| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Elastic resilience | 弹性回弹 |
The amount of energy absorbed in stressing a material up to the elastic limit; or, the amount of energy that can be recovered when stress is released from the elastic limit. 向材料施加应力直至弹性极限所吸收的能量；或者当应力从弹性极限释放时可以恢复的能量值。 |
| T-bolt | T型螺栓 |
A threaded bolt having a square or rectangular end which fits into the T slot of a machine table for clamping workpieces. 一种带有方形或矩形端头的螺栓，可嵌入机床工作台的T形槽中，用于夹紧工件。 |
| PSI (pounds per square inch) | PSI（磅/平方英寸） |
Pressure measurement. Psia (pounds per square inch absolute) measures actual pressure with no allowance for atmospheric pressure. Psig (pounds per square inch gauge) measures pressure with the gauge set to zero (0) at atmospheric pressure (14.7 psia). In other words psig = psia – 14.7. 压力测量。Psia（绝对磅/平方英寸）测量实际压力，不考虑大气压力。Psig（磅/平方英寸表压）在大气压（14.7 psia）下，将表压设置为零（0）时测量压力。换句话说，psig=psia–14.7。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Fillister head | 槽头 |
Similar to a pan head but with a smaller head diameter and a taller head, with higher vertical sides. 类似于盘头，但头部直径较小，头部较高，垂直边较高。 |
| Flattening test | 压扁试验 |
This term as applied to tubing refers to a method of testing a section of tubing by flattening it until the inside walls are parallel and separated by a given distanceusually equal to three times the wall thickness for seamless tubes and five times the wall thickness for lap-welded tubes. Boiler tubes subjected to this test should show no cracks or flaws. The flattening test applied to rivets, consists in flattening a rivet head while hot to a diameter equal to 21⁄2 times the diameter of the shank or body of the rivet. Good rivet steel must not crack at the edges of the flattened head. 该术语适用于管材，是指通过压扁管材直至内壁平行并隔开给定距离（通常等于无缝钢管壁厚的三倍，搭接焊管壁厚的五倍）来测试管材截面的方法。进行该试验的锅炉管应无裂纹或缺陷。适用于铆钉的压扁试验包括在热态下压扁铆钉头，使其直径等于铆钉柄或铆钉体直径的21⁄2倍。良好的铆钉钢不得在扁平头部边缘开裂。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| Ballonet | 气囊 |
An airbag used in a hybrid airship. Helium gas expels air from the ballonet during ascent. Fans draw air in during descent. 混合动力飞艇中使用的安全气囊。氦气在上升过程中将空气从气囊中排出。风扇在下降过程中吸入空气。 |
| Radiosity (J) (Unit W/m²) | 辐射度（J）（单位W/m²） |
The total radiation leaving a given surface per unit area, including emitted, reflected, and transmitted radiation. 每单位面积离开给定表面的总辐射，包括发射、反射和透射辐射。 |
| Shrink fit | 过盈配合 |
A tight interference fit between two components resulting from heating an outer part and/or cooling an inner part to allow easy assembly. The outer component contracts on cooling, while the inner part expands on warming to ambient temperature, thus gripping the two parts together. 由于加热外部部件和/或冷却内部部件而导致的两个部件之间的紧密过盈配合，以便于组装。外部部件在冷却时收缩，而内部部件在加热到环境温度时膨胀，从而将两个部件夹在一起。 |
| Mohs hardness test | 莫氏硬度测试 |
A scratch hardness test for determining comparative hardness using 10 standard minerals—from talc (the softest) to diamond (the hardest). 刮擦硬度测试，用于使用从滑石（最软）到钻石（最硬）的10种标准矿物测定比较硬度。 |
| Tensile strength (Unit Pa) | 抗拉强度（单位Pa） |
In tension testing, the ratio of maximum load to original cross-sectional area. Also known as ultimate strength. The resistance that a material offers to tensile stress. It is defined as the smallest tensile stress required to break the body. (ultimate strength, ultimate tensile strength, UTS, Rm, Rm) The nominal or engineering stress given by the maximum load in a tension test divided by the original cross-sectional area of the specimen. The maximum load could be the fracture load for a brittle material, but for a ductile material it is usually taken as the load at which necking begins, beyond which the load falls. 在拉伸试验中，最大载荷与原始横截面积之比。也称为极限强度。材料对拉伸应力的抵抗力。它被定义为破坏主体所需的最小拉伸应力。（极限强度、极限抗拉强度、UTS、Rm、Rm）拉伸试验中最大载荷除以试样原始横截面积得出的标称或工程应力。对于脆性材料，最大载荷可以是断裂载荷，但对于韧性材料，最大荷载通常被视为颈缩开始时的载荷，超过该载荷时，载荷下降。 |
| Thermoelectric material | 热电材料 |
A material in which any of the thermoelectric phenomena, such as the Peltier, Seebeck, and Thomson effects, are especially strong. 一种热电现象特别强烈的材料，如珀尔帖效应、塞贝克效应和汤姆森效应。 |
| Oil hardening | 油回火 |
The formation of martensite before tempering by quenching suitable steels in oil at lower cooling rates than given by water quenching, thus reducing the likelihood of component fracture or severe residual stresses. Quench-hardening treatment involving cooling in oil. 通过在油中以低于水淬的冷却速率淬火合适的钢，在回火前形成马氏体，从而降低部件断裂或严重残余应力的可能性。是一种淬火硬化处理，包括在油中冷却。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Displacement | 移位 |
The distance that a chosen measurement point on a cracked specimen displaces normal to the crack plane as the crack grows. 随着裂纹扩展，裂纹试样上选定的测量点垂直于裂纹平面位移的距离。 |
| Load and resistance factor design | 负载和阻力系数设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Assigns uncertainties in the strength of (i.e., resistance of) and in the service loads to be placed on a shear joint to estimate the probable strength of the joint. It is a recently defined alternative to the Allowable stress design procedure. 结构连接研究委员会为AISC制定的设计程序。分配剪切接头的强度（即阻力）和工作荷载的不确定性，以估计接头的可能强度。它是最近定义的容许应力设计程序的替代方案。 |
| Metallurgy | 冶金 |
The study of the atomic, crystallographic, microstructural, mechanical, and physical properties of metallic elements and alloys and their applications. 研究金属元素和合金的原子、晶体学、微观结构、机械和物理特性及其应用。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Yielding | 屈服 |
Evidence of plastic deformation in structural materials. Also known as plastic flow or creep. 结构材料塑性变形的证据。也称为塑性流动或蠕变。 |
| Profilometer | 轮廓仪 |
An instrument used to quantify the roughness of a surface. For a contact profilometer, a diamond stylus sweeps across the surface along a series of parallel lines. Noncontact profilometers use optical techniques to map the surface irregularities. 用于量化表面粗糙度的仪器。对于接触式轮廓仪，钻石触针沿一系列平行线扫过表面。非接触式轮廓仪使用光学技术绘制表面不规则。 |
| Durometer hardness | 硬度计硬度 |
Measure of the indentation hardness of plastics. It is the extent to which a spring-loaded steel indenter protrudes beyond the pressure foot into the material. 塑料压痕硬度的测量。它是弹簧加载的钢压头超出压力脚伸入材料的程度。 |
| International Practical Temperature Scale (IPTS) | 国际实用温标（IPTS） |
A close approximation to the thermodynamic temperature scale based upon the triple points of hydrogen (13.8 K), neon (24.6 K), oxygen (54.4 K), argon (83.8 K), mercury (234.3 K), and water (273.2 K); the melting point of gallium (302.9 K); and the freezing points of indium (429.7 K), tin (505.1 K), zinc (692.7 K), aluminium (933.5 K), silver (1 234.9 K), gold (1 337.3 K), and copper (1 基于氢（13.8K）、氖（24.6K）、氧（54.4K）、氩（83.8K），汞（234.3K）和水（273.2K）的三相点的热力学温度标度的近似值；镓的熔点（302.9K）；铟（429.7K）、锡（505.1K）、锌（692.7K），铝（933.5K）、银（1234.9K）、金（1337.3K）和铜等。 |
| Length of engagement | 啮合长度 |
It is the axial measurement within which the external and internal threads have theoretical contact. 它是外螺纹和内螺纹具有理论接触的轴向测量。 |
| Hot-wire test | 热线测试 |
Method used to test heat extraction rates of various quenchants. Faster heat-extracting quenchants will permit more electric current to pass through a standard wire because it is cooled more quickly. Compare with hot-wire analyzer. 用于测试各种淬火剂的热提取率的方法。与热线分析仪相比，更快的热提取淬火剂将允许更多电流通过标准导线，因为标准导线冷却更快。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Coining | 压印 |
A forging operation, employing a closely-fitting punch and die from which no metal is allowed to escape, in which the surface pattern on the punch and die is imprinted on the blank. 一种锻造操作，采用紧密配合的凸模和模具，不允许金属逸出，其中凸模和模具上的表面图案印在坯料上。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Manometer | 压力计 |
An instrument used in the measurement of a pressure difference in a fluid (manometry). 用于测量流体压力差（测压）的仪器。 |
| Stretch forming | 拉伸成型 |
A manufacturing process in which sheet-metal components are physically stretched over a forming die using a press, punch, or edge clamps. Stretching combined with bending reduces springback. 一种制造工艺，其中使用压力机、冲头或边缘夹具在成形模上物理拉伸金属板部件。拉伸与弯曲相结合可减少回弹。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Fastener standard | 紧固件标准 |
A document which details the attributes of a finished fastener and includes such characteristics as geometry, material or chemistry, heat treatment, finish, testing lot size, and packaging. 详细说明紧固件属性的文件，包括几何形状、材料或化学、热处理、表面处理、测试批量和包装等特性。 |
| Pascal’s law | 帕斯卡定律 |
When there is a change in pressure at any point in a confined fluid at rest, there is an equal change at every other point in the fluid volume. 当处于静止状态的受限流体中任何一点的压力发生变化时，流体体积中的每一点的变化都相等。 |
| Vickers hardness test | 维氏硬度测试 |
An indentation hardness test employing a 136° diamond pyramid indenter (Vickers) and variable loads, enabling the use of one hardness scale for all ranges of hardness—from very soft lead to tungsten carbide. Also know as diamond pyramid hardness test. 采用136°金刚石棱锥压头（维氏硬度计）和可变载荷的压痕硬度测试，能够对从极软铅到碳化钨的所有硬度范围使用一个硬度标度。也称为钻石金字塔硬度测试。 |
| Minor diameter | 螺纹小径 |
On a straight thread, the diameter of the imaginary cylinder which just touches the root of an external thread or the crest of an internal thread. 在直螺纹上，仅接触外螺纹根部或内螺纹顶部的假想圆柱体的直径。 |
| Double tempering | 双回火 |
A treatment in which a quench-hardened ferrous metal is subjected to two complete tempering cycles, usually at substantially the same temperature, for the purpose of ensuring completion of the tempering reaction and promoting stability of the resulting microstructure. 一种处理，其中淬火硬化的黑色金属经过两个完整的回火循环，通常在基本相同的温度下，以确保完成回火反应并提高所得微观结构的稳定性。 |
| Rivet | 铆钉 |
A short rod with a head on one end that is inserted through aligned holes in plates to be joined, after which a second head is made on the protruding shank by hammering or forming. The most common head shapes are flat, domed, and inverse conical. In an array, the rivet pitch is the distance between the centres of adjacent rivets. Failure may occur by different mechanisms or modes. A one piece fastener consisting of a head and a body and used for fastening two or more pieces together by passing the body through a hole in each piece and then forming a second head on the body end. It cannot be removed except by taking off the head. 一种一端有头的短杆，插入待连接板上对齐的孔中，然后通过锤击或成型在突出的杆身上制作第二个头。最常见的头部形状是扁平、圆顶和倒锥形。在阵列中，铆钉间距是相邻铆钉中心之间的距离。故障可能由不同的机制或模式发生。一种一体式紧固件，由头部和主体组成，用于将两个或多个部件紧固在一起，方法是将主体穿过每个部件上的孔，然后在主体端部形成第二个头部。除非取下头部，否则无法移除。 |
| Adhesive joint | 粘合接头 |
The point or area in which two structures are held together by an adhesive. 两个结构通过粘合剂粘合在一起的点或区域。 |
| Turn-of-nut | 转动螺母 |
Sometimes used to describe the general rotation of the nut (or bolt head) as the fastener is tightened. More often used to define a particular tightening procedure in which a fastener is first tightened with a preselected torque, and is then tightened further by giving the nut an additional, measured, turn such as ‘‘three flats’’ (180°). 有时用于描述紧固件拧紧时螺母（或螺栓头）的总体旋转。更常用于定义一种特定的紧固程序，在该程序中，首先以预选扭矩拧紧紧固件，然后通过使螺母额外转动，如“三平面”（180°）进一步拧紧。 |
| Coherent precipitate | 相干沉淀 |
A crystalline precipitate that forms from solid solution with an orientation that maintains continuity between the crystal lattice of the precipitate and the lattice of the matrix, usually accompanied by some strain in both lattices. Because the lattices fit at the interface between precipitate and matrix, there is no discernible phase boundary. 由固溶体形成的结晶沉淀物，其取向保持沉淀物晶格和基体晶格之间的连续性，通常伴随着两个晶格中的一些应变。由于晶格适合于沉淀和基体之间的界面，因此不存在可识别的相边界。 |
| Transfer machines | 转印机 |
These specialized machine tools are used to perform various machining operations on parts or parts in fixtures as the parts are moved along on an automatic conveyor which is part of the machine tool set-up. In a set-up, the parts can move in a straight line from their entry point to their exit point, or the setup may be constructed in a U-shape so that the parts are expelled near where they start. 当零件在自动输送机上移动时，这些专用机床用于对零件或夹具中的零件执行各种加工操作，自动输送机是机床设置的一部分。在设置中，零件可以从其入口点直线移动到其出口点，或者设置可以构造为U形，以便零件在其起点附近排出。 |
| Pop rivet | 拉钉 |
A hollow rivet that enables a connexion to be made from one side only of an assembly. 一种空心铆钉，使连接只能从组件的一侧进行。 |
| Lead of thread | 螺纹导程 |
On a single threaded screw, the distance the screw or nut advances in one complete revolution. 在单螺纹螺钉上，螺钉或螺母在一整圈中前进的距离。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Mechanical metallurgy | 机械冶金 |
The science and technology dealing with the behavior of metals when subjected to applied forces. 处理金属在外力作用下的行为的科学技术。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Elastic limit | 弹性极限 |
The maximum stress which a material is capable of sustaining without any permanent strain (deformation) remaining on complete release of the stress. 材料在完全释放应力时能够承受的最大应力，且不会留下任何永久应变（变形）。 |
| Radian (rad) | 弧度（rad） |
A coherent derived SI unit defined as the plane angle subtended at the centre of a circle by an arc having a length equal to the radius. Thus 2π radians are equivalent to 360° and 1 rad ≈ 57.3°. 一种相干导出的国际单位制单位，定义为在圆心处被长度等于半径的弧对向的平面角。因此，2π弧度相当于360°和1弧度≈57.3°. |
| Starting valve (regulator) | 起动阀（调节器） |
A valve which admits steam from the boiler to the cylinder(s) of a steam engine. 将蒸汽从锅炉送入蒸汽机汽缸的阀门。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Bolt stress (Unit Pa) | 螺栓应力（单位Pa） |
The axial tensile stress induced in a bolt by tightening. 通过拧紧在螺栓中产生的轴向拉应力。 |
| Continuous-type furnace | 连续式炉 |
A furnace used for heat treating materials that progress continuously through the furnace, entering one door and being discharged from another. See belt furnac, direct-fired tunnel-type furnac, rotary retort furnace, shaker-hearth furnace. 一种用于热处理材料的炉子，该炉子连续通过炉子，进入一个门并从另一个门排出。参见带式高炉、直燃隧道式高炉、旋转罐式炉、振动炉。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Bioengineering | 生物工程 |
(biological engineering) The application of engineering principles to biology, medicine, agriculture, etc. （生物工程）工程原理在生物学、医学、农业等方面的应用。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| Base metal hardness | 母材硬度 |
Hardness closest to the surface (when traversing from core to outside diameter) just before an increase or decrease occurs, denoting, respectively, carburization or decarburization. 在发生增加或减少之前最接近表面的硬度（从芯部到外径时），分别表示渗碳或脱碳。 |
| Hydrodynamics | 流体力学 |
A term sometimes used to mean fluid dynamics, even when the fluid is a gas or a liquid other than water. 有时用于表示流体动力学的术语，即使流体是气体或水以外的液体。 |
| Finishing temperature | 终轧温度 |
The temperature at which hot working is completed. 完成热加工的温度。 |
| Liquid nitriding | 液体氮化 |
A method of surface hardening in which molten nitrogen-bearing, fused-salt baths containing both cyanides and cyanates are exposed to parts at subcritical temperatures. 一种表面硬化方法，其中含有氰化物和氰酸盐的熔融含氮熔盐浴在亚临界温度下暴露于零件。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Heat-capacity ratio (c*) | 热容量比（c*） |
A non-dimensional parameter that arises in the analysis of heat exchangers, defined as the ratio cMIN/cMAX where cMIN is the heat-capacity rate c for the fluid with the smaller value of c and cMAX the value for the fluid with the larger value of c. Different flow rates and specific-heat values give rise to different values for c. 热交换器分析中出现的无量纲参数，定义为比率cMIN/cMAX其中cMIN是流体的热容率c，c值较小，cMAX是流体的值具有较大的c值。不同的流速和比热值产生不同的c值。 |
| Dew point | 压力露点 |
The temperature and pressure at which a gas begins to condense to a liquid. 气体开始凝结成液体的温度和压力。 |
| Compound pendulum | 复摆 |
A rigid body free to swing about an axis. 可绕轴自由摆动的刚体。 |
| Stress equalizing | 应力均衡 |
A low-temperature heat treatment used to balance stresses in cold-worked material without an appreciable decrease in the mechanical strength produced by cold working. 一种低温热处理，用于平衡冷加工材料中的应力，而不会明显降低冷加工产生的机械强度。 |
| Fluid mechanics | 流体力学 |
The study of fluids in motion (fluid dynamics) or fluid statics where there is no relative motion between fluid particles. Fluid statics concerns primarily the variation of pressure with altitude or depth; it includes aerostatics and hydrostatics. Fluid dynamics includes the topics of aerodynamics, gas dynamics, hydraulics, hydrodynamics and many aspects of acoustics, chemical engineering, flight, lubrication, meteorology, non-Newtonian fluid flow, oceanography, power-plant technology, propulsion, and turbomachinery. 研究运动中的流体（流体动力学）或流体静力学，其中流体粒子之间没有相对运动。流体静力学主要关注压力随高度或深度的变化；它包括空气静力学和流体静力学。流体动力学包括空气动力学、气体动力学、水力学、流体动力学以及声学、化学工程、飞行、润滑、气象学、非牛顿流体流动、海洋学、发电厂技术、推进和涡轮机械的许多方面。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| High-tensile bolt | 高强度螺栓 |
(high-tension bolt) A bolt manufactured from an alloy steel that has a high tensile strength of about 1 GPa. （高压螺栓）由合金钢制成的螺栓，具有约1GPa的高抗拉强度。 |
| Metre (m) | 米（m） |
The base unit of length in the SI system. It is equal to the distance travelled by light in vacuum in 1/299 792 458 seconds. SI系统中长度的基本单位。它等于光在真空中在1/299792458秒内传播的距离。 |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Turbine flow meter | 涡轮流量计 |
(axial flow meter, propeller meter) An in-line flow meter in which the rotation speed N of a propeller or rotor is a measure of the mass flowrate ṁ. Calibration is always necessary but with appropriate design ṁ is closely proportional to N over a wide range. （轴向流量计、螺旋桨流量计）一种串联流量计，其中螺旋桨或转子的转速N是质量流量的测量值ṁ. 校准总是必要的，但需要适当的设计ṁ在很宽的范围内与N成正比。 |
| Forging cracks | 锻造裂纹 |
This may occur during fastener manufacturing at the cutting or forging operations and are located on the top of the head or on the raised periphery of indented head bolts. 这可能发生在紧固件制造过程中的切削或锻造操作中，并且位于头部的顶部或带锯齿的头部螺栓的凸起周边上。 |
| Working section | 工作区 |
That part of a wind tunnel in which models are placed for testing, or where detailed measurements are performed. 风洞中放置模型进行测试或进行详细测量的部分。 |
| Spherical washer | 球面垫圈 |
A washer whose upper surface is semispherical. Used with a nut whose contact face is also semispherical. Reduces bending stress in a bolt or stud, by allowing some self-alignment and some compensation for nonparallel joint surfaces or Angularity. 上表面为半球形的垫圈。与接触面也是半球形的螺母一起使用。减少螺栓或螺柱中的弯曲应力，允许一些自对准，并对不平行的接头表面或角度进行一些补偿。 |
| Creep–time relations | 蠕变时间关系 |
Algebraic or numerical relations between creep strain and time at constant stress. 恒定应力下蠕变应变与时间之间的代数或数值关系。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Supercharging | 增压 |
The process of increasing the mass flow rate of air (or air/fuel mixture) into the cylinder(s) of a piston engine using a compressor driven from the crankshaft (the supercharger). The power output is increased compared with a naturally-aspirated engine of the same capacity. The process also increases the air pressure and density to greater than ambient. In the past, most superchargers were mechanically driven from the engine’s crankshaft, but these have been largely superseded by turbochargers. 使用由曲轴（增压器）驱动的压缩机增加进入活塞式发动机气缸的空气（或空气/燃料混合物）质量流率的过程。与相同容量的自然吸气发动机相比，功率输出增加。该过程还将空气压力和密度增加到大于环境压力和密度。在过去，大多数增压器都是由发动机曲轴机械驱动的，但这些增压器在很大程度上已被涡轮增压器所取代。 |
| Nipple | 喷嘴 |
A device containing a non-return valve screwed into a lubrication point through which grease may be introduced, for example into a bearing. 一种包含止回阀的装置，该止回阀拧入润滑点，通过该润滑点可以将润滑脂引入，例如轴承中。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Safe working load (Unit N) | 安全工作负荷（单位：N） |
The steady or unsteady load against which a component or structure is designed for normal operation. It is lower than that which would cause failure by buckling, fracture, or yielding, so as to accommodate uncertainty, possible fault or accident conditions. 部件或结构设计用于正常运行的稳定或不稳定荷载。该值低于因屈曲、断裂或屈服而导致失效的值，以适应不确定性、可能的故障或事故条件。 |
| Hot strength (Unit Pa) | 热强度（单位Pa） |
The yield stress (or sometimes fracture stress) of a material at temperatures above about half its melting point in kelvins. 材料在高于其熔点一半（以开尔文为单位）的温度下的屈服应力（有时为断裂应力）。 |
| Coil spring | 螺旋弹簧 |
A spiral (‘clockwork’) or helical (cylindrical) spring. A spring steel wire wound in a spiral pattern. 螺旋（“发条”）或螺旋（圆柱形）弹簧。以螺旋状缠绕的弹簧钢丝。 |
| Statistic | 统计 |
A summary value calculated from the observed values in a sample. 根据样本中的观察值计算得出的汇总值。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Distortion | 扭曲 |
Any deviation from an original size, shape, or contour that occurs because of the application of stress or the release of residual stress. 由于施加应力或释放残余应力而发生的与原始尺寸、形状或轮廓的任何偏差。 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Absorption | 吸收 |
The process whereby a fluid permeates a porous solid, or a gas is dissolved by a liquid. 流体渗透多孔固体或气体被液体溶解的过程。 |
| Crack | 裂缝 |
A thin fissure-like defect in a component or structure across which material continuity is lost and which reduces the strength of the body. 部件或结构中的细裂缝状缺陷，材料连续性丧失并降低了身体的强度。 |
| Die screw | 模具螺丝 |
Tool used when threading cylindrical pieces beyond the capacity of a die plate. 对超出模板容量的圆柱件进行螺纹加工时使用的工具。 |
| Turbomachine | 涡轮机械 |
(rotodynamic machine) A machine in which there is a transfer of energy between a continuous stream of fluid and a component, called a rotor, rotating about a fixed axis. Fans and turbines (gas, hydraulic, steam, or wind) are turbomachines in which energy is transferred to the rotor, causing it to rotate. Pumps and compressors are turbomachines in which energy is transferred from the externally driven rotor to the fluid. （旋转动力机器）在连续的流体流和绕固定轴旋转的部件（称为转子）之间进行能量传递的机器。风扇和涡轮机（燃气、液压、蒸汽或风力）是涡轮机械，其中能量传递到转子，使其旋转。泵和压缩机是涡轮机械，其中能量从外部驱动的转子传递到流体。 |
| Specimen | 样品 |
A test object, often of standard dimensions or configuration, that is used for destructive or nondestructive testing. One or more specimens may be cut from each unit of a sample. 用于破坏性或无损检测的测试对象，通常具有标准尺寸或配置。可以从样品的每个单位切割一个或多个样品。 |
| Thermoelectric junction | 热电结 |
A welded, soldered, or twisted connection between the ends of two wires of dissimilar metals, as in a thermocouple. 两根不同金属线的末端之间的焊接、锡焊或绞合连接，如热电偶。 |
| Amontons friction | 阿蒙顿摩擦 |
(Coulomb friction) Friction between surfaces where the ratio of the frictional force F to the normal force N is constant and independent of the area in contact. （库仑摩擦）摩擦力F与法向力N之比恒定且与接触面积无关的表面之间的摩擦。 |
| Nominal stress | 名义应力 |
The stress at a point calculated on the net cross section by simple elasticity theory without taking into account the effect on the stress produced by stress raisers such as holes, grooves, fillets, etc. 通过简单弹性理论在净截面上计算的点处的应力，不考虑孔、槽、圆角等应力提升器产生的应力影响。 |
| Pressure control valve | 压力控制阀 |
A valve used to set the pressure level in a pressure vessel or piping system. 用于设置压力容器或管道系统中压力水平的阀门。 |
| Centrifugal compressor | 离心式压缩机 |
A compressor in which kinetic energy is added to a fluid by radial acceleration in an impeller and then converted into a pressure increase by flow though a diffuser. 一种压缩机，其中动能通过叶轮中的径向加速度添加到流体中，然后通过扩散器的流动转换为压力增加。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Steel-wire rope | 钢丝绳 |
A rope or cable made up of many steel strands wrapped helically about an axis, each strand being made of metal wires twisted together like a helix. 一种绳索或缆绳，由许多绕轴螺旋缠绕的钢绞线组成，每根钢绞线由金属丝缠绕在一起形成螺旋。 |
| Fracture strength | 断裂强度 |
(fracture stress) (Unit Pa) The stress at which a material breaks. It is not absolute for a given material, as it depends on the laws of fracture mechanics and is size-dependent. （断裂应力）（单位Pa）材料断裂时的应力。对于给定的材料，它不是绝对的，因为它取决于断裂力学定律，并且取决于尺寸。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Plug gauge | 塞规 |
A steel gauge used to determine the dimension or dimensions of a hole. It may be straight or tapered, and is typically circular, but in principle can have any cross section. 用于确定孔的尺寸的钢制量规。它可以是直的或锥形的，通常是圆形的，原则上可以有任何横截面。 |
| Depth gauge | 深度计 |
1. A precision instrument, typically consisting of a machine-divided steel rule passing through a hardened-steel cross head, used to measure the depths of slots, holes, shoulders, projections, etc. 2. A device used by divers to indicate the water depth. 1. 一种精密仪器，通常由穿过硬化钢十字头的机器分割钢尺组成，用于测量槽、孔、肩部、突起等的深度。 2. 潜水员用来指示深度的装置水深。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Superheating | 过热 |
Heating above the temperature at which an equilibrium phase transformation should occur without actually obtaining the transformation. 在不实际获得相变的情况下，加热到应发生平衡相变的温度以上。 |
| Aging treatment | 时效处理 |
Heat treatment aimed at age hardening; it comprises solution and precipitation treatments. 针对时效硬化的热处理；它包括溶液和沉淀处理。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Auxiliary power unit (APU) | 辅助动力装置（APU） |
In aircraft–gas–turbine applications, a small gas turbine used to provide start-up power, electrical and hydraulic power, and compressed air for cabin ventilation. In other applications, an APU may be a gas turbine or internal-combustion engine used to provide emergency power. 在飞机-燃气轮机应用中，小型燃气轮机用于提供启动动力、电力和液压动力以及用于机舱通风的压缩空气。在其他应用中，APU可以是用于提供应急动力的燃气轮机或内燃机。 |
| Taper key | 楔键 |
A key with parallel sides but tapering cross section along its length. 边平行但横截面沿其长度逐渐变细的键。 |
| Ductile cast iron | 球墨铸铁 |
A cast iron that has been treated while molten with an element such as magnesium or cerium to induce the formation of free graphite as nodules or spherulites, which imparts a measurable degree of ductility to the cast metal. Also known as nodular cast iron, spherulitic graphite cast iron and SG iron. 一种铸铁，在熔融时用镁或铈等元素进行处理，以诱导游离石墨形成为球粒或球晶，从而赋予铸造金属可测量的延展性。又称球墨铸铁、球晶石墨铸铁和SG铸铁。 |
| Oil-cooled | 油冷却 |
A term for a machine that uses circulating oil to remove heat. 使用循环油散热的机器的术语。 |
| Stove bolt | 炉用螺栓 |
This bolt has been so named because of its use in stove building. It is made in a number of different forms, either with a round button, or flat countersunk head, the head having a slot for a screwdriver and the threaded end being provided with a square or hexagon nut. 这种螺栓因其在炉灶建筑中的用途而得名。它有多种不同的形式，有圆形按钮或平沉头，头部有螺丝刀槽，螺纹端有方形或六角螺母。 |
| Air cleaner | 空气净化器 |
A device, such as a filter, hydrocyclone, or electrostatic precipitator, that removes particles and aerosols from a flow of air. 一种设备，例如过滤器、水力旋流器或静电除尘器，用于从气流中去除颗粒和气溶胶。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Carbon potential | 碳势 |
A measure of the ability of an environment containing active carbon to alter or maintain, under prescribed conditions, the carbon level of the steel. Note: In any particular environment, the carbon level attained will depend on such factors as temperature, time, and steel composition. 衡量含有活性碳的环境在规定条件下改变或保持钢的碳含量的能力。注意：在任何特定环境中，所达到的碳含量将取决于温度、时间和钢成分等因素。 |
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Cycle annealing | 循环退火 |
An annealing process employing a predetermined and closely controlled time-temperature cycle to produce specific properties or microstructures. 采用预定且严格控制的时间-温度循环来产生特定性能或微观结构的退火工艺。 |
| Resistance factor | 阻力系数 |
Probabilistic factor representing the uncertainties in the designer’s estimate of the strength of a shear joint. Used in Load and resistance factor design. 概率系数，表示设计人员对剪切接头强度估计的不确定性。用于载荷和阻力系数设计。 |
| Natural unit system (n.u. system) | 自然单位制（n.u.制） |
A non-SI system of units, based on fundamental constants, used in high-energy and particle physics. The n.u. of speed is the speed of light in a vacuum, c0 = 299 792 458 m/s. 基于基本常数的非国际单位制，用于高能和粒子物理n.u.速度是真空中的光速，c0=299792458m/s。 |
| Captive nut | 松脱螺母 |
A nut attached loosely or rigidly to a sheet member that is too thin to thread and which engages with a cap screw. 松脱地或刚性地连接到薄板构件上的螺母，该螺母太薄而无法拧入，并与带帽螺钉接合。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Absorption dynamometer | 吸收式测功机 |
A dynamometer in which input work or power is dissipated by mechanical friction, electrical resistance, hydraulic resistance, etc. 通过机械摩擦、电阻、液压阻力等耗散输入功或功率的测功机。 |
| Rolled thread | 滚制螺纹 |
A thread formed by plastically deforming the surface of the blank rather than by cutting operations. Increases fatigue life and thread strength, but is not possible (or perhaps economical) on larger sizes. 通过塑性变形坯料表面而不是通过切割操作形成的螺纹。增加疲劳寿命和螺纹强度，但不太可能（或者说是经济上不太可能）用于较大的尺寸。 |
| Centrifuge | 离心机 |
A machine incorporating a rapidly spinning drum in which liquids and suspended particles of different densities are separated by centrifugal action. 一种装有快速旋转滚筒的机器，在该滚筒中，不同密度的液体和悬浮颗粒通过离心作用分离。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Condensate strainer | 冷凝水过滤器 |
A filter in a steam plant used to remove particulate matter from condensate before it is added to feedwater. 蒸汽设备中的过滤器，用于在将冷凝水添加到给水中之前去除冷凝水中的颗粒物。 |
| Lock nut | 锁紧螺母 |
A type of nut that is prevented from loosening under vibration. The locking action is accomplished by squeezing, gripping or jamming against the bolt threads. A nut which provides extra resistance to vibration loosening (beyond that produced by proper Preload ), either by providing some form of Prevailing torque, or, in free-spinning lock nuts, by deforming, cramping, or biting into mating parts when fully tightened. 1. A thin auxiliary nut tightened against another nut to prevent loosening. 2. A single nut with special features that prevent loosening. 一种在振动下防止松动的螺母。锁定动作通过挤压、夹紧或卡住螺栓螺纹来完成。通过提供某种形式的主要扭矩，或在自由旋转锁紧螺母中，通过完全拧紧时变形、夹紧或咬入配合零件，提供额外的抗振动松动能力（超出适当预载产生的能力）。1.一个薄的辅助螺母，拧紧到另一个螺母上以防止松动。2.具有防止松动的特殊功能的单个螺母。 |
| Age hardening | 时效硬化 |
Raising the strength and hardness of an alloy by heating a supersaturated solid solution at a relatively low temperature to induce precipitation of a finely dispersed second phase. Also known as aging or precipitation hardening. Hardening by aging, usually after rapid cooling or cold working. 通过在相对较低的温度下加热过饱和固溶体以诱导细分散的第二相沉淀来提高合金的强度和硬度。也称为时效或沉淀硬化。通常在快速冷却或冷加工后。 |
| Valve spring | 气门弹簧 |
The spring that restores a valve to its closed position after having been opened, and is also intended to prevent valve bounce. 在阀门打开后将其恢复到关闭位置的弹簧，也用于防止阀门反弹。 |
| Stress corrosion cracking (SCC) | 应力腐蚀开裂（SCC） |
A common form of Stress cracking in which an Electrolyte encourages the growth of a crack in a highly stressed bolt. Only a tiny quantity of electrolyte need be present, at the tip or face of the crack. A time-dependent process in which a metallurgically susceptible material fractures prematurely under conditions of simultaneous corrosion and sustained loading at lower stress levels than would be required in the absence of a corrosive environment. Tensile stress is required at the metal surface and may be a residual stress resulting from heat treatment or fabrication of the metal or the result of external loading. Cracking may be intergranular or transgranular, depending on the combination of alloy and environment. 一种常见的应力开裂形式，其中电解液促使高应力螺栓中的裂纹扩展。在裂纹尖端或表面，只需存在少量电解质。一种随时间变化的过程，其中冶金敏感材料在同时腐蚀和持续加载的条件下过早断裂，其应力水平低于无腐蚀环境时的要求。在金属表面需要拉应力，拉应力可以是金属的热处理或制造或外部负载产生的残余应力。裂纹可能是沿晶开裂或穿晶开裂，这取决于合金和环境的组合。 |
| Milling | 铣削 |
A machining process, typically for metals and plastics, in which a multi-tooth rotary cutter removes material to produce flat or profiled surfaces, slots, grooves, etc. Milling is a machining process in which metal is removed by a rotating multiple-tooth cutter; each tooth removes a small amount of metal with each revolution of the spindle. Because both workpiece and cutter can be moved in more than one direction at the same time, surfaces having almost any orientation can be machined. 一种加工工艺，通常用于金属和塑料，其中多齿旋转刀具去除材料以产生平坦或异形表面、槽、槽等。金属由旋转多齿刀具去除；主轴每转一圈，每个齿都会去除少量金属。因为工件和刀具可以同时在多个方向上移动，所以几乎可以加工任何方向的表面。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Elbow | 肘部 |
1. A fitting that connects the ends of two pipes at an angle, 45°, 90°, and 180° being the most common. 2. The third joint on an articulated robot corresponding to the human elbow. 1.以45°、90°和180°角连接两个管道端部的配件。2.示例关节机器人上的第三关节对应于人的肘部。 |
| Ball mill | 球磨机 |
A mill for grinding and pulverizing materials, consisting of a horizontal rotating drum containing loose steel or ceramic balls. 一种用于研磨和粉碎物料的磨机，由装有松散钢球或陶瓷球的水平旋转滚筒组成。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Precision | 精确 |
The closeness of agreement between the results of individual replicated measurements or tests. The standard deviation of the error of measurement may be used as a measure of “imprecision.” 单个重复测量或测试结果之间的一致性。测量误差的标准偏差可用作“不精确性”的度量 |
| Lead angle | 导角 |
The angle of the helix of a screw thread or worm thread. It is the measure of the inclination of a screw thread from a plane perpendicular to the axis of the screw. 螺纹或蜗杆螺纹的螺旋角。它是螺纹从垂直于螺钉轴线的平面的倾斜度的量度。 |
| Verified loading range | 验证加载范围 |
For testing machines, the range of indicated loads for which the testing machine gives results within the permissible variation specified. 对于试验机，试验机在规定允许偏差范围内给出结果的指示载荷范围。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Oldham coupling | 十字联轴节 |
(double-slider coupling) A device for connecting a pair of misaligned parallel shafts, on the end of each of which are flanges having diametral tenons (tongues) that engage with matching slots spaced at 90° in an intermediate disc. As the coupling rotates, the disc compensates for shaft offset by sliding along each tenon in turn. Low-friction surfaces are requisite and the disc is often made of a polymer. An alternative arrangement has the slots in the flanges and the tenons on the disc. （双滑块联轴器）一种连接一对未对准平行轴的装置，在每个平行轴的端部有法兰，法兰具有直径榫（舌），与中间盘中间隔90°的匹配槽接合。当联轴器旋转时，圆盘通过依次沿每个榫头滑动来补偿轴偏移。低摩擦表面是必需的，阀盘通常由聚合物制成。另一种布置方式是法兰上的槽和阀盘上的榫头。 |
| Dead centre | 止点 |
The point at which, in a crank mechanism, the piston connecting rod and crank are all in line so that there can be no driving moment. 在曲柄机构中，活塞连杆和曲柄都在一条线上，因此不会有驱动力矩。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Net weight (Unit N) | 净重（单位：N） |
The difference between the gross weight of any container including its contents and the tare weight of the empty container. 任何容器（包括其内容物）的毛重与空容器皮重之间的差值。 |
| Full size body | 全尺寸螺纹杆 |
The body of a bolt or screw which has a diameter between the minimum and maximum limits of the major diameter of the thread. 螺栓或螺钉的主体，其直径介于螺纹大径的最小和最大限制之间。 |
| High strength low alloy steels | 高强度低合金钢 |
(HSLA steels) Steels with various micro-alloying elements such as copper, nickel, chromium, molybdenum, niobium, titanium, and vanadium in small quantities that give improved strength (as high as 900 MPa) and corrosion properties compared with plain carbon steels. Improvements are due to grain refinement and precipitation hardening, better control of the chemistry during steel making, and accurate rolling temperatures. （HSLA钢）是含有各种微合金元素的钢，如少量的铜、镍、铬、钼、铌、钛和钒，与普通碳钢相比，具有更好的强度（高达900MPa）和腐蚀性能。这些改进归功于晶粒细化和沉淀硬化、炼钢过程中更好的化学控制以及精确的轧制温度。 |
| Shrink ring | 预紧环 |
A ring, which is expanded by heating, is placed around an assembly of parts, and then contracts upon cooling to hold the assembly in place. 通过加热膨胀的环被放置在零件组件周围，然后在冷却时收缩以将组件固定到位。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Stress-concentration factor (Kt) | 应力集中系数（Kt） |
A multiplying factor for applied stress that allows for the presence of a structural discontinuity such as a notch or hole; Kt equals the ratio of the greatest stress in the region of the discontinuity to the nominal stress for the entire section. Also known as theoretical stress-concentration factor. 施加应力的倍增系数，允许存在结构不连续性，如缺口或孔；Kt等于不连续区域的最大应力与整个截面的标称应力之比。也称为理论应力集中系数。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Thermoelectric converter | 热电转换器 |
(thermoelectric generator) A device consisting of series-connected alternate n- and p-type semiconductor elements sandwiched between two ceramic plates. Due to the Seebeck effect, electrical power is generated when a temperature difference is maintained across the plates. Due to the Peltier effect, a thermoelectric converter can act as either a thermoelectric heater or a thermoelectric cooler (thermoelectric refrigerator) by passing an electrical current through it. The thermoelectric figure of merit (Z), with unit 1/K, is a dimensional parameter on which the efficiency of a thermoelectric device is primarily dependent, defined by Z = σα2/k where α is the Seebeck coefficient, σ is the electrical conductivity, and k is the thermal conductivity. The product of Z and a temperature is non-dimensional. （热电发生器）由串联连接的交替的n型和p型半导体元件夹在两块陶瓷板之间组成的装置。由于塞贝克效应，当板之间保持温差时，就会产生电能。由于珀尔帖效应，热电转换器可以通过使电流通过而充当热电加热器或热电冷却器（热电制冷机）。热电优值（Z）和第一单元/K是一个尺寸参数，热电装置的效率主要取决于此，由Z=σα2/K定义，其中α是塞贝克系数，σ是电导率，K是热导率。Z和温度的乘积是无量纲的。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Mechanical properties of solid materials | 固体材料的力学性能 |
The strength and stiffness properties of solid materials such as fracture toughness, the moduli of elasticity, percent elongation, 固体材料的强度和刚度特性，例如断裂韧性、弹性模量、伸长率、 |
| Fracture stress | 断裂应力 |
The true normal stress on the minimum cross-sectional area at the beginning of fracture. This term usually applies to tension tests of unnotched specimens. 断裂开始时最小横截面积上的真实正应力。该术语通常适用于无缺口试样的拉伸试验。 |
| Available head (Unit m) | 可用水头（单位米） |
In a hydroelectric power system, the difference between the vertical height of the water level in the supply reservoir above the turbine inlet less the head loss due to friction and fittings in the duct leading to the turbine. 在水力发电系统中，水轮机入口上方供水水库中水位垂直高度之间的差减去由于通向涡轮机的管道中的摩擦和配件造成的水头损失。 |
| Chafing fatigue | 磨损疲劳 |
Fatigue damage initiated in a surface damaged by rubbing against another body. 因与另一个物体摩擦而损坏的表面引起的疲劳损坏。 |
| Shock load | 冲击载荷 |
The sudden application of an external force that results in a very rapid build-up of stress. 突然施加外力，导致应力迅速增加。 |
| Preload | 预载 |
The tension created in a threaded fastener when the nut is first tightened. Often used interchangeably, but incorrectly, with Working load or bolt force or bolt tension 第一次拧紧螺母时螺纹紧固件中产生的张力。经常与工作载荷或螺栓力或螺栓张力互换使用但容易使用不当。 |
| Cup washer | 杯形垫圈 |
A dished leather or neoprene washer fitted to the rod end in some piston-style pumps. 在某些活塞式泵中，安装在杆端的碟形皮革或氯丁橡胶垫圈。 |
| Galvanic protection | 电流保护 |
The coating on a fastener is said to provide galvanic protection if it is more anodic than the fastener and will, therefore, be destroyed instead of the fastener. Zinc plate (galvanizing) provides galvanic protection to steel fasteners, for example. 如果紧固件上的涂层比紧固件更具阳极性，则据说它可以提供电流保护，将会因此被破坏而不是紧固。例如，锌板（镀锌）为钢紧固件提供电流保护。 |
| Cavitation-resistance inducer | 抗气蚀诱导剂 |
An axial-flow pump used upstream of a main pump in order to prevent cavitation in the latter by increasing the inlet head. 在主泵上游使用的轴流泵，通过增加进口压头防止主泵出现气穴。 |
| Anneal to temper | 退火回火 |
A final partial anneal that softens a cold worked nonferrous alloy to a specified level of hardness or tensile strength. 将冷加工的有色金属合金软化到规定的硬度或抗拉强度水平的最终局部退火。 |
| Turbo generator | 涡轮发电机 |
(turboset) The combination of a steam or gas turbine and an electrical generator with a single shaft or connected coaxial shafts. （汽轮发电机组）蒸汽或燃气轮机与发电机的组合，具有单轴或连接的同轴。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Tangential load (Unit N) | 切向荷载（单位：N） |
The component of load applied to an object, such as a gear, that tends to cause or resist rotation. 旋转力施加在物体上的载荷分量，如齿轮，倾向于引起或阻止旋转。 |
| Failure of the joint | 连接失效 |
Failure of a bolted joint to behave as intended by the designer. Failure can be caused or accompanied by broken or lost bolts, but can also mean joint slip or leakage from a gasketed joint even if all bolts still remain whole and in place. Common reasons for joint failure include vibration loosening, poor assembly practices, improper design, unexpected service loads or conditions, etc. 螺栓连接未达到设计者的预期性能。故障可能由螺栓断裂或丢失引起或伴随而来，但也可能意味着即使所有螺栓仍保持完整和就位，也存在接头滑动或垫圈接头泄漏。接头故障的常见原因包括振动松动、装配不当、设计不当、意外的工作负载或条件等。 |
| Fracture toughness | 断裂韧性 |
A generic term for measures of resistance to extension of a crack. The term is sometimes restricted to results of fracture mechanics tests, which are directly applicable in fracture control. However, the term commonly includes results from simple tests of notched or precracked specimens not based on fracture mechanics analysis. Results from tests of the latter type are often useful for fracture control, based on either service experience or empirical correlations with fracture mechanics tests. 裂纹扩展阻力测量的通用术语。该术语有时仅限于断裂力学试验的结果，这些结果直接适用于断裂控制。该术语通常包括非基于断裂力学分析的切口或预裂纹试样的简单试验结果。基于使用经验或与断裂力学试验的经验相关性，后一类试验的结果通常有助于断裂控制。 |
| Columnar structure | 柱状结构 |
A coarse structure of parallel elongated grains formed by unidirectional growth, most often observed in castings, but sometimes in structures resulting from diffusional growth accompanied by a solid-state transformation. 由单向生长形成的平行细长晶粒的粗略结构，最常见于铸件中，但有时也出现在伴随固态转变的扩散生长产生的结构中。 |
| Bernoulli’s law | 伯努利定律 |
For a steadily flowing fluid (liquid or gas), the sum of the pressure, kinetic energy per unit volume and potential energy per unit volume is constant at any point in the fluid. Using this relationship, it is possible to measure the velocity of a fluid by measuring its pressure at two points, as with a manometer or Pitot tube. 对于稳定流动的流体（液体或气体），压力、每单位体积的动能和每单位体积的势能之和在流体中的任何点都是恒定的。使用这种关系，可以通过在两个点测量流体的压力来测量流体的速度，就像使用压力计或皮托管一样。 |
| Tow | 拖拉 |
1. To cause a vehicle to move by pulling with a rope, chain, bar, etc. 2. A bundle of fibres employed in reinforcement. 1.用绳子、链条、钢筋等拉动车辆移动。2.用于加固的纤维束。 |
| Elongation | 伸张率 |
A term used in mechanical testing to describe the amount of extension of a test piece when stressed. 机械测试中使用的术语，用于描述试样在受力时的延伸量。 |
| Structure | 结构体 |
An assembly, usually load bearing, of connected (pinned, riveted, screwed, bolted, welded, etc.) components, such as bars, tubes, beams, and plates. 由连接（销接、铆接、螺纹连接、螺栓连接、焊接等）部件组成的组件，通常为承重组件，如杆、管、梁和板。 |
| Torque control | 扭矩控制 |
A system of optimizing rotor speed for a variable-speed wind turbine by controlling the torque demands of the generator. 通过控制发电机的扭矩需求来优化变速风力涡轮机的转子速度的系统。 |
| ASME | ASME |
The American Society of Mechanical Engineers. 美国机械工程师学会。 |
| Pressure-relief valve | 减压阀 |
A valve that limits the maximum pressure in a pressure vessel or fluid-power system to a specified level. 将压力容器或流体动力系统中的最大压力限制在规定水平的阀门。 |
| Corrosive wear | 腐蚀磨损 |
Wear in which chemical or electrochemical reaction with the environment is significant. 与环境发生显着化学或电化学反应的磨损。 |
| Radial wave equation | 径向波动方程 |
A differential equation describing the transmission of a wave in a system with radial symmetry. 描述波在径向对称系统中传输的微分方程。 |
| Toothed belt | 齿带 |
A flat belt, typically of a reinforced-rubber material, with transverse teeth that engage with teeth on a wheel or pulley. 一种扁平皮带，通常由增强橡胶材料制成，带有横向齿，与车轮或皮带轮上的齿啮合。 |
| Standard deviation (σ) | 标准偏差（σ） |
A statistical term used to quantify the Scatter in a set of data points. If the standard deviation is small, most of the data points are ‘‘nearly equal.’’ A large deviation means less agreement. The most usual measure of the dispersion of observed values or results expressed as the positive square root of the variance. The square root of variance, a measure of the spread of data about the mean value. 用于量化一组数据点中分散度的统计术语。如果标准偏差很小，则大多数数据点“几乎相等”大的偏差意味着更少的一致性。观测值或结果离散度的最常用度量，表示为方差的正平方根。方差的平方根，衡量平均值的数据分布。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Induction tempering | 感应回火 |
Tempering of steel using low-frequency electrical induction heating. 钢的回火采用低频电感应加热。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Compression failure | 压缩失败 |
The reduction or removal of a component’s load-bearing capacity in compression, caused by buckling, fracture, crease formation in fibre composites, etc. 由纤维复合材料中的屈曲、断裂、折痕形成等引起的部件在压缩中的承载能力的降低或消除。 |
| Standard fit | 标准匹配 |
The fit of a component machined or otherwise manufactured to standardized clearances and tolerances. 根据标准间隙和公差加工或以其他方式制造的部件的配合。 |
| Collapse load (Unit N) | 毁坏荷载（单位N） |
The applied load at which a structure becomes a mechanism owing to the formation of sufficient plastic hinges for collapse to occur. 由于形成足够的塑性铰链以发生坍塌，结构成为机制的施加载荷。 |
| Conduit | 导管 |
A hollow object, of metal, plastic, glass, ceramic, etc., which is relatively long compared with its lateral dimensions and through which there is fluid flow. 由金属、塑料、玻璃、陶瓷等制成的中空物体，与其横向尺寸相比相对较长，并且有流体流过。 |
| Crest | 波峰 |
The highest point of a wave or of a screw thread. 波浪或螺纹的最高点。 |
| Apparent area of contact | 表观接触面积 |
In tribology, the area of contact between two solid surfaces defined by the boundaries of their macroscopic interface. 在摩擦学中，两个固体表面之间的接触区域由其宏观界面的边界定义。 |
| Balancing machine | 平衡机 |
A device that assesses the state of static and dynamic balance of a rotating part, and indicates the magnitude and location of weights to be added to give balance. 一种装置，用于评估旋转部件的静态和动态平衡状态，并指示为获得平衡而添加的砝码的大小和位置。 |
| Ideal crack | 理想裂缝 |
A simplified model of a crack used in elastic-stress analysis. In a stress-free body, the crack has two smooth surfaces that are coincident and join within the body along a smooth curve called the crack front; in two-dimensional representations, the crack front is called the crack tip. 用于弹性应力分析的裂纹简化模型。在无应力物体中，裂纹有两个光滑表面，它们在物体内沿称为裂纹前缘的平滑曲线重合并连接；在二维表示中，裂纹前缘称为裂纹尖端。 |
| Pitch-circle diameter (Unit m) | 节圆直径（单位：m） |
The diameter of the circle (the pitch circle) centred on a component’s axis, around which holes or bolts are equally spaced. 以部件轴为中心的圆（节圆）的直径，孔或螺栓围绕其等距分布。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Dynamics | 动力学 |
The branch of mechanics that deals with objects in motion. Its two main branches are kinematics, which studies motion without regards to its cause, and kinetics, which also takes into account forces that cause motion. 力学中研究运动物体的分支。它的两个主要分支是运动学和动力学，前者研究运动而不考虑其原因，后者也考虑引起运动的力。 |
| Radioactive heat (Unit J) | 放射性热（单位J） |
Thermal energy released from the nucleus of an atom such as uranium235 by fission due to the absorption of a neutron. Heat is also produced by radioactive decay. 铀235等原子核因吸收中子而裂变释放的热能。放射性衰变也会产生热量。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| Composite property | 复合属性 |
In thermodynamics, a property defined in terms of the properties of a closed system and its surroundings, such as the non-flow exergy function. 在热力学中，根据封闭系统及其周围环境的性质定义的性质，例如非流动火用函数。 |
| Atom | 原子 |
The smallest unit of matter that has the properties of a chemical element. The simplest description of an atom (Bohr model) is of a compact nucleus surrounded by one or more orbiting electrons. 具有化学元素性质的最小物质单位。原子的最简单描述（玻尔模型）是由一个或多个轨道电子包围的致密原子核。 |
| Gear pump | 齿轮泵 |
A positive-displacement pump in which fluid is pumped by meshing gears, one driven and the other an idler gear, on parallel axes within a closed casing. 一种容积式泵，其中流体由啮合齿轮泵送，在封闭外壳内的平行轴上一个驱动，另一个为空套齿轮。 |
| Turning angle (θ) | 转向角（θ） |
The change in direction experienced by a gas flow passing through an oblique shock wave or Prandtl–Meyer expansion fan. 气流通过斜激波或Prandtl–Meyer膨胀风机时所经历的方向变化。 |
| Cold treatment | 冷处理 |
Treatment carried out after quenching to transform retained austenite into martensite, involving cooling and holding at a temperature below ambient. 淬火后进行的处理，以将残余奥氏体转变为马氏体，包括冷却和保持在低于环境温度的温度。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Significance level | 显着性水平 |
The stated probability (risk) that a given test of significance will reject the hypothesis that a specified effect is absent when the hypothesis is true. 当假设为真时，给定的显著性检验将拒绝特定效应不存在的假设的所述概率（风险）。 |
| Charles law/Charles' law | 查尔斯定律 |
(Gay–Lussac law) The volume of a fixed mass of gas at constant pressure is proportional to its absolute temperature. The volume of a gas at constant pressure is directly proportional to its absolute temperature. （盖-吕萨克定律）在恒定压力下，固定质量气体的体积与其绝对温度成正比。恒压下气体的体积与其绝对温度成正比。 |
| Biomechanics | 生物力学 |
The application of mechanical-engineering principles, including thermodynamics, fluid mechanics, and solid mechanics together with materials engineering, to biological systems. 机械工程原理（包括热力学、流体力学和固体力学以及材料工程）在生物系统中的应用。 |
| Compressive stress (Unit Pa) | 压缩应力（单位Pa） |
The compressive load per unit area at a point in a component. 部件中某点的每单位面积的压缩载荷。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Dynamic load (Unit N) | 动态负载（单位N） |
1. Loading of a component or structure by a moving object whose point of application changes with time, e.g. the live load of a train passing over a bridge. 2. A load applied to a particular part of a component or structure in a short time interval. 1. 应用点随时间变化的移动物体对部件或结构的加载，例如通过桥梁的火车的活荷载。2. 在短时间内施加到部件或结构的特定部分的载荷。 |
| Austenitizing | 奥氏体化 |
Forming austenite by heating a ferrous alloy into the transformation range (partial austenitizing) or above the transformation range (complete austenitizing). When used without qualification, the term implies complete austenitizing. 通过将铁合金加热到转变范围（部分奥氏体化）或高于转变范围（完全奥氏体化）来形成奥氏体。当不加限定地使用时，该术语意味着完全奥氏体化。 |
| Shank | 螺杆 |
Portion of a bolt which lies under the head. 1. The stem of a tool, such as a broach, drill bit, reamer, or tap, which fits into a holder such as a chuck. 2. The stem of a rivet or the unthreaded part of a screw or bolt. 3. The shaft of a tool connecting the tip and the handle. 螺栓头部下方的部分。1.一种工具的柄部，如拉刀、钻头、铰刀或丝锥，可装入夹具（如卡盘）中。铆钉的杆或螺钉或螺栓的无螺纹部分。3.连接尖端和手柄的工具的轴。 |
| AISC | AISC |
The American Institute of Steel Construction. 美国钢结构学会。 |
| Friction materials | 摩擦材料 |
Materials having a high coefficient of friction which, when coupled with a long life, may be employed as brake linings or the facing of the plates of a clutch. 具有高摩擦系数的材料，当与长寿命相结合时，可用作制动衬片或离合器片的饰面。 |
| Preload adjustments | 预载调整 |
Preloads may be applied directly by axial loading or indirectly by turning of the nut or bolt. When preload is applied by turning of nuts or bolts, a torsion load component is added to the desired axial bolt load. 预载荷可通过轴向载荷直接施加，或通过转动螺母或螺栓间接施加。当通过转动螺母或螺栓施加预载荷时，扭转载荷分量被添加到所需的轴向螺栓载荷中。 |
| Piston pump | 活塞泵 |
A positive-displacement pump in the basic configuration of which a piston reciprocates in a cylinder. On the suction stroke, fluid is drawn into a chamber through the inlet valve, which is then open while the outlet valve is closed. On the delivery stroke the fluid is forced out of the chamber through the outlet valve, which then opens while the inlet valve is closed. Both axial and radial configurations are common. 活塞在气缸中往复运动的一种容积泵。在吸入冲程，流体通过入口阀吸入腔室，然后在出口阀关闭时打开。在输送冲程中，流体通过出口阀被迫流出腔室，然后出口阀打开，同时入口阀关闭。轴向和径向配置都很常见。 |
| Air pump | 气泵 |
A machine for providing a flow of air or for increasing or decreasing the mass and pressure of air in a closed container. The term pump is more usual when the working fluid is a liquid, while compressor is more usual for gases. 一种用于提供空气流动或用于增加或减少密闭容器中空气质量和压力的机器。当工作流体是液体时，术语泵更常用，而气体更常用压缩机。 |
| Balance piston | 平衡活塞 |
(balance drum, dummy piston) A disc attached to the shaft of a turbine or compressor, to one side of which high or low pressure is applied to counteract the axial thrust produced by the pressure change across the machine. A form of thrust bearing. （平衡鼓，假活塞）连接在涡轮机或压缩机轴上的圆盘，在其一侧施加高压或低压，以抵消机器压力变化产生的轴向推力。推力轴承的一种形式。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Gamma iron | 加马铁 |
The face-centered cubic form of pure iron, stable from 910 to 1400 °C (1670 to 2550 °F). 纯铁的面心立方形式，在910至1400°C（1670 2550°F）温度范围内稳定。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Destructive testing | 破坏性测试 |
Measurement of the mechanical properties of a material, component, or structure, by increased loading until the sample fails by fracture, collapse, or buckling. 通过增加载荷测量材料、部件或结构的机械性能，直到样品因断裂、塌陷或屈曲而失效。 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Bulk density (Unit kg/m³) | 容重（单位kg/m³） |
The average density of a mass of granular or powdered material at ambient conditions. 在环境条件下大量粒状或粉状材料的平均密度。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Clevis | U形夹 |
A U-shaped hook with holes at the ends through which a retaining bolt or pin (clevis pin) passes. 一种U形钩，末端有孔，固定螺栓或销（U形销）穿过这些孔。 |
| Grain-boundary liquation | 晶界液化 |
An advanced stage of overheating in which material in the region of austenitic grain boundaries melts. 奥氏体晶界区域的材料熔化的过热阶段。 |
| Torque pack | 扭矩包 |
A geared wrench which multiplies input torque and provides a read-out of output torque. In effect, a combination of a Torque wrench and a Torque multiplier. 一种齿轮扳手，可增加输入扭矩并提供输出扭矩读数。实际上，它是扭矩扳手和扭矩倍增器的组合。 |
| Damage mechanics | 损伤机制 |
The theory of degradation in bodies, particularly fracture by accumulated microstructural damage. Analyses take two approaches: (a) the use of some critical integrated function of stress and strain at which cracking is initiated and propagated; (b) incorporation of damage in the stress–strain curves to reflect weakened material. 物体退化理论，尤其是累积微观结构损伤导致的断裂。分析采用两种方法：（a）使用裂纹开始和扩展时的应力和应变的一些临界积分函数；（b）应力-应变曲线中包含损伤，以反映弱化材料。 |
| Torque arm | 扭力臂 |
A bar fixed at one end used to resist torque applied at the other, for example by an electric drill. 固定在一端的杆，用于抵抗施加在另一端的扭矩，如电钻。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Crossed threads | 交叉螺纹 |
When the axis of a nut offered up to a bolt is not aligned with the axis of a bolt (or a screw to a threaded member), it may be possible for the threads to engage incorrectly and even for the nut or screw to advance a turn or more, but ultimately the misaligned threads become locked together. Forcing the nut in such circumstances may irretrievably damage the threads on both. 当提供给螺栓的螺母的轴线与螺栓（或螺纹构件的螺钉）的轴线不对齐时，螺纹可能会错误接合，甚至螺母或螺钉会提前一圈或更多，但最终未对齐的螺纹会锁定在一起。在这种情况下强行拧入螺母可能会对两侧的螺纹造成无法修复的损坏。 |
| Anelastic | 无弹性 |
Literally ‘not elastic’, but in practice used for materials that display timedependent recovery on unloading. 字面意思是“没有弹性”，但实际上用于在卸载时显示随时间恢复的材料。 |
| Mole number (N) | 摩尔数（N） |
The number of moles in a given mass m of a substance, equal to m divided by the molar mass of the substance. 摩尔数物质给定质量m中的摩尔数，等于m除以物质的摩尔质量。 |
| Punch | 冲床 |
1. A hand tool with a sharp point, used to mark the position of a hole centre in a workpiece prior to drilling. 2. A flat-ended tool with sharp edges, used to shear out a hole in a plate that is supported underneath on a die having a slightly larger same-shaped orifice. 1.一种带有尖头的手动工具，用于在钻孔前标记工件中孔中心的位置。2.一种具有锐边的平头工具，用于剪切板上的孔，该板支撑在具有稍大相同形状孔口的模具下方。 |
| Absolute viscosity | 绝对粘度 |
A measure of the internal shear properties of fluids, expressed as the tangential force per unit area at either of two horizontal planes separated by one unit thickness of a given fluid, one of the planes being fixed and the other moving with unit velocity. 流体内部剪切特性的量度，表示为两个水平面中的任何一个上的单位面积切向力，两个水平面被给定流体的一个单位厚度隔开，其中一个平面固定，另一个以单位速度移动。 |
| Clip gauge | 夹规 |
A displacement gauge consisting of two thin strain-gauged cantilever arms attached through knife edges to a testpiece to give the load–line displacement in fracture mechanics test pieces, or used as an extensometer in tensile tests. 一种位移计，由两个通过刀刃连接到试件上的薄应变测量悬臂组成，以提供断裂力学试件中的载荷线位移，或用作拉伸试验中的引伸计。 |
| Diffusion coating | 扩散涂层 |
Coating on metal for corrosion- and/or oxidation-resistance. Coatings are produced by heating a metal in contact with an alloy in powder, liquid, or gaseous form at elevated temperature such that atoms of the coating diffuse into the substrate. Examples include chromium, aluminium, or silicon on substrates such as nickel-based superalloys, steels, and refractory metals. 金属上的防腐和/或抗氧化涂层。涂层是通过在高温下加热与粉末、液体或气体形式的合金接触的金属，从而使涂层的原子扩散到基体中而产生的。实例包括基底上的铬、铝或硅，如镍基高温合金、钢和耐火金属。 |
| Stud | 螺柱 |
A rod having thread on both ends. A headless threaded fastener, threaded on both ends, with an unthreaded body in the middle section, or threaded from end to end. Used with two nuts, or with one nut and a tapped hole. A plain cylindrical piece having a threaded portion of suitable length at each end or a continuous thread over the entire length. One end is screwed into a machine or workpiece after which a second part is placed over the stud and held in place by a nut. 两端都有螺纹的杆。无头螺纹紧固件，两端有螺纹，中间部分有无螺纹主体，或从一端到另一端有螺纹。与两个螺母或一个螺母和一个螺纹孔一起使用。一种普通的圆柱形部件，其两端具有适当长度的螺纹部分，或在整个长度上具有连续螺纹。一端拧入机器或工件，然后将第二部分放在螺柱上，并用螺母固定到位。 |
| Gauge | 测量 |
1. Any instrument for measuring or checking dimensions, including adjustable gauges such as a micrometer and non-adjustable gauges such as go/no-go limit gauges that indicate the maximum and minimum dimensions allowable in a component during manufacture. 2. A term often used to mean an instrument, e.g. pressure gauge. 3. The diameter of a wire or thickness of a sheet according to a standard. 4. The distance between the rails of a railway track. 1. 任何用于测量或检查尺寸的仪器，包括可调节量规（例如千分尺）和不可调节量规（例如指示制造过程中组件允许的最大和最小尺寸的通过/不通过限制量规）。2. 常用于表示仪器的术语，例如压力表。3.根据标准的线材直径或片材厚度。4.铁路轨道的钢轨之间的距离。 |
| Lüders lines | 吕德斯线 |
Elongated surface markings or depressions, often visible with the unaided eye, that form along the length of sheet metal or a tension specimen at an angle of approximately 45° to the loading axis. Caused by localized plastic deformation, they result from discontinuous (inhomogeneous) yielding. Also known as Lüders bands, Hartmann lines, Piobert lines, or stretcher strains. 拉长的表面标记或凹陷，通常肉眼可见，沿金属板或拉伸试样的长度形成，与加载轴的角度约为45°。由于局部塑性变形，它们是不连续（不均匀）屈服的结果。也被称为吕德斯带、哈特曼线、皮奥伯特线或拉伸线。 |
| Blue brittleness | 蓝色脆性 |
Anomalous loss of ductility when quenched steels are tempered in the range 250–350°C (temperatures that produce blue tints on the surface of components). Brittleness exhibited by some steels after being heated to some temperature within the range of about 205 to 370 °C (400 to 700 °F), particularly if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. 当淬火钢在250–350°C范围内回火（在部件表面产生蓝色色调的温度）时，延展性异常损失。某些钢在加热到约205至370°C（400至700°F）范围内的某个温度后表现出脆性，特别是在高温下加工钢时。镇静钢几乎没有这种脆性。 |
| Stress raisers | 局部应力集中 |
Changes in contour or discontinuities in structure that cause local increases in stress. 导致局部应力增加的轮廓变化或结构不连续性变化。 |
| Air-hardening steel | 空气硬化钢 |
A steel containing sufficient carbon and other alloying elements to harden fully during cooling in air or other gaseous mediums from a temperature above its transformation range. The terms should be restricted to steels that are capable of being hardened by cooling in air in fairly large sections, about 2 in. (50 mm) or more in diameter. Same as self-hardening steel. 一种钢，含有足够的碳和其他合金元素，可以在空气或其他气体介质中从高于其转变范围的温度冷却过程中完全硬化。这些术语应仅限于能够通过在相当大的截面（直径约2英寸（50毫米）或更大）中通过空气冷却而硬化的钢。与自硬钢相同。 |
| Gauge pressure (Unit Pa) | 表压（单位Pa） |
The level of static pressure above the ambient pressure. 高于环境压力的静压水平。 |
| Strain rate | 应变率 |
The time rate of straining for the usual tensile test. Strain as measured directly on the specimen gage length is used for determining strain rate. Because strain is dimensionless, the units of strain rate are reciprocal time. 通常拉伸试验的应变时间速率。直接在试样标距上测量的应变用于确定应变率。因为应变是无因次的，所以应变率的单位是倒数时间。 |
| Catastrophic failure | 灾难性故障 |
A sudden and total failure of a large engineering structure such as an aeroengine, aircraft, space vehicle, bridge, or dam. 大型工程结构（如航空发动机、飞机、航天器、桥梁或水坝）突然完全失效。 |
| Transformation toughening | 相变增韧 |
The improvement of fracture toughness of a material by stress-induced transformation of the microstructure. 通过微结构的应力诱导转变来提高材料的断裂韧性。 |
| Ideal critical diameter | 理想临界直径 |
(DI). Under an ideal quench condition, the bar diameter that has 50% martensite at the center of the bar when the surface is cooled at an infinitely rapid rate (that is, when H = ∞, where H is the quench severity factor). （DI）在理想淬火条件下，当表面以无限快的速度冷却时（即H=∞, 其中H是淬火严重度因子）。 |
| Stroke | 一击 |
1. (stroke length) (Unit m) The linear distance between top dead centre and bottom dead centre of a piston in a reciprocating engine or mechanism. 2. The movement of a piston or plunger in a reciprocating machine to execute a particular function; for example, the exhaust stroke of an engine in which the exhaust gases are expelled from a cylinder. 1.（冲程长度）（单位：m）往复式发动机或机构中活塞上止点和下止点之间的线性距离。2.活塞或柱塞在往复式机器中执行特定功能的运动；例如发动机的排气冲程，其中排气从气缸中排出。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Austempering | 等温淬火 |
A heat treatment for ferrous alloys in which a part is quenched from the austenitizing temperature at a rate fast enough to avoid formation of ferrite or pearlite and then held at a temperature just above Ms until transformation to bainite is complete. Although designated as bainite in both austempered steel and austempered ductile iron (ADI), austempered steel consists of two phase mixtures containing ferrite and carbide, while austempered ductile iron consists of two phase mixtures containing ferrite and austenite. Heat treatment comprising austenitization of a steel article, cooling it to a bainitic range at a rate higher than the critical cooling rate and holding at a fixed temperature until the completion of bainitic transformation. 一种铁合金的热处理，其中零件从奥氏体化温度以足够快的速度淬火，以避免形成铁素体或珠光体，然后保持在略高于Ms的温度，直到完全转变为贝氏体。虽然在奥氏体钢和奥氏体球铁(ADI)中都被指定为贝氏体，但奥氏体钢由含有铁素体和碳化物的两相混合物组成，而奥氏体球墨铸铁由含有铁素体和奥氏体的两相混合物组成。热处理包括钢制品的奥氏体化，以高于临界冷却速率的速率将其冷却到贝氏体范围，并保持在固定温度直到贝氏体转变完成。 |
| Nut factor | 螺母系数 |
An experimental constant used to evaluate or describe the ratio between the torque applied to a fastener and the Preload achieved as a result. 用于评估或描述施加在紧固件上的扭矩与由此获得的预载之间的比率的实验常数。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Brittle lacquer coating | 脆性漆涂层 |
A lacquer that, when painted on to an unloaded body, reveals the direction of maximum tension stresses from the pattern of cracking produced in the lacquer when the body is loaded. 一种漆，当涂在未加载的车身上时，从车身加载时在漆中产生的裂纹图案中显示出最大拉应力的方向。 |
| Centigrade heat unit | 摄氏热量单位 |
(Celsius heat unit, CHU) An obsolete (i.e. non-SI) unit equal to the energy required to increase the temperature of one pound of pure, air-free water from 14.5°C to 15.5°C at a pressure of one standard atmosphere. （摄氏热量单位，CHU）一个已被淘汰的（即非国际单位制）单位，等于在一个标准大气压的压力下将一磅纯净的无空气水的温度从14.5°C提高到15.5°C所需的能量. |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Spring | 弹簧 |
An elastic component which stores mechanical energy and exerts a force when deformed. The slope of the curve of applied force F to the deflexion of a spring x, dF/dx, is termed the spring rate or spring modulus k with unit N/m. For a linear spring, the F(x) curve is proportional and k is called the spring constant. An elastic device which yields under stress or pressure but returns to its original state or position when the stress or pressure is removed. 储存机械能并在变形时施加力的弹性部件。作用力F与弹簧x偏转的曲线斜率dF/dx称为弹簧率或弹簧模量k，单位为N/m。对于线性弹簧，F（x）曲线成比例，k称为弹簧常数。一种弹性装置，在应力或压力下屈服，但在应力和压力消除后恢复到其原始状态或位置。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Physical testing | 物理测试 |
Methods used to determine the entire range of physical properties of a material. In addition to density and thermal, electrical, and magnetic properties, physical testing methods can be used to assess simple fundamental physical properties such as color, crystalline form, and melting point. 用于确定材料整个物理特性范围的方法。除了密度和热、电、磁特性外，物理测试方法还可用于评估简单的基本物理特性，如颜色、结晶形式和熔点。 |
| Mechatronics | 机电一体化 |
The integration of mechanical engineering, electrical engineering, electronic engineering, and software engineering. 机械工程、电气工程、电子工程和软件工程的集成。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Stretch ratio (extension ratio, λ) | 拉伸比（拉伸比，λ） |
A measure, used for highly-extensible materials such as rubber, of the extensional or normal strain of a component subjected to tension and defined as the ratio of the final length l, for a given load, to the initial or gauge length l0, where the coordinate axes are those of principal strain. It is related to the engineering strain e by λ = 1 + e. 用于高度可延展材料（如橡胶）的一种测量方法，用于测量受拉构件的拉伸或法向应变，定义为给定载荷下的最终长度l与初始或标距长度l0之比，其中坐标轴为主应变轴。它与工程应变e的关系为λ=1+e。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Refractory materials | 耐火材料 |
Metals or ceramics that do not melt when exposed to temperature above about 1 500°C or deteriorate rapidly in a continuous temperature above about 550°C. 当暴露于高于约1500°C的温度时不熔化或在高于约550°C的连续温度下快速劣化的金属或陶瓷。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Scoring | 划痕 |
In tribology, a severe form of wear characterized by the formation of extensive grooves and scratches in the direction of sliding. 在摩擦学中，一种严重的磨损形式，其特征是在滑动方向上形成大面积的凹槽和划痕。 |
| Graphitic carbon | 石墨碳 |
Free carbon in steel or cast iron. 钢或铸铁中的游离碳。 |
| Breaking stress | 断裂应力 |
The stress at failure. Also known as rupture stress. 失效时的应力。也称为破裂应力。 |
| Flange | 法兰 |
Flange refers to a head style for bolts where there is a circular ‘flange’ under the head that acts like a washer to distribute a load. A flange is a projected flat rim or collar. 1. Annular rims at the ends of pipes (flanged pipe) or shafts by which they may be coupled together using bolts that pass through holes in the flanges (flange coupling, flange union), or by toggle clamps around the periphery. 2. An extended rim on a wheel that positions it laterally on a track. Commonly used for railway rolling stock. 3. The top and bottom parts of an I-beam. 法兰是指螺栓的头部样式，其中头部下方有一个圆形“法兰”，其作用类似于垫圈以分配载荷。凸缘是凸出的平轮辋或凸缘。1.管道（法兰管）或轴端部的环形边缘，通过这些边缘，可以使用穿过法兰孔的螺栓（法兰联轴器、法兰接头）或通过周边的肘节夹将管道连接在一起。2.车轮上的延伸轮辋，将其横向定位在轨道上。通常用于铁路车辆。3.工字梁的顶部和底部。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Calorie | 卡路里 |
(cal, gram calorie, small calorie) An obsolete (i.e. non-SI) unit of energy equal to 4.186 8 J. It is the amount of energy needed to raise the temperature of 1 gram of pure airfree water from 14.5°C to 15.5°C at standard atmospheric pressure. （卡，克热量，小热量）一种已被淘汰的（即非SI）能量单位，等于4.1868J。它是在标准大气压力下将1克纯无空气水的温度从14.5℃升高到15.5℃所需的能量。 |
| Maximum allowable operating pressure (Unit Pa) | 最大允许使用压力（单位Pa） |
The highest pressure at which any pressure system may be operated, usually 10 to 20% below the maximum allowable working pressure. 任何压力系统可运行的最高压力，通常比最大允许工作压力低10%至20%。 |
| Coefficient of cubic expansion | 立方膨胀系数 |
The fractional increase in volume per unit temperature rise. 每单位温度升高的体积增加分数。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Lap joint | 搭接接头 |
A riveted, welded, or bonded connection between two plates made by overlapping one plate above the other. Lap joints having plates above and below a butt joint avoid the bending moment associated with a simple lap joint. 两块板之间的铆接、焊接或粘结连接，通过将一块板重叠在另一块板上而形成。对接接头上方和下方具有板的搭接接头避免了与简单搭接接头相关的弯矩。 |
| Coated abrasive | 涂附磨具 |
An abrasive tool consisting of a flexible backing material, such as a woven cloth, paper or vulcanized fibre, a bond material, such as a glue or synthetic resin, and grit. 一种研磨工具，由柔性背衬材料（例如编织布、纸或硫化纤维）、粘合材料（例如胶水或合成树脂）和砂砾组成。 |
| Hooke’s law | 胡克定律 |
Within the limit of proportionality, the extension of a material is proportional to the applied force. Approximately, it is the relationship between stress and strain in an elastic material when it is stretched. The law states that the stress (force per unit area) is proportional to the strain (a change in dimensions). The law, which holds only approximately and over a limited range, was discovered in 1676 by Robert Hooke. 在比例极限内，材料的延伸与所施加的力成比例。近似地说，它是弹性材料拉伸时应力和应变之间的关系。该定律指出，应力（单位面积的力）与应变（尺寸变化）成比例。该定律仅适用于有限的范围，由罗伯特·胡克于1676年发现。 |
| Electrode | 电极 |
The two metallic bodies in a battery or Corrosion cell which give up electrons (the Anode) or which attract them (the Cathode). 电池或腐蚀电池中释放电子（阳极）或吸引电子（阴极）的两个金属体。 |
| Grain growth | 晶粒生长 |
An increase in the average size of the grains in polycrystalline metal, usually as a result of heating at elevated temperature. 多晶金属中晶粒平均尺寸的增加，通常是高温加热的结果。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| Unit | 单位 |
A numerical indication of the magnitude of a physical quantity. The basic units of mass, length, time, etc. are relative to agreed standards. 物理量大小的数字指示。质量、长度、时间等基本单位与商定的标准相对应。 |
| Raised-face flange | 凸面法兰 |
A flange which contacts its mating joint member only in the region in which the gasket is located. The flanges do not contact each other at the bolt circle. 仅在垫圈所在区域接触其配合接头构件的法兰。法兰在螺栓圆处不相互接触。 |
| Ablation cooling | 烧蚀冷却 |
The cooling of a surface exposed to very high external gas temperature which causes the surface material to sublime, melt or decompose. The chemical process absorbs heat while the mass flow of material away from the surface blocks the heat flux from the hot gas. 冷却暴露于非常高的外部气体温度的表面，导致表面材料升华、熔化或分解。化学过程吸收热量，而远离表面的物质的质量流阻挡了来自热气体的热通量。 |
| Metric ton (tonne, t) | 公制吨（吨，t） |
An SI-accepted, but non-SI, unit of mass defined as 1 t = 103 kg. SI系统可接受但非国际单位制的质量单位，定义为1t=103kg。 |
| Mass flow meter | 质量流量计 |
An instrument, such as a Coriolis flow meter, which measures the mass flow rate of a fluid flowing through a pipe or other duct, rather than its volume flow rate. 一种仪器，例如科里奥利流量计，一种测量流经管道或其他管道的流体的质量流率而不是其体积流率的仪器。 |
| Shoulder joint | 轴肩关节 |
The second joint on an articulated robot, which has a horizontal axis and is analogous to the human shoulder. 关节机器人上的第二个关节，具有水平轴，类似于人的肩膀。 |
| Vacuum pump | 真空泵 |
A pump for exhausting air and non-condensable gases from a vessel to be maintained at sub-atmospheric pressure. The pirani and thermal-conductivity gauges are vacuum gauges used to measure the absolute pressure within a vacuum system (vacuum level), usually expressed in torr or Pa. 用于从容器中排出空气和不凝性气体以保持在亚大气压的泵。皮拉尼和热导率计是用于测量真空系统内绝对压力（真空水平）的真空计，通常用托或帕表示。 |
| Congruent transformation | 全等变换 |
An isothermal or isobaric phase change in which both of the phases concerned have the same composition throughout the process. 等温或等压相变，其中相关的两个相在整个过程中具有相同的成分。 |
| Creep | 蠕变 |
The slow, plastic deformation of a body under heavy loads. Time-dependent plasticity. Time-dependent and permanent deformation of material under constant load or stress. The strain increases with time at a rate that increases with increasing temperature. Creep can lead to large strain and eventual failure, and so limit the lifetime of components subjected to load at high temperature. Creep in metals becomes significant at homologous temperatures in excess of about 0.4, e.g. 1200°C for tungsten, 504°C for titanium, 450°C for iron, and 100°C for aluminium. 物体在重载荷下缓慢的塑性变形，随时间变化的可塑性，材料在恒定载荷或应力下随时间变化的永久变形。应变随时间以随温度升高而增加的速率增加。蠕变可能导致大应变和最终失效，从而限制部件在高温下承受载荷的寿命。当同源温度超过约0.4℃时，金属蠕变变得显著，例如钨为1200℃，钛为504℃，铁为450℃，铝为100℃。 |
| Plowing | 犁 |
In tribology, the formation of grooves by plastic deformation of the softer of two surfaces in relative motion. 在摩擦学中，通过相对运动的两个表面中较软的表面的塑性变形形成凹槽。 |
| 显示更多数据，请使用查询功能！ | ||