| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Vibrograph | 示振器 |
An instrument that records vibrations in a system over time. 记录系统随时间变化的振动的仪器。 |
| Machine screw | 机械螺丝 |
A countersunk, slotted screw with machined threads such as are found on bolts. A relatively small screw, usually less than 20 mm in diameter, with the thread running along the whole length up to the head, intended to be screwed into threaded holes. If inserted through plain holes in assembled parts and held together by a nut, an undesirable contact surface of threads bearing against the surface of a hole results. 带有机加工螺纹的沉头开槽螺钉，如螺栓上的螺纹。一种相对较小的螺钉，直径通常小于20毫米，螺纹沿整个长度一直延伸到头部，用于拧入螺纹孔中。如果通过装配零件上的平孔插入并用螺母固定在一起，则会导致螺纹与孔表面接触不良。 |
| Edge distance | 边距 |
The distance from the edge of a bearing specimen to the center of the hole in the direction of applied force. 在作用力方向上，从轴承试样的边缘到孔中心的距离。 |
| Shear modulus (G) | 剪切模量（G） |
The ratio of shear stress to the corresponding shear strain for shear stresses below the proportional limit of the material. Values of shear modulus are usually determined by torsion testing. Also known as modulus of rigidity. 对于低于材料比例极限的剪切应力，剪切应力与相应剪切应变之比。剪切模量值通常通过扭转试验确定。也称为刚度模量。 |
| Brittle lacquer coating | 脆性漆涂层 |
A lacquer that, when painted on to an unloaded body, reveals the direction of maximum tension stresses from the pattern of cracking produced in the lacquer when the body is loaded. 一种漆，当涂在未加载的车身上时，从车身加载时在漆中产生的裂纹图案中显示出最大拉应力的方向。 |
| Poisson’s ratio (ν) | 泊松比（ν） |
The absolute value of the ratio of transverse (lateral) strain to the corresponding axial strain resulting from uniformly distributed axial stress below the proportional limit of the material. 横向（侧向）应变与相应轴向应变之比的绝对值，该比值由低于材料比例极限的均匀分布的轴向应力产生。 |
| U-bend | U形管 |
U-bend A 180° bend in a pipe. 180°弯曲的管道。 |
| Testing machine (load-measuring type) | 试验机（负载测量型） |
A mechanical device for applying a load (force) to a specimen. 向试样施加载荷（力）的机械装置。 |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| Thread run-out | 螺纹耗尽 |
That portion of the threads which are not cut or rolled full depth, but which provide the transition between full-depth threads and the body or head. Officially called thread washout or vanish, although the term run-out is more popular. (Run-out is officially reserved for rotational eccentricity, as defined by total indicator readings or the like.) 未全深度切割或轧制的螺纹部分，但提供全深度螺纹与主体或头部之间的过渡。官方称之为螺纹冲蚀或消失，但术语“耗尽”更为流行。（跳动是官方为旋转偏心度保留的，由总指示器读数等定义。） |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Stress cracking | 应力开裂 |
A family of failure modes, each of which involves high stress and chemical action. The family includes Hydrogen embrittlement, Stress corrosion cracking, stress embrittlement, and hydrogen-assisted stress corrosion. 一系列失效模式，每种模式都涉及高应力和化学作用。该系列包括氢脆、应力腐蚀开裂、应力脆化和氢辅助应力腐蚀。 |
| Vibration-testing machine (vibrator) | 振动试验机（振动器） |
Any machine that subjects components or systems to vibration at known amplitudes and frequencies in order to determine the response. vibratory equipment Vibrating process equipment, such as shakers, used to separate small and large particles, or feeders to supply particulate or granular material that may otherwise clog. 使部件或系统以已知振幅和频率振动以确定响应的任何机器。振动设备振动工艺设备，如用于分离小颗粒和大颗粒的振动筛，或用于供应可能堵塞的颗粒或粒状材料的给料机。 |
| Thermodynamic process | 热力学过程 |
A change in equilibrium state undergone by a quantity of matter or a system. 一定量的物质或系统所经历的平衡状态的变化。 |
| Fatigue strength | 疲劳强度 |
The stress to which a metal can be subjected for a specified number of cyclic changes of stress. The maximum stress that can be sustained for a specified number of cycles without failure. The value of the maximum stress and the stress ratio also should be stated. 金属在指定数量的应力循环变化下可以承受的应力。可以在指定的循环次数内持续而不失效的最大应力。还应说明最大应力值和应力比。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Pitch diameter | 中径 |
For screw threads, the diameter of an imaginary cylinder, the surface of which would pass through the threads at such points that would make the width of the groove and width of the land equal to one half the pitch. 对于螺纹，指一个假想圆柱体的直径，其表面将在使凹槽宽度和焊盘宽度等于螺距一半的点穿过螺纹。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| Wrought iron | 锻铁 |
A highly ductile (but anisotropic) type of iron containing elongated slag fibres that resulted from the method of manufacture in which excess carbon in pig iron was burnt and worked out. The yield strength is some 200 MPa, tensile strength 320 MPa, and reduction of area on a 50-mm gauge length up to 35%. Now replaced by steel. 一种高韧性（但各向异性）的铁，含有细长的矿渣纤维，由生铁中多余的碳燃烧和加工的制造方法产生。屈服强度约为200MPa，抗拉强度为320MPa，50mm标距上的面积缩减率高达35%。现在被钢所取代。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Thumb screw | 蝶形螺钉 |
A type of screw having a winged or knurled head for turning by hand when a quick and light clamping effect is desired. 一种螺钉，具有翼形或滚花头，当需要快速、轻夹紧效果时，可手动转动。 |
| Flame straightening | 火焰矫直 |
Correcting distortion in metal structures by localized heating with a gas flame. 通过使用气体火焰进行局部加热来纠正金属结构的变形。 |
| Clearance angle | 后角 |
(relief angle) (Unit °) The angle between the underneath or flank of a cutting tool and the machined surface. （后角）（单位°）切削刀具的底部或侧面与加工表面之间的角度。 |
| Rockwell superficial hardness test | 洛氏表面硬度试验 |
Same as Rockwell hardness test, except that smaller minor and major loads are used. 与洛氏硬度测试相同，只是使用较小的次要载荷和主要载荷。 |
| Biomedical engineering | 生物医学工程 |
The application of engineering principles and methodology to the medical field. Examples involving mechanical engineering include the design and construction of artificial limbs and hearts, heart-lung machines, prosthetic eyes, and orthopaedic implants such as hip joints and pins to stabilize fractured bones. 工程原理和方法在医学领域的应用。涉及机械工程的例子包括假肢和心脏、心肺机、假眼和骨科植入物（如髋关节和用于稳定骨折骨骼的销钉）的设计和建造。 |
| Thermal energy (heat energy) (Unit J) | 热能（单位：J） |
The sensible and latent forms of internal energy. 内能的感知和潜在形式。 |
| Pressure ratio | 压力比 |
One pressure divided by another which may be a reference pressure. In many flow and thermodynamic processes, the pressure ratio is more important than the absolute pressure levels. For example, in compressible gas flow the Mach number is determined by the ratio of the stagnation pressure to the static pressure. 一个压力除以另一个压力，该压力可以是参考压力。在许多流动和热力学过程中，压力比比绝对压力水平更重要。例如，在可压缩气流中，马赫数由停滞压力与静压之比决定。 |
| Cathode | 阴极 |
That electrode in a battery or corrosion cell which attracts electrons. 电池或腐蚀电池中吸引电子的电极。 |
| Blow moulding | 吹塑 |
The manufacture of hollow polymer objects (e.g. bottles) by expanding, with internal air pressure, a tube sealed at one end (parison) against the walls of a cavity mould. 通过使用内部气压使一端密封的管子（型坯）靠在型腔模具的壁上膨胀来制造中空聚合物物体（例如瓶子）。 |
| Diesel engine | 柴油发动机 |
(compression–ignition engine) A piston engine operating on the Diesel cycle in which the air is compressed to a temperature above the autoignition temperature of the fuel and combustion is initiated as the fuel is injected into the hot air. Diesel engines operate at higher compression ratios (typically in the range 12 to 24) than petrol engines. Although named after Rudolf Diesel, the inventor, Diesel engine is often spelled with a lower case d, contrary to normal practice. （压燃式发动机）在柴油循环中运行的活塞式发动机，在该循环中，空气被压缩至高于燃料自燃温度的温度，当燃料喷射到热空气中时，燃烧开始。柴油发动机在比汽油发动机更高的压缩比下运行（通常在12到24的范围内）。虽然以发明人鲁道夫·迪塞尔命名，但迪塞尔发动机通常拼写为小写d，这与正常做法相反。 |
| Alloying element | 合金元素 |
Component added deliberately with the aim of improving the properties of an alloy. Alloying elements can affect the existence range of equilibrium phases present in an unalloyed material, or lead to the occurrence of new phases, or both. In addition, alloying elements strongly affect the kinetics of phase transformations and thus the microstructure formation in alloyed materials. 为改善合金性能而有意添加的成分。合金元素可以影响非合金材料中存在的平衡相的存在范围，或导致新相的出现，或两者兼而有之。此外，合金元素强烈影响相变动力学，从而影响合金材料的微观结构形成。 |
| Effective radius of nut, bolt head, or threads | 螺母、螺栓头或螺纹的有效半径 |
Distance between the geometric center of the part and the circle of points through which the resultant contact forces between mating parts passes. Must be determined by integration. 零件几何中心与配合零件之间的合力通过的点圆之间的距离。必须通过积分来确定。 |
| Assembly line | 流水线 |
A system of mass production in which work is moved progressively from one operation to another, ultimately to give the final complete product. 一种大规模生产系统，其中工作逐渐从一个操作转移到另一个操作，最终得到完整产品。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Coefficient of cubic expansion | 立方膨胀系数 |
The fractional increase in volume per unit temperature rise. 每单位温度升高的体积增加分数。 |
| Bond strength (Unit Pa) | 结合强度（单位Pa） |
The tensile, compressive or shear stress at which joints fail, e.g. by fracture or excessive deformation. 接头失效的拉伸、压缩或剪切应力，例如断裂或过度变形。 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Temper | 回火 |
(1) In heat treatment, reheating hardened steel or hardened cast iron to some temperature below the eutectoid temperature for the purpose of decreasing hardness and increasing toughness. The process also is sometimes applied to normalized steel. (2) In tool steels, temper is sometimes used, but inadvisedly, to denote the carbon content. (3) In nonferrous alloys and in some ferrous alloys (steels that cannot be hardened by heat treatment), the hardness and strength produced by mechanical or thermal treatment, or both, and characterized by a certain structure, mechanical properties, or reduction in area during cold working. （1）在热处理中，将硬化钢或硬化铸铁重新加热到共析温度以下的温度，以降低硬度和增加韧性。该工艺有时也适用于正火钢。（2）在工具钢中，有时使用回火来表示碳含量，但这是不恰当的。（3）在非铁合金和一些铁合金（不能通过热处理硬化的钢）中，通过机械或热处理或两者产生的硬度和强度，其特征是在冷加工过程中具有一定的结构、机械性能或面积减小。 |
| Flame hardening | 火焰硬化 |
A process for hardening the surfaces of hardenable ferrous alloys in which an intense flame is used to heat the surface layers above the upper transformation temperature, whereupon the workpiece is immediately quenched. 一种用于硬化可硬化铁合金表面的工艺，其中使用强烈的火焰将表面层加热到转变温度上限以上，然后立即对工件进行淬火。 |
| Eutectoid | 共析 |
(1) An isothermal reversible reaction in which a solid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectoid point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectoid reaction. （1）一种等温可逆反应，其中固溶体在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）具有平衡图上共析点所示成分的合金。（3）由共析反应形成的混合固体成分的合金结构。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Gasket stress | 垫片应力 |
The contact stress exerted on the gasket by the joint members. 连接件施加在垫片上的接触应力。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Crosshead | 十字头 |
1. A reciprocating member, sliding between guides, to which the piston rod is firmly attached on one side and to which the connecting rod is pinned on the other for the conversion of reciprocating into rotary motion. 2. The moveable beam in early designs of mechanical testing machines. 3. A screwhead having slots in a + shape that takes a mating screwdriver. 1.一种往复式构件，在导轨之间滑动，活塞杆一侧固定在其上，连杆另一侧固定在该构件上，用于将往复式运动转换为旋转运动。2.机械试验机早期设计中的活动梁。3.一种螺钉头，其具有采用配合螺丝刀的+形槽。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Compression fitting | 压缩接头 |
A screwed joint for pipework made resistant to leakage by permanent deformation of a closely-fitting ring, called a ferrule or olive, on tightening. 一种用于管道的螺纹接头，通过紧密配合的环（称为套圈或橄榄形）在拧紧时的永久变形来防止泄漏。 |
| Tensometer | 拉力计 |
A bench-top device, used to perform tension and compression tests. 用于进行拉伸和压缩试验的台式装置。 |
| Standard hole | 标准孔 |
A hole in a workpiece bored to a specified tolerance where clearance with a shaft is accomplished by allowance on the shaft. A standard shaft is machined to a specified tolerance where clearance with a hole is accomplished by allowance on the hole. 工件上的孔，钻孔至规定公差，其中与轴的间隙通过轴上的余量来实现。标准轴加工至规定公差，其中与孔的间隙通过孔上的公差实现。 |
| Diffusion | 扩散 |
(1) Spreading of a constituent in a gas, liquid, or solid, tending to make the composition of all parts uniform. (2) The spontaneous movement of atoms or molecules to new sites within a material. （1） 一种成分在气体、液体或固体中的扩散，趋于使所有部分的成分均匀。（2） 原子或分子自发运动到材料内的新位置。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Isothermal annealing | 等温退火 |
Austenitizing a ferrous alloy and then cooling to and holding at a temperature at which austenite transforms to a relatively soft ferrite carbide aggregate. 将铁合金奥氏体化，然后冷却至奥氏体转变为相对软的铁素体碳化物集合体的温度并保持该温度。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Fatigue failure | 疲劳失效 |
Failure that occurs when a specimen undergoing fatigue completely fractures into two parts or has softened or been otherwise significantly reduced in stiffness by thermal heating or cracking. 当经历疲劳的试样完全断裂成两部分或因热加热或开裂而软化或刚度显着降低时发生的失效。 |
| Malleable cast iron | 可锻铸铁 |
A cast iron made by prolonged annealing of white cast iron in which decarburization or graphitization, or both, take place to eliminate some or all of the cementite. The graphite is in the form of temper carbon. If decarburization is the predominant reaction, the product will exhibit a light fracture surface, hence, “whiteheart malleable;” otherwise, the fracture surface will be dark, hence, “blackheart malleable.” Ferritic malleable has a predominantly ferritic matrix; pearlitic malleable may contain pearlitic, spheroidite or tempered martensite depending on heat treatment and desired hardness. 白口铸铁一种通过长时间退火制成的铸铁，脱碳，石墨化，或两者都发生，以消除部分或全部渗碳体。石墨是回火碳的形式。如果脱碳是主要反应，产品将呈现出较轻的断裂表面，“白心可锻”。否则，断裂表面将变暗，“黑心可锻”。铁素体可锻性材料主要为铁素体基体；根据热处理和所需硬度，珠光体可锻材料可能包含珠光体、球状体或回火马氏体。 |
| Flame annealing | 火焰退火 |
Annealing in which the heat is applied directly by a flame. 通过火焰直接加热的退火。 |
| Lap joint | 搭接接头 |
A riveted, welded, or bonded connection between two plates made by overlapping one plate above the other. Lap joints having plates above and below a butt joint avoid the bending moment associated with a simple lap joint. 两块板之间的铆接、焊接或粘结连接，通过将一块板重叠在另一块板上而形成。对接接头上方和下方具有板的搭接接头避免了与简单搭接接头相关的弯矩。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Valve plug | 阀塞 |
A conical or cylindrical plug, in which there are transverse holes, in a valve, such as a plug valve. Flow through the holes occurs when the plug is rotated. 阀门中的圆锥形或圆柱形阀塞，其中有横向孔，如旋塞阀。旋转阀塞时，会发生通过孔的流动 |
| Compression crease | 压缩折痕 |
A crease formed during the compression of composites having a high volume fraction of filaments. These composites fail in compression by forming a crease at an angle to the loading axis. 在压缩具有高体积分数长丝的复合材料期间形成的折痕。这些复合材料通过形成与加载轴成一定角度的折痕而在压缩中失效。 |
| Fin | 翼 |
A thin projecting rib. 一根细长的凸肋。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Multiple threaded screw | 多螺纹螺钉 |
A screw with two or more threads cut around the periphery of the workpiece to provide an increased lead with a specified pitch. 一种螺钉，具有围绕工件周边切割的两个或多个螺纹，以提供具有指定螺距的增加的导程。 |
| Initial preload | 初始预载 |
The tension created in a single bolt as it is tightened. Will usually be modified by subsequent assembly operations or by in-service loads and conditions. 拧紧单个螺栓时产生的张力。通常会通过后续的装配操作或在役负载和条件进行修改。 |
| Austenitizing | 奥氏体化 |
Forming austenite by heating a ferrous alloy into the transformation range (partial austenitizing) or above the transformation range (complete austenitizing). When used without qualification, the term implies complete austenitizing. 通过将铁合金加热到转变范围（部分奥氏体化）或高于转变范围（完全奥氏体化）来形成奥氏体。当不加限定地使用时，该术语意味着完全奥氏体化。 |
| Coil spring | 螺旋弹簧 |
A spiral (‘clockwork’) or helical (cylindrical) spring. A spring steel wire wound in a spiral pattern. 螺旋（“发条”）或螺旋（圆柱形）弹簧。以螺旋状缠绕的弹簧钢丝。 |
| Creep fatigue | 蠕变疲劳 |
The effects of combined creep and fatigue at high homologous temperatures in metals, and in other materials such as polymers having time-dependent behaviour. 金属和其他材料（例如具有时间相关行为的聚合物）在高同源温度下的组合蠕变和疲劳的影响。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| Spring constant | 弹簧常数 |
The ratio between the forces exerted on a spring (or a bolt) and the deflection thereof. Has the dimensions of force per unit change in length (e.g., lb=in.). Also called Stiffness. 施加在弹簧（或螺栓）上的力与其挠度之间的比率。具有每单位长度变化的力的尺寸（例如lb=in.）。也称为刚度。 |
| Pump | 泵 |
A machine designed to cause a liquid, gas, vapour, or slurry to flow due to the reciprocating motion of pistons, rotation of vanes, or rotation of an impeller. 通过活塞的往复运动、叶片的旋转或叶轮的旋转而使液体、气体、蒸汽或泥浆流动的机器。 |
| Ductility | 延展性 |
The ability of a material to deform plastically before fracturing. Measured by elongation or reduction in area in a tensile test, by height of cupping in a cupping test, or by the radius or angle of bend in a bend test. 材料在断裂前发生塑性变形的能力。通过拉伸试验中的伸长率或面积减少量、杯突试验中的杯突高度或弯曲试验中的弯曲半径或角度来测量。 |
| Torque arm | 扭力臂 |
A bar fixed at one end used to resist torque applied at the other, for example by an electric drill. 固定在一端的杆，用于抵抗施加在另一端的扭矩，如电钻。 |
| Tangent screw | 微动螺旋 |
A worm screw used to adjust measuring instruments such as sextants and vernier callipers. 用于调整六分仪和游标卡尺等测量仪器的蜗杆。 |
| Radiator | 散热器 |
A heat exchanger used to transfer thermal energy from one fluid to another for heating or cooling purposes. Despite the name, the principal mode of heat transfer is convection rather than radiation. In motor vehicles, water circulated through the engine block is cooled as it flows through the tubes of an air-cooled heat exchanger. In domestic radiators, hot water from a boiler is circulated through a heat exchanger with a large surface area which transfers heat to the surrounding air. 一种热交换器，用于将热能从一种流体传递到另一种流体，用于加热或冷却。尽管有这个名字，但热传递的主要方式是对流而不是辐射。在机动车辆中，通过发动机缸体循环的水在流经风冷热交换器的管道时被冷却。在家用散热器中，来自锅炉的热水通过具有大表面积的热交换器循环，该热交换器将热量传递给周围的空气。 |
| Forced-air quench | 强制空气淬火 |
A quench utilizing blasts of compressed air against relatively small parts such as a gear. 利用压缩空气冲击相对较小的零件（例如齿轮）进行的淬火。 |
| Stress difference (Unit Pa) | 应力差（单位Pa） |
The algebraic difference between the largest and least principal stresses in a loaded body, equal to twice the greatest shear stress in the system. For σ1 > σ2 > σ3, it is given by (σ1 − σ3). 载荷体中最大和最小主应力之间的代数差，等于系统中最大剪应力的两倍。由（σ1− σ3).，可得σ1＞σ2＞σ3。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Plane strain | 平面应变 |
The stress condition in linear-elastic fracture mechanics in which there is zero strain in a direction normal to both the axis of applied tensile stress and the direction of crack growth (i.e., parallel to the crack front); most nearly achieved in loading thick plates along a direction parallel to the plate surface. Under plane-strain conditions, the plane of fracture instability is normal to the axis of the principal tensile stress. 线弹性断裂力学中的应力条件，其中在垂直于施加拉应力轴和裂纹扩展方向（即平行于裂纹前沿）的方向上存在零应变；最接近于沿平行于板表面的方向加载厚板。在平面应变条件下，断裂失稳平面垂直于主拉应力轴。 |
| Oxidized surface (on steel) | 氧化表面（在钢上） |
Surface having a thin, tightly adhering, oxidized skin (from straw to blue in color), extending in from the edge of a coil or sheet. Sometimes called annealing border. 表面具有薄的、紧密粘附的氧化皮（从稻草色到蓝色），从线圈或薄片的边缘延伸。有时称为退火边界。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Hypereutectic alloy | 过共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of alloying element compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，任何合金，其组成与共晶组成相比具有过量的合金元素，并且其平衡微观结构包含一些共晶结构。 |
| Strength of bolt | 螺栓强度 |
An ambiguous term which can mean Ultimate strength or Proof load or Endurance limit or Yield strength. 一个模棱两可的术语，可表示极限强度或验证荷载或耐久极限或屈服强度。 |
| Cylinder head | 气缸盖 |
The machined casting, typically of aluminium alloy or cast iron, that fits above the cylinder block of a piston engine and closes off the cylinders. It normally includes part of the combustion chambers and holes for the valves and spark plugs. 活塞式发动机缸体上方的机械铸件，通常由铝合金或铸铁制成，用于封闭气缸。它通常包括燃烧室的一部分以及阀门和火花塞的孔。 |
| R-curve/Resistance curve | 阻力曲线 |
In linear-elastic fracture mechanics, a plot of crack-extension resistance as a function of stable crack extension, which is either the difference between the physical crack size, or the effective crack size, and the original crack size. R-curves normally depend on specimen thickness and, for some materials, on temperature and strain rate. An increase in fracture toughness with crack propagation shown by rising plots of toughness vs growing crack length. 在线弹性断裂力学中，作为稳定裂纹扩展函数的裂纹扩展阻力图，即物理裂纹尺寸或有效裂纹尺寸与原始裂纹尺寸之间的差值。R曲线通常取决于试样厚度，对于某些材料，还取决于温度和应变率。是随着裂纹扩展，断裂韧性增加，表现为韧性与扩展裂纹长度的上升曲线。 |
| Temperature (Unit K or °C) | 温度（单位K或°C） |
A quantitative measure of the molecular kinetic energy of a substance and so how hot or cold it is. 物质分子动能的定量量度，以及它的冷热程度。 |
| Torsional stress | 扭转应力 |
The shear stress on a transverse cross section resulting from a twisting action. 扭转作用在横截面上产生的剪切应力。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Fracture surface | 断裂面 |
The irregular surface produced when a piece of metal is broken. 一块金属破碎时产生的不规则表面。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Shoulder | 轴肩 |
The portion of a shaft, stepped component, or flanged component, where a change in diameter or other dimension occurs. Even for a nominal step change, in practice there will be a radius where shoulder and shaft meet in order to avoid too severe a stress concentration. 轴、阶梯部件或法兰部件的直径或其他尺寸发生变化的部分。即使是名义阶跃变化，在实践中，肩部和轴相交处也会有一个半径，以避免出现过严重的应力集中。 |
| Modulus of rupture | 断裂模量 |
Nominal stress at fracture in a bend test or torsion test. In bending, modulus of rupture is the bending moment at fracture divided by the section modulus. In torsion, modulus of rupture is the torque at fracture divided by the polar section modulus. 弯曲试验或扭转试验中的标称断裂应力。在弯曲中，断裂模量是断裂时的弯矩除以截面模量。在扭转中，断裂模量是断裂时的扭矩除以极截面模量。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Allotropy | 同素异形体 |
A near synonym for polymorphism. Allotropy is generally restricted to describing polymorphic behavior in elements, terminal phases, and alloys whose behavior closely parallels that of the predominant constituent element. 多态性的近义词。同素异形体通常仅限于描述元素、终端相和合金中的多晶型行为，其行为与主要组成元素的行为非常相似。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Centre line | 中心线 |
1. In an engineering drawing, a line of symmetry. 2. An imaginary line along a pipe, duct, or shaft that defines an axis of symmetry. 3. An imaginary straight line parallel to the intended direction of a surface located such that the areas above and below the line and the real wavy (rough) surface cancel out. 1.在工程图中，对称线。2.沿着管道、管道或竖井定义对称轴的假想线。3.一条平行于表面预期方向的假想直线，该直线上方和下方的区域与真实的波状（粗糙）表面相抵消。 |
| Remaining stress | 残留应力 |
The stress remaining at a given time during a stress-relaxation test. See also stress relaxation. 在应力松弛试验期间在给定时间内剩余的应力。参见压力松弛。 |
| Extra hard | 额外硬化 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about one-third of the way from full hard to extra spring temper. 有色合金和一些铁合金的回火，其特征是抗拉强度和硬度大约是从完全硬回火到额外弹簧回火的三分之一。 |
| Relaxation curve | 松弛曲线 |
A plot of either the remaining, or relaxed, stress as a function of time. 剩余压力或松弛压力随时间变化的曲线图。 |
| Overheating | 过热 |
Heating a metal or alloy to such a high temperature that its properties are impaired. When the original properties cannot be restored by further heat treating, by mechanical working, or by a combination of working and heat treating, the overheating is known as burning. 将金属或合金加热至其性能受损的高温。当通过进一步热处理、机械加工或加工与热处理的组合无法恢复原始性能时，过热称为燃烧。 |
| Critical crack length (Unit m) | 临界裂纹长度（单位米） |
The crack length at which a given stress applied to a body will result in crack propagation and fracture. 施加到物体上的给定应力将导致裂纹扩展和断裂的裂纹长度。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Absorber | 吸收器 |
1. An auxiliary vibratory system that favourably modifies the vibration characteristics of a main system. 2. Part of an absorption refrigeration system in which the refrigerant is absorbed by a transport medium. 3. The absorber plate is the receiver of a concentrating solar collector where the radiation is absorbed. 1.一种辅助振动系统，可有利地改变主系统的振动特性。2.吸收式制冷系统的一部分，其中制冷剂被传输介质吸收。3.吸收板是吸收辐射的聚光太阳能集热器的接收器。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| Athermal transformation | 非热变化 |
A reaction that proceeds without benefit of thermal fluctuations; that is, thermal activation is not required. In contrast, a reaction that occurs at constant temperature is an isothermal transformation; thermal activation is necessary in this case and the reaction proceeds as a function of time. 在没有热波动的情况下进行的反应；也就是说，不需要热激活。相反，在恒温下发生的反应是等温转变。在这种情况下，热活化是必要的，并且反应作为时间的函数进行。 |
| Air conditioning | 空调 |
The process of controlling the temperature and humidity in rooms, buildings, aircraft, passenger vehicles, etc. More generally it includes control of dust, levels of radiant heat, etc. 控制房间、建筑物、飞机、客运车辆等的温度和湿度的过程。更一般地说，它包括控制灰尘、辐射热水平等。 |
| Union (union joint) | 活接头 |
A threaded pipe fitting that allows two pipes to be connected anddetached without the need for either to be rotated, and without damaging the pipe ends. 一种螺纹管件，允许连接和拆卸两个管道，而无需旋转任何一个管道，且不会损坏管道端部。 |
| Lock nut | 锁紧螺母 |
A type of nut that is prevented from loosening under vibration. The locking action is accomplished by squeezing, gripping or jamming against the bolt threads. A nut which provides extra resistance to vibration loosening (beyond that produced by proper Preload ), either by providing some form of Prevailing torque, or, in free-spinning lock nuts, by deforming, cramping, or biting into mating parts when fully tightened. 1. A thin auxiliary nut tightened against another nut to prevent loosening. 2. A single nut with special features that prevent loosening. 一种在振动下防止松动的螺母。锁定动作通过挤压、夹紧或卡住螺栓螺纹来完成。通过提供某种形式的主要扭矩，或在自由旋转锁紧螺母中，通过完全拧紧时变形、夹紧或咬入配合零件，提供额外的抗振动松动能力（超出适当预载产生的能力）。1.一个薄的辅助螺母，拧紧到另一个螺母上以防止松动。2.具有防止松动的特殊功能的单个螺母。 |
| Reverse pitch (Unit °) | 反向螺距（单位°） |
The pitch of a variable-pitch propeller that produces negative thrust. 产生负推力的变桨距螺旋桨的桨距。 |
| Fracture | 断裂 |
(rupture) The separation of materials, components, or structures into two or more parts by the propagation of one or more cracks. Cracking may be globally elastic (brittle) or accompanied by varying degrees of plasticity (ductile). （断裂）通过一个或多个裂纹的扩展将材料、部件或结构分离成两个或更多部分。裂纹可能是整体弹性（脆性）或伴有不同程度的塑性（延性）。 |
| Dislocation density | 位错密度 |
The total length of dislocation lines per unit volume, or the number of dislocation lines that cut through a unit cross-sectional area. 每单位体积的位错线的总长度，或穿过单位横截面积的位错线的数量。 |
| mechanical engineering | 机械工业 |
That branch of engineering concerned with energy conversion, stress analysis, vibration, dynamics, and kinematics, especially applied to design (machine design, mechanical-engineering design). 与能量转换、应力分析、振动、动力学和运动学有关的工程分支，尤其适用于设计（机器设计、机械工程设计）。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Maximum-and-minimum thermometer | 最高和最低温度计 |
(minimum-maximum thermometer, Six’s thermometer) A liquid-in-glass instrument designed to register the maximum and minimum temperatures experienced over a given time period. （最低-最高温度计，Six's温度计）一种液体玻璃仪器，用于记录给定时间段内经历的最高和最低温度。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Stress corrosion cracking (SCC) | 应力腐蚀开裂（SCC） |
A common form of Stress cracking in which an Electrolyte encourages the growth of a crack in a highly stressed bolt. Only a tiny quantity of electrolyte need be present, at the tip or face of the crack. A time-dependent process in which a metallurgically susceptible material fractures prematurely under conditions of simultaneous corrosion and sustained loading at lower stress levels than would be required in the absence of a corrosive environment. Tensile stress is required at the metal surface and may be a residual stress resulting from heat treatment or fabrication of the metal or the result of external loading. Cracking may be intergranular or transgranular, depending on the combination of alloy and environment. 一种常见的应力开裂形式，其中电解液促使高应力螺栓中的裂纹扩展。在裂纹尖端或表面，只需存在少量电解质。一种随时间变化的过程，其中冶金敏感材料在同时腐蚀和持续加载的条件下过早断裂，其应力水平低于无腐蚀环境时的要求。在金属表面需要拉应力，拉应力可以是金属的热处理或制造或外部负载产生的残余应力。裂纹可能是沿晶开裂或穿晶开裂，这取决于合金和环境的组合。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Thread rolling | 滚丝 |
Thread rolling (also known as roll threading) is a cold forming process for producing threads or other helical or annular forms by rolling the impression of hardened steel dies into the surface of a cylindrical or conical blank. Polygonal blanks are also thread rolled for the purpose of fabricating thread-forming and self-locking screws. The preferred polygonal shape is trilobular and is produced in flat die machines. 螺纹滚压（也称为滚压螺纹）是一种冷成型工艺，通过将硬化钢模具的压痕滚压到圆柱形或锥形坯料的表面来生产螺纹或其他螺旋或环形形状。多边形坯料也进行螺纹轧制，以制造螺纹成型和自锁螺钉。优选的多边形形状为三棱形，并在平模机中生产。 |
| Columnar structure | 柱状结构 |
A coarse structure of parallel elongated grains formed by unidirectional growth, most often observed in castings, but sometimes in structures resulting from diffusional growth accompanied by a solid-state transformation. 由单向生长形成的平行细长晶粒的粗略结构，最常见于铸件中，但有时也出现在伴随固态转变的扩散生长产生的结构中。 |
| Minor diameter | 螺纹小径 |
On a straight thread, the diameter of the imaginary cylinder which just touches the root of an external thread or the crest of an internal thread. 在直螺纹上，仅接触外螺纹根部或内螺纹顶部的假想圆柱体的直径。 |
| Granular fracture | 粒状断裂 |
A type of irregular surface produced when metal is broken that is characterized by a rough, grainlike appearance, rather than a smooth or fibrous one. It can be subclassified as transgranular or intergranular. 金属破碎时产生的一种不规则表面，其特征是粗糙的颗粒状外观，而不是光滑或纤维状的外观。它可以细分为穿晶或晶间。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Oil-cooled | 油冷却 |
A term for a machine that uses circulating oil to remove heat. 使用循环油散热的机器的术语。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Gauge pressure (Unit Pa) | 表压（单位Pa） |
The level of static pressure above the ambient pressure. 高于环境压力的静压水平。 |
| Combined heat and power plant | 热电联产电厂 |
(CHP plant, COGEN, cogeneration plant, total-energy plant) A plant for the simultaneous production of more than one useful form of energy from the same energy source, such as process heat and electric power. In the arrangement shown, partially expanded steam is extracted from the steam turbine and used to produce process heat. （CHP工厂、COGEN、热电联产工厂、总能源工厂）从同一能源（如过程热能和电力）同时生产一种以上有用能源的工厂。在所示的布置中，部分膨胀的蒸汽从蒸汽轮机中提取并用于产生过程热量。 |
| Plug | 螺塞 |
1. An object, usually tapered, used to block a hole to prevent fluid from escaping or flowing. 2. The central moveable part of a valve. 3. In the flow of a yield-stress fluid through a pipe or duct, the central region is often assumed to take the form of a plug with uniform axial velocity. 4. In thermoforming, a shaping tool that forces a heated plastic sheet into a female mould. 1.一种物体，通常为锥形，用于堵塞孔以防止流体逸出或流动。2.阀门的中心可移动部分。3.在屈服应力流体通过管道或管道的流动中，中心区域通常假定为具有均匀轴向速度的塞子形式。4.在热成型技术中，一种成型工具，将加热的塑料板压入阴模中。 |
| Actual cubic feet per minute | 实际立方英尺每分钟 |
(acfm) An obsolete (i.e. non-SI) measure of volumetric flow rate; the volume of a gas flowing per minute at actual operating pressure and temperature, as opposed to the corresponding volume flow rate at STP. （acfm）已被淘汰的（即非SI）体积流量测量；在实际工作压力和温度下每分钟流动的气体体积，与STP下的相应体积流量相反。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Grain-boundary liquation | 晶界液化 |
An advanced stage of overheating in which material in the region of austenitic grain boundaries melts. 奥氏体晶界区域的材料熔化的过热阶段。 |
| Principal stress (normal) | 主应力（正常） |
The maximum or minimum value of the normal stressat a point in a plane considered with respect to all possible orientations of the considered plane. On such principal planes the shear stress is zero. There are three principal stresses on three mutually perpendicular planes. The state of stress at a point may be: (1) uniaxial, a state of stress in which two of the three principal stresses are zero; (2) biaxial, a state of stress in which only one of the three principal stresses is zero; or (3) triaxial, a state of stress in which none of the principal stresses is zero. Multiaxial stress refers to either biaxial or triaxial stress. 相对于所考虑平面的所有可能方向，所考虑平面中某点处的法向应力的最大值或最小值。在这样的主平面上，剪切应力为零。在三个相互垂直的平面上有三个主应力。一点的应力状态可以是：（1）单轴，三个主应力中的两个为零的应力；（2）双轴，三个主应力中只有一个为零的应力状态；或（3）三轴，即主应力均不为零的应力状态。多轴应力是指双轴或三轴应力。 |
| Dead space | 死区 |
(dead volume) (Unit m³) That volume of a gas-filled thermometer in which the gas is not at the same temperature as that being measured. （死容）（单位m³）充气温度计的体积，其中气体的温度与被测温度不同。 |
| Induction tempering | 感应回火 |
Tempering of steel using low-frequency electrical induction heating. 钢的回火采用低频电感应加热。 |
| Vickers hardness test | 维氏硬度测试 |
An indentation hardness test employing a 136° diamond pyramid indenter (Vickers) and variable loads, enabling the use of one hardness scale for all ranges of hardness—from very soft lead to tungsten carbide. Also know as diamond pyramid hardness test. 采用136°金刚石棱锥压头（维氏硬度计）和可变载荷的压痕硬度测试，能够对从极软铅到碳化钨的所有硬度范围使用一个硬度标度。也称为钻石金字塔硬度测试。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Surface hardness | 表面硬度 |
(superficial hardness) Indentation hardness on, and for some distance below, the surface of a component, as opposed to its bulk hardness. Depending on the resolution required, micro- or nano-hardness testing machines are employed. （表面硬度）与整体硬度相反，部件表面及其下方一定距离的压痕硬度。根据所需的分辨率，可使用微型或纳米硬度测试机。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Acid rain | 酸雨 |
Any form of precipitation, including rain, snow, sleet, fog, dew, and particulates, which contains higher than normal levels of sulfuric and nitric acids. These acids result from natural and man-made emissions of sulfur dioxide and oxides of nitrogen, respectively. Acid soot consists of unburned carbon particles, typically larger than 10 μm, in the atmosphere contaminated with sulfuric acid. The particles result from poor combustion of fossil fuels. 任何形式的降水，包括雨、雪、雨夹雪、雾、露水和颗粒物，其中含有高于正常水平的硫酸和硝酸。这些酸分别来自二氧化硫和氮氧化物的自然排放和人为排放。酸烟灰由未燃烧的碳颗粒组成，通常大于10微米，在被硫酸污染的大气中。这些颗粒是化石燃料燃烧不良造成的。 |
| Transfer moulding | 转移模塑 |
(resin-transfer moulding, RTM) A method of compression moulding polymers in which the dies are closed before the operation starts. （树脂传递模塑，RTM）一种对聚合物进行压缩模塑的方法，其中模具在操作开始前关闭。 |
| Punch | 冲床 |
1. A hand tool with a sharp point, used to mark the position of a hole centre in a workpiece prior to drilling. 2. A flat-ended tool with sharp edges, used to shear out a hole in a plate that is supported underneath on a die having a slightly larger same-shaped orifice. 1.一种带有尖头的手动工具，用于在钻孔前标记工件中孔中心的位置。2.一种具有锐边的平头工具，用于剪切板上的孔，该板支撑在具有稍大相同形状孔口的模具下方。 |
| Wing nut | 蝶形螺母 |
A nut having two opposite protruding wings to permit hand tightening. 一种螺母，有两个相对突出的翼片，可以用手拧紧。 |
| Translational joint | 平移铰 |
A robot joint where the controlled variable is straight line movement. 控制变量为直线运动的机器人关节。 |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Thermoelastic effect | 热弹性效应 |
The change in temperature of material under adiabatic elastic deformation, e.g. when loading is so rapid that the material is not in thermal equilibrium with its surroundings. For most materials, elastic tension lowers the temperature and compression raises it. The reverse occurs in elastomers such as rubber that exhibit entropic elasticity because stretching reduces the number of possible molecular configurations and so reduces the entropy. The thermoelastic effect gives rise to a stress–strain hysteresis loop in cyclic elastic loading and is one mechanism by which vibrational energy is dissipated internally in materials. 材料在绝热弹性变形下的温度变化，例如当加载速度如此之快，以至于材料与其周围环境不处于热平衡时。对于大多数材料，弹性张力降低温度，压缩提高温度。相反的情况发生在弹性体中，如橡胶，其表现出熵弹性，因为拉伸减少了可能的分子构型的数量，从而降低了熵。热弹性效应在循环弹性载荷中产生应力-应变迟滞回线，是振动能量在材料内部耗散的一种机制。 |
| Centrifugal pump | 离心泵 |
A pump into which liquid enters axially through the eye of the casing and is then accelerated through an impeller, thereby increasing both its kinetic energy and pressure before being delivered to a ring diffuser (the volute) that further increases the liquid pressure and from which it leaves. 一种泵，液体通过泵壳的眼轴向进入，然后通过叶轮加速，从而在输送到环形扩散器（蜗壳）之前增加其动能和压力，从而进一步增加液体压力并从中流出树叶。 |
| Second (s) | 秒（s） |
The SI base unit of time equal to 9 192 631 770 times the period of the radiation corresponding to the transition between the two hyperfine levels of the ground state of the caesium-133 atom. SI基时间单位等于9192631770倍的辐射周期，对应于铯-133原子基态的两个超精细能级之间的跃迁。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Galilean transformation | 伽利略变换 |
In steady fluid flow, the addition or subtraction of a constant velocity to the entire flowfield, e.g. so that flow can be considered relative to a moving object or flow feature, such as a shock wave. 在稳定的流体流动中，对整个流场增加或减少恒定速度，例如，可以考虑相对于移动物体或流动特征（例如冲击波）流动。 |
| Knoop hardness test | 努氏硬度试验 |
An indentation-hardness test using calibrated machines to force a rhombic-based pyramidal diamond indenter having specified edge angles, under specified conditions, into the surface of the material under test and to measure the long diagonal after removal of the load. An indentation hardness test in which the indenter is an elongated diamond pyramid that gives an impression in the form of a parallelogram, in which the longer diagonal is about seven times the shorter. Used for studies of anisotropy in solid materials. 使用校准机器进行的一种压痕硬度试验，在规定条件下，将具有规定边缘角的菱形棱锥金刚石压头压入受试材料表面，并在移除荷载后测量长对角线。其中压头是一个细长的菱形棱锥，以平行四边形的形式给出压痕，其中较长的对角线约为较短的七倍。用于研究固体材料的各向异性。 |
| Offset | 偏移 |
The distance along the strain coordinate between the initial portion of a stress-strain curve and a line parallel to the initial portion that intersects the stress-strain curve at a value of stress (commonly 0.2%) that is used as a measure of the yield strength. Used for materials that have no obvious yield point. 应力-应变曲线的初始部分与平行于初始部分的线之间沿应变坐标的距离，该线以应力值（通常为0.2%）与应力-变形曲线相交，该应力值用作屈服强度的度量。用于没有明显屈服点的材料。 |
| Ferritizing anneal | 铁素体化退火 |
A treatment given as-cast gray or ductile (nodular) iron to produce an essentially ferritic matrix. For the term to be meaningful, the final microstructure desired or the time-temperature cycle used must be specified. 给予铸态灰铁或球墨铸铁以产生基本铁素体基体的处理。为了使该术语有意义，必须指定所需的最终微观结构或使用的时间-温度循环。 |
| Working stress (Unit Pa) | 工作应力（单位Pa） |
The stress under which a component or structure is designed to operate under normal conditions. 部件或结构设计为在正常条件下运行的应力。 |
| Millimetre of mercury | 毫米汞柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of mercury 1 mm high. Approximately equal to 133.3 Pa or 1 torr. 一种非SI压力单位，等于1毫米高的垂直水银柱施加的压力。大约等于133.3Pa或1托。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Welding | 焊接 |
In tribology, the bonding between metallic surfaces in direct contact, at any temperature. A joining process in which the mating surfaces are at least softened, or more usually melted, unlike soldering and brazing. In solid-state (non-melting) welding, similar or dissimilar metals or thermoplastics may be joined by applying pressure to hot interfaces. In forge welding, joining is achieved by compression across the join between pre-heated workpieces. In friction welding (spin welding) one of the contacting surfaces is rotated rapidly before being loaded against the other. On contact, heat generated by friction softens the materials and permits severe plastic deformation that seals the joint. In friction stir welding, a wear-resistant tool is rotated rapidly, indents the surfaces and is traversed to form a join line. Resistance welding involves simultaneous pressure and electrically-generated heat, as in spot welding where a heavy electric current is passed for a short time through metal sheets which are pressed together between electrodes. 在摩擦学中，在任何温度下直接接触的金属表面之间的结合。与钎焊和钎焊不同，接合面至少软化或更通常熔化的接合工艺。在固态（非熔化）焊接中，相似或不同的金属或热塑性塑料可通过向热界面施加压力来连接。在锻造焊接中，通过压缩预热工件之间的连接来实现连接。在摩擦焊接（旋转焊接）中，一个接触表面在被加载到另一个表面之前快速旋转。接触时，摩擦产生的热量使材料软化，并允许密封接头的严重塑性变形。在搅拌摩擦焊中，耐磨工具快速旋转，使表面凹陷，并横穿形成连接线。电阻焊涉及同时产生的压力和电产生的热量，如点焊，在点焊中，大电流短时间通过电极之间压在一起的金属板。 |
| Actual power | 实际功率 |
(actual horsepower) (Unit W or hp) The power delivered at the output shaft of an engine, before subsequent transmission through a gearbox etc. （实际马力）（单位W或hp）在随后通过变速箱等传输之前，在发动机输出轴上传递的功率。 |
| V-block | V型块 |
A block having a 90° V-shaped recess; used in a workshop to hold round workpieces. 具有90°V形凹槽的块体；在车间里用来装圆形工件。 |
| Permissible variation | 允许偏差 |
For testing machines, the maximum allowable error in the value of the quantity indicated. It is convenient to express permissible variation in terms of the percent error. 对于试验机，所示数量值的最大允许误差。用误差百分比表示允许偏差是很方便的。 |
| System engineering | 系统工程 |
A methodology which integrates all disciplines and specialty groups into a team effort, forming a structured development process that proceeds from concept to production to operation. 一种将所有学科和专业组整合到团队工作中的方法，形成从概念到生产再到运营的结构化开发过程。 |
| Active vibration suppression | 主动振动抑制 |
The reduction of undesirable vibration in components by feedback control. 通过反馈控制减少部件中的不良振动。 |
| Salt-velocity meter | 盐速计 |
A volume flow meter based on detecting the transit time for a small quantity of salt or radioactive isotope in a flow by measuring electrical conductivity or radiation level. 一种体积流量计，通过测量电导率或辐射水平来检测流量中少量盐或放射性同位素的渡越时间。 |
| Centrifugal fan | 离心风机 |
A machine with a rotor consisting of a number of blades mounted around a hub and used for moving air or other gases. The gas enters the rotor axially and is discharged radially at increased pressure. 一种带有转子的机器，转子由安装在轮毂周围的许多叶片组成，用于移动空气或其他气体。气体轴向进入转子并在增加的压力下径向排出。 |
| Lüders lines | 吕德斯线 |
Elongated surface markings or depressions, often visible with the unaided eye, that form along the length of sheet metal or a tension specimen at an angle of approximately 45° to the loading axis. Caused by localized plastic deformation, they result from discontinuous (inhomogeneous) yielding. Also known as Lüders bands, Hartmann lines, Piobert lines, or stretcher strains. 拉长的表面标记或凹陷，通常肉眼可见，沿金属板或拉伸试样的长度形成，与加载轴的角度约为45°。由于局部塑性变形，它们是不连续（不均匀）屈服的结果。也被称为吕德斯带、哈特曼线、皮奥伯特线或拉伸线。 |
| Turbulent flow (turbulence) | 湍流 |
Fluid motion characterized by disorderly, rotational (i.e. vortical) three-dimensional velocity fluctuations covering a wide range of frequency and length scales. The pressure, temperature, and other fluid properties also fluctuate and the diffusion of heat, mass, and momentum is greatly enhanced. As are laminar and transitional flow, turbulent flow of a Newtonian fluid is governed by the Navier–Stokes equations which can in principle be solved by direct numerical simulation (DNS) in which all time and length scales of the fluctuating motion are resolved. 流体运动的特点是无序、旋转（即旋涡）三维速度波动，覆盖广泛的频率和长度尺度。压力、温度和其他流体特性也会波动，热、质量和动量的扩散会大大增强。与层流和过渡流一样，牛顿流体的湍流由Navier-Stokes方程控制，该方程原则上可以通过直接数值模拟（DNS）求解，在直接数值模拟中，波动运动的所有时间和长度尺度都可以求解。 |
| Torr | 托尔 |
A non-SI unit of pressure commonly used in vacuum systems; defined by 760 torr = 1 atm so that 1 torr = 133.322 368 4 Pa, and approximately equivalent to the pressure corresponding to 1 mm of mercury. 真空系统中常用的非SI压力单位；由760托=1大气压定义，因此1托=133.3223684帕，近似等于对应于1毫米汞柱的压力。 |
| Accelerated testing | 加速测试 |
A type of testing, for rates of wear, fatigue, corrosion etc., in which failure times are reduced by employing greater loads, more frequent power cycling, higher vibration levels, higher humidity, higher temperatures, greater potential differences etc. than would be encountered in normal operation. 一种测试类型，用于测试磨损率、疲劳率、腐蚀率等，通过采用比正常运行中更大的负载、更频繁的功率循环、更高的振动水平、更高湿度、更高温度、更大的电位差等，减少故障时间。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Allowable stress design | 许用应力设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Purposely underestimates the strengths of bolts and joint materials to introduce safety factors into the design of structural steel joints. It is an alternative to the more recently defined load and resistance factor design procedure. 结构连接研究委员会为AISC制定的设计程序。故意低估螺栓和接头材料的强度，以便在结构钢接头的设计中引入安全系数。它是最近定义的荷载和阻力系数设计程序的替代方法。 |
| Solution heat treatment | 固溶热处理 |
Heating an alloy to a suitable temperature, holding at that temperature long enough to cause one or more constituents to enter into solid solution, and then cooling rapidly enough to hold these constituents in solution. 将合金加热到合适的温度，在该温度下保持足够长的时间以使一种或多种成分进入固溶体，然后快速冷却以将这些成分保持在溶液中。 |
| Nanoparticles | 纳米颗粒 |
Particles with dimensions of order 1 nm which have either been introduced into microstructures for reinforcement or are present as impurities. 尺寸为1nm级的颗粒，其已被引入微结构中用于增强或作为杂质存在。 |
| Blowing | 吹气 |
The process by which a gas is transferred through a porous surface over which there is a gas flow. The effect is used to decrease skin friction and increase heat transfer, for example in turbine-blade cooling. 气体通过有气流的多孔表面转移的过程。该效应用于减少表面摩擦和增加传热，例如在涡轮叶片冷却的过程中。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Degradation | 降解 |
The reduction with time of the physical properties of a material. 材料的物理性质随时间的减少。 |
| Torque coefficient | 扭矩系数 |
1. (KT) For a propeller of diameter D, a non-dimensional parameter defined by KT = T/ρΩ2D5 where Ω is the rotational speed (in rad/s) and ρ is the fluid density. 2. (CT) An alternative to (1) for a wind turbine, defined by CT = 2T/ρV2AR where V is the wind speed, A is the swept area of the blades, and R is the blade radius. 3. (K) An empirical coefficient used to calculate the torque T required to achieve an axial load F in a bolt according to T = KFd where d is the nominal bolt diameter. 1.（KT）对于直径为D的螺旋桨，由KT=T/ρΩ2D5定义的无量纲参数，其中Ω是转速（单位为rad/s），ρ是流体密度。2.（CT）对于风力涡轮机（1）的替代方案，由CT=2T/ρV2AR定义，其中V是风速，a是叶片的扫掠面积，R是叶片半径。3.（K）经验系数，用于根据T=KFd计算螺栓中实现轴向载荷F所需的扭矩T，其中d是螺栓标称直径。 |
| Thermal fatigue | 热疲劳 |
Fatigue resulting from the presence of temperature gradients that vary with time in such a manner as to produce cyclic stresses in a structure. 由于温度梯度的存在而产生的疲劳，温度梯度随时间变化，从而在结构中产生循环应力。 |
| Grain size | 晶粒大小 |
A measure of the areas or volumes of grains in a polycrystalline metal, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. For metals, a measure of the areas or volumes of grains in a polycrystalline material, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. Grain sizes are reported in terms of number of grains per unit area or volume, average diameter, or as a grainsize number derived from area measurements. 多晶金属中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。多晶材料中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。晶粒尺寸以每单位面积或体积的晶粒数、平均直径或从面积测量得出的晶粒尺寸数来报告。 |
| Hydrogen embrittlement | 氢脆 |
A condition of low toughness, low ductility or cracking in metals resulting from the absorption of hydrogen. A common and troublesome form of Stress cracking. Several theories have been proposed to explain hydrogen embrittlement, but, at present, the exact mechanism is still unknown. What is known, however, is the fact that if hydrogen is trapped in a bolt by poor electroplating practices, it can encourage stress cracking. Bolts can fail, suddenly and unexpectedly, under normal loads. Premature crack growth over time under tensile stress leading to unexpected failure in certain metals, caused by small amounts of hydrogen in the microstructure. Hydrogen may enter steels during melting or heat treating, or during processes such as electroplating. 因吸收氢而导致金属韧性低、延展性低或开裂的情况，是一种常见且麻烦的应力开裂形式。在拉伸应力下，裂纹随时间过早扩展，导致某些金属发生意外失效，这是由微观结构中的少量氢引起的。在熔化或热处理过程中，或在电镀等过程中，氢可能进入钢中。已经提出了几种理论来解释氢脆，但目前，确切的机理仍然未知。已知的事实是，如果氢因电镀不当而被困在螺栓中，则会导致应力开裂。在正常载荷下，螺栓可能突然意外失效。 |
| Thermal analysis | 热分析 |
A method for determining transformations in a metal by noting the temperatures at which thermal arrests occur. These arrests are manifested by changes in slope of the plotted or mechanically traced heating and cooling curves. When such data are secured under nearly equilibrium conditions of heating and cooling, the method is commonly used for determining certain critical temperatures required for the construction of equilibrium diagrams. 一种通过记录发生热阻的温度来确定金属转变的方法。这些阻力表现为绘制或机械追踪的加热和冷却曲线斜率的变化。当这些数据在加热和冷却的近似平衡条件下得到保证时，该方法通常用于确定构建平衡图所需的某些临界温度。 |
| Thermodynamics laws | 热力学定律 |
The zeroth, first, second, and third laws of thermodynamics. 热力学第零、第一、第二和第三定律。 |
| Archimedes Wave Swing | 阿基米德波摆动 |
A machine for tidal-power energy generation consisting of two concentric, air-filled submerged cylinders. The inner lower cylinder is tethered to the ocean floor while the upper floater unit, which is closed at the top, moves up and down due to the variations in hydrostatic pressure caused by the wave motion. The relative movement of the two cylinders is used to generate electricity in which linear motion replaces the more common rotary motion of an electromagnetic generator. 一种用于潮汐能发电的机器，由两个同心的充气水下气缸组成。内部下部圆柱体系在海底，而顶部封闭的上部浮子单元由于波浪运动引起的静水压力变化而上下移动。两个气缸的相对运动用于发电，其中直线运动取代了电磁发电机更常见的旋转运动。 |
| Shoulder screw | 轴肩螺钉 |
A screw having two or more diameters or shoulders and commonly used for supporting levers and other machine parts that have to operate freely. 一种具有两个或两个以上直径或轴肩的螺钉，通常用于支撑杠杆和其他必须自由操作的机器部件。 |
| Distortion | 扭曲 |
Any deviation from an original size, shape, or contour that occurs because of the application of stress or the release of residual stress. 由于施加应力或释放残余应力而发生的与原始尺寸、形状或轮廓的任何偏差。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Nano machining | 纳米加工 |
The machining of silicon chips typically less than 1 nm thick. 硅芯片的加工通常小于1nm厚。 |
| Ballonet | 气囊 |
An airbag used in a hybrid airship. Helium gas expels air from the ballonet during ascent. Fans draw air in during descent. 混合动力飞艇中使用的安全气囊。氦气在上升过程中将空气从气囊中排出。风扇在下降过程中吸入空气。 |
| Coarse threads | 粗螺纹 |
Threads with relatively large separation between corresponding points on the threads. 螺纹上相应点之间的间距相对较大的螺纹。 |
| Condensate strainer | 冷凝水过滤器 |
A filter in a steam plant used to remove particulate matter from condensate before it is added to feedwater. 蒸汽设备中的过滤器，用于在将冷凝水添加到给水中之前去除冷凝水中的颗粒物。 |
| Cleavage fracture | 解理断裂 |
A fracture, usually of a polycrystalline metal, in which most of the grains have failed by cleavage, resulting in bright reflecting facets. It is one type of crystalline fracture and is associated with low energy brittle fracture. Contrast with shear fracture. A fracture created by splitting (cleavage), as between layers in materials like slate or mica. In brittle metals, and brittle microconstituents in alloys, cleavage occurs along particular crystal planes. 一种通过分裂（劈裂）产生的裂缝断裂，通常是多晶金属的断裂，其中大部分晶粒因解理而失效，产生明亮的反射面。它是一种结晶性断裂，与低能脆性断裂有关。与剪切断裂相对。如板岩或云母等材料的层之间。在脆性金属和合金中的脆性微量成分中，沿特定晶面发生解理。 |
| Crossed threads | 交叉螺纹 |
When the axis of a nut offered up to a bolt is not aligned with the axis of a bolt (or a screw to a threaded member), it may be possible for the threads to engage incorrectly and even for the nut or screw to advance a turn or more, but ultimately the misaligned threads become locked together. Forcing the nut in such circumstances may irretrievably damage the threads on both. 当提供给螺栓的螺母的轴线与螺栓（或螺纹构件的螺钉）的轴线不对齐时，螺纹可能会错误接合，甚至螺母或螺钉会提前一圈或更多，但最终未对齐的螺纹会锁定在一起。在这种情况下强行拧入螺母可能会对两侧的螺纹造成无法修复的损坏。 |
| Brine quenching | 盐水淬火 |
A quench in which brine (salt water-chlorides, carbonates, and cyanides) is the quenching medium. The salt addition improves the efficiency of water at the vapor phase or hot stage of the quenching process. 一种淬火，其中盐水（盐水-氯化物、碳酸盐和氰化物）是淬火介质。添加盐提高了水在淬火过程的气相或热阶段的效率。 |
| Monotron hardness test | 摩诺硬度试验 |
An obsolete method of determining indentation hardnessby measuring the load required to force a spherical penetrator into a metal to a specified depth. 一种已被淘汰的方法，通过测量将球形侵彻体压入金属至规定深度所需的载荷来确定压痕硬度。 |
| Quench annealing | 淬火退火 |
Annealing an austenitic ferrous alloy by solution heat treatment followed by rapid quenching. 通过固溶热处理然后快速淬火对奥氏体铁合金进行退火。 |
| Sharp-notch strength | 锐缺口强度 |
The notch tensile strength measured using specimens with very small notch root radii (approaching the limit for machining capability); values of sharp-notch strength usually depend on notch root radius. 使用缺口根部半径非常小（接近加工能力极限）的试样测量的缺口抗拉强度；锐缺口强度值通常取决于缺口根部半径。 |
| Creep | 蠕变 |
The slow, plastic deformation of a body under heavy loads. Time-dependent plasticity. Time-dependent and permanent deformation of material under constant load or stress. The strain increases with time at a rate that increases with increasing temperature. Creep can lead to large strain and eventual failure, and so limit the lifetime of components subjected to load at high temperature. Creep in metals becomes significant at homologous temperatures in excess of about 0.4, e.g. 1200°C for tungsten, 504°C for titanium, 450°C for iron, and 100°C for aluminium. 物体在重载荷下缓慢的塑性变形，随时间变化的可塑性，材料在恒定载荷或应力下随时间变化的永久变形。应变随时间以随温度升高而增加的速率增加。蠕变可能导致大应变和最终失效，从而限制部件在高温下承受载荷的寿命。当同源温度超过约0.4℃时，金属蠕变变得显著，例如钨为1200℃，钛为504℃，铁为450℃，铝为100℃。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Graham’s laws | 格雷厄姆定律 |
The laws stating that the rates of diffusion and effusion of a gas are inversely proportional to the square root of its density. 规定气体的扩散和渗出速率与其密度的平方根成反比的定律。 |
| Sound pressure (Unit μPa) | 声压（单位：μPa） |
The instantaneous deviation of pressure from the ambient pressure caused by the passage of a sound wave, which can be measured by a microphone in air and a hydrophone in water. 声波传播引起的压力与环境压力的瞬时偏差，可通过空气中的麦克风和水中的水听器测量。 |
| Core | 核心 |
In a ferrous alloy prepared for case hardening, that portion of the alloy that is not part of the case . Typically considered to be the portion that (a) appears light on an etched cross section, (b) has an essentially unaltered chemical composition, or (c) has a hardness, after hardening, less than a specified value. 在为表面硬化而制备的铁合金中，合金中不属于表面的那部分。通常被认为是（a）在蚀刻横截面上看起来很轻，（b）化学成分基本不变，或（c）硬化后硬度低于规定值的那部分。 |
| Total head (hT) (Unit m) | 总水头（hT）（单位：m） |
Total pressure pT expressed in terms of the vertical height of a column of liquid, typically water or mercury, i.e. hT = pT/ρg where g is the acceleration due to gravity and ρ is the liquid density. 总压力pT以液体柱（通常为水或汞）的垂直高度表示，即hT=pT/ρg，其中g为重力加速度，ρ为液体密度。 |
| Reduction in area (RA) | 缩小面积（RA） |
The difference between the original cross-sectional area of a tensile specimen and the smallest area at or after fracture as specified for the material undergoing testing. Also known as reduction of area. 拉伸试样的原始横截面积与试验材料断裂时或断裂后的最小面积之间的差值，也称为减少面积。 |
| Coefficient of thermal expansion | 热膨胀系数 |
(1) Change in unit of length (or volume) accompanying a unit change of temperature, at a specified temperature. (2) The linear or volume expansion of a given material per degree rise of temperature, expressed at an arbitrary base temperature or as a more complicated equation applicable to a wide range. （1） 单位长度（或体积）随温度单位变化的变化。（2） 给定材料每上升一度的线性或体积膨胀，在任意基础温度下表示，或作为适用于宽范围的更复杂方程表示。 |
| Angle of torsion | 扭转角 |
(angle of twist) (Unit ° or rad) The angle relative to a chosen section, normal to the axis of twist, through which another part of a component rotates when subjected to a torque. （扭转角）（单位°或弧度）相对于选定截面的角度，垂直于扭转轴，部件的另一部分在受到扭矩时通过该角度旋转。 |
| Regenerative pump | 涡流泵 |
(regenerative turbine pump, peripheral pump) A pump with a double-sided impeller having a large number of radial blades. The pressure of the pumped liquid increases progressively over several revolutions of the impeller. It is particularly suited to producing large heads at small flow rates without cavitation. （再生涡轮泵，外围泵）具有具有大量径向叶片的双面叶轮的泵。泵送液体的压力在叶轮的几圈内逐渐增加。它特别适合于在小流速下产生大水头且不产生气穴。 |
| Actuating system | 驱动系统 |
A system in which an electrical, pneumatic or hydraulic input supplied to an actuator produces force, torque, or displacement, usually in a controlled way. 一种系统，其中提供给执行器的电气、气动或液压输入通常以受控方式产生力、扭矩或位移。 |
| Available head (Unit m) | 可用水头（单位米） |
In a hydroelectric power system, the difference between the vertical height of the water level in the supply reservoir above the turbine inlet less the head loss due to friction and fittings in the duct leading to the turbine. 在水力发电系统中，水轮机入口上方供水水库中水位垂直高度之间的差减去由于通向涡轮机的管道中的摩擦和配件造成的水头损失。 |
| Single-shear test | 单剪试验 |
(1) A shear test similar to the double-shear test used for round-bar specimens, but that uses only one stationary shear blade. (2) A shear test that uses a sheet or thin-plate specimen. （1）一种剪切试验，类似于用于圆棒试样的双剪切试验，但仅使用一个固定剪切刀片。（2）使用薄板或薄板试样的剪切试验。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Die screw | 模具螺丝 |
Tool used when threading cylindrical pieces beyond the capacity of a die plate. 对超出模板容量的圆柱件进行螺纹加工时使用的工具。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Turbine blades (turbine buckets) | 涡轮叶片 |
1. The aerofoil-shaped vanes that form the rotor and stator of a gas, steam or hydraulic turbine. 2. The cup-shaped vanes of a Pelton wheel. 1.形成燃气、蒸汽或水力涡轮机的转子和定子的翼型叶片。2.冲击轮的杯形叶片。 |
| Least count | 最小计数 |
The smallest value that can be read from an instrument having a graduated scale. Except on instruments provided with a vernier, the least count is that fraction of the smallest division which can be conveniently and reliably estimated; this fraction is ordinarily one-fifth or one-tenth, except where the graduations are very closely spaced. 可从具有刻度尺的仪器中读取的最小值。除配备游标的仪器外，最小计数是可以方便可靠地估计的最小除法的分数；这个分数通常是五分之一或十分之一，除非刻度间隔非常近。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Belt furnace | 带式炉 |
A continuous-type furnace which uses a mesh-type or cast-link belt to carry parts through the furnace. 一种连续式炉，它使用网状或铸造链带将零件运送通过炉子。 |
| Ductile fracture | 韧性断裂 |
Fracture characterized by tearing of metal accompanied by appreciable gross plastic deformation and expenditure of considerable energy. A fracture of a component or structure which is preceded by extensive ductile deformation so that the broken pieces cannot be re-fitted to regain the original size and shape of the component or structure. 以金属撕裂为特征的断裂，伴随着明显的总塑性变形和相当大的能量消耗。一种部件或结构的断裂，在断裂前会发生大范围的延性变形，从而使断裂的碎片无法重新装配以恢复部件或结构原来的尺寸和形状。 |
| Elastic limit | 弹性极限 |
The maximum stress which a material is capable of sustaining without any permanent strain (deformation) remaining on complete release of the stress. 材料在完全释放应力时能够承受的最大应力，且不会留下任何永久应变（变形）。 |
| Brayton cycle | 布雷顿循环 |
(Joule cycle) An air standard cycle that is the ideal cycle for a gasturbine engine. As shown on the diagram of pressure (p) ʋs specific volume (ʋ), it consists of four internally reversible processes: isentropic compression in a compressor (1–2), isobaric heat addition in a combustor (2–3), isentropic expansion in a turbine (3–4) and isobaric heat rejection. The cycle can be extended to include regeneration, reheating, and intercooling. （焦耳循环）一种空气标准循环，是燃气轮机发动机的理想循环。循环可以扩展到包括再生、再热和中冷。 |
| Concentrated load | 集中负荷 |
A load on a component which is distributed over a very small area, idealized as the line load of a wedge or knife edge, and the point load of a cone. 分布在非常小的区域上的部件上的载荷，理想化为楔形或刀刃的线载荷和锥体的点载荷。 |
| Toggle (toggle clamp) | 拨动（拨动夹） |
A device consisting of two pinned levers that are almost in line between two end points in the same plane. Bringing the levers into line generates large forces between the ends. Used to obtain a large mechanical advantage or as a locking mechanism. 由两个销杆组成的装置，在同一平面的两个端点之间几乎成一条直线。将杠杆对齐会在端部之间产生较大的力。用于获得较大的机械优势或用作锁定机构。 |
| Crack-growth rate | 裂纹增长速度 |
Rate of propagation of a crack through a material due to statically or dynamically applied load. 由于静态或动态施加的载荷，裂纹在材料中的扩展速率。 |
| Thermoelectric converter | 热电转换器 |
(thermoelectric generator) A device consisting of series-connected alternate n- and p-type semiconductor elements sandwiched between two ceramic plates. Due to the Seebeck effect, electrical power is generated when a temperature difference is maintained across the plates. Due to the Peltier effect, a thermoelectric converter can act as either a thermoelectric heater or a thermoelectric cooler (thermoelectric refrigerator) by passing an electrical current through it. The thermoelectric figure of merit (Z), with unit 1/K, is a dimensional parameter on which the efficiency of a thermoelectric device is primarily dependent, defined by Z = σα2/k where α is the Seebeck coefficient, σ is the electrical conductivity, and k is the thermal conductivity. The product of Z and a temperature is non-dimensional. （热电发生器）由串联连接的交替的n型和p型半导体元件夹在两块陶瓷板之间组成的装置。由于塞贝克效应，当板之间保持温差时，就会产生电能。由于珀尔帖效应，热电转换器可以通过使电流通过而充当热电加热器或热电冷却器（热电制冷机）。热电优值（Z）和第一单元/K是一个尺寸参数，热电装置的效率主要取决于此，由Z=σα2/K定义，其中α是塞贝克系数，σ是电导率，K是热导率。Z和温度的乘积是无量纲的。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Depth gauge | 深度计 |
1. A precision instrument, typically consisting of a machine-divided steel rule passing through a hardened-steel cross head, used to measure the depths of slots, holes, shoulders, projections, etc. 2. A device used by divers to indicate the water depth. 1. 一种精密仪器，通常由穿过硬化钢十字头的机器分割钢尺组成，用于测量槽、孔、肩部、突起等的深度。 2. 潜水员用来指示深度的装置水深。 |
| Pressure storage tank | 压力贮存器 |
(pressure vessel) A closed container for storing gases or volatile liquids, such as liquefied gases, at pressures significantly above atmospheric pressure. Such tanks are commonly cylindrical with domed ends, spherical, spheroidal, torispherical or hemispherical. （压力容器）密闭容器：在大气压以上的压力下储存气体或挥发性液体，如液化气体的密闭容器。此类贮存器通常为圆柱形，具有半球形端部、球形、球面或半球形。 |
| B-basis | B-基础 |
Mechanical property value above which at least 90% of the population of values is expected to fall, with a confidence of 95%. 机械性能值超过该值时，至少90%的值预计会下降，置信度为95%。 |
| Toothed gearing | 齿轮传动 |
In principle, friction between circular discs in tangential contact could be used to transmit rotation and power between shafts, but the power level would be very limited and the velocity ratio affected by slip. To make the drive positive, gear wheels are used instead in which teeth extend above and below the diameters (the pitch-circle diameters) of discs in ideal rolling contact. The diagram shows the nomenclature for spur gears, the simplest type of gearing between parallel shafts, which are cylindrical in shape with straight teeth parallel to the axis of rotation. 原则上，切向接触的圆盘之间的摩擦可用于在轴之间传递旋转和动力，但动力水平非常有限，速比受滑动的影响。为了使驱动积极，使用齿轮代替，齿轮中的齿延伸到理想滚动接触的圆盘直径（节圆直径）的上方和下方。该图显示了直齿轮的名称，这是平行轴之间最简单的齿轮传动类型，其形状为圆柱形，直齿平行于旋转轴。 |
| Angle of friction | 摩擦角 |
(friction angle, β) (Unit °) For a body in contact with a plane surface, the angle between the normal to the surface and the resultant force between the body and the surface. If the friction force is F and normal force is N, β is given by F/N = μ = tan β where μ is the coefficient of friction. （摩擦角，β）（单位°）对于与平面接触的物体，表面法线与物体与表面之间的合力之间的夹角。如果摩擦力为F，法向力为N，则β由F/N=μ=tanβ给出，其中μ是摩擦系数。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Combustion | 燃烧氧化 |
An exothermic chemical reaction in which a fuel and an oxidant, typically air, react together to release a significant quantity of thermal energy in the presence of a flame. In the case of fluid fuels, ignition may be from an electric spark or compression of the 一种放热化学反应，其中燃料和氧化剂（通常是空气）一起反应，在火焰存在的情况下释放大量热能。 |
| Combustion efficiency | 燃烧效率 |
(source efficiency, ηCOMB) A performance measure for combustion equipment defined by ηCOMB = amount of heat released during combustion/(calorific value of the fuel burned). （源效率，ηCOMB）燃烧设备的性能度量，定义为ηCOMB=燃烧过程中释放的热量/（燃烧燃料的热值）。 |
| Metric ton (tonne, t) | 公制吨（吨，t） |
An SI-accepted, but non-SI, unit of mass defined as 1 t = 103 kg. SI系统可接受但非国际单位制的质量单位，定义为1t=103kg。 |
| Torsional shaft vibration | 扭轴振动 |
The rapid back-and-forth angular twisting along a rotating unbalanced shaft which reaches maxima at critical rotation speeds. Shaft eccentricity, unbalanced mass distribution, oscillatory torque, misalignment, etc. all influence torsional vibration. 沿旋转不平衡轴的快速来回角扭转，在临界转速下达到最大值。轴偏心、质量分布不平衡、振荡扭矩、未对准等都会影响扭转振动。 |
| Fin neck carriage bolt | 翼颈圆头方颈螺栓 |
A plain, circular, oval head bolt with two oppositely located fins to prevent rotation. 一种普通的圆形椭圆头螺栓，有两个相对的翼片以防止旋转。 |
| Graphitic carbon | 石墨碳 |
Free carbon in steel or cast iron. 钢或铸铁中的游离碳。 |
| Cohesive zone | 凝聚力区 |
In fracture-mechanics modelling and simulation, the region at the crack tip over which an assumed traction (load-displacement) relation has to be overcome to permit initiation and propagation of a crack. 在断裂力学建模和模拟中，必须克服假定的牵引（载荷-位移）关系以允许裂纹萌生和扩展的裂纹尖端区域。 |
| Joint diagrams | 接合处关系图 |
Mathematical diagrams which illustrate the forces on and deflections of fasteners and joint members. 说明紧固件和连接件上的力和变形的数学图。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Nautical mile (M) | 海里（M） |
A special unit of distance employed for marine and aerial navigation. The conversion to SI is 1 M = 1 852 m. 用于海上和空中导航的特殊距离单位。SI的转换为1M＝1852m。 |
| Solenoid | 螺线管 |
A coil of electrically-conducting wire wrapped around a metal core, typically iron, to produce a magnetic field and hence a force on the core when an electric current passes through the coil. Solenoids are widely used to produce linear movement to actuate valves (solenoid valves) and other devices. 绕在金属芯（通常为铁）上的导线线圈，当电流通过线圈时产生磁场，从而在芯上产生力。电磁阀广泛用于产生线性运动以驱动阀（电磁阀）和其他装置。 |
| Standard gauge | 标准量规 |
A highly-accurate reference gauge against which to check working gauges. 一种高精度的基准量规，用于检查工作量规。 |
| Kinetic friction | 动摩擦 |
(dynamic friction, sliding friction) (Unit N) The sliding resistance to relative motion of two surfaces in contact with each other. （动摩擦，滑动摩擦）（单位N）两个相互接触的表面相对运动的滑动阻力。 |
| Dynamic modulus | 动态模量 |
The ratio of stress to strain under cyclic conditions (calculated from data obtained from either free or forced vibration tests, in shear, compression, or tension). 循环条件下的应力与应变之比（根据在剪切、压缩或拉伸中的自由或强制振动测试中获得的数据计算得出）。 |
| Neutralization number | 中和值 |
An ASTM number given to quenching oils that reflects the oil’s tendency towards oxidation and sludging. 淬火油的ASTM编号，反映了油的氧化和成泥趋势。 |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| Impact energy (Unit J) | 冲击能量（单位J） |
The amount of energy required to fracture a material, usually measured by means of an Izod test or Charpy test.The type of specimen and test conditions affect the values and therefore should be specified. 1. The sum of the kinetic energies of all the bodies involved at the instant of collision of two or more moving bodies. 2. The energy required to fracture a specimen in a Charpy or Izod impact test. 使材料断裂所需的能量，通常通过悬臂梁式试验或夏比试验测量。试样类型和试验条件会影响数值，因此应加以说明。1.两个或多个运动物体碰撞瞬间所有物体的动能之和。2.夏比或悬臂冲击试验中断裂试样所需的能量。 |
| Fog quenching | 雾淬 |
Quenching in a fine vapor or mist. 在细蒸汽或薄雾中淬火。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Active accommodation | 主动适应能力 |
The use of information from sensors, for example, in a vision system, that allows a robot to show accommodation to the environment. 使用来自传感器的信息，例如在视觉系统中，允许机器人显示对环境的适应。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Eutectic | 共晶 |
(1) An isothermal reversible reaction in which a liquid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectic point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by a eutectic reaction. （1）一种等温可逆反应，其中液体溶液在冷却时转化为两种或两种以上紧密混合的固体，形成的固体数量与系统中组分的数量相同。（2）一种合金，其成分由平衡图上的共晶点表示。（3）由共晶反应形成的混合固体成分的合金结构。 |
| Transmission dynamometer | 传动测功机 |
A dynamometer in which the power transmitted by a shaft is obtained from the product of its rotation speed and the torque determined from measured shear strains along the shaft. 一种测功机，其中轴传递的功率由其转速和扭矩的乘积获得，扭矩由沿轴测得的剪切应变确定。 |
| Slug wrench | 缓动扳手 |
A box wrench with an anvil on the end of the handle. Torque is produced by striking the anvil with a sledge hammer. 柄端有铁砧的套筒扳手。扭矩是通过用大锤敲击铁砧产生的。 |
| Decompression chamber | 减压舱 |
A chamber in which ambient-air pressure can be increased to levels found in deep-sea diving. It is used to gradually acclimatize divers back to normal conditions and avoid ‘the bends’. 环境气压可以提高到深海潜水水平的腔室。它用于逐渐使潜水员适应正常条件，避免“弯曲”。 |
| Impact loads | 冲击载荷 |
Especially severe shock loads such as those caused by instantaneous arrest of a falling mass, shock meeting of two parts (in a mechanical hammer, for example), or by explosive impact, in which there can be an exceptionally rapid build-up of stress. 特别严重的冲击载荷，例如由下落质量的瞬时停止、两部分的冲击碰撞（例如在机械锤中）或爆炸性冲击引起的冲击载荷，其中可能会出现异常快速的应力积聚。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| Fastener manufacturer | 紧固件制造商 |
An organization that fabricates raw steel into a fastener meeting specified standards. 将生钢加工成符合规定标准的紧固件的组织。 |
| Rolled thread | 滚制螺纹 |
A thread formed by plastically deforming the surface of the blank rather than by cutting operations. Increases fatigue life and thread strength, but is not possible (or perhaps economical) on larger sizes. 通过塑性变形坯料表面而不是通过切割操作形成的螺纹。增加疲劳寿命和螺纹强度，但不太可能（或者说是经济上不太可能）用于较大的尺寸。 |
| Breaks | 断裂 |
Creases or ridges usually in “untempered” or in aged material where the yield point has been exceeded. Depending on the origin of the break, it may be termed a cross break, a coil break, an edge break, or a sticker break. 通常在“未回火”或超过屈服点的老化材料中出现折痕或隆起。根据断裂的起源，它可能被称为交叉断裂、线圈断裂、边缘断裂或贴纸断裂。 |
| Crack size (a) | 裂纹尺寸（a） |
A lineal measure of a principal planar dimension of a crack. This measure is commonly used in the calculation of quantities descriptive of the stress and displacement fields. In practice, the value of crack size is obtained from procedures for measurement of physical crack size, original crack size, or effective crack size, as appropriate to the situation under consideration. 裂纹主平面尺寸的线性度量。这种测量通常用于计算描述应力场和位移场的量。在实践中，裂纹尺寸的值是通过测量物理裂纹尺寸、原始裂纹尺寸或有效裂纹尺寸的程序获得的，视情况而定。 |
| Graphitizing | 石墨化退火 |
Annealing a ferrous alloy in such a way that some or all of the carbon is precipitated as graphite. 以使部分或全部碳以石墨的形式沉淀的方式对铁合金进行退火。 |
| Process annealing | 中间退火 |
An imprecise term denoting various treatments used to improve workability. For the term to be meaningful, the condition of the material and the time-temperature cycle used must be stated. 一个不精确的术语，表示用于改善可加工性的各种处理方法。为了使术语有意义，必须说明材料的条件和使用的时间-温度循环。 |
| Temporal decomposition | 时间分解 |
The splitting of a control problem into parts with relatively short and long time constant so that different controllers may be used for the different parts. 将控制问题分解为具有相对较短和较长时间常数的部分，以便不同的部分可以使用不同的控制器。 |
| Counter sink | 台面水槽 |
To cut or shape a depression in an object so that the head of a screw may set flush or below the surface. 在物体上切割或塑造一个凹陷，使螺钉的头部可以齐平或低于表面。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Stability | 稳定性 |
1. A term relating to whether a body, structure, system, or flow is in a state of stable, unstable, or neutral equilibrium. 2. In numerical analysis, whether numerical errors, such as roundoff or input-data errors, are damped, propagate, or cause divergence of the solution as the numerical method proceeds. 3. A control system is often described as stable when a step change in input results in a steady output without continuing oscillation. 1.与物体、结构、系统或流是否处于稳定、不稳定或中性平衡状态有关的术语。2.在数值分析中，随着数值方法的进行，数值误差（如舍入误差或输入数据误差）是否衰减、传播或导致解发散。3.当输入的阶跃变化导致稳定输出而无持续振荡时，控制系统通常被描述为稳定的。 |
| Transition temperature (Unit K) | 转变温度（单位K） |
(1) An arbitrarily defined temperature that lies within the temperature range in which metal fracture characteristics (as usually determined by tests of notched specimens) change rapidly, such as from primarily fibrous (shear)to primarily crystalline (cleavage) fracture. (2) Sometimes used to denote an arbitrarily defined temperature within a range in which the ductility changes rapidly with temperature. (transition point) 1. The temperature at which the mechanism of fracture in metal alloys having a face-centred cubic crystal structure changes from ductile void growth to brittle cleavage. 2. The temperature at which a material changes from one crystal state to another. （1） 任意定义的温度，位于金属断裂特性（通常通过缺口试样的试验确定）快速变化的温度范围内，如从主要纤维（剪切）断裂到主要结晶（解理）断裂。（2） 有时用于表示延性随温度快速变化的范围内的任意定义的温度。（转变点）1.具有面心立方晶体结构的金属合金的断裂机制从韧性孔洞生长转变为脆性解理的温度。2.材料从一种晶体状态转变为另一种晶体的温度。 |
| Fit | 装配 |
The general term used to signify the range of tightness which may result from the application of a specific combination of allowances and tolerances in the design of mating parts. 通用术语，用于表示配合零件设计中公差和公差的特定组合可能导致的紧密性范围。 |
| Turn-of-nut | 转动螺母 |
Sometimes used to describe the general rotation of the nut (or bolt head) as the fastener is tightened. More often used to define a particular tightening procedure in which a fastener is first tightened with a preselected torque, and is then tightened further by giving the nut an additional, measured, turn such as ‘‘three flats’’ (180°). 有时用于描述紧固件拧紧时螺母（或螺栓头）的总体旋转。更常用于定义一种特定的紧固程序，在该程序中，首先以预选扭矩拧紧紧固件，然后通过使螺母额外转动，如“三平面”（180°）进一步拧紧。 |
| Screw pair | 螺旋副 |
Two links connected together to form a kinematic pair, in which the contacting surfaces are screw threads, so that their relative motion consists of rotation and sliding. 两个连杆连接在一起形成运动副，其中接触面为螺纹，因此它们的相对运动包括旋转和滑动。 |
| Total elongation | 总伸长率 |
A total amount of permanent extension of a test piece broken in a tensile test. 拉伸试验中断裂试样的永久延伸总量。 |
| Spray quenching | 喷雾淬火 |
A quenching process using spray nozzles to spray water or other liquids on a part. The quench rate is controlled by the velocity and volume of liquid per unit area per unit of time of impingement. 使用喷嘴将水或其他液体喷射到零件上的淬火过程。淬火速率由每单位撞击时间内每单位面积的液体速度和体积控制。 |
| Unit | 单位 |
A numerical indication of the magnitude of a physical quantity. The basic units of mass, length, time, etc. are relative to agreed standards. 物理量大小的数字指示。质量、长度、时间等基本单位与商定的标准相对应。 |
| Transfer machines | 转印机 |
These specialized machine tools are used to perform various machining operations on parts or parts in fixtures as the parts are moved along on an automatic conveyor which is part of the machine tool set-up. In a set-up, the parts can move in a straight line from their entry point to their exit point, or the setup may be constructed in a U-shape so that the parts are expelled near where they start. 当零件在自动输送机上移动时，这些专用机床用于对零件或夹具中的零件执行各种加工操作，自动输送机是机床设置的一部分。在设置中，零件可以从其入口点直线移动到其出口点，或者设置可以构造为U形，以便零件在其起点附近排出。 |
| Grain refiner | 晶粒细化机 |
A material added to a molten metal to induce a finer-than-normal grain size in the final structure. 添加到熔融金属中以在最终结构中产生比正常晶粒尺寸更细的材料。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| Congruent transformation | 全等变换 |
An isothermal or isobaric phase change in which both of the phases concerned have the same composition throughout the process. 等温或等压相变，其中相关的两个相在整个过程中具有相同的成分。 |
| Caustic quenching | 苛性淬火 |
Quenching with aqueous solutions of 5 to 10% sodium hydroxide (NaOH). 用5%至10%氢氧化钠（NaOH）水溶液淬灭。 |
| Washer | 垫圈 |
An annular disc of metal, rubber, plastic, ceramic, etc., placed between two surfaces in contact either to spread the load (for example, between a surface and a tightened nut or a bolt head), to provide a seal, or to separate or align components. 由金属、橡胶、塑料、陶瓷等制成的环形圆盘，放置在两个接触面之间，以分散载荷（例如，在一个表面和拧紧的螺母或螺栓头之间），提供密封，或分离或对齐部件。 |
| Carbon steels | 碳钢 |
(plain carbon steels) Steels in which carbon is the principal alloying element, and the amount of manganese does not exceed 1.65% and the copper and silicon contents are less than 0.60%. There are three main types: low-carbon steels (0.08–0.35% carbon); medium-carbon steels (0.35–0.50% carbon); and high-carbon steels (0.50–2.0% carbon). （普通碳钢）以碳为主要合金元素，锰含量不超过1.65%，铜和硅含量低于0.60%的钢。主要有三种类型：低碳钢（0.08-0.35%碳）；中碳钢（0.35–0.50%碳）；和高碳钢（0.50–2.0%碳）。 |
| Intercritical annealing | 临界退火 |
Any annealing treatment that involves heating to, and holding at, a temperature between the upper and lower critical temperatures to obtain partial austenitization, followed by either slow cooling or holding at a temperature below the lower critical temperature. 任何退火处理，包括加热至并保持在上临界温度和下临界温度之间的温度，以获得部分奥氏体化，然后缓慢冷却或保持在低于下临界温度的温度。 |
| Ideal crack | 理想裂缝 |
A simplified model of a crack used in elastic-stress analysis. In a stress-free body, the crack has two smooth surfaces that are coincident and join within the body along a smooth curve called the crack front; in two-dimensional representations, the crack front is called the crack tip. 用于弹性应力分析的裂纹简化模型。在无应力物体中，裂纹有两个光滑表面，它们在物体内沿称为裂纹前缘的平滑曲线重合并连接；在二维表示中，裂纹前缘称为裂纹尖端。 |
| Turn-of-nut method | 螺母转动法 |
It applies preload by turning a nut through an angle that corresponds to a given elongation. 它通过将螺母旋转一个与给定伸长率相对应的角度来施加预载荷。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Brittle | 脆性材料 |
A brittle material is one that breaks, often suddenly, with no permanent deformation. Examples of brittle materials are some cast irons, glass, concrete, and some plastics. A bolt is said to be brittle if it will break when stretched only a small amount past its yield point. 脆性材料通常会突然断裂，不会产生永久变形。脆性材料的例子有一些铸铁、玻璃、混凝土和一些塑料。如果螺栓在拉伸时仅超过其屈服点一小部分就会断裂，则称其为脆性螺栓。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Shore hardness | 肖氏硬度 |
A measure of the hardness of materials such as elastomers, plastics, and rubbers determined using a Shore durometer which measures the penetration depth of a hardened steel rod (the indenter) 1.1–1.4 mm in diameter into the test material for a given force applied rapidly with a calibrated spring. There are two main indenter designs: type A (for softer materials) for which the end of the rod is a truncated 35° cone tapering to a diameter of 0.79 mm, and type D (harder materials) for which the end is a 30° cone with a 0.1 mm radius tip. The spring force is 8.05 N for type A and 44.45 N for type D. The hardness value is related to the penetration depth (limited to a maximum of 2.5 mm) such that for zero penetration the hardness is 100 and for maximum penetration the hardness is zero. The relevant standards are ISO 48-1, 48-4, and 48-7. Shore hardness values of selected materials are as follows: ABS 100, cellulose acetate 50–95, high-density polyethylene 60–70, low density polyethylene 40–50, polymethylmethacrylate 90–99, PTFE 50–65, and plasticized PVC 15–70. 使用肖氏硬度计测量弹性体、塑料和橡胶等材料的硬度，肖氏硬度仪测量直径为1.1–1.4mm的硬化钢棒（压头）在用校准弹簧快速施加的给定力下渗入试验材料的深度。有两种主要的压头设计：A型（适用于较软的材料），其杆端为截头35°锥形，逐渐变细至直径0.79 mm；D型（较硬的材料），端部为30°锥形，尖端半径为0.1mm。A型的弹簧力为8.05N，D型为44.45N。硬度值与渗透深度相关（最大限制为2.5mm），因此，对于零渗透，硬度为100，对于最大渗透，硬度是零。相关标准为ISO 48-1、48-4和48-7。所选材料的肖氏硬度值如下：ABS100、醋酸纤维素50-95、高密度聚乙烯60-70、低密度聚乙烯40-50、聚甲基丙烯酸甲酯90-99、PTFE50-65和塑化PVC15-70。 |
| Span (Unit m) | 跨度（单位：m） |
A dimension measured between the extremities of a body or structure, such as between the tips of a wing or the supports of a bridge. 在身体或结构的末端之间测量的尺寸，如机翼尖端或桥梁支架之间。 |