| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Verified loading range | 验证加载范围 |
For testing machines, the range of indicated loads for which the testing machine gives results within the permissible variation specified. 对于试验机，试验机在规定允许偏差范围内给出结果的指示载荷范围。 |
| Maraging steels | 马氏体时效钢 |
Very high-strength iron alloys named after ‘martensitic’ and ‘aging’. They contain nickel, chromium, cobalt, and molybdenum, and form martensite on air cooling with a strength of about 1 GPa. When reheated to about 500°C and aged for some hours, a room-temperature strength of some 2.4 GPa is reached. 以“马氏体”和“时效”命名的超高强度铁合金。它们含有镍、铬、钴和钼，在空气冷却下形成强度约为1GPa的马氏体。当再加热至约500°C并老化数小时时，室温强度达到约2.4GPa。 |
| Cap nut | 盖型螺母 |
A nut with a blind threaded hole, for example a dome nut to cover the end of a bolt. 带有盲螺纹孔的螺母，例如用于覆盖螺栓末端的圆顶螺母。 |
| Thermal efficiency | 热效率 |
The ratio, for a heat engine or thermodynamic cycle, of the net work output to the net heat input into the system. 对于热机或热力循环，净功输出与系统净热输入的比率。 |
| Rated flow (Unit m³/s or kg/s) | 额定流量（单位：m³/s或kg/s） |
In a hydraulic system or machine, the volume or mass flow rate a manufacturer specifies for a component as the maximum desirable for it to function as designed. 在液压系统或机器中，制造商为部件指定的体积或质量流量是其按设计运行所需的最大值。 |
| Interrupted quenching | 间断淬火 |
A quenching procedure in which the workpiece is removed from the first quench at a temperature substantially higher than that of the quenchant and is then subjected to a second quenching system having a different cooling rate than the first. 在该淬火过程中，工件在显著高于淬火剂的温度下从第一次淬火中取出，然后经受具有不同于第一次淬火的冷却速率的第二次淬火系统。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Screw pair | 螺旋副 |
Two links connected together to form a kinematic pair, in which the contacting surfaces are screw threads, so that their relative motion consists of rotation and sliding. 两个连杆连接在一起形成运动副，其中接触面为螺纹，因此它们的相对运动包括旋转和滑动。 |
| Joint | 关节接合处 |
The part of a robot arm permitting either rotational or translational motion. Each joint provides a single degree of freedom, and thus a minimum of six is required if the robot is to be able to position and orientate the end effector anywhere within the workspace. A joint is described by four parameters: the joint angle, joint offset, joint twist, and link length. The joint angle is the angle between an extrapolation of the previous link length and the present link length, measured positive anticlockwise in a plane normal to the joint axis. This is variable in a rotational joint and fixed in a translational joint. The joint offset is the distance between the link length for the previous link and that for the present link, measured along the joint axis. This is variable for a translational joint and fixed for a rotational joint. The joint twist for the nth joint is the angle between the axes of joints Jn and Jn+1, measured positive anticlockwise in a plane normal to the link length and viewed from the position of the Jn+1 joint. The link length is the mutually perpendicular distance between planes passing through the axes of joint Jn and Jn+1. Both the joint twist and link length are fixed in all joints. 机器人手臂上允许旋转或平移运动的部分。每个接合处都有自由度，如果机器人要能够在工作空间内的任何位置定位和定向末端执行器，则至少需要六个接合处具有自由度。关节接合处由四个参数描述：关节角度、关节偏移、关节扭曲和链接长度。关节角度是在垂直于关节轴的平面内逆时针测量的先前连杆长度和当前连杆长度的外推之间的角度。这在旋转关节中是可变的，在平移关节中是固定的。关节偏移是沿关节轴测量的前一个连杆和当前连杆的连杆长度之间的距离。这对于平移关节是可变的，对于旋转关节是固定的。第n个关节的关节扭曲是关节Jn和Jn+1轴之间的角度，在垂直于连杆长度的平面内逆时针测量，从Jn+2关节的位置观察。连杆长度是穿过关节轴Jn和Jn+1的平面之间相互垂直的距离。关节扭曲和连杆长度在所有关节中都是固定的。 |
| Plug gauge | 塞规 |
A steel gauge used to determine the dimension or dimensions of a hole. It may be straight or tapered, and is typically circular, but in principle can have any cross section. 用于确定孔的尺寸的钢制量规。它可以是直的或锥形的，通常是圆形的，原则上可以有任何横截面。 |
| Fine pitch | 细牙螺纹 |
Fine pitch threads are often used within the automotive industry. They are more easily tapped into harder materials and have less tendency to loosen. 细螺距螺纹通常用于汽车行业。它们更容易被敲入较硬的材料中，并且不太容易松动。 |
| Fastener testing | 紧固件测试 |
A determination or verification that the fastener meets its specification requirements. 确定或验证紧固件符合其规范要求。 |
| Available draught (Unit Pa) | 可用通风量（单位Pa） |
The reduced pressure of combustion gases in a furnace or boiler, either forced or due to the buoyancy of hot gases, which is used to draw in combustion air and remove products of combustion. 炉子或锅炉中燃烧气体的压力降低，无论是强制还是由于热气体的浮力，用于吸入燃烧空气并去除燃烧产物。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Atmometer | 气压计 |
(atmidometer, evaporimeter) An instrument that measures the rate of evaporation of water from a surface into the atmosphere. （湿度计，蒸发计）测量水从表面蒸发到大气中的速率的仪器。 |
| Quick coupling | 快速接头 |
(quick disconnect, fast coupling) A hose connection allowing rapid assembly or disassembly and comprising a socket and a plug incorporating a springloaded locking mechanism. （快速断开、快速连接）一种软管连接，允许快速组装或拆卸，包括插座和带有弹簧加载锁定机构的插头。 |
| Mechanical units | 机械单位 |
The units of physical quantities, the dimensions of which includemass, length, and time. 物理量的单位，其量纲包括质量、长度和时间。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Liquid nitriding | 液体氮化 |
A method of surface hardening in which molten nitrogen-bearing, fused-salt baths containing both cyanides and cyanates are exposed to parts at subcritical temperatures. 一种表面硬化方法，其中含有氰化物和氰酸盐的熔融含氮熔盐浴在亚临界温度下暴露于零件。 |
| Tracking problem | 跟踪问题 |
A control problem where the set point changes with time and thus the plant output must follow the changing set point. The opposite of a regulator problem. 一种控制问题，其中设定值随时间变化，因此设备输出必须遵循变化的设定值。与调节器问题相反。 |
| Heat tinting | 热着色 |
Coloration of a metal surface through oxidation by heating to reveal details of the microstructure. 通过加热氧化使金属表面着色，以揭示微观结构的细节。 |
| Stud | 螺柱 |
A rod having thread on both ends. A headless threaded fastener, threaded on both ends, with an unthreaded body in the middle section, or threaded from end to end. Used with two nuts, or with one nut and a tapped hole. A plain cylindrical piece having a threaded portion of suitable length at each end or a continuous thread over the entire length. One end is screwed into a machine or workpiece after which a second part is placed over the stud and held in place by a nut. 两端都有螺纹的杆。无头螺纹紧固件，两端有螺纹，中间部分有无螺纹主体，或从一端到另一端有螺纹。与两个螺母或一个螺母和一个螺纹孔一起使用。一种普通的圆柱形部件，其两端具有适当长度的螺纹部分，或在整个长度上具有连续螺纹。一端拧入机器或工件，然后将第二部分放在螺柱上，并用螺母固定到位。 |
| Brayton cycle | 布雷顿循环 |
(Joule cycle) An air standard cycle that is the ideal cycle for a gasturbine engine. As shown on the diagram of pressure (p) ʋs specific volume (ʋ), it consists of four internally reversible processes: isentropic compression in a compressor (1–2), isobaric heat addition in a combustor (2–3), isentropic expansion in a turbine (3–4) and isobaric heat rejection. The cycle can be extended to include regeneration, reheating, and intercooling. （焦耳循环）一种空气标准循环，是燃气轮机发动机的理想循环。循环可以扩展到包括再生、再热和中冷。 |
| Taper pins | 圆锥销 |
A pin or peg of circular cross section that tapers along its length. Steel pins used for locating and holding the machine parts in position on a shaft. 沿其长度逐渐变细的圆形横截面的销钉或销钉。用于在轴上定位和固定机器零件的钢销。 |
| Shear modulus (G) | 剪切模量（G） |
The ratio of shear stress to the corresponding shear strain for shear stresses below the proportional limit of the material. Values of shear modulus are usually determined by torsion testing. Also known as modulus of rigidity. 对于低于材料比例极限的剪切应力，剪切应力与相应剪切应变之比。剪切模量值通常通过扭转试验确定。也称为刚度模量。 |
| Creep fatigue | 蠕变疲劳 |
The effects of combined creep and fatigue at high homologous temperatures in metals, and in other materials such as polymers having time-dependent behaviour. 金属和其他材料（例如具有时间相关行为的聚合物）在高同源温度下的组合蠕变和疲劳的影响。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Alloy | 合金 |
1. A metallic material composed of two or more elements, one of which is usually a metal to which the other elements are added, e.g. iron-carbon or aluminium-copper (binary alloy); nickel-chromium-iron (ternary alloy). 2. A plastic produced as a blend of two or more immiscible polymers. This results in material that cannot be achieved by polymerization. 1.由两种或多种元素组成的金属材料，其中一种通常是添加了其他元素的金属，例如铁碳或铝铜（二元合金）；镍铬铁（三元合金）。2.由两种或多种不混溶聚合物混合而成的塑料。这导致无法通过聚合获得的材料。 |
| Galling | 磨损 |
An extreme form of adhesive wear, in which large chunks of one part stick to the mating part (during sliding contact). 一种极端形式的粘着磨损，其中一个零件的大块粘在配合零件上（在滑动接触期间）。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Anelastic | 无弹性 |
Literally ‘not elastic’, but in practice used for materials that display timedependent recovery on unloading. 字面意思是“没有弹性”，但实际上用于在卸载时显示随时间恢复的材料。 |
| Seal | 密封件 |
A component which controls or prevents leakage of fluids into or out of parts of a machine. 控制或防止流体流入或流出机器部件的部件。 |
| Torsional stress | 扭转应力 |
The shear stress on a transverse cross section resulting from a twisting action. 扭转作用在横截面上产生的剪切应力。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Compound pendulum | 复摆 |
A rigid body free to swing about an axis. 可绕轴自由摆动的刚体。 |
| Cohesive zone | 凝聚力区 |
In fracture-mechanics modelling and simulation, the region at the crack tip over which an assumed traction (load-displacement) relation has to be overcome to permit initiation and propagation of a crack. 在断裂力学建模和模拟中，必须克服假定的牵引（载荷-位移）关系以允许裂纹萌生和扩展的裂纹尖端区域。 |
| Hexagon nut | 六角螺母 |
A nut having six sides and shaped like a hexagon. 六边形的螺母。 |
| Shear strain rate(Unit 1/s) | 剪切应变率（单位1/s） |
In the deformation of solids, the rate at which shear strain is applied in a test or changes with time in a loaded component or structure. 在固体变形中，在试验中施加剪切应变的速率，或在加载部件或结构中随时间变化的速率。 |
| Atom | 原子 |
The smallest unit of matter that has the properties of a chemical element. The simplest description of an atom (Bohr model) is of a compact nucleus surrounded by one or more orbiting electrons. 具有化学元素性质的最小物质单位。原子的最简单描述（玻尔模型）是由一个或多个轨道电子包围的致密原子核。 |
| Time quenching | 时间淬火 |
A term used to describe a quench in which the cooling rate of the part being quenched must be changed abruptly at some time during the cooling cycle. 用于描述淬火的术语，其中被淬火零件的冷却速率必须在冷却循环的某个时间突然改变。 |
| Positive-displacement machine | 正排量机 |
A machine that incorporates pistons, valves, etc. to ensure positive admission and delivery of a working fluid and prevent undesired reversal of flow. This class of machine incorporates all reciprocating compressors and expanders and some types of rotary compressor, the Roots blower, agear pump, a lobe pump, and a vane pump. 包含活塞、阀门等的机器，以确保工作流体的正向进入和输送，并防止不期望的反向流动。这类机器包括所有往复式压缩机和膨胀机以及一些类型的旋转压缩机、罗茨鼓风机、抽水机、凸轮泵和叶片泵。 |
| Hooke’s law | 胡克定律 |
Within the limit of proportionality, the extension of a material is proportional to the applied force. Approximately, it is the relationship between stress and strain in an elastic material when it is stretched. The law states that the stress (force per unit area) is proportional to the strain (a change in dimensions). The law, which holds only approximately and over a limited range, was discovered in 1676 by Robert Hooke. 在比例极限内，材料的延伸与所施加的力成比例。近似地说，它是弹性材料拉伸时应力和应变之间的关系。该定律指出，应力（单位面积的力）与应变（尺寸变化）成比例。该定律仅适用于有限的范围，由罗伯特·胡克于1676年发现。 |
| Bearing stress | 承受应力 |
The force per unit of bearing area. 每单位承载面积的力。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Displacement | 移位 |
The distance that a chosen measurement point on a cracked specimen displaces normal to the crack plane as the crack grows. 随着裂纹扩展，裂纹试样上选定的测量点垂直于裂纹平面位移的距离。 |
| Transmission | 传输 |
The system that transmits power and torque from a power source; for example a shaft, belts and pulleys, or a gear train. In the case of a motor vehicle, it includes the gearbox, clutch, propeller shaft, differential and final drive shafts. 从动力源传输功率和扭矩的系统；例如轴、皮带和滑轮或齿轮系。对于机动车辆，包括变速箱、离合器、传动轴、差速器和终传动轴。 |
| Dew point | 压力露点 |
The temperature and pressure at which a gas begins to condense to a liquid. 气体开始凝结成液体的温度和压力。 |
| Radial-flow compressor | 离心式压缩机 |
A compressor in which the working gas enters the machine axially and is compressed as it flows radially out through the impeller. 一种压缩机，其中工作气体轴向进入机器，并在通过叶轮径向流出时被压缩。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Translational joint | 平移铰 |
A robot joint where the controlled variable is straight line movement. 控制变量为直线运动的机器人关节。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Fin neck carriage bolt | 翼颈圆头方颈螺栓 |
A plain, circular, oval head bolt with two oppositely located fins to prevent rotation. 一种普通的圆形椭圆头螺栓，有两个相对的翼片以防止旋转。 |
| Springback | 回弹 |
The extent to which metal tends to return to its original shape or contour after undergoing a forming operation. 金属在经历成形操作后趋于恢复其原始形状或轮廓的程度。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Impact extrusion | 冲击挤压 |
The extrusion of separate components of soft metals whose properties permit the action to be performed quickly. 挤压单独的软金属组件，其特性允许快速执行操作。 |
| Hot working | 热加工 |
Plastic deformation of a metal, by rolling, drawing, forging, etc., at a temperature above its recrystallization temperature (in commercial alloys above about 40% of their melting points in kelvins) which results in permanent shape change but no increase in strength or loss of ductility. 金属通过轧制、拉拔、锻造等在高于其再结晶温度（在商业合金中高于其熔点的40%的开尔文）的温度下发生塑性变形，导致永久的形状变化，但不会增加强度或失去延展性。 |
| Expansion bolt | 膨胀螺栓 |
When a through bolt cannot be used for attaching a pipe hanger, bracket, or other part, to a wall or ceiling of brick or concrete, what are known as expansion bolts are often used. The body of an expansion bolt is divided and the arrangement is such that, when the head of the bolt is turned, the sections forming the body of the bolt are forced outward and against the wall of the hole which has been drilled into the brick, concrete, or stone, as the case may be. Bolts of this type are made in quite a variety of designs. The nominal size represents the diameter of the bolt proper and not the diameter of the casing or expansion member. 当不能使用贯穿螺栓将管道吊架、支架或其他部件连接到砖块或混凝土的墙壁或天花板时，通常使用所谓的膨胀螺栓。膨胀螺栓的主体是分开的，其布置方式是，当螺栓头转动时，形成螺栓主体的部分被强制向外并靠在已钻入砖、混凝土或石头中的孔壁上，视情况而定。这种类型的螺栓有多种设计。标称尺寸代表螺栓本身的直径，而不是套管或膨胀构件的直径。 |
| Crack | 裂缝 |
A thin fissure-like defect in a component or structure across which material continuity is lost and which reduces the strength of the body. 部件或结构中的细裂缝状缺陷，材料连续性丧失并降低了身体的强度。 |
| Abrasion | 磨损 |
The removal of surface material by the scratching action of hard particles, either deliberately (abrasive papers, abrasive cleaning, abrasive machining) or as a consequence of operation (wear). 通过硬质颗粒的刮擦作用去除表面材料，可以是故意的（砂纸、研磨清洁、研磨加工），也可以是操作的结果（磨损）。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Range of stress (Sr) | 应力范围（Sr） |
The algebraic difference between the maximum and minimum stress in one cycle—that is, Sr = Smax – Smin 一个循环中最大和最小应力之间的代数差，即Sr=Smax–Smin |
| Equation, long form | 方程，长格式 |
An equation which relates the torque applied to a bolt to the preload created in it, and involves fastener geometry and the coefficient of friction between mating surfaces. A theoretical equation based on rigid body mechanics and the assumption that the geometry of the fastener is perfectly described by blueprint dimensions. 将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来的方程，该方程涉及紧固件几何形状和配合面之间的摩擦系数。基于刚体力学和紧固件几何结构由蓝图尺寸完美描述的假设的理论方程。 |
| Torsion-bar suspension | 扭杆悬架 |
A type of motor-vehicle suspension in which one end of a torsion bar is rigidly fixed to the chassis while the other carries a lever to which are attached the components that carry a wheel. In a torsion-beam suspension, a beam connects the wheels on either side of the vehicle. 一种汽车悬架，其中扭力杆的一端刚性固定在底盘上，而另一端带有一个杠杆，杠杆上连接着承载车轮的部件。在扭转梁悬架中，梁连接车辆两侧的车轮。 |
| Coalescence | 聚结 |
Growth of grains at the expense of the remainder by absorption or the growth of a phase or particle at the expense of the remainder by absorption or reprecipitation. 通过吸收以牺牲剩余为代价的晶粒的生长或以通过吸收或再沉淀为代价的以剩余为代价的相或颗粒的生长。 |
| Raised-face flange | 凸面法兰 |
A flange which contacts its mating joint member only in the region in which the gasket is located. The flanges do not contact each other at the bolt circle. 仅在垫圈所在区域接触其配合接头构件的法兰。法兰在螺栓圆处不相互接触。 |
| Chilled castings | 冷铸件 |
Iron castings cooled at a rate that results in white iron (slow enough to avoid the formation of martensite, yet fast enough to prevent any silicon present from causing decomposition of cementite into iron and graphite). 铸铁件以产生白口铁的速度冷却（足够慢以避免形成马氏体，但足够快以防止任何存在的硅导致渗碳体分解成铁和石墨）。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Controlled cooling | 控制冷却 |
Cooling from an elevated temperature in a predetermined manner, to avoid hardening, cracking, or internal damage, or to produce desired microstructure or mechanical properties. 以预定方式从升高的温度冷却，以避免硬化、开裂或内部损坏，或产生所需的微观结构或机械性能。 |
| Elastic resilience | 弹性回弹 |
The amount of energy absorbed in stressing a material up to the elastic limit; or, the amount of energy that can be recovered when stress is released from the elastic limit. 向材料施加应力直至弹性极限所吸收的能量；或者当应力从弹性极限释放时可以恢复的能量值。 |
| Stainless steels | 不锈钢 |
Iron-base alloys that are highly resistant to corrosion in many environments. The predominant alloying element is chromium, which, like iron at room temperature, has BCC crystal structure. Corrosion resistance by passivation is achieved by the formation of chromium oxide on the steel surface. Nickel, which has FCC crystal structure, is another important addition for some steels. Other additions used to enhance properties include manganese, molybdenum, niobium, and titanium. There are several classes of stainless steel. 在许多环境中具有高度耐腐蚀性的铁基合金。主要的合金元素是铬，与室温下的铁一样，铬具有BCC晶体结构。钝化抗腐蚀性是通过在钢表面形成氧化铬来实现的。具有FCC晶体结构的镍是某些钢的另一种重要添加剂。其他用于增强性能的添加剂包括锰、钼、铌和钛。不锈钢的种类有好几种。 |
| Sigma phase | σ相 |
A hard, brittle, nonmagnetic intermediate phase with a tetragonal crystal structure, containing 30 atoms per unit cell, space group P42/mnm, occurring in many binary and ternary alloys of the transition elements. The composition of this phase in the various systems is not the same, and the phase usually exhibits a wide range in homogeneity. Alloying with a third transition element usually enlarges the field of homogeneity and extends it deep into the ternary section. 一种硬、脆、非磁性中间相，具有四方晶体结构，每单位晶胞含有30个原子，空间群P42/mnm，存在于许多过渡元素的二元和三元合金中。该相在各种系统中的组成不尽相同，并且该相通常表现出宽范围的均匀性。与第三过渡元素的合金化通常会扩大均匀性范围，并将其延伸到三元区。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Continuous precipitation | 连续沉淀 |
Precipitation from a supersaturated solid solution in which the precipitate particles grow by longrange diffusion without recrystallization of the matrix. Continuous precipitates grow from nuclei distributed more or less uniformly throughout the matrix. They usually are randomly oriented, but may form a Widmanstätten structure. 来自过饱和固溶体的沉淀，其中沉淀颗粒通过长程扩散生长而无需基质再结晶。连续析出物从在整个基体中或多或少均匀分布的核生长而来。它们通常是随机取向的，但可能形成魏氏结构。 |
| Hypereutectoid alloy | 过共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of alloying element compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共晶的合金系统中，合金成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Root diameter (Unit m) | 根部直径（单位：m） |
The diameter of the circle passing through the roots of teeth in gear teeth or screw threads. 穿过齿轮齿或螺纹中齿根的圆的直径。 |
| Breaking load (Unit N) | 断裂负荷（单位N） |
The load applied at some point to a component or structure which leads to fracture. The breaking stress (breaking strength) is the average stress at which a member breaks, given by the breaking load divided by the area over which it acts. 在某个点施加到导致断裂的部件或结构的载荷。断裂应力（断裂强度）是构件断裂时的平均应力，由断裂载荷除以其作用的面积给出。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Blind rivet | 盲孔铆钉 |
A rivet that enables a connexion to be made from one side only of an assembly. 一种铆钉，可以仅从组件的一侧进行连接。 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Population | 集合 |
The hypothetical collection of all possible test specimens that could be prepared in the specified way from the material under consideration. Also known as universe. 从所考虑的材料中以规定方式制备的所有可能试样的假设集合。也称为体系。 |
| Variance | 方差 |
A measure of the squared dispersion of observed values or measurements expressed as a function of the sum of the squared deviations from the population mean or sample average. 观测值或测量值的平方离散度的度量，表示为总体平均值或样本平均值的平方偏差之和的函数。 |
| Heat-capacity ratio (c*) | 热容量比（c*） |
A non-dimensional parameter that arises in the analysis of heat exchangers, defined as the ratio cMIN/cMAX where cMIN is the heat-capacity rate c for the fluid with the smaller value of c and cMAX the value for the fluid with the larger value of c. Different flow rates and specific-heat values give rise to different values for c. 热交换器分析中出现的无量纲参数，定义为比率cMIN/cMAX其中cMIN是流体的热容率c，c值较小，cMAX是流体的值具有较大的c值。不同的流速和比热值产生不同的c值。 |
| Wallner lines | Wallner线 |
A distinct pattern of intersecting sets of parallel lines, usually producing a set of V-shaped lines, sometimes observed when viewing brittle fracture surfaces at high magnification in an electron microscope. Wallner lines are attributed to interaction between a shock wave and a brittle crack front propagating at high velocity. Sometimes Wallner lines are misinterpreted as fatigue striations. 一组相交的平行线的独特图案，通常产生一组V形线，有时在电子显微镜下高倍观察脆性断裂表面时观察到。Wallner线归因于高速传播的冲击波和脆性裂纹前沿之间的相互作用。有时Wallner线被误解为疲劳条纹。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Radial flow | 径向流 |
radial flow Fluid flow for which the principal direction of flow is either radially inward or radially outward relative to an axial direction. 径向流动流体流动的主要方向是径向向内或径向向外流动。 |
| Plug | 螺塞 |
1. An object, usually tapered, used to block a hole to prevent fluid from escaping or flowing. 2. The central moveable part of a valve. 3. In the flow of a yield-stress fluid through a pipe or duct, the central region is often assumed to take the form of a plug with uniform axial velocity. 4. In thermoforming, a shaping tool that forces a heated plastic sheet into a female mould. 1.一种物体，通常为锥形，用于堵塞孔以防止流体逸出或流动。2.阀门的中心可移动部分。3.在屈服应力流体通过管道或管道的流动中，中心区域通常假定为具有均匀轴向速度的塞子形式。4.在热成型技术中，一种成型工具，将加热的塑料板压入阴模中。 |
| Standard hole | 标准孔 |
A hole in a workpiece bored to a specified tolerance where clearance with a shaft is accomplished by allowance on the shaft. A standard shaft is machined to a specified tolerance where clearance with a hole is accomplished by allowance on the hole. 工件上的孔，钻孔至规定公差，其中与轴的间隙通过轴上的余量来实现。标准轴加工至规定公差，其中与孔的间隙通过孔上的公差实现。 |
| Hypoeutectoid alloy | 亚共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of base metal compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共析的合金系统中，与共析成分相比，其成分具有过量母材的任何合金，并且其平衡微观结构包含一些共析结构。 |
| Trepanning | 开孔 |
Trepanning is a machining process for producing a circular hole or groove in solid stock, or for producing a disk, cylinder, or tube from solid stock, by the action of a tool containing one or more cutters (usually single-point) revolving around a center. 开孔是一种机械加工工艺，通过包含一个或多个围绕中心旋转的刀具（通常为单点）的作用，在实心坯料中制造圆孔或凹槽，或从实心坯料生产圆盘、圆柱体或管。 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Guided bend | 导向弯曲 |
The bend obtained by use of a plunger to force the specimen into a die in order to produce the desired contour of the outside and inside surfaces of the specimen. 通过使用柱塞将试样压入模具中获得的弯曲，以产生试样外表面和内表面所需的轮廓。 |
| Circular pitch | 齿距 |
The distance from the center of one gear tooth to the center of the next gear tooth measured on the pitch line. 在节线上测量的从一个轮齿中心到下一个轮齿中心的距离。 |
| Total energy (Unit J) | 总能量（单位J） |
The sum of all forms of energy associated with a system, including kinetic, potential, internal, magnetic, chemical, and electrical energy. 与系统相关的所有形式能量的总和，包括动能、势能、内能、磁能、化学能和电能。 |
| Washer | 垫圈 |
An annular disc of metal, rubber, plastic, ceramic, etc., placed between two surfaces in contact either to spread the load (for example, between a surface and a tightened nut or a bolt head), to provide a seal, or to separate or align components. 由金属、橡胶、塑料、陶瓷等制成的环形圆盘，放置在两个接触面之间，以分散载荷（例如，在一个表面和拧紧的螺母或螺栓头之间），提供密封，或分离或对齐部件。 |
| Heat-capacity rate (c) (Unit W/K) | 热容率（c）（单位W/K） |
For fluid flow in a duct with mass flow rate ṁ, the product ṁC where C is the specific-heat capacity, at constant pressure (CP) in the case of a gas. 对于质量流量为ṁ的管道中的流体流动，乘积ṁC其中C是比热容，在气体的情况下为恒定压力（CP）。 |
| Barometer | 气压计 |
An instrument used to measure atmospheric pressure. An instrument for measuring atmospheric pressure. There are two main types – the mercury barometer, and the aneroid barometer. 用于测量大气压力的仪器。有两种主要类型——水银气压计和无液气压计。 |
| Gibbs–Dalton law | 吉布斯-道尔顿定律 |
An extension of Dalton’s law of additive pressures to include the statement that the internal energy, enthalpy, and entropy of a mixture of gases are equal to the sum of the internal energies, enthalpies, and entropies the individual constituents would have if each existed alone at the same temperature and volume. Gibbs rule is that part of the law pertaining to entropy. 道尔顿附加压力定律的扩展，包括以下陈述：气体混合物的内能、焓和熵等于各个成分单独存在时的内能、焓和熵之和。相同的温度和体积。吉布斯定律是与熵有关的定律的一部分。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Combined dimensioning | 组合尺寸标注 |
The use of chain dimensioning and parallel dimensioning on the same engineering drawing. 在同一工程图上使用链式尺寸标注和平行标注。 |
| Sample average | 样本平均值 |
The sum of all the observed values in a sample divided by the sample size. It is a point estimate of the population mean. Also known as arithmetic mean. 样本中所有观察值的总和除以样本大小。它是总体平均值的点估计。也称为算术平均值。 |
| Preheating | 预热 |
Heating before some further thermal or mechanical treatment. For tool steel, heating to an intermediate temperature immediately before final austenitizing. For some nonferrous alloys, heating to a high temperature for a long time, to homogenize the structure before working. In welding and related processes, heating to an intermediate temperature for a short time immediately before welding, brazing, soldering, cutting, or thermal spraying. 在进一步热处理或机械处理之前加热。对于工具钢，在最终奥氏体化之前立即加热至中间温度。对于一些非铁合金，在工作前长时间加热到高温，以使结构均匀化。在焊接和相关工艺中，在焊接、钎焊、钎焊、切割或热喷涂之前，立即加热到中间温度。 |
| Second (s) | 秒（s） |
The SI base unit of time equal to 9 192 631 770 times the period of the radiation corresponding to the transition between the two hyperfine levels of the ground state of the caesium-133 atom. SI基时间单位等于9192631770倍的辐射周期，对应于铯-133原子基态的两个超精细能级之间的跃迁。 |
| Stress relaxation | 应力松弛 |
The slow decrease in stress level within a part (e.g., a bolt) which is heavily loaded under constant deflection conditions. A ‘‘cousin’’ to creep, which is a slow change in geometry under constant stress conditions. The time-dependent decrease in stress in a solid under constant strain at constant temperature due to creep. The stress-relaxation behavior of a metal is usually shown in a stress-relaxation curve. 在恒定挠曲条件下，零件（如螺栓）内的应力水平缓慢降低，该零件承受重荷载。蠕变的“表亲”，是在恒定应力条件下几何结构的缓慢变化。在恒定温度下，由于蠕变，固体在恒定应变下的应力随时间变化的减小。金属的应力松弛行为通常显示在应力松弛曲线中。 |
| Machine tool | 机床工具 |
A powered machine, such as a borer, grinder, lathe, milling machine or planer, used for cutting and shaping metal, plastics, composites, etc. (machining). A machining centre is a CNC machine tool working about several axes, having a stock of tools and automatic tool changing ability, which is capable of diverse machining operations under automated control. 一种动力机器，如钻孔机、磨床、车床、铣床或刨床，用于切割和成形金属、塑料、复合材料等（机加工）。加工中心是围绕多个轴工作的CNC机床，具有刀具库存和自动换刀能力，能够在自动化控制下进行各种加工操作。 |
| Magnetic test | 磁性测试 |
Method used to test heat extraction rates of various quenchants. The test works by utilizing the change in magnetic properties of metals at their Curie point–the temperature above which metals lose their magnetism. 用于测试各种淬火剂的热提取率的方法。该测试通过利用金属在居里点（即金属失去磁性的温度）的磁性变化来进行。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Lathe | 车床 |
A machine tool in which work, gripped in the headstock, is rotated against the cutting tool to produce turned, bored, faced, or threaded components. 一种机床，其中夹持在主轴箱中的工件靠着切削工具旋转，以生产车削、钻孔、端面或螺纹部件。 |
| Fatigue test | 疲劳测试 |
A method for determining the range of alternating (fluctuating)stresses a material can withstand without failing. 一种确定材料可以承受而不会失效的交变（波动）应力范围的方法。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Waist | 腰部 |
The joint in a robot corresponding to the human waist, i.e. providing rotation about a vertical axis. In an articulated robot, the first joint mounted at the base frame. 机器人中的关节对应于人的腰部，即提供绕垂直轴的旋转。在关节式机器人中，第一个关节安装在基架上。 |
| Concentration ratio | 浓度比 |
For a concentrating solar collector, the ratio of the projected area of the concentrator facing the solar beam to the actual area of the receiver. 对于聚光太阳能集热器，集中器面向太阳光束的投影面积与接收器的实际面积之比。 |
| Radiosity (J) (Unit W/m²) | 辐射度（J）（单位W/m²） |
The total radiation leaving a given surface per unit area, including emitted, reflected, and transmitted radiation. 每单位面积离开给定表面的总辐射，包括发射、反射和透射辐射。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Shrink ring | 预紧环 |
A ring, which is expanded by heating, is placed around an assembly of parts, and then contracts upon cooling to hold the assembly in place. 通过加热膨胀的环被放置在零件组件周围，然后在冷却时收缩以将组件固定到位。 |
| Crank pin | 曲柄销 |
It is a short shaft parallel to the axis of the crankshaft but radially offset from it, to which is attached the big end of a connecting rod in a bearing. Sometimes the crank pin is supported at one end only (a wrist pin) but in built-up or one-piece forged crankshafts, the crank pin is supported by thick plates (crank arms, crank webs) at either end. 它是一个短轴，平行于曲轴的轴线，但径向偏移，轴承中连杆的大端连接到该短轴上。有时曲柄销仅在一端支撑（腕销），在组合式或整体锻造曲轴中，曲柄销在两端由厚板（曲柄臂、曲柄腹板）支撑。 |
| Cone pulley | 锥轮 |
A stepped pulley having several diameters which, when linked by a laterallymoveable transmission belt to a corresponding pulley, gives a series of speed ratios. 具有多种直径的阶梯式皮带轮，当通过可横向移动的传动带连接到相应的皮带轮时，会产生一系列速比。 |
| Ratchet coupling | 棘轮联轴器 |
A joint employing a ratchet system between two shafts, so that not only does the driven shaft run in one direction only, but also the driven shaft can, if necessary, run more quickly than the driving shaft. 在两个轴之间采用棘轮系统的接头，这样不仅从动轴只能在一个方向上运行，而且在必要时，从动轴可以比驱动轴运行得更快。 |
| Nut | 螺母 |
A metal fastener of square, hexagon or other shape, having an internal thread which screws onto a bolt, stud or arbor. An internally-threaded fastener used with externally-threaded bolts. Usually hexagonal in shape but there is a multitude of other geometries, such as square, for special purposes and different gripping tools. 一种方形、六角形或其他形状的金属紧固件，具有内螺纹，可拧在螺栓、螺柱或心轴上。与外螺纹螺栓一起使用的内螺纹紧固件。通常为六边形，但也有许多其他几何形状，如方形，用于特殊用途和不同的夹持工具。 |
| Modulus of elasticity (E) | 弹性模量（E） |
The measure of rigidity or stiffness of a metal; the ratio of stress, below the proportional limit, to the corresponding strain. In terms of the stress-strain diagram, the modulus of elasticity is the slope of the stress-strain curve in the range of linear proportionality of stress to strain. 金属的刚度或刚度的量度；低于比例极限的应力与相应应变之比。根据应力应变图，弹性模量是应力应变曲线在应力应变线性比例范围内的斜率。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Proof stress | 弹性极限应力 |
(1) The stress that will cause a specified small permanent set in a material. (2) A specified stress to be applied to a member or structure to indicate its ability to withstand service loads. （1）在材料中引起规定的小永久变形的应力。（2）施加在构件或结构上的规定应力，以表明其承受工作荷载的能力。 |
| Lead of thread | 螺纹导程 |
On a single threaded screw, the distance the screw or nut advances in one complete revolution. 在单螺纹螺钉上，螺钉或螺母在一整圈中前进的距离。 |
| Orange peel | 橘皮 |
A surface roughening in the form of a pebble-grained pattern where a metal of unusually coarse grain is stressed beyond its elastic limit. Also known as pebbles and alligator skin. 一种以卵石颗粒图案形式出现的粗糙化表面，其中晶粒异常粗的金属受到的应力超过其弹性极限。也称为卵石和鳄鱼皮。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Catastrophic failure | 灾难性故障 |
A sudden and total failure of a large engineering structure such as an aeroengine, aircraft, space vehicle, bridge, or dam. 大型工程结构（如航空发动机、飞机、航天器、桥梁或水坝）突然完全失效。 |
| Thermal electromotive force | 热电动势 |
The electromotive force generated in a circuit containing two dissimilar metals when one junction is at a temperature different from that of the other. 当一个结处于不同于另一个结的温度时，在含有两种不同金属的电路中产生的电动势。 |
| Diaphragm meter | 隔膜计 |
A dry flow meter in which there are two or more interconnected chambers, each having a diaphragm in the wall. The chambers empty and fill alternately and the flow rate of gas is determined from the movement of diaphragms. Diaphragm meters are commonly used to monitor domestic and commercial gas supply. 一种干式流量计，其中有两个或多个相互连接的腔室，每个腔室的壁上都有一个隔膜。腔室交替排空和填充，气体流速由隔膜的移动确定。隔膜流量计通常用于监测家用和商用燃气供应。 |
| Vector | 矢量 |
Any physical quantity, such as velocity, acceleration, force, or momentum, that is specified in terms of both its magnitude and its direction. The convention of printing vector quantities in boldface was introduced by the physicist Josiah Willard Gibbs. 任何物理量，如速度、加速度、力或动量，以其大小和方向来表示。用黑体印刷矢量量的惯例是由物理学家约西亚·威拉德·吉布斯提出的。 |
| Weight (W) (Unit N) | 重量（W）（单位：N） |
The force of attraction on a body due to gravity. A body’s weight is the product of its mass and the gravitational field strength at that point. Mass remains constant, but weight depends on the object’s position on the Earth’s surface, decreasing with increasing altitude. If g is the acceleration due to gravity, the weight of a mass m is given by W = mg. On Earth, the acceleration due to gravity is approximately 9.81 m/s², so that the weight of a 1 kg mass is 9.81 N. More generally, the weight is the force exerted on the mass of a body when in the gravitational field of another body. 重力由于重力作用在物体上的吸引力。物体的重量是其质量和该点引力场强度的乘积。质量保持不变，但重量取决于物体在地球表面的位置，随着海拔的升高而减小。如果g是重力引起的加速度，则质量m的重量由W=mg给出。在地球上，重力引起的加速度约为9.81m/s²，因此1千克质量的重量为9.81N。更一般地说，重量是在另一个物体的重力场中施加在物体质量上的力。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Thermomechanical working | 热机械加工 |
A general term covering a variety of processes combining controlled thermal and deformation treatments to obtain specific properties. Same as thermal-mechanical treatment. 一个通用术语，涵盖结合受控热处理和变形处理以获得特定性能的各种工艺。与热机械处理相同。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Tera (T) | 特拉（T） |
An SI unit prefix indicating a multiplier of 1012; thus terawatt (TW) is a unit of power equal to one trillion watts. 指示乘数1012的SI单位前缀；因此，太瓦（TW）是等于1万亿瓦的功率单位。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Recrystallization temperature | 再结晶温度 |
The approximate minimum temperature at which complete recrystallization of a cold-worked metal occurs within a specified time. 冷加工金属在规定时间内发生完全再结晶的近似最低温度。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Gas compressor | 气体压缩机 |
A machine which draws in a gas at low pressure and delivers it at high pressure, usually accompanied by a temperature increase. Compressor designs include axial, centrifugal, diaphragm, reciprocating, and rotary (including the blade compressor). 一种在低压下吸入气体并在高压下输送气体的机器，通常伴随着温度升高。压缩机设计包括轴流式、离心式、隔膜式、往复式和旋转式（包括叶片式压缩机）。 |
| Graham’s laws | 格雷厄姆定律 |
The laws stating that the rates of diffusion and effusion of a gas are inversely proportional to the square root of its density. 规定气体的扩散和渗出速率与其密度的平方根成反比的定律。 |
| Shore hardness | 肖氏硬度 |
A measure of the hardness of materials such as elastomers, plastics, and rubbers determined using a Shore durometer which measures the penetration depth of a hardened steel rod (the indenter) 1.1–1.4 mm in diameter into the test material for a given force applied rapidly with a calibrated spring. There are two main indenter designs: type A (for softer materials) for which the end of the rod is a truncated 35° cone tapering to a diameter of 0.79 mm, and type D (harder materials) for which the end is a 30° cone with a 0.1 mm radius tip. The spring force is 8.05 N for type A and 44.45 N for type D. The hardness value is related to the penetration depth (limited to a maximum of 2.5 mm) such that for zero penetration the hardness is 100 and for maximum penetration the hardness is zero. The relevant standards are ISO 48-1, 48-4, and 48-7. Shore hardness values of selected materials are as follows: ABS 100, cellulose acetate 50–95, high-density polyethylene 60–70, low density polyethylene 40–50, polymethylmethacrylate 90–99, PTFE 50–65, and plasticized PVC 15–70. 使用肖氏硬度计测量弹性体、塑料和橡胶等材料的硬度，肖氏硬度仪测量直径为1.1–1.4mm的硬化钢棒（压头）在用校准弹簧快速施加的给定力下渗入试验材料的深度。有两种主要的压头设计：A型（适用于较软的材料），其杆端为截头35°锥形，逐渐变细至直径0.79 mm；D型（较硬的材料），端部为30°锥形，尖端半径为0.1mm。A型的弹簧力为8.05N，D型为44.45N。硬度值与渗透深度相关（最大限制为2.5mm），因此，对于零渗透，硬度为100，对于最大渗透，硬度是零。相关标准为ISO 48-1、48-4和48-7。所选材料的肖氏硬度值如下：ABS100、醋酸纤维素50-95、高密度聚乙烯60-70、低密度聚乙烯40-50、聚甲基丙烯酸甲酯90-99、PTFE50-65和塑化PVC15-70。 |
| Calorie | 卡路里 |
(cal, gram calorie, small calorie) An obsolete (i.e. non-SI) unit of energy equal to 4.186 8 J. It is the amount of energy needed to raise the temperature of 1 gram of pure airfree water from 14.5°C to 15.5°C at standard atmospheric pressure. （卡，克热量，小热量）一种已被淘汰的（即非SI）能量单位，等于4.1868J。它是在标准大气压力下将1克纯无空气水的温度从14.5℃升高到15.5℃所需的能量。 |
| Hot strength (Unit Pa) | 热强度（单位Pa） |
The yield stress (or sometimes fracture stress) of a material at temperatures above about half its melting point in kelvins. 材料在高于其熔点一半（以开尔文为单位）的温度下的屈服应力（有时为断裂应力）。 |
| Cold working | 冷加工 |
The plastic deformation of a metal, by rolling (cold rolling), drawing, forging (cold forging), etc. at a temperature well below its recrystallization temperature, which results not only in permanent shape change but also increase in strength and loss of ductility owing to work-hardening. 金属在远低于其再结晶温度的温度下通过轧制（冷轧）、拉拔、锻造（冷锻）等方式发生塑性变形，这不仅会导致永久的形状变化，还会增加强度并降低延展性由于加工硬化。 |
| Centi (c) | 厘（c） |
An SI unit prefix indicating a multiplier of 0.01; thus centimetre is a unit of length equal to one one-hundredth of a metre or 10 mm. 表示乘数0.01的SI单位前缀；因此厘米是长度单位，等于一米的百分之一或10毫米。 |
| Torque control | 扭矩控制 |
A system of optimizing rotor speed for a variable-speed wind turbine by controlling the torque demands of the generator. 通过控制发电机的扭矩需求来优化变速风力涡轮机的转子速度的系统。 |
| Design heating load (Unit kW) | 设计热负荷（单位kW） |
The heating requirements based on a specified number of heating degree days, or required to maintain a building or other enclosed space at a specified temperature for a given outside temperature. 基于指定的采暖度日数的加热要求，或在给定的外部温度下将建筑物或其他封闭空间保持在指定温度下所需的加热要求。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Roughness | 粗糙度 |
The deviations from the wavy surface itself, caused by geometry of the cutting tool and its wear, machining conditions, microstructure of the workpiece, vibrations in the system, and so on. Surface roughness changes as a surface goes through the wearing-in process, but may then stabilize. 由刀具的几何形状及其磨损、加工条件、工件的微观结构、系统中的振动等引起的与波状表面本身的偏差。表面粗糙度随着表面经过磨合过程而变化，但随后可能会稳定下来。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Vane engine (vane motor) | 叶片发动机（叶片马达） |
A rotary engine in which high-pressure hydraulic fluid in the spaces between spring-loaded sliding vanes held in an offset rotor acts on the vanes, causing the rotor to revolve within a cylinder. The design is much like a sliding-vane compressor, as is that of a vane pump, used to pump liquids. 一种旋转式发动机，其中偏置转子中装有弹簧的滑动叶片之间的高压液压流体作用在叶片上，使转子在气缸内旋转。这种设计很像滑动叶片压缩机，就像用于泵送液体的叶片泵一样。 |
| Static equilibrium | 静态平衡 |
A solid body, structure, or physical system (or any subdivided part) will be in static equilibrium, either at rest or moving with constant velocity, if the resultants of all external forces and moments acting on it are zero. 如果作用在固体上的所有外力和力矩的合力为零，则固体、结构或物理系统（或任何细分部分）无论是静止还是以恒定速度移动，都是处于静态平衡。 |
| Zero initial conditions | 零初始条件 |
The assumption normally made in control engineering that up to a start time defined as t = 0, all variables have zero value. 在控制工程中通常作出的假设，即在定义为t=0的开始时间内，所有变量均为零值。 |
| Wave spring | 波形弹簧 |
A type of compression spring, similar to a coil spring, but made of strip shaped into waves around the circumference. 一种压缩弹簧，类似于螺旋弹簧，但由沿圆周成波浪形的条状物制成。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Resistance thermometer | 电阻温度计 |
A thermometer in which the sensing element is basically a metal wire, usually of platinum, for which the variation of resistance with temperature is known accurately. A resistance pyrometer is a resistance thermometer intended for use up to about 1 000°C. 一种温度计，其中传感元件基本上是一根金属线，通常是铂，可以准确地知道电阻随温度的变化。电阻高温计是一种电阻温度计，用于高达约1000°C的温度。 |
| DTI | DTI |
Direct tension indicator. A fastener used primarily in the structural steel industry, designed to indicate that a certain minimum amount of tension has been developed in the fastener during assembly. 直接张力指示器。一种主要用于结构钢行业的紧固件，旨在表明在装配过程中紧固件中产生了一定的最小张力。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Fit | 装配 |
The general term used to signify the range of tightness which may result from the application of a specific combination of allowances and tolerances in the design of mating parts. 通用术语，用于表示配合零件设计中公差和公差的特定组合可能导致的紧密性范围。 |
| Mohs scale | 莫氏硬度 |
A scale of scratch hardness originally developed for minerals. 最初为矿物开发的划痕硬度标尺。 |
| Mechanical alloying | 机械合金化 |
Production of alloys from powders by consolidation, e.g. hotpressing or extrusion, followed by hot and/or cold working and final annealing. Materials such as dispersion-strengthened alloys, high-temperature aluminium alloys, and amorphous alloys can be made in this way. 通过固结（例如热压或挤压）从粉末生产合金，然后进行热和/或冷加工和最终退火。用这种方法可以制造弥散强化合金、高温铝合金和非晶合金等材料。 |
| Damage tolerance | 损伤容限 |
(defect tolerance) A design philosophy that takes into account initial imperfections, crack-growth rates and conditions at final fracture, and uses fracture mechanics to demonstrate that cracks should not grow to their critical length within the design life (or at least should be capable of ready detection). （缺陷公差）考虑初始缺陷、裂纹扩展速率和最终断裂条件的设计理念，并使用断裂力学证明裂纹不应在设计寿命内增长到其临界长度（或至少应能够随时检测）。 |
| Mechanical vibration | 机械振动 |
The motion of a particle or body which oscillates about a position of equilibrium. 围绕平衡位置摆动的粒子或物体的运动。 |
| Elastic limit | 弹性极限 |
The maximum stress which a material is capable of sustaining without any permanent strain (deformation) remaining on complete release of the stress. 材料在完全释放应力时能够承受的最大应力，且不会留下任何永久应变（变形）。 |
| Amontons friction | 阿蒙顿摩擦 |
(Coulomb friction) Friction between surfaces where the ratio of the frictional force F to the normal force N is constant and independent of the area in contact. （库仑摩擦）摩擦力F与法向力N之比恒定且与接触面积无关的表面之间的摩擦。 |
| Secondary stresses (Unit Pa) | 二次应力（单位Pa） |
Stresses different from those induced by the major loading but nevertheless resulting from the major loads; for example, the hoop stresses that occur around the circumference of barrelled compression testpieces and forgings. 与主要荷载引起的应力不同，但主要荷载产生的应力；例如，桶装压缩试件和锻件周围产生的环向应力。 |
| Combined carbon | 复合碳 |
The part of the total carbon in steel or cast iron that is present as other than free carbon. 钢或铸铁中总碳中除游离碳外的部分。 |
| Austenite finish temperature (Af) | 奥氏体完成温度（Af） |
Temperature at which the transformation of martensite into austenite completes upon heating. The same designation is also applied to nonferrous alloys in which martensite transforms into some parent phase. 加热时马氏体转变为奥氏体的温度。相同的名称也适用于马氏体转变为某些母相的有色合金。 |
| Transgranular | 穿晶 |
Through or across crystals or grains. Also known as intracrystalline or transcrystalline. 穿过或横穿晶体或颗粒。也称为晶内或晶间。 |
| Carburizing flame | 渗碳火焰 |
A gas flame that will introduce carbon into some heated metals, as during a gas welding operation. A carburizing flame is a reducing flame, but a reducing flame is not necessarily a carburizing flame. 一种气体火焰，会在气焊操作中将碳引入一些加热的金属中。渗碳火焰是还原火焰，但还原火焰不一定是渗碳火焰。 |
| Regenerative pump | 涡流泵 |
(regenerative turbine pump, peripheral pump) A pump with a double-sided impeller having a large number of radial blades. The pressure of the pumped liquid increases progressively over several revolutions of the impeller. It is particularly suited to producing large heads at small flow rates without cavitation. （再生涡轮泵，外围泵）具有具有大量径向叶片的双面叶轮的泵。泵送液体的压力在叶轮的几圈内逐渐增加。它特别适合于在小流速下产生大水头且不产生气穴。 |
| Press quenching | 压淬 |
A quench in which hot dies are pressed and aligned with a part before the quenching process begins. Then the part is placed in contact with a quenching medium in a controlled manner. This process avoids part distortion. 一种淬火方法，在淬火过程开始之前，热模具被压制并与零件对齐。然后将零件以受控方式放置在与淬火介质接触的位置。该过程避免了零件变形。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Peel strength (Unit N) | 剥离强度（单位：N） |
(peel test) The strength of an adhesive bond between two materials as measured by the force required in a given direction to peel apart adhered strips. This force depends on the dimensions and thickness of the adhered strips and their yield stress, together with the fracture toughness of the bond. （剥离试验）两种材料之间的粘合强度，通过给定方向上剥离粘合条所需的力来测量。该力取决于粘合条的尺寸和厚度及其屈服应力，以及粘合剂的断裂韧性。 |
| Quench annealing | 淬火退火 |
Annealing an austenitic ferrous alloy by solution heat treatment followed by rapid quenching. 通过固溶热处理然后快速淬火对奥氏体铁合金进行退火。 |
| Process annealing | 中间退火 |
An imprecise term denoting various treatments used to improve workability. For the term to be meaningful, the condition of the material and the time-temperature cycle used must be stated. 一个不精确的术语，表示用于改善可加工性的各种处理方法。为了使术语有意义，必须说明材料的条件和使用的时间-温度循环。 |
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Gamma iron | 加马铁 |
The face-centered cubic form of pure iron, stable from 910 to 1400 °C (1670 to 2550 °F). 纯铁的面心立方形式，在910至1400°C（1670 2550°F）温度范围内稳定。 |
| Sample standard deviation (s) | 样本标准偏差（s） |
The square root of the sample variance. It is a point estimate of the population standard deviation, a measure of the “spread”of the frequency distribution of a population. This value of sprovides a statistic that is used in computing interval estimates and several test statistics. For small sample sizes, s underestimates the population standard deviation. 样本方差的平方根。它是总体标准偏差的点估计，是总体频率分布“扩散”的度量。SPR的这个值提供了一个用于计算区间估计和若干测试统计量的统计量。对于小样本，s低估了总体标准偏差。 |
| Centrifugal force (Unit N) | 离心力（单位N） |
The inertial reaction force to the centripetal force. It is equal in magnitude but opposite in direction. 惯性反作用力对向心力。它的大小相等，但方向相反。 |
| Brittle | 脆性材料 |
A brittle material is one that breaks, often suddenly, with no permanent deformation. Examples of brittle materials are some cast irons, glass, concrete, and some plastics. A bolt is said to be brittle if it will break when stretched only a small amount past its yield point. 脆性材料通常会突然断裂，不会产生永久变形。脆性材料的例子有一些铸铁、玻璃、混凝土和一些塑料。如果螺栓在拉伸时仅超过其屈服点一小部分就会断裂，则称其为脆性螺栓。 |
| Flame straightening | 火焰矫直 |
Correcting distortion in metal structures by localized heating with a gas flame. 通过使用气体火焰进行局部加热来纠正金属结构的变形。 |
| Dynamic coupling | 动态耦合 |
In vibrations, the existence of inertial terms depending on mass in the governing equations, so that there is only a force if there is a corresponding acceleration. 在振动中，惯性项的存在取决于控制方程中的质量，因此只有当有相应的加速度时才有力。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Age hardening | 时效硬化 |
Raising the strength and hardness of an alloy by heating a supersaturated solid solution at a relatively low temperature to induce precipitation of a finely dispersed second phase. Also known as aging or precipitation hardening. Hardening by aging, usually after rapid cooling or cold working. 通过在相对较低的温度下加热过饱和固溶体以诱导细分散的第二相沉淀来提高合金的强度和硬度。也称为时效或沉淀硬化。通常在快速冷却或冷加工后。 |
| Deposit gauge | 沉积量计 |
(deposition gauge) An instrument employed in air pollution studies for measuring the amount of pollutant deposited on a given area in a given time under given conditions. （沉降计）在空气污染研究中使用的仪器，用于测量在给定条件下在给定时间内沉积在给定区域上的污染物量。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Brake fluid | 制动液 |
The hydraulic fluid used to transmit force to the pistons in disc brakes or the wheel cylinders in drum brakes. Requirements include a high boiling point and low hygroscopy. 用于将力传递到盘式制动器中的活塞或鼓式制动器中的轮缸的液压油。要求包括高沸点和低吸湿性。 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Sizing | 颗粒化 |
1. A finishing operation to ensure the specified dimensions and tolerances for a component are met. 2. (size classification) Separating an aggregate of mixed particles into groups according to size using a series of screens. 1.精加工操作，以确保满足部件的规定尺寸和公差。2.（粒度分类）使用一系列筛网根据粒度将混合颗粒的聚集体分成组。 |
| Torsional angle (ϕ) | 扭转角（ψ） |
(Unit ° or rad) The angular deflexion between two locations on a straight bar subjected to a torque. （单位为°或rad）受扭矩作用的直杆上两个位置之间的角偏转。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Deviation | 偏差 |
The difference between the actual value and the desired value of a controlled variable. 受控变量的实际值与期望值之间的差值。 |
| Design pressure (Unit Pa) | 设计压力（单位Pa） |
The greatest pressure that a closed container is expected to experience under normal operating conditions. 密闭容器在正常操作条件下预期承受的最大压力。 |
| Stress cracking | 应力开裂 |
A family of failure modes, each of which involves high stress and chemical action. The family includes Hydrogen embrittlement, Stress corrosion cracking, stress embrittlement, and hydrogen-assisted stress corrosion. 一系列失效模式，每种模式都涉及高应力和化学作用。该系列包括氢脆、应力腐蚀开裂、应力脆化和氢辅助应力腐蚀。 |
| Welding | 焊接 |
In tribology, the bonding between metallic surfaces in direct contact, at any temperature. A joining process in which the mating surfaces are at least softened, or more usually melted, unlike soldering and brazing. In solid-state (non-melting) welding, similar or dissimilar metals or thermoplastics may be joined by applying pressure to hot interfaces. In forge welding, joining is achieved by compression across the join between pre-heated workpieces. In friction welding (spin welding) one of the contacting surfaces is rotated rapidly before being loaded against the other. On contact, heat generated by friction softens the materials and permits severe plastic deformation that seals the joint. In friction stir welding, a wear-resistant tool is rotated rapidly, indents the surfaces and is traversed to form a join line. Resistance welding involves simultaneous pressure and electrically-generated heat, as in spot welding where a heavy electric current is passed for a short time through metal sheets which are pressed together between electrodes. 在摩擦学中，在任何温度下直接接触的金属表面之间的结合。与钎焊和钎焊不同，接合面至少软化或更通常熔化的接合工艺。在固态（非熔化）焊接中，相似或不同的金属或热塑性塑料可通过向热界面施加压力来连接。在锻造焊接中，通过压缩预热工件之间的连接来实现连接。在摩擦焊接（旋转焊接）中，一个接触表面在被加载到另一个表面之前快速旋转。接触时，摩擦产生的热量使材料软化，并允许密封接头的严重塑性变形。在搅拌摩擦焊中，耐磨工具快速旋转，使表面凹陷，并横穿形成连接线。电阻焊涉及同时产生的压力和电产生的热量，如点焊，在点焊中，大电流短时间通过电极之间压在一起的金属板。 |
| Conditioning heat treatment | 调质热处理 |
A preliminary heat treatment used to prepare a material for desired reaction to a subsequent heat treatment. For the term to be meaningful, the exact heat treatment must be specified. 用于制备材料的初步热处理，以便对随后的热处理进行所需的反应。为了使该术语有意义，必须指定确切的热处理。 |
| Quench-age embrittlement | 淬火时效脆化 |
Embrittlement of low-carbon steels resulting from precipitation of solute carbon at existing dislocations and from precipitation hardening of the steel caused by differences in ferrite at different temperatures. Quenchage embrittlement usually is caused by rapid cooling of the steel from temperatures slightly below Ac1 (the temperature at which austenite begins to form), and can be minimized by quenching from lower temperatures. 低碳钢的脆化是由于溶质碳在现有位错处的沉淀和铁素体在不同温度下的差异导致的钢沉淀硬化造成的。淬火脆性通常是由钢从略低于Ac1的温度（奥氏体开始形成的温度）快速冷却引起的，可以通过从较低温度淬火来最小化。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Slug wrench | 缓动扳手 |
A box wrench with an anvil on the end of the handle. Torque is produced by striking the anvil with a sledge hammer. 柄端有铁砧的套筒扳手。扭矩是通过用大锤敲击铁砧产生的。 |
| Counter sink | 台面水槽 |
To cut or shape a depression in an object so that the head of a screw may set flush or below the surface. 在物体上切割或塑造一个凹陷，使螺钉的头部可以齐平或低于表面。 |
| Butterfly valve | 蝶阀 |
A valve in which a disc rotates on a shaft at right angles to the axis of a pipe to regulate flow. When open, the disc is edge-on to the flow and offers limited resistance. When closed, the disc is pressed against a seat in the valve body. 阀瓣在与管道轴线成直角的轴上旋转以调节流量的阀门。当打开时，圆盘与水流边缘并提供有限的阻力。关闭时，阀瓣被压在阀体内的阀座上。 |
| Stress corrosion cracking (SCC) | 应力腐蚀开裂（SCC） |
A common form of Stress cracking in which an Electrolyte encourages the growth of a crack in a highly stressed bolt. Only a tiny quantity of electrolyte need be present, at the tip or face of the crack. A time-dependent process in which a metallurgically susceptible material fractures prematurely under conditions of simultaneous corrosion and sustained loading at lower stress levels than would be required in the absence of a corrosive environment. Tensile stress is required at the metal surface and may be a residual stress resulting from heat treatment or fabrication of the metal or the result of external loading. Cracking may be intergranular or transgranular, depending on the combination of alloy and environment. 一种常见的应力开裂形式，其中电解液促使高应力螺栓中的裂纹扩展。在裂纹尖端或表面，只需存在少量电解质。一种随时间变化的过程，其中冶金敏感材料在同时腐蚀和持续加载的条件下过早断裂，其应力水平低于无腐蚀环境时的要求。在金属表面需要拉应力，拉应力可以是金属的热处理或制造或外部负载产生的残余应力。裂纹可能是沿晶开裂或穿晶开裂，这取决于合金和环境的组合。 |
| Coextrusion | 复合挤压 |
The simultaneous extrusion through the same die of two or more materials in combination. 通过同一模具同时挤出两种或多种材料的组合。 |
| T-slot | T型槽 |
A recessed or undercut slot made with a special T shaped cutter in the tables of machine tools to receive the square head of a T bolt for clamping workpiece. 在机床工作台上用一种特殊的T形刀具制成的凹槽或底切槽，用于容纳T形螺栓的方头，用于夹紧工件。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Noble metals | 贵金属 |
Metallic elements from periods (rows) 5 and 6 of the periodic table, namely ruthenium, rhodium, palladium, silver, osmium, iridium, platinum, and gold. They resist corrosion and oxidation and are used for electrical contacts, thin-film circuits, and electroplating. Gold, silver, and platinum used for jewellery are also known as precious metals. They have face-centred cubic crystal structure and good ductility. 周期表第5和第6周期（行）中的金属元素，即钌、铑、钯、银、锇、铱、铂和金。它们抗腐蚀和氧化，用于电触点、薄膜电路和电镀。用于珠宝的金、银和铂也被称为贵金属。它们具有面心立方晶体结构和良好的延展性。 |
| Atomizing humidifier | 雾化加湿器 |
A humidifier that functions by spraying fine droplets of water into an airstream. 一种加湿器，通过将细小的水滴喷射到气流中来发挥作用。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Tangential load (Unit N) | 切向荷载（单位：N） |
The component of load applied to an object, such as a gear, that tends to cause or resist rotation. 旋转力施加在物体上的载荷分量，如齿轮，倾向于引起或阻止旋转。 |
| System engineering | 系统工程 |
A methodology which integrates all disciplines and specialty groups into a team effort, forming a structured development process that proceeds from concept to production to operation. 一种将所有学科和专业组整合到团队工作中的方法，形成从概念到生产再到运营的结构化开发过程。 |
| R-curve/Resistance curve | 阻力曲线 |
In linear-elastic fracture mechanics, a plot of crack-extension resistance as a function of stable crack extension, which is either the difference between the physical crack size, or the effective crack size, and the original crack size. R-curves normally depend on specimen thickness and, for some materials, on temperature and strain rate. An increase in fracture toughness with crack propagation shown by rising plots of toughness vs growing crack length. 在线弹性断裂力学中，作为稳定裂纹扩展函数的裂纹扩展阻力图，即物理裂纹尺寸或有效裂纹尺寸与原始裂纹尺寸之间的差值。R曲线通常取决于试样厚度，对于某些材料，还取决于温度和应变率。是随着裂纹扩展，断裂韧性增加，表现为韧性与扩展裂纹长度的上升曲线。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Retaining clip | 固定夹 |
(R-clip, hair cotter pin) A wire clip roughly with the shape of the letter R. The straight part of the clip passes through a hole drilled into a shaft or rod such that a wheel is held in position on the shaft, or the shaft is prevented from moving axially. （R形夹，开口销）大致与字母R形状相同的线夹。线夹的直线部分穿过钻在轴或杆上的孔，从而将车轮固定在轴上，或防止轴轴向移动。 |
| Torque multiplier | 扭矩放大器 |
A gearbox used to multiply the torque produced by a small hand wrench (usually a Torque wrench). The output of the multiplier drives the nut or bolt with a torque that is higher, and a speed that is lower, than input torque and speed. There is no torque gage or readout on the multiplier. 一种齿轮箱，用于增加小手动扳手（通常是扭矩扳手）产生的扭矩。倍增器的输出以比输入扭矩和速度更高的扭矩和更低的速度驱动螺母或螺栓。倍增器上没有扭矩计或读数。 |
| Cotter pin | 开口销 |
(cotter) 1. A tapered wedge or pin passing through a tapered slot or hole in one member and bearing against a second member to fix it in location. 2. A split cotter is commonly called a split pin. A pin with two legs. With legs together, the pin is placed through the hole in a clevis pin. The legs are then opened outward to prevent the cotter pin from backing out of the hole. The cotter pin, in turn, prevents the load-bearing clevis pin from backing out of its retaining hole. （开口）1.锥形楔子或销钉穿过一个构件中的锥形槽或孔，并支撑在第二个构件上以将其固定到位。2.开口开口通常称为开口销。相当于有两条腿的别针，将支腿放在一起，销钉穿过U形夹销上的孔。然后将支腿向外打开以防止开口销从孔中退出。开口销反过来防止承重U形夹销从其固定孔中退出。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Slenderness ratio | 长细比 |
The effective unsupported length of a uniform column divided by the least radius of gyration of the cross-sectional area. 均匀柱的有效无支撑长度除以横截面积的最小回转半径。 |
| Torsion bar | 扭杆 |
A metal bar designed to act as an elastic spring when torque is applied. 当施加扭矩时用作弹性弹簧的金属棒。 |
| Total carbon | 总碳 |
The sum of the free and combined carbon (including carbon in solution) in a ferrous alloy. 铁合金中游离碳和结合碳（包括溶液中的碳）的总和。 |
| Dynamic mechanical measurement | 动态机械测量 |
A technique in which either the modulus and/or damping of a substance under oscillatory load or displacement is measured as a function of temperature, frequency, or time, or a combination thereof. 一种技术，其中在振荡载荷或位移下测量物质的模量和/或阻尼作为温度、频率或时间或其组合的函数。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Chafing fatigue | 磨损疲劳 |
Fatigue damage initiated in a surface damaged by rubbing against another body. 因与另一个物体摩擦而损坏的表面引起的疲劳损坏。 |
| Shear lip | 剪切唇 |
A narrow, slanting ridge along the edge of a fracture surface. The term sometimes also denotes a narrow, often crescent-shaped, fibrous region at the edge of a fracture that is otherwise of the cleavage type, even though this fibrous region is in the same plane as the rest of the fracture surface. 沿断裂面边缘的狭窄倾斜脊。该术语有时还表示断裂边缘处的狭窄、通常为新月形的纤维区域，否则为解理型，即使该纤维区域与断裂表面的其余部分位于同一平面内。 |
| Blade compressor | 叶片式压缩机 |
An oil-free, double-acting rotary compressor in which an angled blade attached to the inner surface of a rotating housing passes through a slot in a disk rotating about an axis perpendicular to that of the housing but offset from it. Air enters through apertures in the housing and leaves through a port in the housing. 一种无油双作用旋转式压缩机，其中连接到旋转外壳内表面的倾斜叶片穿过圆盘上的槽，该槽绕垂直于外壳的轴旋转，但偏离外壳。空气通过壳体中的孔进入，并通过壳体的端口离开。 |
| Thread rolling | 滚丝 |
Thread rolling (also known as roll threading) is a cold forming process for producing threads or other helical or annular forms by rolling the impression of hardened steel dies into the surface of a cylindrical or conical blank. Polygonal blanks are also thread rolled for the purpose of fabricating thread-forming and self-locking screws. The preferred polygonal shape is trilobular and is produced in flat die machines. 螺纹滚压（也称为滚压螺纹）是一种冷成型工艺，通过将硬化钢模具的压痕滚压到圆柱形或锥形坯料的表面来生产螺纹或其他螺旋或环形形状。多边形坯料也进行螺纹轧制，以制造螺纹成型和自锁螺钉。优选的多边形形状为三棱形，并在平模机中生产。 |
| Torsion spring | 扭簧 |
1. A spring in the form of a torsion bar. 2. A helical spring to which torque can be applied at the ends. 1.一种扭杆形式的弹簧。2.一种螺旋弹簧，其端部可施加扭矩。 |
| Radial wave equation | 径向波动方程 |
A differential equation describing the transmission of a wave in a system with radial symmetry. 描述波在径向对称系统中传输的微分方程。 |
| Modulus of rupture | 断裂模量 |
Nominal stress at fracture in a bend test or torsion test. In bending, modulus of rupture is the bending moment at fracture divided by the section modulus. In torsion, modulus of rupture is the torque at fracture divided by the polar section modulus. 弯曲试验或扭转试验中的标称断裂应力。在弯曲中，断裂模量是断裂时的弯矩除以截面模量。在扭转中，断裂模量是断裂时的扭矩除以极截面模量。 |
| Tolerance limits | 公差极限 |
The extreme values (upper and lower) that define the range of permissible variation in size or other quality characteristic of a part. 定义零件尺寸或其他质量特性允许偏差范围的极值（上限和下限）。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| Deformation (Unit 1/s) | 变形（单位1/s） |
A change in the form of a body due to stress, thermal change, change in moisture, or other causes. In solid mechanics, any change, reversible (elastic) or permanent (plastic), in the shape or size of parts of a body, or the whole body, caused by external or internal loading. It includes extension, compression, bending, and twisting. The same state of deformation in a body can appear as different combinations of elongation and shear. To state how much of the total strain is shear, it is split into dilatation and deviatoric components, the former changing volume but not shape, the latter shape but not volume. 由于压力、热变化、水分变化或其他原因导致的身体形态变化。在固体力学中，由外部或内部载荷引起的身体各部分或整个身体的形状或大小的任何可逆（弹性）或永久（塑性）变化。它包括拉伸、压缩、弯曲和扭曲。物体中相同的变形状态可以表现为伸长和剪切的不同组合。为了说明总应变中有多少是剪切，将其分为膨胀分量和偏差分量，前者改变体积但不改变形状，后者改变形状但不改变体积。 |
| Equilibrium diagram | 平衡图 |
A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant. 在完全平衡条件下，合金系统中相场的温度、压力和成分极限的图形表示。在金属系统中，压力通常被认为是恒定的。 |
| Significance level | 显着性水平 |
The stated probability (risk) that a given test of significance will reject the hypothesis that a specified effect is absent when the hypothesis is true. 当假设为真时，给定的显著性检验将拒绝特定效应不存在的假设的所述概率（风险）。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Compression pressure (Unit Pa) | 压缩压力（单位Pa） |
The pressure produced in a cylinder of a piston engine by compression of air in the absence of fuel. 在没有燃料的情况下通过压缩空气在活塞发动机的气缸中产生的压力。 |
| Thermal shock | 热冲击 |
The development of a steep temperature gradient and accompanying high stresses within a structure. 在结构内形成陡峭的温度梯度和伴随的高应力。 |
| Bearing strength | 承载强度 |
The maximum bearing stress that a material is capable of sustaining. 材料能够承受的最大承载应力。 |
| Turbo generator | 涡轮发电机 |
(turboset) The combination of a steam or gas turbine and an electrical generator with a single shaft or connected coaxial shafts. （汽轮发电机组）蒸汽或燃气轮机与发电机的组合，具有单轴或连接的同轴。 |
| Nut box mechanism | 螺母箱机械装置 |
In a lathe it is used to engage and disengage the lead screw for thread cutting. This comprises a pair of half-nuts capable of sliding in vertical slides in or out of mesh with the lead screw. 在车床中，它用于接合和分离丝杠以进行螺纹切削。这包括一对半螺母，能够在与丝杠啮合的垂直滑动中滑动。 |
| Fretting fatigue | 微动疲劳 |
Fatigue fracture that initiate at a surface area where fretting has occurred. The progressive damage to a solid surface that arises from fretting. 在发生微动的表面区域开始的疲劳断裂。由微动引起的对固体表面的渐进性损坏。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Air composition | 空气成分 |
The sea-level composition (in per cent by volume) of air at a temperature of 15°C and a pressure of 1 atm is mainly 78.084% nitrogen, 20.947% oxygen and 0.934% argon. The remaining 0.035% consists of carbon dioxide, neon, helium, methane, krypton, hydrogen, oxides of nitrogen, xenon, ozone, iodine, carbon monoxide, and ammonia. Different sources give slightly different figures for the composition. Not included are water vapour (typically 0.4%) and pollutants such as sulfur dioxide. 在15°C的温度和1个大气压的压力下，空气的海平面成分（体积百分比）主要是78.084%的氮气、20.947%的氧气和0.934%的氩气。剩余的0.035%由二氧化碳、氖、氦、甲烷、氪、氢、氮的氧化物、氙、臭氧、碘、一氧化碳和氨组成。不同的来源给出的组成略有不同。不包括水蒸气（通常为0.4%）和二氧化硫等污染物。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Engine emissions | 发动机排放 |
(exhaust emissions) The pollutants contained in the exhaust gases from an internal-combustion engine. （废气排放）内燃机废气中所含的污染物。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Scratch hardness | 划痕硬度 |
The resistance of a material, such as a metal, alloy, plastic, or mineral, to scratching by a much harder indenter, such as a diamond stylus, moved slowly across the surface. The scratch hardness number is computed from the loads and the dimensions of the residual scratch. 一种材料（如金属、合金、塑料或矿物）对更硬的压头（如金刚石触针）划伤的抵抗力，在表面上缓慢移动。根据载荷和残余划痕的尺寸计算划痕硬度值。 |
| Failure of the bolt | 螺栓失效 |
Term implying that the bolt has broken or the threads have stripped. There can be many reasons for this. 表示螺栓断裂或螺纹脱落的术语。原因可能有很多种。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Transverse direction | 横向 |
Literally, the “across” direction, usually signifying a direction or plane perpendicular to the direction of working. In rolled plate or sheet, the direction across the width is often called long transverse, and the direction through the thickness, short transverse. 从字面上看，“横穿”方向，通常表示与工作方向垂直的方向或平面。在轧制钢板或薄板中，横跨宽度的方向通常称为长横向，穿过厚度的方向称为短横向。 |
| Energy losses (Unit kJ) | 能量损失（单位kJ） |
A commonly-used misnomer in view of the conservation-ofenergy principle, but used to mean energy converted into forms that are not used in a process, for example thermal energy from a heat engine dissipated to the surroundings, or produced by friction in a machine, or by surface drag. 从能量守恒原理来看，这是一个常用的术语错误，但可以用于表示转换为过程中未使用的形式的能量，例如，从热机散发到周围环境的热能，或由机器中的摩擦或表面阻力产生的热能。 |
| Slant fracture | 倾斜裂缝 |
A type of fracture appearance, typical of plane-stress fractures, in which the plane of metal separation is inclined at an angle (usually about 45°) to the axis of the applied stress. 一种断裂现象，典型的平面应力断裂，其中金属分离面与施加应力的轴成一定角度（通常约45°）倾斜。 |
| Kilocalorie | 千卡 |
(Cal, kg-cal, kilogram-calorie, large calorie) An obsolete (i.e. non-SI) unit of energy equal to 1 000 cal. （卡，千克卡，千克卡路里，大卡路里）一种已被淘汰的（即非国际单位制）能量单位，等于1000卡。 |
| Athermal transformation | 非热变化 |
A reaction that proceeds without benefit of thermal fluctuations; that is, thermal activation is not required. In contrast, a reaction that occurs at constant temperature is an isothermal transformation; thermal activation is necessary in this case and the reaction proceeds as a function of time. 在没有热波动的情况下进行的反应；也就是说，不需要热激活。相反，在恒温下发生的反应是等温转变。在这种情况下，热活化是必要的，并且反应作为时间的函数进行。 |
| Dimensional stability | 尺寸稳定性 |
Ability of a plastic part to retain the precise shape in which it was molded, fabricated, or cast. 塑料零件保持其成型、制造或铸造时的精确形状的能力。 |
| Rosette | 玫瑰形的结 |
Strain gages arranged to indicate, at a single position, strain in three different directions. 应变计布置成在单个位置指示三个不同方向的应变。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Natural aging | 自然时效 |
Spontaneous aging of a supersaturated solid solution at room temperature. 过饱和固溶体在室温下的自发时效。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Oldham coupling | 十字联轴节 |
(double-slider coupling) A device for connecting a pair of misaligned parallel shafts, on the end of each of which are flanges having diametral tenons (tongues) that engage with matching slots spaced at 90° in an intermediate disc. As the coupling rotates, the disc compensates for shaft offset by sliding along each tenon in turn. Low-friction surfaces are requisite and the disc is often made of a polymer. An alternative arrangement has the slots in the flanges and the tenons on the disc. （双滑块联轴器）一种连接一对未对准平行轴的装置，在每个平行轴的端部有法兰，法兰具有直径榫（舌），与中间盘中间隔90°的匹配槽接合。当联轴器旋转时，圆盘通过依次沿每个榫头滑动来补偿轴偏移。低摩擦表面是必需的，阀盘通常由聚合物制成。另一种布置方式是法兰上的槽和阀盘上的榫头。 |
| Alloy steels | 合金钢 |
Steels that contain alloying elements such as chromium, nickel, molybdenum, manganese, silicon, tungsten, and vanadium. These are added to improve properties such as the hardenability, toughness, strength, wear resistance, and corrosion resistance compared with those of plain-carbon steel. Low-alloy steels have a total alloy content (including carbon) of less than about 8%. They are hardenable and have strength up to 30% higher than plain-carbon steels. High-alloy steels contain considerably more alloy content and are developed for specific properties such as superior corrosion and chemical resistance. 含有铬、镍、钼、锰、硅、钨和钒等合金元素的钢。添加这些是为了提高与普通碳钢相比的淬透性、韧性、强度、耐磨性和耐腐蚀性等性能。低合金钢的总合金含量（包括碳）小于约8%。它们是可硬化的，强度比普通碳钢高出30%。高合金钢含有相当多的合金含量，并针对特定性能而开发，例如卓越的耐腐蚀性和耐化学性。 |
| Black annealing | 黑退火 |
Box annealing or pot annealing ferrous alloy sheet, strip, wire to impart a black color to the oxidized surface. 对铁合金板、带、线进行箱式退火或罐式退火，使氧化表面呈黑色。 |
| Water column | 水柱 |
Water in a tube, which may be vertical or inclined. If the tube is open to the atmosphere, the vertical height h from a datum level to the water surface is a measure of the water static pressure p at the datum level given by p − B = ρgh where B is the barometric pressure, ρ denotes the water density, and g is the acceleration due to gravity. 管道中的水，可以是垂直的或倾斜的。如果管道向大气开放，则从基准面到水面的垂直高度h是基准面处水静压p的量度，由p给出−B=ρgh，其中B是大气压力，ρ表示水密度，g是重力引起的加速度。 |
| Valve plug | 阀塞 |
A conical or cylindrical plug, in which there are transverse holes, in a valve, such as a plug valve. Flow through the holes occurs when the plug is rotated. 阀门中的圆锥形或圆柱形阀塞，其中有横向孔，如旋塞阀。旋转阀塞时，会发生通过孔的流动 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Sliding-vane compressor | 滑片压缩机 |
(rotary-vane compressor, vane compressor) A rotary compressor in which gas is compressed as the spaces between spring-loaded sliding vanes held in an offset rotor reduce as the rotor revolves within a cylindrical housing. （旋转叶片压缩机，叶片压缩机）一种旋转式压缩机，当转子在圆柱形外壳内旋转时，偏置转子中的弹簧加载滑动叶片之间的空间减小，从而压缩气体。 |
| Design stress (Unit Pa) | 设计应力（单位Pa） |
The greatest allowable stress in a component or structure that will not result in failure under normal operating conditions. 在正常操作条件下不会导致失效的部件或结构中的最大许用应力。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Accelerated testing | 加速测试 |
A type of testing, for rates of wear, fatigue, corrosion etc., in which failure times are reduced by employing greater loads, more frequent power cycling, higher vibration levels, higher humidity, higher temperatures, greater potential differences etc. than would be encountered in normal operation. 一种测试类型，用于测试磨损率、疲劳率、腐蚀率等，通过采用比正常运行中更大的负载、更频繁的功率循环、更高的振动水平、更高湿度、更高温度、更大的电位差等，减少故障时间。 |
| Liquation temperature | 液化温度 |
The lowest temperature at which partial melting can occur in an alloy that exhibits the greatest possible degree of segregation. 偏析程度最高的合金发生部分熔融的最低温度。 |
| Spray quenching | 喷雾淬火 |
A quenching process using spray nozzles to spray water or other liquids on a part. The quench rate is controlled by the velocity and volume of liquid per unit area per unit of time of impingement. 使用喷嘴将水或其他液体喷射到零件上的淬火过程。淬火速率由每单位撞击时间内每单位面积的液体速度和体积控制。 |
| Spring clip | 弹簧夹 |
A clip made of a material such as spring steel which grips an inserted part. 由弹簧钢等材料制成的夹子，用于夹住插入的零件。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Thermal insulation (insulation) | 隔热（绝缘） |
A material that may be a low-conductivity solid, or a porous solid or fabric in which there are voids containing air or another gas, resulting in overall low thermal conductivity. When applied to the surface of a hot or cold object, surface heat transfer is generally reduced. 一种材料，可以是低导电性固体，或多孔固体或织物，其中存在含有空气或其他气体的空隙，从而导致整体低导热性。当应用于热或冷物体的表面时，表面传热通常减少。 |
| Vapour static pressure | 蒸汽静压 |
(Unit Pa or bar) A pressure analogous to hydrostatic pressure, where the fluid is a vapour such as steam. A term used in geothermal applications. （单位Pa或bar）类似于静水压力的压力，其中流体是蒸汽，如蒸汽。地热应用中使用的术语。 |
| Preload accuracy | 预载精度 |
A measure of the precision with which a given tool or procedure creates preload in a bolt when the bolt is tightened. A common torque wrench, for example, is said to produce preload with an accuracy of +30%. The mean preload, however, may not be that which the designer intended, or may not be what he should have intended. Accuracy as used here, in other words, is synonymous with Scatter. 当螺栓拧紧时，给定工具或程序在螺栓中产生预紧力的精度度量。例如，一个普通的扭矩扳手据说可以产生精度为+30%的预载。然而，平均预载可能不是设计者预期的。这里使用的准确度是分散度的同义词。 |
| Combustion | 燃烧氧化 |
An exothermic chemical reaction in which a fuel and an oxidant, typically air, react together to release a significant quantity of thermal energy in the presence of a flame. In the case of fluid fuels, ignition may be from an electric spark or compression of the 一种放热化学反应，其中燃料和氧化剂（通常是空气）一起反应，在火焰存在的情况下释放大量热能。 |
| Rolled thread | 滚制螺纹 |
A thread formed by plastically deforming the surface of the blank rather than by cutting operations. Increases fatigue life and thread strength, but is not possible (or perhaps economical) on larger sizes. 通过塑性变形坯料表面而不是通过切割操作形成的螺纹。增加疲劳寿命和螺纹强度，但不太可能（或者说是经济上不太可能）用于较大的尺寸。 |
| Sample variance (s²) | 样本方差（s²） |
The sum of the squares of the differences between each observed value and the sample average divided by the sample size minus one. It is a point estimate of the population variance. 每个观测值与样本平均值之差的平方和除以样本大小减1。它是总体方差的点估计。 |
| Anti-freeze | 防冻液 |
A substance such as ethylene glycol added to the cooling system of a watercooled engine to lower the freezing point of the cooling water and also inhibit the formation of rust and other deposits. 一种物质，如乙二醇，添加到水冷发动机的冷却系统中，以降低冷却水的冰点，并抑制生锈和其他沉积物的形成。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Radial engine | 径向发动机 |
A piston engine in which the cylinders are arranged radially around the crankshaft, a design commonly used in early aircraft engines. 气缸沿径向围绕曲轴布置的活塞式发动机，这种设计通常用于早期飞机发动机。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Salt-velocity meter | 盐速计 |
A volume flow meter based on detecting the transit time for a small quantity of salt or radioactive isotope in a flow by measuring electrical conductivity or radiation level. 一种体积流量计，通过测量电导率或辐射水平来检测流量中少量盐或放射性同位素的渡越时间。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Critical diameter | 临界直径 |
(D) Diameter of the bar that can be fully hardened with 50% martensite at its center. （D）中心有50%马氏体可完全硬化的棒材直径。 |