| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Bearing strain | 轴承应变 |
The ratio of the deformation of the bearing hole, in the direction of the applied force, to the pin diameter in a bearing test. 轴承孔在作用力方向上的变形与轴承测试中销直径的比值。 |
| Fastener with waisted shank | 带腰柄的紧固件 |
Finished fastener with a shank diameter of ds < d2. 柄径ds |
| Screw thread | 螺纹 |
A ridge of uniform section or shape in the form of a helix on the external or internal surface of a cylinder, or in the form of a conical spiral on the external or internal surface of a cone. 在圆柱体的外表面或内表面上呈螺旋形或在圆锥体的外表面和内表面上以锥形螺旋形的均匀截面或形状的脊。 |
| Elongation | 伸张率 |
A term used in mechanical testing to describe the amount of extension of a test piece when stressed. 机械测试中使用的术语，用于描述试样在受力时的延伸量。 |
| Physical testing | 物理测试 |
Methods used to determine the entire range of physical properties of a material. In addition to density and thermal, electrical, and magnetic properties, physical testing methods can be used to assess simple fundamental physical properties such as color, crystalline form, and melting point. 用于确定材料整个物理特性范围的方法。除了密度和热、电、磁特性外，物理测试方法还可用于评估简单的基本物理特性，如颜色、结晶形式和熔点。 |
| Shore hardness | 肖氏硬度 |
A measure of the hardness of materials such as elastomers, plastics, and rubbers determined using a Shore durometer which measures the penetration depth of a hardened steel rod (the indenter) 1.1–1.4 mm in diameter into the test material for a given force applied rapidly with a calibrated spring. There are two main indenter designs: type A (for softer materials) for which the end of the rod is a truncated 35° cone tapering to a diameter of 0.79 mm, and type D (harder materials) for which the end is a 30° cone with a 0.1 mm radius tip. The spring force is 8.05 N for type A and 44.45 N for type D. The hardness value is related to the penetration depth (limited to a maximum of 2.5 mm) such that for zero penetration the hardness is 100 and for maximum penetration the hardness is zero. The relevant standards are ISO 48-1, 48-4, and 48-7. Shore hardness values of selected materials are as follows: ABS 100, cellulose acetate 50–95, high-density polyethylene 60–70, low density polyethylene 40–50, polymethylmethacrylate 90–99, PTFE 50–65, and plasticized PVC 15–70. 使用肖氏硬度计测量弹性体、塑料和橡胶等材料的硬度，肖氏硬度仪测量直径为1.1–1.4mm的硬化钢棒（压头）在用校准弹簧快速施加的给定力下渗入试验材料的深度。有两种主要的压头设计：A型（适用于较软的材料），其杆端为截头35°锥形，逐渐变细至直径0.79 mm；D型（较硬的材料），端部为30°锥形，尖端半径为0.1mm。A型的弹簧力为8.05N，D型为44.45N。硬度值与渗透深度相关（最大限制为2.5mm），因此，对于零渗透，硬度为100，对于最大渗透，硬度是零。相关标准为ISO 48-1、48-4和48-7。所选材料的肖氏硬度值如下：ABS100、醋酸纤维素50-95、高密度聚乙烯60-70、低密度聚乙烯40-50、聚甲基丙烯酸甲酯90-99、PTFE50-65和塑化PVC15-70。 |
| Kiln | 窑 |
An industrial oven for burning, baking, or drying. 用于燃烧、烘烤或干燥的工业烤箱。 |
| Stroke | 一击 |
1. (stroke length) (Unit m) The linear distance between top dead centre and bottom dead centre of a piston in a reciprocating engine or mechanism. 2. The movement of a piston or plunger in a reciprocating machine to execute a particular function; for example, the exhaust stroke of an engine in which the exhaust gases are expelled from a cylinder. 1.（冲程长度）（单位：m）往复式发动机或机构中活塞上止点和下止点之间的线性距离。2.活塞或柱塞在往复式机器中执行特定功能的运动；例如发动机的排气冲程，其中排气从气缸中排出。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Combined carbon | 复合碳 |
The part of the total carbon in steel or cast iron that is present as other than free carbon. 钢或铸铁中总碳中除游离碳外的部分。 |
| Clearance fit | 间隙配合 |
A range of clearances ranging from close sliding to loose running, i.e. a fit in which the limits for the mating parts always permit assembly. 从紧密滑动到松动运行的一系列间隙，即配合零件的限制始终允许组装的配合。 |
| Cleavage | 分裂 |
The tendency of a material to cleave or split along definite crystallographic planes. 材料沿特定晶面劈裂或分裂的趋势。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Vickers hardness test | 维氏硬度测试 |
An indentation hardness test employing a 136° diamond pyramid indenter (Vickers) and variable loads, enabling the use of one hardness scale for all ranges of hardness—from very soft lead to tungsten carbide. Also know as diamond pyramid hardness test. 采用136°金刚石棱锥压头（维氏硬度计）和可变载荷的压痕硬度测试，能够对从极软铅到碳化钨的所有硬度范围使用一个硬度标度。也称为钻石金字塔硬度测试。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Angle of thread | 螺纹角度 |
The included angle between the sides forming the groove of the screw thread. 形成螺纹凹槽的边之间的夹角。 |
| Net weight (Unit N) | 净重（单位：N） |
The difference between the gross weight of any container including its contents and the tare weight of the empty container. 任何容器（包括其内容物）的毛重与空容器皮重之间的差值。 |
| Full size body | 全尺寸螺纹杆 |
The body of a bolt or screw which has a diameter between the minimum and maximum limits of the major diameter of the thread. 螺栓或螺钉的主体，其直径介于螺纹大径的最小和最大限制之间。 |
| Time quenching | 时间淬火 |
A term used to describe a quench in which the cooling rate of the part being quenched must be changed abruptly at some time during the cooling cycle. 用于描述淬火的术语，其中被淬火零件的冷却速率必须在冷却循环的某个时间突然改变。 |
| Dead space | 死区 |
(dead volume) (Unit m³) That volume of a gas-filled thermometer in which the gas is not at the same temperature as that being measured. （死容）（单位m³）充气温度计的体积，其中气体的温度与被测温度不同。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Single-shear test | 单剪试验 |
(1) A shear test similar to the double-shear test used for round-bar specimens, but that uses only one stationary shear blade. (2) A shear test that uses a sheet or thin-plate specimen. （1）一种剪切试验，类似于用于圆棒试样的双剪切试验，但仅使用一个固定剪切刀片。（2）使用薄板或薄板试样的剪切试验。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Impact strength | 冲击强度 |
The resiliency or toughness of a solid as measured by impact energy. 用冲击能量测量的固体的弹性或韧性。 |
| Grip length | 夹紧长度 |
Combined thickness of all the things clamped together by the bolt and nut, including washers, gaskets, and joint members. 由螺栓和螺母夹紧在一起的所有部件的总厚度，包括垫圈、垫圈和接头构件。 |
| Thread milling | 螺纹铣削 |
Thread milling is a method of cutting screw threads with a milling cutter in a thread mill. Thread milling cutters are either single form or multiple form and are used in either conventional or planetary thread mills. 螺纹铣削是在螺纹铣刀中用铣刀切削螺纹的一种方法。螺纹铣刀为单形或多形，用于传统或行星式螺纹铣刀。 |
| Annealing | 退火 |
A generic term denoting a treatment, consisting of heating to and holding at a suitable temperature followed by cooling at a suitable rate, used primarily to soften metallic materials, but also to simultaneously produce desired changes in other properties or in microstructure. 一个通用术语，表示一种处理，包括加热并保持在合适的温度，然后以合适的速率冷却，主要用于软化金属材料，但也同时产生其他性能或微观结构的所需变化。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Diffusion | 扩散 |
(1) Spreading of a constituent in a gas, liquid, or solid, tending to make the composition of all parts uniform. (2) The spontaneous movement of atoms or molecules to new sites within a material. （1） 一种成分在气体、液体或固体中的扩散，趋于使所有部分的成分均匀。（2） 原子或分子自发运动到材料内的新位置。 |
| Ductile | 延展性材料 |
(ductile material) Describes a material that can be deformed permanently to large strains without fracture. If a bolt can be stretched well past its yield point before breaking, it is said to be ductile. （延展性材料）描述一种可以永久变形到大应变而不断裂的材料。如果螺栓在断裂前可以很好地拉伸超过其屈服点，则称其具有延展性。 |
| Cavitation damage | 气蚀损坏 |
Erosion of a solid surface through the formation and collapse of cavities or bubbles in an adjacent liquid that contains vapor and/or gas. 通过在包含蒸汽和/或气体的相邻液体中形成空穴或气泡并破坏固体表面。 |
| Cavitation tunnel | 空泡试验筒 |
A closed-circuit recirculating water tunnel in which the static pressure can be reduced to sufficiently low levels for cavitation studies to be performed. 一种闭路循环水隧洞，其中静压可降至足够低的水平，以便进行气蚀研究。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Right hand thread | 右旋螺纹 |
A screw thread which advances into the mating part when turned clockwise or to the right. 顺时针或向右转动时进入配合部件的螺纹。 |
| Yield strength | 屈服强度 |
That stress level which will create a permanent deformation of 0.2% or 0.5% or some other small, preselected, amount in a body. Approximately equal to the elastic and proportional limits of the material; a little higher than the proof strength of a bolt. The stress at which a material exhibits a specified deviation from proportionality of stress and strain. An offset of 0.2% is used for many metals. 该应力水平将在物体中产生0.2%或0.5%的永久变形，或其他一些小的、预先选定的量。近似等于材料的弹性和比例极限；略高于螺栓的强度。材料表现出与应力和应变比例的特定偏差的应力。许多金属使用0.2%的偏移量。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Shear stress (Unit Pa) | 剪应力（单位Pa） |
(1) A stress that exists when parallel planes in metal crystals slide across each other. (2) The stress component tangential to the plane on which the forces act. Also known as tangential stress. (shearing stress, tangential stress, τ) 1. The stress which acts parallel to any plane within a solid material. It can arise due to a bending moment, a shear force, or torque applied to the body. 2. The stress corresponding to velocity gradients within a flowing viscous fluid. （剪应力，切向应力，τ）（1）当金属晶体中的平行平面彼此滑动时存在的应力。（2）与力作用平面相切的应力分量。也称为切向应力。1.平行于固体材料内任何平面的应力。它可能是由于施加在身体上的弯矩、剪力或扭矩引起的。2.对应于流动粘性流体内的速度梯度的应力。 |
| Grain refiner | 晶粒细化机 |
A material added to a molten metal to induce a finer-than-normal grain size in the final structure. 添加到熔融金属中以在最终结构中产生比正常晶粒尺寸更细的材料。 |
| Creep | 蠕变 |
The slow, plastic deformation of a body under heavy loads. Time-dependent plasticity. Time-dependent and permanent deformation of material under constant load or stress. The strain increases with time at a rate that increases with increasing temperature. Creep can lead to large strain and eventual failure, and so limit the lifetime of components subjected to load at high temperature. Creep in metals becomes significant at homologous temperatures in excess of about 0.4, e.g. 1200°C for tungsten, 504°C for titanium, 450°C for iron, and 100°C for aluminium. 物体在重载荷下缓慢的塑性变形，随时间变化的可塑性，材料在恒定载荷或应力下随时间变化的永久变形。应变随时间以随温度升高而增加的速率增加。蠕变可能导致大应变和最终失效，从而限制部件在高温下承受载荷的寿命。当同源温度超过约0.4℃时，金属蠕变变得显著，例如钨为1200℃，钛为504℃，铁为450℃，铝为100℃。 |
| Damage | 损伤 |
1. The deterioration of a component or structure in fault or accident conditions, reducing or preventing its ability to perform its intended function. 2. The accumulation of defects or microcracks in the microstructure of a body loaded monotonically or in fatigue, which weakens the body and can lead to crack propagation and failure. 1.部件或结构在故障或事故条件下的劣化，降低或阻止其执行预期功能的能力。2.在承受单调载荷或疲劳载荷的物体的微观结构中累积的缺陷或微裂纹，这会削弱物体，并可能导致裂纹扩展和失效。 |
| Blanking shear test | 落料剪力试验 |
A method used to determine the through-thickness shear strength of sheet material that involves blanking a disk out of flat strip using a simple punch-and-die method. Alson known as punching shear test. 一种用于确定板材全厚度剪切强度的方法，包括使用简单的冲模方法从扁平带材中冲裁出圆盘。也称为冲切试验。 |
| Austenite stabilization | 奥氏体稳定化 |
Decrease, in comparison to a continuous cooling, in the amount of martensite occurring from austenite when cooling is interrupted at a temperature between Ms and Mf. This can be explained by the relaxation of stresses induced in the austenite by martensite crystals occurring before the interruption. The relaxation, in turn, leads to the dislocation rearrangement and their interaction with martensite/austenite interfaces, which makes the interfaces immobile. 与连续冷却相比，当在Ms和Mf之间的温度中断冷却时，从奥氏体中产生的马氏体的量减少。这可以通过中断前发生的马氏体晶体在奥氏体中引起的应力松弛来解释。反过来，松弛导致位错重排及其与马氏体/奥氏体界面的相互作用，这使得界面无法移动。 |
| Malleable cast iron | 可锻铸铁 |
A cast iron made by prolonged annealing of white cast iron in which decarburization or graphitization, or both, take place to eliminate some or all of the cementite. The graphite is in the form of temper carbon. If decarburization is the predominant reaction, the product will exhibit a light fracture surface, hence, “whiteheart malleable;” otherwise, the fracture surface will be dark, hence, “blackheart malleable.” Ferritic malleable has a predominantly ferritic matrix; pearlitic malleable may contain pearlitic, spheroidite or tempered martensite depending on heat treatment and desired hardness. 白口铸铁一种通过长时间退火制成的铸铁，脱碳，石墨化，或两者都发生，以消除部分或全部渗碳体。石墨是回火碳的形式。如果脱碳是主要反应，产品将呈现出较轻的断裂表面，“白心可锻”。否则，断裂表面将变暗，“黑心可锻”。铁素体可锻性材料主要为铁素体基体；根据热处理和所需硬度，珠光体可锻材料可能包含珠光体、球状体或回火马氏体。 |
| Turn-of-nut | 转动螺母 |
Sometimes used to describe the general rotation of the nut (or bolt head) as the fastener is tightened. More often used to define a particular tightening procedure in which a fastener is first tightened with a preselected torque, and is then tightened further by giving the nut an additional, measured, turn such as ‘‘three flats’’ (180°). 有时用于描述紧固件拧紧时螺母（或螺栓头）的总体旋转。更常用于定义一种特定的紧固程序，在该程序中，首先以预选扭矩拧紧紧固件，然后通过使螺母额外转动，如“三平面”（180°）进一步拧紧。 |
| Standard gauge | 标准量规 |
A highly-accurate reference gauge against which to check working gauges. 一种高精度的基准量规，用于检查工作量规。 |
| Tensioner | 张紧器 |
A hydraulic tool used to tighten a fastener by stretching it rather than by applying a substantial torque to the nut. After the tension has stretched the bolt or stud, the nut is run down against the joint with a modest torque, and the tensioner is disengaged from the fastener. The nut holds the stretch produced by the tensioner. 一种液压工具，用于通过拉伸紧固件而不是对螺母施加较大扭矩来拧紧紧固件。张力拉伸螺栓或螺柱后，以适当的扭矩将螺母向下压靠接头，张紧器与紧固件分离。螺母保持张紧器产生的拉伸。 |
| Ultrasonic extensometer | 超声波伸长计 |
An electronic instrument which measures the change in length of a fastener ultrasonically as, or before and after, the fastener is tightened. 一种电子仪器，可在紧固件拧紧时或前后通过超声波测量紧固件长度的变化。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Pulley | 带轮 |
A free or driven wheel on a shaft with an appropriately shaped rim to carry a flat belt, vee belt, notched belt, rope, or chain. Used to transmit power or motion. 轴上的自由轮或从动轮，具有适当形状的轮缘，以承载平皮带、V形皮带、槽口皮带、绳索或链条。用于传递动力或运动。 |
| Heat balance (heat budget) | 热平衡（热预算） |
An energy balance involving only heat transfer across the system boundary and the stored energy. 仅涉及跨系统边界的热传递和存储能量的能量平衡。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Roots blower | 罗茨鼓风机 |
(rotary-piston blower) A positive-displacement gas compressor with two meshing lobed rotors that rotate within a close-fitting casing. Commonly used as a supercharger. （旋转活塞鼓风机）一种容积式气体压缩机，具有两个啮合的凸角转子，在紧密配合的外壳内旋转。通常用作增压器。 |
| Shoulder | 轴肩 |
The portion of a shaft, stepped component, or flanged component, where a change in diameter or other dimension occurs. Even for a nominal step change, in practice there will be a radius where shoulder and shaft meet in order to avoid too severe a stress concentration. 轴、阶梯部件或法兰部件的直径或其他尺寸发生变化的部分。即使是名义阶跃变化，在实践中，肩部和轴相交处也会有一个半径，以避免出现过严重的应力集中。 |
| Dead centre | 止点 |
The point at which, in a crank mechanism, the piston connecting rod and crank are all in line so that there can be no driving moment. 在曲柄机构中，活塞连杆和曲柄都在一条线上，因此不会有驱动力矩。 |
| Rated flow (Unit m³/s or kg/s) | 额定流量（单位：m³/s或kg/s） |
In a hydraulic system or machine, the volume or mass flow rate a manufacturer specifies for a component as the maximum desirable for it to function as designed. 在液压系统或机器中，制造商为部件指定的体积或质量流量是其按设计运行所需的最大值。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Materials selection | 材料选择 |
The process of selecting the most suitable material for a particular application. In the case of solid materials, it involves assessment of candidate materials in terms of their physical properties (density, elastic moduli, fracture toughness, yield strength, hardness, fatigue resistance, coefficient of thermal expansion, thermal conductivity, resistance to thermal shock, creep resistance, corrosion resistance, radiation resistance, etc), and such factors as the function of the final product, its shape, method of manufacture, required tolerances, number to be made, ease of inspection and quality control, cost, and design methodology employed. 为特定应用选择最合适材料的过程。对于固体材料，它涉及根据其物理特性（密度、弹性模量、断裂韧性、屈服强度、硬度、抗疲劳性、热膨胀系数、导热系数、抗热冲击性、抗蠕变性、耐腐蚀性、抗辐射性等）评估候选材料，以及诸如最终产品的功能、其形状、制造方法、所需公差、制造数量、检查和质量控制的容易程度、成本和采用的设计方法等因素。 |
| Cavitation-resistance inducer | 抗气蚀诱导剂 |
An axial-flow pump used upstream of a main pump in order to prevent cavitation in the latter by increasing the inlet head. 在主泵上游使用的轴流泵，通过增加进口压头防止主泵出现气穴。 |
| Solenoid | 螺线管 |
A coil of electrically-conducting wire wrapped around a metal core, typically iron, to produce a magnetic field and hence a force on the core when an electric current passes through the coil. Solenoids are widely used to produce linear movement to actuate valves (solenoid valves) and other devices. 绕在金属芯（通常为铁）上的导线线圈，当电流通过线圈时产生磁场，从而在芯上产生力。电磁阀广泛用于产生线性运动以驱动阀（电磁阀）和其他装置。 |
| Residual stress (Unit Pa) | 残余应力（单位Pa） |
Stresses that remain within a body as the result of thermal or mechanical treatment or both. (internal stress) An internal-stress system found in components that have experienced elastic unloading from non-uniform plastic-strain fields during manufacture. 由于热处理或机械处理或两者兼而有之而留在物体内的应力。（内应力）在制造期间从非均匀塑性应变场经历弹性卸载的部件中发现的内应力系统。 |
| Elasticity | 弹性 |
The property of a material by virtue of which deformation caused by stress disappears on removal of the stress. A perfectly elastic body completely recovers its original shape and dimensions after release of stress. 一种材料的特性，通过这种特性，由应力引起的变形在去除应力后消失。完全弹性体在应力释放后完全恢复其原始形状和尺寸。 |
| Double tempering | 双回火 |
A treatment in which a quench-hardened ferrous metal is subjected to two complete tempering cycles, usually at substantially the same temperature, for the purpose of ensuring completion of the tempering reaction and promoting stability of the resulting microstructure. 一种处理，其中淬火硬化的黑色金属经过两个完整的回火循环，通常在基本相同的温度下，以确保完成回火反应并提高所得微观结构的稳定性。 |
| Honing | 珩磨 |
Honing is a controlled, low-speed sizing and surface-finishing process in which stock is removed by the shearing action to the bonded abrasive grains of a honing stone, or stick. Finish polishing of surfaces and cutting edges in which very fine abrasive powders, such as rouge, are employed. Honing is usually applied to cylindrical surfaces and lapping to flat, but the usage is not consistent. 珩磨是一种受控的低速尺寸和表面精加工工艺，其中通过对珩磨石或棒的粘结磨粒的剪切作用去除原料。表面和切削刃的精抛光，其中使用了非常细的研磨粉，例如胭脂。珩磨通常用于圆柱面，研磨至平面，但用法并不一致。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Brine quenching | 盐水淬火 |
A quench in which brine (salt water-chlorides, carbonates, and cyanides) is the quenching medium. The salt addition improves the efficiency of water at the vapor phase or hot stage of the quenching process. 一种淬火，其中盐水（盐水-氯化物、碳酸盐和氰化物）是淬火介质。添加盐提高了水在淬火过程的气相或热阶段的效率。 |
| Wallner lines | Wallner线 |
A distinct pattern of intersecting sets of parallel lines, usually producing a set of V-shaped lines, sometimes observed when viewing brittle fracture surfaces at high magnification in an electron microscope. Wallner lines are attributed to interaction between a shock wave and a brittle crack front propagating at high velocity. Sometimes Wallner lines are misinterpreted as fatigue striations. 一组相交的平行线的独特图案，通常产生一组V形线，有时在电子显微镜下高倍观察脆性断裂表面时观察到。Wallner线归因于高速传播的冲击波和脆性裂纹前沿之间的相互作用。有时Wallner线被误解为疲劳条纹。 |
| Slip joint | 滑动接头 |
A mechanical connection which allows limited endwise relative movement of two components such as pipes, rods, and ducts. 一种机械连接，允许两个部件（如管道、杆和管道）进行有限的轴向相对运动。 |
| Cylinder head | 气缸盖 |
The machined casting, typically of aluminium alloy or cast iron, that fits above the cylinder block of a piston engine and closes off the cylinders. It normally includes part of the combustion chambers and holes for the valves and spark plugs. 活塞式发动机缸体上方的机械铸件，通常由铝合金或铸铁制成，用于封闭气缸。它通常包括燃烧室的一部分以及阀门和火花塞的孔。 |
| Spring materials | 弹簧材料 |
Mainly metals including plain-carbon and corrosion-resisting steels, phosphor bronze, spring brass, beryllium copper and nickel alloys, all of which in their workhardened states permit large reversible elastic strains without permanent deformation. 主要是金属，包括普通碳钢和耐腐蚀钢、磷青铜、弹簧黄铜、铍铜和镍合金，所有这些金属在其加工硬化状态下都允许大的可逆弹性应变而不会产生永久变形。 |
| Allowable stress | 许用应力 |
The maximum stress a designer can assume that the parts will stand. It is always less than the minimum strength of the material. For example, the ASME Boiler and Pressure Vessel Code typically specifies an allowable stress that is one-quarter of the service temperature yield strength of the material. This introduces a four-to-one safety factor into the design process and is intended to compensate for uncertainties in estimates of strength, service loads, etc. 设计师可以假设零件能够承受的最大应力。它总是小于材料的最小强度。例如，ASME锅炉和压力容器规范通常指定允许应力为材料使用温度屈服强度的四分之一。这在设计过程中引入了四比一的安全系数，旨在补偿强度、服务载荷等估计的不确定性。 |
| Notch ductility | 缺口延展性 |
The percentage reduction in area after complete separation of the metal in a tensile test of a notched specimen. 在缺口试样的拉伸试验中，金属完全分离后的面积减少百分比。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Carburizing flame | 渗碳火焰 |
A gas flame that will introduce carbon into some heated metals, as during a gas welding operation. A carburizing flame is a reducing flame, but a reducing flame is not necessarily a carburizing flame. 一种气体火焰，会在气焊操作中将碳引入一些加热的金属中。渗碳火焰是还原火焰，但还原火焰不一定是渗碳火焰。 |
| Frequency | 频率 |
(temporal frequency, f) (Unit Hz) The number of cycles per second in an oscillation or the repetition rate for a cyclic process. （时间频率，f）（单位Hz）振荡中每秒的周期数或循环过程的重复率。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Drift pin | 冲头 |
A round tapered steel pin used to align rivet holes so that the rivet will pass through the holes easily. 用于对齐铆钉孔的圆形锥形钢销，以便铆钉轻松穿过孔。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Centrifugal force (Unit N) | 离心力（单位N） |
The inertial reaction force to the centripetal force. It is equal in magnitude but opposite in direction. 惯性反作用力对向心力。它的大小相等，但方向相反。 |
| Guided-bend test | 导向弯曲试验 |
A test in which the specimen is bent to a definite shape by means of a punch (mandrel) and a bottom block. 用冲头（心轴）和底块将试样弯曲成一定形状的试验。 |
| Dynamic coupling | 动态耦合 |
In vibrations, the existence of inertial terms depending on mass in the governing equations, so that there is only a force if there is a corresponding acceleration. 在振动中，惯性项的存在取决于控制方程中的质量，因此只有当有相应的加速度时才有力。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Curie temperature | 居里温度 |
The temperature of magnetic transformation below which a metal or alloy is ferromagnetic and above which it is paramagnetic. 磁性转变温度，低于此温度金属或合金为铁磁性，高于此温度则为顺磁性。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Adhesive joint | 粘合接头 |
The point or area in which two structures are held together by an adhesive. 两个结构通过粘合剂粘合在一起的点或区域。 |
| Mean diameter (Unit m) | 平均直径（单位米） |
The average of the inside and outside diameters for a helical spring or hollow circular cylinder or sphere 螺旋弹簧或空心圆柱体或球体的内径和外径的平均值 |
| Black annealing | 黑退火 |
Box annealing or pot annealing ferrous alloy sheet, strip, wire to impart a black color to the oxidized surface. 对铁合金板、带、线进行箱式退火或罐式退火，使氧化表面呈黑色。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Displacement | 移位 |
The distance that a chosen measurement point on a cracked specimen displaces normal to the crack plane as the crack grows. 随着裂纹扩展，裂纹试样上选定的测量点垂直于裂纹平面位移的距离。 |
| Neutralization number | 中和值 |
An ASTM number given to quenching oils that reflects the oil’s tendency towards oxidation and sludging. 淬火油的ASTM编号，反映了油的氧化和成泥趋势。 |
| Depth (Unit m) | 深度（单位米） |
1. The vertical distance below a datum surface, especially the sea surface. 2. The distance between the top and bottom of a hole, step in a surface, or a container. 1.基准面以下的垂直距离，尤其是海面。2. 孔的顶部和底部之间的距离、表面上的台阶或容器中的距离。 |
| Bioenergy | 生物能源 |
1. Energy derived from materials such as purpose-grown energy crops, including sugar cane, maize, wheat, and rice, as well as wood, straw, and animal waste, including sewage, manure, and animal litter. 2. A term sometimes used to cover biomass and biofuels together. 1.来自特定种植的能源作物（包括甘蔗、玉米、小麦和大米）以及木材、稻草和动物粪便（包括污水、粪便和动物垃圾）等材料的能源。2.有时用于同时涵盖生物质和生物燃料的术语。 |
| Balance weight | 平衡器 |
A corrective mass used in the static or dynamic balancing of a rotating object. 用于旋转物体的静态或动态平衡的校正质量。 |
| Sigma phase | σ相 |
A hard, brittle, nonmagnetic intermediate phase with a tetragonal crystal structure, containing 30 atoms per unit cell, space group P42/mnm, occurring in many binary and ternary alloys of the transition elements. The composition of this phase in the various systems is not the same, and the phase usually exhibits a wide range in homogeneity. Alloying with a third transition element usually enlarges the field of homogeneity and extends it deep into the ternary section. 一种硬、脆、非磁性中间相，具有四方晶体结构，每单位晶胞含有30个原子，空间群P42/mnm，存在于许多过渡元素的二元和三元合金中。该相在各种系统中的组成不尽相同，并且该相通常表现出宽范围的均匀性。与第三过渡元素的合金化通常会扩大均匀性范围，并将其延伸到三元区。 |
| V-block | V型块 |
A block having a 90° V-shaped recess; used in a workshop to hold round workpieces. 具有90°V形凹槽的块体；在车间里用来装圆形工件。 |
| Coefficient of cubic expansion | 立方膨胀系数 |
The fractional increase in volume per unit temperature rise. 每单位温度升高的体积增加分数。 |
| Transformation temperature | 相变温度 |
The temperature at which a change in phase occurs. The term is sometimes used to denote the limiting temperature of a transformation range. The following symbols are used for iron and steels. 发生相位变化的温度。该术语有时用于表示转变范围的极限温度。以下符号用于钢铁。 |
| Transverse direction | 横向 |
Literally, the “across” direction, usually signifying a direction or plane perpendicular to the direction of working. In rolled plate or sheet, the direction across the width is often called long transverse, and the direction through the thickness, short transverse. 从字面上看，“横穿”方向，通常表示与工作方向垂直的方向或平面。在轧制钢板或薄板中，横跨宽度的方向通常称为长横向，穿过厚度的方向称为短横向。 |
| Strength (Unit Pa) | 强度（单位Pa） |
The maximum stress, in tension, compression, shear, or combinations thereof, that may be monotonically applied to a material, component, or structure before failure (defined as fracture, yielding, buckling, etc. as appropriate). 在破坏前（视情况定义为断裂、屈服、屈曲等），材料、部件或结构在拉伸、压缩、剪切或其组合中可能单调施加的最大应力。 |
| Relaxation rate | 松弛率 |
The absolute value of the slope of a stress-relaxation curve at a given time. 给定时间应力松弛曲线斜率的绝对值。 |
| Freezing point | 冰点 |
The temperature at which a substance changes phase (or state) from liquid to solid. The freezing point for most substances increases as pressure increases. The reverse process, from solid to liquid, is melting; melting point is the same as freezing point. 物质从液态变为固态的温度。大多数物质的冰点随着压力的增加而增加。从固体到液体的逆过程是熔化；熔点与凝固点相同。 |
| Valve plug | 阀塞 |
A conical or cylindrical plug, in which there are transverse holes, in a valve, such as a plug valve. Flow through the holes occurs when the plug is rotated. 阀门中的圆锥形或圆柱形阀塞，其中有横向孔，如旋塞阀。旋转阀塞时，会发生通过孔的流动 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Diffusion coating | 扩散涂层 |
Coating on metal for corrosion- and/or oxidation-resistance. Coatings are produced by heating a metal in contact with an alloy in powder, liquid, or gaseous form at elevated temperature such that atoms of the coating diffuse into the substrate. Examples include chromium, aluminium, or silicon on substrates such as nickel-based superalloys, steels, and refractory metals. 金属上的防腐和/或抗氧化涂层。涂层是通过在高温下加热与粉末、液体或气体形式的合金接触的金属，从而使涂层的原子扩散到基体中而产生的。实例包括基底上的铬、铝或硅，如镍基高温合金、钢和耐火金属。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Fracture test | 断裂试验 |
A test in which a specimen is broken and its fracture surface is examined with the unaided eye or with a low-power microscope to determine such factors as composition, grain size, case depth, or internal discontinuities. 1. The recording of load-deflexion (or stress–strain) in a specimen loaded monotonically until it breaks in tension, compression, shear, or torsion. 2. In fatigue, determination of the number of cycles to fracture for a specimen under different patterns of repeated loading. 3. Experiments to determine fracture toughness. 一种试验，其中试样被破坏并用肉眼或低倍显微镜检查其断裂表面，以确定成分、晶粒尺寸、表层深度或内部不连续性等因素。1.记录单调加载试样的载荷偏转（或应力-应变），直到其在拉伸、压缩、剪切或扭转中断裂。2.在疲劳技术中，确定试样在不同重复载荷模式下的断裂循环次数。3.测定断裂韧性的实验。 |
| Rated power (Unit kW or hp) | 额定功率（单位：千瓦或马力） |
(rated capacity, rated horsepower) The maximum power output that can be sustained continuously for any power-producing machine or system, such as an engine or a power plant. （额定容量、额定马力）任何发电机器或系统（如发动机或发电厂）可连续维持的最大功率输出。 |
| Physical properties | 物理性质 |
Properties of a material the determination of which does not involve the deformation or destruction of the specimen—for example, density, electrical conductivity, coefficient of thermal expansion, magnetic permeability, and lattice parameter. Does not include chemical reactivity or the properties more appropriately regarded as mechanical properties. 不涉及试样变形或破坏的材料特性，例如密度、电导率、热膨胀系数、磁导率和晶格参数。不包括化学反应性或更适当地视为机械的性质。 |
| Cycle annealing | 循环退火 |
An annealing process employing a predetermined and closely controlled time-temperature cycle to produce specific properties or microstructures. 采用预定且严格控制的时间-温度循环来产生特定性能或微观结构的退火工艺。 |
| Scleroscope hardness number (HSc or HSd) | 硬化镜硬度值（HSc或HSd） |
A number related to the height of rebound of a diamond-tipped hammer dropped on the material being tested. It is measured on a scale determined by dividing into 100 units the average rebound of the hammer from a quenched(to maximum hardness) and untempered AISI W5 tool steel test block. 与落在被测材料上的菱形锤的回弹高度相关的数字。通过将锤子从淬火（达到最大硬度）和未淬火的AISI W5工具钢试块上的平均回弹分为100个单位来测量。 |
| Austenite finish temperature (Af) | 奥氏体完成温度（Af） |
Temperature at which the transformation of martensite into austenite completes upon heating. The same designation is also applied to nonferrous alloys in which martensite transforms into some parent phase. 加热时马氏体转变为奥氏体的温度。相同的名称也适用于马氏体转变为某些母相的有色合金。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Torque coefficient | 扭矩系数 |
1. (KT) For a propeller of diameter D, a non-dimensional parameter defined by KT = T/ρΩ2D5 where Ω is the rotational speed (in rad/s) and ρ is the fluid density. 2. (CT) An alternative to (1) for a wind turbine, defined by CT = 2T/ρV2AR where V is the wind speed, A is the swept area of the blades, and R is the blade radius. 3. (K) An empirical coefficient used to calculate the torque T required to achieve an axial load F in a bolt according to T = KFd where d is the nominal bolt diameter. 1.（KT）对于直径为D的螺旋桨，由KT=T/ρΩ2D5定义的无量纲参数，其中Ω是转速（单位为rad/s），ρ是流体密度。2.（CT）对于风力涡轮机（1）的替代方案，由CT=2T/ρV2AR定义，其中V是风速，a是叶片的扫掠面积，R是叶片半径。3.（K）经验系数，用于根据T=KFd计算螺栓中实现轴向载荷F所需的扭矩T，其中d是螺栓标称直径。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Turbine | 涡轮 |
A turbomachine in which a rotor (turbine wheel) or impeller is caused to rotate and convert flow energy into shaft power or thrust. 转子（涡轮）或叶轮旋转并将流动能量转换为轴功率或推力的涡轮机。 |
| Cap | 帽 |
A cover, often in the form of a short cylinder, one end of which is closed. Typically used to close an orifice or pipe end, on to which it can be pushed, welded, screwed, or attached with fasteners. 一种盖子，通常为短圆柱体，一端封闭。通常用于封闭孔口或管端，可将其推入、焊接、拧紧或用紧固件连接到其上。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Tow | 拖拉 |
1. To cause a vehicle to move by pulling with a rope, chain, bar, etc. 2. A bundle of fibres employed in reinforcement. 1.用绳子、链条、钢筋等拉动车辆移动。2.用于加固的纤维束。 |
| Crosshead | 十字头 |
1. A reciprocating member, sliding between guides, to which the piston rod is firmly attached on one side and to which the connecting rod is pinned on the other for the conversion of reciprocating into rotary motion. 2. The moveable beam in early designs of mechanical testing machines. 3. A screwhead having slots in a + shape that takes a mating screwdriver. 1.一种往复式构件，在导轨之间滑动，活塞杆一侧固定在其上，连杆另一侧固定在该构件上，用于将往复式运动转换为旋转运动。2.机械试验机早期设计中的活动梁。3.一种螺钉头，其具有采用配合螺丝刀的+形槽。 |
| R-curve/Resistance curve | 阻力曲线 |
In linear-elastic fracture mechanics, a plot of crack-extension resistance as a function of stable crack extension, which is either the difference between the physical crack size, or the effective crack size, and the original crack size. R-curves normally depend on specimen thickness and, for some materials, on temperature and strain rate. An increase in fracture toughness with crack propagation shown by rising plots of toughness vs growing crack length. 在线弹性断裂力学中，作为稳定裂纹扩展函数的裂纹扩展阻力图，即物理裂纹尺寸或有效裂纹尺寸与原始裂纹尺寸之间的差值。R曲线通常取决于试样厚度，对于某些材料，还取决于温度和应变率。是随着裂纹扩展，断裂韧性增加，表现为韧性与扩展裂纹长度的上升曲线。 |
| Working load (Unit N) | 工作负荷（单位：N） |
The tension in a bolt in use; tension produced by a combination of Residual preload and a portion (usually) of any External load. The Joint diagram is usually used to predict the approximate working load a fastener will see in service. The load under which a component or structure is designed to operate under normal conditions. 螺栓在使用中的张力；残余预载荷和部分（通常）任何外部载荷的组合产生的张力。连接图通常用于预测紧固件在使用中的近似工作载荷。部件或结构设计为在正常条件下运行的荷载。 |
| Maximum continuous load | 最大连续负载 |
(maximum continuous rating) (Unit kg/s) The maximum rate of steam output that a boiler can supply for a specified period, usually 24 hours. （最大连续额定功率）（单位为kg/s）锅炉在规定时间内（通常为24小时）可供应的最大蒸汽输出率。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Partial annealing | 不完全退火 |
An imprecise term used to denote a treatment given cold-worked material to reduce the strength to a controlled level or to effect stress relief. To be meaningful, the type of material, the degree of cold work, and the time-temperature schedule must be stated. 一个不精确的术语，用于表示冷加工材料的处理，以将强度降低到受控水平或消除应力。为了有意义，必须说明材料类型、冷加工程度和时间-温度计划。 |
| Alloy | 合金 |
1. A metallic material composed of two or more elements, one of which is usually a metal to which the other elements are added, e.g. iron-carbon or aluminium-copper (binary alloy); nickel-chromium-iron (ternary alloy). 2. A plastic produced as a blend of two or more immiscible polymers. This results in material that cannot be achieved by polymerization. 1.由两种或多种元素组成的金属材料，其中一种通常是添加了其他元素的金属，例如铁碳或铝铜（二元合金）；镍铬铁（三元合金）。2.由两种或多种不混溶聚合物混合而成的塑料。这导致无法通过聚合获得的材料。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Atom | 原子 |
The smallest unit of matter that has the properties of a chemical element. The simplest description of an atom (Bohr model) is of a compact nucleus surrounded by one or more orbiting electrons. 具有化学元素性质的最小物质单位。原子的最简单描述（玻尔模型）是由一个或多个轨道电子包围的致密原子核。 |
| Precipitation-hardenable stainless steels | 沉淀硬化不锈钢 |
Precipitation-hardenable stainless steels contain typically 11–18% chromium, 3–10% nickel, 0.05–0.2% carbon, and small additions of manganese, silicon, aluminium, molybdenum, niobium and titanium. These steels can be supplied in a solution-treated condition, which is readily fabricated or machined, and then hardened by an ageing treatment that produces a fine dispersion of second-phase precipitates. They are available in austenitic, semi-austenitic, and martensitic grades. Uses include springs, knives, and pressure vessels. 沉淀硬化不锈钢通常含有11-18%的铬、3-10%的镍、0.05-0.2%的碳以及少量添加的锰、硅、铝、钼、铌和钛。这些钢可在固溶处理条件下供应，该条件易于制造或机加工，然后通过时效处理硬化，从而产生细小的第二相沉淀。它们有奥氏体、半奥氏体和马氏体等级。用途包括弹簧、刀具和压力容器。 |
| Verification | 检验 |
Checking or testing an instrument to ensure conformance with a specification. 检查或测试仪器以确保符合规范。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Compound pendulum | 复摆 |
A rigid body free to swing about an axis. 可绕轴自由摆动的刚体。 |
| Gasket m-factor | 垫片m系数 |
For a gasketed joint of area A in which the clamping force is F, the factor m is defined by F ≥ mpA where p is the pressure that would separate the two halves of the joint and m > 1. 对于面积为A且夹紧力为F的垫片接头，系数m由F≥mpA定义，其中p是分离接头两半的压力，m>1。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Thermoelastic effect | 热弹性效应 |
The change in temperature of material under adiabatic elastic deformation, e.g. when loading is so rapid that the material is not in thermal equilibrium with its surroundings. For most materials, elastic tension lowers the temperature and compression raises it. The reverse occurs in elastomers such as rubber that exhibit entropic elasticity because stretching reduces the number of possible molecular configurations and so reduces the entropy. The thermoelastic effect gives rise to a stress–strain hysteresis loop in cyclic elastic loading and is one mechanism by which vibrational energy is dissipated internally in materials. 材料在绝热弹性变形下的温度变化，例如当加载速度如此之快，以至于材料与其周围环境不处于热平衡时。对于大多数材料，弹性张力降低温度，压缩提高温度。相反的情况发生在弹性体中，如橡胶，其表现出熵弹性，因为拉伸减少了可能的分子构型的数量，从而降低了熵。热弹性效应在循环弹性载荷中产生应力-应变迟滞回线，是振动能量在材料内部耗散的一种机制。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Compression failure | 压缩失败 |
The reduction or removal of a component’s load-bearing capacity in compression, caused by buckling, fracture, crease formation in fibre composites, etc. 由纤维复合材料中的屈曲、断裂、折痕形成等引起的部件在压缩中的承载能力的降低或消除。 |
| Screw feeder | 螺旋给料机 |
A mechanism for handling bulk materials in which a rotating helicoidal screw moves the material axially forward. Similar to a screw conveyor, but required to discharge material at a controlled rate very accurately. It operates with the screw completely full. 一种用于处理散装物料的机构，其中旋转的螺旋螺杆使物料轴向向前移动。类似于螺旋输送机，但需要以受控速率非常精确地排出物料。它在螺杆完全充满的情况下运行。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Minimum stress-intensity factor (Kmin) | 最小应力强度因子（Kmin） |
In fatigue, the minimum value of the stress-intensity factor in a cycle. This value corresponds to the minimum loadwhen the load ratio is 0 and is taken to be 0 when the load ratio is ≤0. 在疲劳中，一个循环中应力强度因子的最小值。该值对应于负载比为0时的最小负载，当负载比为≤0 |
| Overheating | 过热 |
Heating a metal or alloy to such a high temperature that its properties are impaired. When the original properties cannot be restored by further heat treating, by mechanical working, or by a combination of working and heat treating, the overheating is known as burning. 将金属或合金加热至其性能受损的高温。当通过进一步热处理、机械加工或加工与热处理的组合无法恢复原始性能时，过热称为燃烧。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Positive-displacement machine | 正排量机 |
A machine that incorporates pistons, valves, etc. to ensure positive admission and delivery of a working fluid and prevent undesired reversal of flow. This class of machine incorporates all reciprocating compressors and expanders and some types of rotary compressor, the Roots blower, agear pump, a lobe pump, and a vane pump. 包含活塞、阀门等的机器，以确保工作流体的正向进入和输送，并防止不期望的反向流动。这类机器包括所有往复式压缩机和膨胀机以及一些类型的旋转压缩机、罗茨鼓风机、抽水机、凸轮泵和叶片泵。 |
| Standardization | 标准化 |
1. National and international agreements for design, manufacture, materials, performance, practices, requirements, strength, etc. which ensure common results wherever an item is made and wherever used. 2. The manufacture of components so that interchangeability of parts during assembly of new, or repair of old, items is possible without ‘fitting’. 1.关于设计、制造、材料、性能、惯例、要求、强度等的国家和国际协议，确保在任何地方制造和使用物品都能产生共同结果。2.部件的制造，以便在装配新部件或维修旧部件时，无需“装配”即可实现部件的互换性。 |
| Air-hardening steel | 空气硬化钢 |
A steel containing sufficient carbon and other alloying elements to harden fully during cooling in air or other gaseous mediums from a temperature above its transformation range. The terms should be restricted to steels that are capable of being hardened by cooling in air in fairly large sections, about 2 in. (50 mm) or more in diameter. Same as self-hardening steel. 一种钢，含有足够的碳和其他合金元素，可以在空气或其他气体介质中从高于其转变范围的温度冷却过程中完全硬化。这些术语应仅限于能够通过在相当大的截面（直径约2英寸（50毫米）或更大）中通过空气冷却而硬化的钢。与自硬钢相同。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Ferralium | 铁素体钢 |
Ferralium is a type of Super Duplex Stainless Steel which is optimised for use within fasteners. 一种超级双相不锈钢，经过优化用于紧固件。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Computer vision | 计算机视觉 |
The digitization and processing of optical images/patterns by computer in order to recognize parts, orientation, etc. in manufacturing. 通过计算机对光学图像/图案进行数字化和处理，以在制造过程中识别零件、方向等。 |
| Fretting corrosion | 微动腐蚀 |
(1) The accelerated deterioration at the interface between contacting surfaces as the result of corrosion and slight oscillatory movement between the two surfaces. (2) A form of fretting in which chemical reaction predominates. Fretting corrosion is often characterized by the removal of particles and subsequent formation of oxides, which are often abrasive and so increase the wear. Fretting corrosion can involve other chemical reaction products, which may not be abrasive. （1）由于两个表面之间的腐蚀和轻微振荡运动，接触表面之间的界面加速劣化。（2）一种以化学反应为主的微动磨损形式。微动腐蚀通常以颗粒的去除和随后形成的氧化物为特征，这些氧化物通常具有研磨性，因此会增加磨损。微动腐蚀可能涉及其他化学反应产物，这些化学反应产物可能不是磨料。 |
| Shrink ring | 预紧环 |
A ring, which is expanded by heating, is placed around an assembly of parts, and then contracts upon cooling to hold the assembly in place. 通过加热膨胀的环被放置在零件组件周围，然后在冷却时收缩以将组件固定到位。 |
| Finish annealing | 精制退火 |
A subcritical annealing treatment applied to cold-worked low- or medium-carbon steel. Finish annealing, which is a compromise treatment, lowers residual stresses, thereby minimizing the risk of distortion in machining while retaining most of the benefits to machinability contributed by cold working. Compare with final annealing. 适用于冷加工低碳钢或中碳钢的亚临界退火处理。与最终退火相比，精加工退火是一种折衷处理，可降低残余应力，从而最大限度地降低加工中的变形风险，同时保留冷加工对可加工性的大部分好处。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Slip band | 滑带 |
A group of parallel slip lines so closely spaced as to appear as a single line when observed under an optical microscope. 一组平行滑移线，间距如此之近，以至于在光学显微镜下观察时显示为一条直线。 |
| Ideal critical diameter | 理想临界直径 |
(DI). Under an ideal quench condition, the bar diameter that has 50% martensite at the center of the bar when the surface is cooled at an infinitely rapid rate (that is, when H = ∞, where H is the quench severity factor). （DI）在理想淬火条件下，当表面以无限快的速度冷却时（即H=∞, 其中H是淬火严重度因子）。 |
| Fatigue test | 疲劳测试 |
A method for determining the range of alternating (fluctuating)stresses a material can withstand without failing. 一种确定材料可以承受而不会失效的交变（波动）应力范围的方法。 |
| Heat-capacity ratio (c*) | 热容量比（c*） |
A non-dimensional parameter that arises in the analysis of heat exchangers, defined as the ratio cMIN/cMAX where cMIN is the heat-capacity rate c for the fluid with the smaller value of c and cMAX the value for the fluid with the larger value of c. Different flow rates and specific-heat values give rise to different values for c. 热交换器分析中出现的无量纲参数，定义为比率cMIN/cMAX其中cMIN是流体的热容率c，c值较小，cMAX是流体的值具有较大的c值。不同的流速和比热值产生不同的c值。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Screw machine | 螺丝机 |
A machine tool for high-volume manufacture of small turned components from rod or bar. 一种用棒或棒大批量制造小零件的机床。 |
| Complete decarburization | 完全脱碳 |
Decarburization with sufficient carbon loss to show only clearly defined ferrite grains under metallographic examination. 脱碳，具有足够的碳损失，以在金相检查下仅显示清晰定义的铁素体晶粒。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Chain | 链 |
A series of connected links, typically of steel. For lifting, pulling, securing, etc., each link is a closed loop, often in the form of a ring. For power transmission, the links are designed to mesh with the teeth of a sprocket wheel. In contrast to belt drives, chain drives tend to be employed in high-torque applications. 一系列连接的链接，通常是钢制的。对于提升、拉动、固定等，每个链节都是一个闭合环，通常呈环形。对于动力传输，链节设计为与链轮的齿啮合。与皮带传动相比，链传动往往用于高扭矩应用。 |
| Workspace (Unit m³) | 工作空间（单位m³） |
(working-space volume) The volume around the base frame of a robot, defined by the reach of the robot. The robot can thus only perform tasks within this volume. （工作空间体积）机器人基架周围的体积，由机器人的可达范围定义。因此，机器人只能执行该体积内的任务。 |
| Vent | 发泄 |
A small valve that allows the release of pressurized fluid from a pipe, pressure vessel, etc., often to the atmosphere. 一种小阀门，允许将加压流体从管道、压力容器等中释放到大气中。 |
| Nanomanufacturing | 纳米制造 |
1. The manufacture of nanoscale materials. 2. The manufacture of components or devices that have critical dimensions of order 1 nm. 1.纳米材料的制造。2.具有1nm级临界尺寸的部件或装置的制造。 |
| Pressure gauge | 压力表 |
An instrument used to measure absolute or gauge pressure. The sensing element may be a tube which deflects when pressurized, as in a Bourdon gauge, a bellows as in an aneroid barometer, a piezoelectric crystal, a piezoresistive element, etc. 测量绝对压力或表压的仪器。传感元件可以是加压时会偏转的管，如波登压力表、无液气压计中的波纹管、压电晶体、压阻元件等。 |
| Stress relaxation | 应力松弛 |
The slow decrease in stress level within a part (e.g., a bolt) which is heavily loaded under constant deflection conditions. A ‘‘cousin’’ to creep, which is a slow change in geometry under constant stress conditions. The time-dependent decrease in stress in a solid under constant strain at constant temperature due to creep. The stress-relaxation behavior of a metal is usually shown in a stress-relaxation curve. 在恒定挠曲条件下，零件（如螺栓）内的应力水平缓慢降低，该零件承受重荷载。蠕变的“表亲”，是在恒定应力条件下几何结构的缓慢变化。在恒定温度下，由于蠕变，固体在恒定应变下的应力随时间变化的减小。金属的应力松弛行为通常显示在应力松弛曲线中。 |
| Conditioning heat treatment | 调质热处理 |
A preliminary heat treatment used to prepare a material for desired reaction to a subsequent heat treatment. For the term to be meaningful, the exact heat treatment must be specified. 用于制备材料的初步热处理，以便对随后的热处理进行所需的反应。为了使该术语有意义，必须指定确切的热处理。 |
| Circular pitch | 齿距 |
The distance from the center of one gear tooth to the center of the next gear tooth measured on the pitch line. 在节线上测量的从一个轮齿中心到下一个轮齿中心的距离。 |
| Bánki turbine | 班基涡轮机 |
A cross-flow, impulse-type water turbine for very low heads in which a jet of water in the form of a flat sheet passes transversely through the turbine, so going through the runner twice. The thin runner blades which run horizontally across the turbine parallel to the axis of rotation are profiled in cross section. 一种用于非常低水头的横流脉冲式水轮机，其中平板形式的水射流横向穿过涡轮机，因此穿过转轮两次。平行于旋转轴水平穿过涡轮机的薄转轮叶片在横截面上具有轮廓。 |
| Bearing area | 承载面积 |
The product of the pin (or hole) diameter and specimen thickness in a bearing test. (bearing surface) (Unit m²) The projected area of a hole, such as a rivet hole, that carries a transverse load. 轴承测试中销（或孔）直径和试样厚度的乘积。（承载面）（单位m²）承载横向载荷的孔（例如铆钉孔）的投影面积。 |
| Metre (m) | 米（m） |
The base unit of length in the SI system. It is equal to the distance travelled by light in vacuum in 1/299 792 458 seconds. SI系统中长度的基本单位。它等于光在真空中在1/299792458秒内传播的距离。 |
| Finished hexagon bolts | 精制六角螺栓 |
A washer faced or chamfered bearing surface with a close body tolerance. 头下有垫圈面或倒角，尺寸公差小 |
| Carburizing | 渗碳 |
Absorption and diffusion of carbon into solid ferrous alloys by heating, to a temperature usually above Ac3, in contact with a suitable carbonaceous material. A form of case hardening that produces a carbon gradient extending inward from the surface, enabling the surface layer to be hardened either by quenching directly from the carburizing temperature or by cooling to room temperature, then reaustenitizing and quenching. 通过与合适的含碳材料接触加热至通常高于Ac3的温度，将碳吸收和扩散到固体铁合金中。一种表面硬化形式，产生从表面向内延伸的碳梯度，通过直接从渗碳温度淬火或冷却至室温，然后重新奥氏体化和淬火，使表层硬化。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Radian (rad) | 弧度（rad） |
A coherent derived SI unit defined as the plane angle subtended at the centre of a circle by an arc having a length equal to the radius. Thus 2π radians are equivalent to 360° and 1 rad ≈ 57.3°. 一种相干导出的国际单位制单位，定义为在圆心处被长度等于半径的弧对向的平面角。因此，2π弧度相当于360°和1弧度≈57.3°. |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| Slant fracture | 倾斜裂缝 |
A type of fracture appearance, typical of plane-stress fractures, in which the plane of metal separation is inclined at an angle (usually about 45°) to the axis of the applied stress. 一种断裂现象，典型的平面应力断裂，其中金属分离面与施加应力的轴成一定角度（通常约45°）倾斜。 |
| Autonomous energy system | 自主能源系统 |
(stand-alone energy system) A sole source of electricity, usually small-scale, for applications remote from a grid, especially with energy storage in the system. Hydroelectric, photovoltaic, wind-power and other renewable systems are well suited to stand-alone applications. （独立能源系统）一种唯一的电力来源，通常是小规模的，用于远离电网的应用，尤其是系统中的能量存储。水电、光伏、风力和其他可再生能源系统非常适合独立应用。 |
| Proof strength (Unit Pa) | 验证强度（单位Pa） |
(proof stress, Rp, Rp,) The yield strength (offset yield strength) at some fixed value of the permanent strain given by the intersection of a line offset from, but parallel to, the elastic loading line and the engineering stress-engineering strain curve. The offset is arbitrary but is usually 0.1, 0.2, or 0.5% permanent strain (the proof strain). Used for materials which do not exhibit a sharply defined yield point. The notation Rp0.2 or Rp0.2 is employed for the 0.2% proof stress. （验证应力，Rp）在永久应变的某个固定值下的屈服强度（偏移屈服强度），由偏离但平行于弹性加载线的线与工程应力-工程应变曲线的交点给出。偏移是任意的，但通常为0.1、0.2或0.5%的永久应变（验证应变）。用于没有明确定义屈服点的材料。对于0.2%的验证应力，采用符号Rp0.2。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Elastic strain energy | 弹性应变能 |
The energy expended by the action of external forces in deforming a body elastically. Essentially, all the work performed during elastic deformation is stored as elastic energy, and this energy is recovered upon release of the applied force. 在外力作用下使物体弹性变形所消耗的能量。本质上，弹性变形过程中所做的所有功都以弹性能的形式存储，并且在释放所施加的力时恢复该能量。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Reproducibility | 再现性 |
A term used to describe test-result variability associated with specifically defined components of variance obtained both from within a single laboratory and between laboratories. 一个术语，用于描述与从单个实验室内和实验室之间获得的具体定义的方差分量相关的测试结果可变性。 |
| Threading machine | 螺纹机 |
A machine used to cut an external thread on a rod, tube, bolt blank, etc. or an internal thread in a hole, tube, nut blank, etc. 用于切割杆、管、螺栓毛坯等上的外螺纹或孔、管、螺母毛坯等中的内螺纹的机器。 |
| Square thread | 方螺纹 |
A form of screw thread in which the cross–section of the thread forms a square, making the width of the thread equal to the space between the threads. 螺纹的一种形式，螺纹的横截面形成正方形，使螺纹的宽度等于螺纹之间的间距。 |
| Lock-nut pipe thread | 锁紧螺母管螺纹 |
The lock-nut pipe thread is a straight thread of the largest diameter which can be cut on a pipe. Its form is identical with that of the American or Briggs standard taper pipe thread. In general, “Go” gages only are required. These consist of a straight-threaded plug representing the minimum female lock-nut thread, and a straight-threaded ring representing the maximum male lock-nut thread. This thread is used only to hold parts together, or to retain a collar on the pipe. It is never used where a tight threaded joint is required. 锁紧螺母管螺纹是最大直径的直螺纹，可在管道上切割。其形式与美国或布里格斯标准锥管螺纹相同。一般情况下，只需要通规。它们由一个表示最小内螺纹锁紧螺母螺纹的直螺纹塞和一个表示最大外螺纹锁紧螺帽螺纹的直形螺纹环组成。该螺纹仅用于将零件固定在一起，或用于将轴环固定在管道上。切勿使用于需要紧密螺纹接头的情况下。 |
| Expansion bolt | 膨胀螺栓 |
When a through bolt cannot be used for attaching a pipe hanger, bracket, or other part, to a wall or ceiling of brick or concrete, what are known as expansion bolts are often used. The body of an expansion bolt is divided and the arrangement is such that, when the head of the bolt is turned, the sections forming the body of the bolt are forced outward and against the wall of the hole which has been drilled into the brick, concrete, or stone, as the case may be. Bolts of this type are made in quite a variety of designs. The nominal size represents the diameter of the bolt proper and not the diameter of the casing or expansion member. 当不能使用贯穿螺栓将管道吊架、支架或其他部件连接到砖块或混凝土的墙壁或天花板时，通常使用所谓的膨胀螺栓。膨胀螺栓的主体是分开的，其布置方式是，当螺栓头转动时，形成螺栓主体的部分被强制向外并靠在已钻入砖、混凝土或石头中的孔壁上，视情况而定。这种类型的螺栓有多种设计。标称尺寸代表螺栓本身的直径，而不是套管或膨胀构件的直径。 |
| Collapse load (Unit N) | 毁坏荷载（单位N） |
The applied load at which a structure becomes a mechanism owing to the formation of sufficient plastic hinges for collapse to occur. 由于形成足够的塑性铰链以发生坍塌，结构成为机制的施加载荷。 |
| Pressure rating (Unit Pa or bar) | 额定压力（单位Pa或bar） |
The internal pressure at which a pressure vessel, boiler, tank, piping, etc. is designed to operate safely. 压力容器、锅炉、储罐、管道等设计用于安全运行的内部压力。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Critical crack length (Unit m) | 临界裂纹长度（单位米） |
The crack length at which a given stress applied to a body will result in crack propagation and fracture. 施加到物体上的给定应力将导致裂纹扩展和断裂的裂纹长度。 |
| Rockwell superficial hardness test | 洛氏表面硬度试验 |
Same as Rockwell hardness test, except that smaller minor and major loads are used. 与洛氏硬度测试相同，只是使用较小的次要载荷和主要载荷。 |
| Surface tension (σ, γ) (Unit N/m) | 表面张力（σ，γ）（单位：N/m） |
At the interface between a liquid and a gas or two immiscible liquids, unbalanced cohesive forces acting on the liquid molecules at the interface lead to the property surface tension which causes tensile forces to develop as if it were a skin or membrane. 液体和气体或两种不混溶液体之间的界面处，作用在界面处的液体分子上的不平衡内聚力导致表面张力的性质，从而导致张力的发展，就像皮肤或薄膜一样。 |
| Impact | 撞击 |
Sudden loading of a body or component, as in a vehicle collision or striking by a hammer. 物体或部件的突然加载，如车辆碰撞或锤击。 |
| Total elongation | 总伸长率 |
A total amount of permanent extension of a test piece broken in a tensile test. 拉伸试验中断裂试样的永久延伸总量。 |
| Impact wrench | 冲击扳手 |
An air- or electric-powered wrench in which multiple blows from tiny hammers are used to produce output torque to tighten fasteners. A pneumatically-or electrically-powered socket wrench used to tighten or loosen nuts through the application of torque in a rapid series of impulses. 一种气动或电动扳手，使用小锤子多次敲击来产生输出扭矩以拧紧紧固件，用于通过在一系列快速脉冲中施加扭矩来拧紧或松开螺母。 |
| Nano machining | 纳米加工 |
The machining of silicon chips typically less than 1 nm thick. 硅芯片的加工通常小于1nm厚。 |
| Friction loss (Unit J) | 摩擦损失（单位J） |
The conversion of mechanical energy to heat due to friction within a machine, mechanism, linkage, etc. 由于机器、机构、连杆等内部的摩擦而将机械能转化为热能。 |
| Compressor | 压缩机 |
A turbomachine, of either axial or radial type, that increases the pressure of a gas or vapour. 一种增加气体或蒸汽压力的轴向或径向涡轮机。 |
| Wire rope | 钢丝绳 |
A type of cable formed from individual strands of wire with a helical twist. 一种线缆，由具有螺旋扭曲的单独的线股形成。 |
| Spherical washer | 球面垫圈 |
A washer whose upper surface is semispherical. Used with a nut whose contact face is also semispherical. Reduces bending stress in a bolt or stud, by allowing some self-alignment and some compensation for nonparallel joint surfaces or Angularity. 上表面为半球形的垫圈。与接触面也是半球形的螺母一起使用。减少螺栓或螺柱中的弯曲应力，允许一些自对准，并对不平行的接头表面或角度进行一些补偿。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Free ferrite | 游离铁氧体 |
Ferrite that is formed directly from the decomposition of hypoeutectoid austenite during cooling, without the simultaneous formation of cementite. Also proeutectoid ferrite. 在冷却过程中亚共析奥氏体分解直接形成的铁素体，没有同时形成渗碳体。也是先共析铁氧体。 |
| Cavity radiator | 空腔辐射器 |
A heated chamber having a small hole through which radiation, approximating blackbody radiation, passes out. 具有小孔的加热室，近似于黑体辐射的辐射通过该小孔传递出去。 |
| Impact testing | 冲击测试 |
Determination of the mechanical properties of materials under high-rate conditions. Often determined from the behaviour of a testpiece when struck by a pendulum or a weight falling from a known height, or when sandwiched between two Hopkinson bars. 在高速条件下测定材料的机械性能。通常根据测试件在被钟摆撞击或从已知高度坠落的重物或夹在两个霍普金森棒之间时的行为来确定。 |
| Scratch hardness | 划痕硬度 |
The resistance of a material, such as a metal, alloy, plastic, or mineral, to scratching by a much harder indenter, such as a diamond stylus, moved slowly across the surface. The scratch hardness number is computed from the loads and the dimensions of the residual scratch. 一种材料（如金属、合金、塑料或矿物）对更硬的压头（如金刚石触针）划伤的抵抗力，在表面上缓慢移动。根据载荷和残余划痕的尺寸计算划痕硬度值。 |
| Modulus of rupture | 断裂模量 |
Nominal stress at fracture in a bend test or torsion test. In bending, modulus of rupture is the bending moment at fracture divided by the section modulus. In torsion, modulus of rupture is the torque at fracture divided by the polar section modulus. 弯曲试验或扭转试验中的标称断裂应力。在弯曲中，断裂模量是断裂时的弯矩除以截面模量。在扭转中，断裂模量是断裂时的扭矩除以极截面模量。 |
| Vickers hardness number | 维氏硬度值 |
(diamond hardness number, DHN, VHN, VPN) (Unit kg/mm² originally, sometimes now Pa) Indentation hardness given by load divided by the surface area of the permanent impression obtained when the indenter is in the form of a square pyramid whose opposite faces make an angle of 136° with one another. The mean length d of the diagonals of the indentation is determined, from which VPN = 0.927(2W/d2) where W is the load, since the base of the pyramid has an area equal to 0.927 times the surface area. （金刚石硬度值，DHN，VHN，VPN）（最初单位为kg/mm²，有时为Pa）压痕硬度，由载荷除以永久压痕的表面积得出，当压头呈方形棱锥体形式时，其相对面彼此成136°角。确定压痕对角线的平均长度d，其中VPN=0.927（2W/d2），其中W是载荷，因为棱锥底部的面积等于表面积的0.92七倍。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Thermal compressor | 热压缩机 |
1. (thermocompressor) A jet compressor used to boost the pressure of low-pressure waste or exhaust steam. 2. A device consisting of an absorber, a generator, a pump, and a throttling device, used instead of a mechanical vapour compressor in an absorption-cooling refrigeration system. 1.（热压缩机）用于提升低压废蒸汽或排气压力的喷射压缩机。2.一种由吸收器、发电机、泵和节流装置组成的装置，用于替代吸收冷却制冷系统中的机械蒸汽压缩机。 |
| Stress area | 应力面积 |
The effective cross-sectional area of the threaded section of a fastener. Used to compute average stress levels in that section. Based on the mean of pitch and minor diameters. 紧固件螺纹部分的有效横截面积。用于计算该截面中的平均应力水平。基于节距和小直径的平均值。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Normal temperature and pressure (NTP) | 常温常压（NTP） |
Reference conditions defined by NIST as 20°C and 1 atm. NIST定义的参考条件为20°C和1atm。 |
| Transmission | 传输 |
The system that transmits power and torque from a power source; for example a shaft, belts and pulleys, or a gear train. In the case of a motor vehicle, it includes the gearbox, clutch, propeller shaft, differential and final drive shafts. 从动力源传输功率和扭矩的系统；例如轴、皮带和滑轮或齿轮系。对于机动车辆，包括变速箱、离合器、传动轴、差速器和终传动轴。 |
| Dimensioning | 尺寸标注 |
The specification on an engineering drawing of the size (e.g. length, radius, angle, or spacing) and the relative location (e.g. angular position) of each feature of a component. The numerical values often include the tolerances. There should be no more dimensions than are necessary to manufacture the component. 工程图纸上对部件每个特征的尺寸（例如长度、半径、角度或间距）和相对位置（例如角位置）的规范。数值通常包括公差。尺寸不应超过制造组件所需的尺寸。 |
| Specific weight (γ) (Unit N/m³) | 比重（γ）（单位：N/m³） |
The weight per unit volume of a substance: if W is the weight of a volume of the substance, ρ is its density, and g is the acceleration due to gravity, γ = W/ = ρg. 物质单位体积的重量：W是物质体积的重量，ρ是其密度，g是重力引起的加速度，γ=W/=ρg。 |
| Relaxation | 松弛 |
The loss of tension, and therefore Clamping force, in a bolt and joint as a result of Embedment, vibration loosening, gasket creep, differential thermal expansion, etc. 由于嵌入、振动松动、垫圈蠕变、热膨胀差等原因，螺栓和接头中的张力损失，因此夹紧力损失。 |
| Torr | 托尔 |
A non-SI unit of pressure commonly used in vacuum systems; defined by 760 torr = 1 atm so that 1 torr = 133.322 368 4 Pa, and approximately equivalent to the pressure corresponding to 1 mm of mercury. 真空系统中常用的非SI压力单位；由760托=1大气压定义，因此1托=133.3223684帕，近似等于对应于1毫米汞柱的压力。 |
| Ion carburizing | 离子渗碳 |
A method of surface hardening in which carbon ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma carburizing or glowdischarge carburizing. 一种表面硬化方法，利用高压电能将碳离子在真空中扩散到工件中。与等离子渗碳或辉光放电渗碳同义。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Sampling frequency (Unit Hz) | 采样频率（单位Hz） |
(sampling rate) The number of measurement samples per unit time taken from a continuous analogue signal to produce a discrete signal. It is the inverse of the time between successive measurements (sampling interval, sampling period, or sampling time). （采样率）从连续模拟信号中提取以产生离散信号的每单位时间的测量样本数。它是连续测量之间时间的倒数（采样间隔、采样周期或采样时间）。 |
| Sound pressure (Unit μPa) | 声压（单位：μPa） |
The instantaneous deviation of pressure from the ambient pressure caused by the passage of a sound wave, which can be measured by a microphone in air and a hydrophone in water. 声波传播引起的压力与环境压力的瞬时偏差，可通过空气中的麦克风和水中的水听器测量。 |
| Vapour static pressure | 蒸汽静压 |
(Unit Pa or bar) A pressure analogous to hydrostatic pressure, where the fluid is a vapour such as steam. A term used in geothermal applications. （单位Pa或bar）类似于静水压力的压力，其中流体是蒸汽，如蒸汽。地热应用中使用的术语。 |
| Pressure-relief valve | 减压阀 |
A valve that limits the maximum pressure in a pressure vessel or fluid-power system to a specified level. 将压力容器或流体动力系统中的最大压力限制在规定水平的阀门。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Bearing strength | 承载强度 |
The maximum bearing stress that a material is capable of sustaining. 材料能够承受的最大承载应力。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Rosette | 玫瑰形的结 |
Strain gages arranged to indicate, at a single position, strain in three different directions. 应变计布置成在单个位置指示三个不同方向的应变。 |
| Crossed threads | 交叉螺纹 |
When the axis of a nut offered up to a bolt is not aligned with the axis of a bolt (or a screw to a threaded member), it may be possible for the threads to engage incorrectly and even for the nut or screw to advance a turn or more, but ultimately the misaligned threads become locked together. Forcing the nut in such circumstances may irretrievably damage the threads on both. 当提供给螺栓的螺母的轴线与螺栓（或螺纹构件的螺钉）的轴线不对齐时，螺纹可能会错误接合，甚至螺母或螺钉会提前一圈或更多，但最终未对齐的螺纹会锁定在一起。在这种情况下强行拧入螺母可能会对两侧的螺纹造成无法修复的损坏。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Mechanical metallurgy | 机械冶金 |
The science and technology dealing with the behavior of metals when subjected to applied forces. 处理金属在外力作用下的行为的科学技术。 |
| Carbonitriding | 碳氮共渗 |
A case hardening process in which a suitable ferrous material is heated above the lower transformation temperature in a gaseous atmosphere of such composition as to cause simultaneous absorption of carbon and nitrogen by the surface and, by diffusion, create a concentration gradient. The process is completed by cooling at a rate that produces the desired properties in the workpiece. 一种表面硬化工艺，在该工艺中，将合适的含铁材料在气体气氛中加热到较低的转变温度以上，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。该工艺通过以在工件中产生所需性能的速率冷却来完成。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Fibreglass | 玻璃纤维 |
Fibreglass is used in studs and nuts for applications when the fastener should be non-corrosive, low in conductivity, or transparent to electromagnetic waves. 当紧固件应无腐蚀性、低导电性或对电磁波透明时，玻璃纤维用于螺柱和螺母中。 |
| Kilocalorie | 千卡 |
(Cal, kg-cal, kilogram-calorie, large calorie) An obsolete (i.e. non-SI) unit of energy equal to 1 000 cal. （卡，千克卡，千克卡路里，大卡路里）一种已被淘汰的（即非国际单位制）能量单位，等于1000卡。 |
| Turn-of-nut method | 螺母转动法 |
It applies preload by turning a nut through an angle that corresponds to a given elongation. 它通过将螺母旋转一个与给定伸长率相对应的角度来施加预载荷。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Spinner | 旋转器 |
A co-axial streamlined fairing enclosing the hub of a propeller and rotating with it. 一种同轴流线型整流罩，包围螺旋桨毂并随其旋转。 |
| Tensile stress (Unit Pa) | 拉应力（单位Pa） |
A stress that causes two parts of an elastic body, on either side of a typical stress plane, to pull apart. A stress that tends to stretch a component, or local region of a component, when under load. In simple tension it results from the applied axial load, but tensile stresses occur in bending, torsion and other forms of loading. 一种应力，使弹性体的两个部分在典型应力平面的任一侧分离。在负载下，倾向于拉伸部件或部件局部区域的应力。在简单拉伸中，它由施加的轴向载荷产生，但拉伸应力发生在弯曲、扭转和其他形式的载荷中。 |
| Left hand screw | 左螺旋 |
One that screws into the mating part or advances when turned to the left or counter clockwise. 旋入配合部分或向左或逆时针旋转时前进的螺钉。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Furnace | 炉 |
1. A type of combustion chamber in which solid, liquid, or gaseous fuels are burned to supply hot gases to a boiler or other process plant. Examples include the firebox, boiler furnace (steam-generating furnace), hot-air furnace, oil-fired furnace, updraught furnace, and water-cooled furnace. 2. A chamber, sometimes having a controlled atmosphere or under vacuum (vacuum furnace), for heating and melting materials. Examples include the blast furnace, direct- and indirect-arc furnaces, the induction furnace (high-frequency furnace), muffle furnace, reverberatory furnace, and solar furnace. 1.一种燃烧室，其中燃烧固体、液体或气体燃料以向锅炉或其他工艺设备供应热气。示例包括燃烧室、锅炉炉（蒸汽发生炉）、热风炉、燃油炉、上升气流炉和水冷炉。2.用于加热和熔化材料的腔室，有时具有受控气氛或真空（真空炉）。例如高炉、直接和间接电弧炉、感应炉（高频炉）、马弗炉、反射炉和太阳能炉。 |
| Aspect ratio | 纵横比 |
The ratio of the longest to the shortest dimension of a shape or object e.g. the chord-to-thickness ratio of an aerofoil or the span-to-chord ratio of a wing. 形状或物体的最长与最短尺寸之比，例如机翼的弦厚比或机翼的翼展弦比。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Spring clip | 弹簧夹 |
A clip made of a material such as spring steel which grips an inserted part. 由弹簧钢等材料制成的夹子，用于夹住插入的零件。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Elastic calibration device | 弹性校准装置 |
A device for use in verifying the load readings of a testing machine consisting of an elastic member(s) to which loads may be applied, combined with a mechanism or device for indicating the magnitude (or a quantity proportional to the magnitude) of deformation under load. 一种用于验证试验机载荷读数的装置，由可施加载荷的弹性构件组成，与指示载荷下变形量（或与该量成比例的量）的机构或装置相结合。 |
| Fastener standard | 紧固件标准 |
A document which details the attributes of a finished fastener and includes such characteristics as geometry, material or chemistry, heat treatment, finish, testing lot size, and packaging. 详细说明紧固件属性的文件，包括几何形状、材料或化学、热处理、表面处理、测试批量和包装等特性。 |
| Shoulder bolt | 轴肩螺栓 |
A bolt for which the unthreaded cylindrical section between the thread and the head is of larger diameter than the threaded section, precisely machined to length and diameter and hardened 一种螺栓，其螺纹和头部之间的无螺纹圆柱段的直径大于螺纹段的直径，精确加工至长度和直径并硬化 |
| Screw compressor | 螺杆压缩机 |
A positive-displacement rotary compressor in which gas is progressively compressed by two intermeshing, counter-rotating, helical screws. 一种容积式旋转压缩机，其中气体由两个相互啮合、反向旋转的螺旋螺杆逐渐压缩。 |
| Zone melting (zone refining) | 区域熔炼（区域精炼） |
A process of purification of materials in which a narrow molten zone is moved along the length of the material, resulting in impurities being segregated at one end. 一种净化材料的过程，其中一个狭窄的熔融区沿材料长度移动，导致杂质在一端分离。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Activation energy | 活化能 |
(Ea, U) (Unit kJ/mol) The minimum energy for a chemical reaction to occur or for processes such as diffusion to take place in crystals. （Ea, U）（单位kJ/mol）发生化学反应或在晶体中发生扩散等过程的最小能量。 |
| Acoustic pyrometer | 声学高温计 |
A non-intrusive pyrometer based on the principle that the sound speed in a gas is proportional to the square root of its absolute temperature. 一种非侵入式高温计，其原理是气体中的声速与其绝对温度的平方根成正比。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| Gamma iron | 加马铁 |
The face-centered cubic form of pure iron, stable from 910 to 1400 °C (1670 to 2550 °F). 纯铁的面心立方形式，在910至1400°C（1670 2550°F）温度范围内稳定。 |
| Condenser | 冷凝器 |
A heat exchanger in which a substance is changed from its vapour phase to its liquid phase by reducing its temperature to below the saturation temperature. 一种热交换器，通过将物质的温度降低到饱和温度以下，将其从气相变为液相。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Die threading | 模具螺纹 |
Die threading is a machining process for cutting external threads in cylindrical or tapered surfaces by the use of solid or self-opening dies. Die threading is a slower method of producing external threads than thread rolling, but it is faster than single-point threading in a lathe. 模具螺纹加工是一种通过使用实心或自开模具在圆柱形或锥形表面上切削外螺纹的加工工艺。模具螺纹加工是一种比滚丝加工更慢的外螺纹加工方法，但它比车床中的单点螺纹加工要快。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Available draught (Unit Pa) | 可用通风量（单位Pa） |
The reduced pressure of combustion gases in a furnace or boiler, either forced or due to the buoyancy of hot gases, which is used to draw in combustion air and remove products of combustion. 炉子或锅炉中燃烧气体的压力降低，无论是强制还是由于热气体的浮力，用于吸入燃烧空气并去除燃烧产物。 |
| Gage length | 标距 |
The original length of the portion of a specimen over which strain, change of length, or other characteristics are determined. 确定应变、长度变化或其他特性的试样部分的原始长度。 |
| Modulus of elasticity (E) | 弹性模量（E） |
The measure of rigidity or stiffness of a metal; the ratio of stress, below the proportional limit, to the corresponding strain. In terms of the stress-strain diagram, the modulus of elasticity is the slope of the stress-strain curve in the range of linear proportionality of stress to strain. 金属的刚度或刚度的量度；低于比例极限的应力与相应应变之比。根据应力应变图，弹性模量是应力应变曲线在应力应变线性比例范围内的斜率。 |
| Blue annealing | 蓝色退火 |
Heating hot-rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental. 在开放式炉中将热轧铁板加热到转变范围内的温度，然后在空气中冷却，以软化金属。在表面上形成蓝色氧化物是偶然的。 |
| Failure of the joint | 连接失效 |
Failure of a bolted joint to behave as intended by the designer. Failure can be caused or accompanied by broken or lost bolts, but can also mean joint slip or leakage from a gasketed joint even if all bolts still remain whole and in place. Common reasons for joint failure include vibration loosening, poor assembly practices, improper design, unexpected service loads or conditions, etc. 螺栓连接未达到设计者的预期性能。故障可能由螺栓断裂或丢失引起或伴随而来，但也可能意味着即使所有螺栓仍保持完整和就位，也存在接头滑动或垫圈接头泄漏。接头故障的常见原因包括振动松动、装配不当、设计不当、意外的工作负载或条件等。 |
| Tension joint | 张力接头 |
A joint which is primarily subjected to loads acting more or less parallel to the axes of the bolts. 主要承受或多或少平行于螺栓轴线的载荷的接头。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Interrupted quenching | 间断淬火 |
A quenching procedure in which the workpiece is removed from the first quench at a temperature substantially higher than that of the quenchant and is then subjected to a second quenching system having a different cooling rate than the first. 在该淬火过程中，工件在显著高于淬火剂的温度下从第一次淬火中取出，然后经受具有不同于第一次淬火的冷却速率的第二次淬火系统。 |
| Rupture stress | 断裂应力 |
The stress at failure. Also known as breaking stress. 失效时的应力。也称为破裂应力。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Tensiometer | 张力计 |
An instrument used to measure surface tension. 用来测量表面张力的仪器。 |
| Assembly drawing | 装配图纸 |
An engineering drawing that shows how parts are assembled to produce a component or a complete machine. It may include sections to show internal features, dimensions that are critical for assembly, manufacturing information, and part numbers. 显示零件如何组装以生产组件或整机的工程图。它可能包括显示内部特征、对装配至关重要的尺寸、制造信息和零件编号的部分。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Pitting | 点蚀 |
In tribology, a type of wear characterized by the presence of small, sharp surface cavities formed by processes such as fatigue, local adhesion, wear, corrosion, or cavitation. 在摩擦学中的一种磨损，其特征是存在由疲劳、局部粘附、磨损、腐蚀或空穴等过程形成的小而尖锐的表面空穴。 |
| Intercritical annealing | 临界退火 |
Any annealing treatment that involves heating to, and holding at, a temperature between the upper and lower critical temperatures to obtain partial austenitization, followed by either slow cooling or holding at a temperature below the lower critical temperature. 任何退火处理，包括加热至并保持在上临界温度和下临界温度之间的温度，以获得部分奥氏体化，然后缓慢冷却或保持在低于下临界温度的温度。 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Acicular ferrite | 针状铁素体 |
A highly substructured non-equiaxed ferrite that forms upon continuous cooling by a mixed diffusion and shear mode of transformation that begins at a temperature slightly higher than the temperature transformation range for upper bainite. It is distinguished from bainite in that it has a limited amount of carbon available; thus, there is only a small amount of carbide present. Ferrite crystallite growing, apparently, as in the course of bainitic transformation. It has a lath-like shape and an increased dislocation 一种高度亚结构的非等轴铁素体，在连续冷却时通过混合扩散和剪切相变模式形成，其开始温度略高于上贝氏体的温度转变范围。它与贝氏体的区别在于它的碳含量有限。因此，仅存在少量碳化物。显然，铁素体微晶在贝氏体转变过程中生长。它具有板条状的形状和增加的位错。 |
| 显示更多数据，请使用查询功能！ | ||