许机器人显示对环境的适应。 |
| ASME | ASME |
The American Society of Mechanical Engineers. 美国机械工程师学会。 |
| Case hardening | 表面硬化 |
A generic term covering several processes applicable to steel that change the chemical composition of the surface layer by absorption of carbon, nitrogen, or a mixture of the two and, by diffusion, create a concentration gradient. The processes commonly used are carburizing and quench hardening; cyaniding; nitriding; and carbonitriding. The use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于钢的几种工艺，这些工艺通过吸收碳、氮或二者的混合物改变表层的化学成分，并通过扩散形成浓度梯度。常用的工艺有渗碳和淬火硬化，氰化，氮化以及碳氮共渗。优选使用适用的特定工艺名称。 |
| Differential heating | 差动加热 |
Heating that intentionally produces a temperature gradient within an object such that, after cooling, a desired stress distribution or variation in properties is present within the object. 加热有意在物体内产生温度梯度，从而在冷却后，在物体内出现所需的应力分布或特性变化。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Stroke | 一击 |
1. (stroke length) (Unit m) The linear distance between top dead centre and bottom dead centre of a piston in a reciprocating engine or mechanism. 2. The movement of a piston or plunger in a reciprocating machine to execute a particular function; for example, the exhaust stroke of an engine in which the exhaust gases are expelled from a cylinder. 1.（冲程长度）（单位：m）往复式发动机或机构中活塞上止点和下止点之间的线性距离。2.活塞或柱塞在往复式机器中执行特定功能的运动；例如发动机的排气冲程，其中排气从气缸中排出。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| Welding | 焊接 |
In tribology, the bonding between metallic surfaces in direct contact, at any temperature. A joining process in which the mating surfaces are at least softened, or more usually melted, unlike soldering and brazing. In solid-state (non-melting) welding, similar or dissimilar metals or thermoplastics may be joined by applying pressure to hot interfaces. In forge welding, joining is achieved by compression across the join between pre-heated workpieces. In friction welding (spin welding) one of the contacting surfaces is rotated rapidly before being loaded against the other. On contact, heat generated by friction softens the materials and permits severe plastic deformation that seals the joint. In friction stir welding, a wear-resistant tool is rotated rapidly, indents the surfaces and is traversed to form a join line. Resistance welding involves simultaneous pressure and electrically-generated heat, as in spot welding where a heavy electric current is passed for a short time through metal sheets which are pressed together between electrodes. 在摩擦学中，在任何温度下直接接触的金属表面之间的结合。与钎焊和钎焊不同，接合面至少软化或更通常熔化的接合工艺。在固态（非熔化）焊接中，相似或不同的金属或热塑性塑料可通过向热界面施加压力来连接。在锻造焊接中，通过压缩预热工件之间的连接来实现连接。在摩擦焊接（旋转焊接）中，一个接触表面在被加载到另一个表面之前快速旋转。接触时，摩擦产生的热量使材料软化，并允许密封接头的严重塑性变形。在搅拌摩擦焊中，耐磨工具快速旋转，使表面凹陷，并横穿形成连接线。电阻焊涉及同时产生的压力和电产生的热量，如点焊，在点焊中，大电流短时间通过电极之间压在一起的金属板。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| End-quench hardenability test | 端淬淬透性试验 |
A laboratory procedure for determining the hardenability of a steel or other ferrous alloy. Hardenability is determined by heating a standard specimen above the upper critical temperature, placing the hot specimen in a fixture so that a stream of cold water impinges on one end, and, after cooling to room temperature is completed, measuring the hardness near the surface of the specimen at regularly spaced intervals along its length. The data are normally plotted as hardness versus distance from the quenched end. 测定钢或其他铁合金淬透性的实验室程序。淬透性是通过将标准试样加热到高于上临界温度，将热试样放置在夹具中，使冷水流冲击一端，并在冷却至室温后，沿试样长度以规则间隔测量试样表面附近的硬度来确定的。数据通常绘制为硬度与距淬火端距离的关系。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Fatigue test | 疲劳测试 |
A method for determining the range of alternating (fluctuating)stresses a material can withstand without failing. 一种确定材料可以承受而不会失效的交变（波动）应力范围的方法。 |
| Flange rotation | 法兰转角 |
Angular distortion of a flange under the influence of bolt and reaction forces. Measured with respect to the center of the cross section of the flange. 法兰在螺栓和反作用力影响下的角度变形。相对于法兰横截面的中心测量。 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Turning | 车削 |
Turning is a machining process for generating external surfaces of revolution by the action of a cutting tool on a rotating workpiece, usually in a lathe. The rotation of a workpiece held against a cutting tool in a lathe to produce components with a circular cross section. 车削是一种机械加工过程，通常在车床上，通过刀具对旋转工件的作用产生旋转外表面。在车床中，工件靠着刀具旋转，以生产具有圆形横截面的部件。 |
| Machine screw | 机械螺丝 |
A countersunk, slotted screw with machined threads such as are found on bolts. A relatively small screw, usually less than 20 mm in diameter, with the thread running along the whole length up to the head, intended to be screwed into threaded holes. If inserted through plain holes in assembled parts and held together by a nut, an undesirable contact surface of threads bearing against the surface of a hole results. 带有机加工螺纹的沉头开槽螺钉，如螺栓上的螺纹。一种相对较小的螺钉，直径通常小于20毫米，螺纹沿整个长度一直延伸到头部，用于拧入螺纹孔中。如果通过装配零件上的平孔插入并用螺母固定在一起，则会导致螺纹与孔表面接触不良。 |
| Thermoelectric converter | 热电转换器 |
(thermoelectric generator) A device consisting of series-connected alternate n- and p-type semiconductor elements sandwiched between two ceramic plates. Due to the Seebeck effect, electrical power is generated when a temperature difference is maintained across the plates. Due to the Peltier effect, a thermoelectric converter can act as either a thermoelectric heater or a thermoelectric cooler (thermoelectric refrigerator) by passing an electrical current through it. The thermoelectric figure of merit (Z), with unit 1/K, is a dimensional parameter on which the efficiency of a thermoelectric device is primarily dependent, defined by Z = σα2/k where α is the Seebeck coefficient, σ is the electrical conductivity, and k is the thermal conductivity. The product of Z and a temperature is non-dimensional. （热电发生器）由串联连接的交替的n型和p型半导体元件夹在两块陶瓷板之间组成的装置。由于塞贝克效应，当板之间保持温差时，就会产生电能。由于珀尔帖效应，热电转换器可以通过使电流通过而充当热电加热器或热电冷却器（热电制冷机）。热电优值（Z）和第一单元/K是一个尺寸参数，热电装置的效率主要取决于此，由Z=σα2/K定义，其中α是塞贝克系数，σ是电导率，K是热导率。Z和温度的乘积是无量纲的。 |
| Cast steel | 铸钢 |
Steel that is cast into shapes. It has superior properties to most cast irons, but is more expensive to produce. 铸成形状的钢。与大多数铸铁相比，它具有优越的性能，但生产成本更高。 |
| Austenite stabilization | 奥氏体稳定化 |
Decrease, in comparison to a continuous cooling, in the amount of martensite occurring from austenite when cooling is interrupted at a temperature between Ms and Mf. This can be explained by the relaxation of stresses induced in the austenite by martensite crystals occurring before the interruption. The relaxation, in turn, leads to the dislocation rearrangement and their interaction with martensite/austenite interfaces, which makes the interfaces immobile. 与连续冷却相比，当在Ms和Mf之间的温度中断冷却时，从奥氏体中产生的马氏体的量减少。这可以通过中断前发生的马氏体晶体在奥氏体中引起的应力松弛来解释。反过来，松弛导致位错重排及其与马氏体/奥氏体界面的相互作用，这使得界面无法移动。 |
| Atmospheric pressure | 气压 |
The downward force exerted by the atmosphere because of its weight, (gravitational attraction to the Earth), measured by barometers, and usually expressed in units of millibars. Standard atmospheric pressure at sea level is 1013.25 mb.expressed in units of millibars. Standard atmospheric pressure at sea level is 1013.25 mb. 大气由于其重量（对地球的引力）而施加的向下的力，用气压计测量，通常以毫巴为单位表示。海平面的标准大气压为1013.25mb。以毫巴为单位表示。海平面的标准大气压为1013.25mb。 |
| Span (Unit m) | 跨度（单位：m） |
A dimension measured between the extremities of a body or structure, such as between the tips of a wing or the supports of a bridge. 在身体或结构的末端之间测量的尺寸，如机翼尖端或桥梁支架之间。 |
| Granular fracture | 粒状断裂 |
A type of irregular surface produced when metal is broken that is characterized by a rough, grainlike appearance, rather than a smooth or fibrous one. It can be subclassified as transgranular or intergranular. 金属破碎时产生的一种不规则表面，其特征是粗糙的颗粒状外观，而不是光滑或纤维状的外观。它可以细分为穿晶或晶间。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Austenite-stabilizer | 奥氏体稳定剂 |
Alloying element expanding the γ-phase field in the corresponding phase diagram, which manifests itself in a decrease of the A3 temperature and an increase of the A4 temperature in binary alloys Fe–M as well as in a decrease of A1 temperature in ternary alloys Fe–C–M (M is an alloying element). The solubility of austenite-stabilizers in ferrite is much lower than in austenite. Under the influence of austenite-stabilizers, austenite can become thermodynamically stable down to room temperature. 合金元素扩展了相应相图中的γ相场，这表现为二元合金Fe-M中A3温度的降低和A4温度的升高，以及A1温度的降低三元合金Fe–C–M（M是合金元素）。奥氏体稳定剂在铁素体中的溶解度远低于在奥氏体中的溶解度。在奥氏体稳定剂的影响下，奥氏体可以在低至室温时变得热力学稳定。 |
| Strain | 拉紧 |
The unit of change in the size or shape of a body due to force. Also known as nominal strain. 物体的大小或形状因力而变化的单位。也称为标称应变。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Planar anisotropy | 平面异向性 |
A variation in physical and/or mechanical properties with respect to direction within the plane of material in sheet form. 在片状材料平面内，物理和/或机械性能相对于方向的变化。 |
| Valve spring | 气门弹簧 |
The spring that restores a valve to its closed position after having been opened, and is also intended to prevent valve bounce. 在阀门打开后将其恢复到关闭位置的弹簧，也用于防止阀门反弹。 |
| Heat treatment | 热处理 |
(heat treating) Alteration of the mechanical properties of materials, particularly metals, by different sequences of heating, holding at temperature, and cooling at different rates. Heating and cooling a solid metal or alloy in such a way as to obtain desired conditions or properties. Heating for the sole purpose of hot working is excluded from the meaning of this definition. （热处理）材料，特别是金属的机械性能的改变，通过不同的加热顺序、温度保持和不同速率的冷却。加热和冷却固体金属或合金，以获得所需的条件或性能。仅用于热加工的加热不属于本定义的含义。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Solenoid | 螺线管 |
A coil of electrically-conducting wire wrapped around a metal core, typically iron, to produce a magnetic field and hence a force on the core when an electric current passes through the coil. Solenoids are widely used to produce linear movement to actuate valves (solenoid valves) and other devices. 绕在金属芯（通常为铁）上的导线线圈，当电流通过线圈时产生磁场，从而在芯上产生力。电磁阀广泛用于产生线性运动以驱动阀（电磁阀）和其他装置。 |
| Mean diameter (Unit m) | 平均直径（单位米） |
The average of the inside and outside diameters for a helical spring or hollow circular cylinder or sphere 螺旋弹簧或空心圆柱体或球体的内径和外径的平均值 |
| Flat head | 平头 |
Flat top surface and a conical bearing surface. 平顶表面和锥形轴承表面。 |
| Cavitation | 空蚀空化 |
The formation of vapour- or gas-filled cavities in a liquid due to reduction of the local pressure, often due to acceleration of the fluid, such as in flow through a convergent nozzle. If there is no dissolved gas in the liquid, vaporous cavitation occurs when the pressure falls below the saturated vapour pressure. If the bubbles are formed due to high temperature, the process is termed boiling. If there is dissolved gas, gaseous cavitation occurs due to pressure reduction, temperature increase, or diffusion (degassing). At the tips of marine propellers and in hydraulic machinery, the collapse of cavitation bubbles can cause noise and vibration and lead to surface damage in the form of pitting. 由于局部压力降低而在液体中形成充满蒸汽或气体的空腔，通常原因是流体的加速，例如收敛喷嘴的流动。如果液体中没有溶解气体，当压力降至饱和蒸汽压力以下时，会发生蒸汽空化。如果气泡是由于高温形成的，则该过程称为沸腾。如果存在溶解气体，则由于压力降低、温度升高或扩散（脱气），会发生气穴。在船用螺旋桨尖端和液压机械中，空化气泡的破裂可能会引起噪音和振动，并导致以点蚀形式出现的表面损坏。 |
| AISC | AISC |
The American Institute of Steel Construction. 美国钢结构学会。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Pressure surface | 压力面 |
The high-pressure surface of an aerofoil, turbine, or compressor blade. In normal aircraft applications, this is the lower surface of a wing. For applications, such as to high-performance motor vehicles, where the aerofoil is inverted to generate downforce, it is the upper surface. 机翼、涡轮或压缩机叶片的高压表面。在正常的飞机应用中，这是机翼的下表面。对于高性能机动车辆等应用，机翼翻转以产生下压力，它是上表面。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Fatigue limit for p % survival | p%存活率的疲劳极限 |
The limiting value of fatigue strength for p%survival as the number of stress cycles becomes very large; pmay be any number, such as 95, 90, etc. 随着应力循环次数的增加，p%存活率的疲劳强度极限值变得非常大；p可以是任何数字，例如95、90等。 |
| Snap temper | 快速回火 |
A precautionary interim stress-relieving treatment applied to high-hardenability steels immediately after quenching to prevent cracking because of delay in tempering them at the prescribed higher temperature. 在淬火后立即对高淬透性钢进行预防性临时应力消除处理，以防止因在规定的更高温度下回火延迟而开裂。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Stretch forming | 拉伸成型 |
A manufacturing process in which sheet-metal components are physically stretched over a forming die using a press, punch, or edge clamps. Stretching combined with bending reduces springback. 一种制造工艺，其中使用压力机、冲头或边缘夹具在成形模上物理拉伸金属板部件。拉伸与弯曲相结合可减少回弹。 |
| Tensile test (tension test) | 拉伸试验（拉力试验） |
A test in which a precisely-machined tensile specimen (tensile testpiece), typically circular or rectangular in cross section with large end sections that are gripped in the testing machine, is subjected to an increasing tensile load, usually to the point of fracture, to produce a stress–strain curve from which such material properties as modulus of elasticity, limit of proportionality, proof stress, yield point, and ultimate tensile stress can be determined. The relevant standard is ISO 6892-1. 一种试验，在这种试验中，精密加工的拉伸试样（拉伸试件）的横截面通常为圆形或矩形，具有在试验机中夹紧的大端部，受到越来越大的拉伸载荷，通常达到断裂点，以产生应力-应变曲线，从中可以看出弹性模量、比例极限等材料特性，可以确定验证应力、屈服点和极限拉伸应力。相关标准为ISO 6892-1。 |
| Blanking shear test | 落料剪力试验 |
A method used to determine the through-thickness shear strength of sheet material that involves blanking a disk out of flat strip using a simple punch-and-die method. Alson known as punching shear test. 一种用于确定板材全厚度剪切强度的方法，包括使用简单的冲模方法从扁平带材中冲裁出圆盘。也称为冲切试验。 |
| Gear pump | 齿轮泵 |
A positive-displacement pump in which fluid is pumped by meshing gears, one driven and the other an idler gear, on parallel axes within a closed casing. 一种容积式泵，其中流体由啮合齿轮泵送，在封闭外壳内的平行轴上一个驱动，另一个为空套齿轮。 |
| Lockbolt | 锁紧螺栓 |
A fastener which bears a superficial resemblance to a bolt, but which engages a collar (instead of a nut) with annular grooves (instead of threads). The collar is swaged over the grooves on the male fastener to develop preload. 表面上类似于螺栓的紧固件，但与环槽（而不是螺纹）接合的轴环（而不是螺母）。套环在阳紧固件上的凹槽上锻造，以产生预紧力。 |
| Assembly drawing | 装配图纸 |
An engineering drawing that shows how parts are assembled to produce a component or a complete machine. It may include sections to show internal features, dimensions that are critical for assembly, manufacturing information, and part numbers. 显示零件如何组装以生产组件或整机的工程图。它可能包括显示内部特征、对装配至关重要的尺寸、制造信息和零件编号的部分。 |
| Black oxide | 黑色氧化物 |
A black finish on a metal produced by immersing it in hot oxidizing salts or salt solutions. 通过将金属浸入热氧化盐或盐溶液中产生的黑色饰面。 |
| Ductile crack propagation | 延性裂纹扩展 |
Slow crack propagation that is accompanied by noticeable plastic deformation and requires energy to be supplied from outside the body. 缓慢的裂纹扩展，伴随着明显的塑性变形，需要从外部提供能量。 |
| Grain growth | 晶粒生长 |
An increase in the average size of the grains in polycrystalline metal, usually as a result of heating at elevated temperature. 多晶金属中晶粒平均尺寸的增加，通常是高温加热的结果。 |
| Forging cracks | 锻造裂纹 |
This may occur during fastener manufacturing at the cutting or forging operations and are located on the top of the head or on the raised periphery of indented head bolts. 这可能发生在紧固件制造过程中的切削或锻造操作中，并且位于头部的顶部或带锯齿的头部螺栓的凸起周边上。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Composite property | 复合属性 |
In thermodynamics, a property defined in terms of the properties of a closed system and its surroundings, such as the non-flow exergy function. 在热力学中，根据封闭系统及其周围环境的性质定义的性质，例如非流动火用函数。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Bolt blank | 螺栓毛坯 |
A rod on which a head has been formed, but on which no thread has been cut, from which bolts or screws may be made as required. 一种已形成头部但未切割螺纹的杆，可根据需要从中制造螺栓或螺钉。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Toughening mechanisms | 增韧机理 |
Various methods of increasing the resistance to crack initiation and propagation in materials. They include transformation toughening, in which the microstructure around the crack tip alters so as to slow down or arrest cracks; deflexion of cracks; various ways of de-sharpening crack tips; fibre bridging of cracks; and fibre pull-out. 增加材料中裂纹萌生和扩展阻力的各种方法。它们包括相变增韧，其中裂纹尖端周围的微观结构发生变化，以减缓或阻止裂纹；裂纹偏转；消除裂纹尖端锐化的各种方法；纤维桥接裂纹；和纤维拉出。 |
| Olsen cup test | 奥尔森杯测试 |
A cupping test in which a piece of sheet metal, restrained except at the center, is deformed by a standard steel ball until fracture occurs. The height of the cup at time of fracture is a measure of the ductility. 一种杯突试验，其中一块金属板，除了中心以外，被一个标准钢球变形，直到发生断裂。断裂时杯的高度是延展性的量度。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Dimensioning | 尺寸标注 |
The specification on an engineering drawing of the size (e.g. length, radius, angle, or spacing) and the relative location (e.g. angular position) of each feature of a component. The numerical values often include the tolerances. There should be no more dimensions than are necessary to manufacture the component. 工程图纸上对部件每个特征的尺寸（例如长度、半径、角度或间距）和相对位置（例如角位置）的规范。数值通常包括公差。尺寸不应超过制造组件所需的尺寸。 |
| Hot-wire analyzer | 热电阻丝型分析仪 |
An electrical atmosphere analysis device that is based on the fact that the electrical resistivity of steel is a linear function of carbon content over a range from 0.05% C to saturation. The device measures the carbon potential of furnace atmospheres (typically). This term is not to be confused with the hot-wire test which measures heat extraction rates. 一种基于以下事实的电气氛分析设备：钢的电阻率是从0.05%C到饱和范围内的碳含量的线性函数。该设备测量炉内气氛的碳势（通常）。不要将此术语与测量热提取率的热线测试相混淆。 |
| Centi (c) | 厘（c） |
An SI unit prefix indicating a multiplier of 0.01; thus centimetre is a unit of length equal to one one-hundredth of a metre or 10 mm. 表示乘数0.01的SI单位前缀；因此厘米是长度单位，等于一米的百分之一或10毫米。 |
| Coaxial | 同轴 |
A term for components having a common axis such as concentric shafts. 具有共同轴线的部件的术语，例如同心轴。 |
| Applied thermodynamics | 应用热力学 |
(engineering thermodynamics, thermodynamics) The science of the relationship between heat, work and the properties of systems and the ways in which heat energy from fuels can be converted into mechanical work. It involves the study of all aspects of energy use and energy transformation, including power generation, refrigeration, the relevant properties of the substances involved and the relationships between them. The principle of conservation of energy is a fundamental law of nature. （工程热力学、热力学）热、功和系统特性之间关系的科学，以及燃料中的热能可以转化为机械功的方式。它涉及能源使用和能源转换的各个方面的研究，包括发电、制冷、所涉及物质的相关特性以及它们之间的关系。能量守恒定律是自然的基本规律。 |
| Two-phase flow | 两相流 |
A flow in which two phases are present, for example gas bubbles in a liquid, liquid bubbles in another liquid with which it is immiscible, solid particles in a liquid or gas. 两相流动，例如液体中的气泡、与之不混溶的另一种液体中的液体气泡、液体或气体中的固体颗粒。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Length of engagement | 啮合长度 |
It is the axial measurement within which the external and internal threads have theoretical contact. 它是外螺纹和内螺纹具有理论接触的轴向测量。 |
| Normality | 常态 |
The principle that the vector sum of plastic strain increments is perpendicular to the yield surface. 塑性应变增量矢量和垂直于屈服面的原理。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Roughness | 粗糙度 |
The deviations from the wavy surface itself, caused by geometry of the cutting tool and its wear, machining conditions, microstructure of the workpiece, vibrations in the system, and so on. Surface roughness changes as a surface goes through the wearing-in process, but may then stabilize. 由刀具的几何形状及其磨损、加工条件、工件的微观结构、系统中的振动等引起的与波状表面本身的偏差。表面粗糙度随着表面经过磨合过程而变化，但随后可能会稳定下来。 |
| Stator | 定子 |
A ring of non-rotating blades or nozzles in a compressor, turbine, or other turbomachine, which directs fluid flow into an adjacent rotor. 涡轮压缩机、涡轮或其他涡轮机械中的一圈不旋转的叶片或喷嘴，将流体引导到相邻的转子中。 |
| Absorption hygrometer | 吸收式湿度计 |
An instrument that determines the content of water vapour in the atmosphere by it being absorbed into a hygroscopic medium. 通过吸收到吸湿介质中来确定大气中水蒸气含量的仪器。 |
| Relaxation | 松弛 |
The loss of tension, and therefore Clamping force, in a bolt and joint as a result of Embedment, vibration loosening, gasket creep, differential thermal expansion, etc. 由于嵌入、振动松动、垫圈蠕变、热膨胀差等原因，螺栓和接头中的张力损失，因此夹紧力损失。 |
| Tap | 旋塞 |
1. A threaded hard metal plug for cutting screw threads in holes. It has longitudinal grooves for the clearance of chips while cutting. Progressive cutting is achieved by using three taps in succession: taper, second, and plug. First and second taps have tapers to help start the thread along the axis of the hole; the plug tap has no taper and is used on the final cut in a blind hole. 2. A valve in, or at the end of, a pipeline. 1.一种用于在孔中切割螺纹的螺纹硬金属塞。它具有纵向凹槽，用于在切割时清除切屑。渐进式切割通过连续使用三个丝锥实现：锥度、二次和塞。第一和第二丝锥具有锥度，以帮助沿孔的轴线开始螺纹；塞式丝锥没有锥度，用于盲孔的最终切割。2.管道中或管道末端的阀门。 |
| Partial annealing | 不完全退火 |
An imprecise term used to denote a treatment given cold-worked material to reduce the strength to a controlled level or to effect stress relief. To be meaningful, the type of material, the degree of cold work, and the time-temperature schedule must be stated. 一个不精确的术语，用于表示冷加工材料的处理，以将强度降低到受控水平或消除应力。为了有意义，必须说明材料类型、冷加工程度和时间-温度计划。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Slug | 猛击 |
1. A starting workpiece for forging and similar operations, such as a length of wire or rod to make a bolt blank on which a thread can be rolled or cut. 2. (geepound) An obsolete imperial (non-SI) unit of mass, being the mass which under an acceleration of one foot per second squared gives a force of one pound-force. The conversion to SI is 1 slug = 14.593 902 94 kg. 3. A large-scale flow structure which occurs in the transition from laminar to turbulent flow in a pipe. 1.一种用于锻造和类似操作的起始工件，如用于制造螺栓毛坯的一段线材或棒材，在该毛坯上可以轧制或切割螺纹。2.（吉磅）一种已被淘汰的英制（非国际单位制）质量单位，在一英尺/秒平方加速度下产生一磅力的质量。转化为SI国际单位制的转化率为1slug=14.59390294kg。3.一种大规模流动结构，其发生在管道中从层流到湍流的过渡中。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Nipple | 喷嘴 |
A device containing a non-return valve screwed into a lubrication point through which grease may be introduced, for example into a bearing. 一种包含止回阀的装置，该止回阀拧入润滑点，通过该润滑点可以将润滑脂引入，例如轴承中。 |
| Balance piston | 平衡活塞 |
(balance drum, dummy piston) A disc attached to the shaft of a turbine or compressor, to one side of which high or low pressure is applied to counteract the axial thrust produced by the pressure change across the machine. A form of thrust bearing. （平衡鼓，假活塞）连接在涡轮机或压缩机轴上的圆盘，在其一侧施加高压或低压，以抵消机器压力变化产生的轴向推力。推力轴承的一种形式。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| Nano machining | 纳米加工 |
The machining of silicon chips typically less than 1 nm thick. 硅芯片的加工通常小于1nm厚。 |
| Pin or mandrel | 销或心轴 |
In bend testing, the plunger or tool used in making semiguided, guided, or wrap-around tests to apply the bending force to the inside surface of the bend. In free bends or semiguided bends to an angle of180°, a shim or block of the proper thickness may be placed between the legs of the specimen as bending is completed. This shim or block is also referred to as a pin or mandrel. 在弯曲测试中，用于进行半导向、导向或环绕测试以将弯曲力施加到弯曲内表面的柱塞或工具。在180°角的自由弯曲或半导向弯曲中，弯曲完成后，可在试样支腿之间放置适当厚度的垫片或垫块。该垫片或垫块也称为销或心轴。 |
| Scleroscope hardness number (HSc or HSd) | 硬化镜硬度值（HSc或HSd） |
A number related to the height of rebound of a diamond-tipped hammer dropped on the material being tested. It is measured on a scale determined by dividing into 100 units the average rebound of the hammer from a quenched(to maximum hardness) and untempered AISI W5 tool steel test block. 与落在被测材料上的菱形锤的回弹高度相关的数字。通过将锤子从淬火（达到最大硬度）和未淬火的AISI W5工具钢试块上的平均回弹分为100个单位来测量。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Engine | 引擎 |
A machine that converts energy, including the chemical energy in a fuel and electrical energy, into mechanical energy, usually to produce power delivered through a rotating shaft or thrust. Examples include internal-combustion engines, gas and steam turbines, rocket engines, electric, hydraulic and pneumatic motors. 一种将能量（包括燃料中的化学能和电能）转换为机械能的机器，通常通过旋转轴或推力产生动力。例子包括内燃机、燃气轮机和蒸汽轮机、火箭发动机、电动、液压和气动马达。 |
| Free ferrite | 游离铁氧体 |
Ferrite that is formed directly from the decomposition of hypoeutectoid austenite during cooling, without the simultaneous formation of cementite. Also proeutectoid ferrite. 在冷却过程中亚共析奥氏体分解直接形成的铁素体，没有同时形成渗碳体。也是先共析铁氧体。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Combustion chamber | 炉膛 |
1. In a piston engine, the volume between the head of an individual cylinder and the crown of the piston in which the fuel–air mixture burns during each power stroke of the engine. 2. (combustor) In a gas-turbine engine, a ramjet, an afterburner, or a rocket motor, the component, often cylindrical or annular in shape, in which the fuel–air mixture burns in a continuous-flow process. 1.在活塞式发动机中，在发动机的每个动力冲程中，燃料-空气混合物燃烧的单个气缸盖和活塞顶之间的体积。2.（燃烧室）在燃气涡轮发动机、冲压发动机、加力燃烧室或火箭发动机中，燃料-空气混合物在连续流动过程中燃烧的部件，通常为圆柱形或环形。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Achme thread | Achme螺纹 |
A screw thread having an included angle of 29° and largely used for feed screws on machine tools. 一种夹角为29°的螺纹，主要用于机床上的进给丝杠。 |
| Hydrodynamics | 流体力学 |
A term sometimes used to mean fluid dynamics, even when the fluid is a gas or a liquid other than water. 有时用于表示流体动力学的术语，即使流体是气体或水以外的液体。 |
| Resistance factor | 阻力系数 |
Probabilistic factor representing the uncertainties in the designer’s estimate of the strength of a shear joint. Used in Load and resistance factor design. 概率系数，表示设计人员对剪切接头强度估计的不确定性。用于载荷和阻力系数设计。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Dynamic strain aging | 动态应变时效 |
A behavior in metals in which solute atoms are sufficiently mobile to move toward and interact with dislocations. This results in strengthening over a specific range of elevated temperature and strain rate. 金属的一种特点，其中溶质原子具有足够的移动能力，能够向位错移动并与位错相互作用，会导致在特定的高温和应变速率范围内强化。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Equilibrium diagram | 平衡图 |
A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant. 在完全平衡条件下，合金系统中相场的温度、压力和成分极限的图形表示。在金属系统中，压力通常被认为是恒定的。 |
| Vacuum relief valve | 真空安全阀 |
A valve that admits gas to a system under vacuum, should the degree of vacuum become excessive. 如果真空度过高，允许气体在真空下进入系统的阀门。 |
| Shoulder screw | 轴肩螺钉 |
A screw having two or more diameters or shoulders and commonly used for supporting levers and other machine parts that have to operate freely. 一种具有两个或两个以上直径或轴肩的螺钉，通常用于支撑杠杆和其他必须自由操作的机器部件。 |
| Crest of screw thread | 螺纹牙顶 |
The top surface joining the two sides of flanks of a thread. 连接螺纹牙侧两侧的顶面。 |
| Plug | 螺塞 |
1. An object, usually tapered, used to block a hole to prevent fluid from escaping or flowing. 2. The central moveable part of a valve. 3. In the flow of a yield-stress fluid through a pipe or duct, the central region is often assumed to take the form of a plug with uniform axial velocity. 4. In thermoforming, a shaping tool that forces a heated plastic sheet into a female mould. 1.一种物体，通常为锥形，用于堵塞孔以防止流体逸出或流动。2.阀门的中心可移动部分。3.在屈服应力流体通过管道或管道的流动中，中心区域通常假定为具有均匀轴向速度的塞子形式。4.在热成型技术中，一种成型工具，将加热的塑料板压入阴模中。 |
| Effective yield strength | 有效屈服强度 |
An assumed value of uniaxial yield strength that represents the influence of plastic yielding on fracture test parameters. 单轴屈服强度的假设值，代表塑性屈服对断裂试验参数的影响。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Low-E coating | 低辐射涂层 |
(low-emittance coating) A thin metallic or metal-oxide coating on a glass sheet to absorb and reflect infrared radiation. The coating is applied either by a pyrolytic chemical vapour-deposition process (hard coat), or by sputtering (soft coat). （低辐射涂层）玻璃板上的薄金属或金属氧化物涂层，用于吸收和反射红外辐射。通过热解化学气相沉积工艺（硬涂层）或溅射（软涂层）施加涂层。 |
| Brittle | 脆性材料 |
A brittle material is one that breaks, often suddenly, with no permanent deformation. Examples of brittle materials are some cast irons, glass, concrete, and some plastics. A bolt is said to be brittle if it will break when stretched only a small amount past its yield point. 脆性材料通常会突然断裂，不会产生永久变形。脆性材料的例子有一些铸铁、玻璃、混凝土和一些塑料。如果螺栓在拉伸时仅超过其屈服点一小部分就会断裂，则称其为脆性螺栓。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| Blowing | 吹气 |
The process by which a gas is transferred through a porous surface over which there is a gas flow. The effect is used to decrease skin friction and increase heat transfer, for example in turbine-blade cooling. 气体通过有气流的多孔表面转移的过程。该效应用于减少表面摩擦和增加传热，例如在涡轮叶片冷却的过程中。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Shear test | 剪切试验 |
Any of several tests to obtain shear strength of a metal. Common tests used on mill products include the double-shear test, single-shear test, the blanking shear test (also known as the punching shear test) and the torsion test. 获得金属剪切强度的几种测试中的任何一种。轧机产品上常用的试验包括双剪试验、单剪试验、落料剪切试验（也称为冲切试验）和扭转试验。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Isothermal annealing | 等温退火 |
Austenitizing a ferrous alloy and then cooling to and holding at a temperature at which austenite transforms to a relatively soft ferrite carbide aggregate. 将铁合金奥氏体化，然后冷却至奥氏体转变为相对软的铁素体碳化物集合体的温度并保持该温度。 |
| Batch furnace | 间歇式炉 |
A furnace used to heat treat a single load at a time. Batch-type furnaces are necessary for large parts such as heavy forgings and are preferred for complex alloy grades requiring long cycles. 用于一次热处理单个负载的炉子。对于重型锻件等大型零件，间歇式炉是必需的，对于需要长周期的复杂合金牌号来说是首选。 |
| Centrifugal fan | 离心风机 |
A machine with a rotor consisting of a number of blades mounted around a hub and used for moving air or other gases. The gas enters the rotor axially and is discharged radially at increased pressure. 一种带有转子的机器，转子由安装在轮毂周围的许多叶片组成，用于移动空气或其他气体。气体轴向进入转子并在增加的压力下径向排出。 |
| Normal stress (Unit N) | 法向应力（单位：N） |
The stress component perpendicular to a plane on which forces act. Normal stress may be either tensile stress or compressive stress. A stress in a fluid (such as pressure) or a solid, that is perpendicular to the surface on which it acts. The surface may be a real external surface or an imaginary internal one. 垂直于受力平面的应力分量。法向应力可以是拉应力或压应力。流体（如压力）或固体中垂直于其作用表面的应力。该表面可以是真实的外表面或假想的内表面。 |
| Assembly line | 流水线 |
A system of mass production in which work is moved progressively from one operation to another, ultimately to give the final complete product. 一种大规模生产系统，其中工作逐渐从一个操作转移到另一个操作，最终得到完整产品。 |
| Materials science | 材料科学 |
The study of the properties, behaviour, and application of solid substances such as metals, ceramics, glasses, polymers, composites, biomaterials, and semiconductors, at all scales from the atomic to the macroscopic. The topic has its origins in metallurgy. 研究金属、陶瓷、玻璃、聚合物、复合材料、生物材料和半导体等固体物质的特性、行为和应用，涵盖从原子到宏观的所有范围。起源于冶金学。 |
| Natural aging | 自然时效 |
Spontaneous aging of a supersaturated solid solution at room temperature. 过饱和固溶体在室温下的自发时效。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Fastener with waisted shank | 带腰柄的紧固件 |
Finished fastener with a shank diameter of ds < d2. 柄径ds |
| Vapour static pressure | 蒸汽静压 |
(Unit Pa or bar) A pressure analogous to hydrostatic pressure, where the fluid is a vapour such as steam. A term used in geothermal applications. （单位Pa或bar）类似于静水压力的压力，其中流体是蒸汽，如蒸汽。地热应用中使用的术语。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Working load (Unit N) | 工作负荷（单位：N） |
The tension in a bolt in use; tension produced by a combination of Residual preload and a portion (usually) of any External load. The Joint diagram is usually used to predict the approximate working load a fastener will see in service. The load under which a component or structure is designed to operate under normal conditions. 螺栓在使用中的张力；残余预载荷和部分（通常）任何外部载荷的组合产生的张力。连接图通常用于预测紧固件在使用中的近似工作载荷。部件或结构设计为在正常条件下运行的荷载。 |
| Blue annealing | 蓝色退火 |
Heating hot-rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental. 在开放式炉中将热轧铁板加热到转变范围内的温度，然后在空气中冷却，以软化金属。在表面上形成蓝色氧化物是偶然的。 |
| Computer-aided design (CAD) | 计算机辅助设计（CAD） |
Generally, design and calculations performed by computer; more specifically, the use of computer graphics and models to communicate design concepts. Computer-aided design and computer-aided manufacturing (CAD/CAM) is where component dimensions resulting from CAD are passed by electronic means directly to machines for manufacture. 一般由计算机进行设计和计算，更具体地说，使用计算机图形和模型来传达设计概念。计算机辅助设计和计算机辅助制造（CAD/CAM）是由CAD产生的组件尺寸通过电子方式直接传递到机器进行制造。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Angularity | 角度 |
The underfaces of the nut and the bolt head should be exactly perpendicular to the thread or shank axes. If the angle between the face and the axis is, for example, 868 or 948, the fastener is said to have an angularity of 48 (sometimes called Perpendicularity). 螺母和螺栓头的底面应与螺纹或柄轴完全垂直。例如，如果面和轴之间的角度为868或948，则称紧固件的角度为48（有时称为垂直度）。 |
| Twist | 扭转 |
The helix produced in a cylindrical component, such as a shaft, wire, tensioned cable, or rope, when one end is rotated relative to the other. Measured either as the number of turns per unit length, or by the helix angle (twist angle). 当一端相对于另一端旋转时，在圆柱形部件（如轴、钢丝、张紧电缆或绳索）中产生的螺旋。以每单位长度的圈数或螺旋角（扭曲角）测量。 |
| Spring load (Unit N) | 弹簧载荷（单位：N） |
A load exerted on a component by bending, compressing, extending, or twisting an attached spring. Mechanical energy stored in the spring can be released if any constraints on the component are removed. 通过弯曲、压缩、延伸或扭转连接的弹簧而施加在部件上的载荷。如果部件上的任何约束被移除，则可以释放弹簧中存储的机械能。 |
| Proof stress | 弹性极限应力 |
(1) The stress that will cause a specified small permanent set in a material. (2) A specified stress to be applied to a member or structure to indicate its ability to withstand service loads. （1）在材料中引起规定的小永久变形的应力。（2）施加在构件或结构上的规定应力，以表明其承受工作荷载的能力。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Screw | 螺钉 |
Threaded fastener designed to be used in a tapped or untapped (e.g., wood screw) hole, but not with a nut. A fastener with a screw thread cut or rolled into its cylindrical or conical shank, intended either to cut its own thread (as in a wood screw) or engage in a threaded hole. A self-tapping screw (sheet-metal screw, tapping screw) has a sufficiently hard thread that it cuts an internal thread in thin sheet or a component made of soft material when driven into a hole in the sheet or component. The screw head is the part of a screw used to apply torque to the screw. Common screw-head designs are circular in cross section with a diametral slot or cross, or hexagonal and recessed with a cross or hexagon. A screw thread is one or more continuous helical grooves of uniform section along either the exterior surface (male thread) or the interior surface (female thread) of a cylindrical or conical body. The three-dimensional shape that results when the thread cross section is rotated and axially advanced along an axis is called a helicoid, the angle that the thread makes when projected on to the axis being called the angle of inclination. Threads are employed in fasteners such as bolts, nuts, and screws; location and measuring instruments; in power drives; in some electrical fittings (Edison thread); and on the ends of crankshafts to suppress oil leakage (thrower thread). Parallel threads are formed on cylinders; tapered threads on cones, typically with a taper rate of 1:16. A screw with a righthanded thread appears to move away from the observer when turned clockwise. All standard screws, bolts and nuts have right-hand threads, but left-handed threads are sometimes employed. The axial distance between corresponding points on adjacent threads is called the screw pitch or screw rate and, for a single continuous helical groove (a single-start thread), is the same as the change in axial distance (the lead) between a nut and the head of a bolt during one revolution, the number of thread forms per mm then being the reciprocal of the pitch. For the same screw diameter, coarse threads have fewer threads per mm than fine threads. A multiple-start screw thread (usually coarse, see later) consists of two or more identical threads running simultaneously along its axis so as to provide greater bearing area and greater velocity ratio. The starts are separated by 180° (double start), 120° (triple start), 90° (quadruple start) etc., depending upon the number of threads. Thus, in double-start threads, the lead is twice the pitch; and so on. The axial distance between corresponding points on two adjacent threads in a multiple start thread is called the divided pitch. The position on a screw thread where there is equal distance between the flanks on the solid part of the thread and in the space between the threads is the pitch point, the associated diameter of which is termed the pitch diameter. The basic nomenclature for threads, some of which is common with that for toothed gearing, is shown in the diagrams. A helix formed or cut on a cylindrical surface which may advance along the axis to the right or left. The helix may be single or multiple. 一种螺纹紧固件，设计用于攻丝或未攻丝（如木螺钉）孔，但不与螺母配合使用。其螺纹被切割或卷成圆柱形或锥形柄，用于切割自身螺纹（如木螺钉）或嵌入螺纹孔。自攻螺钉（钣金螺钉、自攻螺钉）具有足够硬的螺纹，当打入薄板或部件中的孔时，它会在薄板或软材料部件中切割内螺纹。螺钉头是螺钉的一部分，用于向螺钉施加扭矩。常见的螺钉头设计为横截面为圆形，带有直径槽或十字，或为六边形，并带有十字或六边形凹槽。螺纹是沿圆柱形或锥形体的外表面（外螺纹）或内表面（内螺纹）具有均匀截面的一个或多个连续螺旋槽。当螺纹横截面旋转并沿轴轴向前进时产生的三维形状称为螺旋面，螺纹投影到轴上时形成的角度称为倾角。螺纹用于紧固件，如螺栓、螺母和螺钉；定位和测量仪器；在动力驱动中；在一些电气配件中（爱迪生螺纹）；并安装在曲轴端部，以抑制漏油（抛掷器螺纹）。在圆柱体上形成平行螺纹；圆锥上的锥形螺纹，通常具有1:16的锥形率。当顺时针旋转时，具有右手螺纹的螺钉似乎会远离观察者。所有标准螺钉、螺栓和螺母都有右手螺纹，但有时使用左手螺纹。相邻螺纹上对应点之间的轴向距离称为螺距或螺纹率，对于单个连续螺旋槽（单个起始螺纹），与螺母和螺栓头之间的轴向间距（导程）在一周内的变化相同，每mm的螺纹形式数为螺距的倒数。对于相同的螺钉直径，粗螺纹的每毫米螺纹数少于细螺纹。多头螺纹（通常为粗螺纹，见下文）由两个或多个沿其轴线同时延伸的相同螺纹组成，以提供更大的承载面积和更大的速比。根据螺纹的数量，起点之间的间隔为180°（双起点）、120°（三起点）、90°（四起点）等。因此，在双起始螺纹中，导程是螺距的两倍；多起点螺纹中两个相邻螺纹上对应点之间的轴向距离称为分割螺距。螺纹上的位置，即螺纹实体部分的侧面和螺纹之间的空间之间的距离相等，即节点，其相关直径称为节径。图中显示了螺纹的基本术语，其中一些与齿轮传动的基本术语相同。在圆柱面上形成或切割的螺旋线，可沿轴线向右或向左前进。螺旋可以是单个或多个。 |
| Critical diameter | 临界直径 |
(D) Diameter of the bar that can be fully hardened with 50% martensite at its center. （D）中心有50%马氏体可完全硬化的棒材直径。 |
| British thermal unit (BTU, Btu) | 英热单位（BTU，Btu） |
An obsolete (non-SI) imperial unit of energy defined as the energy required to raise the temperature of one pound of pure water at 68°F by 1°F. The conversion to SI is 1 Btu = 1.055 056 × 103 J. 一种已被淘汰的（非SI）英制能量单位，定义为将68°F的一磅纯水的温度升高1°F所需的能量。转换为SI为1Btu=1.055056×103J。 |
| Relaxed stress | 松弛应力 |
The initial stress minus the remaining stress at a given time during a stress-relaxation test. 在应力松弛试验期间，初始应力减去给定时间的剩余应力。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| Torsional stress | 扭转应力 |
The shear stress on a transverse cross section resulting from a twisting action. 扭转作用在横截面上产生的剪切应力。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Carbon restoration | 碳修复 |
Replacing the carbon lost in the surface layer from previous processing by carburizing this layer to substantially the original carbon level. Sometimes called recarburizing. 通过将该层渗碳到基本上原始的碳水平来替换先前处理中在表面层中损失的碳。有时称为再碳化。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Blind rivet | 盲孔铆钉 |
A rivet that enables a connexion to be made from one side only of an assembly. 一种铆钉，可以仅从组件的一侧进行连接。 |
| Full size body | 全尺寸螺纹杆 |
The body of a bolt or screw which has a diameter between the minimum and maximum limits of the major diameter of the thread. 螺栓或螺钉的主体，其直径介于螺纹大径的最小和最大限制之间。 |
| Kilocalorie | 千卡 |
(Cal, kg-cal, kilogram-calorie, large calorie) An obsolete (i.e. non-SI) unit of energy equal to 1 000 cal. （卡，千克卡，千克卡路里，大卡路里）一种已被淘汰的（即非国际单位制）能量单位，等于1000卡。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Heat (q, Q) (Unit J) | 热量（q, Q）（单位J） |
A form of energy that is transferred across the boundary of a system at one temperature to another system (or the surroundings) at a different temperature by virtue of the temperature difference between them. Heat can be identified only as it crosses the boundary. A body can never be said to contain heat which is thus a transient phenomenon. 一种能量形式，由于它们之间的温差在一个温度下通过系统边界传递到另一个温度不同的系统（或环境）。只有当热量穿过边界时才能识别。一个物体不能说永远含有热量，这是一种瞬态现象。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Load factor (F) | 负载系数（F） |
The ratio between an increase in bolt tension and the external load which has caused the increase. Factors reflecting the probability of an increase in load in a shear joint. Used in load and resistant factor design. 螺栓张力增加与导致增加的外部载荷之间的比率。反映剪切接缝中荷载增加概率的系数。用于载荷和阻力系数设计。 |
| Extensometer | 引伸计 |
An instrument for measuring changes in length over a given gage length caused by application or removal of a force. Commonly used in tension testing of metal specimens. Any instrument which measures the change in length of a part as the part is loaded. 一种用于测量在给定标距上由施加或移除力引起的长度变化，在零件加载时测量零件长度变化的仪器。常用于金属试样的拉力试验。 |
| Sampling | 抽样 |
The process of measuring a series of values of a time-varying quantity. 测量一系列时变量值的过程。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Rockwell superficial hardness test | 洛氏表面硬度试验 |
Same as Rockwell hardness test, except that smaller minor and major loads are used. 与洛氏硬度测试相同，只是使用较小的次要载荷和主要载荷。 |
| Fastener standard | 紧固件标准 |
A document which details the attributes of a finished fastener and includes such characteristics as geometry, material or chemistry, heat treatment, finish, testing lot size, and packaging. 详细说明紧固件属性的文件，包括几何形状、材料或化学、热处理、表面处理、测试批量和包装等特性。 |
| Root diameter (Unit m) | 根部直径（单位：m） |
The diameter of the circle passing through the roots of teeth in gear teeth or screw threads. 穿过齿轮齿或螺纹中齿根的圆的直径。 |
| Threaded fastener | 螺纹紧固件 |
Studs, bolts, and screws of all sorts, with associated nuts. One of the most interesting, complex, useful—and frustrating—components yet devised. 各种螺柱、螺栓和螺钉，以及相关的螺母。 |