| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Nut | 螺母 |
A metal fastener of square, hexagon or other shape, having an internal thread which screws onto a bolt, stud or arbor. An internally-threaded fastener used with externally-threaded bolts. Usually hexagonal in shape but there is a multitude of other geometries, such as square, for special purposes and different gripping tools. 一种方形、六角形或其他形状的金属紧固件，具有内螺纹，可拧在螺栓、螺柱或心轴上。与外螺纹螺栓一起使用的内螺纹紧固件。通常为六边形，但也有许多其他几何形状，如方形，用于特殊用途和不同的夹持工具。 |
| Blow moulding | 吹塑 |
The manufacture of hollow polymer objects (e.g. bottles) by expanding, with internal air pressure, a tube sealed at one end (parison) against the walls of a cavity mould. 通过使用内部气压使一端密封的管子（型坯）靠在型腔模具的壁上膨胀来制造中空聚合物物体（例如瓶子）。 |
| Uniform strain | 均匀应变 |
The strain occurring prior to the beginning of localization of strain (necking); the strain to maximum load in the tension test. 在应变局部化（颈缩）开始之前发生的应变；拉伸试验中最大载荷的应变。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Die | 模具 |
1. A tool having an appropriately-shaped hole through which material may be extruded or drawn. 2. A tool employed in forging. 3. A block having the male or female shape employed in stamping operations. 4. A thick circular disc, driven by a die wrench, with internally-threaded cutting edges for producing a screw thread. A die wrench (die stock) holds a screw-cutting die and has two projecting arms for applying the torque necessary to cut the thread. A die having a hexagonal or square shape (die nut), driven by a spanner, is used in confined spaces where a die wrench cannot be rotated through a full circle. 1.一种具有适当形状的孔的工具，通过该孔可以挤压或拉伸材料。2.一种用于锻造的工具。3.一种用于冲压操作的具有阳或阴形状的块体。4.一种由模具扳手驱动的厚圆盘，具有用于产生螺纹的内螺纹切削刃。冲模扳手（冲模）装有一个螺旋切割模，并有两个突出臂，用于施加切割螺纹所需的扭矩。由扳手驱动的六边形或方形模具（模具螺母）用于模具扳手无法旋转一整圈的受限空间。 |
| Turbulent flow (turbulence) | 湍流 |
Fluid motion characterized by disorderly, rotational (i.e. vortical) three-dimensional velocity fluctuations covering a wide range of frequency and length scales. The pressure, temperature, and other fluid properties also fluctuate and the diffusion of heat, mass, and momentum is greatly enhanced. As are laminar and transitional flow, turbulent flow of a Newtonian fluid is governed by the Navier–Stokes equations which can in principle be solved by direct numerical simulation (DNS) in which all time and length scales of the fluctuating motion are resolved. 流体运动的特点是无序、旋转（即旋涡）三维速度波动，覆盖广泛的频率和长度尺度。压力、温度和其他流体特性也会波动，热、质量和动量的扩散会大大增强。与层流和过渡流一样，牛顿流体的湍流由Navier-Stokes方程控制，该方程原则上可以通过直接数值模拟（DNS）求解，在直接数值模拟中，波动运动的所有时间和长度尺度都可以求解。 |
| Bolt blank | 螺栓毛坯 |
A rod on which a head has been formed, but on which no thread has been cut, from which bolts or screws may be made as required. 一种已形成头部但未切割螺纹的杆，可根据需要从中制造螺栓或螺钉。 |
| Flange bolt | 法兰螺栓 |
A bolt with a built in washer-like flange just below the head. 在头部下方带有内置垫圈状法兰的螺栓。 |
| Crest of screw thread | 螺纹牙顶 |
The top surface joining the two sides of flanks of a thread. 连接螺纹牙侧两侧的顶面。 |
| Brittle lacquer coating | 脆性漆涂层 |
A lacquer that, when painted on to an unloaded body, reveals the direction of maximum tension stresses from the pattern of cracking produced in the lacquer when the body is loaded. 一种漆，当涂在未加载的车身上时，从车身加载时在漆中产生的裂纹图案中显示出最大拉应力的方向。 |
| Unit | 单位 |
A numerical indication of the magnitude of a physical quantity. The basic units of mass, length, time, etc. are relative to agreed standards. 物理量大小的数字指示。质量、长度、时间等基本单位与商定的标准相对应。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Centigrade heat unit | 摄氏热量单位 |
(Celsius heat unit, CHU) An obsolete (i.e. non-SI) unit equal to the energy required to increase the temperature of one pound of pure, air-free water from 14.5°C to 15.5°C at a pressure of one standard atmosphere. （摄氏热量单位，CHU）一个已被淘汰的（即非国际单位制）单位，等于在一个标准大气压的压力下将一磅纯净的无空气水的温度从14.5°C提高到15.5°C所需的能量. |
| Tooth lock washers | 带齿锁紧垫圈 |
These washers serve to lock fasteners, such as bolts and nuts, to the component parts of an assembly, or increase the friction between the fasteners and the assembly. They are designated in a manner similar to helical spring lock washers, and are available in carbon steel. 这些垫圈用于将紧固件（如螺栓和螺母）锁定到组件的零部件上，或增加紧固件与组件之间的摩擦力。它们的设计方式类似于螺旋弹簧锁紧垫圈，可采用碳钢。 |
| Shoulder | 轴肩 |
The portion of a shaft, stepped component, or flanged component, where a change in diameter or other dimension occurs. Even for a nominal step change, in practice there will be a radius where shoulder and shaft meet in order to avoid too severe a stress concentration. 轴、阶梯部件或法兰部件的直径或其他尺寸发生变化的部分。即使是名义阶跃变化，在实践中，肩部和轴相交处也会有一个半径，以避免出现过严重的应力集中。 |
| Thermoelectric material | 热电材料 |
A material in which any of the thermoelectric phenomena, such as the Peltier, Seebeck, and Thomson effects, are especially strong. 一种热电现象特别强烈的材料，如珀尔帖效应、塞贝克效应和汤姆森效应。 |
| Nanotechnology | 纳米技术 |
The science and engineering of materials that have been structured on length scales of 1–100 nm, resulting in modified physical properties owing to changes in the ratio of surface area to volume (atoms on surfaces having different symmetry from those in the bulk) and because many of the fundamental physical processes that underpin the properties of materials have a characteristic length scale of a few nm, so that alteration of microstructure at the nm level alters the bulk properties. 材料科学与工程，其结构长度为1-100nm，由于表面积与体积之比的变化（表面上的原子与体中的原子具有不同的对称性），并且支撑材料性质的许多基本物理过程具有几纳米的特征长度尺度，因此改变纳米级微观结构会改变体性质。 |
| Tap | 旋塞 |
1. A threaded hard metal plug for cutting screw threads in holes. It has longitudinal grooves for the clearance of chips while cutting. Progressive cutting is achieved by using three taps in succession: taper, second, and plug. First and second taps have tapers to help start the thread along the axis of the hole; the plug tap has no taper and is used on the final cut in a blind hole. 2. A valve in, or at the end of, a pipeline. 1.一种用于在孔中切割螺纹的螺纹硬金属塞。它具有纵向凹槽，用于在切割时清除切屑。渐进式切割通过连续使用三个丝锥实现：锥度、二次和塞。第一和第二丝锥具有锥度，以帮助沿孔的轴线开始螺纹；塞式丝锥没有锥度，用于盲孔的最终切割。2.管道中或管道末端的阀门。 |
| Alpha iron | 阿尔法铁 |
The body-centered cubic form of pure iron, stable below 910 °C (1670 °F). 纯铁的体心立方形式，在910°C(1670°F)以下稳定。 |
| Torque wrench | 扭矩扳手 |
A manual wrench which incorporates a gage or measuring apparatus of some sort to measure and display the amount of torque being delivered to the nut or bolt. All wrenches produce torque. Only a torque wrench tells how much torque. A socket wrench or ring spanner that can be set to allow a specific torque to be applied to a nut or bolt head. 一种手动扳手，包括某种量规或测量装置，用于测量和显示传递至螺母或螺栓的扭矩量。所有扳手都产生扭矩。只有扭矩扳手才能显示扭矩大小。一种套筒扳手或梅花扳手，可设置为允许对螺母或螺栓头施加特定扭矩。 |
| Washer | 垫圈 |
An annular disc of metal, rubber, plastic, ceramic, etc., placed between two surfaces in contact either to spread the load (for example, between a surface and a tightened nut or a bolt head), to provide a seal, or to separate or align components. 由金属、橡胶、塑料、陶瓷等制成的环形圆盘，放置在两个接触面之间，以分散载荷（例如，在一个表面和拧紧的螺母或螺栓头之间），提供密封，或分离或对齐部件。 |
| Critical point | 临界点 |
(1) The temperature or pressure at which a change in crystal structure, phase or physical properties occurs. Same as transformation temperature. (2) In an equilibrium diagram, that specific value of composition, temperature and pressure, or combinations thereof, at which the phases of a heterogeneous system are in equilibrium. （1） 晶体结构、相或物理性质发生变化的温度或压力。与转变温度相同。（2） 在平衡图中，指组成、温度和压力或其组合的特定值，在该值下，多相体系的相处于平衡状态。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| Surface hardening | 表面硬化 |
A generic term covering several processes applicable to a suitable ferrous alloy that produces, by quench hardening only, a surface layer that is harder or more wear resistant than the core. There is no significant alteration of the chemical composition of the surface layer. The processes commonly used are carbonitriding, carburizing, induction hardening, flame hardening, nitriding, and nitrocarburizing. Use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于仅通过淬火硬化产生比型芯更硬或更耐磨的表面层的合适铁合金的几种工艺。表面层的化学成分没有显著改变。常用的工艺有碳氮共渗、渗碳、感应淬火、火焰淬火、氮化和氮碳共渗。最好使用适用的特定工艺名称。 |
| Sampling frequency (Unit Hz) | 采样频率（单位Hz） |
(sampling rate) The number of measurement samples per unit time taken from a continuous analogue signal to produce a discrete signal. It is the inverse of the time between successive measurements (sampling interval, sampling period, or sampling time). （采样率）从连续模拟信号中提取以产生离散信号的每单位时间的测量样本数。它是连续测量之间时间的倒数（采样间隔、采样周期或采样时间）。 |
| Embedment | 嵌入 |
Localized plastic deformation in heavily loaded fasteners allows one part to sink into, or smooth the surface of, a softer or more heavily loaded second part. Nuts embed themselves in joint surfaces. Bolt threads embed themselves in nut threads, etc. 重载紧固件中的局部塑性变形允许一个零件陷入较软或更重载的第二零件中，或使其表面光滑。螺母嵌入接合面中。例如螺栓螺纹嵌入螺母螺纹等。 |
| Pitch diameter | 中径 |
For screw threads, the diameter of an imaginary cylinder, the surface of which would pass through the threads at such points that would make the width of the groove and width of the land equal to one half the pitch. 对于螺纹，指一个假想圆柱体的直径，其表面将在使凹槽宽度和焊盘宽度等于螺距一半的点穿过螺纹。 |
| Screw thread | 螺纹 |
A ridge of uniform section or shape in the form of a helix on the external or internal surface of a cylinder, or in the form of a conical spiral on the external or internal surface of a cone. 在圆柱体的外表面或内表面上呈螺旋形或在圆锥体的外表面和内表面上以锥形螺旋形的均匀截面或形状的脊。 |
| Computational domain | 计算域 |
In CFD, FEM, and other numerical methods, the area or volume within which calculations are performed and on the periphery of which the boundary conditions are specified. 在CFD、FEM和其他数值方法中，执行计算的区域或体积以及在其外围指定边界条件的区域或体积。 |
| Differential heating | 差动加热 |
Heating that intentionally produces a temperature gradient within an object such that, after cooling, a desired stress distribution or variation in properties is present within the object. 加热有意在物体内产生温度梯度，从而在冷却后，在物体内出现所需的应力分布或特性变化。 |
| Rotor | 转子 |
A part of a machine that rotates on a shaft (rotor shaft) about its own axis, such as the blade-carrying discs of a turbine, the blades of a helicopter, or the rotating parts of a Roots blower. 绕轴（转子轴）绕其自身轴线旋转的机器部件，如涡轮叶片、直升机叶片或罗茨鼓风机的旋转部件。 |
| Zirconia-toughened alumina composites | 氧化锆增韧氧化铝复合材料 |
(ZTA composites) Ceramic composites based on aluminium oxide to which zirconium oxide is added, resulting in improved fracture toughness. （ZTA复合材料）基于氧化铝的陶瓷复合材料，其中添加了氧化锆，从而提高了断裂韧性。 |
| Compression wave | 压缩波 |
(dilatation wave) In a fluid or a solid, a progressive wave or wavefront that compresses the medium through which it propagates. （膨胀波）在流体或固体中，压缩介质传播的行波或波前。 |
| Atmosphere | 大气 |
1. (atm) An obsolete (non-SI) unit of pressure equal to 101 325 Pa or 1.013 25 bar and approximately equal to the atmospheric pressure (barometric pressure) measured at mean sea level. 1.（atm）一种已被淘汰的（非SI）压力单位，等于101325Pa或1.01325bar，大约等于在平均海平面测量的大气压力（大气压）。 |
| Turbine flow meter | 涡轮流量计 |
(axial flow meter, propeller meter) An in-line flow meter in which the rotation speed N of a propeller or rotor is a measure of the mass flowrate ṁ. Calibration is always necessary but with appropriate design ṁ is closely proportional to N over a wide range. （轴向流量计、螺旋桨流量计）一种串联流量计，其中螺旋桨或转子的转速N是质量流量的测量值ṁ. 校准总是必要的，但需要适当的设计ṁ在很宽的范围内与N成正比。 |
| Variance | 方差 |
A measure of the squared dispersion of observed values or measurements expressed as a function of the sum of the squared deviations from the population mean or sample average. 观测值或测量值的平方离散度的度量，表示为总体平均值或样本平均值的平方偏差之和的函数。 |
| Relative density | 相对密度 |
(specific gravity) The ratio of the density of a substance to that of a reference substance, such as water for liquids and solids, and dry air for gases. （比重）物质密度与参考物质密度之比，如液体和固体为水，气体为干燥空气。 |
| Sliding-vane compressor | 滑片压缩机 |
(rotary-vane compressor, vane compressor) A rotary compressor in which gas is compressed as the spaces between spring-loaded sliding vanes held in an offset rotor reduce as the rotor revolves within a cylindrical housing. （旋转叶片压缩机，叶片压缩机）一种旋转式压缩机，当转子在圆柱形外壳内旋转时，偏置转子中的弹簧加载滑动叶片之间的空间减小，从而压缩气体。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Engineering strain (e) | 工程应变（e） |
A term sometimes used for average linear strain or conventional strain in order to differentiate it from true strain. In tension testing it is calculated by dividing the change in the gage length by the original gage length. 一个术语，有时用于平均线性应变或常规应变，以便将其与真实应变区分开来。在张力测试中，通过将标距变化除以原始标距来计算。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Bearing test | 轴承测试 |
A method of determining the response to stress (load) of metal products that are subjected to riveting, bolting, or a similar fastening procedure. The purpose of the test is to determine the bearing strength of the material and to measure the bearing stress versus the deformation of the hole created by a pin or rod of circular cross section that pierces the sheet perpendicular to the surface. 一种确定经受铆接、螺栓连接或类似紧固程序的金属产品对应力（载荷）的响应的方法。测试的目的是确定材料的承载强度，并测量承载应力与由垂直于表面刺穿板材的圆形横截面的销或杆产生的孔的变形。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Sharp-notch strength | 锐缺口强度 |
The notch tensile strength measured using specimens with very small notch root radii (approaching the limit for machining capability); values of sharp-notch strength usually depend on notch root radius. 使用缺口根部半径非常小（接近加工能力极限）的试样测量的缺口抗拉强度；锐缺口强度值通常取决于缺口根部半径。 |
| Coherent precipitate | 相干沉淀 |
A crystalline precipitate that forms from solid solution with an orientation that maintains continuity between the crystal lattice of the precipitate and the lattice of the matrix, usually accompanied by some strain in both lattices. Because the lattices fit at the interface between precipitate and matrix, there is no discernible phase boundary. 由固溶体形成的结晶沉淀物，其取向保持沉淀物晶格和基体晶格之间的连续性，通常伴随着两个晶格中的一些应变。由于晶格适合于沉淀和基体之间的界面，因此不存在可识别的相边界。 |
| Size effect | 尺寸效应 |
Effect of the dimensions of a piece of metal on its mechanical and other properties and on manufacturing variables such as forging reduction and heat treatment. In general, the mechanical properties are lower for a larger size. 金属件的尺寸对其机械和其他性能以及对制造变量（如锻造、压下和热处理）的影响。一般来说，尺寸越大，机械性能越低。 |
| Mechanical alloying | 机械合金化 |
Production of alloys from powders by consolidation, e.g. hotpressing or extrusion, followed by hot and/or cold working and final annealing. Materials such as dispersion-strengthened alloys, high-temperature aluminium alloys, and amorphous alloys can be made in this way. 通过固结（例如热压或挤压）从粉末生产合金，然后进行热和/或冷加工和最终退火。用这种方法可以制造弥散强化合金、高温铝合金和非晶合金等材料。 |
| Shank | 螺杆 |
Portion of a bolt which lies under the head. 1. The stem of a tool, such as a broach, drill bit, reamer, or tap, which fits into a holder such as a chuck. 2. The stem of a rivet or the unthreaded part of a screw or bolt. 3. The shaft of a tool connecting the tip and the handle. 螺栓头部下方的部分。1.一种工具的柄部，如拉刀、钻头、铰刀或丝锥，可装入夹具（如卡盘）中。铆钉的杆或螺钉或螺栓的无螺纹部分。3.连接尖端和手柄的工具的轴。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Mole number (N) | 摩尔数（N） |
The number of moles in a given mass m of a substance, equal to m divided by the molar mass of the substance. 摩尔数物质给定质量m中的摩尔数，等于m除以物质的摩尔质量。 |
| Terminal temperature difference (Unit K) | 终端温差（单位K） |
The temperature difference between the two fluid streams at either inlet or outlet of a heat exchanger. 热交换器入口或出口处两种流体流之间的温差。 |
| Fastener manufacturer | 紧固件制造商 |
An organization that fabricates raw steel into a fastener meeting specified standards. 将生钢加工成符合规定标准的紧固件的组织。 |
| Verified loading range | 验证加载范围 |
For testing machines, the range of indicated loads for which the testing machine gives results within the permissible variation specified. 对于试验机，试验机在规定允许偏差范围内给出结果的指示载荷范围。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Left hand screw | 左螺旋 |
One that screws into the mating part or advances when turned to the left or counter clockwise. 旋入配合部分或向左或逆时针旋转时前进的螺钉。 |
| Tensile test (tension test) | 拉伸试验（拉力试验） |
A test in which a precisely-machined tensile specimen (tensile testpiece), typically circular or rectangular in cross section with large end sections that are gripped in the testing machine, is subjected to an increasing tensile load, usually to the point of fracture, to produce a stress–strain curve from which such material properties as modulus of elasticity, limit of proportionality, proof stress, yield point, and ultimate tensile stress can be determined. The relevant standard is ISO 6892-1. 一种试验，在这种试验中，精密加工的拉伸试样（拉伸试件）的横截面通常为圆形或矩形，具有在试验机中夹紧的大端部，受到越来越大的拉伸载荷，通常达到断裂点，以产生应力-应变曲线，从中可以看出弹性模量、比例极限等材料特性，可以确定验证应力、屈服点和极限拉伸应力。相关标准为ISO 6892-1。 |
| Eccentric load | 偏心载荷 |
The external load on a fastener or groups of fasteners is said to be eccentric if the resultant of that load does not pass through the centroid of the group of fasteners (eccentric shear load ) or does not coincide with the bolt axis (eccentric tensile load ). 如果一个或多个紧固件上的外部载荷的合力未穿过紧固件组的质心（偏心剪切载荷）或与螺栓轴不重合（偏心拉伸载荷），则称该外部载荷为偏心。 |
| Acceleration due to gravity | 重力加速度 |
(acceleration of free fall, gravitational acceleration, g) (Unit m/s²) The acceleration of a freely-falling body in a vacuum, with a mean value at sea level of approximately 9.81 m/s². （自由落体加速度，重力加速度，g）（单位m/s²）自由落体在真空中的加速度，在海平面处的平均值约为9.81m/s²。 |
| Tangential load (Unit N) | 切向荷载（单位：N） |
The component of load applied to an object, such as a gear, that tends to cause or resist rotation. 旋转力施加在物体上的载荷分量，如齿轮，倾向于引起或阻止旋转。 |
| Tension testing | 张力测试 |
A method of determining the behavior of materials subjected to uniaxial loading, which tends to stretch the metal. A longitudinal specimen of known length and diameter is gripped at both ends and stretched at a slow, controlled rate until rupture occurs. Also known as tensile testing. 一种确定材料在单轴载荷下的行为的方法，这种载荷倾向于拉伸金属。将已知长度和直径的纵向试样夹持在两端，并以缓慢、受控的速率拉伸，直到发生断裂。也称为拉伸测试。 |
| Serrations | 锯齿 |
A row of notches or tooth-like projections on an edge or surface. On an engineering drawing, serrations on the surface of a circular component are shown over about 60° of arc. 边缘或表面上的一排凹口或齿状突起。在工程图纸上，圆形部件表面的锯齿超过约60°的圆弧。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Cooling stresses | 冷却应力 |
Residual stresses resulting from nonuniform distribution of temperature during cooling. 冷却过程中温度分布不均匀导致的残余应力。 |
| Stress-intensity factor | 应力强度因子 |
A scaling factor, usually denoted by the symbol K, used in linear-elastic fracture mechanics to describe the intensification of applied stress at the tip of a crack of known size and shape. At the onset of rapid crack propagation in any structure containing a crack, the factor is called the critical stress-intensity factor, or the fracture toughness. 一种标度因子，通常用符号K表示，在线弹性断裂力学中用于描述已知尺寸和形状的裂纹尖端施加应力的增强。在任何含有裂纹的结构中，裂纹快速扩展开始时，该因子称为临界应力强度因子，或断裂韧性。 |
| Wind tunnel | 风洞 |
A duct in which a controlled flow of air is used for testing and research. Types include blow down, closed circuit, open return, and open section. Closed-circuit tunnels may be pressurized or evacuated. The working section is usually situated immediately downstream of the flow-conditioning elements, which may include a plenum chamber, honeycomb, screens, turbulence grids, and a contraction. Immediately downstream there is usually a diffuser. For basic research the usual requirement is for uniform steady flow in the working section with low swirl and turbulence intensity. For some applications the flow may be density stratified, sheared, unsteady, or of high turbulence intensity. 用于测试和研究的可控气流管道。类型包括排污、闭路、开路回路和开路段。闭路隧道可加压或排空。工作段通常位于流量调节元件的下游，可包括增压室、蜂窝、滤网、湍流格栅和收缩管。紧靠下游通常有一个扩散器。对于基础研究，通常的要求是在低涡流和湍流强度的工作段中实现均匀稳定流动。对于某些应用，流动可能是密度分层、剪切、不稳定或高湍流强度。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Fastener with waisted shank | 带腰柄的紧固件 |
Finished fastener with a shank diameter of ds < d2. 柄径ds |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Bar | 巴（气压单位） |
A widely used (non-SI) unit of pressure approximately equal to normal atmospheric pressure at sea level. The conversion to SI is 1 bar = 105 Pa. Unit of pressure – the pressure created by a column of€mercury 75.006 cm high at 0ºC, or about 33.45 feet of water at 4ºC. It is equal to 105 pascal. Standard atmospheric pressure (at sea level) is 1.01325 bar, or 1013.25 mb. 一种广泛使用的（非SI）压力单位，大约等于海平面上的正常大气压。转换为SI为1bar=105Pa。压力单位——0ºC时75.006厘米高的水银柱或4ºC时约33.45英尺水柱产生的压力。它等于105帕斯卡。标准大气压（海平面）为1.01325bar或1013.25mb。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Mechanical properties of solid materials | 固体材料的力学性能 |
The strength and stiffness properties of solid materials such as fracture toughness, the moduli of elasticity, percent elongation, 固体材料的强度和刚度特性，例如断裂韧性、弹性模量、伸长率、 |
| Wedge | 楔子 |
A short triangular prism whose major surfaces subtend an acute angle, that can be driven between two objects or parts of an object to split, tighten, or secure them, or to widen an opening or raise a heavy object. The acute angle gives a high mechanical advantage. 一种短的三棱镜，其主面对着一个锐角，可在两个物体或物体的一部分之间驱动，以将它们分开、拧紧或固定，或加宽开口或举起重物。锐角具有很高的机械优势。 |
| Radiation pressure (Unit μPa) | 辐射压力（单位：μPa） |
The pressure exerted on a surface exposed to any form of electromagnetic radiation. If the radiation is absorbed, it is equal to the power-flux density divided by the speed of light. 施加在暴露于任何形式电磁辐射的表面上的压力。如果辐射被吸收，它等于功率通量密度除以光速。 |
| Shear test | 剪切试验 |
Any of several tests to obtain shear strength of a metal. Common tests used on mill products include the double-shear test, single-shear test, the blanking shear test (also known as the punching shear test) and the torsion test. 获得金属剪切强度的几种测试中的任何一种。轧机产品上常用的试验包括双剪试验、单剪试验、落料剪切试验（也称为冲切试验）和扭转试验。 |
| Condenser vacuum | 冷凝器真空 |
The sub-atmospheric pressure imposed on the condenser of a steam-power plant which leads to an appreciable increase in overall efficiency. 施加在蒸汽发电厂冷凝器上的低于大气压的压力导致整体效率显着提高。 |
| Angle of thread | 螺纹角度 |
The included angle between the sides forming the groove of the screw thread. 形成螺纹凹槽的边之间的夹角。 |
| Gibbs–Dalton law | 吉布斯-道尔顿定律 |
An extension of Dalton’s law of additive pressures to include the statement that the internal energy, enthalpy, and entropy of a mixture of gases are equal to the sum of the internal energies, enthalpies, and entropies the individual constituents would have if each existed alone at the same temperature and volume. Gibbs rule is that part of the law pertaining to entropy. 道尔顿附加压力定律的扩展，包括以下陈述：气体混合物的内能、焓和熵等于各个成分单独存在时的内能、焓和熵之和。相同的温度和体积。吉布斯定律是与熵有关的定律的一部分。 |
| Shear modulus (G) | 剪切模量（G） |
The ratio of shear stress to the corresponding shear strain for shear stresses below the proportional limit of the material. Values of shear modulus are usually determined by torsion testing. Also known as modulus of rigidity. 对于低于材料比例极限的剪切应力，剪切应力与相应剪切应变之比。剪切模量值通常通过扭转试验确定。也称为刚度模量。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Achme thread | Achme螺纹 |
A screw thread having an included angle of 29° and largely used for feed screws on machine tools. 一种夹角为29°的螺纹，主要用于机床上的进给丝杠。 |
| Tangent screw | 微动螺旋 |
A worm screw used to adjust measuring instruments such as sextants and vernier callipers. 用于调整六分仪和游标卡尺等测量仪器的蜗杆。 |
| Resistance factor | 阻力系数 |
Probabilistic factor representing the uncertainties in the designer’s estimate of the strength of a shear joint. Used in Load and resistance factor design. 概率系数，表示设计人员对剪切接头强度估计的不确定性。用于载荷和阻力系数设计。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Active vibration suppression | 主动振动抑制 |
The reduction of undesirable vibration in components by feedback control. 通过反馈控制减少部件中的不良振动。 |
| Constant-mesh gearbox | 恒啮合齿轮箱 |
A gearbox in which the pairs of gears giving different speed ratios are constantly in mesh, different ratios being obtained by connecting or disconnecting the relevant gear to the driving shaft. 一种齿轮箱，其中提供不同速比的齿轮对始终啮合，通过将相关齿轮连接或断开驱动轴获得不同的速比。 |
| Clevis joint | U形接头 |
A joint formed by two parallel cantilever beams pressed upon a component between the beams. 由两个平行悬臂梁压在梁之间的部件上形成的接头。 |
| Thermodynamic state | 热力学状态 |
The condition of a system or working fluid according to its properties. 系统或工作流体根据其性质的状态。 |
| Mechanical energy (Unit J) | 机械能（单位J） |
The sum of kinetic energy and potential energy for an object or a mechanical system, including the energy stored in springs, etc. 物体或机械系统的动能和势能之和，包括储存在弹簧等中的能量。 |
| Double-shear test | 双剪试验 |
A shear test having two stationary, shear blades and one moving one and that uses solid round bars as test specimens. 一种剪切试验，具有两个固定的剪切刀片和一个移动的刀片，并使用实心圆棒作为试样。 |
| Fibreglass | 玻璃纤维 |
Fibreglass is used in studs and nuts for applications when the fastener should be non-corrosive, low in conductivity, or transparent to electromagnetic waves. 当紧固件应无腐蚀性、低导电性或对电磁波透明时，玻璃纤维用于螺柱和螺母中。 |
| Vector | 矢量 |
Any physical quantity, such as velocity, acceleration, force, or momentum, that is specified in terms of both its magnitude and its direction. The convention of printing vector quantities in boldface was introduced by the physicist Josiah Willard Gibbs. 任何物理量，如速度、加速度、力或动量，以其大小和方向来表示。用黑体印刷矢量量的惯例是由物理学家约西亚·威拉德·吉布斯提出的。 |
| Twist | 扭转 |
The helix produced in a cylindrical component, such as a shaft, wire, tensioned cable, or rope, when one end is rotated relative to the other. Measured either as the number of turns per unit length, or by the helix angle (twist angle). 当一端相对于另一端旋转时，在圆柱形部件（如轴、钢丝、张紧电缆或绳索）中产生的螺旋。以每单位长度的圈数或螺旋角（扭曲角）测量。 |
| Machine screw | 机械螺丝 |
A countersunk, slotted screw with machined threads such as are found on bolts. A relatively small screw, usually less than 20 mm in diameter, with the thread running along the whole length up to the head, intended to be screwed into threaded holes. If inserted through plain holes in assembled parts and held together by a nut, an undesirable contact surface of threads bearing against the surface of a hole results. 带有机加工螺纹的沉头开槽螺钉，如螺栓上的螺纹。一种相对较小的螺钉，直径通常小于20毫米，螺纹沿整个长度一直延伸到头部，用于拧入螺纹孔中。如果通过装配零件上的平孔插入并用螺母固定在一起，则会导致螺纹与孔表面接触不良。 |
| Austenite finish temperature (Af) | 奥氏体完成温度（Af） |
Temperature at which the transformation of martensite into austenite completes upon heating. The same designation is also applied to nonferrous alloys in which martensite transforms into some parent phase. 加热时马氏体转变为奥氏体的温度。相同的名称也适用于马氏体转变为某些母相的有色合金。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| Chilled castings | 冷铸件 |
Iron castings cooled at a rate that results in white iron (slow enough to avoid the formation of martensite, yet fast enough to prevent any silicon present from causing decomposition of cementite into iron and graphite). 铸铁件以产生白口铁的速度冷却（足够慢以避免形成马氏体，但足够快以防止任何存在的硅导致渗碳体分解成铁和石墨）。 |
| Balancing machine | 平衡机 |
A device that assesses the state of static and dynamic balance of a rotating part, and indicates the magnitude and location of weights to be added to give balance. 一种装置，用于评估旋转部件的静态和动态平衡状态，并指示为获得平衡而添加的砝码的大小和位置。 |
| Load | 负载 |
For testing machines, a force applied to a test piece that is measured in units such as pound-force, newton, or kilogram-force. 对于试验机，施加在试件上的力，以磅力、牛顿或千克力等单位测量。 |
| Clearance hole | 间隙孔 |
A hole of specified size such that a bolt, stud, etc. of the same nominal size will always pass through. 指定尺寸的孔，使相同标称尺寸的螺栓、螺柱等可以通过。 |
| Fatigue notch factor (Kf) | 疲劳缺口系数（Kf） |
The ratio of the fatigue strength of an unnotched specimen to the fatigue strength of a notched specimen of the same material and condition; both strengths are determined at the same number of stress cycles. 无缺口试样的疲劳强度与相同材料和条件的有缺口试样的疲劳强度之比；两种强度都是在相同数量的应力循环下确定的。 |
| Eutectic | 共晶 |
(1) An isothermal reversible reaction in which a liquid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectic point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectic reaction. （1）一种等温可逆反应，其中液体溶液在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）一种合金，其成分由平衡图上的共晶点表示。（3）由共晶反应形成的混合固体成分的合金结构。 |
| Crack-extension resistance (KR) | 抗裂扩展性（KR） |
A measure of the resistance of a material to crack extension, expressed in terms of the stress-intensity factor, the crack-extension force, or values of Jderived using the J-integral concept. 材料对裂纹扩展的抵抗力的量度，以应力强度因子、裂纹扩展力或使用J积分概念导出的J值表示。 |
| Engine emissions | 发动机排放 |
(exhaust emissions) The pollutants contained in the exhaust gases from an internal-combustion engine. （废气排放）内燃机废气中所含的污染物。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Notch ductility | 缺口延展性 |
The percentage reduction in area after complete separation of the metal in a tensile test of a notched specimen. 在缺口试样的拉伸试验中，金属完全分离后的面积减少百分比。 |
| Normality | 常态 |
The principle that the vector sum of plastic strain increments is perpendicular to the yield surface. 塑性应变增量矢量和垂直于屈服面的原理。 |
| Contact strength (Unit N) | 接触强度（单位N） |
The maximum allowable load between contacting bodies converted into a stress. 换算成应力的接触体之间的最大允许载荷。 |
| Sample standard deviation (s) | 样本标准偏差（s） |
The square root of the sample variance. It is a point estimate of the population standard deviation, a measure of the “spread”of the frequency distribution of a population. This value of sprovides a statistic that is used in computing interval estimates and several test statistics. For small sample sizes, s underestimates the population standard deviation. 样本方差的平方根。它是总体标准偏差的点估计，是总体频率分布“扩散”的度量。SPR的这个值提供了一个用于计算区间估计和若干测试统计量的统计量。对于小样本，s低估了总体标准偏差。 |
| Strength of bolt | 螺栓强度 |
An ambiguous term which can mean Ultimate strength or Proof load or Endurance limit or Yield strength. 一个模棱两可的术语，可表示极限强度或验证荷载或耐久极限或屈服强度。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| Track rod | 横拉杆 |
A bar connecting the ends of the steering arms in an automotive vehicle. 连接汽车转向臂端部的杆。 |
| O-ring (O-ring seal) | O形圈（O形密封圈） |
A toroidal ring of synthetic rubber seated in a groove machined into a flat or cylindrical surface to act as a seal. 一种环形合成橡胶环，位于加工成平面或圆柱表面的凹槽中，起密封作用。 |
| Elastic limit | 弹性极限 |
The maximum stress which a material is capable of sustaining without any permanent strain (deformation) remaining on complete release of the stress. 材料在完全释放应力时能够承受的最大应力，且不会留下任何永久应变（变形）。 |
| Stainless steels | 不锈钢 |
Iron-base alloys that are highly resistant to corrosion in many environments. The predominant alloying element is chromium, which, like iron at room temperature, has BCC crystal structure. Corrosion resistance by passivation is achieved by the formation of chromium oxide on the steel surface. Nickel, which has FCC crystal structure, is another important addition for some steels. Other additions used to enhance properties include manganese, molybdenum, niobium, and titanium. There are several classes of stainless steel. 在许多环境中具有高度耐腐蚀性的铁基合金。主要的合金元素是铬，与室温下的铁一样，铬具有BCC晶体结构。钝化抗腐蚀性是通过在钢表面形成氧化铬来实现的。具有FCC晶体结构的镍是某些钢的另一种重要添加剂。其他用于增强性能的添加剂包括锰、钼、铌和钛。不锈钢的种类有好几种。 |
| Air classifier | 空气分级机 |
(air elutriator) A device in which an airstream, which may be swirling, sorts particles by a combination of size, shape, and mass. （空气淘析器）一种装置，在该装置中，气流（可能是漩涡）根据大小、形状和质量的组合对颗粒进行分类。 |
| Equilibrium diagram | 平衡图 |
A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant. 在完全平衡条件下，合金系统中相场的温度、压力和成分极限的图形表示。在金属系统中，压力通常被认为是恒定的。 |
| Dynamic hardness | 动态硬度 |
(rebound hardness) The resistance of a material to local indentation by a rapidly-moving rigid indenter. In most practical methods the indenter is allowed to fall under gravity on to the surface of the material when the rebound height is a measure of the dynamic hardness. （回弹硬度）材料对快速移动的刚性压头局部压痕的阻力。在大多数实际方法中，当回弹高度是动态硬度的测量值时，允许压头在重力作用下落在材料表面上。 |
| Stress cracking | 应力开裂 |
A family of failure modes, each of which involves high stress and chemical action. The family includes Hydrogen embrittlement, Stress corrosion cracking, stress embrittlement, and hydrogen-assisted stress corrosion. 一系列失效模式，每种模式都涉及高应力和化学作用。该系列包括氢脆、应力腐蚀开裂、应力脆化和氢辅助应力腐蚀。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Q-factor | 品质因素 |
(quality factor, sharpness of resonance) A non-dimensional parameter that describes, for a given resonant mode, the sharpness of the peak in the frequency response of a lightly-damped linear oscillator: Q = ωRES/Δω where ωRES is the resonance frequency and Δω is the half-power bandwidth of the resonance. It is inversely related to the damping such that a broad peak corresponds to high damping and a narrow peak to low damping. （品质因数，共振尖锐度）一个无量纲参数，用于描述给定共振模式下，轻阻尼线性振荡器频率响应峰值的尖锐度：Q=ωRES/Δω，其中ωRES是共振频率，Δω是共振的半功率带宽。它与阻尼成反比，因此宽峰值对应于高阻尼，窄峰值对应于低阻尼。 |
| Metric ton (tonne, t) | 公制吨（吨，t） |
An SI-accepted, but non-SI, unit of mass defined as 1 t = 103 kg. SI系统可接受但非国际单位制的质量单位，定义为1t=103kg。 |
| DIN | DIN |
Deutsches Institut für Normung, the German Institute for Standardization. Deutsches Institut für Normung，德国标准化研究所。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Corrosion cell | 腐蚀电池 |
A natural ‘‘battery’’ formed when two metals having different electrical potentials (an Anode and a Cathode) are connected together in the presence of a liquid (the Electrolyte). 当两种具有不同电势的金属（阳极和阴极）在液体（电解质）存在下连接在一起时形成的天然“电池”。 |
| Coining | 压印 |
A forging operation, employing a closely-fitting punch and die from which no metal is allowed to escape, in which the surface pattern on the punch and die is imprinted on the blank. 一种锻造操作，采用紧密配合的凸模和模具，不允许金属逸出，其中凸模和模具上的表面图案印在坯料上。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| J-integral | J-积分 |
A mathematical expression describing a line or surface integral that encloses the crack front from one crack surface to the other, used to characterize the fracture toughness of a material having appreciable plasticity before fracture. The J-integral eliminates the need to describe the behavior of the material near the crack tip by considering the local stress-strain field around the crack front; JIc is the critical value of the J-integral required to initiate crack extension from a preexisting crack. 描述从一个裂纹表面到另一个裂纹正面的线或表面积分的数学表达式，用于表征断裂前具有可观塑性的材料的断裂韧性。J积分通过考虑裂纹前缘周围的局部应力应变场，无需描述裂纹尖端附近材料的行为；JIc是从先前存在的裂纹开始裂纹扩展所需的J积分的临界值。 |
| Linear-elastic fracture mechanics | 线弹性断裂力学 |
A method of fracture analysis that can determine the stress (or load) required to induce fracture instability in a structure containing a cracklike flaw of known size and shape. 一种断裂分析方法，可确定在含有已知尺寸和形状裂纹状缺陷的结构中引起断裂不稳定性所需的应力（或载荷）。 |
| Destructive testing | 破坏性测试 |
Measurement of the mechanical properties of a material, component, or structure, by increased loading until the sample fails by fracture, collapse, or buckling. 通过增加载荷测量材料、部件或结构的机械性能，直到样品因断裂、塌陷或屈曲而失效。 |
| Clearance volume | 余隙容积 |
(Unit m³) The ‘dead’ volume above a piston, including the recess in the cylinder head, in a reciprocating compressor or engine when the piston is at top dead centre. （单位m³）活塞位于上止点时活塞上方的“死区”体积，包括气缸盖中的凹槽，在往复式压缩机或发动机中。 |
| Welding | 焊接 |
In tribology, the bonding between metallic surfaces in direct contact, at any temperature. A joining process in which the mating surfaces are at least softened, or more usually melted, unlike soldering and brazing. In solid-state (non-melting) welding, similar or dissimilar metals or thermoplastics may be joined by applying pressure to hot interfaces. In forge welding, joining is achieved by compression across the join between pre-heated workpieces. In friction welding (spin welding) one of the contacting surfaces is rotated rapidly before being loaded against the other. On contact, heat generated by friction softens the materials and permits severe plastic deformation that seals the joint. In friction stir welding, a wear-resistant tool is rotated rapidly, indents the surfaces and is traversed to form a join line. Resistance welding involves simultaneous pressure and electrically-generated heat, as in spot welding where a heavy electric current is passed for a short time through metal sheets which are pressed together between electrodes. 在摩擦学中，在任何温度下直接接触的金属表面之间的结合。与钎焊和钎焊不同，接合面至少软化或更通常熔化的接合工艺。在固态（非熔化）焊接中，相似或不同的金属或热塑性塑料可通过向热界面施加压力来连接。在锻造焊接中，通过压缩预热工件之间的连接来实现连接。在摩擦焊接（旋转焊接）中，一个接触表面在被加载到另一个表面之前快速旋转。接触时，摩擦产生的热量使材料软化，并允许密封接头的严重塑性变形。在搅拌摩擦焊中，耐磨工具快速旋转，使表面凹陷，并横穿形成连接线。电阻焊涉及同时产生的压力和电产生的热量，如点焊，在点焊中，大电流短时间通过电极之间压在一起的金属板。 |
| Breaking load | 断裂载荷 |
The maximum load (or force) applied to a test specimen or structural member loaded to rupture. 施加到加载到破裂的试样或结构构件上的最大载荷（或力）。 |
| Damage | 损伤 |
1. The deterioration of a component or structure in fault or accident conditions, reducing or preventing its ability to perform its intended function. 2. The accumulation of defects or microcracks in the microstructure of a body loaded monotonically or in fatigue, which weakens the body and can lead to crack propagation and failure. 1.部件或结构在故障或事故条件下的劣化，降低或阻止其执行预期功能的能力。2.在承受单调载荷或疲劳载荷的物体的微观结构中累积的缺陷或微裂纹，这会削弱物体，并可能导致裂纹扩展和失效。 |
| Joule | 焦耳 |
The SI unit of energy. One joule is the work done by a force of one newton acting over a distance of one metre. The symbol is J, where 1 J = 1 N m. 国际单位制能量单位。一焦耳是一牛顿的力在一米的距离上所做的功。符号为J，其中1j=1m。 |
| Archimedes screw | 阿基米德螺旋泵 |
A machine which comprises a rotating helical blade inside a closefitting tube, which may be used to pump liquids, slurries (such as sewage), granular materials, etc. If water flows into the top of an inclined or vertical Archimedes screw, the screw will rotate and can be used to drive an electrical generator. 一种机器，它在紧密的管子内包含一个旋转的螺旋叶片，可用于泵送液体、泥浆（如污水）、颗粒材料等。如果水流入倾斜或垂直的阿基米德螺杆的顶部，螺杆将旋转，可用于驱动发电机。 |
| Castellated nut | 槽形螺母 |
A nut having slots across the hexagonal faces, used with a bolt having a drilled hole so that a split (cotter) pin may be inserted through both nut and bolt to prevent unscrewing. 一种在六角面上有槽的螺母，与具有钻孔的螺栓一起使用，以便将开口（开口）销插入穿过螺母和螺栓以防止拧松。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Congruent transformation | 全等变换 |
An isothermal or isobaric phase change in which both of the phases concerned have the same composition throughout the process. 等温或等压相变，其中相关的两个相在整个过程中具有相同的成分。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Profile | 轮廓 |
The shape of a cross section of an object, such as an aerofoil or cam. 物体的横截面形状，如机翼或凸轮。 |
| Collapse load (Unit N) | 毁坏荷载（单位N） |
The applied load at which a structure becomes a mechanism owing to the formation of sufficient plastic hinges for collapse to occur. 由于形成足够的塑性铰链以发生坍塌，结构成为机制的施加载荷。 |
| Rosette | 玫瑰形的结 |
Strain gages arranged to indicate, at a single position, strain in three different directions. 应变计布置成在单个位置指示三个不同方向的应变。 |
| Carbon potential | 碳势 |
A measure of the ability of an environment containing active carbon to alter or maintain, under prescribed conditions, the carbon level of the steel. Note: In any particular environment, the carbon level attained will depend on such factors as temperature, time, and steel composition. 衡量含有活性碳的环境在规定条件下改变或保持钢的碳含量的能力。注意：在任何特定环境中，所达到的碳含量将取决于温度、时间和钢成分等因素。 |
| Toggle (toggle clamp) | 拨动（拨动夹） |
A device consisting of two pinned levers that are almost in line between two end points in the same plane. Bringing the levers into line generates large forces between the ends. Used to obtain a large mechanical advantage or as a locking mechanism. 由两个销杆组成的装置，在同一平面的两个端点之间几乎成一条直线。将杠杆对齐会在端部之间产生较大的力。用于获得较大的机械优势或用作锁定机构。 |
| Fatigue test | 疲劳测试 |
A method for determining the range of alternating (fluctuating)stresses a material can withstand without failing. 一种确定材料可以承受而不会失效的交变（波动）应力范围的方法。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Coefficient of friction (μ) | 摩擦系数（μ） |
(coefficient of kinetic friction, coefficient of sliding friction, friction coefficient, μ) The ratio of the frictional force F to the normal force N between two surfaces in contact, i.e. μ = F/N. Static friction is when there is no relative sliding; kinetic friction when there is. For structural components sliding on one another, the coefficient of friction is the ratio of the force causing the sliding to the force perpendicular to the sliding component surfaces. The coefficient of friction is dimensionless with values between zero and one. The number characterising the force necessary to slide or roll one material along the€surface of another. If an object has a weight N and the coefficient of friction is μ, then the force F necessary to move it without acceleration along a level surface is F = μN. The coefficient of static friction determines the force necessary to initiate movement; the coefficient of kinetic friction determines the force necessary to maintain movement. Kinetic friction is usually smaller than static friction. （动摩擦系数、滑动摩擦系数、摩擦系数，μ）两个接触表面之间摩擦力F与法向力N的比值，即μ=F/N。静摩擦是指没有相对滑动时；有摩擦时的动摩擦。对于相互滑动的结构部件，摩擦系数是引起滑动的力与垂直于滑动部件表面的力的比值。摩擦系数是无量纲的，其值介于0和1之间。代表一种材料沿另一种材料的表面滑动或滚动所需的力的数字。如果一个物体的重量为N并且摩擦系数为μ，那么在没有加速度的情况下沿水平表面移动它所需的力F为F=μN。静摩擦系数决定了启动运动所需的力；动摩擦系数决定了保持运动所需的力。动摩擦通常小于静摩擦。两个物体之间的力（F）与将这些物体压在一起的法向力（N）的无量纲比：μ（或f）=（F/N）。 |
| Pressure-relief valve | 减压阀 |
A valve that limits the maximum pressure in a pressure vessel or fluid-power system to a specified level. 将压力容器或流体动力系统中的最大压力限制在规定水平的阀门。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Belt furnace | 带式炉 |
A continuous-type furnace which uses a mesh-type or cast-link belt to carry parts through the furnace. 一种连续式炉，它使用网状或铸造链带将零件运送通过炉子。 |
| Ultrasonic extensometer | 超声波伸长计 |
An electronic instrument which measures the change in length of a fastener ultrasonically as, or before and after, the fastener is tightened. 一种电子仪器，可在紧固件拧紧时或前后通过超声波测量紧固件长度的变化。 |
| Hydrogen-induced delayed cracking | 氢致延迟开裂 |
A term sometimes used to identify a form of hydrogen embrittlement in which a metal appears to fracture spontaneously under a steady stress less than the yield stress. There is usually a delay between the application of stress (or exposure of the stressed metal to hydrogen) and the onset of cracking. Also referred to as static fatigue. 有时用于识别一种氢脆形式的术语，其中金属在小于屈服应力的稳定应力下似乎会自发断裂。在施加应力（或将受应力金属暴露于氢）与开裂开始之间通常存在延迟。也称为静态疲劳。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Tare weight (Unit N) | 皮重（单位N） |
The weight of an empty container. 空容器的重量。 |
| Cavitation | 空蚀空化 |
The formation of vapour- or gas-filled cavities in a liquid due to reduction of the local pressure, often due to acceleration of the fluid, such as in flow through a convergent nozzle. If there is no dissolved gas in the liquid, vaporous cavitation occurs when the pressure falls below the saturated vapour pressure. If the bubbles are formed due to high temperature, the process is termed boiling. If there is dissolved gas, gaseous cavitation occurs due to pressure reduction, temperature increase, or diffusion (degassing). At the tips of marine propellers and in hydraulic machinery, the collapse of cavitation bubbles can cause noise and vibration and lead to surface damage in the form of pitting. 由于局部压力降低而在液体中形成充满蒸汽或气体的空腔，通常原因是流体的加速，例如收敛喷嘴的流动。如果液体中没有溶解气体，当压力降至饱和蒸汽压力以下时，会发生蒸汽空化。如果气泡是由于高温形成的，则该过程称为沸腾。如果存在溶解气体，则由于压力降低、温度升高或扩散（脱气），会发生气穴。在船用螺旋桨尖端和液压机械中，空化气泡的破裂可能会引起噪音和振动，并导致以点蚀形式出现的表面损坏。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Thermal analysis | 热分析 |
A method for determining transformations in a metal by noting the temperatures at which thermal arrests occur. These arrests are manifested by changes in slope of the plotted or mechanically traced heating and cooling curves. When such data are secured under nearly equilibrium conditions of heating and cooling, the method is commonly used for determining certain critical temperatures required for the construction of equilibrium diagrams. 一种通过记录发生热阻的温度来确定金属转变的方法。这些阻力表现为绘制或机械追踪的加热和冷却曲线斜率的变化。当这些数据在加热和冷却的近似平衡条件下得到保证时，该方法通常用于确定构建平衡图所需的某些临界温度。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Cohesive zone | 凝聚力区 |
In fracture-mechanics modelling and simulation, the region at the crack tip over which an assumed traction (load-displacement) relation has to be overcome to permit initiation and propagation of a crack. 在断裂力学建模和模拟中，必须克服假定的牵引（载荷-位移）关系以允许裂纹萌生和扩展的裂纹尖端区域。 |
| Stress relieving | 应力消除 |
Heating to a suitable temperature, holding long enough to reduce residual stresses, and then cooling slowly enough to minimize the development of new residual stresses. 加热到合适的温度，保持足够长的时间以减少残余应力，然后缓慢冷却以尽量减少新残余应力的产生。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Proof strength (Unit Pa) | 验证强度（单位Pa） |
(proof stress, Rp, Rp,) The yield strength (offset yield strength) at some fixed value of the permanent strain given by the intersection of a line offset from, but parallel to, the elastic loading line and the engineering stress-engineering strain curve. The offset is arbitrary but is usually 0.1, 0.2, or 0.5% permanent strain (the proof strain). Used for materials which do not exhibit a sharply defined yield point. The notation Rp0.2 or Rp0.2 is employed for the 0.2% proof stress. （验证应力，Rp）在永久应变的某个固定值下的屈服强度（偏移屈服强度），由偏离但平行于弹性加载线的线与工程应力-工程应变曲线的交点给出。偏移是任意的，但通常为0.1、0.2或0.5%的永久应变（验证应变）。用于没有明确定义屈服点的材料。对于0.2%的验证应力，采用符号Rp0.2。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Tightness | 紧密度 |
A measure of the mass leak rate from a gasketed joint. 垫圈接头质量泄漏率的测量值。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Scratching | 刮擦 |
In tribology, the mechanical removal or displacement, or both, of material from a surface by the action of abrasive particles or protuberances sliding across the surfaces. 在摩擦学中，通过在表面上滑动的磨粒或突起的作用，材料从表面上的机械移除或移位，或两者兼而有之。 |
| Vice | 老虎钳 |
A workshop tool used to hold a workpiece and consisting of two jaws, one fixed and the other moved by turning a screw. 一种用于夹持工件的车间工具，由两个钳口组成，一个固定，另一个通过转动螺钉移动。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Core | 核心 |
In a ferrous alloy prepared for case hardening, that portion of the alloy that is not part of the case . Typically considered to be the portion that (a) appears light on an etched cross section, (b) has an essentially unaltered chemical composition, or (c) has a hardness, after hardening, less than a specified value. 在为表面硬化而制备的铁合金中，合金中不属于表面的那部分。通常被认为是（a）在蚀刻横截面上看起来很轻，（b）化学成分基本不变，或（c）硬化后硬度低于规定值的那部分。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Creep–time relations | 蠕变时间关系 |
Algebraic or numerical relations between creep strain and time at constant stress. 恒定应力下蠕变应变与时间之间的代数或数值关系。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| True stress (σ) (Unit Pa) | 真应力（σ）（单位Pa） |
The value obtained by dividing the load applied to a member at a given instant by the cross-sectional area over which it acts. Compare with engineering stress. The applied load on a test specimen divided by the current cross-section area over which it acts. σ = s expε where s is the engineering stress given by the applied load divided by the original cross-section area over which it acts, and ε is the true strain. 通过将给定时刻施加在构件上的荷载除以其作用的横截面积而获得的值。与工程应力相比。施加在试样上的荷载除以其作用的当前横截面积。σ=s expε，其中s是由施加荷载除以其作用的原始横截面面积得出的工程应力，ε是真实应变。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Atmometer | 气压计 |
(atmidometer, evaporimeter) An instrument that measures the rate of evaporation of water from a surface into the atmosphere. （湿度计，蒸发计）测量水从表面蒸发到大气中的速率的仪器。 |
| Fin | 翼 |
A thin projecting rib. 一根细长的凸肋。 |
| Water quenching | 水淬 |
A quench in which water is the quenching medium. The major disadvantage of water quenching is its poor efficiency at the beginning or hot stage of the quenching process. 以水为淬火介质的淬火。水淬的主要缺点是在淬火过程的开始或热阶段效率低。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Threaded fastener | 螺纹紧固件 |
Studs, bolts, and screws of all sorts, with associated nuts. One of the most interesting, complex, useful—and frustrating—components yet devised. 各种螺柱、螺栓和螺钉，以及相关的螺母。 |
| Material velocity | 材料速度 |
The velocity of sound in a body (e.g., a bolt). A term used in the ultrasonic measurement of bolt stress or strain. 声音在物体（例如螺栓）中的速度。用于螺栓应力或应变的超声波测量的术语。 |
| Hot-wire analyzer | 热电阻丝型分析仪 |
An electrical atmosphere analysis device that is based on the fact that the electrical resistivity of steel is a linear function of carbon content over a range from 0.05% C to saturation. The device measures the carbon potential of furnace atmospheres (typically). This term is not to be confused with the hot-wire test which measures heat extraction rates. 一种基于以下事实的电气氛分析设备：钢的电阻率是从0.05%C到饱和范围内的碳含量的线性函数。该设备测量炉内气氛的碳势（通常）。不要将此术语与测量热提取率的热线测试相混淆。 |
| Torsional angle (ϕ) | 扭转角（ψ） |
(Unit ° or rad) The angular deflexion between two locations on a straight bar subjected to a torque. （单位为°或rad）受扭矩作用的直杆上两个位置之间的角偏转。 |
| Altitude | 高度 |
(Unit m) Vertical height measured relative to a specified datum such as sea level. （单位m）相对于特定基准（例如海平面）测量的垂直高度。 |
| Transgranular fracture | 穿晶断裂 |
Fracture in crystalline materials where the path of cracking is predominantly across grains. 晶体材料中的断裂，其中裂纹路径主要跨越晶粒。 |
| Precision | 精确 |
The closeness of agreement between the results of individual replicated measurements or tests. The standard deviation of the error of measurement may be used as a measure of “imprecision.” 单个重复测量或测试结果之间的一致性。测量误差的标准偏差可用作“不精确性”的度量 |
| Computed path control | 计算路径控制 |
In CNC or robotics, the use of a control program to determine the required path for the tool or end effector. This required path forms the set points for the motor controllers moving the machine tool or robot. 在CNC或机器人技术中，使用控制程序来确定工具或末端执行器所需的路径。这条所需的路径形成了用于移动机床或机器人的电机控制器的设定点。 |
| Ballonet | 气囊 |
An airbag used in a hybrid airship. Helium gas expels air from the ballonet during ascent. Fans draw air in during descent. 混合动力飞艇中使用的安全气囊。氦气在上升过程中将空气从气囊中排出。风扇在下降过程中吸入空气。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| Case hardening | 表面硬化 |
A generic term covering several processes applicable to steel that change the chemical composition of the surface layer by absorption of carbon, nitrogen, or a mixture of the two and, by diffusion, create a concentration gradient. The processes commonly used are carburizing and quench hardening; cyaniding; nitriding; and carbonitriding. The use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于钢的几种工艺，这些工艺通过吸收碳、氮或二者的混合物改变表层的化学成分，并通过扩散形成浓度梯度。常用的工艺有渗碳和淬火硬化，氰化，氮化以及碳氮共渗。优选使用适用的特定工艺名称。 |
| Kinetic energy | 动能 |
Energy that an object possesses because it is in motion. It is the energy given to an object to set it in motion. On impact, it is converted into other forms of energy such as strain, heat, sound and light. 物体因运动而拥有的能量。它是赋予物体使其运动的能量。撞击时，它被转换成其他形式的能量，如应变、热、声和光。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Shoulder bolt | 轴肩螺栓 |
A bolt for which the unthreaded cylindrical section between the thread and the head is of larger diameter than the threaded section, precisely machined to length and diameter and hardened 一种螺栓，其螺纹和头部之间的无螺纹圆柱段的直径大于螺纹段的直径，精确加工至长度和直径并硬化 |
| Grain growth | 晶粒生长 |
An increase in the average size of the grains in polycrystalline metal, usually as a result of heating at elevated temperature. 多晶金属中晶粒平均尺寸的增加，通常是高温加热的结果。 |
| Pascal’s law | 帕斯卡定律 |
When there is a change in pressure at any point in a confined fluid at rest, there is an equal change at every other point in the fluid volume. 当处于静止状态的受限流体中任何一点的压力发生变化时，流体体积中的每一点的变化都相等。 |
| T-slot | T型槽 |
A recessed or undercut slot made with a special T shaped cutter in the tables of machine tools to receive the square head of a T bolt for clamping workpiece. 在机床工作台上用一种特殊的T形刀具制成的凹槽或底切槽，用于容纳T形螺栓的方头，用于夹紧工件。 |
| Complete decarburization | 完全脱碳 |
Decarburization with sufficient carbon loss to show only clearly defined ferrite grains under metallographic examination. 脱碳，具有足够的碳损失，以在金相检查下仅显示清晰定义的铁素体晶粒。 |
| Curie temperature | 居里温度 |
The temperature of magnetic transformation below which a metal or alloy is ferromagnetic and above which it is paramagnetic. 磁性转变温度，低于此温度金属或合金为铁磁性，高于此温度则为顺磁性。 |
| Stabilizing treatment | 稳定化处理 |
(1) Before finishing to final dimensions, repeatedly heating a ferrous or nonferrous part to or slightly above its normal operating temperature and then cooling to room temperature to ensure dimensional stability in service. (2) Transforming retained austenite in quenched hardenable steels, usually by cold treatment. (3) Heating a solution-treated stabilized grade of austenitic stainless steel to 870 to 900 °C (1600 to 1650 °F) to precipitate all carbon as TiC, NbC, or TaC so that sensitization is avoided on subsequent exposure to elevated temperature. （1）在精加工至最终尺寸之前，反复加热含铁或非铁零件至或略高于其正常工作温度，然后冷却至室温，以确保使用中的尺寸稳定性。（2）在淬火可淬硬钢中转变残余奥氏体，通常通过冷处理。（3）将固溶处理的稳定等级奥氏体不锈钢加热至870至900°C（1600至1650°F），使所有碳沉淀为TiC、NbC或TaC，从而避免在随后暴露于高温时敏化。 |
| Accelerated testing | 加速测试 |
A type of testing, for rates of wear, fatigue, corrosion etc., in which failure times are reduced by employing greater loads, more frequent power cycling, higher vibration levels, higher humidity, higher temperatures, greater potential differences etc. than would be encountered in normal operation. 一种测试类型，用于测试磨损率、疲劳率、腐蚀率等，通过采用比正常运行中更大的负载、更频繁的功率循环、更高的振动水平、更高湿度、更高温度、更大的电位差等，减少故障时间。 |
| Angle of attack (α) | 攻角（α） |
(Unit °) The angle between a reference line on a lifting body and the vector direction of the relative velocity between the body and the fluid through which it is moving. In the case of an aerofoil, turbine, or compressor blade, the usual reference line is the chord line. （单位°）升力体上的参考线与升力体与其运动通过的流体之间的相对速度的矢量方向之间的角度。在机翼、涡轮或压缩机叶片的情况下，通常的参考线是弦线。 |
| Cup washer | 杯形垫圈 |
A dished leather or neoprene washer fitted to the rod end in some piston-style pumps. 在某些活塞式泵中，安装在杆端的碟形皮革或氯丁橡胶垫圈。 |
| Concentration ratio | 浓度比 |
For a concentrating solar collector, the ratio of the projected area of the concentrator facing the solar beam to the actual area of the receiver. 对于聚光太阳能集热器，集中器面向太阳光束的投影面积与接收器的实际面积之比。 |
| Plug | 螺塞 |
1. An object, usually tapered, used to block a hole to prevent fluid from escaping or flowing. 2. The central moveable part of a valve. 3. In the flow of a yield-stress fluid through a pipe or duct, the central region is often assumed to take the form of a plug with uniform axial velocity. 4. In thermoforming, a shaping tool that forces a heated plastic sheet into a female mould. 1.一种物体，通常为锥形，用于堵塞孔以防止流体逸出或流动。2.阀门的中心可移动部分。3.在屈服应力流体通过管道或管道的流动中，中心区域通常假定为具有均匀轴向速度的塞子形式。4.在热成型技术中，一种成型工具，将加热的塑料板压入阴模中。 |
| Total head (hT) (Unit m) | 总水头（hT）（单位：m） |
Total pressure pT expressed in terms of the vertical height of a column of liquid, typically water or mercury, i.e. hT = pT/ρg where g is the acceleration due to gravity and ρ is the liquid density. 总压力pT以液体柱（通常为水或汞）的垂直高度表示，即hT=pT/ρg，其中g为重力加速度，ρ为液体密度。 |
| Radian (rad) | 弧度（rad） |
A coherent derived SI unit defined as the plane angle subtended at the centre of a circle by an arc having a length equal to the radius. Thus 2π radians are equivalent to 360° and 1 rad ≈ 57.3°. 一种相干导出的国际单位制单位，定义为在圆心处被长度等于半径的弧对向的平面角。因此，2π弧度相当于360°和1弧度≈57.3°. |
| Turning | 车削 |
Turning is a machining process for generating external surfaces of revolution by the action of a cutting tool on a rotating workpiece, usually in a lathe. The rotation of a workpiece held against a cutting tool in a lathe to produce components with a circular cross section. 车削是一种机械加工过程，通常在车床上，通过刀具对旋转工件的作用产生旋转外表面。在车床中，工件靠着刀具旋转，以生产具有圆形横截面的部件。 |
| Flange | 法兰 |
Flange refers to a head style for bolts where there is a circular ‘flange’ under the head that acts like a washer to distribute a load. A flange is a projected flat rim or collar. 1. Annular rims at the ends of pipes (flanged pipe) or shafts by which they may be coupled together using bolts that pass through holes in the flanges (flange coupling, flange union), or by toggle clamps around the periphery. 2. An extended rim on a wheel that positions it laterally on a track. Commonly used for railway rolling stock. 3. The top and bottom parts of an I-beam. 法兰是指螺栓的头部样式，其中头部下方有一个圆形“法兰”，其作用类似于垫圈以分配载荷。凸缘是凸出的平轮辋或凸缘。1.管道（法兰管）或轴端部的环形边缘，通过这些边缘，可以使用穿过法兰孔的螺栓（法兰联轴器、法兰接头）或通过周边的肘节夹将管道连接在一起。2.车轮上的延伸轮辋，将其横向定位在轨道上。通常用于铁路车辆。3.工字梁的顶部和底部。 |
| Reproducibility | 再现性 |
A term used to describe test-result variability associated with specifically defined components of variance obtained both from within a single laboratory and between laboratories. 一个术语，用于描述与从单个实验室内和实验室之间获得的具体定义的方差分量相关的测试结果可变性。 |
| Austenite | 奥氏体 |
A solid solution of one or more elements in face-centered cubic iron. Unless otherwise designated (such as nickel austenite), the solute is generally assumed to be carbon. Solid solution of alloying elements and/or carbon in γ-Fe. It is named after British metallurgist W. C. Roberts-Austen. 一种或多种元素在面心立方铁中的固溶体。除非另有说明（如镍奥氏体），溶质通常假定为碳。合金元素和/或碳在γ-Fe中的固溶体。它以英国冶金学家WCRoberts-Austen的名字命名。 |
| Zero time | 零时 |
The time when the given loading or constraint conditions are initially obtained in creep or stressrelaxation tests, respectively. 分别在蠕变或应力松弛试验中初始获得给定载荷或约束条件的时间。 |
| Maximum allowable operating pressure (Unit Pa) | 最大允许使用压力（单位Pa） |
The highest pressure at which any pressure system may be operated, usually 10 to 20% below the maximum allowable working pressure. 任何压力系统可运行的最高压力，通常比最大允许工作压力低10%至20%。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Population | 集合 |
The hypothetical collection of all possible test specimens that could be prepared in the specified way from the material under consideration. Also known as universe. 从所考虑的材料中以规定方式制备的所有可能试样的假设集合。也称为体系。 |
| Expansion bolt | 膨胀螺栓 |
When a through bolt cannot be used for attaching a pipe hanger, bracket, or other part, to a wall or ceiling of brick or concrete, what are known as expansion bolts are often used. The body of an expansion bolt is divided and the arrangement is such that, when the head of the bolt is turned, the sections forming the body of the bolt are forced outward and against the wall of the hole which has been drilled into the brick, concrete, or stone, as the case may be. Bolts of this type are made in quite a variety of designs. The nominal size represents the diameter of the bolt proper and not the diameter of the casing or expansion member. 当不能使用贯穿螺栓将管道吊架、支架或其他部件连接到砖块或混凝土的墙壁或天花板时，通常使用所谓的膨胀螺栓。膨胀螺栓的主体是分开的，其布置方式是，当螺栓头转动时，形成螺栓主体的部分被强制向外并靠在已钻入砖、混凝土或石头中的孔壁上，视情况而定。这种类型的螺栓有多种设计。标称尺寸代表螺栓本身的直径，而不是套管或膨胀构件的直径。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| Relaxation curve | 松弛曲线 |
A plot of either the remaining, or relaxed, stress as a function of time. 剩余压力或松弛压力随时间变化的曲线图。 |
| Turn-of-nut | 转动螺母 |
Sometimes used to describe the general rotation of the nut (or bolt head) as the fastener is tightened. More often used to define a particular tightening procedure in which a fastener is first tightened with a preselected torque, and is then tightened further by giving the nut an additional, measured, turn such as ‘‘three flats’’ (180°). 有时用于描述紧固件拧紧时螺母（或螺栓头）的总体旋转。更常用于定义一种特定的紧固程序，在该程序中，首先以预选扭矩拧紧紧固件，然后通过使螺母额外转动，如“三平面”（180°）进一步拧紧。 |
| Vapour-pressure thermometer | 蒸汽压力温度计 |
(vapour-filled thermometer) A type of fluidexpansion thermometer in which the working fluid is a volatile liquid. （蒸汽填充温度计）一种流体膨胀温度计，其中工作流体为挥发性液体。 |
| Compression test | 压缩测试 |
A method for assessing the ability of a material to withstand compressive loads. The determination of the stress–strain curve of a material by axial loading of a specimen in compression. In brittle materials failure is in the elastic range; more ductile materials will yield before fracture; very ductile materials will plastically deform extensively before failure. The compression strength (compressive strength), with unit Pa, is the compressive stress that causes failure in a component or structure. 一种评估材料承受压缩载荷能力的方法。通过压缩试样的轴向载荷确定材料的应力-应变曲线。在脆性材料中，破坏在弹性范围内；韧性更强的材料在断裂前会屈服；韧性很强的材料在失效前会发生广泛的塑性变形。抗压强度（抗压强度），单位为Pa，是导致部件或结构失效的压应力。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Elastic calibration device | 弹性校准装置 |
A device for use in verifying the load readings of a testing machine consisting of an elastic member(s) to which loads may be applied, combined with a mechanism or device for indicating the magnitude (or a quantity proportional to the magnitude) of deformation under load. 一种用于验证试验机载荷读数的装置，由可施加载荷的弹性构件组成，与指示载荷下变形量（或与该量成比例的量）的机构或装置相结合。 |
| Guided bend | 导向弯曲 |
The bend obtained by use of a plunger to force the specimen into a die in order to produce the desired contour of the outside and inside surfaces of the specimen. 通过使用柱塞将试样压入模具中获得的弯曲，以产生试样外表面和内表面所需的轮廓。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Ideal crack | 理想裂缝 |
A simplified model of a crack used in elastic-stress analysis. In a stress-free body, the crack has two smooth surfaces that are coincident and join within the body along a smooth curve called the crack front; in two-dimensional representations, the crack front is called the crack tip. 用于弹性应力分析的裂纹简化模型。在无应力物体中，裂纹有两个光滑表面，它们在物体内沿称为裂纹前缘的平滑曲线重合并连接；在二维表示中，裂纹前缘称为裂纹尖端。 |
| Brayton cycle | 布雷顿循环 |
(Joule cycle) An air standard cycle that is the ideal cycle for a gasturbine engine. As shown on the diagram of pressure (p) ʋs specific volume (ʋ), it consists of four internally reversible processes: isentropic compression in a compressor (1–2), isobaric heat addition in a combustor (2–3), isentropic expansion in a turbine (3–4) and isobaric heat rejection. The cycle can be extended to include regeneration, reheating, and intercooling. （焦耳循环）一种空气标准循环，是燃气轮机发动机的理想循环。循环可以扩展到包括再生、再热和中冷。 |
| Retaining clip | 固定夹 |
(R-clip, hair cotter pin) A wire clip roughly with the shape of the letter R. The straight part of the clip passes through a hole drilled into a shaft or rod such that a wheel is held in position on the shaft, or the shaft is prevented from moving axially. （R形夹，开口销）大致与字母R形状相同的线夹。线夹的直线部分穿过钻在轴或杆上的孔，从而将车轮固定在轴上，或防止轴轴向移动。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Induction tempering | 感应回火 |
Tempering of steel using low-frequency electrical induction heating. 钢的回火采用低频电感应加热。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Critical load (Unit N) | 临界负荷（单位N） |
1. The applied load that causes propagation of an existing crack of known length, and hence fracture of a component or structure. 2. The applied load that results in buckling of a column of given end fixity. 1.导致已知长度的现有裂纹扩展并因此导致部件或结构断裂的施加荷载。2.导致具有给定端部固定性的柱屈曲的施加荷载。 |
| Modulus of elasticity (E) | 弹性模量（E） |
The measure of rigidity or stiffness of a metal; the ratio of stress, below the proportional limit, to the corresponding strain. In terms of the stress-strain diagram, the modulus of elasticity is the slope of the stress-strain curve in the range of linear proportionality of stress to strain. 金属的刚度或刚度的量度；低于比例极限的应力与相应应变之比。根据应力应变图，弹性模量是应力应变曲线在应力应变线性比例范围内的斜率。 |
| Metallurgy | 冶金 |
The study of the atomic, crystallographic, microstructural, mechanical, and physical properties of metallic elements and alloys and their applications. 研究金属元素和合金的原子、晶体学、微观结构、机械和物理特性及其应用。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Air conditioning | 空调 |
The process of controlling the temperature and humidity in rooms, buildings, aircraft, passenger vehicles, etc. More generally it includes control of dust, levels of radiant heat, etc. 控制房间、建筑物、飞机、客运车辆等的温度和湿度的过程。更一般地说，它包括控制灰尘、辐射热水平等。 |
| Critical crack length (Unit m) | 临界裂纹长度（单位米） |
The crack length at which a given stress applied to a body will result in crack propagation and fracture. 施加到物体上的给定应力将导致裂纹扩展和断裂的裂纹长度。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Median fatigue life | 中位疲劳寿命 |
The middle value when all of the observed fatigue life values of the individual specimens in a group tested under identical conditions are arranged in order of magnitude. When an even number of specimens are tested, the average of the two middlemost values is used. Use of the sample median rather than the arithmetic mean (that is, the average) is usually preferred. 当在相同条件下测试的一组中单个试样的所有观察疲劳寿命值按数量级排列时的中间值。当测试偶数个试样时，使用两个中间值的平均值。通常优选使用样本中值而不是算术平均值（即平均值）。 |
| Thermomechanical working | 热机械加工 |
A general term covering a variety of processes combining controlled thermal and deformation treatments to obtain specific properties. Same as thermal-mechanical treatment. 一个通用术语，涵盖结合受控热处理和变形处理以获得特定性能的各种工艺。与热机械处理相同。 |
| Carburizing flame | 渗碳火焰 |
A gas flame that will introduce carbon into some heated metals, as during a gas welding operation. A carburizing flame is a reducing flame, but a reducing flame is not necessarily a carburizing flame. 一种气体火焰，会在气焊操作中将碳引入一些加热的金属中。渗碳火焰是还原火焰，但还原火焰不一定是渗碳火焰。 |
| Thread rolling | 滚丝 |
Thread rolling (also known as roll threading) is a cold forming process for producing threads or other helical or annular forms by rolling the impression of hardened steel dies into the surface of a cylindrical or conical blank. Polygonal blanks are also thread rolled for the purpose of fabricating thread-forming and self-locking screws. The preferred polygonal shape is trilobular and is produced in flat die machines. 螺纹滚压（也称为滚压螺纹）是一种冷成型工艺，通过将硬化钢模具的压痕滚压到圆柱形或锥形坯料的表面来生产螺纹或其他螺旋或环形形状。多边形坯料也进行螺纹轧制，以制造螺纹成型和自锁螺钉。优选的多边形形状为三棱形，并在平模机中生产。 |
| Grip length | 夹紧长度 |
Combined thickness of all the things clamped together by the bolt and nut, including washers, gaskets, and joint members. 由螺栓和螺母夹紧在一起的所有部件的总厚度，包括垫圈、垫圈和接头构件。 |
| Shear strain rate(Unit 1/s) | 剪切应变率（单位1/s） |
In the deformation of solids, the rate at which shear strain is applied in a test or changes with time in a loaded component or structure. 在固体变形中，在试验中施加剪切应变的速率，或在加载部件或结构中随时间变化的速率。 |
| Superheating | 过热 |
Heating above the temperature at which an equilibrium phase transformation should occur without actually obtaining the transformation. 在不实际获得相变的情况下，加热到应发生平衡相变的温度以上。 |
| Blueing | 发蓝 |
Application of blue dye (‘engineers’ blue’) to identify high spots on surfaces in contact, or for marking out. 应用蓝色染料（“工程师蓝”）来识别接触表面上的高点，或用于标记。 |
| Pop rivet | 拉钉 |
A hollow rivet that enables a connexion to be made from one side only of an assembly. 一种空心铆钉，使连接只能从组件的一侧进行。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Rupture stress | 断裂应力 |
The stress at failure. Also known as breaking stress. 失效时的应力。也称为破裂应力。 |
| Stretch-bending test | 拉伸弯曲试验 |
A simulative test for sheet metal formability in which a strip of sheet metal is clamped at its ends in lock beads and deformed in the center by a punch. Test conditions are chosen so that fracture occurs in the region of punch contact. 金属板成形性的模拟试验，其中金属板条在其端部夹紧在锁珠中，并通过冲头在中心变形。选择试验条件，以便在冲头接触区域发生断裂。 |
| Strain hardening | 应变硬化 |
An increase in hardness and strengthcaused by plastic deformation at temperatures below the recrystallization range. Also known as work hardening. (workhardening) The increase in stress above the initial yield stress required to deform a metal to greater strains in the plastic range at temperatures below the recrystallization range (cold working). Unloading after some strain or work input gives a harder and stronger material. 在低于再结晶范围的温度下，塑性变形导致硬度和强度的增加。也称为加工硬化。（加工硬化）在低于再结晶范围（冷加工）的温度下，使金属在塑性范围内变形至更大应变所需的高于初始屈服应力的应力增加。在一定的应变或功输入后卸载，会得到更硬、更强的材料。 |
| Load ratio, R | 负载比R |
In fatigue, the algebraic ratio of the minimum to maximum load in a fatigue cycle, that is, R = Pmin/Pmax. Also known as stress ratio. 在疲劳中，疲劳循环中最小载荷与最大载荷的代数比，即 R= Pmin/Pmax。也称为应力比。 |
| Auxiliary power unit (APU) | 辅助动力装置（APU） |
In aircraft–gas–turbine applications, a small gas turbine used to provide start-up power, electrical and hydraulic power, and compressed air for cabin ventilation. In other applications, an APU may be a gas turbine or internal-combustion engine used to provide emergency power. 在飞机-燃气轮机应用中，小型燃气轮机用于提供启动动力、电力和液压动力以及用于机舱通风的压缩空气。在其他应用中，APU可以是用于提供应急动力的燃气轮机或内燃机。 |
| Abelian group | 阿贝尔群 |
Property of a group of elements associated with a binary operation. In an Abelian group, the group elements commute under the binary operation. If a and b are any two group elements and if the (+) sign denotes the binary operation, then, for an Abelian group, 与二元运算相关的一组元素的属性。在阿贝尔群中，群元素在二元运算下交换。如果a和b是任意两个群元素并且（+）符号表示二元运算 |
| Damage mechanics | 损伤机制 |
The theory of degradation in bodies, particularly fracture by accumulated microstructural damage. Analyses take two approaches: (a) the use of some critical integrated function of stress and strain at which cracking is initiated and propagated; (b) incorporation of damage in the stress–strain curves to reflect weakened material. 物体退化理论，尤其是累积微观结构损伤导致的断裂。分析采用两种方法：（a）使用裂纹开始和扩展时的应力和应变的一些临界积分函数；（b）应力-应变曲线中包含损伤，以反映弱化材料。 |
| Eyebolt (eyescrew) | 吊环螺栓（眼螺丝） |
A bolt threaded at one end and bent to a loop at the other end. A bolt or screw with a closed loop in place of a head. 一端有螺纹，另一端弯曲成环的螺栓。带有闭合环代替头部的螺栓或螺钉。 |
| Pressure (p) (Unit Pa) | 压力（p）（单位Pa） |
In thermodynamics and fluid mechanics, the compressive force exerted by the fluid per unit area. The pressure exerted by a fluid on a surface acts normal to the surface. 在热力学和流体力学中，每单位面积流体施加的压缩力。流体施加在表面上的压力垂直于表面。 |
| International Practical Temperature Scale (IPTS) | 国际实用温标（IPTS） |
A close approximation to the thermodynamic temperature scale based upon the triple points of hydrogen (13.8 K), neon (24.6 K), oxygen (54.4 K), argon (83.8 K), mercury (234.3 K), and water (273.2 K); the melting point of gallium (302.9 K); and the freezing points of indium (429.7 K), tin (505.1 K), zinc (692.7 K), aluminium (933.5 K), silver (1 234.9 K), gold (1 337.3 K), and copper (1 基于氢（13.8K）、氖（24.6K）、氧（54.4K）、氩（83.8K），汞（234.3K）和水（273.2K）的三相点的热力学温度标度的近似值；镓的熔点（302.9K）；铟（429.7K）、锡（505.1K）、锌（692.7K），铝（933.5K）、银（1234.9K）、金（1337.3K）和铜等。 |
| Assembly line | 流水线 |
A system of mass production in which work is moved progressively from one operation to another, ultimately to give the final complete product. 一种大规模生产系统，其中工作逐渐从一个操作转移到另一个操作，最终得到完整产品。 |
| Guided-bend test | 导向弯曲试验 |
A test in which the specimen is bent to a definite shape by means of a punch (mandrel) and a bottom block. 用冲头（心轴）和底块将试样弯曲成一定形状的试验。 |
| Atomizing humidifier | 雾化加湿器 |
A humidifier that functions by spraying fine droplets of water into an airstream. 一种加湿器，通过将细小的水滴喷射到气流中来发挥作用。 |
| Die screw | 模具螺丝 |
Tool used when threading cylindrical pieces beyond the capacity of a die plate. 对超出模板容量的圆柱件进行螺纹加工时使用的工具。 |
| Compression failure | 压缩失败 |
The reduction or removal of a component’s load-bearing capacity in compression, caused by buckling, fracture, crease formation in fibre composites, etc. 由纤维复合材料中的屈曲、断裂、折痕形成等引起的部件在压缩中的承载能力的降低或消除。 |
| Subcritical annealing | 不完全退火 |
A process anneal performed on ferrous alloys at a temperature below Ac1. 在低于Ac1的温度下对铁合金进行的工艺退火。 |
| Wind pump | 风泵 |
A pump driven directly by a windmill on a tower. Widely used in remote locations. 由塔上的风车直接驱动的泵。广泛应用于偏远地区。 |
| Elastic energy | 弹性能 |
The amount of energy required to deform a material within its elastic range of behavior, neglecting small heat losses due to internal friction. The energy absorbed by a specimen per unit volume of material contained within the gage length being tested. It is determined by measuring the area under the stress-strain curve up to a specified elastic strain. See also modulus of resilience and strain energy. 材料在其弹性行为范围内变形所需的能量，忽略因内耗引起的小热损失。试样在被测标距内每单位体积材料吸收的能量。它是通过测量应力-应变曲线下达到规定弹性应变的面积来确定的。另见弹性模量和应变能。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Strain rate | 应变率 |
The time rate of straining for the usual tensile test. Strain as measured directly on the specimen gage length is used for determining strain rate. Because strain is dimensionless, the units of strain rate are reciprocal time. 通常拉伸试验的应变时间速率。直接在试样标距上测量的应变用于确定应变率。因为应变是无因次的，所以应变率的单位是倒数时间。 |
| Inch-pound force/inch² | 英寸磅力/英寸² |
A non-SI unit for the specific work of fracture (fracture toughness). The conversion to SI is 1 in.lbf/in² = 1.751 268 × 102 J/m². 用于特定断裂功（断裂韧性）的非国际单位制单位。到SI的转换为1英寸。lbf/in²=1.751268×102J/m²。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Laser sintering | 激光烧结 |
A manufacturing technique by which parts are built layer by layer (each typically 20 μm thick) from plastic or metal (Direct Metal Laser Sintering, DMLS) material in powder form, each layer being sintered by a scanning laser. 一种制造技术，通过这种制造技术，零件由粉末形式的塑料或金属（直接金属激光烧结，DMLS）材料逐层（每个厚度通常为 20 微米）构建，每一层都由扫描激光烧结。 |
| Coefficient of thermal expansion | 热膨胀系数 |
(1) Change in unit of length (or volume) accompanying a unit change of temperature, at a specified temperature. (2) The linear or volume expansion of a given material per degree rise of temperature, expressed at an arbitrary base temperature or as a more complicated equation applicable to a wide range. （1） 单位长度（或体积）随温度单位变化的变化。（2） 给定材料每上升一度的线性或体积膨胀，在任意基础温度下表示，或作为适用于宽范围的更复杂方程表示。 |
| Reverse engineering | 逆向工程 |
The disassembly of a machine, mechanism, system or device, measurement of its component parts, and identification of the materials used so that if required, a functioning replica can be produced. 拆卸机器、机构、系统或装置，测量其组成部分，并识别所用材料，以便在需要时可以生产出功能正常的复制品。 |
| Turbine blades (turbine buckets) | 涡轮叶片 |
1. The aerofoil-shaped vanes that form the rotor and stator of a gas, steam or hydraulic turbine. 2. The cup-shaped vanes of a Pelton wheel. 1.形成燃气、蒸汽或水力涡轮机的转子和定子的翼型叶片。2.冲击轮的杯形叶片。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Waist | 腰部 |
The joint in a robot corresponding to the human waist, i.e. providing rotation about a vertical axis. In an articulated robot, the first joint mounted at the base frame. 机器人中的关节对应于人的腰部，即提供绕垂直轴的旋转。在关节式机器人中，第一个关节安装在基架上。 |
| Bolt length | 螺栓长度 |
The bolt length shall be the distance measured parallel to the axis of the product from the bearing surface of the head to the extreme end of the bolt including point. 螺栓长度应为平行于产品轴线测量的从头部的支承面到包括点在内的螺栓末端的距离。 |
| Selective heating | 局部加热 |
Intentionally heating only certain portions of a workpiece. 有意仅加热工件的某些部分。 |
| Observed value | 观测值 |
The particular value of a characteristic determined as a result of a test or measurement. 作为测试或测量结果确定的特性的特定值。 |
| Striation | 条纹组织 |
A fatigue fracture feature, often observed in electron micrographs, that indicates the position of the crack front after each succeeding cycle of stress. The distance between striations indicates the advance of the crack front across that crystal during one stress cycle, and a line normal to the striation indicates the direction of local crack propagation. 一种疲劳断裂特征，通常在电子显微照片中观察到，表明每次应力循环后裂纹前沿的位置。条纹之间的距离表示在一个应力循环期间裂纹前沿穿过该晶体的前进，垂直于条纹的线表示局部裂纹扩展的方向。 |
| Safety valve (safety-relief valve) | 安全阀（安全泄压阀） |
A mechanical valve, fitted by law to all pressure vessels (e.g. steam boilers), which opens to prevent the internal pressure exceeding the maximum design value for that vessel. The valve closes again once the pressure reduces to a safe level. 根据法律安装在所有压力容器（如蒸汽锅炉）上的机械阀，其打开以防止内部压力超过该容器的最大设计值。一旦压力降至安全水平，阀门将再次关闭。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| V-block | V型块 |
A block having a 90° V-shaped recess; used in a workshop to hold round workpieces. 具有90°V形凹槽的块体；在车间里用来装圆形工件。 |
| 显示更多数据，请使用查询功能！ | ||