| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Track rod | 横拉杆 |
A bar connecting the ends of the steering arms in an automotive vehicle. 连接汽车转向臂端部的杆。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Multiple threaded screw | 多螺纹螺钉 |
A screw with two or more threads cut around the periphery of the workpiece to provide an increased lead with a specified pitch. 一种螺钉，具有围绕工件周边切割的两个或多个螺纹，以提供具有指定螺距的增加的导程。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Deformation (Unit 1/s) | 变形（单位1/s） |
A change in the form of a body due to stress, thermal change, change in moisture, or other causes. In solid mechanics, any change, reversible (elastic) or permanent (plastic), in the shape or size of parts of a body, or the whole body, caused by external or internal loading. It includes extension, compression, bending, and twisting. The same state of deformation in a body can appear as different combinations of elongation and shear. To state how much of the total strain is shear, it is split into dilatation and deviatoric components, the former changing volume but not shape, the latter shape but not volume. 由于压力、热变化、水分变化或其他原因导致的身体形态变化。在固体力学中，由外部或内部载荷引起的身体各部分或整个身体的形状或大小的任何可逆（弹性）或永久（塑性）变化。它包括拉伸、压缩、弯曲和扭曲。物体中相同的变形状态可以表现为伸长和剪切的不同组合。为了说明总应变中有多少是剪切，将其分为膨胀分量和偏差分量，前者改变体积但不改变形状，后者改变形状但不改变体积。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Torque pack | 扭矩包 |
A geared wrench which multiplies input torque and provides a read-out of output torque. In effect, a combination of a Torque wrench and a Torque multiplier. 一种齿轮扳手，可增加输入扭矩并提供输出扭矩读数。实际上，它是扭矩扳手和扭矩倍增器的组合。 |
| Static fatigue | 静态疲劳 |
A term referring to a time-dependent reduction in strength with a static (noncyclic) load. The term may refer to hydrogen-induced delayed cracking or the effect of creep on the strength of plastics. Delayed fracture caused by environmental effects under dead-weight loading of materials such as glass. The name is unfortunate, as cyclic loads are not involved and glass is not susceptible to fatigue. 指静态（非循环）载荷下强度随时间变化的降低。该术语可指氢致延迟开裂或蠕变对塑料强度的影响。在玻璃等材料的自重荷载下，由环境影响引起的延迟断裂。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Dimension line | 尺寸线 |
A line on an engineering drawing with a numeral above it that shows the length of a feature, usually in millimetres. 工程图上的一条线，上面有一个数字，表示特征的长度，通常以毫米为单位。 |
| Translational joint | 平移铰 |
A robot joint where the controlled variable is straight line movement. 控制变量为直线运动的机器人关节。 |
| Lubricant | 润滑剂 |
Any substance interposed between two surfaces for the purpose of reducing the friction or wear between them. 为了减少两个表面之间的摩擦或磨损而置于两个表面间的任何物质。 |
| Slip | 滑落 |
Plastic deformation by the irreversible shear displacement (translation)of one part of a crystal relative to another in a definite crystallographic direction and usually on a specific crystallographic plane. Sometimes called glide. 晶体的一部分在一定的晶体学方向上相对于另一部分的不可逆剪切位移（平移）引起的塑性变形，通常在特定的晶体主义平面上。有时被称为滑翔。 |
| Orange peel | 橘皮 |
A surface roughening in the form of a pebble-grained pattern where a metal of unusually coarse grain is stressed beyond its elastic limit. Also known as pebbles and alligator skin. 一种以卵石颗粒图案形式出现的粗糙化表面，其中晶粒异常粗的金属受到的应力超过其弹性极限。也称为卵石和鳄鱼皮。 |
| Sigma phase | σ相 |
A hard, brittle, nonmagnetic intermediate phase with a tetragonal crystal structure, containing 30 atoms per unit cell, space group P42/mnm, occurring in many binary and ternary alloys of the transition elements. The composition of this phase in the various systems is not the same, and the phase usually exhibits a wide range in homogeneity. Alloying with a third transition element usually enlarges the field of homogeneity and extends it deep into the ternary section. 一种硬、脆、非磁性中间相，具有四方晶体结构，每单位晶胞含有30个原子，空间群P42/mnm，存在于许多过渡元素的二元和三元合金中。该相在各种系统中的组成不尽相同，并且该相通常表现出宽范围的均匀性。与第三过渡元素的合金化通常会扩大均匀性范围，并将其延伸到三元区。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Annealing twin | 退火孪晶 |
A twin form in a crystal during recrystallization. 重结晶过程中晶体中的孪晶形式。 |
| Working pressure (Unit Pa) | 工作压力（单位Pa） |
The pressure at which a pressure vessel, such as a boiler, is designed to operate under normal conditions. 压力容器（如锅炉）设计用于在正常条件下运行的压力。 |
| Concentrated load | 集中负荷 |
A load on a component which is distributed over a very small area, idealized as the line load of a wedge or knife edge, and the point load of a cone. 分布在非常小的区域上的部件上的载荷，理想化为楔形或刀刃的线载荷和锥体的点载荷。 |
| Fastener testing | 紧固件测试 |
A determination or verification that the fastener meets its specification requirements. 确定或验证紧固件符合其规范要求。 |
| Working section | 工作区 |
That part of a wind tunnel in which models are placed for testing, or where detailed measurements are performed. 风洞中放置模型进行测试或进行详细测量的部分。 |
| Thermodynamic properties | 热力学性质 |
Temperature, pressure, and the intensive properties that define the state of a working fluid: specific internal energy, specific enthalpy and specific entropy. 温度、压力和定义工作流体状态的密集属性：比内能、比焓和比熵。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Reverse engineering | 逆向工程 |
The disassembly of a machine, mechanism, system or device, measurement of its component parts, and identification of the materials used so that if required, a functioning replica can be produced. 拆卸机器、机构、系统或装置，测量其组成部分，并识别所用材料，以便在需要时可以生产出功能正常的复制品。 |
| Oil-cooled | 油冷却 |
A term for a machine that uses circulating oil to remove heat. 使用循环油散热的机器的术语。 |
| Ductility | 延展性 |
The ability of a material to deform plastically before fracturing. Measured by elongation or reduction in area in a tensile test, by height of cupping in a cupping test, or by the radius or angle of bend in a bend test. 材料在断裂前发生塑性变形的能力。通过拉伸试验中的伸长率或面积减少量、杯突试验中的杯突高度或弯曲试验中的弯曲半径或角度来测量。 |
| Thread insert | 螺纹嵌件 |
(threaded bushing) Either a thin cylinder with an internal thread (and sometimes also an external thread) or a helical coil of wire, pressed or screwed into a hole to accept a bolt or screw. Used in material too soft or a component too thin to be threaded, to change one form of thread to another or to repair a damaged thread. （螺纹衬套）一种带有内螺纹（有时也有外螺纹）的薄圆柱体或螺旋形线圈，压入或拧入孔中以接受螺栓或螺钉。用于材料太软或部件太薄而无法螺纹连接，用于将一种形式的螺纹更换为另一种形式或修复损坏的螺纹。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Trepanning | 开孔 |
Trepanning is a machining process for producing a circular hole or groove in solid stock, or for producing a disk, cylinder, or tube from solid stock, by the action of a tool containing one or more cutters (usually single-point) revolving around a center. 开孔是一种机械加工工艺，通过包含一个或多个围绕中心旋转的刀具（通常为单点）的作用，在实心坯料中制造圆孔或凹槽，或从实心坯料生产圆盘、圆柱体或管。 |
| Durometer hardness | 硬度计硬度 |
Measure of the indentation hardness of plastics. It is the extent to which a spring-loaded steel indenter protrudes beyond the pressure foot into the material. 塑料压痕硬度的测量。它是弹簧加载的钢压头超出压力脚伸入材料的程度。 |
| Cyaniding | 氰化 |
A case-hardening process in which a ferrous material is heated above the lower transformation range in a molten salt containing cyanide to cause simultaneous absorption of carbon and nitrogen at the surface and, by diffusion, create a concentration gradient. Quench hardening completes the process. 一种表面硬化工艺，将含铁材料在含氰化物的熔融盐中加热至低于较低转变范围，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。淬火硬化完成该过程。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Balance weight | 平衡器 |
A corrective mass used in the static or dynamic balancing of a rotating object. 用于旋转物体的静态或动态平衡的校正质量。 |
| Universal joint (Hooke’s joint) | 万向节（胡克接头） |
A double-pivoted connection that allows power and torque to be transmitted between two shafts at an angle to each other. For constant driving angular velocity of the input yoke, the angular velocity of the output yoke fluctuates by amounts depending on the angle of intersection of the shafts. Speeds of the driving and driven shafts may be made identical (giving a constant-velocity joint) when an intermediate shaft, at each end of which there is a universal joint, is interposed. The driving and driven shafts must be equally inclined to the intermediate shaft, the two forks of which must lie in the same plane. 一种双枢轴连接，允许动力和扭矩以一定角度在两个轴之间传递。对于输入磁轭的恒定驱动角速度，输出磁轭的角速度根据轴的相交角度波动。当插入中间轴时，驱动轴和从动轴的速度可以相同（提供恒定速度接头），中间轴的两端都有万向节。主动轴和从动轴必须与中间轴倾斜相等，中间轴的两个叉必须位于同一平面内。 |
| Working stress (Unit Pa) | 工作应力（单位Pa） |
The stress under which a component or structure is designed to operate under normal conditions. 部件或结构设计为在正常条件下运行的应力。 |
| Condensation shock | 冷凝冲击 |
For supersonic flow of a moist gas through a divergent nozzle, condensation occurs in the form of spontaneous nucleation at some point downstream of that at which the temperature falls to the saturation temperature. The condensation process proceeds rapidly, and results in a fairly thick discontinuity termed a condensation shock. 对于通过发散喷嘴的湿气体超音速流动，在温度降至饱和温度的点下游的某个点处，冷凝以自发成核的形式发生。凝结过程进行得很快，导致相当厚的不连续性，称为凝结激波。 |
| Castellated nut | 槽形螺母 |
A nut having slots across the hexagonal faces, used with a bolt having a drilled hole so that a split (cotter) pin may be inserted through both nut and bolt to prevent unscrewing. 一种在六角面上有槽的螺母，与具有钻孔的螺栓一起使用，以便将开口（开口）销插入穿过螺母和螺栓以防止拧松。 |
| Coefficient of friction (μ) | 摩擦系数（μ） |
(coefficient of kinetic friction, coefficient of sliding friction, friction coefficient, μ) The ratio of the frictional force F to the normal force N between two surfaces in contact, i.e. μ = F/N. Static friction is when there is no relative sliding; kinetic friction when there is. For structural components sliding on one another, the coefficient of friction is the ratio of the force causing the sliding to the force perpendicular to the sliding component surfaces. The coefficient of friction is dimensionless with values between zero and one. The number characterising the force necessary to slide or roll one material along the€surface of another. If an object has a weight N and the coefficient of friction is μ, then the force F necessary to move it without acceleration along a level surface is F = μN. The coefficient of static friction determines the force necessary to initiate movement; the coefficient of kinetic friction determines the force necessary to maintain movement. Kinetic friction is usually smaller than static friction. （动摩擦系数、滑动摩擦系数、摩擦系数，μ）两个接触表面之间摩擦力F与法向力N的比值，即μ=F/N。静摩擦是指没有相对滑动时；有摩擦时的动摩擦。对于相互滑动的结构部件，摩擦系数是引起滑动的力与垂直于滑动部件表面的力的比值。摩擦系数是无量纲的，其值介于0和1之间。代表一种材料沿另一种材料的表面滑动或滚动所需的力的数字。如果一个物体的重量为N并且摩擦系数为μ，那么在没有加速度的情况下沿水平表面移动它所需的力F为F=μN。静摩擦系数决定了启动运动所需的力；动摩擦系数决定了保持运动所需的力。动摩擦通常小于静摩擦。两个物体之间的力（F）与将这些物体压在一起的法向力（N）的无量纲比：μ（或f）=（F/N）。 |
| Thermal analysis | 热分析 |
A method for determining transformations in a metal by noting the temperatures at which thermal arrests occur. These arrests are manifested by changes in slope of the plotted or mechanically traced heating and cooling curves. When such data are secured under nearly equilibrium conditions of heating and cooling, the method is commonly used for determining certain critical temperatures required for the construction of equilibrium diagrams. 一种通过记录发生热阻的温度来确定金属转变的方法。这些阻力表现为绘制或机械追踪的加热和冷却曲线斜率的变化。当这些数据在加热和冷却的近似平衡条件下得到保证时，该方法通常用于确定构建平衡图所需的某些临界温度。 |
| Microstrain | 微应变 |
The strain over a gage length comparable to interatomic distances. These are the strains being averaged by the macrostrain measurement. Microstrain is not measurable by currently existing techniques. Variance of the microstrain distribution can, however, be measured by x-ray diffraction. 与原子间距离相当的标距上的应变。这些是通过宏观应变测量得到的平均应变。现有技术无法测量微应变。然而微应变分布的变化可以通过x射线衍射来测量。 |
| Vibrograph | 示振器 |
An instrument that records vibrations in a system over time. 记录系统随时间变化的振动的仪器。 |
| Atomic volume | 原子体积 |
Volume of unit cell per atom. 每个原子的晶胞体积。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Acicular ferrite | 针状铁素体 |
A highly substructured non-equiaxed ferrite that forms upon continuous cooling by a mixed diffusion and shear mode of transformation that begins at a temperature slightly higher than the temperature transformation range for upper bainite. It is distinguished from bainite in that it has a limited amount of carbon available; thus, there is only a small amount of carbide present. Ferrite crystallite growing, apparently, as in the course of bainitic transformation. It has a lath-like shape and an increased dislocation 一种高度亚结构的非等轴铁素体，在连续冷却时通过混合扩散和剪切相变模式形成，其开始温度略高于上贝氏体的温度转变范围。它与贝氏体的区别在于它的碳含量有限。因此，仅存在少量碳化物。显然，铁素体微晶在贝氏体转变过程中生长。它具有板条状的形状和增加的位错。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Condensate strainer | 冷凝水过滤器 |
A filter in a steam plant used to remove particulate matter from condensate before it is added to feedwater. 蒸汽设备中的过滤器，用于在将冷凝水添加到给水中之前去除冷凝水中的颗粒物。 |
| Compression wave | 压缩波 |
(dilatation wave) In a fluid or a solid, a progressive wave or wavefront that compresses the medium through which it propagates. （膨胀波）在流体或固体中，压缩介质传播的行波或波前。 |
| Pitch | 沥青节距 |
The nominal distance between two adjacent thread roots or crests. In screw threads, the distance from a point on one thread to a corresponding point on the next thread measured parallel to the axis. In the case of spur gears, indicates the size of the gear teeth and is correctly called diametral pitch. 两个相邻螺纹根部或顶部之间的标称距离。在螺纹中，从一根螺纹上的一点到下一根螺纹对应点的距离，平行于轴线测量。对于正齿轮，表示齿轮齿的尺寸，正确地称为径向节距。 |
| Condenser | 冷凝器 |
A heat exchanger in which a substance is changed from its vapour phase to its liquid phase by reducing its temperature to below the saturation temperature. 一种热交换器，通过将物质的温度降低到饱和温度以下，将其从气相变为液相。 |
| Bond strength (Unit Pa) | 结合强度（单位Pa） |
The tensile, compressive or shear stress at which joints fail, e.g. by fracture or excessive deformation. 接头失效的拉伸、压缩或剪切应力，例如断裂或过度变形。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Thread run-out | 螺纹耗尽 |
That portion of the threads which are not cut or rolled full depth, but which provide the transition between full-depth threads and the body or head. Officially called thread washout or vanish, although the term run-out is more popular. (Run-out is officially reserved for rotational eccentricity, as defined by total indicator readings or the like.) 未全深度切割或轧制的螺纹部分，但提供全深度螺纹与主体或头部之间的过渡。官方称之为螺纹冲蚀或消失，但术语“耗尽”更为流行。（跳动是官方为旋转偏心度保留的，由总指示器读数等定义。） |
| Absorption | 吸收 |
The process whereby a fluid permeates a porous solid, or a gas is dissolved by a liquid. 流体渗透多孔固体或气体被液体溶解的过程。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Flange bolt | 法兰螺栓 |
A bolt with a built in washer-like flange just below the head. 在头部下方带有内置垫圈状法兰的螺栓。 |
| Octane number | 辛烷值 |
(octane rating) A measure of the anti-knock properties of a fuel taken as the percentage by volume of iso-octane in the fuel. （辛烷值）以燃料中异辛烷的体积百分比表示的燃料抗爆性能的量度。 |
| Strain | 拉紧 |
The unit of change in the size or shape of a body due to force. Also known as nominal strain. 物体的大小或形状因力而变化的单位。也称为标称应变。 |
| Ideal gas laws | 理想气体定律 |
The law relating pressure, temperature and volume of an ideal (perfect) gas pV = mRT, where R is the gas constant. The law implies that at constant temperature T, the product of pressure p and volume V is constant (Boyle’s law), and at constant pressure, the volume is proportional to the temperature (Charles’ law). 与理想（完美）气体的压力、温度和体积相关的定律pV=mRT，其中R是气体常数。该定律意味着在恒定温度T下，压力p和体积V的乘积是恒定的（波义耳定律），而在恒定压力下，体积与温度成正比（查尔斯定律）。 |
| Bánki turbine | 班基涡轮机 |
A cross-flow, impulse-type water turbine for very low heads in which a jet of water in the form of a flat sheet passes transversely through the turbine, so going through the runner twice. The thin runner blades which run horizontally across the turbine parallel to the axis of rotation are profiled in cross section. 一种用于非常低水头的横流脉冲式水轮机，其中平板形式的水射流横向穿过涡轮机，因此穿过转轮两次。平行于旋转轴水平穿过涡轮机的薄转轮叶片在横截面上具有轮廓。 |
| Rotary blower | 旋转鼓风机 |
(rotary compressor) A positive-displacement gas compressor which may be of the blade type, helical-screw type, meshing-lobe type (the Roots blower), or sliding-vane type. （旋转式压缩机）一种容积式气体压缩机，可以是叶片式、螺旋式、啮合凸角式（罗茨鼓风机）或滑动叶片式。 |
| Stress ratio (A or R) | 应力比（A或R） |
The algebraic ratio of two specified stress values in a stress cycle. Two commonly used stress ratios are the ratio of the alternating stress amplitude to the mean stress, A = Sa/Sm, and the ratio of the minimum stress to the maximum stress, R = Smin/Smax. 应力循环中两个指定应力值的代数比。两种常用的应力比是交变应力振幅与平均应力之比，A=Sa/Sm，以及最小应力与最大应力之比R=Smin/Smax。 |
| Acceleration due to gravity | 重力加速度 |
(acceleration of free fall, gravitational acceleration, g) (Unit m/s²) The acceleration of a freely-falling body in a vacuum, with a mean value at sea level of approximately 9.81 m/s². （自由落体加速度，重力加速度，g）（单位m/s²）自由落体在真空中的加速度，在海平面处的平均值约为9.81m/s²。 |
| Millimetre of water | 毫米水柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of water 1 mm high. Approximately equal to 9.81 Pa. 一种非SI压力单位，等于1毫米高的垂直水柱施加的压力。大约等于9.81Pa。 |
| Clevis | U形夹 |
A U-shaped hook with holes at the ends through which a retaining bolt or pin (clevis pin) passes. 一种U形钩，末端有孔，固定螺栓或销（U形销）穿过这些孔。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Dynamic mechanical measurement | 动态机械测量 |
A technique in which either the modulus and/or damping of a substance under oscillatory load or displacement is measured as a function of temperature, frequency, or time, or a combination thereof. 一种技术，其中在振荡载荷或位移下测量物质的模量和/或阻尼作为温度、频率或时间或其组合的函数。 |
| Vacuum servo | 真空服务器 |
A vacuum-operated servomotor which is used in a motor vehicle to provide a brake effort greater than the capability of the driver. 一种真空操作的伺服电机，用于机动车中，以提供大于驾驶员能力的制动力。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Size effect | 尺寸效应 |
Effect of the dimensions of a piece of metal on its mechanical and other properties and on manufacturing variables such as forging reduction and heat treatment. In general, the mechanical properties are lower for a larger size. 金属件的尺寸对其机械和其他性能以及对制造变量（如锻造、压下和热处理）的影响。一般来说，尺寸越大，机械性能越低。 |
| Stress-intensity factor | 应力强度因子 |
A scaling factor, usually denoted by the symbol K, used in linear-elastic fracture mechanics to describe the intensification of applied stress at the tip of a crack of known size and shape. At the onset of rapid crack propagation in any structure containing a crack, the factor is called the critical stress-intensity factor, or the fracture toughness. 一种标度因子，通常用符号K表示，在线弹性断裂力学中用于描述已知尺寸和形状的裂纹尖端施加应力的增强。在任何含有裂纹的结构中，裂纹快速扩展开始时，该因子称为临界应力强度因子，或断裂韧性。 |
| Maximum-and-minimum thermometer | 最高和最低温度计 |
(minimum-maximum thermometer, Six’s thermometer) A liquid-in-glass instrument designed to register the maximum and minimum temperatures experienced over a given time period. （最低-最高温度计，Six's温度计）一种液体玻璃仪器，用于记录给定时间段内经历的最高和最低温度。 |
| Vertical engine | 立式发动机 |
A piston engine having the cylinders above the crankshaft. 气缸位于曲轴上方的活塞发动机。 |
| Free ferrite | 游离铁氧体 |
Ferrite that is formed directly from the decomposition of hypoeutectoid austenite during cooling, without the simultaneous formation of cementite. Also proeutectoid ferrite. 在冷却过程中亚共析奥氏体分解直接形成的铁素体，没有同时形成渗碳体。也是先共析铁氧体。 |
| Isothermal annealing | 等温退火 |
Austenitizing a ferrous alloy and then cooling to and holding at a temperature at which austenite transforms to a relatively soft ferrite carbide aggregate. 将铁合金奥氏体化，然后冷却至奥氏体转变为相对软的铁素体碳化物集合体的温度并保持该温度。 |
| Gasket stress | 垫片应力 |
The contact stress exerted on the gasket by the joint members. 连接件施加在垫片上的接触应力。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Clevis joint | U形接头 |
A joint formed by two parallel cantilever beams pressed upon a component between the beams. 由两个平行悬臂梁压在梁之间的部件上形成的接头。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Heat treatment | 热处理 |
(heat treating) Alteration of the mechanical properties of materials, particularly metals, by different sequences of heating, holding at temperature, and cooling at different rates. Heating and cooling a solid metal or alloy in such a way as to obtain desired conditions or properties. Heating for the sole purpose of hot working is excluded from the meaning of this definition. （热处理）材料，特别是金属的机械性能的改变，通过不同的加热顺序、温度保持和不同速率的冷却。加热和冷却固体金属或合金，以获得所需的条件或性能。仅用于热加工的加热不属于本定义的含义。 |
| Austenite finish temperature (Af) | 奥氏体完成温度（Af） |
Temperature at which the transformation of martensite into austenite completes upon heating. The same designation is also applied to nonferrous alloys in which martensite transforms into some parent phase. 加热时马氏体转变为奥氏体的温度。相同的名称也适用于马氏体转变为某些母相的有色合金。 |
| Thermal reactor | 热反应器 |
An enlarged exhaust manifold bolted directly to the cylinder head of a piston engine, in which the oxidation of carbon monoxide and unburned hydrocarbons in the exhaust gas is enhanced. 一种扩大的排气歧管，直接用螺栓固定在活塞式发动机的气缸盖上，其中一氧化碳和未燃烧碳氢化合物的氧化作用增强。 |
| Material velocity | 材料速度 |
The velocity of sound in a body (e.g., a bolt). A term used in the ultrasonic measurement of bolt stress or strain. 声音在物体（例如螺栓）中的速度。用于螺栓应力或应变的超声波测量的术语。 |
| Wrist pin | 腕销 |
A stud projecting from a crank as an attachment for a connecting rod. wrought alloys Metal alloys that are initially cast and then shaped into final form by processes such as extrusion, forging, or rolling. 从曲柄上伸出的一个螺柱，作为连接杆的附件。锻造合金最初铸造，然后通过挤压、锻造或轧制等工艺成形为最终形状的金属合金。 |
| Damage | 损伤 |
1. The deterioration of a component or structure in fault or accident conditions, reducing or preventing its ability to perform its intended function. 2. The accumulation of defects or microcracks in the microstructure of a body loaded monotonically or in fatigue, which weakens the body and can lead to crack propagation and failure. 1.部件或结构在故障或事故条件下的劣化，降低或阻止其执行预期功能的能力。2.在承受单调载荷或疲劳载荷的物体的微观结构中累积的缺陷或微裂纹，这会削弱物体，并可能导致裂纹扩展和失效。 |
| Edge distance | 边距 |
The distance from the edge of a bearing specimen to the center of the hole in the direction of applied force. 在作用力方向上，从轴承试样的边缘到孔中心的距离。 |
| Compression member | 压缩构件 |
A structural component, the major loading on which is compressive. 一种结构部件，其上的主要载荷是压缩的。 |
| Toothed belt | 齿带 |
A flat belt, typically of a reinforced-rubber material, with transverse teeth that engage with teeth on a wheel or pulley. 一种扁平皮带，通常由增强橡胶材料制成，带有横向齿，与车轮或皮带轮上的齿啮合。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Anneal to temper | 退火回火 |
A final partial anneal that softens a cold worked nonferrous alloy to a specified level of hardness or tensile strength. 将冷加工的有色金属合金软化到规定的硬度或抗拉强度水平的最终局部退火。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Austenite-stabilizer | 奥氏体稳定剂 |
Alloying element expanding the γ-phase field in the corresponding phase diagram, which manifests itself in a decrease of the A3 temperature and an increase of the A4 temperature in binary alloys Fe–M as well as in a decrease of A1 temperature in ternary alloys Fe–C–M (M is an alloying element). The solubility of austenite-stabilizers in ferrite is much lower than in austenite. Under the influence of austenite-stabilizers, austenite can become thermodynamically stable down to room temperature. 合金元素扩展了相应相图中的γ相场，这表现为二元合金Fe-M中A3温度的降低和A4温度的升高，以及A1温度的降低三元合金Fe–C–M（M是合金元素）。奥氏体稳定剂在铁素体中的溶解度远低于在奥氏体中的溶解度。在奥氏体稳定剂的影响下，奥氏体可以在低至室温时变得热力学稳定。 |
| Joint space | 关节空间 |
The description of the position and orientation of a robot in terms of the rotational angles and translational positions of the joints. Kinematic analysis, normally using homogeneous transforms, allows conversion between this description and the end‐effector position and orientation in x,y,z space. 根据关节的旋转角度和平移位置描述机器人的位置和方向。通常使用齐次变换的运动学分析允许在该描述与x、y、z空间中的末端执行器位置和方向之间进行转换。 |
| Extensometer | 引伸计 |
An instrument for measuring changes in length over a given gage length caused by application or removal of a force. Commonly used in tension testing of metal specimens. Any instrument which measures the change in length of a part as the part is loaded. 一种用于测量在给定标距上由施加或移除力引起的长度变化，在零件加载时测量零件长度变化的仪器。常用于金属试样的拉力试验。 |
| Wing nut | 蝶形螺母 |
A nut having two opposite protruding wings to permit hand tightening. 一种螺母，有两个相对突出的翼片，可以用手拧紧。 |
| Swift cup test | 斯威夫特杯测试 |
A simulative cupping test in which circular blanks of various diameters are clamped in a die ring and deep drawn into cups by a flat-bottomed cylindrical punch. 一种模拟拔杯试验，将不同直径的圆形坯料夹紧在模环中，并用平底圆柱冲头将其深拉入杯中。 |
| Active accommodation | 主动适应能力 |
The use of information from sensors, for example, in a vision system, that allows a robot to show accommodation to the environment. 使用来自传感器的信息，例如在视觉系统中，允许机器人显示对环境的适应。 |
| Rockwell superficial hardness test | 洛氏表面硬度试验 |
Same as Rockwell hardness test, except that smaller minor and major loads are used. 与洛氏硬度测试相同，只是使用较小的次要载荷和主要载荷。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| Spring temper | 弹簧回火 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about two-thirds of the way from full hard to extra spring temper. 非铁合金和一些铁合金的一种回火，其特点是抗拉强度和硬度约为全硬回火到超弹性回火的三分之二。 |
| Fretting fatigue | 微动疲劳 |
Fatigue fracture that initiate at a surface area where fretting has occurred. The progressive damage to a solid surface that arises from fretting. 在发生微动的表面区域开始的疲劳断裂。由微动引起的对固体表面的渐进性损坏。 |
| Pressure storage tank | 压力贮存器 |
(pressure vessel) A closed container for storing gases or volatile liquids, such as liquefied gases, at pressures significantly above atmospheric pressure. Such tanks are commonly cylindrical with domed ends, spherical, spheroidal, torispherical or hemispherical. （压力容器）密闭容器：在大气压以上的压力下储存气体或挥发性液体，如液化气体的密闭容器。此类贮存器通常为圆柱形，具有半球形端部、球形、球面或半球形。 |
| Damage mechanics | 损伤机制 |
The theory of degradation in bodies, particularly fracture by accumulated microstructural damage. Analyses take two approaches: (a) the use of some critical integrated function of stress and strain at which cracking is initiated and propagated; (b) incorporation of damage in the stress–strain curves to reflect weakened material. 物体退化理论，尤其是累积微观结构损伤导致的断裂。分析采用两种方法：（a）使用裂纹开始和扩展时的应力和应变的一些临界积分函数；（b）应力-应变曲线中包含损伤，以反映弱化材料。 |
| Allotropy | 同素异形体 |
A near synonym for polymorphism. Allotropy is generally restricted to describing polymorphic behavior in elements, terminal phases, and alloys whose behavior closely parallels that of the predominant constituent element. 多态性的近义词。同素异形体通常仅限于描述元素、终端相和合金中的多晶型行为，其行为与主要组成元素的行为非常相似。 |
| Elastic interactions | 弹性相互作用 |
When a bolt is tightened it partially compresses the joint members ‘‘in its own neighborhood.’’ When nearby bolts are tightened later, they further compress the joint in this region. This allows the first bolt to relax a little (lose a little preload). Tightening bolts on the opposite side of the joint, however, might increase preload in some of the earlier bolts tightened on the near side. These shifts and changes in the elastic energy stored in individual bolts, during assembly, are called elastic interactions. 当螺栓拧紧时，它会“在其自身附近”部分压缩接头构件稍后拧紧附近的螺栓时，进一步压缩该区域的接头。这允许第一个螺栓稍微松弛（失去一点预载）。但拧紧接头另一侧的螺栓可能会增加早期在近侧拧紧的一些螺栓的预载。在装配过程中，储存在单个螺栓中的弹性能量的这些位移和变化称为弹性相互作用。 |
| Modulus of rupture | 断裂模量 |
Nominal stress at fracture in a bend test or torsion test. In bending, modulus of rupture is the bending moment at fracture divided by the section modulus. In torsion, modulus of rupture is the torque at fracture divided by the polar section modulus. 弯曲试验或扭转试验中的标称断裂应力。在弯曲中，断裂模量是断裂时的弯矩除以截面模量。在扭转中，断裂模量是断裂时的扭矩除以极截面模量。 |
| Hot-wire analyzer | 热电阻丝型分析仪 |
An electrical atmosphere analysis device that is based on the fact that the electrical resistivity of steel is a linear function of carbon content over a range from 0.05% C to saturation. The device measures the carbon potential of furnace atmospheres (typically). This term is not to be confused with the hot-wire test which measures heat extraction rates. 一种基于以下事实的电气氛分析设备：钢的电阻率是从0.05%C到饱和范围内的碳含量的线性函数。该设备测量炉内气氛的碳势（通常）。不要将此术语与测量热提取率的热线测试相混淆。 |
| Dynamic compressor | 动态压缩器 |
A machine, such as a centrifugal or axial compressor, that compresses a gas by rotational rather than reciprocating motion. 一种机器，例如离心式或轴流式压缩机，通过旋转而不是往复运动来压缩气体。 |
| Carburizing flame | 渗碳火焰 |
A gas flame that will introduce carbon into some heated metals, as during a gas welding operation. A carburizing flame is a reducing flame, but a reducing flame is not necessarily a carburizing flame. 一种气体火焰，会在气焊操作中将碳引入一些加热的金属中。渗碳火焰是还原火焰，但还原火焰不一定是渗碳火焰。 |
| Cylinder head | 气缸盖 |
The machined casting, typically of aluminium alloy or cast iron, that fits above the cylinder block of a piston engine and closes off the cylinders. It normally includes part of the combustion chambers and holes for the valves and spark plugs. 活塞式发动机缸体上方的机械铸件，通常由铝合金或铸铁制成，用于封闭气缸。它通常包括燃烧室的一部分以及阀门和火花塞的孔。 |
| Chain | 链 |
A series of connected links, typically of steel. For lifting, pulling, securing, etc., each link is a closed loop, often in the form of a ring. For power transmission, the links are designed to mesh with the teeth of a sprocket wheel. In contrast to belt drives, chain drives tend to be employed in high-torque applications. 一系列连接的链接，通常是钢制的。对于提升、拉动、固定等，每个链节都是一个闭合环，通常呈环形。对于动力传输，链节设计为与链轮的齿啮合。与皮带传动相比，链传动往往用于高扭矩应用。 |
| Beta annealing | β退火 |
Producing a beta phase by heating certain titanium alloys in the temperature range of which this phase forms followed by cooling at an appropriate rate to prevent its decomposition. 通过在形成β相的温度范围内加热某些钛合金，然后以适当的速率冷却以防止其分解，从而产生β相。 |
| Full hard | 全硬化 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state beyond which the material can no longer be formed by bending. In specifications, a full hard temper is commonly defined in terms of minimum hardness or minimum tensile strength (or, alternatively, a range of hardness or strength) corresponding to a specific percentage of cold reduction following a full anneal. For aluminum, a full hard temper is equivalent to a reduction of 75% from dead soft ; for austenitic stainless steels, a reduction of about 50 to 55%. 有色金属合金和一些铁合金的回火状态，大致对应于冷加工状态，超过该状态，材料就不能再通过弯曲形成。在规范中，完全硬质回火通常定义为与完全退火后的特定冷压下率百分比相对应的最小硬度或最小抗拉强度（或者，硬度或强度范围）。对于铝来说，完全硬回火相当于从极软状态减少75%；对于奥氏体不锈钢，减少约50%至55%。 |
| Induction tempering | 感应回火 |
Tempering of steel using low-frequency electrical induction heating. 钢的回火采用低频电感应加热。 |
| Pop rivet | 拉钉 |
A hollow rivet that enables a connexion to be made from one side only of an assembly. 一种空心铆钉，使连接只能从组件的一侧进行。 |
| Toothed gearing | 齿轮传动 |
In principle, friction between circular discs in tangential contact could be used to transmit rotation and power between shafts, but the power level would be very limited and the velocity ratio affected by slip. To make the drive positive, gear wheels are used instead in which teeth extend above and below the diameters (the pitch-circle diameters) of discs in ideal rolling contact. The diagram shows the nomenclature for spur gears, the simplest type of gearing between parallel shafts, which are cylindrical in shape with straight teeth parallel to the axis of rotation. 原则上，切向接触的圆盘之间的摩擦可用于在轴之间传递旋转和动力，但动力水平非常有限，速比受滑动的影响。为了使驱动积极，使用齿轮代替，齿轮中的齿延伸到理想滚动接触的圆盘直径（节圆直径）的上方和下方。该图显示了直齿轮的名称，这是平行轴之间最简单的齿轮传动类型，其形状为圆柱形，直齿平行于旋转轴。 |
| Spinner | 旋转器 |
A co-axial streamlined fairing enclosing the hub of a propeller and rotating with it. 一种同轴流线型整流罩，包围螺旋桨毂并随其旋转。 |
| Stress cracking | 应力开裂 |
A family of failure modes, each of which involves high stress and chemical action. The family includes Hydrogen embrittlement, Stress corrosion cracking, stress embrittlement, and hydrogen-assisted stress corrosion. 一系列失效模式，每种模式都涉及高应力和化学作用。该系列包括氢脆、应力腐蚀开裂、应力脆化和氢辅助应力腐蚀。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Composite property | 复合属性 |
In thermodynamics, a property defined in terms of the properties of a closed system and its surroundings, such as the non-flow exergy function. 在热力学中，根据封闭系统及其周围环境的性质定义的性质，例如非流动火用函数。 |
| Atmometer | 气压计 |
(atmidometer, evaporimeter) An instrument that measures the rate of evaporation of water from a surface into the atmosphere. （湿度计，蒸发计）测量水从表面蒸发到大气中的速率的仪器。 |
| Graphitizing | 石墨化退火 |
Annealing a ferrous alloy in such a way that some or all of the carbon is precipitated as graphite. 以使部分或全部碳以石墨的形式沉淀的方式对铁合金进行退火。 |
| Hypereutectic alloy | 过共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of alloying element compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，任何合金，其组成与共晶组成相比具有过量的合金元素，并且其平衡微观结构包含一些共晶结构。 |
| Caustic cracking | 苛性开裂 |
A form of stress-corrosion cracking most frequently encountered in carbon steels or iron-chromiumnickel alloys that are exposed to concentrated hydroxide solutions at temperatures of 200 to 250 °C (400 to 480 °F). Also known as caustic embrittlement. 在200至250°C（400至480°F）的温度下暴露于浓氢氧化物溶液中的碳钢或铁铬镍合金中最常遇到的一种应力腐蚀开裂形式。也称为碱脆。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Ratchet coupling | 棘轮联轴器 |
A joint employing a ratchet system between two shafts, so that not only does the driven shaft run in one direction only, but also the driven shaft can, if necessary, run more quickly than the driving shaft. 在两个轴之间采用棘轮系统的接头，这样不仅从动轴只能在一个方向上运行，而且在必要时，从动轴可以比驱动轴运行得更快。 |
| Strain energy | 应变能 |
A measure of the energy absorption characteristics of a material determined by measuring the area under the stress-strain diagram. 通过测量应力-应变图下的面积确定的材料能量吸收特性的度量。 |
| Oxygen probe | 定氧测头 |
An atmosphere-monitoring device that electronically measures the difference between the partial pressure of oxygen in a furnace or furnace supply atmosphere and the external air. 一种大气监测装置，以电子方式测量熔炉或熔炉供应大气中的氧分压与外部空气之间的差值。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Autonomous energy system | 自主能源系统 |
(stand-alone energy system) A sole source of electricity, usually small-scale, for applications remote from a grid, especially with energy storage in the system. Hydroelectric, photovoltaic, wind-power and other renewable systems are well suited to stand-alone applications. （独立能源系统）一种唯一的电力来源，通常是小规模的，用于远离电网的应用，尤其是系统中的能量存储。水电、光伏、风力和其他可再生能源系统非常适合独立应用。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Distortion | 扭曲 |
Any deviation from an original size, shape, or contour that occurs because of the application of stress or the release of residual stress. 由于施加应力或释放残余应力而发生的与原始尺寸、形状或轮廓的任何偏差。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Centripetal | 向心力 |
Acting or moving in a direction towards the axis of rotation. 在朝向旋转轴的方向上起作用或移动。 |
| Machine tool | 机床工具 |
A powered machine, such as a borer, grinder, lathe, milling machine or planer, used for cutting and shaping metal, plastics, composites, etc. (machining). A machining centre is a CNC machine tool working about several axes, having a stock of tools and automatic tool changing ability, which is capable of diverse machining operations under automated control. 一种动力机器，如钻孔机、磨床、车床、铣床或刨床，用于切割和成形金属、塑料、复合材料等（机加工）。加工中心是围绕多个轴工作的CNC机床，具有刀具库存和自动换刀能力，能够在自动化控制下进行各种加工操作。 |
| Blowing | 吹气 |
The process by which a gas is transferred through a porous surface over which there is a gas flow. The effect is used to decrease skin friction and increase heat transfer, for example in turbine-blade cooling. 气体通过有气流的多孔表面转移的过程。该效应用于减少表面摩擦和增加传热，例如在涡轮叶片冷却的过程中。 |
| Computer-aided manufacturing | 计算机辅助制造 |
(CAM, computer-integrated manufacturing, CIM) The use of computers in all branches of manufacturing, not only to control machines and robots for manufacturing and assembly, but also for process planning, and monitoring progress of materials and components during production, etc. （CAM，计算机集成制造，CIM）在制造的所有分支中使用计算机，不仅可以控制制造和组装的机器和机器人，还可以进行工艺规划，以及在生产过程中监控材料和组件的进度等。 |
| Turbine flow meter | 涡轮流量计 |
(axial flow meter, propeller meter) An in-line flow meter in which the rotation speed N of a propeller or rotor is a measure of the mass flowrate ṁ. Calibration is always necessary but with appropriate design ṁ is closely proportional to N over a wide range. （轴向流量计、螺旋桨流量计）一种串联流量计，其中螺旋桨或转子的转速N是质量流量的测量值ṁ. 校准总是必要的，但需要适当的设计ṁ在很宽的范围内与N成正比。 |
| Tightness | 紧密度 |
A measure of the mass leak rate from a gasketed joint. 垫圈接头质量泄漏率的测量值。 |
| Condenser vacuum | 冷凝器真空 |
The sub-atmospheric pressure imposed on the condenser of a steam-power plant which leads to an appreciable increase in overall efficiency. 施加在蒸汽发电厂冷凝器上的低于大气压的压力导致整体效率显着提高。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Grain refiner | 晶粒细化机 |
A material added to a molten metal to induce a finer-than-normal grain size in the final structure. 添加到熔融金属中以在最终结构中产生比正常晶粒尺寸更细的材料。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Half hard | 半硬化回火 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength about mid-way between that of dead soft and full hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于完全软回火和完全硬回火之间。 |
| Atomizing humidifier | 雾化加湿器 |
A humidifier that functions by spraying fine droplets of water into an airstream. 一种加湿器，通过将细小的水滴喷射到气流中来发挥作用。 |
| Stress relieving | 应力消除 |
Heating to a suitable temperature, holding long enough to reduce residual stresses, and then cooling slowly enough to minimize the development of new residual stresses. 加热到合适的温度，保持足够长的时间以减少残余应力，然后缓慢冷却以尽量减少新残余应力的产生。 |
| Creep fatigue | 蠕变疲劳 |
The effects of combined creep and fatigue at high homologous temperatures in metals, and in other materials such as polymers having time-dependent behaviour. 金属和其他材料（例如具有时间相关行为的聚合物）在高同源温度下的组合蠕变和疲劳的影响。 |
| U-bolt | U型螺栓 |
A rod threaded at both ends and bent into a U-shape. It is used for clamping. An externally threaded fastener bent in the shape of the letter U and with both ends threaded. 两端有螺纹并弯曲成U形的杆。用于夹紧。一种外螺纹紧固件，弯曲成字母U的形状，两端带有螺纹。 |
| Computer vision | 计算机视觉 |
The digitization and processing of optical images/patterns by computer in order to recognize parts, orientation, etc. in manufacturing. 通过计算机对光学图像/图案进行数字化和处理，以在制造过程中识别零件、方向等。 |
| Absolute viscosity | 绝对粘度 |
A measure of the internal shear properties of fluids, expressed as the tangential force per unit area at either of two horizontal planes separated by one unit thickness of a given fluid, one of the planes being fixed and the other moving with unit velocity. 流体内部剪切特性的量度，表示为两个水平面中的任何一个上的单位面积切向力，两个水平面被给定流体的一个单位厚度隔开，其中一个平面固定，另一个以单位速度移动。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Fracture stress | 断裂应力 |
The true normal stress on the minimum cross-sectional area at the beginning of fracture. This term usually applies to tension tests of unnotched specimens. 断裂开始时最小横截面积上的真实正应力。该术语通常适用于无缺口试样的拉伸试验。 |
| Slip line | 滑移线 |
The trace of the slip plane on a viewing surface; the trace is usually observable only if the surface has been polished before deformation. The usual observation on metal crystals (under the light microscope) is of a cluster of slip lines known as a slip band. 滑动平面在观察表面上的轨迹；只有在变形前对表面进行抛光，才能观察到痕迹。通常对金属晶体的观察（在光学显微镜下）是一组称为滑移带的滑移线。 |
| Workspace (Unit m³) | 工作空间（单位m³） |
(working-space volume) The volume around the base frame of a robot, defined by the reach of the robot. The robot can thus only perform tasks within this volume. （工作空间体积）机器人基架周围的体积，由机器人的可达范围定义。因此，机器人只能执行该体积内的任务。 |
| Fatigue failure | 疲劳失效 |
Failure that occurs when a specimen undergoing fatigue completely fractures into two parts or has softened or been otherwise significantly reduced in stiffness by thermal heating or cracking. 当经历疲劳的试样完全断裂成两部分或因热加热或开裂而软化或刚度显着降低时发生的失效。 |
| Maximum load (Pmax) | 最大负载（Pmax） |
(1) The load having the highest algebraic value in the load cycle. Tensile loads are considered positive and compressive loads negative. (2)Used to determine the strength of a structural member; the load that can be borne before failure is apparent. （1）负载循环中具有最高代数值的负载。拉伸荷载视为正荷载，压缩荷载视为负荷载。（2）用于确定结构构件的强度；失效前可承受的载荷是明显的。 |
| Slenderness ratio | 长细比 |
The effective unsupported length of a uniform column divided by the least radius of gyration of the cross-sectional area. 均匀柱的有效无支撑长度除以横截面积的最小回转半径。 |
| Springback | 回弹 |
The extent to which metal tends to return to its original shape or contour after undergoing a forming operation. 金属在经历成形操作后趋于恢复其原始形状或轮廓的程度。 |
| Temperature factor | 温度系数 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. Accounts for the effects of thermal expansion and the temperature-induced change in the velocity of sound. 用于螺栓应力或应变超声波测量的校准常数。说明了热膨胀和温度引起的声速变化的影响。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Design heating load (Unit kW) | 设计热负荷（单位kW） |
The heating requirements based on a specified number of heating degree days, or required to maintain a building or other enclosed space at a specified temperature for a given outside temperature. 基于指定的采暖度日数的加热要求，或在给定的外部温度下将建筑物或其他封闭空间保持在指定温度下所需的加热要求。 |
| Elasticity | 弹性 |
The property of a material by virtue of which deformation caused by stress disappears on removal of the stress. A perfectly elastic body completely recovers its original shape and dimensions after release of stress. 一种材料的特性，通过这种特性，由应力引起的变形在去除应力后消失。完全弹性体在应力释放后完全恢复其原始形状和尺寸。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Thermal compressor | 热压缩机 |
1. (thermocompressor) A jet compressor used to boost the pressure of low-pressure waste or exhaust steam. 2. A device consisting of an absorber, a generator, a pump, and a throttling device, used instead of a mechanical vapour compressor in an absorption-cooling refrigeration system. 1.（热压缩机）用于提升低压废蒸汽或排气压力的喷射压缩机。2.一种由吸收器、发电机、泵和节流装置组成的装置，用于替代吸收冷却制冷系统中的机械蒸汽压缩机。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Complete decarburization | 完全脱碳 |
Decarburization with sufficient carbon loss to show only clearly defined ferrite grains under metallographic examination. 脱碳，具有足够的碳损失，以在金相检查下仅显示清晰定义的铁素体晶粒。 |
| Spring clip | 弹簧夹 |
A clip made of a material such as spring steel which grips an inserted part. 由弹簧钢等材料制成的夹子，用于夹住插入的零件。 |
| Quench annealing | 淬火退火 |
Annealing an austenitic ferrous alloy by solution heat treatment followed by rapid quenching. 通过固溶热处理然后快速淬火对奥氏体铁合金进行退火。 |
| Engine emissions | 发动机排放 |
(exhaust emissions) The pollutants contained in the exhaust gases from an internal-combustion engine. （废气排放）内燃机废气中所含的污染物。 |
| Dynamic hardness | 动态硬度 |
(rebound hardness) The resistance of a material to local indentation by a rapidly-moving rigid indenter. In most practical methods the indenter is allowed to fall under gravity on to the surface of the material when the rebound height is a measure of the dynamic hardness. （回弹硬度）材料对快速移动的刚性压头局部压痕的阻力。在大多数实际方法中，当回弹高度是动态硬度的测量值时，允许压头在重力作用下落在材料表面上。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Anode | 阳极 |
That electrode in a battery or corrosion cell which produces electrons. It is the electrode which is destroyed (corrodes). 电池或腐蚀电池中产生电子的电极。被破坏（腐蚀）的是电极。 |
| Plug gauge | 塞规 |
A steel gauge used to determine the dimension or dimensions of a hole. It may be straight or tapered, and is typically circular, but in principle can have any cross section. 用于确定孔的尺寸的钢制量规。它可以是直的或锥形的，通常是圆形的，原则上可以有任何横截面。 |
| Crack size (a) | 裂纹尺寸（a） |
A lineal measure of a principal planar dimension of a crack. This measure is commonly used in the calculation of quantities descriptive of the stress and displacement fields. In practice, the value of crack size is obtained from procedures for measurement of physical crack size, original crack size, or effective crack size, as appropriate to the situation under consideration. 裂纹主平面尺寸的线性度量。这种测量通常用于计算描述应力场和位移场的量。在实践中，裂纹尺寸的值是通过测量物理裂纹尺寸、原始裂纹尺寸或有效裂纹尺寸的程序获得的，视情况而定。 |
| Hardness profile | 硬度分布 |
Hardness as a function of distance from a fixed reference point (usually from the surface). 硬度作为距固定参考点（通常距表面）的距离的函数。 |
| Clip gauge | 夹规 |
A displacement gauge consisting of two thin strain-gauged cantilever arms attached through knife edges to a testpiece to give the load–line displacement in fracture mechanics test pieces, or used as an extensometer in tensile tests. 一种位移计，由两个通过刀刃连接到试件上的薄应变测量悬臂组成，以提供断裂力学试件中的载荷线位移，或用作拉伸试验中的引伸计。 |
| Thermochemical treatment | 热化学处理 |
Heat treatment carried out in a medium suitably chosen to produce a change in the chemical composition of the object by exchange with the medium. 在适当选择的介质中进行热处理，以通过与介质交换产生物体化学成分的变化。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Cellular materials | 蜂窝材料 |
There are three broad classes of materials that have a sponge-like structure containing many small closed or open (interlinked) pores or cells. Natural cellular materials include bone, cork, sponge, and wood, and have numerous well-known uses. Wide ranges of cellular plastics are produced using blowing or foaming agents, such as air, ammonium carbonate, sodium bicarbonate, etc., to create pores during the processing of thermoplastic or thermosetting polymers. Rigid foams have moderate compressive strength and can be moulded and machined. 有三大类材料具有海绵状结构，包含许多小的封闭或开放（互连）孔或细胞。天然多孔材料包括骨骼、软木、海绵和木材，有许多众所周知的用途。使用发泡剂或发泡剂（如空气、碳酸铵、碳酸氢钠等）生产各种泡沫塑料，以在热塑性或热固性聚合物加工过程中产生孔隙。硬质泡沫具有中等抗压强度，可模制和机加工。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| Compressive stress (Unit Pa) | 压缩应力（单位Pa） |
The compressive load per unit area at a point in a component. 部件中某点的每单位面积的压缩载荷。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Forge | 锻造 |
To shape metal while holt and plastic by a hammering or forcing process. Dies used in process. 通过锤击或强制过程使金属成型，同时保持塑料成型。过程会使用模具。 |
| Dowel | 销钉 |
A headless cylindrical pin that fits into corresponding holes in mating components, thus ensuring relative location. A round metal or wooden pin. A pin, usually of circular shape like a cylinder, used to pin or fasten something in position temporarily or permanently. 一种圆头金属或木制圆柱销，可插入配合组件的相应孔中，从而确保相对位置，用于暂时或永久地将某物固定或固定到位。 |
| Angularity | 角度 |
The underfaces of the nut and the bolt head should be exactly perpendicular to the thread or shank axes. If the angle between the face and the axis is, for example, 868 or 948, the fastener is said to have an angularity of 48 (sometimes called Perpendicularity). 螺母和螺栓头的底面应与螺纹或柄轴完全垂直。例如，如果面和轴之间的角度为868或948，则称紧固件的角度为48（有时称为垂直度）。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Tension joint | 张力接头 |
A joint which is primarily subjected to loads acting more or less parallel to the axes of the bolts. 主要承受或多或少平行于螺栓轴线的载荷的接头。 |
| Torsion-bar suspension | 扭杆悬架 |
A type of motor-vehicle suspension in which one end of a torsion bar is rigidly fixed to the chassis while the other carries a lever to which are attached the components that carry a wheel. In a torsion-beam suspension, a beam connects the wheels on either side of the vehicle. 一种汽车悬架，其中扭力杆的一端刚性固定在底盘上，而另一端带有一个杠杆，杠杆上连接着承载车轮的部件。在扭转梁悬架中，梁连接车辆两侧的车轮。 |
| Following flank | 跟随侧翼 |
The flank of a thread opposite to the leading flank. 与前牙面相对的螺纹牙面。 |
| Feather key | 滑键 |
A parallel key fastened in either the shaft or in the hub of a member sliding on it. When fastened in the shaft, it must be long enough to hold or drive the sliding member in any of its positions on the shaft. When in the sliding member the key need only be as long as the hub. 一种平行键，固定在轴上或在其上滑动的构件的轮毂上。当固定在轴上时，其长度必须足以将滑动构件固定或驱动在轴上的任何位置。当处于滑动构件中时，键只需与轮毂一样长。 |
| Fluid mechanics | 流体力学 |
The study of fluids in motion (fluid dynamics) or fluid statics where there is no relative motion between fluid particles. Fluid statics concerns primarily the variation of pressure with altitude or depth; it includes aerostatics and hydrostatics. Fluid dynamics includes the topics of aerodynamics, gas dynamics, hydraulics, hydrodynamics and many aspects of acoustics, chemical engineering, flight, lubrication, meteorology, non-Newtonian fluid flow, oceanography, power-plant technology, propulsion, and turbomachinery. 研究运动中的流体（流体动力学）或流体静力学，其中流体粒子之间没有相对运动。流体静力学主要关注压力随高度或深度的变化；它包括空气静力学和流体静力学。流体动力学包括空气动力学、气体动力学、水力学、流体动力学以及声学、化学工程、飞行、润滑、气象学、非牛顿流体流动、海洋学、发电厂技术、推进和涡轮机械的许多方面。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Swept volume (Unit m³) | 扫描体（单位m³) |
In the cylinder of a piston engine or other device, the volume between top and bottom dead centre positions of a piston; equal to πR2S where R is the piston radius and S is the stroke. 在活塞发动机或其他装置的气缸中，活塞上止点和下止点位置之间的体积；等于πR2S，其中R是活塞半径，S是冲程。 |
| Dead space | 死区 |
(dead volume) (Unit m³) That volume of a gas-filled thermometer in which the gas is not at the same temperature as that being measured. （死容）（单位m³）充气温度计的体积，其中气体的温度与被测温度不同。 |
| Preheating | 预热 |
Heating before some further thermal or mechanical treatment. For tool steel, heating to an intermediate temperature immediately before final austenitizing. For some nonferrous alloys, heating to a high temperature for a long time, to homogenize the structure before working. In welding and related processes, heating to an intermediate temperature for a short time immediately before welding, brazing, soldering, cutting, or thermal spraying. 在进一步热处理或机械处理之前加热。对于工具钢，在最终奥氏体化之前立即加热至中间温度。对于一些非铁合金，在工作前长时间加热到高温，以使结构均匀化。在焊接和相关工艺中，在焊接、钎焊、钎焊、切割或热喷涂之前，立即加热到中间温度。 |
| Athermal transformation | 非热变化 |
A reaction that proceeds without benefit of thermal fluctuations; that is, thermal activation is not required. In contrast, a reaction that occurs at constant temperature is an isothermal transformation; thermal activation is necessary in this case and the reaction proceeds as a function of time. 在没有热波动的情况下进行的反应；也就是说，不需要热激活。相反，在恒温下发生的反应是等温转变。在这种情况下，热活化是必要的，并且反应作为时间的函数进行。 |
| Finishing temperature | 终轧温度 |
The temperature at which hot working is completed. 完成热加工的温度。 |
| Carbon restoration | 碳修复 |
Replacing the carbon lost in the surface layer from previous processing by carburizing this layer to substantially the original carbon level. Sometimes called recarburizing. 通过将该层渗碳到基本上原始的碳水平来替换先前处理中在表面层中损失的碳。有时称为再碳化。 |
| Zero initial conditions | 零初始条件 |
The assumption normally made in control engineering that up to a start time defined as t = 0, all variables have zero value. 在控制工程中通常作出的假设，即在定义为t=0的开始时间内，所有变量均为零值。 |
| Total heat (Unit kJ) | 总热量（单位kJ） |
An alternative term for enthalpy. It is inappropriate as it suggests that it includes kinetic energy in the same way as total enthalpy, but it does not. Also, heat and enthalpy are quite different quantities, as their definitions show. 焓的另一个术语。这是不恰当的，因为它表明，它包括动能的方式与总焓相同，但它实际上并不是的。此外，热和焓是完全不同的量，正如它们的定义所示。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Diaphragm meter | 隔膜计 |
A dry flow meter in which there are two or more interconnected chambers, each having a diaphragm in the wall. The chambers empty and fill alternately and the flow rate of gas is determined from the movement of diaphragms. Diaphragm meters are commonly used to monitor domestic and commercial gas supply. 一种干式流量计，其中有两个或多个相互连接的腔室，每个腔室的壁上都有一个隔膜。腔室交替排空和填充，气体流速由隔膜的移动确定。隔膜流量计通常用于监测家用和商用燃气供应。 |
| Bypass flow meter | 旁通流量计 |
(shunt flow meter) A flow meter installed in a pipework bypass which may itself be part of the flow meter. An orifice plate is used to ensure a fraction of the main flow passes through the bypass. （分流流量计）安装在管道旁路中的流量计，它本身可能是流量计的一部分。孔板用于确保一部分主流通过旁路。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Welding | 焊接 |
In tribology, the bonding between metallic surfaces in direct contact, at any temperature. A joining process in which the mating surfaces are at least softened, or more usually melted, unlike soldering and brazing. In solid-state (non-melting) welding, similar or dissimilar metals or thermoplastics may be joined by applying pressure to hot interfaces. In forge welding, joining is achieved by compression across the join between pre-heated workpieces. In friction welding (spin welding) one of the contacting surfaces is rotated rapidly before being loaded against the other. On contact, heat generated by friction softens the materials and permits severe plastic deformation that seals the joint. In friction stir welding, a wear-resistant tool is rotated rapidly, indents the surfaces and is traversed to form a join line. Resistance welding involves simultaneous pressure and electrically-generated heat, as in spot welding where a heavy electric current is passed for a short time through metal sheets which are pressed together between electrodes. 在摩擦学中，在任何温度下直接接触的金属表面之间的结合。与钎焊和钎焊不同，接合面至少软化或更通常熔化的接合工艺。在固态（非熔化）焊接中，相似或不同的金属或热塑性塑料可通过向热界面施加压力来连接。在锻造焊接中，通过压缩预热工件之间的连接来实现连接。在摩擦焊接（旋转焊接）中，一个接触表面在被加载到另一个表面之前快速旋转。接触时，摩擦产生的热量使材料软化，并允许密封接头的严重塑性变形。在搅拌摩擦焊中，耐磨工具快速旋转，使表面凹陷，并横穿形成连接线。电阻焊涉及同时产生的压力和电产生的热量，如点焊，在点焊中，大电流短时间通过电极之间压在一起的金属板。 |
| Radial flow | 径向流 |
radial flow Fluid flow for which the principal direction of flow is either radially inward or radially outward relative to an axial direction. 径向流动流体流动的主要方向是径向向内或径向向外流动。 |
| Waste-heat recovery | 废热回收 |
The recovery of thermal energy from flue and exhaust gases, or from liquids heated in industrial processes. Recovery devices include pre-heaters, recuperators, regenerators, and waste-heat boilers. 从烟道和废气中或从工业过程中加热的液体中回收热能。回收装置包括预热器、回热器、再生器和余热锅炉。 |
| Controlled cooling | 控制冷却 |
Cooling from an elevated temperature in a predetermined manner, to avoid hardening, cracking, or internal damage, or to produce desired microstructure or mechanical properties. 以预定方式从升高的温度冷却，以避免硬化、开裂或内部损坏，或产生所需的微观结构或机械性能。 |
| Ultimate strength | 极限应力 |
The maximum tensile strength a bolt or material can support prior to rupture. Always found in the plastic region of the stress–strain or force–elongation curve, and so is not a design strength. Also called Tensile strength and ultimate tensile strength. The maximum stress (tensile, compressive, or shear) a material can sustain without fracture, determined by dividing maximum load by the original cross-sectional area of the specimen. Also known as nominal strength or maximum strength. 螺栓或材料在断裂前可支撑的最大抗拉强度。总是出现在应力-应变或力-伸长率曲线的塑性区域，因此不是设计强度。也称为抗拉强度和极限抗拉强度。材料在不断裂的情况下能够承受的最大应力（拉伸、压缩或剪切），通过将最大载荷除以试样的原始横截面积来确定。也称为标称强度或最大强度。 |
| Transducer | 传感器 |
A device which converts one form of energy into another. An ultrasonic transducer, for example, converts electrical energy into acoustic energy (at ultrasonic frequencies) and vice versa. 将一种形式的能量转换为另一种形式能量的装置。例如，超声换能器将电能转换为声能（在超声频率下），反之亦然。 |
| Reduction in area (RA) | 缩小面积（RA） |
The difference between the original cross-sectional area of a tensile specimen and the smallest area at or after fracture as specified for the material undergoing testing. Also known as reduction of area. 拉伸试样的原始横截面积与试验材料断裂时或断裂后的最小面积之间的差值，也称为减少面积。 |
| Archimedes screw | 阿基米德螺旋泵 |
A machine which comprises a rotating helical blade inside a closefitting tube, which may be used to pump liquids, slurries (such as sewage), granular materials, etc. If water flows into the top of an inclined or vertical Archimedes screw, the screw will rotate and can be used to drive an electrical generator. 一种机器，它在紧密的管子内包含一个旋转的螺旋叶片，可用于泵送液体、泥浆（如污水）、颗粒材料等。如果水流入倾斜或垂直的阿基米德螺杆的顶部，螺杆将旋转，可用于驱动发电机。 |
| Constant-force spring | 恒力弹簧 |
A spring that has the same restoring force regardless of displacement. The most common type takes the form of a coiled strip that, owing to tight coiling during manufacture, is pre-stressed (a steel measuring tape is an example). The uncoiling force is approximately constant as the change of curvature of the strip is approximately constant. Not to be confused with a clockwork spring from which power can be obtained. 无论位移如何，具有相同恢复力的弹簧。最常见的类型是卷绕带，由于制造过程中的紧密卷绕，该卷绕带是预应力的（钢卷尺就是一个例子）。随着带材曲率的变化近似恒定，开卷力近似恒定。不要与可获得动力的发条弹簧混淆。 |
| Angle of attack (α) | 攻角（α） |
(Unit °) The angle between a reference line on a lifting body and the vector direction of the relative velocity between the body and the fluid through which it is moving. In the case of an aerofoil, turbine, or compressor blade, the usual reference line is the chord line. （单位°）升力体上的参考线与升力体与其运动通过的流体之间的相对速度的矢量方向之间的角度。在机翼、涡轮或压缩机叶片的情况下，通常的参考线是弦线。 |
| Kilo (k) | 千（k） |
An SI unit prefix indicating a multiplier of 103; thus kilometre (km) is a unit of length equal to one thousand metres. 表示乘法器103的SI单位前缀；1千米是长度单位，等于1000米。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Transformation toughening | 相变增韧 |
The improvement of fracture toughness of a material by stress-induced transformation of the microstructure. 通过微结构的应力诱导转变来提高材料的断裂韧性。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Mass flow rate (ṁ) (Unit kg/s) | 质量流量（ṁ）（单位kg/s） |
The mass of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. The corresponding mass flux (ṁ″), with unit kg/s.m², is the mass flow across a real surface or through a duct, divided by the surface or cross-sectional area A, i.e. ṁ″ = ṁ/A or ṁ″ = ρV where ρ is the material density and V is its velocity normal to the surface. 单位时间内流过表面或通过管道或其他管道的材料质量，通常是流体或粉末。相应的质量通量（ṁ″），单位为kg/s.m²，是通过真实表面或通过管道的质量流量除以表面或横截面积A，即ṁ″=ṁ/A或ṁ″=ρV，其中ρ是材料密度，V是其垂直于表面的速度。 |
| Form of thread | 螺纹形式 |
The profile of a thread in an axial plane for a length of one pitch. 一个螺距长度的螺纹在轴向平面中的轮廓。 |
| Maraging steels | 马氏体时效钢 |
Very high-strength iron alloys named after ‘martensitic’ and ‘aging’. They contain nickel, chromium, cobalt, and molybdenum, and form martensite on air cooling with a strength of about 1 GPa. When reheated to about 500°C and aged for some hours, a room-temperature strength of some 2.4 GPa is reached. 以“马氏体”和“时效”命名的超高强度铁合金。它们含有镍、铬、钴和钼，在空气冷却下形成强度约为1GPa的马氏体。当再加热至约500°C并老化数小时时，室温强度达到约2.4GPa。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Cavitation-resistance inducer | 抗气蚀诱导剂 |
An axial-flow pump used upstream of a main pump in order to prevent cavitation in the latter by increasing the inlet head. 在主泵上游使用的轴流泵，通过增加进口压头防止主泵出现气穴。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Crack arrest | 止裂 |
Crack propagation that stops of its own accord when the energy release rate of the loaded component or structure falls below a critical value. If predictable, it can be incorporated into structural-integrity assessments. 当加载部件或结构的能量释放率低于临界值时，裂纹自行停止扩展。如果可以预测，可以将其纳入结构完整性评估。 |
| Dynamics | 动力学 |
The branch of mechanics that deals with objects in motion. Its two main branches are kinematics, which studies motion without regards to its cause, and kinetics, which also takes into account forces that cause motion. 力学中研究运动物体的分支。它的两个主要分支是运动学和动力学，前者研究运动而不考虑其原因，后者也考虑引起运动的力。 |
| Natural aging | 自然时效 |
Spontaneous aging of a supersaturated solid solution at room temperature. 过饱和固溶体在室温下的自发时效。 |
| Damage tolerance | 损伤容限 |
(defect tolerance) A design philosophy that takes into account initial imperfections, crack-growth rates and conditions at final fracture, and uses fracture mechanics to demonstrate that cracks should not grow to their critical length within the design life (or at least should be capable of ready detection). （缺陷公差）考虑初始缺陷、裂纹扩展速率和最终断裂条件的设计理念，并使用断裂力学证明裂纹不应在设计寿命内增长到其临界长度（或至少应能够随时检测）。 |
| Absolute humidity | 绝对湿度 |
The weight of water vapor in a gadwater vapor mixture per unit volume of space occupied, expressed, for example, in grains or pounds per cubic foot. 单位体积空间占用的水蒸气混合物中水蒸气的重量，例如，以谷物或磅/立方英尺表示。 |
| Standard gauge | 标准量规 |
A highly-accurate reference gauge against which to check working gauges. 一种高精度的基准量规，用于检查工作量规。 |
| Cast steel | 铸钢 |
Steel that is cast into shapes. It has superior properties to most cast irons, but is more expensive to produce. 铸成形状的钢。与大多数铸铁相比，它具有优越的性能，但生产成本更高。 |
| Poisson’s ratio (ν) | 泊松比（ν） |
The absolute value of the ratio of transverse (lateral) strain to the corresponding axial strain resulting from uniformly distributed axial stress below the proportional limit of the material. 横向（侧向）应变与相应轴向应变之比的绝对值，该比值由低于材料比例极限的均匀分布的轴向应力产生。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Temper color | 回火颜色 |
A thin, tightly adhering oxide skin that forms when steel is tempered at a low temperature, or for a short time, in air or a mildly oxidizing atmosphere. The color, which ranges from straw to blue depending on the thickness of the oxide skin, varies with both tempering time and temperature. 一种薄的、紧密粘附的氧化皮，当钢在低温或短时间内在空气或轻度氧化气氛中回火时形成。颜色范围从稻草色到蓝色，取决于氧化皮的厚度，随回火时间和温度而变化。 |
| Cup washer | 杯形垫圈 |
A dished leather or neoprene washer fitted to the rod end in some piston-style pumps. 在某些活塞式泵中，安装在杆端的碟形皮革或氯丁橡胶垫圈。 |
| Maximum allowable working pressure (Unit Pa) | 最大允许工作压力（单位Pa） |
The pressure on which the design of a pressure system is based and the highest pressure at which relief valves should be set. The lowest-rated component in the system typically has a design safety factor of 4. 压力系统设计所依据的压力和应设置安全阀的最高压力。系统中最低额定部件的设计安全系数通常为4。 |
| Continuous-type furnace | 连续式炉 |
A furnace used for heat treating materials that progress continuously through the furnace, entering one door and being discharged from another. See belt furnac, direct-fired tunnel-type furnac, rotary retort furnace, shaker-hearth furnace. 一种用于热处理材料的炉子，该炉子连续通过炉子，进入一个门并从另一个门排出。参见带式高炉、直燃隧道式高炉、旋转罐式炉、振动炉。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| Shock load | 冲击载荷 |
The sudden application of an external force that results in a very rapid build-up of stress. 突然施加外力，导致应力迅速增加。 |
| Temper embrittlement | 回火脆化 |
Brittleness that results when certain steels are held within, or are cooled slowly through, a certain range of temperature below the transformation range. The brittleness is manifested as an upward shift in ductile-to-brittle transition temperature but only rarely produces a low value of reduction in area in a smooth-bar tension test of the embrittled material. The anomalous reduction in toughness of martensitic stainless steels when tempered in the range 370–600°C. Embrittlement of alloy steels caused by holding within or cooling slowly through a temperature range just below the transformation range. Embrittlement is the result of the segregation at grain boundaries of impurities such as arsenic, antimony, phosphorus, and tin; it is usually manifested as an upward shift in ductile-to-brittle transition temperature. Temper embrittlement can be reversed by retempering above the critical temperature range, then cooling rapidly. 当某些钢保持在低于转变范围的某一温度范围内或缓慢冷却时产生的脆性。脆性表现为延性到脆性转变温度的向上移动，但在脆性材料的平滑棒材拉伸试验中，很少产生较小的面积减小值。马氏体不锈钢在370–600°C范围内回火时的韧性异常降低。合金钢的脆化是由于在低于转变范围的温度范围内保持或缓慢冷却而引起的。脆化是杂质（如砷、锑、磷和锡）在晶界处偏析的结果；它通常表现为韧脆转变温度的上升。回火脆化可以通过在临界温度范围以上重新回火，然后快速冷却来逆转。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Intermediate annealing | 中间退火 |
Annealing wrought metals at one or more stages during manufacture and before final treatment. 在制造过程中和最终处理之前的一个或多个阶段对锻造金属进行退火。 |
| Scale height (Unit m) | 刻度高度（单位：m） |
The altitude H at which the atmospheric pressure has decreased to a certain fraction of its value at sea level B. It depends on the model adopted for the atmosphere: for an isothermal atmosphere, the pressure decreases exponentially with altitude. If H is taken as the altitude at which the pressure has fallen to B/e, then H = RT/g where R is the gas constant for air, T is the absolute temperature T, and g is the acceleration due to gravity. 大气压力降低到其在海平面B处数值的某一部分的高度H。它取决于大气采用的模型：对于等温大气，压力随高度呈指数下降。如果取H作为压力下降到B/e的高度，则H=RT/g，其中R是空气的气体常数，T是绝对温度T，g是重力引起的加速度。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Collar | 圈、箍 |
A ring secured to, or integral with, a shaft to give axial location. 固定在轴上或与轴成一体以提供轴向位置的环。 |
| Ideal crack | 理想裂缝 |
A simplified model of a crack used in elastic-stress analysis. In a stress-free body, the crack has two smooth surfaces that are coincident and join within the body along a smooth curve called the crack front; in two-dimensional representations, the crack front is called the crack tip. 用于弹性应力分析的裂纹简化模型。在无应力物体中，裂纹有两个光滑表面，它们在物体内沿称为裂纹前缘的平滑曲线重合并连接；在二维表示中，裂纹前缘称为裂纹尖端。 |
| Deviation | 偏差 |
The difference between the actual value and the desired value of a controlled variable. 受控变量的实际值与期望值之间的差值。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Grain growth | 晶粒生长 |
An increase in the average size of the grains in polycrystalline metal, usually as a result of heating at elevated temperature. 多晶金属中晶粒平均尺寸的增加，通常是高温加热的结果。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Coated abrasive | 涂附磨具 |
An abrasive tool consisting of a flexible backing material, such as a woven cloth, paper or vulcanized fibre, a bond material, such as a glue or synthetic resin, and grit. 一种研磨工具，由柔性背衬材料（例如编织布、纸或硫化纤维）、粘合材料（例如胶水或合成树脂）和砂砾组成。 |
| Strain hardening | 应变硬化 |
An increase in hardness and strengthcaused by plastic deformation at temperatures below the recrystallization range. Also known as work hardening. (workhardening) The increase in stress above the initial yield stress required to deform a metal to greater strains in the plastic range at temperatures below the recrystallization range (cold working). Unloading after some strain or work input gives a harder and stronger material. 在低于再结晶范围的温度下，塑性变形导致硬度和强度的增加。也称为加工硬化。（加工硬化）在低于再结晶范围（冷加工）的温度下，使金属在塑性范围内变形至更大应变所需的高于初始屈服应力的应力增加。在一定的应变或功输入后卸载，会得到更硬、更强的材料。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| International System of Units | 国际单位制 |
(SI system of units, Le Système international d’unités) The standard system of units now used almost universally in science and engineering except in the United States. The definitive reference on the SI is a booklet published by the International Bureau of Weights and Measures, often referred to as the BIPM SI Brochure. There are seven base units: metre (symbol m) for length; kilogram (kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred.(kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred. （国际单位制，Le Système international d\\\'unités）目前美国除外，在科学和工程中几乎是普遍使用的标准单位制。SI的最终参考是国际度量衡局出版的小册子，通常称为BIPM SI小册子。有七个基本单位：米（符号m）表示长度；质量为千克（kg）；物质量的摩尔（mol）；时间为秒；开尔文（K）表示温度；电流为安培（A）；而坎德拉（cd）表示发光强度。新的国际单位制定义于2019年5月20日生效，该定义基于自然界的普遍常数（也称为基本物理常数：阿伏伽德罗常数、玻尔兹曼常数和普朗克常数）。这些常数的值也进行了少量调整。除了基本单位外，还有22个相干导出单位，包括平面角的弧度（rad）、立体角的斯特拉迪安（sr）、频率的赫兹（Hz）、力的牛顿（N）、压力的帕斯卡（Pa）、能量、功和热量的焦耳（J）以及功率和辐射通量的瓦特（W）。建议的做法是避免N/mm²、MN/m²等组合。 |
| Friction materials | 摩擦材料 |
Materials having a high coefficient of friction which, when coupled with a long life, may be employed as brake linings or the facing of the plates of a clutch. 具有高摩擦系数的材料，当与长寿命相结合时，可用作制动衬片或离合器片的饰面。 |
| Left hand screw | 左螺旋 |
One that screws into the mating part or advances when turned to the left or counter clockwise. 旋入配合部分或向左或逆时针旋转时前进的螺钉。 |
| Screw area (Unit m²) | 螺丝面积（单位m²） |
The area of a circle described by the tips of a propeller. 螺旋桨尖端所描述的圆的面积。 |
| Air-cooled engine | 风冷发动机 |
An internal-combustion engine directly cooled by airflow, rather than by water flowing through the engine block being cooled by a radiator. 一种由气流直接冷却的内燃机，而不是通过流经发动机缸体的水被散热器冷却。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Mean value | 平均值 |
The average value of a number of data points. Computed by dividing the sum of all data by the number of data points. 多个数据点的平均值。通过将所有数据的总和除以数据点的数量来计算。 |
| Preload | 预载 |
The tension created in a threaded fastener when the nut is first tightened. Often used interchangeably, but incorrectly, with Working load or bolt force or bolt tension 第一次拧紧螺母时螺纹紧固件中产生的张力。经常与工作载荷或螺栓力或螺栓张力互换使用但容易使用不当。 |
| Shell hardening | 壳型硬化 |
A surface-hardening process in which a suitable steel workpiece, when heated through and quench hardened, develops a martensitic layer or shell that closely follows the contour of the piece and surrounds a core of essentially pearlitic transformation product. This result is accomplished by a proper balance among section size, steel hardenability, and severity of quench. 一种表面硬化工艺，在该工艺中，合适的钢工件在加热和淬火硬化后，会形成一层马氏体层或壳，该层或壳紧随工件的轮廓，并包围一个基本上为珠光体相变产物的核心。这一结果通过截面尺寸、钢淬透性和淬火强度之间的适当平衡来实现。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Intergranular cracking | 沿晶断裂 |
Cracking or fracturing that occurs between the grains or crystals in a polycrystalline aggregate. Also called intercrystalline cracking. 多晶聚集体中的晶粒或晶体之间发生的开裂或断裂。也称为晶间断裂。 |
| Minimum stress (Smin) | 最小应力（Smin） |
In fatigue, the stress having the lowest algebraic value in the cycle, tensile stress being considered positive and compressive stress negative. 在疲劳中，循环中代数值最低的应力，拉应力被视为正应力，压应力为负应力。 |
| Finish annealing | 精制退火 |
A subcritical annealing treatment applied to cold-worked low- or medium-carbon steel. Finish annealing, which is a compromise treatment, lowers residual stresses, thereby minimizing the risk of distortion in machining while retaining most of the benefits to machinability contributed by cold working. Compare with final annealing. 适用于冷加工低碳钢或中碳钢的亚临界退火处理。与最终退火相比，精加工退火是一种折衷处理，可降低残余应力，从而最大限度地降低加工中的变形风险，同时保留冷加工对可加工性的大部分好处。 |
| Quench cracking | 淬火开裂 |
Fracture of a metal during quenching from elevated temperature. Most frequently observed in hardened carbon steel, alloy steel, or tool steel parts of high hardness and low toughness. Cracks often emanate from fillets, holes, corners, or other stress raisers and result from high stresses due to the volume changes accompanying transformation to martensite. 高温淬火时金属断裂。在高硬度和低韧性的硬化碳钢、合金钢或工具钢零件中最常见。裂纹通常来自圆角、孔、角部或其他应力集中区，并由伴随马氏体转变的体积变化引起的高应力引起。 |
| Equation, long form | 方程，长格式 |
An equation which relates the torque applied to a bolt to the preload created in it, and involves fastener geometry and the coefficient of friction between mating surfaces. A theoretical equation based on rigid body mechanics and the assumption that the geometry of the fastener is perfectly described by blueprint dimensions. 将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来的方程，该方程涉及紧固件几何形状和配合面之间的摩擦系数。基于刚体力学和紧固件几何结构由蓝图尺寸完美描述的假设的理论方程。 |
| Nut box mechanism | 螺母箱机械装置 |
In a lathe it is used to engage and disengage the lead screw for thread cutting. This comprises a pair of half-nuts capable of sliding in vertical slides in or out of mesh with the lead screw. 在车床中，它用于接合和分离丝杠以进行螺纹切削。这包括一对半螺母，能够在与丝杠啮合的垂直滑动中滑动。 |
| Notch brittleness | 缺口脆性 |
Susceptibility of a material to brittle fractureat points of stress concentration. For example, in a notch tensile test, the material is said to be notch brittle if the notch strengthis less than the tensile strength of an unnotched specimen. Otherwise, it is said to be notch ductile. 材料在应力集中点易发生脆性断裂。例如，在缺口拉伸试验中，如果缺口强度小于无缺口试样的抗拉强度，则称材料为缺口脆性材料。否则，称其为缺口韧性。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Bolt gage | 螺栓量规 |
An ultrasonic instrument used to measure the stress or strain in bolts. 用于测量螺栓应力或应变的超声波仪器。 |
| Principal stress (normal) | 主应力（正常） |
The maximum or minimum value of the normal stressat a point in a plane considered with respect to all possible orientations of the considered plane. On such principal planes the shear stress is zero. There are three principal stresses on three mutually perpendicular planes. The state of stress at a point may be: (1) uniaxial, a state of stress in which two of the three principal stresses are zero; (2) biaxial, a state of stress in which only one of the three principal stresses is zero; or (3) triaxial, a state of stress in which none of the principal stresses is zero. Multiaxial stress refers to either biaxial or triaxial stress. 相对于所考虑平面的所有可能方向，所考虑平面中某点处的法向应力的最大值或最小值。在这样的主平面上，剪切应力为零。在三个相互垂直的平面上有三个主应力。一点的应力状态可以是：（1）单轴，三个主应力中的两个为零的应力；（2）双轴，三个主应力中只有一个为零的应力状态；或（3）三轴，即主应力均不为零的应力状态。多轴应力是指双轴或三轴应力。 |
| Centrifuge | 离心机 |
A machine incorporating a rapidly spinning drum in which liquids and suspended particles of different densities are separated by centrifugal action. 一种装有快速旋转滚筒的机器，在该滚筒中，不同密度的液体和悬浮颗粒通过离心作用分离。 |
| Profile | 轮廓 |
The shape of a cross section of an object, such as an aerofoil or cam. 物体的横截面形状，如机翼或凸轮。 |
| GGas turbine | G燃气轮机 |
An engine in which air, compressed by a multi-stage axial compressor and/or one or more centrifugal compressors, flows into a combustion chamber (or chambers) where fuel is burned and the hot gases then drive an axial turbine which powers the compressor. 由多级轴流压缩机和/或一个或多个离心压缩机压缩的空气流入燃烧室（或多个燃烧室），在燃烧室中燃烧燃料，然后热气体驱动轴流涡轮，为压缩机提供动力。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Stability | 稳定性 |
1. A term relating to whether a body, structure, system, or flow is in a state of stable, unstable, or neutral equilibrium. 2. In numerical analysis, whether numerical errors, such as roundoff or input-data errors, are damped, propagate, or cause divergence of the solution as the numerical method proceeds. 3. A control system is often described as stable when a step change in input results in a steady output without continuing oscillation. 1.与物体、结构、系统或流是否处于稳定、不稳定或中性平衡状态有关的术语。2.在数值分析中，随着数值方法的进行，数值误差（如舍入误差或输入数据误差）是否衰减、传播或导致解发散。3.当输入的阶跃变化导致稳定输出而无持续振荡时，控制系统通常被描述为稳定的。 |
| Thumb screw | 蝶形螺钉 |
A type of screw having a winged or knurled head for turning by hand when a quick and light clamping effect is desired. 一种螺钉，具有翼形或滚花头，当需要快速、轻夹紧效果时，可手动转动。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |