| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Regenerative pump | 涡流泵 |
(regenerative turbine pump, peripheral pump) A pump with a double-sided impeller having a large number of radial blades. The pressure of the pumped liquid increases progressively over several revolutions of the impeller. It is particularly suited to producing large heads at small flow rates without cavitation. （再生涡轮泵，外围泵）具有具有大量径向叶片的双面叶轮的泵。泵送液体的压力在叶轮的几圈内逐渐增加。它特别适合于在小流速下产生大水头且不产生气穴。 |
| Bearing stress | 承受应力 |
The force per unit of bearing area. 每单位承载面积的力。 |
| Hydrogen embrittlement | 氢脆 |
A condition of low toughness, low ductility or cracking in metals resulting from the absorption of hydrogen. A common and troublesome form of Stress cracking. Several theories have been proposed to explain hydrogen embrittlement, but, at present, the exact mechanism is still unknown. What is known, however, is the fact that if hydrogen is trapped in a bolt by poor electroplating practices, it can encourage stress cracking. Bolts can fail, suddenly and unexpectedly, under normal loads. Premature crack growth over time under tensile stress leading to unexpected failure in certain metals, caused by small amounts of hydrogen in the microstructure. Hydrogen may enter steels during melting or heat treating, or during processes such as electroplating. 因吸收氢而导致金属韧性低、延展性低或开裂的情况，是一种常见且麻烦的应力开裂形式。在拉伸应力下，裂纹随时间过早扩展，导致某些金属发生意外失效，这是由微观结构中的少量氢引起的。在熔化或热处理过程中，或在电镀等过程中，氢可能进入钢中。已经提出了几种理论来解释氢脆，但目前，确切的机理仍然未知。已知的事实是，如果氢因电镀不当而被困在螺栓中，则会导致应力开裂。在正常载荷下，螺栓可能突然意外失效。 |
| Venturi | 文丘里管 |
A convergent–divergent flow nozzle, usually circular in cross section, with a relatively short convergent section (the confuser) upstream of a throat followed by a gradually diverging section (the diffuser). Such nozzles usually have flanges at either end for installation in a pipeline. Applications include flow meters and ejectors. When a fluid flows through a convergent duct at subsonic speed, there is an increase in velocity accompanied by a decrease in pressure (Venturi effect). 收敛-发散流喷嘴，横截面通常为圆形，喉部上游具有相对较短的收敛段（扰流器），然后是逐渐发散段（扩散器）。这种喷嘴通常在两端都有法兰，以便安装在管道中。应用包括流量计和喷射器。当流体以亚音速流过收敛管道时，速度增加，压力降低（文丘里效应）。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Compressed liquid | 压缩液体 |
A liquid subjected to a pressure greater than the saturation pressure corresponding to its temperature. 承受大于与其温度对应的饱和压力的压力的液体。 |
| Intense quenching | 强烈淬火 |
Quenching in which the quenching medium is cooling the part at a rate at least two and a half times faster than still water. 淬火，其中淬火介质以比静水快至少两倍半的速度冷却零件。 |
| Anti-freeze | 防冻液 |
A substance such as ethylene glycol added to the cooling system of a watercooled engine to lower the freezing point of the cooling water and also inhibit the formation of rust and other deposits. 一种物质，如乙二醇，添加到水冷发动机的冷却系统中，以降低冷却水的冰点，并抑制生锈和其他沉积物的形成。 |
| Bond strength (Unit Pa) | 结合强度（单位Pa） |
The tensile, compressive or shear stress at which joints fail, e.g. by fracture or excessive deformation. 接头失效的拉伸、压缩或剪切应力，例如断裂或过度变形。 |
| Springback | 回弹 |
The extent to which metal tends to return to its original shape or contour after undergoing a forming operation. 金属在经历成形操作后趋于恢复其原始形状或轮廓的程度。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Rockwell hardness number (HR) | 洛氏硬度值（HR） |
A number derived from the net increase in the depth of impression in a Rockwell hardness test as the load on an indenter is increased from a fixed minor load to a major load and then returned to the minor load. Rockwell hardness numbers are always quoted with a scale symbol representing the penetrator, load, and dial used. 当压头上的载荷从固定的小载荷增加到大载荷，然后返回到小载荷时，洛氏硬度试验中压痕深度的净增加值。洛氏硬度值总是用刻度符号引用，表示所用的穿透器、载荷和刻度盘。 |
| Acicular ferrite | 针状铁素体 |
A highly substructured non-equiaxed ferrite that forms upon continuous cooling by a mixed diffusion and shear mode of transformation that begins at a temperature slightly higher than the temperature transformation range for upper bainite. It is distinguished from bainite in that it has a limited amount of carbon available; thus, there is only a small amount of carbide present. Ferrite crystallite growing, apparently, as in the course of bainitic transformation. It has a lath-like shape and an increased dislocation 一种高度亚结构的非等轴铁素体，在连续冷却时通过混合扩散和剪切相变模式形成，其开始温度略高于上贝氏体的温度转变范围。它与贝氏体的区别在于它的碳含量有限。因此，仅存在少量碳化物。显然，铁素体微晶在贝氏体转变过程中生长。它具有板条状的形状和增加的位错。 |
| Ductile fracture | 韧性断裂 |
Fracture characterized by tearing of metal accompanied by appreciable gross plastic deformation and expenditure of considerable energy. A fracture of a component or structure which is preceded by extensive ductile deformation so that the broken pieces cannot be re-fitted to regain the original size and shape of the component or structure. 以金属撕裂为特征的断裂，伴随着明显的总塑性变形和相当大的能量消耗。一种部件或结构的断裂，在断裂前会发生大范围的延性变形，从而使断裂的碎片无法重新装配以恢复部件或结构原来的尺寸和形状。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Actuating system | 驱动系统 |
A system in which an electrical, pneumatic or hydraulic input supplied to an actuator produces force, torque, or displacement, usually in a controlled way. 一种系统，其中提供给执行器的电气、气动或液压输入通常以受控方式产生力、扭矩或位移。 |
| Trepanning | 开孔 |
Trepanning is a machining process for producing a circular hole or groove in solid stock, or for producing a disk, cylinder, or tube from solid stock, by the action of a tool containing one or more cutters (usually single-point) revolving around a center. 开孔是一种机械加工工艺，通过包含一个或多个围绕中心旋转的刀具（通常为单点）的作用，在实心坯料中制造圆孔或凹槽，或从实心坯料生产圆盘、圆柱体或管。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Sigma phase | σ相 |
A hard, brittle, nonmagnetic intermediate phase with a tetragonal crystal structure, containing 30 atoms per unit cell, space group P42/mnm, occurring in many binary and ternary alloys of the transition elements. The composition of this phase in the various systems is not the same, and the phase usually exhibits a wide range in homogeneity. Alloying with a third transition element usually enlarges the field of homogeneity and extends it deep into the ternary section. 一种硬、脆、非磁性中间相，具有四方晶体结构，每单位晶胞含有30个原子，空间群P42/mnm，存在于许多过渡元素的二元和三元合金中。该相在各种系统中的组成不尽相同，并且该相通常表现出宽范围的均匀性。与第三过渡元素的合金化通常会扩大均匀性范围，并将其延伸到三元区。 |
| Austenitic grain size | 奥氏体晶粒尺寸 |
The size attained by the grains of steel when heated to the austenitic region; may be revealed by appropriate etching of cross sections after cooling to room temperature. 当加热到奥氏体区域时钢晶粒达到的尺寸；冷却至室温后，可通过适当蚀刻横截面来显示。 |
| Graphitic carbon | 石墨碳 |
Free carbon in steel or cast iron. 钢或铸铁中的游离碳。 |
| Absorber | 吸收器 |
1. An auxiliary vibratory system that favourably modifies the vibration characteristics of a main system. 2. Part of an absorption refrigeration system in which the refrigerant is absorbed by a transport medium. 3. The absorber plate is the receiver of a concentrating solar collector where the radiation is absorbed. 1.一种辅助振动系统，可有利地改变主系统的振动特性。2.吸收式制冷系统的一部分，其中制冷剂被传输介质吸收。3.吸收板是吸收辐射的聚光太阳能集热器的接收器。 |
| Physical crack size (ap) | 物理裂纹尺寸（ap） |
The distance from a reference plane to the observed crack front. This distance may represent an average of several measurements along the crack front. The reference plane depends on the specimen form, and it is normally taken to be either the boundary or a plane containing either the load line or the centerline of a specimen or plate. 从基准面到观察到的裂纹前沿的距离。该距离可以表示沿裂纹前沿的若干测量的平均值。基准面取决于试样形状，通常视为边界或包含试样或板的载重线或中心线的平面。 |
| Turn-of-nut | 转动螺母 |
Sometimes used to describe the general rotation of the nut (or bolt head) as the fastener is tightened. More often used to define a particular tightening procedure in which a fastener is first tightened with a preselected torque, and is then tightened further by giving the nut an additional, measured, turn such as ‘‘three flats’’ (180°). 有时用于描述紧固件拧紧时螺母（或螺栓头）的总体旋转。更常用于定义一种特定的紧固程序，在该程序中，首先以预选扭矩拧紧紧固件，然后通过使螺母额外转动，如“三平面”（180°）进一步拧紧。 |
| Base metal hardness | 母材硬度 |
Hardness closest to the surface (when traversing from core to outside diameter) just before an increase or decrease occurs, denoting, respectively, carburization or decarburization. 在发生增加或减少之前最接近表面的硬度（从芯部到外径时），分别表示渗碳或脱碳。 |
| Surface roughness (roughness) | 表面粗糙度 |
The small-scale, irregular peaks and troughs in a solid surface which are quantified using a surface analyser. Roughness may be a consequence of wear and corrosion, or of the manufacturing process. It leads to increased friction in solid– solid contact or fluid flow over a surface. Errors of form and waviness are excluded, but surface texture includes roughness and waviness. Surface topography incorporates the small-scale, three-dimensional geometry of a surface including surface roughness, machined, and etched features, typically at sub-mm scales. 固体表面中的小尺度不规则峰谷，使用表面分析仪进行量化。粗糙度可能是磨损和腐蚀或制造过程的结果。它会导致表面上的固-固接触或流体流动中的摩擦增加。不包括形状和波纹度误差，但表面纹理包括粗糙度和波纹度。表面形貌包括表面的小尺度三维几何结构，包括表面粗糙度、机加工和蚀刻特征，通常为亚毫米尺度。 |
| Yield point (Unit Pa) | 屈服点（单位Pa） |
The first stress in a material, usually less than the maximum attainable stress, at which an increase in strain occurs without an increase in stress. Only certain metals—those which exhibit a localized, heterogeneous type of transition from elastic to plastic deformation—produce a yield point. If there is a decrease in stress after yielding, a distinction may be made between upper and lower yield points. The load at which a sudden drop in the flow curve occurs is called the upper yield point. The constant load shown on the flow curve is the lower yield point. (yield strength, yield stress, Rel, Rel) The stress at which the onset of permanent (plastic) deformation (yielding) occurs in a body under increasing loading. In some materials, a yield-point phenomenon occurs in which stress falls on initial yielding and plastic deformation continues without increase in stress as strain increases further. The yield criterion is the combination of normal and shear stresses which produces yielding under multiaxial loading. 材料中的第一应力，通常小于可达到的最大应力，在该应力下应变增加而应力不增加。只有某些金属——表现出从弹性变形到塑性变形的局部、非均匀类型的金属——才会产生屈服点。如果屈服后应力降低，可区分上屈服点和下屈服点。流量曲线突然下降时的荷载称为上屈服点。流量曲线上显示的恒定载荷为较低屈服点。（屈服强度，屈服应力，Rel）在不断增加的载荷下，物体发生永久（塑性）变形（屈服）时的应力。在某些材料中，会出现屈服点现象，即应力在初始屈服时下降，随着应变进一步增加，塑性变形继续，而应力没有增加。屈服准则是在多轴载荷下产生屈服的正应力和剪应力的组合。 |
| Atom | 原子 |
The smallest unit of matter that has the properties of a chemical element. The simplest description of an atom (Bohr model) is of a compact nucleus surrounded by one or more orbiting electrons. 具有化学元素性质的最小物质单位。原子的最简单描述（玻尔模型）是由一个或多个轨道电子包围的致密原子核。 |
| Computational domain | 计算域 |
In CFD, FEM, and other numerical methods, the area or volume within which calculations are performed and on the periphery of which the boundary conditions are specified. 在CFD、FEM和其他数值方法中，执行计算的区域或体积以及在其外围指定边界条件的区域或体积。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Tangential load (Unit N) | 切向荷载（单位：N） |
The component of load applied to an object, such as a gear, that tends to cause or resist rotation. 旋转力施加在物体上的载荷分量，如齿轮，倾向于引起或阻止旋转。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Radial engine | 径向发动机 |
A piston engine in which the cylinders are arranged radially around the crankshaft, a design commonly used in early aircraft engines. 气缸沿径向围绕曲轴布置的活塞式发动机，这种设计通常用于早期飞机发动机。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Effective radius of nut, bolt head, or threads | 螺母、螺栓头或螺纹的有效半径 |
Distance between the geometric center of the part and the circle of points through which the resultant contact forces between mating parts passes. Must be determined by integration. 零件几何中心与配合零件之间的合力通过的点圆之间的距离。必须通过积分来确定。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Dislocation density | 位错密度 |
The total length of dislocation lines per unit volume, or the number of dislocation lines that cut through a unit cross-sectional area. 每单位体积的位错线的总长度，或穿过单位横截面积的位错线的数量。 |
| Compression member | 压缩构件 |
A structural component, the major loading on which is compressive. 一种结构部件，其上的主要载荷是压缩的。 |
| Air cleaner | 空气净化器 |
A device, such as a filter, hydrocyclone, or electrostatic precipitator, that removes particles and aerosols from a flow of air. 一种设备，例如过滤器、水力旋流器或静电除尘器，用于从气流中去除颗粒和气溶胶。 |
| Crest | 波峰 |
The highest point of a wave or of a screw thread. 波浪或螺纹的最高点。 |
| Sampling frequency (Unit Hz) | 采样频率（单位Hz） |
(sampling rate) The number of measurement samples per unit time taken from a continuous analogue signal to produce a discrete signal. It is the inverse of the time between successive measurements (sampling interval, sampling period, or sampling time). （采样率）从连续模拟信号中提取以产生离散信号的每单位时间的测量样本数。它是连续测量之间时间的倒数（采样间隔、采样周期或采样时间）。 |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| Shoulder bolt | 轴肩螺栓 |
A bolt for which the unthreaded cylindrical section between the thread and the head is of larger diameter than the threaded section, precisely machined to length and diameter and hardened 一种螺栓，其螺纹和头部之间的无螺纹圆柱段的直径大于螺纹段的直径，精确加工至长度和直径并硬化 |
| Milling | 铣削 |
A machining process, typically for metals and plastics, in which a multi-tooth rotary cutter removes material to produce flat or profiled surfaces, slots, grooves, etc. Milling is a machining process in which metal is removed by a rotating multiple-tooth cutter; each tooth removes a small amount of metal with each revolution of the spindle. Because both workpiece and cutter can be moved in more than one direction at the same time, surfaces having almost any orientation can be machined. 一种加工工艺，通常用于金属和塑料，其中多齿旋转刀具去除材料以产生平坦或异形表面、槽、槽等。金属由旋转多齿刀具去除；主轴每转一圈，每个齿都会去除少量金属。因为工件和刀具可以同时在多个方向上移动，所以几乎可以加工任何方向的表面。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Computer-aided design (CAD) | 计算机辅助设计（CAD） |
Generally, design and calculations performed by computer; more specifically, the use of computer graphics and models to communicate design concepts. Computer-aided design and computer-aided manufacturing (CAD/CAM) is where component dimensions resulting from CAD are passed by electronic means directly to machines for manufacture. 一般由计算机进行设计和计算，更具体地说，使用计算机图形和模型来传达设计概念。计算机辅助设计和计算机辅助制造（CAD/CAM）是由CAD产生的组件尺寸通过电子方式直接传递到机器进行制造。 |
| Total carbon | 总碳 |
The sum of the free and combined carbon (including carbon in solution) in a ferrous alloy. 铁合金中游离碳和结合碳（包括溶液中的碳）的总和。 |
| Stress relaxation | 应力松弛 |
The slow decrease in stress level within a part (e.g., a bolt) which is heavily loaded under constant deflection conditions. A ‘‘cousin’’ to creep, which is a slow change in geometry under constant stress conditions. The time-dependent decrease in stress in a solid under constant strain at constant temperature due to creep. The stress-relaxation behavior of a metal is usually shown in a stress-relaxation curve. 在恒定挠曲条件下，零件（如螺栓）内的应力水平缓慢降低，该零件承受重荷载。蠕变的“表亲”，是在恒定应力条件下几何结构的缓慢变化。在恒定温度下，由于蠕变，固体在恒定应变下的应力随时间变化的减小。金属的应力松弛行为通常显示在应力松弛曲线中。 |
| Stress ratio (A or R) | 应力比（A或R） |
The algebraic ratio of two specified stress values in a stress cycle. Two commonly used stress ratios are the ratio of the alternating stress amplitude to the mean stress, A = Sa/Sm, and the ratio of the minimum stress to the maximum stress, R = Smin/Smax. 应力循环中两个指定应力值的代数比。两种常用的应力比是交变应力振幅与平均应力之比，A=Sa/Sm，以及最小应力与最大应力之比R=Smin/Smax。 |
| Oil hardening | 油回火 |
The formation of martensite before tempering by quenching suitable steels in oil at lower cooling rates than given by water quenching, thus reducing the likelihood of component fracture or severe residual stresses. Quench-hardening treatment involving cooling in oil. 通过在油中以低于水淬的冷却速率淬火合适的钢，在回火前形成马氏体，从而降低部件断裂或严重残余应力的可能性。是一种淬火硬化处理，包括在油中冷却。 |
| Cylinder head | 气缸盖 |
The machined casting, typically of aluminium alloy or cast iron, that fits above the cylinder block of a piston engine and closes off the cylinders. It normally includes part of the combustion chambers and holes for the valves and spark plugs. 活塞式发动机缸体上方的机械铸件，通常由铝合金或铸铁制成，用于封闭气缸。它通常包括燃烧室的一部分以及阀门和火花塞的孔。 |
| Castellated nut | 槽形螺母 |
A nut having slots across the hexagonal faces, used with a bolt having a drilled hole so that a split (cotter) pin may be inserted through both nut and bolt to prevent unscrewing. 一种在六角面上有槽的螺母，与具有钻孔的螺栓一起使用，以便将开口（开口）销插入穿过螺母和螺栓以防止拧松。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Hypoeutectic alloy | 亚共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of base metal compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，其成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Following flank | 跟随侧翼 |
The flank of a thread opposite to the leading flank. 与前牙面相对的螺纹牙面。 |
| Striation | 条纹组织 |
A fatigue fracture feature, often observed in electron micrographs, that indicates the position of the crack front after each succeeding cycle of stress. The distance between striations indicates the advance of the crack front across that crystal during one stress cycle, and a line normal to the striation indicates the direction of local crack propagation. 一种疲劳断裂特征，通常在电子显微照片中观察到，表明每次应力循环后裂纹前沿的位置。条纹之间的距离表示在一个应力循环期间裂纹前沿穿过该晶体的前进，垂直于条纹的线表示局部裂纹扩展的方向。 |
| Radial load (Unit N) | 径向负荷（单位：N） |
1. Centrifugal loading induced in a rotating body. 2. (through-wallthickness load) The radial component of loading arising from internal or external pressurization of a closed vessel. There will also be axial and hoop loading. 1.旋转体中产生的离心载荷。2.（贯穿壁厚载荷）由封闭容器的内部或外部加压产生的载荷的径向分量。还存在轴向和环向载荷。 |
| Delamination | 分层 |
A mode of failure of composite materials, including radial-ply tyres, in which the layers separate due to repeated cyclic loading, impact, or weak bonding. 复合材料的一种失效模式，包括子午线轮胎，其中层由于重复的循环载荷、冲击或弱粘合而分离。 |
| Liquid nitriding | 液体氮化 |
A method of surface hardening in which molten nitrogen-bearing, fused-salt baths containing both cyanides and cyanates are exposed to parts at subcritical temperatures. 一种表面硬化方法，其中含有氰化物和氰酸盐的熔融含氮熔盐浴在亚临界温度下暴露于零件。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Vacuum pump | 真空泵 |
A pump for exhausting air and non-condensable gases from a vessel to be maintained at sub-atmospheric pressure. The pirani and thermal-conductivity gauges are vacuum gauges used to measure the absolute pressure within a vacuum system (vacuum level), usually expressed in torr or Pa. 用于从容器中排出空气和不凝性气体以保持在亚大气压的泵。皮拉尼和热导率计是用于测量真空系统内绝对压力（真空水平）的真空计，通常用托或帕表示。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Surface tension (σ, γ) (Unit N/m) | 表面张力（σ，γ）（单位：N/m） |
At the interface between a liquid and a gas or two immiscible liquids, unbalanced cohesive forces acting on the liquid molecules at the interface lead to the property surface tension which causes tensile forces to develop as if it were a skin or membrane. 液体和气体或两种不混溶液体之间的界面处，作用在界面处的液体分子上的不平衡内聚力导致表面张力的性质，从而导致张力的发展，就像皮肤或薄膜一样。 |
| Partial annealing | 不完全退火 |
An imprecise term used to denote a treatment given cold-worked material to reduce the strength to a controlled level or to effect stress relief. To be meaningful, the type of material, the degree of cold work, and the time-temperature schedule must be stated. 一个不精确的术语，用于表示冷加工材料的处理，以将强度降低到受控水平或消除应力。为了有意义，必须说明材料类型、冷加工程度和时间-温度计划。 |
| Sample standard deviation (s) | 样本标准偏差（s） |
The square root of the sample variance. It is a point estimate of the population standard deviation, a measure of the “spread”of the frequency distribution of a population. This value of sprovides a statistic that is used in computing interval estimates and several test statistics. For small sample sizes, s underestimates the population standard deviation. 样本方差的平方根。它是总体标准偏差的点估计，是总体频率分布“扩散”的度量。SPR的这个值提供了一个用于计算区间估计和若干测试统计量的统计量。对于小样本，s低估了总体标准偏差。 |
| Angle of thread | 螺纹角度 |
The included angle between the sides forming the groove of the screw thread. 形成螺纹凹槽的边之间的夹角。 |
| Chafing fatigue | 磨损疲劳 |
Fatigue damage initiated in a surface damaged by rubbing against another body. 因与另一个物体摩擦而损坏的表面引起的疲劳损坏。 |
| Fastener identification marking | 紧固件识别标记 |
A stamp, paint, or other permanent identifier that may include manufacturer information and applicable grade markings for certification purposes. 印章、油漆或其他永久性标识符，其中可能包括制造商信息和用于认证的适用等级标记。 |
| Welding | 焊接 |
In tribology, the bonding between metallic surfaces in direct contact, at any temperature. A joining process in which the mating surfaces are at least softened, or more usually melted, unlike soldering and brazing. In solid-state (non-melting) welding, similar or dissimilar metals or thermoplastics may be joined by applying pressure to hot interfaces. In forge welding, joining is achieved by compression across the join between pre-heated workpieces. In friction welding (spin welding) one of the contacting surfaces is rotated rapidly before being loaded against the other. On contact, heat generated by friction softens the materials and permits severe plastic deformation that seals the joint. In friction stir welding, a wear-resistant tool is rotated rapidly, indents the surfaces and is traversed to form a join line. Resistance welding involves simultaneous pressure and electrically-generated heat, as in spot welding where a heavy electric current is passed for a short time through metal sheets which are pressed together between electrodes. 在摩擦学中，在任何温度下直接接触的金属表面之间的结合。与钎焊和钎焊不同，接合面至少软化或更通常熔化的接合工艺。在固态（非熔化）焊接中，相似或不同的金属或热塑性塑料可通过向热界面施加压力来连接。在锻造焊接中，通过压缩预热工件之间的连接来实现连接。在摩擦焊接（旋转焊接）中，一个接触表面在被加载到另一个表面之前快速旋转。接触时，摩擦产生的热量使材料软化，并允许密封接头的严重塑性变形。在搅拌摩擦焊中，耐磨工具快速旋转，使表面凹陷，并横穿形成连接线。电阻焊涉及同时产生的压力和电产生的热量，如点焊，在点焊中，大电流短时间通过电极之间压在一起的金属板。 |
| GGas turbine | G燃气轮机 |
An engine in which air, compressed by a multi-stage axial compressor and/or one or more centrifugal compressors, flows into a combustion chamber (or chambers) where fuel is burned and the hot gases then drive an axial turbine which powers the compressor. 由多级轴流压缩机和/或一个或多个离心压缩机压缩的空气流入燃烧室（或多个燃烧室），在燃烧室中燃烧燃料，然后热气体驱动轴流涡轮，为压缩机提供动力。 |
| Stud | 螺柱 |
A rod having thread on both ends. A headless threaded fastener, threaded on both ends, with an unthreaded body in the middle section, or threaded from end to end. Used with two nuts, or with one nut and a tapped hole. A plain cylindrical piece having a threaded portion of suitable length at each end or a continuous thread over the entire length. One end is screwed into a machine or workpiece after which a second part is placed over the stud and held in place by a nut. 两端都有螺纹的杆。无头螺纹紧固件，两端有螺纹，中间部分有无螺纹主体，或从一端到另一端有螺纹。与两个螺母或一个螺母和一个螺纹孔一起使用。一种普通的圆柱形部件，其两端具有适当长度的螺纹部分，或在整个长度上具有连续螺纹。一端拧入机器或工件，然后将第二部分放在螺柱上，并用螺母固定到位。 |
| Wind pump | 风泵 |
A pump driven directly by a windmill on a tower. Widely used in remote locations. 由塔上的风车直接驱动的泵。广泛应用于偏远地区。 |
| Ideal crack | 理想裂缝 |
A simplified model of a crack used in elastic-stress analysis. In a stress-free body, the crack has two smooth surfaces that are coincident and join within the body along a smooth curve called the crack front; in two-dimensional representations, the crack front is called the crack tip. 用于弹性应力分析的裂纹简化模型。在无应力物体中，裂纹有两个光滑表面，它们在物体内沿称为裂纹前缘的平滑曲线重合并连接；在二维表示中，裂纹前缘称为裂纹尖端。 |
| Friction | 摩擦 |
The resistance that a body encounters when sliding over another body, or experiences when a viscous fluid flows over its surface. 一个物体在另一个物体上滑动时遇到的阻力，或者当粘性流体流过其表面时所经历的阻力。 |
| Mechanical alloying | 机械合金化 |
Production of alloys from powders by consolidation, e.g. hotpressing or extrusion, followed by hot and/or cold working and final annealing. Materials such as dispersion-strengthened alloys, high-temperature aluminium alloys, and amorphous alloys can be made in this way. 通过固结（例如热压或挤压）从粉末生产合金，然后进行热和/或冷加工和最终退火。用这种方法可以制造弥散强化合金、高温铝合金和非晶合金等材料。 |
| Damage mechanics | 损伤机制 |
The theory of degradation in bodies, particularly fracture by accumulated microstructural damage. Analyses take two approaches: (a) the use of some critical integrated function of stress and strain at which cracking is initiated and propagated; (b) incorporation of damage in the stress–strain curves to reflect weakened material. 物体退化理论，尤其是累积微观结构损伤导致的断裂。分析采用两种方法：（a）使用裂纹开始和扩展时的应力和应变的一些临界积分函数；（b）应力-应变曲线中包含损伤，以反映弱化材料。 |
| Fretting corrosion | 微动腐蚀 |
(1) The accelerated deterioration at the interface between contacting surfaces as the result of corrosion and slight oscillatory movement between the two surfaces. (2) A form of fretting in which chemical reaction predominates. Fretting corrosion is often characterized by the removal of particles and subsequent formation of oxides, which are often abrasive and so increase the wear. Fretting corrosion can involve other chemical reaction products, which may not be abrasive. （1）由于两个表面之间的腐蚀和轻微振荡运动，接触表面之间的界面加速劣化。（2）一种以化学反应为主的微动磨损形式。微动腐蚀通常以颗粒的去除和随后形成的氧化物为特征，这些氧化物通常具有研磨性，因此会增加磨损。微动腐蚀可能涉及其他化学反应产物，这些化学反应产物可能不是磨料。 |
| Chain | 链 |
A series of connected links, typically of steel. For lifting, pulling, securing, etc., each link is a closed loop, often in the form of a ring. For power transmission, the links are designed to mesh with the teeth of a sprocket wheel. In contrast to belt drives, chain drives tend to be employed in high-torque applications. 一系列连接的链接，通常是钢制的。对于提升、拉动、固定等，每个链节都是一个闭合环，通常呈环形。对于动力传输，链节设计为与链轮的齿啮合。与皮带传动相比，链传动往往用于高扭矩应用。 |
| Initial preload | 初始预载 |
The tension created in a single bolt as it is tightened. Will usually be modified by subsequent assembly operations or by in-service loads and conditions. 拧紧单个螺栓时产生的张力。通常会通过后续的装配操作或在役负载和条件进行修改。 |
| True stress (σ) (Unit Pa) | 真应力（σ）（单位Pa） |
The value obtained by dividing the load applied to a member at a given instant by the cross-sectional area over which it acts. Compare with engineering stress. The applied load on a test specimen divided by the current cross-section area over which it acts. σ = s expε where s is the engineering stress given by the applied load divided by the original cross-section area over which it acts, and ε is the true strain. 通过将给定时刻施加在构件上的荷载除以其作用的横截面积而获得的值。与工程应力相比。施加在试样上的荷载除以其作用的当前横截面积。σ=s expε，其中s是由施加荷载除以其作用的原始横截面面积得出的工程应力，ε是真实应变。 |
| Hot hardness | 热硬度 |
The hardness of materials at high temperatures, often used to rank the performance of cutting tools. 材料在高温下的硬度，常用来对刀具的性能进行排名。 |
| Carbonization | 碳化 |
Conversion of an organic substance into elemental carbon. 将有机物质转化为元素碳。 |
| Coherent precipitate | 相干沉淀 |
A crystalline precipitate that forms from solid solution with an orientation that maintains continuity between the crystal lattice of the precipitate and the lattice of the matrix, usually accompanied by some strain in both lattices. Because the lattices fit at the interface between precipitate and matrix, there is no discernible phase boundary. 由固溶体形成的结晶沉淀物，其取向保持沉淀物晶格和基体晶格之间的连续性，通常伴随着两个晶格中的一些应变。由于晶格适合于沉淀和基体之间的界面，因此不存在可识别的相边界。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Concurrent engineering | 并行工程 |
The integration of the procedures for product design, material selection and manufacturing method to include life-cycle analysis. 产品设计、材料选择和制造方法程序的整合，包括生命周期分析。 |
| Thermochemical treatment | 热化学处理 |
Heat treatment carried out in a medium suitably chosen to produce a change in the chemical composition of the object by exchange with the medium. 在适当选择的介质中进行热处理，以通过与介质交换产生物体化学成分的变化。 |
| Maraging steels | 马氏体时效钢 |
Very high-strength iron alloys named after ‘martensitic’ and ‘aging’. They contain nickel, chromium, cobalt, and molybdenum, and form martensite on air cooling with a strength of about 1 GPa. When reheated to about 500°C and aged for some hours, a room-temperature strength of some 2.4 GPa is reached. 以“马氏体”和“时效”命名的超高强度铁合金。它们含有镍、铬、钴和钼，在空气冷却下形成强度约为1GPa的马氏体。当再加热至约500°C并老化数小时时，室温强度达到约2.4GPa。 |
| Stiffness | 刚度 |
(1) The ability of a metal or shape to resist elastic deflection.(2) The rate of stress increase with respect to the rate of increase in strain induced in the metal or shape; the greater the stress required to produce a given strain, the stiffer the material is said to be. （1）金属或形状抵抗弹性变形的能力。（2）所述应力增加速率相对于在所述金属或形状中诱导的应变增加速率；产生给定应变所需的应力越大，材料就越硬。 |
| Elastic energy | 弹性能 |
The amount of energy required to deform a material within its elastic range of behavior, neglecting small heat losses due to internal friction. The energy absorbed by a specimen per unit volume of material contained within the gage length being tested. It is determined by measuring the area under the stress-strain curve up to a specified elastic strain. See also modulus of resilience and strain energy. 材料在其弹性行为范围内变形所需的能量，忽略因内耗引起的小热损失。试样在被测标距内每单位体积材料吸收的能量。它是通过测量应力-应变曲线下达到规定弹性应变的面积来确定的。另见弹性模量和应变能。 |
| Half hard | 半硬化回火 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength about mid-way between that of dead soft and full hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于完全软回火和完全硬回火之间。 |
| Metric ton (tonne, t) | 公制吨（吨，t） |
An SI-accepted, but non-SI, unit of mass defined as 1 t = 103 kg. SI系统可接受但非国际单位制的质量单位，定义为1t=103kg。 |
| Significance level | 显着性水平 |
The stated probability (risk) that a given test of significance will reject the hypothesis that a specified effect is absent when the hypothesis is true. 当假设为真时，给定的显著性检验将拒绝特定效应不存在的假设的所述概率（风险）。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Stress relieving | 应力消除 |
Heating to a suitable temperature, holding long enough to reduce residual stresses, and then cooling slowly enough to minimize the development of new residual stresses. 加热到合适的温度，保持足够长的时间以减少残余应力，然后缓慢冷却以尽量减少新残余应力的产生。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Horsepower | 马力 |
Unit indicating the rate at which work is done. The electrical equivalent of one horsepower is 746 watts. 单位表示完成工作的速率。一马力的电当量为746瓦。 |
| Scleroscope hardness number (HSc or HSd) | 硬化镜硬度值（HSc或HSd） |
A number related to the height of rebound of a diamond-tipped hammer dropped on the material being tested. It is measured on a scale determined by dividing into 100 units the average rebound of the hammer from a quenched(to maximum hardness) and untempered AISI W5 tool steel test block. 与落在被测材料上的菱形锤的回弹高度相关的数字。通过将锤子从淬火（达到最大硬度）和未淬火的AISI W5工具钢试块上的平均回弹分为100个单位来测量。 |
| Screw area (Unit m²) | 螺丝面积（单位m²） |
The area of a circle described by the tips of a propeller. 螺旋桨尖端所描述的圆的面积。 |
| Crack-extension resistance (KR) | 抗裂扩展性（KR） |
A measure of the resistance of a material to crack extension, expressed in terms of the stress-intensity factor, the crack-extension force, or values of Jderived using the J-integral concept. 材料对裂纹扩展的抵抗力的量度，以应力强度因子、裂纹扩展力或使用J积分概念导出的J值表示。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Double aging | 双级时效 |
Employment of two different aging treatments to control the type of precipitate formed from a supersaturated matrix in order to obtain the desired properties. The first aging treatment, sometimes referred to as intermediate or stabilizing, is usually carried out at higher temperature than the second. 采用两种不同的时效处理来控制由过饱和基质形成的沉淀物类型，以获得所需的性能。第一次时效处理，有时称为中间处理或稳定处理，通常在比第二次更高的温度下进行。 |
| International Practical Temperature Scale (IPTS) | 国际实用温标（IPTS） |
A close approximation to the thermodynamic temperature scale based upon the triple points of hydrogen (13.8 K), neon (24.6 K), oxygen (54.4 K), argon (83.8 K), mercury (234.3 K), and water (273.2 K); the melting point of gallium (302.9 K); and the freezing points of indium (429.7 K), tin (505.1 K), zinc (692.7 K), aluminium (933.5 K), silver (1 234.9 K), gold (1 337.3 K), and copper (1 基于氢（13.8K）、氖（24.6K）、氧（54.4K）、氩（83.8K），汞（234.3K）和水（273.2K）的三相点的热力学温度标度的近似值；镓的熔点（302.9K）；铟（429.7K）、锡（505.1K）、锌（692.7K），铝（933.5K）、银（1234.9K）、金（1337.3K）和铜等。 |
| Relative humidity (ϕ) | 相对湿度（ψ） |
The ratio or percentage of the actual mass of moisture in a given volume of air at a given temperature to the maximum possible mass of moisture at the same temperature. 给定温度下给定体积空气中的实际水分质量与相同温度下的最大可能水分质量的比率或百分比。 |
| Tensile stress (Unit Pa) | 拉应力（单位Pa） |
A stress that causes two parts of an elastic body, on either side of a typical stress plane, to pull apart. A stress that tends to stretch a component, or local region of a component, when under load. In simple tension it results from the applied axial load, but tensile stresses occur in bending, torsion and other forms of loading. 一种应力，使弹性体的两个部分在典型应力平面的任一侧分离。在负载下，倾向于拉伸部件或部件局部区域的应力。在简单拉伸中，它由施加的轴向载荷产生，但拉伸应力发生在弯曲、扭转和其他形式的载荷中。 |
| Wrist pin | 腕销 |
A stud projecting from a crank as an attachment for a connecting rod. wrought alloys Metal alloys that are initially cast and then shaped into final form by processes such as extrusion, forging, or rolling. 从曲柄上伸出的一个螺柱，作为连接杆的附件。锻造合金最初铸造，然后通过挤压、锻造或轧制等工艺成形为最终形状的金属合金。 |
| Biomechanics | 生物力学 |
The application of mechanical-engineering principles, including thermodynamics, fluid mechanics, and solid mechanics together with materials engineering, to biological systems. 机械工程原理（包括热力学、流体力学和固体力学以及材料工程）在生物系统中的应用。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Stretch forming | 拉伸成型 |
A manufacturing process in which sheet-metal components are physically stretched over a forming die using a press, punch, or edge clamps. Stretching combined with bending reduces springback. 一种制造工艺，其中使用压力机、冲头或边缘夹具在成形模上物理拉伸金属板部件。拉伸与弯曲相结合可减少回弹。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Millimetre of mercury | 毫米汞柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of mercury 1 mm high. Approximately equal to 133.3 Pa or 1 torr. 一种非SI压力单位，等于1毫米高的垂直水银柱施加的压力。大约等于133.3Pa或1托。 |
| Lock nut | 锁紧螺母 |
A type of nut that is prevented from loosening under vibration. The locking action is accomplished by squeezing, gripping or jamming against the bolt threads. A nut which provides extra resistance to vibration loosening (beyond that produced by proper Preload ), either by providing some form of Prevailing torque, or, in free-spinning lock nuts, by deforming, cramping, or biting into mating parts when fully tightened. 1. A thin auxiliary nut tightened against another nut to prevent loosening. 2. A single nut with special features that prevent loosening. 一种在振动下防止松动的螺母。锁定动作通过挤压、夹紧或卡住螺栓螺纹来完成。通过提供某种形式的主要扭矩，或在自由旋转锁紧螺母中，通过完全拧紧时变形、夹紧或咬入配合零件，提供额外的抗振动松动能力（超出适当预载产生的能力）。1.一个薄的辅助螺母，拧紧到另一个螺母上以防止松动。2.具有防止松动的特殊功能的单个螺母。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Cooling stresses | 冷却应力 |
Residual stresses resulting from nonuniform distribution of temperature during cooling. 冷却过程中温度分布不均匀导致的残余应力。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Liquid carburizing | 液体渗碳 |
Surface hardening of steel by immersion into a molten bath consisting of cyanides and other salts. 通过浸入由氰化物和其他盐组成的熔池中对钢进行表面硬化。 |
| Freezing point | 冰点 |
The temperature at which a substance changes phase (or state) from liquid to solid. The freezing point for most substances increases as pressure increases. The reverse process, from solid to liquid, is melting; melting point is the same as freezing point. 物质从液态变为固态的温度。大多数物质的冰点随着压力的增加而增加。从固体到液体的逆过程是熔化；熔点与凝固点相同。 |
| Stress difference (Unit Pa) | 应力差（单位Pa） |
The algebraic difference between the largest and least principal stresses in a loaded body, equal to twice the greatest shear stress in the system. For σ1 > σ2 > σ3, it is given by (σ1 − σ3). 载荷体中最大和最小主应力之间的代数差，等于系统中最大剪应力的两倍。由（σ1− σ3).，可得σ1＞σ2＞σ3。 |
| Turning angle (θ) | 转向角（θ） |
The change in direction experienced by a gas flow passing through an oblique shock wave or Prandtl–Meyer expansion fan. 气流通过斜激波或Prandtl–Meyer膨胀风机时所经历的方向变化。 |
| Alloying element | 合金元素 |
Component added deliberately with the aim of improving the properties of an alloy. Alloying elements can affect the existence range of equilibrium phases present in an unalloyed material, or lead to the occurrence of new phases, or both. In addition, alloying elements strongly affect the kinetics of phase transformations and thus the microstructure formation in alloyed materials. 为改善合金性能而有意添加的成分。合金元素可以影响非合金材料中存在的平衡相的存在范围，或导致新相的出现，或两者兼而有之。此外，合金元素强烈影响相变动力学，从而影响合金材料的微观结构形成。 |
| Austempering | 等温淬火 |
A heat treatment for ferrous alloys in which a part is quenched from the austenitizing temperature at a rate fast enough to avoid formation of ferrite or pearlite and then held at a temperature just above Ms until transformation to bainite is complete. Although designated as bainite in both austempered steel and austempered ductile iron (ADI), austempered steel consists of two phase mixtures containing ferrite and carbide, while austempered ductile iron consists of two phase mixtures containing ferrite and austenite. Heat treatment comprising austenitization of a steel article, cooling it to a bainitic range at a rate higher than the critical cooling rate and holding at a fixed temperature until the completion of bainitic transformation. 一种铁合金的热处理，其中零件从奥氏体化温度以足够快的速度淬火，以避免形成铁素体或珠光体，然后保持在略高于Ms的温度，直到完全转变为贝氏体。虽然在奥氏体钢和奥氏体球铁(ADI)中都被指定为贝氏体，但奥氏体钢由含有铁素体和碳化物的两相混合物组成，而奥氏体球墨铸铁由含有铁素体和奥氏体的两相混合物组成。热处理包括钢制品的奥氏体化，以高于临界冷却速率的速率将其冷却到贝氏体范围，并保持在固定温度直到贝氏体转变完成。 |
| Imperial system | 英制单位体系 |
The units of measurement developed in the UK. Formerly known as the fps system, which is an abbreviation for the ‘foot-pound-second system of units. 英国开发的计量单位。以前称为fps系统，是“英尺-磅-秒（foot-pound-second）单位制”的缩写。 |
| Absolute temperature (Unit K) | 绝对温度（单位K） |
A temperature T measured relative to absolute zero, 0 K or −273.15°C, the lowest temperature achievable at which molecular motion vanishes so that a body would have zero heat energy. The kelvin is equal in magnitude to the degree Celsius (°C). The kelvin temperature scale (kelvin absolute temperature scale) is an absolute or thermodynamic temperature scale derived from the Celsius scale: T(K) = T(°C) + 273.15. The Rankine absolute scale is derived from the Fahrenheit scale such that T(R) = T(°F) + 459.67, i.e. a scale relative to 0 R or −459.67°F where R is the Rankine degree symbol and °F is the Fahrenheit symbol. 相对于绝对零、0K或0K测量的温度T−273.15°C，分子运动消失的最低温度，因此物体的热能为零。开尔文的大小等于摄氏度（℃）。开尔文温度标度（开尔文绝对温度标度）是从摄氏标度得出的绝对或热力学温度标度：T（K）=T（°C）+273.15。兰金绝对标度是从华氏标度得出，使得T（R）=T（°F）+459.67，即相对于0R或0R的标度−459.67°F，其中R是朗肯度符号，°F是华氏度符号。 |
| Cooling curve | 冷却曲线 |
A curve showing the relation between time and temperature during the cooling of a material. 显示材料冷却过程中时间和温度之间关系的曲线。 |
| Roots blower | 罗茨鼓风机 |
(rotary-piston blower) A positive-displacement gas compressor with two meshing lobed rotors that rotate within a close-fitting casing. Commonly used as a supercharger. （旋转活塞鼓风机）一种容积式气体压缩机，具有两个啮合的凸角转子，在紧密配合的外壳内旋转。通常用作增压器。 |
| Bar | 巴（气压单位） |
A widely used (non-SI) unit of pressure approximately equal to normal atmospheric pressure at sea level. The conversion to SI is 1 bar = 105 Pa. Unit of pressure – the pressure created by a column of€mercury 75.006 cm high at 0ºC, or about 33.45 feet of water at 4ºC. It is equal to 105 pascal. Standard atmospheric pressure (at sea level) is 1.01325 bar, or 1013.25 mb. 一种广泛使用的（非SI）压力单位，大约等于海平面上的正常大气压。转换为SI为1bar=105Pa。压力单位——0ºC时75.006厘米高的水银柱或4ºC时约33.45英尺水柱产生的压力。它等于105帕斯卡。标准大气压（海平面）为1.01325bar或1013.25mb。 |
| Decalescence | 退色 |
A phenomenon, associated with the transformation of alpha iron to gamma iron on the heating (superheating) of iron or steel, revealed by the darkening of the metal surface owing to the sudden decrease in temperature caused by the fast absorption of the latent heat of transformation. 一种现象，与铁或钢加热（过热）时α铁向γ铁的转变有关，由于转变潜热的快速吸收导致温度突然降低，金属表面变黑。 |
| Gear pump | 齿轮泵 |
A positive-displacement pump in which fluid is pumped by meshing gears, one driven and the other an idler gear, on parallel axes within a closed casing. 一种容积式泵，其中流体由啮合齿轮泵送，在封闭外壳内的平行轴上一个驱动，另一个为空套齿轮。 |
| Temper | 回火 |
(1) In heat treatment, reheating hardened steel or hardened cast iron to some temperature below the eutectoid temperature for the purpose of decreasing hardness and increasing toughness. The process also is sometimes applied to normalized steel. (2) In tool steels, temper is sometimes used, but inadvisedly, to denote the carbon content. (3) In nonferrous alloys and in some ferrous alloys (steels that cannot be hardened by heat treatment), the hardness and strength produced by mechanical or thermal treatment, or both, and characterized by a certain structure, mechanical properties, or reduction in area during cold working. （1）在热处理中，将硬化钢或硬化铸铁重新加热到共析温度以下的温度，以降低硬度和增加韧性。该工艺有时也适用于正火钢。（2）在工具钢中，有时使用回火来表示碳含量，但这是不恰当的。（3）在非铁合金和一些铁合金（不能通过热处理硬化的钢）中，通过机械或热处理或两者产生的硬度和强度，其特征是在冷加工过程中具有一定的结构、机械性能或面积减小。 |
| Precipitation hardening | 沉淀硬化 |
Hardening caused by the precipitation of a constituent from a supersaturated solid solution. 因成分从过饱和固溶体沉淀而导致的硬化。 |
| Conditioning heat treatment | 调质热处理 |
A preliminary heat treatment used to prepare a material for desired reaction to a subsequent heat treatment. For the term to be meaningful, the exact heat treatment must be specified. 用于制备材料的初步热处理，以便对随后的热处理进行所需的反应。为了使该术语有意义，必须指定确切的热处理。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Acoustic droplet ejection | 声液滴喷射 |
The ejection of small droplets from the surface of a liquid that results from focusing high-intensity ultrasound near the surface. 由于在表面附近聚焦高强度超声波而从液体表面喷射出小液滴。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Scale height (Unit m) | 刻度高度（单位：m） |
The altitude H at which the atmospheric pressure has decreased to a certain fraction of its value at sea level B. It depends on the model adopted for the atmosphere: for an isothermal atmosphere, the pressure decreases exponentially with altitude. If H is taken as the altitude at which the pressure has fallen to B/e, then H = RT/g where R is the gas constant for air, T is the absolute temperature T, and g is the acceleration due to gravity. 大气压力降低到其在海平面B处数值的某一部分的高度H。它取决于大气采用的模型：对于等温大气，压力随高度呈指数下降。如果取H作为压力下降到B/e的高度，则H=RT/g，其中R是空气的气体常数，T是绝对温度T，g是重力引起的加速度。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| Stress | 应力（单位Pa） |
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression)or shear. 1. Stress ‘at a point’ (i.e. over a volume of material that is very small compared with that of the component or structure) is the load per unit area for every face of an infinitesimal cube surrounding the point. 2. In fluid flow the stress tensor σij is the sum of an isotropic part −pδij, δij being the Kronecker delta, having the same form as the stress tensor for a fluid at rest, p being the static pressure, and the non-isotropic, deviatoric stress tensor dij which is due entirely to the fluid motion. 内部分布力或力分量的强度，这些力或力的分量抵抗正在或已经受到外力的材料的体积或形状的变化。应力以单位面积的力表示，并根据试样横截面的原始尺寸计算。应力可以是直接（拉伸或压缩）或剪切。1.“在一点”的应力（即在与组件或结构相比非常小的材料体积上）是围绕该点的无限小立方体的每个面的单位面积载荷。2. 在流体流动中，应力张量σij是各向同性部分-pδij的总和，δij是Kroneckerδ，具有与静止流体的应力张量相同的形式，p是静压，非各向同性, 偏应力张量 dij 完全由流体运动引起。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Mechanical energy (Unit J) | 机械能（单位J） |
The sum of kinetic energy and potential energy for an object or a mechanical system, including the energy stored in springs, etc. 物体或机械系统的动能和势能之和，包括储存在弹簧等中的能量。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Rated load (Unit N) | 额定负荷（单位：N） |
The maximum load that a structure or component has been designed to carry. 结构或部件设计承受的最大荷载。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| Fastener manufacturer | 紧固件制造商 |
An organization that fabricates raw steel into a fastener meeting specified standards. 将生钢加工成符合规定标准的紧固件的组织。 |
| Scuffing | 擦伤 |
A form of adhesive wear that produces superficial scratches or a high polish on the rubbing surfaces. It is observed most often on inadequately lubricated parts. 粘着磨损的一种形式，在摩擦表面上产生表面划痕或高度抛光。通常在润滑不足的零件上观察到。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Dynamic compressor | 动态压缩器 |
A machine, such as a centrifugal or axial compressor, that compresses a gas by rotational rather than reciprocating motion. 一种机器，例如离心式或轴流式压缩机，通过旋转而不是往复运动来压缩气体。 |
| Fine pitch | 细牙螺纹 |
Fine pitch threads are often used within the automotive industry. They are more easily tapped into harder materials and have less tendency to loosen. 细螺距螺纹通常用于汽车行业。它们更容易被敲入较硬的材料中，并且不太容易松动。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Cheese head | 圆柱头 |
A cylindrical head on a screw or bolt. For driving, it may be slotted, or hexagonally recessed. 螺钉或螺栓上的圆柱头。为了驱动，它可以是开槽的，也可以是六角形的。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Strain energy | 应变能 |
A measure of the energy absorption characteristics of a material determined by measuring the area under the stress-strain diagram. 通过测量应力-应变图下的面积确定的材料能量吸收特性的度量。 |
| Galilean transformation | 伽利略变换 |
In steady fluid flow, the addition or subtraction of a constant velocity to the entire flowfield, e.g. so that flow can be considered relative to a moving object or flow feature, such as a shock wave. 在稳定的流体流动中，对整个流场增加或减少恒定速度，例如，可以考虑相对于移动物体或流动特征（例如冲击波）流动。 |
| Apparent area of contact | 表观接触面积 |
In tribology, the area of contact between two solid surfaces defined by the boundaries of their macroscopic interface. 在摩擦学中，两个固体表面之间的接触区域由其宏观界面的边界定义。 |
| Acid rain | 酸雨 |
Any form of precipitation, including rain, snow, sleet, fog, dew, and particulates, which contains higher than normal levels of sulfuric and nitric acids. These acids result from natural and man-made emissions of sulfur dioxide and oxides of nitrogen, respectively. Acid soot consists of unburned carbon particles, typically larger than 10 μm, in the atmosphere contaminated with sulfuric acid. The particles result from poor combustion of fossil fuels. 任何形式的降水，包括雨、雪、雨夹雪、雾、露水和颗粒物，其中含有高于正常水平的硫酸和硝酸。这些酸分别来自二氧化硫和氮氧化物的自然排放和人为排放。酸烟灰由未燃烧的碳颗粒组成，通常大于10微米，在被硫酸污染的大气中。这些颗粒是化石燃料燃烧不良造成的。 |
| Valve spring | 气门弹簧 |
The spring that restores a valve to its closed position after having been opened, and is also intended to prevent valve bounce. 在阀门打开后将其恢复到关闭位置的弹簧，也用于防止阀门反弹。 |
| Vacuum annealing | 真空退火 |
Annealing carried out at subatmospheric pressure. 在低于大气压的压力下进行退火。 |
| Remaining stress | 残留应力 |
The stress remaining at a given time during a stress-relaxation test. See also stress relaxation. 在应力松弛试验期间在给定时间内剩余的应力。参见压力松弛。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Thermal reactor | 热反应器 |
An enlarged exhaust manifold bolted directly to the cylinder head of a piston engine, in which the oxidation of carbon monoxide and unburned hydrocarbons in the exhaust gas is enhanced. 一种扩大的排气歧管，直接用螺栓固定在活塞式发动机的气缸盖上，其中一氧化碳和未燃烧碳氢化合物的氧化作用增强。 |
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Cooling coil | 冷却盘管 |
A simple heat exchanger consisting of a coiled tube, typically of copper or stainless steel, through which is circulated a coolant such as a refrigerant, chilled water, or water mixed with ethylene glycol. Applications include air conditioning, process cooling, and refrigeration. 一种简单的热交换器，由通常由铜或不锈钢制成的盘管组成，冷却剂如制冷剂、冷冻水或与乙二醇混合的水通过盘管循环。应用包括空调、工艺冷却和制冷。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Press quenching | 压淬 |
A quench in which hot dies are pressed and aligned with a part before the quenching process begins. Then the part is placed in contact with a quenching medium in a controlled manner. This process avoids part distortion. 一种淬火方法，在淬火过程开始之前，热模具被压制并与零件对齐。然后将零件以受控方式放置在与淬火介质接触的位置。该过程避免了零件变形。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Nonlinear behavior | 非线性行为 |
A fastener or joint system is said to exhibit nonlinear behavior when the relationship between the External load on the joint and deformation of the parts is nonlinear, or when the relationship between increasing Preload and deformation is nonlinear. 当接头上的外部载荷与零件变形之间的关系是非线性的，或者当增加的预载荷与变形之间的联系是非线性的时，可以说紧固件或接头系统表现出非线性行为。 |
| Torque motor | 力矩电机 |
A type of induction motor that can apply a steady torque even when prevented from rotating. 一种感应电动机，即使被阻止旋转也能施加稳定的转矩。 |
| Grub screw | 平头螺丝 |
A short headless screw with a recess at one end to receive a screw driver or key. 一种短的无头螺钉，一端有一个凹槽，用于安装螺丝刀或钥匙。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Vibration-testing machine (vibrator) | 振动试验机（振动器） |
Any machine that subjects components or systems to vibration at known amplitudes and frequencies in order to determine the response. vibratory equipment Vibrating process equipment, such as shakers, used to separate small and large particles, or feeders to supply particulate or granular material that may otherwise clog. 使部件或系统以已知振幅和频率振动以确定响应的任何机器。振动设备振动工艺设备，如用于分离小颗粒和大颗粒的振动筛，或用于供应可能堵塞的颗粒或粒状材料的给料机。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Decarburization | 脱碳 |
Loss of carbon from the surface layer of a carbon-containing alloy due to reaction with one or more chemical substances in a medium that contacts the surface. 由于与接触表面的介质中的一种或多种化学物质发生反应，含碳合金表面层的碳损失。 |
| Turning | 车削 |
Turning is a machining process for generating external surfaces of revolution by the action of a cutting tool on a rotating workpiece, usually in a lathe. The rotation of a workpiece held against a cutting tool in a lathe to produce components with a circular cross section. 车削是一种机械加工过程，通常在车床上，通过刀具对旋转工件的作用产生旋转外表面。在车床中，工件靠着刀具旋转，以生产具有圆形横截面的部件。 |
| Impact strength 1. (Unit Pa) | 冲击强度1.（单位Pa） |
The stress to cause failure (by yielding or fracture) under conditions of high strain rate. 2. (Unit J) A term sometimes used to describe the energy required to fracture a specimen in a Charpy or Izod impact test even though the unit is not that of strength. 在高应变率条件下导致失效（通过屈服或断裂）的应力。2.（单位J）有时用于描述在夏比或悬臂梁式冲击试验中使样品断裂所需的能量，即使单位不是强度单位。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Scale effect | 规模效应 |
The change in behaviour with size of a material, component, or structure. For example, cube-square scaling where one element changes with volume and another with area, as in the range of a projectile or ship, droplet formation, and fracture mechanics. 性能随材料、部件或结构尺寸的变化。例如，立方体平方比例，其中一个元素随体积变化，另一个元素因面积变化，如在射弹或飞船的射程、液滴形成和断裂力学中。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| Tension | 拉伸 |
The force or load that produces elongation. 1. The condition in a bar, belt, cable, spring, string, wire, etc. that is being pulled from either end. 2. (tensile force) (unit N) The force associated with tension as in (1). It is measured by a tension meter. 伸长力产生伸长的力或载荷。1.从两端拉出的杆、带、电缆、弹簧、线、线等的状态。2.（张力）（单位N）与张力相关的力。 |
| Angström (Å) | 昂斯特罗姆（Å） |
An obsolete (non-SI) unit of length, sometimes still employed for atomic and crystallographic measurements. The conversion to SI is 1 Å = 10−10 m. 一种已被淘汰的（非SI）长度单位，有时仍用于原子和晶体学测量。转换为SI为1Å=10-10m。 |
| Specific weight (γ) (Unit N/m³) | 比重（γ）（单位：N/m³） |
The weight per unit volume of a substance: if W is the weight of a volume of the substance, ρ is its density, and g is the acceleration due to gravity, γ = W/ = ρg. 物质单位体积的重量：W是物质体积的重量，ρ是其密度，g是重力引起的加速度，γ=W/=ρg。 |
| Scleroscope hardness test | 反跃式硬度试验 |
A dynamic indentation-hardness test using a calibrated instrument that drops a diamond-tipped hammer from a fixed height onto the surface of the material being tested. The height of rebound of the hammer is a measure of the hardness of the material. Also known as Shore hardness test. 使用校准仪器的动态压痕硬度测试，该仪器将金刚石锤从固定高度落在被测材料表面上。锤的回弹高度是材料硬度的一种度量。也称为肖氏硬度测试。 |
| Water hammer | 水锤 |
The reflected pressure surge that occurs in a liquid flowing through a pipe, usually as a consequence of sudden closure of a valve. The surge may cause the pipe to vibrate and a hammering noise to be heard. Key factors affecting the surge amplitude are the compressibility of the liquid (especially if it contains undissolved gas) and the elasticity of the pipe wall. 在流经管道的液体中发生的反射压力波动，通常是阀门突然关闭的结果。浪涌可能导致管道振动，并听到锤击噪音。影响喘振幅度的关键因素是液体的可压缩性（特别是当其含有未溶解气体时）和管壁的弹性。 |
| Blade compressor | 叶片式压缩机 |
An oil-free, double-acting rotary compressor in which an angled blade attached to the inner surface of a rotating housing passes through a slot in a disk rotating about an axis perpendicular to that of the housing but offset from it. Air enters through apertures in the housing and leaves through a port in the housing. 一种无油双作用旋转式压缩机，其中连接到旋转外壳内表面的倾斜叶片穿过圆盘上的槽，该槽绕垂直于外壳的轴旋转，但偏离外壳。空气通过壳体中的孔进入，并通过壳体的端口离开。 |
| Core | 核心 |
In a ferrous alloy prepared for case hardening, that portion of the alloy that is not part of the case . Typically considered to be the portion that (a) appears light on an etched cross section, (b) has an essentially unaltered chemical composition, or (c) has a hardness, after hardening, less than a specified value. 在为表面硬化而制备的铁合金中，合金中不属于表面的那部分。通常被认为是（a）在蚀刻横截面上看起来很轻，（b）化学成分基本不变，或（c）硬化后硬度低于规定值的那部分。 |
| Mean value | 平均值 |
The average value of a number of data points. Computed by dividing the sum of all data by the number of data points. 多个数据点的平均值。通过将所有数据的总和除以数据点的数量来计算。 |
| Lockbolt | 锁紧螺栓 |
A fastener which bears a superficial resemblance to a bolt, but which engages a collar (instead of a nut) with annular grooves (instead of threads). The collar is swaged over the grooves on the male fastener to develop preload. 表面上类似于螺栓的紧固件，但与环槽（而不是螺纹）接合的轴环（而不是螺母）。套环在阳紧固件上的凹槽上锻造，以产生预紧力。 |
| Maximum stress (Smax) | 最大应力（Smax） |
The stress having the highest algebraic value in the stress cycle, tensile stress being considered positive and compressive stress negative. The nominal stress is used most commonly. 在应力循环中具有最高代数值的应力，拉应力被认为是正的，压应力被认为是负的。名义应力是最常用的。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Coefficient of restitution (e) | 回弹系数（e） |
The ratio of the relative velocity of two colliding bodies after collision to that before. In perfectly elastic collisions e = 1; when all the impact energy is dissipated, e = 0. 两个碰撞体在碰撞后与碰撞前的相对速度之比。在完全弹性碰撞中e=1；当所有的冲击能量都消散时，e=0。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Available resource | 可用资源 |
(total resource) (Unit J) The total annual energy theoretically available from a renewable-energy source, such as ocean waves, the wind, or the total incident solar energy. （总资源）（单位J）理论上可从可再生能源（例如海浪、风或总入射太阳能）获得的年度总能量。 |
| Hydraulic air compressor | 液压空气压缩机 |
1. A compressor powered by a hydraulic motor. 2. A device in which air is compressed as a result of being entrained in water flowing in a downcomer pipe. The compressed air is released in a chamber at the bottom of the pipe. 1. 由液压马达驱动的压缩机。2.一种装置，其中空气由于夹带在降液管中流动的水中而被压缩。压缩空气在管道底部的腔室中释放。 |
| Closed-die forging | 闭模锻造 |
The forming of a workpiece by compression within a pair of dies having the female form of the component to be manufactured (closed dies), superfluous metal being expelled as flash where the dies meet. 在一对具有待制造部件的阴模的模具（闭模）内通过压缩形成工件，多余的金属在模具相遇处作为飞边排出。 |
| Frequency | 频率 |
(temporal frequency, f) (Unit Hz) The number of cycles per second in an oscillation or the repetition rate for a cyclic process. （时间频率，f）（单位Hz）振荡中每秒的周期数或循环过程的重复率。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Slug | 猛击 |
1. A starting workpiece for forging and similar operations, such as a length of wire or rod to make a bolt blank on which a thread can be rolled or cut. 2. (geepound) An obsolete imperial (non-SI) unit of mass, being the mass which under an acceleration of one foot per second squared gives a force of one pound-force. The conversion to SI is 1 slug = 14.593 902 94 kg. 3. A large-scale flow structure which occurs in the transition from laminar to turbulent flow in a pipe. 1.一种用于锻造和类似操作的起始工件，如用于制造螺栓毛坯的一段线材或棒材，在该毛坯上可以轧制或切割螺纹。2.（吉磅）一种已被淘汰的英制（非国际单位制）质量单位，在一英尺/秒平方加速度下产生一磅力的质量。转化为SI国际单位制的转化率为1slug=14.59390294kg。3.一种大规模流动结构，其发生在管道中从层流到湍流的过渡中。 |
| Dynamic modulus | 动态模量 |
The ratio of stress to strain under cyclic conditions (calculated from data obtained from either free or forced vibration tests, in shear, compression, or tension). 循环条件下的应力与应变之比（根据在剪切、压缩或拉伸中的自由或强制振动测试中获得的数据计算得出）。 |
| Offset modulus | 补偿模量 |
The ratio of the offset yield stress to the extension at the offset point (plastics). 偏移屈服应力与偏移点（塑料）处延伸的比率。 |
| Creep | 蠕变 |
The slow, plastic deformation of a body under heavy loads. Time-dependent plasticity. Time-dependent and permanent deformation of material under constant load or stress. The strain increases with time at a rate that increases with increasing temperature. Creep can lead to large strain and eventual failure, and so limit the lifetime of components subjected to load at high temperature. Creep in metals becomes significant at homologous temperatures in excess of about 0.4, e.g. 1200°C for tungsten, 504°C for titanium, 450°C for iron, and 100°C for aluminium. 物体在重载荷下缓慢的塑性变形，随时间变化的可塑性，材料在恒定载荷或应力下随时间变化的永久变形。应变随时间以随温度升高而增加的速率增加。蠕变可能导致大应变和最终失效，从而限制部件在高温下承受载荷的寿命。当同源温度超过约0.4℃时，金属蠕变变得显著，例如钨为1200℃，钛为504℃，铁为450℃，铝为100℃。 |
| Preload | 预载 |
The tension created in a threaded fastener when the nut is first tightened. Often used interchangeably, but incorrectly, with Working load or bolt force or bolt tension 第一次拧紧螺母时螺纹紧固件中产生的张力。经常与工作载荷或螺栓力或螺栓张力互换使用但容易使用不当。 |
| Water quenching | 水淬 |
A quench in which water is the quenching medium. The major disadvantage of water quenching is its poor efficiency at the beginning or hot stage of the quenching process. 以水为淬火介质的淬火。水淬的主要缺点是在淬火过程的开始或热阶段效率低。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Coalescence | 聚结 |
Growth of grains at the expense of the remainder by absorption or the growth of a phase or particle at the expense of the remainder by absorption or reprecipitation. 通过吸收以牺牲剩余为代价的晶粒的生长或以通过吸收或再沉淀为代价的以剩余为代价的相或颗粒的生长。 |
| Width across flats | 平面宽度 |
A principal dimension of nuts, or of bolt heads. Work hardening The slight increase in hardness and strength produced when a body is loaded past its yield point. Also called strain hardening. 螺母或螺栓头的主要尺寸。加工硬化：当物体被加载超过其屈服点时，硬度和强度略有增加。也称为应变硬化。 |
| Abradant | 研磨剂 |
The differently sized grits of hard materials such as emery employed for grinding, polishing, etc. The abrasive grade is determined by the grit size (grit number) originally related to the hole sizes in wire sieves. 用于研磨、抛光等的硬质材料（例如金刚砂）的不同尺寸粒度。磨料等级由最初与金属丝筛孔尺寸相关的粒度（粒度数）决定。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Shear strength (Unit Pa) | 抗剪强度（单位Pa） |
The maximum shear stress that can be withstood by a material either (a) before plasticity occurs or (b) before rupture. 材料在（a）塑性发生之前或（b）断裂之前能够承受的最大剪切应力。 |
| Barometer | 气压计 |
An instrument used to measure atmospheric pressure. An instrument for measuring atmospheric pressure. There are two main types – the mercury barometer, and the aneroid barometer. 用于测量大气压力的仪器。有两种主要类型——水银气压计和无液气压计。 |
| Constant-force spring | 恒力弹簧 |
A spring that has the same restoring force regardless of displacement. The most common type takes the form of a coiled strip that, owing to tight coiling during manufacture, is pre-stressed (a steel measuring tape is an example). The uncoiling force is approximately constant as the change of curvature of the strip is approximately constant. Not to be confused with a clockwork spring from which power can be obtained. 无论位移如何，具有相同恢复力的弹簧。最常见的类型是卷绕带，由于制造过程中的紧密卷绕，该卷绕带是预应力的（钢卷尺就是一个例子）。随着带材曲率的变化近似恒定，开卷力近似恒定。不要与可获得动力的发条弹簧混淆。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| SI system | SI国际单位制 |
SI is an abbreviation of Système International d’Unités, i.e., the international unit measurement system – an internationally established system of measurement units built on older metric systems. SI是Système International d‘Unités的缩写，即国际单位计量系统——一种基于旧公制的国际公认计量单位系统。 |
| Serrations | 锯齿 |
A row of notches or tooth-like projections on an edge or surface. On an engineering drawing, serrations on the surface of a circular component are shown over about 60° of arc. 边缘或表面上的一排凹口或齿状突起。在工程图纸上，圆形部件表面的锯齿超过约60°的圆弧。 |
| Depth gauge | 深度计 |
1. A precision instrument, typically consisting of a machine-divided steel rule passing through a hardened-steel cross head, used to measure the depths of slots, holes, shoulders, projections, etc. 2. A device used by divers to indicate the water depth. 1. 一种精密仪器，通常由穿过硬化钢十字头的机器分割钢尺组成，用于测量槽、孔、肩部、突起等的深度。 2. 潜水员用来指示深度的装置水深。 |
| Prevailing torque | 有效扭矩 |
Torque required to run a nut down against the joint when some obstruction, such as a plastic insert in the threads, or a noncircular thread, or other, has been introduced to help the fastener resist vibration loosening. Prevailing torque, unlike normal torque on a nut or bolt, is not proportional to the Preload in the fastener. 当引入了一些障碍物（如螺纹中的塑料插件或非圆螺纹或其他障碍物）以帮助紧固件抵抗振动松动时，将螺母向下压靠接头所需的扭矩。与螺母或螺栓上的正常扭矩不同，主要扭矩与紧固件中的预载不成比例。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Cold working | 冷加工 |
The plastic deformation of a metal, by rolling (cold rolling), drawing, forging (cold forging), etc. at a temperature well below its recrystallization temperature, which results not only in permanent shape change but also increase in strength and loss of ductility owing to work-hardening. 金属在远低于其再结晶温度的温度下通过轧制（冷轧）、拉拔、锻造（冷锻）等方式发生塑性变形，这不仅会导致永久的形状变化，还会增加强度并降低延展性由于加工硬化。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Inch-pound force/inch² | 英寸磅力/英寸² |
A non-SI unit for the specific work of fracture (fracture toughness). The conversion to SI is 1 in.lbf/in² = 1.751 268 × 102 J/m². 用于特定断裂功（断裂韧性）的非国际单位制单位。到SI的转换为1英寸。lbf/in²=1.751268×102J/m²。 |
| Black oxide | 黑色氧化物 |
A black finish on a metal produced by immersing it in hot oxidizing salts or salt solutions. 通过将金属浸入热氧化盐或盐溶液中产生的黑色饰面。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Hardness test | 硬度测试 |
1. Any of various tests in which different hard indenters are forced into the surface of a solid under different loads to give permanent impressions, the pressure to cause which being called the hardness. The Brinell test employs a spherical indenter; the Vickers test a square-based pyramid. The relation between indentation hardness H and uniaxial yield stress Y is approximately H = (2.5 ~ 3.0)Y. Originally hardnesses were given in kg/mm² but now are often given in Pa. 2. The tests for scratch and file hardness relate either to one material being able to mark another (Mohs hardness scale for minerals), or to the size of groove produced by a rigid indenter slid under load across a surface. 3. Rebound hardness concerns the height of rebound of a dropped indenter, or an indenter at the end of a pivoted arm, having struck a surface. 1.任何一种试验，其中不同的硬压头在不同载荷下压入固体表面，以产生永久压痕，所产生的压力称为硬度。布氏试验采用球形压头；维氏硬度测试是一个方形金字塔。压痕硬度H与单轴屈服应力Y之间的关系约为H=（2.5~3.0）Y。最初硬度以kg/mm²为单位，但现在通常在Pa.2中给出。划痕和锉刀硬度测试要么与一种材料能够标记另一种材料（矿物的莫氏硬度标度）有关，要么与刚性压头在表面上滑动产生的凹槽大小有关。3.回弹硬度涉及掉落压头或旋转臂端部压头撞击表面后的回弹高度。 |
| Boiler and Pressure Vessel Code | 锅炉和压力容器规范 |
A large and complex document, maintained and published by the American Society of Mechanical Engineers. The code 一份庞大而复杂的文件，由美国机械工程师协会出版和维护。 |
| Hypereutectoid alloy | 过共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of alloying element compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共晶的合金系统中，合金成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Failure | 失效 |
The result when a body, component, or structure is incapable of performing the task for which it was designed. The term is often used without reference to what causes failure, such as fracture, buckling, excessive deformation, wear, or erosion. Failure criteria (failure theories, theories of strength) are mathematical expressions for the combinations of stress, strain, or strain energy at which materials fail, which are employed in design to dimension components. 主体、部件或结构无法执行其设计任务时的结果。该术语通常未提及导致失效的原因，如断裂、屈曲、过度变形、磨损或侵蚀。失效准则（失效理论、强度理论）是材料失效时应力、应变或应变能组合的数学表达式，用于部件尺寸设计。 |
| Cone clutch | 锥形离合器 |
A friction clutch in which an internal cone moves axially in or out of engagement with an external cone. One or both surfaces is lined with high-friction material. 一种摩擦离合器，其中内锥与外锥轴向啮合或脱离啮合。一个或两个表面衬有高摩擦材料。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Residual strength (Unit N) | 剩余强度（单位：N） |
The strength of a damaged body containing defects induced by microcracking, thermal shock, etc. 包含由微裂纹、热冲击等引起的缺陷的受损体的强度。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Full hard | 全硬化 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state beyond which the material can no longer be formed by bending. In specifications, a full hard temper is commonly defined in terms of minimum hardness or minimum tensile strength (or, alternatively, a range of hardness or strength) corresponding to a specific percentage of cold reduction following a full anneal. For aluminum, a full hard temper is equivalent to a reduction of 75% from dead soft ; for austenitic stainless steels, a reduction of about 50 to 55%. 有色金属合金和一些铁合金的回火状态，大致对应于冷加工状态，超过该状态，材料就不能再通过弯曲形成。在规范中，完全硬质回火通常定义为与完全退火后的特定冷压下率百分比相对应的最小硬度或最小抗拉强度（或者，硬度或强度范围）。对于铝来说，完全硬回火相当于从极软状态减少75%；对于奥氏体不锈钢，减少约50%至55%。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Nominal stress | 名义应力 |
The stress at a point calculated on the net cross section by simple elasticity theory without taking into account the effect on the stress produced by stress raisers such as holes, grooves, fillets, etc. 通过简单弹性理论在净截面上计算的点处的应力，不考虑孔、槽、圆角等应力提升器产生的应力影响。 |
| Thermoelectric junction | 热电结 |
A welded, soldered, or twisted connection between the ends of two wires of dissimilar metals, as in a thermocouple. 两根不同金属线的末端之间的焊接、锡焊或绞合连接，如热电偶。 |
| Gibbs–Dalton law | 吉布斯-道尔顿定律 |
An extension of Dalton’s law of additive pressures to include the statement that the internal energy, enthalpy, and entropy of a mixture of gases are equal to the sum of the internal energies, enthalpies, and entropies the individual constituents would have if each existed alone at the same temperature and volume. Gibbs rule is that part of the law pertaining to entropy. 道尔顿附加压力定律的扩展，包括以下陈述：气体混合物的内能、焓和熵等于各个成分单独存在时的内能、焓和熵之和。相同的温度和体积。吉布斯定律是与熵有关的定律的一部分。 |
| Archimedes screw | 阿基米德螺旋泵 |
A machine which comprises a rotating helical blade inside a closefitting tube, which may be used to pump liquids, slurries (such as sewage), granular materials, etc. If water flows into the top of an inclined or vertical Archimedes screw, the screw will rotate and can be used to drive an electrical generator. 一种机器，它在紧密的管子内包含一个旋转的螺旋叶片，可用于泵送液体、泥浆（如污水）、颗粒材料等。如果水流入倾斜或垂直的阿基米德螺杆的顶部，螺杆将旋转，可用于驱动发电机。 |
| Stress-intensity factor | 应力强度因子 |
A scaling factor, usually denoted by the symbol K, used in linear-elastic fracture mechanics to describe the intensification of applied stress at the tip of a crack of known size and shape. At the onset of rapid crack propagation in any structure containing a crack, the factor is called the critical stress-intensity factor, or the fracture toughness. 一种标度因子，通常用符号K表示，在线弹性断裂力学中用于描述已知尺寸和形状的裂纹尖端施加应力的增强。在任何含有裂纹的结构中，裂纹快速扩展开始时，该因子称为临界应力强度因子，或断裂韧性。 |
| Hardness profile | 硬度分布 |
Hardness as a function of distance from a fixed reference point (usually from the surface). 硬度作为距固定参考点（通常距表面）的距离的函数。 |
| Slip band | 滑带 |
A group of parallel slip lines so closely spaced as to appear as a single line when observed under an optical microscope. 一组平行滑移线，间距如此之近，以至于在光学显微镜下观察时显示为一条直线。 |
| Allowable stress design | 许用应力设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Purposely underestimates the strengths of bolts and joint materials to introduce safety factors into the design of structural steel joints. It is an alternative to the more recently defined load and resistance factor design procedure. 结构连接研究委员会为AISC制定的设计程序。故意低估螺栓和接头材料的强度，以便在结构钢接头的设计中引入安全系数。它是最近定义的荷载和阻力系数设计程序的替代方法。 |
| Fatigue test | 疲劳测试 |
A method for determining the range of alternating (fluctuating)stresses a material can withstand without failing. 一种确定材料可以承受而不会失效的交变（波动）应力范围的方法。 |
| Flexural strength | 抗弯强度 |
The maximum stress in the outer fiber at the moment of crack or break. 断裂或断裂时刻外层纤维的最大应力。 |
| Macrodeviation | 宏观偏差 |
Errors from–irregular surface departures from the design profile, often caused by lack of accuracy or stiffness of the machine system. 不规则表面偏离设计轮廓的误差，通常是由于机器系统缺乏准确性或刚度造成的。 |
| Fog quenching | 雾淬 |
Quenching in a fine vapor or mist. 在细蒸汽或薄雾中淬火。 |
| Altitude chamber | 高空舱 |
(hypobaric chamber) A chamber in which conditions at different altitudes are simulated by a combination of appropriate pressures, temperatures and relative humidity. （低压舱）通过适当的压力、温度和相对湿度的组合来模拟不同高度条件的舱室。 |
| Grinding stress (Unit Pa) | 磨削应力（单位Pa） |
The residual stresses left in the surface of a component after grinding, owing to non-uniform cooling from the high surface temperatures produced. 由于产生的高表面温度造成的不均匀冷却，磨削后留在部件表面的残余应力。 |
| Blueing | 发蓝 |
Application of blue dye (‘engineers’ blue’) to identify high spots on surfaces in contact, or for marking out. 应用蓝色染料（“工程师蓝”）来识别接触表面上的高点，或用于标记。 |
| Torque arm | 扭力臂 |
A bar fixed at one end used to resist torque applied at the other, for example by an electric drill. 固定在一端的杆，用于抵抗施加在另一端的扭矩，如电钻。 |
| Temper embrittlement | 回火脆化 |
Brittleness that results when certain steels are held within, or are cooled slowly through, a certain range of temperature below the transformation range. The brittleness is manifested as an upward shift in ductile-to-brittle transition temperature but only rarely produces a low value of reduction in area in a smooth-bar tension test of the embrittled material. The anomalous reduction in toughness of martensitic stainless steels when tempered in the range 370–600°C. Embrittlement of alloy steels caused by holding within or cooling slowly through a temperature range just below the transformation range. Embrittlement is the result of the segregation at grain boundaries of impurities such as arsenic, antimony, phosphorus, and tin; it is usually manifested as an upward shift in ductile-to-brittle transition temperature. Temper embrittlement can be reversed by retempering above the critical temperature range, then cooling rapidly. 当某些钢保持在低于转变范围的某一温度范围内或缓慢冷却时产生的脆性。脆性表现为延性到脆性转变温度的向上移动，但在脆性材料的平滑棒材拉伸试验中，很少产生较小的面积减小值。马氏体不锈钢在370–600°C范围内回火时的韧性异常降低。合金钢的脆化是由于在低于转变范围的温度范围内保持或缓慢冷却而引起的。脆化是杂质（如砷、锑、磷和锡）在晶界处偏析的结果；它通常表现为韧脆转变温度的上升。回火脆化可以通过在临界温度范围以上重新回火，然后快速冷却来逆转。 |
| Critical crack length (Unit m) | 临界裂纹长度（单位米） |
The crack length at which a given stress applied to a body will result in crack propagation and fracture. 施加到物体上的给定应力将导致裂纹扩展和断裂的裂纹长度。 |
| Diffusion coating | 扩散涂层 |
Coating on metal for corrosion- and/or oxidation-resistance. Coatings are produced by heating a metal in contact with an alloy in powder, liquid, or gaseous form at elevated temperature such that atoms of the coating diffuse into the substrate. Examples include chromium, aluminium, or silicon on substrates such as nickel-based superalloys, steels, and refractory metals. 金属上的防腐和/或抗氧化涂层。涂层是通过在高温下加热与粉末、液体或气体形式的合金接触的金属，从而使涂层的原子扩散到基体中而产生的。实例包括基底上的铬、铝或硅，如镍基高温合金、钢和耐火金属。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Pressure regulator | 压力调节器 |
(pressure-regulating valve) A device installed in a pneumatic or gas system to maintain the downstream pressure at the required level. （压力调节阀）安装在气动或气体系统中以将下游压力保持在所需水平的装置。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Bucket | 吊桶 |
1. A cup-shaped vane with a central dividing ridge attached to the periphery of the runner of an impulse water turbine such as a Pelton turbine. 2. A rotor blade in a compressor or turbine. 1.一种杯形叶片，所述杯形叶片具有附接到冲击式水轮机（例如冲击式水轮机台）的转轮的外围的中央分隔脊。2.压缩机或涡轮机中的转子叶片。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Relaxed stress | 松弛应力 |
The initial stress minus the remaining stress at a given time during a stress-relaxation test. 在应力松弛试验期间，初始应力减去给定时间的剩余应力。 |
| Lead angle | 导角 |
The angle of the helix of a screw thread or worm thread. It is the measure of the inclination of a screw thread from a plane perpendicular to the axis of the screw. 螺纹或蜗杆螺纹的螺旋角。它是螺纹从垂直于螺钉轴线的平面的倾斜度的量度。 |
| Steam gauge | 汽压表 |
A pressure gauge used to measure gauge pressure in a line, boiler, cylinder, or other device operating with steam. 一种压力表，用于测量管道、锅炉、汽缸或其他与蒸汽一起工作的装置中的表压。 |
| Preload adjustments | 预载调整 |
Preloads may be applied directly by axial loading or indirectly by turning of the nut or bolt. When preload is applied by turning of nuts or bolts, a torsion load component is added to the desired axial bolt load. 预载荷可通过轴向载荷直接施加，或通过转动螺母或螺栓间接施加。当通过转动螺母或螺栓施加预载荷时，扭转载荷分量被添加到所需的轴向螺栓载荷中。 |
| Blank carburizing | 毛坯渗碳 |
Simulating the carburizing operation without introducing carbon. This is usually accomplished by using an inert material in place of the carburizing agent, or by applying a suitable protective coating to the ferrous alloy. 在不引入碳的情况下模拟渗碳操作。这通常通过使用惰性材料代替渗碳剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Profile | 轮廓 |
The shape of a cross section of an object, such as an aerofoil or cam. 物体的横截面形状，如机翼或凸轮。 |
| Cycle annealing | 循环退火 |
An annealing process employing a predetermined and closely controlled time-temperature cycle to produce specific properties or microstructures. 采用预定且严格控制的时间-温度循环来产生特定性能或微观结构的退火工艺。 |
| Air conditioning | 空调 |
The process of controlling the temperature and humidity in rooms, buildings, aircraft, passenger vehicles, etc. More generally it includes control of dust, levels of radiant heat, etc. 控制房间、建筑物、飞机、客运车辆等的温度和湿度的过程。更一般地说，它包括控制灰尘、辐射热水平等。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Heat-capacity rate (c) (Unit W/K) | 热容率（c）（单位W/K） |
For fluid flow in a duct with mass flow rate ṁ, the product ṁC where C is the specific-heat capacity, at constant pressure (CP) in the case of a gas. 对于质量流量为ṁ的管道中的流体流动，乘积ṁC其中C是比热容，在气体的情况下为恒定压力（CP）。 |
| Bolt stress (Unit Pa) | 螺栓应力（单位Pa） |
The axial tensile stress induced in a bolt by tightening. 通过拧紧在螺栓中产生的轴向拉应力。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| J-integral | J-积分 |
A mathematical expression describing a line or surface integral that encloses the crack front from one crack surface to the other, used to characterize the fracture toughness of a material having appreciable plasticity before fracture. The J-integral eliminates the need to describe the behavior of the material near the crack tip by considering the local stress-strain field around the crack front; JIc is the critical value of the J-integral required to initiate crack extension from a preexisting crack. 描述从一个裂纹表面到另一个裂纹正面的线或表面积分的数学表达式，用于表征断裂前具有可观塑性的材料的断裂韧性。J积分通过考虑裂纹前缘周围的局部应力应变场，无需描述裂纹尖端附近材料的行为；JIc是从先前存在的裂纹开始裂纹扩展所需的J积分的临界值。 |
| Pop rivet | 拉钉 |
A hollow rivet that enables a connexion to be made from one side only of an assembly. 一种空心铆钉，使连接只能从组件的一侧进行。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Torque meter | 扭矩计 |
An instrument for measuring torque using spring-loaded, piezoelectric, or strain-gauged devices. 使用弹簧加载、压电或应变测量装置测量扭矩的仪器。 |
| Wrinkling | 起皱 |
A wavy condition obtained in deep drawing of sheet metal, in the area of the metal between the edge of the flange and the draw radius. Wrinkling may also occur in other forming operations when unbalanced compressive forces are set up. 在金属板深冲过程中，在法兰边缘和拉深半径之间的金属区域内获得的波浪状状态。当设置不平衡压缩力时，在其他成形操作中也可能发生起皱。 |
| Aging treatment | 时效处理 |
Heat treatment aimed at age hardening; it comprises solution and precipitation treatments. 针对时效硬化的热处理；它包括溶液和沉淀处理。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| ASME | ASME |
The American Society of Mechanical Engineers. 美国机械工程师学会。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Finishing washer | 光制垫圈 |
A washer designed for use with countersunk screws. Used to enhance appearance in some applications. 设计用于沉头螺钉的垫圈。在某些应用中用于增强外观。 |
| Length of engagement | 啮合长度 |
It is the axial measurement within which the external and internal threads have theoretical contact. 它是外螺纹和内螺纹具有理论接触的轴向测量。 |
| Standardization | 标准化 |
1. National and international agreements for design, manufacture, materials, performance, practices, requirements, strength, etc. which ensure common results wherever an item is made and wherever used. 2. The manufacture of components so that interchangeability of parts during assembly of new, or repair of old, items is possible without ‘fitting’. 1.关于设计、制造、材料、性能、惯例、要求、强度等的国家和国际协议，确保在任何地方制造和使用物品都能产生共同结果。2.部件的制造，以便在装配新部件或维修旧部件时，无需“装配”即可实现部件的互换性。 |
| Dimension line | 尺寸线 |
A line on an engineering drawing with a numeral above it that shows the length of a feature, usually in millimetres. 工程图上的一条线，上面有一个数字，表示特征的长度，通常以毫米为单位。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Beta annealing | β退火 |
Producing a beta phase by heating certain titanium alloys in the temperature range of which this phase forms followed by cooling at an appropriate rate to prevent its decomposition. 通过在形成β相的温度范围内加热某些钛合金，然后以适当的速率冷却以防止其分解，从而产生β相。 |
| Materials selection | 材料选择 |
The process of selecting the most suitable material for a particular application. In the case of solid materials, it involves assessment of candidate materials in terms of their physical properties (density, elastic moduli, fracture toughness, yield strength, hardness, fatigue resistance, coefficient of thermal expansion, thermal conductivity, resistance to thermal shock, creep resistance, corrosion resistance, radiation resistance, etc), and such factors as the function of the final product, its shape, method of manufacture, required tolerances, number to be made, ease of inspection and quality control, cost, and design methodology employed. 为特定应用选择最合适材料的过程。对于固体材料，它涉及根据其物理特性（密度、弹性模量、断裂韧性、屈服强度、硬度、抗疲劳性、热膨胀系数、导热系数、抗热冲击性、抗蠕变性、耐腐蚀性、抗辐射性等）评估候选材料，以及诸如最终产品的功能、其形状、制造方法、所需公差、制造数量、检查和质量控制的容易程度、成本和采用的设计方法等因素。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Nanotechnology | 纳米技术 |
The science and engineering of materials that have been structured on length scales of 1–100 nm, resulting in modified physical properties owing to changes in the ratio of surface area to volume (atoms on surfaces having different symmetry from those in the bulk) and because many of the fundamental physical processes that underpin the properties of materials have a characteristic length scale of a few nm, so that alteration of microstructure at the nm level alters the bulk properties. 材料科学与工程，其结构长度为1-100nm，由于表面积与体积之比的变化（表面上的原子与体中的原子具有不同的对称性），并且支撑材料性质的许多基本物理过程具有几纳米的特征长度尺度，因此改变纳米级微观结构会改变体性质。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| Differential heating | 差动加热 |
Heating that intentionally produces a temperature gradient within an object such that, after cooling, a desired stress distribution or variation in properties is present within the object. 加热有意在物体内产生温度梯度，从而在冷却后，在物体内出现所需的应力分布或特性变化。 |
| Coated abrasive | 涂附磨具 |
An abrasive tool consisting of a flexible backing material, such as a woven cloth, paper or vulcanized fibre, a bond material, such as a glue or synthetic resin, and grit. 一种研磨工具，由柔性背衬材料（例如编织布、纸或硫化纤维）、粘合材料（例如胶水或合成树脂）和砂砾组成。 |
| Scratching | 刮擦 |
In tribology, the mechanical removal or displacement, or both, of material from a surface by the action of abrasive particles or protuberances sliding across the surfaces. 在摩擦学中，通过在表面上滑动的磨粒或突起的作用，材料从表面上的机械移除或移位，或两者兼而有之。 |