| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Modulus of elasticity (E) | 弹性模量（E） |
The measure of rigidity or stiffness of a metal; the ratio of stress, below the proportional limit, to the corresponding strain. In terms of the stress-strain diagram, the modulus of elasticity is the slope of the stress-strain curve in the range of linear proportionality of stress to strain. 金属的刚度或刚度的量度；低于比例极限的应力与相应应变之比。根据应力应变图，弹性模量是应力应变曲线在应力应变线性比例范围内的斜率。 |
| Two-phase flow | 两相流 |
A flow in which two phases are present, for example gas bubbles in a liquid, liquid bubbles in another liquid with which it is immiscible, solid particles in a liquid or gas. 两相流动，例如液体中的气泡、与之不混溶的另一种液体中的液体气泡、液体或气体中的固体颗粒。 |
| Intense quenching | 强烈淬火 |
Quenching in which the quenching medium is cooling the part at a rate at least two and a half times faster than still water. 淬火，其中淬火介质以比静水快至少两倍半的速度冷却零件。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Acoustic droplet ejection | 声液滴喷射 |
The ejection of small droplets from the surface of a liquid that results from focusing high-intensity ultrasound near the surface. 由于在表面附近聚焦高强度超声波而从液体表面喷射出小液滴。 |
| Pitch-circle diameter (Unit m) | 节圆直径（单位：m） |
The diameter of the circle (the pitch circle) centred on a component’s axis, around which holes or bolts are equally spaced. 以部件轴为中心的圆（节圆）的直径，孔或螺栓围绕其等距分布。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| Mohr–Coulomb fracture criterion | Mohr–Coulomb断裂准则 |
A fracture criterion, primarily for brittle materials, according to which failure occurs when the stress at a point in a material falls outside the envelope created by the Mohr’s circles for uniaxial tensile strength and uniaxial compressive strength. 一种断裂准则，主要适用于脆性材料，根据该准则，当材料中某一点的应力落在单轴抗拉强度和单轴抗压强度的莫尔圆所形成的包络线之外时，就会发生断裂。 |
| Finished fastener | 精制紧固件 |
Fastener for which all manufacturing steps have been completed, with or without any surface coating and with full or reduced loadability, and which has not been machined into a test piece. 已完成所有制造步骤的紧固件，有或没有任何表面涂层，具有完全或降低的承载能力，并且尚未加工成试件。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Cleavage fracture | 解理断裂 |
A fracture, usually of a polycrystalline metal, in which most of the grains have failed by cleavage, resulting in bright reflecting facets. It is one type of crystalline fracture and is associated with low energy brittle fracture. Contrast with shear fracture. A fracture created by splitting (cleavage), as between layers in materials like slate or mica. In brittle metals, and brittle microconstituents in alloys, cleavage occurs along particular crystal planes. 一种通过分裂（劈裂）产生的裂缝断裂，通常是多晶金属的断裂，其中大部分晶粒因解理而失效，产生明亮的反射面。它是一种结晶性断裂，与低能脆性断裂有关。与剪切断裂相对。如板岩或云母等材料的层之间。在脆性金属和合金中的脆性微量成分中，沿特定晶面发生解理。 |
| Fastener quality | 紧固件质量 |
A fastener’s adherence to its specification for dimensional tolerances, mechanical properties, and other requirements stated under applicable standards. 紧固件对尺寸公差、机械性能和适用标准规定的其他要求的规范的遵守情况。 |
| Computer-aided design (CAD) | 计算机辅助设计（CAD） |
Generally, design and calculations performed by computer; more specifically, the use of computer graphics and models to communicate design concepts. Computer-aided design and computer-aided manufacturing (CAD/CAM) is where component dimensions resulting from CAD are passed by electronic means directly to machines for manufacture. 一般由计算机进行设计和计算，更具体地说，使用计算机图形和模型来传达设计概念。计算机辅助设计和计算机辅助制造（CAD/CAM）是由CAD产生的组件尺寸通过电子方式直接传递到机器进行制造。 |
| Critical load (Unit N) | 临界负荷（单位N） |
1. The applied load that causes propagation of an existing crack of known length, and hence fracture of a component or structure. 2. The applied load that results in buckling of a column of given end fixity. 1.导致已知长度的现有裂纹扩展并因此导致部件或结构断裂的施加荷载。2.导致具有给定端部固定性的柱屈曲的施加荷载。 |
| Stabilizing treatment | 稳定化处理 |
(1) Before finishing to final dimensions, repeatedly heating a ferrous or nonferrous part to or slightly above its normal operating temperature and then cooling to room temperature to ensure dimensional stability in service. (2) Transforming retained austenite in quenched hardenable steels, usually by cold treatment. (3) Heating a solution-treated stabilized grade of austenitic stainless steel to 870 to 900 °C (1600 to 1650 °F) to precipitate all carbon as TiC, NbC, or TaC so that sensitization is avoided on subsequent exposure to elevated temperature. （1）在精加工至最终尺寸之前，反复加热含铁或非铁零件至或略高于其正常工作温度，然后冷却至室温，以确保使用中的尺寸稳定性。（2）在淬火可淬硬钢中转变残余奥氏体，通常通过冷处理。（3）将固溶处理的稳定等级奥氏体不锈钢加热至870至900°C（1600至1650°F），使所有碳沉淀为TiC、NbC或TaC，从而避免在随后暴露于高温时敏化。 |
| Melting point (Unit K or °C) | 熔点（单位K或°C） |
The temperature at which a solid material undergoes the phase change to a liquid at a specified pressure, usually 1 atm. Pure metals and eutectics have single-valued melting points, while alloys with other compositions melt over a range of temperature such that there is a well-defined start and end to the melting process, but there are states in between where solid and liquid are both present. 在特定压力下，固体材料发生相变为液体的温度，通常为1大气压。纯金属和共晶具有单值熔点，而具有其他成分的合金在一定温度范围内熔化，熔化过程有一个明确的起点和终点，但其间存在固态和液态并存的状态。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Welding | 焊接 |
In tribology, the bonding between metallic surfaces in direct contact, at any temperature. A joining process in which the mating surfaces are at least softened, or more usually melted, unlike soldering and brazing. In solid-state (non-melting) welding, similar or dissimilar metals or thermoplastics may be joined by applying pressure to hot interfaces. In forge welding, joining is achieved by compression across the join between pre-heated workpieces. In friction welding (spin welding) one of the contacting surfaces is rotated rapidly before being loaded against the other. On contact, heat generated by friction softens the materials and permits severe plastic deformation that seals the joint. In friction stir welding, a wear-resistant tool is rotated rapidly, indents the surfaces and is traversed to form a join line. Resistance welding involves simultaneous pressure and electrically-generated heat, as in spot welding where a heavy electric current is passed for a short time through metal sheets which are pressed together between electrodes. 在摩擦学中，在任何温度下直接接触的金属表面之间的结合。与钎焊和钎焊不同，接合面至少软化或更通常熔化的接合工艺。在固态（非熔化）焊接中，相似或不同的金属或热塑性塑料可通过向热界面施加压力来连接。在锻造焊接中，通过压缩预热工件之间的连接来实现连接。在摩擦焊接（旋转焊接）中，一个接触表面在被加载到另一个表面之前快速旋转。接触时，摩擦产生的热量使材料软化，并允许密封接头的严重塑性变形。在搅拌摩擦焊中，耐磨工具快速旋转，使表面凹陷，并横穿形成连接线。电阻焊涉及同时产生的压力和电产生的热量，如点焊，在点焊中，大电流短时间通过电极之间压在一起的金属板。 |
| Morse taper | 莫氏锥度 |
A self holding, standard taper largely used on drilling tools, drilling machine spindles, and some lathes. 一种自持式标准锥度，主要用于钻孔工具、钻床主轴和一些车床。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Dynamic coupling | 动态耦合 |
In vibrations, the existence of inertial terms depending on mass in the governing equations, so that there is only a force if there is a corresponding acceleration. 在振动中，惯性项的存在取决于控制方程中的质量，因此只有当有相应的加速度时才有力。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Mode of failure | 故障模式 |
The various ways in which a material can fail when subjected to loading, surface damage, chemical attack, heating, cooling, or radiation, in either isolation or combination. The failure modes include fracture, fatigue, creep, corrosion, erosion, and embrittlement. 材料在受到载荷、表面损伤、化学侵蚀、加热、冷却或辐射时，可能发生失效的各种方式，无论是单独还是组合。失效模式包括断裂、疲劳、蠕变、腐蚀、侵蚀和脆化。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Thermal fatigue | 热疲劳 |
Fatigue resulting from the presence of temperature gradients that vary with time in such a manner as to produce cyclic stresses in a structure. 由于温度梯度的存在而产生的疲劳，温度梯度随时间变化，从而在结构中产生循环应力。 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Stainless steels | 不锈钢 |
Iron-base alloys that are highly resistant to corrosion in many environments. The predominant alloying element is chromium, which, like iron at room temperature, has BCC crystal structure. Corrosion resistance by passivation is achieved by the formation of chromium oxide on the steel surface. Nickel, which has FCC crystal structure, is another important addition for some steels. Other additions used to enhance properties include manganese, molybdenum, niobium, and titanium. There are several classes of stainless steel. 在许多环境中具有高度耐腐蚀性的铁基合金。主要的合金元素是铬，与室温下的铁一样，铬具有BCC晶体结构。钝化抗腐蚀性是通过在钢表面形成氧化铬来实现的。具有FCC晶体结构的镍是某些钢的另一种重要添加剂。其他用于增强性能的添加剂包括锰、钼、铌和钛。不锈钢的种类有好几种。 |
| Dynamic mechanical measurement | 动态机械测量 |
A technique in which either the modulus and/or damping of a substance under oscillatory load or displacement is measured as a function of temperature, frequency, or time, or a combination thereof. 一种技术，其中在振荡载荷或位移下测量物质的模量和/或阻尼作为温度、频率或时间或其组合的函数。 |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| Minimum stress-intensity factor (Kmin) | 最小应力强度因子（Kmin） |
In fatigue, the minimum value of the stress-intensity factor in a cycle. This value corresponds to the minimum loadwhen the load ratio is 0 and is taken to be 0 when the load ratio is ≤0. 在疲劳中，一个循环中应力强度因子的最小值。该值对应于负载比为0时的最小负载，当负载比为≤0 |
| Wrinkling | 起皱 |
A wavy condition obtained in deep drawing of sheet metal, in the area of the metal between the edge of the flange and the draw radius. Wrinkling may also occur in other forming operations when unbalanced compressive forces are set up. 在金属板深冲过程中，在法兰边缘和拉深半径之间的金属区域内获得的波浪状状态。当设置不平衡压缩力时，在其他成形操作中也可能发生起皱。 |
| Shoulder joint | 轴肩关节 |
The second joint on an articulated robot, which has a horizontal axis and is analogous to the human shoulder. 关节机器人上的第二个关节，具有水平轴，类似于人的肩膀。 |
| Percent error | 误差百分比 |
For testing machines, the ratio, expressed as a percentage, of the error to the correct value of the applied load. 对于试验机，以百分比表示的误差与所施加载荷的正确值之比。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Vacuum pump | 真空泵 |
A pump for exhausting air and non-condensable gases from a vessel to be maintained at sub-atmospheric pressure. The pirani and thermal-conductivity gauges are vacuum gauges used to measure the absolute pressure within a vacuum system (vacuum level), usually expressed in torr or Pa. 用于从容器中排出空气和不凝性气体以保持在亚大气压的泵。皮拉尼和热导率计是用于测量真空系统内绝对压力（真空水平）的真空计，通常用托或帕表示。 |
| Coated abrasive | 涂附磨具 |
An abrasive tool consisting of a flexible backing material, such as a woven cloth, paper or vulcanized fibre, a bond material, such as a glue or synthetic resin, and grit. 一种研磨工具，由柔性背衬材料（例如编织布、纸或硫化纤维）、粘合材料（例如胶水或合成树脂）和砂砾组成。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Dynamic modulus | 动态模量 |
The ratio of stress to strain under cyclic conditions (calculated from data obtained from either free or forced vibration tests, in shear, compression, or tension). 循环条件下的应力与应变之比（根据在剪切、压缩或拉伸中的自由或强制振动测试中获得的数据计算得出）。 |
| Strength (Unit Pa) | 强度（单位Pa） |
The maximum stress, in tension, compression, shear, or combinations thereof, that may be monotonically applied to a material, component, or structure before failure (defined as fracture, yielding, buckling, etc. as appropriate). 在破坏前（视情况定义为断裂、屈服、屈曲等），材料、部件或结构在拉伸、压缩、剪切或其组合中可能单调施加的最大应力。 |
| Turbine blades (turbine buckets) | 涡轮叶片 |
1. The aerofoil-shaped vanes that form the rotor and stator of a gas, steam or hydraulic turbine. 2. The cup-shaped vanes of a Pelton wheel. 1.形成燃气、蒸汽或水力涡轮机的转子和定子的翼型叶片。2.冲击轮的杯形叶片。 |
| Depth gauge | 深度计 |
1. A precision instrument, typically consisting of a machine-divided steel rule passing through a hardened-steel cross head, used to measure the depths of slots, holes, shoulders, projections, etc. 2. A device used by divers to indicate the water depth. 1. 一种精密仪器，通常由穿过硬化钢十字头的机器分割钢尺组成，用于测量槽、孔、肩部、突起等的深度。 2. 潜水员用来指示深度的装置水深。 |
| Radiosity (J) (Unit W/m²) | 辐射度（J）（单位W/m²） |
The total radiation leaving a given surface per unit area, including emitted, reflected, and transmitted radiation. 每单位面积离开给定表面的总辐射，包括发射、反射和透射辐射。 |
| Autonomous energy system | 自主能源系统 |
(stand-alone energy system) A sole source of electricity, usually small-scale, for applications remote from a grid, especially with energy storage in the system. Hydroelectric, photovoltaic, wind-power and other renewable systems are well suited to stand-alone applications. （独立能源系统）一种唯一的电力来源，通常是小规模的，用于远离电网的应用，尤其是系统中的能量存储。水电、光伏、风力和其他可再生能源系统非常适合独立应用。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Spalling | 剥落 |
The separation of macroscopic particles from a surface in the form of flakes or chips. 以薄片或碎片形式从表面分离宏观颗粒。 |
| Scratch hardness test | 划痕硬度测试 |
A form of hardness test in which a sharp-pointed stylus or corner of a mineral specimen is traversed along a surface so as to determine the resistance of that surface to cutting or abrasion. 硬度测试的一种形式，用尖头笔或矿物样品的一角沿一个表面移动，以确定该表面的抗切割或耐磨性。 |
| Effective length of a bolt | 螺栓的有效长度 |
The grip length plus some portion of the bolt (often one-half of the thickness of the nuts) which lies within the nut(s) plus some portion (often one-half the thickness) of the head. 握持长度加上位于螺母内的螺栓的某些部分（通常是螺母厚度的二分之一）加上头部的某些部分（通常是厚度的二分之一）。 |
| Quench-age embrittlement | 淬火时效脆化 |
Embrittlement of low-carbon steels resulting from precipitation of solute carbon at existing dislocations and from precipitation hardening of the steel caused by differences in ferrite at different temperatures. Quenchage embrittlement usually is caused by rapid cooling of the steel from temperatures slightly below Ac1 (the temperature at which austenite begins to form), and can be minimized by quenching from lower temperatures. 低碳钢的脆化是由于溶质碳在现有位错处的沉淀和铁素体在不同温度下的差异导致的钢沉淀硬化造成的。淬火脆性通常是由钢从略低于Ac1的温度（奥氏体开始形成的温度）快速冷却引起的，可以通过从较低温度淬火来最小化。 |
| Rated power (Unit kW or hp) | 额定功率（单位：千瓦或马力） |
(rated capacity, rated horsepower) The maximum power output that can be sustained continuously for any power-producing machine or system, such as an engine or a power plant. （额定容量、额定马力）任何发电机器或系统（如发动机或发电厂）可连续维持的最大功率输出。 |
| Cavitation damage | 气蚀损坏 |
Erosion of a solid surface through the formation and collapse of cavities or bubbles in an adjacent liquid that contains vapor and/or gas. 通过在包含蒸汽和/或气体的相邻液体中形成空穴或气泡并破坏固体表面。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Lead screw | 丝杠 |
The master screw running along the length of the bed of a lathe from which all screws threads on that machine are cut. Master screw used for cutting a screw thread in a lathe. 沿车床床身长度方向运行的主螺钉，该机床上的所有螺钉和螺纹都从主螺钉上切割下来。用于在车床上切削螺纹的主螺钉。 |
| Joint | 关节接合处 |
The part of a robot arm permitting either rotational or translational motion. Each joint provides a single degree of freedom, and thus a minimum of six is required if the robot is to be able to position and orientate the end effector anywhere within the workspace. A joint is described by four parameters: the joint angle, joint offset, joint twist, and link length. The joint angle is the angle between an extrapolation of the previous link length and the present link length, measured positive anticlockwise in a plane normal to the joint axis. This is variable in a rotational joint and fixed in a translational joint. The joint offset is the distance between the link length for the previous link and that for the present link, measured along the joint axis. This is variable for a translational joint and fixed for a rotational joint. The joint twist for the nth joint is the angle between the axes of joints Jn and Jn+1, measured positive anticlockwise in a plane normal to the link length and viewed from the position of the Jn+1 joint. The link length is the mutually perpendicular distance between planes passing through the axes of joint Jn and Jn+1. Both the joint twist and link length are fixed in all joints. 机器人手臂上允许旋转或平移运动的部分。每个接合处都有自由度，如果机器人要能够在工作空间内的任何位置定位和定向末端执行器，则至少需要六个接合处具有自由度。关节接合处由四个参数描述：关节角度、关节偏移、关节扭曲和链接长度。关节角度是在垂直于关节轴的平面内逆时针测量的先前连杆长度和当前连杆长度的外推之间的角度。这在旋转关节中是可变的，在平移关节中是固定的。关节偏移是沿关节轴测量的前一个连杆和当前连杆的连杆长度之间的距离。这对于平移关节是可变的，对于旋转关节是固定的。第n个关节的关节扭曲是关节Jn和Jn+1轴之间的角度，在垂直于连杆长度的平面内逆时针测量，从Jn+2关节的位置观察。连杆长度是穿过关节轴Jn和Jn+1的平面之间相互垂直的距离。关节扭曲和连杆长度在所有关节中都是固定的。 |
| Shear joint | 剪切接头 |
A joint which is subjected primarily to loads acting more or less perpendicular to the axes of the bolts. 主要承受或多或少垂直于螺栓轴线的载荷的接头。 |
| Nut factor | 螺母系数 |
An experimental constant used to evaluate or describe the ratio between the torque applied to a fastener and the Preload achieved as a result. 用于评估或描述施加在紧固件上的扭矩与由此获得的预载之间的比率的实验常数。 |
| Materials science | 材料科学 |
The study of the properties, behaviour, and application of solid substances such as metals, ceramics, glasses, polymers, composites, biomaterials, and semiconductors, at all scales from the atomic to the macroscopic. The topic has its origins in metallurgy. 研究金属、陶瓷、玻璃、聚合物、复合材料、生物材料和半导体等固体物质的特性、行为和应用，涵盖从原子到宏观的所有范围。起源于冶金学。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Vibration-testing machine (vibrator) | 振动试验机（振动器） |
Any machine that subjects components or systems to vibration at known amplitudes and frequencies in order to determine the response. vibratory equipment Vibrating process equipment, such as shakers, used to separate small and large particles, or feeders to supply particulate or granular material that may otherwise clog. 使部件或系统以已知振幅和频率振动以确定响应的任何机器。振动设备振动工艺设备，如用于分离小颗粒和大颗粒的振动筛，或用于供应可能堵塞的颗粒或粒状材料的给料机。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Wind tunnel | 风洞 |
A duct in which a controlled flow of air is used for testing and research. Types include blow down, closed circuit, open return, and open section. Closed-circuit tunnels may be pressurized or evacuated. The working section is usually situated immediately downstream of the flow-conditioning elements, which may include a plenum chamber, honeycomb, screens, turbulence grids, and a contraction. Immediately downstream there is usually a diffuser. For basic research the usual requirement is for uniform steady flow in the working section with low swirl and turbulence intensity. For some applications the flow may be density stratified, sheared, unsteady, or of high turbulence intensity. 用于测试和研究的可控气流管道。类型包括排污、闭路、开路回路和开路段。闭路隧道可加压或排空。工作段通常位于流量调节元件的下游，可包括增压室、蜂窝、滤网、湍流格栅和收缩管。紧靠下游通常有一个扩散器。对于基础研究，通常的要求是在低涡流和湍流强度的工作段中实现均匀稳定流动。对于某些应用，流动可能是密度分层、剪切、不稳定或高湍流强度。 |
| Balancing machine | 平衡机 |
A device that assesses the state of static and dynamic balance of a rotating part, and indicates the magnitude and location of weights to be added to give balance. 一种装置，用于评估旋转部件的静态和动态平衡状态，并指示为获得平衡而添加的砝码的大小和位置。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Scale height (Unit m) | 刻度高度（单位：m） |
The altitude H at which the atmospheric pressure has decreased to a certain fraction of its value at sea level B. It depends on the model adopted for the atmosphere: for an isothermal atmosphere, the pressure decreases exponentially with altitude. If H is taken as the altitude at which the pressure has fallen to B/e, then H = RT/g where R is the gas constant for air, T is the absolute temperature T, and g is the acceleration due to gravity. 大气压力降低到其在海平面B处数值的某一部分的高度H。它取决于大气采用的模型：对于等温大气，压力随高度呈指数下降。如果取H作为压力下降到B/e的高度，则H=RT/g，其中R是空气的气体常数，T是绝对温度T，g是重力引起的加速度。 |
| Vice | 老虎钳 |
A workshop tool used to hold a workpiece and consisting of two jaws, one fixed and the other moved by turning a screw. 一种用于夹持工件的车间工具，由两个钳口组成，一个固定，另一个通过转动螺钉移动。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Cyaniding | 氰化 |
A case-hardening process in which a ferrous material is heated above the lower transformation range in a molten salt containing cyanide to cause simultaneous absorption of carbon and nitrogen at the surface and, by diffusion, create a concentration gradient. Quench hardening completes the process. 一种表面硬化工艺，将含铁材料在含氰化物的熔融盐中加热至低于较低转变范围，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。淬火硬化完成该过程。 |
| Snap temper | 快速回火 |
A precautionary interim stress-relieving treatment applied to high-hardenability steels immediately after quenching to prevent cracking because of delay in tempering them at the prescribed higher temperature. 在淬火后立即对高淬透性钢进行预防性临时应力消除处理，以防止因在规定的更高温度下回火延迟而开裂。 |
| Torque multiplier | 扭矩放大器 |
A gearbox used to multiply the torque produced by a small hand wrench (usually a Torque wrench). The output of the multiplier drives the nut or bolt with a torque that is higher, and a speed that is lower, than input torque and speed. There is no torque gage or readout on the multiplier. 一种齿轮箱，用于增加小手动扳手（通常是扭矩扳手）产生的扭矩。倍增器的输出以比输入扭矩和速度更高的扭矩和更低的速度驱动螺母或螺栓。倍增器上没有扭矩计或读数。 |
| Constant-force spring | 恒力弹簧 |
A spring that has the same restoring force regardless of displacement. The most common type takes the form of a coiled strip that, owing to tight coiling during manufacture, is pre-stressed (a steel measuring tape is an example). The uncoiling force is approximately constant as the change of curvature of the strip is approximately constant. Not to be confused with a clockwork spring from which power can be obtained. 无论位移如何，具有相同恢复力的弹簧。最常见的类型是卷绕带，由于制造过程中的紧密卷绕，该卷绕带是预应力的（钢卷尺就是一个例子）。随着带材曲率的变化近似恒定，开卷力近似恒定。不要与可获得动力的发条弹簧混淆。 |
| Conditioning heat treatment | 调质热处理 |
A preliminary heat treatment used to prepare a material for desired reaction to a subsequent heat treatment. For the term to be meaningful, the exact heat treatment must be specified. 用于制备材料的初步热处理，以便对随后的热处理进行所需的反应。为了使该术语有意义，必须指定确切的热处理。 |
| Range of stress (Sr) | 应力范围（Sr） |
The algebraic difference between the maximum and minimum stress in one cycle—that is, Sr = Smax – Smin 一个循环中最大和最小应力之间的代数差，即Sr=Smax–Smin |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Transformation toughening | 相变增韧 |
The improvement of fracture toughness of a material by stress-induced transformation of the microstructure. 通过微结构的应力诱导转变来提高材料的断裂韧性。 |
| Wind pressure (Unit Pa) | 风压（单位Pa） |
The dynamic pressure associated with the wind. The static pressure of the wind is the atmospheric pressure. 与风相关的动态压力。风的静压是大气压。 |
| Finished hexagon bolts | 精制六角螺栓 |
A washer faced or chamfered bearing surface with a close body tolerance. 头下有垫圈面或倒角，尺寸公差小 |
| Elastic resilience | 弹性回弹 |
The amount of energy absorbed in stressing a material up to the elastic limit; or, the amount of energy that can be recovered when stress is released from the elastic limit. 向材料施加应力直至弹性极限所吸收的能量；或者当应力从弹性极限释放时可以恢复的能量值。 |
| Air-hardening steel | 空气硬化钢 |
A steel containing sufficient carbon and other alloying elements to harden fully during cooling in air or other gaseous mediums from a temperature above its transformation range. The terms should be restricted to steels that are capable of being hardened by cooling in air in fairly large sections, about 2 in. (50 mm) or more in diameter. Same as self-hardening steel. 一种钢，含有足够的碳和其他合金元素，可以在空气或其他气体介质中从高于其转变范围的温度冷却过程中完全硬化。这些术语应仅限于能够通过在相当大的截面（直径约2英寸（50毫米）或更大）中通过空气冷却而硬化的钢。与自硬钢相同。 |
| Outside diameter (Unit m) | 外径（单位：m） |
(external diameter, OD) The diameter of a circular cylindrical tube or a sphere measured between opposite points on the external surface. （外径，OD）在外表面上的相对点之间测量的圆柱管或球体的直径。 |
| Spinner | 旋转器 |
A co-axial streamlined fairing enclosing the hub of a propeller and rotating with it. 一种同轴流线型整流罩，包围螺旋桨毂并随其旋转。 |
| Engineering stress (s) | 工程应力 |
A term sometimes used for conventional stress in order to differentiate it from true stress. In tension testing, it is calculated by dividing the breaking load applied to the specimen by the original crosssectional area of the specimen. 一个术语，有时用于常规应力，以区别于真实应力。在拉伸试验中，通过将施加在试样上的断裂载荷除以试样的原始横截面积来计算。 |
| Dew point | 压力露点 |
The temperature and pressure at which a gas begins to condense to a liquid. 气体开始凝结成液体的温度和压力。 |
| Newton’s law of viscosity | 牛顿内摩擦定律 |
The shear stress between two parallel layers of fluid is proportional to the velocity of one relative to that of the other, and inversely proportional to the distance between them. The constant of proportionality is the dynamic viscosity μ. For a Newtonian fluid μ is independent of pressure gradient, shear stress, and strain, but may change with temperature and pressure. 两个平行流体层之间的剪切应力与其中一层相对于另一层的速度成正比，与它们之间的距离成反比。比例常数是动态粘度μ。对于牛顿流体，μ与压力梯度、剪切应力和应变无关，但可能随温度和压力而变化。 |
| Edge distance ratio | 边距比 |
The ratio of the edge distance to the pin diameter in a bearing test. 轴承测试中边缘距离与销直径的比值。 |
| Radial engine | 径向发动机 |
A piston engine in which the cylinders are arranged radially around the crankshaft, a design commonly used in early aircraft engines. 气缸沿径向围绕曲轴布置的活塞式发动机，这种设计通常用于早期飞机发动机。 |
| Galling | 磨损 |
An extreme form of adhesive wear, in which large chunks of one part stick to the mating part (during sliding contact). 一种极端形式的粘着磨损，其中一个零件的大块粘在配合零件上（在滑动接触期间）。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Scuffing | 擦伤 |
A form of adhesive wear that produces superficial scratches or a high polish on the rubbing surfaces. It is observed most often on inadequately lubricated parts. 粘着磨损的一种形式，在摩擦表面上产生表面划痕或高度抛光。通常在润滑不足的零件上观察到。 |
| Second (s) | 秒（s） |
The SI base unit of time equal to 9 192 631 770 times the period of the radiation corresponding to the transition between the two hyperfine levels of the ground state of the caesium-133 atom. SI基时间单位等于9192631770倍的辐射周期，对应于铯-133原子基态的两个超精细能级之间的跃迁。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Hydrodynamics | 流体力学 |
A term sometimes used to mean fluid dynamics, even when the fluid is a gas or a liquid other than water. 有时用于表示流体动力学的术语，即使流体是气体或水以外的液体。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Proportional limit | 比例极限 |
The greatest stress a material is capable of developing without a deviation from straight-line proportionality between stress and strain. 材料能够产生的最大应力不偏离应力和应变之间的直线比例。 |
| Initial preload | 初始预载 |
The tension created in a single bolt as it is tightened. Will usually be modified by subsequent assembly operations or by in-service loads and conditions. 拧紧单个螺栓时产生的张力。通常会通过后续的装配操作或在役负载和条件进行修改。 |
| Ferritizing anneal | 铁素体化退火 |
A treatment given as-cast gray or ductile (nodular) iron to produce an essentially ferritic matrix. For the term to be meaningful, the final microstructure desired or the time-temperature cycle used must be specified. 给予铸态灰铁或球墨铸铁以产生基本铁素体基体的处理。为了使该术语有意义，必须指定所需的最终微观结构或使用的时间-温度循环。 |
| Guided bend | 导向弯曲 |
The bend obtained by use of a plunger to force the specimen into a die in order to produce the desired contour of the outside and inside surfaces of the specimen. 通过使用柱塞将试样压入模具中获得的弯曲，以产生试样外表面和内表面所需的轮廓。 |
| Rolled thread | 滚制螺纹 |
A thread formed by plastically deforming the surface of the blank rather than by cutting operations. Increases fatigue life and thread strength, but is not possible (or perhaps economical) on larger sizes. 通过塑性变形坯料表面而不是通过切割操作形成的螺纹。增加疲劳寿命和螺纹强度，但不太可能（或者说是经济上不太可能）用于较大的尺寸。 |
| Coextrusion | 复合挤压 |
The simultaneous extrusion through the same die of two or more materials in combination. 通过同一模具同时挤出两种或多种材料的组合。 |
| Bearing strain | 轴承应变 |
The ratio of the deformation of the bearing hole, in the direction of the applied force, to the pin diameter in a bearing test. 轴承孔在作用力方向上的变形与轴承测试中销直径的比值。 |
| Wrap-around bend | 环绕弯曲 |
The bend obtained when a specimen is wrapped in a closed helix around a cylindrical mandrel. This term is sometimes applied to a semiguided bend of 180° or less. 当试样缠绕在圆柱形心轴周围的闭合螺旋中时获得的弯曲。该术语有时适用于180°或更小的半导弯曲。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Surface roughness (roughness) | 表面粗糙度 |
The small-scale, irregular peaks and troughs in a solid surface which are quantified using a surface analyser. Roughness may be a consequence of wear and corrosion, or of the manufacturing process. It leads to increased friction in solid– solid contact or fluid flow over a surface. Errors of form and waviness are excluded, but surface texture includes roughness and waviness. Surface topography incorporates the small-scale, three-dimensional geometry of a surface including surface roughness, machined, and etched features, typically at sub-mm scales. 固体表面中的小尺度不规则峰谷，使用表面分析仪进行量化。粗糙度可能是磨损和腐蚀或制造过程的结果。它会导致表面上的固-固接触或流体流动中的摩擦增加。不包括形状和波纹度误差，但表面纹理包括粗糙度和波纹度。表面形貌包括表面的小尺度三维几何结构，包括表面粗糙度、机加工和蚀刻特征，通常为亚毫米尺度。 |
| Furnace | 炉 |
1. A type of combustion chamber in which solid, liquid, or gaseous fuels are burned to supply hot gases to a boiler or other process plant. Examples include the firebox, boiler furnace (steam-generating furnace), hot-air furnace, oil-fired furnace, updraught furnace, and water-cooled furnace. 2. A chamber, sometimes having a controlled atmosphere or under vacuum (vacuum furnace), for heating and melting materials. Examples include the blast furnace, direct- and indirect-arc furnaces, the induction furnace (high-frequency furnace), muffle furnace, reverberatory furnace, and solar furnace. 1.一种燃烧室，其中燃烧固体、液体或气体燃料以向锅炉或其他工艺设备供应热气。示例包括燃烧室、锅炉炉（蒸汽发生炉）、热风炉、燃油炉、上升气流炉和水冷炉。2.用于加热和熔化材料的腔室，有时具有受控气氛或真空（真空炉）。例如高炉、直接和间接电弧炉、感应炉（高频炉）、马弗炉、反射炉和太阳能炉。 |
| Two-dimensional flow | 二维流 |
A fluid flow in which the velocity at any time depends upon two spatial coordinates, such as the radial and axial locations in developing pipe flow. 一种流体流动，其中任何时候的速度取决于两个空间坐标，如发展中的管道流中的径向和轴向位置。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Sampling | 抽样 |
The process of measuring a series of values of a time-varying quantity. 测量一系列时变量值的过程。 |
| Available resource | 可用资源 |
(total resource) (Unit J) The total annual energy theoretically available from a renewable-energy source, such as ocean waves, the wind, or the total incident solar energy. （总资源）（单位J）理论上可从可再生能源（例如海浪、风或总入射太阳能）获得的年度总能量。 |
| Chilled castings | 冷铸件 |
Iron castings cooled at a rate that results in white iron (slow enough to avoid the formation of martensite, yet fast enough to prevent any silicon present from causing decomposition of cementite into iron and graphite). 铸铁件以产生白口铁的速度冷却（足够慢以避免形成马氏体，但足够快以防止任何存在的硅导致渗碳体分解成铁和石墨）。 |
| Radioactive heat (Unit J) | 放射性热（单位J） |
Thermal energy released from the nucleus of an atom such as uranium235 by fission due to the absorption of a neutron. Heat is also produced by radioactive decay. 铀235等原子核因吸收中子而裂变释放的热能。放射性衰变也会产生热量。 |
| Abrasivity | 磨蚀性 |
The extent to which a surface, particle, or collection of particles will tend to cause abrasive wear when forced against a solid surface under relative motion and under prescribed conditions. 在相对运动和规定条件下，一个表面、颗粒或颗粒集合在被迫抵靠固体表面时趋向于引起磨粒磨损的程度。 |
| Gauge pressure (Unit Pa) | 表压（单位Pa） |
The level of static pressure above the ambient pressure. 高于环境压力的静压水平。 |
| Compressor bleed | 压缩机排气 |
The removal of air before the final stage of a multistage compressor operating below design speed, to prevent the final stage from choking. 在低于设计速度运行的多级压缩机的末级之前去除空气，以防止末级阻塞。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Ferritic decarburization | 铁素体脱碳 |
Decarburization with sufficient loss of carbon to cause a lighter shade of tempered martensite and a significantly lower hardness than that of the adjacent base metal, with the presence of ferrite grains or grain boundary network under metallographic examination. 脱碳，碳损失充分，导致回火马氏体颜色较浅，硬度明显低于相邻母材，金相检查时存在铁素体晶粒或晶界网络。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Ideal critical diameter | 理想临界直径 |
(DI). Under an ideal quench condition, the bar diameter that has 50% martensite at the center of the bar when the surface is cooled at an infinitely rapid rate (that is, when H = ∞, where H is the quench severity factor). （DI）在理想淬火条件下，当表面以无限快的速度冷却时（即H=∞, 其中H是淬火严重度因子）。 |
| Honing | 珩磨 |
Honing is a controlled, low-speed sizing and surface-finishing process in which stock is removed by the shearing action to the bonded abrasive grains of a honing stone, or stick. Finish polishing of surfaces and cutting edges in which very fine abrasive powders, such as rouge, are employed. Honing is usually applied to cylindrical surfaces and lapping to flat, but the usage is not consistent. 珩磨是一种受控的低速尺寸和表面精加工工艺，其中通过对珩磨石或棒的粘结磨粒的剪切作用去除原料。表面和切削刃的精抛光，其中使用了非常细的研磨粉，例如胭脂。珩磨通常用于圆柱面，研磨至平面，但用法并不一致。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Active vibration suppression | 主动振动抑制 |
The reduction of undesirable vibration in components by feedback control. 通过反馈控制减少部件中的不良振动。 |
| Retaining clip | 固定夹 |
(R-clip, hair cotter pin) A wire clip roughly with the shape of the letter R. The straight part of the clip passes through a hole drilled into a shaft or rod such that a wheel is held in position on the shaft, or the shaft is prevented from moving axially. （R形夹，开口销）大致与字母R形状相同的线夹。线夹的直线部分穿过钻在轴或杆上的孔，从而将车轮固定在轴上，或防止轴轴向移动。 |
| Shear strain | 剪切应变 |
The tangent of the angular change, as a response to force, between two lines originally perpendicular to each other through a point in a body. Also known as shearing strain. 角变化的切线，作为对力的响应，在两条原本通过物体中的一个点相互垂直的线之间。也称为剪切应变。 |
| Plug gauge | 塞规 |
A steel gauge used to determine the dimension or dimensions of a hole. It may be straight or tapered, and is typically circular, but in principle can have any cross section. 用于确定孔的尺寸的钢制量规。它可以是直的或锥形的，通常是圆形的，原则上可以有任何横截面。 |
| Shock load | 冲击载荷 |
The sudden application of an external force that results in a very rapid build-up of stress. 突然施加外力，导致应力迅速增加。 |
| Rivet | 铆钉 |
A short rod with a head on one end that is inserted through aligned holes in plates to be joined, after which a second head is made on the protruding shank by hammering or forming. The most common head shapes are flat, domed, and inverse conical. In an array, the rivet pitch is the distance between the centres of adjacent rivets. Failure may occur by different mechanisms or modes. A one piece fastener consisting of a head and a body and used for fastening two or more pieces together by passing the body through a hole in each piece and then forming a second head on the body end. It cannot be removed except by taking off the head. 一种一端有头的短杆，插入待连接板上对齐的孔中，然后通过锤击或成型在突出的杆身上制作第二个头。最常见的头部形状是扁平、圆顶和倒锥形。在阵列中，铆钉间距是相邻铆钉中心之间的距离。故障可能由不同的机制或模式发生。一种一体式紧固件，由头部和主体组成，用于将两个或多个部件紧固在一起，方法是将主体穿过每个部件上的孔，然后在主体端部形成第二个头部。除非取下头部，否则无法移除。 |
| Black annealing | 黑退火 |
Box annealing or pot annealing ferrous alloy sheet, strip, wire to impart a black color to the oxidized surface. 对铁合金板、带、线进行箱式退火或罐式退火，使氧化表面呈黑色。 |
| Durometer hardness | 硬度计硬度 |
Measure of the indentation hardness of plastics. It is the extent to which a spring-loaded steel indenter protrudes beyond the pressure foot into the material. 塑料压痕硬度的测量。它是弹簧加载的钢压头超出压力脚伸入材料的程度。 |
| Nanotechnology | 纳米技术 |
The science and engineering of materials that have been structured on length scales of 1–100 nm, resulting in modified physical properties owing to changes in the ratio of surface area to volume (atoms on surfaces having different symmetry from those in the bulk) and because many of the fundamental physical processes that underpin the properties of materials have a characteristic length scale of a few nm, so that alteration of microstructure at the nm level alters the bulk properties. 材料科学与工程，其结构长度为1-100nm，由于表面积与体积之比的变化（表面上的原子与体中的原子具有不同的对称性），并且支撑材料性质的许多基本物理过程具有几纳米的特征长度尺度，因此改变纳米级微观结构会改变体性质。 |
| International System of Units | 国际单位制 |
(SI system of units, Le Système international d’unités) The standard system of units now used almost universally in science and engineering except in the United States. The definitive reference on the SI is a booklet published by the International Bureau of Weights and Measures, often referred to as the BIPM SI Brochure. There are seven base units: metre (symbol m) for length; kilogram (kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred.(kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred. （国际单位制，Le Système international d\\\'unités）目前美国除外，在科学和工程中几乎是普遍使用的标准单位制。SI的最终参考是国际度量衡局出版的小册子，通常称为BIPM SI小册子。有七个基本单位：米（符号m）表示长度；质量为千克（kg）；物质量的摩尔（mol）；时间为秒；开尔文（K）表示温度；电流为安培（A）；而坎德拉（cd）表示发光强度。新的国际单位制定义于2019年5月20日生效，该定义基于自然界的普遍常数（也称为基本物理常数：阿伏伽德罗常数、玻尔兹曼常数和普朗克常数）。这些常数的值也进行了少量调整。除了基本单位外，还有22个相干导出单位，包括平面角的弧度（rad）、立体角的斯特拉迪安（sr）、频率的赫兹（Hz）、力的牛顿（N）、压力的帕斯卡（Pa）、能量、功和热量的焦耳（J）以及功率和辐射通量的瓦特（W）。建议的做法是避免N/mm²、MN/m²等组合。 |
| Condensing boiler | 冷凝锅炉 |
A relatively small industrial or domestic boiler that burns sulfur-free natural gas so that the products of combustion do not contain sulfuric acid and can be allowed to condense on heat-transfer surfaces without danger of corrosion. 一种相对较小的工业或家用锅炉，燃烧无硫天然气，因此燃烧产物不含硫酸，并且可以在传热表面上冷凝而没有腐蚀的危险。 |
| Uniform elongation | 均匀伸长 |
The elongation at maximum load and immediately preceding the onset of necking in a tension test. 在拉伸试验中，在最大载荷下和颈缩开始之前的伸长率。 |
| Impact strength | 冲击强度 |
The resiliency or toughness of a solid as measured by impact energy. 用冲击能量测量的固体的弹性或韧性。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Pin or mandrel | 销或心轴 |
In bend testing, the plunger or tool used in making semiguided, guided, or wrap-around tests to apply the bending force to the inside surface of the bend. In free bends or semiguided bends to an angle of180°, a shim or block of the proper thickness may be placed between the legs of the specimen as bending is completed. This shim or block is also referred to as a pin or mandrel. 在弯曲测试中，用于进行半导向、导向或环绕测试以将弯曲力施加到弯曲内表面的柱塞或工具。在180°角的自由弯曲或半导向弯曲中，弯曲完成后，可在试样支腿之间放置适当厚度的垫片或垫块。该垫片或垫块也称为销或心轴。 |
| Testing machine | 试验机 |
A machine used to apply either a steady or oscillatory or impact load to a testpiece. The load may be tensile, compressive, shear, bending, or torsional. 用于向试件施加稳定或振荡或冲击载荷的机器。载荷可以是拉伸的、压缩的、剪切的、弯曲的或扭转的。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Austenitizing | 奥氏体化 |
Forming austenite by heating a ferrous alloy into the transformation range (partial austenitizing) or above the transformation range (complete austenitizing). When used without qualification, the term implies complete austenitizing. 通过将铁合金加热到转变范围（部分奥氏体化）或高于转变范围（完全奥氏体化）来形成奥氏体。当不加限定地使用时，该术语意味着完全奥氏体化。 |
| Absolute expansion | 绝对扩张 |
The true volumetric expansion of a liquid with temperature, after account is taken of any expansion of the container in which it is held. 考虑到容纳液体的容器的任何膨胀后，液体随温度的真实体积膨胀。 |
| Wallner lines | Wallner线 |
A distinct pattern of intersecting sets of parallel lines, usually producing a set of V-shaped lines, sometimes observed when viewing brittle fracture surfaces at high magnification in an electron microscope. Wallner lines are attributed to interaction between a shock wave and a brittle crack front propagating at high velocity. Sometimes Wallner lines are misinterpreted as fatigue striations. 一组相交的平行线的独特图案，通常产生一组V形线，有时在电子显微镜下高倍观察脆性断裂表面时观察到。Wallner线归因于高速传播的冲击波和脆性裂纹前沿之间的相互作用。有时Wallner线被误解为疲劳条纹。 |
| Grain refiner | 晶粒细化机 |
A material added to a molten metal to induce a finer-than-normal grain size in the final structure. 添加到熔融金属中以在最终结构中产生比正常晶粒尺寸更细的材料。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Temper embrittlement | 回火脆化 |
Brittleness that results when certain steels are held within, or are cooled slowly through, a certain range of temperature below the transformation range. The brittleness is manifested as an upward shift in ductile-to-brittle transition temperature but only rarely produces a low value of reduction in area in a smooth-bar tension test of the embrittled material. The anomalous reduction in toughness of martensitic stainless steels when tempered in the range 370–600°C. Embrittlement of alloy steels caused by holding within or cooling slowly through a temperature range just below the transformation range. Embrittlement is the result of the segregation at grain boundaries of impurities such as arsenic, antimony, phosphorus, and tin; it is usually manifested as an upward shift in ductile-to-brittle transition temperature. Temper embrittlement can be reversed by retempering above the critical temperature range, then cooling rapidly. 当某些钢保持在低于转变范围的某一温度范围内或缓慢冷却时产生的脆性。脆性表现为延性到脆性转变温度的向上移动，但在脆性材料的平滑棒材拉伸试验中，很少产生较小的面积减小值。马氏体不锈钢在370–600°C范围内回火时的韧性异常降低。合金钢的脆化是由于在低于转变范围的温度范围内保持或缓慢冷却而引起的。脆化是杂质（如砷、锑、磷和锡）在晶界处偏析的结果；它通常表现为韧脆转变温度的上升。回火脆化可以通过在临界温度范围以上重新回火，然后快速冷却来逆转。 |
| Deposit gauge | 沉积量计 |
(deposition gauge) An instrument employed in air pollution studies for measuring the amount of pollutant deposited on a given area in a given time under given conditions. （沉降计）在空气污染研究中使用的仪器，用于测量在给定条件下在给定时间内沉积在给定区域上的污染物量。 |
| Stress-intensity calibration | 应力强度校准 |
A mathematical expression, based on empirical or analytical results, that relates the stress-intensity factor to load and crack length for a specific specimen planar geometry. Also known as Kcalibration. 基于经验或分析结果的数学表达式，该表达式将特定试样平面几何形状的应力强度因子与载荷和裂纹长度联系起来。也称为K校准。 |
| Widmanstätten structure | 魏氏组织 |
A structure characterized by a geometrical pattern resulting from the formation of a new phase along certain crystallographic planes of the parent solid solution. The orientation of the lattice in the new phase is related crystallographically to the orientation of the lattice in the parent phase. The structure is readily produced in many alloys by appropriate heat treatment. 一种结构，其特征是沿母体固溶体的某些晶体学平面形成新相而形成的几何图案。新相中晶格的取向在晶体学上与母相中晶格的定向相关。通过适当的热处理，在许多合金中容易产生这种结构。 |
| Centrifugal pump | 离心泵 |
A pump into which liquid enters axially through the eye of the casing and is then accelerated through an impeller, thereby increasing both its kinetic energy and pressure before being delivered to a ring diffuser (the volute) that further increases the liquid pressure and from which it leaves. 一种泵，液体通过泵壳的眼轴向进入，然后通过叶轮加速，从而在输送到环形扩散器（蜗壳）之前增加其动能和压力，从而进一步增加液体压力并从中流出树叶。 |
| Stress cycle | 应力循环 |
The smallest segment of the stress-time function that is repeated periodically. 周期性重复的应力时间函数的最小段。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Effective yield strength | 有效屈服强度 |
An assumed value of uniaxial yield strength that represents the influence of plastic yielding on fracture test parameters. 单轴屈服强度的假设值，代表塑性屈服对断裂试验参数的影响。 |
| Strain aging | 应变时效 |
The changes in ductility, hardness, yield point, and tensile strength that occur when a metal or alloy that has been cold worked is stored for some time. In steel, strain aging is characterized by a loss of ductility and a corresponding increase in hardness, yield point, and tensile strength. 已冷加工的金属或合金在储存一段时间后发生的延展性、硬度、屈服点和抗拉强度的变化。在钢中，应变时效的特点是延性损失，硬度、屈服点和抗拉强度相应增加。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Dowel | 销钉 |
A headless cylindrical pin that fits into corresponding holes in mating components, thus ensuring relative location. A round metal or wooden pin. A pin, usually of circular shape like a cylinder, used to pin or fasten something in position temporarily or permanently. 一种圆头金属或木制圆柱销，可插入配合组件的相应孔中，从而确保相对位置，用于暂时或永久地将某物固定或固定到位。 |
| Fin neck carriage bolt | 翼颈圆头方颈螺栓 |
A plain, circular, oval head bolt with two oppositely located fins to prevent rotation. 一种普通的圆形椭圆头螺栓，有两个相对的翼片以防止旋转。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Cup washer | 杯形垫圈 |
A dished leather or neoprene washer fitted to the rod end in some piston-style pumps. 在某些活塞式泵中，安装在杆端的碟形皮革或氯丁橡胶垫圈。 |
| Screw machine | 螺丝机 |
A machine tool for high-volume manufacture of small turned components from rod or bar. 一种用棒或棒大批量制造小零件的机床。 |
| Shell hardening | 壳型硬化 |
A surface-hardening process in which a suitable steel workpiece, when heated through and quench hardened, develops a martensitic layer or shell that closely follows the contour of the piece and surrounds a core of essentially pearlitic transformation product. This result is accomplished by a proper balance among section size, steel hardenability, and severity of quench. 一种表面硬化工艺，在该工艺中，合适的钢工件在加热和淬火硬化后，会形成一层马氏体层或壳，该层或壳紧随工件的轮廓，并包围一个基本上为珠光体相变产物的核心。这一结果通过截面尺寸、钢淬透性和淬火强度之间的适当平衡来实现。 |
| Critical temperature ranges | 临界温度范围 |
Synonymous with transformation ranges, which is the preferred term. 与转换范围同义，这是首选术语。 |
| Absorption | 吸收 |
The process whereby a fluid permeates a porous solid, or a gas is dissolved by a liquid. 流体渗透多孔固体或气体被液体溶解的过程。 |
| Surface hardening | 表面硬化 |
A generic term covering several processes applicable to a suitable ferrous alloy that produces, by quench hardening only, a surface layer that is harder or more wear resistant than the core. There is no significant alteration of the chemical composition of the surface layer. The processes commonly used are carbonitriding, carburizing, induction hardening, flame hardening, nitriding, and nitrocarburizing. Use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于仅通过淬火硬化产生比型芯更硬或更耐磨的表面层的合适铁合金的几种工艺。表面层的化学成分没有显著改变。常用的工艺有碳氮共渗、渗碳、感应淬火、火焰淬火、氮化和氮碳共渗。最好使用适用的特定工艺名称。 |
| Computed path control | 计算路径控制 |
In CNC or robotics, the use of a control program to determine the required path for the tool or end effector. This required path forms the set points for the motor controllers moving the machine tool or robot. 在CNC或机器人技术中，使用控制程序来确定工具或末端执行器所需的路径。这条所需的路径形成了用于移动机床或机器人的电机控制器的设定点。 |
| Thread run-out | 螺纹耗尽 |
That portion of the threads which are not cut or rolled full depth, but which provide the transition between full-depth threads and the body or head. Officially called thread washout or vanish, although the term run-out is more popular. (Run-out is officially reserved for rotational eccentricity, as defined by total indicator readings or the like.) 未全深度切割或轧制的螺纹部分，但提供全深度螺纹与主体或头部之间的过渡。官方称之为螺纹冲蚀或消失，但术语“耗尽”更为流行。（跳动是官方为旋转偏心度保留的，由总指示器读数等定义。） |
| Corrosion fatigue | 腐蚀疲劳 |
Cracking produced by the combined action of repeated or fluctuating stress and a corrosive environment at lower stress levels or fewer cycles than would be required in the absence of a corrosive environment. 由重复或波动的应力和腐蚀环境的联合作用产生的开裂，其应力水平低于没有腐蚀环境时所需的应力水平或循环次数更少。 |
| Precipitation hardening | 沉淀硬化 |
Hardening caused by the precipitation of a constituent from a supersaturated solid solution. 因成分从过饱和固溶体沉淀而导致的硬化。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Specimen | 样品 |
A test object, often of standard dimensions or configuration, that is used for destructive or nondestructive testing. One or more specimens may be cut from each unit of a sample. 用于破坏性或无损检测的测试对象，通常具有标准尺寸或配置。可以从样品的每个单位切割一个或多个样品。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| Gear ratio | 传动比 |
For two gears in contact, the ratio of the number of teeth on the driving gear to that on the driven gear. 对于接触的两个齿轮，主动齿轮上的齿数与从动齿轮上的齿数之比。 |
| Quench annealing | 淬火退火 |
Annealing an austenitic ferrous alloy by solution heat treatment followed by rapid quenching. 通过固溶热处理然后快速淬火对奥氏体铁合金进行退火。 |
| Assembly drawing | 装配图纸 |
An engineering drawing that shows how parts are assembled to produce a component or a complete machine. It may include sections to show internal features, dimensions that are critical for assembly, manufacturing information, and part numbers. 显示零件如何组装以生产组件或整机的工程图。它可能包括显示内部特征、对装配至关重要的尺寸、制造信息和零件编号的部分。 |
| Pop rivet | 拉钉 |
A hollow rivet that enables a connexion to be made from one side only of an assembly. 一种空心铆钉，使连接只能从组件的一侧进行。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Universal joint (Hooke’s joint) | 万向节（胡克接头） |
A double-pivoted connection that allows power and torque to be transmitted between two shafts at an angle to each other. For constant driving angular velocity of the input yoke, the angular velocity of the output yoke fluctuates by amounts depending on the angle of intersection of the shafts. Speeds of the driving and driven shafts may be made identical (giving a constant-velocity joint) when an intermediate shaft, at each end of which there is a universal joint, is interposed. The driving and driven shafts must be equally inclined to the intermediate shaft, the two forks of which must lie in the same plane. 一种双枢轴连接，允许动力和扭矩以一定角度在两个轴之间传递。对于输入磁轭的恒定驱动角速度，输出磁轭的角速度根据轴的相交角度波动。当插入中间轴时，驱动轴和从动轴的速度可以相同（提供恒定速度接头），中间轴的两端都有万向节。主动轴和从动轴必须与中间轴倾斜相等，中间轴的两个叉必须位于同一平面内。 |
| Stroke | 一击 |
1. (stroke length) (Unit m) The linear distance between top dead centre and bottom dead centre of a piston in a reciprocating engine or mechanism. 2. The movement of a piston or plunger in a reciprocating machine to execute a particular function; for example, the exhaust stroke of an engine in which the exhaust gases are expelled from a cylinder. 1.（冲程长度）（单位：m）往复式发动机或机构中活塞上止点和下止点之间的线性距离。2.活塞或柱塞在往复式机器中执行特定功能的运动；例如发动机的排气冲程，其中排气从气缸中排出。 |
| Torque wrench | 扭矩扳手 |
A manual wrench which incorporates a gage or measuring apparatus of some sort to measure and display the amount of torque being delivered to the nut or bolt. All wrenches produce torque. Only a torque wrench tells how much torque. A socket wrench or ring spanner that can be set to allow a specific torque to be applied to a nut or bolt head. 一种手动扳手，包括某种量规或测量装置，用于测量和显示传递至螺母或螺栓的扭矩量。所有扳手都产生扭矩。只有扭矩扳手才能显示扭矩大小。一种套筒扳手或梅花扳手，可设置为允许对螺母或螺栓头施加特定扭矩。 |
| Differential heating | 差动加热 |
Heating that intentionally produces a temperature gradient within an object such that, after cooling, a desired stress distribution or variation in properties is present within the object. 加热有意在物体内产生温度梯度，从而在冷却后，在物体内出现所需的应力分布或特性变化。 |
| Transfer machines | 转印机 |
These specialized machine tools are used to perform various machining operations on parts or parts in fixtures as the parts are moved along on an automatic conveyor which is part of the machine tool set-up. In a set-up, the parts can move in a straight line from their entry point to their exit point, or the setup may be constructed in a U-shape so that the parts are expelled near where they start. 当零件在自动输送机上移动时，这些专用机床用于对零件或夹具中的零件执行各种加工操作，自动输送机是机床设置的一部分。在设置中，零件可以从其入口点直线移动到其出口点，或者设置可以构造为U形，以便零件在其起点附近排出。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Blow moulding | 吹塑 |
The manufacture of hollow polymer objects (e.g. bottles) by expanding, with internal air pressure, a tube sealed at one end (parison) against the walls of a cavity mould. 通过使用内部气压使一端密封的管子（型坯）靠在型腔模具的壁上膨胀来制造中空聚合物物体（例如瓶子）。 |
| Shore hardness | 肖氏硬度 |
A measure of the hardness of materials such as elastomers, plastics, and rubbers determined using a Shore durometer which measures the penetration depth of a hardened steel rod (the indenter) 1.1–1.4 mm in diameter into the test material for a given force applied rapidly with a calibrated spring. There are two main indenter designs: type A (for softer materials) for which the end of the rod is a truncated 35° cone tapering to a diameter of 0.79 mm, and type D (harder materials) for which the end is a 30° cone with a 0.1 mm radius tip. The spring force is 8.05 N for type A and 44.45 N for type D. The hardness value is related to the penetration depth (limited to a maximum of 2.5 mm) such that for zero penetration the hardness is 100 and for maximum penetration the hardness is zero. The relevant standards are ISO 48-1, 48-4, and 48-7. Shore hardness values of selected materials are as follows: ABS 100, cellulose acetate 50–95, high-density polyethylene 60–70, low density polyethylene 40–50, polymethylmethacrylate 90–99, PTFE 50–65, and plasticized PVC 15–70. 使用肖氏硬度计测量弹性体、塑料和橡胶等材料的硬度，肖氏硬度仪测量直径为1.1–1.4mm的硬化钢棒（压头）在用校准弹簧快速施加的给定力下渗入试验材料的深度。有两种主要的压头设计：A型（适用于较软的材料），其杆端为截头35°锥形，逐渐变细至直径0.79 mm；D型（较硬的材料），端部为30°锥形，尖端半径为0.1mm。A型的弹簧力为8.05N，D型为44.45N。硬度值与渗透深度相关（最大限制为2.5mm），因此，对于零渗透，硬度为100，对于最大渗透，硬度是零。相关标准为ISO 48-1、48-4和48-7。所选材料的肖氏硬度值如下：ABS100、醋酸纤维素50-95、高密度聚乙烯60-70、低密度聚乙烯40-50、聚甲基丙烯酸甲酯90-99、PTFE50-65和塑化PVC15-70。 |
| Austenite-stabilizer | 奥氏体稳定剂 |
Alloying element expanding the γ-phase field in the corresponding phase diagram, which manifests itself in a decrease of the A3 temperature and an increase of the A4 temperature in binary alloys Fe–M as well as in a decrease of A1 temperature in ternary alloys Fe–C–M (M is an alloying element). The solubility of austenite-stabilizers in ferrite is much lower than in austenite. Under the influence of austenite-stabilizers, austenite can become thermodynamically stable down to room temperature. 合金元素扩展了相应相图中的γ相场，这表现为二元合金Fe-M中A3温度的降低和A4温度的升高，以及A1温度的降低三元合金Fe–C–M（M是合金元素）。奥氏体稳定剂在铁素体中的溶解度远低于在奥氏体中的溶解度。在奥氏体稳定剂的影响下，奥氏体可以在低至室温时变得热力学稳定。 |
| Grinding stress (Unit Pa) | 磨削应力（单位Pa） |
The residual stresses left in the surface of a component after grinding, owing to non-uniform cooling from the high surface temperatures produced. 由于产生的高表面温度造成的不均匀冷却，磨削后留在部件表面的残余应力。 |
| Thermoelectric material | 热电材料 |
A material in which any of the thermoelectric phenomena, such as the Peltier, Seebeck, and Thomson effects, are especially strong. 一种热电现象特别强烈的材料，如珀尔帖效应、塞贝克效应和汤姆森效应。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Maximum stress-intensity factor (Kmax) | 最大应力强度因子（Kmax） |
The maximum value of the stress-intensity factorin a fatigue cycle. 疲劳循环中应力强度因子的最大值。 |
| Imperial system | 英制单位体系 |
The units of measurement developed in the UK. Formerly known as the fps system, which is an abbreviation for the ‘foot-pound-second system of units. 英国开发的计量单位。以前称为fps系统，是“英尺-磅-秒（foot-pound-second）单位制”的缩写。 |
| Flame straightening | 火焰矫直 |
Correcting distortion in metal structures by localized heating with a gas flame. 通过使用气体火焰进行局部加热来纠正金属结构的变形。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Stiffness | 刚度 |
(1) The ability of a metal or shape to resist elastic deflection.(2) The rate of stress increase with respect to the rate of increase in strain induced in the metal or shape; the greater the stress required to produce a given strain, the stiffer the material is said to be. （1）金属或形状抵抗弹性变形的能力。（2）所述应力增加速率相对于在所述金属或形状中诱导的应变增加速率；产生给定应变所需的应力越大，材料就越硬。 |
| Rotary valve (rotating valve) | 旋转阀 |
A cylindrical or conical plug in which there is a transverse hole through which fluid can flow when the hole is aligned with the adjacent piping. 一种圆柱形或锥形塞，其中有一个横向孔，当该孔与相邻管道对齐时，流体可通过该孔流动。 |
| Lathe | 车床 |
A machine tool in which work, gripped in the headstock, is rotated against the cutting tool to produce turned, bored, faced, or threaded components. 一种机床，其中夹持在主轴箱中的工件靠着切削工具旋转，以生产车削、钻孔、端面或螺纹部件。 |
| Compression failure | 压缩失败 |
The reduction or removal of a component’s load-bearing capacity in compression, caused by buckling, fracture, crease formation in fibre composites, etc. 由纤维复合材料中的屈曲、断裂、折痕形成等引起的部件在压缩中的承载能力的降低或消除。 |
| Bearing area | 承载面积 |
The product of the pin (or hole) diameter and specimen thickness in a bearing test. (bearing surface) (Unit m²) The projected area of a hole, such as a rivet hole, that carries a transverse load. 轴承测试中销（或孔）直径和试样厚度的乘积。（承载面）（单位m²）承载横向载荷的孔（例如铆钉孔）的投影面积。 |
| Specific heat capacity | 比热容 |
The heat necessary to raise the temperature of 1 kg of a substance by 1 K. It is measured in J/(kg K). 将1千克物质的温度升高1K所需的热量。单位为J/（kg K）。 |
| Yield point (Unit Pa) | 屈服点（单位Pa） |
The first stress in a material, usually less than the maximum attainable stress, at which an increase in strain occurs without an increase in stress. Only certain metals—those which exhibit a localized, heterogeneous type of transition from elastic to plastic deformation—produce a yield point. If there is a decrease in stress after yielding, a distinction may be made between upper and lower yield points. The load at which a sudden drop in the flow curve occurs is called the upper yield point. The constant load shown on the flow curve is the lower yield point. (yield strength, yield stress, Rel, Rel) The stress at which the onset of permanent (plastic) deformation (yielding) occurs in a body under increasing loading. In some materials, a yield-point phenomenon occurs in which stress falls on initial yielding and plastic deformation continues without increase in stress as strain increases further. The yield criterion is the combination of normal and shear stresses which produces yielding under multiaxial loading. 材料中的第一应力，通常小于可达到的最大应力，在该应力下应变增加而应力不增加。只有某些金属——表现出从弹性变形到塑性变形的局部、非均匀类型的金属——才会产生屈服点。如果屈服后应力降低，可区分上屈服点和下屈服点。流量曲线突然下降时的荷载称为上屈服点。流量曲线上显示的恒定载荷为较低屈服点。（屈服强度，屈服应力，Rel）在不断增加的载荷下，物体发生永久（塑性）变形（屈服）时的应力。在某些材料中，会出现屈服点现象，即应力在初始屈服时下降，随着应变进一步增加，塑性变形继续，而应力没有增加。屈服准则是在多轴载荷下产生屈服的正应力和剪应力的组合。 |
| Threshold stress for stress-corrosion cracking (σth) | 应力腐蚀开裂阈值应力（σth） |
An experimentally determined critical gross-section stress below which stress-corrosion cracking will not occur under specified test conditions. 实验确定的临界总截面应力，低于该应力，在规定的试验条件下不会发生应力腐蚀开裂。 |
| Root diameter (Unit m) | 根部直径（单位：m） |
The diameter of the circle passing through the roots of teeth in gear teeth or screw threads. 穿过齿轮齿或螺纹中齿根的圆的直径。 |
| Celsius | 摄氏度 |
The temperature scale based on the freezing point of water (0ºC) and the boiling point of water (100ºC). The interval between these points is divided into 100 degrees. The scale was devised by Anders Celsius. 基于水的冰点（0ºC）和水的沸点（100ºC）的温标。这些点之间的间隔被划分为100度。这个比例是由安德斯·摄氏设计的。 |
| Temperature factor | 温度系数 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. Accounts for the effects of thermal expansion and the temperature-induced change in the velocity of sound. 用于螺栓应力或应变超声波测量的校准常数。说明了热膨胀和温度引起的声速变化的影响。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Centrifugal | 离心式 |
Acting or moving in a direction away from the axis of rotation of a rotating body. 沿远离旋转体的旋转轴的方向作用或移动。 |
| PSI (pounds per square inch) | PSI（磅/平方英寸） |
Pressure measurement. Psia (pounds per square inch absolute) measures actual pressure with no allowance for atmospheric pressure. Psig (pounds per square inch gauge) measures pressure with the gauge set to zero (0) at atmospheric pressure (14.7 psia). In other words psig = psia – 14.7. 压力测量。Psia（绝对磅/平方英寸）测量实际压力，不考虑大气压力。Psig（磅/平方英寸表压）在大气压（14.7 psia）下，将表压设置为零（0）时测量压力。换句话说，psig=psia–14.7。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Fatigue notch factor (Kf) | 疲劳缺口系数（Kf） |
The ratio of the fatigue strength of an unnotched specimen to the fatigue strength of a notched specimen of the same material and condition; both strengths are determined at the same number of stress cycles. 无缺口试样的疲劳强度与相同材料和条件的有缺口试样的疲劳强度之比；两种强度都是在相同数量的应力循环下确定的。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Compression fitting | 压缩接头 |
A screwed joint for pipework made resistant to leakage by permanent deformation of a closely-fitting ring, called a ferrule or olive, on tightening. 一种用于管道的螺纹接头，通过紧密配合的环（称为套圈或橄榄形）在拧紧时的永久变形来防止泄漏。 |
| Minor diameter | 螺纹小径 |
On a straight thread, the diameter of the imaginary cylinder which just touches the root of an external thread or the crest of an internal thread. 在直螺纹上，仅接触外螺纹根部或内螺纹顶部的假想圆柱体的直径。 |
| Normalizing | 正火 |
Heating a ferrous alloy to a suitable temperature above the transformation range and then cooling in air to a temperature substantially below the transformation range. 将铁合金加热至高于转变范围的合适温度，然后在空气中冷却至基本低于转变范围的温度。 |
| Physical properties | 物理性质 |
Properties of a material the determination of which does not involve the deformation or destruction of the specimen—for example, density, electrical conductivity, coefficient of thermal expansion, magnetic permeability, and lattice parameter. Does not include chemical reactivity or the properties more appropriately regarded as mechanical properties. 不涉及试样变形或破坏的材料特性，例如密度、电导率、热膨胀系数、磁导率和晶格参数。不包括化学反应性或更适当地视为机械的性质。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Process annealing | 中间退火 |
An imprecise term denoting various treatments used to improve workability. For the term to be meaningful, the condition of the material and the time-temperature cycle used must be stated. 一个不精确的术语，表示用于改善可加工性的各种处理方法。为了使术语有意义，必须说明材料的条件和使用的时间-温度循环。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Cellular materials | 蜂窝材料 |
There are three broad classes of materials that have a sponge-like structure containing many small closed or open (interlinked) pores or cells. Natural cellular materials include bone, cork, sponge, and wood, and have numerous well-known uses. Wide ranges of cellular plastics are produced using blowing or foaming agents, such as air, ammonium carbonate, sodium bicarbonate, etc., to create pores during the processing of thermoplastic or thermosetting polymers. Rigid foams have moderate compressive strength and can be moulded and machined. 有三大类材料具有海绵状结构，包含许多小的封闭或开放（互连）孔或细胞。天然多孔材料包括骨骼、软木、海绵和木材，有许多众所周知的用途。使用发泡剂或发泡剂（如空气、碳酸铵、碳酸氢钠等）生产各种泡沫塑料，以在热塑性或热固性聚合物加工过程中产生孔隙。硬质泡沫具有中等抗压强度，可模制和机加工。 |
| Reduction in area (RA) | 缩小面积（RA） |
The difference between the original cross-sectional area of a tensile specimen and the smallest area at or after fracture as specified for the material undergoing testing. Also known as reduction of area. 拉伸试样的原始横截面积与试验材料断裂时或断裂后的最小面积之间的差值，也称为减少面积。 |
| Fastener with reduced shank | 短柄紧固件 |
Finished fastener with a shank diameter of ds ≈ d2. 柄径为ds≈d2的紧固件。 |
| Knoop hardness test | 努氏硬度试验 |
An indentation-hardness test using calibrated machines to force a rhombic-based pyramidal diamond indenter having specified edge angles, under specified conditions, into the surface of the material under test and to measure the long diagonal after removal of the load. An indentation hardness test in which the indenter is an elongated diamond pyramid that gives an impression in the form of a parallelogram, in which the longer diagonal is about seven times the shorter. Used for studies of anisotropy in solid materials. 使用校准机器进行的一种压痕硬度试验，在规定条件下，将具有规定边缘角的菱形棱锥金刚石压头压入受试材料表面，并在移除荷载后测量长对角线。其中压头是一个细长的菱形棱锥，以平行四边形的形式给出压痕，其中较长的对角线约为较短的七倍。用于研究固体材料的各向异性。 |
| Elastic recovery | 弹性恢复 |
Amount the dimension of a stressed elastic material returns to its original (unstressed) dimension on release of an applied load. In hardness testing, the shortening of the original dimensions of the indentation upon release of the applied load. 在释放施加的载荷时，受应力弹性材料的尺寸恢复到其原始（无应力）尺寸的量。在硬度测试中，当释放所施加的载荷时，压痕的原始尺寸缩短。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Shoulder screw | 轴肩螺钉 |
A screw having two or more diameters or shoulders and commonly used for supporting levers and other machine parts that have to operate freely. 一种具有两个或两个以上直径或轴肩的螺钉，通常用于支撑杠杆和其他必须自由操作的机器部件。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Destructive testing | 破坏性测试 |
Measurement of the mechanical properties of a material, component, or structure, by increased loading until the sample fails by fracture, collapse, or buckling. 通过增加载荷测量材料、部件或结构的机械性能，直到样品因断裂、塌陷或屈曲而失效。 |
| Mole number (N) | 摩尔数（N） |
The number of moles in a given mass m of a substance, equal to m divided by the molar mass of the substance. 摩尔数物质给定质量m中的摩尔数，等于m除以物质的摩尔质量。 |
| Load factor (F) | 负载系数（F） |
The ratio between an increase in bolt tension and the external load which has caused the increase. Factors reflecting the probability of an increase in load in a shear joint. Used in load and resistant factor design. 螺栓张力增加与导致增加的外部载荷之间的比率。反映剪切接缝中荷载增加概率的系数。用于载荷和阻力系数设计。 |
| Computer control | 电脑控制 |
The control of an engineering device or system by pre-programmed computer or by feedback control. 通过预编程计算机或反馈控制对工程设备或系统进行控制。 |
| Deformation (Unit 1/s) | 变形（单位1/s） |
A change in the form of a body due to stress, thermal change, change in moisture, or other causes. In solid mechanics, any change, reversible (elastic) or permanent (plastic), in the shape or size of parts of a body, or the whole body, caused by external or internal loading. It includes extension, compression, bending, and twisting. The same state of deformation in a body can appear as different combinations of elongation and shear. To state how much of the total strain is shear, it is split into dilatation and deviatoric components, the former changing volume but not shape, the latter shape but not volume. 由于压力、热变化、水分变化或其他原因导致的身体形态变化。在固体力学中，由外部或内部载荷引起的身体各部分或整个身体的形状或大小的任何可逆（弹性）或永久（塑性）变化。它包括拉伸、压缩、弯曲和扭曲。物体中相同的变形状态可以表现为伸长和剪切的不同组合。为了说明总应变中有多少是剪切，将其分为膨胀分量和偏差分量，前者改变体积但不改变形状，后者改变形状但不改变体积。 |
| Creep modulus (Unit Pa) | 蠕变模量（单位Pa） |
The ratio of stress/strain at a chosen strain level obtained from creep tests, often plotted against time to show changes in stiffness. 从蠕变测试中获得的选定应变水平下的应力/应变比，通常随时间绘制以显示刚度的变化。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Subcritical annealing | 不完全退火 |
A process anneal performed on ferrous alloys at a temperature below Ac1. 在低于Ac1的温度下对铁合金进行的工艺退火。 |
| Working load (Unit N) | 工作负荷（单位：N） |
The tension in a bolt in use; tension produced by a combination of Residual preload and a portion (usually) of any External load. The Joint diagram is usually used to predict the approximate working load a fastener will see in service. The load under which a component or structure is designed to operate under normal conditions. 螺栓在使用中的张力；残余预载荷和部分（通常）任何外部载荷的组合产生的张力。连接图通常用于预测紧固件在使用中的近似工作载荷。部件或结构设计为在正常条件下运行的荷载。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Crank pin | 曲柄销 |
It is a short shaft parallel to the axis of the crankshaft but radially offset from it, to which is attached the big end of a connecting rod in a bearing. Sometimes the crank pin is supported at one end only (a wrist pin) but in built-up or one-piece forged crankshafts, the crank pin is supported by thick plates (crank arms, crank webs) at either end. 它是一个短轴，平行于曲轴的轴线，但径向偏移，轴承中连杆的大端连接到该短轴上。有时曲柄销仅在一端支撑（腕销），在组合式或整体锻造曲轴中，曲柄销在两端由厚板（曲柄臂、曲柄腹板）支撑。 |
| Metallurgy | 冶金 |
The study of the atomic, crystallographic, microstructural, mechanical, and physical properties of metallic elements and alloys and their applications. 研究金属元素和合金的原子、晶体学、微观结构、机械和物理特性及其应用。 |
| Mole (mol) | 摩尔（mol） |
The base unit of the amount of substance in the SI system. It was previously defined as the amount of substance of a system that contains as many elementary entities as there are atoms in 0.012 kg of carbon-12. From 20 May 2019 it has been defined as the amount of substance containing exactly 6.022 140 76 × 1023 elementary entities. SI国际单位制中物质量的基本单位。此前，它被定义为一个系统中的物质量，该系统包含的基本实体数量与0.012千克碳-12中的原子数量相同。从2019年5月20日起，它已被定义为包含6.02214076×1023个基本实体的物质量。 |
| Diagonal pitch (Unit m) | 对角线间距（单位米） |
The distance, when components in an assembly are staggered, between the position of a component in one row or column and the position of the corresponding component in the next row or column. The term is applied to rivets, turbine or compressor blades in a cascade, vortex generators on the surface of a wing, etc. 当部件中的零部件交错时，一行或一列中零部件的位置与下一行或下一列中相应零部件的位置之间的距离。该术语适用于铆钉、叶栅中的涡轮或压缩机叶片、机翼表面的涡流发生器等。 |
| Multiple threaded screw | 多螺纹螺钉 |
A screw with two or more threads cut around the periphery of the workpiece to provide an increased lead with a specified pitch. 一种螺钉，具有围绕工件周边切割的两个或多个螺纹，以提供具有指定螺距的增加的导程。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Gasket stress | 垫片应力 |
The contact stress exerted on the gasket by the joint members. 连接件施加在垫片上的接触应力。 |
| Slenderness ratio | 长细比 |
The effective unsupported length of a uniform column divided by the least radius of gyration of the cross-sectional area. 均匀柱的有效无支撑长度除以横截面积的最小回转半径。 |
| O-ring (O-ring seal) | O形圈（O形密封圈） |
A toroidal ring of synthetic rubber seated in a groove machined into a flat or cylindrical surface to act as a seal. 一种环形合成橡胶环，位于加工成平面或圆柱表面的凹槽中，起密封作用。 |
| Torque coefficient | 扭矩系数 |
1. (KT) For a propeller of diameter D, a non-dimensional parameter defined by KT = T/ρΩ2D5 where Ω is the rotational speed (in rad/s) and ρ is the fluid density. 2. (CT) An alternative to (1) for a wind turbine, defined by CT = 2T/ρV2AR where V is the wind speed, A is the swept area of the blades, and R is the blade radius. 3. (K) An empirical coefficient used to calculate the torque T required to achieve an axial load F in a bolt according to T = KFd where d is the nominal bolt diameter. 1.（KT）对于直径为D的螺旋桨，由KT=T/ρΩ2D5定义的无量纲参数，其中Ω是转速（单位为rad/s），ρ是流体密度。2.（CT）对于风力涡轮机（1）的替代方案，由CT=2T/ρV2AR定义，其中V是风速，a是叶片的扫掠面积，R是叶片半径。3.（K）经验系数，用于根据T=KFd计算螺栓中实现轴向载荷F所需的扭矩T，其中d是螺栓标称直径。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Sound pressure (Unit μPa) | 声压（单位：μPa） |
The instantaneous deviation of pressure from the ambient pressure caused by the passage of a sound wave, which can be measured by a microphone in air and a hydrophone in water. 声波传播引起的压力与环境压力的瞬时偏差，可通过空气中的麦克风和水中的水听器测量。 |
| Plane strain | 平面应变 |
The stress condition in linear-elastic fracture mechanics in which there is zero strain in a direction normal to both the axis of applied tensile stress and the direction of crack growth (i.e., parallel to the crack front); most nearly achieved in loading thick plates along a direction parallel to the plate surface. Under plane-strain conditions, the plane of fracture instability is normal to the axis of the principal tensile stress. 线弹性断裂力学中的应力条件，其中在垂直于施加拉应力轴和裂纹扩展方向（即平行于裂纹前沿）的方向上存在零应变；最接近于沿平行于板表面的方向加载厚板。在平面应变条件下，断裂失稳平面垂直于主拉应力轴。 |
| Total combustion air (Unit kg/s) | 总燃烧空气（单位：kg/s） |
1. The combination of the stoichiometric flow of air required for combustion together with any excess air. 2. The flow of fresh air into a boiler plus any flue gas recirculated. 1.燃烧所需的化学计量空气流与任何过量空气的组合。2.进入锅炉的新鲜空气流加上再循环的任何烟气。 |
| GGas turbine | G燃气轮机 |
An engine in which air, compressed by a multi-stage axial compressor and/or one or more centrifugal compressors, flows into a combustion chamber (or chambers) where fuel is burned and the hot gases then drive an axial turbine which powers the compressor. 由多级轴流压缩机和/或一个或多个离心压缩机压缩的空气流入燃烧室（或多个燃烧室），在燃烧室中燃烧燃料，然后热气体驱动轴流涡轮，为压缩机提供动力。 |
| Shrink ring | 预紧环 |
A ring, which is expanded by heating, is placed around an assembly of parts, and then contracts upon cooling to hold the assembly in place. 通过加热膨胀的环被放置在零件组件周围，然后在冷却时收缩以将组件固定到位。 |
| Free joint | 万向节 |
The joint on a robot arm and wrist that causes the greatest end-effector movement when a specified force is applied to the end effector, i.e. that has the lowest stiffness with regard to the force. 机器人手臂和手腕上的关节，当指定的力施加到末端执行器时，会导致末端执行器的最大运动，即相对于力具有最低刚度。 |
| Residual stress (Unit Pa) | 残余应力（单位Pa） |
Stresses that remain within a body as the result of thermal or mechanical treatment or both. (internal stress) An internal-stress system found in components that have experienced elastic unloading from non-uniform plastic-strain fields during manufacture. 由于热处理或机械处理或两者兼而有之而留在物体内的应力。（内应力）在制造期间从非均匀塑性应变场经历弹性卸载的部件中发现的内应力系统。 |
| Cycle annealing | 循环退火 |
An annealing process employing a predetermined and closely controlled time-temperature cycle to produce specific properties or microstructures. 采用预定且严格控制的时间-温度循环来产生特定性能或微观结构的退火工艺。 |
| Relative humidity (ϕ) | 相对湿度（ψ） |
The ratio or percentage of the actual mass of moisture in a given volume of air at a given temperature to the maximum possible mass of moisture at the same temperature. 给定温度下给定体积空气中的实际水分质量与相同温度下的最大可能水分质量的比率或百分比。 |
| Swept volume (Unit m³) | 扫描体（单位m³) |
In the cylinder of a piston engine or other device, the volume between top and bottom dead centre positions of a piston; equal to πR2S where R is the piston radius and S is the stroke. 在活塞发动机或其他装置的气缸中，活塞上止点和下止点位置之间的体积；等于πR2S，其中R是活塞半径，S是冲程。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Ductility | 延展性 |
The ability of a material to deform plastically before fracturing. Measured by elongation or reduction in area in a tensile test, by height of cupping in a cupping test, or by the radius or angle of bend in a bend test. 材料在断裂前发生塑性变形的能力。通过拉伸试验中的伸长率或面积减少量、杯突试验中的杯突高度或弯曲试验中的弯曲半径或角度来测量。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Fracture mechanics | 断裂力学 |
The stress analysis of bodies containing cracks. The use of stressconcentration factors and other correction factors of traditional strength of materials is inadequate when flaws are present initially (or develop during loading), since fracture depends not only on stress but also the size of the crack. Traditional strength of materials stress calculations cannot predict either the safe working stress in the presence of a known flaw, or the critical size of flaw just tolerable with a given working stress. 含裂纹物体的应力分析。当初始存在缺陷（或在加载过程中形成缺陷）时，使用应力集中系数和传统材料强度的其他修正系数是不够的，因为断裂不仅取决于应力，还取决于裂纹的大小。传统的材料强度应力计算既不能预测已知缺陷存在时的安全工作应力，也不能预测给定工作应力下可容忍的缺陷临界尺寸。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Strain energy | 应变能 |
A measure of the energy absorption characteristics of a material determined by measuring the area under the stress-strain diagram. 通过测量应力-应变图下的面积确定的材料能量吸收特性的度量。 |
| Mechanical units | 机械单位 |
The units of physical quantities, the dimensions of which includemass, length, and time. 物理量的单位，其量纲包括质量、长度和时间。 |
| Guided-bend test | 导向弯曲试验 |
A test in which the specimen is bent to a definite shape by means of a punch (mandrel) and a bottom block. 用冲头（心轴）和底块将试样弯曲成一定形状的试验。 |
| Bright nitriding | 光亮氮化 |
Nitriding in a protective medium to prevent discoloration of the bright surface. 在保护介质中氮化，以防止光亮表面变色。 |
| Torque (T) (Unit N.m) | 扭矩（T）（单位：N.m） |
The twisting moment, product of force and wrench length, applied to a nut or bolt (for example). The twisting moment of a force or couple about an axis which results in torsion. 施加在螺母或螺栓（例如）上的扭矩，是力和扳手长度的乘积。力或力偶绕轴产生扭转的力矩。 |
| Fatigue striations | 疲劳条纹 |
Parallel lines frequently observed in electron microscope fractographs or fatigue-fracture surfaces. The lines are transverse to the direction of local crack propagation; the distance between successive lines represents the advance of the crack front during the one cycle of stress variation. 在电子显微镜断口图或疲劳断口表面中经常观察到平行线。这些线横向于局部裂纹扩展方向；连续线之间的距离表示在一个应力变化周期内裂纹前沿的前进。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Finishing temperature | 终轧温度 |
The temperature at which hot working is completed. 完成热加工的温度。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| Athermal transformation | 非热变化 |
A reaction that proceeds without benefit of thermal fluctuations; that is, thermal activation is not required. In contrast, a reaction that occurs at constant temperature is an isothermal transformation; thermal activation is necessary in this case and the reaction proceeds as a function of time. 在没有热波动的情况下进行的反应；也就是说，不需要热激活。相反，在恒温下发生的反应是等温转变。在这种情况下，热活化是必要的，并且反应作为时间的函数进行。 |
| Design load (Unit N) | 设计荷载（单位N） |
The greatest load that a component or structure is expected to experience under normal operating conditions. 部件或结构在正常运行条件下预期承受的最大负载。 |
| A-basis | A-基础 |
Mechanical property value above which at least 99% of the population of values is expected to fall, with a confidence of 95%. Also called A-allowable. 机械性能值超过该值时，至少99%的值预计会下降，置信度为95%。也被称为A-容许。 |
| Radial wave equation | 径向波动方程 |
A differential equation describing the transmission of a wave in a system with radial symmetry. 描述波在径向对称系统中传输的微分方程。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Turbulent flow (turbulence) | 湍流 |
Fluid motion characterized by disorderly, rotational (i.e. vortical) three-dimensional velocity fluctuations covering a wide range of frequency and length scales. The pressure, temperature, and other fluid properties also fluctuate and the diffusion of heat, mass, and momentum is greatly enhanced. As are laminar and transitional flow, turbulent flow of a Newtonian fluid is governed by the Navier–Stokes equations which can in principle be solved by direct numerical simulation (DNS) in which all time and length scales of the fluctuating motion are resolved. 流体运动的特点是无序、旋转（即旋涡）三维速度波动，覆盖广泛的频率和长度尺度。压力、温度和其他流体特性也会波动，热、质量和动量的扩散会大大增强。与层流和过渡流一样，牛顿流体的湍流由Navier-Stokes方程控制，该方程原则上可以通过直接数值模拟（DNS）求解，在直接数值模拟中，波动运动的所有时间和长度尺度都可以求解。 |
| Macrodeviation | 宏观偏差 |
Errors from–irregular surface departures from the design profile, often caused by lack of accuracy or stiffness of the machine system. 不规则表面偏离设计轮廓的误差，通常是由于机器系统缺乏准确性或刚度造成的。 |
| Cooling stresses | 冷却应力 |
Residual stresses resulting from nonuniform distribution of temperature during cooling. 冷却过程中温度分布不均匀导致的残余应力。 |
| Time quenching | 时间淬火 |
A term used to describe a quench in which the cooling rate of the part being quenched must be changed abruptly at some time during the cooling cycle. 用于描述淬火的术语，其中被淬火零件的冷却速率必须在冷却循环的某个时间突然改变。 |