| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Minor diameter | 螺纹小径 |
On a straight thread, the diameter of the imaginary cylinder which just touches the root of an external thread or the crest of an internal thread. 在直螺纹上，仅接触外螺纹根部或内螺纹顶部的假想圆柱体的直径。 |
| Breaking load (Unit N) | 断裂负荷（单位N） |
The load applied at some point to a component or structure which leads to fracture. The breaking stress (breaking strength) is the average stress at which a member breaks, given by the breaking load divided by the area over which it acts. 在某个点施加到导致断裂的部件或结构的载荷。断裂应力（断裂强度）是构件断裂时的平均应力，由断裂载荷除以其作用的面积给出。 |
| Free carbon | 游离碳 |
The part of the total carbon in steel or cast iron that is present in elemental form as graphite or temper carbon. Contrast with combined carbon. 钢或铸铁中总碳中以石墨或回火碳等元素形式存在的部分。与结合碳形成对比。 |
| Load range, P | 负载范围P |
In fatigue, the algebraic difference between the maximum and minimum loads in a fatigue cycle. 在疲劳中，疲劳循环中最大和最小载荷之间的代数差。 |
| Crushing strain | 压应变 |
The supposed single strain that results in comminution of a brittle material. The corresponding stress is termed the crushing strength. Neither quantity can be a material constant as they must obey the laws of fracture mechanics and will depend on the type of testpiece, method of loading etc. 导致脆性材料粉碎的假定单应变。相应的应力称为抗压强度。这两个量都不能是材料常数，因为它们必须遵守断裂力学定律，并取决于试件类型、加载方法等。 |
| SI system | SI国际单位制 |
SI is an abbreviation of Système International d’Unités, i.e., the international unit measurement system – an internationally established system of measurement units built on older metric systems. SI是Système International d‘Unités的缩写，即国际单位计量系统——一种基于旧公制的国际公认计量单位系统。 |
| Conduit | 导管 |
A hollow object, of metal, plastic, glass, ceramic, etc., which is relatively long compared with its lateral dimensions and through which there is fluid flow. 由金属、塑料、玻璃、陶瓷等制成的中空物体，与其横向尺寸相比相对较长，并且有流体流过。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Ductility | 延展性 |
The ability of a material to deform plastically before fracturing. Measured by elongation or reduction in area in a tensile test, by height of cupping in a cupping test, or by the radius or angle of bend in a bend test. 材料在断裂前发生塑性变形的能力。通过拉伸试验中的伸长率或面积减少量、杯突试验中的杯突高度或弯曲试验中的弯曲半径或角度来测量。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| mechanical engineering | 机械工业 |
That branch of engineering concerned with energy conversion, stress analysis, vibration, dynamics, and kinematics, especially applied to design (machine design, mechanical-engineering design). 与能量转换、应力分析、振动、动力学和运动学有关的工程分支，尤其适用于设计（机器设计、机械工程设计）。 |
| Acceleration-error constant | 加速度误差常数 |
When the reference (demand) input to a control system is parabolic, the output signal will also be parabolic in steady state. The signal that is constant in this situation is the acceleration and thus for a parabolic input the steady-state error, referred to as the acceleration-error constant, is the error in the acceleration. 当控制系统的参考（需求）输入是抛物线时，输出信号在稳定状态下也将是抛物线。在这种情况下恒定的信号是加速度，因此对于抛物线输入，称为加速度误差常数的稳态误差是加速度中的误差。 |
| Overaging | 过时效 |
Aging under conditions of time and temperature greater than those required to obtain maximum change in a certain property, so that the property is altered in the direction of the initial value. 在时间和温度条件下的时效大于获得某一特性最大变化所需的时间和温度，从而使该特性沿初始值的方向发生变化。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Critical temperature | 临界温度 |
(1) Synonymous with critical point if the pressure is constant. (2) The temperature above which the vapor phase cannot be condensed to liquid by an increase in pressure. （1） 如果压力恒定，则与临界点同义。（2） 高于该温度时，气相不能通过压力升高而冷凝为液体。 |
| Standard deviation (σ) | 标准偏差（σ） |
A statistical term used to quantify the Scatter in a set of data points. If the standard deviation is small, most of the data points are ‘‘nearly equal.’’ A large deviation means less agreement. The most usual measure of the dispersion of observed values or results expressed as the positive square root of the variance. The square root of variance, a measure of the spread of data about the mean value. 用于量化一组数据点中分散度的统计术语。如果标准偏差很小，则大多数数据点“几乎相等”大的偏差意味着更少的一致性。观测值或结果离散度的最常用度量，表示为方差的正平方根。方差的平方根，衡量平均值的数据分布。 |
| Ferritic stainless steels | 铁素体不锈钢 |
Ferritic stainless steels have the ferrite (BCC) crystal structure and contain 10–28% chromium and typically 0.1–0.35% carbon (all in wt%). They are magnetic and can be hardened by cold working. They have good to moderate mechanical properties, good oxidation and corrosion resistance at elevated temperatures, and susceptibility to embrittlement at temperatures between 400 and 540°C. Used for turbine parts, hightemperature valves, automotive exhaust components, and nuclear reactor core components. 铁素体不锈钢具有铁素体（BCC）晶体结构，含有10-28%的铬，通常含有0.1-0.35%的碳（均为重量%）。它们具有磁性，可通过冷加工硬化。它们具有良好至中等的机械性能，在高温下具有良好的抗氧化性和耐腐蚀性，在400至540°C的温度下易脆化。用于涡轮零件、高温阀、汽车排气部件和核反应堆堆芯部件。 |
| Air-cooled condenser | 风冷冷凝器 |
A heat exchanger, in which the cooling medium is air, used to condense the exhaust steam from a steam turbine, the condensate being returned to the boiler. 一种热交换器，其中冷却介质为空气，用于冷凝蒸汽轮机排出的蒸汽，冷凝水返回锅炉。 |
| Maximum-and-minimum thermometer | 最高和最低温度计 |
(minimum-maximum thermometer, Six’s thermometer) A liquid-in-glass instrument designed to register the maximum and minimum temperatures experienced over a given time period. （最低-最高温度计，Six's温度计）一种液体玻璃仪器，用于记录给定时间段内经历的最高和最低温度。 |
| Mechanical units | 机械单位 |
The units of physical quantities, the dimensions of which includemass, length, and time. 物理量的单位，其量纲包括质量、长度和时间。 |
| Infinite life diagram | 无限疲劳寿命图 |
A simple plot experimentally derived fatigue-life data, showing the conditions required for infinite life. 一个简单的曲线图，实验得出的疲劳寿命数据，显示了无限寿命所需的条件。 |
| Mechanical alloying | 机械合金化 |
Production of alloys from powders by consolidation, e.g. hotpressing or extrusion, followed by hot and/or cold working and final annealing. Materials such as dispersion-strengthened alloys, high-temperature aluminium alloys, and amorphous alloys can be made in this way. 通过固结（例如热压或挤压）从粉末生产合金，然后进行热和/或冷加工和最终退火。用这种方法可以制造弥散强化合金、高温铝合金和非晶合金等材料。 |
| Fracture test | 断裂试验 |
A test in which a specimen is broken and its fracture surface is examined with the unaided eye or with a low-power microscope to determine such factors as composition, grain size, case depth, or internal discontinuities. 1. The recording of load-deflexion (or stress–strain) in a specimen loaded monotonically until it breaks in tension, compression, shear, or torsion. 2. In fatigue, determination of the number of cycles to fracture for a specimen under different patterns of repeated loading. 3. Experiments to determine fracture toughness. 一种试验，其中试样被破坏并用肉眼或低倍显微镜检查其断裂表面，以确定成分、晶粒尺寸、表层深度或内部不连续性等因素。1.记录单调加载试样的载荷偏转（或应力-应变），直到其在拉伸、压缩、剪切或扭转中断裂。2.在疲劳技术中，确定试样在不同重复载荷模式下的断裂循环次数。3.测定断裂韧性的实验。 |
| Friction materials | 摩擦材料 |
Materials having a high coefficient of friction which, when coupled with a long life, may be employed as brake linings or the facing of the plates of a clutch. 具有高摩擦系数的材料，当与长寿命相结合时，可用作制动衬片或离合器片的饰面。 |
| Heat balance (heat budget) | 热平衡（热预算） |
An energy balance involving only heat transfer across the system boundary and the stored energy. 仅涉及跨系统边界的热传递和存储能量的能量平衡。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Dimensional stability | 尺寸稳定性 |
Ability of a plastic part to retain the precise shape in which it was molded, fabricated, or cast. 塑料零件保持其成型、制造或铸造时的精确形状的能力。 |
| Raised-face flange | 凸面法兰 |
A flange which contacts its mating joint member only in the region in which the gasket is located. The flanges do not contact each other at the bolt circle. 仅在垫圈所在区域接触其配合接头构件的法兰。法兰在螺栓圆处不相互接触。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Bearing test | 轴承测试 |
A method of determining the response to stress (load) of metal products that are subjected to riveting, bolting, or a similar fastening procedure. The purpose of the test is to determine the bearing strength of the material and to measure the bearing stress versus the deformation of the hole created by a pin or rod of circular cross section that pierces the sheet perpendicular to the surface. 一种确定经受铆接、螺栓连接或类似紧固程序的金属产品对应力（载荷）的响应的方法。测试的目的是确定材料的承载强度，并测量承载应力与由垂直于表面刺穿板材的圆形横截面的销或杆产生的孔的变形。 |
| Torsional shaft vibration | 扭轴振动 |
The rapid back-and-forth angular twisting along a rotating unbalanced shaft which reaches maxima at critical rotation speeds. Shaft eccentricity, unbalanced mass distribution, oscillatory torque, misalignment, etc. all influence torsional vibration. 沿旋转不平衡轴的快速来回角扭转，在临界转速下达到最大值。轴偏心、质量分布不平衡、振荡扭矩、未对准等都会影响扭转振动。 |
| Full hard | 全硬化 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state beyond which the material can no longer be formed by bending. In specifications, a full hard temper is commonly defined in terms of minimum hardness or minimum tensile strength (or, alternatively, a range of hardness or strength) corresponding to a specific percentage of cold reduction following a full anneal. For aluminum, a full hard temper is equivalent to a reduction of 75% from dead soft ; for austenitic stainless steels, a reduction of about 50 to 55%. 有色金属合金和一些铁合金的回火状态，大致对应于冷加工状态，超过该状态，材料就不能再通过弯曲形成。在规范中，完全硬质回火通常定义为与完全退火后的特定冷压下率百分比相对应的最小硬度或最小抗拉强度（或者，硬度或强度范围）。对于铝来说，完全硬回火相当于从极软状态减少75%；对于奥氏体不锈钢，减少约50%至55%。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Atomizing humidifier | 雾化加湿器 |
A humidifier that functions by spraying fine droplets of water into an airstream. 一种加湿器，通过将细小的水滴喷射到气流中来发挥作用。 |
| Hooke’s law | 胡克定律 |
Within the limit of proportionality, the extension of a material is proportional to the applied force. Approximately, it is the relationship between stress and strain in an elastic material when it is stretched. The law states that the stress (force per unit area) is proportional to the strain (a change in dimensions). The law, which holds only approximately and over a limited range, was discovered in 1676 by Robert Hooke. 在比例极限内，材料的延伸与所施加的力成比例。近似地说，它是弹性材料拉伸时应力和应变之间的关系。该定律指出，应力（单位面积的力）与应变（尺寸变化）成比例。该定律仅适用于有限的范围，由罗伯特·胡克于1676年发现。 |
| Galilean transformation | 伽利略变换 |
In steady fluid flow, the addition or subtraction of a constant velocity to the entire flowfield, e.g. so that flow can be considered relative to a moving object or flow feature, such as a shock wave. 在稳定的流体流动中，对整个流场增加或减少恒定速度，例如，可以考虑相对于移动物体或流动特征（例如冲击波）流动。 |
| Olsen cup test | 奥尔森杯测试 |
A cupping test in which a piece of sheet metal, restrained except at the center, is deformed by a standard steel ball until fracture occurs. The height of the cup at time of fracture is a measure of the ductility. 一种杯突试验，其中一块金属板，除了中心以外，被一个标准钢球变形，直到发生断裂。断裂时杯的高度是延展性的量度。 |
| Static equilibrium | 静态平衡 |
A solid body, structure, or physical system (or any subdivided part) will be in static equilibrium, either at rest or moving with constant velocity, if the resultants of all external forces and moments acting on it are zero. 如果作用在固体上的所有外力和力矩的合力为零，则固体、结构或物理系统（或任何细分部分）无论是静止还是以恒定速度移动，都是处于静态平衡。 |
| Engineering strain (e) | 工程应变（e） |
A term sometimes used for average linear strain or conventional strain in order to differentiate it from true strain. In tension testing it is calculated by dividing the change in the gage length by the original gage length. 一个术语，有时用于平均线性应变或常规应变，以便将其与真实应变区分开来。在张力测试中，通过将标距变化除以原始标距来计算。 |
| Tensometer | 拉力计 |
A bench-top device, used to perform tension and compression tests. 用于进行拉伸和压缩试验的台式装置。 |
| Stability | 稳定性 |
1. A term relating to whether a body, structure, system, or flow is in a state of stable, unstable, or neutral equilibrium. 2. In numerical analysis, whether numerical errors, such as roundoff or input-data errors, are damped, propagate, or cause divergence of the solution as the numerical method proceeds. 3. A control system is often described as stable when a step change in input results in a steady output without continuing oscillation. 1.与物体、结构、系统或流是否处于稳定、不稳定或中性平衡状态有关的术语。2.在数值分析中，随着数值方法的进行，数值误差（如舍入误差或输入数据误差）是否衰减、传播或导致解发散。3.当输入的阶跃变化导致稳定输出而无持续振荡时，控制系统通常被描述为稳定的。 |
| Bearing strain | 轴承应变 |
The ratio of the deformation of the bearing hole, in the direction of the applied force, to the pin diameter in a bearing test. 轴承孔在作用力方向上的变形与轴承测试中销直径的比值。 |
| Fillet radius | 圆角半径 |
Concave junction at two intersecting surfaces of a fastener. Often used to describe the junction between the head and the shank of a threaded fastener (under head fillet). 在紧固件的两个相交表面处的凹形接合处。通常用于描述螺纹紧固件的头部和柄部之间的连接处（头部圆角下方）。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Pressure gauge | 压力表 |
An instrument used to measure absolute or gauge pressure. The sensing element may be a tube which deflects when pressurized, as in a Bourdon gauge, a bellows as in an aneroid barometer, a piezoelectric crystal, a piezoresistive element, etc. 测量绝对压力或表压的仪器。传感元件可以是加压时会偏转的管，如波登压力表、无液气压计中的波纹管、压电晶体、压阻元件等。 |
| Air-hardening steel | 空气硬化钢 |
A steel containing sufficient carbon and other alloying elements to harden fully during cooling in air or other gaseous mediums from a temperature above its transformation range. The terms should be restricted to steels that are capable of being hardened by cooling in air in fairly large sections, about 2 in. (50 mm) or more in diameter. Same as self-hardening steel. 一种钢，含有足够的碳和其他合金元素，可以在空气或其他气体介质中从高于其转变范围的温度冷却过程中完全硬化。这些术语应仅限于能够通过在相当大的截面（直径约2英寸（50毫米）或更大）中通过空气冷却而硬化的钢。与自硬钢相同。 |
| Dimensioning | 尺寸标注 |
The specification on an engineering drawing of the size (e.g. length, radius, angle, or spacing) and the relative location (e.g. angular position) of each feature of a component. The numerical values often include the tolerances. There should be no more dimensions than are necessary to manufacture the component. 工程图纸上对部件每个特征的尺寸（例如长度、半径、角度或间距）和相对位置（例如角位置）的规范。数值通常包括公差。尺寸不应超过制造组件所需的尺寸。 |
| Hardness profile | 硬度分布 |
Hardness as a function of distance from a fixed reference point (usually from the surface). 硬度作为距固定参考点（通常距表面）的距离的函数。 |
| Fracture strength | 断裂强度 |
(fracture stress) (Unit Pa) The stress at which a material breaks. It is not absolute for a given material, as it depends on the laws of fracture mechanics and is size-dependent. （断裂应力）（单位Pa）材料断裂时的应力。对于给定的材料，它不是绝对的，因为它取决于断裂力学定律，并且取决于尺寸。 |
| Compressor bleed | 压缩机排气 |
The removal of air before the final stage of a multistage compressor operating below design speed, to prevent the final stage from choking. 在低于设计速度运行的多级压缩机的末级之前去除空气，以防止末级阻塞。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Extra hard | 额外硬化 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about one-third of the way from full hard to extra spring temper. 有色合金和一些铁合金的回火，其特征是抗拉强度和硬度大约是从完全硬回火到额外弹簧回火的三分之一。 |
| Ductile | 延展性材料 |
(ductile material) Describes a material that can be deformed permanently to large strains without fracture. If a bolt can be stretched well past its yield point before breaking, it is said to be ductile. （延展性材料）描述一种可以永久变形到大应变而不断裂的材料。如果螺栓在断裂前可以很好地拉伸超过其屈服点，则称其具有延展性。 |
| Serrations | 锯齿 |
A row of notches or tooth-like projections on an edge or surface. On an engineering drawing, serrations on the surface of a circular component are shown over about 60° of arc. 边缘或表面上的一排凹口或齿状突起。在工程图纸上，圆形部件表面的锯齿超过约60°的圆弧。 |
| Captive nut | 松脱螺母 |
A nut attached loosely or rigidly to a sheet member that is too thin to thread and which engages with a cap screw. 松脱地或刚性地连接到薄板构件上的螺母，该螺母太薄而无法拧入，并与带帽螺钉接合。 |
| Monotron hardness test | 摩诺硬度试验 |
An obsolete method of determining indentation hardnessby measuring the load required to force a spherical penetrator into a metal to a specified depth. 一种已被淘汰的方法，通过测量将球形侵彻体压入金属至规定深度所需的载荷来确定压痕硬度。 |
| Balance weight | 平衡器 |
A corrective mass used in the static or dynamic balancing of a rotating object. 用于旋转物体的静态或动态平衡的校正质量。 |
| Plowing | 犁 |
In tribology, the formation of grooves by plastic deformation of the softer of two surfaces in relative motion. 在摩擦学中，通过相对运动的两个表面中较软的表面的塑性变形形成凹槽。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Mean diameter (Unit m) | 平均直径（单位米） |
The average of the inside and outside diameters for a helical spring or hollow circular cylinder or sphere 螺旋弹簧或空心圆柱体或球体的内径和外径的平均值 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Terminal temperature difference (Unit K) | 终端温差（单位K） |
The temperature difference between the two fluid streams at either inlet or outlet of a heat exchanger. 热交换器入口或出口处两种流体流之间的温差。 |
| Radial-flow compressor | 离心式压缩机 |
A compressor in which the working gas enters the machine axially and is compressed as it flows radially out through the impeller. 一种压缩机，其中工作气体轴向进入机器，并在通过叶轮径向流出时被压缩。 |
| Hot strength (Unit Pa) | 热强度（单位Pa） |
The yield stress (or sometimes fracture stress) of a material at temperatures above about half its melting point in kelvins. 材料在高于其熔点一半（以开尔文为单位）的温度下的屈服应力（有时为断裂应力）。 |
| Cavity radiator | 空腔辐射器 |
A heated chamber having a small hole through which radiation, approximating blackbody radiation, passes out. 具有小孔的加热室，近似于黑体辐射的辐射通过该小孔传递出去。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Torsion bar | 扭杆 |
A metal bar designed to act as an elastic spring when torque is applied. 当施加扭矩时用作弹性弹簧的金属棒。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| Shear strength | 抗剪强度 |
The maximum shear stress that a material is capable of sustaining. Shear strength is calculated from the maximum load during a shear or torsion test and is based on the original dimensions of the cross section of the specimen. 材料能够承受的最大剪切应力。抗剪强度根据剪切或扭转试验期间的最大载荷计算，并基于试样横截面的原始尺寸。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Crosshead | 十字头 |
1. A reciprocating member, sliding between guides, to which the piston rod is firmly attached on one side and to which the connecting rod is pinned on the other for the conversion of reciprocating into rotary motion. 2. The moveable beam in early designs of mechanical testing machines. 3. A screwhead having slots in a + shape that takes a mating screwdriver. 1.一种往复式构件，在导轨之间滑动，活塞杆一侧固定在其上，连杆另一侧固定在该构件上，用于将往复式运动转换为旋转运动。2.机械试验机早期设计中的活动梁。3.一种螺钉头，其具有采用配合螺丝刀的+形槽。 |
| Extensometer | 引伸计 |
An instrument for measuring changes in length over a given gage length caused by application or removal of a force. Commonly used in tension testing of metal specimens. Any instrument which measures the change in length of a part as the part is loaded. 一种用于测量在给定标距上由施加或移除力引起的长度变化，在零件加载时测量零件长度变化的仪器。常用于金属试样的拉力试验。 |
| Scleroscope hardness test | 反跃式硬度试验 |
A dynamic indentation-hardness test using a calibrated instrument that drops a diamond-tipped hammer from a fixed height onto the surface of the material being tested. The height of rebound of the hammer is a measure of the hardness of the material. Also known as Shore hardness test. 使用校准仪器的动态压痕硬度测试，该仪器将金刚石锤从固定高度落在被测材料表面上。锤的回弹高度是材料硬度的一种度量。也称为肖氏硬度测试。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Diffusion | 扩散 |
(1) Spreading of a constituent in a gas, liquid, or solid, tending to make the composition of all parts uniform. (2) The spontaneous movement of atoms or molecules to new sites within a material. （1） 一种成分在气体、液体或固体中的扩散，趋于使所有部分的成分均匀。（2） 原子或分子自发运动到材料内的新位置。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Cold extrusion | 冷挤压 |
In simplest terms, cold extrusion can be defined as the forcing of unheated metal to flow through a shape-forming die. It is a method of shaping metal by plastically deforming it under compression at room temperature while the metal is within a die cavity formed by the tools. The metal issues from the die in at least one direction with the desired cross-sectional contour, as permitted by the orifice created by the tools. Cold extrusion is always performed at a temperature well below the recrystallization temperature of the metal (about 1100 to 1300 degrees F. for steel) so that work-hardening always occurs. In hot extrusion, recrystallization eliminates the effects of work-hardening, unless rapid cooling of the extrusion prevents recrystallization from being completed. 用简单的术语来说，冷挤压可以定义为迫使未加热的金属流过成形模具。这是一种通过在室温下压缩使金属塑性变形来成形金属的方法，同时金属处于由工具形成的模腔中。金属至少在一个方向上从模具中流出，并具有所需的横截面轮廓，这是由工具产生的孔口所允许的。冷挤压总是在远低于金属再结晶温度的温度下进行（钢约1100至1300华氏度），因此总是发生加工硬化。在热挤压中，再结晶消除了加工硬化的影响，除非挤压的快速冷却阻止再结晶完成。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Torque multiplier | 扭矩放大器 |
A gearbox used to multiply the torque produced by a small hand wrench (usually a Torque wrench). The output of the multiplier drives the nut or bolt with a torque that is higher, and a speed that is lower, than input torque and speed. There is no torque gage or readout on the multiplier. 一种齿轮箱，用于增加小手动扳手（通常是扭矩扳手）产生的扭矩。倍增器的输出以比输入扭矩和速度更高的扭矩和更低的速度驱动螺母或螺栓。倍增器上没有扭矩计或读数。 |
| Case hardening | 表面硬化 |
A generic term covering several processes applicable to steel that change the chemical composition of the surface layer by absorption of carbon, nitrogen, or a mixture of the two and, by diffusion, create a concentration gradient. The processes commonly used are carburizing and quench hardening; cyaniding; nitriding; and carbonitriding. The use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于钢的几种工艺，这些工艺通过吸收碳、氮或二者的混合物改变表层的化学成分，并通过扩散形成浓度梯度。常用的工艺有渗碳和淬火硬化，氰化，氮化以及碳氮共渗。优选使用适用的特定工艺名称。 |
| Stove bolt | 炉用螺栓 |
This bolt has been so named because of its use in stove building. It is made in a number of different forms, either with a round button, or flat countersunk head, the head having a slot for a screwdriver and the threaded end being provided with a square or hexagon nut. 这种螺栓因其在炉灶建筑中的用途而得名。它有多种不同的形式，有圆形按钮或平沉头，头部有螺丝刀槽，螺纹端有方形或六角螺母。 |
| Wind energy (Unit kJ) | 风能（单位kJ） |
The kinetic energy associated with wind that can be converted by a wind energy conversion system (WECS) into electrical or mechanical power by a rotor, such as a multi-bladed propeller, exposed to the wind. If the air density is ρ and the wind speed is V, then the kinetic energy flux is ρV3/2. The actual wind power that can be extracted by a wind turbine intercepting a cross section of wind A is CPρAV3/2 where CP is an empirical efficiency factor termed the power coefficient. The wind-energy distribution is a histogram of the calculated wind power that can be generated annually from the windspeed frequency distribution at a given location. A windmill generates mechanical power whereas a wind turbine (wind generator) generates electrical power. The largest wind turbine, manufactured by MHI Vestas, has a power rating of 9.5 MW, a rotor diameter of 164 m, and a hub height of 105 m (the highest wind turbines have heights in the region of 190 m). A wind farm is an array of wind turbines, typically ten to several hundred, at a single location, either onshore or offshore. Energy derived from wind is a major contributor to sustainable energy generation. The largest operational offshore wind farm, located in the Irish Sea, has 87 turbines and a total generating capacity of 659 MW. The largest onshore wind farm is in Kern County, California with some 586 turbines and a total capacity of 1 550 MW. 风能转换系统（WECS）可通过暴露于风中的转子（如多叶片螺旋桨）将与风相关的动能转换为电能或机械能。如果空气密度为ρ，风速为V，则动能通量为ρV3/2。可由截获风a横截面的风力涡轮机提取的实际风功率为CPρAV3/2，其中CP是称为功率系数的经验效率因子。风能分布是根据给定位置处的风速频率分布每年可产生的计算风力的直方图。风车产生机械功率，而风力涡轮机（风力发电机）产生电功率。MHI Vestas制造的最大风力涡轮机的额定功率为9.5MW，转子直径为164m，轮毂高度为105m（最高风力涡轮机的高度为190m）。风电场是一系列风力涡轮机，通常为十到几百台，位于单一位置，无论是陆上还是海上。风能是可持续能源发电的主要贡献者。最大的海上风电场位于爱尔兰海，拥有87台涡轮机，总发电容量为659MW。最大的陆上风电场位于加利福尼亚州克恩县，拥有约586台涡轮机，总容量为1550兆瓦。 |
| Two-stage compressor | 两级压缩机 |
A machine in which gas is compressed from low pressure toan intermediate pressure in a low-pressure cylinder, and then to final pressure in a highpressure cylinder. Efficiency is improved if the two cylinders are separated by an intercooler. 一种机器，其中气体在低压气缸中从低压压缩到中压，然后在高压气缸中压缩到最终压力。如果两个气缸由中冷器分离，则效率提高。 |
| Valve plug | 阀塞 |
A conical or cylindrical plug, in which there are transverse holes, in a valve, such as a plug valve. Flow through the holes occurs when the plug is rotated. 阀门中的圆锥形或圆柱形阀塞，其中有横向孔，如旋塞阀。旋转阀塞时，会发生通过孔的流动 |
| Coefficient of rolling friction | 滚动摩擦系数 |
The ratio of force parallel to a surface, on which an object rolls, to the normal force. Unlike sliding friction, rolling friction depends on the size of the contact patch and the radius of the rolling element, and the behaviour depends on whether the contact is elastic, viscoelastic, or plastic and on hysteresis losses. 平行于物体滚动表面的力与法向力之比。与滑动摩擦不同，滚动摩擦取决于接触片的大小和滚动元件的半径，其行为取决于接触是弹性的、粘弹性的还是塑性的以及滞后损失。 |
| Knoop hardness test | 努氏硬度试验 |
An indentation-hardness test using calibrated machines to force a rhombic-based pyramidal diamond indenter having specified edge angles, under specified conditions, into the surface of the material under test and to measure the long diagonal after removal of the load. An indentation hardness test in which the indenter is an elongated diamond pyramid that gives an impression in the form of a parallelogram, in which the longer diagonal is about seven times the shorter. Used for studies of anisotropy in solid materials. 使用校准机器进行的一种压痕硬度试验，在规定条件下，将具有规定边缘角的菱形棱锥金刚石压头压入受试材料表面，并在移除荷载后测量长对角线。其中压头是一个细长的菱形棱锥，以平行四边形的形式给出压痕，其中较长的对角线约为较短的七倍。用于研究固体材料的各向异性。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Wedge | 楔子 |
A short triangular prism whose major surfaces subtend an acute angle, that can be driven between two objects or parts of an object to split, tighten, or secure them, or to widen an opening or raise a heavy object. The acute angle gives a high mechanical advantage. 一种短的三棱镜，其主面对着一个锐角，可在两个物体或物体的一部分之间驱动，以将它们分开、拧紧或固定，或加宽开口或举起重物。锐角具有很高的机械优势。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Condensate strainer | 冷凝水过滤器 |
A filter in a steam plant used to remove particulate matter from condensate before it is added to feedwater. 蒸汽设备中的过滤器，用于在将冷凝水添加到给水中之前去除冷凝水中的颗粒物。 |
| Decarburization | 脱碳 |
Loss of carbon from the surface layer of a carbon-containing alloy due to reaction with one or more chemical substances in a medium that contacts the surface. 由于与接触表面的介质中的一种或多种化学物质发生反应，含碳合金表面层的碳损失。 |
| Thread form | 螺纹形式 |
The cross-sectional shape of the threads, defining thread angle, root, and crest profiles, etc. Thread length Length of that portion of the fastener which contains threads cut or rolled to full depth. 螺纹的横截面形状，定义螺纹角度、齿根和齿冠轮廓等。螺纹长度：紧固件中包含全深度切割或轧制螺纹的部分的长度。 |
| Clearance hole | 间隙孔 |
A hole of specified size such that a bolt, stud, etc. of the same nominal size will always pass through. 指定尺寸的孔，使相同标称尺寸的螺栓、螺柱等可以通过。 |
| Densimeter | 密度计 |
An instrument used to determine the density or relative density of a solid or liquid. 用于测定固体或液体的密度或相对密度的仪器。 |
| Kiln | 窑 |
An industrial oven for burning, baking, or drying. 用于燃烧、烘烤或干燥的工业烤箱。 |
| Mechatronics | 机电一体化 |
The integration of mechanical engineering, electrical engineering, electronic engineering, and software engineering. 机械工程、电气工程、电子工程和软件工程的集成。 |
| Compression pressure (Unit Pa) | 压缩压力（单位Pa） |
The pressure produced in a cylinder of a piston engine by compression of air in the absence of fuel. 在没有燃料的情况下通过压缩空气在活塞发动机的气缸中产生的压力。 |
| Combined stresses | 复合应力 |
The stress state at a point in a component subjected to combination of axial, bending, torsional loadings etc., acting along all reference axes. 沿所有参考轴作用的受轴向、弯曲、扭转载荷等组合作用的部件中某点的应力状态。 |
| Stress-relaxation curve | 应力松弛曲线 |
A plot of the remaining, or relaxed, stress in a stress-relaxation test as a function of time. The relaxed stress equals the initial stress minus the remaining stress. Also known as a stress-time curve. 应力松弛试验中剩余应力或松弛应力随时间变化的曲线图。松弛应力等于初始应力减去剩余应力。也称为应力-时间曲线。 |
| Median fatigue strength at N cycles | N次循环的中位疲劳强度 |
An estimate of the stress level at which 50% of the population would survive N cycles. The estimate is derived from a particular point of the fatigue life distribution, because there is no test procedure by which a frequency distribution of fatigue strengths at Ncycles can be directly observed. 估计50%的量在N个周期内生存的压力水平。该估计值来自疲劳寿命分布的一个特定点，因为没有试验程序可以直接观察N次循环疲劳强度的频率分布。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Hydrogen-induced delayed cracking | 氢致延迟开裂 |
A term sometimes used to identify a form of hydrogen embrittlement in which a metal appears to fracture spontaneously under a steady stress less than the yield stress. There is usually a delay between the application of stress (or exposure of the stressed metal to hydrogen) and the onset of cracking. Also referred to as static fatigue. 有时用于识别一种氢脆形式的术语，其中金属在小于屈服应力的稳定应力下似乎会自发断裂。在施加应力（或将受应力金属暴露于氢）与开裂开始之间通常存在延迟。也称为静态疲劳。 |
| Dilatation (dilation) | 膨胀 |
A change of volume caused by external load, compression, temperature change, chemical action, etc. 由外部载荷、压缩、温度变化、化学作用等引起的体积变化。 |
| Oil-cooled | 油冷却 |
A term for a machine that uses circulating oil to remove heat. 使用循环油散热的机器的术语。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Fatigue failure | 疲劳失效 |
Failure that occurs when a specimen undergoing fatigue completely fractures into two parts or has softened or been otherwise significantly reduced in stiffness by thermal heating or cracking. 当经历疲劳的试样完全断裂成两部分或因热加热或开裂而软化或刚度显着降低时发生的失效。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Zone melting (zone refining) | 区域熔炼（区域精炼） |
A process of purification of materials in which a narrow molten zone is moved along the length of the material, resulting in impurities being segregated at one end. 一种净化材料的过程，其中一个狭窄的熔融区沿材料长度移动，导致杂质在一端分离。 |
| Rotary piston flow meter | 旋转活塞流量计 |
A rotary liquid flow meter in which a cylindrical rotor, eccentrically mounted within a cylindrical casing, the axes of the two cylinders being parallel, is caused to rotate by the liquid flow. The flow rate is determined from the number of rotations of the rotor in a given time. 一种旋转式液体流量计，其中偏心安装在圆柱形外壳内的圆柱形转子，两个圆柱体的轴线平行，由液体流引起旋转。流量由转子在给定时间内的转数确定。 |
| Isothermal annealing | 等温退火 |
Austenitizing a ferrous alloy and then cooling to and holding at a temperature at which austenite transforms to a relatively soft ferrite carbide aggregate. 将铁合金奥氏体化，然后冷却至奥氏体转变为相对软的铁素体碳化物集合体的温度并保持该温度。 |
| Yield point (Unit Pa) | 屈服点（单位Pa） |
The first stress in a material, usually less than the maximum attainable stress, at which an increase in strain occurs without an increase in stress. Only certain metals—those which exhibit a localized, heterogeneous type of transition from elastic to plastic deformation—produce a yield point. If there is a decrease in stress after yielding, a distinction may be made between upper and lower yield points. The load at which a sudden drop in the flow curve occurs is called the upper yield point. The constant load shown on the flow curve is the lower yield point. (yield strength, yield stress, Rel, Rel) The stress at which the onset of permanent (plastic) deformation (yielding) occurs in a body under increasing loading. In some materials, a yield-point phenomenon occurs in which stress falls on initial yielding and plastic deformation continues without increase in stress as strain increases further. The yield criterion is the combination of normal and shear stresses which produces yielding under multiaxial loading. 材料中的第一应力，通常小于可达到的最大应力，在该应力下应变增加而应力不增加。只有某些金属——表现出从弹性变形到塑性变形的局部、非均匀类型的金属——才会产生屈服点。如果屈服后应力降低，可区分上屈服点和下屈服点。流量曲线突然下降时的荷载称为上屈服点。流量曲线上显示的恒定载荷为较低屈服点。（屈服强度，屈服应力，Rel）在不断增加的载荷下，物体发生永久（塑性）变形（屈服）时的应力。在某些材料中，会出现屈服点现象，即应力在初始屈服时下降，随着应变进一步增加，塑性变形继续，而应力没有增加。屈服准则是在多轴载荷下产生屈服的正应力和剪应力的组合。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Slip band | 滑带 |
A group of parallel slip lines so closely spaced as to appear as a single line when observed under an optical microscope. 一组平行滑移线，间距如此之近，以至于在光学显微镜下观察时显示为一条直线。 |
| PSI (pounds per square inch) | PSI（磅/平方英寸） |
Pressure measurement. Psia (pounds per square inch absolute) measures actual pressure with no allowance for atmospheric pressure. Psig (pounds per square inch gauge) measures pressure with the gauge set to zero (0) at atmospheric pressure (14.7 psia). In other words psig = psia – 14.7. 压力测量。Psia（绝对磅/平方英寸）测量实际压力，不考虑大气压力。Psig（磅/平方英寸表压）在大气压（14.7 psia）下，将表压设置为零（0）时测量压力。换句话说，psig=psia–14.7。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| End-quench hardenability test | 端淬淬透性试验 |
A laboratory procedure for determining the hardenability of a steel or other ferrous alloy. Hardenability is determined by heating a standard specimen above the upper critical temperature, placing the hot specimen in a fixture so that a stream of cold water impinges on one end, and, after cooling to room temperature is completed, measuring the hardness near the surface of the specimen at regularly spaced intervals along its length. The data are normally plotted as hardness versus distance from the quenched end. 测定钢或其他铁合金淬透性的实验室程序。淬透性是通过将标准试样加热到高于上临界温度，将热试样放置在夹具中，使冷水流冲击一端，并在冷却至室温后，沿试样长度以规则间隔测量试样表面附近的硬度来确定的。数据通常绘制为硬度与距淬火端距离的关系。 |
| Normalizing | 正火 |
Heating a ferrous alloy to a suitable temperature above the transformation range and then cooling in air to a temperature substantially below the transformation range. 将铁合金加热至高于转变范围的合适温度，然后在空气中冷却至基本低于转变范围的温度。 |
| Starting valve (regulator) | 起动阀（调节器） |
A valve which admits steam from the boiler to the cylinder(s) of a steam engine. 将蒸汽从锅炉送入蒸汽机汽缸的阀门。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Thermal reactor | 热反应器 |
An enlarged exhaust manifold bolted directly to the cylinder head of a piston engine, in which the oxidation of carbon monoxide and unburned hydrocarbons in the exhaust gas is enhanced. 一种扩大的排气歧管，直接用螺栓固定在活塞式发动机的气缸盖上，其中一氧化碳和未燃烧碳氢化合物的氧化作用增强。 |
| Tensile test (tension test) | 拉伸试验（拉力试验） |
A test in which a precisely-machined tensile specimen (tensile testpiece), typically circular or rectangular in cross section with large end sections that are gripped in the testing machine, is subjected to an increasing tensile load, usually to the point of fracture, to produce a stress–strain curve from which such material properties as modulus of elasticity, limit of proportionality, proof stress, yield point, and ultimate tensile stress can be determined. The relevant standard is ISO 6892-1. 一种试验，在这种试验中，精密加工的拉伸试样（拉伸试件）的横截面通常为圆形或矩形，具有在试验机中夹紧的大端部，受到越来越大的拉伸载荷，通常达到断裂点，以产生应力-应变曲线，从中可以看出弹性模量、比例极限等材料特性，可以确定验证应力、屈服点和极限拉伸应力。相关标准为ISO 6892-1。 |
| Shrink fit | 过盈配合 |
A tight interference fit between two components resulting from heating an outer part and/or cooling an inner part to allow easy assembly. The outer component contracts on cooling, while the inner part expands on warming to ambient temperature, thus gripping the two parts together. 由于加热外部部件和/或冷却内部部件而导致的两个部件之间的紧密过盈配合，以便于组装。外部部件在冷却时收缩，而内部部件在加热到环境温度时膨胀，从而将两个部件夹在一起。 |
| Endurance | 耐力 |
The capacity of a material to withstand repeated application of stress. 材料承受反复施加应力的能力。 |
| Grub screw | 平头螺丝 |
A short headless screw with a recess at one end to receive a screw driver or key. 一种短的无头螺钉，一端有一个凹槽，用于安装螺丝刀或钥匙。 |
| Set screw | 紧定螺钉（平头螺钉、紧定螺栓） |
Usually a hardened steel screw having either no head or a square head and with various degrees of points or ends to lock or tighten adjustable machine parts in position on a shaft. A short, headless screw with a recess at one end to receive a screwdriver or key, the other end being pointed, square, or otherwise shaped. Typically used to secure a pulley, gear, or other component on a shaft. 通常是一种硬化钢螺钉，无头或方头，具有不同程度的点或端部，用于将可调机械部件锁定或拧紧在轴上的适当位置。一端有凹槽，用来装螺丝刀或钥匙，另一端是尖的、方形的或其他形状的。通常用于将皮带轮、齿轮或其他部件固定在轴上。 |
| Absolute zero | 绝对零度 |
Temperature of -273.16″C or 459.69″F or OK at which molecular motion vanishes and a body has no heat energy. 温度为-273.16″C或459.69″F，此时分子运动消失且物体没有热能。 |
| Fillister head | 槽头 |
Similar to a pan head but with a smaller head diameter and a taller head, with higher vertical sides. 类似于盘头，但头部直径较小，头部较高，垂直边较高。 |
| Impact wrench | 冲击扳手 |
An air- or electric-powered wrench in which multiple blows from tiny hammers are used to produce output torque to tighten fasteners. A pneumatically-or electrically-powered socket wrench used to tighten or loosen nuts through the application of torque in a rapid series of impulses. 一种气动或电动扳手，使用小锤子多次敲击来产生输出扭矩以拧紧紧固件，用于通过在一系列快速脉冲中施加扭矩来拧紧或松开螺母。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Stress-intensity factor | 应力强度因子 |
A scaling factor, usually denoted by the symbol K, used in linear-elastic fracture mechanics to describe the intensification of applied stress at the tip of a crack of known size and shape. At the onset of rapid crack propagation in any structure containing a crack, the factor is called the critical stress-intensity factor, or the fracture toughness. 一种标度因子，通常用符号K表示，在线弹性断裂力学中用于描述已知尺寸和形状的裂纹尖端施加应力的增强。在任何含有裂纹的结构中，裂纹快速扩展开始时，该因子称为临界应力强度因子，或断裂韧性。 |
| Slot | 狭槽 |
A groove machined into a component, e.g. to allow for thermal expansion, or in which the tongue or tip of another component can fit or slide. 在部件上加工的凹槽，例如，允许热膨胀，或另一部件的榫舌或尖端可在其中安装或滑动。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Fretting fatigue | 微动疲劳 |
Fatigue fracture that initiate at a surface area where fretting has occurred. The progressive damage to a solid surface that arises from fretting. 在发生微动的表面区域开始的疲劳断裂。由微动引起的对固体表面的渐进性损坏。 |
| Blowing | 吹气 |
The process by which a gas is transferred through a porous surface over which there is a gas flow. The effect is used to decrease skin friction and increase heat transfer, for example in turbine-blade cooling. 气体通过有气流的多孔表面转移的过程。该效应用于减少表面摩擦和增加传热，例如在涡轮叶片冷却的过程中。 |
| Blue annealing | 蓝色退火 |
Heating hot-rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental. 在开放式炉中将热轧铁板加热到转变范围内的温度，然后在空气中冷却，以软化金属。在表面上形成蓝色氧化物是偶然的。 |
| Specific weight (γ) (Unit N/m³) | 比重（γ）（单位：N/m³） |
The weight per unit volume of a substance: if W is the weight of a volume of the substance, ρ is its density, and g is the acceleration due to gravity, γ = W/ = ρg. 物质单位体积的重量：W是物质体积的重量，ρ是其密度，g是重力引起的加速度，γ=W/=ρg。 |
| Absolute value error | 绝对值误差 |
The magnitude of the error dlsregarding the algebraic sign, or, for a vectorial error, disregarding its function. 关于代数符号的误差幅度，或者，对于矢量误差，不考虑其函数。 |
| British Standards Institution (BSI) | 英国标准协会（BSI） |
The Institution in the UK responsible for the preparation and publication of standard specifications (British standards) for manufactured goods, their design, manufacture and testing. 负责为制成品及其设计、制造和测试制定和发布标准规范（英国标准）的英国机构。 |
| Milling | 铣削 |
A machining process, typically for metals and plastics, in which a multi-tooth rotary cutter removes material to produce flat or profiled surfaces, slots, grooves, etc. Milling is a machining process in which metal is removed by a rotating multiple-tooth cutter; each tooth removes a small amount of metal with each revolution of the spindle. Because both workpiece and cutter can be moved in more than one direction at the same time, surfaces having almost any orientation can be machined. 一种加工工艺，通常用于金属和塑料，其中多齿旋转刀具去除材料以产生平坦或异形表面、槽、槽等。金属由旋转多齿刀具去除；主轴每转一圈，每个齿都会去除少量金属。因为工件和刀具可以同时在多个方向上移动，所以几乎可以加工任何方向的表面。 |
| Artificial aging | 人工时效 |
Aging above room temperature. 在室温以上的时效。 |
| Altitude chamber | 高空舱 |
(hypobaric chamber) A chamber in which conditions at different altitudes are simulated by a combination of appropriate pressures, temperatures and relative humidity. （低压舱）通过适当的压力、温度和相对湿度的组合来模拟不同高度条件的舱室。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Collapse load (Unit N) | 毁坏荷载（单位N） |
The applied load at which a structure becomes a mechanism owing to the formation of sufficient plastic hinges for collapse to occur. 由于形成足够的塑性铰链以发生坍塌，结构成为机制的施加载荷。 |
| Clearance angle | 后角 |
(relief angle) (Unit °) The angle between the underneath or flank of a cutting tool and the machined surface. （后角）（单位°）切削刀具的底部或侧面与加工表面之间的角度。 |
| Scuffing | 擦伤 |
A form of adhesive wear that produces superficial scratches or a high polish on the rubbing surfaces. It is observed most often on inadequately lubricated parts. 粘着磨损的一种形式，在摩擦表面上产生表面划痕或高度抛光。通常在润滑不足的零件上观察到。 |
| International Bureau of Weights and Measures | 国际度量衡局IBWM |
(BIPM, Bureau International des Poids et Mesures) The intergovernmental organization which has the mandate to provide the basis for a single, coherent system of measurements, traceable to the International System of Units. （BIPM，国际计量局）政府间组织，其任务是为可追溯到国际单位制的单一、一致的计量系统提供基础。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Aging treatment | 时效处理 |
Heat treatment aimed at age hardening; it comprises solution and precipitation treatments. 针对时效硬化的热处理；它包括溶液和沉淀处理。 |
| Quimby screw pump | 昆比螺杆泵 |
A screw pump with two meshing screws, each having a righthand and a left-hand screw. Liquid enters at either end and is discharged from the middle. 带有两个啮合螺钉的螺杆泵，每个都有一个右旋螺纹和一个左旋螺纹。液体从两端进入，从中间排出。 |
| Salt bath heat treatment | 盐浴热处理 |
Heat treatment carried out in a bath of molten salt. 在熔融盐浴中进行的热处理。 |
| Impact strength 1. (Unit Pa) | 冲击强度1.（单位Pa） |
The stress to cause failure (by yielding or fracture) under conditions of high strain rate. 2. (Unit J) A term sometimes used to describe the energy required to fracture a specimen in a Charpy or Izod impact test even though the unit is not that of strength. 在高应变率条件下导致失效（通过屈服或断裂）的应力。2.（单位J）有时用于描述在夏比或悬臂梁式冲击试验中使样品断裂所需的能量，即使单位不是强度单位。 |
| Fastener standard | 紧固件标准 |
A document which details the attributes of a finished fastener and includes such characteristics as geometry, material or chemistry, heat treatment, finish, testing lot size, and packaging. 详细说明紧固件属性的文件，包括几何形状、材料或化学、热处理、表面处理、测试批量和包装等特性。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Damage | 损伤 |
1. The deterioration of a component or structure in fault or accident conditions, reducing or preventing its ability to perform its intended function. 2. The accumulation of defects or microcracks in the microstructure of a body loaded monotonically or in fatigue, which weakens the body and can lead to crack propagation and failure. 1.部件或结构在故障或事故条件下的劣化，降低或阻止其执行预期功能的能力。2.在承受单调载荷或疲劳载荷的物体的微观结构中累积的缺陷或微裂纹，这会削弱物体，并可能导致裂纹扩展和失效。 |
| Young’s modulus | 杨氏模量 |
A term used synonymously with modulus of elasticity. The ratio of tensile or compressive stresses to the resulting strain. 与弹性模量同义的术语。拉伸或压缩应力与产生应变的比率。 |
| Transfer ratio | 传输比 |
(transfer constant) A complex variable representing the ratio between the output of a transducer and the input causing that output. （传递常数）一个复变量，表示传感器输出与产生该输出的输入之间的比率。 |
| Clevis joint | U形接头 |
A joint formed by two parallel cantilever beams pressed upon a component between the beams. 由两个平行悬臂梁压在梁之间的部件上形成的接头。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Gibbs–Dalton law | 吉布斯-道尔顿定律 |
An extension of Dalton’s law of additive pressures to include the statement that the internal energy, enthalpy, and entropy of a mixture of gases are equal to the sum of the internal energies, enthalpies, and entropies the individual constituents would have if each existed alone at the same temperature and volume. Gibbs rule is that part of the law pertaining to entropy. 道尔顿附加压力定律的扩展，包括以下陈述：气体混合物的内能、焓和熵等于各个成分单独存在时的内能、焓和熵之和。相同的温度和体积。吉布斯定律是与熵有关的定律的一部分。 |
| Metre (m) | 米（m） |
The base unit of length in the SI system. It is equal to the distance travelled by light in vacuum in 1/299 792 458 seconds. SI系统中长度的基本单位。它等于光在真空中在1/299792458秒内传播的距离。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Horizontal batch furnace | 卧式间歇炉 |
A versatile batch-type furnace that can give light or deep case depths, and because the parts are not exposed to air, horizontal batch furnaces can give surfaces almost entirely free of oxides. 一种多功能间歇式炉，可以提供浅或深的外壳深度，并且由于零件不暴露在空气中，卧式间歇式炉可以使表面几乎完全没有氧化物。 |
| Zirconia-toughened alumina composites | 氧化锆增韧氧化铝复合材料 |
(ZTA composites) Ceramic composites based on aluminium oxide to which zirconium oxide is added, resulting in improved fracture toughness. （ZTA复合材料）基于氧化铝的陶瓷复合材料，其中添加了氧化锆，从而提高了断裂韧性。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Time quenching | 时间淬火 |
A term used to describe a quench in which the cooling rate of the part being quenched must be changed abruptly at some time during the cooling cycle. 用于描述淬火的术语，其中被淬火零件的冷却速率必须在冷却循环的某个时间突然改变。 |
| Mole (mol) | 摩尔（mol） |
The base unit of the amount of substance in the SI system. It was previously defined as the amount of substance of a system that contains as many elementary entities as there are atoms in 0.012 kg of carbon-12. From 20 May 2019 it has been defined as the amount of substance containing exactly 6.022 140 76 × 1023 elementary entities. SI国际单位制中物质量的基本单位。此前，它被定义为一个系统中的物质量，该系统包含的基本实体数量与0.012千克碳-12中的原子数量相同。从2019年5月20日起，它已被定义为包含6.02214076×1023个基本实体的物质量。 |
| Lathe | 车床 |
A machine tool in which work, gripped in the headstock, is rotated against the cutting tool to produce turned, bored, faced, or threaded components. 一种机床，其中夹持在主轴箱中的工件靠着切削工具旋转，以生产车削、钻孔、端面或螺纹部件。 |
| Gasket m-factor | 垫片m系数 |
For a gasketed joint of area A in which the clamping force is F, the factor m is defined by F ≥ mpA where p is the pressure that would separate the two halves of the joint and m > 1. 对于面积为A且夹紧力为F的垫片接头，系数m由F≥mpA定义，其中p是分离接头两半的压力，m>1。 |
| Austenite stabilization | 奥氏体稳定化 |
Decrease, in comparison to a continuous cooling, in the amount of martensite occurring from austenite when cooling is interrupted at a temperature between Ms and Mf. This can be explained by the relaxation of stresses induced in the austenite by martensite crystals occurring before the interruption. The relaxation, in turn, leads to the dislocation rearrangement and their interaction with martensite/austenite interfaces, which makes the interfaces immobile. 与连续冷却相比，当在Ms和Mf之间的温度中断冷却时，从奥氏体中产生的马氏体的量减少。这可以通过中断前发生的马氏体晶体在奥氏体中引起的应力松弛来解释。反过来，松弛导致位错重排及其与马氏体/奥氏体界面的相互作用，这使得界面无法移动。 |
| Uniform strain | 均匀应变 |
The strain occurring prior to the beginning of localization of strain (necking); the strain to maximum load in the tension test. 在应变局部化（颈缩）开始之前发生的应变；拉伸试验中最大载荷的应变。 |
| Hydraulics | 液压系统 |
The study of water flow in open channels (including canals, rivers, etc.), water-supply, drainage, and irrigation systems. 研究明渠（包括运河、河流等）、供水、排水和灌溉系统中的水流。 |
| Starting torque (Unit N.m) | 起动扭矩（单位：N.m） |
The torque developed by a motor at zero rotational speed in order to initiate rotation of the applied load. 电机在零转速下产生的扭矩，以启动所施加负载的旋转。 |
| Malleable cast iron | 可锻铸铁 |
A cast iron made by prolonged annealing of white cast iron in which decarburization or graphitization, or both, take place to eliminate some or all of the cementite. The graphite is in the form of temper carbon. If decarburization is the predominant reaction, the product will exhibit a light fracture surface, hence, “whiteheart malleable;” otherwise, the fracture surface will be dark, hence, “blackheart malleable.” Ferritic malleable has a predominantly ferritic matrix; pearlitic malleable may contain pearlitic, spheroidite or tempered martensite depending on heat treatment and desired hardness. 白口铸铁一种通过长时间退火制成的铸铁，脱碳，石墨化，或两者都发生，以消除部分或全部渗碳体。石墨是回火碳的形式。如果脱碳是主要反应，产品将呈现出较轻的断裂表面，“白心可锻”。否则，断裂表面将变暗，“黑心可锻”。铁素体可锻性材料主要为铁素体基体；根据热处理和所需硬度，珠光体可锻材料可能包含珠光体、球状体或回火马氏体。 |
| Rotary valve (rotating valve) | 旋转阀 |
A cylindrical or conical plug in which there is a transverse hole through which fluid can flow when the hole is aligned with the adjacent piping. 一种圆柱形或锥形塞，其中有一个横向孔，当该孔与相邻管道对齐时，流体可通过该孔流动。 |
| Stress-intensity calibration | 应力强度校准 |
A mathematical expression, based on empirical or analytical results, that relates the stress-intensity factor to load and crack length for a specific specimen planar geometry. Also known as Kcalibration. 基于经验或分析结果的数学表达式，该表达式将特定试样平面几何形状的应力强度因子与载荷和裂纹长度联系起来。也称为K校准。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Concurrent engineering | 并行工程 |
The integration of the procedures for product design, material selection and manufacturing method to include life-cycle analysis. 产品设计、材料选择和制造方法程序的整合，包括生命周期分析。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Testing machine (load-measuring type) | 试验机（负载测量型） |
A mechanical device for applying a load (force) to a specimen. 向试样施加载荷（力）的机械装置。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| Plug | 螺塞 |
1. An object, usually tapered, used to block a hole to prevent fluid from escaping or flowing. 2. The central moveable part of a valve. 3. In the flow of a yield-stress fluid through a pipe or duct, the central region is often assumed to take the form of a plug with uniform axial velocity. 4. In thermoforming, a shaping tool that forces a heated plastic sheet into a female mould. 1.一种物体，通常为锥形，用于堵塞孔以防止流体逸出或流动。2.阀门的中心可移动部分。3.在屈服应力流体通过管道或管道的流动中，中心区域通常假定为具有均匀轴向速度的塞子形式。4.在热成型技术中，一种成型工具，将加热的塑料板压入阴模中。 |
| Creep modulus (Unit Pa) | 蠕变模量（单位Pa） |
The ratio of stress/strain at a chosen strain level obtained from creep tests, often plotted against time to show changes in stiffness. 从蠕变测试中获得的选定应变水平下的应力/应变比，通常随时间绘制以显示刚度的变化。 |
| Air classifier | 空气分级机 |
(air elutriator) A device in which an airstream, which may be swirling, sorts particles by a combination of size, shape, and mass. （空气淘析器）一种装置，在该装置中，气流（可能是漩涡）根据大小、形状和质量的组合对颗粒进行分类。 |
| Hot hardness | 热硬度 |
The hardness of materials at high temperatures, often used to rank the performance of cutting tools. 材料在高温下的硬度，常用来对刀具的性能进行排名。 |
| Roughness | 粗糙度 |
The deviations from the wavy surface itself, caused by geometry of the cutting tool and its wear, machining conditions, microstructure of the workpiece, vibrations in the system, and so on. Surface roughness changes as a surface goes through the wearing-in process, but may then stabilize. 由刀具的几何形状及其磨损、加工条件、工件的微观结构、系统中的振动等引起的与波状表面本身的偏差。表面粗糙度随着表面经过磨合过程而变化，但随后可能会稳定下来。 |
| Critical diameter | 临界直径 |
(D) Diameter of the bar that can be fully hardened with 50% martensite at its center. （D）中心有50%马氏体可完全硬化的棒材直径。 |
| Ultrasonic extensometer | 超声波伸长计 |
An electronic instrument which measures the change in length of a fastener ultrasonically as, or before and after, the fastener is tightened. 一种电子仪器，可在紧固件拧紧时或前后通过超声波测量紧固件长度的变化。 |
| Spring clip | 弹簧夹 |
A clip made of a material such as spring steel which grips an inserted part. 由弹簧钢等材料制成的夹子，用于夹住插入的零件。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Millimetre of water | 毫米水柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of water 1 mm high. Approximately equal to 9.81 Pa. 一种非SI压力单位，等于1毫米高的垂直水柱施加的压力。大约等于9.81Pa。 |
| Workspace (Unit m³) | 工作空间（单位m³） |
(working-space volume) The volume around the base frame of a robot, defined by the reach of the robot. The robot can thus only perform tasks within this volume. （工作空间体积）机器人基架周围的体积，由机器人的可达范围定义。因此，机器人只能执行该体积内的任务。 |
| Acid rain | 酸雨 |
Any form of precipitation, including rain, snow, sleet, fog, dew, and particulates, which contains higher than normal levels of sulfuric and nitric acids. These acids result from natural and man-made emissions of sulfur dioxide and oxides of nitrogen, respectively. Acid soot consists of unburned carbon particles, typically larger than 10 μm, in the atmosphere contaminated with sulfuric acid. The particles result from poor combustion of fossil fuels. 任何形式的降水，包括雨、雪、雨夹雪、雾、露水和颗粒物，其中含有高于正常水平的硫酸和硝酸。这些酸分别来自二氧化硫和氮氧化物的自然排放和人为排放。酸烟灰由未燃烧的碳颗粒组成，通常大于10微米，在被硫酸污染的大气中。这些颗粒是化石燃料燃烧不良造成的。 |
| Radial flow | 径向流 |
radial flow Fluid flow for which the principal direction of flow is either radially inward or radially outward relative to an axial direction. 径向流动流体流动的主要方向是径向向内或径向向外流动。 |
| Remaining stress | 残留应力 |
The stress remaining at a given time during a stress-relaxation test. See also stress relaxation. 在应力松弛试验期间在给定时间内剩余的应力。参见压力松弛。 |
| Vacuum relief valve | 真空安全阀 |
A valve that admits gas to a system under vacuum, should the degree of vacuum become excessive. 如果真空度过高，允许气体在真空下进入系统的阀门。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Ablation cooling | 烧蚀冷却 |
The cooling of a surface exposed to very high external gas temperature which causes the surface material to sublime, melt or decompose. The chemical process absorbs heat while the mass flow of material away from the surface blocks the heat flux from the hot gas. 冷却暴露于非常高的外部气体温度的表面，导致表面材料升华、熔化或分解。化学过程吸收热量，而远离表面的物质的质量流阻挡了来自热气体的热通量。 |
| Turbomachine | 涡轮机械 |
(rotodynamic machine) A machine in which there is a transfer of energy between a continuous stream of fluid and a component, called a rotor, rotating about a fixed axis. Fans and turbines (gas, hydraulic, steam, or wind) are turbomachines in which energy is transferred to the rotor, causing it to rotate. Pumps and compressors are turbomachines in which energy is transferred from the externally driven rotor to the fluid. （旋转动力机器）在连续的流体流和绕固定轴旋转的部件（称为转子）之间进行能量传递的机器。风扇和涡轮机（燃气、液压、蒸汽或风力）是涡轮机械，其中能量传递到转子，使其旋转。泵和压缩机是涡轮机械，其中能量从外部驱动的转子传递到流体。 |
| Percent error | 误差百分比 |
For testing machines, the ratio, expressed as a percentage, of the error to the correct value of the applied load. 对于试验机，以百分比表示的误差与所施加载荷的正确值之比。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Heat tinting | 热着色 |
Coloration of a metal surface through oxidation by heating to reveal details of the microstructure. 通过加热氧化使金属表面着色，以揭示微观结构的细节。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Aspect ratio | 纵横比 |
The ratio of the longest to the shortest dimension of a shape or object e.g. the chord-to-thickness ratio of an aerofoil or the span-to-chord ratio of a wing. 形状或物体的最长与最短尺寸之比，例如机翼的弦厚比或机翼的翼展弦比。 |
| Lock nut | 锁紧螺母 |
A type of nut that is prevented from loosening under vibration. The locking action is accomplished by squeezing, gripping or jamming against the bolt threads. A nut which provides extra resistance to vibration loosening (beyond that produced by proper Preload ), either by providing some form of Prevailing torque, or, in free-spinning lock nuts, by deforming, cramping, or biting into mating parts when fully tightened. 1. A thin auxiliary nut tightened against another nut to prevent loosening. 2. A single nut with special features that prevent loosening. 一种在振动下防止松动的螺母。锁定动作通过挤压、夹紧或卡住螺栓螺纹来完成。通过提供某种形式的主要扭矩，或在自由旋转锁紧螺母中，通过完全拧紧时变形、夹紧或咬入配合零件，提供额外的抗振动松动能力（超出适当预载产生的能力）。1.一个薄的辅助螺母，拧紧到另一个螺母上以防止松动。2.具有防止松动的特殊功能的单个螺母。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Atmosphere | 大气 |
1. (atm) An obsolete (non-SI) unit of pressure equal to 101 325 Pa or 1.013 25 bar and approximately equal to the atmospheric pressure (barometric pressure) measured at mean sea level. 1.（atm）一种已被淘汰的（非SI）压力单位，等于101325Pa或1.01325bar，大约等于在平均海平面测量的大气压力（大气压）。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Nut splitter | 螺母分离器 |
A tool for removing rusted-on and corroded nuts from bolts. It consists of a stiff steel ring that is placed around the nut. A screw thread passing through the ring bears diametrically on a wedged-shape tip that indents and cuts though a face of the nut. 从螺栓上去除锈蚀螺母的工具。它由一个围绕螺母放置的刚性钢环组成。穿过环的螺纹径向支撑在楔形尖端上，该尖端凹陷并穿过螺母的表面。 |
| Impact loads | 冲击载荷 |
Especially severe shock loads such as those caused by instantaneous arrest of a falling mass, shock meeting of two parts (in a mechanical hammer, for example), or by explosive impact, in which there can be an exceptionally rapid build-up of stress. 特别严重的冲击载荷，例如由下落质量的瞬时停止、两部分的冲击碰撞（例如在机械锤中）或爆炸性冲击引起的冲击载荷，其中可能会出现异常快速的应力积聚。 |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Centre of pressure | 压力中心 |
1. The location, on an aerofoil or other body that develops lift, of the resultant lift force. 2. The location, on a surface submerged in a liquid, of the resultant force due to the pressure acting on the surface. Because hydrostatic pressure increases with depth, the centre of pressure is generally below the centroid of the surface. 1.在产生升力的机翼或其他物体上，合成升力的位置。2.在浸没在液体中的表面上，由于作用在表面上的压力而产生的合力的位置。由于静水压力随深度增加，压力中心通常低于表面质心。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Minimum stress (Smin) | 最小应力（Smin） |
In fatigue, the stress having the lowest algebraic value in the cycle, tensile stress being considered positive and compressive stress negative. 在疲劳中，循环中代数值最低的应力，拉应力被视为正应力，压应力为负应力。 |
| Pressure storage tank | 压力贮存器 |
(pressure vessel) A closed container for storing gases or volatile liquids, such as liquefied gases, at pressures significantly above atmospheric pressure. Such tanks are commonly cylindrical with domed ends, spherical, spheroidal, torispherical or hemispherical. （压力容器）密闭容器：在大气压以上的压力下储存气体或挥发性液体，如液化气体的密闭容器。此类贮存器通常为圆柱形，具有半球形端部、球形、球面或半球形。 |
| Spring temper | 弹簧回火 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about two-thirds of the way from full hard to extra spring temper. 非铁合金和一些铁合金的一种回火，其特点是抗拉强度和硬度约为全硬回火到超弹性回火的三分之二。 |
| Dead centre | 止点 |
The point at which, in a crank mechanism, the piston connecting rod and crank are all in line so that there can be no driving moment. 在曲柄机构中，活塞连杆和曲柄都在一条线上，因此不会有驱动力矩。 |
| Fit | 装配 |
The general term used to signify the range of tightness which may result from the application of a specific combination of allowances and tolerances in the design of mating parts. 通用术语，用于表示配合零件设计中公差和公差的特定组合可能导致的紧密性范围。 |
| Surface tension (σ, γ) (Unit N/m) | 表面张力（σ，γ）（单位：N/m） |
At the interface between a liquid and a gas or two immiscible liquids, unbalanced cohesive forces acting on the liquid molecules at the interface lead to the property surface tension which causes tensile forces to develop as if it were a skin or membrane. 液体和气体或两种不混溶液体之间的界面处，作用在界面处的液体分子上的不平衡内聚力导致表面张力的性质，从而导致张力的发展，就像皮肤或薄膜一样。 |
| Annealing | 退火 |
A generic term denoting a treatment, consisting of heating to and holding at a suitable temperature followed by cooling at a suitable rate, used primarily to soften metallic materials, but also to simultaneously produce desired changes in other properties or in microstructure. 一个通用术语，表示一种处理，包括加热并保持在合适的温度，然后以合适的速率冷却，主要用于软化金属材料，但也同时产生其他性能或微观结构的所需变化。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| System engineering | 系统工程 |
A methodology which integrates all disciplines and specialty groups into a team effort, forming a structured development process that proceeds from concept to production to operation. 一种将所有学科和专业组整合到团队工作中的方法，形成从概念到生产再到运营的结构化开发过程。 |
| Ferritizing anneal | 铁素体化退火 |
A treatment given as-cast gray or ductile (nodular) iron to produce an essentially ferritic matrix. For the term to be meaningful, the final microstructure desired or the time-temperature cycle used must be specified. 给予铸态灰铁或球墨铸铁以产生基本铁素体基体的处理。为了使该术语有意义，必须指定所需的最终微观结构或使用的时间-温度循环。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Ausforming | 形变热处理 |
Thermomechanical treatment of steel in the metastable austenitic condition below the recrystallization temperature followed by quenching to obtain martensite and/or bainite. 在低于再结晶温度的亚稳态奥氏体条件下对钢进行热机械处理，然后淬火以获得马氏体和/或贝氏体。 |
| Slip | 滑落 |
Plastic deformation by the irreversible shear displacement (translation)of one part of a crystal relative to another in a definite crystallographic direction and usually on a specific crystallographic plane. Sometimes called glide. 晶体的一部分在一定的晶体学方向上相对于另一部分的不可逆剪切位移（平移）引起的塑性变形，通常在特定的晶体主义平面上。有时被称为滑翔。 |
| Screw pair | 螺旋副 |
Two links connected together to form a kinematic pair, in which the contacting surfaces are screw threads, so that their relative motion consists of rotation and sliding. 两个连杆连接在一起形成运动副，其中接触面为螺纹，因此它们的相对运动包括旋转和滑动。 |
| Hot working | 热加工 |
Plastic deformation of a metal, by rolling, drawing, forging, etc., at a temperature above its recrystallization temperature (in commercial alloys above about 40% of their melting points in kelvins) which results in permanent shape change but no increase in strength or loss of ductility. 金属通过轧制、拉拔、锻造等在高于其再结晶温度（在商业合金中高于其熔点的40%的开尔文）的温度下发生塑性变形，导致永久的形状变化，但不会增加强度或失去延展性。 |
| Coextrusion | 复合挤压 |
The simultaneous extrusion through the same die of two or more materials in combination. 通过同一模具同时挤出两种或多种材料的组合。 |
| Kilo (k) | 千（k） |
An SI unit prefix indicating a multiplier of 103; thus kilometre (km) is a unit of length equal to one thousand metres. 表示乘法器103的SI单位前缀；1千米是长度单位，等于1000米。 |
| Biomechanics | 生物力学 |
The application of mechanical-engineering principles, including thermodynamics, fluid mechanics, and solid mechanics together with materials engineering, to biological systems. 机械工程原理（包括热力学、流体力学和固体力学以及材料工程）在生物系统中的应用。 |
| Material velocity | 材料速度 |
The velocity of sound in a body (e.g., a bolt). A term used in the ultrasonic measurement of bolt stress or strain. 声音在物体（例如螺栓）中的速度。用于螺栓应力或应变的超声波测量的术语。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Oxidized surface (on steel) | 氧化表面（在钢上） |
Surface having a thin, tightly adhering, oxidized skin (from straw to blue in color), extending in from the edge of a coil or sheet. Sometimes called annealing border. 表面具有薄的、紧密粘附的氧化皮（从稻草色到蓝色），从线圈或薄片的边缘延伸。有时称为退火边界。 |
| Notch brittleness | 缺口脆性 |
Susceptibility of a material to brittle fractureat points of stress concentration. For example, in a notch tensile test, the material is said to be notch brittle if the notch strengthis less than the tensile strength of an unnotched specimen. Otherwise, it is said to be notch ductile. 材料在应力集中点易发生脆性断裂。例如，在缺口拉伸试验中，如果缺口强度小于无缺口试样的抗拉强度，则称材料为缺口脆性材料。否则，称其为缺口韧性。 |
| Low-E coating | 低辐射涂层 |
(low-emittance coating) A thin metallic or metal-oxide coating on a glass sheet to absorb and reflect infrared radiation. The coating is applied either by a pyrolytic chemical vapour-deposition process (hard coat), or by sputtering (soft coat). （低辐射涂层）玻璃板上的薄金属或金属氧化物涂层，用于吸收和反射红外辐射。通过热解化学气相沉积工艺（硬涂层）或溅射（软涂层）施加涂层。 |
| Square thread | 方螺纹 |
A form of screw thread in which the cross–section of the thread forms a square, making the width of the thread equal to the space between the threads. 螺纹的一种形式，螺纹的横截面形成正方形，使螺纹的宽度等于螺纹之间的间距。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Fracture surface | 断裂面 |
The irregular surface produced when a piece of metal is broken. 一块金属破碎时产生的不规则表面。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Computational domain | 计算域 |
In CFD, FEM, and other numerical methods, the area or volume within which calculations are performed and on the periphery of which the boundary conditions are specified. 在CFD、FEM和其他数值方法中，执行计算的区域或体积以及在其外围指定边界条件的区域或体积。 |
| Ratchet coupling | 棘轮联轴器 |
A joint employing a ratchet system between two shafts, so that not only does the driven shaft run in one direction only, but also the driven shaft can, if necessary, run more quickly than the driving shaft. 在两个轴之间采用棘轮系统的接头，这样不仅从动轴只能在一个方向上运行，而且在必要时，从动轴可以比驱动轴运行得更快。 |
| Thread grinding | 螺纹磨削 |
A method for producing or finishing very precise screw threads using a profiled grinding wheel. 一种使用异形砂轮生产或精加工非常精密螺纹的方法。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Cold die quenching | 冷模淬火 |
A quench utilizing cold, flat, or shaped dies to extract heat from a part. Cold die quenching is slow, expensive, and is limited to smaller parts with large surface areas. 利用冷、平或成型模具从零件中提取热量的淬火。冷模淬火速度慢、成本高，并且仅限于表面积较大的较小零件。 |
| Chain | 链 |
A series of connected links, typically of steel. For lifting, pulling, securing, etc., each link is a closed loop, often in the form of a ring. For power transmission, the links are designed to mesh with the teeth of a sprocket wheel. In contrast to belt drives, chain drives tend to be employed in high-torque applications. 一系列连接的链接，通常是钢制的。对于提升、拉动、固定等，每个链节都是一个闭合环，通常呈环形。对于动力传输，链节设计为与链轮的齿啮合。与皮带传动相比，链传动往往用于高扭矩应用。 |
| Constant-force spring | 恒力弹簧 |
A spring that has the same restoring force regardless of displacement. The most common type takes the form of a coiled strip that, owing to tight coiling during manufacture, is pre-stressed (a steel measuring tape is an example). The uncoiling force is approximately constant as the change of curvature of the strip is approximately constant. Not to be confused with a clockwork spring from which power can be obtained. 无论位移如何，具有相同恢复力的弹簧。最常见的类型是卷绕带，由于制造过程中的紧密卷绕，该卷绕带是预应力的（钢卷尺就是一个例子）。随着带材曲率的变化近似恒定，开卷力近似恒定。不要与可获得动力的发条弹簧混淆。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Torsional stress | 扭转应力 |
The shear stress on a transverse cross section resulting from a twisting action. 扭转作用在横截面上产生的剪切应力。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Crack-growth rate | 裂纹增长速度 |
Rate of propagation of a crack through a material due to statically or dynamically applied load. 由于静态或动态施加的载荷，裂纹在材料中的扩展速率。 |
| Seal | 密封件 |
A component which controls or prevents leakage of fluids into or out of parts of a machine. 控制或防止流体流入或流出机器部件的部件。 |
| Crankshaft | 曲轴 |
The main shaft, of which the cranks are a part, of a reciprocating single-or multi-cylinder machine. Crankshafts may be built up in sections or forged as a single component. In an engine, the reciprocating motion of the pistons transmits power to the crankshaft and causes it to rotate, whereas in a pump the crankshaft is driven and its rotation causes the pistons to reciprocate. 曲柄是往复式单缸或多缸机器主轴的一部分。曲轴可以分段组装或作为单个部件锻造。在发动机中，活塞的往复运动将动力传递给曲轴并使其旋转，而在泵中，曲轴被驱动，其旋转使活塞往复运动。 |
| Critical strain | 临界应变 |
The strain just sufficient to cause recrystallization; because the strain is small, usually only a few percent, recrystallization takes place from only a few nuclei, which produces a recrystallized structure consisting of very large grains. 刚好足以引起再结晶的应变；由于应变很小，通常只有百分之几，再结晶只发生在少数核上，从而产生由非常大的晶粒组成的再结晶结构。 |
| Grip length | 夹紧长度 |
Combined thickness of all the things clamped together by the bolt and nut, including washers, gaskets, and joint members. 由螺栓和螺母夹紧在一起的所有部件的总厚度，包括垫圈、垫圈和接头构件。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Bar | 巴（气压单位） |
A widely used (non-SI) unit of pressure approximately equal to normal atmospheric pressure at sea level. The conversion to SI is 1 bar = 105 Pa. Unit of pressure – the pressure created by a column of€mercury 75.006 cm high at 0ºC, or about 33.45 feet of water at 4ºC. It is equal to 105 pascal. Standard atmospheric pressure (at sea level) is 1.01325 bar, or 1013.25 mb. 一种广泛使用的（非SI）压力单位，大约等于海平面上的正常大气压。转换为SI为1bar=105Pa。压力单位——0ºC时75.006厘米高的水银柱或4ºC时约33.45英尺水柱产生的压力。它等于105帕斯卡。标准大气压（海平面）为1.01325bar或1013.25mb。 |
| Alpha iron | 阿尔法铁 |
The body-centered cubic form of pure iron, stable below 910 °C (1670 °F). 纯铁的体心立方形式，在910°C(1670°F)以下稳定。 |
| Stress-concentration factor (Kt) | 应力集中系数（Kt） |
A multiplying factor for applied stress that allows for the presence of a structural discontinuity such as a notch or hole; Kt equals the ratio of the greatest stress in the region of the discontinuity to the nominal stress for the entire section. Also known as theoretical stress-concentration factor. 施加应力的倍增系数，允许存在结构不连续性，如缺口或孔；Kt等于不连续区域的最大应力与整个截面的标称应力之比。也称为理论应力集中系数。 |
| Weld penetration | 焊接熔深 |
It is the depth below the surfaces, as revealed in microstructural sections of joined metals, which is melted during welding. 它是焊接过程中熔化的连接金属的微观结构截面所显示的表面以下的深度。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Base metal hardness | 母材硬度 |
Hardness closest to the surface (when traversing from core to outside diameter) just before an increase or decrease occurs, denoting, respectively, carburization or decarburization. 在发生增加或减少之前最接近表面的硬度（从芯部到外径时），分别表示渗碳或脱碳。 |
| Bolt gage | 螺栓量规 |
An ultrasonic instrument used to measure the stress or strain in bolts. 用于测量螺栓应力或应变的超声波仪器。 |
| Compressed liquid | 压缩液体 |
A liquid subjected to a pressure greater than the saturation pressure corresponding to its temperature. 承受大于与其温度对应的饱和压力的压力的液体。 |
| Thermoelectric material | 热电材料 |
A material in which any of the thermoelectric phenomena, such as the Peltier, Seebeck, and Thomson effects, are especially strong. 一种热电现象特别强烈的材料，如珀尔帖效应、塞贝克效应和汤姆森效应。 |
| Granular fracture | 粒状断裂 |
A type of irregular surface produced when metal is broken that is characterized by a rough, grainlike appearance, rather than a smooth or fibrous one. It can be subclassified as transgranular or intergranular. 金属破碎时产生的一种不规则表面，其特征是粗糙的颗粒状外观，而不是光滑或纤维状的外观。它可以细分为穿晶或晶间。 |
| Sharp-notch strength | 锐缺口强度 |
The notch tensile strength measured using specimens with very small notch root radii (approaching the limit for machining capability); values of sharp-notch strength usually depend on notch root radius. 使用缺口根部半径非常小（接近加工能力极限）的试样测量的缺口抗拉强度；锐缺口强度值通常取决于缺口根部半径。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| Dead space | 死区 |
(dead volume) (Unit m³) That volume of a gas-filled thermometer in which the gas is not at the same temperature as that being measured. （死容）（单位m³）充气温度计的体积，其中气体的温度与被测温度不同。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Blue brittleness | 蓝色脆性 |
Anomalous loss of ductility when quenched steels are tempered in the range 250–350°C (temperatures that produce blue tints on the surface of components). Brittleness exhibited by some steels after being heated to some temperature within the range of about 205 to 370 °C (400 to 700 °F), particularly if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. 当淬火钢在250–350°C范围内回火（在部件表面产生蓝色色调的温度）时，延展性异常损失。某些钢在加热到约205至370°C（400至700°F）范围内的某个温度后表现出脆性，特别是在高温下加工钢时。镇静钢几乎没有这种脆性。 |
| Hardenability | 淬透性 |
Defined as the ability of a ferrous material to acquire hardness after austenitization and quenching. The relative ability of a ferrous alloy to form martensite when quenched from a temperature above the upper critical temperature. Hardenability is commonly measured as the distance below a quenched surface where the metal exhibits a specific hardness (50 HRC, for example) or a specific percentage of martensite in the microstructure. 定义为黑色金属材料在奥氏体化和淬火后获得硬度的能力。铁合金从高于上临界温度的温度淬火时形成马氏体的相对能力。淬透性通常以淬火表面下方的距离来测量，金属在淬火表面处表现出特定硬度（例如50HRC）或微观结构中马氏体的特定百分比。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Octane number | 辛烷值 |
(octane rating) A measure of the anti-knock properties of a fuel taken as the percentage by volume of iso-octane in the fuel. （辛烷值）以燃料中异辛烷的体积百分比表示的燃料抗爆性能的量度。 |
| Millimetre of mercury | 毫米汞柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of mercury 1 mm high. Approximately equal to 133.3 Pa or 1 torr. 一种非SI压力单位，等于1毫米高的垂直水银柱施加的压力。大约等于133.3Pa或1托。 |
| Breaks | 断裂 |
Creases or ridges usually in “untempered” or in aged material where the yield point has been exceeded. Depending on the origin of the break, it may be termed a cross break, a coil break, an edge break, or a sticker break. 通常在“未回火”或超过屈服点的老化材料中出现折痕或隆起。根据断裂的起源，它可能被称为交叉断裂、线圈断裂、边缘断裂或贴纸断裂。 |
| Strain rate | 应变率 |
The time rate of straining for the usual tensile test. Strain as measured directly on the specimen gage length is used for determining strain rate. Because strain is dimensionless, the units of strain rate are reciprocal time. 通常拉伸试验的应变时间速率。直接在试样标距上测量的应变用于确定应变率。因为应变是无因次的，所以应变率的单位是倒数时间。 |
| Shoulder screw | 轴肩螺钉 |
A screw having two or more diameters or shoulders and commonly used for supporting levers and other machine parts that have to operate freely. 一种具有两个或两个以上直径或轴肩的螺钉，通常用于支撑杠杆和其他必须自由操作的机器部件。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Charles law/Charles' law | 查尔斯定律 |
(Gay–Lussac law) The volume of a fixed mass of gas at constant pressure is proportional to its absolute temperature. The volume of a gas at constant pressure is directly proportional to its absolute temperature. （盖-吕萨克定律）在恒定压力下，固定质量气体的体积与其绝对温度成正比。恒压下气体的体积与其绝对温度成正比。 |
| Absolute humidity | 绝对湿度 |
The weight of water vapor in a gadwater vapor mixture per unit volume of space occupied, expressed, for example, in grains or pounds per cubic foot. 单位体积空间占用的水蒸气混合物中水蒸气的重量，例如，以谷物或磅/立方英尺表示。 |
| Absorption hygrometer | 吸收式湿度计 |
An instrument that determines the content of water vapour in the atmosphere by it being absorbed into a hygroscopic medium. 通过吸收到吸湿介质中来确定大气中水蒸气含量的仪器。 |
| Diaphragm compressor | 隔膜式压缩机 |
A machine in which compression is achieved by the reciprocating motion of a flexible membrane of metal, plastic, or elastomeric material. This arrangement is ideally suited to pumping high-purity, toxic, or explosive gases. A similar machine incorporating check valves is a self-priming positive-displacement pump (diaphragm pump, membrane pump). 通过金属、塑料或弹性材料的柔性薄膜的往复运动实现压缩的机器。这种布置非常适合泵送高纯度、有毒或爆炸性气体。装有止回阀的类似机器是自吸容积泵（隔膜泵、隔膜泵）。 |
| Stress-strain diagram | 应力-应变图 |
A graph in which corresponding values of stress and strain are plotted against each other. Values of stress are usually plotted vertically(ordinates or y-axis) and values of strain horizontally (abscissas or xaxis). Also known as deformation curve and stress-strain curve. 对应的应力和应变值相对绘制的图表。应力值通常垂直绘制（纵坐标或y轴），应变值水平绘制（横坐标或X轴）。也称为变形曲线和应力-应变曲线。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |