| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Cyaniding | 氰化 |
A case-hardening process in which a ferrous material is heated above the lower transformation range in a molten salt containing cyanide to cause simultaneous absorption of carbon and nitrogen at the surface and, by diffusion, create a concentration gradient. Quench hardening completes the process. 一种表面硬化工艺，将含铁材料在含氰化物的熔融盐中加热至低于较低转变范围，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。淬火硬化完成该过程。 |
| Transfer moulding | 转移模塑 |
(resin-transfer moulding, RTM) A method of compression moulding polymers in which the dies are closed before the operation starts. （树脂传递模塑，RTM）一种对聚合物进行压缩模塑的方法，其中模具在操作开始前关闭。 |
| Intergranular cracking | 沿晶断裂 |
Cracking or fracturing that occurs between the grains or crystals in a polycrystalline aggregate. Also called intercrystalline cracking. 多晶聚集体中的晶粒或晶体之间发生的开裂或断裂。也称为晶间断裂。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Fracture test | 断裂试验 |
A test in which a specimen is broken and its fracture surface is examined with the unaided eye or with a low-power microscope to determine such factors as composition, grain size, case depth, or internal discontinuities. 1. The recording of load-deflexion (or stress–strain) in a specimen loaded monotonically until it breaks in tension, compression, shear, or torsion. 2. In fatigue, determination of the number of cycles to fracture for a specimen under different patterns of repeated loading. 3. Experiments to determine fracture toughness. 一种试验，其中试样被破坏并用肉眼或低倍显微镜检查其断裂表面，以确定成分、晶粒尺寸、表层深度或内部不连续性等因素。1.记录单调加载试样的载荷偏转（或应力-应变），直到其在拉伸、压缩、剪切或扭转中断裂。2.在疲劳技术中，确定试样在不同重复载荷模式下的断裂循环次数。3.测定断裂韧性的实验。 |
| Gravity | 重力 |
The attractive force by which bodies are drawn towards the centre of Earth or other celestial object. Its intensity is measured by the acceleration produced. The gravitational force of attraction at the surface of a planet or other celestial body. The Earth’s gravity produces an acceleration of around 9.8m/s² for any unsupported body. 物体被拉向地球中心或其他天体的吸引力，行星或其他天体表面的引力。它的强度是通过产生的加速度来衡量的，对于任何无支撑的物体，地球的重力都会产生大约9.8m/s²的加速度。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Screw conveyor | 螺旋输送机 |
(auger, spiral conveyor, worm conveyor) A machine for bulk handling of semi-solid materials, consisting of a helical screw which rotates in a trough or casing. （螺旋输送机、螺旋输送机、蜗杆输送机）一种用于散装搬运半固态材料的机器，由在槽或外壳中旋转的螺旋螺杆组成。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Fluid mechanics | 流体力学 |
The study of fluids in motion (fluid dynamics) or fluid statics where there is no relative motion between fluid particles. Fluid statics concerns primarily the variation of pressure with altitude or depth; it includes aerostatics and hydrostatics. Fluid dynamics includes the topics of aerodynamics, gas dynamics, hydraulics, hydrodynamics and many aspects of acoustics, chemical engineering, flight, lubrication, meteorology, non-Newtonian fluid flow, oceanography, power-plant technology, propulsion, and turbomachinery. 研究运动中的流体（流体动力学）或流体静力学，其中流体粒子之间没有相对运动。流体静力学主要关注压力随高度或深度的变化；它包括空气静力学和流体静力学。流体动力学包括空气动力学、气体动力学、水力学、流体动力学以及声学、化学工程、飞行、润滑、气象学、非牛顿流体流动、海洋学、发电厂技术、推进和涡轮机械的许多方面。 |
| Tolerances | 公差 |
A fractional allowance for variation from the specifications. In mass production, using automatic machines, parts are intended to be completely or partially interchangeable, and in batch production parts should ideally fit without the need for selection. In practice it is impossible for mass-produced parts to have exactly the same size, owing to tool wear, variations in raw materials, thermal effects, etc. In consequence, variations from exactness, termed tolerances, are assigned to what is permissible on the basic size. 与规范不同的部分公差。在大规模生产中，使用自动机器时，零件应完全或部分可互换，在批量生产中，零件应理想匹配，无需选择。在实践中，由于刀具磨损、原材料变化、热效应等原因，批量生产的零件不可能具有完全相同的尺寸。因此，将精度偏差（称为公差）指定给基本尺寸上允许的尺寸。 |
| Gamma iron | 加马铁 |
The face-centered cubic form of pure iron, stable from 910 to 1400 °C (1670 to 2550 °F). 纯铁的面心立方形式，在910至1400°C（1670 2550°F）温度范围内稳定。 |
| Thread run-out | 螺纹耗尽 |
That portion of the threads which are not cut or rolled full depth, but which provide the transition between full-depth threads and the body or head. Officially called thread washout or vanish, although the term run-out is more popular. (Run-out is officially reserved for rotational eccentricity, as defined by total indicator readings or the like.) 未全深度切割或轧制的螺纹部分，但提供全深度螺纹与主体或头部之间的过渡。官方称之为螺纹冲蚀或消失，但术语“耗尽”更为流行。（跳动是官方为旋转偏心度保留的，由总指示器读数等定义。） |
| Square thread | 方螺纹 |
A form of screw thread in which the cross–section of the thread forms a square, making the width of the thread equal to the space between the threads. 螺纹的一种形式，螺纹的横截面形成正方形，使螺纹的宽度等于螺纹之间的间距。 |
| Clevis | U形夹 |
A U-shaped hook with holes at the ends through which a retaining bolt or pin (clevis pin) passes. 一种U形钩，末端有孔，固定螺栓或销（U形销）穿过这些孔。 |
| Blueing | 发蓝 |
Application of blue dye (‘engineers’ blue’) to identify high spots on surfaces in contact, or for marking out. 应用蓝色染料（“工程师蓝”）来识别接触表面上的高点，或用于标记。 |
| Relaxation curve | 松弛曲线 |
A plot of either the remaining, or relaxed, stress as a function of time. 剩余压力或松弛压力随时间变化的曲线图。 |
| Relaxation | 松弛 |
The loss of tension, and therefore Clamping force, in a bolt and joint as a result of Embedment, vibration loosening, gasket creep, differential thermal expansion, etc. 由于嵌入、振动松动、垫圈蠕变、热膨胀差等原因，螺栓和接头中的张力损失，因此夹紧力损失。 |
| Set screw | 紧定螺钉（平头螺钉、紧定螺栓） |
Usually a hardened steel screw having either no head or a square head and with various degrees of points or ends to lock or tighten adjustable machine parts in position on a shaft. A short, headless screw with a recess at one end to receive a screwdriver or key, the other end being pointed, square, or otherwise shaped. Typically used to secure a pulley, gear, or other component on a shaft. 通常是一种硬化钢螺钉，无头或方头，具有不同程度的点或端部，用于将可调机械部件锁定或拧紧在轴上的适当位置。一端有凹槽，用来装螺丝刀或钥匙，另一端是尖的、方形的或其他形状的。通常用于将皮带轮、齿轮或其他部件固定在轴上。 |
| Wind tunnel | 风洞 |
A duct in which a controlled flow of air is used for testing and research. Types include blow down, closed circuit, open return, and open section. Closed-circuit tunnels may be pressurized or evacuated. The working section is usually situated immediately downstream of the flow-conditioning elements, which may include a plenum chamber, honeycomb, screens, turbulence grids, and a contraction. Immediately downstream there is usually a diffuser. For basic research the usual requirement is for uniform steady flow in the working section with low swirl and turbulence intensity. For some applications the flow may be density stratified, sheared, unsteady, or of high turbulence intensity. 用于测试和研究的可控气流管道。类型包括排污、闭路、开路回路和开路段。闭路隧道可加压或排空。工作段通常位于流量调节元件的下游，可包括增压室、蜂窝、滤网、湍流格栅和收缩管。紧靠下游通常有一个扩散器。对于基础研究，通常的要求是在低涡流和湍流强度的工作段中实现均匀稳定流动。对于某些应用，流动可能是密度分层、剪切、不稳定或高湍流强度。 |
| Tera (T) | 特拉（T） |
An SI unit prefix indicating a multiplier of 1012; thus terawatt (TW) is a unit of power equal to one trillion watts. 指示乘数1012的SI单位前缀；因此，太瓦（TW）是等于1万亿瓦的功率单位。 |
| Turbomachine | 涡轮机械 |
(rotodynamic machine) A machine in which there is a transfer of energy between a continuous stream of fluid and a component, called a rotor, rotating about a fixed axis. Fans and turbines (gas, hydraulic, steam, or wind) are turbomachines in which energy is transferred to the rotor, causing it to rotate. Pumps and compressors are turbomachines in which energy is transferred from the externally driven rotor to the fluid. （旋转动力机器）在连续的流体流和绕固定轴旋转的部件（称为转子）之间进行能量传递的机器。风扇和涡轮机（燃气、液压、蒸汽或风力）是涡轮机械，其中能量传递到转子，使其旋转。泵和压缩机是涡轮机械，其中能量从外部驱动的转子传递到流体。 |
| Fatigue life (N) | 疲劳寿命（N） |
The number of cycles of stress or strain of a specified character that a given specimen sustains before failure occurs. 给定试样在失效发生之前所承受的特定特征的应力或应变的循环次数。 |
| Deformation (Unit 1/s) | 变形（单位1/s） |
A change in the form of a body due to stress, thermal change, change in moisture, or other causes. In solid mechanics, any change, reversible (elastic) or permanent (plastic), in the shape or size of parts of a body, or the whole body, caused by external or internal loading. It includes extension, compression, bending, and twisting. The same state of deformation in a body can appear as different combinations of elongation and shear. To state how much of the total strain is shear, it is split into dilatation and deviatoric components, the former changing volume but not shape, the latter shape but not volume. 由于压力、热变化、水分变化或其他原因导致的身体形态变化。在固体力学中，由外部或内部载荷引起的身体各部分或整个身体的形状或大小的任何可逆（弹性）或永久（塑性）变化。它包括拉伸、压缩、弯曲和扭曲。物体中相同的变形状态可以表现为伸长和剪切的不同组合。为了说明总应变中有多少是剪切，将其分为膨胀分量和偏差分量，前者改变体积但不改变形状，后者改变形状但不改变体积。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Stainless steels | 不锈钢 |
Iron-base alloys that are highly resistant to corrosion in many environments. The predominant alloying element is chromium, which, like iron at room temperature, has BCC crystal structure. Corrosion resistance by passivation is achieved by the formation of chromium oxide on the steel surface. Nickel, which has FCC crystal structure, is another important addition for some steels. Other additions used to enhance properties include manganese, molybdenum, niobium, and titanium. There are several classes of stainless steel. 在许多环境中具有高度耐腐蚀性的铁基合金。主要的合金元素是铬，与室温下的铁一样，铬具有BCC晶体结构。钝化抗腐蚀性是通过在钢表面形成氧化铬来实现的。具有FCC晶体结构的镍是某些钢的另一种重要添加剂。其他用于增强性能的添加剂包括锰、钼、铌和钛。不锈钢的种类有好几种。 |
| Gauge | 测量 |
1. Any instrument for measuring or checking dimensions, including adjustable gauges such as a micrometer and non-adjustable gauges such as go/no-go limit gauges that indicate the maximum and minimum dimensions allowable in a component during manufacture. 2. A term often used to mean an instrument, e.g. pressure gauge. 3. The diameter of a wire or thickness of a sheet according to a standard. 4. The distance between the rails of a railway track. 1. 任何用于测量或检查尺寸的仪器，包括可调节量规（例如千分尺）和不可调节量规（例如指示制造过程中组件允许的最大和最小尺寸的通过/不通过限制量规）。2. 常用于表示仪器的术语，例如压力表。3.根据标准的线材直径或片材厚度。4.铁路轨道的钢轨之间的距离。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Feather key | 滑键 |
A parallel key fastened in either the shaft or in the hub of a member sliding on it. When fastened in the shaft, it must be long enough to hold or drive the sliding member in any of its positions on the shaft. When in the sliding member the key need only be as long as the hub. 一种平行键，固定在轴上或在其上滑动的构件的轮毂上。当固定在轴上时，其长度必须足以将滑动构件固定或驱动在轴上的任何位置。当处于滑动构件中时，键只需与轮毂一样长。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| Slip | 滑落 |
Plastic deformation by the irreversible shear displacement (translation)of one part of a crystal relative to another in a definite crystallographic direction and usually on a specific crystallographic plane. Sometimes called glide. 晶体的一部分在一定的晶体学方向上相对于另一部分的不可逆剪切位移（平移）引起的塑性变形，通常在特定的晶体主义平面上。有时被称为滑翔。 |
| Slack quenching | 欠速淬火 |
The incomplete hardening of steel due to quenching from the austenitizing temperature at a rate slower than the critical cooling rate for the particular steel, resulting in the formation of one or more transformation products in addition to martensite. 由于从奥氏体化温度以低于特定钢临界冷却速度的速度淬火而导致钢的不完全硬化，导致除马氏体外还形成一种或多种相变产物。 |
| Condensation shock | 冷凝冲击 |
For supersonic flow of a moist gas through a divergent nozzle, condensation occurs in the form of spontaneous nucleation at some point downstream of that at which the temperature falls to the saturation temperature. The condensation process proceeds rapidly, and results in a fairly thick discontinuity termed a condensation shock. 对于通过发散喷嘴的湿气体超音速流动，在温度降至饱和温度的点下游的某个点处，冷凝以自发成核的形式发生。凝结过程进行得很快，导致相当厚的不连续性，称为凝结激波。 |
| Relaxation rate | 松弛率 |
The absolute value of the slope of a stress-relaxation curve at a given time. 给定时间应力松弛曲线斜率的绝对值。 |
| Tribology | 摩擦学 |
The science and technology concerned with interacting surfaces in relative motion. 与相对运动中相互作用的表面有关的科学和技术。 |
| SI system | SI国际单位制 |
SI is an abbreviation of Système International d’Unités, i.e., the international unit measurement system – an internationally established system of measurement units built on older metric systems. SI是Système International d‘Unités的缩写，即国际单位计量系统——一种基于旧公制的国际公认计量单位系统。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Coarsening | 粗粒化 |
An increase in the grain size, usually, but not necessarily, by grain growth. 晶粒尺寸的增加，通常但不一定是晶粒变大。 |
| Fastener testing | 紧固件测试 |
A determination or verification that the fastener meets its specification requirements. 确定或验证紧固件符合其规范要求。 |
| Air-cooled condenser | 风冷冷凝器 |
A heat exchanger, in which the cooling medium is air, used to condense the exhaust steam from a steam turbine, the condensate being returned to the boiler. 一种热交换器，其中冷却介质为空气，用于冷凝蒸汽轮机排出的蒸汽，冷凝水返回锅炉。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Archimedes Wave Swing | 阿基米德波摆动 |
A machine for tidal-power energy generation consisting of two concentric, air-filled submerged cylinders. The inner lower cylinder is tethered to the ocean floor while the upper floater unit, which is closed at the top, moves up and down due to the variations in hydrostatic pressure caused by the wave motion. The relative movement of the two cylinders is used to generate electricity in which linear motion replaces the more common rotary motion of an electromagnetic generator. 一种用于潮汐能发电的机器，由两个同心的充气水下气缸组成。内部下部圆柱体系在海底，而顶部封闭的上部浮子单元由于波浪运动引起的静水压力变化而上下移动。两个气缸的相对运动用于发电，其中直线运动取代了电磁发电机更常见的旋转运动。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Torsional angle (ϕ) | 扭转角（ψ） |
(Unit ° or rad) The angular deflexion between two locations on a straight bar subjected to a torque. （单位为°或rad）受扭矩作用的直杆上两个位置之间的角偏转。 |
| Stress relieving | 应力消除 |
Heating to a suitable temperature, holding long enough to reduce residual stresses, and then cooling slowly enough to minimize the development of new residual stresses. 加热到合适的温度，保持足够长的时间以减少残余应力，然后缓慢冷却以尽量减少新残余应力的产生。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Tempered martensite embrittlement | 回火马氏体脆化 |
Embrittlement of ultrahigh-strength steels caused by tempering in the temperature range of 205 to 400 °C (400 to 750 °F); also called 350 °C or 500 °F embrittlement. Tempered martensite embrittlement is thought to result from the combined effects of cementite precipitation on prioraustenite grain boundaries or interlath boundaries and the segregation of impurities at prioraustenite grain boundaries. 超高强度钢在205至400°C（400至750°F）温度范围内回火引起的脆化；也称为350°C或500°F脆化。回火马氏体脆化被认为是由于渗碳体沉淀在原奥氏体晶界或层间晶界上以及杂质在原奥氏体晶粒边界处偏析的综合影响。 |
| Guided bend | 导向弯曲 |
The bend obtained by use of a plunger to force the specimen into a die in order to produce the desired contour of the outside and inside surfaces of the specimen. 通过使用柱塞将试样压入模具中获得的弯曲，以产生试样外表面和内表面所需的轮廓。 |
| Failure of the bolt | 螺栓失效 |
Term implying that the bolt has broken or the threads have stripped. There can be many reasons for this. 表示螺栓断裂或螺纹脱落的术语。原因可能有很多种。 |
| Metre (m) | 米（m） |
The base unit of length in the SI system. It is equal to the distance travelled by light in vacuum in 1/299 792 458 seconds. SI系统中长度的基本单位。它等于光在真空中在1/299792458秒内传播的距离。 |
| Fahrenheit | 华氏度 |
The temperature scale based on the freezing point of water (32ºF) and the boiling point of water (212ºF). The interval between these points is divided into 180 equal parts. Although replaced by the Celsius scale, the Fahrenheit scale is still sometimes used for non-scientific measurements. 温标基于水的冰点（32ºF）和水的沸点（212ºF）。这些点之间的间隔被分成180等份。尽管被摄氏刻度所取代，华氏刻度有时仍用于非科学测量。 |
| Scratch hardness test | 划痕硬度测试 |
A form of hardness test in which a sharp-pointed stylus or corner of a mineral specimen is traversed along a surface so as to determine the resistance of that surface to cutting or abrasion. 硬度测试的一种形式，用尖头笔或矿物样品的一角沿一个表面移动，以确定该表面的抗切割或耐磨性。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| A-basis | A-基础 |
Mechanical property value above which at least 99% of the population of values is expected to fall, with a confidence of 95%. Also called A-allowable. 机械性能值超过该值时，至少99%的值预计会下降，置信度为95%。也被称为A-容许。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| AISC | AISC |
The American Institute of Steel Construction. 美国钢结构学会。 |
| British thermal unit (BTU, Btu) | 英热单位（BTU，Btu） |
An obsolete (non-SI) imperial unit of energy defined as the energy required to raise the temperature of one pound of pure water at 68°F by 1°F. The conversion to SI is 1 Btu = 1.055 056 × 103 J. 一种已被淘汰的（非SI）英制能量单位，定义为将68°F的一磅纯水的温度升高1°F所需的能量。转换为SI为1Btu=1.055056×103J。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Octane number | 辛烷值 |
(octane rating) A measure of the anti-knock properties of a fuel taken as the percentage by volume of iso-octane in the fuel. （辛烷值）以燃料中异辛烷的体积百分比表示的燃料抗爆性能的量度。 |
| Cone clutch | 锥形离合器 |
A friction clutch in which an internal cone moves axially in or out of engagement with an external cone. One or both surfaces is lined with high-friction material. 一种摩擦离合器，其中内锥与外锥轴向啮合或脱离啮合。一个或两个表面衬有高摩擦材料。 |
| Piston pump | 活塞泵 |
A positive-displacement pump in the basic configuration of which a piston reciprocates in a cylinder. On the suction stroke, fluid is drawn into a chamber through the inlet valve, which is then open while the outlet valve is closed. On the delivery stroke the fluid is forced out of the chamber through the outlet valve, which then opens while the inlet valve is closed. Both axial and radial configurations are common. 活塞在气缸中往复运动的一种容积泵。在吸入冲程，流体通过入口阀吸入腔室，然后在出口阀关闭时打开。在输送冲程中，流体通过出口阀被迫流出腔室，然后出口阀打开，同时入口阀关闭。轴向和径向配置都很常见。 |
| Hard temper | 硬化回火 |
Same as full hard temper. 和全硬化回火一样。 |
| Actual cubic feet per minute | 实际立方英尺每分钟 |
(acfm) An obsolete (i.e. non-SI) measure of volumetric flow rate; the volume of a gas flowing per minute at actual operating pressure and temperature, as opposed to the corresponding volume flow rate at STP. （acfm）已被淘汰的（即非SI）体积流量测量；在实际工作压力和温度下每分钟流动的气体体积，与STP下的相应体积流量相反。 |
| Concentration ratio | 浓度比 |
For a concentrating solar collector, the ratio of the projected area of the concentrator facing the solar beam to the actual area of the receiver. 对于聚光太阳能集热器，集中器面向太阳光束的投影面积与接收器的实际面积之比。 |
| Bucket | 吊桶 |
1. A cup-shaped vane with a central dividing ridge attached to the periphery of the runner of an impulse water turbine such as a Pelton turbine. 2. A rotor blade in a compressor or turbine. 1.一种杯形叶片，所述杯形叶片具有附接到冲击式水轮机（例如冲击式水轮机台）的转轮的外围的中央分隔脊。2.压缩机或涡轮机中的转子叶片。 |
| Proof load | 验证载荷（单位 N） |
The maximum, safe, static, tensile load which can be placed on a fastener without yielding it. Sometimes given as a force (in lb or N) sometimes as a stress (in psi or MPa). The test load in quality control to which different components made of different materials must be subjected without failing in order to perform properly. 可施加在紧固件上而不使其屈服的最大安全静态拉伸载荷。有时以力（lb或N）表示，有时以应力（psi或MPa）表示。质量控制中的测试负荷，由不同材料制成的不同部件必须经受该负荷，才能正常运行。 |
| Hardness test | 硬度测试 |
1. Any of various tests in which different hard indenters are forced into the surface of a solid under different loads to give permanent impressions, the pressure to cause which being called the hardness. The Brinell test employs a spherical indenter; the Vickers test a square-based pyramid. The relation between indentation hardness H and uniaxial yield stress Y is approximately H = (2.5 ~ 3.0)Y. Originally hardnesses were given in kg/mm² but now are often given in Pa. 2. The tests for scratch and file hardness relate either to one material being able to mark another (Mohs hardness scale for minerals), or to the size of groove produced by a rigid indenter slid under load across a surface. 3. Rebound hardness concerns the height of rebound of a dropped indenter, or an indenter at the end of a pivoted arm, having struck a surface. 1.任何一种试验，其中不同的硬压头在不同载荷下压入固体表面，以产生永久压痕，所产生的压力称为硬度。布氏试验采用球形压头；维氏硬度测试是一个方形金字塔。压痕硬度H与单轴屈服应力Y之间的关系约为H=（2.5~3.0）Y。最初硬度以kg/mm²为单位，但现在通常在Pa.2中给出。划痕和锉刀硬度测试要么与一种材料能够标记另一种材料（矿物的莫氏硬度标度）有关，要么与刚性压头在表面上滑动产生的凹槽大小有关。3.回弹硬度涉及掉落压头或旋转臂端部压头撞击表面后的回弹高度。 |
| Actual power | 实际功率 |
(actual horsepower) (Unit W or hp) The power delivered at the output shaft of an engine, before subsequent transmission through a gearbox etc. （实际马力）（单位W或hp）在随后通过变速箱等传输之前，在发动机输出轴上传递的功率。 |
| Mohs hardness test | 莫氏硬度测试 |
A scratch hardness test for determining comparative hardness using 10 standard minerals—from talc (the softest) to diamond (the hardest). 刮擦硬度测试，用于使用从滑石（最软）到钻石（最硬）的10种标准矿物测定比较硬度。 |
| Physical properties | 物理性质 |
Properties of a material the determination of which does not involve the deformation or destruction of the specimen—for example, density, electrical conductivity, coefficient of thermal expansion, magnetic permeability, and lattice parameter. Does not include chemical reactivity or the properties more appropriately regarded as mechanical properties. 不涉及试样变形或破坏的材料特性，例如密度、电导率、热膨胀系数、磁导率和晶格参数。不包括化学反应性或更适当地视为机械的性质。 |
| Combined dimensioning | 组合尺寸标注 |
The use of chain dimensioning and parallel dimensioning on the same engineering drawing. 在同一工程图上使用链式尺寸标注和平行标注。 |
| Double-shear test | 双剪试验 |
A shear test having two stationary, shear blades and one moving one and that uses solid round bars as test specimens. 一种剪切试验，具有两个固定的剪切刀片和一个移动的刀片，并使用实心圆棒作为试样。 |
| Annealing | 退火 |
A generic term denoting a treatment, consisting of heating to and holding at a suitable temperature followed by cooling at a suitable rate, used primarily to soften metallic materials, but also to simultaneously produce desired changes in other properties or in microstructure. 一个通用术语，表示一种处理，包括加热并保持在合适的温度，然后以合适的速率冷却，主要用于软化金属材料，但也同时产生其他性能或微观结构的所需变化。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Slot | 狭槽 |
A groove machined into a component, e.g. to allow for thermal expansion, or in which the tongue or tip of another component can fit or slide. 在部件上加工的凹槽，例如，允许热膨胀，或另一部件的榫舌或尖端可在其中安装或滑动。 |
| Clearance volume | 余隙容积 |
(Unit m³) The ‘dead’ volume above a piston, including the recess in the cylinder head, in a reciprocating compressor or engine when the piston is at top dead centre. （单位m³）活塞位于上止点时活塞上方的“死区”体积，包括气缸盖中的凹槽，在往复式压缩机或发动机中。 |
| Cotter pin | 开口销 |
(cotter) 1. A tapered wedge or pin passing through a tapered slot or hole in one member and bearing against a second member to fix it in location. 2. A split cotter is commonly called a split pin. A pin with two legs. With legs together, the pin is placed through the hole in a clevis pin. The legs are then opened outward to prevent the cotter pin from backing out of the hole. The cotter pin, in turn, prevents the load-bearing clevis pin from backing out of its retaining hole. （开口）1.锥形楔子或销钉穿过一个构件中的锥形槽或孔，并支撑在第二个构件上以将其固定到位。2.开口开口通常称为开口销。相当于有两条腿的别针，将支腿放在一起，销钉穿过U形夹销上的孔。然后将支腿向外打开以防止开口销从孔中退出。开口销反过来防止承重U形夹销从其固定孔中退出。 |
| Roots blower | 罗茨鼓风机 |
(rotary-piston blower) A positive-displacement gas compressor with two meshing lobed rotors that rotate within a close-fitting casing. Commonly used as a supercharger. （旋转活塞鼓风机）一种容积式气体压缩机，具有两个啮合的凸角转子，在紧密配合的外壳内旋转。通常用作增压器。 |
| Lathe | 车床 |
A machine tool in which work, gripped in the headstock, is rotated against the cutting tool to produce turned, bored, faced, or threaded components. 一种机床，其中夹持在主轴箱中的工件靠着切削工具旋转，以生产车削、钻孔、端面或螺纹部件。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Heat (q, Q) (Unit J) | 热量（q, Q）（单位J） |
A form of energy that is transferred across the boundary of a system at one temperature to another system (or the surroundings) at a different temperature by virtue of the temperature difference between them. Heat can be identified only as it crosses the boundary. A body can never be said to contain heat which is thus a transient phenomenon. 一种能量形式，由于它们之间的温差在一个温度下通过系统边界传递到另一个温度不同的系统（或环境）。只有当热量穿过边界时才能识别。一个物体不能说永远含有热量，这是一种瞬态现象。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Temporal decomposition | 时间分解 |
The splitting of a control problem into parts with relatively short and long time constant so that different controllers may be used for the different parts. 将控制问题分解为具有相对较短和较长时间常数的部分，以便不同的部分可以使用不同的控制器。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Friction materials | 摩擦材料 |
Materials having a high coefficient of friction which, when coupled with a long life, may be employed as brake linings or the facing of the plates of a clutch. 具有高摩擦系数的材料，当与长寿命相结合时，可用作制动衬片或离合器片的饰面。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Fine pitch | 细牙螺纹 |
Fine pitch threads are often used within the automotive industry. They are more easily tapped into harder materials and have less tendency to loosen. 细螺距螺纹通常用于汽车行业。它们更容易被敲入较硬的材料中，并且不太容易松动。 |
| Dimensioning | 尺寸标注 |
The specification on an engineering drawing of the size (e.g. length, radius, angle, or spacing) and the relative location (e.g. angular position) of each feature of a component. The numerical values often include the tolerances. There should be no more dimensions than are necessary to manufacture the component. 工程图纸上对部件每个特征的尺寸（例如长度、半径、角度或间距）和相对位置（例如角位置）的规范。数值通常包括公差。尺寸不应超过制造组件所需的尺寸。 |
| Edge distance | 边距 |
The distance from the edge of a bearing specimen to the center of the hole in the direction of applied force. 在作用力方向上，从轴承试样的边缘到孔中心的距离。 |
| Base metal hardness | 母材硬度 |
Hardness closest to the surface (when traversing from core to outside diameter) just before an increase or decrease occurs, denoting, respectively, carburization or decarburization. 在发生增加或减少之前最接近表面的硬度（从芯部到外径时），分别表示渗碳或脱碳。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Wheel | 轮 |
A solid disc, or a circular ring with spokes radiating from a central hub, either attached to an axle around which it revolves or which revolves with a rotating axle. 一个实心圆盘，或一个带有辐条的圆环，辐条从一个中心毂放射出来，或附在一个绕其旋转的轴上，或与一个旋转轴一起旋转。 |
| Radial load (Unit N) | 径向负荷（单位：N） |
1. Centrifugal loading induced in a rotating body. 2. (through-wallthickness load) The radial component of loading arising from internal or external pressurization of a closed vessel. There will also be axial and hoop loading. 1.旋转体中产生的离心载荷。2.（贯穿壁厚载荷）由封闭容器的内部或外部加压产生的载荷的径向分量。还存在轴向和环向载荷。 |
| Time quenching | 时间淬火 |
A term used to describe a quench in which the cooling rate of the part being quenched must be changed abruptly at some time during the cooling cycle. 用于描述淬火的术语，其中被淬火零件的冷却速率必须在冷却循环的某个时间突然改变。 |
| Slug | 猛击 |
1. A starting workpiece for forging and similar operations, such as a length of wire or rod to make a bolt blank on which a thread can be rolled or cut. 2. (geepound) An obsolete imperial (non-SI) unit of mass, being the mass which under an acceleration of one foot per second squared gives a force of one pound-force. The conversion to SI is 1 slug = 14.593 902 94 kg. 3. A large-scale flow structure which occurs in the transition from laminar to turbulent flow in a pipe. 1.一种用于锻造和类似操作的起始工件，如用于制造螺栓毛坯的一段线材或棒材，在该毛坯上可以轧制或切割螺纹。2.（吉磅）一种已被淘汰的英制（非国际单位制）质量单位，在一英尺/秒平方加速度下产生一磅力的质量。转化为SI国际单位制的转化率为1slug=14.59390294kg。3.一种大规模流动结构，其发生在管道中从层流到湍流的过渡中。 |
| Notch strength | 缺口强度 |
The maximum load on a notched tensile-test specimen divided by the minimum cross-sectional area (the area at the root of the notch). Also known as notch tensile strength. 缺口拉伸试样上的最大载荷除以最小横截面积（缺口根部的面积）。也称为缺口抗拉强度。 |
| Cold die quenching | 冷模淬火 |
A quench utilizing cold, flat, or shaped dies to extract heat from a part. Cold die quenching is slow, expensive, and is limited to smaller parts with large surface areas. 利用冷、平或成型模具从零件中提取热量的淬火。冷模淬火速度慢、成本高，并且仅限于表面积较大的较小零件。 |
| Thermal analysis | 热分析 |
A method for determining transformations in a metal by noting the temperatures at which thermal arrests occur. These arrests are manifested by changes in slope of the plotted or mechanically traced heating and cooling curves. When such data are secured under nearly equilibrium conditions of heating and cooling, the method is commonly used for determining certain critical temperatures required for the construction of equilibrium diagrams. 一种通过记录发生热阻的温度来确定金属转变的方法。这些阻力表现为绘制或机械追踪的加热和冷却曲线斜率的变化。当这些数据在加热和冷却的近似平衡条件下得到保证时，该方法通常用于确定构建平衡图所需的某些临界温度。 |
| Circlip | 卡簧 |
(snap ring) An external or internal retaining ring that locates parts of circular cross section in an axial direction. It consists of an incomplete ring, with holes on either side of the gap, that may be expanded by a plier-like tool to pass into a groove in a shaft or contracted to pass into a groove in a bore. （卡环）在轴向定位圆形横截面部分的外部或内部保持环。它由一个不完整的环组成，在间隙的任一侧都有孔，可以通过钳形工具将其扩展以进入轴中的凹槽或收缩以进入孔中的凹槽。 |
| Breaking load (Unit N) | 断裂负荷（单位N） |
The load applied at some point to a component or structure which leads to fracture. The breaking stress (breaking strength) is the average stress at which a member breaks, given by the breaking load divided by the area over which it acts. 在某个点施加到导致断裂的部件或结构的载荷。断裂应力（断裂强度）是构件断裂时的平均应力，由断裂载荷除以其作用的面积给出。 |
| Minute (min) | 分钟（min） |
A non-SI unit of time. The conversion to SI is 1 min = 60 s. 非SI时间单位。转换为1分钟=60秒。 |
| Vibration | 振动 |
1. A periodic change with time of the displacements of elements making up a component or structure. 2. The study of the oscillatory motion of bodies and systems and the frequencies, amplitudes, and forces associated with them. 1.组成部件或结构的元件位移随时间的周期性变化。2.研究物体和系统的振荡运动以及与之相关的频率、振幅和力的学科。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Rockwell superficial hardness test | 洛氏表面硬度试验 |
Same as Rockwell hardness test, except that smaller minor and major loads are used. 与洛氏硬度测试相同，只是使用较小的次要载荷和主要载荷。 |
| Thermomechanical working | 热机械加工 |
A general term covering a variety of processes combining controlled thermal and deformation treatments to obtain specific properties. Same as thermal-mechanical treatment. 一个通用术语，涵盖结合受控热处理和变形处理以获得特定性能的各种工艺。与热机械处理相同。 |
| Stress | 应力（单位Pa） |
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression)or shear. 1. Stress ‘at a point’ (i.e. over a volume of material that is very small compared with that of the component or structure) is the load per unit area for every face of an infinitesimal cube surrounding the point. 2. In fluid flow the stress tensor σij is the sum of an isotropic part −pδij, δij being the Kronecker delta, having the same form as the stress tensor for a fluid at rest, p being the static pressure, and the non-isotropic, deviatoric stress tensor dij which is due entirely to the fluid motion. 内部分布力或力分量的强度，这些力或力的分量抵抗正在或已经受到外力的材料的体积或形状的变化。应力以单位面积的力表示，并根据试样横截面的原始尺寸计算。应力可以是直接（拉伸或压缩）或剪切。1.“在一点”的应力（即在与组件或结构相比非常小的材料体积上）是围绕该点的无限小立方体的每个面的单位面积载荷。2. 在流体流动中，应力张量σij是各向同性部分-pδij的总和，δij是Kroneckerδ，具有与静止流体的应力张量相同的形式，p是静压，非各向同性, 偏应力张量 dij 完全由流体运动引起。 |
| Stretch ratio (extension ratio, λ) | 拉伸比（拉伸比，λ） |
A measure, used for highly-extensible materials such as rubber, of the extensional or normal strain of a component subjected to tension and defined as the ratio of the final length l, for a given load, to the initial or gauge length l0, where the coordinate axes are those of principal strain. It is related to the engineering strain e by λ = 1 + e. 用于高度可延展材料（如橡胶）的一种测量方法，用于测量受拉构件的拉伸或法向应变，定义为给定载荷下的最终长度l与初始或标距长度l0之比，其中坐标轴为主应变轴。它与工程应变e的关系为λ=1+e。 |
| Forge | 锻造 |
To shape metal while holt and plastic by a hammering or forcing process. Dies used in process. 通过锤击或强制过程使金属成型，同时保持塑料成型。过程会使用模具。 |
| Homogeneous carburizing | 均匀渗碳 |
Use of a carburizing process to convert a low-carbon ferrous alloy to one of uniform and higher carbon content throughout the section. 使用渗碳工艺将低碳铁合金转化为整个截面中碳含量均匀且较高的合金。 |
| Centrifugal compressor | 离心式压缩机 |
A compressor in which kinetic energy is added to a fluid by radial acceleration in an impeller and then converted into a pressure increase by flow though a diffuser. 一种压缩机，其中动能通过叶轮中的径向加速度添加到流体中，然后通过扩散器的流动转换为压力增加。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Preload adjustments | 预载调整 |
Preloads may be applied directly by axial loading or indirectly by turning of the nut or bolt. When preload is applied by turning of nuts or bolts, a torsion load component is added to the desired axial bolt load. 预载荷可通过轴向载荷直接施加，或通过转动螺母或螺栓间接施加。当通过转动螺母或螺栓施加预载荷时，扭转载荷分量被添加到所需的轴向螺栓载荷中。 |
| Crack-extension resistance (KR) | 抗裂扩展性（KR） |
A measure of the resistance of a material to crack extension, expressed in terms of the stress-intensity factor, the crack-extension force, or values of Jderived using the J-integral concept. 材料对裂纹扩展的抵抗力的量度，以应力强度因子、裂纹扩展力或使用J积分概念导出的J值表示。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Fastener with waisted shank | 带腰柄的紧固件 |
Finished fastener with a shank diameter of ds < d2. 柄径ds |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Carbonization | 碳化 |
Conversion of an organic substance into elemental carbon. 将有机物质转化为元素碳。 |
| Regenerative pump | 涡流泵 |
(regenerative turbine pump, peripheral pump) A pump with a double-sided impeller having a large number of radial blades. The pressure of the pumped liquid increases progressively over several revolutions of the impeller. It is particularly suited to producing large heads at small flow rates without cavitation. （再生涡轮泵，外围泵）具有具有大量径向叶片的双面叶轮的泵。泵送液体的压力在叶轮的几圈内逐渐增加。它特别适合于在小流速下产生大水头且不产生气穴。 |
| Deviation | 偏差 |
The difference between the actual value and the desired value of a controlled variable. 受控变量的实际值与期望值之间的差值。 |
| Nautical mile (M) | 海里（M） |
A special unit of distance employed for marine and aerial navigation. The conversion to SI is 1 M = 1 852 m. 用于海上和空中导航的特殊距离单位。SI的转换为1M＝1852m。 |
| Gage length | 标距 |
The original length of the portion of a specimen over which strain, change of length, or other characteristics are determined. 确定应变、长度变化或其他特性的试样部分的原始长度。 |
| Turbine pump (turbopump) | 涡轮泵 |
An axial or centrifugal pump driven by a turbine. Typically used to supply fuel to the combustion chamber of a rocket engine such as on the space shuttle. 由涡轮驱动的轴向或离心泵。通常用于向火箭发动机（如航天飞机）的燃烧室供应燃料。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Tightness | 紧密度 |
A measure of the mass leak rate from a gasketed joint. 垫圈接头质量泄漏率的测量值。 |
| Sampling frequency (Unit Hz) | 采样频率（单位Hz） |
(sampling rate) The number of measurement samples per unit time taken from a continuous analogue signal to produce a discrete signal. It is the inverse of the time between successive measurements (sampling interval, sampling period, or sampling time). （采样率）从连续模拟信号中提取以产生离散信号的每单位时间的测量样本数。它是连续测量之间时间的倒数（采样间隔、采样周期或采样时间）。 |
| Volume flow rate | 体积流率 |
(volumetric flow rate, , ) (Unit m³/s) The volume of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. （体积流量）（单位m³/s）单位时间内流经表面或管道或其他管道的材料体积，通常为流体或粉末。 |
| Joint | 关节接合处 |
The part of a robot arm permitting either rotational or translational motion. Each joint provides a single degree of freedom, and thus a minimum of six is required if the robot is to be able to position and orientate the end effector anywhere within the workspace. A joint is described by four parameters: the joint angle, joint offset, joint twist, and link length. The joint angle is the angle between an extrapolation of the previous link length and the present link length, measured positive anticlockwise in a plane normal to the joint axis. This is variable in a rotational joint and fixed in a translational joint. The joint offset is the distance between the link length for the previous link and that for the present link, measured along the joint axis. This is variable for a translational joint and fixed for a rotational joint. The joint twist for the nth joint is the angle between the axes of joints Jn and Jn+1, measured positive anticlockwise in a plane normal to the link length and viewed from the position of the Jn+1 joint. The link length is the mutually perpendicular distance between planes passing through the axes of joint Jn and Jn+1. Both the joint twist and link length are fixed in all joints. 机器人手臂上允许旋转或平移运动的部分。每个接合处都有自由度，如果机器人要能够在工作空间内的任何位置定位和定向末端执行器，则至少需要六个接合处具有自由度。关节接合处由四个参数描述：关节角度、关节偏移、关节扭曲和链接长度。关节角度是在垂直于关节轴的平面内逆时针测量的先前连杆长度和当前连杆长度的外推之间的角度。这在旋转关节中是可变的，在平移关节中是固定的。关节偏移是沿关节轴测量的前一个连杆和当前连杆的连杆长度之间的距离。这对于平移关节是可变的，对于旋转关节是固定的。第n个关节的关节扭曲是关节Jn和Jn+1轴之间的角度，在垂直于连杆长度的平面内逆时针测量，从Jn+2关节的位置观察。连杆长度是穿过关节轴Jn和Jn+1的平面之间相互垂直的距离。关节扭曲和连杆长度在所有关节中都是固定的。 |
| Available head (Unit m) | 可用水头（单位米） |
In a hydroelectric power system, the difference between the vertical height of the water level in the supply reservoir above the turbine inlet less the head loss due to friction and fittings in the duct leading to the turbine. 在水力发电系统中，水轮机入口上方供水水库中水位垂直高度之间的差减去由于通向涡轮机的管道中的摩擦和配件造成的水头损失。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Diffusion | 扩散 |
(1) Spreading of a constituent in a gas, liquid, or solid, tending to make the composition of all parts uniform. (2) The spontaneous movement of atoms or molecules to new sites within a material. （1） 一种成分在气体、液体或固体中的扩散，趋于使所有部分的成分均匀。（2） 原子或分子自发运动到材料内的新位置。 |
| Impact loads | 冲击载荷 |
Especially severe shock loads such as those caused by instantaneous arrest of a falling mass, shock meeting of two parts (in a mechanical hammer, for example), or by explosive impact, in which there can be an exceptionally rapid build-up of stress. 特别严重的冲击载荷，例如由下落质量的瞬时停止、两部分的冲击碰撞（例如在机械锤中）或爆炸性冲击引起的冲击载荷，其中可能会出现异常快速的应力积聚。 |
| Carbon potential | 碳势 |
A measure of the ability of an environment containing active carbon to alter or maintain, under prescribed conditions, the carbon level of the steel. Note: In any particular environment, the carbon level attained will depend on such factors as temperature, time, and steel composition. 衡量含有活性碳的环境在规定条件下改变或保持钢的碳含量的能力。注意：在任何特定环境中，所达到的碳含量将取决于温度、时间和钢成分等因素。 |
| Maximum load (Pmax) | 最大负载（Pmax） |
(1) The load having the highest algebraic value in the load cycle. Tensile loads are considered positive and compressive loads negative. (2)Used to determine the strength of a structural member; the load that can be borne before failure is apparent. （1）负载循环中具有最高代数值的负载。拉伸荷载视为正荷载，压缩荷载视为负荷载。（2）用于确定结构构件的强度；失效前可承受的载荷是明显的。 |
| Cup washer | 杯形垫圈 |
A dished leather or neoprene washer fitted to the rod end in some piston-style pumps. 在某些活塞式泵中，安装在杆端的碟形皮革或氯丁橡胶垫圈。 |
| Relaxed stress | 松弛应力 |
The initial stress minus the remaining stress at a given time during a stress-relaxation test. 在应力松弛试验期间，初始应力减去给定时间的剩余应力。 |
| Absolute humidity | 绝对湿度 |
The weight of water vapor in a gadwater vapor mixture per unit volume of space occupied, expressed, for example, in grains or pounds per cubic foot. 单位体积空间占用的水蒸气混合物中水蒸气的重量，例如，以谷物或磅/立方英尺表示。 |
| Plane stress | 平面应力 |
The stress condition in linear-elastic fracture mechanics in which the stress in the thickness direction is zero; most nearly achieved in loading very thin sheet along a direction parallel to the surface of the sheet. Under plane-stress conditions, the plane of fracture instability is inclined 45° to the axis of the principal tensile stress. 线弹性断裂力学中厚度方向上的应力为零的应力条件；在沿着平行于薄片表面的方向加载非常薄的薄片时最接近。在平面应力条件下，断裂失稳平面与主拉应力轴倾斜45°。 |
| Core | 核心 |
In a ferrous alloy prepared for case hardening, that portion of the alloy that is not part of the case . Typically considered to be the portion that (a) appears light on an etched cross section, (b) has an essentially unaltered chemical composition, or (c) has a hardness, after hardening, less than a specified value. 在为表面硬化而制备的铁合金中，合金中不属于表面的那部分。通常被认为是（a）在蚀刻横截面上看起来很轻，（b）化学成分基本不变，或（c）硬化后硬度低于规定值的那部分。 |
| Carbon steels | 碳钢 |
(plain carbon steels) Steels in which carbon is the principal alloying element, and the amount of manganese does not exceed 1.65% and the copper and silicon contents are less than 0.60%. There are three main types: low-carbon steels (0.08–0.35% carbon); medium-carbon steels (0.35–0.50% carbon); and high-carbon steels (0.50–2.0% carbon). （普通碳钢）以碳为主要合金元素，锰含量不超过1.65%，铜和硅含量低于0.60%的钢。主要有三种类型：低碳钢（0.08-0.35%碳）；中碳钢（0.35–0.50%碳）；和高碳钢（0.50–2.0%碳）。 |
| Displacement | 移位 |
The distance that a chosen measurement point on a cracked specimen displaces normal to the crack plane as the crack grows. 随着裂纹扩展，裂纹试样上选定的测量点垂直于裂纹平面位移的距离。 |
| Natural aging | 自然时效 |
Spontaneous aging of a supersaturated solid solution at room temperature. 过饱和固溶体在室温下的自发时效。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Waist | 腰部 |
The joint in a robot corresponding to the human waist, i.e. providing rotation about a vertical axis. In an articulated robot, the first joint mounted at the base frame. 机器人中的关节对应于人的腰部，即提供绕垂直轴的旋转。在关节式机器人中，第一个关节安装在基架上。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Taper key | 楔键 |
A key with parallel sides but tapering cross section along its length. 边平行但横截面沿其长度逐渐变细的键。 |
| Testing machine | 试验机 |
A machine used to apply either a steady or oscillatory or impact load to a testpiece. The load may be tensile, compressive, shear, bending, or torsional. 用于向试件施加稳定或振荡或冲击载荷的机器。载荷可以是拉伸的、压缩的、剪切的、弯曲的或扭转的。 |
| Square | 正方 |
1. A regular quadrilateral, i.e. a polygon with four equal sides and four right angles. 2. An instrument to check angles of internal and external surfaces and flatness. 1.正四边形，即具有四条等边和四个直角的多边形。2.一种检查内外表面角度和平面度的仪器。 |
| Combined stresses | 复合应力 |
The stress state at a point in a component subjected to combination of axial, bending, torsional loadings etc., acting along all reference axes. 沿所有参考轴作用的受轴向、弯曲、扭转载荷等组合作用的部件中某点的应力状态。 |
| Fillister head | 槽头 |
Similar to a pan head but with a smaller head diameter and a taller head, with higher vertical sides. 类似于盘头，但头部直径较小，头部较高，垂直边较高。 |
| Ductile fracture | 韧性断裂 |
Fracture characterized by tearing of metal accompanied by appreciable gross plastic deformation and expenditure of considerable energy. A fracture of a component or structure which is preceded by extensive ductile deformation so that the broken pieces cannot be re-fitted to regain the original size and shape of the component or structure. 以金属撕裂为特征的断裂，伴随着明显的总塑性变形和相当大的能量消耗。一种部件或结构的断裂，在断裂前会发生大范围的延性变形，从而使断裂的碎片无法重新装配以恢复部件或结构原来的尺寸和形状。 |
| Toughness (Unit J/m²) | 韧性（单位：J/m²） |
The ability of a metal to absorb energy and deform plastically before fracturing. 1. The ability of a material to resist crack initiation and propagation. 2. The ability of a material to absorb strain energy without fracturing. 金属在破裂前吸收能量和塑性变形的能力。1.材料抵抗裂纹萌生和扩展的能力。2.材料在不发生断裂的情况下吸收应变能的能力。 |
| Diesel engine | 柴油发动机 |
(compression–ignition engine) A piston engine operating on the Diesel cycle in which the air is compressed to a temperature above the autoignition temperature of the fuel and combustion is initiated as the fuel is injected into the hot air. Diesel engines operate at higher compression ratios (typically in the range 12 to 24) than petrol engines. Although named after Rudolf Diesel, the inventor, Diesel engine is often spelled with a lower case d, contrary to normal practice. （压燃式发动机）在柴油循环中运行的活塞式发动机，在该循环中，空气被压缩至高于燃料自燃温度的温度，当燃料喷射到热空气中时，燃烧开始。柴油发动机在比汽油发动机更高的压缩比下运行（通常在12到24的范围内）。虽然以发明人鲁道夫·迪塞尔命名，但迪塞尔发动机通常拼写为小写d，这与正常做法相反。 |
| Shear test | 剪切试验 |
Any of several tests to obtain shear strength of a metal. Common tests used on mill products include the double-shear test, single-shear test, the blanking shear test (also known as the punching shear test) and the torsion test. 获得金属剪切强度的几种测试中的任何一种。轧机产品上常用的试验包括双剪试验、单剪试验、落料剪切试验（也称为冲切试验）和扭转试验。 |
| Heat-capacity rate (c) (Unit W/K) | 热容率（c）（单位W/K） |
For fluid flow in a duct with mass flow rate ṁ, the product ṁC where C is the specific-heat capacity, at constant pressure (CP) in the case of a gas. 对于质量流量为ṁ的管道中的流体流动，乘积ṁC其中C是比热容，在气体的情况下为恒定压力（CP）。 |
| Semiguided bend | 半导弯曲 |
The bend obtained by applying a force directly to the specimen in the portion that is to be bent. The specimen is either held at one end and forced around a pin or rounded edge, or is supported near the ends and bent by a force applied on the side of the specimen opposite the supports and midway between them. In some instances, the bend is started in this manner and finished in the manner of a free bend. 通过将力直接施加于待弯曲部分中的试样而获得的弯曲。将试样固定在一端，并围绕销或圆边施力，或者在靠近端部的位置支撑试样，并通过施加在试样与支撑件相对的一侧以及两者中间的力进行弯曲。在某些情况下，折弯以此方式开始，然后以自由折弯的方式结束。 |
| Fracture mechanics | 断裂力学 |
The stress analysis of bodies containing cracks. The use of stressconcentration factors and other correction factors of traditional strength of materials is inadequate when flaws are present initially (or develop during loading), since fracture depends not only on stress but also the size of the crack. Traditional strength of materials stress calculations cannot predict either the safe working stress in the presence of a known flaw, or the critical size of flaw just tolerable with a given working stress. 含裂纹物体的应力分析。当初始存在缺陷（或在加载过程中形成缺陷）时，使用应力集中系数和传统材料强度的其他修正系数是不够的，因为断裂不仅取决于应力，还取决于裂纹的大小。传统的材料强度应力计算既不能预测已知缺陷存在时的安全工作应力，也不能预测给定工作应力下可容忍的缺陷临界尺寸。 |
| Uniform elongation | 均匀伸长 |
The elongation at maximum load and immediately preceding the onset of necking in a tension test. 在拉伸试验中，在最大载荷下和颈缩开始之前的伸长率。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Jack | 杰克装置 |
A lifting device that exerts large forces over small displacements, achieved by mechanical gearing or hydraulics. 通过机械传动或液压装置在小位移上施加大力的提升装置。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Hydraulics | 液压系统 |
The study of water flow in open channels (including canals, rivers, etc.), water-supply, drainage, and irrigation systems. 研究明渠（包括运河、河流等）、供水、排水和灌溉系统中的水流。 |
| Chafing fatigue | 磨损疲劳 |
Fatigue damage initiated in a surface damaged by rubbing against another body. 因与另一个物体摩擦而损坏的表面引起的疲劳损坏。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Cylinder head | 气缸盖 |
The machined casting, typically of aluminium alloy or cast iron, that fits above the cylinder block of a piston engine and closes off the cylinders. It normally includes part of the combustion chambers and holes for the valves and spark plugs. 活塞式发动机缸体上方的机械铸件，通常由铝合金或铸铁制成，用于封闭气缸。它通常包括燃烧室的一部分以及阀门和火花塞的孔。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Horizontal batch furnace | 卧式间歇炉 |
A versatile batch-type furnace that can give light or deep case depths, and because the parts are not exposed to air, horizontal batch furnaces can give surfaces almost entirely free of oxides. 一种多功能间歇式炉，可以提供浅或深的外壳深度，并且由于零件不暴露在空气中，卧式间歇式炉可以使表面几乎完全没有氧化物。 |
| Engine | 引擎 |
A machine that converts energy, including the chemical energy in a fuel and electrical energy, into mechanical energy, usually to produce power delivered through a rotating shaft or thrust. Examples include internal-combustion engines, gas and steam turbines, rocket engines, electric, hydraulic and pneumatic motors. 一种将能量（包括燃料中的化学能和电能）转换为机械能的机器，通常通过旋转轴或推力产生动力。例子包括内燃机、燃气轮机和蒸汽轮机、火箭发动机、电动、液压和气动马达。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Fatigue limit | 疲劳极限 |
The maximum stress that presumably leads to fatigue fracture in a specified number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. Compare with endurance limit. 在指定数量的应力循环中可能导致疲劳断裂的最大应力。还应说明最大应力值和应力比。与耐力极限比较。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Tyre | 轮胎 |
A flexible ring-shaped cover mounted on a wheel rim that supports the weight of a vehicle, such as a motor vehicle, aircraft, or bicycle, and transmits power and torque to a road surface. Some pneumatic tyres are inflated directly, others have a separate inner tube that is inflated. For certain applications, solid tyres are used. 车轮罩安装在轮辋上的柔性环形罩，用于支撑车辆（如机动车、飞机或自行车）的重量，并将动力和扭矩传递到路面。有些充气轮胎是直接充气的，有些轮胎有单独的内胎充气。对于某些应用，使用实心轮胎。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Concurrent engineering | 并行工程 |
The integration of the procedures for product design, material selection and manufacturing method to include life-cycle analysis. 产品设计、材料选择和制造方法程序的整合，包括生命周期分析。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Tolerance limits | 公差极限 |
The extreme values (upper and lower) that define the range of permissible variation in size or other quality characteristic of a part. 定义零件尺寸或其他质量特性允许偏差范围的极值（上限和下限）。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Thermodynamic pressure (Unit Pa) | 热力学压力（单位Pa） |
The pressure within a fluid given by an equation of state such as p(ρ,T) where ρ is the fluid density and T is the absolute temperature of the fluid. 流体中的压力由状态方程给出，如p（ρ，T），其中ρ是流体密度，T是流体的绝对温度。 |
| Graham’s laws | 格雷厄姆定律 |
The laws stating that the rates of diffusion and effusion of a gas are inversely proportional to the square root of its density. 规定气体的扩散和渗出速率与其密度的平方根成反比的定律。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Selective heating | 局部加热 |
Intentionally heating only certain portions of a workpiece. 有意仅加热工件的某些部分。 |
| Plastic deformation | 塑性变形 |
The permanent (inelastic) distortion of a material under applied stress that strains the material beyond its elastic limit. 材料在施加应力下的永久（非弹性）变形，使材料应变超过其弹性极限。 |
| Pin expansion test | 插头膨胀试验 |
A test for determining the ability of a tube to be expanded or for revealing the presence of cracks or other longitudinal weaknesses in it, made by forcing a tapered pin into the open end of the tube, similar to flare test. 通过将锥形销压入管道开口端来确定管道膨胀能力或揭示其存在裂纹或其他纵向缺陷的试验，类似于扩口试验。 |
| Hydrogen damage | 氢损伤 |
A general term for the embrittlement, cracking, blistering, and hydride formation that can occur when hydrogen is present in some metals. 当氢存在于某些金属中时可能发生的脆化、开裂、起泡和氢化物形成的总称。 |
| Turbocharging | 涡轮增压 |
A method of supercharging in which the hot exhaust gas from a piston engine is used to drive a turbine which powers the supercharging compressor. A turbocharger is the turbine/compressor combination. The compressor is usually of radial outflow design while radial, axial, and mixed-flow turbines are all in use. The wastegate is a valve that reduces the flow of exhaust gas into the turbine to limit the boost produced or overspeeding. Not shown in the diagram are bearings, oil passages, etc. 一种增压方法，其中活塞发动机的热废气用于驱动涡轮，涡轮为增压压缩机提供动力。涡轮增压器是涡轮/压缩机组合。压缩机通常为径向流出设计，而径向、轴向和混流式涡轮机都在使用。废气旁通阀是一种减少进入涡轮的废气流量以限制产生的增压或超速的阀。 |
| Gibbs–Dalton law | 吉布斯-道尔顿定律 |
An extension of Dalton’s law of additive pressures to include the statement that the internal energy, enthalpy, and entropy of a mixture of gases are equal to the sum of the internal energies, enthalpies, and entropies the individual constituents would have if each existed alone at the same temperature and volume. Gibbs rule is that part of the law pertaining to entropy. 道尔顿附加压力定律的扩展，包括以下陈述：气体混合物的内能、焓和熵等于各个成分单独存在时的内能、焓和熵之和。相同的温度和体积。吉布斯定律是与熵有关的定律的一部分。 |
| Gear pump | 齿轮泵 |
A positive-displacement pump in which fluid is pumped by meshing gears, one driven and the other an idler gear, on parallel axes within a closed casing. 一种容积式泵，其中流体由啮合齿轮泵送，在封闭外壳内的平行轴上一个驱动，另一个为空套齿轮。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Alloy | 合金 |
1. A metallic material composed of two or more elements, one of which is usually a metal to which the other elements are added, e.g. iron-carbon or aluminium-copper (binary alloy); nickel-chromium-iron (ternary alloy). 2. A plastic produced as a blend of two or more immiscible polymers. This results in material that cannot be achieved by polymerization. 1.由两种或多种元素组成的金属材料，其中一种通常是添加了其他元素的金属，例如铁碳或铝铜（二元合金）；镍铬铁（三元合金）。2.由两种或多种不混溶聚合物混合而成的塑料。这导致无法通过聚合获得的材料。 |
| Diaphragm meter | 隔膜计 |
A dry flow meter in which there are two or more interconnected chambers, each having a diaphragm in the wall. The chambers empty and fill alternately and the flow rate of gas is determined from the movement of diaphragms. Diaphragm meters are commonly used to monitor domestic and commercial gas supply. 一种干式流量计，其中有两个或多个相互连接的腔室，每个腔室的壁上都有一个隔膜。腔室交替排空和填充，气体流速由隔膜的移动确定。隔膜流量计通常用于监测家用和商用燃气供应。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Salt bath heat treatment | 盐浴热处理 |
Heat treatment carried out in a bath of molten salt. 在熔融盐浴中进行的热处理。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Absolute zero | 绝对零度 |
Temperature of -273.16″C or 459.69″F or OK at which molecular motion vanishes and a body has no heat energy. 温度为-273.16″C或459.69″F，此时分子运动消失且物体没有热能。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Uniform strain | 均匀应变 |
The strain occurring prior to the beginning of localization of strain (necking); the strain to maximum load in the tension test. 在应变局部化（颈缩）开始之前发生的应变；拉伸试验中最大载荷的应变。 |
| Tension testing | 张力测试 |
A method of determining the behavior of materials subjected to uniaxial loading, which tends to stretch the metal. A longitudinal specimen of known length and diameter is gripped at both ends and stretched at a slow, controlled rate until rupture occurs. Also known as tensile testing. 一种确定材料在单轴载荷下的行为的方法，这种载荷倾向于拉伸金属。将已知长度和直径的纵向试样夹持在两端，并以缓慢、受控的速率拉伸，直到发生断裂。也称为拉伸测试。 |
| Wedge | 楔子 |
A short triangular prism whose major surfaces subtend an acute angle, that can be driven between two objects or parts of an object to split, tighten, or secure them, or to widen an opening or raise a heavy object. The acute angle gives a high mechanical advantage. 一种短的三棱镜，其主面对着一个锐角，可在两个物体或物体的一部分之间驱动，以将它们分开、拧紧或固定，或加宽开口或举起重物。锐角具有很高的机械优势。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Verification | 检验 |
Checking or testing an instrument to ensure conformance with a specification. 检查或测试仪器以确保符合规范。 |
| Absorption dynamometer | 吸收式测功机 |
A dynamometer in which input work or power is dissipated by mechanical friction, electrical resistance, hydraulic resistance, etc. 通过机械摩擦、电阻、液压阻力等耗散输入功或功率的测功机。 |
| Acoustic separation | 声学分离 |
(Unit m) The separation of particles in a fluid using standing acoustic waves, typically ultrasound, to drive them to nodal points (acoustic particle concentration). （单位m）使用驻声波（通常是超声波）将流体中的粒子分离，以将它们驱动到节点（声学粒子浓度）。 |
| Air composition | 空气成分 |
The sea-level composition (in per cent by volume) of air at a temperature of 15°C and a pressure of 1 atm is mainly 78.084% nitrogen, 20.947% oxygen and 0.934% argon. The remaining 0.035% consists of carbon dioxide, neon, helium, methane, krypton, hydrogen, oxides of nitrogen, xenon, ozone, iodine, carbon monoxide, and ammonia. Different sources give slightly different figures for the composition. Not included are water vapour (typically 0.4%) and pollutants such as sulfur dioxide. 在15°C的温度和1个大气压的压力下，空气的海平面成分（体积百分比）主要是78.084%的氮气、20.947%的氧气和0.934%的氩气。剩余的0.035%由二氧化碳、氖、氦、甲烷、氪、氢、氮的氧化物、氙、臭氧、碘、一氧化碳和氨组成。不同的来源给出的组成略有不同。不包括水蒸气（通常为0.4%）和二氧化硫等污染物。 |
| Mechanical properties of solid materials | 固体材料的力学性能 |
The strength and stiffness properties of solid materials such as fracture toughness, the moduli of elasticity, percent elongation, 固体材料的强度和刚度特性，例如断裂韧性、弹性模量、伸长率、 |
| Permanent set | 永久变形 |
The deformation or strain remaining in a previously stressed body after release of load. 释放荷载后，先前受力物体中剩余的变形或应变。 |
| Oxygen probe | 定氧测头 |
An atmosphere-monitoring device that electronically measures the difference between the partial pressure of oxygen in a furnace or furnace supply atmosphere and the external air. 一种大气监测装置，以电子方式测量熔炉或熔炉供应大气中的氧分压与外部空气之间的差值。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| Fracture strength | 断裂强度 |
(fracture stress) (Unit Pa) The stress at which a material breaks. It is not absolute for a given material, as it depends on the laws of fracture mechanics and is size-dependent. （断裂应力）（单位Pa）材料断裂时的应力。对于给定的材料，它不是绝对的，因为它取决于断裂力学定律，并且取决于尺寸。 |
| Hardenability | 淬透性 |
Defined as the ability of a ferrous material to acquire hardness after austenitization and quenching. The relative ability of a ferrous alloy to form martensite when quenched from a temperature above the upper critical temperature. Hardenability is commonly measured as the distance below a quenched surface where the metal exhibits a specific hardness (50 HRC, for example) or a specific percentage of martensite in the microstructure. 定义为黑色金属材料在奥氏体化和淬火后获得硬度的能力。铁合金从高于上临界温度的温度淬火时形成马氏体的相对能力。淬透性通常以淬火表面下方的距离来测量，金属在淬火表面处表现出特定硬度（例如50HRC）或微观结构中马氏体的特定百分比。 |
| Cavitation | 空蚀空化 |
The formation of vapour- or gas-filled cavities in a liquid due to reduction of the local pressure, often due to acceleration of the fluid, such as in flow through a convergent nozzle. If there is no dissolved gas in the liquid, vaporous cavitation occurs when the pressure falls below the saturated vapour pressure. If the bubbles are formed due to high temperature, the process is termed boiling. If there is dissolved gas, gaseous cavitation occurs due to pressure reduction, temperature increase, or diffusion (degassing). At the tips of marine propellers and in hydraulic machinery, the collapse of cavitation bubbles can cause noise and vibration and lead to surface damage in the form of pitting. 由于局部压力降低而在液体中形成充满蒸汽或气体的空腔，通常原因是流体的加速，例如收敛喷嘴的流动。如果液体中没有溶解气体，当压力降至饱和蒸汽压力以下时，会发生蒸汽空化。如果气泡是由于高温形成的，则该过程称为沸腾。如果存在溶解气体，则由于压力降低、温度升高或扩散（脱气），会发生气穴。在船用螺旋桨尖端和液压机械中，空化气泡的破裂可能会引起噪音和振动，并导致以点蚀形式出现的表面损坏。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Brittle lacquer coating | 脆性漆涂层 |
A lacquer that, when painted on to an unloaded body, reveals the direction of maximum tension stresses from the pattern of cracking produced in the lacquer when the body is loaded. 一种漆，当涂在未加载的车身上时，从车身加载时在漆中产生的裂纹图案中显示出最大拉应力的方向。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Vapour static pressure | 蒸汽静压 |
(Unit Pa or bar) A pressure analogous to hydrostatic pressure, where the fluid is a vapour such as steam. A term used in geothermal applications. （单位Pa或bar）类似于静水压力的压力，其中流体是蒸汽，如蒸汽。地热应用中使用的术语。 |
| Sizing | 颗粒化 |
1. A finishing operation to ensure the specified dimensions and tolerances for a component are met. 2. (size classification) Separating an aggregate of mixed particles into groups according to size using a series of screens. 1.精加工操作，以确保满足部件的规定尺寸和公差。2.（粒度分类）使用一系列筛网根据粒度将混合颗粒的聚集体分成组。 |
| Stress difference (Unit Pa) | 应力差（单位Pa） |
The algebraic difference between the largest and least principal stresses in a loaded body, equal to twice the greatest shear stress in the system. For σ1 > σ2 > σ3, it is given by (σ1 − σ3). 载荷体中最大和最小主应力之间的代数差，等于系统中最大剪应力的两倍。由（σ1− σ3).，可得σ1＞σ2＞σ3。 |
| PSI (pounds per square inch) | PSI（磅/平方英寸） |
Pressure measurement. Psia (pounds per square inch absolute) measures actual pressure with no allowance for atmospheric pressure. Psig (pounds per square inch gauge) measures pressure with the gauge set to zero (0) at atmospheric pressure (14.7 psia). In other words psig = psia – 14.7. 压力测量。Psia（绝对磅/平方英寸）测量实际压力，不考虑大气压力。Psig（磅/平方英寸表压）在大气压（14.7 psia）下，将表压设置为零（0）时测量压力。换句话说，psig=psia–14.7。 |
| Essential conditions | 必要条件 |
Each type of failure to which bolted joints are subject is set up by three or four conditions. The conditions vary, depending on the mode of failure, but never number more than four. Eliminating any one of the essential conditions for a particular type of failure can prevent that type of failure. 螺栓连接所遭受的每种类型的故障都由三个或四个条件确定。根据故障模式的不同，情况会有所不同，但数量不得超过四个。消除特定类型故障的任何一个基本条件都可以防止该类型故障。 |
| Centigrade heat unit | 摄氏热量单位 |
(Celsius heat unit, CHU) An obsolete (i.e. non-SI) unit equal to the energy required to increase the temperature of one pound of pure, air-free water from 14.5°C to 15.5°C at a pressure of one standard atmosphere. （摄氏热量单位，CHU）一个已被淘汰的（即非国际单位制）单位，等于在一个标准大气压的压力下将一磅纯净的无空气水的温度从14.5°C提高到15.5°C所需的能量. |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Magnetic test | 磁性测试 |
Method used to test heat extraction rates of various quenchants. The test works by utilizing the change in magnetic properties of metals at their Curie point–the temperature above which metals lose their magnetism. 用于测试各种淬火剂的热提取率的方法。该测试通过利用金属在居里点（即金属失去磁性的温度）的磁性变化来进行。 |
| Fatigue failure | 疲劳失效 |
Failure that occurs when a specimen undergoing fatigue completely fractures into two parts or has softened or been otherwise significantly reduced in stiffness by thermal heating or cracking. 当经历疲劳的试样完全断裂成两部分或因热加热或开裂而软化或刚度显着降低时发生的失效。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Breaking load | 断裂载荷 |
The maximum load (or force) applied to a test specimen or structural member loaded to rupture. 施加到加载到破裂的试样或结构构件上的最大载荷（或力）。 |
| Temper | 回火 |
(1) In heat treatment, reheating hardened steel or hardened cast iron to some temperature below the eutectoid temperature for the purpose of decreasing hardness and increasing toughness. The process also is sometimes applied to normalized steel. (2) In tool steels, temper is sometimes used, but inadvisedly, to denote the carbon content. (3) In nonferrous alloys and in some ferrous alloys (steels that cannot be hardened by heat treatment), the hardness and strength produced by mechanical or thermal treatment, or both, and characterized by a certain structure, mechanical properties, or reduction in area during cold working. （1）在热处理中，将硬化钢或硬化铸铁重新加热到共析温度以下的温度，以降低硬度和增加韧性。该工艺有时也适用于正火钢。（2）在工具钢中，有时使用回火来表示碳含量，但这是不恰当的。（3）在非铁合金和一些铁合金（不能通过热处理硬化的钢）中，通过机械或热处理或两者产生的硬度和强度，其特征是在冷加工过程中具有一定的结构、机械性能或面积减小。 |
| Sample average | 样本平均值 |
The sum of all the observed values in a sample divided by the sample size. It is a point estimate of the population mean. Also known as arithmetic mean. 样本中所有观察值的总和除以样本大小。它是总体平均值的点估计。也称为算术平均值。 |
| Compressor | 压缩机 |
A turbomachine, of either axial or radial type, that increases the pressure of a gas or vapour. 一种增加气体或蒸汽压力的轴向或径向涡轮机。 |
| Guided-bend test | 导向弯曲试验 |
A test in which the specimen is bent to a definite shape by means of a punch (mandrel) and a bottom block. 用冲头（心轴）和底块将试样弯曲成一定形状的试验。 |
| Indentation hardness | 压痕硬度 |
The resistance of a material to indentation as determined by hardness testing. The indenter, which may be spherical or diamond shaped, is pressed into the surface of a metal under specified load for a given time. (Unit Pa or, non-SI, kgf/mm²) A measurement of hardness taken by means of an indenter, pressed into a material by a load, which makes a permanent impression. The hardness is given by the load divided by the projected (sometimes surface) area of the indentation. Plasticity theory shows that the hardness is about 2.5–3 times the uniaxial yield stress. 通过硬度测试确定的材料抗压痕的能力。压头可以是球形或菱形，在规定的载荷下压入金属表面一段时间。（单位Pa或，非国际单位制，kgf/mm²）通过压头测量硬度，压入材料，形成永久压痕。硬度由载荷除以压痕的投影（有时是表面）面积得出。塑性理论表明，硬度约为单轴屈服应力的2.5–3倍。 |
| Dimension line | 尺寸线 |
A line on an engineering drawing with a numeral above it that shows the length of a feature, usually in millimetres. 工程图上的一条线，上面有一个数字，表示特征的长度，通常以毫米为单位。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Full-size fastener | 全尺寸紧固件 |
Finished fastener with a shank diameter of ds ≈ d or ds > d, or screw threaded to the head, or fully threaded stud. 柄径为ds≈d或ds>d的紧固件，或螺纹连接到头部，或全螺纹螺柱。 |
| Absorber | 吸收器 |
1. An auxiliary vibratory system that favourably modifies the vibration characteristics of a main system. 2. Part of an absorption refrigeration system in which the refrigerant is absorbed by a transport medium. 3. The absorber plate is the receiver of a concentrating solar collector where the radiation is absorbed. 1.一种辅助振动系统，可有利地改变主系统的振动特性。2.吸收式制冷系统的一部分，其中制冷剂被传输介质吸收。3.吸收板是吸收辐射的聚光太阳能集热器的接收器。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Refractory materials | 耐火材料 |
Metals or ceramics that do not melt when exposed to temperature above about 1 500°C or deteriorate rapidly in a continuous temperature above about 550°C. 当暴露于高于约1500°C的温度时不熔化或在高于约550°C的连续温度下快速劣化的金属或陶瓷。 |
| Combustion chamber | 炉膛 |
1. In a piston engine, the volume between the head of an individual cylinder and the crown of the piston in which the fuel–air mixture burns during each power stroke of the engine. 2. (combustor) In a gas-turbine engine, a ramjet, an afterburner, or a rocket motor, the component, often cylindrical or annular in shape, in which the fuel–air mixture burns in a continuous-flow process. 1.在活塞式发动机中，在发动机的每个动力冲程中，燃料-空气混合物燃烧的单个气缸盖和活塞顶之间的体积。2.（燃烧室）在燃气涡轮发动机、冲压发动机、加力燃烧室或火箭发动机中，燃料-空气混合物在连续流动过程中燃烧的部件，通常为圆柱形或环形。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Atmometer | 气压计 |
(atmidometer, evaporimeter) An instrument that measures the rate of evaporation of water from a surface into the atmosphere. （湿度计，蒸发计）测量水从表面蒸发到大气中的速率的仪器。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Principal stress (normal) | 主应力（正常） |
The maximum or minimum value of the normal stressat a point in a plane considered with respect to all possible orientations of the considered plane. On such principal planes the shear stress is zero. There are three principal stresses on three mutually perpendicular planes. The state of stress at a point may be: (1) uniaxial, a state of stress in which two of the three principal stresses are zero; (2) biaxial, a state of stress in which only one of the three principal stresses is zero; or (3) triaxial, a state of stress in which none of the principal stresses is zero. Multiaxial stress refers to either biaxial or triaxial stress. 相对于所考虑平面的所有可能方向，所考虑平面中某点处的法向应力的最大值或最小值。在这样的主平面上，剪切应力为零。在三个相互垂直的平面上有三个主应力。一点的应力状态可以是：（1）单轴，三个主应力中的两个为零的应力；（2）双轴，三个主应力中只有一个为零的应力状态；或（3）三轴，即主应力均不为零的应力状态。多轴应力是指双轴或三轴应力。 |
| Flexural strength | 抗弯强度 |
The maximum stress in the outer fiber at the moment of crack or break. 断裂或断裂时刻外层纤维的最大应力。 |
| Die casting | 压铸 |
A process in which molten metal, particularly alloys of aluminium, magnesium, copper, and zinc, is forced under pressure (10 to 200 MPa) into a reusable hardened-steel mould machined into a die. 在压力（10至200MPa）下将熔融金属（特别是铝、镁、铜和锌的合金）强制进入加工成模具的可重复使用的硬化钢模具中的过程。 |
| Torsional shaft vibration | 扭轴振动 |
The rapid back-and-forth angular twisting along a rotating unbalanced shaft which reaches maxima at critical rotation speeds. Shaft eccentricity, unbalanced mass distribution, oscillatory torque, misalignment, etc. all influence torsional vibration. 沿旋转不平衡轴的快速来回角扭转，在临界转速下达到最大值。轴偏心、质量分布不平衡、振荡扭矩、未对准等都会影响扭转振动。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Secant modulus | 割线模量 |
The slope of the secant drawn from the origin to any specified point on a stress-strain curve. Compare with chord modulus. 从原点到应力应变曲线上任何指定点的割线斜率。与弦模量进行比较。 |
| Nut factor | 螺母系数 |
An experimental constant used to evaluate or describe the ratio between the torque applied to a fastener and the Preload achieved as a result. 用于评估或描述施加在紧固件上的扭矩与由此获得的预载之间的比率的实验常数。 |
| Friction | 摩擦 |
The resistance that a body encounters when sliding over another body, or experiences when a viscous fluid flows over its surface. 一个物体在另一个物体上滑动时遇到的阻力，或者当粘性流体流过其表面时所经历的阻力。 |
| Zone melting (zone refining) | 区域熔炼（区域精炼） |
A process of purification of materials in which a narrow molten zone is moved along the length of the material, resulting in impurities being segregated at one end. 一种净化材料的过程，其中一个狭窄的熔融区沿材料长度移动，导致杂质在一端分离。 |
| Final annealing | 最终退火 |
An imprecise term used to denote the last anneal given to a nonferrous alloy prior to shipment. 一个不精确的术语，用于表示有色金属合金在装运前的最后一次退火。 |
| Poisson’s ratio (ν) | 泊松比（ν） |
The absolute value of the ratio of transverse (lateral) strain to the corresponding axial strain resulting from uniformly distributed axial stress below the proportional limit of the material. 横向（侧向）应变与相应轴向应变之比的绝对值，该比值由低于材料比例极限的均匀分布的轴向应力产生。 |
| Wind energy (Unit kJ) | 风能（单位kJ） |
The kinetic energy associated with wind that can be converted by a wind energy conversion system (WECS) into electrical or mechanical power by a rotor, such as a multi-bladed propeller, exposed to the wind. If the air density is ρ and the wind speed is V, then the kinetic energy flux is ρV3/2. The actual wind power that can be extracted by a wind turbine intercepting a cross section of wind A is CPρAV3/2 where CP is an empirical efficiency factor termed the power coefficient. The wind-energy distribution is a histogram of the calculated wind power that can be generated annually from the windspeed frequency distribution at a given location. A windmill generates mechanical power whereas a wind turbine (wind generator) generates electrical power. The largest wind turbine, manufactured by MHI Vestas, has a power rating of 9.5 MW, a rotor diameter of 164 m, and a hub height of 105 m (the highest wind turbines have heights in the region of 190 m). A wind farm is an array of wind turbines, typically ten to several hundred, at a single location, either onshore or offshore. Energy derived from wind is a major contributor to sustainable energy generation. The largest operational offshore wind farm, located in the Irish Sea, has 87 turbines and a total generating capacity of 659 MW. The largest onshore wind farm is in Kern County, California with some 586 turbines and a total capacity of 1 550 MW. 风能转换系统（WECS）可通过暴露于风中的转子（如多叶片螺旋桨）将与风相关的动能转换为电能或机械能。如果空气密度为ρ，风速为V，则动能通量为ρV3/2。可由截获风a横截面的风力涡轮机提取的实际风功率为CPρAV3/2，其中CP是称为功率系数的经验效率因子。风能分布是根据给定位置处的风速频率分布每年可产生的计算风力的直方图。风车产生机械功率，而风力涡轮机（风力发电机）产生电功率。MHI Vestas制造的最大风力涡轮机的额定功率为9.5MW，转子直径为164m，轮毂高度为105m（最高风力涡轮机的高度为190m）。风电场是一系列风力涡轮机，通常为十到几百台，位于单一位置，无论是陆上还是海上。风能是可持续能源发电的主要贡献者。最大的海上风电场位于爱尔兰海，拥有87台涡轮机，总发电容量为659MW。最大的陆上风电场位于加利福尼亚州克恩县，拥有约586台涡轮机，总容量为1550兆瓦。 |
| Deposit gauge | 沉积量计 |
(deposition gauge) An instrument employed in air pollution studies for measuring the amount of pollutant deposited on a given area in a given time under given conditions. （沉降计）在空气污染研究中使用的仪器，用于测量在给定条件下在给定时间内沉积在给定区域上的污染物量。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Thermochemical treatment | 热化学处理 |
Heat treatment carried out in a medium suitably chosen to produce a change in the chemical composition of the object by exchange with the medium. 在适当选择的介质中进行热处理，以通过与介质交换产生物体化学成分的变化。 |
| Quench cracking | 淬火开裂 |
Fracture of a metal during quenching from elevated temperature. Most frequently observed in hardened carbon steel, alloy steel, or tool steel parts of high hardness and low toughness. Cracks often emanate from fillets, holes, corners, or other stress raisers and result from high stresses due to the volume changes accompanying transformation to martensite. 高温淬火时金属断裂。在高硬度和低韧性的硬化碳钢、合金钢或工具钢零件中最常见。裂纹通常来自圆角、孔、角部或其他应力集中区，并由伴随马氏体转变的体积变化引起的高应力引起。 |
| Ductile cast iron | 球墨铸铁 |
A cast iron that has been treated while molten with an element such as magnesium or cerium to induce the formation of free graphite as nodules or spherulites, which imparts a measurable degree of ductility to the cast metal. Also known as nodular cast iron, spherulitic graphite cast iron and SG iron. 一种铸铁，在熔融时用镁或铈等元素进行处理，以诱导游离石墨形成为球粒或球晶，从而赋予铸造金属可测量的延展性。又称球墨铸铁、球晶石墨铸铁和SG铸铁。 |
| Critical strain | 临界应变 |
The strain just sufficient to cause recrystallization; because the strain is small, usually only a few percent, recrystallization takes place from only a few nuclei, which produces a recrystallized structure consisting of very large grains. 刚好足以引起再结晶的应变；由于应变很小，通常只有百分之几，再结晶只发生在少数核上，从而产生由非常大的晶粒组成的再结晶结构。 |
| Quick coupling | 快速接头 |
(quick disconnect, fast coupling) A hose connection allowing rapid assembly or disassembly and comprising a socket and a plug incorporating a springloaded locking mechanism. （快速断开、快速连接）一种软管连接，允许快速组装或拆卸，包括插座和带有弹簧加载锁定机构的插头。 |
| Load and resistance factor design | 负载和阻力系数设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Assigns uncertainties in the strength of (i.e., resistance of) and in the service loads to be placed on a shear joint to estimate the probable strength of the joint. It is a recently defined alternative to the Allowable stress design procedure. 结构连接研究委员会为AISC制定的设计程序。分配剪切接头的强度（即阻力）和工作荷载的不确定性，以估计接头的可能强度。它是最近定义的容许应力设计程序的替代方案。 |
| Ion carburizing | 离子渗碳 |
A method of surface hardening in which carbon ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma carburizing or glowdischarge carburizing. 一种表面硬化方法，利用高压电能将碳离子在真空中扩散到工件中。与等离子渗碳或辉光放电渗碳同义。 |
| Boyle’s law | 波义耳定律 |
The product of the pressure of a gas p and its volume is constant at a given absolute temperature T. Together with Charles law, it yields the ideal gas equation p = Mrt where m is the mass of gas and R is the specific gas constant. The volume of a gas at constant temperature is inversely proportional to the pressure. This means that as pressure increases, the volume of a gas decreases. 在给定的绝对温度T下，气体的压力p与其体积的乘积是恒定的。与查尔斯定律一起，它产生了理想的气体方程p=Mrt，其中m是气体的质量，R是特定的气体常数。恒温下气体的体积与压力成反比。这意味着随着压力的增加，气体的体积会减少。 |
| Ballonet | 气囊 |
An airbag used in a hybrid airship. Helium gas expels air from the ballonet during ascent. Fans draw air in during descent. 混合动力飞艇中使用的安全气囊。氦气在上升过程中将空气从气囊中排出。风扇在下降过程中吸入空气。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| British Standards Institution (BSI) | 英国标准协会（BSI） |
The Institution in the UK responsible for the preparation and publication of standard specifications (British standards) for manufactured goods, their design, manufacture and testing. 负责为制成品及其设计、制造和测试制定和发布标准规范（英国标准）的英国机构。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Destructive testing | 破坏性测试 |
Measurement of the mechanical properties of a material, component, or structure, by increased loading until the sample fails by fracture, collapse, or buckling. 通过增加载荷测量材料、部件或结构的机械性能，直到样品因断裂、塌陷或屈曲而失效。 |
| Slug wrench | 缓动扳手 |
A box wrench with an anvil on the end of the handle. Torque is produced by striking the anvil with a sledge hammer. 柄端有铁砧的套筒扳手。扭矩是通过用大锤敲击铁砧产生的。 |
| Ductile | 延展性材料 |
(ductile material) Describes a material that can be deformed permanently to large strains without fracture. If a bolt can be stretched well past its yield point before breaking, it is said to be ductile. （延展性材料）描述一种可以永久变形到大应变而不断裂的材料。如果螺栓在断裂前可以很好地拉伸超过其屈服点，则称其具有延展性。 |
| Gasket stress | 垫片应力 |
The contact stress exerted on the gasket by the joint members. 连接件施加在垫片上的接触应力。 |
| Face | 表平面 |
To machine a flat surface perpendicular to the axis at rotation on a lathe. 在车床上加工一个垂直于旋转轴的平面。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Structural frame | 结构框架 |
The underlying load-bearing framework of beams, columns, bracing, etc., of steel, concrete, brick, stone, timber etc., required to support the static and dynamic forces a building or component is subjected to, including its weight and that of its contents. 由钢、混凝土、砖、石、木材等制成的梁、柱、支撑等构成的底层承重框架，用于支撑建筑物或构件承受的静态和动态力，包括其重量及其内含物的重量。 |
| Distortion | 扭曲 |
Any deviation from an original size, shape, or contour that occurs because of the application of stress or the release of residual stress. 由于施加应力或释放残余应力而发生的与原始尺寸、形状或轮廓的任何偏差。 |
| T-bolt | T型螺栓 |
A threaded bolt having a square or rectangular end which fits into the T slot of a machine table for clamping workpieces. 一种带有方形或矩形端头的螺栓，可嵌入机床工作台的T形槽中，用于夹紧工件。 |
| Torque monitor | 扭矩监测器 |
A torque tool control system which monitors the amount of torque being developed by the tool during use, but does not control the tool or the torque produced. 一种扭矩工具控制系统，监控工具在使用过程中产生的扭矩量，但不控制工具或产生的扭矩。 |
| Widmanstätten structure | 魏氏组织 |
A structure characterized by a geometrical pattern resulting from the formation of a new phase along certain crystallographic planes of the parent solid solution. The orientation of the lattice in the new phase is related crystallographically to the orientation of the lattice in the parent phase. The structure is readily produced in many alloys by appropriate heat treatment. 一种结构，其特征是沿母体固溶体的某些晶体学平面形成新相而形成的几何图案。新相中晶格的取向在晶体学上与母相中晶格的定向相关。通过适当的热处理，在许多合金中容易产生这种结构。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Shoulder screw | 轴肩螺钉 |
A screw having two or more diameters or shoulders and commonly used for supporting levers and other machine parts that have to operate freely. 一种具有两个或两个以上直径或轴肩的螺钉，通常用于支撑杠杆和其他必须自由操作的机器部件。 |
| Noble metals | 贵金属 |
Metallic elements from periods (rows) 5 and 6 of the periodic table, namely ruthenium, rhodium, palladium, silver, osmium, iridium, platinum, and gold. They resist corrosion and oxidation and are used for electrical contacts, thin-film circuits, and electroplating. Gold, silver, and platinum used for jewellery are also known as precious metals. They have face-centred cubic crystal structure and good ductility. 周期表第5和第6周期（行）中的金属元素，即钌、铑、钯、银、锇、铱、铂和金。它们抗腐蚀和氧化，用于电触点、薄膜电路和电镀。用于珠宝的金、银和铂也被称为贵金属。它们具有面心立方晶体结构和良好的延展性。 |