| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Serrations | 锯齿 |
A row of notches or tooth-like projections on an edge or surface. On an engineering drawing, serrations on the surface of a circular component are shown over about 60° of arc. 边缘或表面上的一排凹口或齿状突起。在工程图纸上，圆形部件表面的锯齿超过约60°的圆弧。 |
| Clamping force | 夹紧力 |
The equal and opposite forces which exist at the interface between two joint members. The clamping force is created by tightening the bolts, but is not always equal to the combined tension in the bolts. Hole interference problems, for example, can create a difference between clamping force and bolt loads. 存在于两个连接构件之间的界面处的相等和相反的力。夹紧力是通过拧紧螺栓产生的，但并不总是等于螺栓中的组合张力。例如，孔干涉问题可能会在夹紧力和螺栓载荷之间产生差异。 |
| Crack-growth rate | 裂纹增长速度 |
Rate of propagation of a crack through a material due to statically or dynamically applied load. 由于静态或动态施加的载荷，裂纹在材料中的扩展速率。 |
| Pressure tap | 测压口 |
A small hole in the wall of a pipe or pressure vessel to which is attached a tube, the other end of which is connected to one side of a pressure transducer. 管子或压力容器壁上的小孔，与管子相连，管子的另一端与压力传感器的一侧相连。 |
| Screw machine | 螺丝机 |
A machine tool for high-volume manufacture of small turned components from rod or bar. 一种用棒或棒大批量制造小零件的机床。 |
| Impact extrusion | 冲击挤压 |
The extrusion of separate components of soft metals whose properties permit the action to be performed quickly. 挤压单独的软金属组件，其特性允许快速执行操作。 |
| Peel strength (Unit N) | 剥离强度（单位：N） |
(peel test) The strength of an adhesive bond between two materials as measured by the force required in a given direction to peel apart adhered strips. This force depends on the dimensions and thickness of the adhered strips and their yield stress, together with the fracture toughness of the bond. （剥离试验）两种材料之间的粘合强度，通过给定方向上剥离粘合条所需的力来测量。该力取决于粘合条的尺寸和厚度及其屈服应力，以及粘合剂的断裂韧性。 |
| Pressure (p) (Unit Pa) | 压力（p）（单位Pa） |
In thermodynamics and fluid mechanics, the compressive force exerted by the fluid per unit area. The pressure exerted by a fluid on a surface acts normal to the surface. 在热力学和流体力学中，每单位面积流体施加的压缩力。流体施加在表面上的压力垂直于表面。 |
| Yield-point elongation | 屈服点延伸 |
During discontinuous yielding, the amount of strain measured from the onset of yielding to the beginning of strain hardening. 在不连续屈服期间，从屈服开始到应变硬化开始测量的应变量。 |
| Shrink fit | 过盈配合 |
A tight interference fit between two components resulting from heating an outer part and/or cooling an inner part to allow easy assembly. The outer component contracts on cooling, while the inner part expands on warming to ambient temperature, thus gripping the two parts together. 由于加热外部部件和/或冷却内部部件而导致的两个部件之间的紧密过盈配合，以便于组装。外部部件在冷却时收缩，而内部部件在加热到环境温度时膨胀，从而将两个部件夹在一起。 |
| Hot pressing | 热压 |
1. Sintering of metal or ceramic powder at high temperature. 2. Formation of components from fibre-reinforced composite material in which bonding is ensured through application of pressure and temperature, often against a mould to give the required shape. 1、金属或陶瓷粉末的高温烧结。2. 由纤维增强复合材料形成部件，其中通过施加压力和温度来确保粘合，通常靠在模具上以形成所需的形状。 |
| Materials selection | 材料选择 |
The process of selecting the most suitable material for a particular application. In the case of solid materials, it involves assessment of candidate materials in terms of their physical properties (density, elastic moduli, fracture toughness, yield strength, hardness, fatigue resistance, coefficient of thermal expansion, thermal conductivity, resistance to thermal shock, creep resistance, corrosion resistance, radiation resistance, etc), and such factors as the function of the final product, its shape, method of manufacture, required tolerances, number to be made, ease of inspection and quality control, cost, and design methodology employed. 为特定应用选择最合适材料的过程。对于固体材料，它涉及根据其物理特性（密度、弹性模量、断裂韧性、屈服强度、硬度、抗疲劳性、热膨胀系数、导热系数、抗热冲击性、抗蠕变性、耐腐蚀性、抗辐射性等）评估候选材料，以及诸如最终产品的功能、其形状、制造方法、所需公差、制造数量、检查和质量控制的容易程度、成本和采用的设计方法等因素。 |
| Die | 模具 |
1. A tool having an appropriately-shaped hole through which material may be extruded or drawn. 2. A tool employed in forging. 3. A block having the male or female shape employed in stamping operations. 4. A thick circular disc, driven by a die wrench, with internally-threaded cutting edges for producing a screw thread. A die wrench (die stock) holds a screw-cutting die and has two projecting arms for applying the torque necessary to cut the thread. A die having a hexagonal or square shape (die nut), driven by a spanner, is used in confined spaces where a die wrench cannot be rotated through a full circle. 1.一种具有适当形状的孔的工具，通过该孔可以挤压或拉伸材料。2.一种用于锻造的工具。3.一种用于冲压操作的具有阳或阴形状的块体。4.一种由模具扳手驱动的厚圆盘，具有用于产生螺纹的内螺纹切削刃。冲模扳手（冲模）装有一个螺旋切割模，并有两个突出臂，用于施加切割螺纹所需的扭矩。由扳手驱动的六边形或方形模具（模具螺母）用于模具扳手无法旋转一整圈的受限空间。 |
| Mechanical vibration | 机械振动 |
The motion of a particle or body which oscillates about a position of equilibrium. 围绕平衡位置摆动的粒子或物体的运动。 |
| Celsius | 摄氏度 |
The temperature scale based on the freezing point of water (0ºC) and the boiling point of water (100ºC). The interval between these points is divided into 100 degrees. The scale was devised by Anders Celsius. 基于水的冰点（0ºC）和水的沸点（100ºC）的温标。这些点之间的间隔被划分为100度。这个比例是由安德斯·摄氏设计的。 |
| Design pressure (Unit Pa) | 设计压力（单位Pa） |
The greatest pressure that a closed container is expected to experience under normal operating conditions. 密闭容器在正常操作条件下预期承受的最大压力。 |
| Extra hard | 额外硬化 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about one-third of the way from full hard to extra spring temper. 有色合金和一些铁合金的回火，其特征是抗拉强度和硬度大约是从完全硬回火到额外弹簧回火的三分之一。 |
| Crushing strain | 压应变 |
The supposed single strain that results in comminution of a brittle material. The corresponding stress is termed the crushing strength. Neither quantity can be a material constant as they must obey the laws of fracture mechanics and will depend on the type of testpiece, method of loading etc. 导致脆性材料粉碎的假定单应变。相应的应力称为抗压强度。这两个量都不能是材料常数，因为它们必须遵守断裂力学定律，并取决于试件类型、加载方法等。 |
| Tare weight (Unit N) | 皮重（单位N） |
The weight of an empty container. 空容器的重量。 |
| Centrifugal | 离心式 |
Acting or moving in a direction away from the axis of rotation of a rotating body. 沿远离旋转体的旋转轴的方向作用或移动。 |
| Impact test | 碰撞测试 |
A test for determining the energy absorbed in fracturing a test piece at high velocity, as distinct from static test. The test may be carried out in tension, bending, or torsion, and the test bar may be notched or unnotched. 测定试件在高速下破裂时吸收的能量的试验，与静态试验不同。测试可以在拉伸、弯曲或扭转条件下进行，测试杆可以有缺口或无缺口。 |
| Intergranular cracking | 沿晶断裂 |
Cracking or fracturing that occurs between the grains or crystals in a polycrystalline aggregate. Also called intercrystalline cracking. 多晶聚集体中的晶粒或晶体之间发生的开裂或断裂。也称为晶间断裂。 |
| Band clutch | 带式离合器 |
A friction clutch in which drive is achieved by a band contracting on to the rim of the clutch. 一种摩擦离合器，其驱动是通过一条带在离合器边缘上收缩来实现的。 |
| Compression | 压缩 |
1. Loading, the principal effect of which is to squeeze and shorten a component or testpiece. 2. The reduction in volume and increase in density of a substance as a consequence of increased pressure. 1.加载，其主要作用是挤压和缩短部件或试件。2.压力增加导致物质体积减少和密度增加。 |
| Shoulder joint | 轴肩关节 |
The second joint on an articulated robot, which has a horizontal axis and is analogous to the human shoulder. 关节机器人上的第二个关节，具有水平轴，类似于人的肩膀。 |
| Adhesive wear | 粘着磨损 |
Wear that develops when two surfaces slide across one another under pressure. The removal or displacement of material from a surface by the welding together and subsequent shearing of minute areas of two surfaces that slide across each other under pressure. In advanced stages, may lead to galling. Contrast with abrasive wear. 当两个表面在压力下相互滑动时产生的磨损。通过焊接在一起并随后剪切在压力下相互滑动的两个表面的微小区域，从表面去除或置换材料。在晚期，可能会导致擦伤。与磨料磨损形成对比。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Pop rivet | 拉钉 |
A hollow rivet that enables a connexion to be made from one side only of an assembly. 一种空心铆钉，使连接只能从组件的一侧进行。 |
| Stress cycle | 应力循环 |
The smallest segment of the stress-time function that is repeated periodically. 周期性重复的应力时间函数的最小段。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Universal joint (Hooke’s joint) | 万向节（胡克接头） |
A double-pivoted connection that allows power and torque to be transmitted between two shafts at an angle to each other. For constant driving angular velocity of the input yoke, the angular velocity of the output yoke fluctuates by amounts depending on the angle of intersection of the shafts. Speeds of the driving and driven shafts may be made identical (giving a constant-velocity joint) when an intermediate shaft, at each end of which there is a universal joint, is interposed. The driving and driven shafts must be equally inclined to the intermediate shaft, the two forks of which must lie in the same plane. 一种双枢轴连接，允许动力和扭矩以一定角度在两个轴之间传递。对于输入磁轭的恒定驱动角速度，输出磁轭的角速度根据轴的相交角度波动。当插入中间轴时，驱动轴和从动轴的速度可以相同（提供恒定速度接头），中间轴的两端都有万向节。主动轴和从动轴必须与中间轴倾斜相等，中间轴的两个叉必须位于同一平面内。 |
| Coefficient of discharge (CD) | 流量系数（CD） |
For flow through a nozzle or orifice plate, the ratio of the actual mass flow rate to the theoretical mass flow rate calculated assuming the flow to be isentropic. The coefficient of velocity (velocity coefficient) is the corresponding ratio of the actual average velocity to the theoretical value. For incompressible flow, the theoretical flow rate and velocity can be calculated using Bernoulli’s equation. 对于通过喷嘴或孔板的流量，实际质量流量与假设流量为等熵计算的理论质量流量之比。速度系数（速度系数）是实际平均速度与理论值的对应比。对于不可压缩流，可以使用伯努利方程计算理论流量和速度。 |
| Wing nut | 蝶形螺母 |
A nut having two opposite protruding wings to permit hand tightening. 一种螺母，有两个相对突出的翼片，可以用手拧紧。 |
| Steady loads | 稳定负载 |
Loads that do not change in intensity or that change so slowly they may be regarded as steady. 强度不变或变化缓慢的荷载可视为稳定荷载。 |
| Precipitation hardening | 沉淀硬化 |
Hardening caused by the precipitation of a constituent from a supersaturated solid solution. 因成分从过饱和固溶体沉淀而导致的硬化。 |
| Finishing temperature | 终轧温度 |
The temperature at which hot working is completed. 完成热加工的温度。 |
| Standard | 标准 |
(standard specification) A set of specifications for components, machines, materials, or processes intended to achieve uniformity, efficiency, and a specified quality. In the UK, standards issued by the British Standards Institution (BSI) are now generally those of the International Organization for Standardization (ISO). （标准规范）为实现一致性、效率和特定质量而制定的一套组件、机器、材料或工艺规范。在英国，英国标准协会（BSI）发布的标准现在基本上是国际标准化组织（ISO）的标准。 |
| Graphitic carbon | 石墨碳 |
Free carbon in steel or cast iron. 钢或铸铁中的游离碳。 |
| Transition metals | 过渡金属 |
Metallic elements from groups (columns) 3 to 12 of the periodic table. They include important metals such as titanium, vanadium, chromium, manganese, iron, cobalt, zirconium, niobium, molybdenum, tantalum, tungsten, and the noble metals. They have either body-centred cubic, face-centred cubic, or hexagonal close-packed crystal structure at room temperature and have a wide range of mechanical and physical properties. 元素周期表第3组至第12组（列）中的金属元素。它们包括重要的金属，如钛、钒、铬、锰、铁、钴、锆、铌、钼、钽、钨和贵金属。它们在室温下具有体心立方、面心立方或六方密排晶体结构，并具有广泛的机械和物理性能。 |
| Recrystallization annealing | 再结晶退火 |
Annealing cold-worked metal to produce a new grain structure without phase change. 退火冷加工金属以产生新的晶粒结构而不发生相变。 |
| Screw | 螺钉 |
Threaded fastener designed to be used in a tapped or untapped (e.g., wood screw) hole, but not with a nut. A fastener with a screw thread cut or rolled into its cylindrical or conical shank, intended either to cut its own thread (as in a wood screw) or engage in a threaded hole. A self-tapping screw (sheet-metal screw, tapping screw) has a sufficiently hard thread that it cuts an internal thread in thin sheet or a component made of soft material when driven into a hole in the sheet or component. The screw head is the part of a screw used to apply torque to the screw. Common screw-head designs are circular in cross section with a diametral slot or cross, or hexagonal and recessed with a cross or hexagon. A screw thread is one or more continuous helical grooves of uniform section along either the exterior surface (male thread) or the interior surface (female thread) of a cylindrical or conical body. The three-dimensional shape that results when the thread cross section is rotated and axially advanced along an axis is called a helicoid, the angle that the thread makes when projected on to the axis being called the angle of inclination. Threads are employed in fasteners such as bolts, nuts, and screws; location and measuring instruments; in power drives; in some electrical fittings (Edison thread); and on the ends of crankshafts to suppress oil leakage (thrower thread). Parallel threads are formed on cylinders; tapered threads on cones, typically with a taper rate of 1:16. A screw with a righthanded thread appears to move away from the observer when turned clockwise. All standard screws, bolts and nuts have right-hand threads, but left-handed threads are sometimes employed. The axial distance between corresponding points on adjacent threads is called the screw pitch or screw rate and, for a single continuous helical groove (a single-start thread), is the same as the change in axial distance (the lead) between a nut and the head of a bolt during one revolution, the number of thread forms per mm then being the reciprocal of the pitch. For the same screw diameter, coarse threads have fewer threads per mm than fine threads. A multiple-start screw thread (usually coarse, see later) consists of two or more identical threads running simultaneously along its axis so as to provide greater bearing area and greater velocity ratio. The starts are separated by 180° (double start), 120° (triple start), 90° (quadruple start) etc., depending upon the number of threads. Thus, in double-start threads, the lead is twice the pitch; and so on. The axial distance between corresponding points on two adjacent threads in a multiple start thread is called the divided pitch. The position on a screw thread where there is equal distance between the flanks on the solid part of the thread and in the space between the threads is the pitch point, the associated diameter of which is termed the pitch diameter. The basic nomenclature for threads, some of which is common with that for toothed gearing, is shown in the diagrams. A helix formed or cut on a cylindrical surface which may advance along the axis to the right or left. The helix may be single or multiple. 一种螺纹紧固件，设计用于攻丝或未攻丝（如木螺钉）孔，但不与螺母配合使用。其螺纹被切割或卷成圆柱形或锥形柄，用于切割自身螺纹（如木螺钉）或嵌入螺纹孔。自攻螺钉（钣金螺钉、自攻螺钉）具有足够硬的螺纹，当打入薄板或部件中的孔时，它会在薄板或软材料部件中切割内螺纹。螺钉头是螺钉的一部分，用于向螺钉施加扭矩。常见的螺钉头设计为横截面为圆形，带有直径槽或十字，或为六边形，并带有十字或六边形凹槽。螺纹是沿圆柱形或锥形体的外表面（外螺纹）或内表面（内螺纹）具有均匀截面的一个或多个连续螺旋槽。当螺纹横截面旋转并沿轴轴向前进时产生的三维形状称为螺旋面，螺纹投影到轴上时形成的角度称为倾角。螺纹用于紧固件，如螺栓、螺母和螺钉；定位和测量仪器；在动力驱动中；在一些电气配件中（爱迪生螺纹）；并安装在曲轴端部，以抑制漏油（抛掷器螺纹）。在圆柱体上形成平行螺纹；圆锥上的锥形螺纹，通常具有1:16的锥形率。当顺时针旋转时，具有右手螺纹的螺钉似乎会远离观察者。所有标准螺钉、螺栓和螺母都有右手螺纹，但有时使用左手螺纹。相邻螺纹上对应点之间的轴向距离称为螺距或螺纹率，对于单个连续螺旋槽（单个起始螺纹），与螺母和螺栓头之间的轴向间距（导程）在一周内的变化相同，每mm的螺纹形式数为螺距的倒数。对于相同的螺钉直径，粗螺纹的每毫米螺纹数少于细螺纹。多头螺纹（通常为粗螺纹，见下文）由两个或多个沿其轴线同时延伸的相同螺纹组成，以提供更大的承载面积和更大的速比。根据螺纹的数量，起点之间的间隔为180°（双起点）、120°（三起点）、90°（四起点）等。因此，在双起始螺纹中，导程是螺距的两倍；多起点螺纹中两个相邻螺纹上对应点之间的轴向距离称为分割螺距。螺纹上的位置，即螺纹实体部分的侧面和螺纹之间的空间之间的距离相等，即节点，其相关直径称为节径。图中显示了螺纹的基本术语，其中一些与齿轮传动的基本术语相同。在圆柱面上形成或切割的螺旋线，可沿轴线向右或向左前进。螺旋可以是单个或多个。 |
| Set pressure (Unit Pa) | 设定压力（单位Pa） |
The pressure at which a relief valve or safety valve is set to open, corresponding to the relevant code or standard which applies to the pressure vessel being protected. 安全阀或安全阀开启时的压力，对应于适用于受保护压力容器的相关规范或标准。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Bearing test | 轴承测试 |
A method of determining the response to stress (load) of metal products that are subjected to riveting, bolting, or a similar fastening procedure. The purpose of the test is to determine the bearing strength of the material and to measure the bearing stress versus the deformation of the hole created by a pin or rod of circular cross section that pierces the sheet perpendicular to the surface. 一种确定经受铆接、螺栓连接或类似紧固程序的金属产品对应力（载荷）的响应的方法。测试的目的是确定材料的承载强度，并测量承载应力与由垂直于表面刺穿板材的圆形横截面的销或杆产生的孔的变形。 |
| Drift pin | 冲头 |
A round tapered steel pin used to align rivet holes so that the rivet will pass through the holes easily. 用于对齐铆钉孔的圆形锥形钢销，以便铆钉轻松穿过孔。 |
| Dead load (Unit N) | 静载（单位N） |
A load on a component or structure that is steady with time, e.g. the self-weight of a bridge. 部件或结构上随时间稳定的载荷，例如桥梁的自重。 |
| Pitch diameter | 中径 |
For screw threads, the diameter of an imaginary cylinder, the surface of which would pass through the threads at such points that would make the width of the groove and width of the land equal to one half the pitch. 对于螺纹，指一个假想圆柱体的直径，其表面将在使凹槽宽度和焊盘宽度等于螺距一半的点穿过螺纹。 |
| Black annealing | 黑退火 |
Box annealing or pot annealing ferrous alloy sheet, strip, wire to impart a black color to the oxidized surface. 对铁合金板、带、线进行箱式退火或罐式退火，使氧化表面呈黑色。 |
| Batch | 一批 |
A definite quantity of some product or material produced under conditions that are considered uniform. A batch is usually smaller than a lot. 在被认为是均匀的条件下生产的一定数量的某些产品或材料。批次通常小于很多。 |
| Crystalline defects | 结晶缺陷 |
The deviations from a perfect three-dimensional atomic packing that are responsible for much of the structure-sensitive properties of the materials. Crystal defects can be point defects (dislocations) or surface defects (vacancies), line defects (dislocations), or surface defects (grain boundaries). 与完美的三维原子堆积的偏差是造成材料的大部分结构敏感特性的原因。晶体缺陷可以是点缺陷（位错）或表面缺陷（空位）、线缺陷（位错）或表面缺陷（晶界）。 |
| Threading machine | 螺纹机 |
A machine used to cut an external thread on a rod, tube, bolt blank, etc. or an internal thread in a hole, tube, nut blank, etc. 用于切割杆、管、螺栓毛坯等上的外螺纹或孔、管、螺母毛坯等中的内螺纹的机器。 |
| Thread run-out | 螺纹耗尽 |
That portion of the threads which are not cut or rolled full depth, but which provide the transition between full-depth threads and the body or head. Officially called thread washout or vanish, although the term run-out is more popular. (Run-out is officially reserved for rotational eccentricity, as defined by total indicator readings or the like.) 未全深度切割或轧制的螺纹部分，但提供全深度螺纹与主体或头部之间的过渡。官方称之为螺纹冲蚀或消失，但术语“耗尽”更为流行。（跳动是官方为旋转偏心度保留的，由总指示器读数等定义。） |
| Double aging | 双级时效 |
Employment of two different aging treatments to control the type of precipitate formed from a supersaturated matrix in order to obtain the desired properties. The first aging treatment, sometimes referred to as intermediate or stabilizing, is usually carried out at higher temperature than the second. 采用两种不同的时效处理来控制由过饱和基质形成的沉淀物类型，以获得所需的性能。第一次时效处理，有时称为中间处理或稳定处理，通常在比第二次更高的温度下进行。 |
| Square thread | 方螺纹 |
A form of screw thread in which the cross–section of the thread forms a square, making the width of the thread equal to the space between the threads. 螺纹的一种形式，螺纹的横截面形成正方形，使螺纹的宽度等于螺纹之间的间距。 |
| Transformation toughening | 相变增韧 |
The improvement of fracture toughness of a material by stress-induced transformation of the microstructure. 通过微结构的应力诱导转变来提高材料的断裂韧性。 |
| Load and resistance factor design | 负载和阻力系数设计 |
A design procedure developed for the AISC by the Research Council on Structural Connections. Assigns uncertainties in the strength of (i.e., resistance of) and in the service loads to be placed on a shear joint to estimate the probable strength of the joint. It is a recently defined alternative to the Allowable stress design procedure. 结构连接研究委员会为AISC制定的设计程序。分配剪切接头的强度（即阻力）和工作荷载的不确定性，以估计接头的可能强度。它是最近定义的容许应力设计程序的替代方案。 |
| Resistance factor | 阻力系数 |
Probabilistic factor representing the uncertainties in the designer’s estimate of the strength of a shear joint. Used in Load and resistance factor design. 概率系数，表示设计人员对剪切接头强度估计的不确定性。用于载荷和阻力系数设计。 |
| Compression ratio | 压缩率 |
The volume of a combustion chamber with the piston at the top of its stroke as a proportion of the total volume of the cylinder with the piston at the bottom of its stroke. For a piston engine, if the swept volume is SW and the clearance volume is CL, the compression ratio is given by ( SW + CL)/CL, i.e. it is a volume ratio rather than a pressure ratio. 活塞位于其冲程顶部的燃烧室的容积与活塞位于其冲程底部的气缸总体积的比例。对于活塞发动机，如果扫气量为SW，间隙容积为CL，则压缩比由(SW+CL)/CL给出，即它是体积比而不是压力比。 |
| Achme thread | Achme螺纹 |
A screw thread having an included angle of 29° and largely used for feed screws on machine tools. 一种夹角为29°的螺纹，主要用于机床上的进给丝杠。 |
| Mohs scale | 莫氏硬度 |
A scale of scratch hardness originally developed for minerals. 最初为矿物开发的划痕硬度标尺。 |
| Yield strength | 屈服强度 |
That stress level which will create a permanent deformation of 0.2% or 0.5% or some other small, preselected, amount in a body. Approximately equal to the elastic and proportional limits of the material; a little higher than the proof strength of a bolt. The stress at which a material exhibits a specified deviation from proportionality of stress and strain. An offset of 0.2% is used for many metals. 该应力水平将在物体中产生0.2%或0.5%的永久变形，或其他一些小的、预先选定的量。近似等于材料的弹性和比例极限；略高于螺栓的强度。材料表现出与应力和应变比例的特定偏差的应力。许多金属使用0.2%的偏移量。 |
| Curie temperature | 居里温度 |
The temperature of magnetic transformation below which a metal or alloy is ferromagnetic and above which it is paramagnetic. 磁性转变温度，低于此温度金属或合金为铁磁性，高于此温度则为顺磁性。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| V-belt | 三角带 |
A drive belt having a trapezoidal cross section which runs in pulleys with V-shaped grooves. Higher torques can be transmitted than with a flat belt. 一种具有梯形横截面的传动带，在带V形槽的皮带轮中运行。与平皮带相比，可以传递更高的扭矩。 |
| Frequency | 频率 |
(temporal frequency, f) (Unit Hz) The number of cycles per second in an oscillation or the repetition rate for a cyclic process. （时间频率，f）（单位Hz）振荡中每秒的周期数或循环过程的重复率。 |
| Stress wave | 应力波 |
An unbalanced force, such as an impact, applied at one location in a body sets the material there into vibration that is transmitted to adjacent elements and ultimately to all parts of the body in the form of stress waves or wave packets. 施加在物体某个位置的不平衡力（如冲击力）会使物体中的材料产生振动，并以应力波或波包的形式传递到相邻元件，最终传递到物体的所有部位。 |
| Hardening | 硬化 |
Increasing hardness by suitable treatment, usually involving heating and cooling. When applicable, the following more specific terms should be used: age hardening, flame hardening, induction hardening, laser hardening, precipitation hardening, and quench hardening. 通过适当的处理增加硬度，通常包括加热和冷却。适用时，应使用以下更具体的术语：时效硬化、火焰硬化、感应硬化、激光硬化、沉淀硬化和淬火硬化。 |
| Rpm (N) | 转速（N） |
An abbreviation for revolutions per minute. It is a widely used non-SI unit for rotational speed. The corresponding angular velocity ω in rad/s is given by πN/30. Rps (revolutions per second) is also used, the angular velocity then being 2πN. 每分钟转数的缩写。它是一种广泛使用的转速非SI单位。相应的角速度ω，单位为rad/s，由πN/30给出。还使用Rps（每秒转数），此时角速度为2πN。 |
| Burning | 燃烧化 |
(1) Permanently damaging a metal or alloy by heating to cause either incipient melting or intergranular oxidation. See overheating, grain-boundary liquation. (2) In grinding, getting the work hot enough to cause discoloration or to change the microstructure by tempering or hardening. （1）通过加热导致初期熔化或晶间氧化而永久损坏金属或合金。参见过热、晶界液化。（2）在磨削过程中，使工件热到足以引起变色或通过回火或硬化改变微观结构。 |
| Safe working load (Unit N) | 安全工作负荷（单位：N） |
The steady or unsteady load against which a component or structure is designed for normal operation. It is lower than that which would cause failure by buckling, fracture, or yielding, so as to accommodate uncertainty, possible fault or accident conditions. 部件或结构设计用于正常运行的稳定或不稳定荷载。该值低于因屈曲、断裂或屈服而导致失效的值，以适应不确定性、可能的故障或事故条件。 |
| Temperature (Unit K or °C) | 温度（单位K或°C） |
A quantitative measure of the molecular kinetic energy of a substance and so how hot or cold it is. 物质分子动能的定量量度，以及它的冷热程度。 |
| Grain size | 晶粒大小 |
A measure of the areas or volumes of grains in a polycrystalline metal, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. For metals, a measure of the areas or volumes of grains in a polycrystalline material, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. Grain sizes are reported in terms of number of grains per unit area or volume, average diameter, or as a grainsize number derived from area measurements. 多晶金属中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。多晶材料中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。晶粒尺寸以每单位面积或体积的晶粒数、平均直径或从面积测量得出的晶粒尺寸数来报告。 |
| Submerged-electrode furnace | 浸入式电极炉 |
A furnace used for liquid carburizing of parts by heating molten salt baths with the use of electrodes submerged in the ceramic lining. 一种通过使用浸入陶瓷衬里中的电极加热熔融盐浴对零件进行液体渗碳的炉。 |
| Total combustion air (Unit kg/s) | 总燃烧空气（单位：kg/s） |
1. The combination of the stoichiometric flow of air required for combustion together with any excess air. 2. The flow of fresh air into a boiler plus any flue gas recirculated. 1.燃烧所需的化学计量空气流与任何过量空气的组合。2.进入锅炉的新鲜空气流加上再循环的任何烟气。 |
| Fog quenching | 雾淬 |
Quenching in a fine vapor or mist. 在细蒸汽或薄雾中淬火。 |
| Net weight (Unit N) | 净重（单位：N） |
The difference between the gross weight of any container including its contents and the tare weight of the empty container. 任何容器（包括其内容物）的毛重与空容器皮重之间的差值。 |
| Impact energy (Unit J) | 冲击能量（单位J） |
The amount of energy required to fracture a material, usually measured by means of an Izod test or Charpy test.The type of specimen and test conditions affect the values and therefore should be specified. 1. The sum of the kinetic energies of all the bodies involved at the instant of collision of two or more moving bodies. 2. The energy required to fracture a specimen in a Charpy or Izod impact test. 使材料断裂所需的能量，通常通过悬臂梁式试验或夏比试验测量。试样类型和试验条件会影响数值，因此应加以说明。1.两个或多个运动物体碰撞瞬间所有物体的动能之和。2.夏比或悬臂冲击试验中断裂试样所需的能量。 |
| Abrasion | 磨损 |
The removal of surface material by the scratching action of hard particles, either deliberately (abrasive papers, abrasive cleaning, abrasive machining) or as a consequence of operation (wear). 通过硬质颗粒的刮擦作用去除表面材料，可以是故意的（砂纸、研磨清洁、研磨加工），也可以是操作的结果（磨损）。 |
| Pitch angle (Unit °) | 俯仰角（单位°） |
For a bevel gear, the angle between the axis and the pitch-cone generator. 对于锥齿轮，轴与节锥生成器之间的角度。 |
| Extensometer | 引伸计 |
An instrument for measuring changes in length over a given gage length caused by application or removal of a force. Commonly used in tension testing of metal specimens. Any instrument which measures the change in length of a part as the part is loaded. 一种用于测量在给定标距上由施加或移除力引起的长度变化，在零件加载时测量零件长度变化的仪器。常用于金属试样的拉力试验。 |
| Sampling frequency (Unit Hz) | 采样频率（单位Hz） |
(sampling rate) The number of measurement samples per unit time taken from a continuous analogue signal to produce a discrete signal. It is the inverse of the time between successive measurements (sampling interval, sampling period, or sampling time). （采样率）从连续模拟信号中提取以产生离散信号的每单位时间的测量样本数。它是连续测量之间时间的倒数（采样间隔、采样周期或采样时间）。 |
| Damage mechanics | 损伤机制 |
The theory of degradation in bodies, particularly fracture by accumulated microstructural damage. Analyses take two approaches: (a) the use of some critical integrated function of stress and strain at which cracking is initiated and propagated; (b) incorporation of damage in the stress–strain curves to reflect weakened material. 物体退化理论，尤其是累积微观结构损伤导致的断裂。分析采用两种方法：（a）使用裂纹开始和扩展时的应力和应变的一些临界积分函数；（b）应力-应变曲线中包含损伤，以反映弱化材料。 |
| Rockwell hardness number (HR) | 洛氏硬度值（HR） |
A number derived from the net increase in the depth of impression in a Rockwell hardness test as the load on an indenter is increased from a fixed minor load to a major load and then returned to the minor load. Rockwell hardness numbers are always quoted with a scale symbol representing the penetrator, load, and dial used. 当压头上的载荷从固定的小载荷增加到大载荷，然后返回到小载荷时，洛氏硬度试验中压痕深度的净增加值。洛氏硬度值总是用刻度符号引用，表示所用的穿透器、载荷和刻度盘。 |
| Counter sink | 台面水槽 |
To cut or shape a depression in an object so that the head of a screw may set flush or below the surface. 在物体上切割或塑造一个凹陷，使螺钉的头部可以齐平或低于表面。 |
| Blank nitriding | 空白渗氮 |
Simulating the nitriding operation without introducing nitrogen. This is usually accomplished by using an inert material in place of the nitriding agent or by applying a suitable protective coating to the ferrous alloy. 在不引入氮气的情况下模拟氮化操作。这通常通过使用惰性材料代替氮化剂或通过在铁合金上施加合适的保护涂层来实现。 |
| Outside diameter (Unit m) | 外径（单位：m） |
(external diameter, OD) The diameter of a circular cylindrical tube or a sphere measured between opposite points on the external surface. （外径，OD）在外表面上的相对点之间测量的圆柱管或球体的直径。 |
| Aerated bath nitriding | 空气搅拌液体渗氮法 |
A type of liquid nitriding in which air is pumped through the molten bath creating agitation and increased chemical activity. 一种液体氮化，其中空气被泵入熔池，产生搅拌并增加化学活性。 |
| Standard deviation (σ) | 标准偏差（σ） |
A statistical term used to quantify the Scatter in a set of data points. If the standard deviation is small, most of the data points are ‘‘nearly equal.’’ A large deviation means less agreement. The most usual measure of the dispersion of observed values or results expressed as the positive square root of the variance. The square root of variance, a measure of the spread of data about the mean value. 用于量化一组数据点中分散度的统计术语。如果标准偏差很小，则大多数数据点“几乎相等”大的偏差意味着更少的一致性。观测值或结果离散度的最常用度量，表示为方差的正平方根。方差的平方根，衡量平均值的数据分布。 |
| Two-phase flow | 两相流 |
A flow in which two phases are present, for example gas bubbles in a liquid, liquid bubbles in another liquid with which it is immiscible, solid particles in a liquid or gas. 两相流动，例如液体中的气泡、与之不混溶的另一种液体中的液体气泡、液体或气体中的固体颗粒。 |
| Ablative materials | 烧蚀材料 |
Materials, especially coating materials, designed to provide thermal protection to a body in a fluid stream through the loss of mass. 材料，尤其是涂层材料，旨在通过质量损失为流体流中的物体提供热保护。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Clearance | 间距 |
(Unit m or μm) 1. The distance (if any) between mating components in an assembly. 2. The distance between two moving parts, or a moving part and stationary part, in a machine (e.g. the gap between a piston and a cylinder head). 3. With threads, the major clearance is the distance between the design form at the root of an internal thread and the crest of its mating external thread; the minor clearance is the corresponding dimension between the crest of an internal thread and the root of the external thread. （单位m或μm）1.装配体中配合组件之间的距离（如果有）。2.机器中两个运动部件之间的距离，或运动部件和静止部件之间的距离（例如活塞和气缸盖之间的间隙）。3.带螺纹时，主要间隙是内螺纹根部的设计形状与其配合的外螺纹牙顶之间的距离；小间隙是内螺纹牙顶和外螺纹牙根之间的对应尺寸。 |
| Newton’s law of gravitation | 牛顿万有引力定律 |
(Newton’s law of universal gravitation) Any two bodies exert a gravitational force of attraction F on each other directed along the line joining their centres of mass, in magnitude proportional to the product of their masses and inversely proportional to the square of the distance r between them. （牛顿万有引力定律）任何两个物体沿其质心连接线相互施加引力F，其大小与其质量乘积成正比，与它们之间距离r的平方成反比。 |
| Air pump | 气泵 |
A machine for providing a flow of air or for increasing or decreasing the mass and pressure of air in a closed container. The term pump is more usual when the working fluid is a liquid, while compressor is more usual for gases. 一种用于提供空气流动或用于增加或减少密闭容器中空气质量和压力的机器。当工作流体是液体时，术语泵更常用，而气体更常用压缩机。 |
| Dew point analyzer | 露点分析仪 |
An atmosphere monitoring device that measures the partial pressure of water vapor in an atmosphere. 一种大气监测装置，用于测量大气中水蒸气的分压。 |
| Concurrent engineering | 并行工程 |
The integration of the procedures for product design, material selection and manufacturing method to include life-cycle analysis. 产品设计、材料选择和制造方法程序的整合，包括生命周期分析。 |
| Size dimension (Unit m) | 尺寸范围（单位：米） |
The specified value of a diameter, length, width, etc. of a feature required to specify the finished form of a component or assembly. 指定部件或组件的成品形状所需的特征的直径、长度、宽度等的指定值。 |
| Cold working | 冷加工 |
The plastic deformation of a metal, by rolling (cold rolling), drawing, forging (cold forging), etc. at a temperature well below its recrystallization temperature, which results not only in permanent shape change but also increase in strength and loss of ductility owing to work-hardening. 金属在远低于其再结晶温度的温度下通过轧制（冷轧）、拉拔、锻造（冷锻）等方式发生塑性变形，这不仅会导致永久的形状变化，还会增加强度并降低延展性由于加工硬化。 |
| End-quench hardenability test | 端淬淬透性试验 |
A laboratory procedure for determining the hardenability of a steel or other ferrous alloy. Hardenability is determined by heating a standard specimen above the upper critical temperature, placing the hot specimen in a fixture so that a stream of cold water impinges on one end, and, after cooling to room temperature is completed, measuring the hardness near the surface of the specimen at regularly spaced intervals along its length. The data are normally plotted as hardness versus distance from the quenched end. 测定钢或其他铁合金淬透性的实验室程序。淬透性是通过将标准试样加热到高于上临界温度，将热试样放置在夹具中，使冷水流冲击一端，并在冷却至室温后，沿试样长度以规则间隔测量试样表面附近的硬度来确定的。数据通常绘制为硬度与距淬火端距离的关系。 |
| Pressure chamber | 压力室 |
A chamber in which components or devices can be subjected to high or low fluid (liquid or gas) pressure. 部件或装置可承受高或低流体（液体或气体）压力的腔室。 |
| Shear test | 剪切试验 |
Any of several tests to obtain shear strength of a metal. Common tests used on mill products include the double-shear test, single-shear test, the blanking shear test (also known as the punching shear test) and the torsion test. 获得金属剪切强度的几种测试中的任何一种。轧机产品上常用的试验包括双剪试验、单剪试验、落料剪切试验（也称为冲切试验）和扭转试验。 |
| Galvanic protection | 电流保护 |
The coating on a fastener is said to provide galvanic protection if it is more anodic than the fastener and will, therefore, be destroyed instead of the fastener. Zinc plate (galvanizing) provides galvanic protection to steel fasteners, for example. 如果紧固件上的涂层比紧固件更具阳极性，则据说它可以提供电流保护，将会因此被破坏而不是紧固。例如，锌板（镀锌）为钢紧固件提供电流保护。 |
| Hydrogen embrittlement | 氢脆 |
A condition of low toughness, low ductility or cracking in metals resulting from the absorption of hydrogen. A common and troublesome form of Stress cracking. Several theories have been proposed to explain hydrogen embrittlement, but, at present, the exact mechanism is still unknown. What is known, however, is the fact that if hydrogen is trapped in a bolt by poor electroplating practices, it can encourage stress cracking. Bolts can fail, suddenly and unexpectedly, under normal loads. Premature crack growth over time under tensile stress leading to unexpected failure in certain metals, caused by small amounts of hydrogen in the microstructure. Hydrogen may enter steels during melting or heat treating, or during processes such as electroplating. 因吸收氢而导致金属韧性低、延展性低或开裂的情况，是一种常见且麻烦的应力开裂形式。在拉伸应力下，裂纹随时间过早扩展，导致某些金属发生意外失效，这是由微观结构中的少量氢引起的。在熔化或热处理过程中，或在电镀等过程中，氢可能进入钢中。已经提出了几种理论来解释氢脆，但目前，确切的机理仍然未知。已知的事实是，如果氢因电镀不当而被困在螺栓中，则会导致应力开裂。在正常载荷下，螺栓可能突然意外失效。 |
| Composite property | 复合属性 |
In thermodynamics, a property defined in terms of the properties of a closed system and its surroundings, such as the non-flow exergy function. 在热力学中，根据封闭系统及其周围环境的性质定义的性质，例如非流动火用函数。 |
| Nanotechnology | 纳米技术 |
The science and engineering of materials that have been structured on length scales of 1–100 nm, resulting in modified physical properties owing to changes in the ratio of surface area to volume (atoms on surfaces having different symmetry from those in the bulk) and because many of the fundamental physical processes that underpin the properties of materials have a characteristic length scale of a few nm, so that alteration of microstructure at the nm level alters the bulk properties. 材料科学与工程，其结构长度为1-100nm，由于表面积与体积之比的变化（表面上的原子与体中的原子具有不同的对称性），并且支撑材料性质的许多基本物理过程具有几纳米的特征长度尺度，因此改变纳米级微观结构会改变体性质。 |
| Tow | 拖拉 |
1. To cause a vehicle to move by pulling with a rope, chain, bar, etc. 2. A bundle of fibres employed in reinforcement. 1.用绳子、链条、钢筋等拉动车辆移动。2.用于加固的纤维束。 |
| Elastic constants | 弹性常数 |
The factors of proportionality that relate elastic displacement of a material to applied forces. 将材料的弹性位移与施加的力相关联的比例因子。 |
| Wrist | 腕关节 |
The final three joints on a robot which simulate rotations provided by the human wrist and thus allow orientation of the end effector to which it is attached by the wrist socket. 机器人上的最后三个关节，模拟人类手腕提供的旋转，从而允许其通过手腕插座连接到的末端执行器的方向。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| Joint diagrams | 接合处关系图 |
Mathematical diagrams which illustrate the forces on and deflections of fasteners and joint members. 说明紧固件和连接件上的力和变形的数学图。 |
| Cavitation-resistance inducer | 抗气蚀诱导剂 |
An axial-flow pump used upstream of a main pump in order to prevent cavitation in the latter by increasing the inlet head. 在主泵上游使用的轴流泵，通过增加进口压头防止主泵出现气穴。 |
| Thermoelectric material | 热电材料 |
A material in which any of the thermoelectric phenomena, such as the Peltier, Seebeck, and Thomson effects, are especially strong. 一种热电现象特别强烈的材料，如珀尔帖效应、塞贝克效应和汤姆森效应。 |
| Wing | 翼 |
A relatively long and thin body with a cross section designed to produce lift when there is motion relative to a fluid. The principal applications are to aircraft and highperformance motor vehicles. 一种相对长而薄的物体，其横截面设计用于在相对于流体运动时产生升力。主要应用于飞机和高性能机动车辆。 |
| Turret lathe | 六角车床 |
A capstan lathe in which the capstan is driven mechanically or hydraulically to provide assigned tool paths to perform a specified sequence of operations in the repetitive production of parts. 一种绞盘车床，其中绞盘由机械或液压驱动，以提供指定的刀具路径，在零件的重复生产中执行指定的操作顺序。 |
| Microindentation hardness test | 显微压痕硬度测试 |
Hardness test using a calibrated machine to force a diamond indenter of specific geometry, under a test load of 1 to 1000 gramforce, into the surface of the test material and to measure the diagonal or diagonals of the indentation optically. 使用校准机器进行硬度试验，以在1至1000克力的试验载荷下，将特定几何形状的金刚石压头压入试验材料表面，并光学测量压痕的对角线。 |
| Dead centre | 止点 |
The point at which, in a crank mechanism, the piston connecting rod and crank are all in line so that there can be no driving moment. 在曲柄机构中，活塞连杆和曲柄都在一条线上，因此不会有驱动力矩。 |
| Artificial aging | 人工时效 |
Aging above room temperature. 在室温以上的时效。 |
| Martensitic stainless steels | 马氏体不锈钢 |
Martensitic stainless steels are hardenable magnetic stainless steels that contain 9–18% chromium, 0.06–1.25% carbon, and typically up to about 2.5% in total of manganese, silicon, nickel, and molybdenum. They can be heat-treated such that martensite is the prime microconstituent, and are usually available in the annealed or quenched-and-tempered condition. They have excellent strength and high hardness, and good corrosion resistance. Uses include cutlery, surgical instruments, rifle barrels, steam turbine tubing and blading, jet engine components, hand tools, machine parts, fasteners, valves, springs, bearings, pump shafts, nozzles, mining equipment, and wear-resistant parts. 马氏体不锈钢是一种可硬化的磁性不锈钢，其铬含量为9-18%，碳含量为0.06-1.25%，锰、硅、镍和钼的总含量通常高达约2.5%。它们可以进行热处理，使马氏体成为主要的微组分，通常可在退火或淬火回火条件下获得。它们具有优异的强度和高硬度，以及良好的耐腐蚀性。用途包括餐具、外科器械、步枪枪管、蒸汽轮机管道和叶片、喷气发动机部件、手动工具、机械零件、紧固件、阀门、弹簧、轴承、泵轴、喷嘴、采矿设备和耐磨零件。 |
| Rockwell superficial hardness test | 洛氏表面硬度试验 |
Same as Rockwell hardness test, except that smaller minor and major loads are used. 与洛氏硬度测试相同，只是使用较小的次要载荷和主要载荷。 |
| Equation, long form | 方程，长格式 |
An equation which relates the torque applied to a bolt to the preload created in it, and involves fastener geometry and the coefficient of friction between mating surfaces. A theoretical equation based on rigid body mechanics and the assumption that the geometry of the fastener is perfectly described by blueprint dimensions. 将施加在螺栓上的扭矩与螺栓中产生的预载荷联系起来的方程，该方程涉及紧固件几何形状和配合面之间的摩擦系数。基于刚体力学和紧固件几何结构由蓝图尺寸完美描述的假设的理论方程。 |
| Elongation measurement | 伸张率测量 |
Bolt elongation is directly proportional to axial stress when the applied stress is within the elastic range of the material. If both ends of a bolt are accessible, a micrometer measurement of bolt length made before and after the application of tension will ensure the required axial stress is applied. 当施加的应力在材料的弹性范围内时，螺栓伸长率与轴向应力成正比。如果螺栓的两端都可以接近，则在施加张力前后对螺栓长度进行测微计测量，以确保施加所需的轴向应力。 |
| Nut | 螺母 |
A metal fastener of square, hexagon or other shape, having an internal thread which screws onto a bolt, stud or arbor. An internally-threaded fastener used with externally-threaded bolts. Usually hexagonal in shape but there is a multitude of other geometries, such as square, for special purposes and different gripping tools. 一种方形、六角形或其他形状的金属紧固件，具有内螺纹，可拧在螺栓、螺柱或心轴上。与外螺纹螺栓一起使用的内螺纹紧固件。通常为六边形，但也有许多其他几何形状，如方形，用于特殊用途和不同的夹持工具。 |
| Sample percentage | 样本百分比 |
The percentage of observed values between two stated values of the variable under consideration. It is a point estimate of the percentage of the population between the same two stated values. 所考虑变量的两个规定值之间的观测值百分比。它是对相同两个规定值之间的总体百分比的点估计。 |
| U-bolt | U型螺栓 |
A rod threaded at both ends and bent into a U-shape. It is used for clamping. An externally threaded fastener bent in the shape of the letter U and with both ends threaded. 两端有螺纹并弯曲成U形的杆。用于夹紧。一种外螺纹紧固件，弯曲成字母U的形状，两端带有螺纹。 |
| Bypass valve | 旁通阀 |
A valve that directs flow through a bypass. 引导流过旁路的阀门。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Heat (q, Q) (Unit J) | 热量（q, Q）（单位J） |
A form of energy that is transferred across the boundary of a system at one temperature to another system (or the surroundings) at a different temperature by virtue of the temperature difference between them. Heat can be identified only as it crosses the boundary. A body can never be said to contain heat which is thus a transient phenomenon. 一种能量形式，由于它们之间的温差在一个温度下通过系统边界传递到另一个温度不同的系统（或环境）。只有当热量穿过边界时才能识别。一个物体不能说永远含有热量，这是一种瞬态现象。 |
| Amplifier | 放大器 |
A device by which the output of a hydraulic, pneumatic, or electrical source is increased. 增加液压、气动或电源输出的装置。 |
| Ultrasonic extensometer | 超声波伸长计 |
An electronic instrument which measures the change in length of a fastener ultrasonically as, or before and after, the fastener is tightened. 一种电子仪器，可在紧固件拧紧时或前后通过超声波测量紧固件长度的变化。 |
| Fatigue failure | 疲劳失效 |
Failure that occurs when a specimen undergoing fatigue completely fractures into two parts or has softened or been otherwise significantly reduced in stiffness by thermal heating or cracking. 当经历疲劳的试样完全断裂成两部分或因热加热或开裂而软化或刚度显着降低时发生的失效。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Guided bend | 导向弯曲 |
The bend obtained by use of a plunger to force the specimen into a die in order to produce the desired contour of the outside and inside surfaces of the specimen. 通过使用柱塞将试样压入模具中获得的弯曲，以产生试样外表面和内表面所需的轮廓。 |
| Cementite | 渗碳体 |
A compound of iron and carbon, known chemically as iron carbide and having the approximate chemical formula Fe3C. It is characterized by an orthorhombic crystal structure. When it occurs as a phase in steel, the chemical composition will be altered by the presence of manganese and other carbide-forming elements. 碳化铁一种铁和碳的化合物，化学上称为碳化铁，化学式近似为Fe3C。其特征在于正交晶体结构。当它在钢中以相形式出现时，锰和其他碳化物形成元素的存在将改变其化学成分。 |
| Vacuum pump | 真空泵 |
A pump for exhausting air and non-condensable gases from a vessel to be maintained at sub-atmospheric pressure. The pirani and thermal-conductivity gauges are vacuum gauges used to measure the absolute pressure within a vacuum system (vacuum level), usually expressed in torr or Pa. 用于从容器中排出空气和不凝性气体以保持在亚大气压的泵。皮拉尼和热导率计是用于测量真空系统内绝对压力（真空水平）的真空计，通常用托或帕表示。 |
| Flange | 法兰 |
Flange refers to a head style for bolts where there is a circular ‘flange’ under the head that acts like a washer to distribute a load. A flange is a projected flat rim or collar. 1. Annular rims at the ends of pipes (flanged pipe) or shafts by which they may be coupled together using bolts that pass through holes in the flanges (flange coupling, flange union), or by toggle clamps around the periphery. 2. An extended rim on a wheel that positions it laterally on a track. Commonly used for railway rolling stock. 3. The top and bottom parts of an I-beam. 法兰是指螺栓的头部样式，其中头部下方有一个圆形“法兰”，其作用类似于垫圈以分配载荷。凸缘是凸出的平轮辋或凸缘。1.管道（法兰管）或轴端部的环形边缘，通过这些边缘，可以使用穿过法兰孔的螺栓（法兰联轴器、法兰接头）或通过周边的肘节夹将管道连接在一起。2.车轮上的延伸轮辋，将其横向定位在轨道上。通常用于铁路车辆。3.工字梁的顶部和底部。 |
| Turbo generator | 涡轮发电机 |
(turboset) The combination of a steam or gas turbine and an electrical generator with a single shaft or connected coaxial shafts. （汽轮发电机组）蒸汽或燃气轮机与发电机的组合，具有单轴或连接的同轴。 |
| Ferritic decarburization | 铁素体脱碳 |
Decarburization with sufficient loss of carbon to cause a lighter shade of tempered martensite and a significantly lower hardness than that of the adjacent base metal, with the presence of ferrite grains or grain boundary network under metallographic examination. 脱碳，碳损失充分，导致回火马氏体颜色较浅，硬度明显低于相邻母材，金相检查时存在铁素体晶粒或晶界网络。 |
| Fracture stress | 断裂应力 |
The true normal stress on the minimum cross-sectional area at the beginning of fracture. This term usually applies to tension tests of unnotched specimens. 断裂开始时最小横截面积上的真实正应力。该术语通常适用于无缺口试样的拉伸试验。 |
| Thermal stresses | 热应力 |
Stresses in metal resulting from nonuniform temperature distribution. 由不均匀温度分布引起的金属应力。 |
| ANSI | ANSI |
The acronym for American National Standards Institute. 美国国家标准协会的缩写。 |
| Scratching | 刮擦 |
In tribology, the mechanical removal or displacement, or both, of material from a surface by the action of abrasive particles or protuberances sliding across the surfaces. 在摩擦学中，通过在表面上滑动的磨粒或突起的作用，材料从表面上的机械移除或移位，或两者兼而有之。 |
| Torricellean barometer | 托里塞莱气压计 |
A vertical glass tube with its upper end sealed and the lower end submerged in a pool of mercury. The space above the mercury is under vacuum. The height to which the mercury rises up the tube is a measure of the barometric pressure. 一种垂直的玻璃管，上端密封，下端浸入汞池中。水银上方的空间处于真空状态。水银在管道中上升的高度是大气压力的量度。 |
| X–Y recorder | X-Y记录仪 |
A device that plots a graph of a variable y against a variable x, both in the form of voltages. 一种绘制变量y和变量x的图形的设备，两者都以伏特数的形式。 |
| Preload relaxation | 预载松弛 |
Local yielding, due to excess bearing stress under nuts and bolt heads (caused by high local spots, rough surface finish, and lack of perfect squareness of bolt and nut bearing surfaces), may result in preload relaxation after preloads are first applied to a bolt. 由于螺母和螺栓头下的轴承应力过大（由局部斑点高、表面粗糙以及螺栓和螺母轴承表面缺乏完美的方正度造成），局部屈服可能会在首次向螺栓施加预载荷后导致预载荷松弛。 |
| Essential conditions | 必要条件 |
Each type of failure to which bolted joints are subject is set up by three or four conditions. The conditions vary, depending on the mode of failure, but never number more than four. Eliminating any one of the essential conditions for a particular type of failure can prevent that type of failure. 螺栓连接所遭受的每种类型的故障都由三个或四个条件确定。根据故障模式的不同，情况会有所不同，但数量不得超过四个。消除特定类型故障的任何一个基本条件都可以防止该类型故障。 |
| Finishing washer | 光制垫圈 |
A washer designed for use with countersunk screws. Used to enhance appearance in some applications. 设计用于沉头螺钉的垫圈。在某些应用中用于增强外观。 |
| Scoring | 划痕 |
In tribology, a severe form of wear characterized by the formation of extensive grooves and scratches in the direction of sliding. 在摩擦学中，一种严重的磨损形式，其特征是在滑动方向上形成大面积的凹槽和划痕。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Computer-aided manufacturing | 计算机辅助制造 |
(CAM, computer-integrated manufacturing, CIM) The use of computers in all branches of manufacturing, not only to control machines and robots for manufacturing and assembly, but also for process planning, and monitoring progress of materials and components during production, etc. （CAM，计算机集成制造，CIM）在制造的所有分支中使用计算机，不仅可以控制制造和组装的机器和机器人，还可以进行工艺规划，以及在生产过程中监控材料和组件的进度等。 |
| Plane strain | 平面应变 |
The stress condition in linear-elastic fracture mechanics in which there is zero strain in a direction normal to both the axis of applied tensile stress and the direction of crack growth (i.e., parallel to the crack front); most nearly achieved in loading thick plates along a direction parallel to the plate surface. Under plane-strain conditions, the plane of fracture instability is normal to the axis of the principal tensile stress. 线弹性断裂力学中的应力条件，其中在垂直于施加拉应力轴和裂纹扩展方向（即平行于裂纹前沿）的方向上存在零应变；最接近于沿平行于板表面的方向加载厚板。在平面应变条件下，断裂失稳平面垂直于主拉应力轴。 |
| Acceleration due to gravity | 重力加速度 |
(acceleration of free fall, gravitational acceleration, g) (Unit m/s²) The acceleration of a freely-falling body in a vacuum, with a mean value at sea level of approximately 9.81 m/s². （自由落体加速度，重力加速度，g）（单位m/s²）自由落体在真空中的加速度，在海平面处的平均值约为9.81m/s²。 |
| Depth (Unit m) | 深度（单位米） |
1. The vertical distance below a datum surface, especially the sea surface. 2. The distance between the top and bottom of a hole, step in a surface, or a container. 1.基准面以下的垂直距离，尤其是海面。2. 孔的顶部和底部之间的距离、表面上的台阶或容器中的距离。 |
| Zero-gravity | 零重力 |
The situation in which there is no force of gravity (i.e. weightlessness). 没有重力的情况（即失重）。 |
| Critical crack length (Unit m) | 临界裂纹长度（单位米） |
The crack length at which a given stress applied to a body will result in crack propagation and fracture. 施加到物体上的给定应力将导致裂纹扩展和断裂的裂纹长度。 |
| Grain growth | 晶粒生长 |
An increase in the average size of the grains in polycrystalline metal, usually as a result of heating at elevated temperature. 多晶金属中晶粒平均尺寸的增加，通常是高温加热的结果。 |
| Annealing carbon | 退火碳 |
Fine, apparently amorphous carbon particles formed in white cast iron and certain steels during prolonged annealing. Also called temper carbon. 白口铸铁和某些钢在长时间退火过程中形成的细小、明显的无定形碳颗粒。也称为回火碳。 |
| Direct quenching | 直接淬火 |
(1) Quenching carburized parts directly from the carburizing operation. (2) Also used for quenching pearlitic malleable parts directly from the malleablizing operation. （1） 直接从渗碳作业中淬火渗碳零件。（2） 也用于直接从可锻操作淬火珠光体可锻零件。 |
| Centripetal | 向心力 |
Acting or moving in a direction towards the axis of rotation. 在朝向旋转轴的方向上起作用或移动。 |
| Gasket factors | 垫片系数 |
Experimentally derived ‘‘constants’’ used to define the behavior of a gasket or the assembly and in-service conditions required for acceptable behavior. 实验得出的“常数”用于定义垫圈的行为或可接受行为所需的组件和使用条件。 |
| Concentration ratio | 浓度比 |
For a concentrating solar collector, the ratio of the projected area of the concentrator facing the solar beam to the actual area of the receiver. 对于聚光太阳能集热器，集中器面向太阳光束的投影面积与接收器的实际面积之比。 |
| Strain energy | 应变能 |
A measure of the energy absorption characteristics of a material determined by measuring the area under the stress-strain diagram. 通过测量应力-应变图下的面积确定的材料能量吸收特性的度量。 |
| Actual cubic feet per minute | 实际立方英尺每分钟 |
(acfm) An obsolete (i.e. non-SI) measure of volumetric flow rate; the volume of a gas flowing per minute at actual operating pressure and temperature, as opposed to the corresponding volume flow rate at STP. （acfm）已被淘汰的（即非SI）体积流量测量；在实际工作压力和温度下每分钟流动的气体体积，与STP下的相应体积流量相反。 |
| Delamination | 分层 |
A mode of failure of composite materials, including radial-ply tyres, in which the layers separate due to repeated cyclic loading, impact, or weak bonding. 复合材料的一种失效模式，包括子午线轮胎，其中层由于重复的循环载荷、冲击或弱粘合而分离。 |
| Gage length | 标距 |
The original length of the portion of a specimen over which strain, change of length, or other characteristics are determined. 确定应变、长度变化或其他特性的试样部分的原始长度。 |
| Conduit | 导管 |
A hollow object, of metal, plastic, glass, ceramic, etc., which is relatively long compared with its lateral dimensions and through which there is fluid flow. 由金属、塑料、玻璃、陶瓷等制成的中空物体，与其横向尺寸相比相对较长，并且有流体流过。 |
| Combustion chamber | 炉膛 |
1. In a piston engine, the volume between the head of an individual cylinder and the crown of the piston in which the fuel–air mixture burns during each power stroke of the engine. 2. (combustor) In a gas-turbine engine, a ramjet, an afterburner, or a rocket motor, the component, often cylindrical or annular in shape, in which the fuel–air mixture burns in a continuous-flow process. 1.在活塞式发动机中，在发动机的每个动力冲程中，燃料-空气混合物燃烧的单个气缸盖和活塞顶之间的体积。2.（燃烧室）在燃气涡轮发动机、冲压发动机、加力燃烧室或火箭发动机中，燃料-空气混合物在连续流动过程中燃烧的部件，通常为圆柱形或环形。 |
| Malleable cast iron | 可锻铸铁 |
A cast iron made by prolonged annealing of white cast iron in which decarburization or graphitization, or both, take place to eliminate some or all of the cementite. The graphite is in the form of temper carbon. If decarburization is the predominant reaction, the product will exhibit a light fracture surface, hence, “whiteheart malleable;” otherwise, the fracture surface will be dark, hence, “blackheart malleable.” Ferritic malleable has a predominantly ferritic matrix; pearlitic malleable may contain pearlitic, spheroidite or tempered martensite depending on heat treatment and desired hardness. 白口铸铁一种通过长时间退火制成的铸铁，脱碳，石墨化，或两者都发生，以消除部分或全部渗碳体。石墨是回火碳的形式。如果脱碳是主要反应，产品将呈现出较轻的断裂表面，“白心可锻”。否则，断裂表面将变暗，“黑心可锻”。铁素体可锻性材料主要为铁素体基体；根据热处理和所需硬度，珠光体可锻材料可能包含珠光体、球状体或回火马氏体。 |
| Compressed liquid | 压缩液体 |
A liquid subjected to a pressure greater than the saturation pressure corresponding to its temperature. 承受大于与其温度对应的饱和压力的压力的液体。 |
| Temperature factor | 温度系数 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. Accounts for the effects of thermal expansion and the temperature-induced change in the velocity of sound. 用于螺栓应力或应变超声波测量的校准常数。说明了热膨胀和温度引起的声速变化的影响。 |
| Finished fastener | 精制紧固件 |
Fastener for which all manufacturing steps have been completed, with or without any surface coating and with full or reduced loadability, and which has not been machined into a test piece. 已完成所有制造步骤的紧固件，有或没有任何表面涂层，具有完全或降低的承载能力，并且尚未加工成试件。 |
| Preload | 预载 |
The tension created in a threaded fastener when the nut is first tightened. Often used interchangeably, but incorrectly, with Working load or bolt force or bolt tension 第一次拧紧螺母时螺纹紧固件中产生的张力。经常与工作载荷或螺栓力或螺栓张力互换使用但容易使用不当。 |
| Relative humidity (ϕ) | 相对湿度（ψ） |
The ratio or percentage of the actual mass of moisture in a given volume of air at a given temperature to the maximum possible mass of moisture at the same temperature. 给定温度下给定体积空气中的实际水分质量与相同温度下的最大可能水分质量的比率或百分比。 |
| Crystalline fracture | 结晶断裂 |
A pattern of brightly reflecting crystal facets on the fracture surface of a polycrystalline metal, resulting from cleavage fracture of many individual crystals. 多晶金属断裂面上明亮反射的晶面图案，由许多单个晶体的解理断裂产生。 |
| Graham’s laws | 格雷厄姆定律 |
The laws stating that the rates of diffusion and effusion of a gas are inversely proportional to the square root of its density. 规定气体的扩散和渗出速率与其密度的平方根成反比的定律。 |
| Altitude chamber | 高空舱 |
(hypobaric chamber) A chamber in which conditions at different altitudes are simulated by a combination of appropriate pressures, temperatures and relative humidity. （低压舱）通过适当的压力、温度和相对湿度的组合来模拟不同高度条件的舱室。 |
| Columnar structure | 柱状结构 |
A coarse structure of parallel elongated grains formed by unidirectional growth, most often observed in castings, but sometimes in structures resulting from diffusional growth accompanied by a solid-state transformation. 由单向生长形成的平行细长晶粒的粗略结构，最常见于铸件中，但有时也出现在伴随固态转变的扩散生长产生的结构中。 |
| Transgranular | 穿晶 |
Through or across crystals or grains. Also known as intracrystalline or transcrystalline. 穿过或横穿晶体或颗粒。也称为晶内或晶间。 |
| Cast steel | 铸钢 |
Steel that is cast into shapes. It has superior properties to most cast irons, but is more expensive to produce. 铸成形状的钢。与大多数铸铁相比，它具有优越的性能，但生产成本更高。 |
| Weld penetration | 焊接熔深 |
It is the depth below the surfaces, as revealed in microstructural sections of joined metals, which is melted during welding. 它是焊接过程中熔化的连接金属的微观结构截面所显示的表面以下的深度。 |
| Flame hardening | 火焰硬化 |
A process for hardening the surfaces of hardenable ferrous alloys in which an intense flame is used to heat the surface layers above the upper transformation temperature, whereupon the workpiece is immediately quenched. 一种用于硬化可硬化铁合金表面的工艺，其中使用强烈的火焰将表面层加热到转变温度上限以上，然后立即对工件进行淬火。 |
| Set screw | 紧定螺钉（平头螺钉、紧定螺栓） |
Usually a hardened steel screw having either no head or a square head and with various degrees of points or ends to lock or tighten adjustable machine parts in position on a shaft. A short, headless screw with a recess at one end to receive a screwdriver or key, the other end being pointed, square, or otherwise shaped. Typically used to secure a pulley, gear, or other component on a shaft. 通常是一种硬化钢螺钉，无头或方头，具有不同程度的点或端部，用于将可调机械部件锁定或拧紧在轴上的适当位置。一端有凹槽，用来装螺丝刀或钥匙，另一端是尖的、方形的或其他形状的。通常用于将皮带轮、齿轮或其他部件固定在轴上。 |
| J-integral | J-积分 |
A mathematical expression describing a line or surface integral that encloses the crack front from one crack surface to the other, used to characterize the fracture toughness of a material having appreciable plasticity before fracture. The J-integral eliminates the need to describe the behavior of the material near the crack tip by considering the local stress-strain field around the crack front; JIc is the critical value of the J-integral required to initiate crack extension from a preexisting crack. 描述从一个裂纹表面到另一个裂纹正面的线或表面积分的数学表达式，用于表征断裂前具有可观塑性的材料的断裂韧性。J积分通过考虑裂纹前缘周围的局部应力应变场，无需描述裂纹尖端附近材料的行为；JIc是从先前存在的裂纹开始裂纹扩展所需的J积分的临界值。 |
| Vacuum annealing | 真空退火 |
Annealing carried out at subatmospheric pressure. 在低于大气压的压力下进行退火。 |
| Composite material | 复合材料 |
(composite structure) A general term used of two or more materials or structures acting in combination (e.g. concrete, reinforced concrete, filamentreinforced polymers, laminated materials, particulate-reinforced materials, flitched beams), resulting in values of strength, stiffness, or toughness greater than the base matrix material alone. （复合结构）用于组合作用的两种或多种材料或结构的通用术语（例如混凝土、钢筋混凝土、纤维增强聚合物、层压材料、颗粒增强材料、切割梁），从而产生强度、刚度或韧性值大于单独的基体材料。 |
| Forced-air quench | 强制空气淬火 |
A quench utilizing blasts of compressed air against relatively small parts such as a gear. 利用压缩空气冲击相对较小的零件（例如齿轮）进行的淬火。 |
| Centrifugal force (Unit N) | 离心力（单位N） |
The inertial reaction force to the centripetal force. It is equal in magnitude but opposite in direction. 惯性反作用力对向心力。它的大小相等，但方向相反。 |
| Computer numerical control (CNC) | 计算机数控（CNC） |
A term relating to machine tools in which the movements of a tool and/or the workpiece are controlled by computer. 与机床相关的术语，其中工具和/或工件的运动由计算机控制。 |
| Alternative energy | 可替代能源 |
(alternate energy) Energy sources that are renewable and do not have the undesired consequences of fossil fuels and nuclear energy. （替代能源）可再生能源，不会产生化石燃料和核能的不良后果。 |
| Cheese head | 圆柱头 |
A cylindrical head on a screw or bolt. For driving, it may be slotted, or hexagonally recessed. 螺钉或螺栓上的圆柱头。为了驱动，它可以是开槽的，也可以是六角形的。 |
| Volumetric efficiency | 容积效率 |
For a piston engine, the ratio of the volume of the induced charge per induction stroke, determined at a reference pressure and temperature, to the swept volume. 对于活塞式发动机，在参考压力和温度下确定的每个进气冲程的进气体积与扫掠体积之比。 |
| Stress relaxation | 应力松弛 |
The slow decrease in stress level within a part (e.g., a bolt) which is heavily loaded under constant deflection conditions. A ‘‘cousin’’ to creep, which is a slow change in geometry under constant stress conditions. The time-dependent decrease in stress in a solid under constant strain at constant temperature due to creep. The stress-relaxation behavior of a metal is usually shown in a stress-relaxation curve. 在恒定挠曲条件下，零件（如螺栓）内的应力水平缓慢降低，该零件承受重荷载。蠕变的“表亲”，是在恒定应力条件下几何结构的缓慢变化。在恒定温度下，由于蠕变，固体在恒定应变下的应力随时间变化的减小。金属的应力松弛行为通常显示在应力松弛曲线中。 |
| Initial strain | 初始应变 |
The strain in a specimen immediately upon achieving the given loading conditions in a creep test (before creep occurs). Sometimes referred to as instantaneous strain. 在蠕变试验中（蠕变发生之前）达到给定载荷条件后，试样立即产生的应变。有时称为瞬时应变。 |
| Nanoparticles | 纳米颗粒 |
Particles with dimensions of order 1 nm which have either been introduced into microstructures for reinforcement or are present as impurities. 尺寸为1nm级的颗粒，其已被引入微结构中用于增强或作为杂质存在。 |
| Free ferrite | 游离铁氧体 |
Ferrite that is formed directly from the decomposition of hypoeutectoid austenite during cooling, without the simultaneous formation of cementite. Also proeutectoid ferrite. 在冷却过程中亚共析奥氏体分解直接形成的铁素体，没有同时形成渗碳体。也是先共析铁氧体。 |
| Compression spring | 压缩弹簧 |
A spring that resists compression forces, usually in the form of a helix with separated coils (giving a linear axial stiffness) or a cone with separated coils (giving a non-linear axial stiffness). 一种抵抗压缩力的弹簧，通常采用带有分离线圈的螺旋形式（提供线性轴向刚度）或带有分离线圈的锥形（提供非线性轴向刚度）。 |
| Minimum stress (Smin) | 最小应力（Smin） |
In fatigue, the stress having the lowest algebraic value in the cycle, tensile stress being considered positive and compressive stress negative. 在疲劳中，循环中代数值最低的应力，拉应力被视为正应力，压应力为负应力。 |
| Indentation hardness | 压痕硬度 |
The resistance of a material to indentation as determined by hardness testing. The indenter, which may be spherical or diamond shaped, is pressed into the surface of a metal under specified load for a given time. (Unit Pa or, non-SI, kgf/mm²) A measurement of hardness taken by means of an indenter, pressed into a material by a load, which makes a permanent impression. The hardness is given by the load divided by the projected (sometimes surface) area of the indentation. Plasticity theory shows that the hardness is about 2.5–3 times the uniaxial yield stress. 通过硬度测试确定的材料抗压痕的能力。压头可以是球形或菱形，在规定的载荷下压入金属表面一段时间。（单位Pa或，非国际单位制，kgf/mm²）通过压头测量硬度，压入材料，形成永久压痕。硬度由载荷除以压痕的投影（有时是表面）面积得出。塑性理论表明，硬度约为单轴屈服应力的2.5–3倍。 |
| Thermodynamic pressure (Unit Pa) | 热力学压力（单位Pa） |
The pressure within a fluid given by an equation of state such as p(ρ,T) where ρ is the fluid density and T is the absolute temperature of the fluid. 流体中的压力由状态方程给出，如p（ρ，T），其中ρ是流体密度，T是流体的绝对温度。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Centrifugal clutch | 离心离合器 |
A clutch that engages and disengages at a defined speed of rotation of the driving shaft, as when expanding friction shoes act against the inside of a drum. 一种离合器，以驱动轴规定的旋转速度接合和分离，如当膨胀的摩擦片作用在滚筒内部时。 |
| Design load (Unit N) | 设计荷载（单位N） |
The greatest load that a component or structure is expected to experience under normal operating conditions. 部件或结构在正常运行条件下预期承受的最大负载。 |
| Compression member | 压缩构件 |
A structural component, the major loading on which is compressive. 一种结构部件，其上的主要载荷是压缩的。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Normal temperature and pressure (NTP) | 常温常压（NTP） |
Reference conditions defined by NIST as 20°C and 1 atm. NIST定义的参考条件为20°C和1atm。 |
| Strength of bolt | 螺栓强度 |
An ambiguous term which can mean Ultimate strength or Proof load or Endurance limit or Yield strength. 一个模棱两可的术语，可表示极限强度或验证荷载或耐久极限或屈服强度。 |
| Microscopic stresses | 微观应力 |
Residual stresses that vary from tension to compression in a distance (presumably approximating the grain size) that is small compared with the gage length in ordinary strain measurements. They are not detectable by dissection methods, but can sometimes be measured from line shift or line broadening in an x-ray diffraction pattern. 与普通应变测量中的标距相比，从拉伸到压缩的距离（大概接近晶粒尺寸）较小的残余应力。它们无法通过解剖方法检测到，但有时可以通过x射线衍射图案中的线位移或线加宽来测量。 |
| International Practical Temperature Scale (IPTS) | 国际实用温标（IPTS） |
A close approximation to the thermodynamic temperature scale based upon the triple points of hydrogen (13.8 K), neon (24.6 K), oxygen (54.4 K), argon (83.8 K), mercury (234.3 K), and water (273.2 K); the melting point of gallium (302.9 K); and the freezing points of indium (429.7 K), tin (505.1 K), zinc (692.7 K), aluminium (933.5 K), silver (1 234.9 K), gold (1 337.3 K), and copper (1 基于氢（13.8K）、氖（24.6K）、氧（54.4K）、氩（83.8K），汞（234.3K）和水（273.2K）的三相点的热力学温度标度的近似值；镓的熔点（302.9K）；铟（429.7K）、锡（505.1K）、锌（692.7K），铝（933.5K）、银（1234.9K）、金（1337.3K）和铜等。 |
| Congruent melting point (Unit K) | 全等熔点（单位K） |
congruent melting point (Unit K) The temperature at which a solid substance at a specified pressure changes phase to a liquid of identical composition. 一致的熔点（单位K）固体物质在特定压力下相变为具有相同成分的液体时的温度。 |
| Eccentric load | 偏心载荷 |
The external load on a fastener or groups of fasteners is said to be eccentric if the resultant of that load does not pass through the centroid of the group of fasteners (eccentric shear load ) or does not coincide with the bolt axis (eccentric tensile load ). 如果一个或多个紧固件上的外部载荷的合力未穿过紧固件组的质心（偏心剪切载荷）或与螺栓轴不重合（偏心拉伸载荷），则称该外部载荷为偏心。 |
| Acid rain | 酸雨 |
Any form of precipitation, including rain, snow, sleet, fog, dew, and particulates, which contains higher than normal levels of sulfuric and nitric acids. These acids result from natural and man-made emissions of sulfur dioxide and oxides of nitrogen, respectively. Acid soot consists of unburned carbon particles, typically larger than 10 μm, in the atmosphere contaminated with sulfuric acid. The particles result from poor combustion of fossil fuels. 任何形式的降水，包括雨、雪、雨夹雪、雾、露水和颗粒物，其中含有高于正常水平的硫酸和硝酸。这些酸分别来自二氧化硫和氮氧化物的自然排放和人为排放。酸烟灰由未燃烧的碳颗粒组成，通常大于10微米，在被硫酸污染的大气中。这些颗粒是化石燃料燃烧不良造成的。 |
| Spring load (Unit N) | 弹簧载荷（单位：N） |
A load exerted on a component by bending, compressing, extending, or twisting an attached spring. Mechanical energy stored in the spring can be released if any constraints on the component are removed. 通过弯曲、压缩、延伸或扭转连接的弹簧而施加在部件上的载荷。如果部件上的任何约束被移除，则可以释放弹簧中存储的机械能。 |
| Martempering | 淬火 |
(1) A hardening procedure in which an austenitized ferrous workpiece is quenched into an appropriate medium whose temperature is maintained substantially at the Ms of the workpiece, held in the medium until its temperature is uniform throughout–but not long enough to permit bainite to form–and then cooled in air. The treatment is frequently followed by tempering. (2) When the process is applied to carburized material, the controlling Ms temperature is that of the case. This variation of the process is frequently called marquenching. （1）一种淬火工艺，将奥氏体化铁质工件淬火到适当的介质中，该介质的温度基本保持在工件的Ms，保持在该介质中直到其温度在整个过程中均匀，但不足以形成贝氏体，然后在空气中冷却。处理后经常进行回火。（2） 当该工艺应用于渗碳材料时，控制Ms温度与实际情况相同。这个过程的变化经常被称为淬火。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Cohesive strength | 内聚强度 |
(Unit Pa) A theoretical fracture strength for solids based on interatomic forces, approximately equal to E/10 where E is Young’s modulus. （单位Pa）基于原子间力的固体理论断裂强度，大约等于E/10，其中E是杨氏模量。 |
| Self-loosening | 自松动 |
The process by which a supposedly tightened fastener becomes loose, as a result of vibration, thermal cycles, shock, or anything else which cause transverse slip between joint members and between male and female threads. Vibration loosening is a common, but special, case of self-loosening. 由于振动、热循环、冲击或任何其他导致接头构件之间以及阳螺纹和阴螺纹之间横向滑动的原因，紧固件松动的过程。振动松动是自松动的一种常见但特殊的情况。 |
| Elastic resilience | 弹性回弹 |
The amount of energy absorbed in stressing a material up to the elastic limit; or, the amount of energy that can be recovered when stress is released from the elastic limit. 向材料施加应力直至弹性极限所吸收的能量；或者当应力从弹性极限释放时可以恢复的能量值。 |
| Turning angle (θ) | 转向角（θ） |
The change in direction experienced by a gas flow passing through an oblique shock wave or Prandtl–Meyer expansion fan. 气流通过斜激波或Prandtl–Meyer膨胀风机时所经历的方向变化。 |
| Physical properties | 物理性质 |
Properties of a material the determination of which does not involve the deformation or destruction of the specimen—for example, density, electrical conductivity, coefficient of thermal expansion, magnetic permeability, and lattice parameter. Does not include chemical reactivity or the properties more appropriately regarded as mechanical properties. 不涉及试样变形或破坏的材料特性，例如密度、电导率、热膨胀系数、磁导率和晶格参数。不包括化学反应性或更适当地视为机械的性质。 |
| Fatigue life for p % survival | p%存活率的疲劳寿命 |
An estimate of the fatigue life that p% of the population would attain or exceed at a given stress level. The observed value of the median fatigue life estimates the fatigue life for 50% survival. Fatigue life for p% survival values, where p is any number, such as 95, 90, etc., may also be estimated from the individual fatigue life values. p%存活在给定应力水平下达到或超过的疲劳寿命估计值。中值疲劳寿命的观察值估计了50%存活率的疲劳寿命。p%存活值的疲劳寿命，其中p为任何数字，如95、90等，也可根据单个疲劳寿命值进行估算。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Tension joint | 张力接头 |
A joint which is primarily subjected to loads acting more or less parallel to the axes of the bolts. 主要承受或多或少平行于螺栓轴线的载荷的接头。 |
| Ablation cooling | 烧蚀冷却 |
The cooling of a surface exposed to very high external gas temperature which causes the surface material to sublime, melt or decompose. The chemical process absorbs heat while the mass flow of material away from the surface blocks the heat flux from the hot gas. 冷却暴露于非常高的外部气体温度的表面，导致表面材料升华、熔化或分解。化学过程吸收热量，而远离表面的物质的质量流阻挡了来自热气体的热通量。 |
| Shear modulus (G) | 剪切模量（G） |
The ratio of shear stress to the corresponding shear strain for shear stresses below the proportional limit of the material. Values of shear modulus are usually determined by torsion testing. Also known as modulus of rigidity. 对于低于材料比例极限的剪切应力，剪切应力与相应剪切应变之比。剪切模量值通常通过扭转试验确定。也称为刚度模量。 |
| Computer control | 电脑控制 |
The control of an engineering device or system by pre-programmed computer or by feedback control. 通过预编程计算机或反馈控制对工程设备或系统进行控制。 |
| Surface hardening | 表面硬化 |
A generic term covering several processes applicable to a suitable ferrous alloy that produces, by quench hardening only, a surface layer that is harder or more wear resistant than the core. There is no significant alteration of the chemical composition of the surface layer. The processes commonly used are carbonitriding, carburizing, induction hardening, flame hardening, nitriding, and nitrocarburizing. Use of the applicable specific process name is preferred. 一个通用术语，涵盖适用于仅通过淬火硬化产生比型芯更硬或更耐磨的表面层的合适铁合金的几种工艺。表面层的化学成分没有显著改变。常用的工艺有碳氮共渗、渗碳、感应淬火、火焰淬火、氮化和氮碳共渗。最好使用适用的特定工艺名称。 |
| Caustic quenching | 苛性淬火 |
Quenching with aqueous solutions of 5 to 10% sodium hydroxide (NaOH). 用5%至10%氢氧化钠（NaOH）水溶液淬灭。 |
| Physical crack size (ap) | 物理裂纹尺寸（ap） |
The distance from a reference plane to the observed crack front. This distance may represent an average of several measurements along the crack front. The reference plane depends on the specimen form, and it is normally taken to be either the boundary or a plane containing either the load line or the centerline of a specimen or plate. 从基准面到观察到的裂纹前沿的距离。该距离可以表示沿裂纹前沿的若干测量的平均值。基准面取决于试样形状，通常视为边界或包含试样或板的载重线或中心线的平面。 |
| Torsional shaft vibration | 扭轴振动 |
The rapid back-and-forth angular twisting along a rotating unbalanced shaft which reaches maxima at critical rotation speeds. Shaft eccentricity, unbalanced mass distribution, oscillatory torque, misalignment, etc. all influence torsional vibration. 沿旋转不平衡轴的快速来回角扭转，在临界转速下达到最大值。轴偏心、质量分布不平衡、振荡扭矩、未对准等都会影响扭转振动。 |
| Linear-elastic fracture mechanics | 线弹性断裂力学 |
A method of fracture analysis that can determine the stress (or load) required to induce fracture instability in a structure containing a cracklike flaw of known size and shape. 一种断裂分析方法，可确定在含有已知尺寸和形状裂纹状缺陷的结构中引起断裂不稳定性所需的应力（或载荷）。 |
| Transmission | 传输 |
The system that transmits power and torque from a power source; for example a shaft, belts and pulleys, or a gear train. In the case of a motor vehicle, it includes the gearbox, clutch, propeller shaft, differential and final drive shafts. 从动力源传输功率和扭矩的系统；例如轴、皮带和滑轮或齿轮系。对于机动车辆，包括变速箱、离合器、传动轴、差速器和终传动轴。 |
| Working stress (Unit Pa) | 工作应力（单位Pa） |
The stress under which a component or structure is designed to operate under normal conditions. 部件或结构设计为在正常条件下运行的应力。 |
| Nanomanufacturing | 纳米制造 |
1. The manufacture of nanoscale materials. 2. The manufacture of components or devices that have critical dimensions of order 1 nm. 1.纳米材料的制造。2.具有1nm级临界尺寸的部件或装置的制造。 |
| Pressure recovery (Unit Pa) | 压力恢复（单位Pa） |
The progressive increase in static pressure for unseparated flow through a diverging nozzle or diffuser. 通过发散喷嘴或扩散器的未分离流的静压逐渐增加。 |
| Concentrated solar power plant (CSP plant) | 聚光太阳能发电厂（CSP发电厂） |
A power plant in which solar radiation is concentrated using mirrors or lenses, typically using parabolic trough mirrors which focus solar radiation on to receiver tubes along the trough’s focal line. In an alternative arrangement molten salt, heated by solar receivers mounted on a tower, is circulated through a steam generator. 使用镜子或透镜集中太阳辐射的发电厂，通常使用抛物面槽镜，将太阳辐射沿着槽的焦线聚焦到接收管上。在另一种布置中，由安装在塔上的太阳能接收器加热的熔盐通过蒸汽发生器循环。 |
| Radial flow | 径向流 |
radial flow Fluid flow for which the principal direction of flow is either radially inward or radially outward relative to an axial direction. 径向流动流体流动的主要方向是径向向内或径向向外流动。 |
| Clearance fit | 间隙配合 |
A range of clearances ranging from close sliding to loose running, i.e. a fit in which the limits for the mating parts always permit assembly. 从紧密滑动到松动运行的一系列间隙，即配合零件的限制始终允许组装的配合。 |
| Vickers hardness test | 维氏硬度测试 |
An indentation hardness test employing a 136° diamond pyramid indenter (Vickers) and variable loads, enabling the use of one hardness scale for all ranges of hardness—from very soft lead to tungsten carbide. Also know as diamond pyramid hardness test. 采用136°金刚石棱锥压头（维氏硬度计）和可变载荷的压痕硬度测试，能够对从极软铅到碳化钨的所有硬度范围使用一个硬度标度。也称为钻石金字塔硬度测试。 |
| Elastic strain energy | 弹性应变能 |
The energy expended by the action of external forces in deforming a body elastically. Essentially, all the work performed during elastic deformation is stored as elastic energy, and this energy is recovered upon release of the applied force. 在外力作用下使物体弹性变形所消耗的能量。本质上，弹性变形过程中所做的所有功都以弹性能的形式存储，并且在释放所施加的力时恢复该能量。 |
| Water hammer | 水锤 |
The reflected pressure surge that occurs in a liquid flowing through a pipe, usually as a consequence of sudden closure of a valve. The surge may cause the pipe to vibrate and a hammering noise to be heard. Key factors affecting the surge amplitude are the compressibility of the liquid (especially if it contains undissolved gas) and the elasticity of the pipe wall. 在流经管道的液体中发生的反射压力波动，通常是阀门突然关闭的结果。浪涌可能导致管道振动，并听到锤击噪音。影响喘振幅度的关键因素是液体的可压缩性（特别是当其含有未溶解气体时）和管壁的弹性。 |
| Mechanical units | 机械单位 |
The units of physical quantities, the dimensions of which includemass, length, and time. 物理量的单位，其量纲包括质量、长度和时间。 |
| Mechanical metallurgy | 机械冶金 |
The science and technology dealing with the behavior of metals when subjected to applied forces. 处理金属在外力作用下的行为的科学技术。 |
| Acoustic droplet ejection | 声液滴喷射 |
The ejection of small droplets from the surface of a liquid that results from focusing high-intensity ultrasound near the surface. 由于在表面附近聚焦高强度超声波而从液体表面喷射出小液滴。 |
| Arbitration bar | 抗弯试棒 |
A test bar, cast with a heat of material, used to determine chemical composition, hardness, tensile strength, and deflection and strength under transverse loading in order to establish the state of acceptability of the casting. 用热材料铸造的测试棒，用于确定化学成分、硬度、抗拉强度、横向载荷下的挠度和强度，以确定铸件的可接受状态。 |
| Torque motor | 力矩电机 |
A type of induction motor that can apply a steady torque even when prevented from rotating. 一种感应电动机，即使被阻止旋转也能施加稳定的转矩。 |
| Elastic interactions | 弹性相互作用 |
When a bolt is tightened it partially compresses the joint members ‘‘in its own neighborhood.’’ When nearby bolts are tightened later, they further compress the joint in this region. This allows the first bolt to relax a little (lose a little preload). Tightening bolts on the opposite side of the joint, however, might increase preload in some of the earlier bolts tightened on the near side. These shifts and changes in the elastic energy stored in individual bolts, during assembly, are called elastic interactions. 当螺栓拧紧时，它会“在其自身附近”部分压缩接头构件稍后拧紧附近的螺栓时，进一步压缩该区域的接头。这允许第一个螺栓稍微松弛（失去一点预载）。但拧紧接头另一侧的螺栓可能会增加早期在近侧拧紧的一些螺栓的预载。在装配过程中，储存在单个螺栓中的弹性能量的这些位移和变化称为弹性相互作用。 |
| Metre (m) | 米（m） |
The base unit of length in the SI system. It is equal to the distance travelled by light in vacuum in 1/299 792 458 seconds. SI系统中长度的基本单位。它等于光在真空中在1/299792458秒内传播的距离。 |
| Bypass ratio | 旁路比 |
In a turbofan engine, the ratio of the mass flow rate of the bypass stream to the mass flow rate through the core of the engine. 在涡扇发动机中，旁通流的质量流量与通过发动机核心的质量流量之比。 |
| Proof strength (Unit Pa) | 验证强度（单位Pa） |
(proof stress, Rp, Rp,) The yield strength (offset yield strength) at some fixed value of the permanent strain given by the intersection of a line offset from, but parallel to, the elastic loading line and the engineering stress-engineering strain curve. The offset is arbitrary but is usually 0.1, 0.2, or 0.5% permanent strain (the proof strain). Used for materials which do not exhibit a sharply defined yield point. The notation Rp0.2 or Rp0.2 is employed for the 0.2% proof stress. （验证应力，Rp）在永久应变的某个固定值下的屈服强度（偏移屈服强度），由偏离但平行于弹性加载线的线与工程应力-工程应变曲线的交点给出。偏移是任意的，但通常为0.1、0.2或0.5%的永久应变（验证应变）。用于没有明确定义屈服点的材料。对于0.2%的验证应力，采用符号Rp0.2。 |
| Transmission dynamometer | 传动测功机 |
A dynamometer in which the power transmitted by a shaft is obtained from the product of its rotation speed and the torque determined from measured shear strains along the shaft. 一种测功机，其中轴传递的功率由其转速和扭矩的乘积获得，扭矩由沿轴测得的剪切应变确定。 |
| Surface roughness (roughness) | 表面粗糙度 |
The small-scale, irregular peaks and troughs in a solid surface which are quantified using a surface analyser. Roughness may be a consequence of wear and corrosion, or of the manufacturing process. It leads to increased friction in solid– solid contact or fluid flow over a surface. Errors of form and waviness are excluded, but surface texture includes roughness and waviness. Surface topography incorporates the small-scale, three-dimensional geometry of a surface including surface roughness, machined, and etched features, typically at sub-mm scales. 固体表面中的小尺度不规则峰谷，使用表面分析仪进行量化。粗糙度可能是磨损和腐蚀或制造过程的结果。它会导致表面上的固-固接触或流体流动中的摩擦增加。不包括形状和波纹度误差，但表面纹理包括粗糙度和波纹度。表面形貌包括表面的小尺度三维几何结构，包括表面粗糙度、机加工和蚀刻特征，通常为亚毫米尺度。 |
| Crank angle (Unit °) | 曲柄角度（单位°） |
The angle between the crank of a slider-crank mechanism and a line from the crankshaft centreline to the piston axis. 曲柄滑块机构的曲柄与曲轴中心线到活塞轴线的直线之间的角度。 |
| Steam gauge | 汽压表 |
A pressure gauge used to measure gauge pressure in a line, boiler, cylinder, or other device operating with steam. 一种压力表，用于测量管道、锅炉、汽缸或其他与蒸汽一起工作的装置中的表压。 |
| True stress (σ) (Unit Pa) | 真应力（σ）（单位Pa） |
The value obtained by dividing the load applied to a member at a given instant by the cross-sectional area over which it acts. Compare with engineering stress. The applied load on a test specimen divided by the current cross-section area over which it acts. σ = s expε where s is the engineering stress given by the applied load divided by the original cross-section area over which it acts, and ε is the true strain. 通过将给定时刻施加在构件上的荷载除以其作用的横截面积而获得的值。与工程应力相比。施加在试样上的荷载除以其作用的当前横截面积。σ=s expε，其中s是由施加荷载除以其作用的原始横截面面积得出的工程应力，ε是真实应变。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Roughness | 粗糙度 |
The deviations from the wavy surface itself, caused by geometry of the cutting tool and its wear, machining conditions, microstructure of the workpiece, vibrations in the system, and so on. Surface roughness changes as a surface goes through the wearing-in process, but may then stabilize. 由刀具的几何形状及其磨损、加工条件、工件的微观结构、系统中的振动等引起的与波状表面本身的偏差。表面粗糙度随着表面经过磨合过程而变化，但随后可能会稳定下来。 |
| Fastener identification marking | 紧固件识别标记 |
A stamp, paint, or other permanent identifier that may include manufacturer information and applicable grade markings for certification purposes. 印章、油漆或其他永久性标识符，其中可能包括制造商信息和用于认证的适用等级标记。 |
| Permanent set | 永久变形 |
The deformation or strain remaining in a previously stressed body after release of load. 释放荷载后，先前受力物体中剩余的变形或应变。 |
| Extra spring | 额外弹簧 |
A temper of nonferrous alloys and some ferrous alloys corresponding approximately to a coldworked state above full hard beyond which further cold work will not measurably increase the strength and hardness. 有色金属合金和一些铁合金的回火状态，大约对应于高于全硬的冷加工状态，超过该状态进一步冷加工将不会显着增加强度和硬度。 |
| Manometer | 压力计 |
An instrument used in the measurement of a pressure difference in a fluid (manometry). 用于测量流体压力差（测压）的仪器。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Orange peel | 橘皮 |
A surface roughening in the form of a pebble-grained pattern where a metal of unusually coarse grain is stressed beyond its elastic limit. Also known as pebbles and alligator skin. 一种以卵石颗粒图案形式出现的粗糙化表面，其中晶粒异常粗的金属受到的应力超过其弹性极限。也称为卵石和鳄鱼皮。 |
| Compressive stress | 压缩应力 |
A stress that causes an elastic body to deform (shorten) in the direction of the applied load. Contrast with tensile stress. 使弹性体沿施加载荷方向变形（缩短）的应力。与拉应力对比。 |
| Pressure ratio | 压力比 |
One pressure divided by another which may be a reference pressure. In many flow and thermodynamic processes, the pressure ratio is more important than the absolute pressure levels. For example, in compressible gas flow the Mach number is determined by the ratio of the stagnation pressure to the static pressure. 一个压力除以另一个压力，该压力可以是参考压力。在许多流动和热力学过程中，压力比比绝对压力水平更重要。例如，在可压缩气流中，马赫数由停滞压力与静压之比决定。 |
| Tab washer (lock washer) | 止动垫圈（锁紧垫圈） |
A washer with one or more protruding tabs which can be bent in such a way that a nut or bolt head is prevented from becoming loose. 一种垫圈，具有一个或多个突出凸耳，可弯曲以防止螺母或螺栓头松动。 |
| Graphitization | 石墨化 |
Formation of graphite in iron or steel. Where graphite is formed during solidification, the phenomenon is called primary graphitization; where formed later by heat treatment, secondary graphitization. 在铁或钢中形成石墨。在凝固过程中形成石墨的现象称为一次石墨化；后来通过热处理，形成二次石墨化。 |
| Compressor bleed | 压缩机排气 |
The removal of air before the final stage of a multistage compressor operating below design speed, to prevent the final stage from choking. 在低于设计速度运行的多级压缩机的末级之前去除空气，以防止末级阻塞。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Lockbolt | 锁紧螺栓 |
A fastener which bears a superficial resemblance to a bolt, but which engages a collar (instead of a nut) with annular grooves (instead of threads). The collar is swaged over the grooves on the male fastener to develop preload. 表面上类似于螺栓的紧固件，但与环槽（而不是螺纹）接合的轴环（而不是螺母）。套环在阳紧固件上的凹槽上锻造，以产生预紧力。 |
| Computer vision | 计算机视觉 |
The digitization and processing of optical images/patterns by computer in order to recognize parts, orientation, etc. in manufacturing. 通过计算机对光学图像/图案进行数字化和处理，以在制造过程中识别零件、方向等。 |
| Quick coupling | 快速接头 |
(quick disconnect, fast coupling) A hose connection allowing rapid assembly or disassembly and comprising a socket and a plug incorporating a springloaded locking mechanism. （快速断开、快速连接）一种软管连接，允许快速组装或拆卸，包括插座和带有弹簧加载锁定机构的插头。 |
| Oxidative wear | 氧化磨损 |
A type of wear resulting from the sliding action between two metallic components that generates oxide films on the metal surfaces. These oxide films prevent the formation of a metallic bond between the sliding surfaces, resulting in fine wear debris and low wear rates. 由两个金属部件之间的滑动作用导致的一种磨损，在金属表面上产生氧化膜。这些氧化膜防止在滑动表面之间形成金属结合，导致细磨屑和低磨损率。 |
| Hydraulics | 液压系统 |
The study of water flow in open channels (including canals, rivers, etc.), water-supply, drainage, and irrigation systems. 研究明渠（包括运河、河流等）、供水、排水和灌溉系统中的水流。 |
| Hydrogen damage | 氢损伤 |
A general term for the embrittlement, cracking, blistering, and hydride formation that can occur when hydrogen is present in some metals. 当氢存在于某些金属中时可能发生的脆化、开裂、起泡和氢化物形成的总称。 |
| Millimetre of water | 毫米水柱 |
A non-SI unit of pressure equal to the pressure exerted by a vertical column of water 1 mm high. Approximately equal to 9.81 Pa. 一种非SI压力单位，等于1毫米高的垂直水柱施加的压力。大约等于9.81Pa。 |
| Scleroscope hardness test | 反跃式硬度试验 |
A dynamic indentation-hardness test using a calibrated instrument that drops a diamond-tipped hammer from a fixed height onto the surface of the material being tested. The height of rebound of the hammer is a measure of the hardness of the material. Also known as Shore hardness test. 使用校准仪器的动态压痕硬度测试，该仪器将金刚石锤从固定高度落在被测材料表面上。锤的回弹高度是材料硬度的一种度量。也称为肖氏硬度测试。 |
| Swept volume (Unit m³) | 扫描体（单位m³) |
In the cylinder of a piston engine or other device, the volume between top and bottom dead centre positions of a piston; equal to πR2S where R is the piston radius and S is the stroke. 在活塞发动机或其他装置的气缸中，活塞上止点和下止点位置之间的体积；等于πR2S，其中R是活塞半径，S是冲程。 |
| Toughness (Unit J/m²) | 韧性（单位：J/m²） |
The ability of a metal to absorb energy and deform plastically before fracturing. 1. The ability of a material to resist crack initiation and propagation. 2. The ability of a material to absorb strain energy without fracturing. 金属在破裂前吸收能量和塑性变形的能力。1.材料抵抗裂纹萌生和扩展的能力。2.材料在不发生断裂的情况下吸收应变能的能力。 |
| Absolute temperature (Unit K) | 绝对温度（单位K） |
A temperature T measured relative to absolute zero, 0 K or −273.15°C, the lowest temperature achievable at which molecular motion vanishes so that a body would have zero heat energy. The kelvin is equal in magnitude to the degree Celsius (°C). The kelvin temperature scale (kelvin absolute temperature scale) is an absolute or thermodynamic temperature scale derived from the Celsius scale: T(K) = T(°C) + 273.15. The Rankine absolute scale is derived from the Fahrenheit scale such that T(R) = T(°F) + 459.67, i.e. a scale relative to 0 R or −459.67°F where R is the Rankine degree symbol and °F is the Fahrenheit symbol. 相对于绝对零、0K或0K测量的温度T−273.15°C，分子运动消失的最低温度，因此物体的热能为零。开尔文的大小等于摄氏度（℃）。开尔文温度标度（开尔文绝对温度标度）是从摄氏标度得出的绝对或热力学温度标度：T（K）=T（°C）+273.15。兰金绝对标度是从华氏标度得出，使得T（R）=T（°F）+459.67，即相对于0R或0R的标度−459.67°F，其中R是朗肯度符号，°F是华氏度符号。 |
| Coefficient of rolling friction | 滚动摩擦系数 |
The ratio of force parallel to a surface, on which an object rolls, to the normal force. Unlike sliding friction, rolling friction depends on the size of the contact patch and the radius of the rolling element, and the behaviour depends on whether the contact is elastic, viscoelastic, or plastic and on hysteresis losses. 平行于物体滚动表面的力与法向力之比。与滑动摩擦不同，滚动摩擦取决于接触片的大小和滚动元件的半径，其行为取决于接触是弹性的、粘弹性的还是塑性的以及滞后损失。 |
| Poisson’s ratio (ν) | 泊松比（ν） |
The absolute value of the ratio of transverse (lateral) strain to the corresponding axial strain resulting from uniformly distributed axial stress below the proportional limit of the material. 横向（侧向）应变与相应轴向应变之比的绝对值，该比值由低于材料比例极限的均匀分布的轴向应力产生。 |
| Volume (Unit m³) | 体积（单位m³） |
The amount of space occupied by a specified mass of substance or by an object. 一定质量的物质或物体占据的空间量。 |
| Fluid mechanics | 流体力学 |
The study of fluids in motion (fluid dynamics) or fluid statics where there is no relative motion between fluid particles. Fluid statics concerns primarily the variation of pressure with altitude or depth; it includes aerostatics and hydrostatics. Fluid dynamics includes the topics of aerodynamics, gas dynamics, hydraulics, hydrodynamics and many aspects of acoustics, chemical engineering, flight, lubrication, meteorology, non-Newtonian fluid flow, oceanography, power-plant technology, propulsion, and turbomachinery. 研究运动中的流体（流体动力学）或流体静力学，其中流体粒子之间没有相对运动。流体静力学主要关注压力随高度或深度的变化；它包括空气静力学和流体静力学。流体动力学包括空气动力学、气体动力学、水力学、流体动力学以及声学、化学工程、飞行、润滑、气象学、非牛顿流体流动、海洋学、发电厂技术、推进和涡轮机械的许多方面。 |
| Valve | 阀门 |
Any of various manual or automatic devices that are able to initiate, regulate, or stop the flow of a fluid through a conduit or from a closed container. 任何一种手动或自动装置，能够启动、调节或停止通过导管或封闭容器的流体流动。 |
| Machine | 机器 |
A mechanism that transmits power in the performance of a useful task. More than one machine in one place, either connected or performing separate functions, is termed machinery. 在执行有用任务时传递能量的机制。一个地方有一台以上的连接或执行单独的功能，称为机器。 |
| Ratchet marks | 棘轮痕 |
Lines on a fatigue fracture surface that result from the intersection and connection of fatigue fractures propagating from multiple origins. Ratchet marks are parallel to the overall direction of crack propagation and are visible to the unaided eye or at low magnification. 疲劳断裂面上由从多个源头传播的疲劳断裂的交叉和连接产生的线。棘轮标记与裂纹扩展的整个方向平行，肉眼或低倍镜下均可看到。 |
| Testing machine | 试验机 |
A machine used to apply either a steady or oscillatory or impact load to a testpiece. The load may be tensile, compressive, shear, bending, or torsional. 用于向试件施加稳定或振荡或冲击载荷的机器。载荷可以是拉伸的、压缩的、剪切的、弯曲的或扭转的。 |
| Compression test | 压缩测试 |
A method for assessing the ability of a material to withstand compressive loads. The determination of the stress–strain curve of a material by axial loading of a specimen in compression. In brittle materials failure is in the elastic range; more ductile materials will yield before fracture; very ductile materials will plastically deform extensively before failure. The compression strength (compressive strength), with unit Pa, is the compressive stress that causes failure in a component or structure. 一种评估材料承受压缩载荷能力的方法。通过压缩试样的轴向载荷确定材料的应力-应变曲线。在脆性材料中，破坏在弹性范围内；韧性更强的材料在断裂前会屈服；韧性很强的材料在失效前会发生广泛的塑性变形。抗压强度（抗压强度），单位为Pa，是导致部件或结构失效的压应力。 |
| Tensile stress (Unit Pa) | 拉应力（单位Pa） |
A stress that causes two parts of an elastic body, on either side of a typical stress plane, to pull apart. A stress that tends to stretch a component, or local region of a component, when under load. In simple tension it results from the applied axial load, but tensile stresses occur in bending, torsion and other forms of loading. 一种应力，使弹性体的两个部分在典型应力平面的任一侧分离。在负载下，倾向于拉伸部件或部件局部区域的应力。在简单拉伸中，它由施加的轴向载荷产生，但拉伸应力发生在弯曲、扭转和其他形式的载荷中。 |
| Radius of bend | 弯曲半径 |
The radius of the cylindrical surface of the pin or mandrel that comes in contact with the inside surface of the bend during bending. For free or semiguided bends to 180° in which a shim or block is used, the radius of bend is one-half the thickness of the shim or block. 在弯曲过程中与弯曲内表面接触的销或心轴的圆柱面半径。对于使用垫片或垫块的180°自由弯曲或半导向弯曲，弯曲半径为垫片或垫板厚度的一半。 |
| Hypereutectoid alloy | 过共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of alloying element compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共晶的合金系统中，合金成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| Standard fit | 标准匹配 |
The fit of a component machined or otherwise manufactured to standardized clearances and tolerances. 根据标准间隙和公差加工或以其他方式制造的部件的配合。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| Turbine blades (turbine buckets) | 涡轮叶片 |
1. The aerofoil-shaped vanes that form the rotor and stator of a gas, steam or hydraulic turbine. 2. The cup-shaped vanes of a Pelton wheel. 1.形成燃气、蒸汽或水力涡轮机的转子和定子的翼型叶片。2.冲击轮的杯形叶片。 |
| Corrosive wear | 腐蚀磨损 |
Wear in which chemical or electrochemical reaction with the environment is significant. 与环境发生显着化学或电化学反应的磨损。 |
| Vice | 老虎钳 |
A workshop tool used to hold a workpiece and consisting of two jaws, one fixed and the other moved by turning a screw. 一种用于夹持工件的车间工具，由两个钳口组成，一个固定，另一个通过转动螺钉移动。 |
| Computed path control | 计算路径控制 |
In CNC or robotics, the use of a control program to determine the required path for the tool or end effector. This required path forms the set points for the motor controllers moving the machine tool or robot. 在CNC或机器人技术中，使用控制程序来确定工具或末端执行器所需的路径。这条所需的路径形成了用于移动机床或机器人的电机控制器的设定点。 |
| Ballonet | 气囊 |
An airbag used in a hybrid airship. Helium gas expels air from the ballonet during ascent. Fans draw air in during descent. 混合动力飞艇中使用的安全气囊。氦气在上升过程中将空气从气囊中排出。风扇在下降过程中吸入空气。 |
| Coherent precipitate | 相干沉淀 |
A crystalline precipitate that forms from solid solution with an orientation that maintains continuity between the crystal lattice of the precipitate and the lattice of the matrix, usually accompanied by some strain in both lattices. Because the lattices fit at the interface between precipitate and matrix, there is no discernible phase boundary. 由固溶体形成的结晶沉淀物，其取向保持沉淀物晶格和基体晶格之间的连续性，通常伴随着两个晶格中的一些应变。由于晶格适合于沉淀和基体之间的界面，因此不存在可识别的相边界。 |
| Absorptance | 吸收率 |
(absorptivity, absorption coefficient, α) The fraction of radiant flux incident on a surface that is absorbed by the surface. The term also applies to absorption of radiation by a volume of fluid. For a semi-transparent surface, α + ρ + τ = 1, where ρ is the reflectance and τ is the transmittance. （吸收率，吸收系数，α）入射到表面的辐射通量被表面吸收的部分。该术语也适用于一定体积的流体对辐射的吸收。对于半透明表面，α+ρ+τ=1，其中ρ是反射率，τ是透射率。 |
| Actual power | 实际功率 |
(actual horsepower) (Unit W or hp) The power delivered at the output shaft of an engine, before subsequent transmission through a gearbox etc. （实际马力）（单位W或hp）在随后通过变速箱等传输之前，在发动机输出轴上传递的功率。 |