| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Fatigue crack growth rate (da/dN) | 疲劳裂纹扩展率（da/dN） |
The rate of crack extension caused by constant-amplitude fatigue loading, expressed in terms of crack extension per cycle of load application. 恒幅疲劳荷载引起的裂纹扩展速率，以每次荷载施加循环的裂纹扩展表示。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Caustic cracking | 苛性开裂 |
A form of stress-corrosion cracking most frequently encountered in carbon steels or iron-chromiumnickel alloys that are exposed to concentrated hydroxide solutions at temperatures of 200 to 250 °C (400 to 480 °F). Also known as caustic embrittlement. 在200至250°C（400至480°F）的温度下暴露于浓氢氧化物溶液中的碳钢或铁铬镍合金中最常遇到的一种应力腐蚀开裂形式。也称为碱脆。 |
| Fastener | 紧固件 |
A fastener is a mechanical device for holding two or more bodies in definite positions with respect to each other. 紧固件是一种机械装置，用于将两个或多个物体相对于彼此固定在确定的位置。 |
| Vapour static pressure | 蒸汽静压 |
(Unit Pa or bar) A pressure analogous to hydrostatic pressure, where the fluid is a vapour such as steam. A term used in geothermal applications. （单位Pa或bar）类似于静水压力的压力，其中流体是蒸汽，如蒸汽。地热应用中使用的术语。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Black annealing | 黑退火 |
Box annealing or pot annealing ferrous alloy sheet, strip, wire to impart a black color to the oxidized surface. 对铁合金板、带、线进行箱式退火或罐式退火，使氧化表面呈黑色。 |
| Quench cracking | 淬火开裂 |
Fracture of a metal during quenching from elevated temperature. Most frequently observed in hardened carbon steel, alloy steel, or tool steel parts of high hardness and low toughness. Cracks often emanate from fillets, holes, corners, or other stress raisers and result from high stresses due to the volume changes accompanying transformation to martensite. 高温淬火时金属断裂。在高硬度和低韧性的硬化碳钢、合金钢或工具钢零件中最常见。裂纹通常来自圆角、孔、角部或其他应力集中区，并由伴随马氏体转变的体积变化引起的高应力引起。 |
| Apparent area of contact | 表观接触面积 |
In tribology, the area of contact between two solid surfaces defined by the boundaries of their macroscopic interface. 在摩擦学中，两个固体表面之间的接触区域由其宏观界面的边界定义。 |
| Thermal compressor | 热压缩机 |
1. (thermocompressor) A jet compressor used to boost the pressure of low-pressure waste or exhaust steam. 2. A device consisting of an absorber, a generator, a pump, and a throttling device, used instead of a mechanical vapour compressor in an absorption-cooling refrigeration system. 1.（热压缩机）用于提升低压废蒸汽或排气压力的喷射压缩机。2.一种由吸收器、发电机、泵和节流装置组成的装置，用于替代吸收冷却制冷系统中的机械蒸汽压缩机。 |
| Rotary blower | 旋转鼓风机 |
(rotary compressor) A positive-displacement gas compressor which may be of the blade type, helical-screw type, meshing-lobe type (the Roots blower), or sliding-vane type. （旋转式压缩机）一种容积式气体压缩机，可以是叶片式、螺旋式、啮合凸角式（罗茨鼓风机）或滑动叶片式。 |
| Threading machine | 螺纹机 |
A machine used to cut an external thread on a rod, tube, bolt blank, etc. or an internal thread in a hole, tube, nut blank, etc. 用于切割杆、管、螺栓毛坯等上的外螺纹或孔、管、螺母毛坯等中的内螺纹的机器。 |
| Fatigue strength | 疲劳强度 |
The stress to which a metal can be subjected for a specified number of cyclic changes of stress. The maximum stress that can be sustained for a specified number of cycles without failure. The value of the maximum stress and the stress ratio also should be stated. 金属在指定数量的应力循环变化下可以承受的应力。可以在指定的循环次数内持续而不失效的最大应力。还应说明最大应力值和应力比。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Decompression chamber | 减压舱 |
A chamber in which ambient-air pressure can be increased to levels found in deep-sea diving. It is used to gradually acclimatize divers back to normal conditions and avoid ‘the bends’. 环境气压可以提高到深海潜水水平的腔室。它用于逐渐使潜水员适应正常条件，避免“弯曲”。 |
| Elastic interactions | 弹性相互作用 |
When a bolt is tightened it partially compresses the joint members ‘‘in its own neighborhood.’’ When nearby bolts are tightened later, they further compress the joint in this region. This allows the first bolt to relax a little (lose a little preload). Tightening bolts on the opposite side of the joint, however, might increase preload in some of the earlier bolts tightened on the near side. These shifts and changes in the elastic energy stored in individual bolts, during assembly, are called elastic interactions. 当螺栓拧紧时，它会“在其自身附近”部分压缩接头构件稍后拧紧附近的螺栓时，进一步压缩该区域的接头。这允许第一个螺栓稍微松弛（失去一点预载）。但拧紧接头另一侧的螺栓可能会增加早期在近侧拧紧的一些螺栓的预载。在装配过程中，储存在单个螺栓中的弹性能量的这些位移和变化称为弹性相互作用。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Allotropy | 同素异形体 |
A near synonym for polymorphism. Allotropy is generally restricted to describing polymorphic behavior in elements, terminal phases, and alloys whose behavior closely parallels that of the predominant constituent element. 多态性的近义词。同素异形体通常仅限于描述元素、终端相和合金中的多晶型行为，其行为与主要组成元素的行为非常相似。 |
| Coherent precipitate | 相干沉淀 |
A crystalline precipitate that forms from solid solution with an orientation that maintains continuity between the crystal lattice of the precipitate and the lattice of the matrix, usually accompanied by some strain in both lattices. Because the lattices fit at the interface between precipitate and matrix, there is no discernible phase boundary. 由固溶体形成的结晶沉淀物，其取向保持沉淀物晶格和基体晶格之间的连续性，通常伴随着两个晶格中的一些应变。由于晶格适合于沉淀和基体之间的界面，因此不存在可识别的相边界。 |
| Double tempering | 双回火 |
A treatment in which a quench-hardened ferrous metal is subjected to two complete tempering cycles, usually at substantially the same temperature, for the purpose of ensuring completion of the tempering reaction and promoting stability of the resulting microstructure. 一种处理，其中淬火硬化的黑色金属经过两个完整的回火循环，通常在基本相同的温度下，以确保完成回火反应并提高所得微观结构的稳定性。 |
| Bearing strain | 轴承应变 |
The ratio of the deformation of the bearing hole, in the direction of the applied force, to the pin diameter in a bearing test. 轴承孔在作用力方向上的变形与轴承测试中销直径的比值。 |
| Catastrophic failure | 灾难性故障 |
A sudden and total failure of a large engineering structure such as an aeroengine, aircraft, space vehicle, bridge, or dam. 大型工程结构（如航空发动机、飞机、航天器、桥梁或水坝）突然完全失效。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Teeth | 齿 |
The projecting elements on gears, cutting tools, etc. 齿轮、刀具等上的突出元件。 |
| Slip joint | 滑动接头 |
A mechanical connection which allows limited endwise relative movement of two components such as pipes, rods, and ducts. 一种机械连接，允许两个部件（如管道、杆和管道）进行有限的轴向相对运动。 |
| Shell hardening | 壳型硬化 |
A surface-hardening process in which a suitable steel workpiece, when heated through and quench hardened, develops a martensitic layer or shell that closely follows the contour of the piece and surrounds a core of essentially pearlitic transformation product. This result is accomplished by a proper balance among section size, steel hardenability, and severity of quench. 一种表面硬化工艺，在该工艺中，合适的钢工件在加热和淬火硬化后，会形成一层马氏体层或壳，该层或壳紧随工件的轮廓，并包围一个基本上为珠光体相变产物的核心。这一结果通过截面尺寸、钢淬透性和淬火强度之间的适当平衡来实现。 |
| Fracture | 断裂 |
(rupture) The separation of materials, components, or structures into two or more parts by the propagation of one or more cracks. Cracking may be globally elastic (brittle) or accompanied by varying degrees of plasticity (ductile). （断裂）通过一个或多个裂纹的扩展将材料、部件或结构分离成两个或更多部分。裂纹可能是整体弹性（脆性）或伴有不同程度的塑性（延性）。 |
| Radial engine | 径向发动机 |
A piston engine in which the cylinders are arranged radially around the crankshaft, a design commonly used in early aircraft engines. 气缸沿径向围绕曲轴布置的活塞式发动机，这种设计通常用于早期飞机发动机。 |
| Cavity radiator | 空腔辐射器 |
A heated chamber having a small hole through which radiation, approximating blackbody radiation, passes out. 具有小孔的加热室，近似于黑体辐射的辐射通过该小孔传递出去。 |
| Valve spring | 气门弹簧 |
The spring that restores a valve to its closed position after having been opened, and is also intended to prevent valve bounce. 在阀门打开后将其恢复到关闭位置的弹簧，也用于防止阀门反弹。 |
| Absorption dynamometer | 吸收式测功机 |
A dynamometer in which input work or power is dissipated by mechanical friction, electrical resistance, hydraulic resistance, etc. 通过机械摩擦、电阻、液压阻力等耗散输入功或功率的测功机。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Strain | 拉紧 |
The unit of change in the size or shape of a body due to force. Also known as nominal strain. 物体的大小或形状因力而变化的单位。也称为标称应变。 |
| Dew point | 压力露点 |
The temperature and pressure at which a gas begins to condense to a liquid. 气体开始凝结成液体的温度和压力。 |
| Manometer | 压力计 |
An instrument used in the measurement of a pressure difference in a fluid (manometry). 用于测量流体压力差（测压）的仪器。 |
| Two-phase flow | 两相流 |
A flow in which two phases are present, for example gas bubbles in a liquid, liquid bubbles in another liquid with which it is immiscible, solid particles in a liquid or gas. 两相流动，例如液体中的气泡、与之不混溶的另一种液体中的液体气泡、液体或气体中的固体颗粒。 |
| Torr | 托尔 |
A non-SI unit of pressure commonly used in vacuum systems; defined by 760 torr = 1 atm so that 1 torr = 133.322 368 4 Pa, and approximately equivalent to the pressure corresponding to 1 mm of mercury. 真空系统中常用的非SI压力单位；由760托=1大气压定义，因此1托=133.3223684帕，近似等于对应于1毫米汞柱的压力。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Crankshaft | 曲轴 |
The main shaft, of which the cranks are a part, of a reciprocating single-or multi-cylinder machine. Crankshafts may be built up in sections or forged as a single component. In an engine, the reciprocating motion of the pistons transmits power to the crankshaft and causes it to rotate, whereas in a pump the crankshaft is driven and its rotation causes the pistons to reciprocate. 曲柄是往复式单缸或多缸机器主轴的一部分。曲轴可以分段组装或作为单个部件锻造。在发动机中，活塞的往复运动将动力传递给曲轴并使其旋转，而在泵中，曲轴被驱动，其旋转使活塞往复运动。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Mass flow meter | 质量流量计 |
An instrument, such as a Coriolis flow meter, which measures the mass flow rate of a fluid flowing through a pipe or other duct, rather than its volume flow rate. 一种仪器，例如科里奥利流量计，一种测量流经管道或其他管道的流体的质量流率而不是其体积流率的仪器。 |
| Thermocouple | 热电偶 |
A device for measuring temperature, consisting of lengths of two dissimilar metals or alloys that are electrically joined at one end and connected to a voltage-measuring instrument at the other end. When one junction is hotter than the other, a thermal electromotive force is produced that is roughly proportional to the difference in temperature between the hot and cold junctions. 一种测量温度的装置，由两种不同的金属或合金组成，一端电连接，另一端与电压测量仪相连。当一个结比另一个结更热时，产生的热电动势大致与热结和冷结之间的温差成比例。 |
| Machine | 机器 |
A mechanism that transmits power in the performance of a useful task. More than one machine in one place, either connected or performing separate functions, is termed machinery. 在执行有用任务时传递能量的机制。一个地方有一台以上的连接或执行单独的功能，称为机器。 |
| Angle of torsion | 扭转角 |
(angle of twist) (Unit ° or rad) The angle relative to a chosen section, normal to the axis of twist, through which another part of a component rotates when subjected to a torque. （扭转角）（单位°或弧度）相对于选定截面的角度，垂直于扭转轴，部件的另一部分在受到扭矩时通过该角度旋转。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Fatigue limit for p % survival | p%存活率的疲劳极限 |
The limiting value of fatigue strength for p%survival as the number of stress cycles becomes very large; pmay be any number, such as 95, 90, etc. 随着应力循环次数的增加，p%存活率的疲劳强度极限值变得非常大；p可以是任何数字，例如95、90等。 |
| Hardness profile | 硬度分布 |
Hardness as a function of distance from a fixed reference point (usually from the surface). 硬度作为距固定参考点（通常距表面）的距离的函数。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Pressure surface | 压力面 |
The high-pressure surface of an aerofoil, turbine, or compressor blade. In normal aircraft applications, this is the lower surface of a wing. For applications, such as to high-performance motor vehicles, where the aerofoil is inverted to generate downforce, it is the upper surface. 机翼、涡轮或压缩机叶片的高压表面。在正常的飞机应用中，这是机翼的下表面。对于高性能机动车辆等应用，机翼翻转以产生下压力，它是上表面。 |
| Range of stress (Sr) | 应力范围（Sr） |
The algebraic difference between the maximum and minimum stress in one cycle—that is, Sr = Smax – Smin 一个循环中最大和最小应力之间的代数差，即Sr=Smax–Smin |
| Starting torque (Unit N.m) | 起动扭矩（单位：N.m） |
The torque developed by a motor at zero rotational speed in order to initiate rotation of the applied load. 电机在零转速下产生的扭矩，以启动所施加负载的旋转。 |
| Aspect ratio | 纵横比 |
The ratio of the longest to the shortest dimension of a shape or object e.g. the chord-to-thickness ratio of an aerofoil or the span-to-chord ratio of a wing. 形状或物体的最长与最短尺寸之比，例如机翼的弦厚比或机翼的翼展弦比。 |
| Scale height (Unit m) | 刻度高度（单位：m） |
The altitude H at which the atmospheric pressure has decreased to a certain fraction of its value at sea level B. It depends on the model adopted for the atmosphere: for an isothermal atmosphere, the pressure decreases exponentially with altitude. If H is taken as the altitude at which the pressure has fallen to B/e, then H = RT/g where R is the gas constant for air, T is the absolute temperature T, and g is the acceleration due to gravity. 大气压力降低到其在海平面B处数值的某一部分的高度H。它取决于大气采用的模型：对于等温大气，压力随高度呈指数下降。如果取H作为压力下降到B/e的高度，则H=RT/g，其中R是空气的气体常数，T是绝对温度T，g是重力引起的加速度。 |
| Physical crack size (ap) | 物理裂纹尺寸（ap） |
The distance from a reference plane to the observed crack front. This distance may represent an average of several measurements along the crack front. The reference plane depends on the specimen form, and it is normally taken to be either the boundary or a plane containing either the load line or the centerline of a specimen or plate. 从基准面到观察到的裂纹前沿的距离。该距离可以表示沿裂纹前沿的若干测量的平均值。基准面取决于试样形状，通常视为边界或包含试样或板的载重线或中心线的平面。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Yielding | 屈服 |
Evidence of plastic deformation in structural materials. Also known as plastic flow or creep. 结构材料塑性变形的证据。也称为塑性流动或蠕变。 |
| Wind tunnel | 风洞 |
A duct in which a controlled flow of air is used for testing and research. Types include blow down, closed circuit, open return, and open section. Closed-circuit tunnels may be pressurized or evacuated. The working section is usually situated immediately downstream of the flow-conditioning elements, which may include a plenum chamber, honeycomb, screens, turbulence grids, and a contraction. Immediately downstream there is usually a diffuser. For basic research the usual requirement is for uniform steady flow in the working section with low swirl and turbulence intensity. For some applications the flow may be density stratified, sheared, unsteady, or of high turbulence intensity. 用于测试和研究的可控气流管道。类型包括排污、闭路、开路回路和开路段。闭路隧道可加压或排空。工作段通常位于流量调节元件的下游，可包括增压室、蜂窝、滤网、湍流格栅和收缩管。紧靠下游通常有一个扩散器。对于基础研究，通常的要求是在低涡流和湍流强度的工作段中实现均匀稳定流动。对于某些应用，流动可能是密度分层、剪切、不稳定或高湍流强度。 |
| Crystalline fracture | 结晶断裂 |
A pattern of brightly reflecting crystal facets on the fracture surface of a polycrystalline metal, resulting from cleavage fracture of many individual crystals. 多晶金属断裂面上明亮反射的晶面图案，由许多单个晶体的解理断裂产生。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Acceleration-error constant | 加速度误差常数 |
When the reference (demand) input to a control system is parabolic, the output signal will also be parabolic in steady state. The signal that is constant in this situation is the acceleration and thus for a parabolic input the steady-state error, referred to as the acceleration-error constant, is the error in the acceleration. 当控制系统的参考（需求）输入是抛物线时，输出信号在稳定状态下也将是抛物线。在这种情况下恒定的信号是加速度，因此对于抛物线输入，称为加速度误差常数的稳态误差是加速度中的误差。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Density | 密度 |
The mass per unit volume of a solid material. (mass density, ρ) (Unit kg/m³) The mass per unit volume of a substance that satisfies the continuum assumption. The reciprocal of specific volume. 固体材料每单位体积的质量。（质量密度，ρ）（单位kg/m³）满足连续统假设的物质每单位体积的质量。和比容相关联。 |
| Elongation measurement | 伸张率测量 |
Bolt elongation is directly proportional to axial stress when the applied stress is within the elastic range of the material. If both ends of a bolt are accessible, a micrometer measurement of bolt length made before and after the application of tension will ensure the required axial stress is applied. 当施加的应力在材料的弹性范围内时，螺栓伸长率与轴向应力成正比。如果螺栓的两端都可以接近，则在施加张力前后对螺栓长度进行测微计测量，以确保施加所需的轴向应力。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Compressor | 压缩机 |
A turbomachine, of either axial or radial type, that increases the pressure of a gas or vapour. 一种增加气体或蒸汽压力的轴向或径向涡轮机。 |
| Amontons friction | 阿蒙顿摩擦 |
(Coulomb friction) Friction between surfaces where the ratio of the frictional force F to the normal force N is constant and independent of the area in contact. （库仑摩擦）摩擦力F与法向力N之比恒定且与接触面积无关的表面之间的摩擦。 |
| Threshold stress for stress-corrosion cracking (σth) | 应力腐蚀开裂阈值应力（σth） |
An experimentally determined critical gross-section stress below which stress-corrosion cracking will not occur under specified test conditions. 实验确定的临界总截面应力，低于该应力，在规定的试验条件下不会发生应力腐蚀开裂。 |
| Rotary piston flow meter | 旋转活塞流量计 |
A rotary liquid flow meter in which a cylindrical rotor, eccentrically mounted within a cylindrical casing, the axes of the two cylinders being parallel, is caused to rotate by the liquid flow. The flow rate is determined from the number of rotations of the rotor in a given time. 一种旋转式液体流量计，其中偏心安装在圆柱形外壳内的圆柱形转子，两个圆柱体的轴线平行，由液体流引起旋转。流量由转子在给定时间内的转数确定。 |
| Air composition | 空气成分 |
The sea-level composition (in per cent by volume) of air at a temperature of 15°C and a pressure of 1 atm is mainly 78.084% nitrogen, 20.947% oxygen and 0.934% argon. The remaining 0.035% consists of carbon dioxide, neon, helium, methane, krypton, hydrogen, oxides of nitrogen, xenon, ozone, iodine, carbon monoxide, and ammonia. Different sources give slightly different figures for the composition. Not included are water vapour (typically 0.4%) and pollutants such as sulfur dioxide. 在15°C的温度和1个大气压的压力下，空气的海平面成分（体积百分比）主要是78.084%的氮气、20.947%的氧气和0.934%的氩气。剩余的0.035%由二氧化碳、氖、氦、甲烷、氪、氢、氮的氧化物、氙、臭氧、碘、一氧化碳和氨组成。不同的来源给出的组成略有不同。不包括水蒸气（通常为0.4%）和二氧化硫等污染物。 |
| Corrosion fatigue | 腐蚀疲劳 |
Cracking produced by the combined action of repeated or fluctuating stress and a corrosive environment at lower stress levels or fewer cycles than would be required in the absence of a corrosive environment. 由重复或波动的应力和腐蚀环境的联合作用产生的开裂，其应力水平低于没有腐蚀环境时所需的应力水平或循环次数更少。 |
| Coated abrasive | 涂附磨具 |
An abrasive tool consisting of a flexible backing material, such as a woven cloth, paper or vulcanized fibre, a bond material, such as a glue or synthetic resin, and grit. 一种研磨工具，由柔性背衬材料（例如编织布、纸或硫化纤维）、粘合材料（例如胶水或合成树脂）和砂砾组成。 |
| Steel-wire rope | 钢丝绳 |
A rope or cable made up of many steel strands wrapped helically about an axis, each strand being made of metal wires twisted together like a helix. 一种绳索或缆绳，由许多绕轴螺旋缠绕的钢绞线组成，每根钢绞线由金属丝缠绕在一起形成螺旋。 |
| Shank | 螺杆 |
Portion of a bolt which lies under the head. 1. The stem of a tool, such as a broach, drill bit, reamer, or tap, which fits into a holder such as a chuck. 2. The stem of a rivet or the unthreaded part of a screw or bolt. 3. The shaft of a tool connecting the tip and the handle. 螺栓头部下方的部分。1.一种工具的柄部，如拉刀、钻头、铰刀或丝锥，可装入夹具（如卡盘）中。铆钉的杆或螺钉或螺栓的无螺纹部分。3.连接尖端和手柄的工具的轴。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Free ferrite | 游离铁氧体 |
Ferrite that is formed directly from the decomposition of hypoeutectoid austenite during cooling, without the simultaneous formation of cementite. Also proeutectoid ferrite. 在冷却过程中亚共析奥氏体分解直接形成的铁素体，没有同时形成渗碳体。也是先共析铁氧体。 |
| Physical properties | 物理性质 |
Properties of a material the determination of which does not involve the deformation or destruction of the specimen—for example, density, electrical conductivity, coefficient of thermal expansion, magnetic permeability, and lattice parameter. Does not include chemical reactivity or the properties more appropriately regarded as mechanical properties. 不涉及试样变形或破坏的材料特性，例如密度、电导率、热膨胀系数、磁导率和晶格参数。不包括化学反应性或更适当地视为机械的性质。 |
| Fastener testing | 紧固件测试 |
A determination or verification that the fastener meets its specification requirements. 确定或验证紧固件符合其规范要求。 |
| Turbo generator | 涡轮发电机 |
(turboset) The combination of a steam or gas turbine and an electrical generator with a single shaft or connected coaxial shafts. （汽轮发电机组）蒸汽或燃气轮机与发电机的组合，具有单轴或连接的同轴。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Alloying element | 合金元素 |
Component added deliberately with the aim of improving the properties of an alloy. Alloying elements can affect the existence range of equilibrium phases present in an unalloyed material, or lead to the occurrence of new phases, or both. In addition, alloying elements strongly affect the kinetics of phase transformations and thus the microstructure formation in alloyed materials. 为改善合金性能而有意添加的成分。合金元素可以影响非合金材料中存在的平衡相的存在范围，或导致新相的出现，或两者兼而有之。此外，合金元素强烈影响相变动力学，从而影响合金材料的微观结构形成。 |
| Overaging | 过时效 |
Aging under conditions of time and temperature greater than those required to obtain maximum change in a certain property, so that the property is altered in the direction of the initial value. 在时间和温度条件下的时效大于获得某一特性最大变化所需的时间和温度，从而使该特性沿初始值的方向发生变化。 |
| Finishing temperature | 终轧温度 |
The temperature at which hot working is completed. 完成热加工的温度。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Scleroscope hardness test | 反跃式硬度试验 |
A dynamic indentation-hardness test using a calibrated instrument that drops a diamond-tipped hammer from a fixed height onto the surface of the material being tested. The height of rebound of the hammer is a measure of the hardness of the material. Also known as Shore hardness test. 使用校准仪器的动态压痕硬度测试，该仪器将金刚石锤从固定高度落在被测材料表面上。锤的回弹高度是材料硬度的一种度量。也称为肖氏硬度测试。 |
| Diffusion coating | 扩散涂层 |
Coating on metal for corrosion- and/or oxidation-resistance. Coatings are produced by heating a metal in contact with an alloy in powder, liquid, or gaseous form at elevated temperature such that atoms of the coating diffuse into the substrate. Examples include chromium, aluminium, or silicon on substrates such as nickel-based superalloys, steels, and refractory metals. 金属上的防腐和/或抗氧化涂层。涂层是通过在高温下加热与粉末、液体或气体形式的合金接触的金属，从而使涂层的原子扩散到基体中而产生的。实例包括基底上的铬、铝或硅，如镍基高温合金、钢和耐火金属。 |
| Ferritic stainless steels | 铁素体不锈钢 |
Ferritic stainless steels have the ferrite (BCC) crystal structure and contain 10–28% chromium and typically 0.1–0.35% carbon (all in wt%). They are magnetic and can be hardened by cold working. They have good to moderate mechanical properties, good oxidation and corrosion resistance at elevated temperatures, and susceptibility to embrittlement at temperatures between 400 and 540°C. Used for turbine parts, hightemperature valves, automotive exhaust components, and nuclear reactor core components. 铁素体不锈钢具有铁素体（BCC）晶体结构，含有10-28%的铬，通常含有0.1-0.35%的碳（均为重量%）。它们具有磁性，可通过冷加工硬化。它们具有良好至中等的机械性能，在高温下具有良好的抗氧化性和耐腐蚀性，在400至540°C的温度下易脆化。用于涡轮零件、高温阀、汽车排气部件和核反应堆堆芯部件。 |
| Torsional shaft vibration | 扭轴振动 |
The rapid back-and-forth angular twisting along a rotating unbalanced shaft which reaches maxima at critical rotation speeds. Shaft eccentricity, unbalanced mass distribution, oscillatory torque, misalignment, etc. all influence torsional vibration. 沿旋转不平衡轴的快速来回角扭转，在临界转速下达到最大值。轴偏心、质量分布不平衡、振荡扭矩、未对准等都会影响扭转振动。 |
| Calorizing | 热化 |
Imparting resistance to oxidation to an iron or steel surface by heating in aluminum powder at 800 to 1000 °C (1470 to 1830 °F). 通过在800至1000°C（1470至1830°F）下加热铝粉，赋予铁或钢表面抗氧化性。 |
| Balance piston | 平衡活塞 |
(balance drum, dummy piston) A disc attached to the shaft of a turbine or compressor, to one side of which high or low pressure is applied to counteract the axial thrust produced by the pressure change across the machine. A form of thrust bearing. （平衡鼓，假活塞）连接在涡轮机或压缩机轴上的圆盘，在其一侧施加高压或低压，以抵消机器压力变化产生的轴向推力。推力轴承的一种形式。 |
| Computational domain | 计算域 |
In CFD, FEM, and other numerical methods, the area or volume within which calculations are performed and on the periphery of which the boundary conditions are specified. 在CFD、FEM和其他数值方法中，执行计算的区域或体积以及在其外围指定边界条件的区域或体积。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| Vertical engine | 立式发动机 |
A piston engine having the cylinders above the crankshaft. 气缸位于曲轴上方的活塞发动机。 |
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Interrupted quenching | 间断淬火 |
A quenching procedure in which the workpiece is removed from the first quench at a temperature substantially higher than that of the quenchant and is then subjected to a second quenching system having a different cooling rate than the first. 在该淬火过程中，工件在显著高于淬火剂的温度下从第一次淬火中取出，然后经受具有不同于第一次淬火的冷却速率的第二次淬火系统。 |
| Brittle | 脆性材料 |
A brittle material is one that breaks, often suddenly, with no permanent deformation. Examples of brittle materials are some cast irons, glass, concrete, and some plastics. A bolt is said to be brittle if it will break when stretched only a small amount past its yield point. 脆性材料通常会突然断裂，不会产生永久变形。脆性材料的例子有一些铸铁、玻璃、混凝土和一些塑料。如果螺栓在拉伸时仅超过其屈服点一小部分就会断裂，则称其为脆性螺栓。 |
| Design heating load (Unit kW) | 设计热负荷（单位kW） |
The heating requirements based on a specified number of heating degree days, or required to maintain a building or other enclosed space at a specified temperature for a given outside temperature. 基于指定的采暖度日数的加热要求，或在给定的外部温度下将建筑物或其他封闭空间保持在指定温度下所需的加热要求。 |
| Galling | 磨损 |
An extreme form of adhesive wear, in which large chunks of one part stick to the mating part (during sliding contact). 一种极端形式的粘着磨损，其中一个零件的大块粘在配合零件上（在滑动接触期间）。 |
| Metallurgy | 冶金 |
The study of the atomic, crystallographic, microstructural, mechanical, and physical properties of metallic elements and alloys and their applications. 研究金属元素和合金的原子、晶体学、微观结构、机械和物理特性及其应用。 |
| Anode | 阳极 |
That electrode in a battery or corrosion cell which produces electrons. It is the electrode which is destroyed (corrodes). 电池或腐蚀电池中产生电子的电极。被破坏（腐蚀）的是电极。 |
| Active vibration suppression | 主动振动抑制 |
The reduction of undesirable vibration in components by feedback control. 通过反馈控制减少部件中的不良振动。 |
| Angle of thread | 螺纹角度 |
The included angle between the sides forming the groove of the screw thread. 形成螺纹凹槽的边之间的夹角。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Dynamic mechanical measurement | 动态机械测量 |
A technique in which either the modulus and/or damping of a substance under oscillatory load or displacement is measured as a function of temperature, frequency, or time, or a combination thereof. 一种技术，其中在振荡载荷或位移下测量物质的模量和/或阻尼作为温度、频率或时间或其组合的函数。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Scratching | 刮擦 |
In tribology, the mechanical removal or displacement, or both, of material from a surface by the action of abrasive particles or protuberances sliding across the surfaces. 在摩擦学中，通过在表面上滑动的磨粒或突起的作用，材料从表面上的机械移除或移位，或两者兼而有之。 |
| Check valve | 止回阀 |
(clack valve, non-return valve) A mechanical device that allows fluid flow in one direction only. The numerous designs include ball, diaphragm, disc, lift, split disc, and swing check valves. （瓣阀、止回阀）一种仅允许流体单向流动的机械装置。众多设计包括球阀、隔膜阀、盘阀、升降阀、分体盘阀和旋启式止回阀。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Work ratio | 工作比 |
The ratio of the net work out to the actual work out for a thermodynamic cycle. 热力学循环的净功与实际功之比。 |
| Following flank | 跟随侧翼 |
The flank of a thread opposite to the leading flank. 与前牙面相对的螺纹牙面。 |
| Stress distribution | 应力分布 |
The manner in which tensile, compressive, and shear stresses are distributed within a loaded body, indicated by loci of constant stress. 拉应力、压应力和剪应力在受载物体内的分布方式，由恒定应力轨迹表示。 |
| Breaks | 断裂 |
Creases or ridges usually in “untempered” or in aged material where the yield point has been exceeded. Depending on the origin of the break, it may be termed a cross break, a coil break, an edge break, or a sticker break. 通常在“未回火”或超过屈服点的老化材料中出现折痕或隆起。根据断裂的起源，它可能被称为交叉断裂、线圈断裂、边缘断裂或贴纸断裂。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Waste-heat recovery | 废热回收 |
The recovery of thermal energy from flue and exhaust gases, or from liquids heated in industrial processes. Recovery devices include pre-heaters, recuperators, regenerators, and waste-heat boilers. 从烟道和废气中或从工业过程中加热的液体中回收热能。回收装置包括预热器、回热器、再生器和余热锅炉。 |
| Elastic energy | 弹性能 |
The amount of energy required to deform a material within its elastic range of behavior, neglecting small heat losses due to internal friction. The energy absorbed by a specimen per unit volume of material contained within the gage length being tested. It is determined by measuring the area under the stress-strain curve up to a specified elastic strain. See also modulus of resilience and strain energy. 材料在其弹性行为范围内变形所需的能量，忽略因内耗引起的小热损失。试样在被测标距内每单位体积材料吸收的能量。它是通过测量应力-应变曲线下达到规定弹性应变的面积来确定的。另见弹性模量和应变能。 |
| Centrifugal pump | 离心泵 |
A pump into which liquid enters axially through the eye of the casing and is then accelerated through an impeller, thereby increasing both its kinetic energy and pressure before being delivered to a ring diffuser (the volute) that further increases the liquid pressure and from which it leaves. 一种泵，液体通过泵壳的眼轴向进入，然后通过叶轮加速，从而在输送到环形扩散器（蜗壳）之前增加其动能和压力，从而进一步增加液体压力并从中流出树叶。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Trepanning | 开孔 |
Trepanning is a machining process for producing a circular hole or groove in solid stock, or for producing a disk, cylinder, or tube from solid stock, by the action of a tool containing one or more cutters (usually single-point) revolving around a center. 开孔是一种机械加工工艺，通过包含一个或多个围绕中心旋转的刀具（通常为单点）的作用，在实心坯料中制造圆孔或凹槽，或从实心坯料生产圆盘、圆柱体或管。 |
| Dislocation density | 位错密度 |
The total length of dislocation lines per unit volume, or the number of dislocation lines that cut through a unit cross-sectional area. 每单位体积的位错线的总长度，或穿过单位横截面积的位错线的数量。 |
| Oldham coupling | 十字联轴节 |
(double-slider coupling) A device for connecting a pair of misaligned parallel shafts, on the end of each of which are flanges having diametral tenons (tongues) that engage with matching slots spaced at 90° in an intermediate disc. As the coupling rotates, the disc compensates for shaft offset by sliding along each tenon in turn. Low-friction surfaces are requisite and the disc is often made of a polymer. An alternative arrangement has the slots in the flanges and the tenons on the disc. （双滑块联轴器）一种连接一对未对准平行轴的装置，在每个平行轴的端部有法兰，法兰具有直径榫（舌），与中间盘中间隔90°的匹配槽接合。当联轴器旋转时，圆盘通过依次沿每个榫头滑动来补偿轴偏移。低摩擦表面是必需的，阀盘通常由聚合物制成。另一种布置方式是法兰上的槽和阀盘上的榫头。 |
| Normal stress (Unit N) | 法向应力（单位：N） |
The stress component perpendicular to a plane on which forces act. Normal stress may be either tensile stress or compressive stress. A stress in a fluid (such as pressure) or a solid, that is perpendicular to the surface on which it acts. The surface may be a real external surface or an imaginary internal one. 垂直于受力平面的应力分量。法向应力可以是拉应力或压应力。流体（如压力）或固体中垂直于其作用表面的应力。该表面可以是真实的外表面或假想的内表面。 |
| Ductile cast iron | 球墨铸铁 |
A cast iron that has been treated while molten with an element such as magnesium or cerium to induce the formation of free graphite as nodules or spherulites, which imparts a measurable degree of ductility to the cast metal. Also known as nodular cast iron, spherulitic graphite cast iron and SG iron. 一种铸铁，在熔融时用镁或铈等元素进行处理，以诱导游离石墨形成为球粒或球晶，从而赋予铸造金属可测量的延展性。又称球墨铸铁、球晶石墨铸铁和SG铸铁。 |
| Blade compressor | 叶片式压缩机 |
An oil-free, double-acting rotary compressor in which an angled blade attached to the inner surface of a rotating housing passes through a slot in a disk rotating about an axis perpendicular to that of the housing but offset from it. Air enters through apertures in the housing and leaves through a port in the housing. 一种无油双作用旋转式压缩机，其中连接到旋转外壳内表面的倾斜叶片穿过圆盘上的槽，该槽绕垂直于外壳的轴旋转，但偏离外壳。空气通过壳体中的孔进入，并通过壳体的端口离开。 |
| Intermediate annealing | 中间退火 |
Annealing wrought metals at one or more stages during manufacture and before final treatment. 在制造过程中和最终处理之前的一个或多个阶段对锻造金属进行退火。 |
| Hard temper | 硬化回火 |
Same as full hard temper. 和全硬化回火一样。 |
| Failure of the joint | 连接失效 |
Failure of a bolted joint to behave as intended by the designer. Failure can be caused or accompanied by broken or lost bolts, but can also mean joint slip or leakage from a gasketed joint even if all bolts still remain whole and in place. Common reasons for joint failure include vibration loosening, poor assembly practices, improper design, unexpected service loads or conditions, etc. 螺栓连接未达到设计者的预期性能。故障可能由螺栓断裂或丢失引起或伴随而来，但也可能意味着即使所有螺栓仍保持完整和就位，也存在接头滑动或垫圈接头泄漏。接头故障的常见原因包括振动松动、装配不当、设计不当、意外的工作负载或条件等。 |
| Bearing area | 承载面积 |
The product of the pin (or hole) diameter and specimen thickness in a bearing test. (bearing surface) (Unit m²) The projected area of a hole, such as a rivet hole, that carries a transverse load. 轴承测试中销（或孔）直径和试样厚度的乘积。（承载面）（单位m²）承载横向载荷的孔（例如铆钉孔）的投影面积。 |
| Intense quenching | 强烈淬火 |
Quenching in which the quenching medium is cooling the part at a rate at least two and a half times faster than still water. 淬火，其中淬火介质以比静水快至少两倍半的速度冷却零件。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Compressive strength | 抗压强度 |
Maximum compressive stress a material is capable of developing. With a brittle material that fails in compression by fracturing, the compressive strength has a definite value. For ductile, malleable, or semiviscous materials (which do not fail in compression by a shattering fracture), the value obtained for compressive strength is an arbitrary value dependent on the degree of distortion that is regarded as effective failure of the material. 材料能够产生的最大压缩应力。如果脆性材料因破裂而无法压缩，则抗压强度具有一定值。对于韧性、可锻性或半粘性材料（不会因破裂而导致压缩失效），获得的抗压强度值是一个任意值，取决于被视为材料有效失效的变形程度。 |
| Air-hardening steel | 空气硬化钢 |
A steel containing sufficient carbon and other alloying elements to harden fully during cooling in air or other gaseous mediums from a temperature above its transformation range. The terms should be restricted to steels that are capable of being hardened by cooling in air in fairly large sections, about 2 in. (50 mm) or more in diameter. Same as self-hardening steel. 一种钢，含有足够的碳和其他合金元素，可以在空气或其他气体介质中从高于其转变范围的温度冷却过程中完全硬化。这些术语应仅限于能够通过在相当大的截面（直径约2英寸（50毫米）或更大）中通过空气冷却而硬化的钢。与自硬钢相同。 |
| Bend test | 弯曲试验 |
A test for determining the relative ductility of metal that is to be formed (usually sheet, strip, plate, or wire) or for determining soundness and toughness of metal (after welding, for example). The specimen is usually repeatedly bent over a specified diameter through a specified angle and then unbent for a specified number of cycles. There are four general types of bend tests, named according to the manner in which the forces are applied to the specimen to make the bend: free bend, guided bend, semiguided bend, and wrap-around bend. 确定待成形金属（通常为薄板、带材、板材或线材）的相对延展性或确定金属的坚固性和韧性（例如，焊接后）的试验。试样通常在规定的直径上重复弯曲一个规定的角度，然后在规定的循环次数内弯曲。弯曲试验有四种一般类型，根据施加在试样上的力进行弯曲的方式命名：自由弯曲、引导弯曲、半引导弯曲和环绕弯曲。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Continuous precipitation | 连续沉淀 |
Precipitation from a supersaturated solid solution in which the precipitate particles grow by longrange diffusion without recrystallization of the matrix. Continuous precipitates grow from nuclei distributed more or less uniformly throughout the matrix. They usually are randomly oriented, but may form a Widmanstätten structure. 来自过饱和固溶体的沉淀，其中沉淀颗粒通过长程扩散生长而无需基质再结晶。连续析出物从在整个基体中或多或少均匀分布的核生长而来。它们通常是随机取向的，但可能形成魏氏结构。 |
| Lubricant | 润滑剂 |
Any substance interposed between two surfaces for the purpose of reducing the friction or wear between them. 为了减少两个表面之间的摩擦或磨损而置于两个表面间的任何物质。 |
| Thread grinding | 螺纹磨削 |
A method for producing or finishing very precise screw threads using a profiled grinding wheel. 一种使用异形砂轮生产或精加工非常精密螺纹的方法。 |
| Fastener specification | 紧固件规格 |
A precise statement of set requirements to be satisfied by a fastener, its material, or its processing. It also indicates the procedure used to determine whether the requirements given are satisfied. 对紧固件、其材料或加工过程要满足的设定要求的精确陈述。它还指出了用于确定是否满足给定要求的程序。 |
| Transformation temperature | 相变温度 |
The temperature at which a change in phase occurs. The term is sometimes used to denote the limiting temperature of a transformation range. The following symbols are used for iron and steels. 发生相位变化的温度。该术语有时用于表示转变范围的极限温度。以下符号用于钢铁。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Ratchet coupling | 棘轮联轴器 |
A joint employing a ratchet system between two shafts, so that not only does the driven shaft run in one direction only, but also the driven shaft can, if necessary, run more quickly than the driving shaft. 在两个轴之间采用棘轮系统的接头，这样不仅从动轴只能在一个方向上运行，而且在必要时，从动轴可以比驱动轴运行得更快。 |
| Nut thickness | 螺母厚度 |
The nut thickness shall be the overall distance measured parallel to the axis of nut, from the top of the nut to the bearing surface, and shall include the thickness of the washer face where provided. 螺母厚度应为平行于螺母轴线测量的从螺母顶部到轴承表面的总距离，还应包括垫圈表面的厚度。 |
| Plug gauge | 塞规 |
A steel gauge used to determine the dimension or dimensions of a hole. It may be straight or tapered, and is typically circular, but in principle can have any cross section. 用于确定孔的尺寸的钢制量规。它可以是直的或锥形的，通常是圆形的，原则上可以有任何横截面。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Torsion bar | 扭杆 |
A metal bar designed to act as an elastic spring when torque is applied. 当施加扭矩时用作弹性弹簧的金属棒。 |
| Swept volume (Unit m³) | 扫描体（单位m³) |
In the cylinder of a piston engine or other device, the volume between top and bottom dead centre positions of a piston; equal to πR2S where R is the piston radius and S is the stroke. 在活塞发动机或其他装置的气缸中，活塞上止点和下止点位置之间的体积；等于πR2S，其中R是活塞半径，S是冲程。 |
| Hot hardness | 热硬度 |
The hardness of materials at high temperatures, often used to rank the performance of cutting tools. 材料在高温下的硬度，常用来对刀具的性能进行排名。 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Square | 正方 |
1. A regular quadrilateral, i.e. a polygon with four equal sides and four right angles. 2. An instrument to check angles of internal and external surfaces and flatness. 1.正四边形，即具有四条等边和四个直角的多边形。2.一种检查内外表面角度和平面度的仪器。 |
| Notch brittleness | 缺口脆性 |
Susceptibility of a material to brittle fractureat points of stress concentration. For example, in a notch tensile test, the material is said to be notch brittle if the notch strengthis less than the tensile strength of an unnotched specimen. Otherwise, it is said to be notch ductile. 材料在应力集中点易发生脆性断裂。例如，在缺口拉伸试验中，如果缺口强度小于无缺口试样的抗拉强度，则称材料为缺口脆性材料。否则，称其为缺口韧性。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Monotron hardness test | 摩诺硬度试验 |
An obsolete method of determining indentation hardnessby measuring the load required to force a spherical penetrator into a metal to a specified depth. 一种已被淘汰的方法，通过测量将球形侵彻体压入金属至规定深度所需的载荷来确定压痕硬度。 |
| Boyle’s law | 波义耳定律 |
The product of the pressure of a gas p and its volume is constant at a given absolute temperature T. Together with Charles law, it yields the ideal gas equation p = Mrt where m is the mass of gas and R is the specific gas constant. The volume of a gas at constant temperature is inversely proportional to the pressure. This means that as pressure increases, the volume of a gas decreases. 在给定的绝对温度T下，气体的压力p与其体积的乘积是恒定的。与查尔斯定律一起，它产生了理想的气体方程p=Mrt，其中m是气体的质量，R是特定的气体常数。恒温下气体的体积与压力成反比。这意味着随着压力的增加，气体的体积会减少。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Clip gauge | 夹规 |
A displacement gauge consisting of two thin strain-gauged cantilever arms attached through knife edges to a testpiece to give the load–line displacement in fracture mechanics test pieces, or used as an extensometer in tensile tests. 一种位移计，由两个通过刀刃连接到试件上的薄应变测量悬臂组成，以提供断裂力学试件中的载荷线位移，或用作拉伸试验中的引伸计。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| Lap joint | 搭接接头 |
A riveted, welded, or bonded connection between two plates made by overlapping one plate above the other. Lap joints having plates above and below a butt joint avoid the bending moment associated with a simple lap joint. 两块板之间的铆接、焊接或粘结连接，通过将一块板重叠在另一块板上而形成。对接接头上方和下方具有板的搭接接头避免了与简单搭接接头相关的弯矩。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Root diameter (Unit m) | 根部直径（单位：m） |
The diameter of the circle passing through the roots of teeth in gear teeth or screw threads. 穿过齿轮齿或螺纹中齿根的圆的直径。 |
| Infinite life diagram | 无限疲劳寿命图 |
A simple plot experimentally derived fatigue-life data, showing the conditions required for infinite life. 一个简单的曲线图，实验得出的疲劳寿命数据，显示了无限寿命所需的条件。 |
| Transgranular | 穿晶 |
Through or across crystals or grains. Also known as intracrystalline or transcrystalline. 穿过或横穿晶体或颗粒。也称为晶内或晶间。 |
| Sizing | 颗粒化 |
1. A finishing operation to ensure the specified dimensions and tolerances for a component are met. 2. (size classification) Separating an aggregate of mixed particles into groups according to size using a series of screens. 1.精加工操作，以确保满足部件的规定尺寸和公差。2.（粒度分类）使用一系列筛网根据粒度将混合颗粒的聚集体分成组。 |
| Flame straightening | 火焰矫直 |
Correcting distortion in metal structures by localized heating with a gas flame. 通过使用气体火焰进行局部加热来纠正金属结构的变形。 |
| Form of thread | 螺纹形式 |
The profile of a thread in an axial plane for a length of one pitch. 一个螺距长度的螺纹在轴向平面中的轮廓。 |
| Radioactive heat (Unit J) | 放射性热（单位J） |
Thermal energy released from the nucleus of an atom such as uranium235 by fission due to the absorption of a neutron. Heat is also produced by radioactive decay. 铀235等原子核因吸收中子而裂变释放的热能。放射性衰变也会产生热量。 |
| Safety valve (safety-relief valve) | 安全阀（安全泄压阀） |
A mechanical valve, fitted by law to all pressure vessels (e.g. steam boilers), which opens to prevent the internal pressure exceeding the maximum design value for that vessel. The valve closes again once the pressure reduces to a safe level. 根据法律安装在所有压力容器（如蒸汽锅炉）上的机械阀，其打开以防止内部压力超过该容器的最大设计值。一旦压力降至安全水平，阀门将再次关闭。 |
| Dimensioning | 尺寸标注 |
The specification on an engineering drawing of the size (e.g. length, radius, angle, or spacing) and the relative location (e.g. angular position) of each feature of a component. The numerical values often include the tolerances. There should be no more dimensions than are necessary to manufacture the component. 工程图纸上对部件每个特征的尺寸（例如长度、半径、角度或间距）和相对位置（例如角位置）的规范。数值通常包括公差。尺寸不应超过制造组件所需的尺寸。 |
| Tension | 拉伸 |
The force or load that produces elongation. 1. The condition in a bar, belt, cable, spring, string, wire, etc. that is being pulled from either end. 2. (tensile force) (unit N) The force associated with tension as in (1). It is measured by a tension meter. 伸长力产生伸长的力或载荷。1.从两端拉出的杆、带、电缆、弹簧、线、线等的状态。2.（张力）（单位N）与张力相关的力。 |
| Young’s modulus | 杨氏模量 |
A term used synonymously with modulus of elasticity. The ratio of tensile or compressive stresses to the resulting strain. 与弹性模量同义的术语。拉伸或压缩应力与产生应变的比率。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Hexagon nut | 六角螺母 |
A nut having six sides and shaped like a hexagon. 六边形的螺母。 |
| Taper key | 楔键 |
A key with parallel sides but tapering cross section along its length. 边平行但横截面沿其长度逐渐变细的键。 |
| Hypereutectoid alloy | 过共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of alloying element compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共晶的合金系统中，合金成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Swift cup test | 斯威夫特杯测试 |
A simulative cupping test in which circular blanks of various diameters are clamped in a die ring and deep drawn into cups by a flat-bottomed cylindrical punch. 一种模拟拔杯试验，将不同直径的圆形坯料夹紧在模环中，并用平底圆柱冲头将其深拉入杯中。 |
| Damage | 损伤 |
1. The deterioration of a component or structure in fault or accident conditions, reducing or preventing its ability to perform its intended function. 2. The accumulation of defects or microcracks in the microstructure of a body loaded monotonically or in fatigue, which weakens the body and can lead to crack propagation and failure. 1.部件或结构在故障或事故条件下的劣化，降低或阻止其执行预期功能的能力。2.在承受单调载荷或疲劳载荷的物体的微观结构中累积的缺陷或微裂纹，这会削弱物体，并可能导致裂纹扩展和失效。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Maximum allowable working pressure (Unit Pa) | 最大允许工作压力（单位Pa） |
The pressure on which the design of a pressure system is based and the highest pressure at which relief valves should be set. The lowest-rated component in the system typically has a design safety factor of 4. 压力系统设计所依据的压力和应设置安全阀的最高压力。系统中最低额定部件的设计安全系数通常为4。 |
| Inch-pound force/inch² | 英寸磅力/英寸² |
A non-SI unit for the specific work of fracture (fracture toughness). The conversion to SI is 1 in.lbf/in² = 1.751 268 × 102 J/m². 用于特定断裂功（断裂韧性）的非国际单位制单位。到SI的转换为1英寸。lbf/in²=1.751268×102J/m²。 |
| Shore hardness | 肖氏硬度 |
A measure of the hardness of materials such as elastomers, plastics, and rubbers determined using a Shore durometer which measures the penetration depth of a hardened steel rod (the indenter) 1.1–1.4 mm in diameter into the test material for a given force applied rapidly with a calibrated spring. There are two main indenter designs: type A (for softer materials) for which the end of the rod is a truncated 35° cone tapering to a diameter of 0.79 mm, and type D (harder materials) for which the end is a 30° cone with a 0.1 mm radius tip. The spring force is 8.05 N for type A and 44.45 N for type D. The hardness value is related to the penetration depth (limited to a maximum of 2.5 mm) such that for zero penetration the hardness is 100 and for maximum penetration the hardness is zero. The relevant standards are ISO 48-1, 48-4, and 48-7. Shore hardness values of selected materials are as follows: ABS 100, cellulose acetate 50–95, high-density polyethylene 60–70, low density polyethylene 40–50, polymethylmethacrylate 90–99, PTFE 50–65, and plasticized PVC 15–70. 使用肖氏硬度计测量弹性体、塑料和橡胶等材料的硬度，肖氏硬度仪测量直径为1.1–1.4mm的硬化钢棒（压头）在用校准弹簧快速施加的给定力下渗入试验材料的深度。有两种主要的压头设计：A型（适用于较软的材料），其杆端为截头35°锥形，逐渐变细至直径0.79 mm；D型（较硬的材料），端部为30°锥形，尖端半径为0.1mm。A型的弹簧力为8.05N，D型为44.45N。硬度值与渗透深度相关（最大限制为2.5mm），因此，对于零渗透，硬度为100，对于最大渗透，硬度是零。相关标准为ISO 48-1、48-4和48-7。所选材料的肖氏硬度值如下：ABS100、醋酸纤维素50-95、高密度聚乙烯60-70、低密度聚乙烯40-50、聚甲基丙烯酸甲酯90-99、PTFE50-65和塑化PVC15-70。 |
| Scoring | 划痕 |
In tribology, a severe form of wear characterized by the formation of extensive grooves and scratches in the direction of sliding. 在摩擦学中，一种严重的磨损形式，其特征是在滑动方向上形成大面积的凹槽和划痕。 |
| Tightness parameter | 密封参数 |
A dimensionless parameter which defines the mass leakage of a gasket as a functionof contained pressure and a contained fluid constant. 一种无量纲参数，将垫圈的质量泄漏定义为所含压力和所含流体常数的函数。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Die casting | 压铸 |
A process in which molten metal, particularly alloys of aluminium, magnesium, copper, and zinc, is forced under pressure (10 to 200 MPa) into a reusable hardened-steel mould machined into a die. 在压力（10至200MPa）下将熔融金属（特别是铝、镁、铜和锌的合金）强制进入加工成模具的可重复使用的硬化钢模具中的过程。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Shear joint | 剪切接头 |
A joint which is subjected primarily to loads acting more or less perpendicular to the axes of the bolts. 主要承受或多或少垂直于螺栓轴线的载荷的接头。 |
| Temper embrittlement | 回火脆化 |
Brittleness that results when certain steels are held within, or are cooled slowly through, a certain range of temperature below the transformation range. The brittleness is manifested as an upward shift in ductile-to-brittle transition temperature but only rarely produces a low value of reduction in area in a smooth-bar tension test of the embrittled material. The anomalous reduction in toughness of martensitic stainless steels when tempered in the range 370–600°C. Embrittlement of alloy steels caused by holding within or cooling slowly through a temperature range just below the transformation range. Embrittlement is the result of the segregation at grain boundaries of impurities such as arsenic, antimony, phosphorus, and tin; it is usually manifested as an upward shift in ductile-to-brittle transition temperature. Temper embrittlement can be reversed by retempering above the critical temperature range, then cooling rapidly. 当某些钢保持在低于转变范围的某一温度范围内或缓慢冷却时产生的脆性。脆性表现为延性到脆性转变温度的向上移动，但在脆性材料的平滑棒材拉伸试验中，很少产生较小的面积减小值。马氏体不锈钢在370–600°C范围内回火时的韧性异常降低。合金钢的脆化是由于在低于转变范围的温度范围内保持或缓慢冷却而引起的。脆化是杂质（如砷、锑、磷和锡）在晶界处偏析的结果；它通常表现为韧脆转变温度的上升。回火脆化可以通过在临界温度范围以上重新回火，然后快速冷却来逆转。 |
| Cellular materials | 蜂窝材料 |
There are three broad classes of materials that have a sponge-like structure containing many small closed or open (interlinked) pores or cells. Natural cellular materials include bone, cork, sponge, and wood, and have numerous well-known uses. Wide ranges of cellular plastics are produced using blowing or foaming agents, such as air, ammonium carbonate, sodium bicarbonate, etc., to create pores during the processing of thermoplastic or thermosetting polymers. Rigid foams have moderate compressive strength and can be moulded and machined. 有三大类材料具有海绵状结构，包含许多小的封闭或开放（互连）孔或细胞。天然多孔材料包括骨骼、软木、海绵和木材，有许多众所周知的用途。使用发泡剂或发泡剂（如空气、碳酸铵、碳酸氢钠等）生产各种泡沫塑料，以在热塑性或热固性聚合物加工过程中产生孔隙。硬质泡沫具有中等抗压强度，可模制和机加工。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Equilibrium diagram | 平衡图 |
A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant. 在完全平衡条件下，合金系统中相场的温度、压力和成分极限的图形表示。在金属系统中，压力通常被认为是恒定的。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Relative density | 相对密度 |
(specific gravity) The ratio of the density of a substance to that of a reference substance, such as water for liquids and solids, and dry air for gases. （比重）物质密度与参考物质密度之比，如液体和固体为水，气体为干燥空气。 |
| Rivet | 铆钉 |
A short rod with a head on one end that is inserted through aligned holes in plates to be joined, after which a second head is made on the protruding shank by hammering or forming. The most common head shapes are flat, domed, and inverse conical. In an array, the rivet pitch is the distance between the centres of adjacent rivets. Failure may occur by different mechanisms or modes. A one piece fastener consisting of a head and a body and used for fastening two or more pieces together by passing the body through a hole in each piece and then forming a second head on the body end. It cannot be removed except by taking off the head. 一种一端有头的短杆，插入待连接板上对齐的孔中，然后通过锤击或成型在突出的杆身上制作第二个头。最常见的头部形状是扁平、圆顶和倒锥形。在阵列中，铆钉间距是相邻铆钉中心之间的距离。故障可能由不同的机制或模式发生。一种一体式紧固件，由头部和主体组成，用于将两个或多个部件紧固在一起，方法是将主体穿过每个部件上的孔，然后在主体端部形成第二个头部。除非取下头部，否则无法移除。 |
| Archimedes Wave Swing | 阿基米德波摆动 |
A machine for tidal-power energy generation consisting of two concentric, air-filled submerged cylinders. The inner lower cylinder is tethered to the ocean floor while the upper floater unit, which is closed at the top, moves up and down due to the variations in hydrostatic pressure caused by the wave motion. The relative movement of the two cylinders is used to generate electricity in which linear motion replaces the more common rotary motion of an electromagnetic generator. 一种用于潮汐能发电的机器，由两个同心的充气水下气缸组成。内部下部圆柱体系在海底，而顶部封闭的上部浮子单元由于波浪运动引起的静水压力变化而上下移动。两个气缸的相对运动用于发电，其中直线运动取代了电磁发电机更常见的旋转运动。 |
| Slip band | 滑带 |
A group of parallel slip lines so closely spaced as to appear as a single line when observed under an optical microscope. 一组平行滑移线，间距如此之近，以至于在光学显微镜下观察时显示为一条直线。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Bolt length | 螺栓长度 |
The bolt length shall be the distance measured parallel to the axis of the product from the bearing surface of the head to the extreme end of the bolt including point. 螺栓长度应为平行于产品轴线测量的从头部的支承面到包括点在内的螺栓末端的距离。 |
| Closed-die forging | 闭模锻造 |
The forming of a workpiece by compression within a pair of dies having the female form of the component to be manufactured (closed dies), superfluous metal being expelled as flash where the dies meet. 在一对具有待制造部件的阴模的模具（闭模）内通过压缩形成工件，多余的金属在模具相遇处作为飞边排出。 |
| Allowable stress design | 许用应力设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Purposely underestimates the strengths of bolts and joint materials to introduce safety factors into the design of structural steel joints. It is an alternative to the more recently defined load and resistance factor design procedure. 结构连接研究委员会为AISC制定的设计程序。故意低估螺栓和接头材料的强度，以便在结构钢接头的设计中引入安全系数。它是最近定义的荷载和阻力系数设计程序的替代方法。 |
| Universal joint (Hooke’s joint) | 万向节（胡克接头） |
A double-pivoted connection that allows power and torque to be transmitted between two shafts at an angle to each other. For constant driving angular velocity of the input yoke, the angular velocity of the output yoke fluctuates by amounts depending on the angle of intersection of the shafts. Speeds of the driving and driven shafts may be made identical (giving a constant-velocity joint) when an intermediate shaft, at each end of which there is a universal joint, is interposed. The driving and driven shafts must be equally inclined to the intermediate shaft, the two forks of which must lie in the same plane. 一种双枢轴连接，允许动力和扭矩以一定角度在两个轴之间传递。对于输入磁轭的恒定驱动角速度，输出磁轭的角速度根据轴的相交角度波动。当插入中间轴时，驱动轴和从动轴的速度可以相同（提供恒定速度接头），中间轴的两端都有万向节。主动轴和从动轴必须与中间轴倾斜相等，中间轴的两个叉必须位于同一平面内。 |
| Compression failure | 压缩失败 |
The reduction or removal of a component’s load-bearing capacity in compression, caused by buckling, fracture, crease formation in fibre composites, etc. 由纤维复合材料中的屈曲、断裂、折痕形成等引起的部件在压缩中的承载能力的降低或消除。 |
| Engine emissions | 发动机排放 |
(exhaust emissions) The pollutants contained in the exhaust gases from an internal-combustion engine. （废气排放）内燃机废气中所含的污染物。 |
| Case hardening | 表面硬化 |
A generic term covering several processes applicable to steel that change the chemical composition of the surface layer by absorption of carbon, nitrogen, or a mixture of the two and, by diffusion, create a concentration gradient. The processes commonly used are carburizing and quench hardening; cyaniding; nitriding; and carbonitriding. The use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于钢的几种工艺，这些工艺通过吸收碳、氮或二者的混合物改变表层的化学成分，并通过扩散形成浓度梯度。常用的工艺有渗碳和淬火硬化，氰化，氮化以及碳氮共渗。优选使用适用的特定工艺名称。 |
| Percent error | 误差百分比 |
For testing machines, the ratio, expressed as a percentage, of the error to the correct value of the applied load. 对于试验机，以百分比表示的误差与所施加载荷的正确值之比。 |
| Bernoulli’s law | 伯努利定律 |
For a steadily flowing fluid (liquid or gas), the sum of the pressure, kinetic energy per unit volume and potential energy per unit volume is constant at any point in the fluid. Using this relationship, it is possible to measure the velocity of a fluid by measuring its pressure at two points, as with a manometer or Pitot tube. 对于稳定流动的流体（液体或气体），压力、每单位体积的动能和每单位体积的势能之和在流体中的任何点都是恒定的。使用这种关系，可以通过在两个点测量流体的压力来测量流体的速度，就像使用压力计或皮托管一样。 |
| Edge distance | 边距 |
The distance from the edge of a bearing specimen to the center of the hole in the direction of applied force. 在作用力方向上，从轴承试样的边缘到孔中心的距离。 |
| Critical temperature | 临界温度 |
(1) Synonymous with critical point if the pressure is constant. (2) The temperature above which the vapor phase cannot be condensed to liquid by an increase in pressure. （1） 如果压力恒定，则与临界点同义。（2） 高于该温度时，气相不能通过压力升高而冷凝为液体。 |
| Lead of thread | 螺纹导程 |
On a single threaded screw, the distance the screw or nut advances in one complete revolution. 在单螺纹螺钉上，螺钉或螺母在一整圈中前进的距离。 |
| Vibration-testing machine (vibrator) | 振动试验机（振动器） |
Any machine that subjects components or systems to vibration at known amplitudes and frequencies in order to determine the response. vibratory equipment Vibrating process equipment, such as shakers, used to separate small and large particles, or feeders to supply particulate or granular material that may otherwise clog. 使部件或系统以已知振幅和频率振动以确定响应的任何机器。振动设备振动工艺设备，如用于分离小颗粒和大颗粒的振动筛，或用于供应可能堵塞的颗粒或粒状材料的给料机。 |
| Spalling | 剥落 |
The separation of macroscopic particles from a surface in the form of flakes or chips. 以薄片或碎片形式从表面分离宏观颗粒。 |
| Alloy | 合金 |
1. A metallic material composed of two or more elements, one of which is usually a metal to which the other elements are added, e.g. iron-carbon or aluminium-copper (binary alloy); nickel-chromium-iron (ternary alloy). 2. A plastic produced as a blend of two or more immiscible polymers. This results in material that cannot be achieved by polymerization. 1.由两种或多种元素组成的金属材料，其中一种通常是添加了其他元素的金属，例如铁碳或铝铜（二元合金）；镍铬铁（三元合金）。2.由两种或多种不混溶聚合物混合而成的塑料。这导致无法通过聚合获得的材料。 |
| Gravity | 重力 |
The attractive force by which bodies are drawn towards the centre of Earth or other celestial object. Its intensity is measured by the acceleration produced. The gravitational force of attraction at the surface of a planet or other celestial body. The Earth’s gravity produces an acceleration of around 9.8m/s² for any unsupported body. 物体被拉向地球中心或其他天体的吸引力，行星或其他天体表面的引力。它的强度是通过产生的加速度来衡量的，对于任何无支撑的物体，地球的重力都会产生大约9.8m/s²的加速度。 |
| Collar | 圈、箍 |
A ring secured to, or integral with, a shaft to give axial location. 固定在轴上或与轴成一体以提供轴向位置的环。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| Compression ratio | 压缩率 |
The volume of a combustion chamber with the piston at the top of its stroke as a proportion of the total volume of the cylinder with the piston at the bottom of its stroke. For a piston engine, if the swept volume is SW and the clearance volume is CL, the compression ratio is given by ( SW + CL)/CL, i.e. it is a volume ratio rather than a pressure ratio. 活塞位于其冲程顶部的燃烧室的容积与活塞位于其冲程底部的气缸总体积的比例。对于活塞发动机，如果扫气量为SW，间隙容积为CL，则压缩比由(SW+CL)/CL给出，即它是体积比而不是压力比。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Brine quenching | 盐水淬火 |
A quench in which brine (salt water-chlorides, carbonates, and cyanides) is the quenching medium. The salt addition improves the efficiency of water at the vapor phase or hot stage of the quenching process. 一种淬火，其中盐水（盐水-氯化物、碳酸盐和氰化物）是淬火介质。添加盐提高了水在淬火过程的气相或热阶段的效率。 |
| Blue annealing | 蓝色退火 |
Heating hot-rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental. 在开放式炉中将热轧铁板加热到转变范围内的温度，然后在空气中冷却，以软化金属。在表面上形成蓝色氧化物是偶然的。 |
| Wind energy (Unit kJ) | 风能（单位kJ） |
The kinetic energy associated with wind that can be converted by a wind energy conversion system (WECS) into electrical or mechanical power by a rotor, such as a multi-bladed propeller, exposed to the wind. If the air density is ρ and the wind speed is V, then the kinetic energy flux is ρV3/2. The actual wind power that can be extracted by a wind turbine intercepting a cross section of wind A is CPρAV3/2 where CP is an empirical efficiency factor termed the power coefficient. The wind-energy distribution is a histogram of the calculated wind power that can be generated annually from the windspeed frequency distribution at a given location. A windmill generates mechanical power whereas a wind turbine (wind generator) generates electrical power. The largest wind turbine, manufactured by MHI Vestas, has a power rating of 9.5 MW, a rotor diameter of 164 m, and a hub height of 105 m (the highest wind turbines have heights in the region of 190 m). A wind farm is an array of wind turbines, typically ten to several hundred, at a single location, either onshore or offshore. Energy derived from wind is a major contributor to sustainable energy generation. The largest operational offshore wind farm, located in the Irish Sea, has 87 turbines and a total generating capacity of 659 MW. The largest onshore wind farm is in Kern County, California with some 586 turbines and a total capacity of 1 550 MW. 风能转换系统（WECS）可通过暴露于风中的转子（如多叶片螺旋桨）将与风相关的动能转换为电能或机械能。如果空气密度为ρ，风速为V，则动能通量为ρV3/2。可由截获风a横截面的风力涡轮机提取的实际风功率为CPρAV3/2，其中CP是称为功率系数的经验效率因子。风能分布是根据给定位置处的风速频率分布每年可产生的计算风力的直方图。风车产生机械功率，而风力涡轮机（风力发电机）产生电功率。MHI Vestas制造的最大风力涡轮机的额定功率为9.5MW，转子直径为164m，轮毂高度为105m（最高风力涡轮机的高度为190m）。风电场是一系列风力涡轮机，通常为十到几百台，位于单一位置，无论是陆上还是海上。风能是可持续能源发电的主要贡献者。最大的海上风电场位于爱尔兰海，拥有87台涡轮机，总发电容量为659MW。最大的陆上风电场位于加利福尼亚州克恩县，拥有约586台涡轮机，总容量为1550兆瓦。 |
| Annealing twin | 退火孪晶 |
A twin form in a crystal during recrystallization. 重结晶过程中晶体中的孪晶形式。 |
| Critical point | 临界点 |
(1) The temperature or pressure at which a change in crystal structure, phase or physical properties occurs. Same as transformation temperature. (2) In an equilibrium diagram, that specific value of composition, temperature and pressure, or combinations thereof, at which the phases of a heterogeneous system are in equilibrium. （1） 晶体结构、相或物理性质发生变化的温度或压力。与转变温度相同。（2） 在平衡图中，指组成、温度和压力或其组合的特定值，在该值下，多相体系的相处于平衡状态。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Rated load (Unit N) | 额定负荷（单位：N） |
The maximum load that a structure or component has been designed to carry. 结构或部件设计承受的最大荷载。 |
| Cohesive zone | 凝聚力区 |
In fracture-mechanics modelling and simulation, the region at the crack tip over which an assumed traction (load-displacement) relation has to be overcome to permit initiation and propagation of a crack. 在断裂力学建模和模拟中，必须克服假定的牵引（载荷-位移）关系以允许裂纹萌生和扩展的裂纹尖端区域。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| Cooling stresses | 冷却应力 |
Residual stresses resulting from nonuniform distribution of temperature during cooling. 冷却过程中温度分布不均匀导致的残余应力。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Normality | 常态 |
The principle that the vector sum of plastic strain increments is perpendicular to the yield surface. 塑性应变增量矢量和垂直于屈服面的原理。 |
| Flexural strength | 抗弯强度 |
The maximum stress in the outer fiber at the moment of crack or break. 断裂或断裂时刻外层纤维的最大应力。 |
| Physical testing | 物理测试 |
Methods used to determine the entire range of physical properties of a material. In addition to density and thermal, electrical, and magnetic properties, physical testing methods can be used to assess simple fundamental physical properties such as color, crystalline form, and melting point. 用于确定材料整个物理特性范围的方法。除了密度和热、电、磁特性外，物理测试方法还可用于评估简单的基本物理特性，如颜色、结晶形式和熔点。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Transition temperature (Unit K) | 转变温度（单位K） |
(1) An arbitrarily defined temperature that lies within the temperature range in which metal fracture characteristics (as usually determined by tests of notched specimens) change rapidly, such as from primarily fibrous (shear)to primarily crystalline (cleavage) fracture. (2) Sometimes used to denote an arbitrarily defined temperature within a range in which the ductility changes rapidly with temperature. (transition point) 1. The temperature at which the mechanism of fracture in metal alloys having a face-centred cubic crystal structure changes from ductile void growth to brittle cleavage. 2. The temperature at which a material changes from one crystal state to another. （1） 任意定义的温度，位于金属断裂特性（通常通过缺口试样的试验确定）快速变化的温度范围内，如从主要纤维（剪切）断裂到主要结晶（解理）断裂。（2） 有时用于表示延性随温度快速变化的范围内的任意定义的温度。（转变点）1.具有面心立方晶体结构的金属合金的断裂机制从韧性孔洞生长转变为脆性解理的温度。2.材料从一种晶体状态转变为另一种晶体的温度。 |
| Carbon restoration | 碳修复 |
Replacing the carbon lost in the surface layer from previous processing by carburizing this layer to substantially the original carbon level. Sometimes called recarburizing. 通过将该层渗碳到基本上原始的碳水平来替换先前处理中在表面层中损失的碳。有时称为再碳化。 |
| Offset | 偏移 |
The distance along the strain coordinate between the initial portion of a stress-strain curve and a line parallel to the initial portion that intersects the stress-strain curve at a value of stress (commonly 0.2%) that is used as a measure of the yield strength. Used for materials that have no obvious yield point. 应力-应变曲线的初始部分与平行于初始部分的线之间沿应变坐标的距离，该线以应力值（通常为0.2%）与应力-变形曲线相交，该应力值用作屈服强度的度量。用于没有明显屈服点的材料。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Shear modulus (G) | 剪切模量（G） |
The ratio of shear stress to the corresponding shear strain for shear stresses below the proportional limit of the material. Values of shear modulus are usually determined by torsion testing. Also known as modulus of rigidity. 对于低于材料比例极限的剪切应力，剪切应力与相应剪切应变之比。剪切模量值通常通过扭转试验确定。也称为刚度模量。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| Blind rivet | 盲孔铆钉 |
A rivet that enables a connexion to be made from one side only of an assembly. 一种铆钉，可以仅从组件的一侧进行连接。 |
| T-bolt | T型螺栓 |
A threaded bolt having a square or rectangular end which fits into the T slot of a machine table for clamping workpieces. 一种带有方形或矩形端头的螺栓，可嵌入机床工作台的T形槽中，用于夹紧工件。 |
| Stress cycles endured (N) | 承受的应力循环（N） |
The number of cycles of a specified character (that produce fluctuating stress and strain) that a specimen has endured at any time in its stress history. 试样在其应力历史中任何时间所经受的特定特征（产生波动应力和应变）的循环次数。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Design stress (Unit Pa) | 设计应力（单位Pa） |
The greatest allowable stress in a component or structure that will not result in failure under normal operating conditions. 在正常操作条件下不会导致失效的部件或结构中的最大许用应力。 |
| Vice | 老虎钳 |
A workshop tool used to hold a workpiece and consisting of two jaws, one fixed and the other moved by turning a screw. 一种用于夹持工件的车间工具，由两个钳口组成，一个固定，另一个通过转动螺钉移动。 |
| Surface hardness | 表面硬度 |
(superficial hardness) Indentation hardness on, and for some distance below, the surface of a component, as opposed to its bulk hardness. Depending on the resolution required, micro- or nano-hardness testing machines are employed. （表面硬度）与整体硬度相反，部件表面及其下方一定距离的压痕硬度。根据所需的分辨率，可使用微型或纳米硬度测试机。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Kilocalorie | 千卡 |
(Cal, kg-cal, kilogram-calorie, large calorie) An obsolete (i.e. non-SI) unit of energy equal to 1 000 cal. （卡，千克卡，千克卡路里，大卡路里）一种已被淘汰的（即非国际单位制）能量单位，等于1000卡。 |
| Stress | 应力（单位Pa） |
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression)or shear. 1. Stress ‘at a point’ (i.e. over a volume of material that is very small compared with that of the component or structure) is the load per unit area for every face of an infinitesimal cube surrounding the point. 2. In fluid flow the stress tensor σij is the sum of an isotropic part −pδij, δij being the Kronecker delta, having the same form as the stress tensor for a fluid at rest, p being the static pressure, and the non-isotropic, deviatoric stress tensor dij which is due entirely to the fluid motion. 内部分布力或力分量的强度，这些力或力的分量抵抗正在或已经受到外力的材料的体积或形状的变化。应力以单位面积的力表示，并根据试样横截面的原始尺寸计算。应力可以是直接（拉伸或压缩）或剪切。1.“在一点”的应力（即在与组件或结构相比非常小的材料体积上）是围绕该点的无限小立方体的每个面的单位面积载荷。2. 在流体流动中，应力张量σij是各向同性部分-pδij的总和，δij是Kroneckerδ，具有与静止流体的应力张量相同的形式，p是静压，非各向同性, 偏应力张量 dij 完全由流体运动引起。 |
| Engineering strain (e) | 工程应变（e） |
A term sometimes used for average linear strain or conventional strain in order to differentiate it from true strain. In tension testing it is calculated by dividing the change in the gage length by the original gage length. 一个术语，有时用于平均线性应变或常规应变，以便将其与真实应变区分开来。在张力测试中，通过将标距变化除以原始标距来计算。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Embrittlement | 脆化 |
The loss of ductility or fracture toughness of materials, either during processing or in service. The severe loss of ductility or toughness or both, of a material, usually a metal or alloy. Many forms of embrittlement can lead to brittle fracture. Many forms can occur during thermal treatment or elevated-temperature service (thermally induced embrittlement). Some of these forms of embrittlement, which affect steels, include blue brittleness, 885 °F (475 °C) embrittlement, quench-age embrittlement, sigma-phase embrittlement, strain-age embrittlement, temper embrittlement, tempered martensite embrittlement, and thermal embrittlement. In addition, steels and other metals and alloys can be embrittled by environmental conditions (environmentally assisted embrittlement). The forms of environmental embrittlement include acid embrittlement, caustic embrittlement, corrosion embrittlement, creep-rupture embrittlement, hydrogen embrittlement, liquid metal embrittlement, neutron embrittlement, solder embrittlement, solid metal embrittlement, and stress-corrosion cracking. 材料在加工或使用过程中的延展性或断裂韧性损失。通常是金属或合金的延展性或韧性或两者的严重损失。多种形式的脆化可导致脆性断裂。在热处理或高温服务期间，可能会出现多种形式（热致脆化）。影响钢的一些脆化形式包括蓝脆、885°F（475°C）脆化、淬火时效脆化、西格玛相脆化、应变时效脆化，回火脆化、回火马氏体脆化和热脆化。此外，钢和其他金属和合金可能因环境条件而脆化（环境辅助脆化）。环境脆化的形式包括酸脆化、碱脆化、腐蚀脆化、蠕变断裂脆化、氢脆化、液态金属脆化、中子脆化、焊料脆化、固态金属脆化和应力腐蚀开裂。 |
| Joint diagrams | 接合处关系图 |
Mathematical diagrams which illustrate the forces on and deflections of fasteners and joint members. 说明紧固件和连接件上的力和变形的数学图。 |
| Turbocharging | 涡轮增压 |
A method of supercharging in which the hot exhaust gas from a piston engine is used to drive a turbine which powers the supercharging compressor. A turbocharger is the turbine/compressor combination. The compressor is usually of radial outflow design while radial, axial, and mixed-flow turbines are all in use. The wastegate is a valve that reduces the flow of exhaust gas into the turbine to limit the boost produced or overspeeding. Not shown in the diagram are bearings, oil passages, etc. 一种增压方法，其中活塞发动机的热废气用于驱动涡轮，涡轮为增压压缩机提供动力。涡轮增压器是涡轮/压缩机组合。压缩机通常为径向流出设计，而径向、轴向和混流式涡轮机都在使用。废气旁通阀是一种减少进入涡轮的废气流量以限制产生的增压或超速的阀。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Fillet radius | 圆角半径 |
Concave junction at two intersecting surfaces of a fastener. Often used to describe the junction between the head and the shank of a threaded fastener (under head fillet). 在紧固件的两个相交表面处的凹形接合处。通常用于描述螺纹紧固件的头部和柄部之间的连接处（头部圆角下方）。 |
| Workspace (Unit m³) | 工作空间（单位m³） |
(working-space volume) The volume around the base frame of a robot, defined by the reach of the robot. The robot can thus only perform tasks within this volume. （工作空间体积）机器人基架周围的体积，由机器人的可达范围定义。因此，机器人只能执行该体积内的任务。 |
| Working load (Unit N) | 工作负荷（单位：N） |
The tension in a bolt in use; tension produced by a combination of Residual preload and a portion (usually) of any External load. The Joint diagram is usually used to predict the approximate working load a fastener will see in service. The load under which a component or structure is designed to operate under normal conditions. 螺栓在使用中的张力；残余预载荷和部分（通常）任何外部载荷的组合产生的张力。连接图通常用于预测紧固件在使用中的近似工作载荷。部件或结构设计为在正常条件下运行的荷载。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Statistic | 统计 |
A summary value calculated from the observed values in a sample. 根据样本中的观察值计算得出的汇总值。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| Elastic constants | 弹性常数 |
The factors of proportionality that relate elastic displacement of a material to applied forces. 将材料的弹性位移与施加的力相关联的比例因子。 |
| Dilatation (dilation) | 膨胀 |
A change of volume caused by external load, compression, temperature change, chemical action, etc. 由外部载荷、压缩、温度变化、化学作用等引起的体积变化。 |
| Hydraulics | 液压系统 |
The study of water flow in open channels (including canals, rivers, etc.), water-supply, drainage, and irrigation systems. 研究明渠（包括运河、河流等）、供水、排水和灌溉系统中的水流。 |
| Tracking problem | 跟踪问题 |
A control problem where the set point changes with time and thus the plant output must follow the changing set point. The opposite of a regulator problem. 一种控制问题，其中设定值随时间变化，因此设备输出必须遵循变化的设定值。与调节器问题相反。 |
| Pressure ratio | 压力比 |
One pressure divided by another which may be a reference pressure. In many flow and thermodynamic processes, the pressure ratio is more important than the absolute pressure levels. For example, in compressible gas flow the Mach number is determined by the ratio of the stagnation pressure to the static pressure. 一个压力除以另一个压力，该压力可以是参考压力。在许多流动和热力学过程中，压力比比绝对压力水平更重要。例如，在可压缩气流中，马赫数由停滞压力与静压之比决定。 |
| Structure | 结构体 |
An assembly, usually load bearing, of connected (pinned, riveted, screwed, bolted, welded, etc.) components, such as bars, tubes, beams, and plates. 由连接（销接、铆接、螺纹连接、螺栓连接、焊接等）部件组成的组件，通常为承重组件，如杆、管、梁和板。 |
| Absorption hygrometer | 吸收式湿度计 |
An instrument that determines the content of water vapour in the atmosphere by it being absorbed into a hygroscopic medium. 通过吸收到吸湿介质中来确定大气中水蒸气含量的仪器。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Yield point (Unit Pa) | 屈服点（单位Pa） |
The first stress in a material, usually less than the maximum attainable stress, at which an increase in strain occurs without an increase in stress. Only certain metals—those which exhibit a localized, heterogeneous type of transition from elastic to plastic deformation—produce a yield point. If there is a decrease in stress after yielding, a distinction may be made between upper and lower yield points. The load at which a sudden drop in the flow curve occurs is called the upper yield point. The constant load shown on the flow curve is the lower yield point. (yield strength, yield stress, Rel, Rel) The stress at which the onset of permanent (plastic) deformation (yielding) occurs in a body under increasing loading. In some materials, a yield-point phenomenon occurs in which stress falls on initial yielding and plastic deformation continues without increase in stress as strain increases further. The yield criterion is the combination of normal and shear stresses which produces yielding under multiaxial loading. 材料中的第一应力，通常小于可达到的最大应力，在该应力下应变增加而应力不增加。只有某些金属——表现出从弹性变形到塑性变形的局部、非均匀类型的金属——才会产生屈服点。如果屈服后应力降低，可区分上屈服点和下屈服点。流量曲线突然下降时的荷载称为上屈服点。流量曲线上显示的恒定载荷为较低屈服点。（屈服强度，屈服应力，Rel）在不断增加的载荷下，物体发生永久（塑性）变形（屈服）时的应力。在某些材料中，会出现屈服点现象，即应力在初始屈服时下降，随着应变进一步增加，塑性变形继续，而应力没有增加。屈服准则是在多轴载荷下产生屈服的正应力和剪应力的组合。 |
| Mohr–Coulomb fracture criterion | Mohr–Coulomb断裂准则 |
A fracture criterion, primarily for brittle materials, according to which failure occurs when the stress at a point in a material falls outside the envelope created by the Mohr’s circles for uniaxial tensile strength and uniaxial compressive strength. 一种断裂准则，主要适用于脆性材料，根据该准则，当材料中某一点的应力落在单轴抗拉强度和单轴抗压强度的莫尔圆所形成的包络线之外时，就会发生断裂。 |
| Oxidized surface (on steel) | 氧化表面（在钢上） |
Surface having a thin, tightly adhering, oxidized skin (from straw to blue in color), extending in from the edge of a coil or sheet. Sometimes called annealing border. 表面具有薄的、紧密粘附的氧化皮（从稻草色到蓝色），从线圈或薄片的边缘延伸。有时称为退火边界。 |
| Torsion spring | 扭簧 |
1. A spring in the form of a torsion bar. 2. A helical spring to which torque can be applied at the ends. 1.一种扭杆形式的弹簧。2.一种螺旋弹簧，其端部可施加扭矩。 |
| Galilean transformation | 伽利略变换 |
In steady fluid flow, the addition or subtraction of a constant velocity to the entire flowfield, e.g. so that flow can be considered relative to a moving object or flow feature, such as a shock wave. 在稳定的流体流动中，对整个流场增加或减少恒定速度，例如，可以考虑相对于移动物体或流动特征（例如冲击波）流动。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Stud | 螺柱 |
A rod having thread on both ends. A headless threaded fastener, threaded on both ends, with an unthreaded body in the middle section, or threaded from end to end. Used with two nuts, or with one nut and a tapped hole. A plain cylindrical piece having a threaded portion of suitable length at each end or a continuous thread over the entire length. One end is screwed into a machine or workpiece after which a second part is placed over the stud and held in place by a nut. 两端都有螺纹的杆。无头螺纹紧固件，两端有螺纹，中间部分有无螺纹主体，或从一端到另一端有螺纹。与两个螺母或一个螺母和一个螺纹孔一起使用。一种普通的圆柱形部件，其两端具有适当长度的螺纹部分，或在整个长度上具有连续螺纹。一端拧入机器或工件，然后将第二部分放在螺柱上，并用螺母固定到位。 |
| Flame hardening | 火焰硬化 |
A process for hardening the surfaces of hardenable ferrous alloys in which an intense flame is used to heat the surface layers above the upper transformation temperature, whereupon the workpiece is immediately quenched. 一种用于硬化可硬化铁合金表面的工艺，其中使用强烈的火焰将表面层加热到转变温度上限以上，然后立即对工件进行淬火。 |
| Furnace | 炉 |
1. A type of combustion chamber in which solid, liquid, or gaseous fuels are burned to supply hot gases to a boiler or other process plant. Examples include the firebox, boiler furnace (steam-generating furnace), hot-air furnace, oil-fired furnace, updraught furnace, and water-cooled furnace. 2. A chamber, sometimes having a controlled atmosphere or under vacuum (vacuum furnace), for heating and melting materials. Examples include the blast furnace, direct- and indirect-arc furnaces, the induction furnace (high-frequency furnace), muffle furnace, reverberatory furnace, and solar furnace. 1.一种燃烧室，其中燃烧固体、液体或气体燃料以向锅炉或其他工艺设备供应热气。示例包括燃烧室、锅炉炉（蒸汽发生炉）、热风炉、燃油炉、上升气流炉和水冷炉。2.用于加热和熔化材料的腔室，有时具有受控气氛或真空（真空炉）。例如高炉、直接和间接电弧炉、感应炉（高频炉）、马弗炉、反射炉和太阳能炉。 |
| Turn-of-nut method | 螺母转动法 |
It applies preload by turning a nut through an angle that corresponds to a given elongation. 它通过将螺母旋转一个与给定伸长率相对应的角度来施加预载荷。 |
| X-ray thickness gauge | X射线厚度计 |
A device comprising an X-ray source and a detector used to determine the thickness of material in sheet or plate form, including metals, paper, plastics, rubber, and ceramics. 一种由X射线源和探测器组成的装置，用于测定片状或平板状材料的厚度，包括金属、纸张、塑料、橡胶和陶瓷。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Counter sink | 台面水槽 |
To cut or shape a depression in an object so that the head of a screw may set flush or below the surface. 在物体上切割或塑造一个凹陷，使螺钉的头部可以齐平或低于表面。 |
| Elongation | 伸张率 |
A term used in mechanical testing to describe the amount of extension of a test piece when stressed. 机械测试中使用的术语，用于描述试样在受力时的延伸量。 |
| Spherical washer | 球面垫圈 |
A washer whose upper surface is semispherical. Used with a nut whose contact face is also semispherical. Reduces bending stress in a bolt or stud, by allowing some self-alignment and some compensation for nonparallel joint surfaces or Angularity. 上表面为半球形的垫圈。与接触面也是半球形的螺母一起使用。减少螺栓或螺柱中的弯曲应力，允许一些自对准，并对不平行的接头表面或角度进行一些补偿。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Eutectic | 共晶 |
(1) An isothermal reversible reaction in which a liquid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectic point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectic reaction. （1）一种等温可逆反应，其中液体溶液在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）一种合金，其成分由平衡图上的共晶点表示。（3）由共晶反应形成的混合固体成分的合金结构。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Absorptance | 吸收率 |
(absorptivity, absorption coefficient, α) The fraction of radiant flux incident on a surface that is absorbed by the surface. The term also applies to absorption of radiation by a volume of fluid. For a semi-transparent surface, α + ρ + τ = 1, where ρ is the reflectance and τ is the transmittance. （吸收率，吸收系数，α）入射到表面的辐射通量被表面吸收的部分。该术语也适用于一定体积的流体对辐射的吸收。对于半透明表面，α+ρ+τ=1，其中ρ是反射率，τ是透射率。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Thermoelectric converter | 热电转换器 |
(thermoelectric generator) A device consisting of series-connected alternate n- and p-type semiconductor elements sandwiched between two ceramic plates. Due to the Seebeck effect, electrical power is generated when a temperature difference is maintained across the plates. Due to the Peltier effect, a thermoelectric converter can act as either a thermoelectric heater or a thermoelectric cooler (thermoelectric refrigerator) by passing an electrical current through it. The thermoelectric figure of merit (Z), with unit 1/K, is a dimensional parameter on which the efficiency of a thermoelectric device is primarily dependent, defined by Z = σα2/k where α is the Seebeck coefficient, σ is the electrical conductivity, and k is the thermal conductivity. The product of Z and a temperature is non-dimensional. （热电发生器）由串联连接的交替的n型和p型半导体元件夹在两块陶瓷板之间组成的装置。由于塞贝克效应，当板之间保持温差时，就会产生电能。由于珀尔帖效应，热电转换器可以通过使电流通过而充当热电加热器或热电冷却器（热电制冷机）。热电优值（Z）和第一单元/K是一个尺寸参数，热电装置的效率主要取决于此，由Z=σα2/K定义，其中α是塞贝克系数，σ是电导率，K是热导率。Z和温度的乘积是无量纲的。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Multiple threaded screw | 多螺纹螺钉 |
A screw with two or more threads cut around the periphery of the workpiece to provide an increased lead with a specified pitch. 一种螺钉，具有围绕工件周边切割的两个或多个螺纹，以提供具有指定螺距的增加的导程。 |
| 显示更多数据，请使用查询功能！ | ||