| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Monotron hardness test | 摩诺硬度试验 |
An obsolete method of determining indentation hardnessby measuring the load required to force a spherical penetrator into a metal to a specified depth. 一种已被淘汰的方法，通过测量将球形侵彻体压入金属至规定深度所需的载荷来确定压痕硬度。 |
| Double-shear test | 双剪试验 |
A shear test having two stationary, shear blades and one moving one and that uses solid round bars as test specimens. 一种剪切试验，具有两个固定的剪切刀片和一个移动的刀片，并使用实心圆棒作为试样。 |
| Radial flow | 径向流 |
radial flow Fluid flow for which the principal direction of flow is either radially inward or radially outward relative to an axial direction. 径向流动流体流动的主要方向是径向向内或径向向外流动。 |
| Vent | 发泄 |
A small valve that allows the release of pressurized fluid from a pipe, pressure vessel, etc., often to the atmosphere. 一种小阀门，允许将加压流体从管道、压力容器等中释放到大气中。 |
| Stress cycle | 应力循环 |
The smallest segment of the stress-time function that is repeated periodically. 周期性重复的应力时间函数的最小段。 |
| Precipitation heat treatment | 沉淀热处理 |
Artificial aging in which a constituent precipitates from a supersaturated solid solution. 成分从过饱和固溶体沉淀的人工时效。 |
| Mohr–Coulomb fracture criterion | Mohr–Coulomb断裂准则 |
A fracture criterion, primarily for brittle materials, according to which failure occurs when the stress at a point in a material falls outside the envelope created by the Mohr’s circles for uniaxial tensile strength and uniaxial compressive strength. 一种断裂准则，主要适用于脆性材料，根据该准则，当材料中某一点的应力落在单轴抗拉强度和单轴抗压强度的莫尔圆所形成的包络线之外时，就会发生断裂。 |
| Fracture stress | 断裂应力 |
The true normal stress on the minimum cross-sectional area at the beginning of fracture. This term usually applies to tension tests of unnotched specimens. 断裂开始时最小横截面积上的真实正应力。该术语通常适用于无缺口试样的拉伸试验。 |
| Combined heat and power plant | 热电联产电厂 |
(CHP plant, COGEN, cogeneration plant, total-energy plant) A plant for the simultaneous production of more than one useful form of energy from the same energy source, such as process heat and electric power. In the arrangement shown, partially expanded steam is extracted from the steam turbine and used to produce process heat. （CHP工厂、COGEN、热电联产工厂、总能源工厂）从同一能源（如过程热能和电力）同时生产一种以上有用能源的工厂。在所示的布置中，部分膨胀的蒸汽从蒸汽轮机中提取并用于产生过程热量。 |
| Strain aging | 应变时效 |
The changes in ductility, hardness, yield point, and tensile strength that occur when a metal or alloy that has been cold worked is stored for some time. In steel, strain aging is characterized by a loss of ductility and a corresponding increase in hardness, yield point, and tensile strength. 已冷加工的金属或合金在储存一段时间后发生的延展性、硬度、屈服点和抗拉强度的变化。在钢中，应变时效的特点是延性损失，硬度、屈服点和抗拉强度相应增加。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Angle of contact | 接触角 |
(Unit °) The angle subtended at the centre of a pulley or sprocket wheel by the circumferential contact of a belt or chain. （单位°）皮带或链条的圆周接触在皮带轮或链轮的中心所对的角度。 |
| Design heating load (Unit kW) | 设计热负荷（单位kW） |
The heating requirements based on a specified number of heating degree days, or required to maintain a building or other enclosed space at a specified temperature for a given outside temperature. 基于指定的采暖度日数的加热要求，或在给定的外部温度下将建筑物或其他封闭空间保持在指定温度下所需的加热要求。 |
| Strain energy | 应变能 |
A measure of the energy absorption characteristics of a material determined by measuring the area under the stress-strain diagram. 通过测量应力-应变图下的面积确定的材料能量吸收特性的度量。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Wind pressure (Unit Pa) | 风压（单位Pa） |
The dynamic pressure associated with the wind. The static pressure of the wind is the atmospheric pressure. 与风相关的动态压力。风的静压是大气压。 |
| Metallurgy | 冶金 |
The study of the atomic, crystallographic, microstructural, mechanical, and physical properties of metallic elements and alloys and their applications. 研究金属元素和合金的原子、晶体学、微观结构、机械和物理特性及其应用。 |
| High-tensile bolt | 高强度螺栓 |
(high-tension bolt) A bolt manufactured from an alloy steel that has a high tensile strength of about 1 GPa. （高压螺栓）由合金钢制成的螺栓，具有约1GPa的高抗拉强度。 |
| Drift pin | 冲头 |
A round tapered steel pin used to align rivet holes so that the rivet will pass through the holes easily. 用于对齐铆钉孔的圆形锥形钢销，以便铆钉轻松穿过孔。 |
| Concurrent engineering | 并行工程 |
The integration of the procedures for product design, material selection and manufacturing method to include life-cycle analysis. 产品设计、材料选择和制造方法程序的整合，包括生命周期分析。 |
| Thermodynamic process | 热力学过程 |
A change in equilibrium state undergone by a quantity of matter or a system. 一定量的物质或系统所经历的平衡状态的变化。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Elbow | 肘部 |
1. A fitting that connects the ends of two pipes at an angle, 45°, 90°, and 180° being the most common. 2. The third joint on an articulated robot corresponding to the human elbow. 1.以45°、90°和180°角连接两个管道端部的配件。2.示例关节机器人上的第三关节对应于人的肘部。 |
| Swift cup test | 斯威夫特杯测试 |
A simulative cupping test in which circular blanks of various diameters are clamped in a die ring and deep drawn into cups by a flat-bottomed cylindrical punch. 一种模拟拔杯试验，将不同直径的圆形坯料夹紧在模环中，并用平底圆柱冲头将其深拉入杯中。 |
| Fastener with reduced shank | 短柄紧固件 |
Finished fastener with a shank diameter of ds ≈ d2. 柄径为ds≈d2的紧固件。 |
| Extra spring | 额外弹簧 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state above full hard beyond which further cold work will not measurably increase the strength and hardness. 有色金属合金和一些铁合金的回火状态，大约对应于高于全硬的冷加工状态，超过该状态进一步冷加工将不会显着增加强度和硬度。 |
| Volume (Unit m³) | 体积（单位m³） |
The amount of space occupied by a specified mass of substance or by an object. 一定质量的物质或物体占据的空间量。 |
| Millimetre of water | 毫米水柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of water 1 mm high. Approximately equal to 9.81 Pa. 一种非SI压力单位，等于1毫米高的垂直水柱施加的压力。大约等于9.81Pa。 |
| Design load (Unit N) | 设计荷载（单位N） |
The greatest load that a component or structure is expected to experience under normal operating conditions. 部件或结构在正常运行条件下预期承受的最大负载。 |
| Stretch forming | 拉伸成型 |
A manufacturing process in which sheet-metal components are physically stretched over a forming die using a press, punch, or edge clamps. Stretching combined with bending reduces springback. 一种制造工艺，其中使用压力机、冲头或边缘夹具在成形模上物理拉伸金属板部件。拉伸与弯曲相结合可减少回弹。 |
| Hard temper | 硬化回火 |
Same as full hard temper. 和全硬化回火一样。 |
| Pulse | 脉冲 |
An increase or decrease in the magnitude of a physical quantity, such as pressure, voltage, or force, with a time scale short compared with other time scales in a process, after which there is a return to the original level. 物理量的大小的增加或减少，如压力、电压或力，与过程中的其他时间尺度相比，时间尺度较短，之后返回到原始水平。 |
| Vice | 老虎钳 |
A workshop tool used to hold a workpiece and consisting of two jaws, one fixed and the other moved by turning a screw. 一种用于夹持工件的车间工具，由两个钳口组成，一个固定，另一个通过转动螺钉移动。 |
| Maximum load (Pmax) | 最大负载（Pmax） |
(1) The load having the highest algebraic value in the load cycle. Tensile loads are considered positive and compressive loads negative. (2)Used to determine the strength of a structural member; the load that can be borne before failure is apparent. （1）负载循环中具有最高代数值的负载。拉伸荷载视为正荷载，压缩荷载视为负荷载。（2）用于确定结构构件的强度；失效前可承受的载荷是明显的。 |
| Horizontal batch furnace | 卧式间歇炉 |
A versatile batch-type furnace that can give light or deep case depths, and because the parts are not exposed to air, horizontal batch furnaces can give surfaces almost entirely free of oxides. 一种多功能间歇式炉，可以提供浅或深的外壳深度，并且由于零件不暴露在空气中，卧式间歇式炉可以使表面几乎完全没有氧化物。 |
| Ferrite | 铁素体 |
A solid solution of one or more elements in body-centered cubic iron. Unless otherwise designated (for instance, as chromium ferrite), the solute is generally assumed to be carbon. On some equilibrium diagrams, there are two ferrite regions separated by an austenite area. The lower area is alpha ferrite; the upper, delta ferrite. If there is no designation, alpha ferrite is assumed. 一种或多种元素在体心立方铁中的固溶体。除非另有说明（例如，铁酸铬），否则通常假定溶质为碳。在一些平衡图上，有两个铁素体区域被一个奥氏体区域隔开。下部区域为α铁素体；上部，δ铁氧体。如果没有指定，则假定为 α 铁氧体。 |
| Mechatronics | 机电一体化 |
The integration of mechanical engineering, electrical engineering, electronic engineering, and software engineering. 机械工程、电气工程、电子工程和软件工程的集成。 |
| Residual strength (Unit N) | 剩余强度（单位：N） |
The strength of a damaged body containing defects induced by microcracking, thermal shock, etc. 包含由微裂纹、热冲击等引起的缺陷的受损体的强度。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Pressure (p) (Unit Pa) | 压力（p）（单位Pa） |
In thermodynamics and fluid mechanics, the compressive force exerted by the fluid per unit area. The pressure exerted by a fluid on a surface acts normal to the surface. 在热力学和流体力学中，每单位面积流体施加的压缩力。流体施加在表面上的压力垂直于表面。 |
| Least count | 最小计数 |
The smallest value that can be read from an instrument having a graduated scale. Except on instruments provided with a vernier, the least count is that fraction of the smallest division which can be conveniently and reliably estimated; this fraction is ordinarily one-fifth or one-tenth, except where the graduations are very closely spaced. 可从具有刻度尺的仪器中读取的最小值。除配备游标的仪器外，最小计数是可以方便可靠地估计的最小除法的分数；这个分数通常是五分之一或十分之一，除非刻度间隔非常近。 |
| Preload | 预载 |
The tension created in a threaded fastener when the nut is first tightened. Often used interchangeably, but incorrectly, with Working load or bolt force or bolt tension 第一次拧紧螺母时螺纹紧固件中产生的张力。经常与工作载荷或螺栓力或螺栓张力互换使用但容易使用不当。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Vacuum servo | 真空服务器 |
A vacuum-operated servomotor which is used in a motor vehicle to provide a brake effort greater than the capability of the driver. 一种真空操作的伺服电机，用于机动车中，以提供大于驾驶员能力的制动力。 |
| Radioactive heat (Unit J) | 放射性热（单位J） |
Thermal energy released from the nucleus of an atom such as uranium235 by fission due to the absorption of a neutron. Heat is also produced by radioactive decay. 铀235等原子核因吸收中子而裂变释放的热能。放射性衰变也会产生热量。 |
| Nut splitter | 螺母分离器 |
A tool for removing rusted-on and corroded nuts from bolts. It consists of a stiff steel ring that is placed around the nut. A screw thread passing through the ring bears diametrically on a wedged-shape tip that indents and cuts though a face of the nut. 从螺栓上去除锈蚀螺母的工具。它由一个围绕螺母放置的刚性钢环组成。穿过环的螺纹径向支撑在楔形尖端上，该尖端凹陷并穿过螺母的表面。 |
| Strain gage | 应变计 |
A device for measuring small amounts of strain produced during tensile and similar tests on metal. A coil of fine wire is mounted on a piece of paper, plastic, or similar carrier matrix (backing material), which is rectangular in shape and usually about 25 mm (1.0 in.) long. This is glued to a portion of metal under test. As the coil extends with the specimen, its electrical resistance increases in direct proportion. This is known as bonded resistance-strain gage. Other types of gages measure the actual deformation. Mechanical, optical, or electronic devices are sometimes used to magnify the strain for easier reading. 一种测量金属拉伸和类似试验中产生的少量应变的装置。将一卷细线安装在一张纸、塑料或类似载体基质（背衬材料）上，该载体基质呈矩形，通常约25mm（1.0in.）长，这是粘在测试金属的一部分。随着线圈随试样延伸，其电阻成正比增加，这被称为粘结电阻应变计。其他类型的量规测量实际变形。机械、光学或电子设备有时用于放大应变以便于读取。 |
| Extensometer | 引伸计 |
An instrument for measuring changes in length over a given gage length caused by application or removal of a force. Commonly used in tension testing of metal specimens. Any instrument which measures the change in length of a part as the part is loaded. 一种用于测量在给定标距上由施加或移除力引起的长度变化，在零件加载时测量零件长度变化的仪器。常用于金属试样的拉力试验。 |
| Full hard | 全硬化 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state beyond which the material can no longer be formed by bending. In specifications, a full hard temper is commonly defined in terms of minimum hardness or minimum tensile strength (or, alternatively, a range of hardness or strength) corresponding to a specific percentage of cold reduction following a full anneal. For aluminum, a full hard temper is equivalent to a reduction of 75% from dead soft ; for austenitic stainless steels, a reduction of about 50 to 55%. 有色金属合金和一些铁合金的回火状态，大致对应于冷加工状态，超过该状态，材料就不能再通过弯曲形成。在规范中，完全硬质回火通常定义为与完全退火后的特定冷压下率百分比相对应的最小硬度或最小抗拉强度（或者，硬度或强度范围）。对于铝来说，完全硬回火相当于从极软状态减少75%；对于奥氏体不锈钢，减少约50%至55%。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Coefficient of friction (μ) | 摩擦系数（μ） |
(coefficient of kinetic friction, coefficient of sliding friction, friction coefficient, μ) The ratio of the frictional force F to the normal force N between two surfaces in contact, i.e. μ = F/N. Static friction is when there is no relative sliding; kinetic friction when there is. For structural components sliding on one another, the coefficient of friction is the ratio of the force causing the sliding to the force perpendicular to the sliding component surfaces. The coefficient of friction is dimensionless with values between zero and one. The number characterising the force necessary to slide or roll one material along the€surface of another. If an object has a weight N and the coefficient of friction is μ, then the force F necessary to move it without acceleration along a level surface is F = μN. The coefficient of static friction determines the force necessary to initiate movement; the coefficient of kinetic friction determines the force necessary to maintain movement. Kinetic friction is usually smaller than static friction. （动摩擦系数、滑动摩擦系数、摩擦系数，μ）两个接触表面之间摩擦力F与法向力N的比值，即μ=F/N。静摩擦是指没有相对滑动时；有摩擦时的动摩擦。对于相互滑动的结构部件，摩擦系数是引起滑动的力与垂直于滑动部件表面的力的比值。摩擦系数是无量纲的，其值介于0和1之间。代表一种材料沿另一种材料的表面滑动或滚动所需的力的数字。如果一个物体的重量为N并且摩擦系数为μ，那么在没有加速度的情况下沿水平表面移动它所需的力F为F=μN。静摩擦系数决定了启动运动所需的力；动摩擦系数决定了保持运动所需的力。动摩擦通常小于静摩擦。两个物体之间的力（F）与将这些物体压在一起的法向力（N）的无量纲比：μ（或f）=（F/N）。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Activation energy | 活化能 |
(Ea, U) (Unit kJ/mol) The minimum energy for a chemical reaction to occur or for processes such as diffusion to take place in crystals. （Ea, U）（单位kJ/mol）发生化学反应或在晶体中发生扩散等过程的最小能量。 |
| Vector | 矢量 |
Any physical quantity, such as velocity, acceleration, force, or momentum, that is specified in terms of both its magnitude and its direction. The convention of printing vector quantities in boldface was introduced by the physicist Josiah Willard Gibbs. 任何物理量，如速度、加速度、力或动量，以其大小和方向来表示。用黑体印刷矢量量的惯例是由物理学家约西亚·威拉德·吉布斯提出的。 |
| Heat capacity (C) (Unit J/K) | 热容量（C）（单位J/K） |
The energy required to raise the temperature of a body by 1K without change of phase. Heat capacity is an extensive thermodynamic property dependent on temperature and pressure. 在不发生相变的情况下将物体的温度提高1K所需的能量。热容量是一种广泛的热力学性质，取决于温度和压力。 |
| Torsion spring | 扭簧 |
1. A spring in the form of a torsion bar. 2. A helical spring to which torque can be applied at the ends. 1.一种扭杆形式的弹簧。2.一种螺旋弹簧，其端部可施加扭矩。 |
| Clevis | U形夹 |
A U-shaped hook with holes at the ends through which a retaining bolt or pin (clevis pin) passes. 一种U形钩，末端有孔，固定螺栓或销（U形销）穿过这些孔。 |
| Galilean transformation | 伽利略变换 |
In steady fluid flow, the addition or subtraction of a constant velocity to the entire flowfield, e.g. so that flow can be considered relative to a moving object or flow feature, such as a shock wave. 在稳定的流体流动中，对整个流场增加或减少恒定速度，例如，可以考虑相对于移动物体或流动特征（例如冲击波）流动。 |
| Centrifugal fan | 离心风机 |
A machine with a rotor consisting of a number of blades mounted around a hub and used for moving air or other gases. The gas enters the rotor axially and is discharged radially at increased pressure. 一种带有转子的机器，转子由安装在轮毂周围的许多叶片组成，用于移动空气或其他气体。气体轴向进入转子并在增加的压力下径向排出。 |
| Fit | 装配 |
The general term used to signify the range of tightness which may result from the application of a specific combination of allowances and tolerances in the design of mating parts. 通用术语，用于表示配合零件设计中公差和公差的特定组合可能导致的紧密性范围。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Tension testing | 张力测试 |
A method of determining the behavior of materials subjected to uniaxial loading, which tends to stretch the metal. A longitudinal specimen of known length and diameter is gripped at both ends and stretched at a slow, controlled rate until rupture occurs. Also known as tensile testing. 一种确定材料在单轴载荷下的行为的方法，这种载荷倾向于拉伸金属。将已知长度和直径的纵向试样夹持在两端，并以缓慢、受控的速率拉伸，直到发生断裂。也称为拉伸测试。 |
| Absolute viscosity | 绝对粘度 |
A measure of the internal shear properties of fluids, expressed as the tangential force per unit area at either of two horizontal planes separated by one unit thickness of a given fluid, one of the planes being fixed and the other moving with unit velocity. 流体内部剪切特性的量度，表示为两个水平面中的任何一个上的单位面积切向力，两个水平面被给定流体的一个单位厚度隔开，其中一个平面固定，另一个以单位速度移动。 |
| Archimedes Wave Swing | 阿基米德波摆动 |
A machine for tidal-power energy generation consisting of two concentric, air-filled submerged cylinders. The inner lower cylinder is tethered to the ocean floor while the upper floater unit, which is closed at the top, moves up and down due to the variations in hydrostatic pressure caused by the wave motion. The relative movement of the two cylinders is used to generate electricity in which linear motion replaces the more common rotary motion of an electromagnetic generator. 一种用于潮汐能发电的机器，由两个同心的充气水下气缸组成。内部下部圆柱体系在海底，而顶部封闭的上部浮子单元由于波浪运动引起的静水压力变化而上下移动。两个气缸的相对运动用于发电，其中直线运动取代了电磁发电机更常见的旋转运动。 |
| Ball screw and nut | 滚珠丝杠和螺母 |
A nut and bolt assembly having semi-circular helical grooves, as opposed to threads, in which run ball bearings. On rotation of the nut, the balls move along the helix and carry the axial load. Balls reaching the end of the groove are recirculated back to the beginning. Such devices have low friction and very little backlash, and are used in some steering mechanisms. 一种螺母和螺栓组件，具有半圆形螺旋槽，与螺纹相反，在其中运行滚珠轴承。在螺母旋转时，滚珠沿螺旋线移动并承受轴向载荷。到达凹槽末端的滚珠被循环回起点。这种装置具有低摩擦和非常小的背隙，并且用于一些转向机构。 |
| Mean diameter (Unit m) | 平均直径（单位米） |
The average of the inside and outside diameters for a helical spring or hollow circular cylinder or sphere 螺旋弹簧或空心圆柱体或球体的内径和外径的平均值 |
| ASME | ASME |
The American Society of Mechanical Engineers. 美国机械工程师学会。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| Hot working | 热加工 |
Plastic deformation of a metal, by rolling, drawing, forging, etc., at a temperature above its recrystallization temperature (in commercial alloys above about 40% of their melting points in kelvins) which results in permanent shape change but no increase in strength or loss of ductility. 金属通过轧制、拉拔、锻造等在高于其再结晶温度（在商业合金中高于其熔点的40%的开尔文）的温度下发生塑性变形，导致永久的形状变化，但不会增加强度或失去延展性。 |
| Edge distance | 边距 |
The distance from the edge of a bearing specimen to the center of the hole in the direction of applied force. 在作用力方向上，从轴承试样的边缘到孔中心的距离。 |
| Relaxed stress | 松弛应力 |
The initial stress minus the remaining stress at a given time during a stress-relaxation test. 在应力松弛试验期间，初始应力减去给定时间的剩余应力。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Equation, short form | 方程式，简写形式 |
An empirical equation which relates the torque applied to the bolt to the preload created in it, and which depends mainly on an experimentally derived factor called the Nut factor. 一个经验公式，将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来，主要取决于一个称为螺母系数的实验得出的系数。 |
| Displacement | 移位 |
The distance that a chosen measurement point on a cracked specimen displaces normal to the crack plane as the crack grows. 随着裂纹扩展，裂纹试样上选定的测量点垂直于裂纹平面位移的距离。 |
| Torr | 托尔 |
A non-SI unit of pressure commonly used in vacuum systems; defined by 760 torr = 1 atm so that 1 torr = 133.322 368 4 Pa, and approximately equivalent to the pressure corresponding to 1 mm of mercury. 真空系统中常用的非SI压力单位；由760托=1大气压定义，因此1托=133.3223684帕，近似等于对应于1毫米汞柱的压力。 |
| Creep–time relations | 蠕变时间关系 |
Algebraic or numerical relations between creep strain and time at constant stress. 恒定应力下蠕变应变与时间之间的代数或数值关系。 |
| Effective length of a bolt | 螺栓的有效长度 |
The grip length plus some portion of the bolt (often one-half of the thickness of the nuts) which lies within the nut(s) plus some portion (often one-half the thickness) of the head. 握持长度加上位于螺母内的螺栓的某些部分（通常是螺母厚度的二分之一）加上头部的某些部分（通常是厚度的二分之一）。 |
| mechanical engineering | 机械工业 |
That branch of engineering concerned with energy conversion, stress analysis, vibration, dynamics, and kinematics, especially applied to design (machine design, mechanical-engineering design). 与能量转换、应力分析、振动、动力学和运动学有关的工程分支，尤其适用于设计（机器设计、机械工程设计）。 |
| Fillet radius | 圆角半径 |
Concave junction at two intersecting surfaces of a fastener. Often used to describe the junction between the head and the shank of a threaded fastener (under head fillet). 在紧固件的两个相交表面处的凹形接合处。通常用于描述螺纹紧固件的头部和柄部之间的连接处（头部圆角下方）。 |
| Actual cubic feet per minute | 实际立方英尺每分钟 |
(acfm) An obsolete (i.e. non-SI) measure of volumetric flow rate; the volume of a gas flowing per minute at actual operating pressure and temperature, as opposed to the corresponding volume flow rate at STP. （acfm）已被淘汰的（即非SI）体积流量测量；在实际工作压力和温度下每分钟流动的气体体积，与STP下的相应体积流量相反。 |
| Finished fastener | 精制紧固件 |
Fastener for which all manufacturing steps have been completed, with or without any surface coating and with full or reduced loadability, and which has not been machined into a test piece. 已完成所有制造步骤的紧固件，有或没有任何表面涂层，具有完全或降低的承载能力，并且尚未加工成试件。 |
| Malleable cast iron | 可锻铸铁 |
A cast iron made by prolonged annealing of white cast iron in which decarburization or graphitization, or both, take place to eliminate some or all of the cementite. The graphite is in the form of temper carbon. If decarburization is the predominant reaction, the product will exhibit a light fracture surface, hence, “whiteheart malleable;” otherwise, the fracture surface will be dark, hence, “blackheart malleable.” Ferritic malleable has a predominantly ferritic matrix; pearlitic malleable may contain pearlitic, spheroidite or tempered martensite depending on heat treatment and desired hardness. 白口铸铁一种通过长时间退火制成的铸铁，脱碳，石墨化，或两者都发生，以消除部分或全部渗碳体。石墨是回火碳的形式。如果脱碳是主要反应，产品将呈现出较轻的断裂表面，“白心可锻”。否则，断裂表面将变暗，“黑心可锻”。铁素体可锻性材料主要为铁素体基体；根据热处理和所需硬度，珠光体可锻材料可能包含珠光体、球状体或回火马氏体。 |
| Spalling | 剥落 |
The separation of macroscopic particles from a surface in the form of flakes or chips. 以薄片或碎片形式从表面分离宏观颗粒。 |
| Catastrophic failure | 灾难性故障 |
A sudden and total failure of a large engineering structure such as an aeroengine, aircraft, space vehicle, bridge, or dam. 大型工程结构（如航空发动机、飞机、航天器、桥梁或水坝）突然完全失效。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Blade compressor | 叶片式压缩机 |
An oil-free, double-acting rotary compressor in which an angled blade attached to the inner surface of a rotating housing passes through a slot in a disk rotating about an axis perpendicular to that of the housing but offset from it. Air enters through apertures in the housing and leaves through a port in the housing. 一种无油双作用旋转式压缩机，其中连接到旋转外壳内表面的倾斜叶片穿过圆盘上的槽，该槽绕垂直于外壳的轴旋转，但偏离外壳。空气通过壳体中的孔进入，并通过壳体的端口离开。 |
| Design pressure (Unit Pa) | 设计压力（单位Pa） |
The greatest pressure that a closed container is expected to experience under normal operating conditions. 密闭容器在正常操作条件下预期承受的最大压力。 |
| Thermoelectric junction | 热电结 |
A welded, soldered, or twisted connection between the ends of two wires of dissimilar metals, as in a thermocouple. 两根不同金属线的末端之间的焊接、锡焊或绞合连接，如热电偶。 |
| Counter sink | 台面水槽 |
To cut or shape a depression in an object so that the head of a screw may set flush or below the surface. 在物体上切割或塑造一个凹陷，使螺钉的头部可以齐平或低于表面。 |
| Coaxial | 同轴 |
A term for components having a common axis such as concentric shafts. 具有共同轴线的部件的术语，例如同心轴。 |
| Zero initial conditions | 零初始条件 |
The assumption normally made in control engineering that up to a start time defined as t = 0, all variables have zero value. 在控制工程中通常作出的假设，即在定义为t=0的开始时间内，所有变量均为零值。 |
| Radial engine | 径向发动机 |
A piston engine in which the cylinders are arranged radially around the crankshaft, a design commonly used in early aircraft engines. 气缸沿径向围绕曲轴布置的活塞式发动机，这种设计通常用于早期飞机发动机。 |
| Bright annealing | 光亮退火 |
Annealing in a protective medium to prevent discoloration of the bright surface. 在保护介质中退火以防止光亮表面变色。 |
| Thermal analysis | 热分析 |
A method for determining transformations in a metal by noting the temperatures at which thermal arrests occur. These arrests are manifested by changes in slope of the plotted or mechanically traced heating and cooling curves. When such data are secured under nearly equilibrium conditions of heating and cooling, the method is commonly used for determining certain critical temperatures required for the construction of equilibrium diagrams. 一种通过记录发生热阻的温度来确定金属转变的方法。这些阻力表现为绘制或机械追踪的加热和冷却曲线斜率的变化。当这些数据在加热和冷却的近似平衡条件下得到保证时，该方法通常用于确定构建平衡图所需的某些临界温度。 |
| Bright nitriding | 光亮氮化 |
Nitriding in a protective medium to prevent discoloration of the bright surface. 在保护介质中氮化，以防止光亮表面变色。 |
| Controlled cooling | 控制冷却 |
Cooling from an elevated temperature in a predetermined manner, to avoid hardening, cracking, or internal damage, or to produce desired microstructure or mechanical properties. 以预定方式从升高的温度冷却，以避免硬化、开裂或内部损坏，或产生所需的微观结构或机械性能。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Precipitation-hardenable stainless steels | 沉淀硬化不锈钢 |
Precipitation-hardenable stainless steels contain typically 11–18% chromium, 3–10% nickel, 0.05–0.2% carbon, and small additions of manganese, silicon, aluminium, molybdenum, niobium and titanium. These steels can be supplied in a solution-treated condition, which is readily fabricated or machined, and then hardened by an ageing treatment that produces a fine dispersion of second-phase precipitates. They are available in austenitic, semi-austenitic, and martensitic grades. Uses include springs, knives, and pressure vessels. 沉淀硬化不锈钢通常含有11-18%的铬、3-10%的镍、0.05-0.2%的碳以及少量添加的锰、硅、铝、钼、铌和钛。这些钢可在固溶处理条件下供应，该条件易于制造或机加工，然后通过时效处理硬化，从而产生细小的第二相沉淀。它们有奥氏体、半奥氏体和马氏体等级。用途包括弹簧、刀具和压力容器。 |
| Destructive testing | 破坏性测试 |
Measurement of the mechanical properties of a material, component, or structure, by increased loading until the sample fails by fracture, collapse, or buckling. 通过增加载荷测量材料、部件或结构的机械性能，直到样品因断裂、塌陷或屈曲而失效。 |
| Double tempering | 双回火 |
A treatment in which a quench-hardened ferrous metal is subjected to two complete tempering cycles, usually at substantially the same temperature, for the purpose of ensuring completion of the tempering reaction and promoting stability of the resulting microstructure. 一种处理，其中淬火硬化的黑色金属经过两个完整的回火循环，通常在基本相同的温度下，以确保完成回火反应并提高所得微观结构的稳定性。 |
| Water column | 水柱 |
Water in a tube, which may be vertical or inclined. If the tube is open to the atmosphere, the vertical height h from a datum level to the water surface is a measure of the water static pressure p at the datum level given by p − B = ρgh where B is the barometric pressure, ρ denotes the water density, and g is the acceleration due to gravity. 管道中的水，可以是垂直的或倾斜的。如果管道向大气开放，则从基准面到水面的垂直高度h是基准面处水静压p的量度，由p给出−B=ρgh，其中B是大气压力，ρ表示水密度，g是重力引起的加速度。 |
| Mean stress (Unit Pa) | 平均应力（单位 Pa） |
The average of the maximum and minimum stresses for a material subjected to a stress cycle, as in a fatigue test. 承受应力循环的材料的最大和最小应力的平均值，如在疲劳试验中。 |
| Austempered steels | 等温钢 |
Medium to high carbon steels with improved mechanical properties as a result of austempering. After heating to between 800° and 900°C to form the austenite phase, they are quenched to, and held at, just above the martensite transformation range (between 260° and 370°C) to form bainite, before cooling further. Austempering of ductile cast irons results in a microstructure of bainite and spheroidal graphite. Austempered ductile irons have excellent toughness and wear properties. 由于等温淬火，机械性能得到改善的中高碳钢。在加热到800°和900°C之间形成奥氏体相后，将它们淬火并保持在略高于马氏体转变范围（260°和370°C之间）以形成贝氏体，然后进一步冷却。球墨铸铁的等温淬火导致贝氏体和球状石墨的微观结构。等温淬火球墨铸铁具有优异的韧性和耐磨性。 |
| Angström (Å) | 昂斯特罗姆（Å） |
An obsolete (non-SI) unit of length, sometimes still employed for atomic and crystallographic measurements. The conversion to SI is 1 Å = 10−10 m. 一种已被淘汰的（非SI）长度单位，有时仍用于原子和晶体学测量。转换为SI为1Å=10-10m。 |
| Batch furnace | 间歇式炉 |
A furnace used to heat treat a single load at a time. Batch-type furnaces are necessary for large parts such as heavy forgings and are preferred for complex alloy grades requiring long cycles. 用于一次热处理单个负载的炉子。对于重型锻件等大型零件，间歇式炉是必需的，对于需要长周期的复杂合金牌号来说是首选。 |
| Peel strength (Unit N) | 剥离强度（单位：N） |
(peel test) The strength of an adhesive bond between two materials as measured by the force required in a given direction to peel apart adhered strips. This force depends on the dimensions and thickness of the adhered strips and their yield stress, together with the fracture toughness of the bond. （剥离试验）两种材料之间的粘合强度，通过给定方向上剥离粘合条所需的力来测量。该力取决于粘合条的尺寸和厚度及其屈服应力，以及粘合剂的断裂韧性。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| International System of Units | 国际单位制 |
(SI system of units, Le Système international d’unités) The standard system of units now used almost universally in science and engineering except in the United States. The definitive reference on the SI is a booklet published by the International Bureau of Weights and Measures, often referred to as the BIPM SI Brochure. There are seven base units: metre (symbol m) for length; kilogram (kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred.(kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred. （国际单位制，Le Système international d\\\'unités）目前美国除外，在科学和工程中几乎是普遍使用的标准单位制。SI的最终参考是国际度量衡局出版的小册子，通常称为BIPM SI小册子。有七个基本单位：米（符号m）表示长度；质量为千克（kg）；物质量的摩尔（mol）；时间为秒；开尔文（K）表示温度；电流为安培（A）；而坎德拉（cd）表示发光强度。新的国际单位制定义于2019年5月20日生效，该定义基于自然界的普遍常数（也称为基本物理常数：阿伏伽德罗常数、玻尔兹曼常数和普朗克常数）。这些常数的值也进行了少量调整。除了基本单位外，还有22个相干导出单位，包括平面角的弧度（rad）、立体角的斯特拉迪安（sr）、频率的赫兹（Hz）、力的牛顿（N）、压力的帕斯卡（Pa）、能量、功和热量的焦耳（J）以及功率和辐射通量的瓦特（W）。建议的做法是避免N/mm²、MN/m²等组合。 |
| Full-size fastener | 全尺寸紧固件 |
Finished fastener with a shank diameter of ds ≈ d or ds > d, or screw threaded to the head, or fully threaded stud. 柄径为ds≈d或ds>d的紧固件，或螺纹连接到头部，或全螺纹螺柱。 |
| Thermal energy (heat energy) (Unit J) | 热能（单位：J） |
The sensible and latent forms of internal energy. 内能的感知和潜在形式。 |
| Impact strength 1. (Unit Pa) | 冲击强度1.（单位Pa） |
The stress to cause failure (by yielding or fracture) under conditions of high strain rate. 2. (Unit J) A term sometimes used to describe the energy required to fracture a specimen in a Charpy or Izod impact test even though the unit is not that of strength. 在高应变率条件下导致失效（通过屈服或断裂）的应力。2.（单位J）有时用于描述在夏比或悬臂梁式冲击试验中使样品断裂所需的能量，即使单位不是强度单位。 |
| Nut factor | 螺母系数 |
An experimental constant used to evaluate or describe the ratio between the torque applied to a fastener and the Preload achieved as a result. 用于评估或描述施加在紧固件上的扭矩与由此获得的预载之间的比率的实验常数。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Interrupted aging | 分段时效 |
Aging at two or more temperatures, by steps, and cooling to room temperature after each step. 分为两个或两个以上的温度时效，按顺序并在每个步骤后冷却至室温。 |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Corrosion | 腐蚀 |
The deterioration of an exposed metal surface due to electrochemical oxidation with its surroundings. In the oxidation reaction, metal atoms give up electrons which are transferred to form another chemical species by a reduction reaction, usually with hydrogen and/or oxygen. A common example is the formation of the iron oxide rust Fe(OH)3 on iron or steel in moist air or water. Rust breaks away easily, exposing fresh iron to the atmosphere, whereas the corrosion product of some metals forms an adherent layer that prevents further oxidation reaction at fresh metal, an effect known as passivation. Examples include aluminium oxide on aluminium, chromium oxide on chromium, chromium oxide on alloys containing chromium such as stainless steels, and the patina formed on copper and zinc. Corrosion protection takes many forms. Good design to avoid crevices and stress is important. In some situations, substances known as inhibitors may be added to the environment to decrease its corrosiveness. The electrochemical nature of corrosion results in some metals having a greater tendency for oxidation than others. Zinc has a stronger tendency than iron and this is made use of in galvanizing. This is one example of cathodic protection, in which one metal is connected electrically to a more reactive metal, called a sacrificial anode, that oxidizes by giving up electrons and so protects the first metal. Coatings may be used to resist corrosion. Paints, plating, and diffusion coatings are the most common and the electrochemical process of anodizing is used to deliberately form a passive layer of oxide on aluminium alloys. Material selection plays a major role. For example, stainless steels with their high chromium content are widely used in corrosive environments. 暴露的金属表面由于与周围环境的电化学氧化而劣化。在氧化反应中，金属原子放弃电子，这些电子通过还原反应（通常与氢和/或氧）转移形成另一种化学物质。一个常见的例子是在潮湿的空气或水中在铁或钢上形成氧化铁锈Fe(OH)3。铁锈很容易脱落，将新鲜铁暴露在大气中，而一些金属的腐蚀产物形成一层粘附层，防止新鲜金属发生进一步的氧化反应，这种效果称为钝化。实例包括铝上的氧化铝、铬上的氧化铬、含铬合金上的氧化铬如不锈钢，以及铜和锌上形成的铜绿。腐蚀防护有多种形式。避免裂缝和应力的良好设计非常重要。在某些情况下，可以向环境中添加称为抑制剂的物质，以降低其腐蚀性。腐蚀的电化学性质导致一些金属比其他金属具有更大的氧化倾向。锌比铁具有更强的倾向性，这可用于镀锌。这是阴极保护的一个例子，其中一种金属与活性更强的金属（称为牺牲阳极）电连接，牺牲阳极通过释放电子进行氧化，从而保护第一种金属。涂层可用于抗腐蚀。油漆、电镀和扩散涂层是最常见的，阳极氧化的电化学过程用于有意在铝合金上形成一层钝化氧化物。材料选择起着重要作用。例如，铬含量高的不锈钢广泛用于腐蚀性环境。 |
| Screw extractor | 螺钉拔 |
A device for removing broken-off screws from threaded holes. It resembles a drill with, for broken right-hand threads, a fast (long-pitch) left-hand thread that is driven into a hole drilled in the broken screw, thus untwisting it. 从螺纹孔中去除断裂螺钉的装置。它类似于一个钻头，对于断裂的右螺纹，一个快速（长螺距）的左螺纹被打入在断裂螺钉上钻的孔中，从而将其松开。 |
| Thermodynamics laws | 热力学定律 |
The zeroth, first, second, and third laws of thermodynamics. 热力学第零、第一、第二和第三定律。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| Rotary pump | 旋转泵 |
A positive-displacement pump that pumps a liquid by rotation of internal components, such as a gear pump, lobe pump (similar to a Roots blower), or progressivecavity pump. 通过内部部件的旋转来泵送液体的容积泵，如齿轮泵、凸轮泵（类似于罗茨鼓风机）或螺杆泵。 |
| Bearing test | 轴承测试 |
A method of determining the response to stress (load) of metal products that are subjected to riveting, bolting, or a similar fastening procedure. The purpose of the test is to determine the bearing strength of the material and to measure the bearing stress versus the deformation of the hole created by a pin or rod of circular cross section that pierces the sheet perpendicular to the surface. 一种确定经受铆接、螺栓连接或类似紧固程序的金属产品对应力（载荷）的响应的方法。测试的目的是确定材料的承载强度，并测量承载应力与由垂直于表面刺穿板材的圆形横截面的销或杆产生的孔的变形。 |
| Kilocalorie | 千卡 |
(Cal, kg-cal, kilogram-calorie, large calorie) An obsolete (i.e. non-SI) unit of energy equal to 1 000 cal. （卡，千克卡，千克卡路里，大卡路里）一种已被淘汰的（即非国际单位制）能量单位，等于1000卡。 |
| Torque coefficient | 扭矩系数 |
1. (KT) For a propeller of diameter D, a non-dimensional parameter defined by KT = T/ρΩ2D5 where Ω is the rotational speed (in rad/s) and ρ is the fluid density. 2. (CT) An alternative to (1) for a wind turbine, defined by CT = 2T/ρV2AR where V is the wind speed, A is the swept area of the blades, and R is the blade radius. 3. (K) An empirical coefficient used to calculate the torque T required to achieve an axial load F in a bolt according to T = KFd where d is the nominal bolt diameter. 1.（KT）对于直径为D的螺旋桨，由KT=T/ρΩ2D5定义的无量纲参数，其中Ω是转速（单位为rad/s），ρ是流体密度。2.（CT）对于风力涡轮机（1）的替代方案，由CT=2T/ρV2AR定义，其中V是风速，a是叶片的扫掠面积，R是叶片半径。3.（K）经验系数，用于根据T=KFd计算螺栓中实现轴向载荷F所需的扭矩T，其中d是螺栓标称直径。 |
| Alloying element | 合金元素 |
Component added deliberately with the aim of improving the properties of an alloy. Alloying elements can affect the existence range of equilibrium phases present in an unalloyed material, or lead to the occurrence of new phases, or both. In addition, alloying elements strongly affect the kinetics of phase transformations and thus the microstructure formation in alloyed materials. 为改善合金性能而有意添加的成分。合金元素可以影响非合金材料中存在的平衡相的存在范围，或导致新相的出现，或两者兼而有之。此外，合金元素强烈影响相变动力学，从而影响合金材料的微观结构形成。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Volume flow rate | 体积流率 |
(volumetric flow rate, , ) (Unit m³/s) The volume of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. （体积流量）（单位m³/s）单位时间内流经表面或管道或其他管道的材料体积，通常为流体或粉末。 |
| Dead space | 死区 |
(dead volume) (Unit m³) That volume of a gas-filled thermometer in which the gas is not at the same temperature as that being measured. （死容）（单位m³）充气温度计的体积，其中气体的温度与被测温度不同。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Bearing stress | 承受应力 |
The force per unit of bearing area. 每单位承载面积的力。 |
| Effective yield strength | 有效屈服强度 |
An assumed value of uniaxial yield strength that represents the influence of plastic yielding on fracture test parameters. 单轴屈服强度的假设值，代表塑性屈服对断裂试验参数的影响。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Taper | 变尖 |
A gradual, often linear, reduction in cross section or shape. A shaft or hole that gets gradually smaller toward one end. 横截面或形状的逐渐减小，通常是线性的。一端逐渐变小的轴或孔。 |
| Coefficient of rolling friction | 滚动摩擦系数 |
The ratio of force parallel to a surface, on which an object rolls, to the normal force. Unlike sliding friction, rolling friction depends on the size of the contact patch and the radius of the rolling element, and the behaviour depends on whether the contact is elastic, viscoelastic, or plastic and on hysteresis losses. 平行于物体滚动表面的力与法向力之比。与滑动摩擦不同，滚动摩擦取决于接触片的大小和滚动元件的半径，其行为取决于接触是弹性的、粘弹性的还是塑性的以及滞后损失。 |
| Centrifugal pump | 离心泵 |
A pump into which liquid enters axially through the eye of the casing and is then accelerated through an impeller, thereby increasing both its kinetic energy and pressure before being delivered to a ring diffuser (the volute) that further increases the liquid pressure and from which it leaves. 一种泵，液体通过泵壳的眼轴向进入，然后通过叶轮加速，从而在输送到环形扩散器（蜗壳）之前增加其动能和压力，从而进一步增加液体压力并从中流出树叶。 |
| Ductile crack propagation | 延性裂纹扩展 |
Slow crack propagation that is accompanied by noticeable plastic deformation and requires energy to be supplied from outside the body. 缓慢的裂纹扩展，伴随着明显的塑性变形，需要从外部提供能量。 |
| Nanomanufacturing | 纳米制造 |
1. The manufacture of nanoscale materials. 2. The manufacture of components or devices that have critical dimensions of order 1 nm. 1.纳米材料的制造。2.具有1nm级临界尺寸的部件或装置的制造。 |
| Brittle lacquer coating | 脆性漆涂层 |
A lacquer that, when painted on to an unloaded body, reveals the direction of maximum tension stresses from the pattern of cracking produced in the lacquer when the body is loaded. 一种漆，当涂在未加载的车身上时，从车身加载时在漆中产生的裂纹图案中显示出最大拉应力的方向。 |
| Yielding | 屈服 |
Evidence of plastic deformation in structural materials. Also known as plastic flow or creep. 结构材料塑性变形的证据。也称为塑性流动或蠕变。 |
| Torque multiplier | 扭矩放大器 |
A gearbox used to multiply the torque produced by a small hand wrench (usually a Torque wrench). The output of the multiplier drives the nut or bolt with a torque that is higher, and a speed that is lower, than input torque and speed. There is no torque gage or readout on the multiplier. 一种齿轮箱，用于增加小手动扳手（通常是扭矩扳手）产生的扭矩。倍增器的输出以比输入扭矩和速度更高的扭矩和更低的速度驱动螺母或螺栓。倍增器上没有扭矩计或读数。 |
| Fatigue | 疲劳 |
The phenomenon leading to fracture under repeated or fluctuating stresses having a maximum value less than the ultimate tensile strength of the material. Fatigue failure generally occurs at loads that, applied statically, would produce little perceptible effect. Fatigue fractures are progressive, beginning as minute cracks that grow under the action of the fluctuating stress. A term referring, in components and structures subjected to either random or cyclic periodically-varying loads, to a progressive reduction in strength leading to failure at stresses lower than those that cause failure under monotonic loading. Variable loads arise from outof-balance machinery and other vibration sources, wind gusts, etc., and a large proportion of service failures is caused by fatigue. Fatigue results from the initiation and slow propagation of cracks. In manufactured components, crack initiation usually occurs at a point of stress concentration. After a period, often of millions of stress cycles, the crack reaches a critical length at which the next peak load causes sudden brittle or ductile fracture. Fracture surfaces resulting from fatigue display characteristic striations or progression marks emanating from the crack initiation site during the slow crack growth period, with a different surface appearance for the final fracture. 在最大值小于材料极限抗拉强度的重复或波动应力下导致断裂的现象。疲劳失效通常发生在静态施加的载荷下，不会产生明显影响。疲劳断裂是渐进性的，从在波动应力作用下生长的微小裂纹开始。在承受随机或周期性变化载荷的部件和结构中，指强度逐渐降低，导致在低于单调载荷下导致失效的应力下发生失效的术语。可变负载由失衡的机械和其他振动源、阵风等引起，大部分故障是由疲劳引起的。疲劳是裂纹萌生和缓慢扩展的结果。在制造部件中，裂纹萌生通常发生在应力集中点。在一段时间（通常是数百万次应力循环）后，裂纹达到临界长度，此时下一个峰值载荷会导致突然脆性或韧性断裂。疲劳产生的断裂表面在缓慢裂纹扩展期间显示出从裂纹萌生部位发出的特征条纹或进展标记，最终断裂的表面外观不同。 |
| Grain | 晶粒 |
1. An individual crystal in a polycrystalline solid. Most engineering materials such as metals and ceramics are used in polycrystalline form. 2. (gr) A non-SI unit of mass. The conversion to SI is 1 gr = 6.479 891 × 10−5 kg. 1.多晶固体中的单个晶体。大多数工程材料，如金属和陶瓷，都以多晶形式使用。2.（gr）非国际单位制的质量单位。转换为SI为1gr=6.479891×10-5kg。 |
| Degree (°) | 度数（°） |
A measure of plane angle such that 1° is 1/360 of a complete revolution and equal to π/180 rad. 平面角度的一种度量，使得1°是一整圈的1/360，等于π/180弧度。 |
| Starting valve (regulator) | 起动阀（调节器） |
A valve which admits steam from the boiler to the cylinder(s) of a steam engine. 将蒸汽从锅炉送入蒸汽机汽缸的阀门。 |
| Yield strength | 屈服强度 |
That stress level which will create a permanent deformation of 0.2% or 0.5% or some other small, preselected, amount in a body. Approximately equal to the elastic and proportional limits of the material; a little higher than the proof strength of a bolt. The stress at which a material exhibits a specified deviation from proportionality of stress and strain. An offset of 0.2% is used for many metals. 该应力水平将在物体中产生0.2%或0.5%的永久变形，或其他一些小的、预先选定的量。近似等于材料的弹性和比例极限；略高于螺栓的强度。材料表现出与应力和应变比例的特定偏差的应力。许多金属使用0.2%的偏移量。 |
| Solution heat treatment | 固溶热处理 |
Heating an alloy to a suitable temperature, holding at that temperature long enough to cause one or more constituents to enter into solid solution, and then cooling rapidly enough to hold these constituents in solution. 将合金加热到合适的温度，在该温度下保持足够长的时间以使一种或多种成分进入固溶体，然后快速冷却以将这些成分保持在溶液中。 |
| Impact | 撞击 |
Sudden loading of a body or component, as in a vehicle collision or striking by a hammer. 物体或部件的突然加载，如车辆碰撞或锤击。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Imperial system | 英制单位体系 |
The units of measurement developed in the UK. Formerly known as the fps system, which is an abbreviation for the ‘foot-pound-second system of units. 英国开发的计量单位。以前称为fps系统，是“英尺-磅-秒（foot-pound-second）单位制”的缩写。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Turbomachine | 涡轮机械 |
(rotodynamic machine) A machine in which there is a transfer of energy between a continuous stream of fluid and a component, called a rotor, rotating about a fixed axis. Fans and turbines (gas, hydraulic, steam, or wind) are turbomachines in which energy is transferred to the rotor, causing it to rotate. Pumps and compressors are turbomachines in which energy is transferred from the externally driven rotor to the fluid. （旋转动力机器）在连续的流体流和绕固定轴旋转的部件（称为转子）之间进行能量传递的机器。风扇和涡轮机（燃气、液压、蒸汽或风力）是涡轮机械，其中能量传递到转子，使其旋转。泵和压缩机是涡轮机械，其中能量从外部驱动的转子传递到流体。 |
| Two-dimensional flow | 二维流 |
A fluid flow in which the velocity at any time depends upon two spatial coordinates, such as the radial and axial locations in developing pipe flow. 一种流体流动，其中任何时候的速度取决于两个空间坐标，如发展中的管道流中的径向和轴向位置。 |
| Thermal compressor | 热压缩机 |
1. (thermocompressor) A jet compressor used to boost the pressure of low-pressure waste or exhaust steam. 2. A device consisting of an absorber, a generator, a pump, and a throttling device, used instead of a mechanical vapour compressor in an absorption-cooling refrigeration system. 1.（热压缩机）用于提升低压废蒸汽或排气压力的喷射压缩机。2.一种由吸收器、发电机、泵和节流装置组成的装置，用于替代吸收冷却制冷系统中的机械蒸汽压缩机。 |
| Hydrogen embrittlement | 氢脆 |
A condition of low toughness, low ductility or cracking in metals resulting from the absorption of hydrogen. A common and troublesome form of Stress cracking. Several theories have been proposed to explain hydrogen embrittlement, but, at present, the exact mechanism is still unknown. What is known, however, is the fact that if hydrogen is trapped in a bolt by poor electroplating practices, it can encourage stress cracking. Bolts can fail, suddenly and unexpectedly, under normal loads. Premature crack growth over time under tensile stress leading to unexpected failure in certain metals, caused by small amounts of hydrogen in the microstructure. Hydrogen may enter steels during melting or heat treating, or during processes such as electroplating. 因吸收氢而导致金属韧性低、延展性低或开裂的情况，是一种常见且麻烦的应力开裂形式。在拉伸应力下，裂纹随时间过早扩展，导致某些金属发生意外失效，这是由微观结构中的少量氢引起的。在熔化或热处理过程中，或在电镀等过程中，氢可能进入钢中。已经提出了几种理论来解释氢脆，但目前，确切的机理仍然未知。已知的事实是，如果氢因电镀不当而被困在螺栓中，则会导致应力开裂。在正常载荷下，螺栓可能突然意外失效。 |
| Set screw | 紧定螺钉（平头螺钉、紧定螺栓） |
Usually a hardened steel screw having either no head or a square head and with various degrees of points or ends to lock or tighten adjustable machine parts in position on a shaft. A short, headless screw with a recess at one end to receive a screwdriver or key, the other end being pointed, square, or otherwise shaped. Typically used to secure a pulley, gear, or other component on a shaft. 通常是一种硬化钢螺钉，无头或方头，具有不同程度的点或端部，用于将可调机械部件锁定或拧紧在轴上的适当位置。一端有凹槽，用来装螺丝刀或钥匙，另一端是尖的、方形的或其他形状的。通常用于将皮带轮、齿轮或其他部件固定在轴上。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Hypoeutectoid alloy | 亚共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of base metal compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共析的合金系统中，与共析成分相比，其成分具有过量母材的任何合金，并且其平衡微观结构包含一些共析结构。 |
| Auxiliary power unit (APU) | 辅助动力装置（APU） |
In aircraft–gas–turbine applications, a small gas turbine used to provide start-up power, electrical and hydraulic power, and compressed air for cabin ventilation. In other applications, an APU may be a gas turbine or internal-combustion engine used to provide emergency power. 在飞机-燃气轮机应用中，小型燃气轮机用于提供启动动力、电力和液压动力以及用于机舱通风的压缩空气。在其他应用中，APU可以是用于提供应急动力的燃气轮机或内燃机。 |
| Torque wrench | 扭矩扳手 |
A manual wrench which incorporates a gage or measuring apparatus of some sort to measure and display the amount of torque being delivered to the nut or bolt. All wrenches produce torque. Only a torque wrench tells how much torque. A socket wrench or ring spanner that can be set to allow a specific torque to be applied to a nut or bolt head. 一种手动扳手，包括某种量规或测量装置，用于测量和显示传递至螺母或螺栓的扭矩量。所有扳手都产生扭矩。只有扭矩扳手才能显示扭矩大小。一种套筒扳手或梅花扳手，可设置为允许对螺母或螺栓头施加特定扭矩。 |
| Proof strength (Unit Pa) | 验证强度（单位Pa） |
(proof stress, Rp, Rp,) The yield strength (offset yield strength) at some fixed value of the permanent strain given by the intersection of a line offset from, but parallel to, the elastic loading line and the engineering stress-engineering strain curve. The offset is arbitrary but is usually 0.1, 0.2, or 0.5% permanent strain (the proof strain). Used for materials which do not exhibit a sharply defined yield point. The notation Rp0.2 or Rp0.2 is employed for the 0.2% proof stress. （验证应力，Rp）在永久应变的某个固定值下的屈服强度（偏移屈服强度），由偏离但平行于弹性加载线的线与工程应力-工程应变曲线的交点给出。偏移是任意的，但通常为0.1、0.2或0.5%的永久应变（验证应变）。用于没有明确定义屈服点的材料。对于0.2%的验证应力，采用符号Rp0.2。 |
| Thermodynamic properties | 热力学性质 |
Temperature, pressure, and the intensive properties that define the state of a working fluid: specific internal energy, specific enthalpy and specific entropy. 温度、压力和定义工作流体状态的密集属性：比内能、比焓和比熵。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Teeth | 齿 |
The projecting elements on gears, cutting tools, etc. 齿轮、刀具等上的突出元件。 |
| Relaxation | 松弛 |
The loss of tension, and therefore Clamping force, in a bolt and joint as a result of Embedment, vibration loosening, gasket creep, differential thermal expansion, etc. 由于嵌入、振动松动、垫圈蠕变、热膨胀差等原因，螺栓和接头中的张力损失，因此夹紧力损失。 |
| Terminal velocity (Unit m/s) | 终端速度（单位：m/s） |
The velocity reached by an object in free fall through a fluid when the upward drag and buoyancy forces just balance the object’s weight. For an object with a density lower than that of the fluid, the terminal velocity is vertically upwards. 当向上的阻力和浮力正好平衡物体的重量时，物体自由下落通过流体达到的速度。对于密度低于流体密度的物体，终端速度垂直向上。 |
| Brake fluid | 制动液 |
The hydraulic fluid used to transmit force to the pistons in disc brakes or the wheel cylinders in drum brakes. Requirements include a high boiling point and low hygroscopy. 用于将力传递到盘式制动器中的活塞或鼓式制动器中的轮缸的液压油。要求包括高沸点和低吸湿性。 |
| Combustion deposit | 燃烧沉积物 |
Ash, carbon, and other incombustible solids, often due to impurities in the fuel, that build up on any surfaces exposed to products of combustion. They can lead to corrosion, reduced heat transfer and so higher flue-gas temperatures and reduced efficiency. 灰、碳和其他不燃固体，通常是由于燃料中的杂质，在暴露于燃烧产物的任何表面上堆积。它们会导致腐蚀、传热降低，从而导致烟气温度升高和效率降低。 |
| Slack quenching | 欠速淬火 |
The incomplete hardening of steel due to quenching from the austenitizing temperature at a rate slower than the critical cooling rate for the particular steel, resulting in the formation of one or more transformation products in addition to martensite. 由于从奥氏体化温度以低于特定钢临界冷却速度的速度淬火而导致钢的不完全硬化，导致除马氏体外还形成一种或多种相变产物。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Strain hardening | 应变硬化 |
An increase in hardness and strengthcaused by plastic deformation at temperatures below the recrystallization range. Also known as work hardening. (workhardening) The increase in stress above the initial yield stress required to deform a metal to greater strains in the plastic range at temperatures below the recrystallization range (cold working). Unloading after some strain or work input gives a harder and stronger material. 在低于再结晶范围的温度下，塑性变形导致硬度和强度的增加。也称为加工硬化。（加工硬化）在低于再结晶范围（冷加工）的温度下，使金属在塑性范围内变形至更大应变所需的高于初始屈服应力的应力增加。在一定的应变或功输入后卸载，会得到更硬、更强的材料。 |
| Autonomous energy system | 自主能源系统 |
(stand-alone energy system) A sole source of electricity, usually small-scale, for applications remote from a grid, especially with energy storage in the system. Hydroelectric, photovoltaic, wind-power and other renewable systems are well suited to stand-alone applications. （独立能源系统）一种唯一的电力来源，通常是小规模的，用于远离电网的应用，尤其是系统中的能量存储。水电、光伏、风力和其他可再生能源系统非常适合独立应用。 |
| Total carbon | 总碳 |
The sum of the free and combined carbon (including carbon in solution) in a ferrous alloy. 铁合金中游离碳和结合碳（包括溶液中的碳）的总和。 |
| Flame annealing | 火焰退火 |
Annealing in which the heat is applied directly by a flame. 通过火焰直接加热的退火。 |
| Thread rolling | 滚丝 |
Thread rolling (also known as roll threading) is a cold forming process for producing threads or other helical or annular forms by rolling the impression of hardened steel dies into the surface of a cylindrical or conical blank. Polygonal blanks are also thread rolled for the purpose of fabricating thread-forming and self-locking screws. The preferred polygonal shape is trilobular and is produced in flat die machines. 螺纹滚压（也称为滚压螺纹）是一种冷成型工艺，通过将硬化钢模具的压痕滚压到圆柱形或锥形坯料的表面来生产螺纹或其他螺旋或环形形状。多边形坯料也进行螺纹轧制，以制造螺纹成型和自锁螺钉。优选的多边形形状为三棱形，并在平模机中生产。 |
| Cooling curve | 冷却曲线 |
A curve showing the relation between time and temperature during the cooling of a material. 显示材料冷却过程中时间和温度之间关系的曲线。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Active accommodation | 主动适应能力 |
The use of information from sensors, for example, in a vision system, that allows a robot to show accommodation to the environment. 使用来自传感器的信息，例如在视觉系统中，允许机器人显示对环境的适应。 |
| Brittle | 脆性材料 |
A brittle material is one that breaks, often suddenly, with no permanent deformation. Examples of brittle materials are some cast irons, glass, concrete, and some plastics. A bolt is said to be brittle if it will break when stretched only a small amount past its yield point. 脆性材料通常会突然断裂，不会产生永久变形。脆性材料的例子有一些铸铁、玻璃、混凝土和一些塑料。如果螺栓在拉伸时仅超过其屈服点一小部分就会断裂，则称其为脆性螺栓。 |
| Radian (rad) | 弧度（rad） |
A coherent derived SI unit defined as the plane angle subtended at the centre of a circle by an arc having a length equal to the radius. Thus 2π radians are equivalent to 360° and 1 rad ≈ 57.3°. 一种相干导出的国际单位制单位，定义为在圆心处被长度等于半径的弧对向的平面角。因此，2π弧度相当于360°和1弧度≈57.3°. |
| Mole (mol) | 摩尔（mol） |
The base unit of the amount of substance in the SI system. It was previously defined as the amount of substance of a system that contains as many elementary entities as there are atoms in 0.012 kg of carbon-12. From 20 May 2019 it has been defined as the amount of substance containing exactly 6.022 140 76 × 1023 elementary entities. SI国际单位制中物质量的基本单位。此前，它被定义为一个系统中的物质量，该系统包含的基本实体数量与0.012千克碳-12中的原子数量相同。从2019年5月20日起，它已被定义为包含6.02214076×1023个基本实体的物质量。 |
| Circlip | 卡簧 |
(snap ring) An external or internal retaining ring that locates parts of circular cross section in an axial direction. It consists of an incomplete ring, with holes on either side of the gap, that may be expanded by a plier-like tool to pass into a groove in a shaft or contracted to pass into a groove in a bore. （卡环）在轴向定位圆形横截面部分的外部或内部保持环。它由一个不完整的环组成，在间隙的任一侧都有孔，可以通过钳形工具将其扩展以进入轴中的凹槽或收缩以进入孔中的凹槽。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Nanoparticles | 纳米颗粒 |
Particles with dimensions of order 1 nm which have either been introduced into microstructures for reinforcement or are present as impurities. 尺寸为1nm级的颗粒，其已被引入微结构中用于增强或作为杂质存在。 |
| Flattening test | 压扁试验 |
This term as applied to tubing refers to a method of testing a section of tubing by flattening it until the inside walls are parallel and separated by a given distanceusually equal to three times the wall thickness for seamless tubes and five times the wall thickness for lap-welded tubes. Boiler tubes subjected to this test should show no cracks or flaws. The flattening test applied to rivets, consists in flattening a rivet head while hot to a diameter equal to 21⁄2 times the diameter of the shank or body of the rivet. Good rivet steel must not crack at the edges of the flattened head. 该术语适用于管材，是指通过压扁管材直至内壁平行并隔开给定距离（通常等于无缝钢管壁厚的三倍，搭接焊管壁厚的五倍）来测试管材截面的方法。进行该试验的锅炉管应无裂纹或缺陷。适用于铆钉的压扁试验包括在热态下压扁铆钉头，使其直径等于铆钉柄或铆钉体直径的21⁄2倍。良好的铆钉钢不得在扁平头部边缘开裂。 |
| Decalescence | 退色 |
A phenomenon, associated with the transformation of alpha iron to gamma iron on the heating (superheating) of iron or steel, revealed by the darkening of the metal surface owing to the sudden decrease in temperature caused by the fast absorption of the latent heat of transformation. 一种现象，与铁或钢加热（过热）时α铁向γ铁的转变有关，由于转变潜热的快速吸收导致温度突然降低，金属表面变黑。 |
| Acceleration due to gravity | 重力加速度 |
(acceleration of free fall, gravitational acceleration, g) (Unit m/s²) The acceleration of a freely-falling body in a vacuum, with a mean value at sea level of approximately 9.81 m/s². （自由落体加速度，重力加速度，g）（单位m/s²）自由落体在真空中的加速度，在海平面处的平均值约为9.81m/s²。 |
| Cold extrusion | 冷挤压 |
In simplest terms, cold extrusion can be defined as the forcing of unheated metal to flow through a shape-forming die. It is a method of shaping metal by plastically deforming it under compression at room temperature while the metal is within a die cavity formed by the tools. The metal issues from the die in at least one direction with the desired cross-sectional contour, as permitted by the orifice created by the tools. Cold extrusion is always performed at a temperature well below the recrystallization temperature of the metal (about 1100 to 1300 degrees F. for steel) so that work-hardening always occurs. In hot extrusion, recrystallization eliminates the effects of work-hardening, unless rapid cooling of the extrusion prevents recrystallization from being completed. 用简单的术语来说，冷挤压可以定义为迫使未加热的金属流过成形模具。这是一种通过在室温下压缩使金属塑性变形来成形金属的方法，同时金属处于由工具形成的模腔中。金属至少在一个方向上从模具中流出，并具有所需的横截面轮廓，这是由工具产生的孔口所允许的。冷挤压总是在远低于金属再结晶温度的温度下进行（钢约1100至1300华氏度），因此总是发生加工硬化。在热挤压中，再结晶消除了加工硬化的影响，除非挤压的快速冷却阻止再结晶完成。 |
| Prying | 撬动 |
The magnification of an External load by a pseudolever action when that load is an Eccentric tensile load. 当外部荷载为偏心拉伸荷载时，通过伪杠杆作用放大外部荷载。 |
| Strength of materials | 材料强度 |
A confusing name for what is really stress analysis, reflecting older engineering design based upon elasticity and ‘theories of strength’ for different materials, without regard to cracks. 对于真正的应力分析，这是一个具有迷惑性的名称，反映了基于弹性和不同材料的“强度理论”的旧工程设计，而不考虑断裂。 |
| Compression fitting | 压缩接头 |
A screwed joint for pipework made resistant to leakage by permanent deformation of a closely-fitting ring, called a ferrule or olive, on tightening. 一种用于管道的螺纹接头，通过紧密配合的环（称为套圈或橄榄形）在拧紧时的永久变形来防止泄漏。 |
| Biomechanics | 生物力学 |
The application of mechanical-engineering principles, including thermodynamics, fluid mechanics, and solid mechanics together with materials engineering, to biological systems. 机械工程原理（包括热力学、流体力学和固体力学以及材料工程）在生物系统中的应用。 |
| Absolute value error | 绝对值误差 |
The magnitude of the error dlsregarding the algebraic sign, or, for a vectorial error, disregarding its function. 关于代数符号的误差幅度，或者，对于矢量误差，不考虑其函数。 |
| Helical spring | 螺旋弹簧 |
A spring manufactured by forming elastic wire into a helix which may be cylindrical, conical, barrel-shaped, or hourglass in overall form. Closed-coiled springs are used in tension; open-coiled in both tension and compression. 一种弹簧，通过将弹性线材制成螺旋形而制成，螺旋形的整体形状可以是圆柱形、圆锥形、桶形或沙漏形。拉力采用闭合盘簧；在拉伸和压缩中都开卷。 |
| Free joint | 万向节 |
The joint on a robot arm and wrist that causes the greatest end-effector movement when a specified force is applied to the end effector, i.e. that has the lowest stiffness with regard to the force. 机器人手臂和手腕上的关节，当指定的力施加到末端执行器时，会导致末端执行器的最大运动，即相对于力具有最低刚度。 |
| Total combustion air (Unit kg/s) | 总燃烧空气（单位：kg/s） |
1. The combination of the stoichiometric flow of air required for combustion together with any excess air. 2. The flow of fresh air into a boiler plus any flue gas recirculated. 1.燃烧所需的化学计量空气流与任何过量空气的组合。2.进入锅炉的新鲜空气流加上再循环的任何烟气。 |
| Induction tempering | 感应回火 |
Tempering of steel using low-frequency electrical induction heating. 钢的回火采用低频电感应加热。 |
| Total energy (Unit J) | 总能量（单位J） |
The sum of all forms of energy associated with a system, including kinetic, potential, internal, magnetic, chemical, and electrical energy. 与系统相关的所有形式能量的总和，包括动能、势能、内能、磁能、化学能和电能。 |
| Gage length | 标距 |
The original length of the portion of a specimen over which strain, change of length, or other characteristics are determined. 确定应变、长度变化或其他特性的试样部分的原始长度。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Concentration ratio | 浓度比 |
For a concentrating solar collector, the ratio of the projected area of the concentrator facing the solar beam to the actual area of the receiver. 对于聚光太阳能集热器，集中器面向太阳光束的投影面积与接收器的实际面积之比。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Castellated nut | 槽形螺母 |
A nut having slots across the hexagonal faces, used with a bolt having a drilled hole so that a split (cotter) pin may be inserted through both nut and bolt to prevent unscrewing. 一种在六角面上有槽的螺母，与具有钻孔的螺栓一起使用，以便将开口（开口）销插入穿过螺母和螺栓以防止拧松。 |
| Brine quenching | 盐水淬火 |
A quench in which brine (salt water-chlorides, carbonates, and cyanides) is the quenching medium. The salt addition improves the efficiency of water at the vapor phase or hot stage of the quenching process. 一种淬火，其中盐水（盐水-氯化物、碳酸盐和氰化物）是淬火介质。添加盐提高了水在淬火过程的气相或热阶段的效率。 |
| Newton’s law of viscosity | 牛顿内摩擦定律 |
The shear stress between two parallel layers of fluid is proportional to the velocity of one relative to that of the other, and inversely proportional to the distance between them. The constant of proportionality is the dynamic viscosity μ. For a Newtonian fluid μ is independent of pressure gradient, shear stress, and strain, but may change with temperature and pressure. 两个平行流体层之间的剪切应力与其中一层相对于另一层的速度成正比，与它们之间的距离成反比。比例常数是动态粘度μ。对于牛顿流体，μ与压力梯度、剪切应力和应变无关，但可能随温度和压力而变化。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Fin neck carriage bolt | 翼颈圆头方颈螺栓 |
A plain, circular, oval head bolt with two oppositely located fins to prevent rotation. 一种普通的圆形椭圆头螺栓，有两个相对的翼片以防止旋转。 |
| Vacuum annealing | 真空退火 |
Annealing carried out at subatmospheric pressure. 在低于大气压的压力下进行退火。 |
| Barrier protection | 屏障保护 |
The coating on a fastener is said to provide barrier protection if it merely isolates the fastener from the environment. Paint, for example, provides barrier protection. 如果仅将紧固件与环境隔离，则据说紧固件上的涂层可提供屏障保护。例如，油漆提供屏障保护。 |
| Heat-treatable alloy | 可热处理合金 |
An alloy that can be hardened by heat treatment. 一种可以通过热处理硬化的合金。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Constant-mesh gearbox | 恒啮合齿轮箱 |
A gearbox in which the pairs of gears giving different speed ratios are constantly in mesh, different ratios being obtained by connecting or disconnecting the relevant gear to the driving shaft. 一种齿轮箱，其中提供不同速比的齿轮对始终啮合，通过将相关齿轮连接或断开驱动轴获得不同的速比。 |
| Notch depth | 缺口深度 |
The distance from the surface of a notched test specimen to the bottom of the notch. In a cylindrical test specimen, the percentage of the original cross-sectional area removed by machining an annular groove. 从缺口试样表面到缺口底部的距离。在圆柱形试样中，通过加工环形槽去除的原始横截面积的百分比。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Poisson’s ratio (ν) | 泊松比（ν） |
The absolute value of the ratio of transverse (lateral) strain to the corresponding axial strain resulting from uniformly distributed axial stress below the proportional limit of the material. 横向（侧向）应变与相应轴向应变之比的绝对值，该比值由低于材料比例极限的均匀分布的轴向应力产生。 |
| Starting friction | 起动摩擦 |
(limiting friction, static friction, stiction) (Unit N) The force required to initiate movement between two bodies in contact. （极限摩擦力、静摩擦力、粘滞）（单位N）在两个接触物体之间启动运动所需的力。 |
| Torsion-bar suspension | 扭杆悬架 |
A type of motor-vehicle suspension in which one end of a torsion bar is rigidly fixed to the chassis while the other carries a lever to which are attached the components that carry a wheel. In a torsion-beam suspension, a beam connects the wheels on either side of the vehicle. 一种汽车悬架，其中扭力杆的一端刚性固定在底盘上，而另一端带有一个杠杆，杠杆上连接着承载车轮的部件。在扭转梁悬架中，梁连接车辆两侧的车轮。 |
| Rupture stress | 断裂应力 |
The stress at failure. Also known as breaking stress. 失效时的应力。也称为破裂应力。 |
| Electrolyte | 电解质 |
The liquid with which the Electrodes of a battery or Corrosion cell are wetted. 润湿电池或腐蚀电池电极的液体。 |
| Transgranular fracture | 穿晶断裂 |
Fracture in crystalline materials where the path of cracking is predominantly across grains. 晶体材料中的断裂，其中裂纹路径主要跨越晶粒。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Impact testing | 冲击测试 |
Determination of the mechanical properties of materials under high-rate conditions. Often determined from the behaviour of a testpiece when struck by a pendulum or a weight falling from a known height, or when sandwiched between two Hopkinson bars. 在高速条件下测定材料的机械性能。通常根据测试件在被钟摆撞击或从已知高度坠落的重物或夹在两个霍普金森棒之间时的行为来确定。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Die | 模具 |
1. A tool having an appropriately-shaped hole through which material may be extruded or drawn. 2. A tool employed in forging. 3. A block having the male or female shape employed in stamping operations. 4. A thick circular disc, driven by a die wrench, with internally-threaded cutting edges for producing a screw thread. A die wrench (die stock) holds a screw-cutting die and has two projecting arms for applying the torque necessary to cut the thread. A die having a hexagonal or square shape (die nut), driven by a spanner, is used in confined spaces where a die wrench cannot be rotated through a full circle. 1.一种具有适当形状的孔的工具，通过该孔可以挤压或拉伸材料。2.一种用于锻造的工具。3.一种用于冲压操作的具有阳或阴形状的块体。4.一种由模具扳手驱动的厚圆盘，具有用于产生螺纹的内螺纹切削刃。冲模扳手（冲模）装有一个螺旋切割模，并有两个突出臂，用于施加切割螺纹所需的扭矩。由扳手驱动的六边形或方形模具（模具螺母）用于模具扳手无法旋转一整圈的受限空间。 |
| Computer numerical control (CNC) | 计算机数控（CNC） |
A term relating to machine tools in which the movements of a tool and/or the workpiece are controlled by computer. 与机床相关的术语，其中工具和/或工件的运动由计算机控制。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Vapour–pressure curve | 蒸汽压力曲线 |
For a pure substance, the curve of saturation pressure plotted vs saturation temperature. 对于纯物质，绘制了饱和压力与饱和温度的曲线。 |
| Acid rain | 酸雨 |
Any form of precipitation, including rain, snow, sleet, fog, dew, and particulates, which contains higher than normal levels of sulfuric and nitric acids. These acids result from natural and man-made emissions of sulfur dioxide and oxides of nitrogen, respectively. Acid soot consists of unburned carbon particles, typically larger than 10 μm, in the atmosphere contaminated with sulfuric acid. The particles result from poor combustion of fossil fuels. 任何形式的降水，包括雨、雪、雨夹雪、雾、露水和颗粒物，其中含有高于正常水平的硫酸和硝酸。这些酸分别来自二氧化硫和氮氧化物的自然排放和人为排放。酸烟灰由未燃烧的碳颗粒组成，通常大于10微米，在被硫酸污染的大气中。这些颗粒是化石燃料燃烧不良造成的。 |
| Wrap-around bend | 环绕弯曲 |
The bend obtained when a specimen is wrapped in a closed helix around a cylindrical mandrel. This term is sometimes applied to a semiguided bend of 180° or less. 当试样缠绕在圆柱形心轴周围的闭合螺旋中时获得的弯曲。该术语有时适用于180°或更小的半导弯曲。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Variance | 方差 |
A measure of the squared dispersion of observed values or measurements expressed as a function of the sum of the squared deviations from the population mean or sample average. 观测值或测量值的平方离散度的度量，表示为总体平均值或样本平均值的平方偏差之和的函数。 |
| Surface hardening | 表面硬化 |
A generic term covering several processes applicable to a suitable ferrous alloy that produces, by quench hardening only, a surface layer that is harder or more wear resistant than the core. There is no significant alteration of the chemical composition of the surface layer. The processes commonly used are carbonitriding, carburizing, induction hardening, flame hardening, nitriding, and nitrocarburizing. Use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于仅通过淬火硬化产生比型芯更硬或更耐磨的表面层的合适铁合金的几种工艺。表面层的化学成分没有显著改变。常用的工艺有碳氮共渗、渗碳、感应淬火、火焰淬火、氮化和氮碳共渗。最好使用适用的特定工艺名称。 |
| Ductile cast iron | 球墨铸铁 |
A cast iron that has been treated while molten with an element such as magnesium or cerium to induce the formation of free graphite as nodules or spherulites, which imparts a measurable degree of ductility to the cast metal. Also known as nodular cast iron, spherulitic graphite cast iron and SG iron. 一种铸铁，在熔融时用镁或铈等元素进行处理，以诱导游离石墨形成为球粒或球晶，从而赋予铸造金属可测量的延展性。又称球墨铸铁、球晶石墨铸铁和SG铸铁。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Atomic volume | 原子体积 |
Volume of unit cell per atom. 每个原子的晶胞体积。 |
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Turbine | 涡轮 |
A turbomachine in which a rotor (turbine wheel) or impeller is caused to rotate and convert flow energy into shaft power or thrust. 转子（涡轮）或叶轮旋转并将流动能量转换为轴功率或推力的涡轮机。 |
| Verification | 检验 |
Checking or testing an instrument to ensure conformance with a specification. 检查或测试仪器以确保符合规范。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Widmanstätten structure | 魏氏组织 |
A structure characterized by a geometrical pattern resulting from the formation of a new phase along certain crystallographic planes of the parent solid solution. The orientation of the lattice in the new phase is related crystallographically to the orientation of the lattice in the parent phase. The structure is readily produced in many alloys by appropriate heat treatment. 一种结构，其特征是沿母体固溶体的某些晶体学平面形成新相而形成的几何图案。新相中晶格的取向在晶体学上与母相中晶格的定向相关。通过适当的热处理，在许多合金中容易产生这种结构。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| Composite material | 复合材料 |
(composite structure) A general term used of two or more materials or structures acting in combination (e.g. concrete, reinforced concrete, filamentreinforced polymers, laminated materials, particulate-reinforced materials, flitched beams), resulting in values of strength, stiffness, or toughness greater than the base matrix material alone. （复合结构）用于组合作用的两种或多种材料或结构的通用术语（例如混凝土、钢筋混凝土、纤维增强聚合物、层压材料、颗粒增强材料、切割梁），从而产生强度、刚度或韧性值大于单独的基体材料。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Cohesive zone | 凝聚力区 |
In fracture-mechanics modelling and simulation, the region at the crack tip over which an assumed traction (load-displacement) relation has to be overcome to permit initiation and propagation of a crack. 在断裂力学建模和模拟中，必须克服假定的牵引（载荷-位移）关系以允许裂纹萌生和扩展的裂纹尖端区域。 |
| Cleavage | 分裂 |
The tendency of a material to cleave or split along definite crystallographic planes. 材料沿特定晶面劈裂或分裂的趋势。 |
| Shear modulus (G) | 剪切模量（G） |
The ratio of shear stress to the corresponding shear strain for shear stresses below the proportional limit of the material. Values of shear modulus are usually determined by torsion testing. Also known as modulus of rigidity. 对于低于材料比例极限的剪切应力，剪切应力与相应剪切应变之比。剪切模量值通常通过扭转试验确定。也称为刚度模量。 |
| Equation, long form | 方程，长格式 |
An equation which relates the torque applied to a bolt to the preload created in it, and involves fastener geometry and the coefficient of friction between mating surfaces. A theoretical equation based on rigid body mechanics and the assumption that the geometry of the fastener is perfectly described by blueprint dimensions. 将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来的方程，该方程涉及紧固件几何形状和配合面之间的摩擦系数。基于刚体力学和紧固件几何结构由蓝图尺寸完美描述的假设的理论方程。 |
| Creep modulus (Unit Pa) | 蠕变模量（单位Pa） |
The ratio of stress/strain at a chosen strain level obtained from creep tests, often plotted against time to show changes in stiffness. 从蠕变测试中获得的选定应变水平下的应力/应变比，通常随时间绘制以显示刚度的变化。 |
| Acicular ferrite | 针状铁素体 |
A highly substructured non-equiaxed ferrite that forms upon continuous cooling by a mixed diffusion and shear mode of transformation that begins at a temperature slightly higher than the temperature transformation range for upper bainite. It is distinguished from bainite in that it has a limited amount of carbon available; thus, there is only a small amount of carbide present. Ferrite crystallite growing, apparently, as in the course of bainitic transformation. It has a lath-like shape and an increased dislocation 一种高度亚结构的非等轴铁素体，在连续冷却时通过混合扩散和剪切相变模式形成，其开始温度略高于上贝氏体的温度转变范围。它与贝氏体的区别在于它的碳含量有限。因此，仅存在少量碳化物。显然，铁素体微晶在贝氏体转变过程中生长。它具有板条状的形状和增加的位错。 |
| Minimum stress-intensity factor (Kmin) | 最小应力强度因子（Kmin） |
In fatigue, the minimum value of the stress-intensity factor in a cycle. This value corresponds to the minimum loadwhen the load ratio is 0 and is taken to be 0 when the load ratio is ≤0. 在疲劳中，一个循环中应力强度因子的最小值。该值对应于负载比为0时的最小负载，当负载比为≤0 |
| Tribology | 摩擦学 |
The science and technology concerned with interacting surfaces in relative motion. 与相对运动中相互作用的表面有关的科学和技术。 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Surface hardness | 表面硬度 |
(superficial hardness) Indentation hardness on, and for some distance below, the surface of a component, as opposed to its bulk hardness. Depending on the resolution required, micro- or nano-hardness testing machines are employed. （表面硬度）与整体硬度相反，部件表面及其下方一定距离的压痕硬度。根据所需的分辨率，可使用微型或纳米硬度测试机。 |
| Repeatability | 重复性 |
A term used to refer to the test-result variability associated with a limited set of specifically defined sources of variability within a single laboratory. 一个术语，用于指与单个实验室内一组有限的特定变异源相关的测试结果变异性。 |
| Jack | 杰克装置 |
A lifting device that exerts large forces over small displacements, achieved by mechanical gearing or hydraulics. 通过机械传动或液压装置在小位移上施加大力的提升装置。 |
| Transverse direction | 横向 |
Literally, the “across” direction, usually signifying a direction or plane perpendicular to the direction of working. In rolled plate or sheet, the direction across the width is often called long transverse, and the direction through the thickness, short transverse. 从字面上看，“横穿”方向，通常表示与工作方向垂直的方向或平面。在轧制钢板或薄板中，横跨宽度的方向通常称为长横向，穿过厚度的方向称为短横向。 |
| Wrought iron | 锻铁 |
A highly ductile (but anisotropic) type of iron containing elongated slag fibres that resulted from the method of manufacture in which excess carbon in pig iron was burnt and worked out. The yield strength is some 200 MPa, tensile strength 320 MPa, and reduction of area on a 50-mm gauge length up to 35%. Now replaced by steel. 一种高韧性（但各向异性）的铁，含有细长的矿渣纤维，由生铁中多余的碳燃烧和加工的制造方法产生。屈服强度约为200MPa，抗拉强度为320MPa，50mm标距上的面积缩减率高达35%。现在被钢所取代。 |
| Structure | 结构体 |
An assembly, usually load bearing, of connected (pinned, riveted, screwed, bolted, welded, etc.) components, such as bars, tubes, beams, and plates. 由连接（销接、铆接、螺纹连接、螺栓连接、焊接等）部件组成的组件，通常为承重组件，如杆、管、梁和板。 |
| Temporal decomposition | 时间分解 |
The splitting of a control problem into parts with relatively short and long time constant so that different controllers may be used for the different parts. 将控制问题分解为具有相对较短和较长时间常数的部分，以便不同的部分可以使用不同的控制器。 |
| Strength (Unit Pa) | 强度（单位Pa） |
The maximum stress, in tension, compression, shear, or combinations thereof, that may be monotonically applied to a material, component, or structure before failure (defined as fracture, yielding, buckling, etc. as appropriate). 在破坏前（视情况定义为断裂、屈服、屈曲等），材料、部件或结构在拉伸、压缩、剪切或其组合中可能单调施加的最大应力。 |
| Starting torque (Unit N.m) | 起动扭矩（单位：N.m） |
The torque developed by a motor at zero rotational speed in order to initiate rotation of the applied load. 电机在零转速下产生的扭矩，以启动所施加负载的旋转。 |
| Torsion bar | 扭杆 |
A metal bar designed to act as an elastic spring when torque is applied. 当施加扭矩时用作弹性弹簧的金属棒。 |
| Oxidized surface (on steel) | 氧化表面（在钢上） |
Surface having a thin, tightly adhering, oxidized skin (from straw to blue in color), extending in from the edge of a coil or sheet. Sometimes called annealing border. 表面具有薄的、紧密粘附的氧化皮（从稻草色到蓝色），从线圈或薄片的边缘延伸。有时称为退火边界。 |
| Allowable stress design | 许用应力设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Purposely underestimates the strengths of bolts and joint materials to introduce safety factors into the design of structural steel joints. It is an alternative to the more recently defined load and resistance factor design procedure. 结构连接研究委员会为AISC制定的设计程序。故意低估螺栓和接头材料的强度，以便在结构钢接头的设计中引入安全系数。它是最近定义的荷载和阻力系数设计程序的替代方法。 |
| Pressure storage tank | 压力贮存器 |
(pressure vessel) A closed container for storing gases or volatile liquids, such as liquefied gases, at pressures significantly above atmospheric pressure. Such tanks are commonly cylindrical with domed ends, spherical, spheroidal, torispherical or hemispherical. （压力容器）密闭容器：在大气压以上的压力下储存气体或挥发性液体，如液化气体的密闭容器。此类贮存器通常为圆柱形，具有半球形端部、球形、球面或半球形。 |
| Torque monitor | 扭矩监测器 |
A torque tool control system which monitors the amount of torque being developed by the tool during use, but does not control the tool or the torque produced. 一种扭矩工具控制系统，监控工具在使用过程中产生的扭矩量，但不控制工具或产生的扭矩。 |
| Embedment | 嵌入 |
Localized plastic deformation in heavily loaded fasteners allows one part to sink into, or smooth the surface of, a softer or more heavily loaded second part. Nuts embed themselves in joint surfaces. Bolt threads embed themselves in nut threads, etc. 重载紧固件中的局部塑性变形允许一个零件陷入较软或更重载的第二零件中，或使其表面光滑。螺母嵌入接合面中。例如螺栓螺纹嵌入螺母螺纹等。 |
| Resistance thermometer | 电阻温度计 |
A thermometer in which the sensing element is basically a metal wire, usually of platinum, for which the variation of resistance with temperature is known accurately. A resistance pyrometer is a resistance thermometer intended for use up to about 1 000°C. 一种温度计，其中传感元件基本上是一根金属线，通常是铂，可以准确地知道电阻随温度的变化。电阻高温计是一种电阻温度计，用于高达约1000°C的温度。 |
| Compression ratio | 压缩率 |
The volume of a combustion chamber with the piston at the top of its stroke as a proportion of the total volume of the cylinder with the piston at the bottom of its stroke. For a piston engine, if the swept volume is SW and the clearance volume is CL, the compression ratio is given by ( SW + CL)/CL, i.e. it is a volume ratio rather than a pressure ratio. 活塞位于其冲程顶部的燃烧室的容积与活塞位于其冲程底部的气缸总体积的比例。对于活塞发动机，如果扫气量为SW，间隙容积为CL，则压缩比由(SW+CL)/CL给出，即它是体积比而不是压力比。 |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Fatigue strength | 疲劳强度 |
The stress to which a metal can be subjected for a specified number of cyclic changes of stress. The maximum stress that can be sustained for a specified number of cycles without failure. The value of the maximum stress and the stress ratio also should be stated. 金属在指定数量的应力循环变化下可以承受的应力。可以在指定的循环次数内持续而不失效的最大应力。还应说明最大应力值和应力比。 |
| Quench hardening | 淬火硬化 |
(1) Hardening suitable alpha-beta alloys (most often certain copper to titanium alloys) by solution treating and quenching to develop a martensitic-like structure. (2) In ferrous alloys, hardening by austenitizing and then cooling at a rate such that a substantial amount of austenite transforms to martensite. （1）通过固溶处理和淬火硬化合适的α-β合金（通常是某些铜-钛合金），以形成类似马氏体的结构。（2）在铁合金中，通过奥氏体化硬化，然后以一定速度冷却，使大量奥氏体转变为马氏体。 |
| Interrupted quenching | 间断淬火 |
A quenching procedure in which the workpiece is removed from the first quench at a temperature substantially higher than that of the quenchant and is then subjected to a second quenching system having a different cooling rate than the first. 在该淬火过程中，工件在显著高于淬火剂的温度下从第一次淬火中取出，然后经受具有不同于第一次淬火的冷却速率的第二次淬火系统。 |
| Elastic constants | 弹性常数 |
The factors of proportionality that relate elastic displacement of a material to applied forces. 将材料的弹性位移与施加的力相关联的比例因子。 |
| Hydrogen damage | 氢损伤 |
A general term for the embrittlement, cracking, blistering, and hydride formation that can occur when hydrogen is present in some metals. 当氢存在于某些金属中时可能发生的脆化、开裂、起泡和氢化物形成的总称。 |
| Cotter pin | 开口销 |
(cotter) 1. A tapered wedge or pin passing through a tapered slot or hole in one member and bearing against a second member to fix it in location. 2. A split cotter is commonly called a split pin. A pin with two legs. With legs together, the pin is placed through the hole in a clevis pin. The legs are then opened outward to prevent the cotter pin from backing out of the hole. The cotter pin, in turn, prevents the load-bearing clevis pin from backing out of its retaining hole. （开口）1.锥形楔子或销钉穿过一个构件中的锥形槽或孔，并支撑在第二个构件上以将其固定到位。2.开口开口通常称为开口销。相当于有两条腿的别针，将支腿放在一起，销钉穿过U形夹销上的孔。然后将支腿向外打开以防止开口销从孔中退出。开口销反过来防止承重U形夹销从其固定孔中退出。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Coarse threads | 粗螺纹 |
Threads with relatively large separation between corresponding points on the threads. 螺纹上相应点之间的间距相对较大的螺纹。 |
| Shear lip | 剪切唇 |
A narrow, slanting ridge along the edge of a fracture surface. The term sometimes also denotes a narrow, often crescent-shaped, fibrous region at the edge of a fracture that is otherwise of the cleavage type, even though this fibrous region is in the same plane as the rest of the fracture surface. 沿断裂面边缘的狭窄倾斜脊。该术语有时还表示断裂边缘处的狭窄、通常为新月形的纤维区域，否则为解理型，即使该纤维区域与断裂表面的其余部分位于同一平面内。 |
| Kinetic energy | 动能 |
Energy that an object possesses because it is in motion. It is the energy given to an object to set it in motion. On impact, it is converted into other forms of energy such as strain, heat, sound and light. 物体因运动而拥有的能量。它是赋予物体使其运动的能量。撞击时，它被转换成其他形式的能量，如应变、热、声和光。 |
| Heat-capacity ratio (c*) | 热容量比（c*） |
A non-dimensional parameter that arises in the analysis of heat exchangers, defined as the ratio cMIN/cMAX where cMIN is the heat-capacity rate c for the fluid with the smaller value of c and cMAX the value for the fluid with the larger value of c. Different flow rates and specific-heat values give rise to different values for c. 热交换器分析中出现的无量纲参数，定义为比率cMIN/cMAX其中cMIN是流体的热容率c，c值较小，cMAX是流体的值具有较大的c值。不同的流速和比热值产生不同的c值。 |