| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Zero time | 零时 |
The time when the given loading or constraint conditions are initially obtained in creep or stressrelaxation tests, respectively. 分别在蠕变或应力松弛试验中初始获得给定载荷或约束条件的时间。 |
| Diaphragm compressor | 隔膜式压缩机 |
A machine in which compression is achieved by the reciprocating motion of a flexible membrane of metal, plastic, or elastomeric material. This arrangement is ideally suited to pumping high-purity, toxic, or explosive gases. A similar machine incorporating check valves is a self-priming positive-displacement pump (diaphragm pump, membrane pump). 通过金属、塑料或弹性材料的柔性薄膜的往复运动实现压缩的机器。这种布置非常适合泵送高纯度、有毒或爆炸性气体。装有止回阀的类似机器是自吸容积泵（隔膜泵、隔膜泵）。 |
| Stabilizing treatment | 稳定化处理 |
(1) Before finishing to final dimensions, repeatedly heating a ferrous or nonferrous part to or slightly above its normal operating temperature and then cooling to room temperature to ensure dimensional stability in service. (2) Transforming retained austenite in quenched hardenable steels, usually by cold treatment. (3) Heating a solution-treated stabilized grade of austenitic stainless steel to 870 to 900 °C (1600 to 1650 °F) to precipitate all carbon as TiC, NbC, or TaC so that sensitization is avoided on subsequent exposure to elevated temperature. （1）在精加工至最终尺寸之前，反复加热含铁或非铁零件至或略高于其正常工作温度，然后冷却至室温，以确保使用中的尺寸稳定性。（2）在淬火可淬硬钢中转变残余奥氏体，通常通过冷处理。（3）将固溶处理的稳定等级奥氏体不锈钢加热至870至900°C（1600至1650°F），使所有碳沉淀为TiC、NbC或TaC，从而避免在随后暴露于高温时敏化。 |
| Absorptance | 吸收率 |
(absorptivity, absorption coefficient, α) The fraction of radiant flux incident on a surface that is absorbed by the surface. The term also applies to absorption of radiation by a volume of fluid. For a semi-transparent surface, α + ρ + τ = 1, where ρ is the reflectance and τ is the transmittance. （吸收率，吸收系数，α）入射到表面的辐射通量被表面吸收的部分。该术语也适用于一定体积的流体对辐射的吸收。对于半透明表面，α+ρ+τ=1，其中ρ是反射率，τ是透射率。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| Deviation | 偏差 |
The difference between the actual value and the desired value of a controlled variable. 受控变量的实际值与期望值之间的差值。 |
| Dead centre | 止点 |
The point at which, in a crank mechanism, the piston connecting rod and crank are all in line so that there can be no driving moment. 在曲柄机构中，活塞连杆和曲柄都在一条线上，因此不会有驱动力矩。 |
| Stretch-bending test | 拉伸弯曲试验 |
A simulative test for sheet metal formability in which a strip of sheet metal is clamped at its ends in lock beads and deformed in the center by a punch. Test conditions are chosen so that fracture occurs in the region of punch contact. 金属板成形性的模拟试验，其中金属板条在其端部夹紧在锁珠中，并通过冲头在中心变形。选择试验条件，以便在冲头接触区域发生断裂。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Turboblower | 涡轮鼓风机 |
A centrifugal or axial compressor or fan. 离心式或轴流式压缩机或风扇。 |
| Bearing strain | 轴承应变 |
The ratio of the deformation of the bearing hole, in the direction of the applied force, to the pin diameter in a bearing test. 轴承孔在作用力方向上的变形与轴承测试中销直径的比值。 |
| Grub screw | 平头螺丝 |
A short headless screw with a recess at one end to receive a screw driver or key. 一种短的无头螺钉，一端有一个凹槽，用于安装螺丝刀或钥匙。 |
| Forced-air quench | 强制空气淬火 |
A quench utilizing blasts of compressed air against relatively small parts such as a gear. 利用压缩空气冲击相对较小的零件（例如齿轮）进行的淬火。 |
| Drift pin | 冲头 |
A round tapered steel pin used to align rivet holes so that the rivet will pass through the holes easily. 用于对齐铆钉孔的圆形锥形钢销，以便铆钉轻松穿过孔。 |
| Helical spring | 螺旋弹簧 |
A spring manufactured by forming elastic wire into a helix which may be cylindrical, conical, barrel-shaped, or hourglass in overall form. Closed-coiled springs are used in tension; open-coiled in both tension and compression. 一种弹簧，通过将弹性线材制成螺旋形而制成，螺旋形的整体形状可以是圆柱形、圆锥形、桶形或沙漏形。拉力采用闭合盘簧；在拉伸和压缩中都开卷。 |
| Austenite | 奥氏体 |
A solid solution of one or more elements in face-centered cubic iron. Unless otherwise designated (such as nickel austenite), the solute is generally assumed to be carbon. Solid solution of alloying elements and/or carbon in γ-Fe. It is named after British metallurgist W. C. Roberts-Austen. 一种或多种元素在面心立方铁中的固溶体。除非另有说明（如镍奥氏体），溶质通常假定为碳。合金元素和/或碳在γ-Fe中的固溶体。它以英国冶金学家WCRoberts-Austen的名字命名。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Vapour | 蒸气 |
The gas-like phase of a substance at a temperature below its critical point. A vapour can be condensed to a liquid or a solid by increasing its pressure or reducing its temperature. 温度低于临界点的物质的类气相。蒸汽可以通过增加压力或降低温度冷凝成液体或固体。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Physical crack size (ap) | 物理裂纹尺寸（ap） |
The distance from a reference plane to the observed crack front. This distance may represent an average of several measurements along the crack front. The reference plane depends on the specimen form, and it is normally taken to be either the boundary or a plane containing either the load line or the centerline of a specimen or plate. 从基准面到观察到的裂纹前沿的距离。该距离可以表示沿裂纹前沿的若干测量的平均值。基准面取决于试样形状，通常视为边界或包含试样或板的载重线或中心线的平面。 |
| Lockbolt | 锁紧螺栓 |
A fastener which bears a superficial resemblance to a bolt, but which engages a collar (instead of a nut) with annular grooves (instead of threads). The collar is swaged over the grooves on the male fastener to develop preload. 表面上类似于螺栓的紧固件，但与环槽（而不是螺纹）接合的轴环（而不是螺母）。套环在阳紧固件上的凹槽上锻造，以产生预紧力。 |
| Profilometer | 轮廓仪 |
An instrument used to quantify the roughness of a surface. For a contact profilometer, a diamond stylus sweeps across the surface along a series of parallel lines. Noncontact profilometers use optical techniques to map the surface irregularities. 用于量化表面粗糙度的仪器。对于接触式轮廓仪，钻石触针沿一系列平行线扫过表面。非接触式轮廓仪使用光学技术绘制表面不规则。 |
| Anneal to temper | 退火回火 |
A final partial anneal that softens a cold worked nonferrous alloy to a specified level of hardness or tensile strength. 将冷加工的有色金属合金软化到规定的硬度或抗拉强度水平的最终局部退火。 |
| Combustible | 易燃 |
(inflammable) A term for substances that can be ignited and burned. （易燃）可点燃和燃烧的物质的术语。 |
| British thermal unit (BTU, Btu) | 英热单位（BTU，Btu） |
An obsolete (non-SI) imperial unit of energy defined as the energy required to raise the temperature of one pound of pure water at 68°F by 1°F. The conversion to SI is 1 Btu = 1.055 056 × 103 J. 一种已被淘汰的（非SI）英制能量单位，定义为将68°F的一磅纯水的温度升高1°F所需的能量。转换为SI为1Btu=1.055056×103J。 |
| Tensile stress (Unit Pa) | 拉应力（单位Pa） |
A stress that causes two parts of an elastic body, on either side of a typical stress plane, to pull apart. A stress that tends to stretch a component, or local region of a component, when under load. In simple tension it results from the applied axial load, but tensile stresses occur in bending, torsion and other forms of loading. 一种应力，使弹性体的两个部分在典型应力平面的任一侧分离。在负载下，倾向于拉伸部件或部件局部区域的应力。在简单拉伸中，它由施加的轴向载荷产生，但拉伸应力发生在弯曲、扭转和其他形式的载荷中。 |
| Austenite finish temperature (Af) | 奥氏体完成温度（Af） |
Temperature at which the transformation of martensite into austenite completes upon heating. The same designation is also applied to nonferrous alloys in which martensite transforms into some parent phase. 加热时马氏体转变为奥氏体的温度。相同的名称也适用于马氏体转变为某些母相的有色合金。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Impact | 撞击 |
Sudden loading of a body or component, as in a vehicle collision or striking by a hammer. 物体或部件的突然加载，如车辆碰撞或锤击。 |
| Yield strength | 屈服强度 |
That stress level which will create a permanent deformation of 0.2% or 0.5% or some other small, preselected, amount in a body. Approximately equal to the elastic and proportional limits of the material; a little higher than the proof strength of a bolt. The stress at which a material exhibits a specified deviation from proportionality of stress and strain. An offset of 0.2% is used for many metals. 该应力水平将在物体中产生0.2%或0.5%的永久变形，或其他一些小的、预先选定的量。近似等于材料的弹性和比例极限；略高于螺栓的强度。材料表现出与应力和应变比例的特定偏差的应力。许多金属使用0.2%的偏移量。 |
| Extensometer | 引伸计 |
An instrument for measuring changes in length over a given gage length caused by application or removal of a force. Commonly used in tension testing of metal specimens. Any instrument which measures the change in length of a part as the part is loaded. 一种用于测量在给定标距上由施加或移除力引起的长度变化，在零件加载时测量零件长度变化的仪器。常用于金属试样的拉力试验。 |
| Torricellean barometer | 托里塞莱气压计 |
A vertical glass tube with its upper end sealed and the lower end submerged in a pool of mercury. The space above the mercury is under vacuum. The height to which the mercury rises up the tube is a measure of the barometric pressure. 一种垂直的玻璃管，上端密封，下端浸入汞池中。水银上方的空间处于真空状态。水银在管道中上升的高度是大气压力的量度。 |
| Double-shear test | 双剪试验 |
A shear test having two stationary, shear blades and one moving one and that uses solid round bars as test specimens. 一种剪切试验，具有两个固定的剪切刀片和一个移动的刀片，并使用实心圆棒作为试样。 |
| Specific heat capacity | 比热容 |
The heat necessary to raise the temperature of 1 kg of a substance by 1 K. It is measured in J/(kg K). 将1千克物质的温度升高1K所需的热量。单位为J/（kg K）。 |
| Flange bolt | 法兰螺栓 |
A bolt with a built in washer-like flange just below the head. 在头部下方带有内置垫圈状法兰的螺栓。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Minute (min) | 分钟（min） |
A non-SI unit of time. The conversion to SI is 1 min = 60 s. 非SI时间单位。转换为1分钟=60秒。 |
| Waste heat | 废热 |
1. Heat generated by internal-combustion engines, gas turbines, electrical generators, electrical equipment, and industrial processes that is not used directly but is expelled to the environment, often in hot flue or exhaust gases. 2. Heat generated from waste 1.内燃机、燃气轮机、发电机、电气设备和工业过程产生的热量，这些热量不是直接使用的，而是通过热烟气或废气排放到环境中。2.废物产生的热量 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Machine tool | 机床工具 |
A powered machine, such as a borer, grinder, lathe, milling machine or planer, used for cutting and shaping metal, plastics, composites, etc. (machining). A machining centre is a CNC machine tool working about several axes, having a stock of tools and automatic tool changing ability, which is capable of diverse machining operations under automated control. 一种动力机器，如钻孔机、磨床、车床、铣床或刨床，用于切割和成形金属、塑料、复合材料等（机加工）。加工中心是围绕多个轴工作的CNC机床，具有刀具库存和自动换刀能力，能够在自动化控制下进行各种加工操作。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| Steady pin | 定位销 |
A dowel, key, or pin that prevents a pulley from turning on its shaft. 防止滑轮在其轴上转动的销钉、键或销。 |
| Load range, P | 负载范围P |
In fatigue, the algebraic difference between the maximum and minimum loads in a fatigue cycle. 在疲劳中，疲劳循环中最大和最小载荷之间的代数差。 |
| Shoulder | 轴肩 |
The portion of a shaft, stepped component, or flanged component, where a change in diameter or other dimension occurs. Even for a nominal step change, in practice there will be a radius where shoulder and shaft meet in order to avoid too severe a stress concentration. 轴、阶梯部件或法兰部件的直径或其他尺寸发生变化的部分。即使是名义阶跃变化，在实践中，肩部和轴相交处也会有一个半径，以避免出现过严重的应力集中。 |
| Oil-cooled | 油冷却 |
A term for a machine that uses circulating oil to remove heat. 使用循环油散热的机器的术语。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Depth gauge | 深度计 |
1. A precision instrument, typically consisting of a machine-divided steel rule passing through a hardened-steel cross head, used to measure the depths of slots, holes, shoulders, projections, etc. 2. A device used by divers to indicate the water depth. 1. 一种精密仪器，通常由穿过硬化钢十字头的机器分割钢尺组成，用于测量槽、孔、肩部、突起等的深度。 2. 潜水员用来指示深度的装置水深。 |
| Annealing carbon | 退火碳 |
Fine, apparently amorphous carbon particles formed in white cast iron and certain steels during prolonged annealing. Also called temper carbon. 白口铸铁和某些钢在长时间退火过程中形成的细小、明显的无定形碳颗粒。也称为回火碳。 |
| Thread form | 螺纹形式 |
The cross-sectional shape of the threads, defining thread angle, root, and crest profiles, etc. Thread length Length of that portion of the fastener which contains threads cut or rolled to full depth. 螺纹的横截面形状，定义螺纹角度、齿根和齿冠轮廓等。螺纹长度：紧固件中包含全深度切割或轧制螺纹的部分的长度。 |
| Vibration | 振动 |
1. A periodic change with time of the displacements of elements making up a component or structure. 2. The study of the oscillatory motion of bodies and systems and the frequencies, amplitudes, and forces associated with them. 1.组成部件或结构的元件位移随时间的周期性变化。2.研究物体和系统的振荡运动以及与之相关的频率、振幅和力的学科。 |
| Residual strength (Unit N) | 剩余强度（单位：N） |
The strength of a damaged body containing defects induced by microcracking, thermal shock, etc. 包含由微裂纹、热冲击等引起的缺陷的受损体的强度。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Grinding stress (Unit Pa) | 磨削应力（单位Pa） |
The residual stresses left in the surface of a component after grinding, owing to non-uniform cooling from the high surface temperatures produced. 由于产生的高表面温度造成的不均匀冷却，磨削后留在部件表面的残余应力。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Nanomanufacturing | 纳米制造 |
1. The manufacture of nanoscale materials. 2. The manufacture of components or devices that have critical dimensions of order 1 nm. 1.纳米材料的制造。2.具有1nm级临界尺寸的部件或装置的制造。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Degrees of freedom | 自由度 |
The number of independent variables (such as temperature, pressure, or concentration within the phases present) that may be altered at will without causing a phase change in an alloy system at equilibrium; or the number of such variables that must be fixed arbitrarily to define the system completely. 可以随意改变而不引起平衡时合金系统相变的自变量的数量（例如存在的相内的温度、压力或浓度）；或必须任意固定以完全定义系统的此类变量的数量。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Stove bolt | 炉用螺栓 |
This bolt has been so named because of its use in stove building. It is made in a number of different forms, either with a round button, or flat countersunk head, the head having a slot for a screwdriver and the threaded end being provided with a square or hexagon nut. 这种螺栓因其在炉灶建筑中的用途而得名。它有多种不同的形式，有圆形按钮或平沉头，头部有螺丝刀槽，螺纹端有方形或六角螺母。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Cavitation tunnel | 空泡试验筒 |
A closed-circuit recirculating water tunnel in which the static pressure can be reduced to sufficiently low levels for cavitation studies to be performed. 一种闭路循环水隧洞，其中静压可降至足够低的水平，以便进行气蚀研究。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Compound pendulum | 复摆 |
A rigid body free to swing about an axis. 可绕轴自由摆动的刚体。 |
| Salt bath heat treatment | 盐浴热处理 |
Heat treatment carried out in a bath of molten salt. 在熔融盐浴中进行的热处理。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Coaxial | 同轴 |
A term for components having a common axis such as concentric shafts. 具有共同轴线的部件的术语，例如同心轴。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Finishing washer | 光制垫圈 |
A washer designed for use with countersunk screws. Used to enhance appearance in some applications. 设计用于沉头螺钉的垫圈。在某些应用中用于增强外观。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| Fibreglass | 玻璃纤维 |
Fibreglass is used in studs and nuts for applications when the fastener should be non-corrosive, low in conductivity, or transparent to electromagnetic waves. 当紧固件应无腐蚀性、低导电性或对电磁波透明时，玻璃纤维用于螺柱和螺母中。 |
| Compression wave | 压缩波 |
(dilatation wave) In a fluid or a solid, a progressive wave or wavefront that compresses the medium through which it propagates. （膨胀波）在流体或固体中，压缩介质传播的行波或波前。 |
| Bypass flow meter | 旁通流量计 |
(shunt flow meter) A flow meter installed in a pipework bypass which may itself be part of the flow meter. An orifice plate is used to ensure a fraction of the main flow passes through the bypass. （分流流量计）安装在管道旁路中的流量计，它本身可能是流量计的一部分。孔板用于确保一部分主流通过旁路。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Austenite stabilization | 奥氏体稳定化 |
Decrease, in comparison to a continuous cooling, in the amount of martensite occurring from austenite when cooling is interrupted at a temperature between Ms and Mf. This can be explained by the relaxation of stresses induced in the austenite by martensite crystals occurring before the interruption. The relaxation, in turn, leads to the dislocation rearrangement and their interaction with martensite/austenite interfaces, which makes the interfaces immobile. 与连续冷却相比，当在Ms和Mf之间的温度中断冷却时，从奥氏体中产生的马氏体的量减少。这可以通过中断前发生的马氏体晶体在奥氏体中引起的应力松弛来解释。反过来，松弛导致位错重排及其与马氏体/奥氏体界面的相互作用，这使得界面无法移动。 |
| Base metal hardness | 母材硬度 |
Hardness closest to the surface (when traversing from core to outside diameter) just before an increase or decrease occurs, denoting, respectively, carburization or decarburization. 在发生增加或减少之前最接近表面的硬度（从芯部到外径时），分别表示渗碳或脱碳。 |
| Maximum-and-minimum thermometer | 最高和最低温度计 |
(minimum-maximum thermometer, Six’s thermometer) A liquid-in-glass instrument designed to register the maximum and minimum temperatures experienced over a given time period. （最低-最高温度计，Six's温度计）一种液体玻璃仪器，用于记录给定时间段内经历的最高和最低温度。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Abrasivity | 磨蚀性 |
The extent to which a surface, particle, or collection of particles will tend to cause abrasive wear when forced against a solid surface under relative motion and under prescribed conditions. 在相对运动和规定条件下，一个表面、颗粒或颗粒集合在被迫抵靠固体表面时趋向于引起磨粒磨损的程度。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Critical diameter | 临界直径 |
(D) Diameter of the bar that can be fully hardened with 50% martensite at its center. （D）中心有50%马氏体可完全硬化的棒材直径。 |
| Mechanical units | 机械单位 |
The units of physical quantities, the dimensions of which includemass, length, and time. 物理量的单位，其量纲包括质量、长度和时间。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Pulse | 脉冲 |
An increase or decrease in the magnitude of a physical quantity, such as pressure, voltage, or force, with a time scale short compared with other time scales in a process, after which there is a return to the original level. 物理量的大小的增加或减少，如压力、电压或力，与过程中的其他时间尺度相比，时间尺度较短，之后返回到原始水平。 |
| Bolt gage | 螺栓量规 |
An ultrasonic instrument used to measure the stress or strain in bolts. 用于测量螺栓应力或应变的超声波仪器。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| Heat treatment | 热处理 |
(heat treating) Alteration of the mechanical properties of materials, particularly metals, by different sequences of heating, holding at temperature, and cooling at different rates. Heating and cooling a solid metal or alloy in such a way as to obtain desired conditions or properties. Heating for the sole purpose of hot working is excluded from the meaning of this definition. （热处理）材料，特别是金属的机械性能的改变，通过不同的加热顺序、温度保持和不同速率的冷却。加热和冷却固体金属或合金，以获得所需的条件或性能。仅用于热加工的加热不属于本定义的含义。 |
| Work ratio | 工作比 |
The ratio of the net work out to the actual work out for a thermodynamic cycle. 热力学循环的净功与实际功之比。 |
| Austenitic grain size | 奥氏体晶粒尺寸 |
The size attained by the grains of steel when heated to the austenitic region; may be revealed by appropriate etching of cross sections after cooling to room temperature. 当加热到奥氏体区域时钢晶粒达到的尺寸；冷却至室温后，可通过适当蚀刻横截面来显示。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Combined stresses | 复合应力 |
The stress state at a point in a component subjected to combination of axial, bending, torsional loadings etc., acting along all reference axes. 沿所有参考轴作用的受轴向、弯曲、扭转载荷等组合作用的部件中某点的应力状态。 |
| Ductile | 延展性材料 |
(ductile material) Describes a material that can be deformed permanently to large strains without fracture. If a bolt can be stretched well past its yield point before breaking, it is said to be ductile. （延展性材料）描述一种可以永久变形到大应变而不断裂的材料。如果螺栓在断裂前可以很好地拉伸超过其屈服点，则称其具有延展性。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Macrodeviation | 宏观偏差 |
Errors from–irregular surface departures from the design profile, often caused by lack of accuracy or stiffness of the machine system. 不规则表面偏离设计轮廓的误差，通常是由于机器系统缺乏准确性或刚度造成的。 |
| Stress cracking | 应力开裂 |
A family of failure modes, each of which involves high stress and chemical action. The family includes Hydrogen embrittlement, Stress corrosion cracking, stress embrittlement, and hydrogen-assisted stress corrosion. 一系列失效模式，每种模式都涉及高应力和化学作用。该系列包括氢脆、应力腐蚀开裂、应力脆化和氢辅助应力腐蚀。 |
| Screw area (Unit m²) | 螺丝面积（单位m²） |
The area of a circle described by the tips of a propeller. 螺旋桨尖端所描述的圆的面积。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Barometer | 气压计 |
An instrument used to measure atmospheric pressure. An instrument for measuring atmospheric pressure. There are two main types – the mercury barometer, and the aneroid barometer. 用于测量大气压力的仪器。有两种主要类型——水银气压计和无液气压计。 |
| Density | 密度 |
The mass per unit volume of a solid material. (mass density, ρ) (Unit kg/m³) The mass per unit volume of a substance that satisfies the continuum assumption. The reciprocal of specific volume. 固体材料每单位体积的质量。（质量密度，ρ）（单位kg/m³）满足连续统假设的物质每单位体积的质量。和比容相关联。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Fracture mechanisms | 断裂机制 |
The microstructural mechanisms that cause fracture, such as void initiation, growth and coalescence, cleavage. 导致断裂的微观结构机制，如空隙的萌生、生长和聚结、解理。 |
| Screw feeder | 螺旋给料机 |
A mechanism for handling bulk materials in which a rotating helicoidal screw moves the material axially forward. Similar to a screw conveyor, but required to discharge material at a controlled rate very accurately. It operates with the screw completely full. 一种用于处理散装物料的机构，其中旋转的螺旋螺杆使物料轴向向前移动。类似于螺旋输送机，但需要以受控速率非常精确地排出物料。它在螺杆完全充满的情况下运行。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Latent heat | 潜热 |
Thermal energy absorbed or released when a substance undergoes a phase change. 物质发生相变时吸收或释放的热能。 |
| Pascal’s law | 帕斯卡定律 |
When there is a change in pressure at any point in a confined fluid at rest, there is an equal change at every other point in the fluid volume. 当处于静止状态的受限流体中任何一点的压力发生变化时，流体体积中的每一点的变化都相等。 |
| Heat-capacity ratio (c*) | 热容量比（c*） |
A non-dimensional parameter that arises in the analysis of heat exchangers, defined as the ratio cMIN/cMAX where cMIN is the heat-capacity rate c for the fluid with the smaller value of c and cMAX the value for the fluid with the larger value of c. Different flow rates and specific-heat values give rise to different values for c. 热交换器分析中出现的无量纲参数，定义为比率cMIN/cMAX其中cMIN是流体的热容率c，c值较小，cMAX是流体的值具有较大的c值。不同的流速和比热值产生不同的c值。 |
| Compression pressure (Unit Pa) | 压缩压力（单位Pa） |
The pressure produced in a cylinder of a piston engine by compression of air in the absence of fuel. 在没有燃料的情况下通过压缩空气在活塞发动机的气缸中产生的压力。 |
| Acceleration-error constant | 加速度误差常数 |
When the reference (demand) input to a control system is parabolic, the output signal will also be parabolic in steady state. The signal that is constant in this situation is the acceleration and thus for a parabolic input the steady-state error, referred to as the acceleration-error constant, is the error in the acceleration. 当控制系统的参考（需求）输入是抛物线时，输出信号在稳定状态下也将是抛物线。在这种情况下恒定的信号是加速度，因此对于抛物线输入，称为加速度误差常数的稳态误差是加速度中的误差。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Pressure regulator | 压力调节器 |
(pressure-regulating valve) A device installed in a pneumatic or gas system to maintain the downstream pressure at the required level. （压力调节阀）安装在气动或气体系统中以将下游压力保持在所需水平的装置。 |
| Wrist pin | 腕销 |
A stud projecting from a crank as an attachment for a connecting rod. wrought alloys Metal alloys that are initially cast and then shaped into final form by processes such as extrusion, forging, or rolling. 从曲柄上伸出的一个螺柱，作为连接杆的附件。锻造合金最初铸造，然后通过挤压、锻造或轧制等工艺成形为最终形状的金属合金。 |
| Extra spring | 额外弹簧 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state above full hard beyond which further cold work will not measurably increase the strength and hardness. 有色金属合金和一些铁合金的回火状态，大约对应于高于全硬的冷加工状态，超过该状态进一步冷加工将不会显着增加强度和硬度。 |
| Checks | 检查 |
Numerous, very fine cracks in a coating or at the surface of a metal part. Checks may appear during processing or during service and are most often associated with thermal treatment or thermal cycling. 涂层中或金属零件表面的许多非常细微的裂纹。在加工或服务期间可能会出现检查，并且通常与热处理或热循环有关。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Turbulent flow (turbulence) | 湍流 |
Fluid motion characterized by disorderly, rotational (i.e. vortical) three-dimensional velocity fluctuations covering a wide range of frequency and length scales. The pressure, temperature, and other fluid properties also fluctuate and the diffusion of heat, mass, and momentum is greatly enhanced. As are laminar and transitional flow, turbulent flow of a Newtonian fluid is governed by the Navier–Stokes equations which can in principle be solved by direct numerical simulation (DNS) in which all time and length scales of the fluctuating motion are resolved. 流体运动的特点是无序、旋转（即旋涡）三维速度波动，覆盖广泛的频率和长度尺度。压力、温度和其他流体特性也会波动，热、质量和动量的扩散会大大增强。与层流和过渡流一样，牛顿流体的湍流由Navier-Stokes方程控制，该方程原则上可以通过直接数值模拟（DNS）求解，在直接数值模拟中，波动运动的所有时间和长度尺度都可以求解。 |
| Toggle (toggle clamp) | 拨动（拨动夹） |
A device consisting of two pinned levers that are almost in line between two end points in the same plane. Bringing the levers into line generates large forces between the ends. Used to obtain a large mechanical advantage or as a locking mechanism. 由两个销杆组成的装置，在同一平面的两个端点之间几乎成一条直线。将杠杆对齐会在端部之间产生较大的力。用于获得较大的机械优势或用作锁定机构。 |
| Reproducibility | 再现性 |
A term used to describe test-result variability associated with specifically defined components of variance obtained both from within a single laboratory and between laboratories. 一个术语，用于描述与从单个实验室内和实验室之间获得的具体定义的方差分量相关的测试结果可变性。 |
| Centripetal | 向心力 |
Acting or moving in a direction towards the axis of rotation. 在朝向旋转轴的方向上起作用或移动。 |
| Morse taper | 莫氏锥度 |
A self holding, standard taper largely used on drilling tools, drilling machine spindles, and some lathes. 一种自持式标准锥度，主要用于钻孔工具、钻床主轴和一些车床。 |
| B-basis | B-基础 |
Mechanical property value above which at least 90% of the population of values is expected to fall, with a confidence of 95%. 机械性能值超过该值时，至少90%的值预计会下降，置信度为95%。 |
| Water quenching | 水淬 |
A quench in which water is the quenching medium. The major disadvantage of water quenching is its poor efficiency at the beginning or hot stage of the quenching process. 以水为淬火介质的淬火。水淬的主要缺点是在淬火过程的开始或热阶段效率低。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Acoustic droplet ejection | 声液滴喷射 |
The ejection of small droplets from the surface of a liquid that results from focusing high-intensity ultrasound near the surface. 由于在表面附近聚焦高强度超声波而从液体表面喷射出小液滴。 |
| Mole (mol) | 摩尔（mol） |
The base unit of the amount of substance in the SI system. It was previously defined as the amount of substance of a system that contains as many elementary entities as there are atoms in 0.012 kg of carbon-12. From 20 May 2019 it has been defined as the amount of substance containing exactly 6.022 140 76 × 1023 elementary entities. SI国际单位制中物质量的基本单位。此前，它被定义为一个系统中的物质量，该系统包含的基本实体数量与0.012千克碳-12中的原子数量相同。从2019年5月20日起，它已被定义为包含6.02214076×1023个基本实体的物质量。 |
| Screw jack | 螺旋千斤顶 |
A lifting device (jack) consisting of a nut and square-threaded shaft at the top of which is a load-bearing pad. Rotation of the nut raises or lowers the pad. 一种起重装置（千斤顶），由螺母和方形螺纹轴组成，其顶部为承重垫。螺母的旋转可升高或降低衬垫。 |
| Transmission dynamometer | 传动测功机 |
A dynamometer in which the power transmitted by a shaft is obtained from the product of its rotation speed and the torque determined from measured shear strains along the shaft. 一种测功机，其中轴传递的功率由其转速和扭矩的乘积获得，扭矩由沿轴测得的剪切应变确定。 |
| Secondary stresses (Unit Pa) | 二次应力（单位Pa） |
Stresses different from those induced by the major loading but nevertheless resulting from the major loads; for example, the hoop stresses that occur around the circumference of barrelled compression testpieces and forgings. 与主要荷载引起的应力不同，但主要荷载产生的应力；例如，桶装压缩试件和锻件周围产生的环向应力。 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Transfer machines | 转印机 |
These specialized machine tools are used to perform various machining operations on parts or parts in fixtures as the parts are moved along on an automatic conveyor which is part of the machine tool set-up. In a set-up, the parts can move in a straight line from their entry point to their exit point, or the setup may be constructed in a U-shape so that the parts are expelled near where they start. 当零件在自动输送机上移动时，这些专用机床用于对零件或夹具中的零件执行各种加工操作，自动输送机是机床设置的一部分。在设置中，零件可以从其入口点直线移动到其出口点，或者设置可以构造为U形，以便零件在其起点附近排出。 |
| Radial load (Unit N) | 径向负荷（单位：N） |
1. Centrifugal loading induced in a rotating body. 2. (through-wallthickness load) The radial component of loading arising from internal or external pressurization of a closed vessel. There will also be axial and hoop loading. 1.旋转体中产生的离心载荷。2.（贯穿壁厚载荷）由封闭容器的内部或外部加压产生的载荷的径向分量。还存在轴向和环向载荷。 |
| Angle of friction | 摩擦角 |
(friction angle, β) (Unit °) For a body in contact with a plane surface, the angle between the normal to the surface and the resultant force between the body and the surface. If the friction force is F and normal force is N, β is given by F/N = μ = tan β where μ is the coefficient of friction. （摩擦角，β）（单位°）对于与平面接触的物体，表面法线与物体与表面之间的合力之间的夹角。如果摩擦力为F，法向力为N，则β由F/N=μ=tanβ给出，其中μ是摩擦系数。 |
| Zone melting (zone refining) | 区域熔炼（区域精炼） |
A process of purification of materials in which a narrow molten zone is moved along the length of the material, resulting in impurities being segregated at one end. 一种净化材料的过程，其中一个狭窄的熔融区沿材料长度移动，导致杂质在一端分离。 |
| Nut thickness | 螺母厚度 |
The nut thickness shall be the overall distance measured parallel to the axis of nut, from the top of the nut to the bearing surface, and shall include the thickness of the washer face where provided. 螺母厚度应为平行于螺母轴线测量的从螺母顶部到轴承表面的总距离，还应包括垫圈表面的厚度。 |
| Pin expansion test | 插头膨胀试验 |
A test for determining the ability of a tube to be expanded or for revealing the presence of cracks or other longitudinal weaknesses in it, made by forcing a tapered pin into the open end of the tube, similar to flare test. 通过将锥形销压入管道开口端来确定管道膨胀能力或揭示其存在裂纹或其他纵向缺陷的试验，类似于扩口试验。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Shoulder bolt | 轴肩螺栓 |
A bolt for which the unthreaded cylindrical section between the thread and the head is of larger diameter than the threaded section, precisely machined to length and diameter and hardened 一种螺栓，其螺纹和头部之间的无螺纹圆柱段的直径大于螺纹段的直径，精确加工至长度和直径并硬化 |
| Adhesive strength | 粘合强度 |
The strength of an adhesively bonded joint, usually measured in tension (perpendicular to the plane of the bonded joint) or in shear 粘合接头的强度，通常以拉伸（垂直于粘合接头的平面）或剪切测量 |
| Turbine pump (turbopump) | 涡轮泵 |
An axial or centrifugal pump driven by a turbine. Typically used to supply fuel to the combustion chamber of a rocket engine such as on the space shuttle. 由涡轮驱动的轴向或离心泵。通常用于向火箭发动机（如航天飞机）的燃烧室供应燃料。 |
| Milling | 铣削 |
A machining process, typically for metals and plastics, in which a multi-tooth rotary cutter removes material to produce flat or profiled surfaces, slots, grooves, etc. Milling is a machining process in which metal is removed by a rotating multiple-tooth cutter; each tooth removes a small amount of metal with each revolution of the spindle. Because both workpiece and cutter can be moved in more than one direction at the same time, surfaces having almost any orientation can be machined. 一种加工工艺，通常用于金属和塑料，其中多齿旋转刀具去除材料以产生平坦或异形表面、槽、槽等。金属由旋转多齿刀具去除；主轴每转一圈，每个齿都会去除少量金属。因为工件和刀具可以同时在多个方向上移动，所以几乎可以加工任何方向的表面。 |
| Permanent set | 永久变形 |
The deformation or strain remaining in a previously stressed body after release of load. 释放荷载后，先前受力物体中剩余的变形或应变。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Oxygen probe | 定氧测头 |
An atmosphere-monitoring device that electronically measures the difference between the partial pressure of oxygen in a furnace or furnace supply atmosphere and the external air. 一种大气监测装置，以电子方式测量熔炉或熔炉供应大气中的氧分压与外部空气之间的差值。 |
| Ideal critical diameter | 理想临界直径 |
(DI). Under an ideal quench condition, the bar diameter that has 50% martensite at the center of the bar when the surface is cooled at an infinitely rapid rate (that is, when H = ∞, where H is the quench severity factor). （DI）在理想淬火条件下，当表面以无限快的速度冷却时（即H=∞, 其中H是淬火严重度因子）。 |
| Hot dipping | 热浸 |
(hot-dip galvanizing) A process of coating an iron, steel, or aluminium object with a thin layer of zinc by passing it through a bath of molten zinc at a temperature of about 460°C. （热浸镀锌）通过使铁、钢或铝物体通过温度约为460°C的熔融锌浴，在铁、钢或铝物体上镀上一层薄薄的锌层的工艺。 |
| Stress | 应力（单位Pa） |
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression)or shear. 1. Stress ‘at a point’ (i.e. over a volume of material that is very small compared with that of the component or structure) is the load per unit area for every face of an infinitesimal cube surrounding the point. 2. In fluid flow the stress tensor σij is the sum of an isotropic part −pδij, δij being the Kronecker delta, having the same form as the stress tensor for a fluid at rest, p being the static pressure, and the non-isotropic, deviatoric stress tensor dij which is due entirely to the fluid motion. 内部分布力或力分量的强度，这些力或力的分量抵抗正在或已经受到外力的材料的体积或形状的变化。应力以单位面积的力表示，并根据试样横截面的原始尺寸计算。应力可以是直接（拉伸或压缩）或剪切。1.“在一点”的应力（即在与组件或结构相比非常小的材料体积上）是围绕该点的无限小立方体的每个面的单位面积载荷。2. 在流体流动中，应力张量σij是各向同性部分-pδij的总和，δij是Kroneckerδ，具有与静止流体的应力张量相同的形式，p是静压，非各向同性, 偏应力张量 dij 完全由流体运动引起。 |
| Amontons friction | 阿蒙顿摩擦 |
(Coulomb friction) Friction between surfaces where the ratio of the frictional force F to the normal force N is constant and independent of the area in contact. （库仑摩擦）摩擦力F与法向力N之比恒定且与接触面积无关的表面之间的摩擦。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Electrode | 电极 |
The two metallic bodies in a battery or Corrosion cell which give up electrons (the Anode) or which attract them (the Cathode). 电池或腐蚀电池中释放电子（阳极）或吸引电子（阴极）的两个金属体。 |
| Creep | 蠕变 |
The slow, plastic deformation of a body under heavy loads. Time-dependent plasticity. Time-dependent and permanent deformation of material under constant load or stress. The strain increases with time at a rate that increases with increasing temperature. Creep can lead to large strain and eventual failure, and so limit the lifetime of components subjected to load at high temperature. Creep in metals becomes significant at homologous temperatures in excess of about 0.4, e.g. 1200°C for tungsten, 504°C for titanium, 450°C for iron, and 100°C for aluminium. 物体在重载荷下缓慢的塑性变形，随时间变化的可塑性，材料在恒定载荷或应力下随时间变化的永久变形。应变随时间以随温度升高而增加的速率增加。蠕变可能导致大应变和最终失效，从而限制部件在高温下承受载荷的寿命。当同源温度超过约0.4℃时，金属蠕变变得显著，例如钨为1200℃，钛为504℃，铁为450℃，铝为100℃。 |
| Ductile cast iron | 球墨铸铁 |
A cast iron that has been treated while molten with an element such as magnesium or cerium to induce the formation of free graphite as nodules or spherulites, which imparts a measurable degree of ductility to the cast metal. Also known as nodular cast iron, spherulitic graphite cast iron and SG iron. 一种铸铁，在熔融时用镁或铈等元素进行处理，以诱导游离石墨形成为球粒或球晶，从而赋予铸造金属可测量的延展性。又称球墨铸铁、球晶石墨铸铁和SG铸铁。 |
| Ferritic stainless steels | 铁素体不锈钢 |
Ferritic stainless steels have the ferrite (BCC) crystal structure and contain 10–28% chromium and typically 0.1–0.35% carbon (all in wt%). They are magnetic and can be hardened by cold working. They have good to moderate mechanical properties, good oxidation and corrosion resistance at elevated temperatures, and susceptibility to embrittlement at temperatures between 400 and 540°C. Used for turbine parts, hightemperature valves, automotive exhaust components, and nuclear reactor core components. 铁素体不锈钢具有铁素体（BCC）晶体结构，含有10-28%的铬，通常含有0.1-0.35%的碳（均为重量%）。它们具有磁性，可通过冷加工硬化。它们具有良好至中等的机械性能，在高温下具有良好的抗氧化性和耐腐蚀性，在400至540°C的温度下易脆化。用于涡轮零件、高温阀、汽车排气部件和核反应堆堆芯部件。 |
| Inch (in) | 英寸（in） |
A non-SI unit of length now defined as 25.4 mm. The conversion to SI is 1 in = 2.54 × 10−2 m. 现在定义为25.4毫米的非SI长度单位。转换为SI为1in=2.54×10-2m。 |
| Crest of screw thread | 螺纹牙顶 |
The top surface joining the two sides of flanks of a thread. 连接螺纹牙侧两侧的顶面。 |
| Vapour static pressure | 蒸汽静压 |
(Unit Pa or bar) A pressure analogous to hydrostatic pressure, where the fluid is a vapour such as steam. A term used in geothermal applications. （单位Pa或bar）类似于静水压力的压力，其中流体是蒸汽，如蒸汽。地热应用中使用的术语。 |
| Transfer moulding | 转移模塑 |
(resin-transfer moulding, RTM) A method of compression moulding polymers in which the dies are closed before the operation starts. （树脂传递模塑，RTM）一种对聚合物进行压缩模塑的方法，其中模具在操作开始前关闭。 |
| Stress-intensity calibration | 应力强度校准 |
A mathematical expression, based on empirical or analytical results, that relates the stress-intensity factor to load and crack length for a specific specimen planar geometry. Also known as Kcalibration. 基于经验或分析结果的数学表达式，该表达式将特定试样平面几何形状的应力强度因子与载荷和裂纹长度联系起来。也称为K校准。 |
| Sample average | 样本平均值 |
The sum of all the observed values in a sample divided by the sample size. It is a point estimate of the population mean. Also known as arithmetic mean. 样本中所有观察值的总和除以样本大小。它是总体平均值的点估计。也称为算术平均值。 |
| Oil hardening | 油回火 |
The formation of martensite before tempering by quenching suitable steels in oil at lower cooling rates than given by water quenching, thus reducing the likelihood of component fracture or severe residual stresses. Quench-hardening treatment involving cooling in oil. 通过在油中以低于水淬的冷却速率淬火合适的钢，在回火前形成马氏体，从而降低部件断裂或严重残余应力的可能性。是一种淬火硬化处理，包括在油中冷却。 |
| Butt joint | 对接接头 |
The end-to-end joining of two plates either by welding or by overlapping plates that are bolted or riveted. 通过焊接或通过螺栓或铆接的重叠板将两块板端对端连接。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Computer vision | 计算机视觉 |
The digitization and processing of optical images/patterns by computer in order to recognize parts, orientation, etc. in manufacturing. 通过计算机对光学图像/图案进行数字化和处理，以在制造过程中识别零件、方向等。 |
| Maximum stress (Smax) | 最大应力（Smax） |
The stress having the highest algebraic value in the stress cycle, tensile stress being considered positive and compressive stress negative. The nominal stress is used most commonly. 在应力循环中具有最高代数值的应力，拉应力被认为是正的，压应力被认为是负的。名义应力是最常用的。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Energy losses (Unit kJ) | 能量损失（单位kJ） |
A commonly-used misnomer in view of the conservation-ofenergy principle, but used to mean energy converted into forms that are not used in a process, for example thermal energy from a heat engine dissipated to the surroundings, or produced by friction in a machine, or by surface drag. 从能量守恒原理来看，这是一个常用的术语错误，但可以用于表示转换为过程中未使用的形式的能量，例如，从热机散发到周围环境的热能，或由机器中的摩擦或表面阻力产生的热能。 |
| Pressure difference (Unit Pa) | 压差（单位Pa） |
(pressure differential, Δp) The difference between two pressures, one of which may be a reference pressure such as barometric pressure. In many flow processes, the pressure difference is more important than the absolute pressure level. （压差，Δp）两个压力之间的差值，其中一个压力可以是参考压力，如大气压力。在许多流动过程中，压差比绝对压力水平更重要。 |
| Fillet radius | 圆角半径 |
Concave junction at two intersecting surfaces of a fastener. Often used to describe the junction between the head and the shank of a threaded fastener (under head fillet). 在紧固件的两个相交表面处的凹形接合处。通常用于描述螺纹紧固件的头部和柄部之间的连接处（头部圆角下方）。 |
| End-quench hardenability test | 端淬淬透性试验 |
A laboratory procedure for determining the hardenability of a steel or other ferrous alloy. Hardenability is determined by heating a standard specimen above the upper critical temperature, placing the hot specimen in a fixture so that a stream of cold water impinges on one end, and, after cooling to room temperature is completed, measuring the hardness near the surface of the specimen at regularly spaced intervals along its length. The data are normally plotted as hardness versus distance from the quenched end. 测定钢或其他铁合金淬透性的实验室程序。淬透性是通过将标准试样加热到高于上临界温度，将热试样放置在夹具中，使冷水流冲击一端，并在冷却至室温后，沿试样长度以规则间隔测量试样表面附近的硬度来确定的。数据通常绘制为硬度与距淬火端距离的关系。 |
| Embedment | 嵌入 |
Localized plastic deformation in heavily loaded fasteners allows one part to sink into, or smooth the surface of, a softer or more heavily loaded second part. Nuts embed themselves in joint surfaces. Bolt threads embed themselves in nut threads, etc. 重载紧固件中的局部塑性变形允许一个零件陷入较软或更重载的第二零件中，或使其表面光滑。螺母嵌入接合面中。例如螺栓螺纹嵌入螺母螺纹等。 |
| Delamination | 分层 |
A mode of failure of composite materials, including radial-ply tyres, in which the layers separate due to repeated cyclic loading, impact, or weak bonding. 复合材料的一种失效模式，包括子午线轮胎，其中层由于重复的循环载荷、冲击或弱粘合而分离。 |
| Precipitation heat treatment | 沉淀热处理 |
Artificial aging in which a constituent precipitates from a supersaturated solid solution. 成分从过饱和固溶体沉淀的人工时效。 |
| Edge distance ratio | 边距比 |
The ratio of the edge distance to the pin diameter in a bearing test. 轴承测试中边缘距离与销直径的比值。 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Active accommodation | 主动适应能力 |
The use of information from sensors, for example, in a vision system, that allows a robot to show accommodation to the environment. 使用来自传感器的信息，例如在视觉系统中，允许机器人显示对环境的适应。 |
| Constant-mesh gearbox | 恒啮合齿轮箱 |
A gearbox in which the pairs of gears giving different speed ratios are constantly in mesh, different ratios being obtained by connecting or disconnecting the relevant gear to the driving shaft. 一种齿轮箱，其中提供不同速比的齿轮对始终啮合，通过将相关齿轮连接或断开驱动轴获得不同的速比。 |
| Stress cycles endured (N) | 承受的应力循环（N） |
The number of cycles of a specified character (that produce fluctuating stress and strain) that a specimen has endured at any time in its stress history. 试样在其应力历史中任何时间所经受的特定特征（产生波动应力和应变）的循环次数。 |
| Nonlinear behavior | 非线性行为 |
A fastener or joint system is said to exhibit nonlinear behavior when the relationship between the External load on the joint and deformation of the parts is nonlinear, or when the relationship between increasing Preload and deformation is nonlinear. 当接头上的外部载荷与零件变形之间的关系是非线性的，或者当增加的预载荷与变形之间的联系是非线性的时，可以说紧固件或接头系统表现出非线性行为。 |
| Dynamic load (Unit N) | 动态负载（单位N） |
1. Loading of a component or structure by a moving object whose point of application changes with time, e.g. the live load of a train passing over a bridge. 2. A load applied to a particular part of a component or structure in a short time interval. 1. 应用点随时间变化的移动物体对部件或结构的加载，例如通过桥梁的火车的活荷载。2. 在短时间内施加到部件或结构的特定部分的载荷。 |
| Archimedes Wave Swing | 阿基米德波摆动 |
A machine for tidal-power energy generation consisting of two concentric, air-filled submerged cylinders. The inner lower cylinder is tethered to the ocean floor while the upper floater unit, which is closed at the top, moves up and down due to the variations in hydrostatic pressure caused by the wave motion. The relative movement of the two cylinders is used to generate electricity in which linear motion replaces the more common rotary motion of an electromagnetic generator. 一种用于潮汐能发电的机器，由两个同心的充气水下气缸组成。内部下部圆柱体系在海底，而顶部封闭的上部浮子单元由于波浪运动引起的静水压力变化而上下移动。两个气缸的相对运动用于发电，其中直线运动取代了电磁发电机更常见的旋转运动。 |
| Pressure surface | 压力面 |
The high-pressure surface of an aerofoil, turbine, or compressor blade. In normal aircraft applications, this is the lower surface of a wing. For applications, such as to high-performance motor vehicles, where the aerofoil is inverted to generate downforce, it is the upper surface. 机翼、涡轮或压缩机叶片的高压表面。在正常的飞机应用中，这是机翼的下表面。对于高性能机动车辆等应用，机翼翻转以产生下压力，它是上表面。 |
| Batch | 一批 |
A definite quantity of some product or material produced under conditions that are considered uniform. A batch is usually smaller than a lot. 在被认为是均匀的条件下生产的一定数量的某些产品或材料。批次通常小于很多。 |
| Breaks | 断裂 |
Creases or ridges usually in “untempered” or in aged material where the yield point has been exceeded. Depending on the origin of the break, it may be termed a cross break, a coil break, an edge break, or a sticker break. 通常在“未回火”或超过屈服点的老化材料中出现折痕或隆起。根据断裂的起源，它可能被称为交叉断裂、线圈断裂、边缘断裂或贴纸断裂。 |
| Wheel | 轮 |
A solid disc, or a circular ring with spokes radiating from a central hub, either attached to an axle around which it revolves or which revolves with a rotating axle. 一个实心圆盘，或一个带有辐条的圆环，辐条从一个中心毂放射出来，或附在一个绕其旋转的轴上，或与一个旋转轴一起旋转。 |
| Endurance | 耐力 |
The capacity of a material to withstand repeated application of stress. 材料承受反复施加应力的能力。 |
| Fit | 装配 |
The general term used to signify the range of tightness which may result from the application of a specific combination of allowances and tolerances in the design of mating parts. 通用术语，用于表示配合零件设计中公差和公差的特定组合可能导致的紧密性范围。 |
| Tooth lock washers | 带齿锁紧垫圈 |
These washers serve to lock fasteners, such as bolts and nuts, to the component parts of an assembly, or increase the friction between the fasteners and the assembly. They are designated in a manner similar to helical spring lock washers, and are available in carbon steel. 这些垫圈用于将紧固件（如螺栓和螺母）锁定到组件的零部件上，或增加紧固件与组件之间的摩擦力。它们的设计方式类似于螺旋弹簧锁紧垫圈，可采用碳钢。 |
| Tensioner | 张紧器 |
A hydraulic tool used to tighten a fastener by stretching it rather than by applying a substantial torque to the nut. After the tension has stretched the bolt or stud, the nut is run down against the joint with a modest torque, and the tensioner is disengaged from the fastener. The nut holds the stretch produced by the tensioner. 一种液压工具，用于通过拉伸紧固件而不是对螺母施加较大扭矩来拧紧紧固件。张力拉伸螺栓或螺柱后，以适当的扭矩将螺母向下压靠接头，张紧器与紧固件分离。螺母保持张紧器产生的拉伸。 |
| Process annealing | 中间退火 |
An imprecise term denoting various treatments used to improve workability. For the term to be meaningful, the condition of the material and the time-temperature cycle used must be stated. 一个不精确的术语，表示用于改善可加工性的各种处理方法。为了使术语有意义，必须说明材料的条件和使用的时间-温度循环。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Nut box mechanism | 螺母箱机械装置 |
In a lathe it is used to engage and disengage the lead screw for thread cutting. This comprises a pair of half-nuts capable of sliding in vertical slides in or out of mesh with the lead screw. 在车床中，它用于接合和分离丝杠以进行螺纹切削。这包括一对半螺母，能够在与丝杠啮合的垂直滑动中滑动。 |
| Brittle | 脆性材料 |
A brittle material is one that breaks, often suddenly, with no permanent deformation. Examples of brittle materials are some cast irons, glass, concrete, and some plastics. A bolt is said to be brittle if it will break when stretched only a small amount past its yield point. 脆性材料通常会突然断裂，不会产生永久变形。脆性材料的例子有一些铸铁、玻璃、混凝土和一些塑料。如果螺栓在拉伸时仅超过其屈服点一小部分就会断裂，则称其为脆性螺栓。 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Indentation hardness | 压痕硬度 |
The resistance of a material to indentation as determined by hardness testing. The indenter, which may be spherical or diamond shaped, is pressed into the surface of a metal under specified load for a given time. (Unit Pa or, non-SI, kgf/mm²) A measurement of hardness taken by means of an indenter, pressed into a material by a load, which makes a permanent impression. The hardness is given by the load divided by the projected (sometimes surface) area of the indentation. Plasticity theory shows that the hardness is about 2.5–3 times the uniaxial yield stress. 通过硬度测试确定的材料抗压痕的能力。压头可以是球形或菱形，在规定的载荷下压入金属表面一段时间。（单位Pa或，非国际单位制，kgf/mm²）通过压头测量硬度，压入材料，形成永久压痕。硬度由载荷除以压痕的投影（有时是表面）面积得出。塑性理论表明，硬度约为单轴屈服应力的2.5–3倍。 |
| Cleavage fracture | 解理断裂 |
A fracture, usually of a polycrystalline metal, in which most of the grains have failed by cleavage, resulting in bright reflecting facets. It is one type of crystalline fracture and is associated with low energy brittle fracture. Contrast with shear fracture. A fracture created by splitting (cleavage), as between layers in materials like slate or mica. In brittle metals, and brittle microconstituents in alloys, cleavage occurs along particular crystal planes. 一种通过分裂（劈裂）产生的裂缝断裂，通常是多晶金属的断裂，其中大部分晶粒因解理而失效，产生明亮的反射面。它是一种结晶性断裂，与低能脆性断裂有关。与剪切断裂相对。如板岩或云母等材料的层之间。在脆性金属和合金中的脆性微量成分中，沿特定晶面发生解理。 |
| Nut factor | 螺母系数 |
An experimental constant used to evaluate or describe the ratio between the torque applied to a fastener and the Preload achieved as a result. 用于评估或描述施加在紧固件上的扭矩与由此获得的预载之间的比率的实验常数。 |
| Offset modulus | 补偿模量 |
The ratio of the offset yield stress to the extension at the offset point (plastics). 偏移屈服应力与偏移点（塑料）处延伸的比率。 |
| Thread grinding | 螺纹磨削 |
A method for producing or finishing very precise screw threads using a profiled grinding wheel. 一种使用异形砂轮生产或精加工非常精密螺纹的方法。 |
| Atmosphere | 大气 |
1. (atm) An obsolete (non-SI) unit of pressure equal to 101 325 Pa or 1.013 25 bar and approximately equal to the atmospheric pressure (barometric pressure) measured at mean sea level. 1.（atm）一种已被淘汰的（非SI）压力单位，等于101325Pa或1.01325bar，大约等于在平均海平面测量的大气压力（大气压）。 |
| Transformation temperature | 相变温度 |
The temperature at which a change in phase occurs. The term is sometimes used to denote the limiting temperature of a transformation range. The following symbols are used for iron and steels. 发生相位变化的温度。该术语有时用于表示转变范围的极限温度。以下符号用于钢铁。 |
| Absorber | 吸收器 |
1. An auxiliary vibratory system that favourably modifies the vibration characteristics of a main system. 2. Part of an absorption refrigeration system in which the refrigerant is absorbed by a transport medium. 3. The absorber plate is the receiver of a concentrating solar collector where the radiation is absorbed. 1.一种辅助振动系统，可有利地改变主系统的振动特性。2.吸收式制冷系统的一部分，其中制冷剂被传输介质吸收。3.吸收板是吸收辐射的聚光太阳能集热器的接收器。 |
| Circlip | 卡簧 |
(snap ring) An external or internal retaining ring that locates parts of circular cross section in an axial direction. It consists of an incomplete ring, with holes on either side of the gap, that may be expanded by a plier-like tool to pass into a groove in a shaft or contracted to pass into a groove in a bore. （卡环）在轴向定位圆形横截面部分的外部或内部保持环。它由一个不完整的环组成，在间隙的任一侧都有孔，可以通过钳形工具将其扩展以进入轴中的凹槽或收缩以进入孔中的凹槽。 |
| Flattening test | 压扁试验 |
This term as applied to tubing refers to a method of testing a section of tubing by flattening it until the inside walls are parallel and separated by a given distanceusually equal to three times the wall thickness for seamless tubes and five times the wall thickness for lap-welded tubes. Boiler tubes subjected to this test should show no cracks or flaws. The flattening test applied to rivets, consists in flattening a rivet head while hot to a diameter equal to 21⁄2 times the diameter of the shank or body of the rivet. Good rivet steel must not crack at the edges of the flattened head. 该术语适用于管材，是指通过压扁管材直至内壁平行并隔开给定距离（通常等于无缝钢管壁厚的三倍，搭接焊管壁厚的五倍）来测试管材截面的方法。进行该试验的锅炉管应无裂纹或缺陷。适用于铆钉的压扁试验包括在热态下压扁铆钉头，使其直径等于铆钉柄或铆钉体直径的21⁄2倍。良好的铆钉钢不得在扁平头部边缘开裂。 |
| Atomic volume | 原子体积 |
Volume of unit cell per atom. 每个原子的晶胞体积。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Notch brittleness | 缺口脆性 |
Susceptibility of a material to brittle fractureat points of stress concentration. For example, in a notch tensile test, the material is said to be notch brittle if the notch strengthis less than the tensile strength of an unnotched specimen. Otherwise, it is said to be notch ductile. 材料在应力集中点易发生脆性断裂。例如，在缺口拉伸试验中，如果缺口强度小于无缺口试样的抗拉强度，则称材料为缺口脆性材料。否则，称其为缺口韧性。 |
| Archimedes screw | 阿基米德螺旋泵 |
A machine which comprises a rotating helical blade inside a closefitting tube, which may be used to pump liquids, slurries (such as sewage), granular materials, etc. If water flows into the top of an inclined or vertical Archimedes screw, the screw will rotate and can be used to drive an electrical generator. 一种机器，它在紧密的管子内包含一个旋转的螺旋叶片，可用于泵送液体、泥浆（如污水）、颗粒材料等。如果水流入倾斜或垂直的阿基米德螺杆的顶部，螺杆将旋转，可用于驱动发电机。 |
| Stability | 稳定性 |
1. A term relating to whether a body, structure, system, or flow is in a state of stable, unstable, or neutral equilibrium. 2. In numerical analysis, whether numerical errors, such as roundoff or input-data errors, are damped, propagate, or cause divergence of the solution as the numerical method proceeds. 3. A control system is often described as stable when a step change in input results in a steady output without continuing oscillation. 1.与物体、结构、系统或流是否处于稳定、不稳定或中性平衡状态有关的术语。2.在数值分析中，随着数值方法的进行，数值误差（如舍入误差或输入数据误差）是否衰减、传播或导致解发散。3.当输入的阶跃变化导致稳定输出而无持续振荡时，控制系统通常被描述为稳定的。 |
| Flange rotation | 法兰转角 |
Angular distortion of a flange under the influence of bolt and reaction forces. Measured with respect to the center of the cross section of the flange. 法兰在螺栓和反作用力影响下的角度变形。相对于法兰横截面的中心测量。 |
| Wind velocity (Unit m/s) | 风速（单位：m/s） |
1. In the Earth’s atmosphere, a vector quantity that quantifies both the magnitude of the wind speed and its direction at a given altitude and location, conveniently represented in the hodograph plane. For convenience, the unit kph is often used. It could in principle also include information about large- and small-scale unsteadiness. Spatial variation in wind velocity, either with altitude or in a horizontal plane, is termed wind shear. 2. The airspeed in the working section of a wind tunnel. 1.在地球大气层中，一种矢量量，用于量化给定高度和位置处的风速大小及其方向，方便地用速度计平面表示。为方便起见，通常使用单位kph。原则上，它还可以包括关于大尺度和小尺度不稳定性的信息。风速随高度或水平面的空间变化称为风切变。2.风洞工作段的空速。 |
| Modulus of elasticity (E) | 弹性模量（E） |
The measure of rigidity or stiffness of a metal; the ratio of stress, below the proportional limit, to the corresponding strain. In terms of the stress-strain diagram, the modulus of elasticity is the slope of the stress-strain curve in the range of linear proportionality of stress to strain. 金属的刚度或刚度的量度；低于比例极限的应力与相应应变之比。根据应力应变图，弹性模量是应力应变曲线在应力应变线性比例范围内的斜率。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Stress ratio (A or R) | 应力比（A或R） |
The algebraic ratio of two specified stress values in a stress cycle. Two commonly used stress ratios are the ratio of the alternating stress amplitude to the mean stress, A = Sa/Sm, and the ratio of the minimum stress to the maximum stress, R = Smin/Smax. 应力循环中两个指定应力值的代数比。两种常用的应力比是交变应力振幅与平均应力之比，A=Sa/Sm，以及最小应力与最大应力之比R=Smin/Smax。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Microstrain | 微应变 |
The strain over a gage length comparable to interatomic distances. These are the strains being averaged by the macrostrain measurement. Microstrain is not measurable by currently existing techniques. Variance of the microstrain distribution can, however, be measured by x-ray diffraction. 与原子间距离相当的标距上的应变。这些是通过宏观应变测量得到的平均应变。现有技术无法测量微应变。然而微应变分布的变化可以通过x射线衍射来测量。 |
| Flame annealing | 火焰退火 |
Annealing in which the heat is applied directly by a flame. 通过火焰直接加热的退火。 |
| Swift cup test | 斯威夫特杯测试 |
A simulative cupping test in which circular blanks of various diameters are clamped in a die ring and deep drawn into cups by a flat-bottomed cylindrical punch. 一种模拟拔杯试验，将不同直径的圆形坯料夹紧在模环中，并用平底圆柱冲头将其深拉入杯中。 |
| Cyaniding | 氰化 |
A case-hardening process in which a ferrous material is heated above the lower transformation range in a molten salt containing cyanide to cause simultaneous absorption of carbon and nitrogen at the surface and, by diffusion, create a concentration gradient. Quench hardening completes the process. 一种表面硬化工艺，将含铁材料在含氰化物的熔融盐中加热至低于较低转变范围，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。淬火硬化完成该过程。 |
| Vernier | 游标 |
A short auxiliary scale that slides along the main instrument scale to permit more accurate fractional reading of the least main division of the main scale. 一种短辅助刻度，沿主仪表刻度滑动，以便更准确地读取主刻度的最小主刻度。 |
| Impact testing | 冲击测试 |
Determination of the mechanical properties of materials under high-rate conditions. Often determined from the behaviour of a testpiece when struck by a pendulum or a weight falling from a known height, or when sandwiched between two Hopkinson bars. 在高速条件下测定材料的机械性能。通常根据测试件在被钟摆撞击或从已知高度坠落的重物或夹在两个霍普金森棒之间时的行为来确定。 |
| Thread run-out | 螺纹耗尽 |
That portion of the threads which are not cut or rolled full depth, but which provide the transition between full-depth threads and the body or head. Officially called thread washout or vanish, although the term run-out is more popular. (Run-out is officially reserved for rotational eccentricity, as defined by total indicator readings or the like.) 未全深度切割或轧制的螺纹部分，但提供全深度螺纹与主体或头部之间的过渡。官方称之为螺纹冲蚀或消失，但术语“耗尽”更为流行。（跳动是官方为旋转偏心度保留的，由总指示器读数等定义。） |
| Starting friction | 起动摩擦 |
(limiting friction, static friction, stiction) (Unit N) The force required to initiate movement between two bodies in contact. （极限摩擦力、静摩擦力、粘滞）（单位N）在两个接触物体之间启动运动所需的力。 |
| Castellated nut | 槽形螺母 |
A nut having slots across the hexagonal faces, used with a bolt having a drilled hole so that a split (cotter) pin may be inserted through both nut and bolt to prevent unscrewing. 一种在六角面上有槽的螺母，与具有钻孔的螺栓一起使用，以便将开口（开口）销插入穿过螺母和螺栓以防止拧松。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Honing | 珩磨 |
Honing is a controlled, low-speed sizing and surface-finishing process in which stock is removed by the shearing action to the bonded abrasive grains of a honing stone, or stick. Finish polishing of surfaces and cutting edges in which very fine abrasive powders, such as rouge, are employed. Honing is usually applied to cylindrical surfaces and lapping to flat, but the usage is not consistent. 珩磨是一种受控的低速尺寸和表面精加工工艺，其中通过对珩磨石或棒的粘结磨粒的剪切作用去除原料。表面和切削刃的精抛光，其中使用了非常细的研磨粉，例如胭脂。珩磨通常用于圆柱面，研磨至平面，但用法并不一致。 |
| Cold die quenching | 冷模淬火 |
A quench utilizing cold, flat, or shaped dies to extract heat from a part. Cold die quenching is slow, expensive, and is limited to smaller parts with large surface areas. 利用冷、平或成型模具从零件中提取热量的淬火。冷模淬火速度慢、成本高，并且仅限于表面积较大的较小零件。 |
| Cap nut | 盖型螺母 |
A nut with a blind threaded hole, for example a dome nut to cover the end of a bolt. 带有盲螺纹孔的螺母，例如用于覆盖螺栓末端的圆顶螺母。 |
| Swept volume (Unit m³) | 扫描体（单位m³) |
In the cylinder of a piston engine or other device, the volume between top and bottom dead centre positions of a piston; equal to πR2S where R is the piston radius and S is the stroke. 在活塞发动机或其他装置的气缸中，活塞上止点和下止点位置之间的体积；等于πR2S，其中R是活塞半径，S是冲程。 |
| Interrupted quenching | 间断淬火 |
A quenching procedure in which the workpiece is removed from the first quench at a temperature substantially higher than that of the quenchant and is then subjected to a second quenching system having a different cooling rate than the first. 在该淬火过程中，工件在显著高于淬火剂的温度下从第一次淬火中取出，然后经受具有不同于第一次淬火的冷却速率的第二次淬火系统。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Sawing | 锯切 |
Sawing is the process of cutting a workpiece with power band saws, hacksaws, and circular saws. Each of these methods is used in cutoff operations (cutting pieces to a required length), although band sawing also provides a method of cutting contours. 锯切是用带锯、钢锯和圆锯切割工件的过程。这些方法中的每一种都用于切割操作（将工件切割到所需长度），尽管带锯也提供了一种切割轮廓的方法。 |
| Material velocity | 材料速度 |
The velocity of sound in a body (e.g., a bolt). A term used in the ultrasonic measurement of bolt stress or strain. 声音在物体（例如螺栓）中的速度。用于螺栓应力或应变的超声波测量的术语。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Radioactive heat (Unit J) | 放射性热（单位J） |
Thermal energy released from the nucleus of an atom such as uranium235 by fission due to the absorption of a neutron. Heat is also produced by radioactive decay. 铀235等原子核因吸收中子而裂变释放的热能。放射性衰变也会产生热量。 |
| Transmissibility | 传递率 |
The ratio of the transmitted force to the disturbing force for a system subjected to a vibratory disturbance. The ratio may also be defined in terms of displacements, velocities, or accelerations. 受到振动干扰的系统的传递力与干扰力之比。该比率也可以用位移、速度或加速度来定义。 |
| Proof load | 验证载荷（单位 N） |
The maximum, safe, static, tensile load which can be placed on a fastener without yielding it. Sometimes given as a force (in lb or N) sometimes as a stress (in psi or MPa). The test load in quality control to which different components made of different materials must be subjected without failing in order to perform properly. 可施加在紧固件上而不使其屈服的最大安全静态拉伸载荷。有时以力（lb或N）表示，有时以应力（psi或MPa）表示。质量控制中的测试负荷，由不同材料制成的不同部件必须经受该负荷，才能正常运行。 |
| Tension joint | 张力接头 |
A joint which is primarily subjected to loads acting more or less parallel to the axes of the bolts. 主要承受或多或少平行于螺栓轴线的载荷的接头。 |
| Binary vapour cycle | 二元蒸气循环 |
A power cycle which combines a steam cycle at relatively low temperature (the bottoming cycle) with a higher temperature cycle (the topping cycle) in which a working fluid such as mercury, sodium or potassium is used. 一种动力循环，它将相对低温的蒸汽循环（底部循环）与高温循环（顶部循环）相结合，其中使用了诸如汞、钠或钾之类的工作流体。 |
| Computer-aided manufacturing | 计算机辅助制造 |
(CAM, computer-integrated manufacturing, CIM) The use of computers in all branches of manufacturing, not only to control machines and robots for manufacturing and assembly, but also for process planning, and monitoring progress of materials and components during production, etc. （CAM，计算机集成制造，CIM）在制造的所有分支中使用计算机，不仅可以控制制造和组装的机器和机器人，还可以进行工艺规划，以及在生产过程中监控材料和组件的进度等。 |
| Nut | 螺母 |
A metal fastener of square, hexagon or other shape, having an internal thread which screws onto a bolt, stud or arbor. An internally-threaded fastener used with externally-threaded bolts. Usually hexagonal in shape but there is a multitude of other geometries, such as square, for special purposes and different gripping tools. 一种方形、六角形或其他形状的金属紧固件，具有内螺纹，可拧在螺栓、螺柱或心轴上。与外螺纹螺栓一起使用的内螺纹紧固件。通常为六边形，但也有许多其他几何形状，如方形，用于特殊用途和不同的夹持工具。 |
| Graphitizing | 石墨化退火 |
Annealing a ferrous alloy in such a way that some or all of the carbon is precipitated as graphite. 以使部分或全部碳以石墨的形式沉淀的方式对铁合金进行退火。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Cooling coil | 冷却盘管 |
A simple heat exchanger consisting of a coiled tube, typically of copper or stainless steel, through which is circulated a coolant such as a refrigerant, chilled water, or water mixed with ethylene glycol. Applications include air conditioning, process cooling, and refrigeration. 一种简单的热交换器，由通常由铜或不锈钢制成的盘管组成，冷却剂如制冷剂、冷冻水或与乙二醇混合的水通过盘管循环。应用包括空调、工艺冷却和制冷。 |
| Amplifier | 放大器 |
A device by which the output of a hydraulic, pneumatic, or electrical source is increased. 增加液压、气动或电源输出的装置。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Spring materials | 弹簧材料 |
Mainly metals including plain-carbon and corrosion-resisting steels, phosphor bronze, spring brass, beryllium copper and nickel alloys, all of which in their workhardened states permit large reversible elastic strains without permanent deformation. 主要是金属，包括普通碳钢和耐腐蚀钢、磷青铜、弹簧黄铜、铍铜和镍合金，所有这些金属在其加工硬化状态下都允许大的可逆弹性应变而不会产生永久变形。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Celsius | 摄氏度 |
The temperature scale based on the freezing point of water (0ºC) and the boiling point of water (100ºC). The interval between these points is divided into 100 degrees. The scale was devised by Anders Celsius. 基于水的冰点（0ºC）和水的沸点（100ºC）的温标。这些点之间的间隔被划分为100度。这个比例是由安德斯·摄氏设计的。 |
| Coefficient of cubic expansion | 立方膨胀系数 |
The fractional increase in volume per unit temperature rise. 每单位温度升高的体积增加分数。 |
| Pulley | 带轮 |
A free or driven wheel on a shaft with an appropriately shaped rim to carry a flat belt, vee belt, notched belt, rope, or chain. Used to transmit power or motion. 轴上的自由轮或从动轮，具有适当形状的轮缘，以承载平皮带、V形皮带、槽口皮带、绳索或链条。用于传递动力或运动。 |
| Displacement | 移位 |
The distance that a chosen measurement point on a cracked specimen displaces normal to the crack plane as the crack grows. 随着裂纹扩展，裂纹试样上选定的测量点垂直于裂纹平面位移的距离。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Wire rope | 钢丝绳 |
A type of cable formed from individual strands of wire with a helical twist. 一种线缆，由具有螺旋扭曲的单独的线股形成。 |
| Belt drive | 带传动 |
Transmission of motion from one shaft to another by means of a continuous plain, or toothed, flexible band (belt) passing over pulleys. In contrast to chain drives, belt drives tend to be employed in low-torque applications. Reduction in transmissible power may occur due to stretch of a plain transmission belt which results in slack in the drive (belt creep) or slip of a belt on a driving or driven pulley (belt slip). 通过穿过滑轮的连续平带或带齿柔性带（带）将运动从一根轴传递到另一根轴。与链条传动相比，皮带传动往往用于低扭矩应用。由于普通传动带的拉伸可能会导致传动松弛（皮带蠕变）或主动或从动皮带轮上的皮带打滑（皮带打滑），从而导致传动功率降低。 |
| Available head (Unit m) | 可用水头（单位米） |
In a hydroelectric power system, the difference between the vertical height of the water level in the supply reservoir above the turbine inlet less the head loss due to friction and fittings in the duct leading to the turbine. 在水力发电系统中，水轮机入口上方供水水库中水位垂直高度之间的差减去由于通向涡轮机的管道中的摩擦和配件造成的水头损失。 |
| Black oxide | 黑色氧化物 |
A black finish on a metal produced by immersing it in hot oxidizing salts or salt solutions. 通过将金属浸入热氧化盐或盐溶液中产生的黑色饰面。 |
| Decompression chamber | 减压舱 |
A chamber in which ambient-air pressure can be increased to levels found in deep-sea diving. It is used to gradually acclimatize divers back to normal conditions and avoid ‘the bends’. 环境气压可以提高到深海潜水水平的腔室。它用于逐渐使潜水员适应正常条件，避免“弯曲”。 |
| Engine emissions | 发动机排放 |
(exhaust emissions) The pollutants contained in the exhaust gases from an internal-combustion engine. （废气排放）内燃机废气中所含的污染物。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| V-block | V型块 |
A block having a 90° V-shaped recess; used in a workshop to hold round workpieces. 具有90°V形凹槽的块体；在车间里用来装圆形工件。 |
| Yielding | 屈服 |
Evidence of plastic deformation in structural materials. Also known as plastic flow or creep. 结构材料塑性变形的证据。也称为塑性流动或蠕变。 |
| Air-cooled engine | 风冷发动机 |
An internal-combustion engine directly cooled by airflow, rather than by water flowing through the engine block being cooled by a radiator. 一种由气流直接冷却的内燃机，而不是通过流经发动机缸体的水被散热器冷却。 |
| Intergranular cracking | 沿晶断裂 |
Cracking or fracturing that occurs between the grains or crystals in a polycrystalline aggregate. Also called intercrystalline cracking. 多晶聚集体中的晶粒或晶体之间发生的开裂或断裂。也称为晶间断裂。 |
| Vacuum relief valve | 真空安全阀 |
A valve that admits gas to a system under vacuum, should the degree of vacuum become excessive. 如果真空度过高，允许气体在真空下进入系统的阀门。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Scleroscope hardness number (HSc or HSd) | 硬化镜硬度值（HSc或HSd） |
A number related to the height of rebound of a diamond-tipped hammer dropped on the material being tested. It is measured on a scale determined by dividing into 100 units the average rebound of the hammer from a quenched(to maximum hardness) and untempered AISI W5 tool steel test block. 与落在被测材料上的菱形锤的回弹高度相关的数字。通过将锤子从淬火（达到最大硬度）和未淬火的AISI W5工具钢试块上的平均回弹分为100个单位来测量。 |
| Strain-hardening exponent (n value) | 应变硬化指数（n值） |
The value n in the relationship σ = Kεn, where σ is the true stress, ε is the true strain, and K, the strength coefficient, is equal to the true stress at a true strain of 1.0. The strain hardening exponent is equal to the slope of the true stress/true strain curve up to maximum load, when plotted on log-log coordinates. The n-value relates to the ability of a sheet of material to be stretched in metalworking operations. The higher the n-value, the better the formability(stretchability). Also known as the strain-hardening coefficient. 关系式σ=Kεn中的值n，其中σ是真应力，ε是真应变，K是强度系数，等于真应变为1.0时的真应力。在对数坐标上绘制时，应变硬化指数等于真应力/真应变曲线的斜率，直到最大载荷。n值与一片材料在金属加工操作中拉伸的能力有关。n值越高，成形性（拉伸性）越好。也称为应变硬化系数。 |
| Oxidized surface (on steel) | 氧化表面（在钢上） |
Surface having a thin, tightly adhering, oxidized skin (from straw to blue in color), extending in from the edge of a coil or sheet. Sometimes called annealing border. 表面具有薄的、紧密粘附的氧化皮（从稻草色到蓝色），从线圈或薄片的边缘延伸。有时称为退火边界。 |
| Mechanical vibration | 机械振动 |
The motion of a particle or body which oscillates about a position of equilibrium. 围绕平衡位置摆动的粒子或物体的运动。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Venturi | 文丘里管 |
A convergent–divergent flow nozzle, usually circular in cross section, with a relatively short convergent section (the confuser) upstream of a throat followed by a gradually diverging section (the diffuser). Such nozzles usually have flanges at either end for installation in a pipeline. Applications include flow meters and ejectors. When a fluid flows through a convergent duct at subsonic speed, there is an increase in velocity accompanied by a decrease in pressure (Venturi effect). 收敛-发散流喷嘴，横截面通常为圆形，喉部上游具有相对较短的收敛段（扰流器），然后是逐渐发散段（扩散器）。这种喷嘴通常在两端都有法兰，以便安装在管道中。应用包括流量计和喷射器。当流体以亚音速流过收敛管道时，速度增加，压力降低（文丘里效应）。 |
| Wind pressure (Unit Pa) | 风压（单位Pa） |
The dynamic pressure associated with the wind. The static pressure of the wind is the atmospheric pressure. 与风相关的动态压力。风的静压是大气压。 |
| Design load (Unit N) | 设计荷载（单位N） |
The greatest load that a component or structure is expected to experience under normal operating conditions. 部件或结构在正常运行条件下预期承受的最大负载。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Imperial system of units | 英制单位 |
British imperial system of units) An obsolete system of units first defined in the British Weights and Measures Act of 1824. Its three base units were second (time), yard (length), and pound avoirdupois (mass). The imperial unit of capacity was the gallon. The many associated units introduced subsequently include cubic inch, cubic foot, cubic yard, pint, and quart for both liquid and dry measures of capacity (i.e. volume); ounce, hundredweight, short and long ton for avoirdupois mass; poundal for force; minute and hour for time; fahrenheit for temperature; and British thermal unit for energy. Closely related to the imperial system of units is the US customary system of units. Each imperial unit is now legally defined in terms of the metric (i.e. SI) equivalent. （英帝国单位制）1824年英国度量衡法首次定义的已被淘汰的单位制。其三个基本单位为秒（时间）、码（长度）和磅（质量）。容量的英制单位是加仑。随后引入的许多相关单位包括立方英寸、立方英尺、立方码、品脱和夸脱，用于液体和干燥容量测量（即体积）；盎司，百分之一百重量，短吨和长吨，以保证重量；磅达表示力；以分钟和小时表示时间；华氏温度；英国热能单位。与帝国单位制密切相关的是美国习惯单位制。现在，每个英制单位在法律上都是以公制（即SI）当量来定义的。 |
| Linear (tensile or compressive) strain | 线性（拉伸或压缩）应变 |
The change per unit length due to force in an original linear dimension. An increase in length is considered positive. 由于原始线性尺寸中的力，每单位长度的变化。长度的增加被认为是正的。 |
| Corrosion fatigue | 腐蚀疲劳 |
Cracking produced by the combined action of repeated or fluctuating stress and a corrosive environment at lower stress levels or fewer cycles than would be required in the absence of a corrosive environment. 由重复或波动的应力和腐蚀环境的联合作用产生的开裂，其应力水平低于没有腐蚀环境时所需的应力水平或循环次数更少。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Seal | 密封件 |
A component which controls or prevents leakage of fluids into or out of parts of a machine. 控制或防止流体流入或流出机器部件的部件。 |
| Centre of pressure | 压力中心 |
1. The location, on an aerofoil or other body that develops lift, of the resultant lift force. 2. The location, on a surface submerged in a liquid, of the resultant force due to the pressure acting on the surface. Because hydrostatic pressure increases with depth, the centre of pressure is generally below the centroid of the surface. 1.在产生升力的机翼或其他物体上，合成升力的位置。2.在浸没在液体中的表面上，由于作用在表面上的压力而产生的合力的位置。由于静水压力随深度增加，压力中心通常低于表面质心。 |
| Magnetic test | 磁性测试 |
Method used to test heat extraction rates of various quenchants. The test works by utilizing the change in magnetic properties of metals at their Curie point–the temperature above which metals lose their magnetism. 用于测试各种淬火剂的热提取率的方法。该测试通过利用金属在居里点（即金属失去磁性的温度）的磁性变化来进行。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Dowel | 销钉 |
A headless cylindrical pin that fits into corresponding holes in mating components, thus ensuring relative location. A round metal or wooden pin. A pin, usually of circular shape like a cylinder, used to pin or fasten something in position temporarily or permanently. 一种圆头金属或木制圆柱销，可插入配合组件的相应孔中，从而确保相对位置，用于暂时或永久地将某物固定或固定到位。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |