| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Design stress (Unit Pa) | 设计应力（单位Pa） |
The greatest allowable stress in a component or structure that will not result in failure under normal operating conditions. 在正常操作条件下不会导致失效的部件或结构中的最大许用应力。 |
| Finishing washer | 光制垫圈 |
A washer designed for use with countersunk screws. Used to enhance appearance in some applications. 设计用于沉头螺钉的垫圈。在某些应用中用于增强外观。 |
| Curie temperature | 居里温度 |
The temperature of magnetic transformation below which a metal or alloy is ferromagnetic and above which it is paramagnetic. 磁性转变温度，低于此温度金属或合金为铁磁性，高于此温度则为顺磁性。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Load ratio, R | 负载比R |
In fatigue, the algebraic ratio of the minimum to maximum load in a fatigue cycle, that is, R = Pmin/Pmax. Also known as stress ratio. 在疲劳中，疲劳循环中最小载荷与最大载荷的代数比，即 R= Pmin/Pmax。也称为应力比。 |
| Air-hardening steel | 空气硬化钢 |
A steel containing sufficient carbon and other alloying elements to harden fully during cooling in air or other gaseous mediums from a temperature above its transformation range. The terms should be restricted to steels that are capable of being hardened by cooling in air in fairly large sections, about 2 in. (50 mm) or more in diameter. Same as self-hardening steel. 一种钢，含有足够的碳和其他合金元素，可以在空气或其他气体介质中从高于其转变范围的温度冷却过程中完全硬化。这些术语应仅限于能够通过在相当大的截面（直径约2英寸（50毫米）或更大）中通过空气冷却而硬化的钢。与自硬钢相同。 |
| Bond strength (Unit Pa) | 结合强度（单位Pa） |
The tensile, compressive or shear stress at which joints fail, e.g. by fracture or excessive deformation. 接头失效的拉伸、压缩或剪切应力，例如断裂或过度变形。 |
| Radial load (Unit N) | 径向负荷（单位：N） |
1. Centrifugal loading induced in a rotating body. 2. (through-wallthickness load) The radial component of loading arising from internal or external pressurization of a closed vessel. There will also be axial and hoop loading. 1.旋转体中产生的离心载荷。2.（贯穿壁厚载荷）由封闭容器的内部或外部加压产生的载荷的径向分量。还存在轴向和环向载荷。 |
| Scragging machine | 刮擦机 |
1. A machine to test springs by impulsive loading 2. A machine to increase the service life of coil springs by compressing them to their minimum solid length before use, thereby inducing favourable residual stresses. 1.一种通过冲击载荷测试弹簧的机器2.一种在使用前将螺旋弹簧压缩至其最小实心长度以提高其使用寿命的机器，从而产生有利的残余应力。 |
| Outside diameter (Unit m) | 外径（单位：m） |
(external diameter, OD) The diameter of a circular cylindrical tube or a sphere measured between opposite points on the external surface. （外径，OD）在外表面上的相对点之间测量的圆柱管或球体的直径。 |
| Grain size | 晶粒大小 |
A measure of the areas or volumes of grains in a polycrystalline metal, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. For metals, a measure of the areas or volumes of grains in a polycrystalline material, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. Grain sizes are reported in terms of number of grains per unit area or volume, average diameter, or as a grainsize number derived from area measurements. 多晶金属中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。多晶材料中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。晶粒尺寸以每单位面积或体积的晶粒数、平均直径或从面积测量得出的晶粒尺寸数来报告。 |
| Screw machine | 螺丝机 |
A machine tool for high-volume manufacture of small turned components from rod or bar. 一种用棒或棒大批量制造小零件的机床。 |
| Vent | 发泄 |
A small valve that allows the release of pressurized fluid from a pipe, pressure vessel, etc., often to the atmosphere. 一种小阀门，允许将加压流体从管道、压力容器等中释放到大气中。 |
| Minor diameter | 螺纹小径 |
On a straight thread, the diameter of the imaginary cylinder which just touches the root of an external thread or the crest of an internal thread. 在直螺纹上，仅接触外螺纹根部或内螺纹顶部的假想圆柱体的直径。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Spray quenching | 喷雾淬火 |
A quenching process using spray nozzles to spray water or other liquids on a part. The quench rate is controlled by the velocity and volume of liquid per unit area per unit of time of impingement. 使用喷嘴将水或其他液体喷射到零件上的淬火过程。淬火速率由每单位撞击时间内每单位面积的液体速度和体积控制。 |
| Car furnace | 车炉 |
A batch-type furnace using a car on rails to enter and leave the furnace area. Car furnaces are used for lower stress relieving ranges. 一种间歇式炉，使用轨道上的小车进出炉区。汽车炉用于较低的应力消除范围。 |
| Shrink ring | 预紧环 |
A ring, which is expanded by heating, is placed around an assembly of parts, and then contracts upon cooling to hold the assembly in place. 通过加热膨胀的环被放置在零件组件周围，然后在冷却时收缩以将组件固定到位。 |
| Threading machine | 螺纹机 |
A machine used to cut an external thread on a rod, tube, bolt blank, etc. or an internal thread in a hole, tube, nut blank, etc. 用于切割杆、管、螺栓毛坯等上的外螺纹或孔、管、螺母毛坯等中的内螺纹的机器。 |
| Wear | 磨损 |
Damage to a solid surface, generally involving progressive loss of material, due to relative motion between that surface and a contacting surface or substance. The deterioration of a component or structure with time and usage, often impairing the function for which it was designed, owing to abrasion, corrosion, fatigue, friction, etc. during relative motion of parts. The wear factor (K), with unit mm³/N.m, is an empirical dimensional factor that quantifies surface wear due to mechanical frictional contact, and defined by K = /Fs where is the worn volume (in mm³), F is the contact load (in N), and s is the sliding distance (in m). 由于固体表面与接触表面或物质之间的相对运动，对固体表面的损坏，通常涉及材料的渐进损失。部件或结构随时间和使用而劣化，通常由于部件相对运动过程中的磨损、腐蚀、疲劳、摩擦等而损害其设计功能。磨损系数（K），单位为mm³/N.m、 是量化机械摩擦接触导致的表面磨损的经验尺寸因子，由K=/Fs定义，其中是磨损体积（单位：mm³），F是接触载荷（单位：N），s是滑动距离（单位：m）。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Kiln | 窑 |
An industrial oven for burning, baking, or drying. 用于燃烧、烘烤或干燥的工业烤箱。 |
| Torque (T) (Unit N.m) | 扭矩（T）（单位：N.m） |
The twisting moment, product of force and wrench length, applied to a nut or bolt (for example). The twisting moment of a force or couple about an axis which results in torsion. 施加在螺母或螺栓（例如）上的扭矩，是力和扳手长度的乘积。力或力偶绕轴产生扭转的力矩。 |
| Wear rate | 磨损率 |
The rate of material removal or dimensional change due to wear per unit of exposure parameter—for example, quantity of material removed(mass, volume, thickness) in unit distance of sliding or unit time. 由于单位暴露参数的磨损而导致的材料去除率或尺寸变化，例如，单位滑动距离或单位时间内去除的材料数量（质量、体积、厚度）。 |
| Material velocity | 材料速度 |
The velocity of sound in a body (e.g., a bolt). A term used in the ultrasonic measurement of bolt stress or strain. 声音在物体（例如螺栓）中的速度。用于螺栓应力或应变的超声波测量的术语。 |
| Dynamics | 动力学 |
The branch of mechanics that deals with objects in motion. Its two main branches are kinematics, which studies motion without regards to its cause, and kinetics, which also takes into account forces that cause motion. 力学中研究运动物体的分支。它的两个主要分支是运动学和动力学，前者研究运动而不考虑其原因，后者也考虑引起运动的力。 |
| Case hardening | 表面硬化 |
A generic term covering several processes applicable to steel that change the chemical composition of the surface layer by absorption of carbon, nitrogen, or a mixture of the two and, by diffusion, create a concentration gradient. The processes commonly used are carburizing and quench hardening; cyaniding; nitriding; and carbonitriding. The use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于钢的几种工艺，这些工艺通过吸收碳、氮或二者的混合物改变表层的化学成分，并通过扩散形成浓度梯度。常用的工艺有渗碳和淬火硬化，氰化，氮化以及碳氮共渗。优选使用适用的特定工艺名称。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Hard temper | 硬化回火 |
Same as full hard temper. 和全硬化回火一样。 |
| System engineering | 系统工程 |
A methodology which integrates all disciplines and specialty groups into a team effort, forming a structured development process that proceeds from concept to production to operation. 一种将所有学科和专业组整合到团队工作中的方法，形成从概念到生产再到运营的结构化开发过程。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Apparent area of contact | 表观接触面积 |
In tribology, the area of contact between two solid surfaces defined by the boundaries of their macroscopic interface. 在摩擦学中，两个固体表面之间的接触区域由其宏观界面的边界定义。 |
| Second (s) | 秒（s） |
The SI base unit of time equal to 9 192 631 770 times the period of the radiation corresponding to the transition between the two hyperfine levels of the ground state of the caesium-133 atom. SI基时间单位等于9192631770倍的辐射周期，对应于铯-133原子基态的两个超精细能级之间的跃迁。 |
| Ratchet coupling | 棘轮联轴器 |
A joint employing a ratchet system between two shafts, so that not only does the driven shaft run in one direction only, but also the driven shaft can, if necessary, run more quickly than the driving shaft. 在两个轴之间采用棘轮系统的接头，这样不仅从动轴只能在一个方向上运行，而且在必要时，从动轴可以比驱动轴运行得更快。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Autonomous energy system | 自主能源系统 |
(stand-alone energy system) A sole source of electricity, usually small-scale, for applications remote from a grid, especially with energy storage in the system. Hydroelectric, photovoltaic, wind-power and other renewable systems are well suited to stand-alone applications. （独立能源系统）一种唯一的电力来源，通常是小规模的，用于远离电网的应用，尤其是系统中的能量存储。水电、光伏、风力和其他可再生能源系统非常适合独立应用。 |
| Alloy steels | 合金钢 |
Steels that contain alloying elements such as chromium, nickel, molybdenum, manganese, silicon, tungsten, and vanadium. These are added to improve properties such as the hardenability, toughness, strength, wear resistance, and corrosion resistance compared with those of plain-carbon steel. Low-alloy steels have a total alloy content (including carbon) of less than about 8%. They are hardenable and have strength up to 30% higher than plain-carbon steels. High-alloy steels contain considerably more alloy content and are developed for specific properties such as superior corrosion and chemical resistance. 含有铬、镍、钼、锰、硅、钨和钒等合金元素的钢。添加这些是为了提高与普通碳钢相比的淬透性、韧性、强度、耐磨性和耐腐蚀性等性能。低合金钢的总合金含量（包括碳）小于约8%。它们是可硬化的，强度比普通碳钢高出30%。高合金钢含有相当多的合金含量，并针对特定性能而开发，例如卓越的耐腐蚀性和耐化学性。 |
| Fastener quality | 紧固件质量 |
A fastener’s adherence to its specification for dimensional tolerances, mechanical properties, and other requirements stated under applicable standards. 紧固件对尺寸公差、机械性能和适用标准规定的其他要求的规范的遵守情况。 |
| Stroke | 一击 |
1. (stroke length) (Unit m) The linear distance between top dead centre and bottom dead centre of a piston in a reciprocating engine or mechanism. 2. The movement of a piston or plunger in a reciprocating machine to execute a particular function; for example, the exhaust stroke of an engine in which the exhaust gases are expelled from a cylinder. 1.（冲程长度）（单位：m）往复式发动机或机构中活塞上止点和下止点之间的线性距离。2.活塞或柱塞在往复式机器中执行特定功能的运动；例如发动机的排气冲程，其中排气从气缸中排出。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Pressure difference (Unit Pa) | 压差（单位Pa） |
(pressure differential, Δp) The difference between two pressures, one of which may be a reference pressure such as barometric pressure. In many flow processes, the pressure difference is more important than the absolute pressure level. （压差，Δp）两个压力之间的差值，其中一个压力可以是参考压力，如大气压力。在许多流动过程中，压差比绝对压力水平更重要。 |
| Anti-freeze | 防冻液 |
A substance such as ethylene glycol added to the cooling system of a watercooled engine to lower the freezing point of the cooling water and also inhibit the formation of rust and other deposits. 一种物质，如乙二醇，添加到水冷发动机的冷却系统中，以降低冷却水的冰点，并抑制生锈和其他沉积物的形成。 |
| Shear strain rate(Unit 1/s) | 剪切应变率（单位1/s） |
In the deformation of solids, the rate at which shear strain is applied in a test or changes with time in a loaded component or structure. 在固体变形中，在试验中施加剪切应变的速率，或在加载部件或结构中随时间变化的速率。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Verification | 检验 |
Checking or testing an instrument to ensure conformance with a specification. 检查或测试仪器以确保符合规范。 |
| Galilean transformation | 伽利略变换 |
In steady fluid flow, the addition or subtraction of a constant velocity to the entire flowfield, e.g. so that flow can be considered relative to a moving object or flow feature, such as a shock wave. 在稳定的流体流动中，对整个流场增加或减少恒定速度，例如，可以考虑相对于移动物体或流动特征（例如冲击波）流动。 |
| Recrystallization temperature | 再结晶温度 |
The approximate minimum temperature at which complete recrystallization of a cold-worked metal occurs within a specified time. 冷加工金属在规定时间内发生完全再结晶的近似最低温度。 |
| Congruent melting point (Unit K) | 全等熔点（单位K） |
congruent melting point (Unit K) The temperature at which a solid substance at a specified pressure changes phase to a liquid of identical composition. 一致的熔点（单位K）固体物质在特定压力下相变为具有相同成分的液体时的温度。 |
| Absorptance | 吸收率 |
(absorptivity, absorption coefficient, α) The fraction of radiant flux incident on a surface that is absorbed by the surface. The term also applies to absorption of radiation by a volume of fluid. For a semi-transparent surface, α + ρ + τ = 1, where ρ is the reflectance and τ is the transmittance. （吸收率，吸收系数，α）入射到表面的辐射通量被表面吸收的部分。该术语也适用于一定体积的流体对辐射的吸收。对于半透明表面，α+ρ+τ=1，其中ρ是反射率，τ是透射率。 |
| Ion nitriding | 离子氮化 |
A method of surface hardening in which nitrogen ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma nitriding or glowdischarge nitriding. 一种表面硬化方法，其中氮离子通过使用高压电能在真空中扩散到工件中。与等离子体氮化或辉光放电氮化同义。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Poisson’s ratio (ν) | 泊松比（ν） |
The absolute value of the ratio of transverse (lateral) strain to the corresponding axial strain resulting from uniformly distributed axial stress below the proportional limit of the material. 横向（侧向）应变与相应轴向应变之比的绝对值，该比值由低于材料比例极限的均匀分布的轴向应力产生。 |
| Critical strain | 临界应变 |
The strain just sufficient to cause recrystallization; because the strain is small, usually only a few percent, recrystallization takes place from only a few nuclei, which produces a recrystallized structure consisting of very large grains. 刚好足以引起再结晶的应变；由于应变很小，通常只有百分之几，再结晶只发生在少数核上，从而产生由非常大的晶粒组成的再结晶结构。 |
| Gibbs–Dalton law | 吉布斯-道尔顿定律 |
An extension of Dalton’s law of additive pressures to include the statement that the internal energy, enthalpy, and entropy of a mixture of gases are equal to the sum of the internal energies, enthalpies, and entropies the individual constituents would have if each existed alone at the same temperature and volume. Gibbs rule is that part of the law pertaining to entropy. 道尔顿附加压力定律的扩展，包括以下陈述：气体混合物的内能、焓和熵等于各个成分单独存在时的内能、焓和熵之和。相同的温度和体积。吉布斯定律是与熵有关的定律的一部分。 |
| Wedge | 楔子 |
A short triangular prism whose major surfaces subtend an acute angle, that can be driven between two objects or parts of an object to split, tighten, or secure them, or to widen an opening or raise a heavy object. The acute angle gives a high mechanical advantage. 一种短的三棱镜，其主面对着一个锐角，可在两个物体或物体的一部分之间驱动，以将它们分开、拧紧或固定，或加宽开口或举起重物。锐角具有很高的机械优势。 |
| Vapour | 蒸气 |
The gas-like phase of a substance at a temperature below its critical point. A vapour can be condensed to a liquid or a solid by increasing its pressure or reducing its temperature. 温度低于临界点的物质的类气相。蒸汽可以通过增加压力或降低温度冷凝成液体或固体。 |
| Forging cracks | 锻造裂纹 |
This may occur during fastener manufacturing at the cutting or forging operations and are located on the top of the head or on the raised periphery of indented head bolts. 这可能发生在紧固件制造过程中的切削或锻造操作中，并且位于头部的顶部或带锯齿的头部螺栓的凸起周边上。 |
| Reverse engineering | 逆向工程 |
The disassembly of a machine, mechanism, system or device, measurement of its component parts, and identification of the materials used so that if required, a functioning replica can be produced. 拆卸机器、机构、系统或装置，测量其组成部分，并识别所用材料，以便在需要时可以生产出功能正常的复制品。 |
| Diffusion coating | 扩散涂层 |
Coating on metal for corrosion- and/or oxidation-resistance. Coatings are produced by heating a metal in contact with an alloy in powder, liquid, or gaseous form at elevated temperature such that atoms of the coating diffuse into the substrate. Examples include chromium, aluminium, or silicon on substrates such as nickel-based superalloys, steels, and refractory metals. 金属上的防腐和/或抗氧化涂层。涂层是通过在高温下加热与粉末、液体或气体形式的合金接触的金属，从而使涂层的原子扩散到基体中而产生的。实例包括基底上的铬、铝或硅，如镍基高温合金、钢和耐火金属。 |
| Two-phase flow | 两相流 |
A flow in which two phases are present, for example gas bubbles in a liquid, liquid bubbles in another liquid with which it is immiscible, solid particles in a liquid or gas. 两相流动，例如液体中的气泡、与之不混溶的另一种液体中的液体气泡、液体或气体中的固体颗粒。 |
| Elongation | 伸张率 |
A term used in mechanical testing to describe the amount of extension of a test piece when stressed. 机械测试中使用的术语，用于描述试样在受力时的延伸量。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Closed system | 封闭系统 |
A closed thermodynamic system consists of a fixed amount of mass. No mass can cross its boundary although energy can, in the form of work or heat, and its volume can change. 一个封闭的热力学系统由一定量的质量组成。能量可以以功或热的形式存在，其体积可以改变，但没有质量可以越过它的边界。 |
| Engineering strain (e) | 工程应变（e） |
A term sometimes used for average linear strain or conventional strain in order to differentiate it from true strain. In tension testing it is calculated by dividing the change in the gage length by the original gage length. 一个术语，有时用于平均线性应变或常规应变，以便将其与真实应变区分开来。在张力测试中，通过将标距变化除以原始标距来计算。 |
| Thermal compressor | 热压缩机 |
1. (thermocompressor) A jet compressor used to boost the pressure of low-pressure waste or exhaust steam. 2. A device consisting of an absorber, a generator, a pump, and a throttling device, used instead of a mechanical vapour compressor in an absorption-cooling refrigeration system. 1.（热压缩机）用于提升低压废蒸汽或排气压力的喷射压缩机。2.一种由吸收器、发电机、泵和节流装置组成的装置，用于替代吸收冷却制冷系统中的机械蒸汽压缩机。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Total energy (Unit J) | 总能量（单位J） |
The sum of all forms of energy associated with a system, including kinetic, potential, internal, magnetic, chemical, and electrical energy. 与系统相关的所有形式能量的总和，包括动能、势能、内能、磁能、化学能和电能。 |
| Positive-displacement compressor | 容积式压缩机 |
Any type of compressor, including piston and rotary-screw types, that delivers a fixed volume of gas at high pressure per unit time. A positive-displacement pump delivers a fixed volume of fluid, usually a liquid, per unit time. 任何类型的压缩机，包括活塞式和旋转螺杆式，在单位时间内以高压输送固定体积的气体。容积泵每单位时间输送固定体积的流体，通常为液体。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Shoulder | 轴肩 |
The portion of a shaft, stepped component, or flanged component, where a change in diameter or other dimension occurs. Even for a nominal step change, in practice there will be a radius where shoulder and shaft meet in order to avoid too severe a stress concentration. 轴、阶梯部件或法兰部件的直径或其他尺寸发生变化的部分。即使是名义阶跃变化，在实践中，肩部和轴相交处也会有一个半径，以避免出现过严重的应力集中。 |
| Retaining clip | 固定夹 |
(R-clip, hair cotter pin) A wire clip roughly with the shape of the letter R. The straight part of the clip passes through a hole drilled into a shaft or rod such that a wheel is held in position on the shaft, or the shaft is prevented from moving axially. （R形夹，开口销）大致与字母R形状相同的线夹。线夹的直线部分穿过钻在轴或杆上的孔，从而将车轮固定在轴上，或防止轴轴向移动。 |
| Working section | 工作区 |
That part of a wind tunnel in which models are placed for testing, or where detailed measurements are performed. 风洞中放置模型进行测试或进行详细测量的部分。 |
| Neutralization number | 中和值 |
An ASTM number given to quenching oils that reflects the oil’s tendency towards oxidation and sludging. 淬火油的ASTM编号，反映了油的氧化和成泥趋势。 |
| Semi-rotary pump | 半回转泵 |
A form of self-priming pump, often hand-operated, suitable for pumping water and light oils such as diesel oil and petrol. As shown in the diagram, liquid is sucked into one side of the pump through flap valves and simultaneously ejected from the other side on one stroke. The sequence is reversed on each successive stroke. 一种自吸泵，通常是手动的，适用于泵送水和轻油，如柴油和汽油。液体通过翻板阀吸入泵的一侧，同时在一个冲程中从另一侧排出。在每个连续冲程上，顺序颠倒。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Proof load | 验证载荷（单位 N） |
The maximum, safe, static, tensile load which can be placed on a fastener without yielding it. Sometimes given as a force (in lb or N) sometimes as a stress (in psi or MPa). The test load in quality control to which different components made of different materials must be subjected without failing in order to perform properly. 可施加在紧固件上而不使其屈服的最大安全静态拉伸载荷。有时以力（lb或N）表示，有时以应力（psi或MPa）表示。质量控制中的测试负荷，由不同材料制成的不同部件必须经受该负荷，才能正常运行。 |
| Hydrogen damage | 氢损伤 |
A general term for the embrittlement, cracking, blistering, and hydride formation that can occur when hydrogen is present in some metals. 当氢存在于某些金属中时可能发生的脆化、开裂、起泡和氢化物形成的总称。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Thermal shock | 热冲击 |
The development of a steep temperature gradient and accompanying high stresses within a structure. 在结构内形成陡峭的温度梯度和伴随的高应力。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Steam gauge | 汽压表 |
A pressure gauge used to measure gauge pressure in a line, boiler, cylinder, or other device operating with steam. 一种压力表，用于测量管道、锅炉、汽缸或其他与蒸汽一起工作的装置中的表压。 |
| Pressure regulator | 压力调节器 |
(pressure-regulating valve) A device installed in a pneumatic or gas system to maintain the downstream pressure at the required level. （压力调节阀）安装在气动或气体系统中以将下游压力保持在所需水平的装置。 |
| Following flank | 跟随侧翼 |
The flank of a thread opposite to the leading flank. 与前牙面相对的螺纹牙面。 |
| Tension testing | 张力测试 |
A method of determining the behavior of materials subjected to uniaxial loading, which tends to stretch the metal. A longitudinal specimen of known length and diameter is gripped at both ends and stretched at a slow, controlled rate until rupture occurs. Also known as tensile testing. 一种确定材料在单轴载荷下的行为的方法，这种载荷倾向于拉伸金属。将已知长度和直径的纵向试样夹持在两端，并以缓慢、受控的速率拉伸，直到发生断裂。也称为拉伸测试。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| DTI | DTI |
Direct tension indicator. A fastener used primarily in the structural steel industry, designed to indicate that a certain minimum amount of tension has been developed in the fastener during assembly. 直接张力指示器。一种主要用于结构钢行业的紧固件，旨在表明在装配过程中紧固件中产生了一定的最小张力。 |
| Maximum-and-minimum thermometer | 最高和最低温度计 |
(minimum-maximum thermometer, Six’s thermometer) A liquid-in-glass instrument designed to register the maximum and minimum temperatures experienced over a given time period. （最低-最高温度计，Six's温度计）一种液体玻璃仪器，用于记录给定时间段内经历的最高和最低温度。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Damage tolerance | 损伤容限 |
(defect tolerance) A design philosophy that takes into account initial imperfections, crack-growth rates and conditions at final fracture, and uses fracture mechanics to demonstrate that cracks should not grow to their critical length within the design life (or at least should be capable of ready detection). （缺陷公差）考虑初始缺陷、裂纹扩展速率和最终断裂条件的设计理念，并使用断裂力学证明裂纹不应在设计寿命内增长到其临界长度（或至少应能够随时检测）。 |
| Shoulder screw | 轴肩螺钉 |
A screw having two or more diameters or shoulders and commonly used for supporting levers and other machine parts that have to operate freely. 一种具有两个或两个以上直径或轴肩的螺钉，通常用于支撑杠杆和其他必须自由操作的机器部件。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Avogadro constant | 阿伏伽德罗常数 |
(Avogadro number, NA) A fundamental physical constant with the fixed numerical value 6.022 140 76 × 1023 mol−1. The mole contains exactly this number of elementary entities. A minor adjustment to the value of the Avogadro constant was made effective on 20 May 2019. （阿伏伽德罗数，NA）一个固定数值为6.02214076×1023mol的基本物理常数−摩尔正好包含这个数量的基本实体。对阿伏伽德罗常数值的微小调整于2019年5月20日生效。 |
| Reverse pitch (Unit °) | 反向螺距（单位°） |
The pitch of a variable-pitch propeller that produces negative thrust. 产生负推力的变桨距螺旋桨的桨距。 |
| X-ray thickness gauge | X射线厚度计 |
A device comprising an X-ray source and a detector used to determine the thickness of material in sheet or plate form, including metals, paper, plastics, rubber, and ceramics. 一种由X射线源和探测器组成的装置，用于测定片状或平板状材料的厚度，包括金属、纸张、塑料、橡胶和陶瓷。 |
| Crest | 波峰 |
The highest point of a wave or of a screw thread. 波浪或螺纹的最高点。 |
| Pressure snubber | 压力缓冲器 |
(pressure-pulse snubber) A device used for filtering, dampening, and the protection of transducers, pressure gauges, and switches, from pressure surges, pressure spikes, and water hammer. A typical design uses a fixed mesh or porous metal disc installed in an inline body. In a piston-type pressure-gauge snubber, a piston is forced against an orifice leading to the gauge. （压力脉冲缓冲器）一种用于过滤、阻尼和保护传感器、压力表和开关免受压力浪涌、压力尖峰和水锤影响的装置。典型的设计使用安装在内联阀体中的固定网格或多孔金属盘。在活塞式压力表缓冲器中，活塞被压靠在通向压力表的孔口上。 |
| Tow | 拖拉 |
1. To cause a vehicle to move by pulling with a rope, chain, bar, etc. 2. A bundle of fibres employed in reinforcement. 1.用绳子、链条、钢筋等拉动车辆移动。2.用于加固的纤维束。 |
| Charles law/Charles' law | 查尔斯定律 |
(Gay–Lussac law) The volume of a fixed mass of gas at constant pressure is proportional to its absolute temperature. The volume of a gas at constant pressure is directly proportional to its absolute temperature. （盖-吕萨克定律）在恒定压力下，固定质量气体的体积与其绝对温度成正比。恒压下气体的体积与其绝对温度成正比。 |
| Sizing | 颗粒化 |
1. A finishing operation to ensure the specified dimensions and tolerances for a component are met. 2. (size classification) Separating an aggregate of mixed particles into groups according to size using a series of screens. 1.精加工操作，以确保满足部件的规定尺寸和公差。2.（粒度分类）使用一系列筛网根据粒度将混合颗粒的聚集体分成组。 |
| Yield strength | 屈服强度 |
That stress level which will create a permanent deformation of 0.2% or 0.5% or some other small, preselected, amount in a body. Approximately equal to the elastic and proportional limits of the material; a little higher than the proof strength of a bolt. The stress at which a material exhibits a specified deviation from proportionality of stress and strain. An offset of 0.2% is used for many metals. 该应力水平将在物体中产生0.2%或0.5%的永久变形，或其他一些小的、预先选定的量。近似等于材料的弹性和比例极限；略高于螺栓的强度。材料表现出与应力和应变比例的特定偏差的应力。许多金属使用0.2%的偏移量。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Stress-concentration factor (Kt) | 应力集中系数（Kt） |
A multiplying factor for applied stress that allows for the presence of a structural discontinuity such as a notch or hole; Kt equals the ratio of the greatest stress in the region of the discontinuity to the nominal stress for the entire section. Also known as theoretical stress-concentration factor. 施加应力的倍增系数，允许存在结构不连续性，如缺口或孔；Kt等于不连续区域的最大应力与整个截面的标称应力之比。也称为理论应力集中系数。 |
| Pressure recovery (Unit Pa) | 压力恢复（单位Pa） |
The progressive increase in static pressure for unseparated flow through a diverging nozzle or diffuser. 通过发散喷嘴或扩散器的未分离流的静压逐渐增加。 |
| Track rod | 横拉杆 |
A bar connecting the ends of the steering arms in an automotive vehicle. 连接汽车转向臂端部的杆。 |
| Effective radius of nut, bolt head, or threads | 螺母、螺栓头或螺纹的有效半径 |
Distance between the geometric center of the part and the circle of points through which the resultant contact forces between mating parts passes. Must be determined by integration. 零件几何中心与配合零件之间的合力通过的点圆之间的距离。必须通过积分来确定。 |
| Vibration isolation | 隔振 |
The prevention of transmission of vibration from one component of a system to another part of the same system, such as a building or other structure. Isolation may be achieved using dampers (vibration damping) or by active feedback-control methods. Mechanical vibration is often attenuated by means of components immersed in oil such as in dashpots (viscous damping). Vibration suppression can be achieved (a) using dampers and absorbers tuned to a particular frequency to suppress vibratory forces in structures and other systems (passive suppression) or (b) by the measurement of vibration at key locations in a structure and the application of cancellation forces (active suppression). 防止振动从系统的一个部件传递到同一系统的另一部分，如建筑物或其他结构。可以使用阻尼器（减振）或主动反馈控制方法实现隔离。机械振动通常通过浸入油中的部件来衰减，例如缓冲罐（粘性阻尼）。可以通过（a）使用调谐到特定频率的阻尼器和吸收器来抑制结构和其他系统中的振动力（被动抑制），或（b）通过测量结构中关键位置的振动并施加抵消力（主动抑制），实现振动抑制。 |
| Destructive testing | 破坏性测试 |
Measurement of the mechanical properties of a material, component, or structure, by increased loading until the sample fails by fracture, collapse, or buckling. 通过增加载荷测量材料、部件或结构的机械性能，直到样品因断裂、塌陷或屈曲而失效。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Altitude chamber | 高空舱 |
(hypobaric chamber) A chamber in which conditions at different altitudes are simulated by a combination of appropriate pressures, temperatures and relative humidity. （低压舱）通过适当的压力、温度和相对湿度的组合来模拟不同高度条件的舱室。 |
| Transmissibility | 传递率 |
The ratio of the transmitted force to the disturbing force for a system subjected to a vibratory disturbance. The ratio may also be defined in terms of displacements, velocities, or accelerations. 受到振动干扰的系统的传递力与干扰力之比。该比率也可以用位移、速度或加速度来定义。 |
| Anelastic | 无弹性 |
Literally ‘not elastic’, but in practice used for materials that display timedependent recovery on unloading. 字面意思是“没有弹性”，但实际上用于在卸载时显示随时间恢复的材料。 |
| Fibreglass | 玻璃纤维 |
Fibreglass is used in studs and nuts for applications when the fastener should be non-corrosive, low in conductivity, or transparent to electromagnetic waves. 当紧固件应无腐蚀性、低导电性或对电磁波透明时，玻璃纤维用于螺柱和螺母中。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Acoustic pyrometer | 声学高温计 |
A non-intrusive pyrometer based on the principle that the sound speed in a gas is proportional to the square root of its absolute temperature. 一种非侵入式高温计，其原理是气体中的声速与其绝对温度的平方根成正比。 |
| Atom | 原子 |
The smallest unit of matter that has the properties of a chemical element. The simplest description of an atom (Bohr model) is of a compact nucleus surrounded by one or more orbiting electrons. 具有化学元素性质的最小物质单位。原子的最简单描述（玻尔模型）是由一个或多个轨道电子包围的致密原子核。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Creep | 蠕变 |
The slow, plastic deformation of a body under heavy loads. Time-dependent plasticity. Time-dependent and permanent deformation of material under constant load or stress. The strain increases with time at a rate that increases with increasing temperature. Creep can lead to large strain and eventual failure, and so limit the lifetime of components subjected to load at high temperature. Creep in metals becomes significant at homologous temperatures in excess of about 0.4, e.g. 1200°C for tungsten, 504°C for titanium, 450°C for iron, and 100°C for aluminium. 物体在重载荷下缓慢的塑性变形，随时间变化的可塑性，材料在恒定载荷或应力下随时间变化的永久变形。应变随时间以随温度升高而增加的速率增加。蠕变可能导致大应变和最终失效，从而限制部件在高温下承受载荷的寿命。当同源温度超过约0.4℃时，金属蠕变变得显著，例如钨为1200℃，钛为504℃，铁为450℃，铝为100℃。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Fine pitch | 细牙螺纹 |
Fine pitch threads are often used within the automotive industry. They are more easily tapped into harder materials and have less tendency to loosen. 细螺距螺纹通常用于汽车行业。它们更容易被敲入较硬的材料中，并且不太容易松动。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Superheating | 过热 |
Heating above the temperature at which an equilibrium phase transformation should occur without actually obtaining the transformation. 在不实际获得相变的情况下，加热到应发生平衡相变的温度以上。 |
| Radiator | 散热器 |
A heat exchanger used to transfer thermal energy from one fluid to another for heating or cooling purposes. Despite the name, the principal mode of heat transfer is convection rather than radiation. In motor vehicles, water circulated through the engine block is cooled as it flows through the tubes of an air-cooled heat exchanger. In domestic radiators, hot water from a boiler is circulated through a heat exchanger with a large surface area which transfers heat to the surrounding air. 一种热交换器，用于将热能从一种流体传递到另一种流体，用于加热或冷却。尽管有这个名字，但热传递的主要方式是对流而不是辐射。在机动车辆中，通过发动机缸体循环的水在流经风冷热交换器的管道时被冷却。在家用散热器中，来自锅炉的热水通过具有大表面积的热交换器循环，该热交换器将热量传递给周围的空气。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Thermodynamic properties | 热力学性质 |
Temperature, pressure, and the intensive properties that define the state of a working fluid: specific internal energy, specific enthalpy and specific entropy. 温度、压力和定义工作流体状态的密集属性：比内能、比焓和比熵。 |
| Stretch forming | 拉伸成型 |
A manufacturing process in which sheet-metal components are physically stretched over a forming die using a press, punch, or edge clamps. Stretching combined with bending reduces springback. 一种制造工艺，其中使用压力机、冲头或边缘夹具在成形模上物理拉伸金属板部件。拉伸与弯曲相结合可减少回弹。 |
| Thread run-out | 螺纹耗尽 |
That portion of the threads which are not cut or rolled full depth, but which provide the transition between full-depth threads and the body or head. Officially called thread washout or vanish, although the term run-out is more popular. (Run-out is officially reserved for rotational eccentricity, as defined by total indicator readings or the like.) 未全深度切割或轧制的螺纹部分，但提供全深度螺纹与主体或头部之间的过渡。官方称之为螺纹冲蚀或消失，但术语“耗尽”更为流行。（跳动是官方为旋转偏心度保留的，由总指示器读数等定义。） |
| Clip gauge | 夹规 |
A displacement gauge consisting of two thin strain-gauged cantilever arms attached through knife edges to a testpiece to give the load–line displacement in fracture mechanics test pieces, or used as an extensometer in tensile tests. 一种位移计，由两个通过刀刃连接到试件上的薄应变测量悬臂组成，以提供断裂力学试件中的载荷线位移，或用作拉伸试验中的引伸计。 |
| Hot hardness | 热硬度 |
The hardness of materials at high temperatures, often used to rank the performance of cutting tools. 材料在高温下的硬度，常用来对刀具的性能进行排名。 |
| Rupture stress | 断裂应力 |
The stress at failure. Also known as breaking stress. 失效时的应力。也称为破裂应力。 |
| Elbow | 肘部 |
1. A fitting that connects the ends of two pipes at an angle, 45°, 90°, and 180° being the most common. 2. The third joint on an articulated robot corresponding to the human elbow. 1.以45°、90°和180°角连接两个管道端部的配件。2.示例关节机器人上的第三关节对应于人的肘部。 |
| Allowable stress design | 许用应力设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Purposely underestimates the strengths of bolts and joint materials to introduce safety factors into the design of structural steel joints. It is an alternative to the more recently defined load and resistance factor design procedure. 结构连接研究委员会为AISC制定的设计程序。故意低估螺栓和接头材料的强度，以便在结构钢接头的设计中引入安全系数。它是最近定义的荷载和阻力系数设计程序的替代方法。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Isothermal annealing | 等温退火 |
Austenitizing a ferrous alloy and then cooling to and holding at a temperature at which austenite transforms to a relatively soft ferrite carbide aggregate. 将铁合金奥氏体化，然后冷却至奥氏体转变为相对软的铁素体碳化物集合体的温度并保持该温度。 |
| Radioactive heat (Unit J) | 放射性热（单位J） |
Thermal energy released from the nucleus of an atom such as uranium235 by fission due to the absorption of a neutron. Heat is also produced by radioactive decay. 铀235等原子核因吸收中子而裂变释放的热能。放射性衰变也会产生热量。 |
| Tangent screw | 微动螺旋 |
A worm screw used to adjust measuring instruments such as sextants and vernier callipers. 用于调整六分仪和游标卡尺等测量仪器的蜗杆。 |
| Pitch diameter | 中径 |
For screw threads, the diameter of an imaginary cylinder, the surface of which would pass through the threads at such points that would make the width of the groove and width of the land equal to one half the pitch. 对于螺纹，指一个假想圆柱体的直径，其表面将在使凹槽宽度和焊盘宽度等于螺距一半的点穿过螺纹。 |
| Quench-age embrittlement | 淬火时效脆化 |
Embrittlement of low-carbon steels resulting from precipitation of solute carbon at existing dislocations and from precipitation hardening of the steel caused by differences in ferrite at different temperatures. Quenchage embrittlement usually is caused by rapid cooling of the steel from temperatures slightly below Ac1 (the temperature at which austenite begins to form), and can be minimized by quenching from lower temperatures. 低碳钢的脆化是由于溶质碳在现有位错处的沉淀和铁素体在不同温度下的差异导致的钢沉淀硬化造成的。淬火脆性通常是由钢从略低于Ac1的温度（奥氏体开始形成的温度）快速冷却引起的，可以通过从较低温度淬火来最小化。 |
| Captive nut | 松脱螺母 |
A nut attached loosely or rigidly to a sheet member that is too thin to thread and which engages with a cap screw. 松脱地或刚性地连接到薄板构件上的螺母，该螺母太薄而无法拧入，并与带帽螺钉接合。 |
| Austenite | 奥氏体 |
A solid solution of one or more elements in face-centered cubic iron. Unless otherwise designated (such as nickel austenite), the solute is generally assumed to be carbon. Solid solution of alloying elements and/or carbon in γ-Fe. It is named after British metallurgist W. C. Roberts-Austen. 一种或多种元素在面心立方铁中的固溶体。除非另有说明（如镍奥氏体），溶质通常假定为碳。合金元素和/或碳在γ-Fe中的固溶体。它以英国冶金学家WCRoberts-Austen的名字命名。 |
| J-integral | J-积分 |
A mathematical expression describing a line or surface integral that encloses the crack front from one crack surface to the other, used to characterize the fracture toughness of a material having appreciable plasticity before fracture. The J-integral eliminates the need to describe the behavior of the material near the crack tip by considering the local stress-strain field around the crack front; JIc is the critical value of the J-integral required to initiate crack extension from a preexisting crack. 描述从一个裂纹表面到另一个裂纹正面的线或表面积分的数学表达式，用于表征断裂前具有可观塑性的材料的断裂韧性。J积分通过考虑裂纹前缘周围的局部应力应变场，无需描述裂纹尖端附近材料的行为；JIc是从先前存在的裂纹开始裂纹扩展所需的J积分的临界值。 |
| Compressive stress (Unit Pa) | 压缩应力（单位Pa） |
The compressive load per unit area at a point in a component. 部件中某点的每单位面积的压缩载荷。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Compression wave | 压缩波 |
(dilatation wave) In a fluid or a solid, a progressive wave or wavefront that compresses the medium through which it propagates. （膨胀波）在流体或固体中，压缩介质传播的行波或波前。 |
| Coaxial | 同轴 |
A term for components having a common axis such as concentric shafts. 具有共同轴线的部件的术语，例如同心轴。 |
| Stud | 螺柱 |
A rod having thread on both ends. A headless threaded fastener, threaded on both ends, with an unthreaded body in the middle section, or threaded from end to end. Used with two nuts, or with one nut and a tapped hole. A plain cylindrical piece having a threaded portion of suitable length at each end or a continuous thread over the entire length. One end is screwed into a machine or workpiece after which a second part is placed over the stud and held in place by a nut. 两端都有螺纹的杆。无头螺纹紧固件，两端有螺纹，中间部分有无螺纹主体，或从一端到另一端有螺纹。与两个螺母或一个螺母和一个螺纹孔一起使用。一种普通的圆柱形部件，其两端具有适当长度的螺纹部分，或在整个长度上具有连续螺纹。一端拧入机器或工件，然后将第二部分放在螺柱上，并用螺母固定到位。 |
| Nominal stress | 名义应力 |
The stress at a point calculated on the net cross section by simple elasticity theory without taking into account the effect on the stress produced by stress raisers such as holes, grooves, fillets, etc. 通过简单弹性理论在净截面上计算的点处的应力，不考虑孔、槽、圆角等应力提升器产生的应力影响。 |
| Hypoeutectic alloy | 亚共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of base metal compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，其成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Mechanical vibration | 机械振动 |
The motion of a particle or body which oscillates about a position of equilibrium. 围绕平衡位置摆动的粒子或物体的运动。 |
| Bernoulli’s law | 伯努利定律 |
For a steadily flowing fluid (liquid or gas), the sum of the pressure, kinetic energy per unit volume and potential energy per unit volume is constant at any point in the fluid. Using this relationship, it is possible to measure the velocity of a fluid by measuring its pressure at two points, as with a manometer or Pitot tube. 对于稳定流动的流体（液体或气体），压力、每单位体积的动能和每单位体积的势能之和在流体中的任何点都是恒定的。使用这种关系，可以通过在两个点测量流体的压力来测量流体的速度，就像使用压力计或皮托管一样。 |
| Newton’s law of viscosity | 牛顿内摩擦定律 |
The shear stress between two parallel layers of fluid is proportional to the velocity of one relative to that of the other, and inversely proportional to the distance between them. The constant of proportionality is the dynamic viscosity μ. For a Newtonian fluid μ is independent of pressure gradient, shear stress, and strain, but may change with temperature and pressure. 两个平行流体层之间的剪切应力与其中一层相对于另一层的速度成正比，与它们之间的距离成反比。比例常数是动态粘度μ。对于牛顿流体，μ与压力梯度、剪切应力和应变无关，但可能随温度和压力而变化。 |
| Melting point (Unit K or °C) | 熔点（单位K或°C） |
The temperature at which a solid material undergoes the phase change to a liquid at a specified pressure, usually 1 atm. Pure metals and eutectics have single-valued melting points, while alloys with other compositions melt over a range of temperature such that there is a well-defined start and end to the melting process, but there are states in between where solid and liquid are both present. 在特定压力下，固体材料发生相变为液体的温度，通常为1大气压。纯金属和共晶具有单值熔点，而具有其他成分的合金在一定温度范围内熔化，熔化过程有一个明确的起点和终点，但其间存在固态和液态并存的状态。 |
| True stress (σ) (Unit Pa) | 真应力（σ）（单位Pa） |
The value obtained by dividing the load applied to a member at a given instant by the cross-sectional area over which it acts. Compare with engineering stress. The applied load on a test specimen divided by the current cross-section area over which it acts. σ = s expε where s is the engineering stress given by the applied load divided by the original cross-section area over which it acts, and ε is the true strain. 通过将给定时刻施加在构件上的荷载除以其作用的横截面积而获得的值。与工程应力相比。施加在试样上的荷载除以其作用的当前横截面积。σ=s expε，其中s是由施加荷载除以其作用的原始横截面面积得出的工程应力，ε是真实应变。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| Vehicle | 车辆 |
A means of conveyance for transporting goods and people, generally with wheels powered by a petrol, diesel, or steam engine, or by an electric motor, or by a hybrid combination of an electric motor and a diesel or petrol engine. 一种运输货物和人员的交通工具，通常由汽油机、柴油机或蒸汽机、电动机或电动机与柴油机或汽油机的混合动力驱动。 |
| Static fatigue | 静态疲劳 |
A term referring to a time-dependent reduction in strength with a static (noncyclic) load. The term may refer to hydrogen-induced delayed cracking or the effect of creep on the strength of plastics. Delayed fracture caused by environmental effects under dead-weight loading of materials such as glass. The name is unfortunate, as cyclic loads are not involved and glass is not susceptible to fatigue. 指静态（非循环）载荷下强度随时间变化的降低。该术语可指氢致延迟开裂或蠕变对塑料强度的影响。在玻璃等材料的自重荷载下，由环境影响引起的延迟断裂。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Kinetic energy | 动能 |
Energy that an object possesses because it is in motion. It is the energy given to an object to set it in motion. On impact, it is converted into other forms of energy such as strain, heat, sound and light. 物体因运动而拥有的能量。它是赋予物体使其运动的能量。撞击时，它被转换成其他形式的能量，如应变、热、声和光。 |
| Vernier | 游标 |
A short auxiliary scale that slides along the main instrument scale to permit more accurate fractional reading of the least main division of the main scale. 一种短辅助刻度，沿主仪表刻度滑动，以便更准确地读取主刻度的最小主刻度。 |
| Torque motor | 力矩电机 |
A type of induction motor that can apply a steady torque even when prevented from rotating. 一种感应电动机，即使被阻止旋转也能施加稳定的转矩。 |
| Sampling | 抽样 |
The process of measuring a series of values of a time-varying quantity. 测量一系列时变量值的过程。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Crack | 裂缝 |
A thin fissure-like defect in a component or structure across which material continuity is lost and which reduces the strength of the body. 部件或结构中的细裂缝状缺陷，材料连续性丧失并降低了身体的强度。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Oil hardening | 油回火 |
The formation of martensite before tempering by quenching suitable steels in oil at lower cooling rates than given by water quenching, thus reducing the likelihood of component fracture or severe residual stresses. Quench-hardening treatment involving cooling in oil. 通过在油中以低于水淬的冷却速率淬火合适的钢，在回火前形成马氏体，从而降低部件断裂或严重残余应力的可能性。是一种淬火硬化处理，包括在油中冷却。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Relaxed stress | 松弛应力 |
The initial stress minus the remaining stress at a given time during a stress-relaxation test. 在应力松弛试验期间，初始应力减去给定时间的剩余应力。 |
| Permanent set | 永久变形 |
The deformation or strain remaining in a previously stressed body after release of load. 释放荷载后，先前受力物体中剩余的变形或应变。 |
| Transgranular | 穿晶 |
Through or across crystals or grains. Also known as intracrystalline or transcrystalline. 穿过或横穿晶体或颗粒。也称为晶内或晶间。 |
| Wind pressure (Unit Pa) | 风压（单位Pa） |
The dynamic pressure associated with the wind. The static pressure of the wind is the atmospheric pressure. 与风相关的动态压力。风的静压是大气压。 |
| Vibration-testing machine (vibrator) | 振动试验机（振动器） |
Any machine that subjects components or systems to vibration at known amplitudes and frequencies in order to determine the response. vibratory equipment Vibrating process equipment, such as shakers, used to separate small and large particles, or feeders to supply particulate or granular material that may otherwise clog. 使部件或系统以已知振幅和频率振动以确定响应的任何机器。振动设备振动工艺设备，如用于分离小颗粒和大颗粒的振动筛，或用于供应可能堵塞的颗粒或粒状材料的给料机。 |
| Snap temper | 快速回火 |
A precautionary interim stress-relieving treatment applied to high-hardenability steels immediately after quenching to prevent cracking because of delay in tempering them at the prescribed higher temperature. 在淬火后立即对高淬透性钢进行预防性临时应力消除处理，以防止因在规定的更高温度下回火延迟而开裂。 |
| Turboblower | 涡轮鼓风机 |
A centrifugal or axial compressor or fan. 离心式或轴流式压缩机或风扇。 |
| Screw feeder | 螺旋给料机 |
A mechanism for handling bulk materials in which a rotating helicoidal screw moves the material axially forward. Similar to a screw conveyor, but required to discharge material at a controlled rate very accurately. It operates with the screw completely full. 一种用于处理散装物料的机构，其中旋转的螺旋螺杆使物料轴向向前移动。类似于螺旋输送机，但需要以受控速率非常精确地排出物料。它在螺杆完全充满的情况下运行。 |
| Ablation cooling | 烧蚀冷却 |
The cooling of a surface exposed to very high external gas temperature which causes the surface material to sublime, melt or decompose. The chemical process absorbs heat while the mass flow of material away from the surface blocks the heat flux from the hot gas. 冷却暴露于非常高的外部气体温度的表面，导致表面材料升华、熔化或分解。化学过程吸收热量，而远离表面的物质的质量流阻挡了来自热气体的热通量。 |
| Engine emissions | 发动机排放 |
(exhaust emissions) The pollutants contained in the exhaust gases from an internal-combustion engine. （废气排放）内燃机废气中所含的污染物。 |
| Brayton cycle | 布雷顿循环 |
(Joule cycle) An air standard cycle that is the ideal cycle for a gasturbine engine. As shown on the diagram of pressure (p) ʋs specific volume (ʋ), it consists of four internally reversible processes: isentropic compression in a compressor (1–2), isobaric heat addition in a combustor (2–3), isentropic expansion in a turbine (3–4) and isobaric heat rejection. The cycle can be extended to include regeneration, reheating, and intercooling. （焦耳循环）一种空气标准循环，是燃气轮机发动机的理想循环。循环可以扩展到包括再生、再热和中冷。 |
| Black oxide | 黑色氧化物 |
A black finish on a metal produced by immersing it in hot oxidizing salts or salt solutions. 通过将金属浸入热氧化盐或盐溶液中产生的黑色饰面。 |
| Compression crease | 压缩折痕 |
A crease formed during the compression of composites having a high volume fraction of filaments. These composites fail in compression by forming a crease at an angle to the loading axis. 在压缩具有高体积分数长丝的复合材料期间形成的折痕。这些复合材料通过形成与加载轴成一定角度的折痕而在压缩中失效。 |
| Relaxation rate | 松弛率 |
The absolute value of the slope of a stress-relaxation curve at a given time. 给定时间应力松弛曲线斜率的绝对值。 |
| Roots blower | 罗茨鼓风机 |
(rotary-piston blower) A positive-displacement gas compressor with two meshing lobed rotors that rotate within a close-fitting casing. Commonly used as a supercharger. （旋转活塞鼓风机）一种容积式气体压缩机，具有两个啮合的凸角转子，在紧密配合的外壳内旋转。通常用作增压器。 |
| Hot dipping | 热浸 |
(hot-dip galvanizing) A process of coating an iron, steel, or aluminium object with a thin layer of zinc by passing it through a bath of molten zinc at a temperature of about 460°C. （热浸镀锌）通过使铁、钢或铝物体通过温度约为460°C的熔融锌浴，在铁、钢或铝物体上镀上一层薄薄的锌层的工艺。 |
| Impact energy (Unit J) | 冲击能量（单位J） |
The amount of energy required to fracture a material, usually measured by means of an Izod test or Charpy test.The type of specimen and test conditions affect the values and therefore should be specified. 1. The sum of the kinetic energies of all the bodies involved at the instant of collision of two or more moving bodies. 2. The energy required to fracture a specimen in a Charpy or Izod impact test. 使材料断裂所需的能量，通常通过悬臂梁式试验或夏比试验测量。试样类型和试验条件会影响数值，因此应加以说明。1.两个或多个运动物体碰撞瞬间所有物体的动能之和。2.夏比或悬臂冲击试验中断裂试样所需的能量。 |
| Temper | 回火 |
(1) In heat treatment, reheating hardened steel or hardened cast iron to some temperature below the eutectoid temperature for the purpose of decreasing hardness and increasing toughness. The process also is sometimes applied to normalized steel. (2) In tool steels, temper is sometimes used, but inadvisedly, to denote the carbon content. (3) In nonferrous alloys and in some ferrous alloys (steels that cannot be hardened by heat treatment), the hardness and strength produced by mechanical or thermal treatment, or both, and characterized by a certain structure, mechanical properties, or reduction in area during cold working. （1）在热处理中，将硬化钢或硬化铸铁重新加热到共析温度以下的温度，以降低硬度和增加韧性。该工艺有时也适用于正火钢。（2）在工具钢中，有时使用回火来表示碳含量，但这是不恰当的。（3）在非铁合金和一些铁合金（不能通过热处理硬化的钢）中，通过机械或热处理或两者产生的硬度和强度，其特征是在冷加工过程中具有一定的结构、机械性能或面积减小。 |
| Crosshead | 十字头 |
1. A reciprocating member, sliding between guides, to which the piston rod is firmly attached on one side and to which the connecting rod is pinned on the other for the conversion of reciprocating into rotary motion. 2. The moveable beam in early designs of mechanical testing machines. 3. A screwhead having slots in a + shape that takes a mating screwdriver. 1.一种往复式构件，在导轨之间滑动，活塞杆一侧固定在其上，连杆另一侧固定在该构件上，用于将往复式运动转换为旋转运动。2.机械试验机早期设计中的活动梁。3.一种螺钉头，其具有采用配合螺丝刀的+形槽。 |
| Spring temper | 弹簧回火 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about two-thirds of the way from full hard to extra spring temper. 非铁合金和一些铁合金的一种回火，其特点是抗拉强度和硬度约为全硬回火到超弹性回火的三分之二。 |
| Bolt blank | 螺栓毛坯 |
A rod on which a head has been formed, but on which no thread has been cut, from which bolts or screws may be made as required. 一种已形成头部但未切割螺纹的杆，可根据需要从中制造螺栓或螺钉。 |
| Celsius | 摄氏度 |
The temperature scale based on the freezing point of water (0ºC) and the boiling point of water (100ºC). The interval between these points is divided into 100 degrees. The scale was devised by Anders Celsius. 基于水的冰点（0ºC）和水的沸点（100ºC）的温标。这些点之间的间隔被划分为100度。这个比例是由安德斯·摄氏设计的。 |
| Materials science | 材料科学 |
The study of the properties, behaviour, and application of solid substances such as metals, ceramics, glasses, polymers, composites, biomaterials, and semiconductors, at all scales from the atomic to the macroscopic. The topic has its origins in metallurgy. 研究金属、陶瓷、玻璃、聚合物、复合材料、生物材料和半导体等固体物质的特性、行为和应用，涵盖从原子到宏观的所有范围。起源于冶金学。 |
| Flame straightening | 火焰矫直 |
Correcting distortion in metal structures by localized heating with a gas flame. 通过使用气体火焰进行局部加热来纠正金属结构的变形。 |
| Blind rivet | 盲孔铆钉 |
A rivet that enables a connexion to be made from one side only of an assembly. 一种铆钉，可以仅从组件的一侧进行连接。 |
| Plastic deformation | 塑性变形 |
The permanent (inelastic) distortion of a material under applied stress that strains the material beyond its elastic limit. 材料在施加应力下的永久（非弹性）变形，使材料应变超过其弹性极限。 |
| Critical load (Unit N) | 临界负荷（单位N） |
1. The applied load that causes propagation of an existing crack of known length, and hence fracture of a component or structure. 2. The applied load that results in buckling of a column of given end fixity. 1.导致已知长度的现有裂纹扩展并因此导致部件或结构断裂的施加荷载。2.导致具有给定端部固定性的柱屈曲的施加荷载。 |
| Offset yield strength | 条件屈服强度 |
The stress at which the strain exceeds by a specified amount (the offset) an extension of the initial proportional portion of the stress-strain curve. Expressed in force per unit area. 应变超过应力-应变曲线初始比例部分延伸规定量（偏移）的应力。以每单位面积的力表示。 |
| Stress | 应力（单位Pa） |
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression)or shear. 1. Stress ‘at a point’ (i.e. over a volume of material that is very small compared with that of the component or structure) is the load per unit area for every face of an infinitesimal cube surrounding the point. 2. In fluid flow the stress tensor σij is the sum of an isotropic part −pδij, δij being the Kronecker delta, having the same form as the stress tensor for a fluid at rest, p being the static pressure, and the non-isotropic, deviatoric stress tensor dij which is due entirely to the fluid motion. 内部分布力或力分量的强度，这些力或力的分量抵抗正在或已经受到外力的材料的体积或形状的变化。应力以单位面积的力表示，并根据试样横截面的原始尺寸计算。应力可以是直接（拉伸或压缩）或剪切。1.“在一点”的应力（即在与组件或结构相比非常小的材料体积上）是围绕该点的无限小立方体的每个面的单位面积载荷。2. 在流体流动中，应力张量σij是各向同性部分-pδij的总和，δij是Kroneckerδ，具有与静止流体的应力张量相同的形式，p是静压，非各向同性, 偏应力张量 dij 完全由流体运动引起。 |
| Wire rope | 钢丝绳 |
A type of cable formed from individual strands of wire with a helical twist. 一种线缆，由具有螺旋扭曲的单独的线股形成。 |
| Die | 模具 |
1. A tool having an appropriately-shaped hole through which material may be extruded or drawn. 2. A tool employed in forging. 3. A block having the male or female shape employed in stamping operations. 4. A thick circular disc, driven by a die wrench, with internally-threaded cutting edges for producing a screw thread. A die wrench (die stock) holds a screw-cutting die and has two projecting arms for applying the torque necessary to cut the thread. A die having a hexagonal or square shape (die nut), driven by a spanner, is used in confined spaces where a die wrench cannot be rotated through a full circle. 1.一种具有适当形状的孔的工具，通过该孔可以挤压或拉伸材料。2.一种用于锻造的工具。3.一种用于冲压操作的具有阳或阴形状的块体。4.一种由模具扳手驱动的厚圆盘，具有用于产生螺纹的内螺纹切削刃。冲模扳手（冲模）装有一个螺旋切割模，并有两个突出臂，用于施加切割螺纹所需的扭矩。由扳手驱动的六边形或方形模具（模具螺母）用于模具扳手无法旋转一整圈的受限空间。 |
| Brittle | 脆性材料 |
A brittle material is one that breaks, often suddenly, with no permanent deformation. Examples of brittle materials are some cast irons, glass, concrete, and some plastics. A bolt is said to be brittle if it will break when stretched only a small amount past its yield point. 脆性材料通常会突然断裂，不会产生永久变形。脆性材料的例子有一些铸铁、玻璃、混凝土和一些塑料。如果螺栓在拉伸时仅超过其屈服点一小部分就会断裂，则称其为脆性螺栓。 |
| Delamination | 分层 |
A mode of failure of composite materials, including radial-ply tyres, in which the layers separate due to repeated cyclic loading, impact, or weak bonding. 复合材料的一种失效模式，包括子午线轮胎，其中层由于重复的循环载荷、冲击或弱粘合而分离。 |
| Lathe | 车床 |
A machine tool in which work, gripped in the headstock, is rotated against the cutting tool to produce turned, bored, faced, or threaded components. 一种机床，其中夹持在主轴箱中的工件靠着切削工具旋转，以生产车削、钻孔、端面或螺纹部件。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Atmosphere | 大气 |
1. (atm) An obsolete (non-SI) unit of pressure equal to 101 325 Pa or 1.013 25 bar and approximately equal to the atmospheric pressure (barometric pressure) measured at mean sea level. 1.（atm）一种已被淘汰的（非SI）压力单位，等于101325Pa或1.01325bar，大约等于在平均海平面测量的大气压力（大气压）。 |
| Coining | 压印 |
A forging operation, employing a closely-fitting punch and die from which no metal is allowed to escape, in which the surface pattern on the punch and die is imprinted on the blank. 一种锻造操作，采用紧密配合的凸模和模具，不允许金属逸出，其中凸模和模具上的表面图案印在坯料上。 |
| Monotron hardness test | 摩诺硬度试验 |
An obsolete method of determining indentation hardnessby measuring the load required to force a spherical penetrator into a metal to a specified depth. 一种已被淘汰的方法，通过测量将球形侵彻体压入金属至规定深度所需的载荷来确定压痕硬度。 |
| Gauge pressure (Unit Pa) | 表压（单位Pa） |
The level of static pressure above the ambient pressure. 高于环境压力的静压水平。 |
| Design heating load (Unit kW) | 设计热负荷（单位kW） |
The heating requirements based on a specified number of heating degree days, or required to maintain a building or other enclosed space at a specified temperature for a given outside temperature. 基于指定的采暖度日数的加热要求，或在给定的外部温度下将建筑物或其他封闭空间保持在指定温度下所需的加热要求。 |
| Millimetre of mercury | 毫米汞柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of mercury 1 mm high. Approximately equal to 133.3 Pa or 1 torr. 一种非SI压力单位，等于1毫米高的垂直水银柱施加的压力。大约等于133.3Pa或1托。 |
| Fastener manufacturer | 紧固件制造商 |
An organization that fabricates raw steel into a fastener meeting specified standards. 将生钢加工成符合规定标准的紧固件的组织。 |
| T-bolt | T型螺栓 |
A threaded bolt having a square or rectangular end which fits into the T slot of a machine table for clamping workpieces. 一种带有方形或矩形端头的螺栓，可嵌入机床工作台的T形槽中，用于夹紧工件。 |
| Knoop hardness test | 努氏硬度试验 |
An indentation-hardness test using calibrated machines to force a rhombic-based pyramidal diamond indenter having specified edge angles, under specified conditions, into the surface of the material under test and to measure the long diagonal after removal of the load. An indentation hardness test in which the indenter is an elongated diamond pyramid that gives an impression in the form of a parallelogram, in which the longer diagonal is about seven times the shorter. Used for studies of anisotropy in solid materials. 使用校准机器进行的一种压痕硬度试验，在规定条件下，将具有规定边缘角的菱形棱锥金刚石压头压入受试材料表面，并在移除荷载后测量长对角线。其中压头是一个细长的菱形棱锥，以平行四边形的形式给出压痕，其中较长的对角线约为较短的七倍。用于研究固体材料的各向异性。 |
| Planar anisotropy | 平面异向性 |
A variation in physical and/or mechanical properties with respect to direction within the plane of material in sheet form. 在片状材料平面内，物理和/或机械性能相对于方向的变化。 |
| Double aging | 双级时效 |
Employment of two different aging treatments to control the type of precipitate formed from a supersaturated matrix in order to obtain the desired properties. The first aging treatment, sometimes referred to as intermediate or stabilizing, is usually carried out at higher temperature than the second. 采用两种不同的时效处理来控制由过饱和基质形成的沉淀物类型，以获得所需的性能。第一次时效处理，有时称为中间处理或稳定处理，通常在比第二次更高的温度下进行。 |
| Caustic quenching | 苛性淬火 |
Quenching with aqueous solutions of 5 to 10% sodium hydroxide (NaOH). 用5%至10%氢氧化钠（NaOH）水溶液淬灭。 |
| Quench cracking | 淬火开裂 |
Fracture of a metal during quenching from elevated temperature. Most frequently observed in hardened carbon steel, alloy steel, or tool steel parts of high hardness and low toughness. Cracks often emanate from fillets, holes, corners, or other stress raisers and result from high stresses due to the volume changes accompanying transformation to martensite. 高温淬火时金属断裂。在高硬度和低韧性的硬化碳钢、合金钢或工具钢零件中最常见。裂纹通常来自圆角、孔、角部或其他应力集中区，并由伴随马氏体转变的体积变化引起的高应力引起。 |
| Microstrain | 微应变 |
The strain over a gage length comparable to interatomic distances. These are the strains being averaged by the macrostrain measurement. Microstrain is not measurable by currently existing techniques. Variance of the microstrain distribution can, however, be measured by x-ray diffraction. 与原子间距离相当的标距上的应变。这些是通过宏观应变测量得到的平均应变。现有技术无法测量微应变。然而微应变分布的变化可以通过x射线衍射来测量。 |
| Taper pins | 圆锥销 |
A pin or peg of circular cross section that tapers along its length. Steel pins used for locating and holding the machine parts in position on a shaft. 沿其长度逐渐变细的圆形横截面的销钉或销钉。用于在轴上定位和固定机器零件的钢销。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| Strength of materials | 材料强度 |
A confusing name for what is really stress analysis, reflecting older engineering design based upon elasticity and ‘theories of strength’ for different materials, without regard to cracks. 对于真正的应力分析，这是一个具有迷惑性的名称，反映了基于弹性和不同材料的“强度理论”的旧工程设计，而不考虑断裂。 |
| Two-dimensional flow | 二维流 |
A fluid flow in which the velocity at any time depends upon two spatial coordinates, such as the radial and axial locations in developing pipe flow. 一种流体流动，其中任何时候的速度取决于两个空间坐标，如发展中的管道流中的径向和轴向位置。 |
| Centrifugal force (Unit N) | 离心力（单位N） |
The inertial reaction force to the centripetal force. It is equal in magnitude but opposite in direction. 惯性反作用力对向心力。它的大小相等，但方向相反。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Vickers hardness number | 维氏硬度值 |
(diamond hardness number, DHN, VHN, VPN) (Unit kg/mm² originally, sometimes now Pa) Indentation hardness given by load divided by the surface area of the permanent impression obtained when the indenter is in the form of a square pyramid whose opposite faces make an angle of 136° with one another. The mean length d of the diagonals of the indentation is determined, from which VPN = 0.927(2W/d2) where W is the load, since the base of the pyramid has an area equal to 0.927 times the surface area. （金刚石硬度值，DHN，VHN，VPN）（最初单位为kg/mm²，有时为Pa）压痕硬度，由载荷除以永久压痕的表面积得出，当压头呈方形棱锥体形式时，其相对面彼此成136°角。确定压痕对角线的平均长度d，其中VPN=0.927（2W/d2），其中W是载荷，因为棱锥底部的面积等于表面积的0.92七倍。 |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Centrifugal fan | 离心风机 |
A machine with a rotor consisting of a number of blades mounted around a hub and used for moving air or other gases. The gas enters the rotor axially and is discharged radially at increased pressure. 一种带有转子的机器，转子由安装在轮毂周围的许多叶片组成，用于移动空气或其他气体。气体轴向进入转子并在增加的压力下径向排出。 |
| Washer | 垫圈 |
An annular disc of metal, rubber, plastic, ceramic, etc., placed between two surfaces in contact either to spread the load (for example, between a surface and a tightened nut or a bolt head), to provide a seal, or to separate or align components. 由金属、橡胶、塑料、陶瓷等制成的环形圆盘，放置在两个接触面之间，以分散载荷（例如，在一个表面和拧紧的螺母或螺栓头之间），提供密封，或分离或对齐部件。 |
| Pressure storage tank | 压力贮存器 |
(pressure vessel) A closed container for storing gases or volatile liquids, such as liquefied gases, at pressures significantly above atmospheric pressure. Such tanks are commonly cylindrical with domed ends, spherical, spheroidal, torispherical or hemispherical. （压力容器）密闭容器：在大气压以上的压力下储存气体或挥发性液体，如液化气体的密闭容器。此类贮存器通常为圆柱形，具有半球形端部、球形、球面或半球形。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Radial engine | 径向发动机 |
A piston engine in which the cylinders are arranged radially around the crankshaft, a design commonly used in early aircraft engines. 气缸沿径向围绕曲轴布置的活塞式发动机，这种设计通常用于早期飞机发动机。 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Weight (W) (Unit N) | 重量（W）（单位：N） |
The force of attraction on a body due to gravity. A body’s weight is the product of its mass and the gravitational field strength at that point. Mass remains constant, but weight depends on the object’s position on the Earth’s surface, decreasing with increasing altitude. If g is the acceleration due to gravity, the weight of a mass m is given by W = mg. On Earth, the acceleration due to gravity is approximately 9.81 m/s², so that the weight of a 1 kg mass is 9.81 N. More generally, the weight is the force exerted on the mass of a body when in the gravitational field of another body. 重力由于重力作用在物体上的吸引力。物体的重量是其质量和该点引力场强度的乘积。质量保持不变，但重量取决于物体在地球表面的位置，随着海拔的升高而减小。如果g是重力引起的加速度，则质量m的重量由W=mg给出。在地球上，重力引起的加速度约为9.81m/s²，因此1千克质量的重量为9.81N。更一般地说，重量是在另一个物体的重力场中施加在物体质量上的力。 |
| Die screw | 模具螺丝 |
Tool used when threading cylindrical pieces beyond the capacity of a die plate. 对超出模板容量的圆柱件进行螺纹加工时使用的工具。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Working load (Unit N) | 工作负荷（单位：N） |
The tension in a bolt in use; tension produced by a combination of Residual preload and a portion (usually) of any External load. The Joint diagram is usually used to predict the approximate working load a fastener will see in service. The load under which a component or structure is designed to operate under normal conditions. 螺栓在使用中的张力；残余预载荷和部分（通常）任何外部载荷的组合产生的张力。连接图通常用于预测紧固件在使用中的近似工作载荷。部件或结构设计为在正常条件下运行的荷载。 |
| Tracking problem | 跟踪问题 |
A control problem where the set point changes with time and thus the plant output must follow the changing set point. The opposite of a regulator problem. 一种控制问题，其中设定值随时间变化，因此设备输出必须遵循变化的设定值。与调节器问题相反。 |
| British Standards Institution (BSI) | 英国标准协会（BSI） |
The Institution in the UK responsible for the preparation and publication of standard specifications (British standards) for manufactured goods, their design, manufacture and testing. 负责为制成品及其设计、制造和测试制定和发布标准规范（英国标准）的英国机构。 |
| Toothed belt | 齿带 |
A flat belt, typically of a reinforced-rubber material, with transverse teeth that engage with teeth on a wheel or pulley. 一种扁平皮带，通常由增强橡胶材料制成，带有横向齿，与车轮或皮带轮上的齿啮合。 |
| Surface hardness | 表面硬度 |
(superficial hardness) Indentation hardness on, and for some distance below, the surface of a component, as opposed to its bulk hardness. Depending on the resolution required, micro- or nano-hardness testing machines are employed. （表面硬度）与整体硬度相反，部件表面及其下方一定距离的压痕硬度。根据所需的分辨率，可使用微型或纳米硬度测试机。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Secant modulus | 割线模量 |
The slope of the secant drawn from the origin to any specified point on a stress-strain curve. Compare with chord modulus. 从原点到应力应变曲线上任何指定点的割线斜率。与弦模量进行比较。 |
| Linear-elastic fracture mechanics | 线弹性断裂力学 |
A method of fracture analysis that can determine the stress (or load) required to induce fracture instability in a structure containing a cracklike flaw of known size and shape. 一种断裂分析方法，可确定在含有已知尺寸和形状裂纹状缺陷的结构中引起断裂不稳定性所需的应力（或载荷）。 |
| Bimetallic strip | 双金属片 |
A strip formed by welding, riveting or brazing together two metals having different coefficients of expansion, which causes the strip to curl when its temperature changes. Typical combinations are steel and copper or steel and brass. 将两种膨胀系数不同的金属焊接、铆接或钎焊在一起形成的带材，当温度变化时，带材会卷曲。典型的组合是钢和铜或钢和黄铜。 |
| Scratch hardness | 划痕硬度 |
The resistance of a material, such as a metal, alloy, plastic, or mineral, to scratching by a much harder indenter, such as a diamond stylus, moved slowly across the surface. The scratch hardness number is computed from the loads and the dimensions of the residual scratch. 一种材料（如金属、合金、塑料或矿物）对更硬的压头（如金刚石触针）划伤的抵抗力，在表面上缓慢移动。根据载荷和残余划痕的尺寸计算划痕硬度值。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Circlip | 卡簧 |
(snap ring) An external or internal retaining ring that locates parts of circular cross section in an axial direction. It consists of an incomplete ring, with holes on either side of the gap, that may be expanded by a plier-like tool to pass into a groove in a shaft or contracted to pass into a groove in a bore. （卡环）在轴向定位圆形横截面部分的外部或内部保持环。它由一个不完整的环组成，在间隙的任一侧都有孔，可以通过钳形工具将其扩展以进入轴中的凹槽或收缩以进入孔中的凹槽。 |
| Relaxation curve | 松弛曲线 |
A plot of either the remaining, or relaxed, stress as a function of time. 剩余压力或松弛压力随时间变化的曲线图。 |
| SI system | SI国际单位制 |
SI is an abbreviation of Système International d’Unités, i.e., the international unit measurement system – an internationally established system of measurement units built on older metric systems. SI是Système International d‘Unités的缩写，即国际单位计量系统——一种基于旧公制的国际公认计量单位系统。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| Shear strain | 剪切应变 |
The tangent of the angular change, as a response to force, between two lines originally perpendicular to each other through a point in a body. Also known as shearing strain. 角变化的切线，作为对力的响应，在两条原本通过物体中的一个点相互垂直的线之间。也称为剪切应变。 |
| Balancing machine | 平衡机 |
A device that assesses the state of static and dynamic balance of a rotating part, and indicates the magnitude and location of weights to be added to give balance. 一种装置，用于评估旋转部件的静态和动态平衡状态，并指示为获得平衡而添加的砝码的大小和位置。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| Ackerman linkage | 阿克曼装置 |
A steering linkage on a motor vehicle that approximately gives rolling without slipping of both wheels about the turning point. This is achieved by having the inner stub axle (on the inside of the turning curve) move through a greater angle than the outer stub axle. 机动车辆上的一种转向联动装置，在转向点附近两个车轮几乎不会打滑。这是通过使内短轴（在转弯曲线的内侧）比外短轴移动更大的角度来实现的。 |
| Concentrated solar power plant (CSP plant) | 聚光太阳能发电厂（CSP发电厂） |
A power plant in which solar radiation is concentrated using mirrors or lenses, typically using parabolic trough mirrors which focus solar radiation on to receiver tubes along the trough’s focal line. In an alternative arrangement molten salt, heated by solar receivers mounted on a tower, is circulated through a steam generator. 使用镜子或透镜集中太阳辐射的发电厂，通常使用抛物面槽镜，将太阳辐射沿着槽的焦线聚焦到接收管上。在另一种布置中，由安装在塔上的太阳能接收器加热的熔盐通过蒸汽发生器循环。 |
| Right hand thread | 右旋螺纹 |
A screw thread which advances into the mating part when turned clockwise or to the right. 顺时针或向右转动时进入配合部件的螺纹。 |
| Maximum allowable working pressure (Unit Pa) | 最大允许工作压力（单位Pa） |
The pressure on which the design of a pressure system is based and the highest pressure at which relief valves should be set. The lowest-rated component in the system typically has a design safety factor of 4. 压力系统设计所依据的压力和应设置安全阀的最高压力。系统中最低额定部件的设计安全系数通常为4。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| Offset modulus | 补偿模量 |
The ratio of the offset yield stress to the extension at the offset point (plastics). 偏移屈服应力与偏移点（塑料）处延伸的比率。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Surface tension (σ, γ) (Unit N/m) | 表面张力（σ，γ）（单位：N/m） |
At the interface between a liquid and a gas or two immiscible liquids, unbalanced cohesive forces acting on the liquid molecules at the interface lead to the property surface tension which causes tensile forces to develop as if it were a skin or membrane. 液体和气体或两种不混溶液体之间的界面处，作用在界面处的液体分子上的不平衡内聚力导致表面张力的性质，从而导致张力的发展，就像皮肤或薄膜一样。 |
| Bulk velocity | 体积速度 |
(average velocity, V) (Unit m/s) For fluid flow in a pipe or duct, the average flow velocity, given by V = ṁ/ρA where ṁ is the mass flow rate, ρ is the fluid density, and A is the duct cross-sectional area. （平均速度，V）（单位m/s）对于管道或管道中的流体流动，平均流速，由V=ṁ/ρA给出，其中ṁ是质量流量，ρ是流体密度，A是管道截面积。 |
| Gear ratio | 传动比 |
For two gears in contact, the ratio of the number of teeth on the driving gear to that on the driven gear. 对于接触的两个齿轮，主动齿轮上的齿数与从动齿轮上的齿数之比。 |
| Air-cooled condenser | 风冷冷凝器 |
A heat exchanger, in which the cooling medium is air, used to condense the exhaust steam from a steam turbine, the condensate being returned to the boiler. 一种热交换器，其中冷却介质为空气，用于冷凝蒸汽轮机排出的蒸汽，冷凝水返回锅炉。 |
| Conduit | 导管 |
A hollow object, of metal, plastic, glass, ceramic, etc., which is relatively long compared with its lateral dimensions and through which there is fluid flow. 由金属、塑料、玻璃、陶瓷等制成的中空物体，与其横向尺寸相比相对较长，并且有流体流过。 |
| Turbine flow meter | 涡轮流量计 |
(axial flow meter, propeller meter) An in-line flow meter in which the rotation speed N of a propeller or rotor is a measure of the mass flowrate ṁ. Calibration is always necessary but with appropriate design ṁ is closely proportional to N over a wide range. （轴向流量计、螺旋桨流量计）一种串联流量计，其中螺旋桨或转子的转速N是质量流量的测量值ṁ. 校准总是必要的，但需要适当的设计ṁ在很宽的范围内与N成正比。 |
| Hydrodynamics | 流体力学 |
A term sometimes used to mean fluid dynamics, even when the fluid is a gas or a liquid other than water. 有时用于表示流体动力学的术语，即使流体是气体或水以外的液体。 |
| Clearance fit | 间隙配合 |
A range of clearances ranging from close sliding to loose running, i.e. a fit in which the limits for the mating parts always permit assembly. 从紧密滑动到松动运行的一系列间隙，即配合零件的限制始终允许组装的配合。 |
| Eccentric load | 偏心载荷 |
The external load on a fastener or groups of fasteners is said to be eccentric if the resultant of that load does not pass through the centroid of the group of fasteners (eccentric shear load ) or does not coincide with the bolt axis (eccentric tensile load ). 如果一个或多个紧固件上的外部载荷的合力未穿过紧固件组的质心（偏心剪切载荷）或与螺栓轴不重合（偏心拉伸载荷），则称该外部载荷为偏心。 |
| Decalescence | 退色 |
A phenomenon, associated with the transformation of alpha iron to gamma iron on the heating (superheating) of iron or steel, revealed by the darkening of the metal surface owing to the sudden decrease in temperature caused by the fast absorption of the latent heat of transformation. 一种现象，与铁或钢加热（过热）时α铁向γ铁的转变有关，由于转变潜热的快速吸收导致温度突然降低，金属表面变黑。 |
| Partial annealing | 不完全退火 |
An imprecise term used to denote a treatment given cold-worked material to reduce the strength to a controlled level or to effect stress relief. To be meaningful, the type of material, the degree of cold work, and the time-temperature schedule must be stated. 一个不精确的术语，用于表示冷加工材料的处理，以将强度降低到受控水平或消除应力。为了有意义，必须说明材料类型、冷加工程度和时间-温度计划。 |
| Wrap-around bend | 环绕弯曲 |
The bend obtained when a specimen is wrapped in a closed helix around a cylindrical mandrel. This term is sometimes applied to a semiguided bend of 180° or less. 当试样缠绕在圆柱形心轴周围的闭合螺旋中时获得的弯曲。该术语有时适用于180°或更小的半导弯曲。 |
| Preheating | 预热 |
Heating before some further thermal or mechanical treatment. For tool steel, heating to an intermediate temperature immediately before final austenitizing. For some nonferrous alloys, heating to a high temperature for a long time, to homogenize the structure before working. In welding and related processes, heating to an intermediate temperature for a short time immediately before welding, brazing, soldering, cutting, or thermal spraying. 在进一步热处理或机械处理之前加热。对于工具钢，在最终奥氏体化之前立即加热至中间温度。对于一些非铁合金，在工作前长时间加热到高温，以使结构均匀化。在焊接和相关工艺中，在焊接、钎焊、钎焊、切割或热喷涂之前，立即加热到中间温度。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Dimension line | 尺寸线 |
A line on an engineering drawing with a numeral above it that shows the length of a feature, usually in millimetres. 工程图上的一条线，上面有一个数字，表示特征的长度，通常以毫米为单位。 |
| Aging treatment | 时效处理 |
Heat treatment aimed at age hardening; it comprises solution and precipitation treatments. 针对时效硬化的热处理；它包括溶液和沉淀处理。 |
| Semiguided bend | 半导弯曲 |
The bend obtained by applying a force directly to the specimen in the portion that is to be bent. The specimen is either held at one end and forced around a pin or rounded edge, or is supported near the ends and bent by a force applied on the side of the specimen opposite the supports and midway between them. In some instances, the bend is started in this manner and finished in the manner of a free bend. 通过将力直接施加于待弯曲部分中的试样而获得的弯曲。将试样固定在一端，并围绕销或圆边施力，或者在靠近端部的位置支撑试样，并通过施加在试样与支撑件相对的一侧以及两者中间的力进行弯曲。在某些情况下，折弯以此方式开始，然后以自由折弯的方式结束。 |
| Vacuum servo | 真空服务器 |
A vacuum-operated servomotor which is used in a motor vehicle to provide a brake effort greater than the capability of the driver. 一种真空操作的伺服电机，用于机动车中，以提供大于驾驶员能力的制动力。 |
| Square | 正方 |
1. A regular quadrilateral, i.e. a polygon with four equal sides and four right angles. 2. An instrument to check angles of internal and external surfaces and flatness. 1.正四边形，即具有四条等边和四个直角的多边形。2.一种检查内外表面角度和平面度的仪器。 |
| Atomizing humidifier | 雾化加湿器 |
A humidifier that functions by spraying fine droplets of water into an airstream. 一种加湿器，通过将细小的水滴喷射到气流中来发挥作用。 |
| Secondary stresses (Unit Pa) | 二次应力（单位Pa） |
Stresses different from those induced by the major loading but nevertheless resulting from the major loads; for example, the hoop stresses that occur around the circumference of barrelled compression testpieces and forgings. 与主要荷载引起的应力不同，但主要荷载产生的应力；例如，桶装压缩试件和锻件周围产生的环向应力。 |
| Overaging | 过时效 |
Aging under conditions of time and temperature greater than those required to obtain maximum change in a certain property, so that the property is altered in the direction of the initial value. 在时间和温度条件下的时效大于获得某一特性最大变化所需的时间和温度，从而使该特性沿初始值的方向发生变化。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Circular pitch | 齿距 |
The distance from the center of one gear tooth to the center of the next gear tooth measured on the pitch line. 在节线上测量的从一个轮齿中心到下一个轮齿中心的距离。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Liquation temperature | 液化温度 |
The lowest temperature at which partial melting can occur in an alloy that exhibits the greatest possible degree of segregation. 偏析程度最高的合金发生部分熔融的最低温度。 |
| Shore hardness | 肖氏硬度 |
A measure of the hardness of materials such as elastomers, plastics, and rubbers determined using a Shore durometer which measures the penetration depth of a hardened steel rod (the indenter) 1.1–1.4 mm in diameter into the test material for a given force applied rapidly with a calibrated spring. There are two main indenter designs: type A (for softer materials) for which the end of the rod is a truncated 35° cone tapering to a diameter of 0.79 mm, and type D (harder materials) for which the end is a 30° cone with a 0.1 mm radius tip. The spring force is 8.05 N for type A and 44.45 N for type D. The hardness value is related to the penetration depth (limited to a maximum of 2.5 mm) such that for zero penetration the hardness is 100 and for maximum penetration the hardness is zero. The relevant standards are ISO 48-1, 48-4, and 48-7. Shore hardness values of selected materials are as follows: ABS 100, cellulose acetate 50–95, high-density polyethylene 60–70, low density polyethylene 40–50, polymethylmethacrylate 90–99, PTFE 50–65, and plasticized PVC 15–70. 使用肖氏硬度计测量弹性体、塑料和橡胶等材料的硬度，肖氏硬度仪测量直径为1.1–1.4mm的硬化钢棒（压头）在用校准弹簧快速施加的给定力下渗入试验材料的深度。有两种主要的压头设计：A型（适用于较软的材料），其杆端为截头35°锥形，逐渐变细至直径0.79 mm；D型（较硬的材料），端部为30°锥形，尖端半径为0.1mm。A型的弹簧力为8.05N，D型为44.45N。硬度值与渗透深度相关（最大限制为2.5mm），因此，对于零渗透，硬度为100，对于最大渗透，硬度是零。相关标准为ISO 48-1、48-4和48-7。所选材料的肖氏硬度值如下：ABS100、醋酸纤维素50-95、高密度聚乙烯60-70、低密度聚乙烯40-50、聚甲基丙烯酸甲酯90-99、PTFE50-65和塑化PVC15-70。 |