| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Ackerman linkage | 阿克曼装置 |
A steering linkage on a motor vehicle that approximately gives rolling without slipping of both wheels about the turning point. This is achieved by having the inner stub axle (on the inside of the turning curve) move through a greater angle than the outer stub axle. 机动车辆上的一种转向联动装置，在转向点附近两个车轮几乎不会打滑。这是通过使内短轴（在转弯曲线的内侧）比外短轴移动更大的角度来实现的。 |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Hoseclip | 软管夹 |
(hose clamp) A circular metal band, one end of which has a screw mechanism through which passes the other end such that the screw engages with indentations in the band, allowing the clip to be tightened or loosened. Used to hold a hose on to a pipe such as a water outlet. （软管夹）一种圆形金属带，其一端有一个螺钉组织，另一端穿过该螺钉组织，使螺钉与带子上的凹口啮合，从而可以拧紧或松开夹子。用于将软管固定在管道上，例如出水口。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Cold extrusion | 冷挤压 |
In simplest terms, cold extrusion can be defined as the forcing of unheated metal to flow through a shape-forming die. It is a method of shaping metal by plastically deforming it under compression at room temperature while the metal is within a die cavity formed by the tools. The metal issues from the die in at least one direction with the desired cross-sectional contour, as permitted by the orifice created by the tools. Cold extrusion is always performed at a temperature well below the recrystallization temperature of the metal (about 1100 to 1300 degrees F. for steel) so that work-hardening always occurs. In hot extrusion, recrystallization eliminates the effects of work-hardening, unless rapid cooling of the extrusion prevents recrystallization from being completed. 用简单的术语来说，冷挤压可以定义为迫使未加热的金属流过成形模具。这是一种通过在室温下压缩使金属塑性变形来成形金属的方法，同时金属处于由工具形成的模腔中。金属至少在一个方向上从模具中流出，并具有所需的横截面轮廓，这是由工具产生的孔口所允许的。冷挤压总是在远低于金属再结晶温度的温度下进行（钢约1100至1300华氏度），因此总是发生加工硬化。在热挤压中，再结晶消除了加工硬化的影响，除非挤压的快速冷却阻止再结晶完成。 |
| Combined heat and power plant | 热电联产电厂 |
(CHP plant, COGEN, cogeneration plant, total-energy plant) A plant for the simultaneous production of more than one useful form of energy from the same energy source, such as process heat and electric power. In the arrangement shown, partially expanded steam is extracted from the steam turbine and used to produce process heat. （CHP工厂、COGEN、热电联产工厂、总能源工厂）从同一能源（如过程热能和电力）同时生产一种以上有用能源的工厂。在所示的布置中，部分膨胀的蒸汽从蒸汽轮机中提取并用于产生过程热量。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Millimetre of water | 毫米水柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of water 1 mm high. Approximately equal to 9.81 Pa. 一种非SI压力单位，等于1毫米高的垂直水柱施加的压力。大约等于9.81Pa。 |
| Impact energy (Unit J) | 冲击能量（单位J） |
The amount of energy required to fracture a material, usually measured by means of an Izod test or Charpy test.The type of specimen and test conditions affect the values and therefore should be specified. 1. The sum of the kinetic energies of all the bodies involved at the instant of collision of two or more moving bodies. 2. The energy required to fracture a specimen in a Charpy or Izod impact test. 使材料断裂所需的能量，通常通过悬臂梁式试验或夏比试验测量。试样类型和试验条件会影响数值，因此应加以说明。1.两个或多个运动物体碰撞瞬间所有物体的动能之和。2.夏比或悬臂冲击试验中断裂试样所需的能量。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Radiator | 散热器 |
A heat exchanger used to transfer thermal energy from one fluid to another for heating or cooling purposes. Despite the name, the principal mode of heat transfer is convection rather than radiation. In motor vehicles, water circulated through the engine block is cooled as it flows through the tubes of an air-cooled heat exchanger. In domestic radiators, hot water from a boiler is circulated through a heat exchanger with a large surface area which transfers heat to the surrounding air. 一种热交换器，用于将热能从一种流体传递到另一种流体，用于加热或冷却。尽管有这个名字，但热传递的主要方式是对流而不是辐射。在机动车辆中，通过发动机缸体循环的水在流经风冷热交换器的管道时被冷却。在家用散热器中，来自锅炉的热水通过具有大表面积的热交换器循环，该热交换器将热量传递给周围的空气。 |
| Variance | 方差 |
A measure of the squared dispersion of observed values or measurements expressed as a function of the sum of the squared deviations from the population mean or sample average. 观测值或测量值的平方离散度的度量，表示为总体平均值或样本平均值的平方偏差之和的函数。 |
| Tangential load (Unit N) | 切向荷载（单位：N） |
The component of load applied to an object, such as a gear, that tends to cause or resist rotation. 旋转力施加在物体上的载荷分量，如齿轮，倾向于引起或阻止旋转。 |
| Centi (c) | 厘（c） |
An SI unit prefix indicating a multiplier of 0.01; thus centimetre is a unit of length equal to one one-hundredth of a metre or 10 mm. 表示乘数0.01的SI单位前缀；因此厘米是长度单位，等于一米的百分之一或10毫米。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Sigma phase | σ相 |
A hard, brittle, nonmagnetic intermediate phase with a tetragonal crystal structure, containing 30 atoms per unit cell, space group P42/mnm, occurring in many binary and ternary alloys of the transition elements. The composition of this phase in the various systems is not the same, and the phase usually exhibits a wide range in homogeneity. Alloying with a third transition element usually enlarges the field of homogeneity and extends it deep into the ternary section. 一种硬、脆、非磁性中间相，具有四方晶体结构，每单位晶胞含有30个原子，空间群P42/mnm，存在于许多过渡元素的二元和三元合金中。该相在各种系统中的组成不尽相同，并且该相通常表现出宽范围的均匀性。与第三过渡元素的合金化通常会扩大均匀性范围，并将其延伸到三元区。 |
| Torsion bar | 扭杆 |
A metal bar designed to act as an elastic spring when torque is applied. 当施加扭矩时用作弹性弹簧的金属棒。 |
| DIN | DIN |
Deutsches Institut für Normung, the German Institute for Standardization. Deutsches Institut für Normung，德国标准化研究所。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Two-stage compressor | 两级压缩机 |
A machine in which gas is compressed from low pressure toan intermediate pressure in a low-pressure cylinder, and then to final pressure in a highpressure cylinder. Efficiency is improved if the two cylinders are separated by an intercooler. 一种机器，其中气体在低压气缸中从低压压缩到中压，然后在高压气缸中压缩到最终压力。如果两个气缸由中冷器分离，则效率提高。 |
| Allotropy | 同素异形体 |
A near synonym for polymorphism. Allotropy is generally restricted to describing polymorphic behavior in elements, terminal phases, and alloys whose behavior closely parallels that of the predominant constituent element. 多态性的近义词。同素异形体通常仅限于描述元素、终端相和合金中的多晶型行为，其行为与主要组成元素的行为非常相似。 |
| Maximum allowable working pressure (Unit Pa) | 最大允许工作压力（单位Pa） |
The pressure on which the design of a pressure system is based and the highest pressure at which relief valves should be set. The lowest-rated component in the system typically has a design safety factor of 4. 压力系统设计所依据的压力和应设置安全阀的最高压力。系统中最低额定部件的设计安全系数通常为4。 |
| Maximum continuous load | 最大连续负载 |
(maximum continuous rating) (Unit kg/s) The maximum rate of steam output that a boiler can supply for a specified period, usually 24 hours. （最大连续额定功率）（单位为kg/s）锅炉在规定时间内（通常为24小时）可供应的最大蒸汽输出率。 |
| Acoustic separation | 声学分离 |
(Unit m) The separation of particles in a fluid using standing acoustic waves, typically ultrasound, to drive them to nodal points (acoustic particle concentration). （单位m）使用驻声波（通常是超声波）将流体中的粒子分离，以将它们驱动到节点（声学粒子浓度）。 |
| Coaxial | 同轴 |
A term for components having a common axis such as concentric shafts. 具有共同轴线的部件的术语，例如同心轴。 |
| Maximum allowable operating pressure (Unit Pa) | 最大允许使用压力（单位Pa） |
The highest pressure at which any pressure system may be operated, usually 10 to 20% below the maximum allowable working pressure. 任何压力系统可运行的最高压力，通常比最大允许工作压力低10%至20%。 |
| Flexural strength | 抗弯强度 |
The maximum stress in the outer fiber at the moment of crack or break. 断裂或断裂时刻外层纤维的最大应力。 |
| Wind pump | 风泵 |
A pump driven directly by a windmill on a tower. Widely used in remote locations. 由塔上的风车直接驱动的泵。广泛应用于偏远地区。 |
| Strength of bolt | 螺栓强度 |
An ambiguous term which can mean Ultimate strength or Proof load or Endurance limit or Yield strength. 一个模棱两可的术语，可表示极限强度或验证荷载或耐久极限或屈服强度。 |
| Unison ring | 协调环 |
In a turbomachine with adjustable guide or stator vanes, the ring to which a set of vanes is linked such that when the ring is rotated, all vane angles are adjusted. 在具有可调导向叶片或定子叶片的涡轮机中，一组叶片连接到的环，当环旋转时，所有叶片角度都可调整。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Weight (W) (Unit N) | 重量（W）（单位：N） |
The force of attraction on a body due to gravity. A body’s weight is the product of its mass and the gravitational field strength at that point. Mass remains constant, but weight depends on the object’s position on the Earth’s surface, decreasing with increasing altitude. If g is the acceleration due to gravity, the weight of a mass m is given by W = mg. On Earth, the acceleration due to gravity is approximately 9.81 m/s², so that the weight of a 1 kg mass is 9.81 N. More generally, the weight is the force exerted on the mass of a body when in the gravitational field of another body. 重力由于重力作用在物体上的吸引力。物体的重量是其质量和该点引力场强度的乘积。质量保持不变，但重量取决于物体在地球表面的位置，随着海拔的升高而减小。如果g是重力引起的加速度，则质量m的重量由W=mg给出。在地球上，重力引起的加速度约为9.81m/s²，因此1千克质量的重量为9.81N。更一般地说，重量是在另一个物体的重力场中施加在物体质量上的力。 |
| Median fatigue strength at N cycles | N次循环的中位疲劳强度 |
An estimate of the stress level at which 50% of the population would survive N cycles. The estimate is derived from a particular point of the fatigue life distribution, because there is no test procedure by which a frequency distribution of fatigue strengths at Ncycles can be directly observed. 估计50%的量在N个周期内生存的压力水平。该估计值来自疲劳寿命分布的一个特定点，因为没有试验程序可以直接观察N次循环疲劳强度的频率分布。 |
| Degradation failure | 退化失效 |
Failure of a system, component, or structure owing to material degradation. 由于材料退化导致的系统、组件或结构失效。 |
| Computed path control | 计算路径控制 |
In CNC or robotics, the use of a control program to determine the required path for the tool or end effector. This required path forms the set points for the motor controllers moving the machine tool or robot. 在CNC或机器人技术中，使用控制程序来确定工具或末端执行器所需的路径。这条所需的路径形成了用于移动机床或机器人的电机控制器的设定点。 |
| Fracture test | 断裂试验 |
A test in which a specimen is broken and its fracture surface is examined with the unaided eye or with a low-power microscope to determine such factors as composition, grain size, case depth, or internal discontinuities. 1. The recording of load-deflexion (or stress–strain) in a specimen loaded monotonically until it breaks in tension, compression, shear, or torsion. 2. In fatigue, determination of the number of cycles to fracture for a specimen under different patterns of repeated loading. 3. Experiments to determine fracture toughness. 一种试验，其中试样被破坏并用肉眼或低倍显微镜检查其断裂表面，以确定成分、晶粒尺寸、表层深度或内部不连续性等因素。1.记录单调加载试样的载荷偏转（或应力-应变），直到其在拉伸、压缩、剪切或扭转中断裂。2.在疲劳技术中，确定试样在不同重复载荷模式下的断裂循环次数。3.测定断裂韧性的实验。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Shoulder joint | 轴肩关节 |
The second joint on an articulated robot, which has a horizontal axis and is analogous to the human shoulder. 关节机器人上的第二个关节，具有水平轴，类似于人的肩膀。 |
| Effective radius of nut, bolt head, or threads | 螺母、螺栓头或螺纹的有效半径 |
Distance between the geometric center of the part and the circle of points through which the resultant contact forces between mating parts passes. Must be determined by integration. 零件几何中心与配合零件之间的合力通过的点圆之间的距离。必须通过积分来确定。 |
| Dynamics | 动力学 |
The branch of mechanics that deals with objects in motion. Its two main branches are kinematics, which studies motion without regards to its cause, and kinetics, which also takes into account forces that cause motion. 力学中研究运动物体的分支。它的两个主要分支是运动学和动力学，前者研究运动而不考虑其原因，后者也考虑引起运动的力。 |
| Artificial aging | 人工时效 |
Aging above room temperature. 在室温以上的时效。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Multiple threaded screw | 多螺纹螺钉 |
A screw with two or more threads cut around the periphery of the workpiece to provide an increased lead with a specified pitch. 一种螺钉，具有围绕工件周边切割的两个或多个螺纹，以提供具有指定螺距的增加的导程。 |
| Breaking load | 断裂载荷 |
The maximum load (or force) applied to a test specimen or structural member loaded to rupture. 施加到加载到破裂的试样或结构构件上的最大载荷（或力）。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Vibration-testing machine (vibrator) | 振动试验机（振动器） |
Any machine that subjects components or systems to vibration at known amplitudes and frequencies in order to determine the response. vibratory equipment Vibrating process equipment, such as shakers, used to separate small and large particles, or feeders to supply particulate or granular material that may otherwise clog. 使部件或系统以已知振幅和频率振动以确定响应的任何机器。振动设备振动工艺设备，如用于分离小颗粒和大颗粒的振动筛，或用于供应可能堵塞的颗粒或粒状材料的给料机。 |
| Radiation pressure (Unit μPa) | 辐射压力（单位：μPa） |
The pressure exerted on a surface exposed to any form of electromagnetic radiation. If the radiation is absorbed, it is equal to the power-flux density divided by the speed of light. 施加在暴露于任何形式电磁辐射的表面上的压力。如果辐射被吸收，它等于功率通量密度除以光速。 |
| Minimum material condition | 最小材料条件 |
(minimum metal condition) The situation where the volume of a manufactured component corresponds to the lower limit of all toleranced external dimensions and to the upper limit for all internal dimensions. （最小金属条件）制造部件的体积对应于所有公差外部尺寸的下限和所有内部尺寸的上限的情况。 |
| Horizontal batch furnace | 卧式间歇炉 |
A versatile batch-type furnace that can give light or deep case depths, and because the parts are not exposed to air, horizontal batch furnaces can give surfaces almost entirely free of oxides. 一种多功能间歇式炉，可以提供浅或深的外壳深度，并且由于零件不暴露在空气中，卧式间歇式炉可以使表面几乎完全没有氧化物。 |
| Nanomanufacturing | 纳米制造 |
1. The manufacture of nanoscale materials. 2. The manufacture of components or devices that have critical dimensions of order 1 nm. 1.纳米材料的制造。2.具有1nm级临界尺寸的部件或装置的制造。 |
| Rosette | 玫瑰形的结 |
Strain gages arranged to indicate, at a single position, strain in three different directions. 应变计布置成在单个位置指示三个不同方向的应变。 |
| Gas compressor | 气体压缩机 |
A machine which draws in a gas at low pressure and delivers it at high pressure, usually accompanied by a temperature increase. Compressor designs include axial, centrifugal, diaphragm, reciprocating, and rotary (including the blade compressor). 一种在低压下吸入气体并在高压下输送气体的机器，通常伴随着温度升高。压缩机设计包括轴流式、离心式、隔膜式、往复式和旋转式（包括叶片式压缩机）。 |
| Maximum load (Pmax) | 最大负载（Pmax） |
(1) The load having the highest algebraic value in the load cycle. Tensile loads are considered positive and compressive loads negative. (2)Used to determine the strength of a structural member; the load that can be borne before failure is apparent. （1）负载循环中具有最高代数值的负载。拉伸荷载视为正荷载，压缩荷载视为负荷载。（2）用于确定结构构件的强度；失效前可承受的载荷是明显的。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| British thermal unit (BTU, Btu) | 英热单位（BTU，Btu） |
An obsolete (non-SI) imperial unit of energy defined as the energy required to raise the temperature of one pound of pure water at 68°F by 1°F. The conversion to SI is 1 Btu = 1.055 056 × 103 J. 一种已被淘汰的（非SI）英制能量单位，定义为将68°F的一磅纯水的温度升高1°F所需的能量。转换为SI为1Btu=1.055056×103J。 |
| Positive-displacement machine | 正排量机 |
A machine that incorporates pistons, valves, etc. to ensure positive admission and delivery of a working fluid and prevent undesired reversal of flow. This class of machine incorporates all reciprocating compressors and expanders and some types of rotary compressor, the Roots blower, agear pump, a lobe pump, and a vane pump. 包含活塞、阀门等的机器，以确保工作流体的正向进入和输送，并防止不期望的反向流动。这类机器包括所有往复式压缩机和膨胀机以及一些类型的旋转压缩机、罗茨鼓风机、抽水机、凸轮泵和叶片泵。 |
| Mole (mol) | 摩尔（mol） |
The base unit of the amount of substance in the SI system. It was previously defined as the amount of substance of a system that contains as many elementary entities as there are atoms in 0.012 kg of carbon-12. From 20 May 2019 it has been defined as the amount of substance containing exactly 6.022 140 76 × 1023 elementary entities. SI国际单位制中物质量的基本单位。此前，它被定义为一个系统中的物质量，该系统包含的基本实体数量与0.012千克碳-12中的原子数量相同。从2019年5月20日起，它已被定义为包含6.02214076×1023个基本实体的物质量。 |
| Diaphragm meter | 隔膜计 |
A dry flow meter in which there are two or more interconnected chambers, each having a diaphragm in the wall. The chambers empty and fill alternately and the flow rate of gas is determined from the movement of diaphragms. Diaphragm meters are commonly used to monitor domestic and commercial gas supply. 一种干式流量计，其中有两个或多个相互连接的腔室，每个腔室的壁上都有一个隔膜。腔室交替排空和填充，气体流速由隔膜的移动确定。隔膜流量计通常用于监测家用和商用燃气供应。 |
| Computer-aided manufacturing | 计算机辅助制造 |
(CAM, computer-integrated manufacturing, CIM) The use of computers in all branches of manufacturing, not only to control machines and robots for manufacturing and assembly, but also for process planning, and monitoring progress of materials and components during production, etc. （CAM，计算机集成制造，CIM）在制造的所有分支中使用计算机，不仅可以控制制造和组装的机器和机器人，还可以进行工艺规划，以及在生产过程中监控材料和组件的进度等。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Breaking stress | 断裂应力 |
The stress at failure. Also known as rupture stress. 失效时的应力。也称为破裂应力。 |
| Toothed gearing | 齿轮传动 |
In principle, friction between circular discs in tangential contact could be used to transmit rotation and power between shafts, but the power level would be very limited and the velocity ratio affected by slip. To make the drive positive, gear wheels are used instead in which teeth extend above and below the diameters (the pitch-circle diameters) of discs in ideal rolling contact. The diagram shows the nomenclature for spur gears, the simplest type of gearing between parallel shafts, which are cylindrical in shape with straight teeth parallel to the axis of rotation. 原则上，切向接触的圆盘之间的摩擦可用于在轴之间传递旋转和动力，但动力水平非常有限，速比受滑动的影响。为了使驱动积极，使用齿轮代替，齿轮中的齿延伸到理想滚动接触的圆盘直径（节圆直径）的上方和下方。该图显示了直齿轮的名称，这是平行轴之间最简单的齿轮传动类型，其形状为圆柱形，直齿平行于旋转轴。 |
| Proof strength (Unit Pa) | 验证强度（单位Pa） |
(proof stress, Rp, Rp,) The yield strength (offset yield strength) at some fixed value of the permanent strain given by the intersection of a line offset from, but parallel to, the elastic loading line and the engineering stress-engineering strain curve. The offset is arbitrary but is usually 0.1, 0.2, or 0.5% permanent strain (the proof strain). Used for materials which do not exhibit a sharply defined yield point. The notation Rp0.2 or Rp0.2 is employed for the 0.2% proof stress. （验证应力，Rp）在永久应变的某个固定值下的屈服强度（偏移屈服强度），由偏离但平行于弹性加载线的线与工程应力-工程应变曲线的交点给出。偏移是任意的，但通常为0.1、0.2或0.5%的永久应变（验证应变）。用于没有明确定义屈服点的材料。对于0.2%的验证应力，采用符号Rp0.2。 |
| Generator | 发电机 |
1. A machine for converting mechanical energy to electrical energy. 2. (generatrix) A point, line, or surface regarded as moving and so forming a line, a surface, or a volume, respectively. 1.将机械能转化为电能的机器。2.（母线）被认为是运动的点、线或面，因此分别形成一条线、一个面或一个体积。 |
| Pressure difference (Unit Pa) | 压差（单位Pa） |
(pressure differential, Δp) The difference between two pressures, one of which may be a reference pressure such as barometric pressure. In many flow processes, the pressure difference is more important than the absolute pressure level. （压差，Δp）两个压力之间的差值，其中一个压力可以是参考压力，如大气压力。在许多流动过程中，压差比绝对压力水平更重要。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Pascal’s law | 帕斯卡定律 |
When there is a change in pressure at any point in a confined fluid at rest, there is an equal change at every other point in the fluid volume. 当处于静止状态的受限流体中任何一点的压力发生变化时，流体体积中的每一点的变化都相等。 |
| Slant fracture | 倾斜裂缝 |
A type of fracture appearance, typical of plane-stress fractures, in which the plane of metal separation is inclined at an angle (usually about 45°) to the axis of the applied stress. 一种断裂现象，典型的平面应力断裂，其中金属分离面与施加应力的轴成一定角度（通常约45°）倾斜。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| Crack arrest | 止裂 |
Crack propagation that stops of its own accord when the energy release rate of the loaded component or structure falls below a critical value. If predictable, it can be incorporated into structural-integrity assessments. 当加载部件或结构的能量释放率低于临界值时，裂纹自行停止扩展。如果可以预测，可以将其纳入结构完整性评估。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Stead’s brittleness | 斯特德脆性 |
A condition of brittleness that causes transcrystalline fracture in the coarse grain structure that results from prolonged annealing of thin sheets of low-carbon steel previously rolled at a temperature below about 705 °C (1300 °F). The fracture usually occurs at about 45° to the direction of rolling. 一种脆性状态，导致粗晶结构中发生穿晶断裂，这是由于之前在低于约705°C（1300°F）的温度下轧制的低碳钢薄板经过长时间退火造成的。断裂通常发生在与轧制方向约45°处。 |
| Quick coupling | 快速接头 |
(quick disconnect, fast coupling) A hose connection allowing rapid assembly or disassembly and comprising a socket and a plug incorporating a springloaded locking mechanism. （快速断开、快速连接）一种软管连接，允许快速组装或拆卸，包括插座和带有弹簧加载锁定机构的插头。 |
| Differential heating | 差动加热 |
Heating that intentionally produces a temperature gradient within an object such that, after cooling, a desired stress distribution or variation in properties is present within the object. 加热有意在物体内产生温度梯度，从而在冷却后，在物体内出现所需的应力分布或特性变化。 |
| Stress | 应力（单位Pa） |
The intensity of the internally distributed forces or components of forces that resist a change in the volume or shape of a material that is or has been subjected to external forces. Stress is expressed in force per unit area and is calculated on the basis of the original dimensions of the cross section of the specimen. Stress can be either direct (tension or compression)or shear. 1. Stress ‘at a point’ (i.e. over a volume of material that is very small compared with that of the component or structure) is the load per unit area for every face of an infinitesimal cube surrounding the point. 2. In fluid flow the stress tensor σij is the sum of an isotropic part −pδij, δij being the Kronecker delta, having the same form as the stress tensor for a fluid at rest, p being the static pressure, and the non-isotropic, deviatoric stress tensor dij which is due entirely to the fluid motion. 内部分布力或力分量的强度，这些力或力的分量抵抗正在或已经受到外力的材料的体积或形状的变化。应力以单位面积的力表示，并根据试样横截面的原始尺寸计算。应力可以是直接（拉伸或压缩）或剪切。1.“在一点”的应力（即在与组件或结构相比非常小的材料体积上）是围绕该点的无限小立方体的每个面的单位面积载荷。2. 在流体流动中，应力张量σij是各向同性部分-pδij的总和，δij是Kroneckerδ，具有与静止流体的应力张量相同的形式，p是静压，非各向同性, 偏应力张量 dij 完全由流体运动引起。 |
| Starting valve (regulator) | 起动阀（调节器） |
A valve which admits steam from the boiler to the cylinder(s) of a steam engine. 将蒸汽从锅炉送入蒸汽机汽缸的阀门。 |
| Galvanic protection | 电流保护 |
The coating on a fastener is said to provide galvanic protection if it is more anodic than the fastener and will, therefore, be destroyed instead of the fastener. Zinc plate (galvanizing) provides galvanic protection to steel fasteners, for example. 如果紧固件上的涂层比紧固件更具阳极性，则据说它可以提供电流保护，将会因此被破坏而不是紧固。例如，锌板（镀锌）为钢紧固件提供电流保护。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Workspace (Unit m³) | 工作空间（单位m³） |
(working-space volume) The volume around the base frame of a robot, defined by the reach of the robot. The robot can thus only perform tasks within this volume. （工作空间体积）机器人基架周围的体积，由机器人的可达范围定义。因此，机器人只能执行该体积内的任务。 |
| Atmosphere | 大气 |
1. (atm) An obsolete (non-SI) unit of pressure equal to 101 325 Pa or 1.013 25 bar and approximately equal to the atmospheric pressure (barometric pressure) measured at mean sea level. 1.（atm）一种已被淘汰的（非SI）压力单位，等于101325Pa或1.01325bar，大约等于在平均海平面测量的大气压力（大气压）。 |
| Double aging | 双级时效 |
Employment of two different aging treatments to control the type of precipitate formed from a supersaturated matrix in order to obtain the desired properties. The first aging treatment, sometimes referred to as intermediate or stabilizing, is usually carried out at higher temperature than the second. 采用两种不同的时效处理来控制由过饱和基质形成的沉淀物类型，以获得所需的性能。第一次时效处理，有时称为中间处理或稳定处理，通常在比第二次更高的温度下进行。 |
| Normal temperature and pressure (NTP) | 常温常压（NTP） |
Reference conditions defined by NIST as 20°C and 1 atm. NIST定义的参考条件为20°C和1atm。 |
| Critical temperature | 临界温度 |
(1) Synonymous with critical point if the pressure is constant. (2) The temperature above which the vapor phase cannot be condensed to liquid by an increase in pressure. （1） 如果压力恒定，则与临界点同义。（2） 高于该温度时，气相不能通过压力升高而冷凝为液体。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Preload accuracy | 预载精度 |
A measure of the precision with which a given tool or procedure creates preload in a bolt when the bolt is tightened. A common torque wrench, for example, is said to produce preload with an accuracy of +30%. The mean preload, however, may not be that which the designer intended, or may not be what he should have intended. Accuracy as used here, in other words, is synonymous with Scatter. 当螺栓拧紧时，给定工具或程序在螺栓中产生预紧力的精度度量。例如，一个普通的扭矩扳手据说可以产生精度为+30%的预载。然而，平均预载可能不是设计者预期的。这里使用的准确度是分散度的同义词。 |
| Flange rotation | 法兰转角 |
Angular distortion of a flange under the influence of bolt and reaction forces. Measured with respect to the center of the cross section of the flange. 法兰在螺栓和反作用力影响下的角度变形。相对于法兰横截面的中心测量。 |
| Working fluid | 工作流体 |
In thermodynamics, the fluid contained within the boundary of a system that experiences changes in its properties during any fluid dynamic or thermodynamic process. 在热力学中，包含在系统边界内的流体，在任何流体动力学或热力学过程中其性质发生变化。 |
| Nonlinear behavior | 非线性行为 |
A fastener or joint system is said to exhibit nonlinear behavior when the relationship between the External load on the joint and deformation of the parts is nonlinear, or when the relationship between increasing Preload and deformation is nonlinear. 当接头上的外部载荷与零件变形之间的关系是非线性的，或者当增加的预载荷与变形之间的联系是非线性的时，可以说紧固件或接头系统表现出非线性行为。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Fastener identification marking | 紧固件识别标记 |
A stamp, paint, or other permanent identifier that may include manufacturer information and applicable grade markings for certification purposes. 印章、油漆或其他永久性标识符，其中可能包括制造商信息和用于认证的适用等级标记。 |
| Critical crack length (Unit m) | 临界裂纹长度（单位米） |
The crack length at which a given stress applied to a body will result in crack propagation and fracture. 施加到物体上的给定应力将导致裂纹扩展和断裂的裂纹长度。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Vapour–pressure curve | 蒸汽压力曲线 |
For a pure substance, the curve of saturation pressure plotted vs saturation temperature. 对于纯物质，绘制了饱和压力与饱和温度的曲线。 |
| Archimedes Wave Swing | 阿基米德波摆动 |
A machine for tidal-power energy generation consisting of two concentric, air-filled submerged cylinders. The inner lower cylinder is tethered to the ocean floor while the upper floater unit, which is closed at the top, moves up and down due to the variations in hydrostatic pressure caused by the wave motion. The relative movement of the two cylinders is used to generate electricity in which linear motion replaces the more common rotary motion of an electromagnetic generator. 一种用于潮汐能发电的机器，由两个同心的充气水下气缸组成。内部下部圆柱体系在海底，而顶部封闭的上部浮子单元由于波浪运动引起的静水压力变化而上下移动。两个气缸的相对运动用于发电，其中直线运动取代了电磁发电机更常见的旋转运动。 |
| Octane number | 辛烷值 |
(octane rating) A measure of the anti-knock properties of a fuel taken as the percentage by volume of iso-octane in the fuel. （辛烷值）以燃料中异辛烷的体积百分比表示的燃料抗爆性能的量度。 |
| Shoulder bolt | 轴肩螺栓 |
A bolt for which the unthreaded cylindrical section between the thread and the head is of larger diameter than the threaded section, precisely machined to length and diameter and hardened 一种螺栓，其螺纹和头部之间的无螺纹圆柱段的直径大于螺纹段的直径，精确加工至长度和直径并硬化 |
| Grinding | 研磨 |
1. A process of high-speed multiple scratching of surfaces by a wheel formed from hard grits and a binder which are progressively exposed as the binder wears away. It is a process of micromachining employed particularly in accurate finishing operations on hard materials. 2. A form of comminution. 1.一种通过由硬砂砾和粘合剂形成的轮对表面进行高速多次刮擦的方法，所述硬砂砾和粘结剂随着粘合剂的磨损而逐渐暴露。这是一种微机械加工工艺，特别适用于硬材料的精确精加工操作。2.一种粉碎形式。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Fretting corrosion | 微动腐蚀 |
(1) The accelerated deterioration at the interface between contacting surfaces as the result of corrosion and slight oscillatory movement between the two surfaces. (2) A form of fretting in which chemical reaction predominates. Fretting corrosion is often characterized by the removal of particles and subsequent formation of oxides, which are often abrasive and so increase the wear. Fretting corrosion can involve other chemical reaction products, which may not be abrasive. （1）由于两个表面之间的腐蚀和轻微振荡运动，接触表面之间的界面加速劣化。（2）一种以化学反应为主的微动磨损形式。微动腐蚀通常以颗粒的去除和随后形成的氧化物为特征，这些氧化物通常具有研磨性，因此会增加磨损。微动腐蚀可能涉及其他化学反应产物，这些化学反应产物可能不是磨料。 |
| Compression pressure (Unit Pa) | 压缩压力（单位Pa） |
The pressure produced in a cylinder of a piston engine by compression of air in the absence of fuel. 在没有燃料的情况下通过压缩空气在活塞发动机的气缸中产生的压力。 |
| Dislocation density | 位错密度 |
The total length of dislocation lines per unit volume, or the number of dislocation lines that cut through a unit cross-sectional area. 每单位体积的位错线的总长度，或穿过单位横截面积的位错线的数量。 |
| Angström (Å) | 昂斯特罗姆（Å） |
An obsolete (non-SI) unit of length, sometimes still employed for atomic and crystallographic measurements. The conversion to SI is 1 Å = 10−10 m. 一种已被淘汰的（非SI）长度单位，有时仍用于原子和晶体学测量。转换为SI为1Å=10-10m。 |
| Air compressor | 空气压缩机 |
A turbomachine that draws in air and delivers it at higher pressure, temperature, and density. It can be of axial, fan, reciprocating, or rotary design. 一种涡轮机，它吸入空气并以更高的压力、温度和密度输送空气。它可以是轴流式、风扇式、往复式或旋转式设计。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Bernoulli’s law | 伯努利定律 |
For a steadily flowing fluid (liquid or gas), the sum of the pressure, kinetic energy per unit volume and potential energy per unit volume is constant at any point in the fluid. Using this relationship, it is possible to measure the velocity of a fluid by measuring its pressure at two points, as with a manometer or Pitot tube. 对于稳定流动的流体（液体或气体），压力、每单位体积的动能和每单位体积的势能之和在流体中的任何点都是恒定的。使用这种关系，可以通过在两个点测量流体的压力来测量流体的速度，就像使用压力计或皮托管一样。 |
| Lock nut | 锁紧螺母 |
A type of nut that is prevented from loosening under vibration. The locking action is accomplished by squeezing, gripping or jamming against the bolt threads. A nut which provides extra resistance to vibration loosening (beyond that produced by proper Preload ), either by providing some form of Prevailing torque, or, in free-spinning lock nuts, by deforming, cramping, or biting into mating parts when fully tightened. 1. A thin auxiliary nut tightened against another nut to prevent loosening. 2. A single nut with special features that prevent loosening. 一种在振动下防止松动的螺母。锁定动作通过挤压、夹紧或卡住螺栓螺纹来完成。通过提供某种形式的主要扭矩，或在自由旋转锁紧螺母中，通过完全拧紧时变形、夹紧或咬入配合零件，提供额外的抗振动松动能力（超出适当预载产生的能力）。1.一个薄的辅助螺母，拧紧到另一个螺母上以防止松动。2.具有防止松动的特殊功能的单个螺母。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Tempered martensite embrittlement | 回火马氏体脆化 |
Embrittlement of ultrahigh-strength steels caused by tempering in the temperature range of 205 to 400 °C (400 to 750 °F); also called 350 °C or 500 °F embrittlement. Tempered martensite embrittlement is thought to result from the combined effects of cementite precipitation on prioraustenite grain boundaries or interlath boundaries and the segregation of impurities at prioraustenite grain boundaries. 超高强度钢在205至400°C（400至750°F）温度范围内回火引起的脆化；也称为350°C或500°F脆化。回火马氏体脆化被认为是由于渗碳体沉淀在原奥氏体晶界或层间晶界上以及杂质在原奥氏体晶粒边界处偏析的综合影响。 |
| Pascal (Pa) | 帕斯卡（Pa） |
The SI unit of pressure, 1 Pa = 1 N/m². 压力的国际单位制，1Pa=1N/m²。 |
| Verified loading range | 验证加载范围 |
For testing machines, the range of indicated loads for which the testing machine gives results within the permissible variation specified. 对于试验机，试验机在规定允许偏差范围内给出结果的指示载荷范围。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Water column | 水柱 |
Water in a tube, which may be vertical or inclined. If the tube is open to the atmosphere, the vertical height h from a datum level to the water surface is a measure of the water static pressure p at the datum level given by p − B = ρgh where B is the barometric pressure, ρ denotes the water density, and g is the acceleration due to gravity. 管道中的水，可以是垂直的或倾斜的。如果管道向大气开放，则从基准面到水面的垂直高度h是基准面处水静压p的量度，由p给出−B=ρgh，其中B是大气压力，ρ表示水密度，g是重力引起的加速度。 |
| Track rod | 横拉杆 |
A bar connecting the ends of the steering arms in an automotive vehicle. 连接汽车转向臂端部的杆。 |
| Age softening | 时效软化 |
Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain hardened alloys, especially those of aluminum. 某些应变硬化合金，尤其是铝合金，在室温下会发生强度和硬度的自发降低。 |
| Transition temperature (Unit K) | 转变温度（单位K） |
(1) An arbitrarily defined temperature that lies within the temperature range in which metal fracture characteristics (as usually determined by tests of notched specimens) change rapidly, such as from primarily fibrous (shear)to primarily crystalline (cleavage) fracture. (2) Sometimes used to denote an arbitrarily defined temperature within a range in which the ductility changes rapidly with temperature. (transition point) 1. The temperature at which the mechanism of fracture in metal alloys having a face-centred cubic crystal structure changes from ductile void growth to brittle cleavage. 2. The temperature at which a material changes from one crystal state to another. （1） 任意定义的温度，位于金属断裂特性（通常通过缺口试样的试验确定）快速变化的温度范围内，如从主要纤维（剪切）断裂到主要结晶（解理）断裂。（2） 有时用于表示延性随温度快速变化的范围内的任意定义的温度。（转变点）1.具有面心立方晶体结构的金属合金的断裂机制从韧性孔洞生长转变为脆性解理的温度。2.材料从一种晶体状态转变为另一种晶体的温度。 |
| Deformation (Unit 1/s) | 变形（单位1/s） |
A change in the form of a body due to stress, thermal change, change in moisture, or other causes. In solid mechanics, any change, reversible (elastic) or permanent (plastic), in the shape or size of parts of a body, or the whole body, caused by external or internal loading. It includes extension, compression, bending, and twisting. The same state of deformation in a body can appear as different combinations of elongation and shear. To state how much of the total strain is shear, it is split into dilatation and deviatoric components, the former changing volume but not shape, the latter shape but not volume. 由于压力、热变化、水分变化或其他原因导致的身体形态变化。在固体力学中，由外部或内部载荷引起的身体各部分或整个身体的形状或大小的任何可逆（弹性）或永久（塑性）变化。它包括拉伸、压缩、弯曲和扭曲。物体中相同的变形状态可以表现为伸长和剪切的不同组合。为了说明总应变中有多少是剪切，将其分为膨胀分量和偏差分量，前者改变体积但不改变形状，后者改变形状但不改变体积。 |
| Least count | 最小计数 |
The smallest value that can be read from an instrument having a graduated scale. Except on instruments provided with a vernier, the least count is that fraction of the smallest division which can be conveniently and reliably estimated; this fraction is ordinarily one-fifth or one-tenth, except where the graduations are very closely spaced. 可从具有刻度尺的仪器中读取的最小值。除配备游标的仪器外，最小计数是可以方便可靠地估计的最小除法的分数；这个分数通常是五分之一或十分之一，除非刻度间隔非常近。 |
| Ball mill | 球磨机 |
A mill for grinding and pulverizing materials, consisting of a horizontal rotating drum containing loose steel or ceramic balls. 一种用于研磨和粉碎物料的磨机，由装有松散钢球或陶瓷球的水平旋转滚筒组成。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| mechanical engineering | 机械工业 |
That branch of engineering concerned with energy conversion, stress analysis, vibration, dynamics, and kinematics, especially applied to design (machine design, mechanical-engineering design). 与能量转换、应力分析、振动、动力学和运动学有关的工程分支，尤其适用于设计（机器设计、机械工程设计）。 |
| Permanent set | 永久变形 |
The deformation or strain remaining in a previously stressed body after release of load. 释放荷载后，先前受力物体中剩余的变形或应变。 |
| Shear | 扭剪 |
The type of force that causes or tends to cause two contiguous parts of the same body to slide relative to each other in a direction parallel to their plane of contact. 导致或倾向于导致同一物体的两个相邻部分在平行于其接触面的方向上相对滑动的力的类型。 |
| Newton’s law of viscosity | 牛顿内摩擦定律 |
The shear stress between two parallel layers of fluid is proportional to the velocity of one relative to that of the other, and inversely proportional to the distance between them. The constant of proportionality is the dynamic viscosity μ. For a Newtonian fluid μ is independent of pressure gradient, shear stress, and strain, but may change with temperature and pressure. 两个平行流体层之间的剪切应力与其中一层相对于另一层的速度成正比，与它们之间的距离成反比。比例常数是动态粘度μ。对于牛顿流体，μ与压力梯度、剪切应力和应变无关，但可能随温度和压力而变化。 |
| Root diameter (Unit m) | 根部直径（单位：m） |
The diameter of the circle passing through the roots of teeth in gear teeth or screw threads. 穿过齿轮齿或螺纹中齿根的圆的直径。 |
| Compressible flow | 可压缩流动 |
A gas flow in which the Mach number M is sufficiently high for the gas density to change significantly. For air, this is when M > 0.3. 马赫数M高到足以使气体密度发生显着变化的气流。对于空气，这是当M>0.3时。 |
| Design load (Unit N) | 设计荷载（单位N） |
The greatest load that a component or structure is expected to experience under normal operating conditions. 部件或结构在正常运行条件下预期承受的最大负载。 |
| Coalescence | 聚结 |
Growth of grains at the expense of the remainder by absorption or the growth of a phase or particle at the expense of the remainder by absorption or reprecipitation. 通过吸收以牺牲剩余为代价的晶粒的生长或以通过吸收或再沉淀为代价的以剩余为代价的相或颗粒的生长。 |
| Rubber hardness | 橡胶硬度 |
The indentation hardness of rubber-like materials in which the depth of indentation under load is measured. This is a measure of elastic moduli rather than yield stress as with ductile materials, since there is little, if any, permanent impression remaining on unloading rubbery materials. 测量负载下压痕深度的橡胶类材料的压痕硬度。这是对弹性模量的测量，而不是对韧性材料的屈服应力，因为卸载橡胶材料时几乎没有（如果有的话）永久压痕。 |
| Combustion chamber | 炉膛 |
1. In a piston engine, the volume between the head of an individual cylinder and the crown of the piston in which the fuel–air mixture burns during each power stroke of the engine. 2. (combustor) In a gas-turbine engine, a ramjet, an afterburner, or a rocket motor, the component, often cylindrical or annular in shape, in which the fuel–air mixture burns in a continuous-flow process. 1.在活塞式发动机中，在发动机的每个动力冲程中，燃料-空气混合物燃烧的单个气缸盖和活塞顶之间的体积。2.（燃烧室）在燃气涡轮发动机、冲压发动机、加力燃烧室或火箭发动机中，燃料-空气混合物在连续流动过程中燃烧的部件，通常为圆柱形或环形。 |
| Fastener specification | 紧固件规格 |
A precise statement of set requirements to be satisfied by a fastener, its material, or its processing. It also indicates the procedure used to determine whether the requirements given are satisfied. 对紧固件、其材料或加工过程要满足的设定要求的精确陈述。它还指出了用于确定是否满足给定要求的程序。 |
| Flat head | 平头 |
Flat top surface and a conical bearing surface. 平顶表面和锥形轴承表面。 |
| Velocity ratio | 速度比 |
1. The ratio between the input velocity to a machine, train of gears, etc. and the output velocity. 2. The ratio between the displacement of an applied force at one part of a mechanism and the movement of the load at a different part. 1.机器、齿轮系等的输入速度与输出速度之间的比率。2.在机构的一个部分处施加的力的位移与在不同部分处的载荷的移动之间的比率。 |
| High strength low alloy steels | 高强度低合金钢 |
(HSLA steels) Steels with various micro-alloying elements such as copper, nickel, chromium, molybdenum, niobium, titanium, and vanadium in small quantities that give improved strength (as high as 900 MPa) and corrosion properties compared with plain carbon steels. Improvements are due to grain refinement and precipitation hardening, better control of the chemistry during steel making, and accurate rolling temperatures. （HSLA钢）是含有各种微合金元素的钢，如少量的铜、镍、铬、钼、铌、钛和钒，与普通碳钢相比，具有更好的强度（高达900MPa）和腐蚀性能。这些改进归功于晶粒细化和沉淀硬化、炼钢过程中更好的化学控制以及精确的轧制温度。 |
| Size effect | 尺寸效应 |
Effect of the dimensions of a piece of metal on its mechanical and other properties and on manufacturing variables such as forging reduction and heat treatment. In general, the mechanical properties are lower for a larger size. 金属件的尺寸对其机械和其他性能以及对制造变量（如锻造、压下和热处理）的影响。一般来说，尺寸越大，机械性能越低。 |
| Gearbox | 变速箱 |
A mechanism consisting of meshing gears which transmit power and torque to an output shaft from an input shaft directly connected to an engine. The mechanism is normally contained within a casing filled with lubricating oil. The diagram shows a simple four-speed sliding-mesh gearbox in which gears with different numbers of teeth are slid along parallel splined shafts within the gearbox to mesh with each other and change the ratio of output to input speed (gear ratio). 一种由啮合齿轮组成的机构，将动力和扭矩从直接连接到发动机的输入轴传递到输出轴。该机构通常包含在充满润滑油的外壳内。示例一个简单的四速滑动啮合齿轮箱，其中具有不同齿数的齿轮沿着齿轮箱内的平行花键轴滑动，以相互啮合并改变输出与输入速度的比率（齿轮比）。 |
| Concurrent engineering | 并行工程 |
The integration of the procedures for product design, material selection and manufacturing method to include life-cycle analysis. 产品设计、材料选择和制造方法程序的整合，包括生命周期分析。 |
| Wind energy (Unit kJ) | 风能（单位kJ） |
The kinetic energy associated with wind that can be converted by a wind energy conversion system (WECS) into electrical or mechanical power by a rotor, such as a multi-bladed propeller, exposed to the wind. If the air density is ρ and the wind speed is V, then the kinetic energy flux is ρV3/2. The actual wind power that can be extracted by a wind turbine intercepting a cross section of wind A is CPρAV3/2 where CP is an empirical efficiency factor termed the power coefficient. The wind-energy distribution is a histogram of the calculated wind power that can be generated annually from the windspeed frequency distribution at a given location. A windmill generates mechanical power whereas a wind turbine (wind generator) generates electrical power. The largest wind turbine, manufactured by MHI Vestas, has a power rating of 9.5 MW, a rotor diameter of 164 m, and a hub height of 105 m (the highest wind turbines have heights in the region of 190 m). A wind farm is an array of wind turbines, typically ten to several hundred, at a single location, either onshore or offshore. Energy derived from wind is a major contributor to sustainable energy generation. The largest operational offshore wind farm, located in the Irish Sea, has 87 turbines and a total generating capacity of 659 MW. The largest onshore wind farm is in Kern County, California with some 586 turbines and a total capacity of 1 550 MW. 风能转换系统（WECS）可通过暴露于风中的转子（如多叶片螺旋桨）将与风相关的动能转换为电能或机械能。如果空气密度为ρ，风速为V，则动能通量为ρV3/2。可由截获风a横截面的风力涡轮机提取的实际风功率为CPρAV3/2，其中CP是称为功率系数的经验效率因子。风能分布是根据给定位置处的风速频率分布每年可产生的计算风力的直方图。风车产生机械功率，而风力涡轮机（风力发电机）产生电功率。MHI Vestas制造的最大风力涡轮机的额定功率为9.5MW，转子直径为164m，轮毂高度为105m（最高风力涡轮机的高度为190m）。风电场是一系列风力涡轮机，通常为十到几百台，位于单一位置，无论是陆上还是海上。风能是可持续能源发电的主要贡献者。最大的海上风电场位于爱尔兰海，拥有87台涡轮机，总发电容量为659MW。最大的陆上风电场位于加利福尼亚州克恩县，拥有约586台涡轮机，总容量为1550兆瓦。 |
| Head height | 头部高度 |
The head height shall be that overall distance measured parallel to the axis of the product from the top of the head to the bearing surface and shall include the thickness of the washer face. Raised grade and manufacturer’s identification are excluded from head height. 头部高度应为平行于产品轴线从封头顶部到支承面测量的总距离，并应包括垫圈表面的厚度。提升等级和制造商标识不包括在头部高度中。 |
| Effective length of a bolt | 螺栓的有效长度 |
The grip length plus some portion of the bolt (often one-half of the thickness of the nuts) which lies within the nut(s) plus some portion (often one-half the thickness) of the head. 握持长度加上位于螺母内的螺栓的某些部分（通常是螺母厚度的二分之一）加上头部的某些部分（通常是厚度的二分之一）。 |
| Creep fatigue | 蠕变疲劳 |
The effects of combined creep and fatigue at high homologous temperatures in metals, and in other materials such as polymers having time-dependent behaviour. 金属和其他材料（例如具有时间相关行为的聚合物）在高同源温度下的组合蠕变和疲劳的影响。 |
| Ion nitriding | 离子氮化 |
A method of surface hardening in which nitrogen ions are diffused into a workpiece in a vacuum through the use of high-voltage electrical energy. Synonymous with plasma nitriding or glowdischarge nitriding. 一种表面硬化方法，其中氮离子通过使用高压电能在真空中扩散到工件中。与等离子体氮化或辉光放电氮化同义。 |
| Corrosion cell | 腐蚀电池 |
A natural ‘‘battery’’ formed when two metals having different electrical potentials (an Anode and a Cathode) are connected together in the presence of a liquid (the Electrolyte). 当两种具有不同电势的金属（阳极和阴极）在液体（电解质）存在下连接在一起时形成的天然“电池”。 |
| Transmission dynamometer | 传动测功机 |
A dynamometer in which the power transmitted by a shaft is obtained from the product of its rotation speed and the torque determined from measured shear strains along the shaft. 一种测功机，其中轴传递的功率由其转速和扭矩的乘积获得，扭矩由沿轴测得的剪切应变确定。 |
| Inch (in) | 英寸（in） |
A non-SI unit of length now defined as 25.4 mm. The conversion to SI is 1 in = 2.54 × 10−2 m. 现在定义为25.4毫米的非SI长度单位。转换为SI为1in=2.54×10-2m。 |
| Mechanical units | 机械单位 |
The units of physical quantities, the dimensions of which includemass, length, and time. 物理量的单位，其量纲包括质量、长度和时间。 |
| Coefficient of thermal expansion | 热膨胀系数 |
(1) Change in unit of length (or volume) accompanying a unit change of temperature, at a specified temperature. (2) The linear or volume expansion of a given material per degree rise of temperature, expressed at an arbitrary base temperature or as a more complicated equation applicable to a wide range. （1） 单位长度（或体积）随温度单位变化的变化。（2） 给定材料每上升一度的线性或体积膨胀，在任意基础温度下表示，或作为适用于宽范围的更复杂方程表示。 |
| Total combustion air (Unit kg/s) | 总燃烧空气（单位：kg/s） |
1. The combination of the stoichiometric flow of air required for combustion together with any excess air. 2. The flow of fresh air into a boiler plus any flue gas recirculated. 1.燃烧所需的化学计量空气流与任何过量空气的组合。2.进入锅炉的新鲜空气流加上再循环的任何烟气。 |
| Coarsening | 粗粒化 |
An increase in the grain size, usually, but not necessarily, by grain growth. 晶粒尺寸的增加，通常但不一定是晶粒变大。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Deposit gauge | 沉积量计 |
(deposition gauge) An instrument employed in air pollution studies for measuring the amount of pollutant deposited on a given area in a given time under given conditions. （沉降计）在空气污染研究中使用的仪器，用于测量在给定条件下在给定时间内沉积在给定区域上的污染物量。 |
| Relaxation curve | 松弛曲线 |
A plot of either the remaining, or relaxed, stress as a function of time. 剩余压力或松弛压力随时间变化的曲线图。 |
| Transmission | 传输 |
The system that transmits power and torque from a power source; for example a shaft, belts and pulleys, or a gear train. In the case of a motor vehicle, it includes the gearbox, clutch, propeller shaft, differential and final drive shafts. 从动力源传输功率和扭矩的系统；例如轴、皮带和滑轮或齿轮系。对于机动车辆，包括变速箱、离合器、传动轴、差速器和终传动轴。 |
| Initial stress | 初始应力 |
The stress produced by strain in a specimen immediately on achieving the given constant-strain conditions in a stress-relaxation test before stress-relaxation occurs. Sometimes referred to as instantaneous stress. 在应力松弛发生之前，在应力松弛试验中达到给定的恒定应变条件时，试样立即应变所产生的应力。有时称为瞬时压力。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Thermodynamic process | 热力学过程 |
A change in equilibrium state undergone by a quantity of matter or a system. 一定量的物质或系统所经历的平衡状态的变化。 |
| Belt drive | 带传动 |
Transmission of motion from one shaft to another by means of a continuous plain, or toothed, flexible band (belt) passing over pulleys. In contrast to chain drives, belt drives tend to be employed in low-torque applications. Reduction in transmissible power may occur due to stretch of a plain transmission belt which results in slack in the drive (belt creep) or slip of a belt on a driving or driven pulley (belt slip). 通过穿过滑轮的连续平带或带齿柔性带（带）将运动从一根轴传递到另一根轴。与链条传动相比，皮带传动往往用于低扭矩应用。由于普通传动带的拉伸可能会导致传动松弛（皮带蠕变）或主动或从动皮带轮上的皮带打滑（皮带打滑），从而导致传动功率降低。 |
| Axial load (Unit N) | 轴向载荷（单位N） |
In general, a tensile or compressive load directed along the axis of a component. Strictly the load should pass through the centroid of the cross section to avoid inducing bending moments and be perpendicular to the plane of the section. 通常，沿部件的轴定向的拉伸或压缩载荷。严格来说，载荷应通过横截面的质心以避免产生弯矩并垂直于横截面。 |
| Cold treatment | 冷处理 |
Treatment carried out after quenching to transform retained austenite into martensite, involving cooling and holding at a temperature below ambient. 淬火后进行的处理，以将残余奥氏体转变为马氏体，包括冷却和保持在低于环境温度的温度。 |
| Critical point | 临界点 |
(1) The temperature or pressure at which a change in crystal structure, phase or physical properties occurs. Same as transformation temperature. (2) In an equilibrium diagram, that specific value of composition, temperature and pressure, or combinations thereof, at which the phases of a heterogeneous system are in equilibrium. （1） 晶体结构、相或物理性质发生变化的温度或压力。与转变温度相同。（2） 在平衡图中，指组成、温度和压力或其组合的特定值，在该值下，多相体系的相处于平衡状态。 |
| Extra spring | 额外弹簧 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state above full hard beyond which further cold work will not measurably increase the strength and hardness. 有色金属合金和一些铁合金的回火状态，大约对应于高于全硬的冷加工状态，超过该状态进一步冷加工将不会显着增加强度和硬度。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Pressure recovery (Unit Pa) | 压力恢复（单位Pa） |
The progressive increase in static pressure for unseparated flow through a diverging nozzle or diffuser. 通过发散喷嘴或扩散器的未分离流的静压逐渐增加。 |
| Die | 模具 |
1. A tool having an appropriately-shaped hole through which material may be extruded or drawn. 2. A tool employed in forging. 3. A block having the male or female shape employed in stamping operations. 4. A thick circular disc, driven by a die wrench, with internally-threaded cutting edges for producing a screw thread. A die wrench (die stock) holds a screw-cutting die and has two projecting arms for applying the torque necessary to cut the thread. A die having a hexagonal or square shape (die nut), driven by a spanner, is used in confined spaces where a die wrench cannot be rotated through a full circle. 1.一种具有适当形状的孔的工具，通过该孔可以挤压或拉伸材料。2.一种用于锻造的工具。3.一种用于冲压操作的具有阳或阴形状的块体。4.一种由模具扳手驱动的厚圆盘，具有用于产生螺纹的内螺纹切削刃。冲模扳手（冲模）装有一个螺旋切割模，并有两个突出臂，用于施加切割螺纹所需的扭矩。由扳手驱动的六边形或方形模具（模具螺母）用于模具扳手无法旋转一整圈的受限空间。 |
| Helical spring | 螺旋弹簧 |
A spring manufactured by forming elastic wire into a helix which may be cylindrical, conical, barrel-shaped, or hourglass in overall form. Closed-coiled springs are used in tension; open-coiled in both tension and compression. 一种弹簧，通过将弹性线材制成螺旋形而制成，螺旋形的整体形状可以是圆柱形、圆锥形、桶形或沙漏形。拉力采用闭合盘簧；在拉伸和压缩中都开卷。 |
| Centrifugal force (Unit N) | 离心力（单位N） |
The inertial reaction force to the centripetal force. It is equal in magnitude but opposite in direction. 惯性反作用力对向心力。它的大小相等，但方向相反。 |
| Blanking shear test | 落料剪力试验 |
A method used to determine the through-thickness shear strength of sheet material that involves blanking a disk out of flat strip using a simple punch-and-die method. Alson known as punching shear test. 一种用于确定板材全厚度剪切强度的方法，包括使用简单的冲模方法从扁平带材中冲裁出圆盘。也称为冲切试验。 |
| Complete decarburization | 完全脱碳 |
Decarburization with sufficient carbon loss to show only clearly defined ferrite grains under metallographic examination. 脱碳，具有足够的碳损失，以在金相检查下仅显示清晰定义的铁素体晶粒。 |
| Plastic deformation | 塑性变形 |
The permanent (inelastic) distortion of a material under applied stress that strains the material beyond its elastic limit. 材料在施加应力下的永久（非弹性）变形，使材料应变超过其弹性极限。 |
| Spring constant | 弹簧常数 |
The ratio between the forces exerted on a spring (or a bolt) and the deflection thereof. Has the dimensions of force per unit change in length (e.g., lb=in.). Also called Stiffness. 施加在弹簧（或螺栓）上的力与其挠度之间的比率。具有每单位长度变化的力的尺寸（例如lb=in.）。也称为刚度。 |
| Stretch-bending test | 拉伸弯曲试验 |
A simulative test for sheet metal formability in which a strip of sheet metal is clamped at its ends in lock beads and deformed in the center by a punch. Test conditions are chosen so that fracture occurs in the region of punch contact. 金属板成形性的模拟试验，其中金属板条在其端部夹紧在锁珠中，并通过冲头在中心变形。选择试验条件，以便在冲头接触区域发生断裂。 |
| Centrifuge | 离心机 |
A machine incorporating a rapidly spinning drum in which liquids and suspended particles of different densities are separated by centrifugal action. 一种装有快速旋转滚筒的机器，在该滚筒中，不同密度的液体和悬浮颗粒通过离心作用分离。 |
| Stiffness | 刚度 |
(1) The ability of a metal or shape to resist elastic deflection.(2) The rate of stress increase with respect to the rate of increase in strain induced in the metal or shape; the greater the stress required to produce a given strain, the stiffer the material is said to be. （1）金属或形状抵抗弹性变形的能力。（2）所述应力增加速率相对于在所述金属或形状中诱导的应变增加速率；产生给定应变所需的应力越大，材料就越硬。 |
| Load range, P | 负载范围P |
In fatigue, the algebraic difference between the maximum and minimum loads in a fatigue cycle. 在疲劳中，疲劳循环中最大和最小载荷之间的代数差。 |
| Abrasion | 磨损 |
The removal of surface material by the scratching action of hard particles, either deliberately (abrasive papers, abrasive cleaning, abrasive machining) or as a consequence of operation (wear). 通过硬质颗粒的刮擦作用去除表面材料，可以是故意的（砂纸、研磨清洁、研磨加工），也可以是操作的结果（磨损）。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Weld penetration | 焊接熔深 |
It is the depth below the surfaces, as revealed in microstructural sections of joined metals, which is melted during welding. 它是焊接过程中熔化的连接金属的微观结构截面所显示的表面以下的深度。 |
| Tare weight (Unit N) | 皮重（单位N） |
The weight of an empty container. 空容器的重量。 |
| Taper key | 楔键 |
A key with parallel sides but tapering cross section along its length. 边平行但横截面沿其长度逐渐变细的键。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Magnetic test | 磁性测试 |
Method used to test heat extraction rates of various quenchants. The test works by utilizing the change in magnetic properties of metals at their Curie point–the temperature above which metals lose their magnetism. 用于测试各种淬火剂的热提取率的方法。该测试通过利用金属在居里点（即金属失去磁性的温度）的磁性变化来进行。 |
| Scratch hardness test | 划痕硬度测试 |
A form of hardness test in which a sharp-pointed stylus or corner of a mineral specimen is traversed along a surface so as to determine the resistance of that surface to cutting or abrasion. 硬度测试的一种形式，用尖头笔或矿物样品的一角沿一个表面移动，以确定该表面的抗切割或耐磨性。 |
| Decalescence | 退色 |
A phenomenon, associated with the transformation of alpha iron to gamma iron on the heating (superheating) of iron or steel, revealed by the darkening of the metal surface owing to the sudden decrease in temperature caused by the fast absorption of the latent heat of transformation. 一种现象，与铁或钢加热（过热）时α铁向γ铁的转变有关，由于转变潜热的快速吸收导致温度突然降低，金属表面变黑。 |
| Crossed threads | 交叉螺纹 |
When the axis of a nut offered up to a bolt is not aligned with the axis of a bolt (or a screw to a threaded member), it may be possible for the threads to engage incorrectly and even for the nut or screw to advance a turn or more, but ultimately the misaligned threads become locked together. Forcing the nut in such circumstances may irretrievably damage the threads on both. 当提供给螺栓的螺母的轴线与螺栓（或螺纹构件的螺钉）的轴线不对齐时，螺纹可能会错误接合，甚至螺母或螺钉会提前一圈或更多，但最终未对齐的螺纹会锁定在一起。在这种情况下强行拧入螺母可能会对两侧的螺纹造成无法修复的损坏。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Form of thread | 螺纹形式 |
The profile of a thread in an axial plane for a length of one pitch. 一个螺距长度的螺纹在轴向平面中的轮廓。 |
| Circlip | 卡簧 |
(snap ring) An external or internal retaining ring that locates parts of circular cross section in an axial direction. It consists of an incomplete ring, with holes on either side of the gap, that may be expanded by a plier-like tool to pass into a groove in a shaft or contracted to pass into a groove in a bore. （卡环）在轴向定位圆形横截面部分的外部或内部保持环。它由一个不完整的环组成，在间隙的任一侧都有孔，可以通过钳形工具将其扩展以进入轴中的凹槽或收缩以进入孔中的凹槽。 |
| Kilocalorie | 千卡 |
(Cal, kg-cal, kilogram-calorie, large calorie) An obsolete (i.e. non-SI) unit of energy equal to 1 000 cal. （卡，千克卡，千克卡路里，大卡路里）一种已被淘汰的（即非国际单位制）能量单位，等于1000卡。 |
| Transfer moulding | 转移模塑 |
(resin-transfer moulding, RTM) A method of compression moulding polymers in which the dies are closed before the operation starts. （树脂传递模塑，RTM）一种对聚合物进行压缩模塑的方法，其中模具在操作开始前关闭。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Load ratio, R | 负载比R |
In fatigue, the algebraic ratio of the minimum to maximum load in a fatigue cycle, that is, R = Pmin/Pmax. Also known as stress ratio. 在疲劳中，疲劳循环中最小载荷与最大载荷的代数比，即 R= Pmin/Pmax。也称为应力比。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Acoustic power | 声功率 |
(sound power) (Unit W) The rate of flow of acoustic energy across a specified surface. （声功率）（单位W）声能流过指定表面的速率。 |
| Progressive aging | 渐进时效 |
Aging by increasing the temperature in steps or continuously during the aging cycle. 通过在时效周期中逐步或连续升高温度进行增加时效。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Tera (T) | 特拉（T） |
An SI unit prefix indicating a multiplier of 1012; thus terawatt (TW) is a unit of power equal to one trillion watts. 指示乘数1012的SI单位前缀；因此，太瓦（TW）是等于1万亿瓦的功率单位。 |
| Diffusion coefficient | 扩散系数 |
A factor of proportionality representing the amount of substance diffusing across a unit area through a unit concentration gradient in unit time. 一个比例因子，表示在单位时间内通过单位浓度梯度扩散到单位面积上的物质量。 |
| Vapour | 蒸气 |
The gas-like phase of a substance at a temperature below its critical point. A vapour can be condensed to a liquid or a solid by increasing its pressure or reducing its temperature. 温度低于临界点的物质的类气相。蒸汽可以通过增加压力或降低温度冷凝成液体或固体。 |
| Tribology | 摩擦学 |
The science and technology concerned with interacting surfaces in relative motion. 与相对运动中相互作用的表面有关的科学和技术。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Brine quenching | 盐水淬火 |
A quench in which brine (salt water-chlorides, carbonates, and cyanides) is the quenching medium. The salt addition improves the efficiency of water at the vapor phase or hot stage of the quenching process. 一种淬火，其中盐水（盐水-氯化物、碳酸盐和氰化物）是淬火介质。添加盐提高了水在淬火过程的气相或热阶段的效率。 |
| Cooling curve | 冷却曲线 |
A curve showing the relation between time and temperature during the cooling of a material. 显示材料冷却过程中时间和温度之间关系的曲线。 |
| Fracture toughness | 断裂韧性 |
A generic term for measures of resistance to extension of a crack. The term is sometimes restricted to results of fracture mechanics tests, which are directly applicable in fracture control. However, the term commonly includes results from simple tests of notched or precracked specimens not based on fracture mechanics analysis. Results from tests of the latter type are often useful for fracture control, based on either service experience or empirical correlations with fracture mechanics tests. 裂纹扩展阻力测量的通用术语。该术语有时仅限于断裂力学试验的结果，这些结果直接适用于断裂控制。该术语通常包括非基于断裂力学分析的切口或预裂纹试样的简单试验结果。基于使用经验或与断裂力学试验的经验相关性，后一类试验的结果通常有助于断裂控制。 |
| Cementation | 胶结 |
The introduction of one or more elements into the outer portion of a metal object by means of diffusion at high temperature. 在高温下通过扩散将一种或多种元素引入金属物体的外部。 |
| Chafing fatigue | 磨损疲劳 |
Fatigue damage initiated in a surface damaged by rubbing against another body. 因与另一个物体摩擦而损坏的表面引起的疲劳损坏。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Structural-integrity analysis | 结构完整性分析 |
Assessment of components and structures for likelihood of failure by buckling, fracture, yielding, etc. under conditions of normal and accident loading. 在正常和事故荷载条件下，评估部件和结构因屈曲、断裂、屈服等而失效的可能性。 |
| Effective discharge area (Unit m²) | 有效排放面积（单位m²） |
A nominal area for flow through a pressure relief valve used to determine the valve’s flow capacity given the pressure difference across it, the fluid density and correction factors to allow for compressibility, the back pressure and the coefficient of discharge. 流经泄压阀的标称面积，用于确定阀门的流量，给定压力差、流体密度和允许可压缩性的校正因子、背压和排放系数。 |
| Nut thickness | 螺母厚度 |
The nut thickness shall be the overall distance measured parallel to the axis of nut, from the top of the nut to the bearing surface, and shall include the thickness of the washer face where provided. 螺母厚度应为平行于螺母轴线测量的从螺母顶部到轴承表面的总距离，还应包括垫圈表面的厚度。 |
| Shear strain rate(Unit 1/s) | 剪切应变率（单位1/s） |
In the deformation of solids, the rate at which shear strain is applied in a test or changes with time in a loaded component or structure. 在固体变形中，在试验中施加剪切应变的速率，或在加载部件或结构中随时间变化的速率。 |
| Centre of pressure | 压力中心 |
1. The location, on an aerofoil or other body that develops lift, of the resultant lift force. 2. The location, on a surface submerged in a liquid, of the resultant force due to the pressure acting on the surface. Because hydrostatic pressure increases with depth, the centre of pressure is generally below the centroid of the surface. 1.在产生升力的机翼或其他物体上，合成升力的位置。2.在浸没在液体中的表面上，由于作用在表面上的压力而产生的合力的位置。由于静水压力随深度增加，压力中心通常低于表面质心。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Activation energy | 活化能 |
(Ea, U) (Unit kJ/mol) The minimum energy for a chemical reaction to occur or for processes such as diffusion to take place in crystals. （Ea, U）（单位kJ/mol）发生化学反应或在晶体中发生扩散等过程的最小能量。 |
| Strain-age embrittlement | 应变时效脆化 |
A loss in ductility accompanied by an increase in hardness and strength that occurs when low-carbon steel (especially rimmed or capped steel) is aged following plastic deformation. The degree of embrittlement is a function of aging time and temperature, occurring in a matter of minutes at about 200°C (400 °F), but requiring a few hours to a year at room temperature. 塑性变形后低碳钢（尤其是边缘钢或封顶钢）时效时发生的延展性损失，伴随着硬度和强度的增加。脆化程度是老化时间和温度的函数，在大约200°C（400°F）的温度下，在几分钟内发生，但在室温下需要几小时到一年。 |
| Bulk velocity | 体积速度 |
(average velocity, V) (Unit m/s) For fluid flow in a pipe or duct, the average flow velocity, given by V = ṁ/ρA where ṁ is the mass flow rate, ρ is the fluid density, and A is the duct cross-sectional area. （平均速度，V）（单位m/s）对于管道或管道中的流体流动，平均流速，由V=ṁ/ρA给出，其中ṁ是质量流量，ρ是流体密度，A是管道截面积。 |
| Diagonal pitch (Unit m) | 对角线间距（单位米） |
The distance, when components in an assembly are staggered, between the position of a component in one row or column and the position of the corresponding component in the next row or column. The term is applied to rivets, turbine or compressor blades in a cascade, vortex generators on the surface of a wing, etc. 当部件中的零部件交错时，一行或一列中零部件的位置与下一行或下一列中相应零部件的位置之间的距离。该术语适用于铆钉、叶栅中的涡轮或压缩机叶片、机翼表面的涡流发生器等。 |
| Thermal electromotive force | 热电动势 |
The electromotive force generated in a circuit containing two dissimilar metals when one junction is at a temperature different from that of the other. 当一个结处于不同于另一个结的温度时，在含有两种不同金属的电路中产生的电动势。 |
| Endurance | 耐力 |
The capacity of a material to withstand repeated application of stress. 材料承受反复施加应力的能力。 |
| Median fatigue life | 中位疲劳寿命 |
The middle value when all of the observed fatigue life values of the individual specimens in a group tested under identical conditions are arranged in order of magnitude. When an even number of specimens are tested, the average of the two middlemost values is used. Use of the sample median rather than the arithmetic mean (that is, the average) is usually preferred. 当在相同条件下测试的一组中单个试样的所有观察疲劳寿命值按数量级排列时的中间值。当测试偶数个试样时，使用两个中间值的平均值。通常优选使用样本中值而不是算术平均值（即平均值）。 |
| Collapse load (Unit N) | 毁坏荷载（单位N） |
The applied load at which a structure becomes a mechanism owing to the formation of sufficient plastic hinges for collapse to occur. 由于形成足够的塑性铰链以发生坍塌，结构成为机制的施加载荷。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Equation, long form | 方程，长格式 |
An equation which relates the torque applied to a bolt to the preload created in it, and involves fastener geometry and the coefficient of friction between mating surfaces. A theoretical equation based on rigid body mechanics and the assumption that the geometry of the fastener is perfectly described by blueprint dimensions. 将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来的方程，该方程涉及紧固件几何形状和配合面之间的摩擦系数。基于刚体力学和紧固件几何结构由蓝图尺寸完美描述的假设的理论方程。 |
| Air conditioning | 空调 |
The process of controlling the temperature and humidity in rooms, buildings, aircraft, passenger vehicles, etc. More generally it includes control of dust, levels of radiant heat, etc. 控制房间、建筑物、飞机、客运车辆等的温度和湿度的过程。更一般地说，它包括控制灰尘、辐射热水平等。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Threshold stress for stress-corrosion cracking (σth) | 应力腐蚀开裂阈值应力（σth） |
An experimentally determined critical gross-section stress below which stress-corrosion cracking will not occur under specified test conditions. 实验确定的临界总截面应力，低于该应力，在规定的试验条件下不会发生应力腐蚀开裂。 |
| Mode of failure | 故障模式 |
The various ways in which a material can fail when subjected to loading, surface damage, chemical attack, heating, cooling, or radiation, in either isolation or combination. The failure modes include fracture, fatigue, creep, corrosion, erosion, and embrittlement. 材料在受到载荷、表面损伤、化学侵蚀、加热、冷却或辐射时，可能发生失效的各种方式，无论是单独还是组合。失效模式包括断裂、疲劳、蠕变、腐蚀、侵蚀和脆化。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Crack-extension resistance (KR) | 抗裂扩展性（KR） |
A measure of the resistance of a material to crack extension, expressed in terms of the stress-intensity factor, the crack-extension force, or values of Jderived using the J-integral concept. 材料对裂纹扩展的抵抗力的量度，以应力强度因子、裂纹扩展力或使用J积分概念导出的J值表示。 |
| Profiling machine | 仿形机 |
(profile milling machine) A milling machine in which the cutter is guided by the contour of a pattern having the required shape. （仿形铣床）铣刀由具有所需形状的图案轮廓引导的铣床。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Joint diagrams | 接合处关系图 |
Mathematical diagrams which illustrate the forces on and deflections of fasteners and joint members. 说明紧固件和连接件上的力和变形的数学图。 |
| Wheel | 轮 |
A solid disc, or a circular ring with spokes radiating from a central hub, either attached to an axle around which it revolves or which revolves with a rotating axle. 一个实心圆盘，或一个带有辐条的圆环，辐条从一个中心毂放射出来，或附在一个绕其旋转的轴上，或与一个旋转轴一起旋转。 |
| Fatigue limit | 疲劳极限 |
The maximum stress that presumably leads to fatigue fracture in a specified number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. Compare with endurance limit. 在指定数量的应力循环中可能导致疲劳断裂的最大应力。还应说明最大应力值和应力比。与耐力极限比较。 |
| Free joint | 万向节 |
The joint on a robot arm and wrist that causes the greatest end-effector movement when a specified force is applied to the end effector, i.e. that has the lowest stiffness with regard to the force. 机器人手臂和手腕上的关节，当指定的力施加到末端执行器时，会导致末端执行器的最大运动，即相对于力具有最低刚度。 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Angle of friction | 摩擦角 |
(friction angle, β) (Unit °) For a body in contact with a plane surface, the angle between the normal to the surface and the resultant force between the body and the surface. If the friction force is F and normal force is N, β is given by F/N = μ = tan β where μ is the coefficient of friction. （摩擦角，β）（单位°）对于与平面接触的物体，表面法线与物体与表面之间的合力之间的夹角。如果摩擦力为F，法向力为N，则β由F/N=μ=tanβ给出，其中μ是摩擦系数。 |
| Set screw | 紧定螺钉（平头螺钉、紧定螺栓） |
Usually a hardened steel screw having either no head or a square head and with various degrees of points or ends to lock or tighten adjustable machine parts in position on a shaft. A short, headless screw with a recess at one end to receive a screwdriver or key, the other end being pointed, square, or otherwise shaped. Typically used to secure a pulley, gear, or other component on a shaft. 通常是一种硬化钢螺钉，无头或方头，具有不同程度的点或端部，用于将可调机械部件锁定或拧紧在轴上的适当位置。一端有凹槽，用来装螺丝刀或钥匙，另一端是尖的、方形的或其他形状的。通常用于将皮带轮、齿轮或其他部件固定在轴上。 |
| Torque motor | 力矩电机 |
A type of induction motor that can apply a steady torque even when prevented from rotating. 一种感应电动机，即使被阻止旋转也能施加稳定的转矩。 |
| Clearance fit | 间隙配合 |
A range of clearances ranging from close sliding to loose running, i.e. a fit in which the limits for the mating parts always permit assembly. 从紧密滑动到松动运行的一系列间隙，即配合零件的限制始终允许组装的配合。 |
| Decompression chamber | 减压舱 |
A chamber in which ambient-air pressure can be increased to levels found in deep-sea diving. It is used to gradually acclimatize divers back to normal conditions and avoid ‘the bends’. 环境气压可以提高到深海潜水水平的腔室。它用于逐渐使潜水员适应正常条件，避免“弯曲”。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Gauge | 测量 |
1. Any instrument for measuring or checking dimensions, including adjustable gauges such as a micrometer and non-adjustable gauges such as go/no-go limit gauges that indicate the maximum and minimum dimensions allowable in a component during manufacture. 2. A term often used to mean an instrument, e.g. pressure gauge. 3. The diameter of a wire or thickness of a sheet according to a standard. 4. The distance between the rails of a railway track. 1. 任何用于测量或检查尺寸的仪器，包括可调节量规（例如千分尺）和不可调节量规（例如指示制造过程中组件允许的最大和最小尺寸的通过/不通过限制量规）。2. 常用于表示仪器的术语，例如压力表。3.根据标准的线材直径或片材厚度。4.铁路轨道的钢轨之间的距离。 |
| Shear lip | 剪切唇 |
A narrow, slanting ridge along the edge of a fracture surface. The term sometimes also denotes a narrow, often crescent-shaped, fibrous region at the edge of a fracture that is otherwise of the cleavage type, even though this fibrous region is in the same plane as the rest of the fracture surface. 沿断裂面边缘的狭窄倾斜脊。该术语有时还表示断裂边缘处的狭窄、通常为新月形的纤维区域，否则为解理型，即使该纤维区域与断裂表面的其余部分位于同一平面内。 |
| Screw pair | 螺旋副 |
Two links connected together to form a kinematic pair, in which the contacting surfaces are screw threads, so that their relative motion consists of rotation and sliding. 两个连杆连接在一起形成运动副，其中接触面为螺纹，因此它们的相对运动包括旋转和滑动。 |
| Transverse direction | 横向 |
Literally, the “across” direction, usually signifying a direction or plane perpendicular to the direction of working. In rolled plate or sheet, the direction across the width is often called long transverse, and the direction through the thickness, short transverse. 从字面上看，“横穿”方向，通常表示与工作方向垂直的方向或平面。在轧制钢板或薄板中，横跨宽度的方向通常称为长横向，穿过厚度的方向称为短横向。 |
| Latent heat | 潜热 |
Thermal energy absorbed or released when a substance undergoes a phase change. 物质发生相变时吸收或释放的热能。 |
| Conditioning heat treatment | 调质热处理 |
A preliminary heat treatment used to prepare a material for desired reaction to a subsequent heat treatment. For the term to be meaningful, the exact heat treatment must be specified. 用于制备材料的初步热处理，以便对随后的热处理进行所需的反应。为了使该术语有意义，必须指定确切的热处理。 |
| Design pressure (Unit Pa) | 设计压力（单位Pa） |
The greatest pressure that a closed container is expected to experience under normal operating conditions. 密闭容器在正常操作条件下预期承受的最大压力。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Structure | 结构体 |
An assembly, usually load bearing, of connected (pinned, riveted, screwed, bolted, welded, etc.) components, such as bars, tubes, beams, and plates. 由连接（销接、铆接、螺纹连接、螺栓连接、焊接等）部件组成的组件，通常为承重组件，如杆、管、梁和板。 |
| Fastener with reduced shank | 短柄紧固件 |
Finished fastener with a shank diameter of ds ≈ d2. 柄径为ds≈d2的紧固件。 |
| Nominal power (Unit kW) | 公称功率（单位kW） |
1. For an internal combustion engine, the average power output of a typical production engine under normal working conditions measured according to SAE standard J 1349/ISO 1585. 2. For an electric motor, the rated equivalent mechanical power output. 1.对于内燃机，根据SAE标准J 1349/ISO 1585测量的正常工作条件下典型生产发动机的平均功率输出。2.对于电动机，额定等效机械功率输出。 |
| Heat-capacity rate (c) (Unit W/K) | 热容率（c）（单位W/K） |
For fluid flow in a duct with mass flow rate ṁ, the product ṁC where C is the specific-heat capacity, at constant pressure (CP) in the case of a gas. 对于质量流量为ṁ的管道中的流体流动，乘积ṁC其中C是比热容，在气体的情况下为恒定压力（CP）。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Closed system | 封闭系统 |
A closed thermodynamic system consists of a fixed amount of mass. No mass can cross its boundary although energy can, in the form of work or heat, and its volume can change. 一个封闭的热力学系统由一定量的质量组成。能量可以以功或热的形式存在，其体积可以改变，但没有质量可以越过它的边界。 |
| Alternating stress | 交替应力 |
(Unit Pa) Originally, stresses of changing sign (tension-tocompression-to-tension, etc.) in a component produced by alternating forces acting in opposite directions, but now generally used to describe stresses that vary but may keep the same sign, as produced by periodic, out-of–balance, or vibrational loads. （单位Pa）最初，构件中由相反方向的交变力产生的符号变化的应力（张力到压缩到张力等），但现在通常用于描述变化但可能保持相同符号的应力，如由周期性、失衡或振动载荷产生的应力。 |
| Two-stroke engine | 二冲程发动机 |
(two-cycle engine) A petrol or diesel engine in which an air/fuel charge is introduced through an induction port, compressed and burned, expanded and then exhausted through an exhaust port. The two ports in the cylinder wall are opened and closed by the piston. There are two strokes in each revolution of the crankshaft. In total-loss lubrication petrol engines, the lubricating oil is mixed with the fuel. （双循环发动机）一种汽油或柴油发动机，其中空气/燃料通过进气口引入，压缩和燃烧，膨胀，然后通过排气口排出。气缸壁上的两个口由活塞打开和关闭。曲轴每转一圈有两个冲程。在全失润滑汽油发动机中，润滑油与燃油混合。 |
| Graphitic carbon | 石墨碳 |
Free carbon in steel or cast iron. 钢或铸铁中的游离碳。 |
| SI system | SI国际单位制 |
SI is an abbreviation of Système International d’Unités, i.e., the international unit measurement system – an internationally established system of measurement units built on older metric systems. SI是Système International d‘Unités的缩写，即国际单位计量系统——一种基于旧公制的国际公认计量单位系统。 |
| Malleable cast iron | 可锻铸铁 |
A cast iron made by prolonged annealing of white cast iron in which decarburization or graphitization, or both, take place to eliminate some or all of the cementite. The graphite is in the form of temper carbon. If decarburization is the predominant reaction, the product will exhibit a light fracture surface, hence, “whiteheart malleable;” otherwise, the fracture surface will be dark, hence, “blackheart malleable.” Ferritic malleable has a predominantly ferritic matrix; pearlitic malleable may contain pearlitic, spheroidite or tempered martensite depending on heat treatment and desired hardness. 白口铸铁一种通过长时间退火制成的铸铁，脱碳，石墨化，或两者都发生，以消除部分或全部渗碳体。石墨是回火碳的形式。如果脱碳是主要反应，产品将呈现出较轻的断裂表面，“白心可锻”。否则，断裂表面将变暗，“黑心可锻”。铁素体可锻性材料主要为铁素体基体；根据热处理和所需硬度，珠光体可锻材料可能包含珠光体、球状体或回火马氏体。 |
| Crack length (depth) (a) | 裂纹长度（深度）（a） |
In fatigue and stress corrosion cracking, the physical crack size used to determine the crack growth rate and the stress-intensity factor. For the compact-type specimen, crack length is measured from the line connecting the bearing points of load application. For the center-cracked-tension specimen, crack length is measured from the perpendicular bisector of the central crack. 在疲劳和应力腐蚀裂纹中，用于确定裂纹扩展速率和应力强度因子的物理裂纹尺寸。对于紧凑型试样，裂纹长度从连接载荷施加点的线开始测量。对于中心裂纹拉伸试样，从中心裂纹的垂直平分线测量裂纹长度。 |
| Tightness | 紧密度 |
A measure of the mass leak rate from a gasketed joint. 垫圈接头质量泄漏率的测量值。 |
| Gasket m-factor | 垫片m系数 |
For a gasketed joint of area A in which the clamping force is F, the factor m is defined by F ≥ mpA where p is the pressure that would separate the two halves of the joint and m > 1. 对于面积为A且夹紧力为F的垫片接头，系数m由F≥mpA定义，其中p是分离接头两半的压力，m>1。 |
| Carbon potential | 碳势 |
A measure of the ability of an environment containing active carbon to alter or maintain, under prescribed conditions, the carbon level of the steel. Note: In any particular environment, the carbon level attained will depend on such factors as temperature, time, and steel composition. 衡量含有活性碳的环境在规定条件下改变或保持钢的碳含量的能力。注意：在任何特定环境中，所达到的碳含量将取决于温度、时间和钢成分等因素。 |
| Erosion | 侵蚀 |
Progressive loss of original material from a solid surface due to mechanical interaction between that surface and a fluid, a multicomponent fluid, or impinging liquid or solid particles. 由于固体表面与流体、多组分流体或撞击液体或固体颗粒之间的机械相互作用，原始材料从固体表面逐渐损失。 |
| Mean diameter (Unit m) | 平均直径（单位米） |
The average of the inside and outside diameters for a helical spring or hollow circular cylinder or sphere 螺旋弹簧或空心圆柱体或球体的内径和外径的平均值 |
| Work ratio | 工作比 |
The ratio of the net work out to the actual work out for a thermodynamic cycle. 热力学循环的净功与实际功之比。 |
| Bond strength (Unit Pa) | 结合强度（单位Pa） |
The tensile, compressive or shear stress at which joints fail, e.g. by fracture or excessive deformation. 接头失效的拉伸、压缩或剪切应力，例如断裂或过度变形。 |
| Overheating | 过热 |
Heating a metal or alloy to such a high temperature that its properties are impaired. When the original properties cannot be restored by further heat treating, by mechanical working, or by a combination of working and heat treating, the overheating is known as burning. 将金属或合金加热至其性能受损的高温。当通过进一步热处理、机械加工或加工与热处理的组合无法恢复原始性能时，过热称为燃烧。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Residual strength (Unit N) | 剩余强度（单位：N） |
The strength of a damaged body containing defects induced by microcracking, thermal shock, etc. 包含由微裂纹、热冲击等引起的缺陷的受损体的强度。 |
| Pitch (Unit m) | 间距（单位：m） |
1. In a cascade of identical turbine or compressor blades, the distance between successive blades measured parallel to the leading edges. 2. For a screw thread, the distance between adjacent thread forms measured parallel to the thread axis. 3. For an aircraft, the vertical relationship between the nose and the horizon. The pitch axis is an axis in the plane of the wings of an aircraft, perpendicular to the centreline, about which the aircraft rotates. Pitch motion is the corresponding up or down movement of the aircraft nose. Pitch attitude is the angle between the centreline of an aircraft and the horizontal. The angle is positive when the nose is above its position when the centreline is horizontal. 1.在相同涡轮或压缩机叶片的叶栅中，平行于前缘测量的连续叶片之间的距离。2.对于螺纹，平行于螺纹轴线测量的相邻螺纹形状之间的距离。3.对于飞机，机头和水平线之间的垂直关系。俯仰轴是飞机机翼平面内垂直于中心线的轴，飞机绕中心线旋转。俯仰运动是飞机机头的相应向上或向下运动。俯仰姿态是飞机中心线与水平线之间的角度。当中心线水平时，当机头高于其位置时，角度为正。 |
| Corrosion | 腐蚀 |
The deterioration of an exposed metal surface due to electrochemical oxidation with its surroundings. In the oxidation reaction, metal atoms give up electrons which are transferred to form another chemical species by a reduction reaction, usually with hydrogen and/or oxygen. A common example is the formation of the iron oxide rust Fe(OH)3 on iron or steel in moist air or water. Rust breaks away easily, exposing fresh iron to the atmosphere, whereas the corrosion product of some metals forms an adherent layer that prevents further oxidation reaction at fresh metal, an effect known as passivation. Examples include aluminium oxide on aluminium, chromium oxide on chromium, chromium oxide on alloys containing chromium such as stainless steels, and the patina formed on copper and zinc. Corrosion protection takes many forms. Good design to avoid crevices and stress is important. In some situations, substances known as inhibitors may be added to the environment to decrease its corrosiveness. The electrochemical nature of corrosion results in some metals having a greater tendency for oxidation than others. Zinc has a stronger tendency than iron and this is made use of in galvanizing. This is one example of cathodic protection, in which one metal is connected electrically to a more reactive metal, called a sacrificial anode, that oxidizes by giving up electrons and so protects the first metal. Coatings may be used to resist corrosion. Paints, plating, and diffusion coatings are the most common and the electrochemical process of anodizing is used to deliberately form a passive layer of oxide on aluminium alloys. Material selection plays a major role. For example, stainless steels with their high chromium content are widely used in corrosive environments. 暴露的金属表面由于与周围环境的电化学氧化而劣化。在氧化反应中，金属原子放弃电子，这些电子通过还原反应（通常与氢和/或氧）转移形成另一种化学物质。一个常见的例子是在潮湿的空气或水中在铁或钢上形成氧化铁锈Fe(OH)3。铁锈很容易脱落，将新鲜铁暴露在大气中，而一些金属的腐蚀产物形成一层粘附层，防止新鲜金属发生进一步的氧化反应，这种效果称为钝化。实例包括铝上的氧化铝、铬上的氧化铬、含铬合金上的氧化铬如不锈钢，以及铜和锌上形成的铜绿。腐蚀防护有多种形式。避免裂缝和应力的良好设计非常重要。在某些情况下，可以向环境中添加称为抑制剂的物质，以降低其腐蚀性。腐蚀的电化学性质导致一些金属比其他金属具有更大的氧化倾向。锌比铁具有更强的倾向性，这可用于镀锌。这是阴极保护的一个例子，其中一种金属与活性更强的金属（称为牺牲阳极）电连接，牺牲阳极通过释放电子进行氧化，从而保护第一种金属。涂层可用于抗腐蚀。油漆、电镀和扩散涂层是最常见的，阳极氧化的电化学过程用于有意在铝合金上形成一层钝化氧化物。材料选择起着重要作用。例如，铬含量高的不锈钢广泛用于腐蚀性环境。 |
| Vibrograph | 示振器 |
An instrument that records vibrations in a system over time. 记录系统随时间变化的振动的仪器。 |
| Biomechanics | 生物力学 |
The application of mechanical-engineering principles, including thermodynamics, fluid mechanics, and solid mechanics together with materials engineering, to biological systems. 机械工程原理（包括热力学、流体力学和固体力学以及材料工程）在生物系统中的应用。 |
| Aging treatment | 时效处理 |
Heat treatment aimed at age hardening; it comprises solution and precipitation treatments. 针对时效硬化的热处理；它包括溶液和沉淀处理。 |
| Curie temperature | 居里温度 |
The temperature of magnetic transformation below which a metal or alloy is ferromagnetic and above which it is paramagnetic. 磁性转变温度，低于此温度金属或合金为铁磁性，高于此温度则为顺磁性。 |
| Slip | 滑落 |
Plastic deformation by the irreversible shear displacement (translation)of one part of a crystal relative to another in a definite crystallographic direction and usually on a specific crystallographic plane. Sometimes called glide. 晶体的一部分在一定的晶体学方向上相对于另一部分的不可逆剪切位移（平移）引起的塑性变形，通常在特定的晶体主义平面上。有时被称为滑翔。 |
| Sample median | 样本中间值 |
The middle value when all observed values in a sample are arranged in order of magnitude. If an even number of samples are tested, the average of the two middlemost values is used. It is a point estimate of the population median, or 50% point. 当样本中的所有观测值按数量级排列时的中间值。如果测试的样本数为偶数，则使用两个中间值的平均值。这是人口中位数的一个点估计值，或50%的点。 |
| Conduit | 导管 |
A hollow object, of metal, plastic, glass, ceramic, etc., which is relatively long compared with its lateral dimensions and through which there is fluid flow. 由金属、塑料、玻璃、陶瓷等制成的中空物体，与其横向尺寸相比相对较长，并且有流体流过。 |
| Constant life diagram | 恒定寿命图 |
A plot of experimentally derived fatigue-life data; perhaps the most complex and complete of the popular charts used to represent such data. 实验得出的疲劳寿命数据图；可能是用于表示此类数据的最复杂和最完整的流行图表。 |
| Catastrophic failure | 灾难性故障 |
A sudden and total failure of a large engineering structure such as an aeroengine, aircraft, space vehicle, bridge, or dam. 大型工程结构（如航空发动机、飞机、航天器、桥梁或水坝）突然完全失效。 |
| Hot working | 热加工 |
Plastic deformation of a metal, by rolling, drawing, forging, etc., at a temperature above its recrystallization temperature (in commercial alloys above about 40% of their melting points in kelvins) which results in permanent shape change but no increase in strength or loss of ductility. 金属通过轧制、拉拔、锻造等在高于其再结晶温度（在商业合金中高于其熔点的40%的开尔文）的温度下发生塑性变形，导致永久的形状变化，但不会增加强度或失去延展性。 |
| Vibration | 振动 |
1. A periodic change with time of the displacements of elements making up a component or structure. 2. The study of the oscillatory motion of bodies and systems and the frequencies, amplitudes, and forces associated with them. 1.组成部件或结构的元件位移随时间的周期性变化。2.研究物体和系统的振荡运动以及与之相关的频率、振幅和力的学科。 |
| Ausforming | 形变热处理 |
Thermomechanical treatment of steel in the metastable austenitic condition below the recrystallization temperature followed by quenching to obtain martensite and/or bainite. 在低于再结晶温度的亚稳态奥氏体条件下对钢进行热机械处理，然后淬火以获得马氏体和/或贝氏体。 |
| Pin expansion test | 插头膨胀试验 |
A test for determining the ability of a tube to be expanded or for revealing the presence of cracks or other longitudinal weaknesses in it, made by forcing a tapered pin into the open end of the tube, similar to flare test. 通过将锥形销压入管道开口端来确定管道膨胀能力或揭示其存在裂纹或其他纵向缺陷的试验，类似于扩口试验。 |
| Tensile test (tension test) | 拉伸试验（拉力试验） |
A test in which a precisely-machined tensile specimen (tensile testpiece), typically circular or rectangular in cross section with large end sections that are gripped in the testing machine, is subjected to an increasing tensile load, usually to the point of fracture, to produce a stress–strain curve from which such material properties as modulus of elasticity, limit of proportionality, proof stress, yield point, and ultimate tensile stress can be determined. The relevant standard is ISO 6892-1. 一种试验，在这种试验中，精密加工的拉伸试样（拉伸试件）的横截面通常为圆形或矩形，具有在试验机中夹紧的大端部，受到越来越大的拉伸载荷，通常达到断裂点，以产生应力-应变曲线，从中可以看出弹性模量、比例极限等材料特性，可以确定验证应力、屈服点和极限拉伸应力。相关标准为ISO 6892-1。 |
| Computer-aided design (CAD) | 计算机辅助设计（CAD） |
Generally, design and calculations performed by computer; more specifically, the use of computer graphics and models to communicate design concepts. Computer-aided design and computer-aided manufacturing (CAD/CAM) is where component dimensions resulting from CAD are passed by electronic means directly to machines for manufacture. 一般由计算机进行设计和计算，更具体地说，使用计算机图形和模型来传达设计概念。计算机辅助设计和计算机辅助制造（CAD/CAM）是由CAD产生的组件尺寸通过电子方式直接传递到机器进行制造。 |
| Black oxide | 黑色氧化物 |
A black finish on a metal produced by immersing it in hot oxidizing salts or salt solutions. 通过将金属浸入热氧化盐或盐溶液中产生的黑色饰面。 |
| Critical compression ratio | 临界压缩比 |
1. The compression ratio for incipient knock of hydrocarbon fuels as determined in a variable-compression single-cylinder piston engine. 2. The compression ratio at which an air–fuel mixture will spontaneously ignite due to the temperature increase produced. 1.在可变压缩单缸活塞发动机中确定的烃类燃料初期爆震的压缩比。2.空气-燃料混合物由于产生的温度升高而自燃的压缩比。 |
| Hardness profile | 硬度分布 |
Hardness as a function of distance from a fixed reference point (usually from the surface). 硬度作为距固定参考点（通常距表面）的距离的函数。 |
| International Practical Temperature Scale (IPTS) | 国际实用温标（IPTS） |
A close approximation to the thermodynamic temperature scale based upon the triple points of hydrogen (13.8 K), neon (24.6 K), oxygen (54.4 K), argon (83.8 K), mercury (234.3 K), and water (273.2 K); the melting point of gallium (302.9 K); and the freezing points of indium (429.7 K), tin (505.1 K), zinc (692.7 K), aluminium (933.5 K), silver (1 234.9 K), gold (1 337.3 K), and copper (1 基于氢（13.8K）、氖（24.6K）、氧（54.4K）、氩（83.8K），汞（234.3K）和水（273.2K）的三相点的热力学温度标度的近似值；镓的熔点（302.9K）；铟（429.7K）、锡（505.1K）、锌（692.7K），铝（933.5K）、银（1234.9K）、金（1337.3K）和铜等。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Gear pump | 齿轮泵 |
A positive-displacement pump in which fluid is pumped by meshing gears, one driven and the other an idler gear, on parallel axes within a closed casing. 一种容积式泵，其中流体由啮合齿轮泵送，在封闭外壳内的平行轴上一个驱动，另一个为空套齿轮。 |
| Essential conditions | 必要条件 |
Each type of failure to which bolted joints are subject is set up by three or four conditions. The conditions vary, depending on the mode of failure, but never number more than four. Eliminating any one of the essential conditions for a particular type of failure can prevent that type of failure. 螺栓连接所遭受的每种类型的故障都由三个或四个条件确定。根据故障模式的不同，情况会有所不同，但数量不得超过四个。消除特定类型故障的任何一个基本条件都可以防止该类型故障。 |
| Thread grinding | 螺纹磨削 |
A method for producing or finishing very precise screw threads using a profiled grinding wheel. 一种使用异形砂轮生产或精加工非常精密螺纹的方法。 |