| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Fatigue | 疲劳 |
The phenomenon leading to fracture under repeated or fluctuating stresses having a maximum value less than the ultimate tensile strength of the material. Fatigue failure generally occurs at loads that, applied statically, would produce little perceptible effect. Fatigue fractures are progressive, beginning as minute cracks that grow under the action of the fluctuating stress. A term referring, in components and structures subjected to either random or cyclic periodically-varying loads, to a progressive reduction in strength leading to failure at stresses lower than those that cause failure under monotonic loading. Variable loads arise from outof-balance machinery and other vibration sources, wind gusts, etc., and a large proportion of service failures is caused by fatigue. Fatigue results from the initiation and slow propagation of cracks. In manufactured components, crack initiation usually occurs at a point of stress concentration. After a period, often of millions of stress cycles, the crack reaches a critical length at which the next peak load causes sudden brittle or ductile fracture. Fracture surfaces resulting from fatigue display characteristic striations or progression marks emanating from the crack initiation site during the slow crack growth period, with a different surface appearance for the final fracture. 在最大值小于材料极限抗拉强度的重复或波动应力下导致断裂的现象。疲劳失效通常发生在静态施加的载荷下，不会产生明显影响。疲劳断裂是渐进性的，从在波动应力作用下生长的微小裂纹开始。在承受随机或周期性变化载荷的部件和结构中，指强度逐渐降低，导致在低于单调载荷下导致失效的应力下发生失效的术语。可变负载由失衡的机械和其他振动源、阵风等引起，大部分故障是由疲劳引起的。疲劳是裂纹萌生和缓慢扩展的结果。在制造部件中，裂纹萌生通常发生在应力集中点。在一段时间（通常是数百万次应力循环）后，裂纹达到临界长度，此时下一个峰值载荷会导致突然脆性或韧性断裂。疲劳产生的断裂表面在缓慢裂纹扩展期间显示出从裂纹萌生部位发出的特征条纹或进展标记，最终断裂的表面外观不同。 |
| Controlled cooling | 控制冷却 |
Cooling from an elevated temperature in a predetermined manner, to avoid hardening, cracking, or internal damage, or to produce desired microstructure or mechanical properties. 以预定方式从升高的温度冷却，以避免硬化、开裂或内部损坏，或产生所需的微观结构或机械性能。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Stretch forming | 拉伸成型 |
A manufacturing process in which sheet-metal components are physically stretched over a forming die using a press, punch, or edge clamps. Stretching combined with bending reduces springback. 一种制造工艺，其中使用压力机、冲头或边缘夹具在成形模上物理拉伸金属板部件。拉伸与弯曲相结合可减少回弹。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Plane stress | 平面应力 |
The stress condition in linear-elastic fracture mechanics in which the stress in the thickness direction is zero; most nearly achieved in loading very thin sheet along a direction parallel to the surface of the sheet. Under plane-stress conditions, the plane of fracture instability is inclined 45° to the axis of the principal tensile stress. 线弹性断裂力学中厚度方向上的应力为零的应力条件；在沿着平行于薄片表面的方向加载非常薄的薄片时最接近。在平面应力条件下，断裂失稳平面与主拉应力轴倾斜45°。 |
| Breaking stress | 断裂应力 |
The stress at failure. Also known as rupture stress. 失效时的应力。也称为破裂应力。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Counter sink | 台面水槽 |
To cut or shape a depression in an object so that the head of a screw may set flush or below the surface. 在物体上切割或塑造一个凹陷，使螺钉的头部可以齐平或低于表面。 |
| Shear modulus (G) | 剪切模量（G） |
The ratio of shear stress to the corresponding shear strain for shear stresses below the proportional limit of the material. Values of shear modulus are usually determined by torsion testing. Also known as modulus of rigidity. 对于低于材料比例极限的剪切应力，剪切应力与相应剪切应变之比。剪切模量值通常通过扭转试验确定。也称为刚度模量。 |
| Tyre | 轮胎 |
A flexible ring-shaped cover mounted on a wheel rim that supports the weight of a vehicle, such as a motor vehicle, aircraft, or bicycle, and transmits power and torque to a road surface. Some pneumatic tyres are inflated directly, others have a separate inner tube that is inflated. For certain applications, solid tyres are used. 车轮罩安装在轮辋上的柔性环形罩，用于支撑车辆（如机动车、飞机或自行车）的重量，并将动力和扭矩传递到路面。有些充气轮胎是直接充气的，有些轮胎有单独的内胎充气。对于某些应用，使用实心轮胎。 |
| Load and resistance factor design | 负载和阻力系数设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Assigns uncertainties in the strength of (i.e., resistance of) and in the service loads to be placed on a shear joint to estimate the probable strength of the joint. It is a recently defined alternative to the Allowable stress design procedure. 结构连接研究委员会为AISC制定的设计程序。分配剪切接头的强度（即阻力）和工作荷载的不确定性，以估计接头的可能强度。它是最近定义的容许应力设计程序的替代方案。 |
| Final annealing | 最终退火 |
An imprecise term used to denote the last anneal given to a nonferrous alloy prior to shipment. 一个不精确的术语，用于表示有色金属合金在装运前的最后一次退火。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Indentation hardness | 压痕硬度 |
The resistance of a material to indentation as determined by hardness testing. The indenter, which may be spherical or diamond shaped, is pressed into the surface of a metal under specified load for a given time. (Unit Pa or, non-SI, kgf/mm²) A measurement of hardness taken by means of an indenter, pressed into a material by a load, which makes a permanent impression. The hardness is given by the load divided by the projected (sometimes surface) area of the indentation. Plasticity theory shows that the hardness is about 2.5–3 times the uniaxial yield stress. 通过硬度测试确定的材料抗压痕的能力。压头可以是球形或菱形，在规定的载荷下压入金属表面一段时间。（单位Pa或，非国际单位制，kgf/mm²）通过压头测量硬度，压入材料，形成永久压痕。硬度由载荷除以压痕的投影（有时是表面）面积得出。塑性理论表明，硬度约为单轴屈服应力的2.5–3倍。 |
| Altitude | 高度 |
(Unit m) Vertical height measured relative to a specified datum such as sea level. （单位m）相对于特定基准（例如海平面）测量的垂直高度。 |
| Transducer | 传感器 |
A device which converts one form of energy into another. An ultrasonic transducer, for example, converts electrical energy into acoustic energy (at ultrasonic frequencies) and vice versa. 将一种形式的能量转换为另一种形式能量的装置。例如，超声换能器将电能转换为声能（在超声频率下），反之亦然。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Hooke’s law | 胡克定律 |
Within the limit of proportionality, the extension of a material is proportional to the applied force. Approximately, it is the relationship between stress and strain in an elastic material when it is stretched. The law states that the stress (force per unit area) is proportional to the strain (a change in dimensions). The law, which holds only approximately and over a limited range, was discovered in 1676 by Robert Hooke. 在比例极限内，材料的延伸与所施加的力成比例。近似地说，它是弹性材料拉伸时应力和应变之间的关系。该定律指出，应力（单位面积的力）与应变（尺寸变化）成比例。该定律仅适用于有限的范围，由罗伯特·胡克于1676年发现。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Hot-wire test | 热线测试 |
Method used to test heat extraction rates of various quenchants. Faster heat-extracting quenchants will permit more electric current to pass through a standard wire because it is cooled more quickly. Compare with hot-wire analyzer. 用于测试各种淬火剂的热提取率的方法。与热线分析仪相比，更快的热提取淬火剂将允许更多电流通过标准导线，因为标准导线冷却更快。 |
| Shrink ring | 预紧环 |
A ring, which is expanded by heating, is placed around an assembly of parts, and then contracts upon cooling to hold the assembly in place. 通过加热膨胀的环被放置在零件组件周围，然后在冷却时收缩以将组件固定到位。 |
| Corrosion fatigue | 腐蚀疲劳 |
Cracking produced by the combined action of repeated or fluctuating stress and a corrosive environment at lower stress levels or fewer cycles than would be required in the absence of a corrosive environment. 由重复或波动的应力和腐蚀环境的联合作用产生的开裂，其应力水平低于没有腐蚀环境时所需的应力水平或循环次数更少。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Transmissibility | 传递率 |
The ratio of the transmitted force to the disturbing force for a system subjected to a vibratory disturbance. The ratio may also be defined in terms of displacements, velocities, or accelerations. 受到振动干扰的系统的传递力与干扰力之比。该比率也可以用位移、速度或加速度来定义。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Embrittlement | 脆化 |
The loss of ductility or fracture toughness of materials, either during processing or in service. The severe loss of ductility or toughness or both, of a material, usually a metal or alloy. Many forms of embrittlement can lead to brittle fracture. Many forms can occur during thermal treatment or elevated-temperature service (thermally induced embrittlement). Some of these forms of embrittlement, which affect steels, include blue brittleness, 885 °F (475 °C) embrittlement, quench-age embrittlement, sigma-phase embrittlement, strain-age embrittlement, temper embrittlement, tempered martensite embrittlement, and thermal embrittlement. In addition, steels and other metals and alloys can be embrittled by environmental conditions (environmentally assisted embrittlement). The forms of environmental embrittlement include acid embrittlement, caustic embrittlement, corrosion embrittlement, creep-rupture embrittlement, hydrogen embrittlement, liquid metal embrittlement, neutron embrittlement, solder embrittlement, solid metal embrittlement, and stress-corrosion cracking. 材料在加工或使用过程中的延展性或断裂韧性损失。通常是金属或合金的延展性或韧性或两者的严重损失。多种形式的脆化可导致脆性断裂。在热处理或高温服务期间，可能会出现多种形式（热致脆化）。影响钢的一些脆化形式包括蓝脆、885°F（475°C）脆化、淬火时效脆化、西格玛相脆化、应变时效脆化，回火脆化、回火马氏体脆化和热脆化。此外，钢和其他金属和合金可能因环境条件而脆化（环境辅助脆化）。环境脆化的形式包括酸脆化、碱脆化、腐蚀脆化、蠕变断裂脆化、氢脆化、液态金属脆化、中子脆化、焊料脆化、固态金属脆化和应力腐蚀开裂。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Pitch | 沥青节距 |
The nominal distance between two adjacent thread roots or crests. In screw threads, the distance from a point on one thread to a corresponding point on the next thread measured parallel to the axis. In the case of spur gears, indicates the size of the gear teeth and is correctly called diametral pitch. 两个相邻螺纹根部或顶部之间的标称距离。在螺纹中，从一根螺纹上的一点到下一根螺纹对应点的距离，平行于轴线测量。对于正齿轮，表示齿轮齿的尺寸，正确地称为径向节距。 |
| Fracture | 断裂 |
(rupture) The separation of materials, components, or structures into two or more parts by the propagation of one or more cracks. Cracking may be globally elastic (brittle) or accompanied by varying degrees of plasticity (ductile). （断裂）通过一个或多个裂纹的扩展将材料、部件或结构分离成两个或更多部分。裂纹可能是整体弹性（脆性）或伴有不同程度的塑性（延性）。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Carbonitriding | 碳氮共渗 |
A case hardening process in which a suitable ferrous material is heated above the lower transformation temperature in a gaseous atmosphere of such composition as to cause simultaneous absorption of carbon and nitrogen by the surface and, by diffusion, create a concentration gradient. The process is completed by cooling at a rate that produces the desired properties in the workpiece. 一种表面硬化工艺，在该工艺中，将合适的含铁材料在气体气氛中加热到较低的转变温度以上，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。该工艺通过以在工件中产生所需性能的速率冷却来完成。 |
| Isothermal annealing | 等温退火 |
Austenitizing a ferrous alloy and then cooling to and holding at a temperature at which austenite transforms to a relatively soft ferrite carbide aggregate. 将铁合金奥氏体化，然后冷却至奥氏体转变为相对软的铁素体碳化物集合体的温度并保持该温度。 |
| Fibreglass | 玻璃纤维 |
Fibreglass is used in studs and nuts for applications when the fastener should be non-corrosive, low in conductivity, or transparent to electromagnetic waves. 当紧固件应无腐蚀性、低导电性或对电磁波透明时，玻璃纤维用于螺柱和螺母中。 |
| Carbon restoration | 碳修复 |
Replacing the carbon lost in the surface layer from previous processing by carburizing this layer to substantially the original carbon level. Sometimes called recarburizing. 通过将该层渗碳到基本上原始的碳水平来替换先前处理中在表面层中损失的碳。有时称为再碳化。 |
| Calorie | 卡路里 |
(cal, gram calorie, small calorie) An obsolete (i.e. non-SI) unit of energy equal to 4.186 8 J. It is the amount of energy needed to raise the temperature of 1 gram of pure airfree water from 14.5°C to 15.5°C at standard atmospheric pressure. （卡，克热量，小热量）一种已被淘汰的（即非SI）能量单位，等于4.1868J。它是在标准大气压力下将1克纯无空气水的温度从14.5℃升高到15.5℃所需的能量。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Clearance fit | 间隙配合 |
A range of clearances ranging from close sliding to loose running, i.e. a fit in which the limits for the mating parts always permit assembly. 从紧密滑动到松动运行的一系列间隙，即配合零件的限制始终允许组装的配合。 |
| Annealing twin | 退火孪晶 |
A twin form in a crystal during recrystallization. 重结晶过程中晶体中的孪晶形式。 |
| Flame annealing | 火焰退火 |
Annealing in which the heat is applied directly by a flame. 通过火焰直接加热的退火。 |
| Water hammer | 水锤 |
The reflected pressure surge that occurs in a liquid flowing through a pipe, usually as a consequence of sudden closure of a valve. The surge may cause the pipe to vibrate and a hammering noise to be heard. Key factors affecting the surge amplitude are the compressibility of the liquid (especially if it contains undissolved gas) and the elasticity of the pipe wall. 在流经管道的液体中发生的反射压力波动，通常是阀门突然关闭的结果。浪涌可能导致管道振动，并听到锤击噪音。影响喘振幅度的关键因素是液体的可压缩性（特别是当其含有未溶解气体时）和管壁的弹性。 |
| Plug gauge | 塞规 |
A steel gauge used to determine the dimension or dimensions of a hole. It may be straight or tapered, and is typically circular, but in principle can have any cross section. 用于确定孔的尺寸的钢制量规。它可以是直的或锥形的，通常是圆形的，原则上可以有任何横截面。 |
| Degradation failure | 退化失效 |
Failure of a system, component, or structure owing to material degradation. 由于材料退化导致的系统、组件或结构失效。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Striation | 条纹组织 |
A fatigue fracture feature, often observed in electron micrographs, that indicates the position of the crack front after each succeeding cycle of stress. The distance between striations indicates the advance of the crack front across that crystal during one stress cycle, and a line normal to the striation indicates the direction of local crack propagation. 一种疲劳断裂特征，通常在电子显微照片中观察到，表明每次应力循环后裂纹前沿的位置。条纹之间的距离表示在一个应力循环期间裂纹前沿穿过该晶体的前进，垂直于条纹的线表示局部裂纹扩展的方向。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Computer control | 电脑控制 |
The control of an engineering device or system by pre-programmed computer or by feedback control. 通过预编程计算机或反馈控制对工程设备或系统进行控制。 |
| Spring clip | 弹簧夹 |
A clip made of a material such as spring steel which grips an inserted part. 由弹簧钢等材料制成的夹子，用于夹住插入的零件。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Diffusion | 扩散 |
(1) Spreading of a constituent in a gas, liquid, or solid, tending to make the composition of all parts uniform. (2) The spontaneous movement of atoms or molecules to new sites within a material. （1） 一种成分在气体、液体或固体中的扩散，趋于使所有部分的成分均匀。（2） 原子或分子自发运动到材料内的新位置。 |
| Centrifuge | 离心机 |
A machine incorporating a rapidly spinning drum in which liquids and suspended particles of different densities are separated by centrifugal action. 一种装有快速旋转滚筒的机器，在该滚筒中，不同密度的液体和悬浮颗粒通过离心作用分离。 |
| Noble metals | 贵金属 |
Metallic elements from periods (rows) 5 and 6 of the periodic table, namely ruthenium, rhodium, palladium, silver, osmium, iridium, platinum, and gold. They resist corrosion and oxidation and are used for electrical contacts, thin-film circuits, and electroplating. Gold, silver, and platinum used for jewellery are also known as precious metals. They have face-centred cubic crystal structure and good ductility. 周期表第5和第6周期（行）中的金属元素，即钌、铑、钯、银、锇、铱、铂和金。它们抗腐蚀和氧化，用于电触点、薄膜电路和电镀。用于珠宝的金、银和铂也被称为贵金属。它们具有面心立方晶体结构和良好的延展性。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Normalizing | 正火 |
Heating a ferrous alloy to a suitable temperature above the transformation range and then cooling in air to a temperature substantially below the transformation range. 将铁合金加热至高于转变范围的合适温度，然后在空气中冷却至基本低于转变范围的温度。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| constitutive equation | 本构方程 |
(constitutive relation) 1. In solid mechanics or fluid mechanics, an algebraic or numerical relation for the dependency of stress on deformation, strain, strain rate, temperature, etc. in a material. In solid mechanics such a relation is sometimes called an equation of state. Simple linear examples include Hooke’s law and Newton’s viscosity law. 2. In heat transfer, a relation, such as Fourier’s law of heat conduction, connecting heat flux with temperature gradient. （本构关系）1.在固体力学或流体力学中，应力与材料的变形、应变、应变率、温度等之间的代数或数值关系。在固体力学中，这种关系有时称为状态方程。简单的线性例子包括胡克定律和牛顿粘度定律。2.在传热学中，将热流与温度梯度联系起来的一种关系，如傅立叶热传导定律。 |
| Dimension line | 尺寸线 |
A line on an engineering drawing with a numeral above it that shows the length of a feature, usually in millimetres. 工程图上的一条线，上面有一个数字，表示特征的长度，通常以毫米为单位。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Lockbolt | 锁紧螺栓 |
A fastener which bears a superficial resemblance to a bolt, but which engages a collar (instead of a nut) with annular grooves (instead of threads). The collar is swaged over the grooves on the male fastener to develop preload. 表面上类似于螺栓的紧固件，但与环槽（而不是螺纹）接合的轴环（而不是螺母）。套环在阳紧固件上的凹槽上锻造，以产生预紧力。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Stress corrosion cracking (SCC) | 应力腐蚀开裂（SCC） |
A common form of Stress cracking in which an Electrolyte encourages the growth of a crack in a highly stressed bolt. Only a tiny quantity of electrolyte need be present, at the tip or face of the crack. A time-dependent process in which a metallurgically susceptible material fractures prematurely under conditions of simultaneous corrosion and sustained loading at lower stress levels than would be required in the absence of a corrosive environment. Tensile stress is required at the metal surface and may be a residual stress resulting from heat treatment or fabrication of the metal or the result of external loading. Cracking may be intergranular or transgranular, depending on the combination of alloy and environment. 一种常见的应力开裂形式，其中电解液促使高应力螺栓中的裂纹扩展。在裂纹尖端或表面，只需存在少量电解质。一种随时间变化的过程，其中冶金敏感材料在同时腐蚀和持续加载的条件下过早断裂，其应力水平低于无腐蚀环境时的要求。在金属表面需要拉应力，拉应力可以是金属的热处理或制造或外部负载产生的残余应力。裂纹可能是沿晶开裂或穿晶开裂，这取决于合金和环境的组合。 |
| Radial-flow compressor | 离心式压缩机 |
A compressor in which the working gas enters the machine axially and is compressed as it flows radially out through the impeller. 一种压缩机，其中工作气体轴向进入机器，并在通过叶轮径向流出时被压缩。 |
| Radial load (Unit N) | 径向负荷（单位：N） |
1. Centrifugal loading induced in a rotating body. 2. (through-wallthickness load) The radial component of loading arising from internal or external pressurization of a closed vessel. There will also be axial and hoop loading. 1.旋转体中产生的离心载荷。2.（贯穿壁厚载荷）由封闭容器的内部或外部加压产生的载荷的径向分量。还存在轴向和环向载荷。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Plane strain | 平面应变 |
The stress condition in linear-elastic fracture mechanics in which there is zero strain in a direction normal to both the axis of applied tensile stress and the direction of crack growth (i.e., parallel to the crack front); most nearly achieved in loading thick plates along a direction parallel to the plate surface. Under plane-strain conditions, the plane of fracture instability is normal to the axis of the principal tensile stress. 线弹性断裂力学中的应力条件，其中在垂直于施加拉应力轴和裂纹扩展方向（即平行于裂纹前沿）的方向上存在零应变；最接近于沿平行于板表面的方向加载厚板。在平面应变条件下，断裂失稳平面垂直于主拉应力轴。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Acoustic separation | 声学分离 |
(Unit m) The separation of particles in a fluid using standing acoustic waves, typically ultrasound, to drive them to nodal points (acoustic particle concentration). （单位m）使用驻声波（通常是超声波）将流体中的粒子分离，以将它们驱动到节点（声学粒子浓度）。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Joule | 焦耳 |
The SI unit of energy. One joule is the work done by a force of one newton acting over a distance of one metre. The symbol is J, where 1 J = 1 N m. 国际单位制能量单位。一焦耳是一牛顿的力在一米的距离上所做的功。符号为J，其中1j=1m。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Threaded fastener | 螺纹紧固件 |
Studs, bolts, and screws of all sorts, with associated nuts. One of the most interesting, complex, useful—and frustrating—components yet devised. 各种螺柱、螺栓和螺钉，以及相关的螺母。 |
| Collapse load (Unit N) | 毁坏荷载（单位N） |
The applied load at which a structure becomes a mechanism owing to the formation of sufficient plastic hinges for collapse to occur. 由于形成足够的塑性铰链以发生坍塌，结构成为机制的施加载荷。 |
| Age hardening | 时效硬化 |
Raising the strength and hardness of an alloy by heating a supersaturated solid solution at a relatively low temperature to induce precipitation of a finely dispersed second phase. Also known as aging or precipitation hardening. Hardening by aging, usually after rapid cooling or cold working. 通过在相对较低的温度下加热过饱和固溶体以诱导细分散的第二相沉淀来提高合金的强度和硬度。也称为时效或沉淀硬化。通常在快速冷却或冷加工后。 |
| Energy losses (Unit kJ) | 能量损失（单位kJ） |
A commonly-used misnomer in view of the conservation-ofenergy principle, but used to mean energy converted into forms that are not used in a process, for example thermal energy from a heat engine dissipated to the surroundings, or produced by friction in a machine, or by surface drag. 从能量守恒原理来看，这是一个常用的术语错误，但可以用于表示转换为过程中未使用的形式的能量，例如，从热机散发到周围环境的热能，或由机器中的摩擦或表面阻力产生的热能。 |
| Overheating | 过热 |
Heating a metal or alloy to such a high temperature that its properties are impaired. When the original properties cannot be restored by further heat treating, by mechanical working, or by a combination of working and heat treating, the overheating is known as burning. 将金属或合金加热至其性能受损的高温。当通过进一步热处理、机械加工或加工与热处理的组合无法恢复原始性能时，过热称为燃烧。 |
| Eutectic melting | 共晶熔化 |
Melting of localized microscopic areas whose composition corresponds to that of the eutectic in the system. 局部微观区域的熔化，其成分对应于系统中的共晶成分。 |
| Specimen | 样品 |
A test object, often of standard dimensions or configuration, that is used for destructive or nondestructive testing. One or more specimens may be cut from each unit of a sample. 用于破坏性或无损检测的测试对象，通常具有标准尺寸或配置。可以从样品的每个单位切割一个或多个样品。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Gear ratio | 传动比 |
For two gears in contact, the ratio of the number of teeth on the driving gear to that on the driven gear. 对于接触的两个齿轮，主动齿轮上的齿数与从动齿轮上的齿数之比。 |
| Manometer | 压力计 |
An instrument used in the measurement of a pressure difference in a fluid (manometry). 用于测量流体压力差（测压）的仪器。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Combined heat and power plant | 热电联产电厂 |
(CHP plant, COGEN, cogeneration plant, total-energy plant) A plant for the simultaneous production of more than one useful form of energy from the same energy source, such as process heat and electric power. In the arrangement shown, partially expanded steam is extracted from the steam turbine and used to produce process heat. （CHP工厂、COGEN、热电联产工厂、总能源工厂）从同一能源（如过程热能和电力）同时生产一种以上有用能源的工厂。在所示的布置中，部分膨胀的蒸汽从蒸汽轮机中提取并用于产生过程热量。 |
| Reproducibility | 再现性 |
A term used to describe test-result variability associated with specifically defined components of variance obtained both from within a single laboratory and between laboratories. 一个术语，用于描述与从单个实验室内和实验室之间获得的具体定义的方差分量相关的测试结果可变性。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Track rod | 横拉杆 |
A bar connecting the ends of the steering arms in an automotive vehicle. 连接汽车转向臂端部的杆。 |
| DIN | DIN |
Deutsches Institut für Normung, the German Institute for Standardization. Deutsches Institut für Normung，德国标准化研究所。 |
| Bearing stress | 承受应力 |
The force per unit of bearing area. 每单位承载面积的力。 |
| Design load (Unit N) | 设计荷载（单位N） |
The greatest load that a component or structure is expected to experience under normal operating conditions. 部件或结构在正常运行条件下预期承受的最大负载。 |
| Specific weight (γ) (Unit N/m³) | 比重（γ）（单位：N/m³） |
The weight per unit volume of a substance: if W is the weight of a volume of the substance, ρ is its density, and g is the acceleration due to gravity, γ = W/ = ρg. 物质单位体积的重量：W是物质体积的重量，ρ是其密度，g是重力引起的加速度，γ=W/=ρg。 |
| Transmission dynamometer | 传动测功机 |
A dynamometer in which the power transmitted by a shaft is obtained from the product of its rotation speed and the torque determined from measured shear strains along the shaft. 一种测功机，其中轴传递的功率由其转速和扭矩的乘积获得，扭矩由沿轴测得的剪切应变确定。 |
| Microstrain | 微应变 |
The strain over a gage length comparable to interatomic distances. These are the strains being averaged by the macrostrain measurement. Microstrain is not measurable by currently existing techniques. Variance of the microstrain distribution can, however, be measured by x-ray diffraction. 与原子间距离相当的标距上的应变。这些是通过宏观应变测量得到的平均应变。现有技术无法测量微应变。然而微应变分布的变化可以通过x射线衍射来测量。 |
| Slip line | 滑移线 |
The trace of the slip plane on a viewing surface; the trace is usually observable only if the surface has been polished before deformation. The usual observation on metal crystals (under the light microscope) is of a cluster of slip lines known as a slip band. 滑动平面在观察表面上的轨迹；只有在变形前对表面进行抛光，才能观察到痕迹。通常对金属晶体的观察（在光学显微镜下）是一组称为滑移带的滑移线。 |
| Anisotropy | 各向异性 |
The characteristic of exhibiting different values of a property in different directions with respect to a fixed reference system in the material. 相对于材料中的固定参考系统，在不同方向上表现出不同属性值的特性。 |
| Actual cubic feet per minute | 实际立方英尺每分钟 |
(acfm) An obsolete (i.e. non-SI) measure of volumetric flow rate; the volume of a gas flowing per minute at actual operating pressure and temperature, as opposed to the corresponding volume flow rate at STP. （acfm）已被淘汰的（即非SI）体积流量测量；在实际工作压力和温度下每分钟流动的气体体积，与STP下的相应体积流量相反。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Mole (mol) | 摩尔（mol） |
The base unit of the amount of substance in the SI system. It was previously defined as the amount of substance of a system that contains as many elementary entities as there are atoms in 0.012 kg of carbon-12. From 20 May 2019 it has been defined as the amount of substance containing exactly 6.022 140 76 × 1023 elementary entities. SI国际单位制中物质量的基本单位。此前，它被定义为一个系统中的物质量，该系统包含的基本实体数量与0.012千克碳-12中的原子数量相同。从2019年5月20日起，它已被定义为包含6.02214076×1023个基本实体的物质量。 |
| Slant fracture | 倾斜裂缝 |
A type of fracture appearance, typical of plane-stress fractures, in which the plane of metal separation is inclined at an angle (usually about 45°) to the axis of the applied stress. 一种断裂现象，典型的平面应力断裂，其中金属分离面与施加应力的轴成一定角度（通常约45°）倾斜。 |
| Orange peel | 橘皮 |
A surface roughening in the form of a pebble-grained pattern where a metal of unusually coarse grain is stressed beyond its elastic limit. Also known as pebbles and alligator skin. 一种以卵石颗粒图案形式出现的粗糙化表面，其中晶粒异常粗的金属受到的应力超过其弹性极限。也称为卵石和鳄鱼皮。 |
| Semi-rotary pump | 半回转泵 |
A form of self-priming pump, often hand-operated, suitable for pumping water and light oils such as diesel oil and petrol. As shown in the diagram, liquid is sucked into one side of the pump through flap valves and simultaneously ejected from the other side on one stroke. The sequence is reversed on each successive stroke. 一种自吸泵，通常是手动的，适用于泵送水和轻油，如柴油和汽油。液体通过翻板阀吸入泵的一侧，同时在一个冲程中从另一侧排出。在每个连续冲程上，顺序颠倒。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Failure of the bolt | 螺栓失效 |
Term implying that the bolt has broken or the threads have stripped. There can be many reasons for this. 表示螺栓断裂或螺纹脱落的术语。原因可能有很多种。 |
| Median fatigue strength at N cycles | N次循环的中位疲劳强度 |
An estimate of the stress level at which 50% of the population would survive N cycles. The estimate is derived from a particular point of the fatigue life distribution, because there is no test procedure by which a frequency distribution of fatigue strengths at Ncycles can be directly observed. 估计50%的量在N个周期内生存的压力水平。该估计值来自疲劳寿命分布的一个特定点，因为没有试验程序可以直接观察N次循环疲劳强度的频率分布。 |
| Population | 集合 |
The hypothetical collection of all possible test specimens that could be prepared in the specified way from the material under consideration. Also known as universe. 从所考虑的材料中以规定方式制备的所有可能试样的假设集合。也称为体系。 |
| Overaging | 过时效 |
Aging under conditions of time and temperature greater than those required to obtain maximum change in a certain property, so that the property is altered in the direction of the initial value. 在时间和温度条件下的时效大于获得某一特性最大变化所需的时间和温度，从而使该特性沿初始值的方向发生变化。 |
| Batch | 一批 |
A definite quantity of some product or material produced under conditions that are considered uniform. A batch is usually smaller than a lot. 在被认为是均匀的条件下生产的一定数量的某些产品或材料。批次通常小于很多。 |
| Creep fatigue | 蠕变疲劳 |
The effects of combined creep and fatigue at high homologous temperatures in metals, and in other materials such as polymers having time-dependent behaviour. 金属和其他材料（例如具有时间相关行为的聚合物）在高同源温度下的组合蠕变和疲劳的影响。 |
| Checks | 检查 |
Numerous, very fine cracks in a coating or at the surface of a metal part. Checks may appear during processing or during service and are most often associated with thermal treatment or thermal cycling. 涂层中或金属零件表面的许多非常细微的裂纹。在加工或服务期间可能会出现检查，并且通常与热处理或热循环有关。 |
| Unit | 单位 |
A numerical indication of the magnitude of a physical quantity. The basic units of mass, length, time, etc. are relative to agreed standards. 物理量大小的数字指示。质量、长度、时间等基本单位与商定的标准相对应。 |
| Ion nitriding | 离子氮化 |
A method of surface hardening in which nitrogen ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma nitriding or glowdischarge nitriding. 一种表面硬化方法，其中氮离子通过使用高压电能在真空中扩散到工件中。与等离子体氮化或辉光放电氮化同义。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Planar anisotropy | 平面异向性 |
A variation in physical and/or mechanical properties with respect to direction within the plane of material in sheet form. 在片状材料平面内，物理和/或机械性能相对于方向的变化。 |
| Radial engine | 径向发动机 |
A piston engine in which the cylinders are arranged radially around the crankshaft, a design commonly used in early aircraft engines. 气缸沿径向围绕曲轴布置的活塞式发动机，这种设计通常用于早期飞机发动机。 |
| Acceleration-error constant | 加速度误差常数 |
When the reference (demand) input to a control system is parabolic, the output signal will also be parabolic in steady state. The signal that is constant in this situation is the acceleration and thus for a parabolic input the steady-state error, referred to as the acceleration-error constant, is the error in the acceleration. 当控制系统的参考（需求）输入是抛物线时，输出信号在稳定状态下也将是抛物线。在这种情况下恒定的信号是加速度，因此对于抛物线输入，称为加速度误差常数的稳态误差是加速度中的误差。 |
| Densimeter | 密度计 |
An instrument used to determine the density or relative density of a solid or liquid. 用于测定固体或液体的密度或相对密度的仪器。 |
| Nut | 螺母 |
A metal fastener of square, hexagon or other shape, having an internal thread which screws onto a bolt, stud or arbor. An internally-threaded fastener used with externally-threaded bolts. Usually hexagonal in shape but there is a multitude of other geometries, such as square, for special purposes and different gripping tools. 一种方形、六角形或其他形状的金属紧固件，具有内螺纹，可拧在螺栓、螺柱或心轴上。与外螺纹螺栓一起使用的内螺纹紧固件。通常为六边形，但也有许多其他几何形状，如方形，用于特殊用途和不同的夹持工具。 |
| Minor diameter | 螺纹小径 |
On a straight thread, the diameter of the imaginary cylinder which just touches the root of an external thread or the crest of an internal thread. 在直螺纹上，仅接触外螺纹根部或内螺纹顶部的假想圆柱体的直径。 |
| Fretting corrosion | 微动腐蚀 |
(1) The accelerated deterioration at the interface between contacting surfaces as the result of corrosion and slight oscillatory movement between the two surfaces. (2) A form of fretting in which chemical reaction predominates. Fretting corrosion is often characterized by the removal of particles and subsequent formation of oxides, which are often abrasive and so increase the wear. Fretting corrosion can involve other chemical reaction products, which may not be abrasive. （1）由于两个表面之间的腐蚀和轻微振荡运动，接触表面之间的界面加速劣化。（2）一种以化学反应为主的微动磨损形式。微动腐蚀通常以颗粒的去除和随后形成的氧化物为特征，这些氧化物通常具有研磨性，因此会增加磨损。微动腐蚀可能涉及其他化学反应产物，这些化学反应产物可能不是磨料。 |
| Gasket m-factor | 垫片m系数 |
For a gasketed joint of area A in which the clamping force is F, the factor m is defined by F ≥ mpA where p is the pressure that would separate the two halves of the joint and m > 1. 对于面积为A且夹紧力为F的垫片接头，系数m由F≥mpA定义，其中p是分离接头两半的压力，m>1。 |
| Cap | 帽 |
A cover, often in the form of a short cylinder, one end of which is closed. Typically used to close an orifice or pipe end, on to which it can be pushed, welded, screwed, or attached with fasteners. 一种盖子，通常为短圆柱体，一端封闭。通常用于封闭孔口或管端，可将其推入、焊接、拧紧或用紧固件连接到其上。 |
| Rockwell hardness test | 洛氏硬度测试 |
An indentation-hardness test using a calibrated machine that utilizes the depth of indentation, under constant load, as a measure of hardness. A direct-reading hardness test based on depth of indentation, in which a minor load (typically 30 to 100 N) is applied before the major load (typically 120 to 1 500 N). There are different scales using conical or spherical indenters for different ranges of hardness. An indentation hardness test based on the depth of penetration of a specified penetrator into the specimen under certain arbitrarily fixed conditions. 使用校准机器进行的压痕硬度测试，该机器利用恒定载荷下的压痕深度作为硬度测量值。一种基于压痕深度的直读硬度测试，其中在主要载荷（通常为120至1500N）之前施加较小载荷（通常是30至100N）。对于不同的硬度范围，使用锥形或球形压头有不同的刻度。在某些任意固定条件下，基于指定穿透器穿透试样深度的压痕硬度试验。 |
| Macrodeviation | 宏观偏差 |
Errors from–irregular surface departures from the design profile, often caused by lack of accuracy or stiffness of the machine system. 不规则表面偏离设计轮廓的误差，通常是由于机器系统缺乏准确性或刚度造成的。 |
| Water quenching | 水淬 |
A quench in which water is the quenching medium. The major disadvantage of water quenching is its poor efficiency at the beginning or hot stage of the quenching process. 以水为淬火介质的淬火。水淬的主要缺点是在淬火过程的开始或热阶段效率低。 |
| Check valve | 止回阀 |
(clack valve, non-return valve) A mechanical device that allows fluid flow in one direction only. The numerous designs include ball, diaphragm, disc, lift, split disc, and swing check valves. （瓣阀、止回阀）一种仅允许流体单向流动的机械装置。众多设计包括球阀、隔膜阀、盘阀、升降阀、分体盘阀和旋启式止回阀。 |
| Corrosion failure | 腐蚀失效 |
1. The failure of a component or structure after corrosion has reduced the load-bearing area to an unsupportable level. 2. A situation in which a mechanism cannot function owing to corrosion products preventing free movement at joints. 1、部件或结构在腐蚀后失效，使承重面积减少到无法支撑的程度。2.由于腐蚀产物阻止关节处的自由运动，导致机构无法运行的情况。 |
| Free joint | 万向节 |
The joint on a robot arm and wrist that causes the greatest end-effector movement when a specified force is applied to the end effector, i.e. that has the lowest stiffness with regard to the force. 机器人手臂和手腕上的关节，当指定的力施加到末端执行器时，会导致末端执行器的最大运动，即相对于力具有最低刚度。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| Temporal decomposition | 时间分解 |
The splitting of a control problem into parts with relatively short and long time constant so that different controllers may be used for the different parts. 将控制问题分解为具有相对较短和较长时间常数的部分，以便不同的部分可以使用不同的控制器。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Rotor | 转子 |
A part of a machine that rotates on a shaft (rotor shaft) about its own axis, such as the blade-carrying discs of a turbine, the blades of a helicopter, or the rotating parts of a Roots blower. 绕轴（转子轴）绕其自身轴线旋转的机器部件，如涡轮叶片、直升机叶片或罗茨鼓风机的旋转部件。 |
| Differential heating | 差动加热 |
Heating that intentionally produces a temperature gradient within an object such that, after cooling, a desired stress distribution or variation in properties is present within the object. 加热有意在物体内产生温度梯度，从而在冷却后，在物体内出现所需的应力分布或特性变化。 |
| Specific heat capacity | 比热容 |
The heat necessary to raise the temperature of 1 kg of a substance by 1 K. It is measured in J/(kg K). 将1千克物质的温度升高1K所需的热量。单位为J/（kg K）。 |
| Root diameter (Unit m) | 根部直径（单位：m） |
The diameter of the circle passing through the roots of teeth in gear teeth or screw threads. 穿过齿轮齿或螺纹中齿根的圆的直径。 |
| Stretch ratio (extension ratio, λ) | 拉伸比（拉伸比，λ） |
A measure, used for highly-extensible materials such as rubber, of the extensional or normal strain of a component subjected to tension and defined as the ratio of the final length l, for a given load, to the initial or gauge length l0, where the coordinate axes are those of principal strain. It is related to the engineering strain e by λ = 1 + e. 用于高度可延展材料（如橡胶）的一种测量方法，用于测量受拉构件的拉伸或法向应变，定义为给定载荷下的最终长度l与初始或标距长度l0之比，其中坐标轴为主应变轴。它与工程应变e的关系为λ=1+e。 |
| Punch | 冲床 |
1. A hand tool with a sharp point, used to mark the position of a hole centre in a workpiece prior to drilling. 2. A flat-ended tool with sharp edges, used to shear out a hole in a plate that is supported underneath on a die having a slightly larger same-shaped orifice. 1.一种带有尖头的手动工具，用于在钻孔前标记工件中孔中心的位置。2.一种具有锐边的平头工具，用于剪切板上的孔，该板支撑在具有稍大相同形状孔口的模具下方。 |
| Fatigue life (N) | 疲劳寿命（N） |
The number of cycles of stress or strain of a specified character that a given specimen sustains before failure occurs. 给定试样在失效发生之前所承受的特定特征的应力或应变的循环次数。 |
| Engineering strain (e) | 工程应变（e） |
A term sometimes used for average linear strain or conventional strain in order to differentiate it from true strain. In tension testing it is calculated by dividing the change in the gage length by the original gage length. 一个术语，有时用于平均线性应变或常规应变，以便将其与真实应变区分开来。在张力测试中，通过将标距变化除以原始标距来计算。 |
| Mass flow meter | 质量流量计 |
An instrument, such as a Coriolis flow meter, which measures the mass flow rate of a fluid flowing through a pipe or other duct, rather than its volume flow rate. 一种仪器，例如科里奥利流量计，一种测量流经管道或其他管道的流体的质量流率而不是其体积流率的仪器。 |
| Compressibility (Unit 1/Pa) | 可压缩性（单位1/Pa） |
A measure of the reduction in volume or increase in density when a substance is subjected to an increase of pressure. It is defined as the reciprocal of the bulk modulus. Liquids and solids are normally considered incompressible, whereas gases are highly compressible. 当物质受到压力增加时体积减少或密度增加的量度。它被定义为体积模量的倒数。液体和固体通常被认为是不可压缩的，而气体是高度可压缩的。 |
| Cementation | 胶结 |
The introduction of one or more elements into the outer portion of a metal object by means of diffusion at high temperature. 在高温下通过扩散将一种或多种元素引入金属物体的外部。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Centrifugal pump | 离心泵 |
A pump into which liquid enters axially through the eye of the casing and is then accelerated through an impeller, thereby increasing both its kinetic energy and pressure before being delivered to a ring diffuser (the volute) that further increases the liquid pressure and from which it leaves. 一种泵，液体通过泵壳的眼轴向进入，然后通过叶轮加速，从而在输送到环形扩散器（蜗壳）之前增加其动能和压力，从而进一步增加液体压力并从中流出树叶。 |
| Cotter pin | 开口销 |
(cotter) 1. A tapered wedge or pin passing through a tapered slot or hole in one member and bearing against a second member to fix it in location. 2. A split cotter is commonly called a split pin. A pin with two legs. With legs together, the pin is placed through the hole in a clevis pin. The legs are then opened outward to prevent the cotter pin from backing out of the hole. The cotter pin, in turn, prevents the load-bearing clevis pin from backing out of its retaining hole. （开口）1.锥形楔子或销钉穿过一个构件中的锥形槽或孔，并支撑在第二个构件上以将其固定到位。2.开口开口通常称为开口销。相当于有两条腿的别针，将支腿放在一起，销钉穿过U形夹销上的孔。然后将支腿向外打开以防止开口销从孔中退出。开口销反过来防止承重U形夹销从其固定孔中退出。 |
| Anneal to temper | 退火回火 |
A final partial anneal that softens a cold worked nonferrous alloy to a specified level of hardness or tensile strength. 将冷加工的有色金属合金软化到规定的硬度或抗拉强度水平的最终局部退火。 |
| Two-stage compressor | 两级压缩机 |
A machine in which gas is compressed from low pressure toan intermediate pressure in a low-pressure cylinder, and then to final pressure in a highpressure cylinder. Efficiency is improved if the two cylinders are separated by an intercooler. 一种机器，其中气体在低压气缸中从低压压缩到中压，然后在高压气缸中压缩到最终压力。如果两个气缸由中冷器分离，则效率提高。 |
| Vernier | 游标 |
A short auxiliary scale that slides along the main instrument scale to permit more accurate fractional reading of the least main division of the main scale. 一种短辅助刻度，沿主仪表刻度滑动，以便更准确地读取主刻度的最小主刻度。 |
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Rated load (Unit N) | 额定负荷（单位：N） |
The maximum load that a structure or component has been designed to carry. 结构或部件设计承受的最大荷载。 |
| Interrupted aging | 分段时效 |
Aging at two or more temperatures, by steps, and cooling to room temperature after each step. 分为两个或两个以上的温度时效，按顺序并在每个步骤后冷却至室温。 |
| Bucket | 吊桶 |
1. A cup-shaped vane with a central dividing ridge attached to the periphery of the runner of an impulse water turbine such as a Pelton turbine. 2. A rotor blade in a compressor or turbine. 1.一种杯形叶片，所述杯形叶片具有附接到冲击式水轮机（例如冲击式水轮机台）的转轮的外围的中央分隔脊。2.压缩机或涡轮机中的转子叶片。 |
| Volume (Unit m³) | 体积（单位m³） |
The amount of space occupied by a specified mass of substance or by an object. 一定质量的物质或物体占据的空间量。 |
| Transformation toughening | 相变增韧 |
The improvement of fracture toughness of a material by stress-induced transformation of the microstructure. 通过微结构的应力诱导转变来提高材料的断裂韧性。 |
| Boyle’s law | 波义耳定律 |
The product of the pressure of a gas p and its volume is constant at a given absolute temperature T. Together with Charles law, it yields the ideal gas equation p = Mrt where m is the mass of gas and R is the specific gas constant. The volume of a gas at constant temperature is inversely proportional to the pressure. This means that as pressure increases, the volume of a gas decreases. 在给定的绝对温度T下，气体的压力p与其体积的乘积是恒定的。与查尔斯定律一起，它产生了理想的气体方程p=Mrt，其中m是气体的质量，R是特定的气体常数。恒温下气体的体积与压力成反比。这意味着随着压力的增加，气体的体积会减少。 |
| Helical spring | 螺旋弹簧 |
A spring manufactured by forming elastic wire into a helix which may be cylindrical, conical, barrel-shaped, or hourglass in overall form. Closed-coiled springs are used in tension; open-coiled in both tension and compression. 一种弹簧，通过将弹性线材制成螺旋形而制成，螺旋形的整体形状可以是圆柱形、圆锥形、桶形或沙漏形。拉力采用闭合盘簧；在拉伸和压缩中都开卷。 |
| Screw jack | 螺旋千斤顶 |
A lifting device (jack) consisting of a nut and square-threaded shaft at the top of which is a load-bearing pad. Rotation of the nut raises or lowers the pad. 一种起重装置（千斤顶），由螺母和方形螺纹轴组成，其顶部为承重垫。螺母的旋转可升高或降低衬垫。 |
| Biomechanics | 生物力学 |
The application of mechanical-engineering principles, including thermodynamics, fluid mechanics, and solid mechanics together with materials engineering, to biological systems. 机械工程原理（包括热力学、流体力学和固体力学以及材料工程）在生物系统中的应用。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| T-bolt | T型螺栓 |
A threaded bolt having a square or rectangular end which fits into the T slot of a machine table for clamping workpieces. 一种带有方形或矩形端头的螺栓，可嵌入机床工作台的T形槽中，用于夹紧工件。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Slip | 滑落 |
Plastic deformation by the irreversible shear displacement (translation)of one part of a crystal relative to another in a definite crystallographic direction and usually on a specific crystallographic plane. Sometimes called glide. 晶体的一部分在一定的晶体学方向上相对于另一部分的不可逆剪切位移（平移）引起的塑性变形，通常在特定的晶体主义平面上。有时被称为滑翔。 |
| Lock-nut pipe thread | 锁紧螺母管螺纹 |
The lock-nut pipe thread is a straight thread of the largest diameter which can be cut on a pipe. Its form is identical with that of the American or Briggs standard taper pipe thread. In general, “Go” gages only are required. These consist of a straight-threaded plug representing the minimum female lock-nut thread, and a straight-threaded ring representing the maximum male lock-nut thread. This thread is used only to hold parts together, or to retain a collar on the pipe. It is never used where a tight threaded joint is required. 锁紧螺母管螺纹是最大直径的直螺纹，可在管道上切割。其形式与美国或布里格斯标准锥管螺纹相同。一般情况下，只需要通规。它们由一个表示最小内螺纹锁紧螺母螺纹的直螺纹塞和一个表示最大外螺纹锁紧螺帽螺纹的直形螺纹环组成。该螺纹仅用于将零件固定在一起，或用于将轴环固定在管道上。切勿使用于需要紧密螺纹接头的情况下。 |
| Plastic deformation | 塑性变形 |
The permanent (inelastic) distortion of a material under applied stress that strains the material beyond its elastic limit. 材料在施加应力下的永久（非弹性）变形，使材料应变超过其弹性极限。 |
| Observed value | 观测值 |
The particular value of a characteristic determined as a result of a test or measurement. 作为测试或测量结果确定的特性的特定值。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Compressive strength | 抗压强度 |
Maximum compressive stress a material is capable of developing. With a brittle material that fails in compression by fracturing, the compressive strength has a definite value. For ductile, malleable, or semiviscous materials (which do not fail in compression by a shattering fracture), the value obtained for compressive strength is an arbitrary value dependent on the degree of distortion that is regarded as effective failure of the material. 材料能够产生的最大压缩应力。如果脆性材料因破裂而无法压缩，则抗压强度具有一定值。对于韧性、可锻性或半粘性材料（不会因破裂而导致压缩失效），获得的抗压强度值是一个任意值，取决于被视为材料有效失效的变形程度。 |
| Activation energy | 活化能 |
(Ea, U) (Unit kJ/mol) The minimum energy for a chemical reaction to occur or for processes such as diffusion to take place in crystals. （Ea, U）（单位kJ/mol）发生化学反应或在晶体中发生扩散等过程的最小能量。 |
| Blade compressor | 叶片式压缩机 |
An oil-free, double-acting rotary compressor in which an angled blade attached to the inner surface of a rotating housing passes through a slot in a disk rotating about an axis perpendicular to that of the housing but offset from it. Air enters through apertures in the housing and leaves through a port in the housing. 一种无油双作用旋转式压缩机，其中连接到旋转外壳内表面的倾斜叶片穿过圆盘上的槽，该槽绕垂直于外壳的轴旋转，但偏离外壳。空气通过壳体中的孔进入，并通过壳体的端口离开。 |
| Crushing strain | 压应变 |
The supposed single strain that results in comminution of a brittle material. The corresponding stress is termed the crushing strength. Neither quantity can be a material constant as they must obey the laws of fracture mechanics and will depend on the type of testpiece, method of loading etc. 导致脆性材料粉碎的假定单应变。相应的应力称为抗压强度。这两个量都不能是材料常数，因为它们必须遵守断裂力学定律，并取决于试件类型、加载方法等。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Surface roughness (roughness) | 表面粗糙度 |
The small-scale, irregular peaks and troughs in a solid surface which are quantified using a surface analyser. Roughness may be a consequence of wear and corrosion, or of the manufacturing process. It leads to increased friction in solid– solid contact or fluid flow over a surface. Errors of form and waviness are excluded, but surface texture includes roughness and waviness. Surface topography incorporates the small-scale, three-dimensional geometry of a surface including surface roughness, machined, and etched features, typically at sub-mm scales. 固体表面中的小尺度不规则峰谷，使用表面分析仪进行量化。粗糙度可能是磨损和腐蚀或制造过程的结果。它会导致表面上的固-固接触或流体流动中的摩擦增加。不包括形状和波纹度误差，但表面纹理包括粗糙度和波纹度。表面形貌包括表面的小尺度三维几何结构，包括表面粗糙度、机加工和蚀刻特征，通常为亚毫米尺度。 |
| Shear strain | 剪切应变 |
The tangent of the angular change, as a response to force, between two lines originally perpendicular to each other through a point in a body. Also known as shearing strain. 角变化的切线，作为对力的响应，在两条原本通过物体中的一个点相互垂直的线之间。也称为剪切应变。 |
| Cheese head | 圆柱头 |
A cylindrical head on a screw or bolt. For driving, it may be slotted, or hexagonally recessed. 螺钉或螺栓上的圆柱头。为了驱动，它可以是开槽的，也可以是六角形的。 |
| Case hardening | 表面硬化 |
A generic term covering several processes applicable to steel that change the chemical composition of the surface layer by absorption of carbon, nitrogen, or a mixture of the two and, by diffusion, create a concentration gradient. The processes commonly used are carburizing and quench hardening; cyaniding; nitriding; and carbonitriding. The use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于钢的几种工艺，这些工艺通过吸收碳、氮或二者的混合物改变表层的化学成分，并通过扩散形成浓度梯度。常用的工艺有渗碳和淬火硬化，氰化，氮化以及碳氮共渗。优选使用适用的特定工艺名称。 |
| Steel-wire rope | 钢丝绳 |
A rope or cable made up of many steel strands wrapped helically about an axis, each strand being made of metal wires twisted together like a helix. 一种绳索或缆绳，由许多绕轴螺旋缠绕的钢绞线组成，每根钢绞线由金属丝缠绕在一起形成螺旋。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Rotary blower | 旋转鼓风机 |
(rotary compressor) A positive-displacement gas compressor which may be of the blade type, helical-screw type, meshing-lobe type (the Roots blower), or sliding-vane type. （旋转式压缩机）一种容积式气体压缩机，可以是叶片式、螺旋式、啮合凸角式（罗茨鼓风机）或滑动叶片式。 |
| Nanoparticles | 纳米颗粒 |
Particles with dimensions of order 1 nm which have either been introduced into microstructures for reinforcement or are present as impurities. 尺寸为1nm级的颗粒，其已被引入微结构中用于增强或作为杂质存在。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Time quenching | 时间淬火 |
A term used to describe a quench in which the cooling rate of the part being quenched must be changed abruptly at some time during the cooling cycle. 用于描述淬火的术语，其中被淬火零件的冷却速率必须在冷却循环的某个时间突然改变。 |
| Design stress (Unit Pa) | 设计应力（单位Pa） |
The greatest allowable stress in a component or structure that will not result in failure under normal operating conditions. 在正常操作条件下不会导致失效的部件或结构中的最大许用应力。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Stator | 定子 |
A ring of non-rotating blades or nozzles in a compressor, turbine, or other turbomachine, which directs fluid flow into an adjacent rotor. 涡轮压缩机、涡轮或其他涡轮机械中的一圈不旋转的叶片或喷嘴，将流体引导到相邻的转子中。 |
| Lüders lines | 吕德斯线 |
Elongated surface markings or depressions, often visible with the unaided eye, that form along the length of sheet metal or a tension specimen at an angle of approximately 45° to the loading axis. Caused by localized plastic deformation, they result from discontinuous (inhomogeneous) yielding. Also known as Lüders bands, Hartmann lines, Piobert lines, or stretcher strains. 拉长的表面标记或凹陷，通常肉眼可见，沿金属板或拉伸试样的长度形成，与加载轴的角度约为45°。由于局部塑性变形，它们是不连续（不均匀）屈服的结果。也被称为吕德斯带、哈特曼线、皮奥伯特线或拉伸线。 |
| Twist | 扭转 |
The helix produced in a cylindrical component, such as a shaft, wire, tensioned cable, or rope, when one end is rotated relative to the other. Measured either as the number of turns per unit length, or by the helix angle (twist angle). 当一端相对于另一端旋转时，在圆柱形部件（如轴、钢丝、张紧电缆或绳索）中产生的螺旋。以每单位长度的圈数或螺旋角（扭曲角）测量。 |
| Absorptance | 吸收率 |
(absorptivity, absorption coefficient, α) The fraction of radiant flux incident on a surface that is absorbed by the surface. The term also applies to absorption of radiation by a volume of fluid. For a semi-transparent surface, α + ρ + τ = 1, where ρ is the reflectance and τ is the transmittance. （吸收率，吸收系数，α）入射到表面的辐射通量被表面吸收的部分。该术语也适用于一定体积的流体对辐射的吸收。对于半透明表面，α+ρ+τ=1，其中ρ是反射率，τ是透射率。 |
| Secant modulus | 割线模量 |
The slope of the secant drawn from the origin to any specified point on a stress-strain curve. Compare with chord modulus. 从原点到应力应变曲线上任何指定点的割线斜率。与弦模量进行比较。 |
| Absorber | 吸收器 |
1. An auxiliary vibratory system that favourably modifies the vibration characteristics of a main system. 2. Part of an absorption refrigeration system in which the refrigerant is absorbed by a transport medium. 3. The absorber plate is the receiver of a concentrating solar collector where the radiation is absorbed. 1.一种辅助振动系统，可有利地改变主系统的振动特性。2.吸收式制冷系统的一部分，其中制冷剂被传输介质吸收。3.吸收板是吸收辐射的聚光太阳能集热器的接收器。 |
| Scratching | 刮擦 |
In tribology, the mechanical removal or displacement, or both, of material from a surface by the action of abrasive particles or protuberances sliding across the surfaces. 在摩擦学中，通过在表面上滑动的磨粒或突起的作用，材料从表面上的机械移除或移位，或两者兼而有之。 |
| Scale height (Unit m) | 刻度高度（单位：m） |
The altitude H at which the atmospheric pressure has decreased to a certain fraction of its value at sea level B. It depends on the model adopted for the atmosphere: for an isothermal atmosphere, the pressure decreases exponentially with altitude. If H is taken as the altitude at which the pressure has fallen to B/e, then H = RT/g where R is the gas constant for air, T is the absolute temperature T, and g is the acceleration due to gravity. 大气压力降低到其在海平面B处数值的某一部分的高度H。它取决于大气采用的模型：对于等温大气，压力随高度呈指数下降。如果取H作为压力下降到B/e的高度，则H=RT/g，其中R是空气的气体常数，T是绝对温度T，g是重力引起的加速度。 |
| Finish annealing | 精制退火 |
A subcritical annealing treatment applied to cold-worked low- or medium-carbon steel. Finish annealing, which is a compromise treatment, lowers residual stresses, thereby minimizing the risk of distortion in machining while retaining most of the benefits to machinability contributed by cold working. Compare with final annealing. 适用于冷加工低碳钢或中碳钢的亚临界退火处理。与最终退火相比，精加工退火是一种折衷处理，可降低残余应力，从而最大限度地降低加工中的变形风险，同时保留冷加工对可加工性的大部分好处。 |
| Coalescence | 聚结 |
Growth of grains at the expense of the remainder by absorption or the growth of a phase or particle at the expense of the remainder by absorption or reprecipitation. 通过吸收以牺牲剩余为代价的晶粒的生长或以通过吸收或再沉淀为代价的以剩余为代价的相或颗粒的生长。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Ultrasonic extensometer | 超声波伸长计 |
An electronic instrument which measures the change in length of a fastener ultrasonically as, or before and after, the fastener is tightened. 一种电子仪器，可在紧固件拧紧时或前后通过超声波测量紧固件长度的变化。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Surface hardening | 表面硬化 |
A generic term covering several processes applicable to a suitable ferrous alloy that produces, by quench hardening only, a surface layer that is harder or more wear resistant than the core. There is no significant alteration of the chemical composition of the surface layer. The processes commonly used are carbonitriding, carburizing, induction hardening, flame hardening, nitriding, and nitrocarburizing. Use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于仅通过淬火硬化产生比型芯更硬或更耐磨的表面层的合适铁合金的几种工艺。表面层的化学成分没有显著改变。常用的工艺有碳氮共渗、渗碳、感应淬火、火焰淬火、氮化和氮碳共渗。最好使用适用的特定工艺名称。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Solenoid | 螺线管 |
A coil of electrically-conducting wire wrapped around a metal core, typically iron, to produce a magnetic field and hence a force on the core when an electric current passes through the coil. Solenoids are widely used to produce linear movement to actuate valves (solenoid valves) and other devices. 绕在金属芯（通常为铁）上的导线线圈，当电流通过线圈时产生磁场，从而在芯上产生力。电磁阀广泛用于产生线性运动以驱动阀（电磁阀）和其他装置。 |
| Flange bolt | 法兰螺栓 |
A bolt with a built in washer-like flange just below the head. 在头部下方带有内置垫圈状法兰的螺栓。 |
| Stabilizing treatment | 稳定化处理 |
(1) Before finishing to final dimensions, repeatedly heating a ferrous or nonferrous part to or slightly above its normal operating temperature and then cooling to room temperature to ensure dimensional stability in service. (2) Transforming retained austenite in quenched hardenable steels, usually by cold treatment. (3) Heating a solution-treated stabilized grade of austenitic stainless steel to 870 to 900 °C (1600 to 1650 °F) to precipitate all carbon as TiC, NbC, or TaC so that sensitization is avoided on subsequent exposure to elevated temperature. （1）在精加工至最终尺寸之前，反复加热含铁或非铁零件至或略高于其正常工作温度，然后冷却至室温，以确保使用中的尺寸稳定性。（2）在淬火可淬硬钢中转变残余奥氏体，通常通过冷处理。（3）将固溶处理的稳定等级奥氏体不锈钢加热至870至900°C（1600至1650°F），使所有碳沉淀为TiC、NbC或TaC，从而避免在随后暴露于高温时敏化。 |
| Cold die quenching | 冷模淬火 |
A quench utilizing cold, flat, or shaped dies to extract heat from a part. Cold die quenching is slow, expensive, and is limited to smaller parts with large surface areas. 利用冷、平或成型模具从零件中提取热量的淬火。冷模淬火速度慢、成本高，并且仅限于表面积较大的较小零件。 |
| Temper | 回火 |
(1) In heat treatment, reheating hardened steel or hardened cast iron to some temperature below the eutectoid temperature for the purpose of decreasing hardness and increasing toughness. The process also is sometimes applied to normalized steel. (2) In tool steels, temper is sometimes used, but inadvisedly, to denote the carbon content. (3) In nonferrous alloys and in some ferrous alloys (steels that cannot be hardened by heat treatment), the hardness and strength produced by mechanical or thermal treatment, or both, and characterized by a certain structure, mechanical properties, or reduction in area during cold working. （1）在热处理中，将硬化钢或硬化铸铁重新加热到共析温度以下的温度，以降低硬度和增加韧性。该工艺有时也适用于正火钢。（2）在工具钢中，有时使用回火来表示碳含量，但这是不恰当的。（3）在非铁合金和一些铁合金（不能通过热处理硬化的钢）中，通过机械或热处理或两者产生的硬度和强度，其特征是在冷加工过程中具有一定的结构、机械性能或面积减小。 |
| Bainitic hardening | 贝氏体硬化 |
Quench-hardening treatment resulting principally in the formation of bainite. 淬火硬化处理主要导致贝氏体的形成。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Blind rivet | 盲孔铆钉 |
A rivet that enables a connexion to be made from one side only of an assembly. 一种铆钉，可以仅从组件的一侧进行连接。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Fracture surface | 断裂面 |
The irregular surface produced when a piece of metal is broken. 一块金属破碎时产生的不规则表面。 |
| Two-phase flow | 两相流 |
A flow in which two phases are present, for example gas bubbles in a liquid, liquid bubbles in another liquid with which it is immiscible, solid particles in a liquid or gas. 两相流动，例如液体中的气泡、与之不混溶的另一种液体中的液体气泡、液体或气体中的固体颗粒。 |
| Forging cracks | 锻造裂纹 |
This may occur during fastener manufacturing at the cutting or forging operations and are located on the top of the head or on the raised periphery of indented head bolts. 这可能发生在紧固件制造过程中的切削或锻造操作中，并且位于头部的顶部或带锯齿的头部螺栓的凸起周边上。 |
| X-ray thickness gauge | X射线厚度计 |
A device comprising an X-ray source and a detector used to determine the thickness of material in sheet or plate form, including metals, paper, plastics, rubber, and ceramics. 一种由X射线源和探测器组成的装置，用于测定片状或平板状材料的厚度，包括金属、纸张、塑料、橡胶和陶瓷。 |
| Scoring | 划痕 |
In tribology, a severe form of wear characterized by the formation of extensive grooves and scratches in the direction of sliding. 在摩擦学中，一种严重的磨损形式，其特征是在滑动方向上形成大面积的凹槽和划痕。 |
| Weight (W) (Unit N) | 重量（W）（单位：N） |
The force of attraction on a body due to gravity. A body’s weight is the product of its mass and the gravitational field strength at that point. Mass remains constant, but weight depends on the object’s position on the Earth’s surface, decreasing with increasing altitude. If g is the acceleration due to gravity, the weight of a mass m is given by W = mg. On Earth, the acceleration due to gravity is approximately 9.81 m/s², so that the weight of a 1 kg mass is 9.81 N. More generally, the weight is the force exerted on the mass of a body when in the gravitational field of another body. 重力由于重力作用在物体上的吸引力。物体的重量是其质量和该点引力场强度的乘积。质量保持不变，但重量取决于物体在地球表面的位置，随着海拔的升高而减小。如果g是重力引起的加速度，则质量m的重量由W=mg给出。在地球上，重力引起的加速度约为9.81m/s²，因此1千克质量的重量为9.81N。更一般地说，重量是在另一个物体的重力场中施加在物体质量上的力。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Bolt length | 螺栓长度 |
The bolt length shall be the distance measured parallel to the axis of the product from the bearing surface of the head to the extreme end of the bolt including point. 螺栓长度应为平行于产品轴线测量的从头部的支承面到包括点在内的螺栓末端的距离。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Ideal critical diameter | 理想临界直径 |
(DI). Under an ideal quench condition, the bar diameter that has 50% martensite at the center of the bar when the surface is cooled at an infinitely rapid rate (that is, when H = ∞, where H is the quench severity factor). （DI）在理想淬火条件下，当表面以无限快的速度冷却时（即H=∞, 其中H是淬火严重度因子）。 |
| Mode of failure | 故障模式 |
The various ways in which a material can fail when subjected to loading, surface damage, chemical attack, heating, cooling, or radiation, in either isolation or combination. The failure modes include fracture, fatigue, creep, corrosion, erosion, and embrittlement. 材料在受到载荷、表面损伤、化学侵蚀、加热、冷却或辐射时，可能发生失效的各种方式，无论是单独还是组合。失效模式包括断裂、疲劳、蠕变、腐蚀、侵蚀和脆化。 |
| Slip joint | 滑动接头 |
A mechanical connection which allows limited endwise relative movement of two components such as pipes, rods, and ducts. 一种机械连接，允许两个部件（如管道、杆和管道）进行有限的轴向相对运动。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Coil spring | 螺旋弹簧 |
A spiral (‘clockwork’) or helical (cylindrical) spring. A spring steel wire wound in a spiral pattern. 螺旋（“发条”）或螺旋（圆柱形）弹簧。以螺旋状缠绕的弹簧钢丝。 |
| Ablation cooling | 烧蚀冷却 |
The cooling of a surface exposed to very high external gas temperature which causes the surface material to sublime, melt or decompose. The chemical process absorbs heat while the mass flow of material away from the surface blocks the heat flux from the hot gas. 冷却暴露于非常高的外部气体温度的表面，导致表面材料升华、熔化或分解。化学过程吸收热量，而远离表面的物质的质量流阻挡了来自热气体的热通量。 |
| Tempered martensite embrittlement | 回火马氏体脆化 |
Embrittlement of ultrahigh-strength steels caused by tempering in the temperature range of 205 to 400 °C (400 to 750 °F); also called 350 °C or 500 °F embrittlement. Tempered martensite embrittlement is thought to result from the combined effects of cementite precipitation on prioraustenite grain boundaries or interlath boundaries and the segregation of impurities at prioraustenite grain boundaries. 超高强度钢在205至400°C（400至750°F）温度范围内回火引起的脆化；也称为350°C或500°F脆化。回火马氏体脆化被认为是由于渗碳体沉淀在原奥氏体晶界或层间晶界上以及杂质在原奥氏体晶粒边界处偏析的综合影响。 |
| Turbocharging | 涡轮增压 |
A method of supercharging in which the hot exhaust gas from a piston engine is used to drive a turbine which powers the supercharging compressor. A turbocharger is the turbine/compressor combination. The compressor is usually of radial outflow design while radial, axial, and mixed-flow turbines are all in use. The wastegate is a valve that reduces the flow of exhaust gas into the turbine to limit the boost produced or overspeeding. Not shown in the diagram are bearings, oil passages, etc. 一种增压方法，其中活塞发动机的热废气用于驱动涡轮，涡轮为增压压缩机提供动力。涡轮增压器是涡轮/压缩机组合。压缩机通常为径向流出设计，而径向、轴向和混流式涡轮机都在使用。废气旁通阀是一种减少进入涡轮的废气流量以限制产生的增压或超速的阀。 |
| Fracture mechanisms | 断裂机制 |
The microstructural mechanisms that cause fracture, such as void initiation, growth and coalescence, cleavage. 导致断裂的微观结构机制，如空隙的萌生、生长和聚结、解理。 |
| Inch-pound force/inch² | 英寸磅力/英寸² |
A non-SI unit for the specific work of fracture (fracture toughness). The conversion to SI is 1 in.lbf/in² = 1.751 268 × 102 J/m². 用于特定断裂功（断裂韧性）的非国际单位制单位。到SI的转换为1英寸。lbf/in²=1.751268×102J/m²。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Applied thermodynamics | 应用热力学 |
(engineering thermodynamics, thermodynamics) The science of the relationship between heat, work and the properties of systems and the ways in which heat energy from fuels can be converted into mechanical work. It involves the study of all aspects of energy use and energy transformation, including power generation, refrigeration, the relevant properties of the substances involved and the relationships between them. The principle of conservation of energy is a fundamental law of nature. （工程热力学、热力学）热、功和系统特性之间关系的科学，以及燃料中的热能可以转化为机械功的方式。它涉及能源使用和能源转换的各个方面的研究，包括发电、制冷、所涉及物质的相关特性以及它们之间的关系。能量守恒定律是自然的基本规律。 |
| Oxidized surface (on steel) | 氧化表面（在钢上） |
Surface having a thin, tightly adhering, oxidized skin (from straw to blue in color), extending in from the edge of a coil or sheet. Sometimes called annealing border. 表面具有薄的、紧密粘附的氧化皮（从稻草色到蓝色），从线圈或薄片的边缘延伸。有时称为退火边界。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Vibrograph | 示振器 |
An instrument that records vibrations in a system over time. 记录系统随时间变化的振动的仪器。 |
| Torsion spring | 扭簧 |
1. A spring in the form of a torsion bar. 2. A helical spring to which torque can be applied at the ends. 1.一种扭杆形式的弹簧。2.一种螺旋弹簧，其端部可施加扭矩。 |
| Gamma iron | 加马铁 |
The face-centered cubic form of pure iron, stable from 910 to 1400 °C (1670 to 2550 °F). 纯铁的面心立方形式，在910至1400°C（1670 2550°F）温度范围内稳定。 |
| Wallner lines | Wallner线 |
A distinct pattern of intersecting sets of parallel lines, usually producing a set of V-shaped lines, sometimes observed when viewing brittle fracture surfaces at high magnification in an electron microscope. Wallner lines are attributed to interaction between a shock wave and a brittle crack front propagating at high velocity. Sometimes Wallner lines are misinterpreted as fatigue striations. 一组相交的平行线的独特图案，通常产生一组V形线，有时在电子显微镜下高倍观察脆性断裂表面时观察到。Wallner线归因于高速传播的冲击波和脆性裂纹前沿之间的相互作用。有时Wallner线被误解为疲劳条纹。 |
| Vapour–pressure curve | 蒸汽压力曲线 |
For a pure substance, the curve of saturation pressure plotted vs saturation temperature. 对于纯物质，绘制了饱和压力与饱和温度的曲线。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Metallurgy | 冶金 |
The study of the atomic, crystallographic, microstructural, mechanical, and physical properties of metallic elements and alloys and their applications. 研究金属元素和合金的原子、晶体学、微观结构、机械和物理特性及其应用。 |
| Radial wave equation | 径向波动方程 |
A differential equation describing the transmission of a wave in a system with radial symmetry. 描述波在径向对称系统中传输的微分方程。 |
| Combustible | 易燃 |
(inflammable) A term for substances that can be ignited and burned. （易燃）可点燃和燃烧的物质的术语。 |
| Total elongation | 总伸长率 |
A total amount of permanent extension of a test piece broken in a tensile test. 拉伸试验中断裂试样的永久延伸总量。 |
| Profile | 轮廓 |
The shape of a cross section of an object, such as an aerofoil or cam. 物体的横截面形状，如机翼或凸轮。 |
| Breaking load (Unit N) | 断裂负荷（单位N） |
The load applied at some point to a component or structure which leads to fracture. The breaking stress (breaking strength) is the average stress at which a member breaks, given by the breaking load divided by the area over which it acts. 在某个点施加到导致断裂的部件或结构的载荷。断裂应力（断裂强度）是构件断裂时的平均应力，由断裂载荷除以其作用的面积给出。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Stress equalizing | 应力均衡 |
A low-temperature heat treatment used to balance stresses in cold-worked material without an appreciable decrease in the mechanical strength produced by cold working. 一种低温热处理，用于平衡冷加工材料中的应力，而不会明显降低冷加工产生的机械强度。 |
| Safe working load (Unit N) | 安全工作负荷（单位：N） |
The steady or unsteady load against which a component or structure is designed for normal operation. It is lower than that which would cause failure by buckling, fracture, or yielding, so as to accommodate uncertainty, possible fault or accident conditions. 部件或结构设计用于正常运行的稳定或不稳定荷载。该值低于因屈曲、断裂或屈服而导致失效的值，以适应不确定性、可能的故障或事故条件。 |
| Creep–time relations | 蠕变时间关系 |
Algebraic or numerical relations between creep strain and time at constant stress. 恒定应力下蠕变应变与时间之间的代数或数值关系。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Cathode | 阴极 |
That electrode in a battery or corrosion cell which attracts electrons. 电池或腐蚀电池中吸引电子的电极。 |
| Supercooling | 过冷 |
Cooling below the temperature at which an equilibrium phase transformation can take place, without actually obtaining the transformation. 在没有实际获得相变的情况下，冷却到可以发生平衡相变的温度以下。 |
| Torque control | 扭矩控制 |
A system of optimizing rotor speed for a variable-speed wind turbine by controlling the torque demands of the generator. 通过控制发电机的扭矩需求来优化变速风力涡轮机的转子速度的系统。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Accelerated testing | 加速测试 |
A type of testing, for rates of wear, fatigue, corrosion etc., in which failure times are reduced by employing greater loads, more frequent power cycling, higher vibration levels, higher humidity, higher temperatures, greater potential differences etc. than would be encountered in normal operation. 一种测试类型，用于测试磨损率、疲劳率、腐蚀率等，通过采用比正常运行中更大的负载、更频繁的功率循环、更高的振动水平、更高湿度、更高温度、更大的电位差等，减少故障时间。 |
| Torsional stress | 扭转应力 |
The shear stress on a transverse cross section resulting from a twisting action. 扭转作用在横截面上产生的剪切应力。 |
| Centi (c) | 厘（c） |
An SI unit prefix indicating a multiplier of 0.01; thus centimetre is a unit of length equal to one one-hundredth of a metre or 10 mm. 表示乘数0.01的SI单位前缀；因此厘米是长度单位，等于一米的百分之一或10毫米。 |
| Right hand thread | 右旋螺纹 |
A screw thread which advances into the mating part when turned clockwise or to the right. 顺时针或向右转动时进入配合部件的螺纹。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Pressure difference (Unit Pa) | 压差（单位Pa） |
(pressure differential, Δp) The difference between two pressures, one of which may be a reference pressure such as barometric pressure. In many flow processes, the pressure difference is more important than the absolute pressure level. （压差，Δp）两个压力之间的差值，其中一个压力可以是参考压力，如大气压力。在许多流动过程中，压差比绝对压力水平更重要。 |
| Curie temperature | 居里温度 |
The temperature of magnetic transformation below which a metal or alloy is ferromagnetic and above which it is paramagnetic. 磁性转变温度，低于此温度金属或合金为铁磁性，高于此温度则为顺磁性。 |
| Fillister head | 槽头 |
Similar to a pan head but with a smaller head diameter and a taller head, with higher vertical sides. 类似于盘头，但头部直径较小，头部较高，垂直边较高。 |
| Vacuum relief valve | 真空安全阀 |
A valve that admits gas to a system under vacuum, should the degree of vacuum become excessive. 如果真空度过高，允许气体在真空下进入系统的阀门。 |
| Annealing carbon | 退火碳 |
Fine, apparently amorphous carbon particles formed in white cast iron and certain steels during prolonged annealing. Also called temper carbon. 白口铸铁和某些钢在长时间退火过程中形成的细小、明显的无定形碳颗粒。也称为回火碳。 |
| Compounding | 复合串联 |
In a steam engine (compound steam engine) or impulse turbine, the progressive reduction in pressure (expansion) across two or more stages in series. 在蒸汽机（复合蒸汽机）或脉冲涡轮机中，通过串联的两个或多个级逐渐降低压力（膨胀）。 |
| Fatigue notch factor (Kf) | 疲劳缺口系数（Kf） |
The ratio of the fatigue strength of an unnotched specimen to the fatigue strength of a notched specimen of the same material and condition; both strengths are determined at the same number of stress cycles. 无缺口试样的疲劳强度与相同材料和条件的有缺口试样的疲劳强度之比；两种强度都是在相同数量的应力循环下确定的。 |
| Brayton cycle | 布雷顿循环 |
(Joule cycle) An air standard cycle that is the ideal cycle for a gasturbine engine. As shown on the diagram of pressure (p) ʋs specific volume (ʋ), it consists of four internally reversible processes: isentropic compression in a compressor (1–2), isobaric heat addition in a combustor (2–3), isentropic expansion in a turbine (3–4) and isobaric heat rejection. The cycle can be extended to include regeneration, reheating, and intercooling. （焦耳循环）一种空气标准循环，是燃气轮机发动机的理想循环。循环可以扩展到包括再生、再热和中冷。 |
| Stress-relaxation curve | 应力松弛曲线 |
A plot of the remaining, or relaxed, stress in a stress-relaxation test as a function of time. The relaxed stress equals the initial stress minus the remaining stress. Also known as a stress-time curve. 应力松弛试验中剩余应力或松弛应力随时间变化的曲线图。松弛应力等于初始应力减去剩余应力。也称为应力-时间曲线。 |
| Degradation of energy | 能源退化 |
Conversion of energy into forms of lower usefulness due to irreversibilities in energy transfer and conversion processes. The increase in entropy can be regarded as a measure of the degradation of energy. 由于能量转移和转换过程中的不可逆性，将能量转换为低效形式。熵的增加可以看作是能量退化的量度。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Process annealing | 中间退火 |
An imprecise term denoting various treatments used to improve workability. For the term to be meaningful, the condition of the material and the time-temperature cycle used must be stated. 一个不精确的术语，表示用于改善可加工性的各种处理方法。为了使术语有意义，必须说明材料的条件和使用的时间-温度循环。 |
| Dead load (Unit N) | 静载（单位N） |
A load on a component or structure that is steady with time, e.g. the self-weight of a bridge. 部件或结构上随时间稳定的载荷，例如桥梁的自重。 |
| Precipitation heat treatment | 沉淀热处理 |
Artificial aging in which a constituent precipitates from a supersaturated solid solution. 成分从过饱和固溶体沉淀的人工时效。 |
| Biomedical engineering | 生物医学工程 |
The application of engineering principles and methodology to the medical field. Examples involving mechanical engineering include the design and construction of artificial limbs and hearts, heart-lung machines, prosthetic eyes, and orthopaedic implants such as hip joints and pins to stabilize fractured bones. 工程原理和方法在医学领域的应用。涉及机械工程的例子包括假肢和心脏、心肺机、假眼和骨科植入物（如髋关节和用于稳定骨折骨骼的销钉）的设计和建造。 |
| Washer | 垫圈 |
An annular disc of metal, rubber, plastic, ceramic, etc., placed between two surfaces in contact either to spread the load (for example, between a surface and a tightened nut or a bolt head), to provide a seal, or to separate or align components. 由金属、橡胶、塑料、陶瓷等制成的环形圆盘，放置在两个接触面之间，以分散载荷（例如，在一个表面和拧紧的螺母或螺栓头之间），提供密封，或分离或对齐部件。 |
| Sound pressure (Unit μPa) | 声压（单位：μPa） |
The instantaneous deviation of pressure from the ambient pressure caused by the passage of a sound wave, which can be measured by a microphone in air and a hydrophone in water. 声波传播引起的压力与环境压力的瞬时偏差，可通过空气中的麦克风和水中的水听器测量。 |
| Liquid carburizing | 液体渗碳 |
Surface hardening of steel by immersion into a molten bath consisting of cyanides and other salts. 通过浸入由氰化物和其他盐组成的熔池中对钢进行表面硬化。 |
| Rotary piston flow meter | 旋转活塞流量计 |
A rotary liquid flow meter in which a cylindrical rotor, eccentrically mounted within a cylindrical casing, the axes of the two cylinders being parallel, is caused to rotate by the liquid flow. The flow rate is determined from the number of rotations of the rotor in a given time. 一种旋转式液体流量计，其中偏心安装在圆柱形外壳内的圆柱形转子，两个圆柱体的轴线平行，由液体流引起旋转。流量由转子在给定时间内的转数确定。 |
| Strain-hardening exponent (n value) | 应变硬化指数（n值） |
The value n in the relationship σ = Kεn, where σ is the true stress, ε is the true strain, and K, the strength coefficient, is equal to the true stress at a true strain of 1.0. The strain hardening exponent is equal to the slope of the true stress/true strain curve up to maximum load, when plotted on log-log coordinates. The n-value relates to the ability of a sheet of material to be stretched in metalworking operations. The higher the n-value, the better the formability(stretchability). Also known as the strain-hardening coefficient. 关系式σ=Kεn中的值n，其中σ是真应力，ε是真应变，K是强度系数，等于真应变为1.0时的真应力。在对数坐标上绘制时，应变硬化指数等于真应力/真应变曲线的斜率，直到最大载荷。n值与一片材料在金属加工操作中拉伸的能力有关。n值越高，成形性（拉伸性）越好。也称为应变硬化系数。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Laser sintering | 激光烧结 |
A manufacturing technique by which parts are built layer by layer (each typically 20 μm thick) from plastic or metal (Direct Metal Laser Sintering, DMLS) material in powder form, each layer being sintered by a scanning laser. 一种制造技术，通过这种制造技术，零件由粉末形式的塑料或金属（直接金属激光烧结，DMLS）材料逐层（每个厚度通常为 20 微米）构建，每一层都由扫描激光烧结。 |
| Compound pendulum | 复摆 |
A rigid body free to swing about an axis. 可绕轴自由摆动的刚体。 |
| Fracture toughness | 断裂韧性 |
A generic term for measures of resistance to extension of a crack. The term is sometimes restricted to results of fracture mechanics tests, which are directly applicable in fracture control. However, the term commonly includes results from simple tests of notched or precracked specimens not based on fracture mechanics analysis. Results from tests of the latter type are often useful for fracture control, based on either service experience or empirical correlations with fracture mechanics tests. 裂纹扩展阻力测量的通用术语。该术语有时仅限于断裂力学试验的结果，这些结果直接适用于断裂控制。该术语通常包括非基于断裂力学分析的切口或预裂纹试样的简单试验结果。基于使用经验或与断裂力学试验的经验相关性，后一类试验的结果通常有助于断裂控制。 |
| Secondary hardening | 二次硬化 |
The process whereby some low-alloy steels, quenched to produce martensite, produce fine precipitates when tempered above 550°C, which inhibit dislocation motion and reverse the trend towards lower strength at higher tempering temperatures. 某些低合金钢经淬火产生马氏体，在550°C以上回火时产生细小沉淀的过程，这抑制了位错运动，扭转了在较高回火温度下强度降低的趋势。 |
| Tap | 旋塞 |
1. A threaded hard metal plug for cutting screw threads in holes. It has longitudinal grooves for the clearance of chips while cutting. Progressive cutting is achieved by using three taps in succession: taper, second, and plug. First and second taps have tapers to help start the thread along the axis of the hole; the plug tap has no taper and is used on the final cut in a blind hole. 2. A valve in, or at the end of, a pipeline. 1.一种用于在孔中切割螺纹的螺纹硬金属塞。它具有纵向凹槽，用于在切割时清除切屑。渐进式切割通过连续使用三个丝锥实现：锥度、二次和塞。第一和第二丝锥具有锥度，以帮助沿孔的轴线开始螺纹；塞式丝锥没有锥度，用于盲孔的最终切割。2.管道中或管道末端的阀门。 |
| Spalling | 剥落 |
The separation of macroscopic particles from a surface in the form of flakes or chips. 以薄片或碎片形式从表面分离宏观颗粒。 |