| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Modulus of resilience | 回弹系数 |
The amount of energy stored in a material when loaded to its elastic limit. It is determined by measuring the area under the stress-strain curve up to the elastic limit. 当加载到其弹性极限时，材料中储存的能量量。通过测量应力-应变曲线下直至弹性极限的面积来确定。 |
| Waste-heat recovery | 废热回收 |
The recovery of thermal energy from flue and exhaust gases, or from liquids heated in industrial processes. Recovery devices include pre-heaters, recuperators, regenerators, and waste-heat boilers. 从烟道和废气中或从工业过程中加热的液体中回收热能。回收装置包括预热器、回热器、再生器和余热锅炉。 |
| Checks | 检查 |
Numerous, very fine cracks in a coating or at the surface of a metal part. Checks may appear during processing or during service and are most often associated with thermal treatment or thermal cycling. 涂层中或金属零件表面的许多非常细微的裂纹。在加工或服务期间可能会出现检查，并且通常与热处理或热循环有关。 |
| Balance weight | 平衡器 |
A corrective mass used in the static or dynamic balancing of a rotating object. 用于旋转物体的静态或动态平衡的校正质量。 |
| Surface hardening | 表面硬化 |
A generic term covering several processes applicable to a suitable ferrous alloy that produces, by quench hardening only, a surface layer that is harder or more wear resistant than the core. There is no significant alteration of the chemical composition of the surface layer. The processes commonly used are carbonitriding, carburizing, induction hardening, flame hardening, nitriding, and nitrocarburizing. Use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于仅通过淬火硬化产生比型芯更硬或更耐磨的表面层的合适铁合金的几种工艺。表面层的化学成分没有显著改变。常用的工艺有碳氮共渗、渗碳、感应淬火、火焰淬火、氮化和氮碳共渗。最好使用适用的特定工艺名称。 |
| Centrifugal | 离心式 |
Acting or moving in a direction away from the axis of rotation of a rotating body. 沿远离旋转体的旋转轴的方向作用或移动。 |
| Clevis joint | U形接头 |
A joint formed by two parallel cantilever beams pressed upon a component between the beams. 由两个平行悬臂梁压在梁之间的部件上形成的接头。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Pressure control valve | 压力控制阀 |
A valve used to set the pressure level in a pressure vessel or piping system. 用于设置压力容器或管道系统中压力水平的阀门。 |
| Abelian group | 阿贝尔群 |
Property of a group of elements associated with a binary operation. In an Abelian group, the group elements commute under the binary operation. If a and b are any two group elements and if the (+) sign denotes the binary operation, then, for an Abelian group, 与二元运算相关的一组元素的属性。在阿贝尔群中，群元素在二元运算下交换。如果a和b是任意两个群元素并且（+）符号表示二元运算 |
| Tension, bolt | 螺栓张力 |
Tension (tensile stress) created in the bolt by assembly preloads and=or such things as thermal expansion, service loads, etc. 由组件预载和=或热膨胀、工作载荷等因素在螺栓中产生的张力（拉伸应力）。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Cap nut | 盖型螺母 |
A nut with a blind threaded hole, for example a dome nut to cover the end of a bolt. 带有盲螺纹孔的螺母，例如用于覆盖螺栓末端的圆顶螺母。 |
| Pitch (Unit m) | 间距（单位：m） |
1. In a cascade of identical turbine or compressor blades, the distance between successive blades measured parallel to the leading edges. 2. For a screw thread, the distance between adjacent thread forms measured parallel to the thread axis. 3. For an aircraft, the vertical relationship between the nose and the horizon. The pitch axis is an axis in the plane of the wings of an aircraft, perpendicular to the centreline, about which the aircraft rotates. Pitch motion is the corresponding up or down movement of the aircraft nose. Pitch attitude is the angle between the centreline of an aircraft and the horizontal. The angle is positive when the nose is above its position when the centreline is horizontal. 1.在相同涡轮或压缩机叶片的叶栅中，平行于前缘测量的连续叶片之间的距离。2.对于螺纹，平行于螺纹轴线测量的相邻螺纹形状之间的距离。3.对于飞机，机头和水平线之间的垂直关系。俯仰轴是飞机机翼平面内垂直于中心线的轴，飞机绕中心线旋转。俯仰运动是飞机机头的相应向上或向下运动。俯仰姿态是飞机中心线与水平线之间的角度。当中心线水平时，当机头高于其位置时，角度为正。 |
| Sigma phase | σ相 |
A hard, brittle, nonmagnetic intermediate phase with a tetragonal crystal structure, containing 30 atoms per unit cell, space group P42/mnm, occurring in many binary and ternary alloys of the transition elements. The composition of this phase in the various systems is not the same, and the phase usually exhibits a wide range in homogeneity. Alloying with a third transition element usually enlarges the field of homogeneity and extends it deep into the ternary section. 一种硬、脆、非磁性中间相，具有四方晶体结构，每单位晶胞含有30个原子，空间群P42/mnm，存在于许多过渡元素的二元和三元合金中。该相在各种系统中的组成不尽相同，并且该相通常表现出宽范围的均匀性。与第三过渡元素的合金化通常会扩大均匀性范围，并将其延伸到三元区。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| Hypereutectic alloy | 过共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of alloying element compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，任何合金，其组成与共晶组成相比具有过量的合金元素，并且其平衡微观结构包含一些共晶结构。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Hypoeutectic alloy | 亚共晶合金 |
In an alloy system exhibiting a eutectic, any alloy whose composition has an excess of base metal compared with the eutectic composition, and whose equilibrium microstructure contains some eutectic structure. 在呈现共晶的合金系统中，其成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Swift cup test | 斯威夫特杯测试 |
A simulative cupping test in which circular blanks of various diameters are clamped in a die ring and deep drawn into cups by a flat-bottomed cylindrical punch. 一种模拟拔杯试验，将不同直径的圆形坯料夹紧在模环中，并用平底圆柱冲头将其深拉入杯中。 |
| Bias pressure (Unit Pa) | 偏压（单位Pa） |
In a fluidic device controlled by pressure difference, the magnitude of that difference. 在由压力差控制的流体装置中，该差值的大小。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Oil hardening | 油回火 |
The formation of martensite before tempering by quenching suitable steels in oil at lower cooling rates than given by water quenching, thus reducing the likelihood of component fracture or severe residual stresses. Quench-hardening treatment involving cooling in oil. 通过在油中以低于水淬的冷却速率淬火合适的钢，在回火前形成马氏体，从而降低部件断裂或严重残余应力的可能性。是一种淬火硬化处理，包括在油中冷却。 |
| Die | 模具 |
1. A tool having an appropriately-shaped hole through which material may be extruded or drawn. 2. A tool employed in forging. 3. A block having the male or female shape employed in stamping operations. 4. A thick circular disc, driven by a die wrench, with internally-threaded cutting edges for producing a screw thread. A die wrench (die stock) holds a screw-cutting die and has two projecting arms for applying the torque necessary to cut the thread. A die having a hexagonal or square shape (die nut), driven by a spanner, is used in confined spaces where a die wrench cannot be rotated through a full circle. 1.一种具有适当形状的孔的工具，通过该孔可以挤压或拉伸材料。2.一种用于锻造的工具。3.一种用于冲压操作的具有阳或阴形状的块体。4.一种由模具扳手驱动的厚圆盘，具有用于产生螺纹的内螺纹切削刃。冲模扳手（冲模）装有一个螺旋切割模，并有两个突出臂，用于施加切割螺纹所需的扭矩。由扳手驱动的六边形或方形模具（模具螺母）用于模具扳手无法旋转一整圈的受限空间。 |
| Cone clutch | 锥形离合器 |
A friction clutch in which an internal cone moves axially in or out of engagement with an external cone. One or both surfaces is lined with high-friction material. 一种摩擦离合器，其中内锥与外锥轴向啮合或脱离啮合。一个或两个表面衬有高摩擦材料。 |
| Nominal power (Unit kW) | 公称功率（单位kW） |
1. For an internal combustion engine, the average power output of a typical production engine under normal working conditions measured according to SAE standard J 1349/ISO 1585. 2. For an electric motor, the rated equivalent mechanical power output. 1.对于内燃机，根据SAE标准J 1349/ISO 1585测量的正常工作条件下典型生产发动机的平均功率输出。2.对于电动机，额定等效机械功率输出。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Reverse engineering | 逆向工程 |
The disassembly of a machine, mechanism, system or device, measurement of its component parts, and identification of the materials used so that if required, a functioning replica can be produced. 拆卸机器、机构、系统或装置，测量其组成部分，并识别所用材料，以便在需要时可以生产出功能正常的复制品。 |
| Transmission dynamometer | 传动测功机 |
A dynamometer in which the power transmitted by a shaft is obtained from the product of its rotation speed and the torque determined from measured shear strains along the shaft. 一种测功机，其中轴传递的功率由其转速和扭矩的乘积获得，扭矩由沿轴测得的剪切应变确定。 |
| Hydrogen embrittlement | 氢脆 |
A condition of low toughness, low ductility or cracking in metals resulting from the absorption of hydrogen. A common and troublesome form of Stress cracking. Several theories have been proposed to explain hydrogen embrittlement, but, at present, the exact mechanism is still unknown. What is known, however, is the fact that if hydrogen is trapped in a bolt by poor electroplating practices, it can encourage stress cracking. Bolts can fail, suddenly and unexpectedly, under normal loads. Premature crack growth over time under tensile stress leading to unexpected failure in certain metals, caused by small amounts of hydrogen in the microstructure. Hydrogen may enter steels during melting or heat treating, or during processes such as electroplating. 因吸收氢而导致金属韧性低、延展性低或开裂的情况，是一种常见且麻烦的应力开裂形式。在拉伸应力下，裂纹随时间过早扩展，导致某些金属发生意外失效，这是由微观结构中的少量氢引起的。在熔化或热处理过程中，或在电镀等过程中，氢可能进入钢中。已经提出了几种理论来解释氢脆，但目前，确切的机理仍然未知。已知的事实是，如果氢因电镀不当而被困在螺栓中，则会导致应力开裂。在正常载荷下，螺栓可能突然意外失效。 |
| Proportional limit | 比例极限 |
The greatest stress a material is capable of developing without a deviation from straight-line proportionality between stress and strain. 材料能够产生的最大应力不偏离应力和应变之间的直线比例。 |
| Surface hardness | 表面硬度 |
(superficial hardness) Indentation hardness on, and for some distance below, the surface of a component, as opposed to its bulk hardness. Depending on the resolution required, micro- or nano-hardness testing machines are employed. （表面硬度）与整体硬度相反，部件表面及其下方一定距离的压痕硬度。根据所需的分辨率，可使用微型或纳米硬度测试机。 |
| Screw | 螺钉 |
Threaded fastener designed to be used in a tapped or untapped (e.g., wood screw) hole, but not with a nut. A fastener with a screw thread cut or rolled into its cylindrical or conical shank, intended either to cut its own thread (as in a wood screw) or engage in a threaded hole. A self-tapping screw (sheet-metal screw, tapping screw) has a sufficiently hard thread that it cuts an internal thread in thin sheet or a component made of soft material when driven into a hole in the sheet or component. The screw head is the part of a screw used to apply torque to the screw. Common screw-head designs are circular in cross section with a diametral slot or cross, or hexagonal and recessed with a cross or hexagon. A screw thread is one or more continuous helical grooves of uniform section along either the exterior surface (male thread) or the interior surface (female thread) of a cylindrical or conical body. The three-dimensional shape that results when the thread cross section is rotated and axially advanced along an axis is called a helicoid, the angle that the thread makes when projected on to the axis being called the angle of inclination. Threads are employed in fasteners such as bolts, nuts, and screws; location and measuring instruments; in power drives; in some electrical fittings (Edison thread); and on the ends of crankshafts to suppress oil leakage (thrower thread). Parallel threads are formed on cylinders; tapered threads on cones, typically with a taper rate of 1:16. A screw with a righthanded thread appears to move away from the observer when turned clockwise. All standard screws, bolts and nuts have right-hand threads, but left-handed threads are sometimes employed. The axial distance between corresponding points on adjacent threads is called the screw pitch or screw rate and, for a single continuous helical groove (a single-start thread), is the same as the change in axial distance (the lead) between a nut and the head of a bolt during one revolution, the number of thread forms per mm then being the reciprocal of the pitch. For the same screw diameter, coarse threads have fewer threads per mm than fine threads. A multiple-start screw thread (usually coarse, see later) consists of two or more identical threads running simultaneously along its axis so as to provide greater bearing area and greater velocity ratio. The starts are separated by 180° (double start), 120° (triple start), 90° (quadruple start) etc., depending upon the number of threads. Thus, in double-start threads, the lead is twice the pitch; and so on. The axial distance between corresponding points on two adjacent threads in a multiple start thread is called the divided pitch. The position on a screw thread where there is equal distance between the flanks on the solid part of the thread and in the space between the threads is the pitch point, the associated diameter of which is termed the pitch diameter. The basic nomenclature for threads, some of which is common with that for toothed gearing, is shown in the diagrams. A helix formed or cut on a cylindrical surface which may advance along the axis to the right or left. The helix may be single or multiple. 一种螺纹紧固件，设计用于攻丝或未攻丝（如木螺钉）孔，但不与螺母配合使用。其螺纹被切割或卷成圆柱形或锥形柄，用于切割自身螺纹（如木螺钉）或嵌入螺纹孔。自攻螺钉（钣金螺钉、自攻螺钉）具有足够硬的螺纹，当打入薄板或部件中的孔时，它会在薄板或软材料部件中切割内螺纹。螺钉头是螺钉的一部分，用于向螺钉施加扭矩。常见的螺钉头设计为横截面为圆形，带有直径槽或十字，或为六边形，并带有十字或六边形凹槽。螺纹是沿圆柱形或锥形体的外表面（外螺纹）或内表面（内螺纹）具有均匀截面的一个或多个连续螺旋槽。当螺纹横截面旋转并沿轴轴向前进时产生的三维形状称为螺旋面，螺纹投影到轴上时形成的角度称为倾角。螺纹用于紧固件，如螺栓、螺母和螺钉；定位和测量仪器；在动力驱动中；在一些电气配件中（爱迪生螺纹）；并安装在曲轴端部，以抑制漏油（抛掷器螺纹）。在圆柱体上形成平行螺纹；圆锥上的锥形螺纹，通常具有1:16的锥形率。当顺时针旋转时，具有右手螺纹的螺钉似乎会远离观察者。所有标准螺钉、螺栓和螺母都有右手螺纹，但有时使用左手螺纹。相邻螺纹上对应点之间的轴向距离称为螺距或螺纹率，对于单个连续螺旋槽（单个起始螺纹），与螺母和螺栓头之间的轴向间距（导程）在一周内的变化相同，每mm的螺纹形式数为螺距的倒数。对于相同的螺钉直径，粗螺纹的每毫米螺纹数少于细螺纹。多头螺纹（通常为粗螺纹，见下文）由两个或多个沿其轴线同时延伸的相同螺纹组成，以提供更大的承载面积和更大的速比。根据螺纹的数量，起点之间的间隔为180°（双起点）、120°（三起点）、90°（四起点）等。因此，在双起始螺纹中，导程是螺距的两倍；多起点螺纹中两个相邻螺纹上对应点之间的轴向距离称为分割螺距。螺纹上的位置，即螺纹实体部分的侧面和螺纹之间的空间之间的距离相等，即节点，其相关直径称为节径。图中显示了螺纹的基本术语，其中一些与齿轮传动的基本术语相同。在圆柱面上形成或切割的螺旋线，可沿轴线向右或向左前进。螺旋可以是单个或多个。 |
| Stress cycle | 应力循环 |
The smallest segment of the stress-time function that is repeated periodically. 周期性重复的应力时间函数的最小段。 |
| Kiln | 窑 |
An industrial oven for burning, baking, or drying. 用于燃烧、烘烤或干燥的工业烤箱。 |
| Vibrometer | 测振仪 |
A device used to measure the motion of a vibrating surface, typically using a contactless laser-based technique. 一种用于测量振动表面运动的装置，通常使用非接触激光技术。 |
| Shear strength | 抗剪强度 |
The maximum shear stress that a material is capable of sustaining. Shear strength is calculated from the maximum load during a shear or torsion test and is based on the original dimensions of the cross section of the specimen. 材料能够承受的最大剪切应力。抗剪强度根据剪切或扭转试验期间的最大载荷计算，并基于试样横截面的原始尺寸。 |
| Sample standard deviation (s) | 样本标准偏差（s） |
The square root of the sample variance. It is a point estimate of the population standard deviation, a measure of the “spread”of the frequency distribution of a population. This value of sprovides a statistic that is used in computing interval estimates and several test statistics. For small sample sizes, s underestimates the population standard deviation. 样本方差的平方根。它是总体标准偏差的点估计，是总体频率分布“扩散”的度量。SPR的这个值提供了一个用于计算区间估计和若干测试统计量的统计量。对于小样本，s低估了总体标准偏差。 |
| Temper color | 回火颜色 |
A thin, tightly adhering oxide skin that forms when steel is tempered at a low temperature, or for a short time, in air or a mildly oxidizing atmosphere. The color, which ranges from straw to blue depending on the thickness of the oxide skin, varies with both tempering time and temperature. 一种薄的、紧密粘附的氧化皮，当钢在低温或短时间内在空气或轻度氧化气氛中回火时形成。颜色范围从稻草色到蓝色，取决于氧化皮的厚度，随回火时间和温度而变化。 |
| Dynamic compressor | 动态压缩器 |
A machine, such as a centrifugal or axial compressor, that compresses a gas by rotational rather than reciprocating motion. 一种机器，例如离心式或轴流式压缩机，通过旋转而不是往复运动来压缩气体。 |
| Thread form | 螺纹形式 |
The cross-sectional shape of the threads, defining thread angle, root, and crest profiles, etc. Thread length Length of that portion of the fastener which contains threads cut or rolled to full depth. 螺纹的横截面形状，定义螺纹角度、齿根和齿冠轮廓等。螺纹长度：紧固件中包含全深度切割或轧制螺纹的部分的长度。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| Material velocity | 材料速度 |
The velocity of sound in a body (e.g., a bolt). A term used in the ultrasonic measurement of bolt stress or strain. 声音在物体（例如螺栓）中的速度。用于螺栓应力或应变的超声波测量的术语。 |
| Fahrenheit | 华氏度 |
The temperature scale based on the freezing point of water (32ºF) and the boiling point of water (212ºF). The interval between these points is divided into 180 equal parts. Although replaced by the Celsius scale, the Fahrenheit scale is still sometimes used for non-scientific measurements. 温标基于水的冰点（32ºF）和水的沸点（212ºF）。这些点之间的间隔被分成180等份。尽管被摄氏刻度所取代，华氏刻度有时仍用于非科学测量。 |
| Micrometer | 千分尺 |
(micrometer gauge) A mechanical-contact device for the accurate measurement of the length, width, diameter, etc. of an object, the depth of a hole, the height of a step, etc. The usual arrangement is a spindle that is moved by rotation of a thimble, the distance then being read off a vernier scale. （千分尺）一种机械接触装置，用于精确测量物体的长度、宽度、直径等、孔的深度、台阶的高度等。通常的布置是通过顶针的旋转移动主轴，然后通过游标尺读取距离。 |
| Oxidizing agent | 氧化剂 |
A compound that causes oxidation, thereby itself becoming reduced. 一种引起氧化从而自身被还原的化合物。 |
| Inspection gauge | 检验规 |
Any of various gauges used in manufacturing and quality control to check dimensions, finish, etc. 任何用于制造和质量控制的各种量规，以检查尺寸、光洁度等。 |
| Applied thermodynamics | 应用热力学 |
(engineering thermodynamics, thermodynamics) The science of the relationship between heat, work and the properties of systems and the ways in which heat energy from fuels can be converted into mechanical work. It involves the study of all aspects of energy use and energy transformation, including power generation, refrigeration, the relevant properties of the substances involved and the relationships between them. The principle of conservation of energy is a fundamental law of nature. （工程热力学、热力学）热、功和系统特性之间关系的科学，以及燃料中的热能可以转化为机械功的方式。它涉及能源使用和能源转换的各个方面的研究，包括发电、制冷、所涉及物质的相关特性以及它们之间的关系。能量守恒定律是自然的基本规律。 |
| Decompression chamber | 减压舱 |
A chamber in which ambient-air pressure can be increased to levels found in deep-sea diving. It is used to gradually acclimatize divers back to normal conditions and avoid ‘the bends’. 环境气压可以提高到深海潜水水平的腔室。它用于逐渐使潜水员适应正常条件，避免“弯曲”。 |
| Verification | 检验 |
Checking or testing an instrument to ensure conformance with a specification. 检查或测试仪器以确保符合规范。 |
| Pre-stress | 预应力 |
To induce stresses into a component or structure before it is subjected to operating loads. 在部件或结构承受操作载荷之前，将应力引入部件或结构。 |
| Compressive strength | 抗压强度 |
Maximum compressive stress a material is capable of developing. With a brittle material that fails in compression by fracturing, the compressive strength has a definite value. For ductile, malleable, or semiviscous materials (which do not fail in compression by a shattering fracture), the value obtained for compressive strength is an arbitrary value dependent on the degree of distortion that is regarded as effective failure of the material. 材料能够产生的最大压缩应力。如果脆性材料因破裂而无法压缩，则抗压强度具有一定值。对于韧性、可锻性或半粘性材料（不会因破裂而导致压缩失效），获得的抗压强度值是一个任意值，取决于被视为材料有效失效的变形程度。 |
| Bar | 巴（气压单位） |
A widely used (non-SI) unit of pressure approximately equal to normal atmospheric pressure at sea level. The conversion to SI is 1 bar = 105 Pa. Unit of pressure – the pressure created by a column of€mercury 75.006 cm high at 0ºC, or about 33.45 feet of water at 4ºC. It is equal to 105 pascal. Standard atmospheric pressure (at sea level) is 1.01325 bar, or 1013.25 mb. 一种广泛使用的（非SI）压力单位，大约等于海平面上的正常大气压。转换为SI为1bar=105Pa。压力单位——0ºC时75.006厘米高的水银柱或4ºC时约33.45英尺水柱产生的压力。它等于105帕斯卡。标准大气压（海平面）为1.01325bar或1013.25mb。 |
| Nut thickness | 螺母厚度 |
The nut thickness shall be the overall distance measured parallel to the axis of nut, from the top of the nut to the bearing surface, and shall include the thickness of the washer face where provided. 螺母厚度应为平行于螺母轴线测量的从螺母顶部到轴承表面的总距离，还应包括垫圈表面的厚度。 |
| Fastener | 紧固件 |
A fastener is a mechanical device for holding two or more bodies in definite positions with respect to each other. 紧固件是一种机械装置，用于将两个或多个物体相对于彼此固定在确定的位置。 |
| Load ratio, R | 负载比R |
In fatigue, the algebraic ratio of the minimum to maximum load in a fatigue cycle, that is, R = Pmin/Pmax. Also known as stress ratio. 在疲劳中，疲劳循环中最小载荷与最大载荷的代数比，即 R= Pmin/Pmax。也称为应力比。 |
| Milling | 铣削 |
A machining process, typically for metals and plastics, in which a multi-tooth rotary cutter removes material to produce flat or profiled surfaces, slots, grooves, etc. Milling is a machining process in which metal is removed by a rotating multiple-tooth cutter; each tooth removes a small amount of metal with each revolution of the spindle. Because both workpiece and cutter can be moved in more than one direction at the same time, surfaces having almost any orientation can be machined. 一种加工工艺，通常用于金属和塑料，其中多齿旋转刀具去除材料以产生平坦或异形表面、槽、槽等。金属由旋转多齿刀具去除；主轴每转一圈，每个齿都会去除少量金属。因为工件和刀具可以同时在多个方向上移动，所以几乎可以加工任何方向的表面。 |
| Single thread | 单头螺纹 |
A screw thread cut around a cylinder having a single start in which the lead is equal to the pitch. 一种螺纹，在一个圆柱体上切割而成，具有一个单一的起点，在这个起点上，导程等于螺距。 |
| Celsius temperature scale | 摄氏温标 |
(centigrade temperature scale) A relative, non-SI, temperature scale now defined in terms of the Kelvin absolute temperature scale as °C = K − 273.15, where °C is the symbol for degrees Celsius. The scale was previously called the centigrade scale, with two fixed points: the melting point of ice (the ice point) as 0°C, and the boiling point of water (the steam point) as 100°C. （摄氏度温度标度）现在以开尔文绝对温度标度定义的相对非国际温度标度为°C=K-273.15，其中°C是摄氏度的符号。该刻度以前称为摄氏度刻度，有两个固定点：冰的熔点（冰点）为0°C，水的沸点（蒸汽点）为100°C。 |
| Pressure difference (Unit Pa) | 压差（单位Pa） |
(pressure differential, Δp) The difference between two pressures, one of which may be a reference pressure such as barometric pressure. In many flow processes, the pressure difference is more important than the absolute pressure level. （压差，Δp）两个压力之间的差值，其中一个压力可以是参考压力，如大气压力。在许多流动过程中，压差比绝对压力水平更重要。 |
| Ferritic decarburization | 铁素体脱碳 |
Decarburization with sufficient loss of carbon to cause a lighter shade of tempered martensite and a significantly lower hardness than that of the adjacent base metal, with the presence of ferrite grains or grain boundary network under metallographic examination. 脱碳，碳损失充分，导致回火马氏体颜色较浅，硬度明显低于相邻母材，金相检查时存在铁素体晶粒或晶界网络。 |
| Non-ferrous metal | 有色金属 |
Strictly, all metals and alloys that do not contain iron, but usually taken to mean aluminium- and copper-based alloys. 严格来说，所有不含铁的金属和合金，但通常指铝基和铜基合金。 |
| Wave spring | 波形弹簧 |
A type of compression spring, similar to a coil spring, but made of strip shaped into waves around the circumference. 一种压缩弹簧，类似于螺旋弹簧，但由沿圆周成波浪形的条状物制成。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Safety valve (safety-relief valve) | 安全阀（安全泄压阀） |
A mechanical valve, fitted by law to all pressure vessels (e.g. steam boilers), which opens to prevent the internal pressure exceeding the maximum design value for that vessel. The valve closes again once the pressure reduces to a safe level. 根据法律安装在所有压力容器（如蒸汽锅炉）上的机械阀，其打开以防止内部压力超过该容器的最大设计值。一旦压力降至安全水平，阀门将再次关闭。 |
| Air-cooled engine | 风冷发动机 |
An internal-combustion engine directly cooled by airflow, rather than by water flowing through the engine block being cooled by a radiator. 一种由气流直接冷却的内燃机，而不是通过流经发动机缸体的水被散热器冷却。 |
| Threshold stress for stress-corrosion cracking (σth) | 应力腐蚀开裂阈值应力（σth） |
An experimentally determined critical gross-section stress below which stress-corrosion cracking will not occur under specified test conditions. 实验确定的临界总截面应力，低于该应力，在规定的试验条件下不会发生应力腐蚀开裂。 |
| Edge distance | 边距 |
The distance from the edge of a bearing specimen to the center of the hole in the direction of applied force. 在作用力方向上，从轴承试样的边缘到孔中心的距离。 |
| Dead load (Unit N) | 静载（单位N） |
A load on a component or structure that is steady with time, e.g. the self-weight of a bridge. 部件或结构上随时间稳定的载荷，例如桥梁的自重。 |
| Sample variance (s²) | 样本方差（s²） |
The sum of the squares of the differences between each observed value and the sample average divided by the sample size minus one. It is a point estimate of the population variance. 每个观测值与样本平均值之差的平方和除以样本大小减1。它是总体方差的点估计。 |
| Friction loss (Unit J) | 摩擦损失（单位J） |
The conversion of mechanical energy to heat due to friction within a machine, mechanism, linkage, etc. 由于机器、机构、连杆等内部的摩擦而将机械能转化为热能。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Selective heating | 局部加热 |
Intentionally heating only certain portions of a workpiece. 有意仅加热工件的某些部分。 |
| Breaking load (Unit N) | 断裂负荷（单位N） |
The load applied at some point to a component or structure which leads to fracture. The breaking stress (breaking strength) is the average stress at which a member breaks, given by the breaking load divided by the area over which it acts. 在某个点施加到导致断裂的部件或结构的载荷。断裂应力（断裂强度）是构件断裂时的平均应力，由断裂载荷除以其作用的面积给出。 |
| Heat-capacity rate (c) (Unit W/K) | 热容率（c）（单位W/K） |
For fluid flow in a duct with mass flow rate ṁ, the product ṁC where C is the specific-heat capacity, at constant pressure (CP) in the case of a gas. 对于质量流量为ṁ的管道中的流体流动，乘积ṁC其中C是比热容，在气体的情况下为恒定压力（CP）。 |
| Fatigue limit for p % survival | p%存活率的疲劳极限 |
The limiting value of fatigue strength for p%survival as the number of stress cycles becomes very large; pmay be any number, such as 95, 90, etc. 随着应力循环次数的增加，p%存活率的疲劳强度极限值变得非常大；p可以是任何数字，例如95、90等。 |
| Centi (c) | 厘（c） |
An SI unit prefix indicating a multiplier of 0.01; thus centimetre is a unit of length equal to one one-hundredth of a metre or 10 mm. 表示乘数0.01的SI单位前缀；因此厘米是长度单位，等于一米的百分之一或10毫米。 |
| Altitude | 高度 |
(Unit m) Vertical height measured relative to a specified datum such as sea level. （单位m）相对于特定基准（例如海平面）测量的垂直高度。 |
| Fin neck carriage bolt | 翼颈圆头方颈螺栓 |
A plain, circular, oval head bolt with two oppositely located fins to prevent rotation. 一种普通的圆形椭圆头螺栓，有两个相对的翼片以防止旋转。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Specimen | 样品 |
A test object, often of standard dimensions or configuration, that is used for destructive or nondestructive testing. One or more specimens may be cut from each unit of a sample. 用于破坏性或无损检测的测试对象，通常具有标准尺寸或配置。可以从样品的每个单位切割一个或多个样品。 |
| Hot quenching | 热淬火 |
An imprecise term used to cover a variety of quenching procedures in which a quenching medium is maintained at a prescribed temperature above 70 °C (160 °F) 一个不精确的术语，用于涵盖各种淬火程序，其中淬火介质规定温度保持在70°C（160°F）以上。 |
| Precipitation-hardenable stainless steels | 沉淀硬化不锈钢 |
Precipitation-hardenable stainless steels contain typically 11–18% chromium, 3–10% nickel, 0.05–0.2% carbon, and small additions of manganese, silicon, aluminium, molybdenum, niobium and titanium. These steels can be supplied in a solution-treated condition, which is readily fabricated or machined, and then hardened by an ageing treatment that produces a fine dispersion of second-phase precipitates. They are available in austenitic, semi-austenitic, and martensitic grades. Uses include springs, knives, and pressure vessels. 沉淀硬化不锈钢通常含有11-18%的铬、3-10%的镍、0.05-0.2%的碳以及少量添加的锰、硅、铝、钼、铌和钛。这些钢可在固溶处理条件下供应，该条件易于制造或机加工，然后通过时效处理硬化，从而产生细小的第二相沉淀。它们有奥氏体、半奥氏体和马氏体等级。用途包括弹簧、刀具和压力容器。 |
| Lubricant | 润滑剂 |
Any substance interposed between two surfaces for the purpose of reducing the friction or wear between them. 为了减少两个表面之间的摩擦或磨损而置于两个表面间的任何物质。 |
| Bolt blank | 螺栓毛坯 |
A rod on which a head has been formed, but on which no thread has been cut, from which bolts or screws may be made as required. 一种已形成头部但未切割螺纹的杆，可根据需要从中制造螺栓或螺钉。 |
| Compressometer | 压力计 |
Instrument for measuring change in length over a given gage length caused by application or removal of a force. Commonly used in compression testing of metal specimens. 用于测量在给定标距上由施加或移除力引起的长度变化的仪器。常用于金属试样的压缩试验。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Screw extractor | 螺钉拔 |
A device for removing broken-off screws from threaded holes. It resembles a drill with, for broken right-hand threads, a fast (long-pitch) left-hand thread that is driven into a hole drilled in the broken screw, thus untwisting it. 从螺纹孔中去除断裂螺钉的装置。它类似于一个钻头，对于断裂的右螺纹，一个快速（长螺距）的左螺纹被打入在断裂螺钉上钻的孔中，从而将其松开。 |
| Drift pin | 冲头 |
A round tapered steel pin used to align rivet holes so that the rivet will pass through the holes easily. 用于对齐铆钉孔的圆形锥形钢销，以便铆钉轻松穿过孔。 |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Embedment | 嵌入 |
Localized plastic deformation in heavily loaded fasteners allows one part to sink into, or smooth the surface of, a softer or more heavily loaded second part. Nuts embed themselves in joint surfaces. Bolt threads embed themselves in nut threads, etc. 重载紧固件中的局部塑性变形允许一个零件陷入较软或更重载的第二零件中，或使其表面光滑。螺母嵌入接合面中。例如螺栓螺纹嵌入螺母螺纹等。 |
| Computer control | 电脑控制 |
The control of an engineering device or system by pre-programmed computer or by feedback control. 通过预编程计算机或反馈控制对工程设备或系统进行控制。 |
| Linear-elastic fracture mechanics | 线弹性断裂力学 |
A method of fracture analysis that can determine the stress (or load) required to induce fracture instability in a structure containing a cracklike flaw of known size and shape. 一种断裂分析方法，可确定在含有已知尺寸和形状裂纹状缺陷的结构中引起断裂不稳定性所需的应力（或载荷）。 |
| Vacuum servo | 真空服务器 |
A vacuum-operated servomotor which is used in a motor vehicle to provide a brake effort greater than the capability of the driver. 一种真空操作的伺服电机，用于机动车中，以提供大于驾驶员能力的制动力。 |
| Newton (N) | 牛顿（N） |
The basic unit of force in the SI system, defined as the force that results in an acceleration of 1 m/s² when acting on a 1 kg mass. SI国际单位制中力的基本单位，定义为作用于1kg质量时产生1m/s²加速度的力。 |
| Clip gauge | 夹规 |
A displacement gauge consisting of two thin strain-gauged cantilever arms attached through knife edges to a testpiece to give the load–line displacement in fracture mechanics test pieces, or used as an extensometer in tensile tests. 一种位移计，由两个通过刀刃连接到试件上的薄应变测量悬臂组成，以提供断裂力学试件中的载荷线位移，或用作拉伸试验中的引伸计。 |
| Secondary hardening | 二次硬化 |
The process whereby some low-alloy steels, quenched to produce martensite, produce fine precipitates when tempered above 550°C, which inhibit dislocation motion and reverse the trend towards lower strength at higher tempering temperatures. 某些低合金钢经淬火产生马氏体，在550°C以上回火时产生细小沉淀的过程，这抑制了位错运动，扭转了在较高回火温度下强度降低的趋势。 |
| Swept volume (Unit m³) | 扫描体（单位m³) |
In the cylinder of a piston engine or other device, the volume between top and bottom dead centre positions of a piston; equal to πR2S where R is the piston radius and S is the stroke. 在活塞发动机或其他装置的气缸中，活塞上止点和下止点位置之间的体积；等于πR2S，其中R是活塞半径，S是冲程。 |
| Heat tinting | 热着色 |
Coloration of a metal surface through oxidation by heating to reveal details of the microstructure. 通过加热氧化使金属表面着色，以揭示微观结构的细节。 |
| Piston pump | 活塞泵 |
A positive-displacement pump in the basic configuration of which a piston reciprocates in a cylinder. On the suction stroke, fluid is drawn into a chamber through the inlet valve, which is then open while the outlet valve is closed. On the delivery stroke the fluid is forced out of the chamber through the outlet valve, which then opens while the inlet valve is closed. Both axial and radial configurations are common. 活塞在气缸中往复运动的一种容积泵。在吸入冲程，流体通过入口阀吸入腔室，然后在出口阀关闭时打开。在输送冲程中，流体通过出口阀被迫流出腔室，然后出口阀打开，同时入口阀关闭。轴向和径向配置都很常见。 |
| Compressor | 压缩机 |
A turbomachine, of either axial or radial type, that increases the pressure of a gas or vapour. 一种增加气体或蒸汽压力的轴向或径向涡轮机。 |
| Deflection temperature under load (DTUL) | 负载变形温度（DTUL） |
The temperature at which a simple cantilever beam deflects a given amount under load. Formerly called heat distortion temperature. 简单悬臂梁在负载下偏转给定量的温度。以前称为热变形温度。 |
| Torsional angle (ϕ) | 扭转角（ψ） |
(Unit ° or rad) The angular deflexion between two locations on a straight bar subjected to a torque. （单位为°或rad）受扭矩作用的直杆上两个位置之间的角偏转。 |
| Partial annealing | 不完全退火 |
An imprecise term used to denote a treatment given cold-worked material to reduce the strength to a controlled level or to effect stress relief. To be meaningful, the type of material, the degree of cold work, and the time-temperature schedule must be stated. 一个不精确的术语，用于表示冷加工材料的处理，以将强度降低到受控水平或消除应力。为了有意义，必须说明材料类型、冷加工程度和时间-温度计划。 |
| Shear strain | 剪切应变 |
The tangent of the angular change, as a response to force, between two lines originally perpendicular to each other through a point in a body. Also known as shearing strain. 角变化的切线，作为对力的响应，在两条原本通过物体中的一个点相互垂直的线之间。也称为剪切应变。 |
| Castellated nut | 槽形螺母 |
A nut having slots across the hexagonal faces, used with a bolt having a drilled hole so that a split (cotter) pin may be inserted through both nut and bolt to prevent unscrewing. 一种在六角面上有槽的螺母，与具有钻孔的螺栓一起使用，以便将开口（开口）销插入穿过螺母和螺栓以防止拧松。 |
| Physical properties | 物理性质 |
Properties of a material the determination of which does not involve the deformation or destruction of the specimen—for example, density, electrical conductivity, coefficient of thermal expansion, magnetic permeability, and lattice parameter. Does not include chemical reactivity or the properties more appropriately regarded as mechanical properties. 不涉及试样变形或破坏的材料特性，例如密度、电导率、热膨胀系数、磁导率和晶格参数。不包括化学反应性或更适当地视为机械的性质。 |
| Acoustic droplet ejection | 声液滴喷射 |
The ejection of small droplets from the surface of a liquid that results from focusing high-intensity ultrasound near the surface. 由于在表面附近聚焦高强度超声波而从液体表面喷射出小液滴。 |
| Compressive stress (Unit Pa) | 压缩应力（单位Pa） |
The compressive load per unit area at a point in a component. 部件中某点的每单位面积的压缩载荷。 |
| Air-cooled condenser | 风冷冷凝器 |
A heat exchanger, in which the cooling medium is air, used to condense the exhaust steam from a steam turbine, the condensate being returned to the boiler. 一种热交换器，其中冷却介质为空气，用于冷凝蒸汽轮机排出的蒸汽，冷凝水返回锅炉。 |
| Bucket | 吊桶 |
1. A cup-shaped vane with a central dividing ridge attached to the periphery of the runner of an impulse water turbine such as a Pelton turbine. 2. A rotor blade in a compressor or turbine. 1.一种杯形叶片，所述杯形叶片具有附接到冲击式水轮机（例如冲击式水轮机台）的转轮的外围的中央分隔脊。2.压缩机或涡轮机中的转子叶片。 |
| Transgranular fracture | 穿晶断裂 |
Fracture in crystalline materials where the path of cracking is predominantly across grains. 晶体材料中的断裂，其中裂纹路径主要跨越晶粒。 |
| Thermal shock | 热冲击 |
The development of a steep temperature gradient and accompanying high stresses within a structure. 在结构内形成陡峭的温度梯度和伴随的高应力。 |
| Turning angle (θ) | 转向角（θ） |
The change in direction experienced by a gas flow passing through an oblique shock wave or Prandtl–Meyer expansion fan. 气流通过斜激波或Prandtl–Meyer膨胀风机时所经历的方向变化。 |
| Turbomachine | 涡轮机械 |
(rotodynamic machine) A machine in which there is a transfer of energy between a continuous stream of fluid and a component, called a rotor, rotating about a fixed axis. Fans and turbines (gas, hydraulic, steam, or wind) are turbomachines in which energy is transferred to the rotor, causing it to rotate. Pumps and compressors are turbomachines in which energy is transferred from the externally driven rotor to the fluid. （旋转动力机器）在连续的流体流和绕固定轴旋转的部件（称为转子）之间进行能量传递的机器。风扇和涡轮机（燃气、液压、蒸汽或风力）是涡轮机械，其中能量传递到转子，使其旋转。泵和压缩机是涡轮机械，其中能量从外部驱动的转子传递到流体。 |
| Adhesive joint | 粘合接头 |
The point or area in which two structures are held together by an adhesive. 两个结构通过粘合剂粘合在一起的点或区域。 |
| Temperature factor | 温度系数 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. Accounts for the effects of thermal expansion and the temperature-induced change in the velocity of sound. 用于螺栓应力或应变超声波测量的校准常数。说明了热膨胀和温度引起的声速变化的影响。 |
| Precision | 精确 |
The closeness of agreement between the results of individual replicated measurements or tests. The standard deviation of the error of measurement may be used as a measure of “imprecision.” 单个重复测量或测试结果之间的一致性。测量误差的标准偏差可用作“不精确性”的度量 |
| Morse taper | 莫氏锥度 |
A self holding, standard taper largely used on drilling tools, drilling machine spindles, and some lathes. 一种自持式标准锥度，主要用于钻孔工具、钻床主轴和一些车床。 |
| Mechatronics | 机电一体化 |
The integration of mechanical engineering, electrical engineering, electronic engineering, and software engineering. 机械工程、电气工程、电子工程和软件工程的集成。 |
| Hardness | 硬度 |
A measure of the resistance of a material to surface indentation or abrasion; may be thought of as a function of the stress required to produce some specified type of surface deformation. There is no absolute scale for hardness; therefore, to express hardness quantitatively, each type of test has its own scale of arbitrarily defined hardness. Indentation hardness can be measured by Brinell hardness test, Rockwell hardness test, Vickers hardness test, Knoop hardness test, and the Scleroscope hardness test. The ability of a ductile material to resist permanent deformation. It is a measure of plastic flow properties determined principally by indentation testing, but scratch hardness and rebound hardness are also employed. hardness scales The different measures of hardness given by different tests, such as indentation pressure in the Brinell and in the Vickers hardness tests, and the different Rockwell hardness numbers. 测量材料对表面压痕或磨损的阻力；可以认为是产生某些特定类型的表面变形所需的应力的函数。硬度没有绝对刻度，因此为了定量表示硬度，每种类型的试验都有自己的任意定义硬度等级。压痕硬度可通过布氏硬度试验、洛氏硬度试验，维氏硬度试验和努氏硬度试验以及硬化镜硬度试验进行测量。延展性材料具有抵抗永久变形的能力，它是主要通过压痕测试确定的塑性流动性能的量度，也使用划痕硬度和回弹硬度。硬度标度不同试验给出的不同硬度测量值，如布氏硬度试验和维氏硬度试验中的压痕压力，以及不同的洛氏硬度值。 |
| Gauge | 测量 |
1. Any instrument for measuring or checking dimensions, including adjustable gauges such as a micrometer and non-adjustable gauges such as go/no-go limit gauges that indicate the maximum and minimum dimensions allowable in a component during manufacture. 2. A term often used to mean an instrument, e.g. pressure gauge. 3. The diameter of a wire or thickness of a sheet according to a standard. 4. The distance between the rails of a railway track. 1. 任何用于测量或检查尺寸的仪器，包括可调节量规（例如千分尺）和不可调节量规（例如指示制造过程中组件允许的最大和最小尺寸的通过/不通过限制量规）。2. 常用于表示仪器的术语，例如压力表。3.根据标准的线材直径或片材厚度。4.铁路轨道的钢轨之间的距离。 |
| Wrinkling | 起皱 |
A wavy condition obtained in deep drawing of sheet metal, in the area of the metal between the edge of the flange and the draw radius. Wrinkling may also occur in other forming operations when unbalanced compressive forces are set up. 在金属板深冲过程中，在法兰边缘和拉深半径之间的金属区域内获得的波浪状状态。当设置不平衡压缩力时，在其他成形操作中也可能发生起皱。 |
| Thermoelectric junction | 热电结 |
A welded, soldered, or twisted connection between the ends of two wires of dissimilar metals, as in a thermocouple. 两根不同金属线的末端之间的焊接、锡焊或绞合连接，如热电偶。 |
| Junker machine | 容克机 |
A test machine, first proposed by Gerhard Junker, for testing the vibration resistance of fasteners. 由Gerhard Junker首次提出的测试机，用于测试紧固件的抗振性。 |
| Testing machine (load-measuring type) | 试验机（负载测量型） |
A mechanical device for applying a load (force) to a specimen. 向试样施加载荷（力）的机械装置。 |
| Continuous precipitation | 连续沉淀 |
Precipitation from a supersaturated solid solution in which the precipitate particles grow by longrange diffusion without recrystallization of the matrix. Continuous precipitates grow from nuclei distributed more or less uniformly throughout the matrix. They usually are randomly oriented, but may form a Widmanstätten structure. 来自过饱和固溶体的沉淀，其中沉淀颗粒通过长程扩散生长而无需基质再结晶。连续析出物从在整个基体中或多或少均匀分布的核生长而来。它们通常是随机取向的，但可能形成魏氏结构。 |
| Cavitation damage | 气蚀损坏 |
Erosion of a solid surface through the formation and collapse of cavities or bubbles in an adjacent liquid that contains vapor and/or gas. 通过在包含蒸汽和/或气体的相邻液体中形成空穴或气泡并破坏固体表面。 |
| Tangent modulus | 切线模量 |
The slope of the stress-strain curve at any specified stress or strain. See also modulus of elasticity. 在任何规定的应力或应变下，应力-应变曲线的斜率。另见弹性模量。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Wing nut | 蝶形螺母 |
A nut having two opposite protruding wings to permit hand tightening. 一种螺母，有两个相对突出的翼片，可以用手拧紧。 |
| Inch-pound force/inch² | 英寸磅力/英寸² |
A non-SI unit for the specific work of fracture (fracture toughness). The conversion to SI is 1 in.lbf/in² = 1.751 268 × 102 J/m². 用于特定断裂功（断裂韧性）的非国际单位制单位。到SI的转换为1英寸。lbf/in²=1.751268×102J/m²。 |
| Regenerative pump | 涡流泵 |
(regenerative turbine pump, peripheral pump) A pump with a double-sided impeller having a large number of radial blades. The pressure of the pumped liquid increases progressively over several revolutions of the impeller. It is particularly suited to producing large heads at small flow rates without cavitation. （再生涡轮泵，外围泵）具有具有大量径向叶片的双面叶轮的泵。泵送液体的压力在叶轮的几圈内逐渐增加。它特别适合于在小流速下产生大水头且不产生气穴。 |
| Austenitic stainless steels | 奥氏体不锈钢 |
Austenitic stainless steels are non-magnetic. They contain significant additions of chromium (16–30%), but have the austenite (FCC) crystal structure, stabilized by the addition of nickel in the composition range 6–20%. Carbon content ranges from about 0.03 to 0.15%. The ‘18–8’ stainless steels containing approximately 18% chromium and 8% nickel are typical of the class. Austenitic stainless steels have high strength and corrosion resistance even at elevated temperatures, good ductility, good low-temperature properties, and good weldability. Used for aircraft and transport equipment, cutlery, chemical and food-processing equipment, surgical instruments, and cryogenic vessels. 奥氏体不锈钢是非磁性的。它们含有显着添加的铬（16–30%），但具有奥氏体（FCC）晶体结构，通过在6–20%的成分范围内添加镍来稳定。碳含量范围约为0.03至0.15%。含有大约18%铬和8%镍的“18-8”不锈钢是该级别的典型不锈钢。奥氏体不锈钢即使在高温下也具有高强度和耐腐蚀性，良好的延展性，良好的低温性能和良好的焊接性。用于飞机和运输设备、餐具、化学和食品加工设备、手术器械和低温容器。 |
| Pressure ratio | 压力比 |
One pressure divided by another which may be a reference pressure. In many flow and thermodynamic processes, the pressure ratio is more important than the absolute pressure levels. For example, in compressible gas flow the Mach number is determined by the ratio of the stagnation pressure to the static pressure. 一个压力除以另一个压力，该压力可以是参考压力。在许多流动和热力学过程中，压力比比绝对压力水平更重要。例如，在可压缩气流中，马赫数由停滞压力与静压之比决定。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Water column | 水柱 |
Water in a tube, which may be vertical or inclined. If the tube is open to the atmosphere, the vertical height h from a datum level to the water surface is a measure of the water static pressure p at the datum level given by p − B = ρgh where B is the barometric pressure, ρ denotes the water density, and g is the acceleration due to gravity. 管道中的水，可以是垂直的或倾斜的。如果管道向大气开放，则从基准面到水面的垂直高度h是基准面处水静压p的量度，由p给出−B=ρgh，其中B是大气压力，ρ表示水密度，g是重力引起的加速度。 |
| Spinner | 旋转器 |
A co-axial streamlined fairing enclosing the hub of a propeller and rotating with it. 一种同轴流线型整流罩，包围螺旋桨毂并随其旋转。 |
| Natural aging | 自然时效 |
Spontaneous aging of a supersaturated solid solution at room temperature. 过饱和固溶体在室温下的自发时效。 |
| Starting torque (Unit N.m) | 起动扭矩（单位：N.m） |
The torque developed by a motor at zero rotational speed in order to initiate rotation of the applied load. 电机在零转速下产生的扭矩，以启动所施加负载的旋转。 |
| Transmissibility | 传递率 |
The ratio of the transmitted force to the disturbing force for a system subjected to a vibratory disturbance. The ratio may also be defined in terms of displacements, velocities, or accelerations. 受到振动干扰的系统的传递力与干扰力之比。该比率也可以用位移、速度或加速度来定义。 |
| Residual preload | 残余预载荷 |
The tension which remains in an unloaded bolted joint after Relaxation. 松弛后未加载螺栓连接中保持的张力。 |
| Compounding | 复合串联 |
In a steam engine (compound steam engine) or impulse turbine, the progressive reduction in pressure (expansion) across two or more stages in series. 在蒸汽机（复合蒸汽机）或脉冲涡轮机中，通过串联的两个或多个级逐渐降低压力（膨胀）。 |
| Load and resistance factor design | 负载和阻力系数设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Assigns uncertainties in the strength of (i.e., resistance of) and in the service loads to be placed on a shear joint to estimate the probable strength of the joint. It is a recently defined alternative to the Allowable stress design procedure. 结构连接研究委员会为AISC制定的设计程序。分配剪切接头的强度（即阻力）和工作荷载的不确定性，以估计接头的可能强度。它是最近定义的容许应力设计程序的替代方案。 |
| Profile | 轮廓 |
The shape of a cross section of an object, such as an aerofoil or cam. 物体的横截面形状，如机翼或凸轮。 |
| Breaking stress | 断裂应力 |
The stress at failure. Also known as rupture stress. 失效时的应力。也称为破裂应力。 |
| Slack quenching | 欠速淬火 |
The incomplete hardening of steel due to quenching from the austenitizing temperature at a rate slower than the critical cooling rate for the particular steel, resulting in the formation of one or more transformation products in addition to martensite. 由于从奥氏体化温度以低于特定钢临界冷却速度的速度淬火而导致钢的不完全硬化，导致除马氏体外还形成一种或多种相变产物。 |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Millimetre of water | 毫米水柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of water 1 mm high. Approximately equal to 9.81 Pa. 一种非SI压力单位，等于1毫米高的垂直水柱施加的压力。大约等于9.81Pa。 |
| Impact strength 1. (Unit Pa) | 冲击强度1.（单位Pa） |
The stress to cause failure (by yielding or fracture) under conditions of high strain rate. 2. (Unit J) A term sometimes used to describe the energy required to fracture a specimen in a Charpy or Izod impact test even though the unit is not that of strength. 在高应变率条件下导致失效（通过屈服或断裂）的应力。2.（单位J）有时用于描述在夏比或悬臂梁式冲击试验中使样品断裂所需的能量，即使单位不是强度单位。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Tensioner | 张紧器 |
A hydraulic tool used to tighten a fastener by stretching it rather than by applying a substantial torque to the nut. After the tension has stretched the bolt or stud, the nut is run down against the joint with a modest torque, and the tensioner is disengaged from the fastener. The nut holds the stretch produced by the tensioner. 一种液压工具，用于通过拉伸紧固件而不是对螺母施加较大扭矩来拧紧紧固件。张力拉伸螺栓或螺柱后，以适当的扭矩将螺母向下压靠接头，张紧器与紧固件分离。螺母保持张紧器产生的拉伸。 |
| Carbon steels | 碳钢 |
(plain carbon steels) Steels in which carbon is the principal alloying element, and the amount of manganese does not exceed 1.65% and the copper and silicon contents are less than 0.60%. There are three main types: low-carbon steels (0.08–0.35% carbon); medium-carbon steels (0.35–0.50% carbon); and high-carbon steels (0.50–2.0% carbon). （普通碳钢）以碳为主要合金元素，锰含量不超过1.65%，铜和硅含量低于0.60%的钢。主要有三种类型：低碳钢（0.08-0.35%碳）；中碳钢（0.35–0.50%碳）；和高碳钢（0.50–2.0%碳）。 |
| Low-E coating | 低辐射涂层 |
(low-emittance coating) A thin metallic or metal-oxide coating on a glass sheet to absorb and reflect infrared radiation. The coating is applied either by a pyrolytic chemical vapour-deposition process (hard coat), or by sputtering (soft coat). （低辐射涂层）玻璃板上的薄金属或金属氧化物涂层，用于吸收和反射红外辐射。通过热解化学气相沉积工艺（硬涂层）或溅射（软涂层）施加涂层。 |
| Stress wave | 应力波 |
An unbalanced force, such as an impact, applied at one location in a body sets the material there into vibration that is transmitted to adjacent elements and ultimately to all parts of the body in the form of stress waves or wave packets. 施加在物体某个位置的不平衡力（如冲击力）会使物体中的材料产生振动，并以应力波或波包的形式传递到相邻元件，最终传递到物体的所有部位。 |
| Coextrusion | 复合挤压 |
The simultaneous extrusion through the same die of two or more materials in combination. 通过同一模具同时挤出两种或多种材料的组合。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Pitting | 点蚀 |
In tribology, a type of wear characterized by the presence of small, sharp surface cavities formed by processes such as fatigue, local adhesion, wear, corrosion, or cavitation. 在摩擦学中的一种磨损，其特征是存在由疲劳、局部粘附、磨损、腐蚀或空穴等过程形成的小而尖锐的表面空穴。 |
| Stress–strain curve | 应力-应变曲线 |
(stress–strain diagram) A plot of stress vs strain for a solid material obtained from a test in which a specimen is loaded in tension, compression, shear, or combinations thereof. Diagrams of true stress vs true strain deviate from those of nominal stress vs nominal strain only at large strains where appreciable changes in cross section of testpieces occur. （应力-应变图）从试验中获得的固体材料的应力与应变图，其中试样在拉伸、压缩、剪切或其组合中加载。只有在试件横截面发生明显变化的大应变下，真实应力与真实应变图与标称应力与标称应变图不同。 |
| Altitude chamber | 高空舱 |
(hypobaric chamber) A chamber in which conditions at different altitudes are simulated by a combination of appropriate pressures, temperatures and relative humidity. （低压舱）通过适当的压力、温度和相对湿度的组合来模拟不同高度条件的舱室。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Pressure (p) (Unit Pa) | 压力（p）（单位Pa） |
In thermodynamics and fluid mechanics, the compressive force exerted by the fluid per unit area. The pressure exerted by a fluid on a surface acts normal to the surface. 在热力学和流体力学中，每单位面积流体施加的压缩力。流体施加在表面上的压力垂直于表面。 |
| Radiation pressure (Unit μPa) | 辐射压力（单位：μPa） |
The pressure exerted on a surface exposed to any form of electromagnetic radiation. If the radiation is absorbed, it is equal to the power-flux density divided by the speed of light. 施加在暴露于任何形式电磁辐射的表面上的压力。如果辐射被吸收，它等于功率通量密度除以光速。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Cap screw | 帽螺钉 |
A bolt where the thread runs right up to the head and engages in a threaded hole or captive nut in an adjoining member. A finished screw 5mm or larger, used for fastening two pieces together by passing the screw through a clearance hole in one part and screwing in into a tapped hole in the other. A finished screw, used for fastening two pieces together by passing the screw through a clearance hole in one part and screwing it into a tapped hole in the other. Heads may be hexagon, round, flat, fillister or socket type. 一个5毫米或更大的螺钉，其螺纹一直延伸到头部，并与相邻构件的螺纹孔或外加螺母啮合,用于将两个部件固定在一起，方法是将螺钉穿过一个部分的间隙孔，然后拧入另一个部分的螺纹孔。头部可以是六角形、圆形、扁平形、圆角形或套筒形。 |
| Coefficient of thermal expansion | 热膨胀系数 |
(1) Change in unit of length (or volume) accompanying a unit change of temperature, at a specified temperature. (2) The linear or volume expansion of a given material per degree rise of temperature, expressed at an arbitrary base temperature or as a more complicated equation applicable to a wide range. （1） 单位长度（或体积）随温度单位变化的变化。（2） 给定材料每上升一度的线性或体积膨胀，在任意基础温度下表示，或作为适用于宽范围的更复杂方程表示。 |
| Standard hole | 标准孔 |
A hole in a workpiece bored to a specified tolerance where clearance with a shaft is accomplished by allowance on the shaft. A standard shaft is machined to a specified tolerance where clearance with a hole is accomplished by allowance on the hole. 工件上的孔，钻孔至规定公差，其中与轴的间隙通过轴上的余量来实现。标准轴加工至规定公差，其中与孔的间隙通过孔上的公差实现。 |
| Blind rivet | 盲孔铆钉 |
A rivet that enables a connexion to be made from one side only of an assembly. 一种铆钉，可以仅从组件的一侧进行连接。 |
| Machine tool | 机床工具 |
A powered machine, such as a borer, grinder, lathe, milling machine or planer, used for cutting and shaping metal, plastics, composites, etc. (machining). A machining centre is a CNC machine tool working about several axes, having a stock of tools and automatic tool changing ability, which is capable of diverse machining operations under automated control. 一种动力机器，如钻孔机、磨床、车床、铣床或刨床，用于切割和成形金属、塑料、复合材料等（机加工）。加工中心是围绕多个轴工作的CNC机床，具有刀具库存和自动换刀能力，能够在自动化控制下进行各种加工操作。 |
| Vibration | 振动 |
1. A periodic change with time of the displacements of elements making up a component or structure. 2. The study of the oscillatory motion of bodies and systems and the frequencies, amplitudes, and forces associated with them. 1.组成部件或结构的元件位移随时间的周期性变化。2.研究物体和系统的振荡运动以及与之相关的频率、振幅和力的学科。 |
| Ultimate strength | 极限应力 |
The maximum tensile strength a bolt or material can support prior to rupture. Always found in the plastic region of the stress–strain or force–elongation curve, and so is not a design strength. Also called Tensile strength and ultimate tensile strength. The maximum stress (tensile, compressive, or shear) a material can sustain without fracture, determined by dividing maximum load by the original cross-sectional area of the specimen. Also known as nominal strength or maximum strength. 螺栓或材料在断裂前可支撑的最大抗拉强度。总是出现在应力-应变或力-伸长率曲线的塑性区域，因此不是设计强度。也称为抗拉强度和极限抗拉强度。材料在不断裂的情况下能够承受的最大应力（拉伸、压缩或剪切），通过将最大载荷除以试样的原始横截面积来确定。也称为标称强度或最大强度。 |
| Surface roughness (roughness) | 表面粗糙度 |
The small-scale, irregular peaks and troughs in a solid surface which are quantified using a surface analyser. Roughness may be a consequence of wear and corrosion, or of the manufacturing process. It leads to increased friction in solid– solid contact or fluid flow over a surface. Errors of form and waviness are excluded, but surface texture includes roughness and waviness. Surface topography incorporates the small-scale, three-dimensional geometry of a surface including surface roughness, machined, and etched features, typically at sub-mm scales. 固体表面中的小尺度不规则峰谷，使用表面分析仪进行量化。粗糙度可能是磨损和腐蚀或制造过程的结果。它会导致表面上的固-固接触或流体流动中的摩擦增加。不包括形状和波纹度误差，但表面纹理包括粗糙度和波纹度。表面形貌包括表面的小尺度三维几何结构，包括表面粗糙度、机加工和蚀刻特征，通常为亚毫米尺度。 |
| Angularity | 角度 |
The underfaces of the nut and the bolt head should be exactly perpendicular to the thread or shank axes. If the angle between the face and the axis is, for example, 868 or 948, the fastener is said to have an angularity of 48 (sometimes called Perpendicularity). 螺母和螺栓头的底面应与螺纹或柄轴完全垂直。例如，如果面和轴之间的角度为868或948，则称紧固件的角度为48（有时称为垂直度）。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Multiple threaded screw | 多螺纹螺钉 |
A screw with two or more threads cut around the periphery of the workpiece to provide an increased lead with a specified pitch. 一种螺钉，具有围绕工件周边切割的两个或多个螺纹，以提供具有指定螺距的增加的导程。 |
| A-basis | A-基础 |
Mechanical property value above which at least 99% of the population of values is expected to fall, with a confidence of 95%. Also called A-allowable. 机械性能值超过该值时，至少99%的值预计会下降，置信度为95%。也被称为A-容许。 |
| Anode | 阳极 |
That electrode in a battery or corrosion cell which produces electrons. It is the electrode which is destroyed (corrodes). 电池或腐蚀电池中产生电子的电极。被破坏（腐蚀）的是电极。 |
| Activation energy | 活化能 |
(Ea, U) (Unit kJ/mol) The minimum energy for a chemical reaction to occur or for processes such as diffusion to take place in crystals. （Ea, U）（单位kJ/mol）发生化学反应或在晶体中发生扩散等过程的最小能量。 |
| Quimby screw pump | 昆比螺杆泵 |
A screw pump with two meshing screws, each having a righthand and a left-hand screw. Liquid enters at either end and is discharged from the middle. 带有两个啮合螺钉的螺杆泵，每个都有一个右旋螺纹和一个左旋螺纹。液体从两端进入，从中间排出。 |
| Zone melting (zone refining) | 区域熔炼（区域精炼） |
A process of purification of materials in which a narrow molten zone is moved along the length of the material, resulting in impurities being segregated at one end. 一种净化材料的过程，其中一个狭窄的熔融区沿材料长度移动，导致杂质在一端分离。 |
| Fastener with waisted shank | 带腰柄的紧固件 |
Finished fastener with a shank diameter of ds < d2. 柄径ds |
| Hot stamping | 热冲压 |
Hot forging of brass and bronze alloys. 黄铜和青铜合金的热锻。 |
| Effective length of a bolt | 螺栓的有效长度 |
The grip length plus some portion of the bolt (often one-half of the thickness of the nuts) which lies within the nut(s) plus some portion (often one-half the thickness) of the head. 握持长度加上位于螺母内的螺栓的某些部分（通常是螺母厚度的二分之一）加上头部的某些部分（通常是厚度的二分之一）。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Zero initial conditions | 零初始条件 |
The assumption normally made in control engineering that up to a start time defined as t = 0, all variables have zero value. 在控制工程中通常作出的假设，即在定义为t=0的开始时间内，所有变量均为零值。 |
| Tempered martensite embrittlement | 回火马氏体脆化 |
Embrittlement of ultrahigh-strength steels caused by tempering in the temperature range of 205 to 400 °C (400 to 750 °F); also called 350 °C or 500 °F embrittlement. Tempered martensite embrittlement is thought to result from the combined effects of cementite precipitation on prioraustenite grain boundaries or interlath boundaries and the segregation of impurities at prioraustenite grain boundaries. 超高强度钢在205至400°C（400至750°F）温度范围内回火引起的脆化；也称为350°C或500°F脆化。回火马氏体脆化被认为是由于渗碳体沉淀在原奥氏体晶界或层间晶界上以及杂质在原奥氏体晶粒边界处偏析的综合影响。 |
| Materials science | 材料科学 |
The study of the properties, behaviour, and application of solid substances such as metals, ceramics, glasses, polymers, composites, biomaterials, and semiconductors, at all scales from the atomic to the macroscopic. The topic has its origins in metallurgy. 研究金属、陶瓷、玻璃、聚合物、复合材料、生物材料和半导体等固体物质的特性、行为和应用，涵盖从原子到宏观的所有范围。起源于冶金学。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| Achme thread | Achme螺纹 |
A screw thread having an included angle of 29° and largely used for feed screws on machine tools. 一种夹角为29°的螺纹，主要用于机床上的进给丝杠。 |
| Vent | 发泄 |
A small valve that allows the release of pressurized fluid from a pipe, pressure vessel, etc., often to the atmosphere. 一种小阀门，允许将加压流体从管道、压力容器等中释放到大气中。 |
| Solution heat treatment | 固溶热处理 |
Heating an alloy to a suitable temperature, holding at that temperature long enough to cause one or more constituents to enter into solid solution, and then cooling rapidly enough to hold these constituents in solution. 将合金加热到合适的温度，在该温度下保持足够长的时间以使一种或多种成分进入固溶体，然后快速冷却以将这些成分保持在溶液中。 |
| Union (union joint) | 活接头 |
A threaded pipe fitting that allows two pipes to be connected anddetached without the need for either to be rotated, and without damaging the pipe ends. 一种螺纹管件，允许连接和拆卸两个管道，而无需旋转任何一个管道，且不会损坏管道端部。 |
| Radial flow | 径向流 |
radial flow Fluid flow for which the principal direction of flow is either radially inward or radially outward relative to an axial direction. 径向流动流体流动的主要方向是径向向内或径向向外流动。 |
| Fastener specification | 紧固件规格 |
A precise statement of set requirements to be satisfied by a fastener, its material, or its processing. It also indicates the procedure used to determine whether the requirements given are satisfied. 对紧固件、其材料或加工过程要满足的设定要求的精确陈述。它还指出了用于确定是否满足给定要求的程序。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Caustic cracking | 苛性开裂 |
A form of stress-corrosion cracking most frequently encountered in carbon steels or iron-chromiumnickel alloys that are exposed to concentrated hydroxide solutions at temperatures of 200 to 250 °C (400 to 480 °F). Also known as caustic embrittlement. 在200至250°C（400至480°F）的温度下暴露于浓氢氧化物溶液中的碳钢或铁铬镍合金中最常遇到的一种应力腐蚀开裂形式。也称为碱脆。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Crack arrest | 止裂 |
Crack propagation that stops of its own accord when the energy release rate of the loaded component or structure falls below a critical value. If predictable, it can be incorporated into structural-integrity assessments. 当加载部件或结构的能量释放率低于临界值时，裂纹自行停止扩展。如果可以预测，可以将其纳入结构完整性评估。 |
| International System of Units | 国际单位制 |
(SI system of units, Le Système international d’unités) The standard system of units now used almost universally in science and engineering except in the United States. The definitive reference on the SI is a booklet published by the International Bureau of Weights and Measures, often referred to as the BIPM SI Brochure. There are seven base units: metre (symbol m) for length; kilogram (kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred.(kg) for mass; mole (mol) for amount of substance; second (s) for time; kelvin (K) for temperature; ampere (A) for electric current; and candela (cd) for luminous intensity. New SI unit definitions, based upon the values of the universal constants of nature (also termed the fundamental physical constants: the Avogadro constant, the Boltzmann constant, and the Planck constant), came into effect on 20 May 2019. Minor adjustments were also made to the values of these constants. In addition to the base units, there are 22 coherent derived units, including radian (rad) for plane angle, steradian (sr) for solid angle, hertz (Hz) for frequency, newton (N) for force, pascal (Pa) for pressure, joule (J) for energy, work, and amount of heat, and watt (W) for power and radiant flux. Recommended practice is to avoid combinations such as N/mm², MN/m² being preferred. （国际单位制，Le Système international d\\\'unités）目前美国除外，在科学和工程中几乎是普遍使用的标准单位制。SI的最终参考是国际度量衡局出版的小册子，通常称为BIPM SI小册子。有七个基本单位：米（符号m）表示长度；质量为千克（kg）；物质量的摩尔（mol）；时间为秒；开尔文（K）表示温度；电流为安培（A）；而坎德拉（cd）表示发光强度。新的国际单位制定义于2019年5月20日生效，该定义基于自然界的普遍常数（也称为基本物理常数：阿伏伽德罗常数、玻尔兹曼常数和普朗克常数）。这些常数的值也进行了少量调整。除了基本单位外，还有22个相干导出单位，包括平面角的弧度（rad）、立体角的斯特拉迪安（sr）、频率的赫兹（Hz）、力的牛顿（N）、压力的帕斯卡（Pa）、能量、功和热量的焦耳（J）以及功率和辐射通量的瓦特（W）。建议的做法是避免N/mm²、MN/m²等组合。 |
| Mechanical efficiency (η) | 机械效率（η） |
1. In general for a machine, the ratio of output work to input work. 2. For a compressor, the ratio of indicated power to shaft power; for a reciprocating engine or an expander, the ratio of shaft power to indicated power. 1.一般而言，机器的输出功与输入功之比。2.对于压缩机，指示功率与轴功率之比；对于往复式发动机或膨胀机，轴功率与指示功率之比。 |
| Secant modulus | 割线模量 |
The slope of the secant drawn from the origin to any specified point on a stress-strain curve. Compare with chord modulus. 从原点到应力应变曲线上任何指定点的割线斜率。与弦模量进行比较。 |
| Nipple | 喷嘴 |
A device containing a non-return valve screwed into a lubrication point through which grease may be introduced, for example into a bearing. 一种包含止回阀的装置，该止回阀拧入润滑点，通过该润滑点可以将润滑脂引入，例如轴承中。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Vane engine (vane motor) | 叶片发动机（叶片马达） |
A rotary engine in which high-pressure hydraulic fluid in the spaces between spring-loaded sliding vanes held in an offset rotor acts on the vanes, causing the rotor to revolve within a cylinder. The design is much like a sliding-vane compressor, as is that of a vane pump, used to pump liquids. 一种旋转式发动机，其中偏置转子中装有弹簧的滑动叶片之间的高压液压流体作用在叶片上，使转子在气缸内旋转。这种设计很像滑动叶片压缩机，就像用于泵送液体的叶片泵一样。 |
| Forge | 锻造 |
To shape metal while holt and plastic by a hammering or forcing process. Dies used in process. 通过锤击或强制过程使金属成型，同时保持塑料成型。过程会使用模具。 |
| Heat balance (heat budget) | 热平衡（热预算） |
An energy balance involving only heat transfer across the system boundary and the stored energy. 仅涉及跨系统边界的热传递和存储能量的能量平衡。 |
| Thermodynamic pressure (Unit Pa) | 热力学压力（单位Pa） |
The pressure within a fluid given by an equation of state such as p(ρ,T) where ρ is the fluid density and T is the absolute temperature of the fluid. 流体中的压力由状态方程给出，如p（ρ，T），其中ρ是流体密度，T是流体的绝对温度。 |
| Design heating load (Unit kW) | 设计热负荷（单位kW） |
The heating requirements based on a specified number of heating degree days, or required to maintain a building or other enclosed space at a specified temperature for a given outside temperature. 基于指定的采暖度日数的加热要求，或在给定的外部温度下将建筑物或其他封闭空间保持在指定温度下所需的加热要求。 |
| Proof stress | 弹性极限应力 |
(1) The stress that will cause a specified small permanent set in a material. (2) A specified stress to be applied to a member or structure to indicate its ability to withstand service loads. （1）在材料中引起规定的小永久变形的应力。（2）施加在构件或结构上的规定应力，以表明其承受工作荷载的能力。 |
| Dilatation (dilation) | 膨胀 |
A change of volume caused by external load, compression, temperature change, chemical action, etc. 由外部载荷、压缩、温度变化、化学作用等引起的体积变化。 |
| Scratch hardness | 划痕硬度 |
The resistance of a material, such as a metal, alloy, plastic, or mineral, to scratching by a much harder indenter, such as a diamond stylus, moved slowly across the surface. The scratch hardness number is computed from the loads and the dimensions of the residual scratch. 一种材料（如金属、合金、塑料或矿物）对更硬的压头（如金刚石触针）划伤的抵抗力，在表面上缓慢移动。根据载荷和残余划痕的尺寸计算划痕硬度值。 |
| Median fatigue strength at N cycles | N次循环的中位疲劳强度 |
An estimate of the stress level at which 50% of the population would survive N cycles. The estimate is derived from a particular point of the fatigue life distribution, because there is no test procedure by which a frequency distribution of fatigue strengths at Ncycles can be directly observed. 估计50%的量在N个周期内生存的压力水平。该估计值来自疲劳寿命分布的一个特定点，因为没有试验程序可以直接观察N次循环疲劳强度的频率分布。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Angle of attack (α) | 攻角（α） |
(Unit °) The angle between a reference line on a lifting body and the vector direction of the relative velocity between the body and the fluid through which it is moving. In the case of an aerofoil, turbine, or compressor blade, the usual reference line is the chord line. （单位°）升力体上的参考线与升力体与其运动通过的流体之间的相对速度的矢量方向之间的角度。在机翼、涡轮或压缩机叶片的情况下，通常的参考线是弦线。 |
| Tera (T) | 特拉（T） |
An SI unit prefix indicating a multiplier of 1012; thus terawatt (TW) is a unit of power equal to one trillion watts. 指示乘数1012的SI单位前缀；因此，太瓦（TW）是等于1万亿瓦的功率单位。 |
| Dislocation density | 位错密度 |
The total length of dislocation lines per unit volume, or the number of dislocation lines that cut through a unit cross-sectional area. 每单位体积的位错线的总长度，或穿过单位横截面积的位错线的数量。 |
| Fitted bolt | 装配螺栓 |
A bolt with a plain unthreaded portion immediately beneath the head. 一种螺栓，其头部正下方有一个普通的无螺纹部分。 |
| Specific heat capacity | 比热容 |
The heat necessary to raise the temperature of 1 kg of a substance by 1 K. It is measured in J/(kg K). 将1千克物质的温度升高1K所需的热量。单位为J/（kg K）。 |
| Torque converter | 变矩器 |
A turbomachine used for torque amplification consisting of an impeller, a turbine, and a reaction member. Applications include motor-vehicle transmissions. 用于扭矩放大的涡轮机，由叶轮、涡轮机和反作用构件组成。应用包括机动车变速器。 |
| Anisotropy | 各向异性 |
The characteristic of exhibiting different values of a property in different directions with respect to a fixed reference system in the material. 相对于材料中的固定参考系统，在不同方向上表现出不同属性值的特性。 |
| Damage tolerance | 损伤容限 |
(defect tolerance) A design philosophy that takes into account initial imperfections, crack-growth rates and conditions at final fracture, and uses fracture mechanics to demonstrate that cracks should not grow to their critical length within the design life (or at least should be capable of ready detection). （缺陷公差）考虑初始缺陷、裂纹扩展速率和最终断裂条件的设计理念，并使用断裂力学证明裂纹不应在设计寿命内增长到其临界长度（或至少应能够随时检测）。 |
| Sinter (sintering) | 烧结 |
A solid-state diffusion densification process for the production of objects, particularly porous objects, from raw material in powder, granular, mesh, perforatedsheet, or fibre form by heating to a temperature below the melting point until the constituents bond together. It is used for ceramic materials and metals. Applications of sintered materials include filtration, separation, flow control, fluidization, and noise reduction. The bonding of adjacent surfaces in a mass of particles by molecular or atomic attraction on heating at high temperatures below the melting temperature of any constituent in the material. Sintering strengthens a powder mass and normally produces densification and, in powdered metals, recrystallization. 一种固态扩散致密化工艺，用于从粉末、粒状、网状、穿孔片或纤维形式的原材料中生产物体，尤其是多孔物体，方法是加热至低于熔点的温度，直到成分结合在一起。它用于陶瓷材料和金属。烧结材料的应用包括过滤、分离、流量控制、流化和降噪。在低于材料中任何成分熔化温度的高温下加热时，通过分子或原子引力将大量颗粒的相邻表面结合起来。烧结增强了粉末质量，通常会产生致密化，在粉末金属中还会产生再结晶。 |
| Pin expansion test | 插头膨胀试验 |
A test for determining the ability of a tube to be expanded or for revealing the presence of cracks or other longitudinal weaknesses in it, made by forcing a tapered pin into the open end of the tube, similar to flare test. 通过将锥形销压入管道开口端来确定管道膨胀能力或揭示其存在裂纹或其他纵向缺陷的试验，类似于扩口试验。 |
| Typical basis | 典型基础 |
The typical property value is an average value. No statistical assurance is associated with this basis. 典型的属性值是平均值。没有与此基础相关的统计保证。 |
| Shear lip | 剪切唇 |
A narrow, slanting ridge along the edge of a fracture surface. The term sometimes also denotes a narrow, often crescent-shaped, fibrous region at the edge of a fracture that is otherwise of the cleavage type, even though this fibrous region is in the same plane as the rest of the fracture surface. 沿断裂面边缘的狭窄倾斜脊。该术语有时还表示断裂边缘处的狭窄、通常为新月形的纤维区域，否则为解理型，即使该纤维区域与断裂表面的其余部分位于同一平面内。 |
| Cone pulley | 锥轮 |
A stepped pulley having several diameters which, when linked by a laterallymoveable transmission belt to a corresponding pulley, gives a series of speed ratios. 具有多种直径的阶梯式皮带轮，当通过可横向移动的传动带连接到相应的皮带轮时，会产生一系列速比。 |
| Lead screw | 丝杠 |
The master screw running along the length of the bed of a lathe from which all screws threads on that machine are cut. Master screw used for cutting a screw thread in a lathe. 沿车床床身长度方向运行的主螺钉，该机床上的所有螺钉和螺纹都从主螺钉上切割下来。用于在车床上切削螺纹的主螺钉。 |
| Steady pin | 定位销 |
A dowel, key, or pin that prevents a pulley from turning on its shaft. 防止滑轮在其轴上转动的销钉、键或销。 |
| Spray quenching | 喷雾淬火 |
A quenching process using spray nozzles to spray water or other liquids on a part. The quench rate is controlled by the velocity and volume of liquid per unit area per unit of time of impingement. 使用喷嘴将水或其他液体喷射到零件上的淬火过程。淬火速率由每单位撞击时间内每单位面积的液体速度和体积控制。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Collar | 圈、箍 |
A ring secured to, or integral with, a shaft to give axial location. 固定在轴上或与轴成一体以提供轴向位置的环。 |
| Sampling | 抽样 |
The process of measuring a series of values of a time-varying quantity. 测量一系列时变量值的过程。 |
| Clearance | 间距 |
(Unit m or μm) 1. The distance (if any) between mating components in an assembly. 2. The distance between two moving parts, or a moving part and stationary part, in a machine (e.g. the gap between a piston and a cylinder head). 3. With threads, the major clearance is the distance between the design form at the root of an internal thread and the crest of its mating external thread; the minor clearance is the corresponding dimension between the crest of an internal thread and the root of the external thread. （单位m或μm）1.装配体中配合组件之间的距离（如果有）。2.机器中两个运动部件之间的距离，或运动部件和静止部件之间的距离（例如活塞和气缸盖之间的间隙）。3.带螺纹时，主要间隙是内螺纹根部的设计形状与其配合的外螺纹牙顶之间的距离；小间隙是内螺纹牙顶和外螺纹牙根之间的对应尺寸。 |
| Radial load (Unit N) | 径向负荷（单位：N） |
1. Centrifugal loading induced in a rotating body. 2. (through-wallthickness load) The radial component of loading arising from internal or external pressurization of a closed vessel. There will also be axial and hoop loading. 1.旋转体中产生的离心载荷。2.（贯穿壁厚载荷）由封闭容器的内部或外部加压产生的载荷的径向分量。还存在轴向和环向载荷。 |
| Fatigue | 疲劳 |
The phenomenon leading to fracture under repeated or fluctuating stresses having a maximum value less than the ultimate tensile strength of the material. Fatigue failure generally occurs at loads that, applied statically, would produce little perceptible effect. Fatigue fractures are progressive, beginning as minute cracks that grow under the action of the fluctuating stress. A term referring, in components and structures subjected to either random or cyclic periodically-varying loads, to a progressive reduction in strength leading to failure at stresses lower than those that cause failure under monotonic loading. Variable loads arise from outof-balance machinery and other vibration sources, wind gusts, etc., and a large proportion of service failures is caused by fatigue. Fatigue results from the initiation and slow propagation of cracks. In manufactured components, crack initiation usually occurs at a point of stress concentration. After a period, often of millions of stress cycles, the crack reaches a critical length at which the next peak load causes sudden brittle or ductile fracture. Fracture surfaces resulting from fatigue display characteristic striations or progression marks emanating from the crack initiation site during the slow crack growth period, with a different surface appearance for the final fracture. 在最大值小于材料极限抗拉强度的重复或波动应力下导致断裂的现象。疲劳失效通常发生在静态施加的载荷下，不会产生明显影响。疲劳断裂是渐进性的，从在波动应力作用下生长的微小裂纹开始。在承受随机或周期性变化载荷的部件和结构中，指强度逐渐降低，导致在低于单调载荷下导致失效的应力下发生失效的术语。可变负载由失衡的机械和其他振动源、阵风等引起，大部分故障是由疲劳引起的。疲劳是裂纹萌生和缓慢扩展的结果。在制造部件中，裂纹萌生通常发生在应力集中点。在一段时间（通常是数百万次应力循环）后，裂纹达到临界长度，此时下一个峰值载荷会导致突然脆性或韧性断裂。疲劳产生的断裂表面在缓慢裂纹扩展期间显示出从裂纹萌生部位发出的特征条纹或进展标记，最终断裂的表面外观不同。 |
| DTI | DTI |
Direct tension indicator. A fastener used primarily in the structural steel industry, designed to indicate that a certain minimum amount of tension has been developed in the fastener during assembly. 直接张力指示器。一种主要用于结构钢行业的紧固件，旨在表明在装配过程中紧固件中产生了一定的最小张力。 |
| Cold treatment | 冷处理 |
Treatment carried out after quenching to transform retained austenite into martensite, involving cooling and holding at a temperature below ambient. 淬火后进行的处理，以将残余奥氏体转变为马氏体，包括冷却和保持在低于环境温度的温度。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Abrasive wear | 磨料磨损 |
The removal or displacement of material from a surface when hard particles slide or roll across the surface under pressure. The particles may be loose or may be part of another surface in contact with the surface being worn. Contrast with adhesive wear. 当硬质颗粒在压力下在表面上滑动或滚动时，材料从表面上的去除或位移。颗粒可能是松散的或可能是与被磨损表面接触的另一个表面的一部分。与粘着磨损形成对比。 |
| Slug wrench | 缓动扳手 |
A box wrench with an anvil on the end of the handle. Torque is produced by striking the anvil with a sledge hammer. 柄端有铁砧的套筒扳手。扭矩是通过用大锤敲击铁砧产生的。 |
| Quarter hard | （1/4H）低硬（回火） |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength aboutmidway between that of dead soft and half hard tempers. 非铁合金和某些铁合金的一种回火，其特点是抗拉强度介于软态和半硬态之间。 |
| Crankshaft | 曲轴 |
The main shaft, of which the cranks are a part, of a reciprocating single-or multi-cylinder machine. Crankshafts may be built up in sections or forged as a single component. In an engine, the reciprocating motion of the pistons transmits power to the crankshaft and causes it to rotate, whereas in a pump the crankshaft is driven and its rotation causes the pistons to reciprocate. 曲柄是往复式单缸或多缸机器主轴的一部分。曲轴可以分段组装或作为单个部件锻造。在发动机中，活塞的往复运动将动力传递给曲轴并使其旋转，而在泵中，曲轴被驱动，其旋转使活塞往复运动。 |
| Cycle annealing | 循环退火 |
An annealing process employing a predetermined and closely controlled time-temperature cycle to produce specific properties or microstructures. 采用预定且严格控制的时间-温度循环来产生特定性能或微观结构的退火工艺。 |
| Screw machine | 螺丝机 |
A machine tool for high-volume manufacture of small turned components from rod or bar. 一种用棒或棒大批量制造小零件的机床。 |
| Condenser vacuum | 冷凝器真空 |
The sub-atmospheric pressure imposed on the condenser of a steam-power plant which leads to an appreciable increase in overall efficiency. 施加在蒸汽发电厂冷凝器上的低于大气压的压力导致整体效率显着提高。 |
| Slip | 滑落 |
Plastic deformation by the irreversible shear displacement (translation)of one part of a crystal relative to another in a definite crystallographic direction and usually on a specific crystallographic plane. Sometimes called glide. 晶体的一部分在一定的晶体学方向上相对于另一部分的不可逆剪切位移（平移）引起的塑性变形，通常在特定的晶体主义平面上。有时被称为滑翔。 |
| Grip length | 夹紧长度 |
Combined thickness of all the things clamped together by the bolt and nut, including washers, gaskets, and joint members. 由螺栓和螺母夹紧在一起的所有部件的总厚度，包括垫圈、垫圈和接头构件。 |
| Impact | 撞击 |
Sudden loading of a body or component, as in a vehicle collision or striking by a hammer. 物体或部件的突然加载，如车辆碰撞或锤击。 |
| Bolt gage | 螺栓量规 |
An ultrasonic instrument used to measure the stress or strain in bolts. 用于测量螺栓应力或应变的超声波仪器。 |
| Stud | 螺柱 |
A rod having thread on both ends. A headless threaded fastener, threaded on both ends, with an unthreaded body in the middle section, or threaded from end to end. Used with two nuts, or with one nut and a tapped hole. A plain cylindrical piece having a threaded portion of suitable length at each end or a continuous thread over the entire length. One end is screwed into a machine or workpiece after which a second part is placed over the stud and held in place by a nut. 两端都有螺纹的杆。无头螺纹紧固件，两端有螺纹，中间部分有无螺纹主体，或从一端到另一端有螺纹。与两个螺母或一个螺母和一个螺纹孔一起使用。一种普通的圆柱形部件，其两端具有适当长度的螺纹部分，或在整个长度上具有连续螺纹。一端拧入机器或工件，然后将第二部分放在螺柱上，并用螺母固定到位。 |
| Critical diameter | 临界直径 |
(D) Diameter of the bar that can be fully hardened with 50% martensite at its center. （D）中心有50%马氏体可完全硬化的棒材直径。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Standardization | 标准化 |
1. National and international agreements for design, manufacture, materials, performance, practices, requirements, strength, etc. which ensure common results wherever an item is made and wherever used. 2. The manufacture of components so that interchangeability of parts during assembly of new, or repair of old, items is possible without ‘fitting’. 1.关于设计、制造、材料、性能、惯例、要求、强度等的国家和国际协议，确保在任何地方制造和使用物品都能产生共同结果。2.部件的制造，以便在装配新部件或维修旧部件时，无需“装配”即可实现部件的互换性。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| Condenser | 冷凝器 |
A heat exchanger in which a substance is changed from its vapour phase to its liquid phase by reducing its temperature to below the saturation temperature. 一种热交换器，通过将物质的温度降低到饱和温度以下，将其从气相变为液相。 |
| ASME | ASME |
The American Society of Mechanical Engineers. 美国机械工程师学会。 |
| Mechanical alloying | 机械合金化 |
Production of alloys from powders by consolidation, e.g. hotpressing or extrusion, followed by hot and/or cold working and final annealing. Materials such as dispersion-strengthened alloys, high-temperature aluminium alloys, and amorphous alloys can be made in this way. 通过固结（例如热压或挤压）从粉末生产合金，然后进行热和/或冷加工和最终退火。用这种方法可以制造弥散强化合金、高温铝合金和非晶合金等材料。 |
| Fin | 翼 |
A thin projecting rib. 一根细长的凸肋。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Grain growth | 晶粒生长 |
An increase in the average size of the grains in polycrystalline metal, usually as a result of heating at elevated temperature. 多晶金属中晶粒平均尺寸的增加，通常是高温加热的结果。 |
| Fatigue striations | 疲劳条纹 |
Parallel lines frequently observed in electron microscope fractographs or fatigue-fracture surfaces. The lines are transverse to the direction of local crack propagation; the distance between successive lines represents the advance of the crack front during the one cycle of stress variation. 在电子显微镜断口图或疲劳断口表面中经常观察到平行线。这些线横向于局部裂纹扩展方向；连续线之间的距离表示在一个应力变化周期内裂纹前沿的前进。 |
| Stiffness | 刚度 |
(1) The ability of a metal or shape to resist elastic deflection.(2) The rate of stress increase with respect to the rate of increase in strain induced in the metal or shape; the greater the stress required to produce a given strain, the stiffer the material is said to be. （1）金属或形状抵抗弹性变形的能力。（2）所述应力增加速率相对于在所述金属或形状中诱导的应变增加速率；产生给定应变所需的应力越大，材料就越硬。 |
| Subcritical annealing | 不完全退火 |
A process anneal performed on ferrous alloys at a temperature below Ac1. 在低于Ac1的温度下对铁合金进行的工艺退火。 |
| Cold die quenching | 冷模淬火 |
A quench utilizing cold, flat, or shaped dies to extract heat from a part. Cold die quenching is slow, expensive, and is limited to smaller parts with large surface areas. 利用冷、平或成型模具从零件中提取热量的淬火。冷模淬火速度慢、成本高，并且仅限于表面积较大的较小零件。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Recrystallization temperature | 再结晶温度 |
The approximate minimum temperature at which complete recrystallization of a cold-worked metal occurs within a specified time. 冷加工金属在规定时间内发生完全再结晶的近似最低温度。 |
| Slip band | 滑带 |
A group of parallel slip lines so closely spaced as to appear as a single line when observed under an optical microscope. 一组平行滑移线，间距如此之近，以至于在光学显微镜下观察时显示为一条直线。 |
| Serrations | 锯齿 |
A row of notches or tooth-like projections on an edge or surface. On an engineering drawing, serrations on the surface of a circular component are shown over about 60° of arc. 边缘或表面上的一排凹口或齿状突起。在工程图纸上，圆形部件表面的锯齿超过约60°的圆弧。 |
| Tap wrench | 螺丝攻扳手 |
A lever with an adjustable square hole at its centre into which is fitted the shank of a tap so that torque can be applied to cut a thread. 一种杠杆，其中心有一个可调节的方孔，丝锥柄安装在该孔中，以便施加扭矩以切断螺纹。 |
| Compressor blades | 压缩机叶片 |
The aerofoil-shaped vanes that form the rotor(s) and stator(s) of an axial-flow compressor. The aerodynamic design is more critical than is the case for turbine blades because there is an increase in pressure across each row of blades. The arrows in the diagram indicate the flow direction relative to the blades. 形成轴流式压缩机的转子和定子的翼型叶片。空气动力学设计比涡轮叶片的情况更为关键，因为每排叶片的压力都会增加。图中的箭头表示相对于叶片的流动方向。 |
| Liquid carburizing | 液体渗碳 |
Surface hardening of steel by immersion into a molten bath consisting of cyanides and other salts. 通过浸入由氰化物和其他盐组成的熔池中对钢进行表面硬化。 |
| Structural analysis | 结构分析 |
The determination of the forces, displacements, stresses, and strains in a given structure. 确定给定结构中的力、位移、应力和应变。 |
| Horizontal batch furnace | 卧式间歇炉 |
A versatile batch-type furnace that can give light or deep case depths, and because the parts are not exposed to air, horizontal batch furnaces can give surfaces almost entirely free of oxides. 一种多功能间歇式炉，可以提供浅或深的外壳深度，并且由于零件不暴露在空气中，卧式间歇式炉可以使表面几乎完全没有氧化物。 |
| Rated flow (Unit m³/s or kg/s) | 额定流量（单位：m³/s或kg/s） |
In a hydraulic system or machine, the volume or mass flow rate a manufacturer specifies for a component as the maximum desirable for it to function as designed. 在液压系统或机器中，制造商为部件指定的体积或质量流量是其按设计运行所需的最大值。 |
| Burning | 燃烧化 |
(1) Permanently damaging a metal or alloy by heating to cause either incipient melting or intergranular oxidation. See overheating, grain-boundary liquation. (2) In grinding, getting the work hot enough to cause discoloration or to change the microstructure by tempering or hardening. （1）通过加热导致初期熔化或晶间氧化而永久损坏金属或合金。参见过热、晶界液化。（2）在磨削过程中，使工件热到足以引起变色或通过回火或硬化改变微观结构。 |
| Effective yield strength | 有效屈服强度 |
An assumed value of uniaxial yield strength that represents the influence of plastic yielding on fracture test parameters. 单轴屈服强度的假设值，代表塑性屈服对断裂试验参数的影响。 |
| Age hardening | 时效硬化 |
Raising the strength and hardness of an alloy by heating a supersaturated solid solution at a relatively low temperature to induce precipitation of a finely dispersed second phase. Also known as aging or precipitation hardening. Hardening by aging, usually after rapid cooling or cold working. 通过在相对较低的温度下加热过饱和固溶体以诱导细分散的第二相沉淀来提高合金的强度和硬度。也称为时效或沉淀硬化。通常在快速冷却或冷加工后。 |
| Pressure gauge | 压力表 |
An instrument used to measure absolute or gauge pressure. The sensing element may be a tube which deflects when pressurized, as in a Bourdon gauge, a bellows as in an aneroid barometer, a piezoelectric crystal, a piezoresistive element, etc. 测量绝对压力或表压的仪器。传感元件可以是加压时会偏转的管，如波登压力表、无液气压计中的波纹管、压电晶体、压阻元件等。 |
| Mechanical energy (Unit J) | 机械能（单位J） |
The sum of kinetic energy and potential energy for an object or a mechanical system, including the energy stored in springs, etc. 物体或机械系统的动能和势能之和，包括储存在弹簧等中的能量。 |
| Positive-displacement compressor | 容积式压缩机 |
Any type of compressor, including piston and rotary-screw types, that delivers a fixed volume of gas at high pressure per unit time. A positive-displacement pump delivers a fixed volume of fluid, usually a liquid, per unit time. 任何类型的压缩机，包括活塞式和旋转螺杆式，在单位时间内以高压输送固定体积的气体。容积泵每单位时间输送固定体积的流体，通常为液体。 |
| Brayton cycle | 布雷顿循环 |
(Joule cycle) An air standard cycle that is the ideal cycle for a gasturbine engine. As shown on the diagram of pressure (p) ʋs specific volume (ʋ), it consists of four internally reversible processes: isentropic compression in a compressor (1–2), isobaric heat addition in a combustor (2–3), isentropic expansion in a turbine (3–4) and isobaric heat rejection. The cycle can be extended to include regeneration, reheating, and intercooling. （焦耳循环）一种空气标准循环，是燃气轮机发动机的理想循环。循环可以扩展到包括再生、再热和中冷。 |
| Gasket m-factor | 垫片m系数 |
For a gasketed joint of area A in which the clamping force is F, the factor m is defined by F ≥ mpA where p is the pressure that would separate the two halves of the joint and m > 1. 对于面积为A且夹紧力为F的垫片接头，系数m由F≥mpA定义，其中p是分离接头两半的压力，m>1。 |
| Infinite life diagram | 无限疲劳寿命图 |
A simple plot experimentally derived fatigue-life data, showing the conditions required for infinite life. 一个简单的曲线图，实验得出的疲劳寿命数据，显示了无限寿命所需的条件。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Wheel | 轮 |
A solid disc, or a circular ring with spokes radiating from a central hub, either attached to an axle around which it revolves or which revolves with a rotating axle. 一个实心圆盘，或一个带有辐条的圆环，辐条从一个中心毂放射出来，或附在一个绕其旋转的轴上，或与一个旋转轴一起旋转。 |
| Major diameter | 螺纹大径 |
On a straight thread, the diameter of the imaginary cylinder that just touches the crest of an external thread or the root of an internal thread. 在直螺纹上，仅接触外螺纹顶部或内螺纹根部的假想圆柱体的直径。 |
| Dynamic coupling | 动态耦合 |
In vibrations, the existence of inertial terms depending on mass in the governing equations, so that there is only a force if there is a corresponding acceleration. 在振动中，惯性项的存在取决于控制方程中的质量，因此只有当有相应的加速度时才有力。 |
| Silky fracture | 丝状断口 |
A metal fracture in which the broken metal surface has a fine texture, usually dull in appearance. Characteristic of tough and strong metals. 一种金属断裂，断裂的金属表面具有精细的纹理，通常外观暗淡。具有坚韧和坚固金属的特征。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Granular fracture | 粒状断裂 |
A type of irregular surface produced when metal is broken that is characterized by a rough, grainlike appearance, rather than a smooth or fibrous one. It can be subclassified as transgranular or intergranular. 金属破碎时产生的一种不规则表面，其特征是粗糙的颗粒状外观，而不是光滑或纤维状的外观。它可以细分为穿晶或晶间。 |
| Maximum-and-minimum thermometer | 最高和最低温度计 |
(minimum-maximum thermometer, Six’s thermometer) A liquid-in-glass instrument designed to register the maximum and minimum temperatures experienced over a given time period. （最低-最高温度计，Six's温度计）一种液体玻璃仪器，用于记录给定时间段内经历的最高和最低温度。 |
| Rotor | 转子 |
A part of a machine that rotates on a shaft (rotor shaft) about its own axis, such as the blade-carrying discs of a turbine, the blades of a helicopter, or the rotating parts of a Roots blower. 绕轴（转子轴）绕其自身轴线旋转的机器部件，如涡轮叶片、直升机叶片或罗茨鼓风机的旋转部件。 |
| Blueing | 发蓝 |
Application of blue dye (‘engineers’ blue’) to identify high spots on surfaces in contact, or for marking out. 应用蓝色染料（“工程师蓝”）来识别接触表面上的高点，或用于标记。 |
| Shear fracture | 剪切断裂 |
A ductile fracture in which a crystal (or a polycrystalline mass)has separated by sliding or tearing under the action of shear stresses. Contrast with cleavage fracture. 在剪切应力作用下，晶体（或多晶块）通过滑动或撕裂而分离的韧性断裂。与解理断裂形成对比。 |
| Laser sintering | 激光烧结 |
A manufacturing technique by which parts are built layer by layer (each typically 20 μm thick) from plastic or metal (Direct Metal Laser Sintering, DMLS) material in powder form, each layer being sintered by a scanning laser. 一种制造技术，通过这种制造技术，零件由粉末形式的塑料或金属（直接金属激光烧结，DMLS）材料逐层（每个厚度通常为 20 微米）构建，每一层都由扫描激光烧结。 |
| Calorizing | 热化 |
Imparting resistance to oxidation to an iron or steel surface by heating in aluminum powder at 800 to 1000 °C (1470 to 1830 °F). 通过在800至1000°C（1470至1830°F）下加热铝粉，赋予铁或钢表面抗氧化性。 |
| Hot hardness | 热硬度 |
The hardness of materials at high temperatures, often used to rank the performance of cutting tools. 材料在高温下的硬度，常用来对刀具的性能进行排名。 |
| Artificial aging | 人工时效 |
Aging above room temperature. 在室温以上的时效。 |