| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| British thermal unit (BTU, Btu) | 英热单位（BTU，Btu） |
An obsolete (non-SI) imperial unit of energy defined as the energy required to raise the temperature of one pound of pure water at 68°F by 1°F. The conversion to SI is 1 Btu = 1.055 056 × 103 J. 一种已被淘汰的（非SI）英制能量单位，定义为将68°F的一磅纯水的温度升高1°F所需的能量。转换为SI为1Btu=1.055056×103J。 |
| Full-size fastener | 全尺寸紧固件 |
Finished fastener with a shank diameter of ds ≈ d or ds > d, or screw threaded to the head, or fully threaded stud. 柄径为ds≈d或ds>d的紧固件，或螺纹连接到头部，或全螺纹螺柱。 |
| Plane-stress fracture toughness (Kc) | 平面应力断裂韧性（Kc） |
In linear-elastic fracture mechanics, the value of the crack-extension resistance at the instability condition determined from the tangency between the R-curve and the critical crack-extension force curve of the specimen. 在线弹性断裂力学中，由试样的R曲线和临界裂纹扩展力曲线之间的切线确定的不稳定条件下裂纹扩展阻力的值。 |
| Atmospheric pressure | 气压 |
The downward force exerted by the atmosphere because of its weight, (gravitational attraction to the Earth), measured by barometers, and usually expressed in units of millibars. Standard atmospheric pressure at sea level is 1013.25 mb.expressed in units of millibars. Standard atmospheric pressure at sea level is 1013.25 mb. 大气由于其重量（对地球的引力）而施加的向下的力，用气压计测量，通常以毫巴为单位表示。海平面的标准大气压为1013.25mb。以毫巴为单位表示。海平面的标准大气压为1013.25mb。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Compression member | 压缩构件 |
A structural component, the major loading on which is compressive. 一种结构部件，其上的主要载荷是压缩的。 |
| Gauge | 测量 |
1. Any instrument for measuring or checking dimensions, including adjustable gauges such as a micrometer and non-adjustable gauges such as go/no-go limit gauges that indicate the maximum and minimum dimensions allowable in a component during manufacture. 2. A term often used to mean an instrument, e.g. pressure gauge. 3. The diameter of a wire or thickness of a sheet according to a standard. 4. The distance between the rails of a railway track. 1. 任何用于测量或检查尺寸的仪器，包括可调节量规（例如千分尺）和不可调节量规（例如指示制造过程中组件允许的最大和最小尺寸的通过/不通过限制量规）。2. 常用于表示仪器的术语，例如压力表。3.根据标准的线材直径或片材厚度。4.铁路轨道的钢轨之间的距离。 |
| Sawing | 锯切 |
Sawing is the process of cutting a workpiece with power band saws, hacksaws, and circular saws. Each of these methods is used in cutoff operations (cutting pieces to a required length), although band sawing also provides a method of cutting contours. 锯切是用带锯、钢锯和圆锯切割工件的过程。这些方法中的每一种都用于切割操作（将工件切割到所需长度），尽管带锯也提供了一种切割轮廓的方法。 |
| B-basis | B-基础 |
Mechanical property value above which at least 90% of the population of values is expected to fall, with a confidence of 95%. 机械性能值超过该值时，至少90%的值预计会下降，置信度为95%。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Radial wave equation | 径向波动方程 |
A differential equation describing the transmission of a wave in a system with radial symmetry. 描述波在径向对称系统中传输的微分方程。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| Static fatigue | 静态疲劳 |
A term referring to a time-dependent reduction in strength with a static (noncyclic) load. The term may refer to hydrogen-induced delayed cracking or the effect of creep on the strength of plastics. Delayed fracture caused by environmental effects under dead-weight loading of materials such as glass. The name is unfortunate, as cyclic loads are not involved and glass is not susceptible to fatigue. 指静态（非循环）载荷下强度随时间变化的降低。该术语可指氢致延迟开裂或蠕变对塑料强度的影响。在玻璃等材料的自重荷载下，由环境影响引起的延迟断裂。 |
| Ratchet marks | 棘轮痕 |
Lines on a fatigue fracture surface that result from the intersection and connection of fatigue fractures propagating from multiple origins. Ratchet marks are parallel to the overall direction of crack propagation and are visible to the unaided eye or at low magnification. 疲劳断裂面上由从多个源头传播的疲劳断裂的交叉和连接产生的线。棘轮标记与裂纹扩展的整个方向平行，肉眼或低倍镜下均可看到。 |
| Preload | 预载 |
The tension created in a threaded fastener when the nut is first tightened. Often used interchangeably, but incorrectly, with Working load or bolt force or bolt tension 第一次拧紧螺母时螺纹紧固件中产生的张力。经常与工作载荷或螺栓力或螺栓张力互换使用但容易使用不当。 |
| Coefficient of thermal expansion | 热膨胀系数 |
(1) Change in unit of length (or volume) accompanying a unit change of temperature, at a specified temperature. (2) The linear or volume expansion of a given material per degree rise of temperature, expressed at an arbitrary base temperature or as a more complicated equation applicable to a wide range. （1） 单位长度（或体积）随温度单位变化的变化。（2） 给定材料每上升一度的线性或体积膨胀，在任意基础温度下表示，或作为适用于宽范围的更复杂方程表示。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| Ideal gas laws | 理想气体定律 |
The law relating pressure, temperature and volume of an ideal (perfect) gas pV = mRT, where R is the gas constant. The law implies that at constant temperature T, the product of pressure p and volume V is constant (Boyle’s law), and at constant pressure, the volume is proportional to the temperature (Charles’ law). 与理想（完美）气体的压力、温度和体积相关的定律pV=mRT，其中R是气体常数。该定律意味着在恒定温度T下，压力p和体积V的乘积是恒定的（波义耳定律），而在恒定压力下，体积与温度成正比（查尔斯定律）。 |
| Engineering strain (e) | 工程应变（e） |
A term sometimes used for average linear strain or conventional strain in order to differentiate it from true strain. In tension testing it is calculated by dividing the change in the gage length by the original gage length. 一个术语，有时用于平均线性应变或常规应变，以便将其与真实应变区分开来。在张力测试中，通过将标距变化除以原始标距来计算。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Plug gauge | 塞规 |
A steel gauge used to determine the dimension or dimensions of a hole. It may be straight or tapered, and is typically circular, but in principle can have any cross section. 用于确定孔的尺寸的钢制量规。它可以是直的或锥形的，通常是圆形的，原则上可以有任何横截面。 |
| Spinner | 旋转器 |
A co-axial streamlined fairing enclosing the hub of a propeller and rotating with it. 一种同轴流线型整流罩，包围螺旋桨毂并随其旋转。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| Swift cup test | 斯威夫特杯测试 |
A simulative cupping test in which circular blanks of various diameters are clamped in a die ring and deep drawn into cups by a flat-bottomed cylindrical punch. 一种模拟拔杯试验，将不同直径的圆形坯料夹紧在模环中，并用平底圆柱冲头将其深拉入杯中。 |
| Available draught (Unit Pa) | 可用通风量（单位Pa） |
The reduced pressure of combustion gases in a furnace or boiler, either forced or due to the buoyancy of hot gases, which is used to draw in combustion air and remove products of combustion. 炉子或锅炉中燃烧气体的压力降低，无论是强制还是由于热气体的浮力，用于吸入燃烧空气并去除燃烧产物。 |
| Peel strength (Unit N) | 剥离强度（单位：N） |
(peel test) The strength of an adhesive bond between two materials as measured by the force required in a given direction to peel apart adhered strips. This force depends on the dimensions and thickness of the adhered strips and their yield stress, together with the fracture toughness of the bond. （剥离试验）两种材料之间的粘合强度，通过给定方向上剥离粘合条所需的力来测量。该力取决于粘合条的尺寸和厚度及其屈服应力，以及粘合剂的断裂韧性。 |
| Secondary stresses (Unit Pa) | 二次应力（单位Pa） |
Stresses different from those induced by the major loading but nevertheless resulting from the major loads; for example, the hoop stresses that occur around the circumference of barrelled compression testpieces and forgings. 与主要荷载引起的应力不同，但主要荷载产生的应力；例如，桶装压缩试件和锻件周围产生的环向应力。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Air-cooled engine | 风冷发动机 |
An internal-combustion engine directly cooled by airflow, rather than by water flowing through the engine block being cooled by a radiator. 一种由气流直接冷却的内燃机，而不是通过流经发动机缸体的水被散热器冷却。 |
| Pitch-circle diameter (Unit m) | 节圆直径（单位：m） |
The diameter of the circle (the pitch circle) centred on a component’s axis, around which holes or bolts are equally spaced. 以部件轴为中心的圆（节圆）的直径，孔或螺栓围绕其等距分布。 |
| Tolerances | 公差 |
A fractional allowance for variation from the specifications. In mass production, using automatic machines, parts are intended to be completely or partially interchangeable, and in batch production parts should ideally fit without the need for selection. In practice it is impossible for mass-produced parts to have exactly the same size, owing to tool wear, variations in raw materials, thermal effects, etc. In consequence, variations from exactness, termed tolerances, are assigned to what is permissible on the basic size. 与规范不同的部分公差。在大规模生产中，使用自动机器时，零件应完全或部分可互换，在批量生产中，零件应理想匹配，无需选择。在实践中，由于刀具磨损、原材料变化、热效应等原因，批量生产的零件不可能具有完全相同的尺寸。因此，将精度偏差（称为公差）指定给基本尺寸上允许的尺寸。 |
| Finish annealing | 精制退火 |
A subcritical annealing treatment applied to cold-worked low- or medium-carbon steel. Finish annealing, which is a compromise treatment, lowers residual stresses, thereby minimizing the risk of distortion in machining while retaining most of the benefits to machinability contributed by cold working. Compare with final annealing. 适用于冷加工低碳钢或中碳钢的亚临界退火处理。与最终退火相比，精加工退火是一种折衷处理，可降低残余应力，从而最大限度地降低加工中的变形风险，同时保留冷加工对可加工性的大部分好处。 |
| Two-phase flow | 两相流 |
A flow in which two phases are present, for example gas bubbles in a liquid, liquid bubbles in another liquid with which it is immiscible, solid particles in a liquid or gas. 两相流动，例如液体中的气泡、与之不混溶的另一种液体中的液体气泡、液体或气体中的固体颗粒。 |
| Ductile cast iron | 球墨铸铁 |
A cast iron that has been treated while molten with an element such as magnesium or cerium to induce the formation of free graphite as nodules or spherulites, which imparts a measurable degree of ductility to the cast metal. Also known as nodular cast iron, spherulitic graphite cast iron and SG iron. 一种铸铁，在熔融时用镁或铈等元素进行处理，以诱导游离石墨形成为球粒或球晶，从而赋予铸造金属可测量的延展性。又称球墨铸铁、球晶石墨铸铁和SG铸铁。 |
| Dynamic load rating (Unit N) | 额定动载荷（单位N） |
The allowable load on a component or structure when the loading is not static. 当负载不是静态时，组件或结构上的允许负载。 |
| Left hand screw | 左螺旋 |
One that screws into the mating part or advances when turned to the left or counter clockwise. 旋入配合部分或向左或逆时针旋转时前进的螺钉。 |
| Thermodynamic properties | 热力学性质 |
Temperature, pressure, and the intensive properties that define the state of a working fluid: specific internal energy, specific enthalpy and specific entropy. 温度、压力和定义工作流体状态的密集属性：比内能、比焓和比熵。 |
| Zero initial conditions | 零初始条件 |
The assumption normally made in control engineering that up to a start time defined as t = 0, all variables have zero value. 在控制工程中通常作出的假设，即在定义为t=0的开始时间内，所有变量均为零值。 |
| Checks | 检查 |
Numerous, very fine cracks in a coating or at the surface of a metal part. Checks may appear during processing or during service and are most often associated with thermal treatment or thermal cycling. 涂层中或金属零件表面的许多非常细微的裂纹。在加工或服务期间可能会出现检查，并且通常与热处理或热循环有关。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Size effect | 尺寸效应 |
Effect of the dimensions of a piece of metal on its mechanical and other properties and on manufacturing variables such as forging reduction and heat treatment. In general, the mechanical properties are lower for a larger size. 金属件的尺寸对其机械和其他性能以及对制造变量（如锻造、压下和热处理）的影响。一般来说，尺寸越大，机械性能越低。 |
| High strength low alloy steels | 高强度低合金钢 |
(HSLA steels) Steels with various micro-alloying elements such as copper, nickel, chromium, molybdenum, niobium, titanium, and vanadium in small quantities that give improved strength (as high as 900 MPa) and corrosion properties compared with plain carbon steels. Improvements are due to grain refinement and precipitation hardening, better control of the chemistry during steel making, and accurate rolling temperatures. （HSLA钢）是含有各种微合金元素的钢，如少量的铜、镍、铬、钼、铌、钛和钒，与普通碳钢相比，具有更好的强度（高达900MPa）和腐蚀性能。这些改进归功于晶粒细化和沉淀硬化、炼钢过程中更好的化学控制以及精确的轧制温度。 |
| Velocity defect (Unit m/s) | 速度亏损（单位：m/s） |
In a viscous flow, such as a boundary layer or wake, the reduction in velocity, due to friction, compared with that of the free stream. 在粘性流中，如边界层或尾迹，由于摩擦，与自由流相比，速度降低。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Standardization | 标准化 |
1. National and international agreements for design, manufacture, materials, performance, practices, requirements, strength, etc. which ensure common results wherever an item is made and wherever used. 2. The manufacture of components so that interchangeability of parts during assembly of new, or repair of old, items is possible without ‘fitting’. 1.关于设计、制造、材料、性能、惯例、要求、强度等的国家和国际协议，确保在任何地方制造和使用物品都能产生共同结果。2.部件的制造，以便在装配新部件或维修旧部件时，无需“装配”即可实现部件的互换性。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| Abradant | 研磨剂 |
The differently sized grits of hard materials such as emery employed for grinding, polishing, etc. The abrasive grade is determined by the grit size (grit number) originally related to the hole sizes in wire sieves. 用于研磨、抛光等的硬质材料（例如金刚砂）的不同尺寸粒度。磨料等级由最初与金属丝筛孔尺寸相关的粒度（粒度数）决定。 |
| Spring constant | 弹簧常数 |
The ratio between the forces exerted on a spring (or a bolt) and the deflection thereof. Has the dimensions of force per unit change in length (e.g., lb=in.). Also called Stiffness. 施加在弹簧（或螺栓）上的力与其挠度之间的比率。具有每单位长度变化的力的尺寸（例如lb=in.）。也称为刚度。 |
| Combustion | 燃烧氧化 |
An exothermic chemical reaction in which a fuel and an oxidant, typically air, react together to release a significant quantity of thermal energy in the presence of a flame. In the case of fluid fuels, ignition may be from an electric spark or compression of the 一种放热化学反应，其中燃料和氧化剂（通常是空气）一起反应，在火焰存在的情况下释放大量热能。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Crack | 裂缝 |
A thin fissure-like defect in a component or structure across which material continuity is lost and which reduces the strength of the body. 部件或结构中的细裂缝状缺陷，材料连续性丧失并降低了身体的强度。 |
| Combustion deposit | 燃烧沉积物 |
Ash, carbon, and other incombustible solids, often due to impurities in the fuel, that build up on any surfaces exposed to products of combustion. They can lead to corrosion, reduced heat transfer and so higher flue-gas temperatures and reduced efficiency. 灰、碳和其他不燃固体，通常是由于燃料中的杂质，在暴露于燃烧产物的任何表面上堆积。它们会导致腐蚀、传热降低，从而导致烟气温度升高和效率降低。 |
| Fit | 装配 |
The general term used to signify the range of tightness which may result from the application of a specific combination of allowances and tolerances in the design of mating parts. 通用术语，用于表示配合零件设计中公差和公差的特定组合可能导致的紧密性范围。 |
| Closed system | 封闭系统 |
A closed thermodynamic system consists of a fixed amount of mass. No mass can cross its boundary although energy can, in the form of work or heat, and its volume can change. 一个封闭的热力学系统由一定量的质量组成。能量可以以功或热的形式存在，其体积可以改变，但没有质量可以越过它的边界。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Essential conditions | 必要条件 |
Each type of failure to which bolted joints are subject is set up by three or four conditions. The conditions vary, depending on the mode of failure, but never number more than four. Eliminating any one of the essential conditions for a particular type of failure can prevent that type of failure. 螺栓连接所遭受的每种类型的故障都由三个或四个条件确定。根据故障模式的不同，情况会有所不同，但数量不得超过四个。消除特定类型故障的任何一个基本条件都可以防止该类型故障。 |
| Cap screw | 帽螺钉 |
A bolt where the thread runs right up to the head and engages in a threaded hole or captive nut in an adjoining member. A finished screw 5mm or larger, used for fastening two pieces together by passing the screw through a clearance hole in one part and screwing in into a tapped hole in the other. A finished screw, used for fastening two pieces together by passing the screw through a clearance hole in one part and screwing it into a tapped hole in the other. Heads may be hexagon, round, flat, fillister or socket type. 一个5毫米或更大的螺钉，其螺纹一直延伸到头部，并与相邻构件的螺纹孔或外加螺母啮合,用于将两个部件固定在一起，方法是将螺钉穿过一个部分的间隙孔，然后拧入另一个部分的螺纹孔。头部可以是六角形、圆形、扁平形、圆角形或套筒形。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Bond strength (Unit Pa) | 结合强度（单位Pa） |
The tensile, compressive or shear stress at which joints fail, e.g. by fracture or excessive deformation. 接头失效的拉伸、压缩或剪切应力，例如断裂或过度变形。 |
| Structural frame | 结构框架 |
The underlying load-bearing framework of beams, columns, bracing, etc., of steel, concrete, brick, stone, timber etc., required to support the static and dynamic forces a building or component is subjected to, including its weight and that of its contents. 由钢、混凝土、砖、石、木材等制成的梁、柱、支撑等构成的底层承重框架，用于支撑建筑物或构件承受的静态和动态力，包括其重量及其内含物的重量。 |
| Eutectic melting | 共晶熔化 |
Melting of localized microscopic areas whose composition corresponds to that of the eutectic in the system. 局部微观区域的熔化，其成分对应于系统中的共晶成分。 |
| Extra hard | 额外硬化 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about one-third of the way from full hard to extra spring temper. 有色合金和一些铁合金的回火，其特征是抗拉强度和硬度大约是从完全硬回火到额外弹簧回火的三分之一。 |
| Terminal velocity (Unit m/s) | 终端速度（单位：m/s） |
The velocity reached by an object in free fall through a fluid when the upward drag and buoyancy forces just balance the object’s weight. For an object with a density lower than that of the fluid, the terminal velocity is vertically upwards. 当向上的阻力和浮力正好平衡物体的重量时，物体自由下落通过流体达到的速度。对于密度低于流体密度的物体，终端速度垂直向上。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Transverse direction | 横向 |
Literally, the “across” direction, usually signifying a direction or plane perpendicular to the direction of working. In rolled plate or sheet, the direction across the width is often called long transverse, and the direction through the thickness, short transverse. 从字面上看，“横穿”方向，通常表示与工作方向垂直的方向或平面。在轧制钢板或薄板中，横跨宽度的方向通常称为长横向，穿过厚度的方向称为短横向。 |
| Fitted bolt | 装配螺栓 |
A bolt with a plain unthreaded portion immediately beneath the head. 一种螺栓，其头部正下方有一个普通的无螺纹部分。 |
| Vickers hardness test | 维氏硬度测试 |
An indentation hardness test employing a 136° diamond pyramid indenter (Vickers) and variable loads, enabling the use of one hardness scale for all ranges of hardness—from very soft lead to tungsten carbide. Also know as diamond pyramid hardness test. 采用136°金刚石棱锥压头（维氏硬度计）和可变载荷的压痕硬度测试，能够对从极软铅到碳化钨的所有硬度范围使用一个硬度标度。也称为钻石金字塔硬度测试。 |
| Pascal’s law | 帕斯卡定律 |
When there is a change in pressure at any point in a confined fluid at rest, there is an equal change at every other point in the fluid volume. 当处于静止状态的受限流体中任何一点的压力发生变化时，流体体积中的每一点的变化都相等。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| Statistic | 统计 |
A summary value calculated from the observed values in a sample. 根据样本中的观察值计算得出的汇总值。 |
| International Bureau of Weights and Measures | 国际度量衡局IBWM |
(BIPM, Bureau International des Poids et Mesures) The intergovernmental organization which has the mandate to provide the basis for a single, coherent system of measurements, traceable to the International System of Units. （BIPM，国际计量局）政府间组织，其任务是为可追溯到国际单位制的单一、一致的计量系统提供基础。 |
| Temporal decomposition | 时间分解 |
The splitting of a control problem into parts with relatively short and long time constant so that different controllers may be used for the different parts. 将控制问题分解为具有相对较短和较长时间常数的部分，以便不同的部分可以使用不同的控制器。 |
| Finishing washer | 光制垫圈 |
A washer designed for use with countersunk screws. Used to enhance appearance in some applications. 设计用于沉头螺钉的垫圈。在某些应用中用于增强外观。 |
| Barometer | 气压计 |
An instrument used to measure atmospheric pressure. An instrument for measuring atmospheric pressure. There are two main types – the mercury barometer, and the aneroid barometer. 用于测量大气压力的仪器。有两种主要类型——水银气压计和无液气压计。 |
| Collapse load (Unit N) | 毁坏荷载（单位N） |
The applied load at which a structure becomes a mechanism owing to the formation of sufficient plastic hinges for collapse to occur. 由于形成足够的塑性铰链以发生坍塌，结构成为机制的施加载荷。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Batch furnace | 间歇式炉 |
A furnace used to heat treat a single load at a time. Batch-type furnaces are necessary for large parts such as heavy forgings and are preferred for complex alloy grades requiring long cycles. 用于一次热处理单个负载的炉子。对于重型锻件等大型零件，间歇式炉是必需的，对于需要长周期的复杂合金牌号来说是首选。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Thread grinding | 螺纹磨削 |
A method for producing or finishing very precise screw threads using a profiled grinding wheel. 一种使用异形砂轮生产或精加工非常精密螺纹的方法。 |
| Bar | 巴（气压单位） |
A widely used (non-SI) unit of pressure approximately equal to normal atmospheric pressure at sea level. The conversion to SI is 1 bar = 105 Pa. Unit of pressure – the pressure created by a column of€mercury 75.006 cm high at 0ºC, or about 33.45 feet of water at 4ºC. It is equal to 105 pascal. Standard atmospheric pressure (at sea level) is 1.01325 bar, or 1013.25 mb. 一种广泛使用的（非SI）压力单位，大约等于海平面上的正常大气压。转换为SI为1bar=105Pa。压力单位——0ºC时75.006厘米高的水银柱或4ºC时约33.45英尺水柱产生的压力。它等于105帕斯卡。标准大气压（海平面）为1.01325bar或1013.25mb。 |
| Widmanstätten structure | 魏氏组织 |
A structure characterized by a geometrical pattern resulting from the formation of a new phase along certain crystallographic planes of the parent solid solution. The orientation of the lattice in the new phase is related crystallographically to the orientation of the lattice in the parent phase. The structure is readily produced in many alloys by appropriate heat treatment. 一种结构，其特征是沿母体固溶体的某些晶体学平面形成新相而形成的几何图案。新相中晶格的取向在晶体学上与母相中晶格的定向相关。通过适当的热处理，在许多合金中容易产生这种结构。 |
| Screw machine | 螺丝机 |
A machine tool for high-volume manufacture of small turned components from rod or bar. 一种用棒或棒大批量制造小零件的机床。 |
| Ideal crack | 理想裂缝 |
A simplified model of a crack used in elastic-stress analysis. In a stress-free body, the crack has two smooth surfaces that are coincident and join within the body along a smooth curve called the crack front; in two-dimensional representations, the crack front is called the crack tip. 用于弹性应力分析的裂纹简化模型。在无应力物体中，裂纹有两个光滑表面，它们在物体内沿称为裂纹前缘的平滑曲线重合并连接；在二维表示中，裂纹前缘称为裂纹尖端。 |
| Degradation | 降解 |
The reduction with time of the physical properties of a material. 材料的物理性质随时间的减少。 |
| Angle of friction | 摩擦角 |
(friction angle, β) (Unit °) For a body in contact with a plane surface, the angle between the normal to the surface and the resultant force between the body and the surface. If the friction force is F and normal force is N, β is given by F/N = μ = tan β where μ is the coefficient of friction. （摩擦角，β）（单位°）对于与平面接触的物体，表面法线与物体与表面之间的合力之间的夹角。如果摩擦力为F，法向力为N，则β由F/N=μ=tanβ给出，其中μ是摩擦系数。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Rockwell superficial hardness test | 洛氏表面硬度试验 |
Same as Rockwell hardness test, except that smaller minor and major loads are used. 与洛氏硬度测试相同，只是使用较小的次要载荷和主要载荷。 |
| Assembly drawing | 装配图纸 |
An engineering drawing that shows how parts are assembled to produce a component or a complete machine. It may include sections to show internal features, dimensions that are critical for assembly, manufacturing information, and part numbers. 显示零件如何组装以生产组件或整机的工程图。它可能包括显示内部特征、对装配至关重要的尺寸、制造信息和零件编号的部分。 |
| Fatigue crack growth rate (da/dN) | 疲劳裂纹扩展率（da/dN） |
The rate of crack extension caused by constant-amplitude fatigue loading, expressed in terms of crack extension per cycle of load application. 恒幅疲劳荷载引起的裂纹扩展速率，以每次荷载施加循环的裂纹扩展表示。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Fatigue life (N) | 疲劳寿命（N） |
The number of cycles of stress or strain of a specified character that a given specimen sustains before failure occurs. 给定试样在失效发生之前所承受的特定特征的应力或应变的循环次数。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Rotary blower | 旋转鼓风机 |
(rotary compressor) A positive-displacement gas compressor which may be of the blade type, helical-screw type, meshing-lobe type (the Roots blower), or sliding-vane type. （旋转式压缩机）一种容积式气体压缩机，可以是叶片式、螺旋式、啮合凸角式（罗茨鼓风机）或滑动叶片式。 |
| Thermal insulation (insulation) | 隔热（绝缘） |
A material that may be a low-conductivity solid, or a porous solid or fabric in which there are voids containing air or another gas, resulting in overall low thermal conductivity. When applied to the surface of a hot or cold object, surface heat transfer is generally reduced. 一种材料，可以是低导电性固体，或多孔固体或织物，其中存在含有空气或其他气体的空隙，从而导致整体低导热性。当应用于热或冷物体的表面时，表面传热通常减少。 |
| Inch-pound force/inch² | 英寸磅力/英寸² |
A non-SI unit for the specific work of fracture (fracture toughness). The conversion to SI is 1 in.lbf/in² = 1.751 268 × 102 J/m². 用于特定断裂功（断裂韧性）的非国际单位制单位。到SI的转换为1英寸。lbf/in²=1.751268×102J/m²。 |
| Thermal efficiency | 热效率 |
The ratio, for a heat engine or thermodynamic cycle, of the net work output to the net heat input into the system. 对于热机或热力循环，净功输出与系统净热输入的比率。 |
| Nautical mile (M) | 海里（M） |
A special unit of distance employed for marine and aerial navigation. The conversion to SI is 1 M = 1 852 m. 用于海上和空中导航的特殊距离单位。SI的转换为1M＝1852m。 |
| Shock load | 冲击载荷 |
The sudden application of an external force that results in a very rapid build-up of stress. 突然施加外力，导致应力迅速增加。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| Forging cracks | 锻造裂纹 |
This may occur during fastener manufacturing at the cutting or forging operations and are located on the top of the head or on the raised periphery of indented head bolts. 这可能发生在紧固件制造过程中的切削或锻造操作中，并且位于头部的顶部或带锯齿的头部螺栓的凸起周边上。 |
| Initial preload | 初始预载 |
The tension created in a single bolt as it is tightened. Will usually be modified by subsequent assembly operations or by in-service loads and conditions. 拧紧单个螺栓时产生的张力。通常会通过后续的装配操作或在役负载和条件进行修改。 |
| Selective heating | 局部加热 |
Intentionally heating only certain portions of a workpiece. 有意仅加热工件的某些部分。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Dead load (Unit N) | 静载（单位N） |
A load on a component or structure that is steady with time, e.g. the self-weight of a bridge. 部件或结构上随时间稳定的载荷，例如桥梁的自重。 |
| Liquid nitriding | 液体氮化 |
A method of surface hardening in which molten nitrogen-bearing, fused-salt baths containing both cyanides and cyanates are exposed to parts at subcritical temperatures. 一种表面硬化方法，其中含有氰化物和氰酸盐的熔融含氮熔盐浴在亚临界温度下暴露于零件。 |
| Computer-aided manufacturing | 计算机辅助制造 |
(CAM, computer-integrated manufacturing, CIM) The use of computers in all branches of manufacturing, not only to control machines and robots for manufacturing and assembly, but also for process planning, and monitoring progress of materials and components during production, etc. （CAM，计算机集成制造，CIM）在制造的所有分支中使用计算机，不仅可以控制制造和组装的机器和机器人，还可以进行工艺规划，以及在生产过程中监控材料和组件的进度等。 |
| Delamination | 分层 |
A mode of failure of composite materials, including radial-ply tyres, in which the layers separate due to repeated cyclic loading, impact, or weak bonding. 复合材料的一种失效模式，包括子午线轮胎，其中层由于重复的循环载荷、冲击或弱粘合而分离。 |
| Proof strength (Unit Pa) | 验证强度（单位Pa） |
(proof stress, Rp, Rp,) The yield strength (offset yield strength) at some fixed value of the permanent strain given by the intersection of a line offset from, but parallel to, the elastic loading line and the engineering stress-engineering strain curve. The offset is arbitrary but is usually 0.1, 0.2, or 0.5% permanent strain (the proof strain). Used for materials which do not exhibit a sharply defined yield point. The notation Rp0.2 or Rp0.2 is employed for the 0.2% proof stress. （验证应力，Rp）在永久应变的某个固定值下的屈服强度（偏移屈服强度），由偏离但平行于弹性加载线的线与工程应力-工程应变曲线的交点给出。偏移是任意的，但通常为0.1、0.2或0.5%的永久应变（验证应变）。用于没有明确定义屈服点的材料。对于0.2%的验证应力，采用符号Rp0.2。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| R-curve/Resistance curve | 阻力曲线 |
In linear-elastic fracture mechanics, a plot of crack-extension resistance as a function of stable crack extension, which is either the difference between the physical crack size, or the effective crack size, and the original crack size. R-curves normally depend on specimen thickness and, for some materials, on temperature and strain rate. An increase in fracture toughness with crack propagation shown by rising plots of toughness vs growing crack length. 在线弹性断裂力学中，作为稳定裂纹扩展函数的裂纹扩展阻力图，即物理裂纹尺寸或有效裂纹尺寸与原始裂纹尺寸之间的差值。R曲线通常取决于试样厚度，对于某些材料，还取决于温度和应变率。是随着裂纹扩展，断裂韧性增加，表现为韧性与扩展裂纹长度的上升曲线。 |
| Radial load (Unit N) | 径向负荷（单位：N） |
1. Centrifugal loading induced in a rotating body. 2. (through-wallthickness load) The radial component of loading arising from internal or external pressurization of a closed vessel. There will also be axial and hoop loading. 1.旋转体中产生的离心载荷。2.（贯穿壁厚载荷）由封闭容器的内部或外部加压产生的载荷的径向分量。还存在轴向和环向载荷。 |
| Dynamic load (Unit N) | 动态负载（单位N） |
1. Loading of a component or structure by a moving object whose point of application changes with time, e.g. the live load of a train passing over a bridge. 2. A load applied to a particular part of a component or structure in a short time interval. 1. 应用点随时间变化的移动物体对部件或结构的加载，例如通过桥梁的火车的活荷载。2. 在短时间内施加到部件或结构的特定部分的载荷。 |
| Batch | 一批 |
A definite quantity of some product or material produced under conditions that are considered uniform. A batch is usually smaller than a lot. 在被认为是均匀的条件下生产的一定数量的某些产品或材料。批次通常小于很多。 |
| Slenderness ratio | 长细比 |
The effective unsupported length of a uniform column divided by the least radius of gyration of the cross-sectional area. 均匀柱的有效无支撑长度除以横截面积的最小回转半径。 |
| Effective crack size (ae) | 有效裂纹尺寸（ae） |
The physical crack size augmented for the effects of cracking plastic deformation. Sometimes the effective crack size is calculated from a measured value of a physical crack size plus a calculated value of a plastic-zone adjustment. A preferred method for calculation of effective crack size compares compliance from the secant of a load-deflection trace with the elastic compliance from a calibration for the type of specimen. 由于裂纹塑性变形的影响，物理裂纹尺寸增大。有时，根据物理裂纹尺寸的测量值加上塑性区调整的计算值来计算有效裂纹尺寸。计算有效裂纹尺寸的首选方法是将载荷-挠度轨迹正割的柔度与试样类型校准的弹性柔度进行比较。 |
| Lead screw | 丝杠 |
The master screw running along the length of the bed of a lathe from which all screws threads on that machine are cut. Master screw used for cutting a screw thread in a lathe. 沿车床床身长度方向运行的主螺钉，该机床上的所有螺钉和螺纹都从主螺钉上切割下来。用于在车床上切削螺纹的主螺钉。 |
| Condenser vacuum | 冷凝器真空 |
The sub-atmospheric pressure imposed on the condenser of a steam-power plant which leads to an appreciable increase in overall efficiency. 施加在蒸汽发电厂冷凝器上的低于大气压的压力导致整体效率显着提高。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Stress distribution | 应力分布 |
The manner in which tensile, compressive, and shear stresses are distributed within a loaded body, indicated by loci of constant stress. 拉应力、压应力和剪应力在受载物体内的分布方式，由恒定应力轨迹表示。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Hydraulic air compressor | 液压空气压缩机 |
1. A compressor powered by a hydraulic motor. 2. A device in which air is compressed as a result of being entrained in water flowing in a downcomer pipe. The compressed air is released in a chamber at the bottom of the pipe. 1. 由液压马达驱动的压缩机。2.一种装置，其中空气由于夹带在降液管中流动的水中而被压缩。压缩空气在管道底部的腔室中释放。 |
| Ductile crack propagation | 延性裂纹扩展 |
Slow crack propagation that is accompanied by noticeable plastic deformation and requires energy to be supplied from outside the body. 缓慢的裂纹扩展，伴随着明显的塑性变形，需要从外部提供能量。 |
| Centrifugal compressor | 离心式压缩机 |
A compressor in which kinetic energy is added to a fluid by radial acceleration in an impeller and then converted into a pressure increase by flow though a diffuser. 一种压缩机，其中动能通过叶轮中的径向加速度添加到流体中，然后通过扩散器的流动转换为压力增加。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Screw extractor | 螺钉拔 |
A device for removing broken-off screws from threaded holes. It resembles a drill with, for broken right-hand threads, a fast (long-pitch) left-hand thread that is driven into a hole drilled in the broken screw, thus untwisting it. 从螺纹孔中去除断裂螺钉的装置。它类似于一个钻头，对于断裂的右螺纹，一个快速（长螺距）的左螺纹被打入在断裂螺钉上钻的孔中，从而将其松开。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Semi-rotary pump | 半回转泵 |
A form of self-priming pump, often hand-operated, suitable for pumping water and light oils such as diesel oil and petrol. As shown in the diagram, liquid is sucked into one side of the pump through flap valves and simultaneously ejected from the other side on one stroke. The sequence is reversed on each successive stroke. 一种自吸泵，通常是手动的，适用于泵送水和轻油，如柴油和汽油。液体通过翻板阀吸入泵的一侧，同时在一个冲程中从另一侧排出。在每个连续冲程上，顺序颠倒。 |
| Diesel engine | 柴油发动机 |
(compression–ignition engine) A piston engine operating on the Diesel cycle in which the air is compressed to a temperature above the autoignition temperature of the fuel and combustion is initiated as the fuel is injected into the hot air. Diesel engines operate at higher compression ratios (typically in the range 12 to 24) than petrol engines. Although named after Rudolf Diesel, the inventor, Diesel engine is often spelled with a lower case d, contrary to normal practice. （压燃式发动机）在柴油循环中运行的活塞式发动机，在该循环中，空气被压缩至高于燃料自燃温度的温度，当燃料喷射到热空气中时，燃烧开始。柴油发动机在比汽油发动机更高的压缩比下运行（通常在12到24的范围内）。虽然以发明人鲁道夫·迪塞尔命名，但迪塞尔发动机通常拼写为小写d，这与正常做法相反。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Castellated nut | 槽形螺母 |
A nut having slots across the hexagonal faces, used with a bolt having a drilled hole so that a split (cotter) pin may be inserted through both nut and bolt to prevent unscrewing. 一种在六角面上有槽的螺母，与具有钻孔的螺栓一起使用，以便将开口（开口）销插入穿过螺母和螺栓以防止拧松。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Newton (N) | 牛顿（N） |
The basic unit of force in the SI system, defined as the force that results in an acceleration of 1 m/s² when acting on a 1 kg mass. SI国际单位制中力的基本单位，定义为作用于1kg质量时产生1m/s²加速度的力。 |
| Fastener testing | 紧固件测试 |
A determination or verification that the fastener meets its specification requirements. 确定或验证紧固件符合其规范要求。 |
| Manometer | 压力计 |
An instrument used in the measurement of a pressure difference in a fluid (manometry). 用于测量流体压力差（测压）的仪器。 |
| Heat-capacity ratio (c*) | 热容量比（c*） |
A non-dimensional parameter that arises in the analysis of heat exchangers, defined as the ratio cMIN/cMAX where cMIN is the heat-capacity rate c for the fluid with the smaller value of c and cMAX the value for the fluid with the larger value of c. Different flow rates and specific-heat values give rise to different values for c. 热交换器分析中出现的无量纲参数，定义为比率cMIN/cMAX其中cMIN是流体的热容率c，c值较小，cMAX是流体的值具有较大的c值。不同的流速和比热值产生不同的c值。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| Crushing strain | 压应变 |
The supposed single strain that results in comminution of a brittle material. The corresponding stress is termed the crushing strength. Neither quantity can be a material constant as they must obey the laws of fracture mechanics and will depend on the type of testpiece, method of loading etc. 导致脆性材料粉碎的假定单应变。相应的应力称为抗压强度。这两个量都不能是材料常数，因为它们必须遵守断裂力学定律，并取决于试件类型、加载方法等。 |
| Shear strength (Unit Pa) | 抗剪强度（单位Pa） |
The maximum shear stress that can be withstood by a material either (a) before plasticity occurs or (b) before rupture. 材料在（a）塑性发生之前或（b）断裂之前能够承受的最大剪切应力。 |
| Profilometer | 轮廓仪 |
An instrument used to quantify the roughness of a surface. For a contact profilometer, a diamond stylus sweeps across the surface along a series of parallel lines. Noncontact profilometers use optical techniques to map the surface irregularities. 用于量化表面粗糙度的仪器。对于接触式轮廓仪，钻石触针沿一系列平行线扫过表面。非接触式轮廓仪使用光学技术绘制表面不规则。 |
| Gear ratio | 传动比 |
For two gears in contact, the ratio of the number of teeth on the driving gear to that on the driven gear. 对于接触的两个齿轮，主动齿轮上的齿数与从动齿轮上的齿数之比。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Pin or mandrel | 销或心轴 |
In bend testing, the plunger or tool used in making semiguided, guided, or wrap-around tests to apply the bending force to the inside surface of the bend. In free bends or semiguided bends to an angle of180°, a shim or block of the proper thickness may be placed between the legs of the specimen as bending is completed. This shim or block is also referred to as a pin or mandrel. 在弯曲测试中，用于进行半导向、导向或环绕测试以将弯曲力施加到弯曲内表面的柱塞或工具。在180°角的自由弯曲或半导向弯曲中，弯曲完成后，可在试样支腿之间放置适当厚度的垫片或垫块。该垫片或垫块也称为销或心轴。 |
| Nut box mechanism | 螺母箱机械装置 |
In a lathe it is used to engage and disengage the lead screw for thread cutting. This comprises a pair of half-nuts capable of sliding in vertical slides in or out of mesh with the lead screw. 在车床中，它用于接合和分离丝杠以进行螺纹切削。这包括一对半螺母，能够在与丝杠啮合的垂直滑动中滑动。 |
| Turbine pump (turbopump) | 涡轮泵 |
An axial or centrifugal pump driven by a turbine. Typically used to supply fuel to the combustion chamber of a rocket engine such as on the space shuttle. 由涡轮驱动的轴向或离心泵。通常用于向火箭发动机（如航天飞机）的燃烧室供应燃料。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Stress raisers | 局部应力集中 |
Changes in contour or discontinuities in structure that cause local increases in stress. 导致局部应力增加的轮廓变化或结构不连续性变化。 |
| Anti-freeze | 防冻液 |
A substance such as ethylene glycol added to the cooling system of a watercooled engine to lower the freezing point of the cooling water and also inhibit the formation of rust and other deposits. 一种物质，如乙二醇，添加到水冷发动机的冷却系统中，以降低冷却水的冰点，并抑制生锈和其他沉积物的形成。 |
| Semiguided bend | 半导弯曲 |
The bend obtained by applying a force directly to the specimen in the portion that is to be bent. The specimen is either held at one end and forced around a pin or rounded edge, or is supported near the ends and bent by a force applied on the side of the specimen opposite the supports and midway between them. In some instances, the bend is started in this manner and finished in the manner of a free bend. 通过将力直接施加于待弯曲部分中的试样而获得的弯曲。将试样固定在一端，并围绕销或圆边施力，或者在靠近端部的位置支撑试样，并通过施加在试样与支撑件相对的一侧以及两者中间的力进行弯曲。在某些情况下，折弯以此方式开始，然后以自由折弯的方式结束。 |
| Thermochemical treatment | 热化学处理 |
Heat treatment carried out in a medium suitably chosen to produce a change in the chemical composition of the object by exchange with the medium. 在适当选择的介质中进行热处理，以通过与介质交换产生物体化学成分的变化。 |
| Slip line | 滑移线 |
The trace of the slip plane on a viewing surface; the trace is usually observable only if the surface has been polished before deformation. The usual observation on metal crystals (under the light microscope) is of a cluster of slip lines known as a slip band. 滑动平面在观察表面上的轨迹；只有在变形前对表面进行抛光，才能观察到痕迹。通常对金属晶体的观察（在光学显微镜下）是一组称为滑移带的滑移线。 |
| Balance piston | 平衡活塞 |
(balance drum, dummy piston) A disc attached to the shaft of a turbine or compressor, to one side of which high or low pressure is applied to counteract the axial thrust produced by the pressure change across the machine. A form of thrust bearing. （平衡鼓，假活塞）连接在涡轮机或压缩机轴上的圆盘，在其一侧施加高压或低压，以抵消机器压力变化产生的轴向推力。推力轴承的一种形式。 |
| Fillister head | 槽头 |
Similar to a pan head but with a smaller head diameter and a taller head, with higher vertical sides. 类似于盘头，但头部直径较小，头部较高，垂直边较高。 |
| Centrifugal pump | 离心泵 |
A pump into which liquid enters axially through the eye of the casing and is then accelerated through an impeller, thereby increasing both its kinetic energy and pressure before being delivered to a ring diffuser (the volute) that further increases the liquid pressure and from which it leaves. 一种泵，液体通过泵壳的眼轴向进入，然后通过叶轮加速，从而在输送到环形扩散器（蜗壳）之前增加其动能和压力，从而进一步增加液体压力并从中流出树叶。 |
| Dynamic compressor | 动态压缩器 |
A machine, such as a centrifugal or axial compressor, that compresses a gas by rotational rather than reciprocating motion. 一种机器，例如离心式或轴流式压缩机，通过旋转而不是往复运动来压缩气体。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Failure of the bolt | 螺栓失效 |
Term implying that the bolt has broken or the threads have stripped. There can be many reasons for this. 表示螺栓断裂或螺纹脱落的术语。原因可能有很多种。 |
| Kiln | 窑 |
An industrial oven for burning, baking, or drying. 用于燃烧、烘烤或干燥的工业烤箱。 |
| Impact strength | 冲击强度 |
The resiliency or toughness of a solid as measured by impact energy. 用冲击能量测量的固体的弹性或韧性。 |
| Flame annealing | 火焰退火 |
Annealing in which the heat is applied directly by a flame. 通过火焰直接加热的退火。 |
| Centrifugal fan | 离心风机 |
A machine with a rotor consisting of a number of blades mounted around a hub and used for moving air or other gases. The gas enters the rotor axially and is discharged radially at increased pressure. 一种带有转子的机器，转子由安装在轮毂周围的许多叶片组成，用于移动空气或其他气体。气体轴向进入转子并在增加的压力下径向排出。 |
| Proof stress | 弹性极限应力 |
(1) The stress that will cause a specified small permanent set in a material. (2) A specified stress to be applied to a member or structure to indicate its ability to withstand service loads. （1）在材料中引起规定的小永久变形的应力。（2）施加在构件或结构上的规定应力，以表明其承受工作荷载的能力。 |
| Die screw | 模具螺丝 |
Tool used when threading cylindrical pieces beyond the capacity of a die plate. 对超出模板容量的圆柱件进行螺纹加工时使用的工具。 |
| Coil spring | 螺旋弹簧 |
A spiral (‘clockwork’) or helical (cylindrical) spring. A spring steel wire wound in a spiral pattern. 螺旋（“发条”）或螺旋（圆柱形）弹簧。以螺旋状缠绕的弹簧钢丝。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Turn-of-nut method | 螺母转动法 |
It applies preload by turning a nut through an angle that corresponds to a given elongation. 它通过将螺母旋转一个与给定伸长率相对应的角度来施加预载荷。 |
| Toothed gearing | 齿轮传动 |
In principle, friction between circular discs in tangential contact could be used to transmit rotation and power between shafts, but the power level would be very limited and the velocity ratio affected by slip. To make the drive positive, gear wheels are used instead in which teeth extend above and below the diameters (the pitch-circle diameters) of discs in ideal rolling contact. The diagram shows the nomenclature for spur gears, the simplest type of gearing between parallel shafts, which are cylindrical in shape with straight teeth parallel to the axis of rotation. 原则上，切向接触的圆盘之间的摩擦可用于在轴之间传递旋转和动力，但动力水平非常有限，速比受滑动的影响。为了使驱动积极，使用齿轮代替，齿轮中的齿延伸到理想滚动接触的圆盘直径（节圆直径）的上方和下方。该图显示了直齿轮的名称，这是平行轴之间最简单的齿轮传动类型，其形状为圆柱形，直齿平行于旋转轴。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Flexural strength | 抗弯强度 |
The maximum stress in the outer fiber at the moment of crack or break. 断裂或断裂时刻外层纤维的最大应力。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Face | 表平面 |
To machine a flat surface perpendicular to the axis at rotation on a lathe. 在车床上加工一个垂直于旋转轴的平面。 |
| Washer | 垫圈 |
An annular disc of metal, rubber, plastic, ceramic, etc., placed between two surfaces in contact either to spread the load (for example, between a surface and a tightened nut or a bolt head), to provide a seal, or to separate or align components. 由金属、橡胶、塑料、陶瓷等制成的环形圆盘，放置在两个接触面之间，以分散载荷（例如，在一个表面和拧紧的螺母或螺栓头之间），提供密封，或分离或对齐部件。 |
| Lock-nut pipe thread | 锁紧螺母管螺纹 |
The lock-nut pipe thread is a straight thread of the largest diameter which can be cut on a pipe. Its form is identical with that of the American or Briggs standard taper pipe thread. In general, “Go” gages only are required. These consist of a straight-threaded plug representing the minimum female lock-nut thread, and a straight-threaded ring representing the maximum male lock-nut thread. This thread is used only to hold parts together, or to retain a collar on the pipe. It is never used where a tight threaded joint is required. 锁紧螺母管螺纹是最大直径的直螺纹，可在管道上切割。其形式与美国或布里格斯标准锥管螺纹相同。一般情况下，只需要通规。它们由一个表示最小内螺纹锁紧螺母螺纹的直螺纹塞和一个表示最大外螺纹锁紧螺帽螺纹的直形螺纹环组成。该螺纹仅用于将零件固定在一起，或用于将轴环固定在管道上。切勿使用于需要紧密螺纹接头的情况下。 |
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Fastener manufacturer | 紧固件制造商 |
An organization that fabricates raw steel into a fastener meeting specified standards. 将生钢加工成符合规定标准的紧固件的组织。 |
| Turbo generator | 涡轮发电机 |
(turboset) The combination of a steam or gas turbine and an electrical generator with a single shaft or connected coaxial shafts. （汽轮发电机组）蒸汽或燃气轮机与发电机的组合，具有单轴或连接的同轴。 |
| Square thread | 方螺纹 |
A form of screw thread in which the cross–section of the thread forms a square, making the width of the thread equal to the space between the threads. 螺纹的一种形式，螺纹的横截面形成正方形，使螺纹的宽度等于螺纹之间的间距。 |
| Testing machine (load-measuring type) | 试验机（负载测量型） |
A mechanical device for applying a load (force) to a specimen. 向试样施加载荷（力）的机械装置。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Grinding stress (Unit Pa) | 磨削应力（单位Pa） |
The residual stresses left in the surface of a component after grinding, owing to non-uniform cooling from the high surface temperatures produced. 由于产生的高表面温度造成的不均匀冷却，磨削后留在部件表面的残余应力。 |
| Amplifier | 放大器 |
A device by which the output of a hydraulic, pneumatic, or electrical source is increased. 增加液压、气动或电源输出的装置。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Depth gauge | 深度计 |
1. A precision instrument, typically consisting of a machine-divided steel rule passing through a hardened-steel cross head, used to measure the depths of slots, holes, shoulders, projections, etc. 2. A device used by divers to indicate the water depth. 1. 一种精密仪器，通常由穿过硬化钢十字头的机器分割钢尺组成，用于测量槽、孔、肩部、突起等的深度。 2. 潜水员用来指示深度的装置水深。 |
| Turbine flow meter | 涡轮流量计 |
(axial flow meter, propeller meter) An in-line flow meter in which the rotation speed N of a propeller or rotor is a measure of the mass flowrate ṁ. Calibration is always necessary but with appropriate design ṁ is closely proportional to N over a wide range. （轴向流量计、螺旋桨流量计）一种串联流量计，其中螺旋桨或转子的转速N是质量流量的测量值ṁ. 校准总是必要的，但需要适当的设计ṁ在很宽的范围内与N成正比。 |
| Temperature (Unit K or °C) | 温度（单位K或°C） |
A quantitative measure of the molecular kinetic energy of a substance and so how hot or cold it is. 物质分子动能的定量量度，以及它的冷热程度。 |
| Spalling | 剥落 |
The separation of macroscopic particles from a surface in the form of flakes or chips. 以薄片或碎片形式从表面分离宏观颗粒。 |
| Nominal power (Unit kW) | 公称功率（单位kW） |
1. For an internal combustion engine, the average power output of a typical production engine under normal working conditions measured according to SAE standard J 1349/ISO 1585. 2. For an electric motor, the rated equivalent mechanical power output. 1.对于内燃机，根据SAE标准J 1349/ISO 1585测量的正常工作条件下典型生产发动机的平均功率输出。2.对于电动机，额定等效机械功率输出。 |
| Union (union joint) | 活接头 |
A threaded pipe fitting that allows two pipes to be connected anddetached without the need for either to be rotated, and without damaging the pipe ends. 一种螺纹管件，允许连接和拆卸两个管道，而无需旋转任何一个管道，且不会损坏管道端部。 |
| Air composition | 空气成分 |
The sea-level composition (in per cent by volume) of air at a temperature of 15°C and a pressure of 1 atm is mainly 78.084% nitrogen, 20.947% oxygen and 0.934% argon. The remaining 0.035% consists of carbon dioxide, neon, helium, methane, krypton, hydrogen, oxides of nitrogen, xenon, ozone, iodine, carbon monoxide, and ammonia. Different sources give slightly different figures for the composition. Not included are water vapour (typically 0.4%) and pollutants such as sulfur dioxide. 在15°C的温度和1个大气压的压力下，空气的海平面成分（体积百分比）主要是78.084%的氮气、20.947%的氧气和0.934%的氩气。剩余的0.035%由二氧化碳、氖、氦、甲烷、氪、氢、氮的氧化物、氙、臭氧、碘、一氧化碳和氨组成。不同的来源给出的组成略有不同。不包括水蒸气（通常为0.4%）和二氧化硫等污染物。 |
| Annealing twin | 退火孪晶 |
A twin form in a crystal during recrystallization. 重结晶过程中晶体中的孪晶形式。 |
| Inch (in) | 英寸（in） |
A non-SI unit of length now defined as 25.4 mm. The conversion to SI is 1 in = 2.54 × 10−2 m. 现在定义为25.4毫米的非SI长度单位。转换为SI为1in=2.54×10-2m。 |
| Pressure regulator | 压力调节器 |
(pressure-regulating valve) A device installed in a pneumatic or gas system to maintain the downstream pressure at the required level. （压力调节阀）安装在气动或气体系统中以将下游压力保持在所需水平的装置。 |
| Toggle (toggle clamp) | 拨动（拨动夹） |
A device consisting of two pinned levers that are almost in line between two end points in the same plane. Bringing the levers into line generates large forces between the ends. Used to obtain a large mechanical advantage or as a locking mechanism. 由两个销杆组成的装置，在同一平面的两个端点之间几乎成一条直线。将杠杆对齐会在端部之间产生较大的力。用于获得较大的机械优势或用作锁定机构。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Tensile strength (Unit Pa) | 抗拉强度（单位Pa） |
In tension testing, the ratio of maximum load to original cross-sectional area. Also known as ultimate strength. The resistance that a material offers to tensile stress. It is defined as the smallest tensile stress required to break the body. (ultimate strength, ultimate tensile strength, UTS, Rm, Rm) The nominal or engineering stress given by the maximum load in a tension test divided by the original cross-sectional area of the specimen. The maximum load could be the fracture load for a brittle material, but for a ductile material it is usually taken as the load at which necking begins, beyond which the load falls. 在拉伸试验中，最大载荷与原始横截面积之比。也称为极限强度。材料对拉伸应力的抵抗力。它被定义为破坏主体所需的最小拉伸应力。（极限强度、极限抗拉强度、UTS、Rm、Rm）拉伸试验中最大载荷除以试样原始横截面积得出的标称或工程应力。对于脆性材料，最大载荷可以是断裂载荷，但对于韧性材料，最大荷载通常被视为颈缩开始时的载荷，超过该载荷时，载荷下降。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Tightness | 紧密度 |
A measure of the mass leak rate from a gasketed joint. 垫圈接头质量泄漏率的测量值。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Ferritizing anneal | 铁素体化退火 |
A treatment given as-cast gray or ductile (nodular) iron to produce an essentially ferritic matrix. For the term to be meaningful, the final microstructure desired or the time-temperature cycle used must be specified. 给予铸态灰铁或球墨铸铁以产生基本铁素体基体的处理。为了使该术语有意义，必须指定所需的最终微观结构或使用的时间-温度循环。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Twist | 扭转 |
The helix produced in a cylindrical component, such as a shaft, wire, tensioned cable, or rope, when one end is rotated relative to the other. Measured either as the number of turns per unit length, or by the helix angle (twist angle). 当一端相对于另一端旋转时，在圆柱形部件（如轴、钢丝、张紧电缆或绳索）中产生的螺旋。以每单位长度的圈数或螺旋角（扭曲角）测量。 |
| Hypereutectic alloy | 过共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of alloying element compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，任何合金，其组成与共晶组成相比具有过量的合金元素，并且其平衡微观结构包含一些共晶结构。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| Corrosion cell | 腐蚀电池 |
A natural ‘‘battery’’ formed when two metals having different electrical potentials (an Anode and a Cathode) are connected together in the presence of a liquid (the Electrolyte). 当两种具有不同电势的金属（阳极和阴极）在液体（电解质）存在下连接在一起时形成的天然“电池”。 |
| Pressure rating (Unit Pa or bar) | 额定压力（单位Pa或bar） |
The internal pressure at which a pressure vessel, boiler, tank, piping, etc. is designed to operate safely. 压力容器、锅炉、储罐、管道等设计用于安全运行的内部压力。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Principal stress (normal) | 主应力（正常） |
The maximum or minimum value of the normal stressat a point in a plane considered with respect to all possible orientations of the considered plane. On such principal planes the shear stress is zero. There are three principal stresses on three mutually perpendicular planes. The state of stress at a point may be: (1) uniaxial, a state of stress in which two of the three principal stresses are zero; (2) biaxial, a state of stress in which only one of the three principal stresses is zero; or (3) triaxial, a state of stress in which none of the principal stresses is zero. Multiaxial stress refers to either biaxial or triaxial stress. 相对于所考虑平面的所有可能方向，所考虑平面中某点处的法向应力的最大值或最小值。在这样的主平面上，剪切应力为零。在三个相互垂直的平面上有三个主应力。一点的应力状态可以是：（1）单轴，三个主应力中的两个为零的应力；（2）双轴，三个主应力中只有一个为零的应力状态；或（3）三轴，即主应力均不为零的应力状态。多轴应力是指双轴或三轴应力。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Acceleration due to gravity | 重力加速度 |
(acceleration of free fall, gravitational acceleration, g) (Unit m/s²) The acceleration of a freely-falling body in a vacuum, with a mean value at sea level of approximately 9.81 m/s². （自由落体加速度，重力加速度，g）（单位m/s²）自由落体在真空中的加速度，在海平面处的平均值约为9.81m/s²。 |
| Compression pressure (Unit Pa) | 压缩压力（单位Pa） |
The pressure produced in a cylinder of a piston engine by compression of air in the absence of fuel. 在没有燃料的情况下通过压缩空气在活塞发动机的气缸中产生的压力。 |
| International Practical Temperature Scale (IPTS) | 国际实用温标（IPTS） |
A close approximation to the thermodynamic temperature scale based upon the triple points of hydrogen (13.8 K), neon (24.6 K), oxygen (54.4 K), argon (83.8 K), mercury (234.3 K), and water (273.2 K); the melting point of gallium (302.9 K); and the freezing points of indium (429.7 K), tin (505.1 K), zinc (692.7 K), aluminium (933.5 K), silver (1 234.9 K), gold (1 337.3 K), and copper (1 基于氢（13.8K）、氖（24.6K）、氧（54.4K）、氩（83.8K），汞（234.3K）和水（273.2K）的三相点的热力学温度标度的近似值；镓的熔点（302.9K）；铟（429.7K）、锡（505.1K）、锌（692.7K），铝（933.5K）、银（1234.9K）、金（1337.3K）和铜等。 |
| Relative density | 相对密度 |
(specific gravity) The ratio of the density of a substance to that of a reference substance, such as water for liquids and solids, and dry air for gases. （比重）物质密度与参考物质密度之比，如液体和固体为水，气体为干燥空气。 |
| Strain-hardening exponent (n value) | 应变硬化指数（n值） |
The value n in the relationship σ = Kεn, where σ is the true stress, ε is the true strain, and K, the strength coefficient, is equal to the true stress at a true strain of 1.0. The strain hardening exponent is equal to the slope of the true stress/true strain curve up to maximum load, when plotted on log-log coordinates. The n-value relates to the ability of a sheet of material to be stretched in metalworking operations. The higher the n-value, the better the formability(stretchability). Also known as the strain-hardening coefficient. 关系式σ=Kεn中的值n，其中σ是真应力，ε是真应变，K是强度系数，等于真应变为1.0时的真应力。在对数坐标上绘制时，应变硬化指数等于真应力/真应变曲线的斜率，直到最大载荷。n值与一片材料在金属加工操作中拉伸的能力有关。n值越高，成形性（拉伸性）越好。也称为应变硬化系数。 |
| Fatigue | 疲劳 |
The phenomenon leading to fracture under repeated or fluctuating stresses having a maximum value less than the ultimate tensile strength of the material. Fatigue failure generally occurs at loads that, applied statically, would produce little perceptible effect. Fatigue fractures are progressive, beginning as minute cracks that grow under the action of the fluctuating stress. A term referring, in components and structures subjected to either random or cyclic periodically-varying loads, to a progressive reduction in strength leading to failure at stresses lower than those that cause failure under monotonic loading. Variable loads arise from outof-balance machinery and other vibration sources, wind gusts, etc., and a large proportion of service failures is caused by fatigue. Fatigue results from the initiation and slow propagation of cracks. In manufactured components, crack initiation usually occurs at a point of stress concentration. After a period, often of millions of stress cycles, the crack reaches a critical length at which the next peak load causes sudden brittle or ductile fracture. Fracture surfaces resulting from fatigue display characteristic striations or progression marks emanating from the crack initiation site during the slow crack growth period, with a different surface appearance for the final fracture. 在最大值小于材料极限抗拉强度的重复或波动应力下导致断裂的现象。疲劳失效通常发生在静态施加的载荷下，不会产生明显影响。疲劳断裂是渐进性的，从在波动应力作用下生长的微小裂纹开始。在承受随机或周期性变化载荷的部件和结构中，指强度逐渐降低，导致在低于单调载荷下导致失效的应力下发生失效的术语。可变负载由失衡的机械和其他振动源、阵风等引起，大部分故障是由疲劳引起的。疲劳是裂纹萌生和缓慢扩展的结果。在制造部件中，裂纹萌生通常发生在应力集中点。在一段时间（通常是数百万次应力循环）后，裂纹达到临界长度，此时下一个峰值载荷会导致突然脆性或韧性断裂。疲劳产生的断裂表面在缓慢裂纹扩展期间显示出从裂纹萌生部位发出的特征条纹或进展标记，最终断裂的表面外观不同。 |
| Pitch (Unit m) | 间距（单位：m） |
1. In a cascade of identical turbine or compressor blades, the distance between successive blades measured parallel to the leading edges. 2. For a screw thread, the distance between adjacent thread forms measured parallel to the thread axis. 3. For an aircraft, the vertical relationship between the nose and the horizon. The pitch axis is an axis in the plane of the wings of an aircraft, perpendicular to the centreline, about which the aircraft rotates. Pitch motion is the corresponding up or down movement of the aircraft nose. Pitch attitude is the angle between the centreline of an aircraft and the horizontal. The angle is positive when the nose is above its position when the centreline is horizontal. 1.在相同涡轮或压缩机叶片的叶栅中，平行于前缘测量的连续叶片之间的距离。2.对于螺纹，平行于螺纹轴线测量的相邻螺纹形状之间的距离。3.对于飞机，机头和水平线之间的垂直关系。俯仰轴是飞机机翼平面内垂直于中心线的轴，飞机绕中心线旋转。俯仰运动是飞机机头的相应向上或向下运动。俯仰姿态是飞机中心线与水平线之间的角度。当中心线水平时，当机头高于其位置时，角度为正。 |
| Heat balance (heat budget) | 热平衡（热预算） |
An energy balance involving only heat transfer across the system boundary and the stored energy. 仅涉及跨系统边界的热传递和存储能量的能量平衡。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| Rotor | 转子 |
A part of a machine that rotates on a shaft (rotor shaft) about its own axis, such as the blade-carrying discs of a turbine, the blades of a helicopter, or the rotating parts of a Roots blower. 绕轴（转子轴）绕其自身轴线旋转的机器部件，如涡轮叶片、直升机叶片或罗茨鼓风机的旋转部件。 |
| Creep–time relations | 蠕变时间关系 |
Algebraic or numerical relations between creep strain and time at constant stress. 恒定应力下蠕变应变与时间之间的代数或数值关系。 |
| Centrifugal | 离心式 |
Acting or moving in a direction away from the axis of rotation of a rotating body. 沿远离旋转体的旋转轴的方向作用或移动。 |
| Serrations | 锯齿 |
A row of notches or tooth-like projections on an edge or surface. On an engineering drawing, serrations on the surface of a circular component are shown over about 60° of arc. 边缘或表面上的一排凹口或齿状突起。在工程图纸上，圆形部件表面的锯齿超过约60°的圆弧。 |
| Friction materials | 摩擦材料 |
Materials having a high coefficient of friction which, when coupled with a long life, may be employed as brake linings or the facing of the plates of a clutch. 具有高摩擦系数的材料，当与长寿命相结合时，可用作制动衬片或离合器片的饰面。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Working stress (Unit Pa) | 工作应力（单位Pa） |
The stress under which a component or structure is designed to operate under normal conditions. 部件或结构设计为在正常条件下运行的应力。 |
| Degradation of energy | 能源退化 |
Conversion of energy into forms of lower usefulness due to irreversibilities in energy transfer and conversion processes. The increase in entropy can be regarded as a measure of the degradation of energy. 由于能量转移和转换过程中的不可逆性，将能量转换为低效形式。熵的增加可以看作是能量退化的量度。 |
| Two-stage compressor | 两级压缩机 |
A machine in which gas is compressed from low pressure toan intermediate pressure in a low-pressure cylinder, and then to final pressure in a highpressure cylinder. Efficiency is improved if the two cylinders are separated by an intercooler. 一种机器，其中气体在低压气缸中从低压压缩到中压，然后在高压气缸中压缩到最终压力。如果两个气缸由中冷器分离，则效率提高。 |
| Torque monitor | 扭矩监测器 |
A torque tool control system which monitors the amount of torque being developed by the tool during use, but does not control the tool or the torque produced. 一种扭矩工具控制系统，监控工具在使用过程中产生的扭矩量，但不控制工具或产生的扭矩。 |
| Wire rope | 钢丝绳 |
A type of cable formed from individual strands of wire with a helical twist. 一种线缆，由具有螺旋扭曲的单独的线股形成。 |
| Cementation | 胶结 |
The introduction of one or more elements into the outer portion of a metal object by means of diffusion at high temperature. 在高温下通过扩散将一种或多种元素引入金属物体的外部。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Grip length | 夹紧长度 |
Combined thickness of all the things clamped together by the bolt and nut, including washers, gaskets, and joint members. 由螺栓和螺母夹紧在一起的所有部件的总厚度，包括垫圈、垫圈和接头构件。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Turbocharging | 涡轮增压 |
A method of supercharging in which the hot exhaust gas from a piston engine is used to drive a turbine which powers the supercharging compressor. A turbocharger is the turbine/compressor combination. The compressor is usually of radial outflow design while radial, axial, and mixed-flow turbines are all in use. The wastegate is a valve that reduces the flow of exhaust gas into the turbine to limit the boost produced or overspeeding. Not shown in the diagram are bearings, oil passages, etc. 一种增压方法，其中活塞发动机的热废气用于驱动涡轮，涡轮为增压压缩机提供动力。涡轮增压器是涡轮/压缩机组合。压缩机通常为径向流出设计，而径向、轴向和混流式涡轮机都在使用。废气旁通阀是一种减少进入涡轮的废气流量以限制产生的增压或超速的阀。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Absorptance | 吸收率 |
(absorptivity, absorption coefficient, α) The fraction of radiant flux incident on a surface that is absorbed by the surface. The term also applies to absorption of radiation by a volume of fluid. For a semi-transparent surface, α + ρ + τ = 1, where ρ is the reflectance and τ is the transmittance. （吸收率，吸收系数，α）入射到表面的辐射通量被表面吸收的部分。该术语也适用于一定体积的流体对辐射的吸收。对于半透明表面，α+ρ+τ=1，其中ρ是反射率，τ是透射率。 |
| Fastener quality | 紧固件质量 |
A fastener’s adherence to its specification for dimensional tolerances, mechanical properties, and other requirements stated under applicable standards. 紧固件对尺寸公差、机械性能和适用标准规定的其他要求的规范的遵守情况。 |
| Columnar structure | 柱状结构 |
A coarse structure of parallel elongated grains formed by unidirectional growth, most often observed in castings, but sometimes in structures resulting from diffusional growth accompanied by a solid-state transformation. 由单向生长形成的平行细长晶粒的粗略结构，最常见于铸件中，但有时也出现在伴随固态转变的扩散生长产生的结构中。 |
| Sampling frequency (Unit Hz) | 采样频率（单位Hz） |
(sampling rate) The number of measurement samples per unit time taken from a continuous analogue signal to produce a discrete signal. It is the inverse of the time between successive measurements (sampling interval, sampling period, or sampling time). （采样率）从连续模拟信号中提取以产生离散信号的每单位时间的测量样本数。它是连续测量之间时间的倒数（采样间隔、采样周期或采样时间）。 |
| Punch | 冲床 |
1. A hand tool with a sharp point, used to mark the position of a hole centre in a workpiece prior to drilling. 2. A flat-ended tool with sharp edges, used to shear out a hole in a plate that is supported underneath on a die having a slightly larger same-shaped orifice. 1.一种带有尖头的手动工具，用于在钻孔前标记工件中孔中心的位置。2.一种具有锐边的平头工具，用于剪切板上的孔，该板支撑在具有稍大相同形状孔口的模具下方。 |
| Screw pair | 螺旋副 |
Two links connected together to form a kinematic pair, in which the contacting surfaces are screw threads, so that their relative motion consists of rotation and sliding. 两个连杆连接在一起形成运动副，其中接触面为螺纹，因此它们的相对运动包括旋转和滑动。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Total elongation | 总伸长率 |
A total amount of permanent extension of a test piece broken in a tensile test. 拉伸试验中断裂试样的永久延伸总量。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Pressure snubber | 压力缓冲器 |
(pressure-pulse snubber) A device used for filtering, dampening, and the protection of transducers, pressure gauges, and switches, from pressure surges, pressure spikes, and water hammer. A typical design uses a fixed mesh or porous metal disc installed in an inline body. In a piston-type pressure-gauge snubber, a piston is forced against an orifice leading to the gauge. （压力脉冲缓冲器）一种用于过滤、阻尼和保护传感器、压力表和开关免受压力浪涌、压力尖峰和水锤影响的装置。典型的设计使用安装在内联阀体中的固定网格或多孔金属盘。在活塞式压力表缓冲器中，活塞被压靠在通向压力表的孔口上。 |
| Bolt stress (Unit Pa) | 螺栓应力（单位Pa） |
The axial tensile stress induced in a bolt by tightening. 通过拧紧在螺栓中产生的轴向拉应力。 |
| Multiple threaded screw | 多螺纹螺钉 |
A screw with two or more threads cut around the periphery of the workpiece to provide an increased lead with a specified pitch. 一种螺钉，具有围绕工件周边切割的两个或多个螺纹，以提供具有指定螺距的增加的导程。 |
| DIN | DIN |
Deutsches Institut für Normung, the German Institute for Standardization. Deutsches Institut für Normung，德国标准化研究所。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Natural unit system (n.u. system) | 自然单位制（n.u.制） |
A non-SI system of units, based on fundamental constants, used in high-energy and particle physics. The n.u. of speed is the speed of light in a vacuum, c0 = 299 792 458 m/s. 基于基本常数的非国际单位制，用于高能和粒子物理n.u.速度是真空中的光速，c0=299792458m/s。 |
| Shoulder joint | 轴肩关节 |
The second joint on an articulated robot, which has a horizontal axis and is analogous to the human shoulder. 关节机器人上的第二个关节，具有水平轴，类似于人的肩膀。 |
| Compressor | 压缩机 |
A turbomachine, of either axial or radial type, that increases the pressure of a gas or vapour. 一种增加气体或蒸汽压力的轴向或径向涡轮机。 |
| Laser sintering | 激光烧结 |
A manufacturing technique by which parts are built layer by layer (each typically 20 μm thick) from plastic or metal (Direct Metal Laser Sintering, DMLS) material in powder form, each layer being sintered by a scanning laser. 一种制造技术，通过这种制造技术，零件由粉末形式的塑料或金属（直接金属激光烧结，DMLS）材料逐层（每个厚度通常为 20 微米）构建，每一层都由扫描激光烧结。 |
| Cooling coil | 冷却盘管 |
A simple heat exchanger consisting of a coiled tube, typically of copper or stainless steel, through which is circulated a coolant such as a refrigerant, chilled water, or water mixed with ethylene glycol. Applications include air conditioning, process cooling, and refrigeration. 一种简单的热交换器，由通常由铜或不锈钢制成的盘管组成，冷却剂如制冷剂、冷冻水或与乙二醇混合的水通过盘管循环。应用包括空调、工艺冷却和制冷。 |
| Extra spring | 额外弹簧 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state above full hard beyond which further cold work will not measurably increase the strength and hardness. 有色金属合金和一些铁合金的回火状态，大约对应于高于全硬的冷加工状态，超过该状态进一步冷加工将不会显着增加强度和硬度。 |
| Weld penetration | 焊接熔深 |
It is the depth below the surfaces, as revealed in microstructural sections of joined metals, which is melted during welding. 它是焊接过程中熔化的连接金属的微观结构截面所显示的表面以下的深度。 |
| Bypass flow meter | 旁通流量计 |
(shunt flow meter) A flow meter installed in a pipework bypass which may itself be part of the flow meter. An orifice plate is used to ensure a fraction of the main flow passes through the bypass. （分流流量计）安装在管道旁路中的流量计，它本身可能是流量计的一部分。孔板用于确保一部分主流通过旁路。 |
| Assembly line | 流水线 |
A system of mass production in which work is moved progressively from one operation to another, ultimately to give the final complete product. 一种大规模生产系统，其中工作逐渐从一个操作转移到另一个操作，最终得到完整产品。 |
| Anelastic | 无弹性 |
Literally ‘not elastic’, but in practice used for materials that display timedependent recovery on unloading. 字面意思是“没有弹性”，但实际上用于在卸载时显示随时间恢复的材料。 |
| Condensation shock | 冷凝冲击 |
For supersonic flow of a moist gas through a divergent nozzle, condensation occurs in the form of spontaneous nucleation at some point downstream of that at which the temperature falls to the saturation temperature. The condensation process proceeds rapidly, and results in a fairly thick discontinuity termed a condensation shock. 对于通过发散喷嘴的湿气体超音速流动，在温度降至饱和温度的点下游的某个点处，冷凝以自发成核的形式发生。凝结过程进行得很快，导致相当厚的不连续性，称为凝结激波。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Bulk velocity | 体积速度 |
(average velocity, V) (Unit m/s) For fluid flow in a pipe or duct, the average flow velocity, given by V = ṁ/ρA where ṁ is the mass flow rate, ρ is the fluid density, and A is the duct cross-sectional area. （平均速度，V）（单位m/s）对于管道或管道中的流体流动，平均流速，由V=ṁ/ρA给出，其中ṁ是质量流量，ρ是流体密度，A是管道截面积。 |
| Densimeter | 密度计 |
An instrument used to determine the density or relative density of a solid or liquid. 用于测定固体或液体的密度或相对密度的仪器。 |
| Computer numerical control (CNC) | 计算机数控（CNC） |
A term relating to machine tools in which the movements of a tool and/or the workpiece are controlled by computer. 与机床相关的术语，其中工具和/或工件的运动由计算机控制。 |
| Absolute humidity | 绝对湿度 |
The weight of water vapor in a gadwater vapor mixture per unit volume of space occupied, expressed, for example, in grains or pounds per cubic foot. 单位体积空间占用的水蒸气混合物中水蒸气的重量，例如，以谷物或磅/立方英尺表示。 |
| Preload accuracy | 预载精度 |
A measure of the precision with which a given tool or procedure creates preload in a bolt when the bolt is tightened. A common torque wrench, for example, is said to produce preload with an accuracy of +30%. The mean preload, however, may not be that which the designer intended, or may not be what he should have intended. Accuracy as used here, in other words, is synonymous with Scatter. 当螺栓拧紧时，给定工具或程序在螺栓中产生预紧力的精度度量。例如，一个普通的扭矩扳手据说可以产生精度为+30%的预载。然而，平均预载可能不是设计者预期的。这里使用的准确度是分散度的同义词。 |
| Breaks | 断裂 |
Creases or ridges usually in “untempered” or in aged material where the yield point has been exceeded. Depending on the origin of the break, it may be termed a cross break, a coil break, an edge break, or a sticker break. 通常在“未回火”或超过屈服点的老化材料中出现折痕或隆起。根据断裂的起源，它可能被称为交叉断裂、线圈断裂、边缘断裂或贴纸断裂。 |
| Engineering stress (s) | 工程应力 |
A term sometimes used for conventional stress in order to differentiate it from true stress. In tension testing, it is calculated by dividing the breaking load applied to the specimen by the original crosssectional area of the specimen. 一个术语，有时用于常规应力，以区别于真实应力。在拉伸试验中，通过将施加在试样上的断裂载荷除以试样的原始横截面积来计算。 |
| Remaining stress | 残留应力 |
The stress remaining at a given time during a stress-relaxation test. See also stress relaxation. 在应力松弛试验期间在给定时间内剩余的应力。参见压力松弛。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Clearance | 间距 |
(Unit m or μm) 1. The distance (if any) between mating components in an assembly. 2. The distance between two moving parts, or a moving part and stationary part, in a machine (e.g. the gap between a piston and a cylinder head). 3. With threads, the major clearance is the distance between the design form at the root of an internal thread and the crest of its mating external thread; the minor clearance is the corresponding dimension between the crest of an internal thread and the root of the external thread. （单位m或μm）1.装配体中配合组件之间的距离（如果有）。2.机器中两个运动部件之间的距离，或运动部件和静止部件之间的距离（例如活塞和气缸盖之间的间隙）。3.带螺纹时，主要间隙是内螺纹根部的设计形状与其配合的外螺纹牙顶之间的距离；小间隙是内螺纹牙顶和外螺纹牙根之间的对应尺寸。 |
| Cavitation tunnel | 空泡试验筒 |
A closed-circuit recirculating water tunnel in which the static pressure can be reduced to sufficiently low levels for cavitation studies to be performed. 一种闭路循环水隧洞，其中静压可降至足够低的水平，以便进行气蚀研究。 |
| Seal | 密封件 |
A component which controls or prevents leakage of fluids into or out of parts of a machine. 控制或防止流体流入或流出机器部件的部件。 |
| Dead centre | 止点 |
The point at which, in a crank mechanism, the piston connecting rod and crank are all in line so that there can be no driving moment. 在曲柄机构中，活塞连杆和曲柄都在一条线上，因此不会有驱动力矩。 |
| Track rod | 横拉杆 |
A bar connecting the ends of the steering arms in an automotive vehicle. 连接汽车转向臂端部的杆。 |
| Condensate strainer | 冷凝水过滤器 |
A filter in a steam plant used to remove particulate matter from condensate before it is added to feedwater. 蒸汽设备中的过滤器，用于在将冷凝水添加到给水中之前去除冷凝水中的颗粒物。 |
| Noble metals | 贵金属 |
Metallic elements from periods (rows) 5 and 6 of the periodic table, namely ruthenium, rhodium, palladium, silver, osmium, iridium, platinum, and gold. They resist corrosion and oxidation and are used for electrical contacts, thin-film circuits, and electroplating. Gold, silver, and platinum used for jewellery are also known as precious metals. They have face-centred cubic crystal structure and good ductility. 周期表第5和第6周期（行）中的金属元素，即钌、铑、钯、银、锇、铱、铂和金。它们抗腐蚀和氧化，用于电触点、薄膜电路和电镀。用于珠宝的金、银和铂也被称为贵金属。它们具有面心立方晶体结构和良好的延展性。 |
| Jack | 杰克装置 |
A lifting device that exerts large forces over small displacements, achieved by mechanical gearing or hydraulics. 通过机械传动或液压装置在小位移上施加大力的提升装置。 |
| Salt bath heat treatment | 盐浴热处理 |
Heat treatment carried out in a bath of molten salt. 在熔融盐浴中进行的热处理。 |
| Austenitic grain size | 奥氏体晶粒尺寸 |
The size attained by the grains of steel when heated to the austenitic region; may be revealed by appropriate etching of cross sections after cooling to room temperature. 当加热到奥氏体区域时钢晶粒达到的尺寸；冷却至室温后，可通过适当蚀刻横截面来显示。 |
| Starting torque (Unit N.m) | 起动扭矩（单位：N.m） |
The torque developed by a motor at zero rotational speed in order to initiate rotation of the applied load. 电机在零转速下产生的扭矩，以启动所施加负载的旋转。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Alloy | 合金 |
1. A metallic material composed of two or more elements, one of which is usually a metal to which the other elements are added, e.g. iron-carbon or aluminium-copper (binary alloy); nickel-chromium-iron (ternary alloy). 2. A plastic produced as a blend of two or more immiscible polymers. This results in material that cannot be achieved by polymerization. 1.由两种或多种元素组成的金属材料，其中一种通常是添加了其他元素的金属，例如铁碳或铝铜（二元合金）；镍铬铁（三元合金）。2.由两种或多种不混溶聚合物混合而成的塑料。这导致无法通过聚合获得的材料。 |