| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Ductility | 延展性 |
The ability of a material to deform plastically before fracturing. Measured by elongation or reduction in area in a tensile test, by height of cupping in a cupping test, or by the radius or angle of bend in a bend test. 材料在断裂前发生塑性变形的能力。通过拉伸试验中的伸长率或面积减少量、杯突试验中的杯突高度或弯曲试验中的弯曲半径或角度来测量。 |
| Absolute viscosity | 绝对粘度 |
A measure of the internal shear properties of fluids, expressed as the tangential force per unit area at either of two horizontal planes separated by one unit thickness of a given fluid, one of the planes being fixed and the other moving with unit velocity. 流体内部剪切特性的量度，表示为两个水平面中的任何一个上的单位面积切向力，两个水平面被给定流体的一个单位厚度隔开，其中一个平面固定，另一个以单位速度移动。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Brittle lacquer coating | 脆性漆涂层 |
A lacquer that, when painted on to an unloaded body, reveals the direction of maximum tension stresses from the pattern of cracking produced in the lacquer when the body is loaded. 一种漆，当涂在未加载的车身上时，从车身加载时在漆中产生的裂纹图案中显示出最大拉应力的方向。 |
| Abradant | 研磨剂 |
The differently sized grits of hard materials such as emery employed for grinding, polishing, etc. The abrasive grade is determined by the grit size (grit number) originally related to the hole sizes in wire sieves. 用于研磨、抛光等的硬质材料（例如金刚砂）的不同尺寸粒度。磨料等级由最初与金属丝筛孔尺寸相关的粒度（粒度数）决定。 |
| High strength low alloy steels | 高强度低合金钢 |
(HSLA steels) Steels with various micro-alloying elements such as copper, nickel, chromium, molybdenum, niobium, titanium, and vanadium in small quantities that give improved strength (as high as 900 MPa) and corrosion properties compared with plain carbon steels. Improvements are due to grain refinement and precipitation hardening, better control of the chemistry during steel making, and accurate rolling temperatures. （HSLA钢）是含有各种微合金元素的钢，如少量的铜、镍、铬、钼、铌、钛和钒，与普通碳钢相比，具有更好的强度（高达900MPa）和腐蚀性能。这些改进归功于晶粒细化和沉淀硬化、炼钢过程中更好的化学控制以及精确的轧制温度。 |
| Accelerated testing | 加速测试 |
A type of testing, for rates of wear, fatigue, corrosion etc., in which failure times are reduced by employing greater loads, more frequent power cycling, higher vibration levels, higher humidity, higher temperatures, greater potential differences etc. than would be encountered in normal operation. 一种测试类型，用于测试磨损率、疲劳率、腐蚀率等，通过采用比正常运行中更大的负载、更频繁的功率循环、更高的振动水平、更高湿度、更高温度、更大的电位差等，减少故障时间。 |
| Prevailing torque | 有效扭矩 |
Torque required to run a nut down against the joint when some obstruction, such as a plastic insert in the threads, or a noncircular thread, or other, has been introduced to help the fastener resist vibration loosening. Prevailing torque, unlike normal torque on a nut or bolt, is not proportional to the Preload in the fastener. 当引入了一些障碍物（如螺纹中的塑料插件或非圆螺纹或其他障碍物）以帮助紧固件抵抗振动松动时，将螺母向下压靠接头所需的扭矩。与螺母或螺栓上的正常扭矩不同，主要扭矩与紧固件中的预载不成比例。 |
| Air-hardening steel | 空气硬化钢 |
A steel containing sufficient carbon and other alloying elements to harden fully during cooling in air or other gaseous mediums from a temperature above its transformation range. The terms should be restricted to steels that are capable of being hardened by cooling in air in fairly large sections, about 2 in. (50 mm) or more in diameter. Same as self-hardening steel. 一种钢，含有足够的碳和其他合金元素，可以在空气或其他气体介质中从高于其转变范围的温度冷却过程中完全硬化。这些术语应仅限于能够通过在相当大的截面（直径约2英寸（50毫米）或更大）中通过空气冷却而硬化的钢。与自硬钢相同。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Coalescence | 聚结 |
Growth of grains at the expense of the remainder by absorption or the growth of a phase or particle at the expense of the remainder by absorption or reprecipitation. 通过吸收以牺牲剩余为代价的晶粒的生长或以通过吸收或再沉淀为代价的以剩余为代价的相或颗粒的生长。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Closed system | 封闭系统 |
A closed thermodynamic system consists of a fixed amount of mass. No mass can cross its boundary although energy can, in the form of work or heat, and its volume can change. 一个封闭的热力学系统由一定量的质量组成。能量可以以功或热的形式存在，其体积可以改变，但没有质量可以越过它的边界。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| Dynamic hardness | 动态硬度 |
(rebound hardness) The resistance of a material to local indentation by a rapidly-moving rigid indenter. In most practical methods the indenter is allowed to fall under gravity on to the surface of the material when the rebound height is a measure of the dynamic hardness. （回弹硬度）材料对快速移动的刚性压头局部压痕的阻力。在大多数实际方法中，当回弹高度是动态硬度的测量值时，允许压头在重力作用下落在材料表面上。 |
| Thermal analysis | 热分析 |
A method for determining transformations in a metal by noting the temperatures at which thermal arrests occur. These arrests are manifested by changes in slope of the plotted or mechanically traced heating and cooling curves. When such data are secured under nearly equilibrium conditions of heating and cooling, the method is commonly used for determining certain critical temperatures required for the construction of equilibrium diagrams. 一种通过记录发生热阻的温度来确定金属转变的方法。这些阻力表现为绘制或机械追踪的加热和冷却曲线斜率的变化。当这些数据在加热和冷却的近似平衡条件下得到保证时，该方法通常用于确定构建平衡图所需的某些临界温度。 |
| Weight (W) (Unit N) | 重量（W）（单位：N） |
The force of attraction on a body due to gravity. A body’s weight is the product of its mass and the gravitational field strength at that point. Mass remains constant, but weight depends on the object’s position on the Earth’s surface, decreasing with increasing altitude. If g is the acceleration due to gravity, the weight of a mass m is given by W = mg. On Earth, the acceleration due to gravity is approximately 9.81 m/s², so that the weight of a 1 kg mass is 9.81 N. More generally, the weight is the force exerted on the mass of a body when in the gravitational field of another body. 重力由于重力作用在物体上的吸引力。物体的重量是其质量和该点引力场强度的乘积。质量保持不变，但重量取决于物体在地球表面的位置，随着海拔的升高而减小。如果g是重力引起的加速度，则质量m的重量由W=mg给出。在地球上，重力引起的加速度约为9.81m/s²，因此1千克质量的重量为9.81N。更一般地说，重量是在另一个物体的重力场中施加在物体质量上的力。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Binary vapour cycle | 二元蒸气循环 |
A power cycle which combines a steam cycle at relatively low temperature (the bottoming cycle) with a higher temperature cycle (the topping cycle) in which a working fluid such as mercury, sodium or potassium is used. 一种动力循环，它将相对低温的蒸汽循环（底部循环）与高温循环（顶部循环）相结合，其中使用了诸如汞、钠或钾之类的工作流体。 |
| Melting point (Unit K or °C) | 熔点（单位K或°C） |
The temperature at which a solid material undergoes the phase change to a liquid at a specified pressure, usually 1 atm. Pure metals and eutectics have single-valued melting points, while alloys with other compositions melt over a range of temperature such that there is a well-defined start and end to the melting process, but there are states in between where solid and liquid are both present. 在特定压力下，固体材料发生相变为液体的温度，通常为1大气压。纯金属和共晶具有单值熔点，而具有其他成分的合金在一定温度范围内熔化，熔化过程有一个明确的起点和终点，但其间存在固态和液态并存的状态。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| Fillister head | 槽头 |
Similar to a pan head but with a smaller head diameter and a taller head, with higher vertical sides. 类似于盘头，但头部直径较小，头部较高，垂直边较高。 |
| Mohr–Coulomb fracture criterion | Mohr–Coulomb断裂准则 |
A fracture criterion, primarily for brittle materials, according to which failure occurs when the stress at a point in a material falls outside the envelope created by the Mohr’s circles for uniaxial tensile strength and uniaxial compressive strength. 一种断裂准则，主要适用于脆性材料，根据该准则，当材料中某一点的应力落在单轴抗拉强度和单轴抗压强度的莫尔圆所形成的包络线之外时，就会发生断裂。 |
| Vane engine (vane motor) | 叶片发动机（叶片马达） |
A rotary engine in which high-pressure hydraulic fluid in the spaces between spring-loaded sliding vanes held in an offset rotor acts on the vanes, causing the rotor to revolve within a cylinder. The design is much like a sliding-vane compressor, as is that of a vane pump, used to pump liquids. 一种旋转式发动机，其中偏置转子中装有弹簧的滑动叶片之间的高压液压流体作用在叶片上，使转子在气缸内旋转。这种设计很像滑动叶片压缩机，就像用于泵送液体的叶片泵一样。 |
| Alternating stress | 交替应力 |
(Unit Pa) Originally, stresses of changing sign (tension-tocompression-to-tension, etc.) in a component produced by alternating forces acting in opposite directions, but now generally used to describe stresses that vary but may keep the same sign, as produced by periodic, out-of–balance, or vibrational loads. （单位Pa）最初，构件中由相反方向的交变力产生的符号变化的应力（张力到压缩到张力等），但现在通常用于描述变化但可能保持相同符号的应力，如由周期性、失衡或振动载荷产生的应力。 |
| Cooling curve | 冷却曲线 |
A curve showing the relation between time and temperature during the cooling of a material. 显示材料冷却过程中时间和温度之间关系的曲线。 |
| Transfer ratio | 传输比 |
(transfer constant) A complex variable representing the ratio between the output of a transducer and the input causing that output. （传递常数）一个复变量，表示传感器输出与产生该输出的输入之间的比率。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Elbow | 肘部 |
1. A fitting that connects the ends of two pipes at an angle, 45°, 90°, and 180° being the most common. 2. The third joint on an articulated robot corresponding to the human elbow. 1.以45°、90°和180°角连接两个管道端部的配件。2.示例关节机器人上的第三关节对应于人的肘部。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Failure of the joint | 连接失效 |
Failure of a bolted joint to behave as intended by the designer. Failure can be caused or accompanied by broken or lost bolts, but can also mean joint slip or leakage from a gasketed joint even if all bolts still remain whole and in place. Common reasons for joint failure include vibration loosening, poor assembly practices, improper design, unexpected service loads or conditions, etc. 螺栓连接未达到设计者的预期性能。故障可能由螺栓断裂或丢失引起或伴随而来，但也可能意味着即使所有螺栓仍保持完整和就位，也存在接头滑动或垫圈接头泄漏。接头故障的常见原因包括振动松动、装配不当、设计不当、意外的工作负载或条件等。 |
| Corrosive wear | 腐蚀磨损 |
Wear in which chemical or electrochemical reaction with the environment is significant. 与环境发生显着化学或电化学反应的磨损。 |
| Impact strength | 冲击强度 |
The resiliency or toughness of a solid as measured by impact energy. 用冲击能量测量的固体的弹性或韧性。 |
| Standard fit | 标准匹配 |
The fit of a component machined or otherwise manufactured to standardized clearances and tolerances. 根据标准间隙和公差加工或以其他方式制造的部件的配合。 |
| Effective radius of nut, bolt head, or threads | 螺母、螺栓头或螺纹的有效半径 |
Distance between the geometric center of the part and the circle of points through which the resultant contact forces between mating parts passes. Must be determined by integration. 零件几何中心与配合零件之间的合力通过的点圆之间的距离。必须通过积分来确定。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Dead load (Unit N) | 静载（单位N） |
A load on a component or structure that is steady with time, e.g. the self-weight of a bridge. 部件或结构上随时间稳定的载荷，例如桥梁的自重。 |
| Compression pressure (Unit Pa) | 压缩压力（单位Pa） |
The pressure produced in a cylinder of a piston engine by compression of air in the absence of fuel. 在没有燃料的情况下通过压缩空气在活塞发动机的气缸中产生的压力。 |
| Die | 模具 |
1. A tool having an appropriately-shaped hole through which material may be extruded or drawn. 2. A tool employed in forging. 3. A block having the male or female shape employed in stamping operations. 4. A thick circular disc, driven by a die wrench, with internally-threaded cutting edges for producing a screw thread. A die wrench (die stock) holds a screw-cutting die and has two projecting arms for applying the torque necessary to cut the thread. A die having a hexagonal or square shape (die nut), driven by a spanner, is used in confined spaces where a die wrench cannot be rotated through a full circle. 1.一种具有适当形状的孔的工具，通过该孔可以挤压或拉伸材料。2.一种用于锻造的工具。3.一种用于冲压操作的具有阳或阴形状的块体。4.一种由模具扳手驱动的厚圆盘，具有用于产生螺纹的内螺纹切削刃。冲模扳手（冲模）装有一个螺旋切割模，并有两个突出臂，用于施加切割螺纹所需的扭矩。由扳手驱动的六边形或方形模具（模具螺母）用于模具扳手无法旋转一整圈的受限空间。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Fracture surface | 断裂面 |
The irregular surface produced when a piece of metal is broken. 一块金属破碎时产生的不规则表面。 |
| Hydrogen damage | 氢损伤 |
A general term for the embrittlement, cracking, blistering, and hydride formation that can occur when hydrogen is present in some metals. 当氢存在于某些金属中时可能发生的脆化、开裂、起泡和氢化物形成的总称。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Variance | 方差 |
A measure of the squared dispersion of observed values or measurements expressed as a function of the sum of the squared deviations from the population mean or sample average. 观测值或测量值的平方离散度的度量，表示为总体平均值或样本平均值的平方偏差之和的函数。 |
| Nut splitter | 螺母分离器 |
A tool for removing rusted-on and corroded nuts from bolts. It consists of a stiff steel ring that is placed around the nut. A screw thread passing through the ring bears diametrically on a wedged-shape tip that indents and cuts though a face of the nut. 从螺栓上去除锈蚀螺母的工具。它由一个围绕螺母放置的刚性钢环组成。穿过环的螺纹径向支撑在楔形尖端上，该尖端凹陷并穿过螺母的表面。 |
| Fatigue strength | 疲劳强度 |
The stress to which a metal can be subjected for a specified number of cyclic changes of stress. The maximum stress that can be sustained for a specified number of cycles without failure. The value of the maximum stress and the stress ratio also should be stated. 金属在指定数量的应力循环变化下可以承受的应力。可以在指定的循环次数内持续而不失效的最大应力。还应说明最大应力值和应力比。 |
| Yield strength | 屈服强度 |
That stress level which will create a permanent deformation of 0.2% or 0.5% or some other small, preselected, amount in a body. Approximately equal to the elastic and proportional limits of the material; a little higher than the proof strength of a bolt. The stress at which a material exhibits a specified deviation from proportionality of stress and strain. An offset of 0.2% is used for many metals. 该应力水平将在物体中产生0.2%或0.5%的永久变形，或其他一些小的、预先选定的量。近似等于材料的弹性和比例极限；略高于螺栓的强度。材料表现出与应力和应变比例的特定偏差的应力。许多金属使用0.2%的偏移量。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Centigrade heat unit | 摄氏热量单位 |
(Celsius heat unit, CHU) An obsolete (i.e. non-SI) unit equal to the energy required to increase the temperature of one pound of pure, air-free water from 14.5°C to 15.5°C at a pressure of one standard atmosphere. （摄氏热量单位，CHU）一个已被淘汰的（即非国际单位制）单位，等于在一个标准大气压的压力下将一磅纯净的无空气水的温度从14.5°C提高到15.5°C所需的能量. |
| Load | 负载 |
For testing machines, a force applied to a test piece that is measured in units such as pound-force, newton, or kilogram-force. 对于试验机，施加在试件上的力，以磅力、牛顿或千克力等单位测量。 |
| Congruent melting point (Unit K) | 全等熔点（单位K） |
congruent melting point (Unit K) The temperature at which a solid substance at a specified pressure changes phase to a liquid of identical composition. 一致的熔点（单位K）固体物质在特定压力下相变为具有相同成分的液体时的温度。 |
| Blank carburizing | 毛坯渗碳 |
Simulating the carburizing operation without introducing carbon. This is usually accomplished by using an inert material in place of the carburizing agent, or by applying a suitable protective coating to the ferrous alloy. 在不引入碳的情况下模拟渗碳操作。这通常通过使用惰性材料代替渗碳剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Fastener standard | 紧固件标准 |
A document which details the attributes of a finished fastener and includes such characteristics as geometry, material or chemistry, heat treatment, finish, testing lot size, and packaging. 详细说明紧固件属性的文件，包括几何形状、材料或化学、热处理、表面处理、测试批量和包装等特性。 |
| Grain-boundary liquation | 晶界液化 |
An advanced stage of overheating in which material in the region of austenitic grain boundaries melts. 奥氏体晶界区域的材料熔化的过热阶段。 |
| Condensation shock | 冷凝冲击 |
For supersonic flow of a moist gas through a divergent nozzle, condensation occurs in the form of spontaneous nucleation at some point downstream of that at which the temperature falls to the saturation temperature. The condensation process proceeds rapidly, and results in a fairly thick discontinuity termed a condensation shock. 对于通过发散喷嘴的湿气体超音速流动，在温度降至饱和温度的点下游的某个点处，冷凝以自发成核的形式发生。凝结过程进行得很快，导致相当厚的不连续性，称为凝结激波。 |
| Lüders lines | 吕德斯线 |
Elongated surface markings or depressions, often visible with the unaided eye, that form along the length of sheet metal or a tension specimen at an angle of approximately 45° to the loading axis. Caused by localized plastic deformation, they result from discontinuous (inhomogeneous) yielding. Also known as Lüders bands, Hartmann lines, Piobert lines, or stretcher strains. 拉长的表面标记或凹陷，通常肉眼可见，沿金属板或拉伸试样的长度形成，与加载轴的角度约为45°。由于局部塑性变形，它们是不连续（不均匀）屈服的结果。也被称为吕德斯带、哈特曼线、皮奥伯特线或拉伸线。 |
| Anode | 阳极 |
That electrode in a battery or corrosion cell which produces electrons. It is the electrode which is destroyed (corrodes). 电池或腐蚀电池中产生电子的电极。被破坏（腐蚀）的是电极。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Thermodynamics laws | 热力学定律 |
The zeroth, first, second, and third laws of thermodynamics. 热力学第零、第一、第二和第三定律。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| Austenite stabilization | 奥氏体稳定化 |
Decrease, in comparison to a continuous cooling, in the amount of martensite occurring from austenite when cooling is interrupted at a temperature between Ms and Mf. This can be explained by the relaxation of stresses induced in the austenite by martensite crystals occurring before the interruption. The relaxation, in turn, leads to the dislocation rearrangement and their interaction with martensite/austenite interfaces, which makes the interfaces immobile. 与连续冷却相比，当在Ms和Mf之间的温度中断冷却时，从奥氏体中产生的马氏体的量减少。这可以通过中断前发生的马氏体晶体在奥氏体中引起的应力松弛来解释。反过来，松弛导致位错重排及其与马氏体/奥氏体界面的相互作用，这使得界面无法移动。 |
| Screw area (Unit m²) | 螺丝面积（单位m²） |
The area of a circle described by the tips of a propeller. 螺旋桨尖端所描述的圆的面积。 |
| Heat capacity (C) (Unit J/K) | 热容量（C）（单位J/K） |
The energy required to raise the temperature of a body by 1K without change of phase. Heat capacity is an extensive thermodynamic property dependent on temperature and pressure. 在不发生相变的情况下将物体的温度提高1K所需的能量。热容量是一种广泛的热力学性质，取决于温度和压力。 |
| Tera (T) | 特拉（T） |
An SI unit prefix indicating a multiplier of 1012; thus terawatt (TW) is a unit of power equal to one trillion watts. 指示乘数1012的SI单位前缀；因此，太瓦（TW）是等于1万亿瓦的功率单位。 |
| Water quenching | 水淬 |
A quench in which water is the quenching medium. The major disadvantage of water quenching is its poor efficiency at the beginning or hot stage of the quenching process. 以水为淬火介质的淬火。水淬的主要缺点是在淬火过程的开始或热阶段效率低。 |
| Belt drive | 带传动 |
Transmission of motion from one shaft to another by means of a continuous plain, or toothed, flexible band (belt) passing over pulleys. In contrast to chain drives, belt drives tend to be employed in low-torque applications. Reduction in transmissible power may occur due to stretch of a plain transmission belt which results in slack in the drive (belt creep) or slip of a belt on a driving or driven pulley (belt slip). 通过穿过滑轮的连续平带或带齿柔性带（带）将运动从一根轴传递到另一根轴。与链条传动相比，皮带传动往往用于低扭矩应用。由于普通传动带的拉伸可能会导致传动松弛（皮带蠕变）或主动或从动皮带轮上的皮带打滑（皮带打滑），从而导致传动功率降低。 |
| Torque arm | 扭力臂 |
A bar fixed at one end used to resist torque applied at the other, for example by an electric drill. 固定在一端的杆，用于抵抗施加在另一端的扭矩，如电钻。 |
| Pascal’s law | 帕斯卡定律 |
When there is a change in pressure at any point in a confined fluid at rest, there is an equal change at every other point in the fluid volume. 当处于静止状态的受限流体中任何一点的压力发生变化时，流体体积中的每一点的变化都相等。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Normality | 常态 |
The principle that the vector sum of plastic strain increments is perpendicular to the yield surface. 塑性应变增量矢量和垂直于屈服面的原理。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Tightness parameter | 密封参数 |
A dimensionless parameter which defines the mass leakage of a gasket as a functionof contained pressure and a contained fluid constant. 一种无量纲参数，将垫圈的质量泄漏定义为所含压力和所含流体常数的函数。 |
| Population | 集合 |
The hypothetical collection of all possible test specimens that could be prepared in the specified way from the material under consideration. Also known as universe. 从所考虑的材料中以规定方式制备的所有可能试样的假设集合。也称为体系。 |
| Carbonitriding | 碳氮共渗 |
A case hardening process in which a suitable ferrous material is heated above the lower transformation temperature in a gaseous atmosphere of such composition as to cause simultaneous absorption of carbon and nitrogen by the surface and, by diffusion, create a concentration gradient. The process is completed by cooling at a rate that produces the desired properties in the workpiece. 一种表面硬化工艺，在该工艺中，将合适的含铁材料在气体气氛中加热到较低的转变温度以上，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。该工艺通过以在工件中产生所需性能的速率冷却来完成。 |
| Secondary stresses (Unit Pa) | 二次应力（单位Pa） |
Stresses different from those induced by the major loading but nevertheless resulting from the major loads; for example, the hoop stresses that occur around the circumference of barrelled compression testpieces and forgings. 与主要荷载引起的应力不同，但主要荷载产生的应力；例如，桶装压缩试件和锻件周围产生的环向应力。 |
| Turbine pump (turbopump) | 涡轮泵 |
An axial or centrifugal pump driven by a turbine. Typically used to supply fuel to the combustion chamber of a rocket engine such as on the space shuttle. 由涡轮驱动的轴向或离心泵。通常用于向火箭发动机（如航天飞机）的燃烧室供应燃料。 |
| Thermal insulation (insulation) | 隔热（绝缘） |
A material that may be a low-conductivity solid, or a porous solid or fabric in which there are voids containing air or another gas, resulting in overall low thermal conductivity. When applied to the surface of a hot or cold object, surface heat transfer is generally reduced. 一种材料，可以是低导电性固体，或多孔固体或织物，其中存在含有空气或其他气体的空隙，从而导致整体低导热性。当应用于热或冷物体的表面时，表面传热通常减少。 |
| Relaxation rate | 松弛率 |
The absolute value of the slope of a stress-relaxation curve at a given time. 给定时间应力松弛曲线斜率的绝对值。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Creep modulus (Unit Pa) | 蠕变模量（单位Pa） |
The ratio of stress/strain at a chosen strain level obtained from creep tests, often plotted against time to show changes in stiffness. 从蠕变测试中获得的选定应变水平下的应力/应变比，通常随时间绘制以显示刚度的变化。 |
| Hot working | 热加工 |
Plastic deformation of a metal, by rolling, drawing, forging, etc., at a temperature above its recrystallization temperature (in commercial alloys above about 40% of their melting points in kelvins) which results in permanent shape change but no increase in strength or loss of ductility. 金属通过轧制、拉拔、锻造等在高于其再结晶温度（在商业合金中高于其熔点的40%的开尔文）的温度下发生塑性变形，导致永久的形状变化，但不会增加强度或失去延展性。 |
| Anti-freeze | 防冻液 |
A substance such as ethylene glycol added to the cooling system of a watercooled engine to lower the freezing point of the cooling water and also inhibit the formation of rust and other deposits. 一种物质，如乙二醇，添加到水冷发动机的冷却系统中，以降低冷却水的冰点，并抑制生锈和其他沉积物的形成。 |
| Degree (°) | 度数（°） |
A measure of plane angle such that 1° is 1/360 of a complete revolution and equal to π/180 rad. 平面角度的一种度量，使得1°是一整圈的1/360，等于π/180弧度。 |
| Lock-nut pipe thread | 锁紧螺母管螺纹 |
The lock-nut pipe thread is a straight thread of the largest diameter which can be cut on a pipe. Its form is identical with that of the American or Briggs standard taper pipe thread. In general, “Go” gages only are required. These consist of a straight-threaded plug representing the minimum female lock-nut thread, and a straight-threaded ring representing the maximum male lock-nut thread. This thread is used only to hold parts together, or to retain a collar on the pipe. It is never used where a tight threaded joint is required. 锁紧螺母管螺纹是最大直径的直螺纹，可在管道上切割。其形式与美国或布里格斯标准锥管螺纹相同。一般情况下，只需要通规。它们由一个表示最小内螺纹锁紧螺母螺纹的直螺纹塞和一个表示最大外螺纹锁紧螺帽螺纹的直形螺纹环组成。该螺纹仅用于将零件固定在一起，或用于将轴环固定在管道上。切勿使用于需要紧密螺纹接头的情况下。 |
| Turbomachine | 涡轮机械 |
(rotodynamic machine) A machine in which there is a transfer of energy between a continuous stream of fluid and a component, called a rotor, rotating about a fixed axis. Fans and turbines (gas, hydraulic, steam, or wind) are turbomachines in which energy is transferred to the rotor, causing it to rotate. Pumps and compressors are turbomachines in which energy is transferred from the externally driven rotor to the fluid. （旋转动力机器）在连续的流体流和绕固定轴旋转的部件（称为转子）之间进行能量传递的机器。风扇和涡轮机（燃气、液压、蒸汽或风力）是涡轮机械，其中能量传递到转子，使其旋转。泵和压缩机是涡轮机械，其中能量从外部驱动的转子传递到流体。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Stress-concentration factor (Kt) | 应力集中系数（Kt） |
A multiplying factor for applied stress that allows for the presence of a structural discontinuity such as a notch or hole; Kt equals the ratio of the greatest stress in the region of the discontinuity to the nominal stress for the entire section. Also known as theoretical stress-concentration factor. 施加应力的倍增系数，允许存在结构不连续性，如缺口或孔；Kt等于不连续区域的最大应力与整个截面的标称应力之比。也称为理论应力集中系数。 |
| Linear-elastic fracture mechanics | 线弹性断裂力学 |
A method of fracture analysis that can determine the stress (or load) required to induce fracture instability in a structure containing a cracklike flaw of known size and shape. 一种断裂分析方法，可确定在含有已知尺寸和形状裂纹状缺陷的结构中引起断裂不稳定性所需的应力（或载荷）。 |
| Degradation of energy | 能源退化 |
Conversion of energy into forms of lower usefulness due to irreversibilities in energy transfer and conversion processes. The increase in entropy can be regarded as a measure of the degradation of energy. 由于能量转移和转换过程中的不可逆性，将能量转换为低效形式。熵的增加可以看作是能量退化的量度。 |
| Butterfly valve | 蝶阀 |
A valve in which a disc rotates on a shaft at right angles to the axis of a pipe to regulate flow. When open, the disc is edge-on to the flow and offers limited resistance. When closed, the disc is pressed against a seat in the valve body. 阀瓣在与管道轴线成直角的轴上旋转以调节流量的阀门。当打开时，圆盘与水流边缘并提供有限的阻力。关闭时，阀瓣被压在阀体内的阀座上。 |
| R-curve/Resistance curve | 阻力曲线 |
In linear-elastic fracture mechanics, a plot of crack-extension resistance as a function of stable crack extension, which is either the difference between the physical crack size, or the effective crack size, and the original crack size. R-curves normally depend on specimen thickness and, for some materials, on temperature and strain rate. An increase in fracture toughness with crack propagation shown by rising plots of toughness vs growing crack length. 在线弹性断裂力学中，作为稳定裂纹扩展函数的裂纹扩展阻力图，即物理裂纹尺寸或有效裂纹尺寸与原始裂纹尺寸之间的差值。R曲线通常取决于试样厚度，对于某些材料，还取决于温度和应变率。是随着裂纹扩展，断裂韧性增加，表现为韧性与扩展裂纹长度的上升曲线。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Scoring | 划痕 |
In tribology, a severe form of wear characterized by the formation of extensive grooves and scratches in the direction of sliding. 在摩擦学中，一种严重的磨损形式，其特征是在滑动方向上形成大面积的凹槽和划痕。 |
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Maximum continuous load | 最大连续负载 |
(maximum continuous rating) (Unit kg/s) The maximum rate of steam output that a boiler can supply for a specified period, usually 24 hours. （最大连续额定功率）（单位为kg/s）锅炉在规定时间内（通常为24小时）可供应的最大蒸汽输出率。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Design pressure (Unit Pa) | 设计压力（单位Pa） |
The greatest pressure that a closed container is expected to experience under normal operating conditions. 密闭容器在正常操作条件下预期承受的最大压力。 |
| Critical strain | 临界应变 |
The strain just sufficient to cause recrystallization; because the strain is small, usually only a few percent, recrystallization takes place from only a few nuclei, which produces a recrystallized structure consisting of very large grains. 刚好足以引起再结晶的应变；由于应变很小，通常只有百分之几，再结晶只发生在少数核上，从而产生由非常大的晶粒组成的再结晶结构。 |
| Rotary valve (rotating valve) | 旋转阀 |
A cylindrical or conical plug in which there is a transverse hole through which fluid can flow when the hole is aligned with the adjacent piping. 一种圆柱形或锥形塞，其中有一个横向孔，当该孔与相邻管道对齐时，流体可通过该孔流动。 |
| Ion nitriding | 离子氮化 |
A method of surface hardening in which nitrogen ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma nitriding or glowdischarge nitriding. 一种表面硬化方法，其中氮离子通过使用高压电能在真空中扩散到工件中。与等离子体氮化或辉光放电氮化同义。 |
| Maximum allowable operating pressure (Unit Pa) | 最大允许使用压力（单位Pa） |
The highest pressure at which any pressure system may be operated, usually 10 to 20% below the maximum allowable working pressure. 任何压力系统可运行的最高压力，通常比最大允许工作压力低10%至20%。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Compressor | 压缩机 |
A turbomachine, of either axial or radial type, that increases the pressure of a gas or vapour. 一种增加气体或蒸汽压力的轴向或径向涡轮机。 |
| Scale effect | 规模效应 |
The change in behaviour with size of a material, component, or structure. For example, cube-square scaling where one element changes with volume and another with area, as in the range of a projectile or ship, droplet formation, and fracture mechanics. 性能随材料、部件或结构尺寸的变化。例如，立方体平方比例，其中一个元素随体积变化，另一个元素因面积变化，如在射弹或飞船的射程、液滴形成和断裂力学中。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Stator | 定子 |
A ring of non-rotating blades or nozzles in a compressor, turbine, or other turbomachine, which directs fluid flow into an adjacent rotor. 涡轮压缩机、涡轮或其他涡轮机械中的一圈不旋转的叶片或喷嘴，将流体引导到相邻的转子中。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Fretting fatigue | 微动疲劳 |
Fatigue fracture that initiate at a surface area where fretting has occurred. The progressive damage to a solid surface that arises from fretting. 在发生微动的表面区域开始的疲劳断裂。由微动引起的对固体表面的渐进性损坏。 |
| Dynamics | 动力学 |
The branch of mechanics that deals with objects in motion. Its two main branches are kinematics, which studies motion without regards to its cause, and kinetics, which also takes into account forces that cause motion. 力学中研究运动物体的分支。它的两个主要分支是运动学和动力学，前者研究运动而不考虑其原因，后者也考虑引起运动的力。 |
| Ideal critical diameter | 理想临界直径 |
(DI). Under an ideal quench condition, the bar diameter that has 50% martensite at the center of the bar when the surface is cooled at an infinitely rapid rate (that is, when H = ∞, where H is the quench severity factor). （DI）在理想淬火条件下，当表面以无限快的速度冷却时（即H=∞, 其中H是淬火严重度因子）。 |
| Active vibration suppression | 主动振动抑制 |
The reduction of undesirable vibration in components by feedback control. 通过反馈控制减少部件中的不良振动。 |
| Temper color | 回火颜色 |
A thin, tightly adhering oxide skin that forms when steel is tempered at a low temperature, or for a short time, in air or a mildly oxidizing atmosphere. The color, which ranges from straw to blue depending on the thickness of the oxide skin, varies with both tempering time and temperature. 一种薄的、紧密粘附的氧化皮，当钢在低温或短时间内在空气或轻度氧化气氛中回火时形成。颜色范围从稻草色到蓝色，取决于氧化皮的厚度，随回火时间和温度而变化。 |
| Absolute humidity | 绝对湿度 |
The weight of water vapor in a gadwater vapor mixture per unit volume of space occupied, expressed, for example, in grains or pounds per cubic foot. 单位体积空间占用的水蒸气混合物中水蒸气的重量，例如，以谷物或磅/立方英尺表示。 |
| Threading machine | 螺纹机 |
A machine used to cut an external thread on a rod, tube, bolt blank, etc. or an internal thread in a hole, tube, nut blank, etc. 用于切割杆、管、螺栓毛坯等上的外螺纹或孔、管、螺母毛坯等中的内螺纹的机器。 |
| Computer control | 电脑控制 |
The control of an engineering device or system by pre-programmed computer or by feedback control. 通过预编程计算机或反馈控制对工程设备或系统进行控制。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Socket wrench | 套筒扳手 |
A form of spanner with an internally ridged steel socket to fit a nut or the head of a bolt or screw. 扳手的一种形式，带有内脊钢套筒，用于安装螺母或螺栓或螺钉的头部。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Crankshaft | 曲轴 |
The main shaft, of which the cranks are a part, of a reciprocating single-or multi-cylinder machine. Crankshafts may be built up in sections or forged as a single component. In an engine, the reciprocating motion of the pistons transmits power to the crankshaft and causes it to rotate, whereas in a pump the crankshaft is driven and its rotation causes the pistons to reciprocate. 曲柄是往复式单缸或多缸机器主轴的一部分。曲轴可以分段组装或作为单个部件锻造。在发动机中，活塞的往复运动将动力传递给曲轴并使其旋转，而在泵中，曲轴被驱动，其旋转使活塞往复运动。 |
| Actuating system | 驱动系统 |
A system in which an electrical, pneumatic or hydraulic input supplied to an actuator produces force, torque, or displacement, usually in a controlled way. 一种系统，其中提供给执行器的电气、气动或液压输入通常以受控方式产生力、扭矩或位移。 |
| Cold die quenching | 冷模淬火 |
A quench utilizing cold, flat, or shaped dies to extract heat from a part. Cold die quenching is slow, expensive, and is limited to smaller parts with large surface areas. 利用冷、平或成型模具从零件中提取热量的淬火。冷模淬火速度慢、成本高，并且仅限于表面积较大的较小零件。 |
| Torsion bar | 扭杆 |
A metal bar designed to act as an elastic spring when torque is applied. 当施加扭矩时用作弹性弹簧的金属棒。 |
| Ideal gas laws | 理想气体定律 |
The law relating pressure, temperature and volume of an ideal (perfect) gas pV = mRT, where R is the gas constant. The law implies that at constant temperature T, the product of pressure p and volume V is constant (Boyle’s law), and at constant pressure, the volume is proportional to the temperature (Charles’ law). 与理想（完美）气体的压力、温度和体积相关的定律pV=mRT，其中R是气体常数。该定律意味着在恒定温度T下，压力p和体积V的乘积是恒定的（波义耳定律），而在恒定压力下，体积与温度成正比（查尔斯定律）。 |
| Fracture mechanics | 断裂力学 |
The stress analysis of bodies containing cracks. The use of stressconcentration factors and other correction factors of traditional strength of materials is inadequate when flaws are present initially (or develop during loading), since fracture depends not only on stress but also the size of the crack. Traditional strength of materials stress calculations cannot predict either the safe working stress in the presence of a known flaw, or the critical size of flaw just tolerable with a given working stress. 含裂纹物体的应力分析。当初始存在缺陷（或在加载过程中形成缺陷）时，使用应力集中系数和传统材料强度的其他修正系数是不够的，因为断裂不仅取决于应力，还取决于裂纹的大小。传统的材料强度应力计算既不能预测已知缺陷存在时的安全工作应力，也不能预测给定工作应力下可容忍的缺陷临界尺寸。 |
| Deformation (Unit 1/s) | 变形（单位1/s） |
A change in the form of a body due to stress, thermal change, change in moisture, or other causes. In solid mechanics, any change, reversible (elastic) or permanent (plastic), in the shape or size of parts of a body, or the whole body, caused by external or internal loading. It includes extension, compression, bending, and twisting. The same state of deformation in a body can appear as different combinations of elongation and shear. To state how much of the total strain is shear, it is split into dilatation and deviatoric components, the former changing volume but not shape, the latter shape but not volume. 由于压力、热变化、水分变化或其他原因导致的身体形态变化。在固体力学中，由外部或内部载荷引起的身体各部分或整个身体的形状或大小的任何可逆（弹性）或永久（塑性）变化。它包括拉伸、压缩、弯曲和扭曲。物体中相同的变形状态可以表现为伸长和剪切的不同组合。为了说明总应变中有多少是剪切，将其分为膨胀分量和偏差分量，前者改变体积但不改变形状，后者改变形状但不改变体积。 |
| Rotor | 转子 |
A part of a machine that rotates on a shaft (rotor shaft) about its own axis, such as the blade-carrying discs of a turbine, the blades of a helicopter, or the rotating parts of a Roots blower. 绕轴（转子轴）绕其自身轴线旋转的机器部件，如涡轮叶片、直升机叶片或罗茨鼓风机的旋转部件。 |
| Residual preload | 残余预载荷 |
The tension which remains in an unloaded bolted joint after Relaxation. 松弛后未加载螺栓连接中保持的张力。 |
| X-ray thickness gauge | X射线厚度计 |
A device comprising an X-ray source and a detector used to determine the thickness of material in sheet or plate form, including metals, paper, plastics, rubber, and ceramics. 一种由X射线源和探测器组成的装置，用于测定片状或平板状材料的厚度，包括金属、纸张、塑料、橡胶和陶瓷。 |
| Bright nitriding | 光亮氮化 |
Nitriding in a protective medium to prevent discoloration of the bright surface. 在保护介质中氮化，以防止光亮表面变色。 |
| Translational joint | 平移铰 |
A robot joint where the controlled variable is straight line movement. 控制变量为直线运动的机器人关节。 |
| Grain refiner | 晶粒细化机 |
A material added to a molten metal to induce a finer-than-normal grain size in the final structure. 添加到熔融金属中以在最终结构中产生比正常晶粒尺寸更细的材料。 |
| Austenite | 奥氏体 |
A solid solution of one or more elements in face-centered cubic iron. Unless otherwise designated (such as nickel austenite), the solute is generally assumed to be carbon. Solid solution of alloying elements and/or carbon in γ-Fe. It is named after British metallurgist W. C. Roberts-Austen. 一种或多种元素在面心立方铁中的固溶体。除非另有说明（如镍奥氏体），溶质通常假定为碳。合金元素和/或碳在γ-Fe中的固溶体。它以英国冶金学家WCRoberts-Austen的名字命名。 |
| Air pump | 气泵 |
A machine for providing a flow of air or for increasing or decreasing the mass and pressure of air in a closed container. The term pump is more usual when the working fluid is a liquid, while compressor is more usual for gases. 一种用于提供空气流动或用于增加或减少密闭容器中空气质量和压力的机器。当工作流体是液体时，术语泵更常用，而气体更常用压缩机。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Strength of bolt | 螺栓强度 |
An ambiguous term which can mean Ultimate strength or Proof load or Endurance limit or Yield strength. 一个模棱两可的术语，可表示极限强度或验证荷载或耐久极限或屈服强度。 |
| Zone melting (zone refining) | 区域熔炼（区域精炼） |
A process of purification of materials in which a narrow molten zone is moved along the length of the material, resulting in impurities being segregated at one end. 一种净化材料的过程，其中一个狭窄的熔融区沿材料长度移动，导致杂质在一端分离。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Friction loss (Unit J) | 摩擦损失（单位J） |
The conversion of mechanical energy to heat due to friction within a machine, mechanism, linkage, etc. 由于机器、机构、连杆等内部的摩擦而将机械能转化为热能。 |
| Cohesive zone | 凝聚力区 |
In fracture-mechanics modelling and simulation, the region at the crack tip over which an assumed traction (load-displacement) relation has to be overcome to permit initiation and propagation of a crack. 在断裂力学建模和模拟中，必须克服假定的牵引（载荷-位移）关系以允许裂纹萌生和扩展的裂纹尖端区域。 |
| Shear strength | 抗剪强度 |
The maximum shear stress that a material is capable of sustaining. Shear strength is calculated from the maximum load during a shear or torsion test and is based on the original dimensions of the cross section of the specimen. 材料能够承受的最大剪切应力。抗剪强度根据剪切或扭转试验期间的最大载荷计算，并基于试样横截面的原始尺寸。 |
| Contact strength (Unit N) | 接触强度（单位N） |
The maximum allowable load between contacting bodies converted into a stress. 换算成应力的接触体之间的最大允许载荷。 |
| Magnetic test | 磁性测试 |
Method used to test heat extraction rates of various quenchants. The test works by utilizing the change in magnetic properties of metals at their Curie point–the temperature above which metals lose their magnetism. 用于测试各种淬火剂的热提取率的方法。该测试通过利用金属在居里点（即金属失去磁性的温度）的磁性变化来进行。 |
| Quench-age embrittlement | 淬火时效脆化 |
Embrittlement of low-carbon steels resulting from precipitation of solute carbon at existing dislocations and from precipitation hardening of the steel caused by differences in ferrite at different temperatures. Quenchage embrittlement usually is caused by rapid cooling of the steel from temperatures slightly below Ac1 (the temperature at which austenite begins to form), and can be minimized by quenching from lower temperatures. 低碳钢的脆化是由于溶质碳在现有位错处的沉淀和铁素体在不同温度下的差异导致的钢沉淀硬化造成的。淬火脆性通常是由钢从略低于Ac1的温度（奥氏体开始形成的温度）快速冷却引起的，可以通过从较低温度淬火来最小化。 |
| Centripetal | 向心力 |
Acting or moving in a direction towards the axis of rotation. 在朝向旋转轴的方向上起作用或移动。 |
| Fracture strength | 断裂强度 |
(fracture stress) (Unit Pa) The stress at which a material breaks. It is not absolute for a given material, as it depends on the laws of fracture mechanics and is size-dependent. （断裂应力）（单位Pa）材料断裂时的应力。对于给定的材料，它不是绝对的，因为它取决于断裂力学定律，并且取决于尺寸。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| Cylinder head | 气缸盖 |
The machined casting, typically of aluminium alloy or cast iron, that fits above the cylinder block of a piston engine and closes off the cylinders. It normally includes part of the combustion chambers and holes for the valves and spark plugs. 活塞式发动机缸体上方的机械铸件，通常由铝合金或铸铁制成，用于封闭气缸。它通常包括燃烧室的一部分以及阀门和火花塞的孔。 |
| Ratchet coupling | 棘轮联轴器 |
A joint employing a ratchet system between two shafts, so that not only does the driven shaft run in one direction only, but also the driven shaft can, if necessary, run more quickly than the driving shaft. 在两个轴之间采用棘轮系统的接头，这样不仅从动轴只能在一个方向上运行，而且在必要时，从动轴可以比驱动轴运行得更快。 |
| Scleroscope hardness number (HSc or HSd) | 硬化镜硬度值（HSc或HSd） |
A number related to the height of rebound of a diamond-tipped hammer dropped on the material being tested. It is measured on a scale determined by dividing into 100 units the average rebound of the hammer from a quenched(to maximum hardness) and untempered AISI W5 tool steel test block. 与落在被测材料上的菱形锤的回弹高度相关的数字。通过将锤子从淬火（达到最大硬度）和未淬火的AISI W5工具钢试块上的平均回弹分为100个单位来测量。 |
| Cohesive strength | 内聚强度 |
(Unit Pa) A theoretical fracture strength for solids based on interatomic forces, approximately equal to E/10 where E is Young’s modulus. （单位Pa）基于原子间力的固体理论断裂强度，大约等于E/10，其中E是杨氏模量。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Impact loads | 冲击载荷 |
Especially severe shock loads such as those caused by instantaneous arrest of a falling mass, shock meeting of two parts (in a mechanical hammer, for example), or by explosive impact, in which there can be an exceptionally rapid build-up of stress. 特别严重的冲击载荷，例如由下落质量的瞬时停止、两部分的冲击碰撞（例如在机械锤中）或爆炸性冲击引起的冲击载荷，其中可能会出现异常快速的应力积聚。 |
| Total carbon | 总碳 |
The sum of the free and combined carbon (including carbon in solution) in a ferrous alloy. 铁合金中游离碳和结合碳（包括溶液中的碳）的总和。 |
| Bearing test | 轴承测试 |
A method of determining the response to stress (load) of metal products that are subjected to riveting, bolting, or a similar fastening procedure. The purpose of the test is to determine the bearing strength of the material and to measure the bearing stress versus the deformation of the hole created by a pin or rod of circular cross section that pierces the sheet perpendicular to the surface. 一种确定经受铆接、螺栓连接或类似紧固程序的金属产品对应力（载荷）的响应的方法。测试的目的是确定材料的承载强度，并测量承载应力与由垂直于表面刺穿板材的圆形横截面的销或杆产生的孔的变形。 |
| Gauge pressure (Unit Pa) | 表压（单位Pa） |
The level of static pressure above the ambient pressure. 高于环境压力的静压水平。 |
| Total head (hT) (Unit m) | 总水头（hT）（单位：m） |
Total pressure pT expressed in terms of the vertical height of a column of liquid, typically water or mercury, i.e. hT = pT/ρg where g is the acceleration due to gravity and ρ is the liquid density. 总压力pT以液体柱（通常为水或汞）的垂直高度表示，即hT=pT/ρg，其中g为重力加速度，ρ为液体密度。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Physical crack size (ap) | 物理裂纹尺寸（ap） |
The distance from a reference plane to the observed crack front. This distance may represent an average of several measurements along the crack front. The reference plane depends on the specimen form, and it is normally taken to be either the boundary or a plane containing either the load line or the centerline of a specimen or plate. 从基准面到观察到的裂纹前沿的距离。该距离可以表示沿裂纹前沿的若干测量的平均值。基准面取决于试样形状，通常视为边界或包含试样或板的载重线或中心线的平面。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Relative density | 相对密度 |
(specific gravity) The ratio of the density of a substance to that of a reference substance, such as water for liquids and solids, and dry air for gases. （比重）物质密度与参考物质密度之比，如液体和固体为水，气体为干燥空气。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Stress wave | 应力波 |
An unbalanced force, such as an impact, applied at one location in a body sets the material there into vibration that is transmitted to adjacent elements and ultimately to all parts of the body in the form of stress waves or wave packets. 施加在物体某个位置的不平衡力（如冲击力）会使物体中的材料产生振动，并以应力波或波包的形式传递到相邻元件，最终传递到物体的所有部位。 |
| Toothed belt | 齿带 |
A flat belt, typically of a reinforced-rubber material, with transverse teeth that engage with teeth on a wheel or pulley. 一种扁平皮带，通常由增强橡胶材料制成，带有横向齿，与车轮或皮带轮上的齿啮合。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Wedge | 楔子 |
A short triangular prism whose major surfaces subtend an acute angle, that can be driven between two objects or parts of an object to split, tighten, or secure them, or to widen an opening or raise a heavy object. The acute angle gives a high mechanical advantage. 一种短的三棱镜，其主面对着一个锐角，可在两个物体或物体的一部分之间驱动，以将它们分开、拧紧或固定，或加宽开口或举起重物。锐角具有很高的机械优势。 |
| Clearance angle | 后角 |
(relief angle) (Unit °) The angle between the underneath or flank of a cutting tool and the machined surface. （后角）（单位°）切削刀具的底部或侧面与加工表面之间的角度。 |
| Cold treatment | 冷处理 |
Treatment carried out after quenching to transform retained austenite into martensite, involving cooling and holding at a temperature below ambient. 淬火后进行的处理，以将残余奥氏体转变为马氏体，包括冷却和保持在低于环境温度的温度。 |
| Crack-extension force (G) | 裂纹扩展力（G） |
The elastic energy per unit of new separation area that would be made available at the front of an ideal crack in an elastic solid during a virtual increment of forward crack extension. 在向前裂纹扩展的虚拟增量期间，在弹性固体中理想裂纹的前端可获得的每单位新分离面积的弹性能量。 |
| Acoustic pyrometer | 声学高温计 |
A non-intrusive pyrometer based on the principle that the sound speed in a gas is proportional to the square root of its absolute temperature. 一种非侵入式高温计，其原理是气体中的声速与其绝对温度的平方根成正比。 |
| Punch | 冲床 |
1. A hand tool with a sharp point, used to mark the position of a hole centre in a workpiece prior to drilling. 2. A flat-ended tool with sharp edges, used to shear out a hole in a plate that is supported underneath on a die having a slightly larger same-shaped orifice. 1.一种带有尖头的手动工具，用于在钻孔前标记工件中孔中心的位置。2.一种具有锐边的平头工具，用于剪切板上的孔，该板支撑在具有稍大相同形状孔口的模具下方。 |
| Horsepower | 马力 |
Unit indicating the rate at which work is done. The electrical equivalent of one horsepower is 746 watts. 单位表示完成工作的速率。一马力的电当量为746瓦。 |
| Nut | 螺母 |
A metal fastener of square, hexagon or other shape, having an internal thread which screws onto a bolt, stud or arbor. An internally-threaded fastener used with externally-threaded bolts. Usually hexagonal in shape but there is a multitude of other geometries, such as square, for special purposes and different gripping tools. 一种方形、六角形或其他形状的金属紧固件，具有内螺纹，可拧在螺栓、螺柱或心轴上。与外螺纹螺栓一起使用的内螺纹紧固件。通常为六边形，但也有许多其他几何形状，如方形，用于特殊用途和不同的夹持工具。 |
| Clip gauge | 夹规 |
A displacement gauge consisting of two thin strain-gauged cantilever arms attached through knife edges to a testpiece to give the load–line displacement in fracture mechanics test pieces, or used as an extensometer in tensile tests. 一种位移计，由两个通过刀刃连接到试件上的薄应变测量悬臂组成，以提供断裂力学试件中的载荷线位移，或用作拉伸试验中的引伸计。 |
| Piston pump | 活塞泵 |
A positive-displacement pump in the basic configuration of which a piston reciprocates in a cylinder. On the suction stroke, fluid is drawn into a chamber through the inlet valve, which is then open while the outlet valve is closed. On the delivery stroke the fluid is forced out of the chamber through the outlet valve, which then opens while the inlet valve is closed. Both axial and radial configurations are common. 活塞在气缸中往复运动的一种容积泵。在吸入冲程，流体通过入口阀吸入腔室，然后在出口阀关闭时打开。在输送冲程中，流体通过出口阀被迫流出腔室，然后出口阀打开，同时入口阀关闭。轴向和径向配置都很常见。 |
| Wrap-around bend | 环绕弯曲 |
The bend obtained when a specimen is wrapped in a closed helix around a cylindrical mandrel. This term is sometimes applied to a semiguided bend of 180° or less. 当试样缠绕在圆柱形心轴周围的闭合螺旋中时获得的弯曲。该术语有时适用于180°或更小的半导弯曲。 |
| Subcritical annealing | 不完全退火 |
A process anneal performed on ferrous alloys at a temperature below Ac1. 在低于Ac1的温度下对铁合金进行的工艺退火。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Shear stress (Unit Pa) | 剪应力（单位Pa） |
(1) A stress that exists when parallel planes in metal crystals slide across each other. (2) The stress component tangential to the plane on which the forces act. Also known as tangential stress. (shearing stress, tangential stress, τ) 1. The stress which acts parallel to any plane within a solid material. It can arise due to a bending moment, a shear force, or torque applied to the body. 2. The stress corresponding to velocity gradients within a flowing viscous fluid. （剪应力，切向应力，τ）（1）当金属晶体中的平行平面彼此滑动时存在的应力。（2）与力作用平面相切的应力分量。也称为切向应力。1.平行于固体材料内任何平面的应力。它可能是由于施加在身体上的弯矩、剪力或扭矩引起的。2.对应于流动粘性流体内的速度梯度的应力。 |
| Spring constant | 弹簧常数 |
The ratio between the forces exerted on a spring (or a bolt) and the deflection thereof. Has the dimensions of force per unit change in length (e.g., lb=in.). Also called Stiffness. 施加在弹簧（或螺栓）上的力与其挠度之间的比率。具有每单位长度变化的力的尺寸（例如lb=in.）。也称为刚度。 |
| Tangent modulus | 切线模量 |
The slope of the stress-strain curve at any specified stress or strain. See also modulus of elasticity. 在任何规定的应力或应变下，应力-应变曲线的斜率。另见弹性模量。 |
| Cup washer | 杯形垫圈 |
A dished leather or neoprene washer fitted to the rod end in some piston-style pumps. 在某些活塞式泵中，安装在杆端的碟形皮革或氯丁橡胶垫圈。 |
| Deposit gauge | 沉积量计 |
(deposition gauge) An instrument employed in air pollution studies for measuring the amount of pollutant deposited on a given area in a given time under given conditions. （沉降计）在空气污染研究中使用的仪器，用于测量在给定条件下在给定时间内沉积在给定区域上的污染物量。 |
| Steel-wire rope | 钢丝绳 |
A rope or cable made up of many steel strands wrapped helically about an axis, each strand being made of metal wires twisted together like a helix. 一种绳索或缆绳，由许多绕轴螺旋缠绕的钢绞线组成，每根钢绞线由金属丝缠绕在一起形成螺旋。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Bainitic hardening | 贝氏体硬化 |
Quench-hardening treatment resulting principally in the formation of bainite. 淬火硬化处理主要导致贝氏体的形成。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Proof load | 验证载荷（单位 N） |
The maximum, safe, static, tensile load which can be placed on a fastener without yielding it. Sometimes given as a force (in lb or N) sometimes as a stress (in psi or MPa). The test load in quality control to which different components made of different materials must be subjected without failing in order to perform properly. 可施加在紧固件上而不使其屈服的最大安全静态拉伸载荷。有时以力（lb或N）表示，有时以应力（psi或MPa）表示。质量控制中的测试负荷，由不同材料制成的不同部件必须经受该负荷，才能正常运行。 |
| Continuous-type furnace | 连续式炉 |
A furnace used for heat treating materials that progress continuously through the furnace, entering one door and being discharged from another. See belt furnac, direct-fired tunnel-type furnac, rotary retort furnace, shaker-hearth furnace. 一种用于热处理材料的炉子，该炉子连续通过炉子，进入一个门并从另一个门排出。参见带式高炉、直燃隧道式高炉、旋转罐式炉、振动炉。 |
| V-block | V型块 |
A block having a 90° V-shaped recess; used in a workshop to hold round workpieces. 具有90°V形凹槽的块体；在车间里用来装圆形工件。 |
| International System of Units | 国际单位制 |
(SI system of units, Le Système international d’unités) The standard system of units now used almost universally in science and engineering except in the United States. The definitive reference on the SI is a booklet published by the International Bureau of Weights and Measures, often referred to as the BIPM SI Brochure. There are seven base units: metre (symbol m) for length; kilogram (kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred.(kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred. （国际单位制，Le Système international d\\\'unités）目前美国除外，在科学和工程中几乎是普遍使用的标准单位制。SI的最终参考是国际度量衡局出版的小册子，通常称为BIPM SI小册子。有七个基本单位：米（符号m）表示长度；质量为千克（kg）；物质量的摩尔（mol）；时间为秒；开尔文（K）表示温度；电流为安培（A）；而坎德拉（cd）表示发光强度。新的国际单位制定义于2019年5月20日生效，该定义基于自然界的普遍常数（也称为基本物理常数：阿伏伽德罗常数、玻尔兹曼常数和普朗克常数）。这些常数的值也进行了少量调整。除了基本单位外，还有22个相干导出单位，包括平面角的弧度（rad）、立体角的斯特拉迪安（sr）、频率的赫兹（Hz）、力的牛顿（N）、压力的帕斯卡（Pa）、能量、功和热量的焦耳（J）以及功率和辐射通量的瓦特（W）。建议的做法是避免N/mm²、MN/m²等组合。 |
| Edge distance ratio | 边距比 |
The ratio of the edge distance to the pin diameter in a bearing test. 轴承测试中边缘距离与销直径的比值。 |
| Stroke | 一击 |
1. (stroke length) (Unit m) The linear distance between top dead centre and bottom dead centre of a piston in a reciprocating engine or mechanism. 2. The movement of a piston or plunger in a reciprocating machine to execute a particular function; for example, the exhaust stroke of an engine in which the exhaust gases are expelled from a cylinder. 1.（冲程长度）（单位：m）往复式发动机或机构中活塞上止点和下止点之间的线性距离。2.活塞或柱塞在往复式机器中执行特定功能的运动；例如发动机的排气冲程，其中排气从气缸中排出。 |
| Fluid mechanics | 流体力学 |
The study of fluids in motion (fluid dynamics) or fluid statics where there is no relative motion between fluid particles. Fluid statics concerns primarily the variation of pressure with altitude or depth; it includes aerostatics and hydrostatics. Fluid dynamics includes the topics of aerodynamics, gas dynamics, hydraulics, hydrodynamics and many aspects of acoustics, chemical engineering, flight, lubrication, meteorology, non-Newtonian fluid flow, oceanography, power-plant technology, propulsion, and turbomachinery. 研究运动中的流体（流体动力学）或流体静力学，其中流体粒子之间没有相对运动。流体静力学主要关注压力随高度或深度的变化；它包括空气静力学和流体静力学。流体动力学包括空气动力学、气体动力学、水力学、流体动力学以及声学、化学工程、飞行、润滑、气象学、非牛顿流体流动、海洋学、发电厂技术、推进和涡轮机械的许多方面。 |
| Ductile cast iron | 球墨铸铁 |
A cast iron that has been treated while molten with an element such as magnesium or cerium to induce the formation of free graphite as nodules or spherulites, which imparts a measurable degree of ductility to the cast metal. Also known as nodular cast iron, spherulitic graphite cast iron and SG iron. 一种铸铁，在熔融时用镁或铈等元素进行处理，以诱导游离石墨形成为球粒或球晶，从而赋予铸造金属可测量的延展性。又称球墨铸铁、球晶石墨铸铁和SG铸铁。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Significance level | 显着性水平 |
The stated probability (risk) that a given test of significance will reject the hypothesis that a specified effect is absent when the hypothesis is true. 当假设为真时，给定的显著性检验将拒绝特定效应不存在的假设的所述概率（风险）。 |
| Mechanical alloying | 机械合金化 |
Production of alloys from powders by consolidation, e.g. hotpressing or extrusion, followed by hot and/or cold working and final annealing. Materials such as dispersion-strengthened alloys, high-temperature aluminium alloys, and amorphous alloys can be made in this way. 通过固结（例如热压或挤压）从粉末生产合金，然后进行热和/或冷加工和最终退火。用这种方法可以制造弥散强化合金、高温铝合金和非晶合金等材料。 |
| Permanent set | 永久变形 |
The deformation or strain remaining in a previously stressed body after release of load. 释放荷载后，先前受力物体中剩余的变形或应变。 |
| Thermal compressor | 热压缩机 |
1. (thermocompressor) A jet compressor used to boost the pressure of low-pressure waste or exhaust steam. 2. A device consisting of an absorber, a generator, a pump, and a throttling device, used instead of a mechanical vapour compressor in an absorption-cooling refrigeration system. 1.（热压缩机）用于提升低压废蒸汽或排气压力的喷射压缩机。2.一种由吸收器、发电机、泵和节流装置组成的装置，用于替代吸收冷却制冷系统中的机械蒸汽压缩机。 |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Deviation | 偏差 |
The difference between the actual value and the desired value of a controlled variable. 受控变量的实际值与期望值之间的差值。 |
| Sliding-vane compressor | 滑片压缩机 |
(rotary-vane compressor, vane compressor) A rotary compressor in which gas is compressed as the spaces between spring-loaded sliding vanes held in an offset rotor reduce as the rotor revolves within a cylindrical housing. （旋转叶片压缩机，叶片压缩机）一种旋转式压缩机，当转子在圆柱形外壳内旋转时，偏置转子中的弹簧加载滑动叶片之间的空间减小，从而压缩气体。 |
| Working stress (Unit Pa) | 工作应力（单位Pa） |
The stress under which a component or structure is designed to operate under normal conditions. 部件或结构设计为在正常条件下运行的应力。 |
| Cotter pin | 开口销 |
(cotter) 1. A tapered wedge or pin passing through a tapered slot or hole in one member and bearing against a second member to fix it in location. 2. A split cotter is commonly called a split pin. A pin with two legs. With legs together, the pin is placed through the hole in a clevis pin. The legs are then opened outward to prevent the cotter pin from backing out of the hole. The cotter pin, in turn, prevents the load-bearing clevis pin from backing out of its retaining hole. （开口）1.锥形楔子或销钉穿过一个构件中的锥形槽或孔，并支撑在第二个构件上以将其固定到位。2.开口开口通常称为开口销。相当于有两条腿的别针，将支腿放在一起，销钉穿过U形夹销上的孔。然后将支腿向外打开以防止开口销从孔中退出。开口销反过来防止承重U形夹销从其固定孔中退出。 |
| Kinetic energy | 动能 |
Energy that an object possesses because it is in motion. It is the energy given to an object to set it in motion. On impact, it is converted into other forms of energy such as strain, heat, sound and light. 物体因运动而拥有的能量。它是赋予物体使其运动的能量。撞击时，它被转换成其他形式的能量，如应变、热、声和光。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| Crest of screw thread | 螺纹牙顶 |
The top surface joining the two sides of flanks of a thread. 连接螺纹牙侧两侧的顶面。 |
| Chain | 链 |
A series of connected links, typically of steel. For lifting, pulling, securing, etc., each link is a closed loop, often in the form of a ring. For power transmission, the links are designed to mesh with the teeth of a sprocket wheel. In contrast to belt drives, chain drives tend to be employed in high-torque applications. 一系列连接的链接，通常是钢制的。对于提升、拉动、固定等，每个链节都是一个闭合环，通常呈环形。对于动力传输，链节设计为与链轮的齿啮合。与皮带传动相比，链传动往往用于高扭矩应用。 |
| Centrifugal compressor | 离心式压缩机 |
A compressor in which kinetic energy is added to a fluid by radial acceleration in an impeller and then converted into a pressure increase by flow though a diffuser. 一种压缩机，其中动能通过叶轮中的径向加速度添加到流体中，然后通过扩散器的流动转换为压力增加。 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Frequency | 频率 |
(temporal frequency, f) (Unit Hz) The number of cycles per second in an oscillation or the repetition rate for a cyclic process. （时间频率，f）（单位Hz）振荡中每秒的周期数或循环过程的重复率。 |
| Semi-rotary pump | 半回转泵 |
A form of self-priming pump, often hand-operated, suitable for pumping water and light oils such as diesel oil and petrol. As shown in the diagram, liquid is sucked into one side of the pump through flap valves and simultaneously ejected from the other side on one stroke. The sequence is reversed on each successive stroke. 一种自吸泵，通常是手动的，适用于泵送水和轻油，如柴油和汽油。液体通过翻板阀吸入泵的一侧，同时在一个冲程中从另一侧排出。在每个连续冲程上，顺序颠倒。 |
| Fahrenheit | 华氏度 |
The temperature scale based on the freezing point of water (32ºF) and the boiling point of water (212ºF). The interval between these points is divided into 180 equal parts. Although replaced by the Celsius scale, the Fahrenheit scale is still sometimes used for non-scientific measurements. 温标基于水的冰点（32ºF）和水的沸点（212ºF）。这些点之间的间隔被分成180等份。尽管被摄氏刻度所取代，华氏刻度有时仍用于非科学测量。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Conditioning heat treatment | 调质热处理 |
A preliminary heat treatment used to prepare a material for desired reaction to a subsequent heat treatment. For the term to be meaningful, the exact heat treatment must be specified. 用于制备材料的初步热处理，以便对随后的热处理进行所需的反应。为了使该术语有意义，必须指定确切的热处理。 |
| Honing | 珩磨 |
Honing is a controlled, low-speed sizing and surface-finishing process in which stock is removed by the shearing action to the bonded abrasive grains of a honing stone, or stick. Finish polishing of surfaces and cutting edges in which very fine abrasive powders, such as rouge, are employed. Honing is usually applied to cylindrical surfaces and lapping to flat, but the usage is not consistent. 珩磨是一种受控的低速尺寸和表面精加工工艺，其中通过对珩磨石或棒的粘结磨粒的剪切作用去除原料。表面和切削刃的精抛光，其中使用了非常细的研磨粉，例如胭脂。珩磨通常用于圆柱面，研磨至平面，但用法并不一致。 |
| Liquid nitriding | 液体氮化 |
A method of surface hardening in which molten nitrogen-bearing, fused-salt baths containing both cyanides and cyanates are exposed to parts at subcritical temperatures. 一种表面硬化方法，其中含有氰化物和氰酸盐的熔融含氮熔盐浴在亚临界温度下暴露于零件。 |
| Yielding | 屈服 |
Evidence of plastic deformation in structural materials. Also known as plastic flow or creep. 结构材料塑性变形的证据。也称为塑性流动或蠕变。 |
| Centrifugal | 离心式 |
Acting or moving in a direction away from the axis of rotation of a rotating body. 沿远离旋转体的旋转轴的方向作用或移动。 |
| Air-cooled condenser | 风冷冷凝器 |
A heat exchanger, in which the cooling medium is air, used to condense the exhaust steam from a steam turbine, the condensate being returned to the boiler. 一种热交换器，其中冷却介质为空气，用于冷凝蒸汽轮机排出的蒸汽，冷凝水返回锅炉。 |
| Fin | 翼 |
A thin projecting rib. 一根细长的凸肋。 |
| Venturi | 文丘里管 |
A convergent–divergent flow nozzle, usually circular in cross section, with a relatively short convergent section (the confuser) upstream of a throat followed by a gradually diverging section (the diffuser). Such nozzles usually have flanges at either end for installation in a pipeline. Applications include flow meters and ejectors. When a fluid flows through a convergent duct at subsonic speed, there is an increase in velocity accompanied by a decrease in pressure (Venturi effect). 收敛-发散流喷嘴，横截面通常为圆形，喉部上游具有相对较短的收敛段（扰流器），然后是逐渐发散段（扩散器）。这种喷嘴通常在两端都有法兰，以便安装在管道中。应用包括流量计和喷射器。当流体以亚音速流过收敛管道时，速度增加，压力降低（文丘里效应）。 |
| Hooke’s law | 胡克定律 |
Within the limit of proportionality, the extension of a material is proportional to the applied force. Approximately, it is the relationship between stress and strain in an elastic material when it is stretched. The law states that the stress (force per unit area) is proportional to the strain (a change in dimensions). The law, which holds only approximately and over a limited range, was discovered in 1676 by Robert Hooke. 在比例极限内，材料的延伸与所施加的力成比例。近似地说，它是弹性材料拉伸时应力和应变之间的关系。该定律指出，应力（单位面积的力）与应变（尺寸变化）成比例。该定律仅适用于有限的范围，由罗伯特·胡克于1676年发现。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| Densimeter | 密度计 |
An instrument used to determine the density or relative density of a solid or liquid. 用于测定固体或液体的密度或相对密度的仪器。 |
| Nautical mile (M) | 海里（M） |
A special unit of distance employed for marine and aerial navigation. The conversion to SI is 1 M = 1 852 m. 用于海上和空中导航的特殊距离单位。SI的转换为1M＝1852m。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Centrifugal fan | 离心风机 |
A machine with a rotor consisting of a number of blades mounted around a hub and used for moving air or other gases. The gas enters the rotor axially and is discharged radially at increased pressure. 一种带有转子的机器，转子由安装在轮毂周围的许多叶片组成，用于移动空气或其他气体。气体轴向进入转子并在增加的压力下径向排出。 |
| Coil spring | 螺旋弹簧 |
A spiral (‘clockwork’) or helical (cylindrical) spring. A spring steel wire wound in a spiral pattern. 螺旋（“发条”）或螺旋（圆柱形）弹簧。以螺旋状缠绕的弹簧钢丝。 |
| Constant-mesh gearbox | 恒啮合齿轮箱 |
A gearbox in which the pairs of gears giving different speed ratios are constantly in mesh, different ratios being obtained by connecting or disconnecting the relevant gear to the driving shaft. 一种齿轮箱，其中提供不同速比的齿轮对始终啮合，通过将相关齿轮连接或断开驱动轴获得不同的速比。 |
| Double aging | 双级时效 |
Employment of two different aging treatments to control the type of precipitate formed from a supersaturated matrix in order to obtain the desired properties. The first aging treatment, sometimes referred to as intermediate or stabilizing, is usually carried out at higher temperature than the second. 采用两种不同的时效处理来控制由过饱和基质形成的沉淀物类型，以获得所需的性能。第一次时效处理，有时称为中间处理或稳定处理，通常在比第二次更高的温度下进行。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Stress relieving | 应力消除 |
Heating to a suitable temperature, holding long enough to reduce residual stresses, and then cooling slowly enough to minimize the development of new residual stresses. 加热到合适的温度，保持足够长的时间以减少残余应力，然后缓慢冷却以尽量减少新残余应力的产生。 |
| Pulse | 脉冲 |
An increase or decrease in the magnitude of a physical quantity, such as pressure, voltage, or force, with a time scale short compared with other time scales in a process, after which there is a return to the original level. 物理量的大小的增加或减少，如压力、电压或力，与过程中的其他时间尺度相比，时间尺度较短，之后返回到原始水平。 |
| Thermal fatigue | 热疲劳 |
Fatigue resulting from the presence of temperature gradients that vary with time in such a manner as to produce cyclic stresses in a structure. 由于温度梯度的存在而产生的疲劳，温度梯度随时间变化，从而在结构中产生循环应力。 |
| Heat balance (heat budget) | 热平衡（热预算） |
An energy balance involving only heat transfer across the system boundary and the stored energy. 仅涉及跨系统边界的热传递和存储能量的能量平衡。 |
| Alpha iron | 阿尔法铁 |
The body-centered cubic form of pure iron, stable below 910 °C (1670 °F). 纯铁的体心立方形式，在910°C(1670°F)以下稳定。 |
| Dynamic compressor | 动态压缩器 |
A machine, such as a centrifugal or axial compressor, that compresses a gas by rotational rather than reciprocating motion. 一种机器，例如离心式或轴流式压缩机，通过旋转而不是往复运动来压缩气体。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Final annealing | 最终退火 |
An imprecise term used to denote the last anneal given to a nonferrous alloy prior to shipment. 一个不精确的术语，用于表示有色金属合金在装运前的最后一次退火。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Die screw | 模具螺丝 |
Tool used when threading cylindrical pieces beyond the capacity of a die plate. 对超出模板容量的圆柱件进行螺纹加工时使用的工具。 |
| Absolute temperature (Unit K) | 绝对温度（单位K） |
A temperature T measured relative to absolute zero, 0 K or −273.15°C, the lowest temperature achievable at which molecular motion vanishes so that a body would have zero heat energy. The kelvin is equal in magnitude to the degree Celsius (°C). The kelvin temperature scale (kelvin absolute temperature scale) is an absolute or thermodynamic temperature scale derived from the Celsius scale: T(K) = T(°C) + 273.15. The Rankine absolute scale is derived from the Fahrenheit scale such that T(R) = T(°F) + 459.67, i.e. a scale relative to 0 R or −459.67°F where R is the Rankine degree symbol and °F is the Fahrenheit symbol. 相对于绝对零、0K或0K测量的温度T−273.15°C，分子运动消失的最低温度，因此物体的热能为零。开尔文的大小等于摄氏度（℃）。开尔文温度标度（开尔文绝对温度标度）是从摄氏标度得出的绝对或热力学温度标度：T（K）=T（°C）+273.15。兰金绝对标度是从华氏标度得出，使得T（R）=T（°F）+459.67，即相对于0R或0R的标度−459.67°F，其中R是朗肯度符号，°F是华氏度符号。 |
| Absolute pressure | 绝对压力 |
1. The pressure measured relative to zero pressure (vacuum). 2. Gage pressure plus barometric pressure in the same units. 1.相对于零压力（真空）测量的压力。2.表压加上大气压力的单位相同。 |
| Butt joint | 对接接头 |
The end-to-end joining of two plates either by welding or by overlapping plates that are bolted or riveted. 通过焊接或通过螺栓或铆接的重叠板将两块板端对端连接。 |
| Homogeneous carburizing | 均匀渗碳 |
Use of a carburizing process to convert a low-carbon ferrous alloy to one of uniform and higher carbon content throughout the section. 使用渗碳工艺将低碳铁合金转化为整个截面中碳含量均匀且较高的合金。 |
| Salt-velocity meter | 盐速计 |
A volume flow meter based on detecting the transit time for a small quantity of salt or radioactive isotope in a flow by measuring electrical conductivity or radiation level. 一种体积流量计，通过测量电导率或辐射水平来检测流量中少量盐或放射性同位素的渡越时间。 |
| Strength (Unit Pa) | 强度（单位Pa） |
The maximum stress, in tension, compression, shear, or combinations thereof, that may be monotonically applied to a material, component, or structure before failure (defined as fracture, yielding, buckling, etc. as appropriate). 在破坏前（视情况定义为断裂、屈服、屈曲等），材料、部件或结构在拉伸、压缩、剪切或其组合中可能单调施加的最大应力。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Cavitation | 空蚀空化 |
The formation of vapour- or gas-filled cavities in a liquid due to reduction of the local pressure, often due to acceleration of the fluid, such as in flow through a convergent nozzle. If there is no dissolved gas in the liquid, vaporous cavitation occurs when the pressure falls below the saturated vapour pressure. If the bubbles are formed due to high temperature, the process is termed boiling. If there is dissolved gas, gaseous cavitation occurs due to pressure reduction, temperature increase, or diffusion (degassing). At the tips of marine propellers and in hydraulic machinery, the collapse of cavitation bubbles can cause noise and vibration and lead to surface damage in the form of pitting. 由于局部压力降低而在液体中形成充满蒸汽或气体的空腔，通常原因是流体的加速，例如收敛喷嘴的流动。如果液体中没有溶解气体，当压力降至饱和蒸汽压力以下时，会发生蒸汽空化。如果气泡是由于高温形成的，则该过程称为沸腾。如果存在溶解气体，则由于压力降低、温度升高或扩散（脱气），会发生气穴。在船用螺旋桨尖端和液压机械中，空化气泡的破裂可能会引起噪音和振动，并导致以点蚀形式出现的表面损坏。 |
| Flange | 法兰 |
Flange refers to a head style for bolts where there is a circular ‘flange’ under the head that acts like a washer to distribute a load. A flange is a projected flat rim or collar. 1. Annular rims at the ends of pipes (flanged pipe) or shafts by which they may be coupled together using bolts that pass through holes in the flanges (flange coupling, flange union), or by toggle clamps around the periphery. 2. An extended rim on a wheel that positions it laterally on a track. Commonly used for railway rolling stock. 3. The top and bottom parts of an I-beam. 法兰是指螺栓的头部样式，其中头部下方有一个圆形“法兰”，其作用类似于垫圈以分配载荷。凸缘是凸出的平轮辋或凸缘。1.管道（法兰管）或轴端部的环形边缘，通过这些边缘，可以使用穿过法兰孔的螺栓（法兰联轴器、法兰接头）或通过周边的肘节夹将管道连接在一起。2.车轮上的延伸轮辋，将其横向定位在轨道上。通常用于铁路车辆。3.工字梁的顶部和底部。 |
| Dynamic modulus | 动态模量 |
The ratio of stress to strain under cyclic conditions (calculated from data obtained from either free or forced vibration tests, in shear, compression, or tension). 循环条件下的应力与应变之比（根据在剪切、压缩或拉伸中的自由或强制振动测试中获得的数据计算得出）。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Surface roughness (roughness) | 表面粗糙度 |
The small-scale, irregular peaks and troughs in a solid surface which are quantified using a surface analyser. Roughness may be a consequence of wear and corrosion, or of the manufacturing process. It leads to increased friction in solid– solid contact or fluid flow over a surface. Errors of form and waviness are excluded, but surface texture includes roughness and waviness. Surface topography incorporates the small-scale, three-dimensional geometry of a surface including surface roughness, machined, and etched features, typically at sub-mm scales. 固体表面中的小尺度不规则峰谷，使用表面分析仪进行量化。粗糙度可能是磨损和腐蚀或制造过程的结果。它会导致表面上的固-固接触或流体流动中的摩擦增加。不包括形状和波纹度误差，但表面纹理包括粗糙度和波纹度。表面形貌包括表面的小尺度三维几何结构，包括表面粗糙度、机加工和蚀刻特征，通常为亚毫米尺度。 |
| Flange bolt | 法兰螺栓 |
A bolt with a built in washer-like flange just below the head. 在头部下方带有内置垫圈状法兰的螺栓。 |
| Threshold stress for stress-corrosion cracking (σth) | 应力腐蚀开裂阈值应力（σth） |
An experimentally determined critical gross-section stress below which stress-corrosion cracking will not occur under specified test conditions. 实验确定的临界总截面应力，低于该应力，在规定的试验条件下不会发生应力腐蚀开裂。 |
| Pin expansion test | 插头膨胀试验 |
A test for determining the ability of a tube to be expanded or for revealing the presence of cracks or other longitudinal weaknesses in it, made by forcing a tapered pin into the open end of the tube, similar to flare test. 通过将锥形销压入管道开口端来确定管道膨胀能力或揭示其存在裂纹或其他纵向缺陷的试验，类似于扩口试验。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Slug wrench | 缓动扳手 |
A box wrench with an anvil on the end of the handle. Torque is produced by striking the anvil with a sledge hammer. 柄端有铁砧的套筒扳手。扭矩是通过用大锤敲击铁砧产生的。 |
| Shoulder screw | 轴肩螺钉 |
A screw having two or more diameters or shoulders and commonly used for supporting levers and other machine parts that have to operate freely. 一种具有两个或两个以上直径或轴肩的螺钉，通常用于支撑杠杆和其他必须自由操作的机器部件。 |
| Stress-strain diagram | 应力-应变图 |
A graph in which corresponding values of stress and strain are plotted against each other. Values of stress are usually plotted vertically(ordinates or y-axis) and values of strain horizontally (abscissas or xaxis). Also known as deformation curve and stress-strain curve. 对应的应力和应变值相对绘制的图表。应力值通常垂直绘制（纵坐标或y轴），应变值水平绘制（横坐标或X轴）。也称为变形曲线和应力-应变曲线。 |
| Tension | 拉伸 |
The force or load that produces elongation. 1. The condition in a bar, belt, cable, spring, string, wire, etc. that is being pulled from either end. 2. (tensile force) (unit N) The force associated with tension as in (1). It is measured by a tension meter. 伸长力产生伸长的力或载荷。1.从两端拉出的杆、带、电缆、弹簧、线、线等的状态。2.（张力）（单位N）与张力相关的力。 |
| Composite material | 复合材料 |
(composite structure) A general term used of two or more materials or structures acting in combination (e.g. concrete, reinforced concrete, filamentreinforced polymers, laminated materials, particulate-reinforced materials, flitched beams), resulting in values of strength, stiffness, or toughness greater than the base matrix material alone. （复合结构）用于组合作用的两种或多种材料或结构的通用术语（例如混凝土、钢筋混凝土、纤维增强聚合物、层压材料、颗粒增强材料、切割梁），从而产生强度、刚度或韧性值大于单独的基体材料。 |
| Coefficient of cubic expansion | 立方膨胀系数 |
The fractional increase in volume per unit temperature rise. 每单位温度升高的体积增加分数。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Vibrograph | 示振器 |
An instrument that records vibrations in a system over time. 记录系统随时间变化的振动的仪器。 |
| Rated power (Unit kW or hp) | 额定功率（单位：千瓦或马力） |
(rated capacity, rated horsepower) The maximum power output that can be sustained continuously for any power-producing machine or system, such as an engine or a power plant. （额定容量、额定马力）任何发电机器或系统（如发动机或发电厂）可连续维持的最大功率输出。 |
| Impact | 撞击 |
Sudden loading of a body or component, as in a vehicle collision or striking by a hammer. 物体或部件的突然加载，如车辆碰撞或锤击。 |
| Transfer moulding | 转移模塑 |
(resin-transfer moulding, RTM) A method of compression moulding polymers in which the dies are closed before the operation starts. （树脂传递模塑，RTM）一种对聚合物进行压缩模塑的方法，其中模具在操作开始前关闭。 |
| Ratchet marks | 棘轮痕 |
Lines on a fatigue fracture surface that result from the intersection and connection of fatigue fractures propagating from multiple origins. Ratchet marks are parallel to the overall direction of crack propagation and are visible to the unaided eye or at low magnification. 疲劳断裂面上由从多个源头传播的疲劳断裂的交叉和连接产生的线。棘轮标记与裂纹扩展的整个方向平行，肉眼或低倍镜下均可看到。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Steady pin | 定位销 |
A dowel, key, or pin that prevents a pulley from turning on its shaft. 防止滑轮在其轴上转动的销钉、键或销。 |
| Maximum stress (Smax) | 最大应力（Smax） |
The stress having the highest algebraic value in the stress cycle, tensile stress being considered positive and compressive stress negative. The nominal stress is used most commonly. 在应力循环中具有最高代数值的应力，拉应力被认为是正的，压应力被认为是负的。名义应力是最常用的。 |
| Vapour | 蒸气 |
The gas-like phase of a substance at a temperature below its critical point. A vapour can be condensed to a liquid or a solid by increasing its pressure or reducing its temperature. 温度低于临界点的物质的类气相。蒸汽可以通过增加压力或降低温度冷凝成液体或固体。 |
| Captive nut | 松脱螺母 |
A nut attached loosely or rigidly to a sheet member that is too thin to thread and which engages with a cap screw. 松脱地或刚性地连接到薄板构件上的螺母，该螺母太薄而无法拧入，并与带帽螺钉接合。 |
| Strain gage | 应变计 |
A device for measuring small amounts of strain produced during tensile and similar tests on metal. A coil of fine wire is mounted on a piece of paper, plastic, or similar carrier matrix (backing material), which is rectangular in shape and usually about 25 mm (1.0 in.) long. This is glued to a portion of metal under test. As the coil extends with the specimen, its electrical resistance increases in direct proportion. This is known as bonded resistance-strain gage. Other types of gages measure the actual deformation. Mechanical, optical, or electronic devices are sometimes used to magnify the strain for easier reading. 一种测量金属拉伸和类似试验中产生的少量应变的装置。将一卷细线安装在一张纸、塑料或类似载体基质（背衬材料）上，该载体基质呈矩形，通常约25mm（1.0in.）长，这是粘在测试金属的一部分。随着线圈随试样延伸，其电阻成正比增加，这被称为粘结电阻应变计。其他类型的量规测量实际变形。机械、光学或电子设备有时用于放大应变以便于读取。 |
| Fastener quality | 紧固件质量 |
A fastener’s adherence to its specification for dimensional tolerances, mechanical properties, and other requirements stated under applicable standards. 紧固件对尺寸公差、机械性能和适用标准规定的其他要求的规范的遵守情况。 |
| Oxidizing agent | 氧化剂 |
A compound that causes oxidation, thereby itself becoming reduced. 一种引起氧化从而自身被还原的化合物。 |
| Slip line | 滑移线 |
The trace of the slip plane on a viewing surface; the trace is usually observable only if the surface has been polished before deformation. The usual observation on metal crystals (under the light microscope) is of a cluster of slip lines known as a slip band. 滑动平面在观察表面上的轨迹；只有在变形前对表面进行抛光，才能观察到痕迹。通常对金属晶体的观察（在光学显微镜下）是一组称为滑移带的滑移线。 |
| Ductile fracture | 韧性断裂 |
Fracture characterized by tearing of metal accompanied by appreciable gross plastic deformation and expenditure of considerable energy. A fracture of a component or structure which is preceded by extensive ductile deformation so that the broken pieces cannot be re-fitted to regain the original size and shape of the component or structure. 以金属撕裂为特征的断裂，伴随着明显的总塑性变形和相当大的能量消耗。一种部件或结构的断裂，在断裂前会发生大范围的延性变形，从而使断裂的碎片无法重新装配以恢复部件或结构原来的尺寸和形状。 |
| Caustic quenching | 苛性淬火 |
Quenching with aqueous solutions of 5 to 10% sodium hydroxide (NaOH). 用5%至10%氢氧化钠（NaOH）水溶液淬灭。 |
| Heat-capacity rate (c) (Unit W/K) | 热容率（c）（单位W/K） |
For fluid flow in a duct with mass flow rate ṁ, the product ṁC where C is the specific-heat capacity, at constant pressure (CP) in the case of a gas. 对于质量流量为ṁ的管道中的流体流动，乘积ṁC其中C是比热容，在气体的情况下为恒定压力（CP）。 |
| Equilibrium diagram | 平衡图 |
A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant. 在完全平衡条件下，合金系统中相场的温度、压力和成分极限的图形表示。在金属系统中，压力通常被认为是恒定的。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Screw feeder | 螺旋给料机 |
A mechanism for handling bulk materials in which a rotating helicoidal screw moves the material axially forward. Similar to a screw conveyor, but required to discharge material at a controlled rate very accurately. It operates with the screw completely full. 一种用于处理散装物料的机构，其中旋转的螺旋螺杆使物料轴向向前移动。类似于螺旋输送机，但需要以受控速率非常精确地排出物料。它在螺杆完全充满的情况下运行。 |
| Longitudinal direction | 纵向 |
The principal direction of flow in a worked metal. See also normal direction and transverse direction. 加工金属中的主要流动方向。另请参见法向和横向。 |