| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Lüders lines | 吕德斯线 |
Elongated surface markings or depressions, often visible with the unaided eye, that form along the length of sheet metal or a tension specimen at an angle of approximately 45° to the loading axis. Caused by localized plastic deformation, they result from discontinuous (inhomogeneous) yielding. Also known as Lüders bands, Hartmann lines, Piobert lines, or stretcher strains. 拉长的表面标记或凹陷，通常肉眼可见，沿金属板或拉伸试样的长度形成，与加载轴的角度约为45°。由于局部塑性变形，它们是不连续（不均匀）屈服的结果。也被称为吕德斯带、哈特曼线、皮奥伯特线或拉伸线。 |
| Coaxial | 同轴 |
A term for components having a common axis such as concentric shafts. 具有共同轴线的部件的术语，例如同心轴。 |
| Austempering | 等温淬火 |
A heat treatment for ferrous alloys in which a part is quenched from the austenitizing temperature at a rate fast enough to avoid formation of ferrite or pearlite and then held at a temperature just above Ms until transformation to bainite is complete. Although designated as bainite in both austempered steel and austempered ductile iron (ADI), austempered steel consists of two phase mixtures containing ferrite and carbide, while austempered ductile iron consists of two phase mixtures containing ferrite and austenite. Heat treatment comprising austenitization of a steel article, cooling it to a bainitic range at a rate higher than the critical cooling rate and holding at a fixed temperature until the completion of bainitic transformation. 一种铁合金的热处理，其中零件从奥氏体化温度以足够快的速度淬火，以避免形成铁素体或珠光体，然后保持在略高于Ms的温度，直到完全转变为贝氏体。虽然在奥氏体钢和奥氏体球铁(ADI)中都被指定为贝氏体，但奥氏体钢由含有铁素体和碳化物的两相混合物组成，而奥氏体球墨铸铁由含有铁素体和奥氏体的两相混合物组成。热处理包括钢制品的奥氏体化，以高于临界冷却速率的速率将其冷却到贝氏体范围，并保持在固定温度直到贝氏体转变完成。 |
| Magnetic materials | 磁性材料 |
Materials in which the magnetic moment of adjacent atoms can adopt either parallel or antiparallel alignment. Ferromagnetism occurs when the magnetic moments adopt parallel alignment. When adjacent magnetic moments cancel due to antiparallel alignment, the material exhibits antiferromagnetism and has no overall magnetic moment. Examples of the latter include ferrous oxide and manganese oxide. The phenomenon of ferrimagnetism occurs when adjacent magnetic moments adopt antiparallel alignment but have unequal magnitude. The region of ferromagnetic or ferrimagnetic material in which the magnetic moments are aligned is known as a magnetic domain and adjacent regions are separated by domain walls. Diamagnetic and paramagnetic materials exhibit weak forms of magnetism that results from independent (uncoupled) alignment of magnetic atomic dipoles induced by an applied magnetic field. Ferromagnetic and ferrimagnetic materials can acquire high degrees of magnetization in relatively weak magnetic fields. They have different hysteresis characteristics and are classified as either hard magnets or soft magnets. Hard magnets retain large magnetization in the absence of an applied magnetic field and are used as permanent magnets. Conventional materials include magnet steels alloyed with tungsten or cobalt. Rare-earth magnets made from alloys of rare-earth elements produce significantly stronger magnetic fields. The most common of these are samarium-cobalt and neodymiumiron-boron permanent magnets. Their strength allows them to be small and used in numerous applications, including cordless tools, disk drives, headphones, toys, and motors for automotive components such as wipers, fans, washers, and windows. Soft magnets may be magnetized and demagnetized relatively easily. When subjected to an alternating magnetic field the energy loss due to hysteresis is small. Common materials include iron-silicon alloys (known as electrical steels), nickel-iron alloys (permalloy), soft ferrites, and amorphous nanocrystalline alloys, the last of which can be produced in the form of tape by meltspinning. Soft magnets are used to enhance the magnetic flux produced by an electric current. 相邻原子的磁矩可以采用平行或反平行排列的材料。当磁矩采用平行排列时，会产生铁磁性。当相邻磁矩因反平行排列而抵消时，材料表现出反铁磁性，没有总磁矩。后者的实例包括氧化亚铁和氧化锰。当相邻磁矩采用反平行排列但大小不等时，就会出现铁磁现象。磁矩对齐的铁磁或铁磁材料区域称为磁畴，相邻区域由磁畴壁分隔。抗磁和顺磁材料表现出弱磁性形式，这是由外加磁场诱导的磁原子偶极子的独立（非耦合）排列引起的。铁磁性和铁磁性材料可以在相对弱的磁场中获得高磁化度。它们具有不同的磁滞特性，分为硬磁铁和软磁铁。硬磁铁在没有外加磁场的情况下保持较大的磁化强度，用作永磁体。常规材料包括与钨或钴合金化的磁钢。由稀土元素合金制成的稀土磁体产生明显更强的磁场。其中最常见的是钐钴和钕硼永磁体。它们的强度使其体积小，可用于多种应用，包括无绳工具、磁盘驱动器、耳机、玩具和汽车部件（如雨刷、风扇、洗衣机和车窗）的电机。软磁体可以相对容易地磁化和退磁。当受到交变磁场时，由于磁滞引起的能量损失很小。常见材料包括铁硅合金（称为电工钢）、镍铁合金（坡莫合金）、软铁氧体和非晶纳米晶合金，最后一种可以通过熔钉以胶带的形式生产。软磁铁用于增强电流产生的磁通量。 |
| Die casting | 压铸 |
A process in which molten metal, particularly alloys of aluminium, magnesium, copper, and zinc, is forced under pressure (10 to 200 MPa) into a reusable hardened-steel mould machined into a die. 在压力（10至200MPa）下将熔融金属（特别是铝、镁、铜和锌的合金）强制进入加工成模具的可重复使用的硬化钢模具中的过程。 |
| Nautical mile (M) | 海里（M） |
A special unit of distance employed for marine and aerial navigation. The conversion to SI is 1 M = 1 852 m. 用于海上和空中导航的特殊距离单位。SI的转换为1M＝1852m。 |
| Carbonitriding | 碳氮共渗 |
A case hardening process in which a suitable ferrous material is heated above the lower transformation temperature in a gaseous atmosphere of such composition as to cause simultaneous absorption of carbon and nitrogen by the surface and, by diffusion, create a concentration gradient. The process is completed by cooling at a rate that produces the desired properties in the workpiece. 一种表面硬化工艺，在该工艺中，将合适的含铁材料在气体气氛中加热到较低的转变温度以上，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。该工艺通过以在工件中产生所需性能的速率冷却来完成。 |
| Pressure control valve | 压力控制阀 |
A valve used to set the pressure level in a pressure vessel or piping system. 用于设置压力容器或管道系统中压力水平的阀门。 |
| Carbon restoration | 碳修复 |
Replacing the carbon lost in the surface layer from previous processing by carburizing this layer to substantially the original carbon level. Sometimes called recarburizing. 通过将该层渗碳到基本上原始的碳水平来替换先前处理中在表面层中损失的碳。有时称为再碳化。 |
| Tension testing | 张力测试 |
A method of determining the behavior of materials subjected to uniaxial loading, which tends to stretch the metal. A longitudinal specimen of known length and diameter is gripped at both ends and stretched at a slow, controlled rate until rupture occurs. Also known as tensile testing. 一种确定材料在单轴载荷下的行为的方法，这种载荷倾向于拉伸金属。将已知长度和直径的纵向试样夹持在两端，并以缓慢、受控的速率拉伸，直到发生断裂。也称为拉伸测试。 |
| Centigrade heat unit | 摄氏热量单位 |
(Celsius heat unit, CHU) An obsolete (i.e. non-SI) unit equal to the energy required to increase the temperature of one pound of pure, air-free water from 14.5°C to 15.5°C at a pressure of one standard atmosphere. （摄氏热量单位，CHU）一个已被淘汰的（即非国际单位制）单位，等于在一个标准大气压的压力下将一磅纯净的无空气水的温度从14.5°C提高到15.5°C所需的能量. |
| Face | 表平面 |
To machine a flat surface perpendicular to the axis at rotation on a lathe. 在车床上加工一个垂直于旋转轴的平面。 |
| Grinding stress (Unit Pa) | 磨削应力（单位Pa） |
The residual stresses left in the surface of a component after grinding, owing to non-uniform cooling from the high surface temperatures produced. 由于产生的高表面温度造成的不均匀冷却，磨削后留在部件表面的残余应力。 |
| Engine | 引擎 |
A machine that converts energy, including the chemical energy in a fuel and electrical energy, into mechanical energy, usually to produce power delivered through a rotating shaft or thrust. Examples include internal-combustion engines, gas and steam turbines, rocket engines, electric, hydraulic and pneumatic motors. 一种将能量（包括燃料中的化学能和电能）转换为机械能的机器，通常通过旋转轴或推力产生动力。例子包括内燃机、燃气轮机和蒸汽轮机、火箭发动机、电动、液压和气动马达。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Screw compressor | 螺杆压缩机 |
A positive-displacement rotary compressor in which gas is progressively compressed by two intermeshing, counter-rotating, helical screws. 一种容积式旋转压缩机，其中气体由两个相互啮合、反向旋转的螺旋螺杆逐渐压缩。 |
| Homogeneous carburizing | 均匀渗碳 |
Use of a carburizing process to convert a low-carbon ferrous alloy to one of uniform and higher carbon content throughout the section. 使用渗碳工艺将低碳铁合金转化为整个截面中碳含量均匀且较高的合金。 |
| Minute (min) | 分钟（min） |
A non-SI unit of time. The conversion to SI is 1 min = 60 s. 非SI时间单位。转换为1分钟=60秒。 |
| Flat head | 平头 |
Flat top surface and a conical bearing surface. 平顶表面和锥形轴承表面。 |
| Cooling coil | 冷却盘管 |
A simple heat exchanger consisting of a coiled tube, typically of copper or stainless steel, through which is circulated a coolant such as a refrigerant, chilled water, or water mixed with ethylene glycol. Applications include air conditioning, process cooling, and refrigeration. 一种简单的热交换器，由通常由铜或不锈钢制成的盘管组成，冷却剂如制冷剂、冷冻水或与乙二醇混合的水通过盘管循环。应用包括空调、工艺冷却和制冷。 |
| Stretch ratio (extension ratio, λ) | 拉伸比（拉伸比，λ） |
A measure, used for highly-extensible materials such as rubber, of the extensional or normal strain of a component subjected to tension and defined as the ratio of the final length l, for a given load, to the initial or gauge length l0, where the coordinate axes are those of principal strain. It is related to the engineering strain e by λ = 1 + e. 用于高度可延展材料（如橡胶）的一种测量方法，用于测量受拉构件的拉伸或法向应变，定义为给定载荷下的最终长度l与初始或标距长度l0之比，其中坐标轴为主应变轴。它与工程应变e的关系为λ=1+e。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Secondary hardening | 二次硬化 |
The process whereby some low-alloy steels, quenched to produce martensite, produce fine precipitates when tempered above 550°C, which inhibit dislocation motion and reverse the trend towards lower strength at higher tempering temperatures. 某些低合金钢经淬火产生马氏体，在550°C以上回火时产生细小沉淀的过程，这抑制了位错运动，扭转了在较高回火温度下强度降低的趋势。 |
| Bioenergy | 生物能源 |
1. Energy derived from materials such as purpose-grown energy crops, including sugar cane, maize, wheat, and rice, as well as wood, straw, and animal waste, including sewage, manure, and animal litter. 2. A term sometimes used to cover biomass and biofuels together. 1.来自特定种植的能源作物（包括甘蔗、玉米、小麦和大米）以及木材、稻草和动物粪便（包括污水、粪便和动物垃圾）等材料的能源。2.有时用于同时涵盖生物质和生物燃料的术语。 |
| Quench cracking | 淬火开裂 |
Fracture of a metal during quenching from elevated temperature. Most frequently observed in hardened carbon steel, alloy steel, or tool steel parts of high hardness and low toughness. Cracks often emanate from fillets, holes, corners, or other stress raisers and result from high stresses due to the volume changes accompanying transformation to martensite. 高温淬火时金属断裂。在高硬度和低韧性的硬化碳钢、合金钢或工具钢零件中最常见。裂纹通常来自圆角、孔、角部或其他应力集中区，并由伴随马氏体转变的体积变化引起的高应力引起。 |
| Radial wave equation | 径向波动方程 |
A differential equation describing the transmission of a wave in a system with radial symmetry. 描述波在径向对称系统中传输的微分方程。 |
| Normal temperature and pressure (NTP) | 常温常压（NTP） |
Reference conditions defined by NIST as 20°C and 1 atm. NIST定义的参考条件为20°C和1atm。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Maraging steels | 马氏体时效钢 |
Very high-strength iron alloys named after ‘martensitic’ and ‘aging’. They contain nickel, chromium, cobalt, and molybdenum, and form martensite on air cooling with a strength of about 1 GPa. When reheated to about 500°C and aged for some hours, a room-temperature strength of some 2.4 GPa is reached. 以“马氏体”和“时效”命名的超高强度铁合金。它们含有镍、铬、钴和钼，在空气冷却下形成强度约为1GPa的马氏体。当再加热至约500°C并老化数小时时，室温强度达到约2.4GPa。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Forging cracks | 锻造裂纹 |
This may occur during fastener manufacturing at the cutting or forging operations and are located on the top of the head or on the raised periphery of indented head bolts. 这可能发生在紧固件制造过程中的切削或锻造操作中，并且位于头部的顶部或带锯齿的头部螺栓的凸起周边上。 |
| Finished fastener | 精制紧固件 |
Fastener for which all manufacturing steps have been completed, with or without any surface coating and with full or reduced loadability, and which has not been machined into a test piece. 已完成所有制造步骤的紧固件，有或没有任何表面涂层，具有完全或降低的承载能力，并且尚未加工成试件。 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Scoring | 划痕 |
In tribology, a severe form of wear characterized by the formation of extensive grooves and scratches in the direction of sliding. 在摩擦学中，一种严重的磨损形式，其特征是在滑动方向上形成大面积的凹槽和划痕。 |
| Kilo (k) | 千（k） |
An SI unit prefix indicating a multiplier of 103; thus kilometre (km) is a unit of length equal to one thousand metres. 表示乘法器103的SI单位前缀；1千米是长度单位，等于1000米。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Nut box mechanism | 螺母箱机械装置 |
In a lathe it is used to engage and disengage the lead screw for thread cutting. This comprises a pair of half-nuts capable of sliding in vertical slides in or out of mesh with the lead screw. 在车床中，它用于接合和分离丝杠以进行螺纹切削。这包括一对半螺母，能够在与丝杠啮合的垂直滑动中滑动。 |
| Forced-air quench | 强制空气淬火 |
A quench utilizing blasts of compressed air against relatively small parts such as a gear. 利用压缩空气冲击相对较小的零件（例如齿轮）进行的淬火。 |
| Working section | 工作区 |
That part of a wind tunnel in which models are placed for testing, or where detailed measurements are performed. 风洞中放置模型进行测试或进行详细测量的部分。 |
| Uniform strain | 均匀应变 |
The strain occurring prior to the beginning of localization of strain (necking); the strain to maximum load in the tension test. 在应变局部化（颈缩）开始之前发生的应变；拉伸试验中最大载荷的应变。 |
| Longitudinal direction | 纵向 |
The principal direction of flow in a worked metal. See also normal direction and transverse direction. 加工金属中的主要流动方向。另请参见法向和横向。 |
| Swift cup test | 斯威夫特杯测试 |
A simulative cupping test in which circular blanks of various diameters are clamped in a die ring and deep drawn into cups by a flat-bottomed cylindrical punch. 一种模拟拔杯试验，将不同直径的圆形坯料夹紧在模环中，并用平底圆柱冲头将其深拉入杯中。 |
| Plane-strain fracture toughness (KIc) | 平面应变断裂韧性（KIc） |
The crack extension resistance under conditions of crack-tip plane strain. 裂纹尖端平面应变条件下的裂纹扩展阻力。 |
| Safe working load (Unit N) | 安全工作负荷（单位：N） |
The steady or unsteady load against which a component or structure is designed for normal operation. It is lower than that which would cause failure by buckling, fracture, or yielding, so as to accommodate uncertainty, possible fault or accident conditions. 部件或结构设计用于正常运行的稳定或不稳定荷载。该值低于因屈曲、断裂或屈服而导致失效的值，以适应不确定性、可能的故障或事故条件。 |
| Stator | 定子 |
A ring of non-rotating blades or nozzles in a compressor, turbine, or other turbomachine, which directs fluid flow into an adjacent rotor. 涡轮压缩机、涡轮或其他涡轮机械中的一圈不旋转的叶片或喷嘴，将流体引导到相邻的转子中。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Fatigue life (N) | 疲劳寿命（N） |
The number of cycles of stress or strain of a specified character that a given specimen sustains before failure occurs. 给定试样在失效发生之前所承受的特定特征的应力或应变的循环次数。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Strength (Unit Pa) | 强度（单位Pa） |
The maximum stress, in tension, compression, shear, or combinations thereof, that may be monotonically applied to a material, component, or structure before failure (defined as fracture, yielding, buckling, etc. as appropriate). 在破坏前（视情况定义为断裂、屈服、屈曲等），材料、部件或结构在拉伸、压缩、剪切或其组合中可能单调施加的最大应力。 |
| Combustion deposit | 燃烧沉积物 |
Ash, carbon, and other incombustible solids, often due to impurities in the fuel, that build up on any surfaces exposed to products of combustion. They can lead to corrosion, reduced heat transfer and so higher flue-gas temperatures and reduced efficiency. 灰、碳和其他不燃固体，通常是由于燃料中的杂质，在暴露于燃烧产物的任何表面上堆积。它们会导致腐蚀、传热降低，从而导致烟气温度升高和效率降低。 |
| Pitch-circle diameter (Unit m) | 节圆直径（单位：m） |
The diameter of the circle (the pitch circle) centred on a component’s axis, around which holes or bolts are equally spaced. 以部件轴为中心的圆（节圆）的直径，孔或螺栓围绕其等距分布。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Cheese head | 圆柱头 |
A cylindrical head on a screw or bolt. For driving, it may be slotted, or hexagonally recessed. 螺钉或螺栓上的圆柱头。为了驱动，它可以是开槽的，也可以是六角形的。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Grain growth | 晶粒生长 |
An increase in the average size of the grains in polycrystalline metal, usually as a result of heating at elevated temperature. 多晶金属中晶粒平均尺寸的增加，通常是高温加热的结果。 |
| Mode of failure | 故障模式 |
The various ways in which a material can fail when subjected to loading, surface damage, chemical attack, heating, cooling, or radiation, in either isolation or combination. The failure modes include fracture, fatigue, creep, corrosion, erosion, and embrittlement. 材料在受到载荷、表面损伤、化学侵蚀、加热、冷却或辐射时，可能发生失效的各种方式，无论是单独还是组合。失效模式包括断裂、疲劳、蠕变、腐蚀、侵蚀和脆化。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Gear motor | 齿轮马达 |
Essentially a gear pump run in reverse, in which high-pressure fluid supplied to one side of the casing causes the gears to rotate. 本质上是一个齿轮泵反向运行，其中供应到外壳一侧的高压流体导致齿轮旋转。 |
| Vice | 老虎钳 |
A workshop tool used to hold a workpiece and consisting of two jaws, one fixed and the other moved by turning a screw. 一种用于夹持工件的车间工具，由两个钳口组成，一个固定，另一个通过转动螺钉移动。 |
| Thermodynamic state | 热力学状态 |
The condition of a system or working fluid according to its properties. 系统或工作流体根据其性质的状态。 |
| Bearing stress | 承受应力 |
The force per unit of bearing area. 每单位承载面积的力。 |
| Countersinking | 埋头孔 |
The flaring out of the rim of a drilled hole to form a truncated conical depression to receive a screw having a conical head, thus giving a flush fitting. 从钻孔的边缘向外张开以形成截锥形凹陷，以容纳具有锥形头的螺钉，从而提供齐平的配件。 |
| Compressive stress (Unit Pa) | 压缩应力（单位Pa） |
The compressive load per unit area at a point in a component. 部件中某点的每单位面积的压缩载荷。 |
| Cellular materials | 蜂窝材料 |
There are three broad classes of materials that have a sponge-like structure containing many small closed or open (interlinked) pores or cells. Natural cellular materials include bone, cork, sponge, and wood, and have numerous well-known uses. Wide ranges of cellular plastics are produced using blowing or foaming agents, such as air, ammonium carbonate, sodium bicarbonate, etc., to create pores during the processing of thermoplastic or thermosetting polymers. Rigid foams have moderate compressive strength and can be moulded and machined. 有三大类材料具有海绵状结构，包含许多小的封闭或开放（互连）孔或细胞。天然多孔材料包括骨骼、软木、海绵和木材，有许多众所周知的用途。使用发泡剂或发泡剂（如空气、碳酸铵、碳酸氢钠等）生产各种泡沫塑料，以在热塑性或热固性聚合物加工过程中产生孔隙。硬质泡沫具有中等抗压强度，可模制和机加工。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Stress distribution | 应力分布 |
The manner in which tensile, compressive, and shear stresses are distributed within a loaded body, indicated by loci of constant stress. 拉应力、压应力和剪应力在受载物体内的分布方式，由恒定应力轨迹表示。 |
| Stress equalizing | 应力均衡 |
A low-temperature heat treatment used to balance stresses in cold-worked material without an appreciable decrease in the mechanical strength produced by cold working. 一种低温热处理，用于平衡冷加工材料中的应力，而不会明显降低冷加工产生的机械强度。 |
| Check valve | 止回阀 |
(clack valve, non-return valve) A mechanical device that allows fluid flow in one direction only. The numerous designs include ball, diaphragm, disc, lift, split disc, and swing check valves. （瓣阀、止回阀）一种仅允许流体单向流动的机械装置。众多设计包括球阀、隔膜阀、盘阀、升降阀、分体盘阀和旋启式止回阀。 |
| Left hand screw | 左螺旋 |
One that screws into the mating part or advances when turned to the left or counter clockwise. 旋入配合部分或向左或逆时针旋转时前进的螺钉。 |
| Heat-capacity rate (c) (Unit W/K) | 热容率（c）（单位W/K） |
For fluid flow in a duct with mass flow rate ṁ, the product ṁC where C is the specific-heat capacity, at constant pressure (CP) in the case of a gas. 对于质量流量为ṁ的管道中的流体流动，乘积ṁC其中C是比热容，在气体的情况下为恒定压力（CP）。 |
| Following flank | 跟随侧翼 |
The flank of a thread opposite to the leading flank. 与前牙面相对的螺纹牙面。 |
| Bar | 巴（气压单位） |
A widely used (non-SI) unit of pressure approximately equal to normal atmospheric pressure at sea level. The conversion to SI is 1 bar = 105 Pa. Unit of pressure – the pressure created by a column of€mercury 75.006 cm high at 0ºC, or about 33.45 feet of water at 4ºC. It is equal to 105 pascal. Standard atmospheric pressure (at sea level) is 1.01325 bar, or 1013.25 mb. 一种广泛使用的（非SI）压力单位，大约等于海平面上的正常大气压。转换为SI为1bar=105Pa。压力单位——0ºC时75.006厘米高的水银柱或4ºC时约33.45英尺水柱产生的压力。它等于105帕斯卡。标准大气压（海平面）为1.01325bar或1013.25mb。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Slip joint | 滑动接头 |
A mechanical connection which allows limited endwise relative movement of two components such as pipes, rods, and ducts. 一种机械连接，允许两个部件（如管道、杆和管道）进行有限的轴向相对运动。 |
| Slip line | 滑移线 |
The trace of the slip plane on a viewing surface; the trace is usually observable only if the surface has been polished before deformation. The usual observation on metal crystals (under the light microscope) is of a cluster of slip lines known as a slip band. 滑动平面在观察表面上的轨迹；只有在变形前对表面进行抛光，才能观察到痕迹。通常对金属晶体的观察（在光学显微镜下）是一组称为滑移带的滑移线。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Strain hardening | 应变硬化 |
An increase in hardness and strengthcaused by plastic deformation at temperatures below the recrystallization range. Also known as work hardening. (workhardening) The increase in stress above the initial yield stress required to deform a metal to greater strains in the plastic range at temperatures below the recrystallization range (cold working). Unloading after some strain or work input gives a harder and stronger material. 在低于再结晶范围的温度下，塑性变形导致硬度和强度的增加。也称为加工硬化。（加工硬化）在低于再结晶范围（冷加工）的温度下，使金属在塑性范围内变形至更大应变所需的高于初始屈服应力的应力增加。在一定的应变或功输入后卸载，会得到更硬、更强的材料。 |
| Fracture test | 断裂试验 |
A test in which a specimen is broken and its fracture surface is examined with the unaided eye or with a low-power microscope to determine such factors as composition, grain size, case depth, or internal discontinuities. 1. The recording of load-deflexion (or stress–strain) in a specimen loaded monotonically until it breaks in tension, compression, shear, or torsion. 2. In fatigue, determination of the number of cycles to fracture for a specimen under different patterns of repeated loading. 3. Experiments to determine fracture toughness. 一种试验，其中试样被破坏并用肉眼或低倍显微镜检查其断裂表面，以确定成分、晶粒尺寸、表层深度或内部不连续性等因素。1.记录单调加载试样的载荷偏转（或应力-应变），直到其在拉伸、压缩、剪切或扭转中断裂。2.在疲劳技术中，确定试样在不同重复载荷模式下的断裂循环次数。3.测定断裂韧性的实验。 |
| Quimby screw pump | 昆比螺杆泵 |
A screw pump with two meshing screws, each having a righthand and a left-hand screw. Liquid enters at either end and is discharged from the middle. 带有两个啮合螺钉的螺杆泵，每个都有一个右旋螺纹和一个左旋螺纹。液体从两端进入，从中间排出。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Distortion | 扭曲 |
Any deviation from an original size, shape, or contour that occurs because of the application of stress or the release of residual stress. 由于施加应力或释放残余应力而发生的与原始尺寸、形状或轮廓的任何偏差。 |
| Failure of the joint | 连接失效 |
Failure of a bolted joint to behave as intended by the designer. Failure can be caused or accompanied by broken or lost bolts, but can also mean joint slip or leakage from a gasketed joint even if all bolts still remain whole and in place. Common reasons for joint failure include vibration loosening, poor assembly practices, improper design, unexpected service loads or conditions, etc. 螺栓连接未达到设计者的预期性能。故障可能由螺栓断裂或丢失引起或伴随而来，但也可能意味着即使所有螺栓仍保持完整和就位，也存在接头滑动或垫圈接头泄漏。接头故障的常见原因包括振动松动、装配不当、设计不当、意外的工作负载或条件等。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Tensioner | 张紧器 |
A hydraulic tool used to tighten a fastener by stretching it rather than by applying a substantial torque to the nut. After the tension has stretched the bolt or stud, the nut is run down against the joint with a modest torque, and the tensioner is disengaged from the fastener. The nut holds the stretch produced by the tensioner. 一种液压工具，用于通过拉伸紧固件而不是对螺母施加较大扭矩来拧紧紧固件。张力拉伸螺栓或螺柱后，以适当的扭矩将螺母向下压靠接头，张紧器与紧固件分离。螺母保持张紧器产生的拉伸。 |
| Ferrite | 铁素体 |
A solid solution of one or more elements in body-centered cubic iron. Unless otherwise designated (for instance, as chromium ferrite), the solute is generally assumed to be carbon. On some equilibrium diagrams, there are two ferrite regions separated by an austenite area. The lower area is alpha ferrite; the upper, delta ferrite. If there is no designation, alpha ferrite is assumed. 一种或多种元素在体心立方铁中的固溶体。除非另有说明（例如，铁酸铬），否则通常假定溶质为碳。在一些平衡图上，有两个铁素体区域被一个奥氏体区域隔开。下部区域为α铁素体；上部，δ铁氧体。如果没有指定，则假定为 α 铁氧体。 |
| Raised-face flange | 凸面法兰 |
A flange which contacts its mating joint member only in the region in which the gasket is located. The flanges do not contact each other at the bolt circle. 仅在垫圈所在区域接触其配合接头构件的法兰。法兰在螺栓圆处不相互接触。 |
| Stress difference (Unit Pa) | 应力差（单位Pa） |
The algebraic difference between the largest and least principal stresses in a loaded body, equal to twice the greatest shear stress in the system. For σ1 > σ2 > σ3, it is given by (σ1 − σ3). 载荷体中最大和最小主应力之间的代数差，等于系统中最大剪应力的两倍。由（σ1− σ3).，可得σ1＞σ2＞σ3。 |
| Dynamic strain aging | 动态应变时效 |
A behavior in metals in which solute atoms are sufficiently mobile to move toward and interact with dislocations. This results in strengthening over a specific range of elevated temperature and strain rate. 金属的一种特点，其中溶质原子具有足够的移动能力，能够向位错移动并与位错相互作用，会导致在特定的高温和应变速率范围内强化。 |
| Flange rotation | 法兰转角 |
Angular distortion of a flange under the influence of bolt and reaction forces. Measured with respect to the center of the cross section of the flange. 法兰在螺栓和反作用力影响下的角度变形。相对于法兰横截面的中心测量。 |
| Stress-intensity calibration | 应力强度校准 |
A mathematical expression, based on empirical or analytical results, that relates the stress-intensity factor to load and crack length for a specific specimen planar geometry. Also known as Kcalibration. 基于经验或分析结果的数学表达式，该表达式将特定试样平面几何形状的应力强度因子与载荷和裂纹长度联系起来。也称为K校准。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Biomedical engineering | 生物医学工程 |
The application of engineering principles and methodology to the medical field. Examples involving mechanical engineering include the design and construction of artificial limbs and hearts, heart-lung machines, prosthetic eyes, and orthopaedic implants such as hip joints and pins to stabilize fractured bones. 工程原理和方法在医学领域的应用。涉及机械工程的例子包括假肢和心脏、心肺机、假眼和骨科植入物（如髋关节和用于稳定骨折骨骼的销钉）的设计和建造。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Carburizing | 渗碳 |
Absorption and diffusion of carbon into solid ferrous alloys by heating, to a temperature usually above Ac3, in contact with a suitable carbonaceous material. A form of case hardening that produces a carbon gradient extending inward from the surface, enabling the surface layer to be hardened either by quenching directly from the carburizing temperature or by cooling to room temperature, then reaustenitizing and quenching. 通过与合适的含碳材料接触加热至通常高于Ac3的温度，将碳吸收和扩散到固体铁合金中。一种表面硬化形式，产生从表面向内延伸的碳梯度，通过直接从渗碳温度淬火或冷却至室温，然后重新奥氏体化和淬火，使表层硬化。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Ferritizing anneal | 铁素体化退火 |
A treatment given as-cast gray or ductile (nodular) iron to produce an essentially ferritic matrix. For the term to be meaningful, the final microstructure desired or the time-temperature cycle used must be specified. 给予铸态灰铁或球墨铸铁以产生基本铁素体基体的处理。为了使该术语有意义，必须指定所需的最终微观结构或使用的时间-温度循环。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Indentation hardness | 压痕硬度 |
The resistance of a material to indentation as determined by hardness testing. The indenter, which may be spherical or diamond shaped, is pressed into the surface of a metal under specified load for a given time. (Unit Pa or, non-SI, kgf/mm²) A measurement of hardness taken by means of an indenter, pressed into a material by a load, which makes a permanent impression. The hardness is given by the load divided by the projected (sometimes surface) area of the indentation. Plasticity theory shows that the hardness is about 2.5–3 times the uniaxial yield stress. 通过硬度测试确定的材料抗压痕的能力。压头可以是球形或菱形，在规定的载荷下压入金属表面一段时间。（单位Pa或，非国际单位制，kgf/mm²）通过压头测量硬度，压入材料，形成永久压痕。硬度由载荷除以压痕的投影（有时是表面）面积得出。塑性理论表明，硬度约为单轴屈服应力的2.5–3倍。 |
| Absolute viscosity | 绝对粘度 |
A measure of the internal shear properties of fluids, expressed as the tangential force per unit area at either of two horizontal planes separated by one unit thickness of a given fluid, one of the planes being fixed and the other moving with unit velocity. 流体内部剪切特性的量度，表示为两个水平面中的任何一个上的单位面积切向力，两个水平面被给定流体的一个单位厚度隔开，其中一个平面固定，另一个以单位速度移动。 |
| Strain | 拉紧 |
The unit of change in the size or shape of a body due to force. Also known as nominal strain. 物体的大小或形状因力而变化的单位。也称为标称应变。 |
| Quench-age embrittlement | 淬火时效脆化 |
Embrittlement of low-carbon steels resulting from precipitation of solute carbon at existing dislocations and from precipitation hardening of the steel caused by differences in ferrite at different temperatures. Quenchage embrittlement usually is caused by rapid cooling of the steel from temperatures slightly below Ac1 (the temperature at which austenite begins to form), and can be minimized by quenching from lower temperatures. 低碳钢的脆化是由于溶质碳在现有位错处的沉淀和铁素体在不同温度下的差异导致的钢沉淀硬化造成的。淬火脆性通常是由钢从略低于Ac1的温度（奥氏体开始形成的温度）快速冷却引起的，可以通过从较低温度淬火来最小化。 |
| Shear strain rate(Unit 1/s) | 剪切应变率（单位1/s） |
In the deformation of solids, the rate at which shear strain is applied in a test or changes with time in a loaded component or structure. 在固体变形中，在试验中施加剪切应变的速率，或在加载部件或结构中随时间变化的速率。 |
| Newton’s law of gravitation | 牛顿万有引力定律 |
(Newton’s law of universal gravitation) Any two bodies exert a gravitational force of attraction F on each other directed along the line joining their centres of mass, in magnitude proportional to the product of their masses and inversely proportional to the square of the distance r between them. （牛顿万有引力定律）任何两个物体沿其质心连接线相互施加引力F，其大小与其质量乘积成正比，与它们之间距离r的平方成反比。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Tightness parameter | 密封参数 |
A dimensionless parameter which defines the mass leakage of a gasket as a functionof contained pressure and a contained fluid constant. 一种无量纲参数，将垫圈的质量泄漏定义为所含压力和所含流体常数的函数。 |
| Chain | 链 |
A series of connected links, typically of steel. For lifting, pulling, securing, etc., each link is a closed loop, often in the form of a ring. For power transmission, the links are designed to mesh with the teeth of a sprocket wheel. In contrast to belt drives, chain drives tend to be employed in high-torque applications. 一系列连接的链接，通常是钢制的。对于提升、拉动、固定等，每个链节都是一个闭合环，通常呈环形。对于动力传输，链节设计为与链轮的齿啮合。与皮带传动相比，链传动往往用于高扭矩应用。 |
| Absorptance | 吸收率 |
(absorptivity, absorption coefficient, α) The fraction of radiant flux incident on a surface that is absorbed by the surface. The term also applies to absorption of radiation by a volume of fluid. For a semi-transparent surface, α + ρ + τ = 1, where ρ is the reflectance and τ is the transmittance. （吸收率，吸收系数，α）入射到表面的辐射通量被表面吸收的部分。该术语也适用于一定体积的流体对辐射的吸收。对于半透明表面，α+ρ+τ=1，其中ρ是反射率，τ是透射率。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Taper key | 楔键 |
A key with parallel sides but tapering cross section along its length. 边平行但横截面沿其长度逐渐变细的键。 |
| Graphitic carbon | 石墨碳 |
Free carbon in steel or cast iron. 钢或铸铁中的游离碳。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Wheel | 轮 |
A solid disc, or a circular ring with spokes radiating from a central hub, either attached to an axle around which it revolves or which revolves with a rotating axle. 一个实心圆盘，或一个带有辐条的圆环，辐条从一个中心毂放射出来，或附在一个绕其旋转的轴上，或与一个旋转轴一起旋转。 |
| Cohesive strength | 内聚强度 |
(Unit Pa) A theoretical fracture strength for solids based on interatomic forces, approximately equal to E/10 where E is Young’s modulus. （单位Pa）基于原子间力的固体理论断裂强度，大约等于E/10，其中E是杨氏模量。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Cold die quenching | 冷模淬火 |
A quench utilizing cold, flat, or shaped dies to extract heat from a part. Cold die quenching is slow, expensive, and is limited to smaller parts with large surface areas. 利用冷、平或成型模具从零件中提取热量的淬火。冷模淬火速度慢、成本高，并且仅限于表面积较大的较小零件。 |
| Dimensional stability | 尺寸稳定性 |
Ability of a plastic part to retain the precise shape in which it was molded, fabricated, or cast. 塑料零件保持其成型、制造或铸造时的精确形状的能力。 |
| Tension joint | 张力接头 |
A joint which is primarily subjected to loads acting more or less parallel to the axes of the bolts. 主要承受或多或少平行于螺栓轴线的载荷的接头。 |
| Interrupted aging | 分段时效 |
Aging at two or more temperatures, by steps, and cooling to room temperature after each step. 分为两个或两个以上的温度时效，按顺序并在每个步骤后冷却至室温。 |
| Grip length | 夹紧长度 |
Combined thickness of all the things clamped together by the bolt and nut, including washers, gaskets, and joint members. 由螺栓和螺母夹紧在一起的所有部件的总厚度，包括垫圈、垫圈和接头构件。 |
| Design pressure (Unit Pa) | 设计压力（单位Pa） |
The greatest pressure that a closed container is expected to experience under normal operating conditions. 密闭容器在正常操作条件下预期承受的最大压力。 |
| Stress amplitude | 应力幅值 |
One-half the algebraic difference between the maximum and minimum stress in one cycle of a repetitively varying stress. 重复变化应力的一个循环中最大和最小应力之间代数差的一半。 |
| Q-factor | 品质因素 |
(quality factor, sharpness of resonance) A non-dimensional parameter that describes, for a given resonant mode, the sharpness of the peak in the frequency response of a lightly-damped linear oscillator: Q = ωRES/Δω where ωRES is the resonance frequency and Δω is the half-power bandwidth of the resonance. It is inversely related to the damping such that a broad peak corresponds to high damping and a narrow peak to low damping. （品质因数，共振尖锐度）一个无量纲参数，用于描述给定共振模式下，轻阻尼线性振荡器频率响应峰值的尖锐度：Q=ωRES/Δω，其中ωRES是共振频率，Δω是共振的半功率带宽。它与阻尼成反比，因此宽峰值对应于高阻尼，窄峰值对应于低阻尼。 |
| Tangent screw | 微动螺旋 |
A worm screw used to adjust measuring instruments such as sextants and vernier callipers. 用于调整六分仪和游标卡尺等测量仪器的蜗杆。 |
| Positive-displacement machine | 正排量机 |
A machine that incorporates pistons, valves, etc. to ensure positive admission and delivery of a working fluid and prevent undesired reversal of flow. This class of machine incorporates all reciprocating compressors and expanders and some types of rotary compressor, the Roots blower, agear pump, a lobe pump, and a vane pump. 包含活塞、阀门等的机器，以确保工作流体的正向进入和输送，并防止不期望的反向流动。这类机器包括所有往复式压缩机和膨胀机以及一些类型的旋转压缩机、罗茨鼓风机、抽水机、凸轮泵和叶片泵。 |
| Ultimate strength | 极限应力 |
The maximum tensile strength a bolt or material can support prior to rupture. Always found in the plastic region of the stress–strain or force–elongation curve, and so is not a design strength. Also called Tensile strength and ultimate tensile strength. The maximum stress (tensile, compressive, or shear) a material can sustain without fracture, determined by dividing maximum load by the original cross-sectional area of the specimen. Also known as nominal strength or maximum strength. 螺栓或材料在断裂前可支撑的最大抗拉强度。总是出现在应力-应变或力-伸长率曲线的塑性区域，因此不是设计强度。也称为抗拉强度和极限抗拉强度。材料在不断裂的情况下能够承受的最大应力（拉伸、压缩或剪切），通过将最大载荷除以试样的原始横截面积来确定。也称为标称强度或最大强度。 |
| Hot-wire test | 热线测试 |
Method used to test heat extraction rates of various quenchants. Faster heat-extracting quenchants will permit more electric current to pass through a standard wire because it is cooled more quickly. Compare with hot-wire analyzer. 用于测试各种淬火剂的热提取率的方法。与热线分析仪相比，更快的热提取淬火剂将允许更多电流通过标准导线，因为标准导线冷却更快。 |
| Stress cycles endured (N) | 承受的应力循环（N） |
The number of cycles of a specified character (that produce fluctuating stress and strain) that a specimen has endured at any time in its stress history. 试样在其应力历史中任何时间所经受的特定特征（产生波动应力和应变）的循环次数。 |
| Dimension line | 尺寸线 |
A line on an engineering drawing with a numeral above it that shows the length of a feature, usually in millimetres. 工程图上的一条线，上面有一个数字，表示特征的长度，通常以毫米为单位。 |
| Clearance | 间距 |
(Unit m or μm) 1. The distance (if any) between mating components in an assembly. 2. The distance between two moving parts, or a moving part and stationary part, in a machine (e.g. the gap between a piston and a cylinder head). 3. With threads, the major clearance is the distance between the design form at the root of an internal thread and the crest of its mating external thread; the minor clearance is the corresponding dimension between the crest of an internal thread and the root of the external thread. （单位m或μm）1.装配体中配合组件之间的距离（如果有）。2.机器中两个运动部件之间的距离，或运动部件和静止部件之间的距离（例如活塞和气缸盖之间的间隙）。3.带螺纹时，主要间隙是内螺纹根部的设计形状与其配合的外螺纹牙顶之间的距离；小间隙是内螺纹牙顶和外螺纹牙根之间的对应尺寸。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Alloy steels | 合金钢 |
Steels that contain alloying elements such as chromium, nickel, molybdenum, manganese, silicon, tungsten, and vanadium. These are added to improve properties such as the hardenability, toughness, strength, wear resistance, and corrosion resistance compared with those of plain-carbon steel. Low-alloy steels have a total alloy content (including carbon) of less than about 8%. They are hardenable and have strength up to 30% higher than plain-carbon steels. High-alloy steels contain considerably more alloy content and are developed for specific properties such as superior corrosion and chemical resistance. 含有铬、镍、钼、锰、硅、钨和钒等合金元素的钢。添加这些是为了提高与普通碳钢相比的淬透性、韧性、强度、耐磨性和耐腐蚀性等性能。低合金钢的总合金含量（包括碳）小于约8%。它们是可硬化的，强度比普通碳钢高出30%。高合金钢含有相当多的合金含量，并针对特定性能而开发，例如卓越的耐腐蚀性和耐化学性。 |
| Sampling | 抽样 |
The process of measuring a series of values of a time-varying quantity. 测量一系列时变量值的过程。 |
| Water column | 水柱 |
Water in a tube, which may be vertical or inclined. If the tube is open to the atmosphere, the vertical height h from a datum level to the water surface is a measure of the water static pressure p at the datum level given by p − B = ρgh where B is the barometric pressure, ρ denotes the water density, and g is the acceleration due to gravity. 管道中的水，可以是垂直的或倾斜的。如果管道向大气开放，则从基准面到水面的垂直高度h是基准面处水静压p的量度，由p给出−B=ρgh，其中B是大气压力，ρ表示水密度，g是重力引起的加速度。 |
| Vapour-pressure thermometer | 蒸汽压力温度计 |
(vapour-filled thermometer) A type of fluidexpansion thermometer in which the working fluid is a volatile liquid. （蒸汽填充温度计）一种流体膨胀温度计，其中工作流体为挥发性液体。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Torque meter | 扭矩计 |
An instrument for measuring torque using spring-loaded, piezoelectric, or strain-gauged devices. 使用弹簧加载、压电或应变测量装置测量扭矩的仪器。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Friction loss (Unit J) | 摩擦损失（单位J） |
The conversion of mechanical energy to heat due to friction within a machine, mechanism, linkage, etc. 由于机器、机构、连杆等内部的摩擦而将机械能转化为热能。 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Tare weight (Unit N) | 皮重（单位N） |
The weight of an empty container. 空容器的重量。 |
| Activation energy | 活化能 |
(Ea, U) (Unit kJ/mol) The minimum energy for a chemical reaction to occur or for processes such as diffusion to take place in crystals. （Ea, U）（单位kJ/mol）发生化学反应或在晶体中发生扩散等过程的最小能量。 |
| Finish annealing | 精制退火 |
A subcritical annealing treatment applied to cold-worked low- or medium-carbon steel. Finish annealing, which is a compromise treatment, lowers residual stresses, thereby minimizing the risk of distortion in machining while retaining most of the benefits to machinability contributed by cold working. Compare with final annealing. 适用于冷加工低碳钢或中碳钢的亚临界退火处理。与最终退火相比，精加工退火是一种折衷处理，可降低残余应力，从而最大限度地降低加工中的变形风险，同时保留冷加工对可加工性的大部分好处。 |
| GGas turbine | G燃气轮机 |
An engine in which air, compressed by a multi-stage axial compressor and/or one or more centrifugal compressors, flows into a combustion chamber (or chambers) where fuel is burned and the hot gases then drive an axial turbine which powers the compressor. 由多级轴流压缩机和/或一个或多个离心压缩机压缩的空气流入燃烧室（或多个燃烧室），在燃烧室中燃烧燃料，然后热气体驱动轴流涡轮，为压缩机提供动力。 |
| Ratchet marks | 棘轮痕 |
Lines on a fatigue fracture surface that result from the intersection and connection of fatigue fractures propagating from multiple origins. Ratchet marks are parallel to the overall direction of crack propagation and are visible to the unaided eye or at low magnification. 疲劳断裂面上由从多个源头传播的疲劳断裂的交叉和连接产生的线。棘轮标记与裂纹扩展的整个方向平行，肉眼或低倍镜下均可看到。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Volume flow rate | 体积流率 |
(volumetric flow rate, , ) (Unit m³/s) The volume of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. （体积流量）（单位m³/s）单位时间内流经表面或管道或其他管道的材料体积，通常为流体或粉末。 |
| Absolute zero | 绝对零度 |
Temperature of -273.16″C or 459.69″F or OK at which molecular motion vanishes and a body has no heat energy. 温度为-273.16″C或459.69″F，此时分子运动消失且物体没有热能。 |
| Superheating | 过热 |
Heating above the temperature at which an equilibrium phase transformation should occur without actually obtaining the transformation. 在不实际获得相变的情况下，加热到应发生平衡相变的温度以上。 |
| Surface hardness | 表面硬度 |
(superficial hardness) Indentation hardness on, and for some distance below, the surface of a component, as opposed to its bulk hardness. Depending on the resolution required, micro- or nano-hardness testing machines are employed. （表面硬度）与整体硬度相反，部件表面及其下方一定距离的压痕硬度。根据所需的分辨率，可使用微型或纳米硬度测试机。 |
| Fatigue limit | 疲劳极限 |
The maximum stress that presumably leads to fatigue fracture in a specified number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. Compare with endurance limit. 在指定数量的应力循环中可能导致疲劳断裂的最大应力。还应说明最大应力值和应力比。与耐力极限比较。 |
| Brake lining | 制动衬片 |
The replaceable friction material that covers a brake shoe in an internally expanding brake. 在内膨胀制动器中覆盖制动的可更换摩擦材料。 |
| Vertical engine | 立式发动机 |
A piston engine having the cylinders above the crankshaft. 气缸位于曲轴上方的活塞发动机。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Acoustic pyrometer | 声学高温计 |
A non-intrusive pyrometer based on the principle that the sound speed in a gas is proportional to the square root of its absolute temperature. 一种非侵入式高温计，其原理是气体中的声速与其绝对温度的平方根成正比。 |
| Precipitation hardening | 沉淀硬化 |
Hardening caused by the precipitation of a constituent from a supersaturated solid solution. 因成分从过饱和固溶体沉淀而导致的硬化。 |
| Pressure ratio | 压力比 |
One pressure divided by another which may be a reference pressure. In many flow and thermodynamic processes, the pressure ratio is more important than the absolute pressure levels. For example, in compressible gas flow the Mach number is determined by the ratio of the stagnation pressure to the static pressure. 一个压力除以另一个压力，该压力可以是参考压力。在许多流动和热力学过程中，压力比比绝对压力水平更重要。例如，在可压缩气流中，马赫数由停滞压力与静压之比决定。 |
| Pressure-relief valve | 减压阀 |
A valve that limits the maximum pressure in a pressure vessel or fluid-power system to a specified level. 将压力容器或流体动力系统中的最大压力限制在规定水平的阀门。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Slot | 狭槽 |
A groove machined into a component, e.g. to allow for thermal expansion, or in which the tongue or tip of another component can fit or slide. 在部件上加工的凹槽，例如，允许热膨胀，或另一部件的榫舌或尖端可在其中安装或滑动。 |
| Stress-intensity factor | 应力强度因子 |
A scaling factor, usually denoted by the symbol K, used in linear-elastic fracture mechanics to describe the intensification of applied stress at the tip of a crack of known size and shape. At the onset of rapid crack propagation in any structure containing a crack, the factor is called the critical stress-intensity factor, or the fracture toughness. 一种标度因子，通常用符号K表示，在线弹性断裂力学中用于描述已知尺寸和形状的裂纹尖端施加应力的增强。在任何含有裂纹的结构中，裂纹快速扩展开始时，该因子称为临界应力强度因子，或断裂韧性。 |
| Octane number | 辛烷值 |
(octane rating) A measure of the anti-knock properties of a fuel taken as the percentage by volume of iso-octane in the fuel. （辛烷值）以燃料中异辛烷的体积百分比表示的燃料抗爆性能的量度。 |
| Intermediate annealing | 中间退火 |
Annealing wrought metals at one or more stages during manufacture and before final treatment. 在制造过程中和最终处理之前的一个或多个阶段对锻造金属进行退火。 |
| Proof strength (Unit Pa) | 验证强度（单位Pa） |
(proof stress, Rp, Rp,) The yield strength (offset yield strength) at some fixed value of the permanent strain given by the intersection of a line offset from, but parallel to, the elastic loading line and the engineering stress-engineering strain curve. The offset is arbitrary but is usually 0.1, 0.2, or 0.5% permanent strain (the proof strain). Used for materials which do not exhibit a sharply defined yield point. The notation Rp0.2 or Rp0.2 is employed for the 0.2% proof stress. （验证应力，Rp）在永久应变的某个固定值下的屈服强度（偏移屈服强度），由偏离但平行于弹性加载线的线与工程应力-工程应变曲线的交点给出。偏移是任意的，但通常为0.1、0.2或0.5%的永久应变（验证应变）。用于没有明确定义屈服点的材料。对于0.2%的验证应力，采用符号Rp0.2。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Angle of torsion | 扭转角 |
(angle of twist) (Unit ° or rad) The angle relative to a chosen section, normal to the axis of twist, through which another part of a component rotates when subjected to a torque. （扭转角）（单位°或弧度）相对于选定截面的角度，垂直于扭转轴，部件的另一部分在受到扭矩时通过该角度旋转。 |
| Hysteresis | 滞后 |
The phenomenon of permanently absorbed or lost energy that occurs during any cycle of loading or unloading when a material is subjected to repeated loading. 当材料经受重复加载时，在任何加载或卸载循环期间发生的永久吸收或损失能量的现象。 |
| Graham’s laws | 格雷厄姆定律 |
The laws stating that the rates of diffusion and effusion of a gas are inversely proportional to the square root of its density. 规定气体的扩散和渗出速率与其密度的平方根成反比的定律。 |
| Congruent melting point (Unit K) | 全等熔点（单位K） |
congruent melting point (Unit K) The temperature at which a solid substance at a specified pressure changes phase to a liquid of identical composition. 一致的熔点（单位K）固体物质在特定压力下相变为具有相同成分的液体时的温度。 |
| Total heat (Unit kJ) | 总热量（单位kJ） |
An alternative term for enthalpy. It is inappropriate as it suggests that it includes kinetic energy in the same way as total enthalpy, but it does not. Also, heat and enthalpy are quite different quantities, as their definitions show. 焓的另一个术语。这是不恰当的，因为它表明，它包括动能的方式与总焓相同，但它实际上并不是的。此外，热和焓是完全不同的量，正如它们的定义所示。 |
| Impact strength 1. (Unit Pa) | 冲击强度1.（单位Pa） |
The stress to cause failure (by yielding or fracture) under conditions of high strain rate. 2. (Unit J) A term sometimes used to describe the energy required to fracture a specimen in a Charpy or Izod impact test even though the unit is not that of strength. 在高应变率条件下导致失效（通过屈服或断裂）的应力。2.（单位J）有时用于描述在夏比或悬臂梁式冲击试验中使样品断裂所需的能量，即使单位不是强度单位。 |
| Austenite-stabilizer | 奥氏体稳定剂 |
Alloying element expanding the γ-phase field in the corresponding phase diagram, which manifests itself in a decrease of the A3 temperature and an increase of the A4 temperature in binary alloys Fe–M as well as in a decrease of A1 temperature in ternary alloys Fe–C–M (M is an alloying element). The solubility of austenite-stabilizers in ferrite is much lower than in austenite. Under the influence of austenite-stabilizers, austenite can become thermodynamically stable down to room temperature. 合金元素扩展了相应相图中的γ相场，这表现为二元合金Fe-M中A3温度的降低和A4温度的升高，以及A1温度的降低三元合金Fe–C–M（M是合金元素）。奥氏体稳定剂在铁素体中的溶解度远低于在奥氏体中的溶解度。在奥氏体稳定剂的影响下，奥氏体可以在低至室温时变得热力学稳定。 |
| Calorie | 卡路里 |
(cal, gram calorie, small calorie) An obsolete (i.e. non-SI) unit of energy equal to 4.186 8 J. It is the amount of energy needed to raise the temperature of 1 gram of pure airfree water from 14.5°C to 15.5°C at standard atmospheric pressure. （卡，克热量，小热量）一种已被淘汰的（即非SI）能量单位，等于4.1868J。它是在标准大气压力下将1克纯无空气水的温度从14.5℃升高到15.5℃所需的能量。 |
| Accelerated testing | 加速测试 |
A type of testing, for rates of wear, fatigue, corrosion etc., in which failure times are reduced by employing greater loads, more frequent power cycling, higher vibration levels, higher humidity, higher temperatures, greater potential differences etc. than would be encountered in normal operation. 一种测试类型，用于测试磨损率、疲劳率、腐蚀率等，通过采用比正常运行中更大的负载、更频繁的功率循环、更高的振动水平、更高湿度、更高温度、更大的电位差等，减少故障时间。 |
| Interrupted quenching | 间断淬火 |
A quenching procedure in which the workpiece is removed from the first quench at a temperature substantially higher than that of the quenchant and is then subjected to a second quenching system having a different cooling rate than the first. 在该淬火过程中，工件在显著高于淬火剂的温度下从第一次淬火中取出，然后经受具有不同于第一次淬火的冷却速率的第二次淬火系统。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Slack quenching | 欠速淬火 |
The incomplete hardening of steel due to quenching from the austenitizing temperature at a rate slower than the critical cooling rate for the particular steel, resulting in the formation of one or more transformation products in addition to martensite. 由于从奥氏体化温度以低于特定钢临界冷却速度的速度淬火而导致钢的不完全硬化，导致除马氏体外还形成一种或多种相变产物。 |
| Fin | 翼 |
A thin projecting rib. 一根细长的凸肋。 |
| Starting torque (Unit N.m) | 起动扭矩（单位：N.m） |
The torque developed by a motor at zero rotational speed in order to initiate rotation of the applied load. 电机在零转速下产生的扭矩，以启动所施加负载的旋转。 |
| Joint diagrams | 接合处关系图 |
Mathematical diagrams which illustrate the forces on and deflections of fasteners and joint members. 说明紧固件和连接件上的力和变形的数学图。 |
| Elasticity | 弹性 |
The property of a material by virtue of which deformation caused by stress disappears on removal of the stress. A perfectly elastic body completely recovers its original shape and dimensions after release of stress. 一种材料的特性，通过这种特性，由应力引起的变形在去除应力后消失。完全弹性体在应力释放后完全恢复其原始形状和尺寸。 |
| Vapour | 蒸气 |
The gas-like phase of a substance at a temperature below its critical point. A vapour can be condensed to a liquid or a solid by increasing its pressure or reducing its temperature. 温度低于临界点的物质的类气相。蒸汽可以通过增加压力或降低温度冷凝成液体或固体。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| B-basis | B-基础 |
Mechanical property value above which at least 90% of the population of values is expected to fall, with a confidence of 95%. 机械性能值超过该值时，至少90%的值预计会下降，置信度为95%。 |
| Hardness profile | 硬度分布 |
Hardness as a function of distance from a fixed reference point (usually from the surface). 硬度作为距固定参考点（通常距表面）的距离的函数。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| T-slot | T型槽 |
A recessed or undercut slot made with a special T shaped cutter in the tables of machine tools to receive the square head of a T bolt for clamping workpiece. 在机床工作台上用一种特殊的T形刀具制成的凹槽或底切槽，用于容纳T形螺栓的方头，用于夹紧工件。 |
| Continuous precipitation | 连续沉淀 |
Precipitation from a supersaturated solid solution in which the precipitate particles grow by longrange diffusion without recrystallization of the matrix. Continuous precipitates grow from nuclei distributed more or less uniformly throughout the matrix. They usually are randomly oriented, but may form a Widmanstätten structure. 来自过饱和固溶体的沉淀，其中沉淀颗粒通过长程扩散生长而无需基质再结晶。连续析出物从在整个基体中或多或少均匀分布的核生长而来。它们通常是随机取向的，但可能形成魏氏结构。 |
| Thermal compressor | 热压缩机 |
1. (thermocompressor) A jet compressor used to boost the pressure of low-pressure waste or exhaust steam. 2. A device consisting of an absorber, a generator, a pump, and a throttling device, used instead of a mechanical vapour compressor in an absorption-cooling refrigeration system. 1.（热压缩机）用于提升低压废蒸汽或排气压力的喷射压缩机。2.一种由吸收器、发电机、泵和节流装置组成的装置，用于替代吸收冷却制冷系统中的机械蒸汽压缩机。 |
| Swept volume (Unit m³) | 扫描体（单位m³) |
In the cylinder of a piston engine or other device, the volume between top and bottom dead centre positions of a piston; equal to πR2S where R is the piston radius and S is the stroke. 在活塞发动机或其他装置的气缸中，活塞上止点和下止点位置之间的体积；等于πR2S，其中R是活塞半径，S是冲程。 |
| Maximum continuous load | 最大连续负载 |
(maximum continuous rating) (Unit kg/s) The maximum rate of steam output that a boiler can supply for a specified period, usually 24 hours. （最大连续额定功率）（单位为kg/s）锅炉在规定时间内（通常为24小时）可供应的最大蒸汽输出率。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Torsion | 扭矩 |
A twisting deformation of a solid body about an axis in which lines that were initially parallel to the axis become helices. The twisting of an object about an axis due to an applied couple (torque). 一种固体绕轴的扭转变形，在该变形中，最初平行于轴的线变成螺旋线。由于施加的力偶（扭矩），物体绕轴扭曲。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Precipitation-hardenable stainless steels | 沉淀硬化不锈钢 |
Precipitation-hardenable stainless steels contain typically 11–18% chromium, 3–10% nickel, 0.05–0.2% carbon, and small additions of manganese, silicon, aluminium, molybdenum, niobium and titanium. These steels can be supplied in a solution-treated condition, which is readily fabricated or machined, and then hardened by an ageing treatment that produces a fine dispersion of second-phase precipitates. They are available in austenitic, semi-austenitic, and martensitic grades. Uses include springs, knives, and pressure vessels. 沉淀硬化不锈钢通常含有11-18%的铬、3-10%的镍、0.05-0.2%的碳以及少量添加的锰、硅、铝、钼、铌和钛。这些钢可在固溶处理条件下供应，该条件易于制造或机加工，然后通过时效处理硬化，从而产生细小的第二相沉淀。它们有奥氏体、半奥氏体和马氏体等级。用途包括弹簧、刀具和压力容器。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Computer vision | 计算机视觉 |
The digitization and processing of optical images/patterns by computer in order to recognize parts, orientation, etc. in manufacturing. 通过计算机对光学图像/图案进行数字化和处理，以在制造过程中识别零件、方向等。 |
| Dimensioning | 尺寸标注 |
The specification on an engineering drawing of the size (e.g. length, radius, angle, or spacing) and the relative location (e.g. angular position) of each feature of a component. The numerical values often include the tolerances. There should be no more dimensions than are necessary to manufacture the component. 工程图纸上对部件每个特征的尺寸（例如长度、半径、角度或间距）和相对位置（例如角位置）的规范。数值通常包括公差。尺寸不应超过制造组件所需的尺寸。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Elastic recovery | 弹性恢复 |
Amount the dimension of a stressed elastic material returns to its original (unstressed) dimension on release of an applied load. In hardness testing, the shortening of the original dimensions of the indentation upon release of the applied load. 在释放施加的载荷时，受应力弹性材料的尺寸恢复到其原始（无应力）尺寸的量。在硬度测试中，当释放所施加的载荷时，压痕的原始尺寸缩短。 |
| Creep modulus (Unit Pa) | 蠕变模量（单位Pa） |
The ratio of stress/strain at a chosen strain level obtained from creep tests, often plotted against time to show changes in stiffness. 从蠕变测试中获得的选定应变水平下的应力/应变比，通常随时间绘制以显示刚度的变化。 |
| Charles law/Charles' law | 查尔斯定律 |
(Gay–Lussac law) The volume of a fixed mass of gas at constant pressure is proportional to its absolute temperature. The volume of a gas at constant pressure is directly proportional to its absolute temperature. （盖-吕萨克定律）在恒定压力下，固定质量气体的体积与其绝对温度成正比。恒压下气体的体积与其绝对温度成正比。 |
| Yield stress | 屈服应力 |
The stress level of highly ductile materials, such as structural steels, at which large strains take place without further increase in stress. 高韧性材料（如结构钢）的应力水平，在该应力水平下发生大应变而不会进一步增加。 |
| Freezing point | 冰点 |
The temperature at which a substance changes phase (or state) from liquid to solid. The freezing point for most substances increases as pressure increases. The reverse process, from solid to liquid, is melting; melting point is the same as freezing point. 物质从液态变为固态的温度。大多数物质的冰点随着压力的增加而增加。从固体到液体的逆过程是熔化；熔点与凝固点相同。 |
| Notch brittleness | 缺口脆性 |
Susceptibility of a material to brittle fractureat points of stress concentration. For example, in a notch tensile test, the material is said to be notch brittle if the notch strengthis less than the tensile strength of an unnotched specimen. Otherwise, it is said to be notch ductile. 材料在应力集中点易发生脆性断裂。例如，在缺口拉伸试验中，如果缺口强度小于无缺口试样的抗拉强度，则称材料为缺口脆性材料。否则，称其为缺口韧性。 |
| Constant-velocity universal joint | 等速万向节 |
(CV joint, homokinetic joint) A connexion that transmits constant angular velocity between two shafts that are neither necessarily in line nor whose axial position is necessarily fixed. （CV关节，匀速关节）在两个轴之间传递恒定角速度的连接，这两个轴既不必在一条直线上，也不必固定其轴向位置。 |
| Induction tempering | 感应回火 |
Tempering of steel using low-frequency electrical induction heating. 钢的回火采用低频电感应加热。 |
| Range of stress (Sr) | 应力范围（Sr） |
The algebraic difference between the maximum and minimum stress in one cycle—that is, Sr = Smax – Smin 一个循环中最大和最小应力之间的代数差，即Sr=Smax–Smin |
| Computer control | 电脑控制 |
The control of an engineering device or system by pre-programmed computer or by feedback control. 通过预编程计算机或反馈控制对工程设备或系统进行控制。 |
| Kinetic energy | 动能 |
Energy that an object possesses because it is in motion. It is the energy given to an object to set it in motion. On impact, it is converted into other forms of energy such as strain, heat, sound and light. 物体因运动而拥有的能量。它是赋予物体使其运动的能量。撞击时，它被转换成其他形式的能量，如应变、热、声和光。 |
| Remaining stress | 残留应力 |
The stress remaining at a given time during a stress-relaxation test. See also stress relaxation. 在应力松弛试验期间在给定时间内剩余的应力。参见压力松弛。 |
| Normal stress (Unit N) | 法向应力（单位：N） |
The stress component perpendicular to a plane on which forces act. Normal stress may be either tensile stress or compressive stress. A stress in a fluid (such as pressure) or a solid, that is perpendicular to the surface on which it acts. The surface may be a real external surface or an imaginary internal one. 垂直于受力平面的应力分量。法向应力可以是拉应力或压应力。流体（如压力）或固体中垂直于其作用表面的应力。该表面可以是真实的外表面或假想的内表面。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Imperial system | 英制单位体系 |
The units of measurement developed in the UK. Formerly known as the fps system, which is an abbreviation for the ‘foot-pound-second system of units. 英国开发的计量单位。以前称为fps系统，是“英尺-磅-秒（foot-pound-second）单位制”的缩写。 |
| Scratch hardness | 划痕硬度 |
The resistance of a material, such as a metal, alloy, plastic, or mineral, to scratching by a much harder indenter, such as a diamond stylus, moved slowly across the surface. The scratch hardness number is computed from the loads and the dimensions of the residual scratch. 一种材料（如金属、合金、塑料或矿物）对更硬的压头（如金刚石触针）划伤的抵抗力，在表面上缓慢移动。根据载荷和残余划痕的尺寸计算划痕硬度值。 |
| Turbomachine | 涡轮机械 |
(rotodynamic machine) A machine in which there is a transfer of energy between a continuous stream of fluid and a component, called a rotor, rotating about a fixed axis. Fans and turbines (gas, hydraulic, steam, or wind) are turbomachines in which energy is transferred to the rotor, causing it to rotate. Pumps and compressors are turbomachines in which energy is transferred from the externally driven rotor to the fluid. （旋转动力机器）在连续的流体流和绕固定轴旋转的部件（称为转子）之间进行能量传递的机器。风扇和涡轮机（燃气、液压、蒸汽或风力）是涡轮机械，其中能量传递到转子，使其旋转。泵和压缩机是涡轮机械，其中能量从外部驱动的转子传递到流体。 |
| Angle of contact | 接触角 |
(Unit °) The angle subtended at the centre of a pulley or sprocket wheel by the circumferential contact of a belt or chain. （单位°）皮带或链条的圆周接触在皮带轮或链轮的中心所对的角度。 |
| Trepanning | 开孔 |
Trepanning is a machining process for producing a circular hole or groove in solid stock, or for producing a disk, cylinder, or tube from solid stock, by the action of a tool containing one or more cutters (usually single-point) revolving around a center. 开孔是一种机械加工工艺，通过包含一个或多个围绕中心旋转的刀具（通常为单点）的作用，在实心坯料中制造圆孔或凹槽，或从实心坯料生产圆盘、圆柱体或管。 |
| Clevis | U形夹 |
A U-shaped hook with holes at the ends through which a retaining bolt or pin (clevis pin) passes. 一种U形钩，末端有孔，固定螺栓或销（U形销）穿过这些孔。 |
| Hypoeutectic alloy | 亚共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of base metal compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，其成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Hot strength (Unit Pa) | 热强度（单位Pa） |
The yield stress (or sometimes fracture stress) of a material at temperatures above about half its melting point in kelvins. 材料在高于其熔点一半（以开尔文为单位）的温度下的屈服应力（有时为断裂应力）。 |
| Controlled cooling | 控制冷却 |
Cooling from an elevated temperature in a predetermined manner, to avoid hardening, cracking, or internal damage, or to produce desired microstructure or mechanical properties. 以预定方式从升高的温度冷却，以避免硬化、开裂或内部损坏，或产生所需的微观结构或机械性能。 |
| Blueing | 发蓝 |
Application of blue dye (‘engineers’ blue’) to identify high spots on surfaces in contact, or for marking out. 应用蓝色染料（“工程师蓝”）来识别接触表面上的高点，或用于标记。 |
| Load and resistance factor design | 负载和阻力系数设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Assigns uncertainties in the strength of (i.e., resistance of) and in the service loads to be placed on a shear joint to estimate the probable strength of the joint. It is a recently defined alternative to the Allowable stress design procedure. 结构连接研究委员会为AISC制定的设计程序。分配剪切接头的强度（即阻力）和工作荷载的不确定性，以估计接头的可能强度。它是最近定义的容许应力设计程序的替代方案。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Impact wrench | 冲击扳手 |
An air- or electric-powered wrench in which multiple blows from tiny hammers are used to produce output torque to tighten fasteners. A pneumatically-or electrically-powered socket wrench used to tighten or loosen nuts through the application of torque in a rapid series of impulses. 一种气动或电动扳手，使用小锤子多次敲击来产生输出扭矩以拧紧紧固件，用于通过在一系列快速脉冲中施加扭矩来拧紧或松开螺母。 |
| Bolt blank | 螺栓毛坯 |
A rod on which a head has been formed, but on which no thread has been cut, from which bolts or screws may be made as required. 一种已形成头部但未切割螺纹的杆，可根据需要从中制造螺栓或螺钉。 |
| Morse taper | 莫氏锥度 |
A self holding, standard taper largely used on drilling tools, drilling machine spindles, and some lathes. 一种自持式标准锥度，主要用于钻孔工具、钻床主轴和一些车床。 |
| Elastic limit | 弹性极限 |
The maximum stress which a material is capable of sustaining without any permanent strain (deformation) remaining on complete release of the stress. 材料在完全释放应力时能够承受的最大应力，且不会留下任何永久应变（变形）。 |
| Torricellean barometer | 托里塞莱气压计 |
A vertical glass tube with its upper end sealed and the lower end submerged in a pool of mercury. The space above the mercury is under vacuum. The height to which the mercury rises up the tube is a measure of the barometric pressure. 一种垂直的玻璃管，上端密封，下端浸入汞池中。水银上方的空间处于真空状态。水银在管道中上升的高度是大气压力的量度。 |
| Fatigue striations | 疲劳条纹 |
Parallel lines frequently observed in electron microscope fractographs or fatigue-fracture surfaces. The lines are transverse to the direction of local crack propagation; the distance between successive lines represents the advance of the crack front during the one cycle of stress variation. 在电子显微镜断口图或疲劳断口表面中经常观察到平行线。这些线横向于局部裂纹扩展方向；连续线之间的距离表示在一个应力变化周期内裂纹前沿的前进。 |
| Bioengineering | 生物工程 |
(biological engineering) The application of engineering principles to biology, medicine, agriculture, etc. （生物工程）工程原理在生物学、医学、农业等方面的应用。 |
| Coining | 压印 |
A forging operation, employing a closely-fitting punch and die from which no metal is allowed to escape, in which the surface pattern on the punch and die is imprinted on the blank. 一种锻造操作，采用紧密配合的凸模和模具，不允许金属逸出，其中凸模和模具上的表面图案印在坯料上。 |
| Double-shear test | 双剪试验 |
A shear test having two stationary, shear blades and one moving one and that uses solid round bars as test specimens. 一种剪切试验，具有两个固定的剪切刀片和一个移动的刀片，并使用实心圆棒作为试样。 |
| Forging | 锻造处理 |
The process of forming raw steel into specified shapes. Some examples of forged products would be hex bolts, clevises, and barrier pins. 1. A method of component manufacture by hammering metal by hand or by machine (drop forge, press). 2. A part made by the process of forging. 将生钢制成特定形状的过程。锻造产品的一些例子是六角螺栓、U形夹和障碍销。 1. 一种通过手工或机器锤击金属（落锻、压力机）制造部件的方法。2.通过锻造工艺制成的零件。 |
| Spanner (wrench) | 扳手 |
A tool for applying torque to tighten or loosen a nut, bolt, or screw. Grip is applied by a serrated ring or an open U-shape at the end of the tool. On imperial-size spanners, the BSW and BSF marking refers to the diameter of the screw thread; similarly for BA spanners. Spanners for unified and metric threads are marked with the distance across the flats (‘A/F’) of the nut or head of the bolt. 拧紧或松开螺母、螺栓或螺丝的工具。通过工具端部的锯齿环或开口U形应用夹持。在英制扳手上，BSW和BSF标记是指螺纹的直径；类似于BA扳手。用于统一螺纹和公制螺纹的扳手在螺母或螺栓头的平面（'A/F'）上标记距离。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Macrodeviation | 宏观偏差 |
Errors from–irregular surface departures from the design profile, often caused by lack of accuracy or stiffness of the machine system. 不规则表面偏离设计轮廓的误差，通常是由于机器系统缺乏准确性或刚度造成的。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Torsion bar | 扭杆 |
A metal bar designed to act as an elastic spring when torque is applied. 当施加扭矩时用作弹性弹簧的金属棒。 |
| Granular fracture | 粒状断裂 |
A type of irregular surface produced when metal is broken that is characterized by a rough, grainlike appearance, rather than a smooth or fibrous one. It can be subclassified as transgranular or intergranular. 金属破碎时产生的一种不规则表面，其特征是粗糙的颗粒状外观，而不是光滑或纤维状的外观。它可以细分为穿晶或晶间。 |
| Dynamic load rating (Unit N) | 额定动载荷（单位N） |
The allowable load on a component or structure when the loading is not static. 当负载不是静态时，组件或结构上的允许负载。 |
| Degree (°) | 度数（°） |
A measure of plane angle such that 1° is 1/360 of a complete revolution and equal to π/180 rad. 平面角度的一种度量，使得1°是一整圈的1/360，等于π/180弧度。 |
| Modulus of elasticity (E) | 弹性模量（E） |
The measure of rigidity or stiffness of a metal; the ratio of stress, below the proportional limit, to the corresponding strain. In terms of the stress-strain diagram, the modulus of elasticity is the slope of the stress-strain curve in the range of linear proportionality of stress to strain. 金属的刚度或刚度的量度；低于比例极限的应力与相应应变之比。根据应力应变图，弹性模量是应力应变曲线在应力应变线性比例范围内的斜率。 |
| Dynamic coupling | 动态耦合 |
In vibrations, the existence of inertial terms depending on mass in the governing equations, so that there is only a force if there is a corresponding acceleration. 在振动中，惯性项的存在取决于控制方程中的质量，因此只有当有相应的加速度时才有力。 |
| Computational domain | 计算域 |
In CFD, FEM, and other numerical methods, the area or volume within which calculations are performed and on the periphery of which the boundary conditions are specified. 在CFD、FEM和其他数值方法中，执行计算的区域或体积以及在其外围指定边界条件的区域或体积。 |
| Newton’s law of viscosity | 牛顿内摩擦定律 |
The shear stress between two parallel layers of fluid is proportional to the velocity of one relative to that of the other, and inversely proportional to the distance between them. The constant of proportionality is the dynamic viscosity μ. For a Newtonian fluid μ is independent of pressure gradient, shear stress, and strain, but may change with temperature and pressure. 两个平行流体层之间的剪切应力与其中一层相对于另一层的速度成正比，与它们之间的距离成反比。比例常数是动态粘度μ。对于牛顿流体，μ与压力梯度、剪切应力和应变无关，但可能随温度和压力而变化。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Spring load (Unit N) | 弹簧载荷（单位：N） |
A load exerted on a component by bending, compressing, extending, or twisting an attached spring. Mechanical energy stored in the spring can be released if any constraints on the component are removed. 通过弯曲、压缩、延伸或扭转连接的弹簧而施加在部件上的载荷。如果部件上的任何约束被移除，则可以释放弹簧中存储的机械能。 |
| Centrifuge | 离心机 |
A machine incorporating a rapidly spinning drum in which liquids and suspended particles of different densities are separated by centrifugal action. 一种装有快速旋转滚筒的机器，在该滚筒中，不同密度的液体和悬浮颗粒通过离心作用分离。 |
| Peel strength (Unit N) | 剥离强度（单位：N） |
(peel test) The strength of an adhesive bond between two materials as measured by the force required in a given direction to peel apart adhered strips. This force depends on the dimensions and thickness of the adhered strips and their yield stress, together with the fracture toughness of the bond. （剥离试验）两种材料之间的粘合强度，通过给定方向上剥离粘合条所需的力来测量。该力取决于粘合条的尺寸和厚度及其屈服应力，以及粘合剂的断裂韧性。 |
| Mass flow rate (ṁ) (Unit kg/s) | 质量流量（ṁ）（单位kg/s） |
The mass of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. The corresponding mass flux (ṁ″), with unit kg/s.m², is the mass flow across a real surface or through a duct, divided by the surface or cross-sectional area A, i.e. ṁ″ = ṁ/A or ṁ″ = ρV where ρ is the material density and V is its velocity normal to the surface. 单位时间内流过表面或通过管道或其他管道的材料质量，通常是流体或粉末。相应的质量通量（ṁ″），单位为kg/s.m²，是通过真实表面或通过管道的质量流量除以表面或横截面积A，即ṁ″=ṁ/A或ṁ″=ρV，其中ρ是材料密度，V是其垂直于表面的速度。 |
| Mohs hardness test | 莫氏硬度测试 |
A scratch hardness test for determining comparative hardness using 10 standard minerals—from talc (the softest) to diamond (the hardest). 刮擦硬度测试，用于使用从滑石（最软）到钻石（最硬）的10种标准矿物测定比较硬度。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| Notch ductility | 缺口延展性 |
The percentage reduction in area after complete separation of the metal in a tensile test of a notched specimen. 在缺口试样的拉伸试验中，金属完全分离后的面积减少百分比。 |
| High-tensile bolt | 高强度螺栓 |
(high-tension bolt) A bolt manufactured from an alloy steel that has a high tensile strength of about 1 GPa. （高压螺栓）由合金钢制成的螺栓，具有约1GPa的高抗拉强度。 |
| Wind pump | 风泵 |
A pump driven directly by a windmill on a tower. Widely used in remote locations. 由塔上的风车直接驱动的泵。广泛应用于偏远地区。 |
| Stress corrosion cracking (SCC) | 应力腐蚀开裂（SCC） |
A common form of Stress cracking in which an Electrolyte encourages the growth of a crack in a highly stressed bolt. Only a tiny quantity of electrolyte need be present, at the tip or face of the crack. A time-dependent process in which a metallurgically susceptible material fractures prematurely under conditions of simultaneous corrosion and sustained loading at lower stress levels than would be required in the absence of a corrosive environment. Tensile stress is required at the metal surface and may be a residual stress resulting from heat treatment or fabrication of the metal or the result of external loading. Cracking may be intergranular or transgranular, depending on the combination of alloy and environment. 一种常见的应力开裂形式，其中电解液促使高应力螺栓中的裂纹扩展。在裂纹尖端或表面，只需存在少量电解质。一种随时间变化的过程，其中冶金敏感材料在同时腐蚀和持续加载的条件下过早断裂，其应力水平低于无腐蚀环境时的要求。在金属表面需要拉应力，拉应力可以是金属的热处理或制造或外部负载产生的残余应力。裂纹可能是沿晶开裂或穿晶开裂，这取决于合金和环境的组合。 |
| Condensate strainer | 冷凝水过滤器 |
A filter in a steam plant used to remove particulate matter from condensate before it is added to feedwater. 蒸汽设备中的过滤器，用于在将冷凝水添加到给水中之前去除冷凝水中的颗粒物。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Standard gauge | 标准量规 |
A highly-accurate reference gauge against which to check working gauges. 一种高精度的基准量规，用于检查工作量规。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Twist drill | 麻花钻 |
A hardened-steel drill bit having one or more helical flutes running from a conical tip to the smooth part of the shank. 一种淬火钢钻头，具有一个或多个螺旋槽，从锥形尖端延伸到柄部的光滑部分。 |
| Electroplating | 电镀 |
Deposition of one metal on to another using electrolysis. The metal to be plated forms the cathode in an electrolytic cell, and the metal to be deposited forms the anode. 使用电解将一种金属沉积到另一种金属上。待镀金属形成电解池中的阴极，待沉积金属形成阳极。 |
| Impact extrusion | 冲击挤压 |
The extrusion of separate components of soft metals whose properties permit the action to be performed quickly. 挤压单独的软金属组件，其特性允许快速执行操作。 |
| Breaking load (Unit N) | 断裂负荷（单位N） |
The load applied at some point to a component or structure which leads to fracture. The breaking stress (breaking strength) is the average stress at which a member breaks, given by the breaking load divided by the area over which it acts. 在某个点施加到导致断裂的部件或结构的载荷。断裂应力（断裂强度）是构件断裂时的平均应力，由断裂载荷除以其作用的面积给出。 |
| Terminal velocity (Unit m/s) | 终端速度（单位：m/s） |
The velocity reached by an object in free fall through a fluid when the upward drag and buoyancy forces just balance the object’s weight. For an object with a density lower than that of the fluid, the terminal velocity is vertically upwards. 当向上的阻力和浮力正好平衡物体的重量时，物体自由下落通过流体达到的速度。对于密度低于流体密度的物体，终端速度垂直向上。 |
| Bernoulli’s law | 伯努利定律 |
For a steadily flowing fluid (liquid or gas), the sum of the pressure, kinetic energy per unit volume and potential energy per unit volume is constant at any point in the fluid. Using this relationship, it is possible to measure the velocity of a fluid by measuring its pressure at two points, as with a manometer or Pitot tube. 对于稳定流动的流体（液体或气体），压力、每单位体积的动能和每单位体积的势能之和在流体中的任何点都是恒定的。使用这种关系，可以通过在两个点测量流体的压力来测量流体的速度，就像使用压力计或皮托管一样。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Vapour static pressure | 蒸汽静压 |
(Unit Pa or bar) A pressure analogous to hydrostatic pressure, where the fluid is a vapour such as steam. A term used in geothermal applications. （单位Pa或bar）类似于静水压力的压力，其中流体是蒸汽，如蒸汽。地热应用中使用的术语。 |
| Mole (mol) | 摩尔（mol） |
The base unit of the amount of substance in the SI system. It was previously defined as the amount of substance of a system that contains as many elementary entities as there are atoms in 0.012 kg of carbon-12. From 20 May 2019 it has been defined as the amount of substance containing exactly 6.022 140 76 × 1023 elementary entities. SI国际单位制中物质量的基本单位。此前，它被定义为一个系统中的物质量，该系统包含的基本实体数量与0.012千克碳-12中的原子数量相同。从2019年5月20日起，它已被定义为包含6.02214076×1023个基本实体的物质量。 |
| Net weight (Unit N) | 净重（单位：N） |
The difference between the gross weight of any container including its contents and the tare weight of the empty container. 任何容器（包括其内容物）的毛重与空容器皮重之间的差值。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Fatigue crack growth rate (da/dN) | 疲劳裂纹扩展率（da/dN） |
The rate of crack extension caused by constant-amplitude fatigue loading, expressed in terms of crack extension per cycle of load application. 恒幅疲劳荷载引起的裂纹扩展速率，以每次荷载施加循环的裂纹扩展表示。 |
| Transmission dynamometer | 传动测功机 |
A dynamometer in which the power transmitted by a shaft is obtained from the product of its rotation speed and the torque determined from measured shear strains along the shaft. 一种测功机，其中轴传递的功率由其转速和扭矩的乘积获得，扭矩由沿轴测得的剪切应变确定。 |
| Wrinkling | 起皱 |
A wavy condition obtained in deep drawing of sheet metal, in the area of the metal between the edge of the flange and the draw radius. Wrinkling may also occur in other forming operations when unbalanced compressive forces are set up. 在金属板深冲过程中，在法兰边缘和拉深半径之间的金属区域内获得的波浪状状态。当设置不平衡压缩力时，在其他成形操作中也可能发生起皱。 |
| Shear strength (Unit Pa) | 抗剪强度（单位Pa） |
The maximum shear stress that can be withstood by a material either (a) before plasticity occurs or (b) before rupture. 材料在（a）塑性发生之前或（b）断裂之前能够承受的最大剪切应力。 |
| Shell hardening | 壳型硬化 |
A surface-hardening process in which a suitable steel workpiece, when heated through and quench hardened, develops a martensitic layer or shell that closely follows the contour of the piece and surrounds a core of essentially pearlitic transformation product. This result is accomplished by a proper balance among section size, steel hardenability, and severity of quench. 一种表面硬化工艺，在该工艺中，合适的钢工件在加热和淬火硬化后，会形成一层马氏体层或壳，该层或壳紧随工件的轮廓，并包围一个基本上为珠光体相变产物的核心。这一结果通过截面尺寸、钢淬透性和淬火强度之间的适当平衡来实现。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Fracture surface | 断裂面 |
The irregular surface produced when a piece of metal is broken. 一块金属破碎时产生的不规则表面。 |
| Solenoid | 螺线管 |
A coil of electrically-conducting wire wrapped around a metal core, typically iron, to produce a magnetic field and hence a force on the core when an electric current passes through the coil. Solenoids are widely used to produce linear movement to actuate valves (solenoid valves) and other devices. 绕在金属芯（通常为铁）上的导线线圈，当电流通过线圈时产生磁场，从而在芯上产生力。电磁阀广泛用于产生线性运动以驱动阀（电磁阀）和其他装置。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Thermocouple | 热电偶 |
A device for measuring temperature, consisting of lengths of two dissimilar metals or alloys that are electrically joined at one end and connected to a voltage-measuring instrument at the other end. When one junction is hotter than the other, a thermal electromotive force is produced that is roughly proportional to the difference in temperature between the hot and cold junctions. 一种测量温度的装置，由两种不同的金属或合金组成，一端电连接，另一端与电压测量仪相连。当一个结比另一个结更热时，产生的热电动势大致与热结和冷结之间的温差成比例。 |
| Endurance | 耐力 |
The capacity of a material to withstand repeated application of stress. 材料承受反复施加应力的能力。 |
| Elastic resilience | 弹性回弹 |
The amount of energy absorbed in stressing a material up to the elastic limit; or, the amount of energy that can be recovered when stress is released from the elastic limit. 向材料施加应力直至弹性极限所吸收的能量；或者当应力从弹性极限释放时可以恢复的能量值。 |
| Supercharging | 增压 |
The process of increasing the mass flow rate of air (or air/fuel mixture) into the cylinder(s) of a piston engine using a compressor driven from the crankshaft (the supercharger). The power output is increased compared with a naturally-aspirated engine of the same capacity. The process also increases the air pressure and density to greater than ambient. In the past, most superchargers were mechanically driven from the engine’s crankshaft, but these have been largely superseded by turbochargers. 使用由曲轴（增压器）驱动的压缩机增加进入活塞式发动机气缸的空气（或空气/燃料混合物）质量流率的过程。与相同容量的自然吸气发动机相比，功率输出增加。该过程还将空气压力和密度增加到大于环境压力和密度。在过去，大多数增压器都是由发动机曲轴机械驱动的，但这些增压器在很大程度上已被涡轮增压器所取代。 |
| Computer-aided manufacturing | 计算机辅助制造 |
(CAM, computer-integrated manufacturing, CIM) The use of computers in all branches of manufacturing, not only to control machines and robots for manufacturing and assembly, but also for process planning, and monitoring progress of materials and components during production, etc. （CAM，计算机集成制造，CIM）在制造的所有分支中使用计算机，不仅可以控制制造和组装的机器和机器人，还可以进行工艺规划，以及在生产过程中监控材料和组件的进度等。 |
| Standard deviation (σ) | 标准偏差（σ） |
A statistical term used to quantify the Scatter in a set of data points. If the standard deviation is small, most of the data points are ‘‘nearly equal.’’ A large deviation means less agreement. The most usual measure of the dispersion of observed values or results expressed as the positive square root of the variance. The square root of variance, a measure of the spread of data about the mean value. 用于量化一组数据点中分散度的统计术语。如果标准偏差很小，则大多数数据点“几乎相等”大的偏差意味着更少的一致性。观测值或结果离散度的最常用度量，表示为方差的正平方根。方差的平方根，衡量平均值的数据分布。 |
| Principal stress (normal) | 主应力（正常） |
The maximum or minimum value of the normal stressat a point in a plane considered with respect to all possible orientations of the considered plane. On such principal planes the shear stress is zero. There are three principal stresses on three mutually perpendicular planes. The state of stress at a point may be: (1) uniaxial, a state of stress in which two of the three principal stresses are zero; (2) biaxial, a state of stress in which only one of the three principal stresses is zero; or (3) triaxial, a state of stress in which none of the principal stresses is zero. Multiaxial stress refers to either biaxial or triaxial stress. 相对于所考虑平面的所有可能方向，所考虑平面中某点处的法向应力的最大值或最小值。在这样的主平面上，剪切应力为零。在三个相互垂直的平面上有三个主应力。一点的应力状态可以是：（1）单轴，三个主应力中的两个为零的应力；（2）双轴，三个主应力中只有一个为零的应力状态；或（3）三轴，即主应力均不为零的应力状态。多轴应力是指双轴或三轴应力。 |
| Concentrated load | 集中负荷 |
A load on a component which is distributed over a very small area, idealized as the line load of a wedge or knife edge, and the point load of a cone. 分布在非常小的区域上的部件上的载荷，理想化为楔形或刀刃的线载荷和锥体的点载荷。 |
| Orange peel | 橘皮 |
A surface roughening in the form of a pebble-grained pattern where a metal of unusually coarse grain is stressed beyond its elastic limit. Also known as pebbles and alligator skin. 一种以卵石颗粒图案形式出现的粗糙化表面，其中晶粒异常粗的金属受到的应力超过其弹性极限。也称为卵石和鳄鱼皮。 |