| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Transverse strain | 横向应变 |
Linear strain in a plane perpendicular to the loading axis of a specimen. 垂直于试样加载轴的平面内的线性应变。 |
| Shear joint | 剪切接头 |
A joint which is subjected primarily to loads acting more or less perpendicular to the axes of the bolts. 主要承受或多或少垂直于螺栓轴线的载荷的接头。 |
| A-basis | A-基础 |
Mechanical property value above which at least 99% of the population of values is expected to fall, with a confidence of 95%. Also called A-allowable. 机械性能值超过该值时，至少99%的值预计会下降，置信度为95%。也被称为A-容许。 |
| Abradant | 研磨剂 |
The differently sized grits of hard materials such as emery employed for grinding, polishing, etc. The abrasive grade is determined by the grit size (grit number) originally related to the hole sizes in wire sieves. 用于研磨、抛光等的硬质材料（例如金刚砂）的不同尺寸粒度。磨料等级由最初与金属丝筛孔尺寸相关的粒度（粒度数）决定。 |
| Car furnace | 车炉 |
A batch-type furnace using a car on rails to enter and leave the furnace area. Car furnaces are used for lower stress relieving ranges. 一种间歇式炉，使用轨道上的小车进出炉区。汽车炉用于较低的应力消除范围。 |
| Congruent melting point (Unit K) | 全等熔点（单位K） |
congruent melting point (Unit K) The temperature at which a solid substance at a specified pressure changes phase to a liquid of identical composition. 一致的熔点（单位K）固体物质在特定压力下相变为具有相同成分的液体时的温度。 |
| Transformation temperature | 相变温度 |
The temperature at which a change in phase occurs. The term is sometimes used to denote the limiting temperature of a transformation range. The following symbols are used for iron and steels. 发生相位变化的温度。该术语有时用于表示转变范围的极限温度。以下符号用于钢铁。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Cone pulley | 锥轮 |
A stepped pulley having several diameters which, when linked by a laterallymoveable transmission belt to a corresponding pulley, gives a series of speed ratios. 具有多种直径的阶梯式皮带轮，当通过可横向移动的传动带连接到相应的皮带轮时，会产生一系列速比。 |
| Flame hardening | 火焰硬化 |
A process for hardening the surfaces of hardenable ferrous alloys in which an intense flame is used to heat the surface layers above the upper transformation temperature, whereupon the workpiece is immediately quenched. 一种用于硬化可硬化铁合金表面的工艺，其中使用强烈的火焰将表面层加热到转变温度上限以上，然后立即对工件进行淬火。 |
| Congruent transformation | 全等变换 |
An isothermal or isobaric phase change in which both of the phases concerned have the same composition throughout the process. 等温或等压相变，其中相关的两个相在整个过程中具有相同的成分。 |
| International Bureau of Weights and Measures | 国际度量衡局IBWM |
(BIPM, Bureau International des Poids et Mesures) The intergovernmental organization which has the mandate to provide the basis for a single, coherent system of measurements, traceable to the International System of Units. （BIPM，国际计量局）政府间组织，其任务是为可追溯到国际单位制的单一、一致的计量系统提供基础。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Centrifugal compressor | 离心式压缩机 |
A compressor in which kinetic energy is added to a fluid by radial acceleration in an impeller and then converted into a pressure increase by flow though a diffuser. 一种压缩机，其中动能通过叶轮中的径向加速度添加到流体中，然后通过扩散器的流动转换为压力增加。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Coefficient of thermal expansion | 热膨胀系数 |
(1) Change in unit of length (or volume) accompanying a unit change of temperature, at a specified temperature. (2) The linear or volume expansion of a given material per degree rise of temperature, expressed at an arbitrary base temperature or as a more complicated equation applicable to a wide range. （1） 单位长度（或体积）随温度单位变化的变化。（2） 给定材料每上升一度的线性或体积膨胀，在任意基础温度下表示，或作为适用于宽范围的更复杂方程表示。 |
| Humidify | 加湿 |
To add water vapour to air or another gas to increase its humidity. 将水蒸气添加到空气或其他气体中以增加其湿度。 |
| Bearing test | 轴承测试 |
A method of determining the response to stress (load) of metal products that are subjected to riveting, bolting, or a similar fastening procedure. The purpose of the test is to determine the bearing strength of the material and to measure the bearing stress versus the deformation of the hole created by a pin or rod of circular cross section that pierces the sheet perpendicular to the surface. 一种确定经受铆接、螺栓连接或类似紧固程序的金属产品对应力（载荷）的响应的方法。测试的目的是确定材料的承载强度，并测量承载应力与由垂直于表面刺穿板材的圆形横截面的销或杆产生的孔的变形。 |
| Extra spring | 额外弹簧 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state above full hard beyond which further cold work will not measurably increase the strength and hardness. 有色金属合金和一些铁合金的回火状态，大约对应于高于全硬的冷加工状态，超过该状态进一步冷加工将不会显着增加强度和硬度。 |
| Torricellean barometer | 托里塞莱气压计 |
A vertical glass tube with its upper end sealed and the lower end submerged in a pool of mercury. The space above the mercury is under vacuum. The height to which the mercury rises up the tube is a measure of the barometric pressure. 一种垂直的玻璃管，上端密封，下端浸入汞池中。水银上方的空间处于真空状态。水银在管道中上升的高度是大气压力的量度。 |
| Bearing yield strength | 轴承屈服强度 |
The bearing stress at which a material exhibits a specified limiting deviation from the proportionality of bearing stress to bearing strain in a bearing test. 在轴承测试中，材料在轴承应力与轴承应变的比例之间表现出特定的极限偏差时的轴承应力。 |
| Failure of the joint | 连接失效 |
Failure of a bolted joint to behave as intended by the designer. Failure can be caused or accompanied by broken or lost bolts, but can also mean joint slip or leakage from a gasketed joint even if all bolts still remain whole and in place. Common reasons for joint failure include vibration loosening, poor assembly practices, improper design, unexpected service loads or conditions, etc. 螺栓连接未达到设计者的预期性能。故障可能由螺栓断裂或丢失引起或伴随而来，但也可能意味着即使所有螺栓仍保持完整和就位，也存在接头滑动或垫圈接头泄漏。接头故障的常见原因包括振动松动、装配不当、设计不当、意外的工作负载或条件等。 |
| Bearing stress | 承受应力 |
The force per unit of bearing area. 每单位承载面积的力。 |
| Toggle (toggle clamp) | 拨动（拨动夹） |
A device consisting of two pinned levers that are almost in line between two end points in the same plane. Bringing the levers into line generates large forces between the ends. Used to obtain a large mechanical advantage or as a locking mechanism. 由两个销杆组成的装置，在同一平面的两个端点之间几乎成一条直线。将杠杆对齐会在端部之间产生较大的力。用于获得较大的机械优势或用作锁定机构。 |
| Vertical engine | 立式发动机 |
A piston engine having the cylinders above the crankshaft. 气缸位于曲轴上方的活塞发动机。 |
| Secondary stresses (Unit Pa) | 二次应力（单位Pa） |
Stresses different from those induced by the major loading but nevertheless resulting from the major loads; for example, the hoop stresses that occur around the circumference of barrelled compression testpieces and forgings. 与主要荷载引起的应力不同，但主要荷载产生的应力；例如，桶装压缩试件和锻件周围产生的环向应力。 |
| Specimen | 样品 |
A test object, often of standard dimensions or configuration, that is used for destructive or nondestructive testing. One or more specimens may be cut from each unit of a sample. 用于破坏性或无损检测的测试对象，通常具有标准尺寸或配置。可以从样品的每个单位切割一个或多个样品。 |
| Ventilation | 通风系统 |
A system for circulating fresh air in a room, building, passenger vehicle, orother enclosed space. 在房间、建筑物、乘用车或其他封闭空间中循环新鲜空气的系统。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Hydrogen damage | 氢损伤 |
A general term for the embrittlement, cracking, blistering, and hydride formation that can occur when hydrogen is present in some metals. 当氢存在于某些金属中时可能发生的脆化、开裂、起泡和氢化物形成的总称。 |
| Circlip | 卡簧 |
(snap ring) An external or internal retaining ring that locates parts of circular cross section in an axial direction. It consists of an incomplete ring, with holes on either side of the gap, that may be expanded by a plier-like tool to pass into a groove in a shaft or contracted to pass into a groove in a bore. （卡环）在轴向定位圆形横截面部分的外部或内部保持环。它由一个不完整的环组成，在间隙的任一侧都有孔，可以通过钳形工具将其扩展以进入轴中的凹槽或收缩以进入孔中的凹槽。 |
| Sample variance (s²) | 样本方差（s²） |
The sum of the squares of the differences between each observed value and the sample average divided by the sample size minus one. It is a point estimate of the population variance. 每个观测值与样本平均值之差的平方和除以样本大小减1。它是总体方差的点估计。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Imperial system of units | 英制单位 |
British imperial system of units) An obsolete system of units first defined in the British Weights and Measures Act of 1824. Its three base units were second (time), yard (length), and pound avoirdupois (mass). The imperial unit of capacity was the gallon. The many associated units introduced subsequently include cubic inch, cubic foot, cubic yard, pint, and quart for both liquid and dry measures of capacity (i.e. volume); ounce, hundredweight, short and long ton for avoirdupois mass; poundal for force; minute and hour for time; fahrenheit for temperature; and British thermal unit for energy. Closely related to the imperial system of units is the US customary system of units. Each imperial unit is now legally defined in terms of the metric (i.e. SI) equivalent. （英帝国单位制）1824年英国度量衡法首次定义的已被淘汰的单位制。其三个基本单位为秒（时间）、码（长度）和磅（质量）。容量的英制单位是加仑。随后引入的许多相关单位包括立方英寸、立方英尺、立方码、品脱和夸脱，用于液体和干燥容量测量（即体积）；盎司，百分之一百重量，短吨和长吨，以保证重量；磅达表示力；以分钟和小时表示时间；华氏温度；英国热能单位。与帝国单位制密切相关的是美国习惯单位制。现在，每个英制单位在法律上都是以公制（即SI）当量来定义的。 |
| Strain hardening | 应变硬化 |
An increase in hardness and strengthcaused by plastic deformation at temperatures below the recrystallization range. Also known as work hardening. (workhardening) The increase in stress above the initial yield stress required to deform a metal to greater strains in the plastic range at temperatures below the recrystallization range (cold working). Unloading after some strain or work input gives a harder and stronger material. 在低于再结晶范围的温度下，塑性变形导致硬度和强度的增加。也称为加工硬化。（加工硬化）在低于再结晶范围（冷加工）的温度下，使金属在塑性范围内变形至更大应变所需的高于初始屈服应力的应力增加。在一定的应变或功输入后卸载，会得到更硬、更强的材料。 |
| Pitch-circle diameter (Unit m) | 节圆直径（单位：m） |
The diameter of the circle (the pitch circle) centred on a component’s axis, around which holes or bolts are equally spaced. 以部件轴为中心的圆（节圆）的直径，孔或螺栓围绕其等距分布。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Nonlinear behavior | 非线性行为 |
A fastener or joint system is said to exhibit nonlinear behavior when the relationship between the External load on the joint and deformation of the parts is nonlinear, or when the relationship between increasing Preload and deformation is nonlinear. 当接头上的外部载荷与零件变形之间的关系是非线性的，或者当增加的预载荷与变形之间的联系是非线性的时，可以说紧固件或接头系统表现出非线性行为。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Normal stress (Unit N) | 法向应力（单位：N） |
The stress component perpendicular to a plane on which forces act. Normal stress may be either tensile stress or compressive stress. A stress in a fluid (such as pressure) or a solid, that is perpendicular to the surface on which it acts. The surface may be a real external surface or an imaginary internal one. 垂直于受力平面的应力分量。法向应力可以是拉应力或压应力。流体（如压力）或固体中垂直于其作用表面的应力。该表面可以是真实的外表面或假想的内表面。 |
| Austenite finish temperature (Af) | 奥氏体完成温度（Af） |
Temperature at which the transformation of martensite into austenite completes upon heating. The same designation is also applied to nonferrous alloys in which martensite transforms into some parent phase. 加热时马氏体转变为奥氏体的温度。相同的名称也适用于马氏体转变为某些母相的有色合金。 |
| Kilo (k) | 千（k） |
An SI unit prefix indicating a multiplier of 103; thus kilometre (km) is a unit of length equal to one thousand metres. 表示乘法器103的SI单位前缀；1千米是长度单位，等于1000米。 |
| Fatigue wear | 疲劳磨损 |
Wear of a solid surface caused by fracture arising from material fatigue. 由材料疲劳引起的断裂引起的固体表面磨损。 |
| Air-cooled engine | 风冷发动机 |
An internal-combustion engine directly cooled by airflow, rather than by water flowing through the engine block being cooled by a radiator. 一种由气流直接冷却的内燃机，而不是通过流经发动机缸体的水被散热器冷却。 |
| Damage | 损伤 |
1. The deterioration of a component or structure in fault or accident conditions, reducing or preventing its ability to perform its intended function. 2. The accumulation of defects or microcracks in the microstructure of a body loaded monotonically or in fatigue, which weakens the body and can lead to crack propagation and failure. 1.部件或结构在故障或事故条件下的劣化，降低或阻止其执行预期功能的能力。2.在承受单调载荷或疲劳载荷的物体的微观结构中累积的缺陷或微裂纹，这会削弱物体，并可能导致裂纹扩展和失效。 |
| Compounding | 复合串联 |
In a steam engine (compound steam engine) or impulse turbine, the progressive reduction in pressure (expansion) across two or more stages in series. 在蒸汽机（复合蒸汽机）或脉冲涡轮机中，通过串联的两个或多个级逐渐降低压力（膨胀）。 |
| Zirconia-toughened alumina composites | 氧化锆增韧氧化铝复合材料 |
(ZTA composites) Ceramic composites based on aluminium oxide to which zirconium oxide is added, resulting in improved fracture toughness. （ZTA复合材料）基于氧化铝的陶瓷复合材料，其中添加了氧化锆，从而提高了断裂韧性。 |
| B-basis | B-基础 |
Mechanical property value above which at least 90% of the population of values is expected to fall, with a confidence of 95%. 机械性能值超过该值时，至少90%的值预计会下降，置信度为95%。 |
| Lobe | 凸轮 |
The projecting part such as rotor lobe or the cam lobe. 转子凸角或凸轮凸角等突出部分。 |
| Galling | 磨损 |
An extreme form of adhesive wear, in which large chunks of one part stick to the mating part (during sliding contact). 一种极端形式的粘着磨损，其中一个零件的大块粘在配合零件上（在滑动接触期间）。 |
| Hydrogen-induced delayed cracking | 氢致延迟开裂 |
A term sometimes used to identify a form of hydrogen embrittlement in which a metal appears to fracture spontaneously under a steady stress less than the yield stress. There is usually a delay between the application of stress (or exposure of the stressed metal to hydrogen) and the onset of cracking. Also referred to as static fatigue. 有时用于识别一种氢脆形式的术语，其中金属在小于屈服应力的稳定应力下似乎会自发断裂。在施加应力（或将受应力金属暴露于氢）与开裂开始之间通常存在延迟。也称为静态疲劳。 |
| Machine tool | 机床工具 |
A powered machine, such as a borer, grinder, lathe, milling machine or planer, used for cutting and shaping metal, plastics, composites, etc. (machining). A machining centre is a CNC machine tool working about several axes, having a stock of tools and automatic tool changing ability, which is capable of diverse machining operations under automated control. 一种动力机器，如钻孔机、磨床、车床、铣床或刨床，用于切割和成形金属、塑料、复合材料等（机加工）。加工中心是围绕多个轴工作的CNC机床，具有刀具库存和自动换刀能力，能够在自动化控制下进行各种加工操作。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Thermoelectric junction | 热电结 |
A welded, soldered, or twisted connection between the ends of two wires of dissimilar metals, as in a thermocouple. 两根不同金属线的末端之间的焊接、锡焊或绞合连接，如热电偶。 |
| Sawing | 锯切 |
Sawing is the process of cutting a workpiece with power band saws, hacksaws, and circular saws. Each of these methods is used in cutoff operations (cutting pieces to a required length), although band sawing also provides a method of cutting contours. 锯切是用带锯、钢锯和圆锯切割工件的过程。这些方法中的每一种都用于切割操作（将工件切割到所需长度），尽管带锯也提供了一种切割轮廓的方法。 |
| Initial preload | 初始预载 |
The tension created in a single bolt as it is tightened. Will usually be modified by subsequent assembly operations or by in-service loads and conditions. 拧紧单个螺栓时产生的张力。通常会通过后续的装配操作或在役负载和条件进行修改。 |
| Sample average | 样本平均值 |
The sum of all the observed values in a sample divided by the sample size. It is a point estimate of the population mean. Also known as arithmetic mean. 样本中所有观察值的总和除以样本大小。它是总体平均值的点估计。也称为算术平均值。 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Impact wrench | 冲击扳手 |
An air- or electric-powered wrench in which multiple blows from tiny hammers are used to produce output torque to tighten fasteners. A pneumatically-or electrically-powered socket wrench used to tighten or loosen nuts through the application of torque in a rapid series of impulses. 一种气动或电动扳手，使用小锤子多次敲击来产生输出扭矩以拧紧紧固件，用于通过在一系列快速脉冲中施加扭矩来拧紧或松开螺母。 |
| Belt drive | 带传动 |
Transmission of motion from one shaft to another by means of a continuous plain, or toothed, flexible band (belt) passing over pulleys. In contrast to chain drives, belt drives tend to be employed in low-torque applications. Reduction in transmissible power may occur due to stretch of a plain transmission belt which results in slack in the drive (belt creep) or slip of a belt on a driving or driven pulley (belt slip). 通过穿过滑轮的连续平带或带齿柔性带（带）将运动从一根轴传递到另一根轴。与链条传动相比，皮带传动往往用于低扭矩应用。由于普通传动带的拉伸可能会导致传动松弛（皮带蠕变）或主动或从动皮带轮上的皮带打滑（皮带打滑），从而导致传动功率降低。 |
| Stress corrosion cracking (SCC) | 应力腐蚀开裂（SCC） |
A common form of Stress cracking in which an Electrolyte encourages the growth of a crack in a highly stressed bolt. Only a tiny quantity of electrolyte need be present, at the tip or face of the crack. A time-dependent process in which a metallurgically susceptible material fractures prematurely under conditions of simultaneous corrosion and sustained loading at lower stress levels than would be required in the absence of a corrosive environment. Tensile stress is required at the metal surface and may be a residual stress resulting from heat treatment or fabrication of the metal or the result of external loading. Cracking may be intergranular or transgranular, depending on the combination of alloy and environment. 一种常见的应力开裂形式，其中电解液促使高应力螺栓中的裂纹扩展。在裂纹尖端或表面，只需存在少量电解质。一种随时间变化的过程，其中冶金敏感材料在同时腐蚀和持续加载的条件下过早断裂，其应力水平低于无腐蚀环境时的要求。在金属表面需要拉应力，拉应力可以是金属的热处理或制造或外部负载产生的残余应力。裂纹可能是沿晶开裂或穿晶开裂，这取决于合金和环境的组合。 |
| Carbon steels | 碳钢 |
(plain carbon steels) Steels in which carbon is the principal alloying element, and the amount of manganese does not exceed 1.65% and the copper and silicon contents are less than 0.60%. There are three main types: low-carbon steels (0.08–0.35% carbon); medium-carbon steels (0.35–0.50% carbon); and high-carbon steels (0.50–2.0% carbon). （普通碳钢）以碳为主要合金元素，锰含量不超过1.65%，铜和硅含量低于0.60%的钢。主要有三种类型：低碳钢（0.08-0.35%碳）；中碳钢（0.35–0.50%碳）；和高碳钢（0.50–2.0%碳）。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Corrosion fatigue | 腐蚀疲劳 |
Cracking produced by the combined action of repeated or fluctuating stress and a corrosive environment at lower stress levels or fewer cycles than would be required in the absence of a corrosive environment. 由重复或波动的应力和腐蚀环境的联合作用产生的开裂，其应力水平低于没有腐蚀环境时所需的应力水平或循环次数更少。 |
| Lüders lines | 吕德斯线 |
Elongated surface markings or depressions, often visible with the unaided eye, that form along the length of sheet metal or a tension specimen at an angle of approximately 45° to the loading axis. Caused by localized plastic deformation, they result from discontinuous (inhomogeneous) yielding. Also known as Lüders bands, Hartmann lines, Piobert lines, or stretcher strains. 拉长的表面标记或凹陷，通常肉眼可见，沿金属板或拉伸试样的长度形成，与加载轴的角度约为45°。由于局部塑性变形，它们是不连续（不均匀）屈服的结果。也被称为吕德斯带、哈特曼线、皮奥伯特线或拉伸线。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Striation | 条纹组织 |
A fatigue fracture feature, often observed in electron micrographs, that indicates the position of the crack front after each succeeding cycle of stress. The distance between striations indicates the advance of the crack front across that crystal during one stress cycle, and a line normal to the striation indicates the direction of local crack propagation. 一种疲劳断裂特征，通常在电子显微照片中观察到，表明每次应力循环后裂纹前沿的位置。条纹之间的距离表示在一个应力循环期间裂纹前沿穿过该晶体的前进，垂直于条纹的线表示局部裂纹扩展的方向。 |
| Overaging | 过时效 |
Aging under conditions of time and temperature greater than those required to obtain maximum change in a certain property, so that the property is altered in the direction of the initial value. 在时间和温度条件下的时效大于获得某一特性最大变化所需的时间和温度，从而使该特性沿初始值的方向发生变化。 |
| Pressure regulator | 压力调节器 |
(pressure-regulating valve) A device installed in a pneumatic or gas system to maintain the downstream pressure at the required level. （压力调节阀）安装在气动或气体系统中以将下游压力保持在所需水平的装置。 |
| Torsion spring | 扭簧 |
1. A spring in the form of a torsion bar. 2. A helical spring to which torque can be applied at the ends. 1.一种扭杆形式的弹簧。2.一种螺旋弹簧，其端部可施加扭矩。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Stator | 定子 |
A ring of non-rotating blades or nozzles in a compressor, turbine, or other turbomachine, which directs fluid flow into an adjacent rotor. 涡轮压缩机、涡轮或其他涡轮机械中的一圈不旋转的叶片或喷嘴，将流体引导到相邻的转子中。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Horizontal batch furnace | 卧式间歇炉 |
A versatile batch-type furnace that can give light or deep case depths, and because the parts are not exposed to air, horizontal batch furnaces can give surfaces almost entirely free of oxides. 一种多功能间歇式炉，可以提供浅或深的外壳深度，并且由于零件不暴露在空气中，卧式间歇式炉可以使表面几乎完全没有氧化物。 |
| Quench-age embrittlement | 淬火时效脆化 |
Embrittlement of low-carbon steels resulting from precipitation of solute carbon at existing dislocations and from precipitation hardening of the steel caused by differences in ferrite at different temperatures. Quenchage embrittlement usually is caused by rapid cooling of the steel from temperatures slightly below Ac1 (the temperature at which austenite begins to form), and can be minimized by quenching from lower temperatures. 低碳钢的脆化是由于溶质碳在现有位错处的沉淀和铁素体在不同温度下的差异导致的钢沉淀硬化造成的。淬火脆性通常是由钢从略低于Ac1的温度（奥氏体开始形成的温度）快速冷却引起的，可以通过从较低温度淬火来最小化。 |
| Vickers hardness test | 维氏硬度测试 |
An indentation hardness test employing a 136° diamond pyramid indenter (Vickers) and variable loads, enabling the use of one hardness scale for all ranges of hardness—from very soft lead to tungsten carbide. Also know as diamond pyramid hardness test. 采用136°金刚石棱锥压头（维氏硬度计）和可变载荷的压痕硬度测试，能够对从极软铅到碳化钨的所有硬度范围使用一个硬度标度。也称为钻石金字塔硬度测试。 |
| Blank carburizing | 毛坯渗碳 |
Simulating the carburizing operation without introducing carbon. This is usually accomplished by using an inert material in place of the carburizing agent, or by applying a suitable protective coating to the ferrous alloy. 在不引入碳的情况下模拟渗碳操作。这通常通过使用惰性材料代替渗碳剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Transgranular | 穿晶 |
Through or across crystals or grains. Also known as intracrystalline or transcrystalline. 穿过或横穿晶体或颗粒。也称为晶内或晶间。 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Breaking load | 断裂载荷 |
The maximum load (or force) applied to a test specimen or structural member loaded to rupture. 施加到加载到破裂的试样或结构构件上的最大载荷（或力）。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Starting taper | 起始锥度 |
The taper on the end of a reamer or tap which aids in starting the cut. 铰刀或丝锥端部的锥度，有助于开始切割。 |
| Nominal stress | 名义应力 |
The stress at a point calculated on the net cross section by simple elasticity theory without taking into account the effect on the stress produced by stress raisers such as holes, grooves, fillets, etc. 通过简单弹性理论在净截面上计算的点处的应力，不考虑孔、槽、圆角等应力提升器产生的应力影响。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Kilocalorie | 千卡 |
(Cal, kg-cal, kilogram-calorie, large calorie) An obsolete (i.e. non-SI) unit of energy equal to 1 000 cal. （卡，千克卡，千克卡路里，大卡路里）一种已被淘汰的（即非国际单位制）能量单位，等于1000卡。 |
| Stress cycles endured (N) | 承受的应力循环（N） |
The number of cycles of a specified character (that produce fluctuating stress and strain) that a specimen has endured at any time in its stress history. 试样在其应力历史中任何时间所经受的特定特征（产生波动应力和应变）的循环次数。 |
| Weld penetration | 焊接熔深 |
It is the depth below the surfaces, as revealed in microstructural sections of joined metals, which is melted during welding. 它是焊接过程中熔化的连接金属的微观结构截面所显示的表面以下的深度。 |
| Rolled thread | 滚制螺纹 |
A thread formed by plastically deforming the surface of the blank rather than by cutting operations. Increases fatigue life and thread strength, but is not possible (or perhaps economical) on larger sizes. 通过塑性变形坯料表面而不是通过切割操作形成的螺纹。增加疲劳寿命和螺纹强度，但不太可能（或者说是经济上不太可能）用于较大的尺寸。 |
| Sizing | 颗粒化 |
1. A finishing operation to ensure the specified dimensions and tolerances for a component are met. 2. (size classification) Separating an aggregate of mixed particles into groups according to size using a series of screens. 1.精加工操作，以确保满足部件的规定尺寸和公差。2.（粒度分类）使用一系列筛网根据粒度将混合颗粒的聚集体分成组。 |
| Intense quenching | 强烈淬火 |
Quenching in which the quenching medium is cooling the part at a rate at least two and a half times faster than still water. 淬火，其中淬火介质以比静水快至少两倍半的速度冷却零件。 |
| Compressive stress (Unit Pa) | 压缩应力（单位Pa） |
The compressive load per unit area at a point in a component. 部件中某点的每单位面积的压缩载荷。 |
| Normal temperature and pressure (NTP) | 常温常压（NTP） |
Reference conditions defined by NIST as 20°C and 1 atm. NIST定义的参考条件为20°C和1atm。 |
| Abelian group | 阿贝尔群 |
Property of a group of elements associated with a binary operation. In an Abelian group, the group elements commute under the binary operation. If a and b are any two group elements and if the (+) sign denotes the binary operation, then, for an Abelian group, 与二元运算相关的一组元素的属性。在阿贝尔群中，群元素在二元运算下交换。如果a和b是任意两个群元素并且（+）符号表示二元运算 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Plug | 螺塞 |
1. An object, usually tapered, used to block a hole to prevent fluid from escaping or flowing. 2. The central moveable part of a valve. 3. In the flow of a yield-stress fluid through a pipe or duct, the central region is often assumed to take the form of a plug with uniform axial velocity. 4. In thermoforming, a shaping tool that forces a heated plastic sheet into a female mould. 1.一种物体，通常为锥形，用于堵塞孔以防止流体逸出或流动。2.阀门的中心可移动部分。3.在屈服应力流体通过管道或管道的流动中，中心区域通常假定为具有均匀轴向速度的塞子形式。4.在热成型技术中，一种成型工具，将加热的塑料板压入阴模中。 |
| Vacuum relief valve | 真空安全阀 |
A valve that admits gas to a system under vacuum, should the degree of vacuum become excessive. 如果真空度过高，允许气体在真空下进入系统的阀门。 |
| Proportional limit | 比例极限 |
The greatest stress a material is capable of developing without a deviation from straight-line proportionality between stress and strain. 材料能够产生的最大应力不偏离应力和应变之间的直线比例。 |
| Die casting | 压铸 |
A process in which molten metal, particularly alloys of aluminium, magnesium, copper, and zinc, is forced under pressure (10 to 200 MPa) into a reusable hardened-steel mould machined into a die. 在压力（10至200MPa）下将熔融金属（特别是铝、镁、铜和锌的合金）强制进入加工成模具的可重复使用的硬化钢模具中的过程。 |
| Cohesive zone | 凝聚力区 |
In fracture-mechanics modelling and simulation, the region at the crack tip over which an assumed traction (load-displacement) relation has to be overcome to permit initiation and propagation of a crack. 在断裂力学建模和模拟中，必须克服假定的牵引（载荷-位移）关系以允许裂纹萌生和扩展的裂纹尖端区域。 |
| Coefficient of restitution (e) | 回弹系数（e） |
The ratio of the relative velocity of two colliding bodies after collision to that before. In perfectly elastic collisions e = 1; when all the impact energy is dissipated, e = 0. 两个碰撞体在碰撞后与碰撞前的相对速度之比。在完全弹性碰撞中e=1；当所有的冲击能量都消散时，e=0。 |
| Expansion bolt | 膨胀螺栓 |
When a through bolt cannot be used for attaching a pipe hanger, bracket, or other part, to a wall or ceiling of brick or concrete, what are known as expansion bolts are often used. The body of an expansion bolt is divided and the arrangement is such that, when the head of the bolt is turned, the sections forming the body of the bolt are forced outward and against the wall of the hole which has been drilled into the brick, concrete, or stone, as the case may be. Bolts of this type are made in quite a variety of designs. The nominal size represents the diameter of the bolt proper and not the diameter of the casing or expansion member. 当不能使用贯穿螺栓将管道吊架、支架或其他部件连接到砖块或混凝土的墙壁或天花板时，通常使用所谓的膨胀螺栓。膨胀螺栓的主体是分开的，其布置方式是，当螺栓头转动时，形成螺栓主体的部分被强制向外并靠在已钻入砖、混凝土或石头中的孔壁上，视情况而定。这种类型的螺栓有多种设计。标称尺寸代表螺栓本身的直径，而不是套管或膨胀构件的直径。 |
| Elasticity | 弹性 |
The property of a material by virtue of which deformation caused by stress disappears on removal of the stress. A perfectly elastic body completely recovers its original shape and dimensions after release of stress. 一种材料的特性，通过这种特性，由应力引起的变形在去除应力后消失。完全弹性体在应力释放后完全恢复其原始形状和尺寸。 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Flat head | 平头 |
Flat top surface and a conical bearing surface. 平顶表面和锥形轴承表面。 |
| Dimensional stability | 尺寸稳定性 |
Ability of a plastic part to retain the precise shape in which it was molded, fabricated, or cast. 塑料零件保持其成型、制造或铸造时的精确形状的能力。 |
| Offset modulus | 补偿模量 |
The ratio of the offset yield stress to the extension at the offset point (plastics). 偏移屈服应力与偏移点（塑料）处延伸的比率。 |
| Freezing point | 冰点 |
The temperature at which a substance changes phase (or state) from liquid to solid. The freezing point for most substances increases as pressure increases. The reverse process, from solid to liquid, is melting; melting point is the same as freezing point. 物质从液态变为固态的温度。大多数物质的冰点随着压力的增加而增加。从固体到液体的逆过程是熔化；熔点与凝固点相同。 |
| Mechanical energy (Unit J) | 机械能（单位J） |
The sum of kinetic energy and potential energy for an object or a mechanical system, including the energy stored in springs, etc. 物体或机械系统的动能和势能之和，包括储存在弹簧等中的能量。 |
| Torsion test | 扭力测试 |
A test designed to provide data for the calculation of the shear modulus, modulus of rupture in torsion, and yield strength in shear. 为计算剪切模量、扭转断裂模量和剪切屈服强度而设计的试验。 |
| Blue brittleness | 蓝色脆性 |
Anomalous loss of ductility when quenched steels are tempered in the range 250–350°C (temperatures that produce blue tints on the surface of components). Brittleness exhibited by some steels after being heated to some temperature within the range of about 205 to 370 °C (400 to 700 °F), particularly if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. 当淬火钢在250–350°C范围内回火（在部件表面产生蓝色色调的温度）时，延展性异常损失。某些钢在加热到约205至370°C（400至700°F）范围内的某个温度后表现出脆性，特别是在高温下加工钢时。镇静钢几乎没有这种脆性。 |
| Scale effect | 规模效应 |
The change in behaviour with size of a material, component, or structure. For example, cube-square scaling where one element changes with volume and another with area, as in the range of a projectile or ship, droplet formation, and fracture mechanics. 性能随材料、部件或结构尺寸的变化。例如，立方体平方比例，其中一个元素随体积变化，另一个元素因面积变化，如在射弹或飞船的射程、液滴形成和断裂力学中。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Shim | 垫片 |
A thin piece of material, such as metal of accurately-known thickness, placed between two surfaces to ensure they are the correct distance apart. A thin piece of material placed between two surfaces to obtain a proper fit, adjustment, or alignment. The piece can also be analyzed to measure furnace carbon potential (that is, because while in the furnace it will quickly carburize to a level equal to the furnace carbon potential). 一块薄的材料，如厚度精确已知的金属，放置在两个表面之间，以确保它们之间的距离正确。放置在两个表面之间以获得适当配合、调整或对齐的一块薄材料。还可以对工件进行分析，以测量熔炉碳势（也就是说，在熔炉中，工件将快速渗碳至与熔炉碳势能相等的水平）。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| Median fatigue life | 中位疲劳寿命 |
The middle value when all of the observed fatigue life values of the individual specimens in a group tested under identical conditions are arranged in order of magnitude. When an even number of specimens are tested, the average of the two middlemost values is used. Use of the sample median rather than the arithmetic mean (that is, the average) is usually preferred. 当在相同条件下测试的一组中单个试样的所有观察疲劳寿命值按数量级排列时的中间值。当测试偶数个试样时，使用两个中间值的平均值。通常优选使用样本中值而不是算术平均值（即平均值）。 |
| Damage tolerance | 损伤容限 |
(defect tolerance) A design philosophy that takes into account initial imperfections, crack-growth rates and conditions at final fracture, and uses fracture mechanics to demonstrate that cracks should not grow to their critical length within the design life (or at least should be capable of ready detection). （缺陷公差）考虑初始缺陷、裂纹扩展速率和最终断裂条件的设计理念，并使用断裂力学证明裂纹不应在设计寿命内增长到其临界长度（或至少应能够随时检测）。 |
| Vapour–pressure curve | 蒸汽压力曲线 |
For a pure substance, the curve of saturation pressure plotted vs saturation temperature. 对于纯物质，绘制了饱和压力与饱和温度的曲线。 |
| Crest clearance (Unit m) | 顶隙（单位米） |
For screw threads and gearing, the radial clearance between the crest of a thread (or gear) and the root of the engaging thread (or gear). 对于螺纹和齿轮，螺纹（或齿轮）的顶部与啮合螺纹（或齿轮）的根部之间的径向间隙。 |
| Ferralium | 铁素体钢 |
Ferralium is a type of Super Duplex Stainless Steel which is optimised for use within fasteners. 一种超级双相不锈钢，经过优化用于紧固件。 |
| Crankshaft | 曲轴 |
The main shaft, of which the cranks are a part, of a reciprocating single-or multi-cylinder machine. Crankshafts may be built up in sections or forged as a single component. In an engine, the reciprocating motion of the pistons transmits power to the crankshaft and causes it to rotate, whereas in a pump the crankshaft is driven and its rotation causes the pistons to reciprocate. 曲柄是往复式单缸或多缸机器主轴的一部分。曲轴可以分段组装或作为单个部件锻造。在发动机中，活塞的往复运动将动力传递给曲轴并使其旋转，而在泵中，曲轴被驱动，其旋转使活塞往复运动。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Nut thickness | 螺母厚度 |
The nut thickness shall be the overall distance measured parallel to the axis of nut, from the top of the nut to the bearing surface, and shall include the thickness of the washer face where provided. 螺母厚度应为平行于螺母轴线测量的从螺母顶部到轴承表面的总距离，还应包括垫圈表面的厚度。 |
| Thermodynamic process | 热力学过程 |
A change in equilibrium state undergone by a quantity of matter or a system. 一定量的物质或系统所经历的平衡状态的变化。 |
| Stress wave | 应力波 |
An unbalanced force, such as an impact, applied at one location in a body sets the material there into vibration that is transmitted to adjacent elements and ultimately to all parts of the body in the form of stress waves or wave packets. 施加在物体某个位置的不平衡力（如冲击力）会使物体中的材料产生振动，并以应力波或波包的形式传递到相邻元件，最终传递到物体的所有部位。 |
| Velocity ratio | 速度比 |
1. The ratio between the input velocity to a machine, train of gears, etc. and the output velocity. 2. The ratio between the displacement of an applied force at one part of a mechanism and the movement of the load at a different part. 1.机器、齿轮系等的输入速度与输出速度之间的比率。2.在机构的一个部分处施加的力的位移与在不同部分处的载荷的移动之间的比率。 |
| Allotropy | 同素异形体 |
A near synonym for polymorphism. Allotropy is generally restricted to describing polymorphic behavior in elements, terminal phases, and alloys whose behavior closely parallels that of the predominant constituent element. 多态性的近义词。同素异形体通常仅限于描述元素、终端相和合金中的多晶型行为，其行为与主要组成元素的行为非常相似。 |
| Statistic | 统计 |
A summary value calculated from the observed values in a sample. 根据样本中的观察值计算得出的汇总值。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| Cleavage | 分裂 |
The tendency of a material to cleave or split along definite crystallographic planes. 材料沿特定晶面劈裂或分裂的趋势。 |
| Degradation | 降解 |
The reduction with time of the physical properties of a material. 材料的物理性质随时间的减少。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| Press quenching | 压淬 |
A quench in which hot dies are pressed and aligned with a part before the quenching process begins. Then the part is placed in contact with a quenching medium in a controlled manner. This process avoids part distortion. 一种淬火方法，在淬火过程开始之前，热模具被压制并与零件对齐。然后将零件以受控方式放置在与淬火介质接触的位置。该过程避免了零件变形。 |
| Torque wrench | 扭矩扳手 |
A manual wrench which incorporates a gage or measuring apparatus of some sort to measure and display the amount of torque being delivered to the nut or bolt. All wrenches produce torque. Only a torque wrench tells how much torque. A socket wrench or ring spanner that can be set to allow a specific torque to be applied to a nut or bolt head. 一种手动扳手，包括某种量规或测量装置，用于测量和显示传递至螺母或螺栓的扭矩量。所有扳手都产生扭矩。只有扭矩扳手才能显示扭矩大小。一种套筒扳手或梅花扳手，可设置为允许对螺母或螺栓头施加特定扭矩。 |
| Oxygen probe | 定氧测头 |
An atmosphere-monitoring device that electronically measures the difference between the partial pressure of oxygen in a furnace or furnace supply atmosphere and the external air. 一种大气监测装置，以电子方式测量熔炉或熔炉供应大气中的氧分压与外部空气之间的差值。 |
| Load ratio, R | 负载比R |
In fatigue, the algebraic ratio of the minimum to maximum load in a fatigue cycle, that is, R = Pmin/Pmax. Also known as stress ratio. 在疲劳中，疲劳循环中最小载荷与最大载荷的代数比，即 R= Pmin/Pmax。也称为应力比。 |
| Screw jack | 螺旋千斤顶 |
A lifting device (jack) consisting of a nut and square-threaded shaft at the top of which is a load-bearing pad. Rotation of the nut raises or lowers the pad. 一种起重装置（千斤顶），由螺母和方形螺纹轴组成，其顶部为承重垫。螺母的旋转可升高或降低衬垫。 |
| Elbow | 肘部 |
1. A fitting that connects the ends of two pipes at an angle, 45°, 90°, and 180° being the most common. 2. The third joint on an articulated robot corresponding to the human elbow. 1.以45°、90°和180°角连接两个管道端部的配件。2.示例关节机器人上的第三关节对应于人的肘部。 |
| Design stress (Unit Pa) | 设计应力（单位Pa） |
The greatest allowable stress in a component or structure that will not result in failure under normal operating conditions. 在正常操作条件下不会导致失效的部件或结构中的最大许用应力。 |
| Threaded fastener | 螺纹紧固件 |
Studs, bolts, and screws of all sorts, with associated nuts. One of the most interesting, complex, useful—and frustrating—components yet devised. 各种螺柱、螺栓和螺钉，以及相关的螺母。 |
| Cylinder head | 气缸盖 |
The machined casting, typically of aluminium alloy or cast iron, that fits above the cylinder block of a piston engine and closes off the cylinders. It normally includes part of the combustion chambers and holes for the valves and spark plugs. 活塞式发动机缸体上方的机械铸件，通常由铝合金或铸铁制成，用于封闭气缸。它通常包括燃烧室的一部分以及阀门和火花塞的孔。 |
| Tempered martensite embrittlement | 回火马氏体脆化 |
Embrittlement of ultrahigh-strength steels caused by tempering in the temperature range of 205 to 400 °C (400 to 750 °F); also called 350 °C or 500 °F embrittlement. Tempered martensite embrittlement is thought to result from the combined effects of cementite precipitation on prioraustenite grain boundaries or interlath boundaries and the segregation of impurities at prioraustenite grain boundaries. 超高强度钢在205至400°C（400至750°F）温度范围内回火引起的脆化；也称为350°C或500°F脆化。回火马氏体脆化被认为是由于渗碳体沉淀在原奥氏体晶界或层间晶界上以及杂质在原奥氏体晶粒边界处偏析的综合影响。 |
| Absolute specific gravity | 绝对比重 |
The ratio of the weight of any volume of a substance to the weight of an equal volume of a reference substance at the same temperature, often water at 4°C, both measured in a vacuum to avoid any effect of buoyancy. 在相同温度下，任何体积的物质的重量与等体积的参考物质的重量之比，通常是4°C的水，两者都是在真空中测量的，以避免任何浮力的影响。 |
| Diffusion coefficient | 扩散系数 |
A factor of proportionality representing the amount of substance diffusing across a unit area through a unit concentration gradient in unit time. 一个比例因子，表示在单位时间内通过单位浓度梯度扩散到单位面积上的物质量。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Spring clip | 弹簧夹 |
A clip made of a material such as spring steel which grips an inserted part. 由弹簧钢等材料制成的夹子，用于夹住插入的零件。 |
| Concentrated load | 集中负荷 |
A load on a component which is distributed over a very small area, idealized as the line load of a wedge or knife edge, and the point load of a cone. 分布在非常小的区域上的部件上的载荷，理想化为楔形或刀刃的线载荷和锥体的点载荷。 |
| Pitting | 点蚀 |
In tribology, a type of wear characterized by the presence of small, sharp surface cavities formed by processes such as fatigue, local adhesion, wear, corrosion, or cavitation. 在摩擦学中的一种磨损，其特征是存在由疲劳、局部粘附、磨损、腐蚀或空穴等过程形成的小而尖锐的表面空穴。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Corrosion | 腐蚀 |
The deterioration of an exposed metal surface due to electrochemical oxidation with its surroundings. In the oxidation reaction, metal atoms give up electrons which are transferred to form another chemical species by a reduction reaction, usually with hydrogen and/or oxygen. A common example is the formation of the iron oxide rust Fe(OH)3 on iron or steel in moist air or water. Rust breaks away easily, exposing fresh iron to the atmosphere, whereas the corrosion product of some metals forms an adherent layer that prevents further oxidation reaction at fresh metal, an effect known as passivation. Examples include aluminium oxide on aluminium, chromium oxide on chromium, chromium oxide on alloys containing chromium such as stainless steels, and the patina formed on copper and zinc. Corrosion protection takes many forms. Good design to avoid crevices and stress is important. In some situations, substances known as inhibitors may be added to the environment to decrease its corrosiveness. The electrochemical nature of corrosion results in some metals having a greater tendency for oxidation than others. Zinc has a stronger tendency than iron and this is made use of in galvanizing. This is one example of cathodic protection, in which one metal is connected electrically to a more reactive metal, called a sacrificial anode, that oxidizes by giving up electrons and so protects the first metal. Coatings may be used to resist corrosion. Paints, plating, and diffusion coatings are the most common and the electrochemical process of anodizing is used to deliberately form a passive layer of oxide on aluminium alloys. Material selection plays a major role. For example, stainless steels with their high chromium content are widely used in corrosive environments. 暴露的金属表面由于与周围环境的电化学氧化而劣化。在氧化反应中，金属原子放弃电子，这些电子通过还原反应（通常与氢和/或氧）转移形成另一种化学物质。一个常见的例子是在潮湿的空气或水中在铁或钢上形成氧化铁锈Fe(OH)3。铁锈很容易脱落，将新鲜铁暴露在大气中，而一些金属的腐蚀产物形成一层粘附层，防止新鲜金属发生进一步的氧化反应，这种效果称为钝化。实例包括铝上的氧化铝、铬上的氧化铬、含铬合金上的氧化铬如不锈钢，以及铜和锌上形成的铜绿。腐蚀防护有多种形式。避免裂缝和应力的良好设计非常重要。在某些情况下，可以向环境中添加称为抑制剂的物质，以降低其腐蚀性。腐蚀的电化学性质导致一些金属比其他金属具有更大的氧化倾向。锌比铁具有更强的倾向性，这可用于镀锌。这是阴极保护的一个例子，其中一种金属与活性更强的金属（称为牺牲阳极）电连接，牺牲阳极通过释放电子进行氧化，从而保护第一种金属。涂层可用于抗腐蚀。油漆、电镀和扩散涂层是最常见的，阳极氧化的电化学过程用于有意在铝合金上形成一层钝化氧化物。材料选择起着重要作用。例如，铬含量高的不锈钢广泛用于腐蚀性环境。 |
| Double tempering | 双回火 |
A treatment in which a quench-hardened ferrous metal is subjected to two complete tempering cycles, usually at substantially the same temperature, for the purpose of ensuring completion of the tempering reaction and promoting stability of the resulting microstructure. 一种处理，其中淬火硬化的黑色金属经过两个完整的回火循环，通常在基本相同的温度下，以确保完成回火反应并提高所得微观结构的稳定性。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| constitutive equation | 本构方程 |
(constitutive relation) 1. In solid mechanics or fluid mechanics, an algebraic or numerical relation for the dependency of stress on deformation, strain, strain rate, temperature, etc. in a material. In solid mechanics such a relation is sometimes called an equation of state. Simple linear examples include Hooke’s law and Newton’s viscosity law. 2. In heat transfer, a relation, such as Fourier’s law of heat conduction, connecting heat flux with temperature gradient. （本构关系）1.在固体力学或流体力学中，应力与材料的变形、应变、应变率、温度等之间的代数或数值关系。在固体力学中，这种关系有时称为状态方程。简单的线性例子包括胡克定律和牛顿粘度定律。2.在传热学中，将热流与温度梯度联系起来的一种关系，如傅立叶热传导定律。 |
| Pitch angle (Unit °) | 俯仰角（单位°） |
For a bevel gear, the angle between the axis and the pitch-cone generator. 对于锥齿轮，轴与节锥生成器之间的角度。 |
| Deposit gauge | 沉积量计 |
(deposition gauge) An instrument employed in air pollution studies for measuring the amount of pollutant deposited on a given area in a given time under given conditions. （沉降计）在空气污染研究中使用的仪器，用于测量在给定条件下在给定时间内沉积在给定区域上的污染物量。 |
| Crossed threads | 交叉螺纹 |
When the axis of a nut offered up to a bolt is not aligned with the axis of a bolt (or a screw to a threaded member), it may be possible for the threads to engage incorrectly and even for the nut or screw to advance a turn or more, but ultimately the misaligned threads become locked together. Forcing the nut in such circumstances may irretrievably damage the threads on both. 当提供给螺栓的螺母的轴线与螺栓（或螺纹构件的螺钉）的轴线不对齐时，螺纹可能会错误接合，甚至螺母或螺钉会提前一圈或更多，但最终未对齐的螺纹会锁定在一起。在这种情况下强行拧入螺母可能会对两侧的螺纹造成无法修复的损坏。 |
| Cooling coil | 冷却盘管 |
A simple heat exchanger consisting of a coiled tube, typically of copper or stainless steel, through which is circulated a coolant such as a refrigerant, chilled water, or water mixed with ethylene glycol. Applications include air conditioning, process cooling, and refrigeration. 一种简单的热交换器，由通常由铜或不锈钢制成的盘管组成，冷却剂如制冷剂、冷冻水或与乙二醇混合的水通过盘管循环。应用包括空调、工艺冷却和制冷。 |
| Transition temperature (Unit K) | 转变温度（单位K） |
(1) An arbitrarily defined temperature that lies within the temperature range in which metal fracture characteristics (as usually determined by tests of notched specimens) change rapidly, such as from primarily fibrous (shear)to primarily crystalline (cleavage) fracture. (2) Sometimes used to denote an arbitrarily defined temperature within a range in which the ductility changes rapidly with temperature. (transition point) 1. The temperature at which the mechanism of fracture in metal alloys having a face-centred cubic crystal structure changes from ductile void growth to brittle cleavage. 2. The temperature at which a material changes from one crystal state to another. （1） 任意定义的温度，位于金属断裂特性（通常通过缺口试样的试验确定）快速变化的温度范围内，如从主要纤维（剪切）断裂到主要结晶（解理）断裂。（2） 有时用于表示延性随温度快速变化的范围内的任意定义的温度。（转变点）1.具有面心立方晶体结构的金属合金的断裂机制从韧性孔洞生长转变为脆性解理的温度。2.材料从一种晶体状态转变为另一种晶体的温度。 |
| Vibration | 振动 |
1. A periodic change with time of the displacements of elements making up a component or structure. 2. The study of the oscillatory motion of bodies and systems and the frequencies, amplitudes, and forces associated with them. 1.组成部件或结构的元件位移随时间的周期性变化。2.研究物体和系统的振荡运动以及与之相关的频率、振幅和力的学科。 |
| Speed of rotation (N) | 转速（N） |
(Unit rps or rpm) For an object rotating about a fixed axis, the speed of rotation is the number of turns (revolutions) of the object per unit time. It is equal to the angular velocity Ω (or ω) (unit rad/s) divided by 2π. （单位rps或rpm）对于绕固定轴旋转的物体，旋转速度是物体每单位时间的转数。它等于角速度Ω（或ω）（单位rad/s）除以2π。 |
| Concentrated solar power plant (CSP plant) | 聚光太阳能发电厂（CSP发电厂） |
A power plant in which solar radiation is concentrated using mirrors or lenses, typically using parabolic trough mirrors which focus solar radiation on to receiver tubes along the trough’s focal line. In an alternative arrangement molten salt, heated by solar receivers mounted on a tower, is circulated through a steam generator. 使用镜子或透镜集中太阳辐射的发电厂，通常使用抛物面槽镜，将太阳辐射沿着槽的焦线聚焦到接收管上。在另一种布置中，由安装在塔上的太阳能接收器加热的熔盐通过蒸汽发生器循环。 |
| Elastic energy | 弹性能 |
The amount of energy required to deform a material within its elastic range of behavior, neglecting small heat losses due to internal friction. The energy absorbed by a specimen per unit volume of material contained within the gage length being tested. It is determined by measuring the area under the stress-strain curve up to a specified elastic strain. See also modulus of resilience and strain energy. 材料在其弹性行为范围内变形所需的能量，忽略因内耗引起的小热损失。试样在被测标距内每单位体积材料吸收的能量。它是通过测量应力-应变曲线下达到规定弹性应变的面积来确定的。另见弹性模量和应变能。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Forge | 锻造 |
To shape metal while holt and plastic by a hammering or forcing process. Dies used in process. 通过锤击或强制过程使金属成型，同时保持塑料成型。过程会使用模具。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Air cleaner | 空气净化器 |
A device, such as a filter, hydrocyclone, or electrostatic precipitator, that removes particles and aerosols from a flow of air. 一种设备，例如过滤器、水力旋流器或静电除尘器，用于从气流中去除颗粒和气溶胶。 |
| Bolt blank | 螺栓毛坯 |
A rod on which a head has been formed, but on which no thread has been cut, from which bolts or screws may be made as required. 一种已形成头部但未切割螺纹的杆，可根据需要从中制造螺栓或螺钉。 |
| Austenite-stabilizer | 奥氏体稳定剂 |
Alloying element expanding the γ-phase field in the corresponding phase diagram, which manifests itself in a decrease of the A3 temperature and an increase of the A4 temperature in binary alloys Fe–M as well as in a decrease of A1 temperature in ternary alloys Fe–C–M (M is an alloying element). The solubility of austenite-stabilizers in ferrite is much lower than in austenite. Under the influence of austenite-stabilizers, austenite can become thermodynamically stable down to room temperature. 合金元素扩展了相应相图中的γ相场，这表现为二元合金Fe-M中A3温度的降低和A4温度的升高，以及A1温度的降低三元合金Fe–C–M（M是合金元素）。奥氏体稳定剂在铁素体中的溶解度远低于在奥氏体中的溶解度。在奥氏体稳定剂的影响下，奥氏体可以在低至室温时变得热力学稳定。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Cyaniding | 氰化 |
A case-hardening process in which a ferrous material is heated above the lower transformation range in a molten salt containing cyanide to cause simultaneous absorption of carbon and nitrogen at the surface and, by diffusion, create a concentration gradient. Quench hardening completes the process. 一种表面硬化工艺，将含铁材料在含氰化物的熔融盐中加热至低于较低转变范围，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。淬火硬化完成该过程。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Induction heating | 感应加热 |
Heating by combined electrical resistance and hysteresis losses induced by subjecting a metal to the varying magnetic field surrounding a coil carrying alternating current. 通过将金属置于承载交流电的线圈周围的变化磁场中而引起的电阻和磁滞损耗的组合加热。 |
| Catastrophic failure | 灾难性故障 |
A sudden and total failure of a large engineering structure such as an aeroengine, aircraft, space vehicle, bridge, or dam. 大型工程结构（如航空发动机、飞机、航天器、桥梁或水坝）突然完全失效。 |
| Pump | 泵 |
A machine designed to cause a liquid, gas, vapour, or slurry to flow due to the reciprocating motion of pistons, rotation of vanes, or rotation of an impeller. 通过活塞的往复运动、叶片的旋转或叶轮的旋转而使液体、气体、蒸汽或泥浆流动的机器。 |
| Tribology | 摩擦学 |
The science and technology concerned with interacting surfaces in relative motion. 与相对运动中相互作用的表面有关的科学和技术。 |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| DTI | DTI |
Direct tension indicator. A fastener used primarily in the structural steel industry, designed to indicate that a certain minimum amount of tension has been developed in the fastener during assembly. 直接张力指示器。一种主要用于结构钢行业的紧固件，旨在表明在装配过程中紧固件中产生了一定的最小张力。 |
| Joule | 焦耳 |
The SI unit of energy. One joule is the work done by a force of one newton acting over a distance of one metre. The symbol is J, where 1 J = 1 N m. 国际单位制能量单位。一焦耳是一牛顿的力在一米的距离上所做的功。符号为J，其中1j=1m。 |
| Turn-of-nut | 转动螺母 |
Sometimes used to describe the general rotation of the nut (or bolt head) as the fastener is tightened. More often used to define a particular tightening procedure in which a fastener is first tightened with a preselected torque, and is then tightened further by giving the nut an additional, measured, turn such as ‘‘three flats’’ (180°). 有时用于描述紧固件拧紧时螺母（或螺栓头）的总体旋转。更常用于定义一种特定的紧固程序，在该程序中，首先以预选扭矩拧紧紧固件，然后通过使螺母额外转动，如“三平面”（180°）进一步拧紧。 |
| Latent heat | 潜热 |
Thermal energy absorbed or released when a substance undergoes a phase change. 物质发生相变时吸收或释放的热能。 |
| Fracture mechanisms | 断裂机制 |
The microstructural mechanisms that cause fracture, such as void initiation, growth and coalescence, cleavage. 导致断裂的微观结构机制，如空隙的萌生、生长和聚结、解理。 |
| Transverse direction | 横向 |
Literally, the “across” direction, usually signifying a direction or plane perpendicular to the direction of working. In rolled plate or sheet, the direction across the width is often called long transverse, and the direction through the thickness, short transverse. 从字面上看，“横穿”方向，通常表示与工作方向垂直的方向或平面。在轧制钢板或薄板中，横跨宽度的方向通常称为长横向，穿过厚度的方向称为短横向。 |
| Clearance fit | 间隙配合 |
A range of clearances ranging from close sliding to loose running, i.e. a fit in which the limits for the mating parts always permit assembly. 从紧密滑动到松动运行的一系列间隙，即配合零件的限制始终允许组装的配合。 |
| Rivet | 铆钉 |
A short rod with a head on one end that is inserted through aligned holes in plates to be joined, after which a second head is made on the protruding shank by hammering or forming. The most common head shapes are flat, domed, and inverse conical. In an array, the rivet pitch is the distance between the centres of adjacent rivets. Failure may occur by different mechanisms or modes. A one piece fastener consisting of a head and a body and used for fastening two or more pieces together by passing the body through a hole in each piece and then forming a second head on the body end. It cannot be removed except by taking off the head. 一种一端有头的短杆，插入待连接板上对齐的孔中，然后通过锤击或成型在突出的杆身上制作第二个头。最常见的头部形状是扁平、圆顶和倒锥形。在阵列中，铆钉间距是相邻铆钉中心之间的距离。故障可能由不同的机制或模式发生。一种一体式紧固件，由头部和主体组成，用于将两个或多个部件紧固在一起，方法是将主体穿过每个部件上的孔，然后在主体端部形成第二个头部。除非取下头部，否则无法移除。 |
| Shock load | 冲击载荷 |
The sudden application of an external force that results in a very rapid build-up of stress. 突然施加外力，导致应力迅速增加。 |
| Diaphragm compressor | 隔膜式压缩机 |
A machine in which compression is achieved by the reciprocating motion of a flexible membrane of metal, plastic, or elastomeric material. This arrangement is ideally suited to pumping high-purity, toxic, or explosive gases. A similar machine incorporating check valves is a self-priming positive-displacement pump (diaphragm pump, membrane pump). 通过金属、塑料或弹性材料的柔性薄膜的往复运动实现压缩的机器。这种布置非常适合泵送高纯度、有毒或爆炸性气体。装有止回阀的类似机器是自吸容积泵（隔膜泵、隔膜泵）。 |
| Static fatigue | 静态疲劳 |
A term referring to a time-dependent reduction in strength with a static (noncyclic) load. The term may refer to hydrogen-induced delayed cracking or the effect of creep on the strength of plastics. Delayed fracture caused by environmental effects under dead-weight loading of materials such as glass. The name is unfortunate, as cyclic loads are not involved and glass is not susceptible to fatigue. 指静态（非循环）载荷下强度随时间变化的降低。该术语可指氢致延迟开裂或蠕变对塑料强度的影响。在玻璃等材料的自重荷载下，由环境影响引起的延迟断裂。 |
| Positive-displacement compressor | 容积式压缩机 |
Any type of compressor, including piston and rotary-screw types, that delivers a fixed volume of gas at high pressure per unit time. A positive-displacement pump delivers a fixed volume of fluid, usually a liquid, per unit time. 任何类型的压缩机，包括活塞式和旋转螺杆式，在单位时间内以高压输送固定体积的气体。容积泵每单位时间输送固定体积的流体，通常为液体。 |
| Mechanical units | 机械单位 |
The units of physical quantities, the dimensions of which includemass, length, and time. 物理量的单位，其量纲包括质量、长度和时间。 |
| Morse taper | 莫氏锥度 |
A self holding, standard taper largely used on drilling tools, drilling machine spindles, and some lathes. 一种自持式标准锥度，主要用于钻孔工具、钻床主轴和一些车床。 |
| Belt furnace | 带式炉 |
A continuous-type furnace which uses a mesh-type or cast-link belt to carry parts through the furnace. 一种连续式炉，它使用网状或铸造链带将零件运送通过炉子。 |
| Diesel engine | 柴油发动机 |
(compression–ignition engine) A piston engine operating on the Diesel cycle in which the air is compressed to a temperature above the autoignition temperature of the fuel and combustion is initiated as the fuel is injected into the hot air. Diesel engines operate at higher compression ratios (typically in the range 12 to 24) than petrol engines. Although named after Rudolf Diesel, the inventor, Diesel engine is often spelled with a lower case d, contrary to normal practice. （压燃式发动机）在柴油循环中运行的活塞式发动机，在该循环中，空气被压缩至高于燃料自燃温度的温度，当燃料喷射到热空气中时，燃烧开始。柴油发动机在比汽油发动机更高的压缩比下运行（通常在12到24的范围内）。虽然以发明人鲁道夫·迪塞尔命名，但迪塞尔发动机通常拼写为小写d，这与正常做法相反。 |
| Vane engine (vane motor) | 叶片发动机（叶片马达） |
A rotary engine in which high-pressure hydraulic fluid in the spaces between spring-loaded sliding vanes held in an offset rotor acts on the vanes, causing the rotor to revolve within a cylinder. The design is much like a sliding-vane compressor, as is that of a vane pump, used to pump liquids. 一种旋转式发动机，其中偏置转子中装有弹簧的滑动叶片之间的高压液压流体作用在叶片上，使转子在气缸内旋转。这种设计很像滑动叶片压缩机，就像用于泵送液体的叶片泵一样。 |
| Critical load (Unit N) | 临界负荷（单位N） |
1. The applied load that causes propagation of an existing crack of known length, and hence fracture of a component or structure. 2. The applied load that results in buckling of a column of given end fixity. 1.导致已知长度的现有裂纹扩展并因此导致部件或结构断裂的施加荷载。2.导致具有给定端部固定性的柱屈曲的施加荷载。 |
| Pressure ratio | 压力比 |
One pressure divided by another which may be a reference pressure. In many flow and thermodynamic processes, the pressure ratio is more important than the absolute pressure levels. For example, in compressible gas flow the Mach number is determined by the ratio of the stagnation pressure to the static pressure. 一个压力除以另一个压力，该压力可以是参考压力。在许多流动和热力学过程中，压力比比绝对压力水平更重要。例如，在可压缩气流中，马赫数由停滞压力与静压之比决定。 |
| Inch-pound force/inch² | 英寸磅力/英寸² |
A non-SI unit for the specific work of fracture (fracture toughness). The conversion to SI is 1 in.lbf/in² = 1.751 268 × 102 J/m². 用于特定断裂功（断裂韧性）的非国际单位制单位。到SI的转换为1英寸。lbf/in²=1.751268×102J/m²。 |
| Testing machine | 试验机 |
A machine used to apply either a steady or oscillatory or impact load to a testpiece. The load may be tensile, compressive, shear, bending, or torsional. 用于向试件施加稳定或振荡或冲击载荷的机器。载荷可以是拉伸的、压缩的、剪切的、弯曲的或扭转的。 |
| Set screw | 紧定螺钉（平头螺钉、紧定螺栓） |
Usually a hardened steel screw having either no head or a square head and with various degrees of points or ends to lock or tighten adjustable machine parts in position on a shaft. A short, headless screw with a recess at one end to receive a screwdriver or key, the other end being pointed, square, or otherwise shaped. Typically used to secure a pulley, gear, or other component on a shaft. 通常是一种硬化钢螺钉，无头或方头，具有不同程度的点或端部，用于将可调机械部件锁定或拧紧在轴上的适当位置。一端有凹槽，用来装螺丝刀或钥匙，另一端是尖的、方形的或其他形状的。通常用于将皮带轮、齿轮或其他部件固定在轴上。 |
| Acceleration due to gravity | 重力加速度 |
(acceleration of free fall, gravitational acceleration, g) (Unit m/s²) The acceleration of a freely-falling body in a vacuum, with a mean value at sea level of approximately 9.81 m/s². （自由落体加速度，重力加速度，g）（单位m/s²）自由落体在真空中的加速度，在海平面处的平均值约为9.81m/s²。 |
| Compression ratio | 压缩率 |
The volume of a combustion chamber with the piston at the top of its stroke as a proportion of the total volume of the cylinder with the piston at the bottom of its stroke. For a piston engine, if the swept volume is SW and the clearance volume is CL, the compression ratio is given by ( SW + CL)/CL, i.e. it is a volume ratio rather than a pressure ratio. 活塞位于其冲程顶部的燃烧室的容积与活塞位于其冲程底部的气缸总体积的比例。对于活塞发动机，如果扫气量为SW，间隙容积为CL，则压缩比由(SW+CL)/CL给出，即它是体积比而不是压力比。 |
| Total carbon | 总碳 |
The sum of the free and combined carbon (including carbon in solution) in a ferrous alloy. 铁合金中游离碳和结合碳（包括溶液中的碳）的总和。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Alloy | 合金 |
1. A metallic material composed of two or more elements, one of which is usually a metal to which the other elements are added, e.g. iron-carbon or aluminium-copper (binary alloy); nickel-chromium-iron (ternary alloy). 2. A plastic produced as a blend of two or more immiscible polymers. This results in material that cannot be achieved by polymerization. 1.由两种或多种元素组成的金属材料，其中一种通常是添加了其他元素的金属，例如铁碳或铝铜（二元合金）；镍铬铁（三元合金）。2.由两种或多种不混溶聚合物混合而成的塑料。这导致无法通过聚合获得的材料。 |
| Coherent structure | 相干结构 |
A term given to the larger eddies of turbulent shear flow, such as boundary layers, jets, and wakes, that show distinctive correlated patterns of motion. 一个术语，用于表示湍流剪切流的较大涡流，例如边界层、射流和尾流，它们显示出独特的相关运动模式。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Gear wheel | 齿轮 |
Any form of toothed wheel, particularly those having conjugate teeth employed in the transmission of motion and power. 任何形式的齿轮，特别是用于传递运动和动力的共轭齿的齿轮。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Closed system | 封闭系统 |
A closed thermodynamic system consists of a fixed amount of mass. No mass can cross its boundary although energy can, in the form of work or heat, and its volume can change. 一个封闭的热力学系统由一定量的质量组成。能量可以以功或热的形式存在，其体积可以改变，但没有质量可以越过它的边界。 |
| Uniaxial strain | 单轴应变 |
Increase (or decrease) in length resulting from a stress acting parallel to the longitudinal axis of the specimen. 由平行于试样纵轴的应力引起的长度增加（或减少）。 |
| Load range, P | 负载范围P |
In fatigue, the algebraic difference between the maximum and minimum loads in a fatigue cycle. 在疲劳中，疲劳循环中最大和最小载荷之间的代数差。 |
| Wrist | 腕关节 |
The final three joints on a robot which simulate rotations provided by the human wrist and thus allow orientation of the end effector to which it is attached by the wrist socket. 机器人上的最后三个关节，模拟人类手腕提供的旋转，从而允许其通过手腕插座连接到的末端执行器的方向。 |
| Homogenizing | 均质化 |
Holding at high temperature to eliminate or decrease chemical segregation by diffusion. 保持高温以消除或减少扩散引起的化学偏析。 |
| Width across flats | 平面宽度 |
A principal dimension of nuts, or of bolt heads. Work hardening The slight increase in hardness and strength produced when a body is loaded past its yield point. Also called strain hardening. 螺母或螺栓头的主要尺寸。加工硬化：当物体被加载超过其屈服点时，硬度和强度略有增加。也称为应变硬化。 |
| Sampling | 抽样 |
The process of measuring a series of values of a time-varying quantity. 测量一系列时变量值的过程。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Alpha iron | 阿尔法铁 |
The body-centered cubic form of pure iron, stable below 910 °C (1670 °F). 纯铁的体心立方形式，在910°C(1670°F)以下稳定。 |
| Structural frame | 结构框架 |
The underlying load-bearing framework of beams, columns, bracing, etc., of steel, concrete, brick, stone, timber etc., required to support the static and dynamic forces a building or component is subjected to, including its weight and that of its contents. 由钢、混凝土、砖、石、木材等制成的梁、柱、支撑等构成的底层承重框架，用于支撑建筑物或构件承受的静态和动态力，包括其重量及其内含物的重量。 |
| Wind pump | 风泵 |
A pump driven directly by a windmill on a tower. Widely used in remote locations. 由塔上的风车直接驱动的泵。广泛应用于偏远地区。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Acceleration-error constant | 加速度误差常数 |
When the reference (demand) input to a control system is parabolic, the output signal will also be parabolic in steady state. The signal that is constant in this situation is the acceleration and thus for a parabolic input the steady-state error, referred to as the acceleration-error constant, is the error in the acceleration. 当控制系统的参考（需求）输入是抛物线时，输出信号在稳定状态下也将是抛物线。在这种情况下恒定的信号是加速度，因此对于抛物线输入，称为加速度误差常数的稳态误差是加速度中的误差。 |
| Screw pump | 螺杆泵 |
A positive-displacement pump that uses one or more helical rotors rotating within a casing to transfer liquids or slurries. 一种容积式泵，使用一个或多个在外壳内旋转的螺旋转子输送液体或泥浆。 |
| Athermal transformation | 非热变化 |
A reaction that proceeds without benefit of thermal fluctuations; that is, thermal activation is not required. In contrast, a reaction that occurs at constant temperature is an isothermal transformation; thermal activation is necessary in this case and the reaction proceeds as a function of time. 在没有热波动的情况下进行的反应；也就是说，不需要热激活。相反，在恒温下发生的反应是等温转变。在这种情况下，热活化是必要的，并且反应作为时间的函数进行。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Stress corrosion | 应力腐蚀 |
(stress-corrosion cracking) Corrosion failure accelerated by local stresses (particularly tensile) which enhance cracking in both monotonic and fatigue loading. （应力腐蚀开裂）局部应力（特别是拉伸应力）加速的腐蚀失效，该局部应力在单调载荷和疲劳载荷下都会增强开裂。 |
| Wind energy (Unit kJ) | 风能（单位kJ） |
The kinetic energy associated with wind that can be converted by a wind energy conversion system (WECS) into electrical or mechanical power by a rotor, such as a multi-bladed propeller, exposed to the wind. If the air density is ρ and the wind speed is V, then the kinetic energy flux is ρV3/2. The actual wind power that can be extracted by a wind turbine intercepting a cross section of wind A is CPρAV3/2 where CP is an empirical efficiency factor termed the power coefficient. The wind-energy distribution is a histogram of the calculated wind power that can be generated annually from the windspeed frequency distribution at a given location. A windmill generates mechanical power whereas a wind turbine (wind generator) generates electrical power. The largest wind turbine, manufactured by MHI Vestas, has a power rating of 9.5 MW, a rotor diameter of 164 m, and a hub height of 105 m (the highest wind turbines have heights in the region of 190 m). A wind farm is an array of wind turbines, typically ten to several hundred, at a single location, either onshore or offshore. Energy derived from wind is a major contributor to sustainable energy generation. The largest operational offshore wind farm, located in the Irish Sea, has 87 turbines and a total generating capacity of 659 MW. The largest onshore wind farm is in Kern County, California with some 586 turbines and a total capacity of 1 550 MW. 风能转换系统（WECS）可通过暴露于风中的转子（如多叶片螺旋桨）将与风相关的动能转换为电能或机械能。如果空气密度为ρ，风速为V，则动能通量为ρV3/2。可由截获风a横截面的风力涡轮机提取的实际风功率为CPρAV3/2，其中CP是称为功率系数的经验效率因子。风能分布是根据给定位置处的风速频率分布每年可产生的计算风力的直方图。风车产生机械功率，而风力涡轮机（风力发电机）产生电功率。MHI Vestas制造的最大风力涡轮机的额定功率为9.5MW，转子直径为164m，轮毂高度为105m（最高风力涡轮机的高度为190m）。风电场是一系列风力涡轮机，通常为十到几百台，位于单一位置，无论是陆上还是海上。风能是可持续能源发电的主要贡献者。最大的海上风电场位于爱尔兰海，拥有87台涡轮机，总发电容量为659MW。最大的陆上风电场位于加利福尼亚州克恩县，拥有约586台涡轮机，总容量为1550兆瓦。 |
| Aging treatment | 时效处理 |
Heat treatment aimed at age hardening; it comprises solution and precipitation treatments. 针对时效硬化的热处理；它包括溶液和沉淀处理。 |
| Annealing carbon | 退火碳 |
Fine, apparently amorphous carbon particles formed in white cast iron and certain steels during prolonged annealing. Also called temper carbon. 白口铸铁和某些钢在长时间退火过程中形成的细小、明显的无定形碳颗粒。也称为回火碳。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Radial marks | 径向标记 |
Lines on a fracture surface that radiate from the fracture origin and are visible to the unaided eye or at low magnification. Radial lines result from the intersection and connection of brittle fractures propagating at different levels. Also known as shear ledges. 断裂表面上的线，从断裂起点辐射，肉眼可见或在低放大率下可见。径向线是在不同层面上传播的脆性断裂相交和连接的结果。也称为剪切壁架。 |
| Scratching | 刮擦 |
In tribology, the mechanical removal or displacement, or both, of material from a surface by the action of abrasive particles or protuberances sliding across the surfaces. 在摩擦学中，通过在表面上滑动的磨粒或突起的作用，材料从表面上的机械移除或移位，或两者兼而有之。 |
| Dead load (Unit N) | 静载（单位N） |
A load on a component or structure that is steady with time, e.g. the self-weight of a bridge. 部件或结构上随时间稳定的载荷，例如桥梁的自重。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Dimension line | 尺寸线 |
A line on an engineering drawing with a numeral above it that shows the length of a feature, usually in millimetres. 工程图上的一条线，上面有一个数字，表示特征的长度，通常以毫米为单位。 |
| Maximum allowable operating pressure (Unit Pa) | 最大允许使用压力（单位Pa） |
The highest pressure at which any pressure system may be operated, usually 10 to 20% below the maximum allowable working pressure. 任何压力系统可运行的最高压力，通常比最大允许工作压力低10%至20%。 |
| Profilometer | 轮廓仪 |
An instrument used to quantify the roughness of a surface. For a contact profilometer, a diamond stylus sweeps across the surface along a series of parallel lines. Noncontact profilometers use optical techniques to map the surface irregularities. 用于量化表面粗糙度的仪器。对于接触式轮廓仪，钻石触针沿一系列平行线扫过表面。非接触式轮廓仪使用光学技术绘制表面不规则。 |
| Wedge | 楔子 |
A short triangular prism whose major surfaces subtend an acute angle, that can be driven between two objects or parts of an object to split, tighten, or secure them, or to widen an opening or raise a heavy object. The acute angle gives a high mechanical advantage. 一种短的三棱镜，其主面对着一个锐角，可在两个物体或物体的一部分之间驱动，以将它们分开、拧紧或固定，或加宽开口或举起重物。锐角具有很高的机械优势。 |
| Dead space | 死区 |
(dead volume) (Unit m³) That volume of a gas-filled thermometer in which the gas is not at the same temperature as that being measured. （死容）（单位m³）充气温度计的体积，其中气体的温度与被测温度不同。 |
| Anneal to temper | 退火回火 |
A final partial anneal that softens a cold worked nonferrous alloy to a specified level of hardness or tensile strength. 将冷加工的有色金属合金软化到规定的硬度或抗拉强度水平的最终局部退火。 |
| Surface hardness | 表面硬度 |
(superficial hardness) Indentation hardness on, and for some distance below, the surface of a component, as opposed to its bulk hardness. Depending on the resolution required, micro- or nano-hardness testing machines are employed. （表面硬度）与整体硬度相反，部件表面及其下方一定距离的压痕硬度。根据所需的分辨率，可使用微型或纳米硬度测试机。 |
| Milling | 铣削 |
A machining process, typically for metals and plastics, in which a multi-tooth rotary cutter removes material to produce flat or profiled surfaces, slots, grooves, etc. Milling is a machining process in which metal is removed by a rotating multiple-tooth cutter; each tooth removes a small amount of metal with each revolution of the spindle. Because both workpiece and cutter can be moved in more than one direction at the same time, surfaces having almost any orientation can be machined. 一种加工工艺，通常用于金属和塑料，其中多齿旋转刀具去除材料以产生平坦或异形表面、槽、槽等。金属由旋转多齿刀具去除；主轴每转一圈，每个齿都会去除少量金属。因为工件和刀具可以同时在多个方向上移动，所以几乎可以加工任何方向的表面。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Austenitizing | 奥氏体化 |
Forming austenite by heating a ferrous alloy into the transformation range (partial austenitizing) or above the transformation range (complete austenitizing). When used without qualification, the term implies complete austenitizing. 通过将铁合金加热到转变范围（部分奥氏体化）或高于转变范围（完全奥氏体化）来形成奥氏体。当不加限定地使用时，该术语意味着完全奥氏体化。 |
| Degree (°) | 度数（°） |
A measure of plane angle such that 1° is 1/360 of a complete revolution and equal to π/180 rad. 平面角度的一种度量，使得1°是一整圈的1/360，等于π/180弧度。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Unit | 单位 |
A numerical indication of the magnitude of a physical quantity. The basic units of mass, length, time, etc. are relative to agreed standards. 物理量大小的数字指示。质量、长度、时间等基本单位与商定的标准相对应。 |
| Kilogram (kg) | 千克（kg） |
The base unit of mass in the SI system. It was previously defined as being equal to the mass of the International Prototype Kilogram, a right cylinder of height and diameter 39.17 mm made of an alloy of 90% (by mass) platinum and 10% iridium. From 20 May 2019 it has been defined by taking the fixed numerical value of the Planck constant h to be 6.626 070 150 × 10−34 when expressed in the unit J.s, which is equal to kg.m².s. 国际单位制中的基本质量单位。它以前被定义为等于国际原型千克的质量，一个高度和直径为39.17毫米的右圆柱体，由90%（质量）的铂和10%的铱合金制成。从2019年5月20日起，普朗克常数h的固定数值被定义为6.626070150×10−34当以单位J.s表示时，和kg.m².s一样。 |
| Shrink fit | 过盈配合 |
A tight interference fit between two components resulting from heating an outer part and/or cooling an inner part to allow easy assembly. The outer component contracts on cooling, while the inner part expands on warming to ambient temperature, thus gripping the two parts together. 由于加热外部部件和/或冷却内部部件而导致的两个部件之间的紧密过盈配合，以便于组装。外部部件在冷却时收缩，而内部部件在加热到环境温度时膨胀，从而将两个部件夹在一起。 |
| Total head (hT) (Unit m) | 总水头（hT）（单位：m） |
Total pressure pT expressed in terms of the vertical height of a column of liquid, typically water or mercury, i.e. hT = pT/ρg where g is the acceleration due to gravity and ρ is the liquid density. 总压力pT以液体柱（通常为水或汞）的垂直高度表示，即hT=pT/ρg，其中g为重力加速度，ρ为液体密度。 |
| Scuffing | 擦伤 |
A form of adhesive wear that produces superficial scratches or a high polish on the rubbing surfaces. It is observed most often on inadequately lubricated parts. 粘着磨损的一种形式，在摩擦表面上产生表面划痕或高度抛光。通常在润滑不足的零件上观察到。 |
| Fatigue test | 疲劳测试 |
A method for determining the range of alternating (fluctuating)stresses a material can withstand without failing. 一种确定材料可以承受而不会失效的交变（波动）应力范围的方法。 |
| Manometer | 压力计 |
An instrument used in the measurement of a pressure difference in a fluid (manometry). 用于测量流体压力差（测压）的仪器。 |
| Olsen cup test | 奥尔森杯测试 |
A cupping test in which a piece of sheet metal, restrained except at the center, is deformed by a standard steel ball until fracture occurs. The height of the cup at time of fracture is a measure of the ductility. 一种杯突试验，其中一块金属板，除了中心以外，被一个标准钢球变形，直到发生断裂。断裂时杯的高度是延展性的量度。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| Universal joint (Hooke’s joint) | 万向节（胡克接头） |
A double-pivoted connection that allows power and torque to be transmitted between two shafts at an angle to each other. For constant driving angular velocity of the input yoke, the angular velocity of the output yoke fluctuates by amounts depending on the angle of intersection of the shafts. Speeds of the driving and driven shafts may be made identical (giving a constant-velocity joint) when an intermediate shaft, at each end of which there is a universal joint, is interposed. The driving and driven shafts must be equally inclined to the intermediate shaft, the two forks of which must lie in the same plane. 一种双枢轴连接，允许动力和扭矩以一定角度在两个轴之间传递。对于输入磁轭的恒定驱动角速度，输出磁轭的角速度根据轴的相交角度波动。当插入中间轴时，驱动轴和从动轴的速度可以相同（提供恒定速度接头），中间轴的两端都有万向节。主动轴和从动轴必须与中间轴倾斜相等，中间轴的两个叉必须位于同一平面内。 |
| Anelastic | 无弹性 |
Literally ‘not elastic’, but in practice used for materials that display timedependent recovery on unloading. 字面意思是“没有弹性”，但实际上用于在卸载时显示随时间恢复的材料。 |
| Biaxial stress | 双轴应力 |
Generalized loading of a body in a single plane with no loading normal to it. 物体在一个平面内的广义载荷，没有垂直于它的载荷。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Base metal hardness | 母材硬度 |
Hardness closest to the surface (when traversing from core to outside diameter) just before an increase or decrease occurs, denoting, respectively, carburization or decarburization. 在发生增加或减少之前最接近表面的硬度（从芯部到外径时），分别表示渗碳或脱碳。 |
| Decarburization | 脱碳 |
Loss of carbon from the surface layer of a carbon-containing alloy due to reaction with one or more chemical substances in a medium that contacts the surface. 由于与接触表面的介质中的一种或多种化学物质发生反应，含碳合金表面层的碳损失。 |
| Crack-extension force (G) | 裂纹扩展力（G） |
The elastic energy per unit of new separation area that would be made available at the front of an ideal crack in an elastic solid during a virtual increment of forward crack extension. 在向前裂纹扩展的虚拟增量期间，在弹性固体中理想裂纹的前端可获得的每单位新分离面积的弹性能量。 |
| Standard hole | 标准孔 |
A hole in a workpiece bored to a specified tolerance where clearance with a shaft is accomplished by allowance on the shaft. A standard shaft is machined to a specified tolerance where clearance with a hole is accomplished by allowance on the hole. 工件上的孔，钻孔至规定公差，其中与轴的间隙通过轴上的余量来实现。标准轴加工至规定公差，其中与孔的间隙通过孔上的公差实现。 |
| Impact | 撞击 |
Sudden loading of a body or component, as in a vehicle collision or striking by a hammer. 物体或部件的突然加载，如车辆碰撞或锤击。 |
| Recrystallization temperature | 再结晶温度 |
The approximate minimum temperature at which complete recrystallization of a cold-worked metal occurs within a specified time. 冷加工金属在规定时间内发生完全再结晶的近似最低温度。 |
| Peel strength (Unit N) | 剥离强度（单位：N） |
(peel test) The strength of an adhesive bond between two materials as measured by the force required in a given direction to peel apart adhered strips. This force depends on the dimensions and thickness of the adhered strips and their yield stress, together with the fracture toughness of the bond. （剥离试验）两种材料之间的粘合强度，通过给定方向上剥离粘合条所需的力来测量。该力取决于粘合条的尺寸和厚度及其屈服应力，以及粘合剂的断裂韧性。 |
| Thread form | 螺纹形式 |
The cross-sectional shape of the threads, defining thread angle, root, and crest profiles, etc. Thread length Length of that portion of the fastener which contains threads cut or rolled to full depth. 螺纹的横截面形状，定义螺纹角度、齿根和齿冠轮廓等。螺纹长度：紧固件中包含全深度切割或轧制螺纹的部分的长度。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Fracture | 断裂 |
(rupture) The separation of materials, components, or structures into two or more parts by the propagation of one or more cracks. Cracking may be globally elastic (brittle) or accompanied by varying degrees of plasticity (ductile). （断裂）通过一个或多个裂纹的扩展将材料、部件或结构分离成两个或更多部分。裂纹可能是整体弹性（脆性）或伴有不同程度的塑性（延性）。 |
| Salt-velocity meter | 盐速计 |
A volume flow meter based on detecting the transit time for a small quantity of salt or radioactive isotope in a flow by measuring electrical conductivity or radiation level. 一种体积流量计，通过测量电导率或辐射水平来检测流量中少量盐或放射性同位素的渡越时间。 |
| Ferritic decarburization | 铁素体脱碳 |
Decarburization with sufficient loss of carbon to cause a lighter shade of tempered martensite and a significantly lower hardness than that of the adjacent base metal, with the presence of ferrite grains or grain boundary network under metallographic examination. 脱碳，碳损失充分，导致回火马氏体颜色较浅，硬度明显低于相邻母材，金相检查时存在铁素体晶粒或晶界网络。 |
| Barometer | 气压计 |
An instrument used to measure atmospheric pressure. An instrument for measuring atmospheric pressure. There are two main types – the mercury barometer, and the aneroid barometer. 用于测量大气压力的仪器。有两种主要类型——水银气压计和无液气压计。 |
| Strength (Unit Pa) | 强度（单位Pa） |
The maximum stress, in tension, compression, shear, or combinations thereof, that may be monotonically applied to a material, component, or structure before failure (defined as fracture, yielding, buckling, etc. as appropriate). 在破坏前（视情况定义为断裂、屈服、屈曲等），材料、部件或结构在拉伸、压缩、剪切或其组合中可能单调施加的最大应力。 |
| Applied thermodynamics | 应用热力学 |
(engineering thermodynamics, thermodynamics) The science of the relationship between heat, work and the properties of systems and the ways in which heat energy from fuels can be converted into mechanical work. It involves the study of all aspects of energy use and energy transformation, including power generation, refrigeration, the relevant properties of the substances involved and the relationships between them. The principle of conservation of energy is a fundamental law of nature. （工程热力学、热力学）热、功和系统特性之间关系的科学，以及燃料中的热能可以转化为机械功的方式。它涉及能源使用和能源转换的各个方面的研究，包括发电、制冷、所涉及物质的相关特性以及它们之间的关系。能量守恒定律是自然的基本规律。 |
| Normality | 常态 |
The principle that the vector sum of plastic strain increments is perpendicular to the yield surface. 塑性应变增量矢量和垂直于屈服面的原理。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| Amontons friction | 阿蒙顿摩擦 |
(Coulomb friction) Friction between surfaces where the ratio of the frictional force F to the normal force N is constant and independent of the area in contact. （库仑摩擦）摩擦力F与法向力N之比恒定且与接触面积无关的表面之间的摩擦。 |
| Form of thread | 螺纹形式 |
The profile of a thread in an axial plane for a length of one pitch. 一个螺距长度的螺纹在轴向平面中的轮廓。 |
| Lockbolt | 锁紧螺栓 |
A fastener which bears a superficial resemblance to a bolt, but which engages a collar (instead of a nut) with annular grooves (instead of threads). The collar is swaged over the grooves on the male fastener to develop preload. 表面上类似于螺栓的紧固件，但与环槽（而不是螺纹）接合的轴环（而不是螺母）。套环在阳紧固件上的凹槽上锻造，以产生预紧力。 |
| Fitted bolt | 装配螺栓 |
A bolt with a plain unthreaded portion immediately beneath the head. 一种螺栓，其头部正下方有一个普通的无螺纹部分。 |
| Knot (kn) | 节（kn） |
A non-SI unit defined as one nautical mile per hour. The conversion to SI is 1 kn = 5.144 444 444×10−1 m/s. 非国际单位制单位，定义为每小时一海里。转换为SI为1kN=5.144444×10−1米/秒。 |
| Pin expansion test | 插头膨胀试验 |
A test for determining the ability of a tube to be expanded or for revealing the presence of cracks or other longitudinal weaknesses in it, made by forcing a tapered pin into the open end of the tube, similar to flare test. 通过将锥形销压入管道开口端来确定管道膨胀能力或揭示其存在裂纹或其他纵向缺陷的试验，类似于扩口试验。 |
| Absolute manometer | 绝对压力计 |
A manometer that measures absolute pressure, i.e. pressure measured relative to a perfect vacuum. Absolute pressure cannot be negative. 测量绝对压力的压力计，即相对于完美真空测量的压力。绝对压力不能为负。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| Verified loading range | 验证加载范围 |
For testing machines, the range of indicated loads for which the testing machine gives results within the permissible variation specified. 对于试验机，试验机在规定允许偏差范围内给出结果的指示载荷范围。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Bucket | 吊桶 |
1. A cup-shaped vane with a central dividing ridge attached to the periphery of the runner of an impulse water turbine such as a Pelton turbine. 2. A rotor blade in a compressor or turbine. 1.一种杯形叶片，所述杯形叶片具有附接到冲击式水轮机（例如冲击式水轮机台）的转轮的外围的中央分隔脊。2.压缩机或涡轮机中的转子叶片。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Coil spring | 螺旋弹簧 |
A spiral (‘clockwork’) or helical (cylindrical) spring. A spring steel wire wound in a spiral pattern. 螺旋（“发条”）或螺旋（圆柱形）弹簧。以螺旋状缠绕的弹簧钢丝。 |
| Tolerance limits | 公差极限 |
The extreme values (upper and lower) that define the range of permissible variation in size or other quality characteristic of a part. 定义零件尺寸或其他质量特性允许偏差范围的极值（上限和下限）。 |
| Oxidizing agent | 氧化剂 |
A compound that causes oxidation, thereby itself becoming reduced. 一种引起氧化从而自身被还原的化合物。 |
| Mechanical metallurgy | 机械冶金 |
The science and technology dealing with the behavior of metals when subjected to applied forces. 处理金属在外力作用下的行为的科学技术。 |
| 显示更多数据，请使用查询功能！ | ||