| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Caustic cracking | 苛性开裂 |
A form of stress-corrosion cracking most frequently encountered in carbon steels or iron-chromiumnickel alloys that are exposed to concentrated hydroxide solutions at temperatures of 200 to 250 °C (400 to 480 °F). Also known as caustic embrittlement. 在200至250°C（400至480°F）的温度下暴露于浓氢氧化物溶液中的碳钢或铁铬镍合金中最常遇到的一种应力腐蚀开裂形式。也称为碱脆。 |
| Thermal energy (heat energy) (Unit J) | 热能（单位：J） |
The sensible and latent forms of internal energy. 内能的感知和潜在形式。 |
| Fastener manufacturer | 紧固件制造商 |
An organization that fabricates raw steel into a fastener meeting specified standards. 将生钢加工成符合规定标准的紧固件的组织。 |
| Congruent melting point (Unit K) | 全等熔点（单位K） |
congruent melting point (Unit K) The temperature at which a solid substance at a specified pressure changes phase to a liquid of identical composition. 一致的熔点（单位K）固体物质在特定压力下相变为具有相同成分的液体时的温度。 |
| O-ring (O-ring seal) | O形圈（O形密封圈） |
A toroidal ring of synthetic rubber seated in a groove machined into a flat or cylindrical surface to act as a seal. 一种环形合成橡胶环，位于加工成平面或圆柱表面的凹槽中，起密封作用。 |
| True stress (σ) (Unit Pa) | 真应力（σ）（单位Pa） |
The value obtained by dividing the load applied to a member at a given instant by the cross-sectional area over which it acts. Compare with engineering stress. The applied load on a test specimen divided by the current cross-section area over which it acts. σ = s expε where s is the engineering stress given by the applied load divided by the original cross-section area over which it acts, and ε is the true strain. 通过将给定时刻施加在构件上的荷载除以其作用的横截面积而获得的值。与工程应力相比。施加在试样上的荷载除以其作用的当前横截面积。σ=s expε，其中s是由施加荷载除以其作用的原始横截面面积得出的工程应力，ε是真实应变。 |
| Horsepower | 马力 |
Unit indicating the rate at which work is done. The electrical equivalent of one horsepower is 746 watts. 单位表示完成工作的速率。一马力的电当量为746瓦。 |
| Achme thread | Achme螺纹 |
A screw thread having an included angle of 29° and largely used for feed screws on machine tools. 一种夹角为29°的螺纹，主要用于机床上的进给丝杠。 |
| Wind pump | 风泵 |
A pump driven directly by a windmill on a tower. Widely used in remote locations. 由塔上的风车直接驱动的泵。广泛应用于偏远地区。 |
| High strength low alloy steels | 高强度低合金钢 |
(HSLA steels) Steels with various micro-alloying elements such as copper, nickel, chromium, molybdenum, niobium, titanium, and vanadium in small quantities that give improved strength (as high as 900 MPa) and corrosion properties compared with plain carbon steels. Improvements are due to grain refinement and precipitation hardening, better control of the chemistry during steel making, and accurate rolling temperatures. （HSLA钢）是含有各种微合金元素的钢，如少量的铜、镍、铬、钼、铌、钛和钒，与普通碳钢相比，具有更好的强度（高达900MPa）和腐蚀性能。这些改进归功于晶粒细化和沉淀硬化、炼钢过程中更好的化学控制以及精确的轧制温度。 |
| Ratchet marks | 棘轮痕 |
Lines on a fatigue fracture surface that result from the intersection and connection of fatigue fractures propagating from multiple origins. Ratchet marks are parallel to the overall direction of crack propagation and are visible to the unaided eye or at low magnification. 疲劳断裂面上由从多个源头传播的疲劳断裂的交叉和连接产生的线。棘轮标记与裂纹扩展的整个方向平行，肉眼或低倍镜下均可看到。 |
| Blade compressor | 叶片式压缩机 |
An oil-free, double-acting rotary compressor in which an angled blade attached to the inner surface of a rotating housing passes through a slot in a disk rotating about an axis perpendicular to that of the housing but offset from it. Air enters through apertures in the housing and leaves through a port in the housing. 一种无油双作用旋转式压缩机，其中连接到旋转外壳内表面的倾斜叶片穿过圆盘上的槽，该槽绕垂直于外壳的轴旋转，但偏离外壳。空气通过壳体中的孔进入，并通过壳体的端口离开。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Safe working load (Unit N) | 安全工作负荷（单位：N） |
The steady or unsteady load against which a component or structure is designed for normal operation. It is lower than that which would cause failure by buckling, fracture, or yielding, so as to accommodate uncertainty, possible fault or accident conditions. 部件或结构设计用于正常运行的稳定或不稳定荷载。该值低于因屈曲、断裂或屈服而导致失效的值，以适应不确定性、可能的故障或事故条件。 |
| Semiguided bend | 半导弯曲 |
The bend obtained by applying a force directly to the specimen in the portion that is to be bent. The specimen is either held at one end and forced around a pin or rounded edge, or is supported near the ends and bent by a force applied on the side of the specimen opposite the supports and midway between them. In some instances, the bend is started in this manner and finished in the manner of a free bend. 通过将力直接施加于待弯曲部分中的试样而获得的弯曲。将试样固定在一端，并围绕销或圆边施力，或者在靠近端部的位置支撑试样，并通过施加在试样与支撑件相对的一侧以及两者中间的力进行弯曲。在某些情况下，折弯以此方式开始，然后以自由折弯的方式结束。 |
| Balance piston | 平衡活塞 |
(balance drum, dummy piston) A disc attached to the shaft of a turbine or compressor, to one side of which high or low pressure is applied to counteract the axial thrust produced by the pressure change across the machine. A form of thrust bearing. （平衡鼓，假活塞）连接在涡轮机或压缩机轴上的圆盘，在其一侧施加高压或低压，以抵消机器压力变化产生的轴向推力。推力轴承的一种形式。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Quimby screw pump | 昆比螺杆泵 |
A screw pump with two meshing screws, each having a righthand and a left-hand screw. Liquid enters at either end and is discharged from the middle. 带有两个啮合螺钉的螺杆泵，每个都有一个右旋螺纹和一个左旋螺纹。液体从两端进入，从中间排出。 |
| Cheese head | 圆柱头 |
A cylindrical head on a screw or bolt. For driving, it may be slotted, or hexagonally recessed. 螺钉或螺栓上的圆柱头。为了驱动，它可以是开槽的，也可以是六角形的。 |
| Inch (in) | 英寸（in） |
A non-SI unit of length now defined as 25.4 mm. The conversion to SI is 1 in = 2.54 × 10−2 m. 现在定义为25.4毫米的非SI长度单位。转换为SI为1in=2.54×10-2m。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Hot-wire analyzer | 热电阻丝型分析仪 |
An electrical atmosphere analysis device that is based on the fact that the electrical resistivity of steel is a linear function of carbon content over a range from 0.05% C to saturation. The device measures the carbon potential of furnace atmospheres (typically). This term is not to be confused with the hot-wire test which measures heat extraction rates. 一种基于以下事实的电气氛分析设备：钢的电阻率是从0.05%C到饱和范围内的碳含量的线性函数。该设备测量炉内气氛的碳势（通常）。不要将此术语与测量热提取率的热线测试相混淆。 |
| Centrifugal force (Unit N) | 离心力（单位N） |
The inertial reaction force to the centripetal force. It is equal in magnitude but opposite in direction. 惯性反作用力对向心力。它的大小相等，但方向相反。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Toggle (toggle clamp) | 拨动（拨动夹） |
A device consisting of two pinned levers that are almost in line between two end points in the same plane. Bringing the levers into line generates large forces between the ends. Used to obtain a large mechanical advantage or as a locking mechanism. 由两个销杆组成的装置，在同一平面的两个端点之间几乎成一条直线。将杠杆对齐会在端部之间产生较大的力。用于获得较大的机械优势或用作锁定机构。 |
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Impact testing | 冲击测试 |
Determination of the mechanical properties of materials under high-rate conditions. Often determined from the behaviour of a testpiece when struck by a pendulum or a weight falling from a known height, or when sandwiched between two Hopkinson bars. 在高速条件下测定材料的机械性能。通常根据测试件在被钟摆撞击或从已知高度坠落的重物或夹在两个霍普金森棒之间时的行为来确定。 |
| Spherical washer | 球面垫圈 |
A washer whose upper surface is semispherical. Used with a nut whose contact face is also semispherical. Reduces bending stress in a bolt or stud, by allowing some self-alignment and some compensation for nonparallel joint surfaces or Angularity. 上表面为半球形的垫圈。与接触面也是半球形的螺母一起使用。减少螺栓或螺柱中的弯曲应力，允许一些自对准，并对不平行的接头表面或角度进行一些补偿。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Fastener with reduced shank | 短柄紧固件 |
Finished fastener with a shank diameter of ds ≈ d2. 柄径为ds≈d2的紧固件。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Carbon steels | 碳钢 |
(plain carbon steels) Steels in which carbon is the principal alloying element, and the amount of manganese does not exceed 1.65% and the copper and silicon contents are less than 0.60%. There are three main types: low-carbon steels (0.08–0.35% carbon); medium-carbon steels (0.35–0.50% carbon); and high-carbon steels (0.50–2.0% carbon). （普通碳钢）以碳为主要合金元素，锰含量不超过1.65%，铜和硅含量低于0.60%的钢。主要有三种类型：低碳钢（0.08-0.35%碳）；中碳钢（0.35–0.50%碳）；和高碳钢（0.50–2.0%碳）。 |
| Pascal’s law | 帕斯卡定律 |
When there is a change in pressure at any point in a confined fluid at rest, there is an equal change at every other point in the fluid volume. 当处于静止状态的受限流体中任何一点的压力发生变化时，流体体积中的每一点的变化都相等。 |
| Pitch angle (Unit °) | 俯仰角（单位°） |
For a bevel gear, the angle between the axis and the pitch-cone generator. 对于锥齿轮，轴与节锥生成器之间的角度。 |
| Ion carburizing | 离子渗碳 |
A method of surface hardening in which carbon ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma carburizing or glowdischarge carburizing. 一种表面硬化方法，利用高压电能将碳离子在真空中扩散到工件中。与等离子渗碳或辉光放电渗碳同义。 |
| Torque meter | 扭矩计 |
An instrument for measuring torque using spring-loaded, piezoelectric, or strain-gauged devices. 使用弹簧加载、压电或应变测量装置测量扭矩的仪器。 |
| Grinding stress (Unit Pa) | 磨削应力（单位Pa） |
The residual stresses left in the surface of a component after grinding, owing to non-uniform cooling from the high surface temperatures produced. 由于产生的高表面温度造成的不均匀冷却，磨削后留在部件表面的残余应力。 |
| Hydrogen damage | 氢损伤 |
A general term for the embrittlement, cracking, blistering, and hydride formation that can occur when hydrogen is present in some metals. 当氢存在于某些金属中时可能发生的脆化、开裂、起泡和氢化物形成的总称。 |
| Archimedes screw | 阿基米德螺旋泵 |
A machine which comprises a rotating helical blade inside a closefitting tube, which may be used to pump liquids, slurries (such as sewage), granular materials, etc. If water flows into the top of an inclined or vertical Archimedes screw, the screw will rotate and can be used to drive an electrical generator. 一种机器，它在紧密的管子内包含一个旋转的螺旋叶片，可用于泵送液体、泥浆（如污水）、颗粒材料等。如果水流入倾斜或垂直的阿基米德螺杆的顶部，螺杆将旋转，可用于驱动发电机。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Hypereutectic alloy | 过共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of alloying element compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，任何合金，其组成与共晶组成相比具有过量的合金元素，并且其平衡微观结构包含一些共晶结构。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Absolute specific gravity | 绝对比重 |
The ratio of the weight of any volume of a substance to the weight of an equal volume of a reference substance at the same temperature, often water at 4°C, both measured in a vacuum to avoid any effect of buoyancy. 在相同温度下，任何体积的物质的重量与等体积的参考物质的重量之比，通常是4°C的水，两者都是在真空中测量的，以避免任何浮力的影响。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Observed value | 观测值 |
The particular value of a characteristic determined as a result of a test or measurement. 作为测试或测量结果确定的特性的特定值。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Continuous precipitation | 连续沉淀 |
Precipitation from a supersaturated solid solution in which the precipitate particles grow by longrange diffusion without recrystallization of the matrix. Continuous precipitates grow from nuclei distributed more or less uniformly throughout the matrix. They usually are randomly oriented, but may form a Widmanstätten structure. 来自过饱和固溶体的沉淀，其中沉淀颗粒通过长程扩散生长而无需基质再结晶。连续析出物从在整个基体中或多或少均匀分布的核生长而来。它们通常是随机取向的，但可能形成魏氏结构。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Galling | 磨损 |
An extreme form of adhesive wear, in which large chunks of one part stick to the mating part (during sliding contact). 一种极端形式的粘着磨损，其中一个零件的大块粘在配合零件上（在滑动接触期间）。 |
| Stress corrosion cracking (SCC) | 应力腐蚀开裂（SCC） |
A common form of Stress cracking in which an Electrolyte encourages the growth of a crack in a highly stressed bolt. Only a tiny quantity of electrolyte need be present, at the tip or face of the crack. A time-dependent process in which a metallurgically susceptible material fractures prematurely under conditions of simultaneous corrosion and sustained loading at lower stress levels than would be required in the absence of a corrosive environment. Tensile stress is required at the metal surface and may be a residual stress resulting from heat treatment or fabrication of the metal or the result of external loading. Cracking may be intergranular or transgranular, depending on the combination of alloy and environment. 一种常见的应力开裂形式，其中电解液促使高应力螺栓中的裂纹扩展。在裂纹尖端或表面，只需存在少量电解质。一种随时间变化的过程，其中冶金敏感材料在同时腐蚀和持续加载的条件下过早断裂，其应力水平低于无腐蚀环境时的要求。在金属表面需要拉应力，拉应力可以是金属的热处理或制造或外部负载产生的残余应力。裂纹可能是沿晶开裂或穿晶开裂，这取决于合金和环境的组合。 |
| Turbulent flow (turbulence) | 湍流 |
Fluid motion characterized by disorderly, rotational (i.e. vortical) three-dimensional velocity fluctuations covering a wide range of frequency and length scales. The pressure, temperature, and other fluid properties also fluctuate and the diffusion of heat, mass, and momentum is greatly enhanced. As are laminar and transitional flow, turbulent flow of a Newtonian fluid is governed by the Navier–Stokes equations which can in principle be solved by direct numerical simulation (DNS) in which all time and length scales of the fluctuating motion are resolved. 流体运动的特点是无序、旋转（即旋涡）三维速度波动，覆盖广泛的频率和长度尺度。压力、温度和其他流体特性也会波动，热、质量和动量的扩散会大大增强。与层流和过渡流一样，牛顿流体的湍流由Navier-Stokes方程控制，该方程原则上可以通过直接数值模拟（DNS）求解，在直接数值模拟中，波动运动的所有时间和长度尺度都可以求解。 |
| Carbon restoration | 碳修复 |
Replacing the carbon lost in the surface layer from previous processing by carburizing this layer to substantially the original carbon level. Sometimes called recarburizing. 通过将该层渗碳到基本上原始的碳水平来替换先前处理中在表面层中损失的碳。有时称为再碳化。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Cone clutch | 锥形离合器 |
A friction clutch in which an internal cone moves axially in or out of engagement with an external cone. One or both surfaces is lined with high-friction material. 一种摩擦离合器，其中内锥与外锥轴向啮合或脱离啮合。一个或两个表面衬有高摩擦材料。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Shear lip | 剪切唇 |
A narrow, slanting ridge along the edge of a fracture surface. The term sometimes also denotes a narrow, often crescent-shaped, fibrous region at the edge of a fracture that is otherwise of the cleavage type, even though this fibrous region is in the same plane as the rest of the fracture surface. 沿断裂面边缘的狭窄倾斜脊。该术语有时还表示断裂边缘处的狭窄、通常为新月形的纤维区域，否则为解理型，即使该纤维区域与断裂表面的其余部分位于同一平面内。 |
| Angle of thread | 螺纹角度 |
The included angle between the sides forming the groove of the screw thread. 形成螺纹凹槽的边之间的夹角。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Tare weight (Unit N) | 皮重（单位N） |
The weight of an empty container. 空容器的重量。 |
| Turn-of-nut method | 螺母转动法 |
It applies preload by turning a nut through an angle that corresponds to a given elongation. 它通过将螺母旋转一个与给定伸长率相对应的角度来施加预载荷。 |
| Vacuum pump | 真空泵 |
A pump for exhausting air and non-condensable gases from a vessel to be maintained at sub-atmospheric pressure. The pirani and thermal-conductivity gauges are vacuum gauges used to measure the absolute pressure within a vacuum system (vacuum level), usually expressed in torr or Pa. 用于从容器中排出空气和不凝性气体以保持在亚大气压的泵。皮拉尼和热导率计是用于测量真空系统内绝对压力（真空水平）的真空计，通常用托或帕表示。 |
| Coefficient of rolling friction | 滚动摩擦系数 |
The ratio of force parallel to a surface, on which an object rolls, to the normal force. Unlike sliding friction, rolling friction depends on the size of the contact patch and the radius of the rolling element, and the behaviour depends on whether the contact is elastic, viscoelastic, or plastic and on hysteresis losses. 平行于物体滚动表面的力与法向力之比。与滑动摩擦不同，滚动摩擦取决于接触片的大小和滚动元件的半径，其行为取决于接触是弹性的、粘弹性的还是塑性的以及滞后损失。 |
| Homogenizing | 均质化 |
Holding at high temperature to eliminate or decrease chemical segregation by diffusion. 保持高温以消除或减少扩散引起的化学偏析。 |
| Proof stress | 弹性极限应力 |
(1) The stress that will cause a specified small permanent set in a material. (2) A specified stress to be applied to a member or structure to indicate its ability to withstand service loads. （1）在材料中引起规定的小永久变形的应力。（2）施加在构件或结构上的规定应力，以表明其承受工作荷载的能力。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| Machine tool | 机床工具 |
A powered machine, such as a borer, grinder, lathe, milling machine or planer, used for cutting and shaping metal, plastics, composites, etc. (machining). A machining centre is a CNC machine tool working about several axes, having a stock of tools and automatic tool changing ability, which is capable of diverse machining operations under automated control. 一种动力机器，如钻孔机、磨床、车床、铣床或刨床，用于切割和成形金属、塑料、复合材料等（机加工）。加工中心是围绕多个轴工作的CNC机床，具有刀具库存和自动换刀能力，能够在自动化控制下进行各种加工操作。 |
| Clevis | U形夹 |
A U-shaped hook with holes at the ends through which a retaining bolt or pin (clevis pin) passes. 一种U形钩，末端有孔，固定螺栓或销（U形销）穿过这些孔。 |
| Permissible variation | 允许偏差 |
For testing machines, the maximum allowable error in the value of the quantity indicated. It is convenient to express permissible variation in terms of the percent error. 对于试验机，所示数量值的最大允许误差。用误差百分比表示允许偏差是很方便的。 |
| Oldham coupling | 十字联轴节 |
(double-slider coupling) A device for connecting a pair of misaligned parallel shafts, on the end of each of which are flanges having diametral tenons (tongues) that engage with matching slots spaced at 90° in an intermediate disc. As the coupling rotates, the disc compensates for shaft offset by sliding along each tenon in turn. Low-friction surfaces are requisite and the disc is often made of a polymer. An alternative arrangement has the slots in the flanges and the tenons on the disc. （双滑块联轴器）一种连接一对未对准平行轴的装置，在每个平行轴的端部有法兰，法兰具有直径榫（舌），与中间盘中间隔90°的匹配槽接合。当联轴器旋转时，圆盘通过依次沿每个榫头滑动来补偿轴偏移。低摩擦表面是必需的，阀盘通常由聚合物制成。另一种布置方式是法兰上的槽和阀盘上的榫头。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Proportional limit | 比例极限 |
The greatest stress a material is capable of developing without a deviation from straight-line proportionality between stress and strain. 材料能够产生的最大应力不偏离应力和应变之间的直线比例。 |
| Stretch ratio (extension ratio, λ) | 拉伸比（拉伸比，λ） |
A measure, used for highly-extensible materials such as rubber, of the extensional or normal strain of a component subjected to tension and defined as the ratio of the final length l, for a given load, to the initial or gauge length l0, where the coordinate axes are those of principal strain. It is related to the engineering strain e by λ = 1 + e. 用于高度可延展材料（如橡胶）的一种测量方法，用于测量受拉构件的拉伸或法向应变，定义为给定载荷下的最终长度l与初始或标距长度l0之比，其中坐标轴为主应变轴。它与工程应变e的关系为λ=1+e。 |
| Carbon potential | 碳势 |
A measure of the ability of an environment containing active carbon to alter or maintain, under prescribed conditions, the carbon level of the steel. Note: In any particular environment, the carbon level attained will depend on such factors as temperature, time, and steel composition. 衡量含有活性碳的环境在规定条件下改变或保持钢的碳含量的能力。注意：在任何特定环境中，所达到的碳含量将取决于温度、时间和钢成分等因素。 |
| Spinner | 旋转器 |
A co-axial streamlined fairing enclosing the hub of a propeller and rotating with it. 一种同轴流线型整流罩，包围螺旋桨毂并随其旋转。 |
| Flange rotation | 法兰转角 |
Angular distortion of a flange under the influence of bolt and reaction forces. Measured with respect to the center of the cross section of the flange. 法兰在螺栓和反作用力影响下的角度变形。相对于法兰横截面的中心测量。 |
| Effective length of a bolt | 螺栓的有效长度 |
The grip length plus some portion of the bolt (often one-half of the thickness of the nuts) which lies within the nut(s) plus some portion (often one-half the thickness) of the head. 握持长度加上位于螺母内的螺栓的某些部分（通常是螺母厚度的二分之一）加上头部的某些部分（通常是厚度的二分之一）。 |
| Elbow | 肘部 |
1. A fitting that connects the ends of two pipes at an angle, 45°, 90°, and 180° being the most common. 2. The third joint on an articulated robot corresponding to the human elbow. 1.以45°、90°和180°角连接两个管道端部的配件。2.示例关节机器人上的第三关节对应于人的肘部。 |
| Dilatation (dilation) | 膨胀 |
A change of volume caused by external load, compression, temperature change, chemical action, etc. 由外部载荷、压缩、温度变化、化学作用等引起的体积变化。 |
| Corrosion fatigue | 腐蚀疲劳 |
Cracking produced by the combined action of repeated or fluctuating stress and a corrosive environment at lower stress levels or fewer cycles than would be required in the absence of a corrosive environment. 由重复或波动的应力和腐蚀环境的联合作用产生的开裂，其应力水平低于没有腐蚀环境时所需的应力水平或循环次数更少。 |
| Coining | 压印 |
A forging operation, employing a closely-fitting punch and die from which no metal is allowed to escape, in which the surface pattern on the punch and die is imprinted on the blank. 一种锻造操作，采用紧密配合的凸模和模具，不允许金属逸出，其中凸模和模具上的表面图案印在坯料上。 |
| Galilean transformation | 伽利略变换 |
In steady fluid flow, the addition or subtraction of a constant velocity to the entire flowfield, e.g. so that flow can be considered relative to a moving object or flow feature, such as a shock wave. 在稳定的流体流动中，对整个流场增加或减少恒定速度，例如，可以考虑相对于移动物体或流动特征（例如冲击波）流动。 |
| Vacuum relief valve | 真空安全阀 |
A valve that admits gas to a system under vacuum, should the degree of vacuum become excessive. 如果真空度过高，允许气体在真空下进入系统的阀门。 |
| Wrap-around bend | 环绕弯曲 |
The bend obtained when a specimen is wrapped in a closed helix around a cylindrical mandrel. This term is sometimes applied to a semiguided bend of 180° or less. 当试样缠绕在圆柱形心轴周围的闭合螺旋中时获得的弯曲。该术语有时适用于180°或更小的半导弯曲。 |
| ABS polymer | ABS聚合物 |
A class of thermoplastic co-polymer consisting of the three monomers acrylonitrile, butadiene and styrene that has improved properties (particularly toughness) over the individual constituents. 一类由丙烯腈、丁二烯和苯乙烯三种单体组成的热塑性共聚物，其性能（特别是韧性）优于单个成分。 |
| Contact strength (Unit N) | 接触强度（单位N） |
The maximum allowable load between contacting bodies converted into a stress. 换算成应力的接触体之间的最大允许载荷。 |
| Combustion efficiency | 燃烧效率 |
(source efficiency, ηCOMB) A performance measure for combustion equipment defined by ηCOMB = amount of heat released during combustion/(calorific value of the fuel burned). （源效率，ηCOMB）燃烧设备的性能度量，定义为ηCOMB=燃烧过程中释放的热量/（燃烧燃料的热值）。 |
| Wire rope | 钢丝绳 |
A type of cable formed from individual strands of wire with a helical twist. 一种线缆，由具有螺旋扭曲的单独的线股形成。 |
| Rotary valve (rotating valve) | 旋转阀 |
A cylindrical or conical plug in which there is a transverse hole through which fluid can flow when the hole is aligned with the adjacent piping. 一种圆柱形或锥形塞，其中有一个横向孔，当该孔与相邻管道对齐时，流体可通过该孔流动。 |
| Rockwell hardness number (HR) | 洛氏硬度值（HR） |
A number derived from the net increase in the depth of impression in a Rockwell hardness test as the load on an indenter is increased from a fixed minor load to a major load and then returned to the minor load. Rockwell hardness numbers are always quoted with a scale symbol representing the penetrator, load, and dial used. 当压头上的载荷从固定的小载荷增加到大载荷，然后返回到小载荷时，洛氏硬度试验中压痕深度的净增加值。洛氏硬度值总是用刻度符号引用，表示所用的穿透器、载荷和刻度盘。 |
| Gibbs–Dalton law | 吉布斯-道尔顿定律 |
An extension of Dalton’s law of additive pressures to include the statement that the internal energy, enthalpy, and entropy of a mixture of gases are equal to the sum of the internal energies, enthalpies, and entropies the individual constituents would have if each existed alone at the same temperature and volume. Gibbs rule is that part of the law pertaining to entropy. 道尔顿附加压力定律的扩展，包括以下陈述：气体混合物的内能、焓和熵等于各个成分单独存在时的内能、焓和熵之和。相同的温度和体积。吉布斯定律是与熵有关的定律的一部分。 |
| Flat head | 平头 |
Flat top surface and a conical bearing surface. 平顶表面和锥形轴承表面。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Milling | 铣削 |
A machining process, typically for metals and plastics, in which a multi-tooth rotary cutter removes material to produce flat or profiled surfaces, slots, grooves, etc. Milling is a machining process in which metal is removed by a rotating multiple-tooth cutter; each tooth removes a small amount of metal with each revolution of the spindle. Because both workpiece and cutter can be moved in more than one direction at the same time, surfaces having almost any orientation can be machined. 一种加工工艺，通常用于金属和塑料，其中多齿旋转刀具去除材料以产生平坦或异形表面、槽、槽等。金属由旋转多齿刀具去除；主轴每转一圈，每个齿都会去除少量金属。因为工件和刀具可以同时在多个方向上移动，所以几乎可以加工任何方向的表面。 |
| Fatigue striations | 疲劳条纹 |
Parallel lines frequently observed in electron microscope fractographs or fatigue-fracture surfaces. The lines are transverse to the direction of local crack propagation; the distance between successive lines represents the advance of the crack front during the one cycle of stress variation. 在电子显微镜断口图或疲劳断口表面中经常观察到平行线。这些线横向于局部裂纹扩展方向；连续线之间的距离表示在一个应力变化周期内裂纹前沿的前进。 |
| Total combustion air (Unit kg/s) | 总燃烧空气（单位：kg/s） |
1. The combination of the stoichiometric flow of air required for combustion together with any excess air. 2. The flow of fresh air into a boiler plus any flue gas recirculated. 1.燃烧所需的化学计量空气流与任何过量空气的组合。2.进入锅炉的新鲜空气流加上再循环的任何烟气。 |
| Hydraulics | 液压系统 |
The study of water flow in open channels (including canals, rivers, etc.), water-supply, drainage, and irrigation systems. 研究明渠（包括运河、河流等）、供水、排水和灌溉系统中的水流。 |
| Die casting | 压铸 |
A process in which molten metal, particularly alloys of aluminium, magnesium, copper, and zinc, is forced under pressure (10 to 200 MPa) into a reusable hardened-steel mould machined into a die. 在压力（10至200MPa）下将熔融金属（特别是铝、镁、铜和锌的合金）强制进入加工成模具的可重复使用的硬化钢模具中的过程。 |
| Relaxation curve | 松弛曲线 |
A plot of either the remaining, or relaxed, stress as a function of time. 剩余压力或松弛压力随时间变化的曲线图。 |
| Thermomechanical working | 热机械加工 |
A general term covering a variety of processes combining controlled thermal and deformation treatments to obtain specific properties. Same as thermal-mechanical treatment. 一个通用术语，涵盖结合受控热处理和变形处理以获得特定性能的各种工艺。与热机械处理相同。 |
| Maximum stress-intensity factor (Kmax) | 最大应力强度因子（Kmax） |
The maximum value of the stress-intensity factorin a fatigue cycle. 疲劳循环中应力强度因子的最大值。 |
| Design pressure (Unit Pa) | 设计压力（单位Pa） |
The greatest pressure that a closed container is expected to experience under normal operating conditions. 密闭容器在正常操作条件下预期承受的最大压力。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Flange bolt | 法兰螺栓 |
A bolt with a built in washer-like flange just below the head. 在头部下方带有内置垫圈状法兰的螺栓。 |
| Water column | 水柱 |
Water in a tube, which may be vertical or inclined. If the tube is open to the atmosphere, the vertical height h from a datum level to the water surface is a measure of the water static pressure p at the datum level given by p − B = ρgh where B is the barometric pressure, ρ denotes the water density, and g is the acceleration due to gravity. 管道中的水，可以是垂直的或倾斜的。如果管道向大气开放，则从基准面到水面的垂直高度h是基准面处水静压p的量度，由p给出−B=ρgh，其中B是大气压力，ρ表示水密度，g是重力引起的加速度。 |
| Failure of the bolt | 螺栓失效 |
Term implying that the bolt has broken or the threads have stripped. There can be many reasons for this. 表示螺栓断裂或螺纹脱落的术语。原因可能有很多种。 |
| Fastener standard | 紧固件标准 |
A document which details the attributes of a finished fastener and includes such characteristics as geometry, material or chemistry, heat treatment, finish, testing lot size, and packaging. 详细说明紧固件属性的文件，包括几何形状、材料或化学、热处理、表面处理、测试批量和包装等特性。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Blowing | 吹气 |
The process by which a gas is transferred through a porous surface over which there is a gas flow. The effect is used to decrease skin friction and increase heat transfer, for example in turbine-blade cooling. 气体通过有气流的多孔表面转移的过程。该效应用于减少表面摩擦和增加传热，例如在涡轮叶片冷却的过程中。 |
| Preload accuracy | 预载精度 |
A measure of the precision with which a given tool or procedure creates preload in a bolt when the bolt is tightened. A common torque wrench, for example, is said to produce preload with an accuracy of +30%. The mean preload, however, may not be that which the designer intended, or may not be what he should have intended. Accuracy as used here, in other words, is synonymous with Scatter. 当螺栓拧紧时，给定工具或程序在螺栓中产生预紧力的精度度量。例如，一个普通的扭矩扳手据说可以产生精度为+30%的预载。然而，平均预载可能不是设计者预期的。这里使用的准确度是分散度的同义词。 |
| Damage tolerance | 损伤容限 |
(defect tolerance) A design philosophy that takes into account initial imperfections, crack-growth rates and conditions at final fracture, and uses fracture mechanics to demonstrate that cracks should not grow to their critical length within the design life (or at least should be capable of ready detection). （缺陷公差）考虑初始缺陷、裂纹扩展速率和最终断裂条件的设计理念，并使用断裂力学证明裂纹不应在设计寿命内增长到其临界长度（或至少应能够随时检测）。 |
| Total carbon | 总碳 |
The sum of the free and combined carbon (including carbon in solution) in a ferrous alloy. 铁合金中游离碳和结合碳（包括溶液中的碳）的总和。 |
| Transfer ratio | 传输比 |
(transfer constant) A complex variable representing the ratio between the output of a transducer and the input causing that output. （传递常数）一个复变量，表示传感器输出与产生该输出的输入之间的比率。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Computer-aided design (CAD) | 计算机辅助设计（CAD） |
Generally, design and calculations performed by computer; more specifically, the use of computer graphics and models to communicate design concepts. Computer-aided design and computer-aided manufacturing (CAD/CAM) is where component dimensions resulting from CAD are passed by electronic means directly to machines for manufacture. 一般由计算机进行设计和计算，更具体地说，使用计算机图形和模型来传达设计概念。计算机辅助设计和计算机辅助制造（CAD/CAM）是由CAD产生的组件尺寸通过电子方式直接传递到机器进行制造。 |
| Depth gauge | 深度计 |
1. A precision instrument, typically consisting of a machine-divided steel rule passing through a hardened-steel cross head, used to measure the depths of slots, holes, shoulders, projections, etc. 2. A device used by divers to indicate the water depth. 1. 一种精密仪器，通常由穿过硬化钢十字头的机器分割钢尺组成，用于测量槽、孔、肩部、突起等的深度。 2. 潜水员用来指示深度的装置水深。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Combined carbon | 复合碳 |
The part of the total carbon in steel or cast iron that is present as other than free carbon. 钢或铸铁中总碳中除游离碳外的部分。 |
| SI system | SI国际单位制 |
SI is an abbreviation of Système International d’Unités, i.e., the international unit measurement system – an internationally established system of measurement units built on older metric systems. SI是Système International d‘Unités的缩写，即国际单位计量系统——一种基于旧公制的国际公认计量单位系统。 |
| Notch depth | 缺口深度 |
The distance from the surface of a notched test specimen to the bottom of the notch. In a cylindrical test specimen, the percentage of the original cross-sectional area removed by machining an annular groove. 从缺口试样表面到缺口底部的距离。在圆柱形试样中，通过加工环形槽去除的原始横截面积的百分比。 |
| Balance weight | 平衡器 |
A corrective mass used in the static or dynamic balancing of a rotating object. 用于旋转物体的静态或动态平衡的校正质量。 |
| Tensiometer | 张力计 |
An instrument used to measure surface tension. 用来测量表面张力的仪器。 |
| A-basis | A-基础 |
Mechanical property value above which at least 99% of the population of values is expected to fall, with a confidence of 95%. Also called A-allowable. 机械性能值超过该值时，至少99%的值预计会下降，置信度为95%。也被称为A-容许。 |
| Intercritical annealing | 临界退火 |
Any annealing treatment that involves heating to, and holding at, a temperature between the upper and lower critical temperatures to obtain partial austenitization, followed by either slow cooling or holding at a temperature below the lower critical temperature. 任何退火处理，包括加热至并保持在上临界温度和下临界温度之间的温度，以获得部分奥氏体化，然后缓慢冷却或保持在低于下临界温度的温度。 |
| Columnar structure | 柱状结构 |
A coarse structure of parallel elongated grains formed by unidirectional growth, most often observed in castings, but sometimes in structures resulting from diffusional growth accompanied by a solid-state transformation. 由单向生长形成的平行细长晶粒的粗略结构，最常见于铸件中，但有时也出现在伴随固态转变的扩散生长产生的结构中。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Absorber | 吸收器 |
1. An auxiliary vibratory system that favourably modifies the vibration characteristics of a main system. 2. Part of an absorption refrigeration system in which the refrigerant is absorbed by a transport medium. 3. The absorber plate is the receiver of a concentrating solar collector where the radiation is absorbed. 1.一种辅助振动系统，可有利地改变主系统的振动特性。2.吸收式制冷系统的一部分，其中制冷剂被传输介质吸收。3.吸收板是吸收辐射的聚光太阳能集热器的接收器。 |
| Gage length | 标距 |
The original length of the portion of a specimen over which strain, change of length, or other characteristics are determined. 确定应变、长度变化或其他特性的试样部分的原始长度。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Coextrusion | 复合挤压 |
The simultaneous extrusion through the same die of two or more materials in combination. 通过同一模具同时挤出两种或多种材料的组合。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Atmosphere | 大气 |
1. (atm) An obsolete (non-SI) unit of pressure equal to 101 325 Pa or 1.013 25 bar and approximately equal to the atmospheric pressure (barometric pressure) measured at mean sea level. 1.（atm）一种已被淘汰的（非SI）压力单位，等于101325Pa或1.01325bar，大约等于在平均海平面测量的大气压力（大气压）。 |
| Tangential load (Unit N) | 切向荷载（单位：N） |
The component of load applied to an object, such as a gear, that tends to cause or resist rotation. 旋转力施加在物体上的载荷分量，如齿轮，倾向于引起或阻止旋转。 |
| Diaphragm meter | 隔膜计 |
A dry flow meter in which there are two or more interconnected chambers, each having a diaphragm in the wall. The chambers empty and fill alternately and the flow rate of gas is determined from the movement of diaphragms. Diaphragm meters are commonly used to monitor domestic and commercial gas supply. 一种干式流量计，其中有两个或多个相互连接的腔室，每个腔室的壁上都有一个隔膜。腔室交替排空和填充，气体流速由隔膜的移动确定。隔膜流量计通常用于监测家用和商用燃气供应。 |
| Recrystallization temperature | 再结晶温度 |
The approximate minimum temperature at which complete recrystallization of a cold-worked metal occurs within a specified time. 冷加工金属在规定时间内发生完全再结晶的近似最低温度。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Abrasion | 磨损 |
The removal of surface material by the scratching action of hard particles, either deliberately (abrasive papers, abrasive cleaning, abrasive machining) or as a consequence of operation (wear). 通过硬质颗粒的刮擦作用去除表面材料，可以是故意的（砂纸、研磨清洁、研磨加工），也可以是操作的结果（磨损）。 |
| Activation energy | 活化能 |
(Ea, U) (Unit kJ/mol) The minimum energy for a chemical reaction to occur or for processes such as diffusion to take place in crystals. （Ea, U）（单位kJ/mol）发生化学反应或在晶体中发生扩散等过程的最小能量。 |
| Circular pitch | 齿距 |
The distance from the center of one gear tooth to the center of the next gear tooth measured on the pitch line. 在节线上测量的从一个轮齿中心到下一个轮齿中心的距离。 |
| Temper embrittlement | 回火脆化 |
Brittleness that results when certain steels are held within, or are cooled slowly through, a certain range of temperature below the transformation range. The brittleness is manifested as an upward shift in ductile-to-brittle transition temperature but only rarely produces a low value of reduction in area in a smooth-bar tension test of the embrittled material. The anomalous reduction in toughness of martensitic stainless steels when tempered in the range 370–600°C. Embrittlement of alloy steels caused by holding within or cooling slowly through a temperature range just below the transformation range. Embrittlement is the result of the segregation at grain boundaries of impurities such as arsenic, antimony, phosphorus, and tin; it is usually manifested as an upward shift in ductile-to-brittle transition temperature. Temper embrittlement can be reversed by retempering above the critical temperature range, then cooling rapidly. 当某些钢保持在低于转变范围的某一温度范围内或缓慢冷却时产生的脆性。脆性表现为延性到脆性转变温度的向上移动，但在脆性材料的平滑棒材拉伸试验中，很少产生较小的面积减小值。马氏体不锈钢在370–600°C范围内回火时的韧性异常降低。合金钢的脆化是由于在低于转变范围的温度范围内保持或缓慢冷却而引起的。脆化是杂质（如砷、锑、磷和锡）在晶界处偏析的结果；它通常表现为韧脆转变温度的上升。回火脆化可以通过在临界温度范围以上重新回火，然后快速冷却来逆转。 |
| Stroke | 一击 |
1. (stroke length) (Unit m) The linear distance between top dead centre and bottom dead centre of a piston in a reciprocating engine or mechanism. 2. The movement of a piston or plunger in a reciprocating machine to execute a particular function; for example, the exhaust stroke of an engine in which the exhaust gases are expelled from a cylinder. 1.（冲程长度）（单位：m）往复式发动机或机构中活塞上止点和下止点之间的线性距离。2.活塞或柱塞在往复式机器中执行特定功能的运动；例如发动机的排气冲程，其中排气从气缸中排出。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Cathode | 阴极 |
That electrode in a battery or corrosion cell which attracts electrons. 电池或腐蚀电池中吸引电子的电极。 |
| Creep | 蠕变 |
The slow, plastic deformation of a body under heavy loads. Time-dependent plasticity. Time-dependent and permanent deformation of material under constant load or stress. The strain increases with time at a rate that increases with increasing temperature. Creep can lead to large strain and eventual failure, and so limit the lifetime of components subjected to load at high temperature. Creep in metals becomes significant at homologous temperatures in excess of about 0.4, e.g. 1200°C for tungsten, 504°C for titanium, 450°C for iron, and 100°C for aluminium. 物体在重载荷下缓慢的塑性变形，随时间变化的可塑性，材料在恒定载荷或应力下随时间变化的永久变形。应变随时间以随温度升高而增加的速率增加。蠕变可能导致大应变和最终失效，从而限制部件在高温下承受载荷的寿命。当同源温度超过约0.4℃时，金属蠕变变得显著，例如钨为1200℃，钛为504℃，铁为450℃，铝为100℃。 |
| Twist | 扭转 |
The helix produced in a cylindrical component, such as a shaft, wire, tensioned cable, or rope, when one end is rotated relative to the other. Measured either as the number of turns per unit length, or by the helix angle (twist angle). 当一端相对于另一端旋转时，在圆柱形部件（如轴、钢丝、张紧电缆或绳索）中产生的螺旋。以每单位长度的圈数或螺旋角（扭曲角）测量。 |
| Fatigue limit | 疲劳极限 |
The maximum stress that presumably leads to fatigue fracture in a specified number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. Compare with endurance limit. 在指定数量的应力循环中可能导致疲劳断裂的最大应力。还应说明最大应力值和应力比。与耐力极限比较。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Flange | 法兰 |
Flange refers to a head style for bolts where there is a circular ‘flange’ under the head that acts like a washer to distribute a load. A flange is a projected flat rim or collar. 1. Annular rims at the ends of pipes (flanged pipe) or shafts by which they may be coupled together using bolts that pass through holes in the flanges (flange coupling, flange union), or by toggle clamps around the periphery. 2. An extended rim on a wheel that positions it laterally on a track. Commonly used for railway rolling stock. 3. The top and bottom parts of an I-beam. 法兰是指螺栓的头部样式，其中头部下方有一个圆形“法兰”，其作用类似于垫圈以分配载荷。凸缘是凸出的平轮辋或凸缘。1.管道（法兰管）或轴端部的环形边缘，通过这些边缘，可以使用穿过法兰孔的螺栓（法兰联轴器、法兰接头）或通过周边的肘节夹将管道连接在一起。2.车轮上的延伸轮辋，将其横向定位在轨道上。通常用于铁路车辆。3.工字梁的顶部和底部。 |
| Hot hardness | 热硬度 |
The hardness of materials at high temperatures, often used to rank the performance of cutting tools. 材料在高温下的硬度，常用来对刀具的性能进行排名。 |
| Single-shear test | 单剪试验 |
(1) A shear test similar to the double-shear test used for round-bar specimens, but that uses only one stationary shear blade. (2) A shear test that uses a sheet or thin-plate specimen. （1）一种剪切试验，类似于用于圆棒试样的双剪切试验，但仅使用一个固定剪切刀片。（2）使用薄板或薄板试样的剪切试验。 |
| Corrosion failure | 腐蚀失效 |
1. The failure of a component or structure after corrosion has reduced the load-bearing area to an unsupportable level. 2. A situation in which a mechanism cannot function owing to corrosion products preventing free movement at joints. 1、部件或结构在腐蚀后失效，使承重面积减少到无法支撑的程度。2.由于腐蚀产物阻止关节处的自由运动，导致机构无法运行的情况。 |
| British Standards Institution (BSI) | 英国标准协会（BSI） |
The Institution in the UK responsible for the preparation and publication of standard specifications (British standards) for manufactured goods, their design, manufacture and testing. 负责为制成品及其设计、制造和测试制定和发布标准规范（英国标准）的英国机构。 |
| Mass flow rate (ṁ) (Unit kg/s) | 质量流量（ṁ）（单位kg/s） |
The mass of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. The corresponding mass flux (ṁ″), with unit kg/s.m², is the mass flow across a real surface or through a duct, divided by the surface or cross-sectional area A, i.e. ṁ″ = ṁ/A or ṁ″ = ρV where ρ is the material density and V is its velocity normal to the surface. 单位时间内流过表面或通过管道或其他管道的材料质量，通常是流体或粉末。相应的质量通量（ṁ″），单位为kg/s.m²，是通过真实表面或通过管道的质量流量除以表面或横截面积A，即ṁ″=ṁ/A或ṁ″=ρV，其中ρ是材料密度，V是其垂直于表面的速度。 |
| Chilled castings | 冷铸件 |
Iron castings cooled at a rate that results in white iron (slow enough to avoid the formation of martensite, yet fast enough to prevent any silicon present from causing decomposition of cementite into iron and graphite). 铸铁件以产生白口铁的速度冷却（足够慢以避免形成马氏体，但足够快以防止任何存在的硅导致渗碳体分解成铁和石墨）。 |
| Pressure recovery (Unit Pa) | 压力恢复（单位Pa） |
The progressive increase in static pressure for unseparated flow through a diverging nozzle or diffuser. 通过发散喷嘴或扩散器的未分离流的静压逐渐增加。 |
| Total elongation | 总伸长率 |
A total amount of permanent extension of a test piece broken in a tensile test. 拉伸试验中断裂试样的永久延伸总量。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Precision | 精确 |
The closeness of agreement between the results of individual replicated measurements or tests. The standard deviation of the error of measurement may be used as a measure of “imprecision.” 单个重复测量或测试结果之间的一致性。测量误差的标准偏差可用作“不精确性”的度量 |
| Shank | 螺杆 |
Portion of a bolt which lies under the head. 1. The stem of a tool, such as a broach, drill bit, reamer, or tap, which fits into a holder such as a chuck. 2. The stem of a rivet or the unthreaded part of a screw or bolt. 3. The shaft of a tool connecting the tip and the handle. 螺栓头部下方的部分。1.一种工具的柄部，如拉刀、钻头、铰刀或丝锥，可装入夹具（如卡盘）中。铆钉的杆或螺钉或螺栓的无螺纹部分。3.连接尖端和手柄的工具的轴。 |
| Stability | 稳定性 |
1. A term relating to whether a body, structure, system, or flow is in a state of stable, unstable, or neutral equilibrium. 2. In numerical analysis, whether numerical errors, such as roundoff or input-data errors, are damped, propagate, or cause divergence of the solution as the numerical method proceeds. 3. A control system is often described as stable when a step change in input results in a steady output without continuing oscillation. 1.与物体、结构、系统或流是否处于稳定、不稳定或中性平衡状态有关的术语。2.在数值分析中，随着数值方法的进行，数值误差（如舍入误差或输入数据误差）是否衰减、传播或导致解发散。3.当输入的阶跃变化导致稳定输出而无持续振荡时，控制系统通常被描述为稳定的。 |
| Eccentric load | 偏心载荷 |
The external load on a fastener or groups of fasteners is said to be eccentric if the resultant of that load does not pass through the centroid of the group of fasteners (eccentric shear load ) or does not coincide with the bolt axis (eccentric tensile load ). 如果一个或多个紧固件上的外部载荷的合力未穿过紧固件组的质心（偏心剪切载荷）或与螺栓轴不重合（偏心拉伸载荷），则称该外部载荷为偏心。 |
| Available resource | 可用资源 |
(total resource) (Unit J) The total annual energy theoretically available from a renewable-energy source, such as ocean waves, the wind, or the total incident solar energy. （总资源）（单位J）理论上可从可再生能源（例如海浪、风或总入射太阳能）获得的年度总能量。 |
| Notch strength | 缺口强度 |
The maximum load on a notched tensile-test specimen divided by the minimum cross-sectional area (the area at the root of the notch). Also known as notch tensile strength. 缺口拉伸试样上的最大载荷除以最小横截面积（缺口根部的面积）。也称为缺口抗拉强度。 |
| Selective heating | 局部加热 |
Intentionally heating only certain portions of a workpiece. 有意仅加热工件的某些部分。 |
| Collar | 圈、箍 |
A ring secured to, or integral with, a shaft to give axial location. 固定在轴上或与轴成一体以提供轴向位置的环。 |
| Tensometer | 拉力计 |
A bench-top device, used to perform tension and compression tests. 用于进行拉伸和压缩试验的台式装置。 |
| Cooling coil | 冷却盘管 |
A simple heat exchanger consisting of a coiled tube, typically of copper or stainless steel, through which is circulated a coolant such as a refrigerant, chilled water, or water mixed with ethylene glycol. Applications include air conditioning, process cooling, and refrigeration. 一种简单的热交换器，由通常由铜或不锈钢制成的盘管组成，冷却剂如制冷剂、冷冻水或与乙二醇混合的水通过盘管循环。应用包括空调、工艺冷却和制冷。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Finishing washer | 光制垫圈 |
A washer designed for use with countersunk screws. Used to enhance appearance in some applications. 设计用于沉头螺钉的垫圈。在某些应用中用于增强外观。 |
| Wave spring | 波形弹簧 |
A type of compression spring, similar to a coil spring, but made of strip shaped into waves around the circumference. 一种压缩弹簧，类似于螺旋弹簧，但由沿圆周成波浪形的条状物制成。 |
| Fine pitch | 细牙螺纹 |
Fine pitch threads are often used within the automotive industry. They are more easily tapped into harder materials and have less tendency to loosen. 细螺距螺纹通常用于汽车行业。它们更容易被敲入较硬的材料中，并且不太容易松动。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| Wind pressure (Unit Pa) | 风压（单位Pa） |
The dynamic pressure associated with the wind. The static pressure of the wind is the atmospheric pressure. 与风相关的动态压力。风的静压是大气压。 |
| Scragging machine | 刮擦机 |
1. A machine to test springs by impulsive loading 2. A machine to increase the service life of coil springs by compressing them to their minimum solid length before use, thereby inducing favourable residual stresses. 1.一种通过冲击载荷测试弹簧的机器2.一种在使用前将螺旋弹簧压缩至其最小实心长度以提高其使用寿命的机器，从而产生有利的残余应力。 |
| Span (Unit m) | 跨度（单位：m） |
A dimension measured between the extremities of a body or structure, such as between the tips of a wing or the supports of a bridge. 在身体或结构的末端之间测量的尺寸，如机翼尖端或桥梁支架之间。 |
| Finished fastener | 精制紧固件 |
Fastener for which all manufacturing steps have been completed, with or without any surface coating and with full or reduced loadability, and which has not been machined into a test piece. 已完成所有制造步骤的紧固件，有或没有任何表面涂层，具有完全或降低的承载能力，并且尚未加工成试件。 |
| Furnace | 炉 |
1. A type of combustion chamber in which solid, liquid, or gaseous fuels are burned to supply hot gases to a boiler or other process plant. Examples include the firebox, boiler furnace (steam-generating furnace), hot-air furnace, oil-fired furnace, updraught furnace, and water-cooled furnace. 2. A chamber, sometimes having a controlled atmosphere or under vacuum (vacuum furnace), for heating and melting materials. Examples include the blast furnace, direct- and indirect-arc furnaces, the induction furnace (high-frequency furnace), muffle furnace, reverberatory furnace, and solar furnace. 1.一种燃烧室，其中燃烧固体、液体或气体燃料以向锅炉或其他工艺设备供应热气。示例包括燃烧室、锅炉炉（蒸汽发生炉）、热风炉、燃油炉、上升气流炉和水冷炉。2.用于加热和熔化材料的腔室，有时具有受控气氛或真空（真空炉）。例如高炉、直接和间接电弧炉、感应炉（高频炉）、马弗炉、反射炉和太阳能炉。 |
| Translational joint | 平移铰 |
A robot joint where the controlled variable is straight line movement. 控制变量为直线运动的机器人关节。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Thermocouple | 热电偶 |
A device for measuring temperature, consisting of lengths of two dissimilar metals or alloys that are electrically joined at one end and connected to a voltage-measuring instrument at the other end. When one junction is hotter than the other, a thermal electromotive force is produced that is roughly proportional to the difference in temperature between the hot and cold junctions. 一种测量温度的装置，由两种不同的金属或合金组成，一端电连接，另一端与电压测量仪相连。当一个结比另一个结更热时，产生的热电动势大致与热结和冷结之间的温差成比例。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Coefficient of restitution (e) | 回弹系数（e） |
The ratio of the relative velocity of two colliding bodies after collision to that before. In perfectly elastic collisions e = 1; when all the impact energy is dissipated, e = 0. 两个碰撞体在碰撞后与碰撞前的相对速度之比。在完全弹性碰撞中e=1；当所有的冲击能量都消散时，e=0。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Static equilibrium | 静态平衡 |
A solid body, structure, or physical system (or any subdivided part) will be in static equilibrium, either at rest or moving with constant velocity, if the resultants of all external forces and moments acting on it are zero. 如果作用在固体上的所有外力和力矩的合力为零，则固体、结构或物理系统（或任何细分部分）无论是静止还是以恒定速度移动，都是处于静态平衡。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Joule | 焦耳 |
The SI unit of energy. One joule is the work done by a force of one newton acting over a distance of one metre. The symbol is J, where 1 J = 1 N m. 国际单位制能量单位。一焦耳是一牛顿的力在一米的距离上所做的功。符号为J，其中1j=1m。 |
| Decompression chamber | 减压舱 |
A chamber in which ambient-air pressure can be increased to levels found in deep-sea diving. It is used to gradually acclimatize divers back to normal conditions and avoid ‘the bends’. 环境气压可以提高到深海潜水水平的腔室。它用于逐渐使潜水员适应正常条件，避免“弯曲”。 |
| Equation, long form | 方程，长格式 |
An equation which relates the torque applied to a bolt to the preload created in it, and involves fastener geometry and the coefficient of friction between mating surfaces. A theoretical equation based on rigid body mechanics and the assumption that the geometry of the fastener is perfectly described by blueprint dimensions. 将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来的方程，该方程涉及紧固件几何形状和配合面之间的摩擦系数。基于刚体力学和紧固件几何结构由蓝图尺寸完美描述的假设的理论方程。 |
| Taper key | 楔键 |
A key with parallel sides but tapering cross section along its length. 边平行但横截面沿其长度逐渐变细的键。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Thermal insulation (insulation) | 隔热（绝缘） |
A material that may be a low-conductivity solid, or a porous solid or fabric in which there are voids containing air or another gas, resulting in overall low thermal conductivity. When applied to the surface of a hot or cold object, surface heat transfer is generally reduced. 一种材料，可以是低导电性固体，或多孔固体或织物，其中存在含有空气或其他气体的空隙，从而导致整体低导热性。当应用于热或冷物体的表面时，表面传热通常减少。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Carburizing flame | 渗碳火焰 |
A gas flame that will introduce carbon into some heated metals, as during a gas welding operation. A carburizing flame is a reducing flame, but a reducing flame is not necessarily a carburizing flame. 一种气体火焰，会在气焊操作中将碳引入一些加热的金属中。渗碳火焰是还原火焰，但还原火焰不一定是渗碳火焰。 |
| Thread rolling | 滚丝 |
Thread rolling (also known as roll threading) is a cold forming process for producing threads or other helical or annular forms by rolling the impression of hardened steel dies into the surface of a cylindrical or conical blank. Polygonal blanks are also thread rolled for the purpose of fabricating thread-forming and self-locking screws. The preferred polygonal shape is trilobular and is produced in flat die machines. 螺纹滚压（也称为滚压螺纹）是一种冷成型工艺，通过将硬化钢模具的压痕滚压到圆柱形或锥形坯料的表面来生产螺纹或其他螺旋或环形形状。多边形坯料也进行螺纹轧制，以制造螺纹成型和自锁螺钉。优选的多边形形状为三棱形，并在平模机中生产。 |
| Crack-extension force (G) | 裂纹扩展力（G） |
The elastic energy per unit of new separation area that would be made available at the front of an ideal crack in an elastic solid during a virtual increment of forward crack extension. 在向前裂纹扩展的虚拟增量期间，在弹性固体中理想裂纹的前端可获得的每单位新分离面积的弹性能量。 |
| Cooling curve | 冷却曲线 |
A curve showing the relation between time and temperature during the cooling of a material. 显示材料冷却过程中时间和温度之间关系的曲线。 |
| Rotor | 转子 |
A part of a machine that rotates on a shaft (rotor shaft) about its own axis, such as the blade-carrying discs of a turbine, the blades of a helicopter, or the rotating parts of a Roots blower. 绕轴（转子轴）绕其自身轴线旋转的机器部件，如涡轮叶片、直升机叶片或罗茨鼓风机的旋转部件。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Torque control | 扭矩控制 |
A system of optimizing rotor speed for a variable-speed wind turbine by controlling the torque demands of the generator. 通过控制发电机的扭矩需求来优化变速风力涡轮机的转子速度的系统。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Principal stress (normal) | 主应力（正常） |
The maximum or minimum value of the normal stressat a point in a plane considered with respect to all possible orientations of the considered plane. On such principal planes the shear stress is zero. There are three principal stresses on three mutually perpendicular planes. The state of stress at a point may be: (1) uniaxial, a state of stress in which two of the three principal stresses are zero; (2) biaxial, a state of stress in which only one of the three principal stresses is zero; or (3) triaxial, a state of stress in which none of the principal stresses is zero. Multiaxial stress refers to either biaxial or triaxial stress. 相对于所考虑平面的所有可能方向，所考虑平面中某点处的法向应力的最大值或最小值。在这样的主平面上，剪切应力为零。在三个相互垂直的平面上有三个主应力。一点的应力状态可以是：（1）单轴，三个主应力中的两个为零的应力；（2）双轴，三个主应力中只有一个为零的应力状态；或（3）三轴，即主应力均不为零的应力状态。多轴应力是指双轴或三轴应力。 |
| Fastener | 紧固件 |
A fastener is a mechanical device for holding two or more bodies in definite positions with respect to each other. 紧固件是一种机械装置，用于将两个或多个物体相对于彼此固定在确定的位置。 |
| Valve spring | 气门弹簧 |
The spring that restores a valve to its closed position after having been opened, and is also intended to prevent valve bounce. 在阀门打开后将其恢复到关闭位置的弹簧，也用于防止阀门反弹。 |
| Vapour | 蒸气 |
The gas-like phase of a substance at a temperature below its critical point. A vapour can be condensed to a liquid or a solid by increasing its pressure or reducing its temperature. 温度低于临界点的物质的类气相。蒸汽可以通过增加压力或降低温度冷凝成液体或固体。 |
| Combined dimensioning | 组合尺寸标注 |
The use of chain dimensioning and parallel dimensioning on the same engineering drawing. 在同一工程图上使用链式尺寸标注和平行标注。 |
| Austenite-stabilizer | 奥氏体稳定剂 |
Alloying element expanding the γ-phase field in the corresponding phase diagram, which manifests itself in a decrease of the A3 temperature and an increase of the A4 temperature in binary alloys Fe–M as well as in a decrease of A1 temperature in ternary alloys Fe–C–M (M is an alloying element). The solubility of austenite-stabilizers in ferrite is much lower than in austenite. Under the influence of austenite-stabilizers, austenite can become thermodynamically stable down to room temperature. 合金元素扩展了相应相图中的γ相场，这表现为二元合金Fe-M中A3温度的降低和A4温度的升高，以及A1温度的降低三元合金Fe–C–M（M是合金元素）。奥氏体稳定剂在铁素体中的溶解度远低于在奥氏体中的溶解度。在奥氏体稳定剂的影响下，奥氏体可以在低至室温时变得热力学稳定。 |
| Refractory materials | 耐火材料 |
Metals or ceramics that do not melt when exposed to temperature above about 1 500°C or deteriorate rapidly in a continuous temperature above about 550°C. 当暴露于高于约1500°C的温度时不熔化或在高于约550°C的连续温度下快速劣化的金属或陶瓷。 |
| Melting point (Unit K or °C) | 熔点（单位K或°C） |
The temperature at which a solid material undergoes the phase change to a liquid at a specified pressure, usually 1 atm. Pure metals and eutectics have single-valued melting points, while alloys with other compositions melt over a range of temperature such that there is a well-defined start and end to the melting process, but there are states in between where solid and liquid are both present. 在特定压力下，固体材料发生相变为液体的温度，通常为1大气压。纯金属和共晶具有单值熔点，而具有其他成分的合金在一定温度范围内熔化，熔化过程有一个明确的起点和终点，但其间存在固态和液态并存的状态。 |
| Radiator | 散热器 |
A heat exchanger used to transfer thermal energy from one fluid to another for heating or cooling purposes. Despite the name, the principal mode of heat transfer is convection rather than radiation. In motor vehicles, water circulated through the engine block is cooled as it flows through the tubes of an air-cooled heat exchanger. In domestic radiators, hot water from a boiler is circulated through a heat exchanger with a large surface area which transfers heat to the surrounding air. 一种热交换器，用于将热能从一种流体传递到另一种流体，用于加热或冷却。尽管有这个名字，但热传递的主要方式是对流而不是辐射。在机动车辆中，通过发动机缸体循环的水在流经风冷热交换器的管道时被冷却。在家用散热器中，来自锅炉的热水通过具有大表面积的热交换器循环，该热交换器将热量传递给周围的空气。 |
| Belt furnace | 带式炉 |
A continuous-type furnace which uses a mesh-type or cast-link belt to carry parts through the furnace. 一种连续式炉，它使用网状或铸造链带将零件运送通过炉子。 |
| Flattening test | 压扁试验 |
This term as applied to tubing refers to a method of testing a section of tubing by flattening it until the inside walls are parallel and separated by a given distanceusually equal to three times the wall thickness for seamless tubes and five times the wall thickness for lap-welded tubes. Boiler tubes subjected to this test should show no cracks or flaws. The flattening test applied to rivets, consists in flattening a rivet head while hot to a diameter equal to 21⁄2 times the diameter of the shank or body of the rivet. Good rivet steel must not crack at the edges of the flattened head. 该术语适用于管材，是指通过压扁管材直至内壁平行并隔开给定距离（通常等于无缝钢管壁厚的三倍，搭接焊管壁厚的五倍）来测试管材截面的方法。进行该试验的锅炉管应无裂纹或缺陷。适用于铆钉的压扁试验包括在热态下压扁铆钉头，使其直径等于铆钉柄或铆钉体直径的21⁄2倍。良好的铆钉钢不得在扁平头部边缘开裂。 |
| Vapour-pressure thermometer | 蒸汽压力温度计 |
(vapour-filled thermometer) A type of fluidexpansion thermometer in which the working fluid is a volatile liquid. （蒸汽填充温度计）一种流体膨胀温度计，其中工作流体为挥发性液体。 |
| Gear ratio | 传动比 |
For two gears in contact, the ratio of the number of teeth on the driving gear to that on the driven gear. 对于接触的两个齿轮，主动齿轮上的齿数与从动齿轮上的齿数之比。 |
| Indentation hardness | 压痕硬度 |
The resistance of a material to indentation as determined by hardness testing. The indenter, which may be spherical or diamond shaped, is pressed into the surface of a metal under specified load for a given time. (Unit Pa or, non-SI, kgf/mm²) A measurement of hardness taken by means of an indenter, pressed into a material by a load, which makes a permanent impression. The hardness is given by the load divided by the projected (sometimes surface) area of the indentation. Plasticity theory shows that the hardness is about 2.5–3 times the uniaxial yield stress. 通过硬度测试确定的材料抗压痕的能力。压头可以是球形或菱形，在规定的载荷下压入金属表面一段时间。（单位Pa或，非国际单位制，kgf/mm²）通过压头测量硬度，压入材料，形成永久压痕。硬度由载荷除以压痕的投影（有时是表面）面积得出。塑性理论表明，硬度约为单轴屈服应力的2.5–3倍。 |
| Longitudinal direction | 纵向 |
The principal direction of flow in a worked metal. See also normal direction and transverse direction. 加工金属中的主要流动方向。另请参见法向和横向。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Hexagon nut | 六角螺母 |
A nut having six sides and shaped like a hexagon. 六边形的螺母。 |
| Static fatigue | 静态疲劳 |
A term referring to a time-dependent reduction in strength with a static (noncyclic) load. The term may refer to hydrogen-induced delayed cracking or the effect of creep on the strength of plastics. Delayed fracture caused by environmental effects under dead-weight loading of materials such as glass. The name is unfortunate, as cyclic loads are not involved and glass is not susceptible to fatigue. 指静态（非循环）载荷下强度随时间变化的降低。该术语可指氢致延迟开裂或蠕变对塑料强度的影响。在玻璃等材料的自重荷载下，由环境影响引起的延迟断裂。 |
| Quench hardening | 淬火硬化 |
(1) Hardening suitable alpha-beta alloys (most often certain copper to titanium alloys) by solution treating and quenching to develop a martensitic-like structure. (2) In ferrous alloys, hardening by austenitizing and then cooling at a rate such that a substantial amount of austenite transforms to martensite. （1）通过固溶处理和淬火硬化合适的α-β合金（通常是某些铜-钛合金），以形成类似马氏体的结构。（2）在铁合金中，通过奥氏体化硬化，然后以一定速度冷却，使大量奥氏体转变为马氏体。 |
| Gauge | 测量 |
1. Any instrument for measuring or checking dimensions, including adjustable gauges such as a micrometer and non-adjustable gauges such as go/no-go limit gauges that indicate the maximum and minimum dimensions allowable in a component during manufacture. 2. A term often used to mean an instrument, e.g. pressure gauge. 3. The diameter of a wire or thickness of a sheet according to a standard. 4. The distance between the rails of a railway track. 1. 任何用于测量或检查尺寸的仪器，包括可调节量规（例如千分尺）和不可调节量规（例如指示制造过程中组件允许的最大和最小尺寸的通过/不通过限制量规）。2. 常用于表示仪器的术语，例如压力表。3.根据标准的线材直径或片材厚度。4.铁路轨道的钢轨之间的距离。 |
| Degradation | 降解 |
The reduction with time of the physical properties of a material. 材料的物理性质随时间的减少。 |
| Structural frame | 结构框架 |
The underlying load-bearing framework of beams, columns, bracing, etc., of steel, concrete, brick, stone, timber etc., required to support the static and dynamic forces a building or component is subjected to, including its weight and that of its contents. 由钢、混凝土、砖、石、木材等制成的梁、柱、支撑等构成的底层承重框架，用于支撑建筑物或构件承受的静态和动态力，包括其重量及其内含物的重量。 |
| Transmissibility | 传递率 |
The ratio of the transmitted force to the disturbing force for a system subjected to a vibratory disturbance. The ratio may also be defined in terms of displacements, velocities, or accelerations. 受到振动干扰的系统的传递力与干扰力之比。该比率也可以用位移、速度或加速度来定义。 |
| Altitude | 高度 |
(Unit m) Vertical height measured relative to a specified datum such as sea level. （单位m）相对于特定基准（例如海平面）测量的垂直高度。 |
| Transition temperature (Unit K) | 转变温度（单位K） |
(1) An arbitrarily defined temperature that lies within the temperature range in which metal fracture characteristics (as usually determined by tests of notched specimens) change rapidly, such as from primarily fibrous (shear)to primarily crystalline (cleavage) fracture. (2) Sometimes used to denote an arbitrarily defined temperature within a range in which the ductility changes rapidly with temperature. (transition point) 1. The temperature at which the mechanism of fracture in metal alloys having a face-centred cubic crystal structure changes from ductile void growth to brittle cleavage. 2. The temperature at which a material changes from one crystal state to another. （1） 任意定义的温度，位于金属断裂特性（通常通过缺口试样的试验确定）快速变化的温度范围内，如从主要纤维（剪切）断裂到主要结晶（解理）断裂。（2） 有时用于表示延性随温度快速变化的范围内的任意定义的温度。（转变点）1.具有面心立方晶体结构的金属合金的断裂机制从韧性孔洞生长转变为脆性解理的温度。2.材料从一种晶体状态转变为另一种晶体的温度。 |
| T-bolt | T型螺栓 |
A threaded bolt having a square or rectangular end which fits into the T slot of a machine table for clamping workpieces. 一种带有方形或矩形端头的螺栓，可嵌入机床工作台的T形槽中，用于夹紧工件。 |
| Compressed liquid | 压缩液体 |
A liquid subjected to a pressure greater than the saturation pressure corresponding to its temperature. 承受大于与其温度对应的饱和压力的压力的液体。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Crystalline fracture | 结晶断裂 |
A pattern of brightly reflecting crystal facets on the fracture surface of a polycrystalline metal, resulting from cleavage fracture of many individual crystals. 多晶金属断裂面上明亮反射的晶面图案，由许多单个晶体的解理断裂产生。 |
| Liquid carburizing | 液体渗碳 |
Surface hardening of steel by immersion into a molten bath consisting of cyanides and other salts. 通过浸入由氰化物和其他盐组成的熔池中对钢进行表面硬化。 |
| Vacuum servo | 真空服务器 |
A vacuum-operated servomotor which is used in a motor vehicle to provide a brake effort greater than the capability of the driver. 一种真空操作的伺服电机，用于机动车中，以提供大于驾驶员能力的制动力。 |
| Orange peel | 橘皮 |
A surface roughening in the form of a pebble-grained pattern where a metal of unusually coarse grain is stressed beyond its elastic limit. Also known as pebbles and alligator skin. 一种以卵石颗粒图案形式出现的粗糙化表面，其中晶粒异常粗的金属受到的应力超过其弹性极限。也称为卵石和鳄鱼皮。 |
| Belt drive | 带传动 |
Transmission of motion from one shaft to another by means of a continuous plain, or toothed, flexible band (belt) passing over pulleys. In contrast to chain drives, belt drives tend to be employed in low-torque applications. Reduction in transmissible power may occur due to stretch of a plain transmission belt which results in slack in the drive (belt creep) or slip of a belt on a driving or driven pulley (belt slip). 通过穿过滑轮的连续平带或带齿柔性带（带）将运动从一根轴传递到另一根轴。与链条传动相比，皮带传动往往用于低扭矩应用。由于普通传动带的拉伸可能会导致传动松弛（皮带蠕变）或主动或从动皮带轮上的皮带打滑（皮带打滑），从而导致传动功率降低。 |
| Caterpillar | 毛虫式履带 |
(crawler vehicle) A vehicle that ‘lays its own road’ by running on endless belts, driven by toothed wheels, on each side. Used on soft ground where spreading of the load reduces contact stress. （履带式车辆）通过在每一侧由齿轮驱动的环形皮带运行来“铺设自己的道路”的车辆。用于负载分散可减少接触应力的松软地面。 |
| Fracture stress | 断裂应力 |
The true normal stress on the minimum cross-sectional area at the beginning of fracture. This term usually applies to tension tests of unnotched specimens. 断裂开始时最小横截面积上的真实正应力。该术语通常适用于无缺口试样的拉伸试验。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Wrist | 腕关节 |
The final three joints on a robot which simulate rotations provided by the human wrist and thus allow orientation of the end effector to which it is attached by the wrist socket. 机器人上的最后三个关节，模拟人类手腕提供的旋转，从而允许其通过手腕插座连接到的末端执行器的方向。 |
| Lock-nut pipe thread | 锁紧螺母管螺纹 |
The lock-nut pipe thread is a straight thread of the largest diameter which can be cut on a pipe. Its form is identical with that of the American or Briggs standard taper pipe thread. In general, “Go” gages only are required. These consist of a straight-threaded plug representing the minimum female lock-nut thread, and a straight-threaded ring representing the maximum male lock-nut thread. This thread is used only to hold parts together, or to retain a collar on the pipe. It is never used where a tight threaded joint is required. 锁紧螺母管螺纹是最大直径的直螺纹，可在管道上切割。其形式与美国或布里格斯标准锥管螺纹相同。一般情况下，只需要通规。它们由一个表示最小内螺纹锁紧螺母螺纹的直螺纹塞和一个表示最大外螺纹锁紧螺帽螺纹的直形螺纹环组成。该螺纹仅用于将零件固定在一起，或用于将轴环固定在管道上。切勿使用于需要紧密螺纹接头的情况下。 |
| Hot dipping | 热浸 |
(hot-dip galvanizing) A process of coating an iron, steel, or aluminium object with a thin layer of zinc by passing it through a bath of molten zinc at a temperature of about 460°C. （热浸镀锌）通过使铁、钢或铝物体通过温度约为460°C的熔融锌浴，在铁、钢或铝物体上镀上一层薄薄的锌层的工艺。 |
| Adhesive joint | 粘合接头 |
The point or area in which two structures are held together by an adhesive. 两个结构通过粘合剂粘合在一起的点或区域。 |
| Clearance angle | 后角 |
(relief angle) (Unit °) The angle between the underneath or flank of a cutting tool and the machined surface. （后角）（单位°）切削刀具的底部或侧面与加工表面之间的角度。 |
| Solution heat treatment | 固溶热处理 |
Heating an alloy to a suitable temperature, holding at that temperature long enough to cause one or more constituents to enter into solid solution, and then cooling rapidly enough to hold these constituents in solution. 将合金加热到合适的温度，在该温度下保持足够长的时间以使一种或多种成分进入固溶体，然后快速冷却以将这些成分保持在溶液中。 |
| Concentration ratio | 浓度比 |
For a concentrating solar collector, the ratio of the projected area of the concentrator facing the solar beam to the actual area of the receiver. 对于聚光太阳能集热器，集中器面向太阳光束的投影面积与接收器的实际面积之比。 |
| Shoulder | 轴肩 |
The portion of a shaft, stepped component, or flanged component, where a change in diameter or other dimension occurs. Even for a nominal step change, in practice there will be a radius where shoulder and shaft meet in order to avoid too severe a stress concentration. 轴、阶梯部件或法兰部件的直径或其他尺寸发生变化的部分。即使是名义阶跃变化，在实践中，肩部和轴相交处也会有一个半径，以避免出现过严重的应力集中。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Partial annealing | 不完全退火 |
An imprecise term used to denote a treatment given cold-worked material to reduce the strength to a controlled level or to effect stress relief. To be meaningful, the type of material, the degree of cold work, and the time-temperature schedule must be stated. 一个不精确的术语，用于表示冷加工材料的处理，以将强度降低到受控水平或消除应力。为了有意义，必须说明材料类型、冷加工程度和时间-温度计划。 |
| Tangent modulus | 切线模量 |
The slope of the stress-strain curve at any specified stress or strain. See also modulus of elasticity. 在任何规定的应力或应变下，应力-应变曲线的斜率。另见弹性模量。 |
| Secondary hardening | 二次硬化 |
The process whereby some low-alloy steels, quenched to produce martensite, produce fine precipitates when tempered above 550°C, which inhibit dislocation motion and reverse the trend towards lower strength at higher tempering temperatures. 某些低合金钢经淬火产生马氏体，在550°C以上回火时产生细小沉淀的过程，这抑制了位错运动，扭转了在较高回火温度下强度降低的趋势。 |
| Impact loads | 冲击载荷 |
Especially severe shock loads such as those caused by instantaneous arrest of a falling mass, shock meeting of two parts (in a mechanical hammer, for example), or by explosive impact, in which there can be an exceptionally rapid build-up of stress. 特别严重的冲击载荷，例如由下落质量的瞬时停止、两部分的冲击碰撞（例如在机械锤中）或爆炸性冲击引起的冲击载荷，其中可能会出现异常快速的应力积聚。 |
| Thermodynamic state | 热力学状态 |
The condition of a system or working fluid according to its properties. 系统或工作流体根据其性质的状态。 |
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Standard fit | 标准匹配 |
The fit of a component machined or otherwise manufactured to standardized clearances and tolerances. 根据标准间隙和公差加工或以其他方式制造的部件的配合。 |
| Tracking problem | 跟踪问题 |
A control problem where the set point changes with time and thus the plant output must follow the changing set point. The opposite of a regulator problem. 一种控制问题，其中设定值随时间变化，因此设备输出必须遵循变化的设定值。与调节器问题相反。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| R-curve/Resistance curve | 阻力曲线 |
In linear-elastic fracture mechanics, a plot of crack-extension resistance as a function of stable crack extension, which is either the difference between the physical crack size, or the effective crack size, and the original crack size. R-curves normally depend on specimen thickness and, for some materials, on temperature and strain rate. An increase in fracture toughness with crack propagation shown by rising plots of toughness vs growing crack length. 在线弹性断裂力学中，作为稳定裂纹扩展函数的裂纹扩展阻力图，即物理裂纹尺寸或有效裂纹尺寸与原始裂纹尺寸之间的差值。R曲线通常取决于试样厚度，对于某些材料，还取决于温度和应变率。是随着裂纹扩展，断裂韧性增加，表现为韧性与扩展裂纹长度的上升曲线。 |
| ASME | ASME |
The American Society of Mechanical Engineers. 美国机械工程师学会。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Air composition | 空气成分 |
The sea-level composition (in per cent by volume) of air at a temperature of 15°C and a pressure of 1 atm is mainly 78.084% nitrogen, 20.947% oxygen and 0.934% argon. The remaining 0.035% consists of carbon dioxide, neon, helium, methane, krypton, hydrogen, oxides of nitrogen, xenon, ozone, iodine, carbon monoxide, and ammonia. Different sources give slightly different figures for the composition. Not included are water vapour (typically 0.4%) and pollutants such as sulfur dioxide. 在15°C的温度和1个大气压的压力下，空气的海平面成分（体积百分比）主要是78.084%的氮气、20.947%的氧气和0.934%的氩气。剩余的0.035%由二氧化碳、氖、氦、甲烷、氪、氢、氮的氧化物、氙、臭氧、碘、一氧化碳和氨组成。不同的来源给出的组成略有不同。不包括水蒸气（通常为0.4%）和二氧化硫等污染物。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Machine | 机器 |
A mechanism that transmits power in the performance of a useful task. More than one machine in one place, either connected or performing separate functions, is termed machinery. 在执行有用任务时传递能量的机制。一个地方有一台以上的连接或执行单独的功能，称为机器。 |
| Punch | 冲床 |
1. A hand tool with a sharp point, used to mark the position of a hole centre in a workpiece prior to drilling. 2. A flat-ended tool with sharp edges, used to shear out a hole in a plate that is supported underneath on a die having a slightly larger same-shaped orifice. 1.一种带有尖头的手动工具，用于在钻孔前标记工件中孔中心的位置。2.一种具有锐边的平头工具，用于剪切板上的孔，该板支撑在具有稍大相同形状孔口的模具下方。 |
| Newton’s law of gravitation | 牛顿万有引力定律 |
(Newton’s law of universal gravitation) Any two bodies exert a gravitational force of attraction F on each other directed along the line joining their centres of mass, in magnitude proportional to the product of their masses and inversely proportional to the square of the distance r between them. （牛顿万有引力定律）任何两个物体沿其质心连接线相互施加引力F，其大小与其质量乘积成正比，与它们之间距离r的平方成反比。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Thermodynamics laws | 热力学定律 |
The zeroth, first, second, and third laws of thermodynamics. 热力学第零、第一、第二和第三定律。 |
| Precipitation heat treatment | 沉淀热处理 |
Artificial aging in which a constituent precipitates from a supersaturated solid solution. 成分从过饱和固溶体沉淀的人工时效。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Diesel engine | 柴油发动机 |
(compression–ignition engine) A piston engine operating on the Diesel cycle in which the air is compressed to a temperature above the autoignition temperature of the fuel and combustion is initiated as the fuel is injected into the hot air. Diesel engines operate at higher compression ratios (typically in the range 12 to 24) than petrol engines. Although named after Rudolf Diesel, the inventor, Diesel engine is often spelled with a lower case d, contrary to normal practice. （压燃式发动机）在柴油循环中运行的活塞式发动机，在该循环中，空气被压缩至高于燃料自燃温度的温度，当燃料喷射到热空气中时，燃烧开始。柴油发动机在比汽油发动机更高的压缩比下运行（通常在12到24的范围内）。虽然以发明人鲁道夫·迪塞尔命名，但迪塞尔发动机通常拼写为小写d，这与正常做法相反。 |
| Fracture toughness | 断裂韧性 |
A generic term for measures of resistance to extension of a crack. The term is sometimes restricted to results of fracture mechanics tests, which are directly applicable in fracture control. However, the term commonly includes results from simple tests of notched or precracked specimens not based on fracture mechanics analysis. Results from tests of the latter type are often useful for fracture control, based on either service experience or empirical correlations with fracture mechanics tests. 裂纹扩展阻力测量的通用术语。该术语有时仅限于断裂力学试验的结果，这些结果直接适用于断裂控制。该术语通常包括非基于断裂力学分析的切口或预裂纹试样的简单试验结果。基于使用经验或与断裂力学试验的经验相关性，后一类试验的结果通常有助于断裂控制。 |
| Torque motor | 力矩电机 |
A type of induction motor that can apply a steady torque even when prevented from rotating. 一种感应电动机，即使被阻止旋转也能施加稳定的转矩。 |
| Crossed threads | 交叉螺纹 |
When the axis of a nut offered up to a bolt is not aligned with the axis of a bolt (or a screw to a threaded member), it may be possible for the threads to engage incorrectly and even for the nut or screw to advance a turn or more, but ultimately the misaligned threads become locked together. Forcing the nut in such circumstances may irretrievably damage the threads on both. 当提供给螺栓的螺母的轴线与螺栓（或螺纹构件的螺钉）的轴线不对齐时，螺纹可能会错误接合，甚至螺母或螺钉会提前一圈或更多，但最终未对齐的螺纹会锁定在一起。在这种情况下强行拧入螺母可能会对两侧的螺纹造成无法修复的损坏。 |
| Transgranular fracture | 穿晶断裂 |
Fracture in crystalline materials where the path of cracking is predominantly across grains. 晶体材料中的断裂，其中裂纹路径主要跨越晶粒。 |
| Wind energy (Unit kJ) | 风能（单位kJ） |
The kinetic energy associated with wind that can be converted by a wind energy conversion system (WECS) into electrical or mechanical power by a rotor, such as a multi-bladed propeller, exposed to the wind. If the air density is ρ and the wind speed is V, then the kinetic energy flux is ρV3/2. The actual wind power that can be extracted by a wind turbine intercepting a cross section of wind A is CPρAV3/2 where CP is an empirical efficiency factor termed the power coefficient. The wind-energy distribution is a histogram of the calculated wind power that can be generated annually from the windspeed frequency distribution at a given location. A windmill generates mechanical power whereas a wind turbine (wind generator) generates electrical power. The largest wind turbine, manufactured by MHI Vestas, has a power rating of 9.5 MW, a rotor diameter of 164 m, and a hub height of 105 m (the highest wind turbines have heights in the region of 190 m). A wind farm is an array of wind turbines, typically ten to several hundred, at a single location, either onshore or offshore. Energy derived from wind is a major contributor to sustainable energy generation. The largest operational offshore wind farm, located in the Irish Sea, has 87 turbines and a total generating capacity of 659 MW. The largest onshore wind farm is in Kern County, California with some 586 turbines and a total capacity of 1 550 MW. 风能转换系统（WECS）可通过暴露于风中的转子（如多叶片螺旋桨）将与风相关的动能转换为电能或机械能。如果空气密度为ρ，风速为V，则动能通量为ρV3/2。可由截获风a横截面的风力涡轮机提取的实际风功率为CPρAV3/2，其中CP是称为功率系数的经验效率因子。风能分布是根据给定位置处的风速频率分布每年可产生的计算风力的直方图。风车产生机械功率，而风力涡轮机（风力发电机）产生电功率。MHI Vestas制造的最大风力涡轮机的额定功率为9.5MW，转子直径为164m，轮毂高度为105m（最高风力涡轮机的高度为190m）。风电场是一系列风力涡轮机，通常为十到几百台，位于单一位置，无论是陆上还是海上。风能是可持续能源发电的主要贡献者。最大的海上风电场位于爱尔兰海，拥有87台涡轮机，总发电容量为659MW。最大的陆上风电场位于加利福尼亚州克恩县，拥有约586台涡轮机，总容量为1550兆瓦。 |
| Anisotropy | 各向异性 |
The characteristic of exhibiting different values of a property in different directions with respect to a fixed reference system in the material. 相对于材料中的固定参考系统，在不同方向上表现出不同属性值的特性。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Breaking load | 断裂载荷 |
The maximum load (or force) applied to a test specimen or structural member loaded to rupture. 施加到加载到破裂的试样或结构构件上的最大载荷（或力）。 |
| Combustion deposit | 燃烧沉积物 |
Ash, carbon, and other incombustible solids, often due to impurities in the fuel, that build up on any surfaces exposed to products of combustion. They can lead to corrosion, reduced heat transfer and so higher flue-gas temperatures and reduced efficiency. 灰、碳和其他不燃固体，通常是由于燃料中的杂质，在暴露于燃烧产物的任何表面上堆积。它们会导致腐蚀、传热降低，从而导致烟气温度升高和效率降低。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Q-factor | 品质因素 |
(quality factor, sharpness of resonance) A non-dimensional parameter that describes, for a given resonant mode, the sharpness of the peak in the frequency response of a lightly-damped linear oscillator: Q = ωRES/Δω where ωRES is the resonance frequency and Δω is the half-power bandwidth of the resonance. It is inversely related to the damping such that a broad peak corresponds to high damping and a narrow peak to low damping. （品质因数，共振尖锐度）一个无量纲参数，用于描述给定共振模式下，轻阻尼线性振荡器频率响应峰值的尖锐度：Q=ωRES/Δω，其中ωRES是共振频率，Δω是共振的半功率带宽。它与阻尼成反比，因此宽峰值对应于高阻尼，窄峰值对应于低阻尼。 |