| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Temper color | 回火颜色 |
A thin, tightly adhering oxide skin that forms when steel is tempered at a low temperature, or for a short time, in air or a mildly oxidizing atmosphere. The color, which ranges from straw to blue depending on the thickness of the oxide skin, varies with both tempering time and temperature. 一种薄的、紧密粘附的氧化皮，当钢在低温或短时间内在空气或轻度氧化气氛中回火时形成。颜色范围从稻草色到蓝色，取决于氧化皮的厚度，随回火时间和温度而变化。 |
| Abrasivity | 磨蚀性 |
The extent to which a surface, particle, or collection of particles will tend to cause abrasive wear when forced against a solid surface under relative motion and under prescribed conditions. 在相对运动和规定条件下，一个表面、颗粒或颗粒集合在被迫抵靠固体表面时趋向于引起磨粒磨损的程度。 |
| Torque (T) (Unit N.m) | 扭矩（T）（单位：N.m） |
The twisting moment, product of force and wrench length, applied to a nut or bolt (for example). The twisting moment of a force or couple about an axis which results in torsion. 施加在螺母或螺栓（例如）上的扭矩，是力和扳手长度的乘积。力或力偶绕轴产生扭转的力矩。 |
| Square | 正方 |
1. A regular quadrilateral, i.e. a polygon with four equal sides and four right angles. 2. An instrument to check angles of internal and external surfaces and flatness. 1.正四边形，即具有四条等边和四个直角的多边形。2.一种检查内外表面角度和平面度的仪器。 |
| Coarse threads | 粗螺纹 |
Threads with relatively large separation between corresponding points on the threads. 螺纹上相应点之间的间距相对较大的螺纹。 |
| Hot-wire test | 热线测试 |
Method used to test heat extraction rates of various quenchants. Faster heat-extracting quenchants will permit more electric current to pass through a standard wire because it is cooled more quickly. Compare with hot-wire analyzer. 用于测试各种淬火剂的热提取率的方法。与热线分析仪相比，更快的热提取淬火剂将允许更多电流通过标准导线，因为标准导线冷却更快。 |
| Vacuum relief valve | 真空安全阀 |
A valve that admits gas to a system under vacuum, should the degree of vacuum become excessive. 如果真空度过高，允许气体在真空下进入系统的阀门。 |
| Machine tool | 机床工具 |
A powered machine, such as a borer, grinder, lathe, milling machine or planer, used for cutting and shaping metal, plastics, composites, etc. (machining). A machining centre is a CNC machine tool working about several axes, having a stock of tools and automatic tool changing ability, which is capable of diverse machining operations under automated control. 一种动力机器，如钻孔机、磨床、车床、铣床或刨床，用于切割和成形金属、塑料、复合材料等（机加工）。加工中心是围绕多个轴工作的CNC机床，具有刀具库存和自动换刀能力，能够在自动化控制下进行各种加工操作。 |
| Thumb screw | 蝶形螺钉 |
A type of screw having a winged or knurled head for turning by hand when a quick and light clamping effect is desired. 一种螺钉，具有翼形或滚花头，当需要快速、轻夹紧效果时，可手动转动。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Kinetic energy | 动能 |
Energy that an object possesses because it is in motion. It is the energy given to an object to set it in motion. On impact, it is converted into other forms of energy such as strain, heat, sound and light. 物体因运动而拥有的能量。它是赋予物体使其运动的能量。撞击时，它被转换成其他形式的能量，如应变、热、声和光。 |
| Wind velocity (Unit m/s) | 风速（单位：m/s） |
1. In the Earth’s atmosphere, a vector quantity that quantifies both the magnitude of the wind speed and its direction at a given altitude and location, conveniently represented in the hodograph plane. For convenience, the unit kph is often used. It could in principle also include information about large- and small-scale unsteadiness. Spatial variation in wind velocity, either with altitude or in a horizontal plane, is termed wind shear. 2. The airspeed in the working section of a wind tunnel. 1.在地球大气层中，一种矢量量，用于量化给定高度和位置处的风速大小及其方向，方便地用速度计平面表示。为方便起见，通常使用单位kph。原则上，它还可以包括关于大尺度和小尺度不稳定性的信息。风速随高度或水平面的空间变化称为风切变。2.风洞工作段的空速。 |
| Load ratio, R | 负载比R |
In fatigue, the algebraic ratio of the minimum to maximum load in a fatigue cycle, that is, R = Pmin/Pmax. Also known as stress ratio. 在疲劳中，疲劳循环中最小载荷与最大载荷的代数比，即 R= Pmin/Pmax。也称为应力比。 |
| Blowing | 吹气 |
The process by which a gas is transferred through a porous surface over which there is a gas flow. The effect is used to decrease skin friction and increase heat transfer, for example in turbine-blade cooling. 气体通过有气流的多孔表面转移的过程。该效应用于减少表面摩擦和增加传热，例如在涡轮叶片冷却的过程中。 |
| Turning | 车削 |
Turning is a machining process for generating external surfaces of revolution by the action of a cutting tool on a rotating workpiece, usually in a lathe. The rotation of a workpiece held against a cutting tool in a lathe to produce components with a circular cross section. 车削是一种机械加工过程，通常在车床上，通过刀具对旋转工件的作用产生旋转外表面。在车床中，工件靠着刀具旋转，以生产具有圆形横截面的部件。 |
| Equilibrium diagram | 平衡图 |
A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant. 在完全平衡条件下，合金系统中相场的温度、压力和成分极限的图形表示。在金属系统中，压力通常被认为是恒定的。 |
| Statistic | 统计 |
A summary value calculated from the observed values in a sample. 根据样本中的观察值计算得出的汇总值。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Abradant | 研磨剂 |
The differently sized grits of hard materials such as emery employed for grinding, polishing, etc. The abrasive grade is determined by the grit size (grit number) originally related to the hole sizes in wire sieves. 用于研磨、抛光等的硬质材料（例如金刚砂）的不同尺寸粒度。磨料等级由最初与金属丝筛孔尺寸相关的粒度（粒度数）决定。 |
| Hexagon nut | 六角螺母 |
A nut having six sides and shaped like a hexagon. 六边形的螺母。 |
| Stress-concentration factor (Kt) | 应力集中系数（Kt） |
A multiplying factor for applied stress that allows for the presence of a structural discontinuity such as a notch or hole; Kt equals the ratio of the greatest stress in the region of the discontinuity to the nominal stress for the entire section. Also known as theoretical stress-concentration factor. 施加应力的倍增系数，允许存在结构不连续性，如缺口或孔；Kt等于不连续区域的最大应力与整个截面的标称应力之比。也称为理论应力集中系数。 |
| Assembly line | 流水线 |
A system of mass production in which work is moved progressively from one operation to another, ultimately to give the final complete product. 一种大规模生产系统，其中工作逐渐从一个操作转移到另一个操作，最终得到完整产品。 |
| Complete decarburization | 完全脱碳 |
Decarburization with sufficient carbon loss to show only clearly defined ferrite grains under metallographic examination. 脱碳，具有足够的碳损失，以在金相检查下仅显示清晰定义的铁素体晶粒。 |
| Elastic recovery | 弹性恢复 |
Amount the dimension of a stressed elastic material returns to its original (unstressed) dimension on release of an applied load. In hardness testing, the shortening of the original dimensions of the indentation upon release of the applied load. 在释放施加的载荷时，受应力弹性材料的尺寸恢复到其原始（无应力）尺寸的量。在硬度测试中，当释放所施加的载荷时，压痕的原始尺寸缩短。 |
| Pressure surface | 压力面 |
The high-pressure surface of an aerofoil, turbine, or compressor blade. In normal aircraft applications, this is the lower surface of a wing. For applications, such as to high-performance motor vehicles, where the aerofoil is inverted to generate downforce, it is the upper surface. 机翼、涡轮或压缩机叶片的高压表面。在正常的飞机应用中，这是机翼的下表面。对于高性能机动车辆等应用，机翼翻转以产生下压力，它是上表面。 |
| Ballonet | 气囊 |
An airbag used in a hybrid airship. Helium gas expels air from the ballonet during ascent. Fans draw air in during descent. 混合动力飞艇中使用的安全气囊。氦气在上升过程中将空气从气囊中排出。风扇在下降过程中吸入空气。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| Turbo generator | 涡轮发电机 |
(turboset) The combination of a steam or gas turbine and an electrical generator with a single shaft or connected coaxial shafts. （汽轮发电机组）蒸汽或燃气轮机与发电机的组合，具有单轴或连接的同轴。 |
| Corrosion cell | 腐蚀电池 |
A natural ‘‘battery’’ formed when two metals having different electrical potentials (an Anode and a Cathode) are connected together in the presence of a liquid (the Electrolyte). 当两种具有不同电势的金属（阳极和阴极）在液体（电解质）存在下连接在一起时形成的天然“电池”。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Breaking stress | 断裂应力 |
The stress at failure. Also known as rupture stress. 失效时的应力。也称为破裂应力。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| High strength low alloy steels | 高强度低合金钢 |
(HSLA steels) Steels with various micro-alloying elements such as copper, nickel, chromium, molybdenum, niobium, titanium, and vanadium in small quantities that give improved strength (as high as 900 MPa) and corrosion properties compared with plain carbon steels. Improvements are due to grain refinement and precipitation hardening, better control of the chemistry during steel making, and accurate rolling temperatures. （HSLA钢）是含有各种微合金元素的钢，如少量的铜、镍、铬、钼、铌、钛和钒，与普通碳钢相比，具有更好的强度（高达900MPa）和腐蚀性能。这些改进归功于晶粒细化和沉淀硬化、炼钢过程中更好的化学控制以及精确的轧制温度。 |
| Least count | 最小计数 |
The smallest value that can be read from an instrument having a graduated scale. Except on instruments provided with a vernier, the least count is that fraction of the smallest division which can be conveniently and reliably estimated; this fraction is ordinarily one-fifth or one-tenth, except where the graduations are very closely spaced. 可从具有刻度尺的仪器中读取的最小值。除配备游标的仪器外，最小计数是可以方便可靠地估计的最小除法的分数；这个分数通常是五分之一或十分之一，除非刻度间隔非常近。 |
| Full hard | 全硬化 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state beyond which the material can no longer be formed by bending. In specifications, a full hard temper is commonly defined in terms of minimum hardness or minimum tensile strength (or, alternatively, a range of hardness or strength) corresponding to a specific percentage of cold reduction following a full anneal. For aluminum, a full hard temper is equivalent to a reduction of 75% from dead soft ; for austenitic stainless steels, a reduction of about 50 to 55%. 有色金属合金和一些铁合金的回火状态，大致对应于冷加工状态，超过该状态，材料就不能再通过弯曲形成。在规范中，完全硬质回火通常定义为与完全退火后的特定冷压下率百分比相对应的最小硬度或最小抗拉强度（或者，硬度或强度范围）。对于铝来说，完全硬回火相当于从极软状态减少75%；对于奥氏体不锈钢，减少约50%至55%。 |
| Imperial system of units | 英制单位 |
British imperial system of units) An obsolete system of units first defined in the British Weights and Measures Act of 1824. Its three base units were second (time), yard (length), and pound avoirdupois (mass). The imperial unit of capacity was the gallon. The many associated units introduced subsequently include cubic inch, cubic foot, cubic yard, pint, and quart for both liquid and dry measures of capacity (i.e. volume); ounce, hundredweight, short and long ton for avoirdupois mass; poundal for force; minute and hour for time; fahrenheit for temperature; and British thermal unit for energy. Closely related to the imperial system of units is the US customary system of units. Each imperial unit is now legally defined in terms of the metric (i.e. SI) equivalent. （英帝国单位制）1824年英国度量衡法首次定义的已被淘汰的单位制。其三个基本单位为秒（时间）、码（长度）和磅（质量）。容量的英制单位是加仑。随后引入的许多相关单位包括立方英寸、立方英尺、立方码、品脱和夸脱，用于液体和干燥容量测量（即体积）；盎司，百分之一百重量，短吨和长吨，以保证重量；磅达表示力；以分钟和小时表示时间；华氏温度；英国热能单位。与帝国单位制密切相关的是美国习惯单位制。现在，每个英制单位在法律上都是以公制（即SI）当量来定义的。 |
| Displacement | 移位 |
The distance that a chosen measurement point on a cracked specimen displaces normal to the crack plane as the crack grows. 随着裂纹扩展，裂纹试样上选定的测量点垂直于裂纹平面位移的距离。 |
| Tension | 拉伸 |
The force or load that produces elongation. 1. The condition in a bar, belt, cable, spring, string, wire, etc. that is being pulled from either end. 2. (tensile force) (unit N) The force associated with tension as in (1). It is measured by a tension meter. 伸长力产生伸长的力或载荷。1.从两端拉出的杆、带、电缆、弹簧、线、线等的状态。2.（张力）（单位N）与张力相关的力。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Heat tinting | 热着色 |
Coloration of a metal surface through oxidation by heating to reveal details of the microstructure. 通过加热氧化使金属表面着色，以揭示微观结构的细节。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Engine | 引擎 |
A machine that converts energy, including the chemical energy in a fuel and electrical energy, into mechanical energy, usually to produce power delivered through a rotating shaft or thrust. Examples include internal-combustion engines, gas and steam turbines, rocket engines, electric, hydraulic and pneumatic motors. 一种将能量（包括燃料中的化学能和电能）转换为机械能的机器，通常通过旋转轴或推力产生动力。例子包括内燃机、燃气轮机和蒸汽轮机、火箭发动机、电动、液压和气动马达。 |
| Water hammer | 水锤 |
The reflected pressure surge that occurs in a liquid flowing through a pipe, usually as a consequence of sudden closure of a valve. The surge may cause the pipe to vibrate and a hammering noise to be heard. Key factors affecting the surge amplitude are the compressibility of the liquid (especially if it contains undissolved gas) and the elasticity of the pipe wall. 在流经管道的液体中发生的反射压力波动，通常是阀门突然关闭的结果。浪涌可能导致管道振动，并听到锤击噪音。影响喘振幅度的关键因素是液体的可压缩性（特别是当其含有未溶解气体时）和管壁的弹性。 |
| Bypass flow meter | 旁通流量计 |
(shunt flow meter) A flow meter installed in a pipework bypass which may itself be part of the flow meter. An orifice plate is used to ensure a fraction of the main flow passes through the bypass. （分流流量计）安装在管道旁路中的流量计，它本身可能是流量计的一部分。孔板用于确保一部分主流通过旁路。 |
| Offset modulus | 补偿模量 |
The ratio of the offset yield stress to the extension at the offset point (plastics). 偏移屈服应力与偏移点（塑料）处延伸的比率。 |
| Tension testing | 张力测试 |
A method of determining the behavior of materials subjected to uniaxial loading, which tends to stretch the metal. A longitudinal specimen of known length and diameter is gripped at both ends and stretched at a slow, controlled rate until rupture occurs. Also known as tensile testing. 一种确定材料在单轴载荷下的行为的方法，这种载荷倾向于拉伸金属。将已知长度和直径的纵向试样夹持在两端，并以缓慢、受控的速率拉伸，直到发生断裂。也称为拉伸测试。 |
| Lockbolt | 锁紧螺栓 |
A fastener which bears a superficial resemblance to a bolt, but which engages a collar (instead of a nut) with annular grooves (instead of threads). The collar is swaged over the grooves on the male fastener to develop preload. 表面上类似于螺栓的紧固件，但与环槽（而不是螺纹）接合的轴环（而不是螺母）。套环在阳紧固件上的凹槽上锻造，以产生预紧力。 |
| Density | 密度 |
The mass per unit volume of a solid material. (mass density, ρ) (Unit kg/m³) The mass per unit volume of a substance that satisfies the continuum assumption. The reciprocal of specific volume. 固体材料每单位体积的质量。（质量密度，ρ）（单位kg/m³）满足连续统假设的物质每单位体积的质量。和比容相关联。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Residual stress (Unit Pa) | 残余应力（单位Pa） |
Stresses that remain within a body as the result of thermal or mechanical treatment or both. (internal stress) An internal-stress system found in components that have experienced elastic unloading from non-uniform plastic-strain fields during manufacture. 由于热处理或机械处理或两者兼而有之而留在物体内的应力。（内应力）在制造期间从非均匀塑性应变场经历弹性卸载的部件中发现的内应力系统。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Distortion | 扭曲 |
Any deviation from an original size, shape, or contour that occurs because of the application of stress or the release of residual stress. 由于施加应力或释放残余应力而发生的与原始尺寸、形状或轮廓的任何偏差。 |
| Supercharging | 增压 |
The process of increasing the mass flow rate of air (or air/fuel mixture) into the cylinder(s) of a piston engine using a compressor driven from the crankshaft (the supercharger). The power output is increased compared with a naturally-aspirated engine of the same capacity. The process also increases the air pressure and density to greater than ambient. In the past, most superchargers were mechanically driven from the engine’s crankshaft, but these have been largely superseded by turbochargers. 使用由曲轴（增压器）驱动的压缩机增加进入活塞式发动机气缸的空气（或空气/燃料混合物）质量流率的过程。与相同容量的自然吸气发动机相比，功率输出增加。该过程还将空气压力和密度增加到大于环境压力和密度。在过去，大多数增压器都是由发动机曲轴机械驱动的，但这些增压器在很大程度上已被涡轮增压器所取代。 |
| Mechanical metallurgy | 机械冶金 |
The science and technology dealing with the behavior of metals when subjected to applied forces. 处理金属在外力作用下的行为的科学技术。 |
| Breaking load | 断裂载荷 |
The maximum load (or force) applied to a test specimen or structural member loaded to rupture. 施加到加载到破裂的试样或结构构件上的最大载荷（或力）。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Galvanic protection | 电流保护 |
The coating on a fastener is said to provide galvanic protection if it is more anodic than the fastener and will, therefore, be destroyed instead of the fastener. Zinc plate (galvanizing) provides galvanic protection to steel fasteners, for example. 如果紧固件上的涂层比紧固件更具阳极性，则据说它可以提供电流保护，将会因此被破坏而不是紧固。例如，锌板（镀锌）为钢紧固件提供电流保护。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Dynamics | 动力学 |
The branch of mechanics that deals with objects in motion. Its two main branches are kinematics, which studies motion without regards to its cause, and kinetics, which also takes into account forces that cause motion. 力学中研究运动物体的分支。它的两个主要分支是运动学和动力学，前者研究运动而不考虑其原因，后者也考虑引起运动的力。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Wind energy (Unit kJ) | 风能（单位kJ） |
The kinetic energy associated with wind that can be converted by a wind energy conversion system (WECS) into electrical or mechanical power by a rotor, such as a multi-bladed propeller, exposed to the wind. If the air density is ρ and the wind speed is V, then the kinetic energy flux is ρV3/2. The actual wind power that can be extracted by a wind turbine intercepting a cross section of wind A is CPρAV3/2 where CP is an empirical efficiency factor termed the power coefficient. The wind-energy distribution is a histogram of the calculated wind power that can be generated annually from the windspeed frequency distribution at a given location. A windmill generates mechanical power whereas a wind turbine (wind generator) generates electrical power. The largest wind turbine, manufactured by MHI Vestas, has a power rating of 9.5 MW, a rotor diameter of 164 m, and a hub height of 105 m (the highest wind turbines have heights in the region of 190 m). A wind farm is an array of wind turbines, typically ten to several hundred, at a single location, either onshore or offshore. Energy derived from wind is a major contributor to sustainable energy generation. The largest operational offshore wind farm, located in the Irish Sea, has 87 turbines and a total generating capacity of 659 MW. The largest onshore wind farm is in Kern County, California with some 586 turbines and a total capacity of 1 550 MW. 风能转换系统（WECS）可通过暴露于风中的转子（如多叶片螺旋桨）将与风相关的动能转换为电能或机械能。如果空气密度为ρ，风速为V，则动能通量为ρV3/2。可由截获风a横截面的风力涡轮机提取的实际风功率为CPρAV3/2，其中CP是称为功率系数的经验效率因子。风能分布是根据给定位置处的风速频率分布每年可产生的计算风力的直方图。风车产生机械功率，而风力涡轮机（风力发电机）产生电功率。MHI Vestas制造的最大风力涡轮机的额定功率为9.5MW，转子直径为164m，轮毂高度为105m（最高风力涡轮机的高度为190m）。风电场是一系列风力涡轮机，通常为十到几百台，位于单一位置，无论是陆上还是海上。风能是可持续能源发电的主要贡献者。最大的海上风电场位于爱尔兰海，拥有87台涡轮机，总发电容量为659MW。最大的陆上风电场位于加利福尼亚州克恩县，拥有约586台涡轮机，总容量为1550兆瓦。 |
| Secondary hardening | 二次硬化 |
The process whereby some low-alloy steels, quenched to produce martensite, produce fine precipitates when tempered above 550°C, which inhibit dislocation motion and reverse the trend towards lower strength at higher tempering temperatures. 某些低合金钢经淬火产生马氏体，在550°C以上回火时产生细小沉淀的过程，这抑制了位错运动，扭转了在较高回火温度下强度降低的趋势。 |
| Tempered martensite embrittlement | 回火马氏体脆化 |
Embrittlement of ultrahigh-strength steels caused by tempering in the temperature range of 205 to 400 °C (400 to 750 °F); also called 350 °C or 500 °F embrittlement. Tempered martensite embrittlement is thought to result from the combined effects of cementite precipitation on prioraustenite grain boundaries or interlath boundaries and the segregation of impurities at prioraustenite grain boundaries. 超高强度钢在205至400°C（400至750°F）温度范围内回火引起的脆化；也称为350°C或500°F脆化。回火马氏体脆化被认为是由于渗碳体沉淀在原奥氏体晶界或层间晶界上以及杂质在原奥氏体晶粒边界处偏析的综合影响。 |
| Crack size (a) | 裂纹尺寸（a） |
A lineal measure of a principal planar dimension of a crack. This measure is commonly used in the calculation of quantities descriptive of the stress and displacement fields. In practice, the value of crack size is obtained from procedures for measurement of physical crack size, original crack size, or effective crack size, as appropriate to the situation under consideration. 裂纹主平面尺寸的线性度量。这种测量通常用于计算描述应力场和位移场的量。在实践中，裂纹尺寸的值是通过测量物理裂纹尺寸、原始裂纹尺寸或有效裂纹尺寸的程序获得的，视情况而定。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Preload | 预载 |
The tension created in a threaded fastener when the nut is first tightened. Often used interchangeably, but incorrectly, with Working load or bolt force or bolt tension 第一次拧紧螺母时螺纹紧固件中产生的张力。经常与工作载荷或螺栓力或螺栓张力互换使用但容易使用不当。 |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Transgranular | 穿晶 |
Through or across crystals or grains. Also known as intracrystalline or transcrystalline. 穿过或横穿晶体或颗粒。也称为晶内或晶间。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| Actual power | 实际功率 |
(actual horsepower) (Unit W or hp) The power delivered at the output shaft of an engine, before subsequent transmission through a gearbox etc. （实际马力）（单位W或hp）在随后通过变速箱等传输之前，在发动机输出轴上传递的功率。 |
| Compression ratio | 压缩率 |
The volume of a combustion chamber with the piston at the top of its stroke as a proportion of the total volume of the cylinder with the piston at the bottom of its stroke. For a piston engine, if the swept volume is SW and the clearance volume is CL, the compression ratio is given by ( SW + CL)/CL, i.e. it is a volume ratio rather than a pressure ratio. 活塞位于其冲程顶部的燃烧室的容积与活塞位于其冲程底部的气缸总体积的比例。对于活塞发动机，如果扫气量为SW，间隙容积为CL，则压缩比由(SW+CL)/CL给出，即它是体积比而不是压力比。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Shrink fit | 过盈配合 |
A tight interference fit between two components resulting from heating an outer part and/or cooling an inner part to allow easy assembly. The outer component contracts on cooling, while the inner part expands on warming to ambient temperature, thus gripping the two parts together. 由于加热外部部件和/或冷却内部部件而导致的两个部件之间的紧密过盈配合，以便于组装。外部部件在冷却时收缩，而内部部件在加热到环境温度时膨胀，从而将两个部件夹在一起。 |
| Applied thermodynamics | 应用热力学 |
(engineering thermodynamics, thermodynamics) The science of the relationship between heat, work and the properties of systems and the ways in which heat energy from fuels can be converted into mechanical work. It involves the study of all aspects of energy use and energy transformation, including power generation, refrigeration, the relevant properties of the substances involved and the relationships between them. The principle of conservation of energy is a fundamental law of nature. （工程热力学、热力学）热、功和系统特性之间关系的科学，以及燃料中的热能可以转化为机械功的方式。它涉及能源使用和能源转换的各个方面的研究，包括发电、制冷、所涉及物质的相关特性以及它们之间的关系。能量守恒定律是自然的基本规律。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Diffusion coefficient | 扩散系数 |
A factor of proportionality representing the amount of substance diffusing across a unit area through a unit concentration gradient in unit time. 一个比例因子，表示在单位时间内通过单位浓度梯度扩散到单位面积上的物质量。 |
| Condenser | 冷凝器 |
A heat exchanger in which a substance is changed from its vapour phase to its liquid phase by reducing its temperature to below the saturation temperature. 一种热交换器，通过将物质的温度降低到饱和温度以下，将其从气相变为液相。 |
| Computed path control | 计算路径控制 |
In CNC or robotics, the use of a control program to determine the required path for the tool or end effector. This required path forms the set points for the motor controllers moving the machine tool or robot. 在CNC或机器人技术中，使用控制程序来确定工具或末端执行器所需的路径。这条所需的路径形成了用于移动机床或机器人的电机控制器的设定点。 |
| Raised-face flange | 凸面法兰 |
A flange which contacts its mating joint member only in the region in which the gasket is located. The flanges do not contact each other at the bolt circle. 仅在垫圈所在区域接触其配合接头构件的法兰。法兰在螺栓圆处不相互接触。 |
| Austempered steels | 等温钢 |
Medium to high carbon steels with improved mechanical properties as a result of austempering. After heating to between 800° and 900°C to form the austenite phase, they are quenched to, and held at, just above the martensite transformation range (between 260° and 370°C) to form bainite, before cooling further. Austempering of ductile cast irons results in a microstructure of bainite and spheroidal graphite. Austempered ductile irons have excellent toughness and wear properties. 由于等温淬火，机械性能得到改善的中高碳钢。在加热到800°和900°C之间形成奥氏体相后，将它们淬火并保持在略高于马氏体转变范围（260°和370°C之间）以形成贝氏体，然后进一步冷却。球墨铸铁的等温淬火导致贝氏体和球状石墨的微观结构。等温淬火球墨铸铁具有优异的韧性和耐磨性。 |
| Tribology | 摩擦学 |
The science and technology concerned with interacting surfaces in relative motion. 与相对运动中相互作用的表面有关的科学和技术。 |
| Fastener manufacturer | 紧固件制造商 |
An organization that fabricates raw steel into a fastener meeting specified standards. 将生钢加工成符合规定标准的紧固件的组织。 |
| Austenitic grain size | 奥氏体晶粒尺寸 |
The size attained by the grains of steel when heated to the austenitic region; may be revealed by appropriate etching of cross sections after cooling to room temperature. 当加热到奥氏体区域时钢晶粒达到的尺寸；冷却至室温后，可通过适当蚀刻横截面来显示。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Sliding-vane compressor | 滑片压缩机 |
(rotary-vane compressor, vane compressor) A rotary compressor in which gas is compressed as the spaces between spring-loaded sliding vanes held in an offset rotor reduce as the rotor revolves within a cylindrical housing. （旋转叶片压缩机，叶片压缩机）一种旋转式压缩机，当转子在圆柱形外壳内旋转时，偏置转子中的弹簧加载滑动叶片之间的空间减小，从而压缩气体。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Liquid carburizing | 液体渗碳 |
Surface hardening of steel by immersion into a molten bath consisting of cyanides and other salts. 通过浸入由氰化物和其他盐组成的熔池中对钢进行表面硬化。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Clearance angle | 后角 |
(relief angle) (Unit °) The angle between the underneath or flank of a cutting tool and the machined surface. （后角）（单位°）切削刀具的底部或侧面与加工表面之间的角度。 |
| Pressure (p) (Unit Pa) | 压力（p）（单位Pa） |
In thermodynamics and fluid mechanics, the compressive force exerted by the fluid per unit area. The pressure exerted by a fluid on a surface acts normal to the surface. 在热力学和流体力学中，每单位面积流体施加的压缩力。流体施加在表面上的压力垂直于表面。 |
| Honing | 珩磨 |
Honing is a controlled, low-speed sizing and surface-finishing process in which stock is removed by the shearing action to the bonded abrasive grains of a honing stone, or stick. Finish polishing of surfaces and cutting edges in which very fine abrasive powders, such as rouge, are employed. Honing is usually applied to cylindrical surfaces and lapping to flat, but the usage is not consistent. 珩磨是一种受控的低速尺寸和表面精加工工艺，其中通过对珩磨石或棒的粘结磨粒的剪切作用去除原料。表面和切削刃的精抛光，其中使用了非常细的研磨粉，例如胭脂。珩磨通常用于圆柱面，研磨至平面，但用法并不一致。 |
| Coefficient of thermal expansion | 热膨胀系数 |
(1) Change in unit of length (or volume) accompanying a unit change of temperature, at a specified temperature. (2) The linear or volume expansion of a given material per degree rise of temperature, expressed at an arbitrary base temperature or as a more complicated equation applicable to a wide range. （1） 单位长度（或体积）随温度单位变化的变化。（2） 给定材料每上升一度的线性或体积膨胀，在任意基础温度下表示，或作为适用于宽范围的更复杂方程表示。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| Newton’s law of gravitation | 牛顿万有引力定律 |
(Newton’s law of universal gravitation) Any two bodies exert a gravitational force of attraction F on each other directed along the line joining their centres of mass, in magnitude proportional to the product of their masses and inversely proportional to the square of the distance r between them. （牛顿万有引力定律）任何两个物体沿其质心连接线相互施加引力F，其大小与其质量乘积成正比，与它们之间距离r的平方成反比。 |
| Heat balance (heat budget) | 热平衡（热预算） |
An energy balance involving only heat transfer across the system boundary and the stored energy. 仅涉及跨系统边界的热传递和存储能量的能量平衡。 |
| Dowel | 销钉 |
A headless cylindrical pin that fits into corresponding holes in mating components, thus ensuring relative location. A round metal or wooden pin. A pin, usually of circular shape like a cylinder, used to pin or fasten something in position temporarily or permanently. 一种圆头金属或木制圆柱销，可插入配合组件的相应孔中，从而确保相对位置，用于暂时或永久地将某物固定或固定到位。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Combustion chamber | 炉膛 |
1. In a piston engine, the volume between the head of an individual cylinder and the crown of the piston in which the fuel–air mixture burns during each power stroke of the engine. 2. (combustor) In a gas-turbine engine, a ramjet, an afterburner, or a rocket motor, the component, often cylindrical or annular in shape, in which the fuel–air mixture burns in a continuous-flow process. 1.在活塞式发动机中，在发动机的每个动力冲程中，燃料-空气混合物燃烧的单个气缸盖和活塞顶之间的体积。2.（燃烧室）在燃气涡轮发动机、冲压发动机、加力燃烧室或火箭发动机中，燃料-空气混合物在连续流动过程中燃烧的部件，通常为圆柱形或环形。 |
| Millimetre of water | 毫米水柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of water 1 mm high. Approximately equal to 9.81 Pa. 一种非SI压力单位，等于1毫米高的垂直水柱施加的压力。大约等于9.81Pa。 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Plane stress | 平面应力 |
The stress condition in linear-elastic fracture mechanics in which the stress in the thickness direction is zero; most nearly achieved in loading very thin sheet along a direction parallel to the surface of the sheet. Under plane-stress conditions, the plane of fracture instability is inclined 45° to the axis of the principal tensile stress. 线弹性断裂力学中厚度方向上的应力为零的应力条件；在沿着平行于薄片表面的方向加载非常薄的薄片时最接近。在平面应力条件下，断裂失稳平面与主拉应力轴倾斜45°。 |
| Total heat (Unit kJ) | 总热量（单位kJ） |
An alternative term for enthalpy. It is inappropriate as it suggests that it includes kinetic energy in the same way as total enthalpy, but it does not. Also, heat and enthalpy are quite different quantities, as their definitions show. 焓的另一个术语。这是不恰当的，因为它表明，它包括动能的方式与总焓相同，但它实际上并不是的。此外，热和焓是完全不同的量，正如它们的定义所示。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| Water quenching | 水淬 |
A quench in which water is the quenching medium. The major disadvantage of water quenching is its poor efficiency at the beginning or hot stage of the quenching process. 以水为淬火介质的淬火。水淬的主要缺点是在淬火过程的开始或热阶段效率低。 |
| Compression pressure (Unit Pa) | 压缩压力（单位Pa） |
The pressure produced in a cylinder of a piston engine by compression of air in the absence of fuel. 在没有燃料的情况下通过压缩空气在活塞发动机的气缸中产生的压力。 |
| High-tensile bolt | 高强度螺栓 |
(high-tension bolt) A bolt manufactured from an alloy steel that has a high tensile strength of about 1 GPa. （高压螺栓）由合金钢制成的螺栓，具有约1GPa的高抗拉强度。 |
| Crack-extension force (G) | 裂纹扩展力（G） |
The elastic energy per unit of new separation area that would be made available at the front of an ideal crack in an elastic solid during a virtual increment of forward crack extension. 在向前裂纹扩展的虚拟增量期间，在弹性固体中理想裂纹的前端可获得的每单位新分离面积的弹性能量。 |
| Austenite stabilization | 奥氏体稳定化 |
Decrease, in comparison to a continuous cooling, in the amount of martensite occurring from austenite when cooling is interrupted at a temperature between Ms and Mf. This can be explained by the relaxation of stresses induced in the austenite by martensite crystals occurring before the interruption. The relaxation, in turn, leads to the dislocation rearrangement and their interaction with martensite/austenite interfaces, which makes the interfaces immobile. 与连续冷却相比，当在Ms和Mf之间的温度中断冷却时，从奥氏体中产生的马氏体的量减少。这可以通过中断前发生的马氏体晶体在奥氏体中引起的应力松弛来解释。反过来，松弛导致位错重排及其与马氏体/奥氏体界面的相互作用，这使得界面无法移动。 |
| Young’s modulus | 杨氏模量 |
A term used synonymously with modulus of elasticity. The ratio of tensile or compressive stresses to the resulting strain. 与弹性模量同义的术语。拉伸或压缩应力与产生应变的比率。 |
| Form of thread | 螺纹形式 |
The profile of a thread in an axial plane for a length of one pitch. 一个螺距长度的螺纹在轴向平面中的轮廓。 |
| Intense quenching | 强烈淬火 |
Quenching in which the quenching medium is cooling the part at a rate at least two and a half times faster than still water. 淬火，其中淬火介质以比静水快至少两倍半的速度冷却零件。 |
| Socket wrench | 套筒扳手 |
A form of spanner with an internally ridged steel socket to fit a nut or the head of a bolt or screw. 扳手的一种形式，带有内脊钢套筒，用于安装螺母或螺栓或螺钉的头部。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| Blue brittleness | 蓝色脆性 |
Anomalous loss of ductility when quenched steels are tempered in the range 250–350°C (temperatures that produce blue tints on the surface of components). Brittleness exhibited by some steels after being heated to some temperature within the range of about 205 to 370 °C (400 to 700 °F), particularly if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. 当淬火钢在250–350°C范围内回火（在部件表面产生蓝色色调的温度）时，延展性异常损失。某些钢在加热到约205至370°C（400至700°F）范围内的某个温度后表现出脆性，特别是在高温下加工钢时。镇静钢几乎没有这种脆性。 |
| Maximum load (Pmax) | 最大负载（Pmax） |
(1) The load having the highest algebraic value in the load cycle. Tensile loads are considered positive and compressive loads negative. (2)Used to determine the strength of a structural member; the load that can be borne before failure is apparent. （1）负载循环中具有最高代数值的负载。拉伸荷载视为正荷载，压缩荷载视为负荷载。（2）用于确定结构构件的强度；失效前可承受的载荷是明显的。 |
| Turbine | 涡轮 |
A turbomachine in which a rotor (turbine wheel) or impeller is caused to rotate and convert flow energy into shaft power or thrust. 转子（涡轮）或叶轮旋转并将流动能量转换为轴功率或推力的涡轮机。 |
| Double aging | 双级时效 |
Employment of two different aging treatments to control the type of precipitate formed from a supersaturated matrix in order to obtain the desired properties. The first aging treatment, sometimes referred to as intermediate or stabilizing, is usually carried out at higher temperature than the second. 采用两种不同的时效处理来控制由过饱和基质形成的沉淀物类型，以获得所需的性能。第一次时效处理，有时称为中间处理或稳定处理，通常在比第二次更高的温度下进行。 |
| Shoulder bolt | 轴肩螺栓 |
A bolt for which the unthreaded cylindrical section between the thread and the head is of larger diameter than the threaded section, precisely machined to length and diameter and hardened 一种螺栓，其螺纹和头部之间的无螺纹圆柱段的直径大于螺纹段的直径，精确加工至长度和直径并硬化 |
| Deviation | 偏差 |
The difference between the actual value and the desired value of a controlled variable. 受控变量的实际值与期望值之间的差值。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Torque wrench | 扭矩扳手 |
A manual wrench which incorporates a gage or measuring apparatus of some sort to measure and display the amount of torque being delivered to the nut or bolt. All wrenches produce torque. Only a torque wrench tells how much torque. A socket wrench or ring spanner that can be set to allow a specific torque to be applied to a nut or bolt head. 一种手动扳手，包括某种量规或测量装置，用于测量和显示传递至螺母或螺栓的扭矩量。所有扳手都产生扭矩。只有扭矩扳手才能显示扭矩大小。一种套筒扳手或梅花扳手，可设置为允许对螺母或螺栓头施加特定扭矩。 |
| Pitch | 沥青节距 |
The nominal distance between two adjacent thread roots or crests. In screw threads, the distance from a point on one thread to a corresponding point on the next thread measured parallel to the axis. In the case of spur gears, indicates the size of the gear teeth and is correctly called diametral pitch. 两个相邻螺纹根部或顶部之间的标称距离。在螺纹中，从一根螺纹上的一点到下一根螺纹对应点的距离，平行于轴线测量。对于正齿轮，表示齿轮齿的尺寸，正确地称为径向节距。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Active vibration suppression | 主动振动抑制 |
The reduction of undesirable vibration in components by feedback control. 通过反馈控制减少部件中的不良振动。 |
| Working stress (Unit Pa) | 工作应力（单位Pa） |
The stress under which a component or structure is designed to operate under normal conditions. 部件或结构设计为在正常条件下运行的应力。 |
| Carbonization | 碳化 |
Conversion of an organic substance into elemental carbon. 将有机物质转化为元素碳。 |
| Galling | 磨损 |
An extreme form of adhesive wear, in which large chunks of one part stick to the mating part (during sliding contact). 一种极端形式的粘着磨损，其中一个零件的大块粘在配合零件上（在滑动接触期间）。 |
| Constant-force spring | 恒力弹簧 |
A spring that has the same restoring force regardless of displacement. The most common type takes the form of a coiled strip that, owing to tight coiling during manufacture, is pre-stressed (a steel measuring tape is an example). The uncoiling force is approximately constant as the change of curvature of the strip is approximately constant. Not to be confused with a clockwork spring from which power can be obtained. 无论位移如何，具有相同恢复力的弹簧。最常见的类型是卷绕带，由于制造过程中的紧密卷绕，该卷绕带是预应力的（钢卷尺就是一个例子）。随着带材曲率的变化近似恒定，开卷力近似恒定。不要与可获得动力的发条弹簧混淆。 |
| Fatigue strength | 疲劳强度 |
The stress to which a metal can be subjected for a specified number of cyclic changes of stress. The maximum stress that can be sustained for a specified number of cycles without failure. The value of the maximum stress and the stress ratio also should be stated. 金属在指定数量的应力循环变化下可以承受的应力。可以在指定的循环次数内持续而不失效的最大应力。还应说明最大应力值和应力比。 |
| Nut factor | 螺母系数 |
An experimental constant used to evaluate or describe the ratio between the torque applied to a fastener and the Preload achieved as a result. 用于评估或描述施加在紧固件上的扭矩与由此获得的预载之间的比率的实验常数。 |
| Spray quenching | 喷雾淬火 |
A quenching process using spray nozzles to spray water or other liquids on a part. The quench rate is controlled by the velocity and volume of liquid per unit area per unit of time of impingement. 使用喷嘴将水或其他液体喷射到零件上的淬火过程。淬火速率由每单位撞击时间内每单位面积的液体速度和体积控制。 |
| Thermal fatigue | 热疲劳 |
Fatigue resulting from the presence of temperature gradients that vary with time in such a manner as to produce cyclic stresses in a structure. 由于温度梯度的存在而产生的疲劳，温度梯度随时间变化，从而在结构中产生循环应力。 |
| Specimen | 样品 |
A test object, often of standard dimensions or configuration, that is used for destructive or nondestructive testing. One or more specimens may be cut from each unit of a sample. 用于破坏性或无损检测的测试对象，通常具有标准尺寸或配置。可以从样品的每个单位切割一个或多个样品。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Diagonal pitch (Unit m) | 对角线间距（单位米） |
The distance, when components in an assembly are staggered, between the position of a component in one row or column and the position of the corresponding component in the next row or column. The term is applied to rivets, turbine or compressor blades in a cascade, vortex generators on the surface of a wing, etc. 当部件中的零部件交错时，一行或一列中零部件的位置与下一行或下一列中相应零部件的位置之间的距离。该术语适用于铆钉、叶栅中的涡轮或压缩机叶片、机翼表面的涡流发生器等。 |
| Solenoid | 螺线管 |
A coil of electrically-conducting wire wrapped around a metal core, typically iron, to produce a magnetic field and hence a force on the core when an electric current passes through the coil. Solenoids are widely used to produce linear movement to actuate valves (solenoid valves) and other devices. 绕在金属芯（通常为铁）上的导线线圈，当电流通过线圈时产生磁场，从而在芯上产生力。电磁阀广泛用于产生线性运动以驱动阀（电磁阀）和其他装置。 |
| Caustic quenching | 苛性淬火 |
Quenching with aqueous solutions of 5 to 10% sodium hydroxide (NaOH). 用5%至10%氢氧化钠（NaOH）水溶液淬灭。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Safety valve (safety-relief valve) | 安全阀（安全泄压阀） |
A mechanical valve, fitted by law to all pressure vessels (e.g. steam boilers), which opens to prevent the internal pressure exceeding the maximum design value for that vessel. The valve closes again once the pressure reduces to a safe level. 根据法律安装在所有压力容器（如蒸汽锅炉）上的机械阀，其打开以防止内部压力超过该容器的最大设计值。一旦压力降至安全水平，阀门将再次关闭。 |
| Torsional shaft vibration | 扭轴振动 |
The rapid back-and-forth angular twisting along a rotating unbalanced shaft which reaches maxima at critical rotation speeds. Shaft eccentricity, unbalanced mass distribution, oscillatory torque, misalignment, etc. all influence torsional vibration. 沿旋转不平衡轴的快速来回角扭转，在临界转速下达到最大值。轴偏心、质量分布不平衡、振荡扭矩、未对准等都会影响扭转振动。 |
| Total elongation | 总伸长率 |
A total amount of permanent extension of a test piece broken in a tensile test. 拉伸试验中断裂试样的永久延伸总量。 |
| Steam gauge | 汽压表 |
A pressure gauge used to measure gauge pressure in a line, boiler, cylinder, or other device operating with steam. 一种压力表，用于测量管道、锅炉、汽缸或其他与蒸汽一起工作的装置中的表压。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Bias pressure (Unit Pa) | 偏压（单位Pa） |
In a fluidic device controlled by pressure difference, the magnitude of that difference. 在由压力差控制的流体装置中，该差值的大小。 |
| Screw conveyor | 螺旋输送机 |
(auger, spiral conveyor, worm conveyor) A machine for bulk handling of semi-solid materials, consisting of a helical screw which rotates in a trough or casing. （螺旋输送机、螺旋输送机、蜗杆输送机）一种用于散装搬运半固态材料的机器，由在槽或外壳中旋转的螺旋螺杆组成。 |
| Rockwell hardness number (HR) | 洛氏硬度值（HR） |
A number derived from the net increase in the depth of impression in a Rockwell hardness test as the load on an indenter is increased from a fixed minor load to a major load and then returned to the minor load. Rockwell hardness numbers are always quoted with a scale symbol representing the penetrator, load, and dial used. 当压头上的载荷从固定的小载荷增加到大载荷，然后返回到小载荷时，洛氏硬度试验中压痕深度的净增加值。洛氏硬度值总是用刻度符号引用，表示所用的穿透器、载荷和刻度盘。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Dimensioning | 尺寸标注 |
The specification on an engineering drawing of the size (e.g. length, radius, angle, or spacing) and the relative location (e.g. angular position) of each feature of a component. The numerical values often include the tolerances. There should be no more dimensions than are necessary to manufacture the component. 工程图纸上对部件每个特征的尺寸（例如长度、半径、角度或间距）和相对位置（例如角位置）的规范。数值通常包括公差。尺寸不应超过制造组件所需的尺寸。 |
| Zero time | 零时 |
The time when the given loading or constraint conditions are initially obtained in creep or stressrelaxation tests, respectively. 分别在蠕变或应力松弛试验中初始获得给定载荷或约束条件的时间。 |
| International System of Units | 国际单位制 |
(SI system of units, Le Système international d’unités) The standard system of units now used almost universally in science and engineering except in the United States. The definitive reference on the SI is a booklet published by the International Bureau of Weights and Measures, often referred to as the BIPM SI Brochure. There are seven base units: metre (symbol m) for length; kilogram (kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred.(kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred. （国际单位制，Le Système international d\\\'unités）目前美国除外，在科学和工程中几乎是普遍使用的标准单位制。SI的最终参考是国际度量衡局出版的小册子，通常称为BIPM SI小册子。有七个基本单位：米（符号m）表示长度；质量为千克（kg）；物质量的摩尔（mol）；时间为秒；开尔文（K）表示温度；电流为安培（A）；而坎德拉（cd）表示发光强度。新的国际单位制定义于2019年5月20日生效，该定义基于自然界的普遍常数（也称为基本物理常数：阿伏伽德罗常数、玻尔兹曼常数和普朗克常数）。这些常数的值也进行了少量调整。除了基本单位外，还有22个相干导出单位，包括平面角的弧度（rad）、立体角的斯特拉迪安（sr）、频率的赫兹（Hz）、力的牛顿（N）、压力的帕斯卡（Pa）、能量、功和热量的焦耳（J）以及功率和辐射通量的瓦特（W）。建议的做法是避免N/mm²、MN/m²等组合。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Fracture | 断裂 |
(rupture) The separation of materials, components, or structures into two or more parts by the propagation of one or more cracks. Cracking may be globally elastic (brittle) or accompanied by varying degrees of plasticity (ductile). （断裂）通过一个或多个裂纹的扩展将材料、部件或结构分离成两个或更多部分。裂纹可能是整体弹性（脆性）或伴有不同程度的塑性（延性）。 |
| Materials science | 材料科学 |
The study of the properties, behaviour, and application of solid substances such as metals, ceramics, glasses, polymers, composites, biomaterials, and semiconductors, at all scales from the atomic to the macroscopic. The topic has its origins in metallurgy. 研究金属、陶瓷、玻璃、聚合物、复合材料、生物材料和半导体等固体物质的特性、行为和应用，涵盖从原子到宏观的所有范围。起源于冶金学。 |
| Quench-age embrittlement | 淬火时效脆化 |
Embrittlement of low-carbon steels resulting from precipitation of solute carbon at existing dislocations and from precipitation hardening of the steel caused by differences in ferrite at different temperatures. Quenchage embrittlement usually is caused by rapid cooling of the steel from temperatures slightly below Ac1 (the temperature at which austenite begins to form), and can be minimized by quenching from lower temperatures. 低碳钢的脆化是由于溶质碳在现有位错处的沉淀和铁素体在不同温度下的差异导致的钢沉淀硬化造成的。淬火脆性通常是由钢从略低于Ac1的温度（奥氏体开始形成的温度）快速冷却引起的，可以通过从较低温度淬火来最小化。 |
| Oil-cooled | 油冷却 |
A term for a machine that uses circulating oil to remove heat. 使用循环油散热的机器的术语。 |
| Design load (Unit N) | 设计荷载（单位N） |
The greatest load that a component or structure is expected to experience under normal operating conditions. 部件或结构在正常运行条件下预期承受的最大负载。 |
| Computer control | 电脑控制 |
The control of an engineering device or system by pre-programmed computer or by feedback control. 通过预编程计算机或反馈控制对工程设备或系统进行控制。 |
| Hooke’s law | 胡克定律 |
Within the limit of proportionality, the extension of a material is proportional to the applied force. Approximately, it is the relationship between stress and strain in an elastic material when it is stretched. The law states that the stress (force per unit area) is proportional to the strain (a change in dimensions). The law, which holds only approximately and over a limited range, was discovered in 1676 by Robert Hooke. 在比例极限内，材料的延伸与所施加的力成比例。近似地说，它是弹性材料拉伸时应力和应变之间的关系。该定律指出，应力（单位面积的力）与应变（尺寸变化）成比例。该定律仅适用于有限的范围，由罗伯特·胡克于1676年发现。 |
| Chilled castings | 冷铸件 |
Iron castings cooled at a rate that results in white iron (slow enough to avoid the formation of martensite, yet fast enough to prevent any silicon present from causing decomposition of cementite into iron and graphite). 铸铁件以产生白口铁的速度冷却（足够慢以避免形成马氏体，但足够快以防止任何存在的硅导致渗碳体分解成铁和石墨）。 |
| Vickers hardness number | 维氏硬度值 |
(diamond hardness number, DHN, VHN, VPN) (Unit kg/mm² originally, sometimes now Pa) Indentation hardness given by load divided by the surface area of the permanent impression obtained when the indenter is in the form of a square pyramid whose opposite faces make an angle of 136° with one another. The mean length d of the diagonals of the indentation is determined, from which VPN = 0.927(2W/d2) where W is the load, since the base of the pyramid has an area equal to 0.927 times the surface area. （金刚石硬度值，DHN，VHN，VPN）（最初单位为kg/mm²，有时为Pa）压痕硬度，由载荷除以永久压痕的表面积得出，当压头呈方形棱锥体形式时，其相对面彼此成136°角。确定压痕对角线的平均长度d，其中VPN=0.927（2W/d2），其中W是载荷，因为棱锥底部的面积等于表面积的0.92七倍。 |
| Thermochemical treatment | 热化学处理 |
Heat treatment carried out in a medium suitably chosen to produce a change in the chemical composition of the object by exchange with the medium. 在适当选择的介质中进行热处理，以通过与介质交换产生物体化学成分的变化。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Cone clutch | 锥形离合器 |
A friction clutch in which an internal cone moves axially in or out of engagement with an external cone. One or both surfaces is lined with high-friction material. 一种摩擦离合器，其中内锥与外锥轴向啮合或脱离啮合。一个或两个表面衬有高摩擦材料。 |
| Tightness | 紧密度 |
A measure of the mass leak rate from a gasketed joint. 垫圈接头质量泄漏率的测量值。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Centrifugal compressor | 离心式压缩机 |
A compressor in which kinetic energy is added to a fluid by radial acceleration in an impeller and then converted into a pressure increase by flow though a diffuser. 一种压缩机，其中动能通过叶轮中的径向加速度添加到流体中，然后通过扩散器的流动转换为压力增加。 |
| Captive nut | 松脱螺母 |
A nut attached loosely or rigidly to a sheet member that is too thin to thread and which engages with a cap screw. 松脱地或刚性地连接到薄板构件上的螺母，该螺母太薄而无法拧入，并与带帽螺钉接合。 |
| Compression member | 压缩构件 |
A structural component, the major loading on which is compressive. 一种结构部件，其上的主要载荷是压缩的。 |
| Normality | 常态 |
The principle that the vector sum of plastic strain increments is perpendicular to the yield surface. 塑性应变增量矢量和垂直于屈服面的原理。 |
| Continuous-type furnace | 连续式炉 |
A furnace used for heat treating materials that progress continuously through the furnace, entering one door and being discharged from another. See belt furnac, direct-fired tunnel-type furnac, rotary retort furnace, shaker-hearth furnace. 一种用于热处理材料的炉子，该炉子连续通过炉子，进入一个门并从另一个门排出。参见带式高炉、直燃隧道式高炉、旋转罐式炉、振动炉。 |
| Working load (Unit N) | 工作负荷（单位：N） |
The tension in a bolt in use; tension produced by a combination of Residual preload and a portion (usually) of any External load. The Joint diagram is usually used to predict the approximate working load a fastener will see in service. The load under which a component or structure is designed to operate under normal conditions. 螺栓在使用中的张力；残余预载荷和部分（通常）任何外部载荷的组合产生的张力。连接图通常用于预测紧固件在使用中的近似工作载荷。部件或结构设计为在正常条件下运行的荷载。 |
| Allowable stress design | 许用应力设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Purposely underestimates the strengths of bolts and joint materials to introduce safety factors into the design of structural steel joints. It is an alternative to the more recently defined load and resistance factor design procedure. 结构连接研究委员会为AISC制定的设计程序。故意低估螺栓和接头材料的强度，以便在结构钢接头的设计中引入安全系数。它是最近定义的荷载和阻力系数设计程序的替代方法。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Endurance | 耐力 |
The capacity of a material to withstand repeated application of stress. 材料承受反复施加应力的能力。 |
| Toughening mechanisms | 增韧机理 |
Various methods of increasing the resistance to crack initiation and propagation in materials. They include transformation toughening, in which the microstructure around the crack tip alters so as to slow down or arrest cracks; deflexion of cracks; various ways of de-sharpening crack tips; fibre bridging of cracks; and fibre pull-out. 增加材料中裂纹萌生和扩展阻力的各种方法。它们包括相变增韧，其中裂纹尖端周围的微观结构发生变化，以减缓或阻止裂纹；裂纹偏转；消除裂纹尖端锐化的各种方法；纤维桥接裂纹；和纤维拉出。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Brine quenching | 盐水淬火 |
A quench in which brine (salt water-chlorides, carbonates, and cyanides) is the quenching medium. The salt addition improves the efficiency of water at the vapor phase or hot stage of the quenching process. 一种淬火，其中盐水（盐水-氯化物、碳酸盐和氰化物）是淬火介质。添加盐提高了水在淬火过程的气相或热阶段的效率。 |
| Screw thread | 螺纹 |
A ridge of uniform section or shape in the form of a helix on the external or internal surface of a cylinder, or in the form of a conical spiral on the external or internal surface of a cone. 在圆柱体的外表面或内表面上呈螺旋形或在圆锥体的外表面和内表面上以锥形螺旋形的均匀截面或形状的脊。 |
| Population | 集合 |
The hypothetical collection of all possible test specimens that could be prepared in the specified way from the material under consideration. Also known as universe. 从所考虑的材料中以规定方式制备的所有可能试样的假设集合。也称为体系。 |
| Engineering stress (s) | 工程应力 |
A term sometimes used for conventional stress in order to differentiate it from true stress. In tension testing, it is calculated by dividing the breaking load applied to the specimen by the original crosssectional area of the specimen. 一个术语，有时用于常规应力，以区别于真实应力。在拉伸试验中，通过将施加在试样上的断裂载荷除以试样的原始横截面积来计算。 |
| Crack-growth rate | 裂纹增长速度 |
Rate of propagation of a crack through a material due to statically or dynamically applied load. 由于静态或动态施加的载荷，裂纹在材料中的扩展速率。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Diffusion | 扩散 |
(1) Spreading of a constituent in a gas, liquid, or solid, tending to make the composition of all parts uniform. (2) The spontaneous movement of atoms or molecules to new sites within a material. （1） 一种成分在气体、液体或固体中的扩散，趋于使所有部分的成分均匀。（2） 原子或分子自发运动到材料内的新位置。 |
| Drift pin | 冲头 |
A round tapered steel pin used to align rivet holes so that the rivet will pass through the holes easily. 用于对齐铆钉孔的圆形锥形钢销，以便铆钉轻松穿过孔。 |
| Depth (Unit m) | 深度（单位米） |
1. The vertical distance below a datum surface, especially the sea surface. 2. The distance between the top and bottom of a hole, step in a surface, or a container. 1.基准面以下的垂直距离，尤其是海面。2. 孔的顶部和底部之间的距离、表面上的台阶或容器中的距离。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Fatigue crack growth rate (da/dN) | 疲劳裂纹扩展率（da/dN） |
The rate of crack extension caused by constant-amplitude fatigue loading, expressed in terms of crack extension per cycle of load application. 恒幅疲劳荷载引起的裂纹扩展速率，以每次荷载施加循环的裂纹扩展表示。 |
| Atom | 原子 |
The smallest unit of matter that has the properties of a chemical element. The simplest description of an atom (Bohr model) is of a compact nucleus surrounded by one or more orbiting electrons. 具有化学元素性质的最小物质单位。原子的最简单描述（玻尔模型）是由一个或多个轨道电子包围的致密原子核。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| End-quench hardenability test | 端淬淬透性试验 |
A laboratory procedure for determining the hardenability of a steel or other ferrous alloy. Hardenability is determined by heating a standard specimen above the upper critical temperature, placing the hot specimen in a fixture so that a stream of cold water impinges on one end, and, after cooling to room temperature is completed, measuring the hardness near the surface of the specimen at regularly spaced intervals along its length. The data are normally plotted as hardness versus distance from the quenched end. 测定钢或其他铁合金淬透性的实验室程序。淬透性是通过将标准试样加热到高于上临界温度，将热试样放置在夹具中，使冷水流冲击一端，并在冷却至室温后，沿试样长度以规则间隔测量试样表面附近的硬度来确定的。数据通常绘制为硬度与距淬火端距离的关系。 |
| Relaxed stress | 松弛应力 |
The initial stress minus the remaining stress at a given time during a stress-relaxation test. 在应力松弛试验期间，初始应力减去给定时间的剩余应力。 |
| Volume flow rate | 体积流率 |
(volumetric flow rate, , ) (Unit m³/s) The volume of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. （体积流量）（单位m³/s）单位时间内流经表面或管道或其他管道的材料体积，通常为流体或粉末。 |
| Stress-intensity calibration | 应力强度校准 |
A mathematical expression, based on empirical or analytical results, that relates the stress-intensity factor to load and crack length for a specific specimen planar geometry. Also known as Kcalibration. 基于经验或分析结果的数学表达式，该表达式将特定试样平面几何形状的应力强度因子与载荷和裂纹长度联系起来。也称为K校准。 |
| Brake fluid | 制动液 |
The hydraulic fluid used to transmit force to the pistons in disc brakes or the wheel cylinders in drum brakes. Requirements include a high boiling point and low hygroscopy. 用于将力传递到盘式制动器中的活塞或鼓式制动器中的轮缸的液压油。要求包括高沸点和低吸湿性。 |
| Wrap-around bend | 环绕弯曲 |
The bend obtained when a specimen is wrapped in a closed helix around a cylindrical mandrel. This term is sometimes applied to a semiguided bend of 180° or less. 当试样缠绕在圆柱形心轴周围的闭合螺旋中时获得的弯曲。该术语有时适用于180°或更小的半导弯曲。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Cohesive strength | 内聚强度 |
(Unit Pa) A theoretical fracture strength for solids based on interatomic forces, approximately equal to E/10 where E is Young’s modulus. （单位Pa）基于原子间力的固体理论断裂强度，大约等于E/10，其中E是杨氏模量。 |
| X-ray thickness gauge | X射线厚度计 |
A device comprising an X-ray source and a detector used to determine the thickness of material in sheet or plate form, including metals, paper, plastics, rubber, and ceramics. 一种由X射线源和探测器组成的装置，用于测定片状或平板状材料的厚度，包括金属、纸张、塑料、橡胶和陶瓷。 |
| Balance piston | 平衡活塞 |
(balance drum, dummy piston) A disc attached to the shaft of a turbine or compressor, to one side of which high or low pressure is applied to counteract the axial thrust produced by the pressure change across the machine. A form of thrust bearing. （平衡鼓，假活塞）连接在涡轮机或压缩机轴上的圆盘，在其一侧施加高压或低压，以抵消机器压力变化产生的轴向推力。推力轴承的一种形式。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Plane-stress fracture toughness (Kc) | 平面应力断裂韧性（Kc） |
In linear-elastic fracture mechanics, the value of the crack-extension resistance at the instability condition determined from the tangency between the R-curve and the critical crack-extension force curve of the specimen. 在线弹性断裂力学中，由试样的R曲线和临界裂纹扩展力曲线之间的切线确定的不稳定条件下裂纹扩展阻力的值。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Air-cooled condenser | 风冷冷凝器 |
A heat exchanger, in which the cooling medium is air, used to condense the exhaust steam from a steam turbine, the condensate being returned to the boiler. 一种热交换器，其中冷却介质为空气，用于冷凝蒸汽轮机排出的蒸汽，冷凝水返回锅炉。 |
| Melting point (Unit K or °C) | 熔点（单位K或°C） |
The temperature at which a solid material undergoes the phase change to a liquid at a specified pressure, usually 1 atm. Pure metals and eutectics have single-valued melting points, while alloys with other compositions melt over a range of temperature such that there is a well-defined start and end to the melting process, but there are states in between where solid and liquid are both present. 在特定压力下，固体材料发生相变为液体的温度，通常为1大气压。纯金属和共晶具有单值熔点，而具有其他成分的合金在一定温度范围内熔化，熔化过程有一个明确的起点和终点，但其间存在固态和液态并存的状态。 |
| Mass flow meter | 质量流量计 |
An instrument, such as a Coriolis flow meter, which measures the mass flow rate of a fluid flowing through a pipe or other duct, rather than its volume flow rate. 一种仪器，例如科里奥利流量计，一种测量流经管道或其他管道的流体的质量流率而不是其体积流率的仪器。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Newton (N) | 牛顿（N） |
The basic unit of force in the SI system, defined as the force that results in an acceleration of 1 m/s² when acting on a 1 kg mass. SI国际单位制中力的基本单位，定义为作用于1kg质量时产生1m/s²加速度的力。 |
| Tensile strength (Unit Pa) | 抗拉强度（单位Pa） |
In tension testing, the ratio of maximum load to original cross-sectional area. Also known as ultimate strength. The resistance that a material offers to tensile stress. It is defined as the smallest tensile stress required to break the body. (ultimate strength, ultimate tensile strength, UTS, Rm, Rm) The nominal or engineering stress given by the maximum load in a tension test divided by the original cross-sectional area of the specimen. The maximum load could be the fracture load for a brittle material, but for a ductile material it is usually taken as the load at which necking begins, beyond which the load falls. 在拉伸试验中，最大载荷与原始横截面积之比。也称为极限强度。材料对拉伸应力的抵抗力。它被定义为破坏主体所需的最小拉伸应力。（极限强度、极限抗拉强度、UTS、Rm、Rm）拉伸试验中最大载荷除以试样原始横截面积得出的标称或工程应力。对于脆性材料，最大载荷可以是断裂载荷，但对于韧性材料，最大荷载通常被视为颈缩开始时的载荷，超过该载荷时，载荷下降。 |
| Spring constant | 弹簧常数 |
The ratio between the forces exerted on a spring (or a bolt) and the deflection thereof. Has the dimensions of force per unit change in length (e.g., lb=in.). Also called Stiffness. 施加在弹簧（或螺栓）上的力与其挠度之间的比率。具有每单位长度变化的力的尺寸（例如lb=in.）。也称为刚度。 |
| Diaphragm compressor | 隔膜式压缩机 |
A machine in which compression is achieved by the reciprocating motion of a flexible membrane of metal, plastic, or elastomeric material. This arrangement is ideally suited to pumping high-purity, toxic, or explosive gases. A similar machine incorporating check valves is a self-priming positive-displacement pump (diaphragm pump, membrane pump). 通过金属、塑料或弹性材料的柔性薄膜的往复运动实现压缩的机器。这种布置非常适合泵送高纯度、有毒或爆炸性气体。装有止回阀的类似机器是自吸容积泵（隔膜泵、隔膜泵）。 |
| Rated power (Unit kW or hp) | 额定功率（单位：千瓦或马力） |
(rated capacity, rated horsepower) The maximum power output that can be sustained continuously for any power-producing machine or system, such as an engine or a power plant. （额定容量、额定马力）任何发电机器或系统（如发动机或发电厂）可连续维持的最大功率输出。 |
| Radiosity (J) (Unit W/m²) | 辐射度（J）（单位W/m²） |
The total radiation leaving a given surface per unit area, including emitted, reflected, and transmitted radiation. 每单位面积离开给定表面的总辐射，包括发射、反射和透射辐射。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Modulus of rupture | 断裂模量 |
Nominal stress at fracture in a bend test or torsion test. In bending, modulus of rupture is the bending moment at fracture divided by the section modulus. In torsion, modulus of rupture is the torque at fracture divided by the polar section modulus. 弯曲试验或扭转试验中的标称断裂应力。在弯曲中，断裂模量是断裂时的弯矩除以截面模量。在扭转中，断裂模量是断裂时的扭矩除以极截面模量。 |
| Crosshead | 十字头 |
1. A reciprocating member, sliding between guides, to which the piston rod is firmly attached on one side and to which the connecting rod is pinned on the other for the conversion of reciprocating into rotary motion. 2. The moveable beam in early designs of mechanical testing machines. 3. A screwhead having slots in a + shape that takes a mating screwdriver. 1.一种往复式构件，在导轨之间滑动，活塞杆一侧固定在其上，连杆另一侧固定在该构件上，用于将往复式运动转换为旋转运动。2.机械试验机早期设计中的活动梁。3.一种螺钉头，其具有采用配合螺丝刀的+形槽。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Flattening test | 压扁试验 |
This term as applied to tubing refers to a method of testing a section of tubing by flattening it until the inside walls are parallel and separated by a given distanceusually equal to three times the wall thickness for seamless tubes and five times the wall thickness for lap-welded tubes. Boiler tubes subjected to this test should show no cracks or flaws. The flattening test applied to rivets, consists in flattening a rivet head while hot to a diameter equal to 21⁄2 times the diameter of the shank or body of the rivet. Good rivet steel must not crack at the edges of the flattened head. 该术语适用于管材，是指通过压扁管材直至内壁平行并隔开给定距离（通常等于无缝钢管壁厚的三倍，搭接焊管壁厚的五倍）来测试管材截面的方法。进行该试验的锅炉管应无裂纹或缺陷。适用于铆钉的压扁试验包括在热态下压扁铆钉头，使其直径等于铆钉柄或铆钉体直径的21⁄2倍。良好的铆钉钢不得在扁平头部边缘开裂。 |
| Biomechanics | 生物力学 |
The application of mechanical-engineering principles, including thermodynamics, fluid mechanics, and solid mechanics together with materials engineering, to biological systems. 机械工程原理（包括热力学、流体力学和固体力学以及材料工程）在生物系统中的应用。 |
| Actuating system | 驱动系统 |
A system in which an electrical, pneumatic or hydraulic input supplied to an actuator produces force, torque, or displacement, usually in a controlled way. 一种系统，其中提供给执行器的电气、气动或液压输入通常以受控方式产生力、扭矩或位移。 |
| Turboblower | 涡轮鼓风机 |
A centrifugal or axial compressor or fan. 离心式或轴流式压缩机或风扇。 |
| Track rod | 横拉杆 |
A bar connecting the ends of the steering arms in an automotive vehicle. 连接汽车转向臂端部的杆。 |
| Checks | 检查 |
Numerous, very fine cracks in a coating or at the surface of a metal part. Checks may appear during processing or during service and are most often associated with thermal treatment or thermal cycling. 涂层中或金属零件表面的许多非常细微的裂纹。在加工或服务期间可能会出现检查，并且通常与热处理或热循环有关。 |
| Threading machine | 螺纹机 |
A machine used to cut an external thread on a rod, tube, bolt blank, etc. or an internal thread in a hole, tube, nut blank, etc. 用于切割杆、管、螺栓毛坯等上的外螺纹或孔、管、螺母毛坯等中的内螺纹的机器。 |
| Thermoelastic effect | 热弹性效应 |
The change in temperature of material under adiabatic elastic deformation, e.g. when loading is so rapid that the material is not in thermal equilibrium with its surroundings. For most materials, elastic tension lowers the temperature and compression raises it. The reverse occurs in elastomers such as rubber that exhibit entropic elasticity because stretching reduces the number of possible molecular configurations and so reduces the entropy. The thermoelastic effect gives rise to a stress–strain hysteresis loop in cyclic elastic loading and is one mechanism by which vibrational energy is dissipated internally in materials. 材料在绝热弹性变形下的温度变化，例如当加载速度如此之快，以至于材料与其周围环境不处于热平衡时。对于大多数材料，弹性张力降低温度，压缩提高温度。相反的情况发生在弹性体中，如橡胶，其表现出熵弹性，因为拉伸减少了可能的分子构型的数量，从而降低了熵。热弹性效应在循环弹性载荷中产生应力-应变迟滞回线，是振动能量在材料内部耗散的一种机制。 |
| Fracture mechanisms | 断裂机制 |
The microstructural mechanisms that cause fracture, such as void initiation, growth and coalescence, cleavage. 导致断裂的微观结构机制，如空隙的萌生、生长和聚结、解理。 |
| Torque multiplier | 扭矩放大器 |
A gearbox used to multiply the torque produced by a small hand wrench (usually a Torque wrench). The output of the multiplier drives the nut or bolt with a torque that is higher, and a speed that is lower, than input torque and speed. There is no torque gage or readout on the multiplier. 一种齿轮箱，用于增加小手动扳手（通常是扭矩扳手）产生的扭矩。倍增器的输出以比输入扭矩和速度更高的扭矩和更低的速度驱动螺母或螺栓。倍增器上没有扭矩计或读数。 |
| Teeth | 齿 |
The projecting elements on gears, cutting tools, etc. 齿轮、刀具等上的突出元件。 |
| Magnetic test | 磁性测试 |
Method used to test heat extraction rates of various quenchants. The test works by utilizing the change in magnetic properties of metals at their Curie point–the temperature above which metals lose their magnetism. 用于测试各种淬火剂的热提取率的方法。该测试通过利用金属在居里点（即金属失去磁性的温度）的磁性变化来进行。 |
| Pulley | 带轮 |
A free or driven wheel on a shaft with an appropriately shaped rim to carry a flat belt, vee belt, notched belt, rope, or chain. Used to transmit power or motion. 轴上的自由轮或从动轮，具有适当形状的轮缘，以承载平皮带、V形皮带、槽口皮带、绳索或链条。用于传递动力或运动。 |
| Full-size fastener | 全尺寸紧固件 |
Finished fastener with a shank diameter of ds ≈ d or ds > d, or screw threaded to the head, or fully threaded stud. 柄径为ds≈d或ds>d的紧固件，或螺纹连接到头部，或全螺纹螺柱。 |
| Mode of failure | 故障模式 |
The various ways in which a material can fail when subjected to loading, surface damage, chemical attack, heating, cooling, or radiation, in either isolation or combination. The failure modes include fracture, fatigue, creep, corrosion, erosion, and embrittlement. 材料在受到载荷、表面损伤、化学侵蚀、加热、冷却或辐射时，可能发生失效的各种方式，无论是单独还是组合。失效模式包括断裂、疲劳、蠕变、腐蚀、侵蚀和脆化。 |
| Strain-hardening exponent (n value) | 应变硬化指数（n值） |
The value n in the relationship σ = Kεn, where σ is the true stress, ε is the true strain, and K, the strength coefficient, is equal to the true stress at a true strain of 1.0. The strain hardening exponent is equal to the slope of the true stress/true strain curve up to maximum load, when plotted on log-log coordinates. The n-value relates to the ability of a sheet of material to be stretched in metalworking operations. The higher the n-value, the better the formability(stretchability). Also known as the strain-hardening coefficient. 关系式σ=Kεn中的值n，其中σ是真应力，ε是真应变，K是强度系数，等于真应变为1.0时的真应力。在对数坐标上绘制时，应变硬化指数等于真应力/真应变曲线的斜率，直到最大载荷。n值与一片材料在金属加工操作中拉伸的能力有关。n值越高，成形性（拉伸性）越好。也称为应变硬化系数。 |
| Initial preload | 初始预载 |
The tension created in a single bolt as it is tightened. Will usually be modified by subsequent assembly operations or by in-service loads and conditions. 拧紧单个螺栓时产生的张力。通常会通过后续的装配操作或在役负载和条件进行修改。 |
| Starting friction | 起动摩擦 |
(limiting friction, static friction, stiction) (Unit N) The force required to initiate movement between two bodies in contact. （极限摩擦力、静摩擦力、粘滞）（单位N）在两个接触物体之间启动运动所需的力。 |
| Threaded fastener | 螺纹紧固件 |
Studs, bolts, and screws of all sorts, with associated nuts. One of the most interesting, complex, useful—and frustrating—components yet devised. 各种螺柱、螺栓和螺钉，以及相关的螺母。 |
| Coarsening | 粗粒化 |
An increase in the grain size, usually, but not necessarily, by grain growth. 晶粒尺寸的增加，通常但不一定是晶粒变大。 |
| Maximum allowable working pressure (Unit Pa) | 最大允许工作压力（单位Pa） |
The pressure on which the design of a pressure system is based and the highest pressure at which relief valves should be set. The lowest-rated component in the system typically has a design safety factor of 4. 压力系统设计所依据的压力和应设置安全阀的最高压力。系统中最低额定部件的设计安全系数通常为4。 |
| Stator | 定子 |
A ring of non-rotating blades or nozzles in a compressor, turbine, or other turbomachine, which directs fluid flow into an adjacent rotor. 涡轮压缩机、涡轮或其他涡轮机械中的一圈不旋转的叶片或喷嘴，将流体引导到相邻的转子中。 |
| Blueing | 发蓝 |
Application of blue dye (‘engineers’ blue’) to identify high spots on surfaces in contact, or for marking out. 应用蓝色染料（“工程师蓝”）来识别接触表面上的高点，或用于标记。 |
| Secant modulus | 割线模量 |
The slope of the secant drawn from the origin to any specified point on a stress-strain curve. Compare with chord modulus. 从原点到应力应变曲线上任何指定点的割线斜率。与弦模量进行比较。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Belt drive | 带传动 |
Transmission of motion from one shaft to another by means of a continuous plain, or toothed, flexible band (belt) passing over pulleys. In contrast to chain drives, belt drives tend to be employed in low-torque applications. Reduction in transmissible power may occur due to stretch of a plain transmission belt which results in slack in the drive (belt creep) or slip of a belt on a driving or driven pulley (belt slip). 通过穿过滑轮的连续平带或带齿柔性带（带）将运动从一根轴传递到另一根轴。与链条传动相比，皮带传动往往用于低扭矩应用。由于普通传动带的拉伸可能会导致传动松弛（皮带蠕变）或主动或从动皮带轮上的皮带打滑（皮带打滑），从而导致传动功率降低。 |
| Stress difference (Unit Pa) | 应力差（单位Pa） |
The algebraic difference between the largest and least principal stresses in a loaded body, equal to twice the greatest shear stress in the system. For σ1 > σ2 > σ3, it is given by (σ1 − σ3). 载荷体中最大和最小主应力之间的代数差，等于系统中最大剪应力的两倍。由（σ1− σ3).，可得σ1＞σ2＞σ3。 |
| Fatigue striations | 疲劳条纹 |
Parallel lines frequently observed in electron microscope fractographs or fatigue-fracture surfaces. The lines are transverse to the direction of local crack propagation; the distance between successive lines represents the advance of the crack front during the one cycle of stress variation. 在电子显微镜断口图或疲劳断口表面中经常观察到平行线。这些线横向于局部裂纹扩展方向；连续线之间的距离表示在一个应力变化周期内裂纹前沿的前进。 |
| Fastener standard | 紧固件标准 |
A document which details the attributes of a finished fastener and includes such characteristics as geometry, material or chemistry, heat treatment, finish, testing lot size, and packaging. 详细说明紧固件属性的文件，包括几何形状、材料或化学、热处理、表面处理、测试批量和包装等特性。 |
| Compression crease | 压缩折痕 |
A crease formed during the compression of composites having a high volume fraction of filaments. These composites fail in compression by forming a crease at an angle to the loading axis. 在压缩具有高体积分数长丝的复合材料期间形成的折痕。这些复合材料通过形成与加载轴成一定角度的折痕而在压缩中失效。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Thread insert | 螺纹嵌件 |
(threaded bushing) Either a thin cylinder with an internal thread (and sometimes also an external thread) or a helical coil of wire, pressed or screwed into a hole to accept a bolt or screw. Used in material too soft or a component too thin to be threaded, to change one form of thread to another or to repair a damaged thread. （螺纹衬套）一种带有内螺纹（有时也有外螺纹）的薄圆柱体或螺旋形线圈，压入或拧入孔中以接受螺栓或螺钉。用于材料太软或部件太薄而无法螺纹连接，用于将一种形式的螺纹更换为另一种形式或修复损坏的螺纹。 |
| Metric ton (tonne, t) | 公制吨（吨，t） |
An SI-accepted, but non-SI, unit of mass defined as 1 t = 103 kg. SI系统可接受但非国际单位制的质量单位，定义为1t=103kg。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Barometer | 气压计 |
An instrument used to measure atmospheric pressure. An instrument for measuring atmospheric pressure. There are two main types – the mercury barometer, and the aneroid barometer. 用于测量大气压力的仪器。有两种主要类型——水银气压计和无液气压计。 |
| Frequency | 频率 |
(temporal frequency, f) (Unit Hz) The number of cycles per second in an oscillation or the repetition rate for a cyclic process. （时间频率，f）（单位Hz）振荡中每秒的周期数或循环过程的重复率。 |
| Tensiometer | 张力计 |
An instrument used to measure surface tension. 用来测量表面张力的仪器。 |
| Core | 核心 |
In a ferrous alloy prepared for case hardening, that portion of the alloy that is not part of the case . Typically considered to be the portion that (a) appears light on an etched cross section, (b) has an essentially unaltered chemical composition, or (c) has a hardness, after hardening, less than a specified value. 在为表面硬化而制备的铁合金中，合金中不属于表面的那部分。通常被认为是（a）在蚀刻横截面上看起来很轻，（b）化学成分基本不变，或（c）硬化后硬度低于规定值的那部分。 |
| Blank carburizing | 毛坯渗碳 |
Simulating the carburizing operation without introducing carbon. This is usually accomplished by using an inert material in place of the carburizing agent, or by applying a suitable protective coating to the ferrous alloy. 在不引入碳的情况下模拟渗碳操作。这通常通过使用惰性材料代替渗碳剂或通过在铁合金上施加合适的保护涂层来实现。 |
| AISC | AISC |
The American Institute of Steel Construction. 美国钢结构学会。 |
| Air cleaner | 空气净化器 |
A device, such as a filter, hydrocyclone, or electrostatic precipitator, that removes particles and aerosols from a flow of air. 一种设备，例如过滤器、水力旋流器或静电除尘器，用于从气流中去除颗粒和气溶胶。 |
| Hardness test | 硬度测试 |
1. Any of various tests in which different hard indenters are forced into the surface of a solid under different loads to give permanent impressions, the pressure to cause which being called the hardness. The Brinell test employs a spherical indenter; the Vickers test a square-based pyramid. The relation between indentation hardness H and uniaxial yield stress Y is approximately H = (2.5 ~ 3.0)Y. Originally hardnesses were given in kg/mm² but now are often given in Pa. 2. The tests for scratch and file hardness relate either to one material being able to mark another (Mohs hardness scale for minerals), or to the size of groove produced by a rigid indenter slid under load across a surface. 3. Rebound hardness concerns the height of rebound of a dropped indenter, or an indenter at the end of a pivoted arm, having struck a surface. 1.任何一种试验，其中不同的硬压头在不同载荷下压入固体表面，以产生永久压痕，所产生的压力称为硬度。布氏试验采用球形压头；维氏硬度测试是一个方形金字塔。压痕硬度H与单轴屈服应力Y之间的关系约为H=（2.5~3.0）Y。最初硬度以kg/mm²为单位，但现在通常在Pa.2中给出。划痕和锉刀硬度测试要么与一种材料能够标记另一种材料（矿物的莫氏硬度标度）有关，要么与刚性压头在表面上滑动产生的凹槽大小有关。3.回弹硬度涉及掉落压头或旋转臂端部压头撞击表面后的回弹高度。 |
| Grub screw | 平头螺丝 |
A short headless screw with a recess at one end to receive a screw driver or key. 一种短的无头螺钉，一端有一个凹槽，用于安装螺丝刀或钥匙。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Degree (°) | 度数（°） |
A measure of plane angle such that 1° is 1/360 of a complete revolution and equal to π/180 rad. 平面角度的一种度量，使得1°是一整圈的1/360，等于π/180弧度。 |
| Ideal crack | 理想裂缝 |
A simplified model of a crack used in elastic-stress analysis. In a stress-free body, the crack has two smooth surfaces that are coincident and join within the body along a smooth curve called the crack front; in two-dimensional representations, the crack front is called the crack tip. 用于弹性应力分析的裂纹简化模型。在无应力物体中，裂纹有两个光滑表面，它们在物体内沿称为裂纹前缘的平滑曲线重合并连接；在二维表示中，裂纹前缘称为裂纹尖端。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Standardization | 标准化 |
1. National and international agreements for design, manufacture, materials, performance, practices, requirements, strength, etc. which ensure common results wherever an item is made and wherever used. 2. The manufacture of components so that interchangeability of parts during assembly of new, or repair of old, items is possible without ‘fitting’. 1.关于设计、制造、材料、性能、惯例、要求、强度等的国家和国际协议，确保在任何地方制造和使用物品都能产生共同结果。2.部件的制造，以便在装配新部件或维修旧部件时，无需“装配”即可实现部件的互换性。 |
| Precipitation heat treatment | 沉淀热处理 |
Artificial aging in which a constituent precipitates from a supersaturated solid solution. 成分从过饱和固溶体沉淀的人工时效。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Gasket stress | 垫片应力 |
The contact stress exerted on the gasket by the joint members. 连接件施加在垫片上的接触应力。 |
| Velocity defect (Unit m/s) | 速度亏损（单位：m/s） |
In a viscous flow, such as a boundary layer or wake, the reduction in velocity, due to friction, compared with that of the free stream. 在粘性流中，如边界层或尾迹，由于摩擦，与自由流相比，速度降低。 |
| Eyebolt (eyescrew) | 吊环螺栓（眼螺丝） |
A bolt threaded at one end and bent to a loop at the other end. A bolt or screw with a closed loop in place of a head. 一端有螺纹，另一端弯曲成环的螺栓。带有闭合环代替头部的螺栓或螺钉。 |
| Stress cracking | 应力开裂 |
A family of failure modes, each of which involves high stress and chemical action. The family includes Hydrogen embrittlement, Stress corrosion cracking, stress embrittlement, and hydrogen-assisted stress corrosion. 一系列失效模式，每种模式都涉及高应力和化学作用。该系列包括氢脆、应力腐蚀开裂、应力脆化和氢辅助应力腐蚀。 |
| Fastener quality | 紧固件质量 |
A fastener’s adherence to its specification for dimensional tolerances, mechanical properties, and other requirements stated under applicable standards. 紧固件对尺寸公差、机械性能和适用标准规定的其他要求的规范的遵守情况。 |
| Overheating | 过热 |
Heating a metal or alloy to such a high temperature that its properties are impaired. When the original properties cannot be restored by further heat treating, by mechanical working, or by a combination of working and heat treating, the overheating is known as burning. 将金属或合金加热至其性能受损的高温。当通过进一步热处理、机械加工或加工与热处理的组合无法恢复原始性能时，过热称为燃烧。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Fracture test | 断裂试验 |
A test in which a specimen is broken and its fracture surface is examined with the unaided eye or with a low-power microscope to determine such factors as composition, grain size, case depth, or internal discontinuities. 1. The recording of load-deflexion (or stress–strain) in a specimen loaded monotonically until it breaks in tension, compression, shear, or torsion. 2. In fatigue, determination of the number of cycles to fracture for a specimen under different patterns of repeated loading. 3. Experiments to determine fracture toughness. 一种试验，其中试样被破坏并用肉眼或低倍显微镜检查其断裂表面，以确定成分、晶粒尺寸、表层深度或内部不连续性等因素。1.记录单调加载试样的载荷偏转（或应力-应变），直到其在拉伸、压缩、剪切或扭转中断裂。2.在疲劳技术中，确定试样在不同重复载荷模式下的断裂循环次数。3.测定断裂韧性的实验。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Relative humidity (ϕ) | 相对湿度（ψ） |
The ratio or percentage of the actual mass of moisture in a given volume of air at a given temperature to the maximum possible mass of moisture at the same temperature. 给定温度下给定体积空气中的实际水分质量与相同温度下的最大可能水分质量的比率或百分比。 |
| Octane number | 辛烷值 |
(octane rating) A measure of the anti-knock properties of a fuel taken as the percentage by volume of iso-octane in the fuel. （辛烷值）以燃料中异辛烷的体积百分比表示的燃料抗爆性能的量度。 |
| Balancing machine | 平衡机 |
A device that assesses the state of static and dynamic balance of a rotating part, and indicates the magnitude and location of weights to be added to give balance. 一种装置，用于评估旋转部件的静态和动态平衡状态，并指示为获得平衡而添加的砝码的大小和位置。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Torque motor | 力矩电机 |
A type of induction motor that can apply a steady torque even when prevented from rotating. 一种感应电动机，即使被阻止旋转也能施加稳定的转矩。 |
| Temperature factor | 温度系数 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. Accounts for the effects of thermal expansion and the temperature-induced change in the velocity of sound. 用于螺栓应力或应变超声波测量的校准常数。说明了热膨胀和温度引起的声速变化的影响。 |
| Pressure-relief valve | 减压阀 |
A valve that limits the maximum pressure in a pressure vessel or fluid-power system to a specified level. 将压力容器或流体动力系统中的最大压力限制在规定水平的阀门。 |
| Thread rolling | 滚丝 |
Thread rolling (also known as roll threading) is a cold forming process for producing threads or other helical or annular forms by rolling the impression of hardened steel dies into the surface of a cylindrical or conical blank. Polygonal blanks are also thread rolled for the purpose of fabricating thread-forming and self-locking screws. The preferred polygonal shape is trilobular and is produced in flat die machines. 螺纹滚压（也称为滚压螺纹）是一种冷成型工艺，通过将硬化钢模具的压痕滚压到圆柱形或锥形坯料的表面来生产螺纹或其他螺旋或环形形状。多边形坯料也进行螺纹轧制，以制造螺纹成型和自锁螺钉。优选的多边形形状为三棱形，并在平模机中生产。 |