| 词或词组 | 中文 | 英文解释中文解释 |
|---|---|---|
| Elastic limit | 弹性极限 |
The maximum stress which a material is capable of sustaining without any permanent strain (deformation) remaining on complete release of the stress. 材料在完全释放应力时能够承受的最大应力，且不会留下任何永久应变（变形）。 |
| Heat-capacity ratio (c*) | 热容量比（c*） |
A non-dimensional parameter that arises in the analysis of heat exchangers, defined as the ratio cMIN/cMAX where cMIN is the heat-capacity rate c for the fluid with the smaller value of c and cMAX the value for the fluid with the larger value of c. Different flow rates and specific-heat values give rise to different values for c. 热交换器分析中出现的无量纲参数，定义为比率cMIN/cMAX其中cMIN是流体的热容率c，c值较小，cMAX是流体的值具有较大的c值。不同的流速和比热值产生不同的c值。 |
| V-block | V型块 |
A block having a 90° V-shaped recess; used in a workshop to hold round workpieces. 具有90°V形凹槽的块体；在车间里用来装圆形工件。 |
| Austenitizing | 奥氏体化 |
Forming austenite by heating a ferrous alloy into the transformation range (partial austenitizing) or above the transformation range (complete austenitizing). When used without qualification, the term implies complete austenitizing. 通过将铁合金加热到转变范围（部分奥氏体化）或高于转变范围（完全奥氏体化）来形成奥氏体。当不加限定地使用时，该术语意味着完全奥氏体化。 |
| Maximum stress (Smax) | 最大应力（Smax） |
The stress having the highest algebraic value in the stress cycle, tensile stress being considered positive and compressive stress negative. The nominal stress is used most commonly. 在应力循环中具有最高代数值的应力，拉应力被认为是正的，压应力被认为是负的。名义应力是最常用的。 |
| Single-shear test | 单剪试验 |
(1) A shear test similar to the double-shear test used for round-bar specimens, but that uses only one stationary shear blade. (2) A shear test that uses a sheet or thin-plate specimen. （1）一种剪切试验，类似于用于圆棒试样的双剪切试验，但仅使用一个固定剪切刀片。（2）使用薄板或薄板试样的剪切试验。 |
| Socket head | 凹头 |
Screw head having a hexagonal or other form of recessed socket in the head so that the screw can be turned with a wrench or key, as a hexagon key. 螺钉头上有六角或其他形式的凹座，可以用扳手或钥匙（如六角钥匙）转动螺钉。 |
| Transformation toughening | 相变增韧 |
The improvement of fracture toughness of a material by stress-induced transformation of the microstructure. 通过微结构的应力诱导转变来提高材料的断裂韧性。 |
| Static fatigue | 静态疲劳 |
A term referring to a time-dependent reduction in strength with a static (noncyclic) load. The term may refer to hydrogen-induced delayed cracking or the effect of creep on the strength of plastics. Delayed fracture caused by environmental effects under dead-weight loading of materials such as glass. The name is unfortunate, as cyclic loads are not involved and glass is not susceptible to fatigue. 指静态（非循环）载荷下强度随时间变化的降低。该术语可指氢致延迟开裂或蠕变对塑料强度的影响。在玻璃等材料的自重荷载下，由环境影响引起的延迟断裂。 |
| Absolute stability | 绝对稳定 |
Condtion of a linear system in which there exists a limiting value of the open-loop gain such that the system is stable for all lower values of that gain, and unstable for all higher values. 线性系统的条件，其中存在开环增益的限制值，使得系统对于该增益的所有较低值都是稳定的，而对于所有较高值来说都是不稳定的。 |
| Torsion-bar suspension | 扭杆悬架 |
A type of motor-vehicle suspension in which one end of a torsion bar is rigidly fixed to the chassis while the other carries a lever to which are attached the components that carry a wheel. In a torsion-beam suspension, a beam connects the wheels on either side of the vehicle. 一种汽车悬架，其中扭力杆的一端刚性固定在底盘上，而另一端带有一个杠杆，杠杆上连接着承载车轮的部件。在扭转梁悬架中，梁连接车辆两侧的车轮。 |
| Maximum material condition | 最大材料条件 |
(maximum metal condition) The situation where the volume of a manufactured component corresponds to the upper limit for all toleranced external dimensions, and to the lower limit for all internal dimensions. （最大金属条件）制造部件的体积对应于所有公差外部尺寸的上限和所有内部尺寸的下限的情况。 |
| Austenitic grain size | 奥氏体晶粒尺寸 |
The size attained by the grains of steel when heated to the austenitic region; may be revealed by appropriate etching of cross sections after cooling to room temperature. 当加热到奥氏体区域时钢晶粒达到的尺寸；冷却至室温后，可通过适当蚀刻横截面来显示。 |
| Creep limit (Unit Pa) | 蠕变极限（单位Pa） |
The maximum allowable stress under the action of which creep deformation of a material does not exceed a specified limit. 材料在其作用下的蠕变变形不超过规定限度的最大许用应力。 |
| Auxetic materials | 拉胀材料 |
Those man-made materials for which Poisson’s ratio is negative, so that the cross section expands when subjected to a longitudinal tensile stress and contracts when subjected to a longitudinal compressive stress. 泊松比为负的人造材料，其横截面在受到纵向拉应力时会膨胀，在受到纵向压应力时会收缩。 |
| Biodiesel | 生物柴油 |
A substitute for diesel fuel derived from the oily seeds of sunflowers, oilseed rape, soya beans, etc. 从向日葵、油菜、大豆等的油性种子中提取的柴油的替代品。 |
| Dynamic mechanical measurement | 动态机械测量 |
A technique in which either the modulus and/or damping of a substance under oscillatory load or displacement is measured as a function of temperature, frequency, or time, or a combination thereof. 一种技术，其中在振荡载荷或位移下测量物质的模量和/或阻尼作为温度、频率或时间或其组合的函数。 |
| Anisotropy | 各向异性 |
The characteristic of exhibiting different values of a property in different directions with respect to a fixed reference system in the material. 相对于材料中的固定参考系统，在不同方向上表现出不同属性值的特性。 |
| Natural unit system (n.u. system) | 自然单位制（n.u.制） |
A non-SI system of units, based on fundamental constants, used in high-energy and particle physics. The n.u. of speed is the speed of light in a vacuum, c0 = 299 792 458 m/s. 基于基本常数的非国际单位制，用于高能和粒子物理n.u.速度是真空中的光速，c0=299792458m/s。 |
| Tension | 拉伸 |
The force or load that produces elongation. 1. The condition in a bar, belt, cable, spring, string, wire, etc. that is being pulled from either end. 2. (tensile force) (unit N) The force associated with tension as in (1). It is measured by a tension meter. 伸长力产生伸长的力或载荷。1.从两端拉出的杆、带、电缆、弹簧、线、线等的状态。2.（张力）（单位N）与张力相关的力。 |
| Linear (tensile or compressive) strain | 线性（拉伸或压缩）应变 |
The change per unit length due to force in an original linear dimension. An increase in length is considered positive. 由于原始线性尺寸中的力，每单位长度的变化。长度的增加被认为是正的。 |
| Fastener testing | 紧固件测试 |
A determination or verification that the fastener meets its specification requirements. 确定或验证紧固件符合其规范要求。 |
| Air pump | 气泵 |
A machine for providing a flow of air or for increasing or decreasing the mass and pressure of air in a closed container. The term pump is more usual when the working fluid is a liquid, while compressor is more usual for gases. 一种用于提供空气流动或用于增加或减少密闭容器中空气质量和压力的机器。当工作流体是液体时，术语泵更常用，而气体更常用压缩机。 |
| Power | 力能 |
The rate of doing work or of producing or consuming energy. The unit of power is the watt, W, where 1 W = 1 N m/s. 做功或产生或消耗能量的速度。功率单位为瓦特，W，其中1W=1N m/s。 |
| Impact extrusion | 冲击挤压 |
The extrusion of separate components of soft metals whose properties permit the action to be performed quickly. 挤压单独的软金属组件，其特性允许快速执行操作。 |
| Clutch | 离合器 |
A device for connecting and disconnecting rotating shafts, for example between an engine and a gearbox. 一种用于连接和断开旋转轴的装置，例如在发动机和变速箱之间。 |
| Centre of pressure | 压力中心 |
1. The location, on an aerofoil or other body that develops lift, of the resultant lift force. 2. The location, on a surface submerged in a liquid, of the resultant force due to the pressure acting on the surface. Because hydrostatic pressure increases with depth, the centre of pressure is generally below the centroid of the surface. 1.在产生升力的机翼或其他物体上，合成升力的位置。2.在浸没在液体中的表面上，由于作用在表面上的压力而产生的合力的位置。由于静水压力随深度增加，压力中心通常低于表面质心。 |
| Liquid nitriding | 液体氮化 |
A method of surface hardening in which molten nitrogen-bearing, fused-salt baths containing both cyanides and cyanates are exposed to parts at subcritical temperatures. 一种表面硬化方法，其中含有氰化物和氰酸盐的熔融含氮熔盐浴在亚临界温度下暴露于零件。 |
| Nanomaterial | 纳米材料 |
A material defined by the European Commission as ‘A natural, incidental or manufactured material containing particles, in an unbound state or as an aggregate or as an agglomerate and where, for 50% or more of the particles in the number size distribution, one or more external dimensions is in the size range 1–100 nm. In specific cases and where warranted by concerns for the environment, health, safety or competitiveness the number size distribution threshold of 50% may be replaced by a threshold between 1 and 50%.’ 由欧盟委员会定义为“含有颗粒的天然、偶然或人造材料，处于未结合状态或聚集体或凝聚体，其中，对于数量-尺寸分布中的50%或更多颗粒，一个或多个外部尺寸在1-100nm的尺寸范围内”。在特定情况下，如果考虑到环境、健康、安全或竞争力，50%的数量大小分布阈值可以由1%到50%之间的阈值代替。 |
| Fahrenheit | 华氏度 |
The temperature scale based on the freezing point of water (32ºF) and the boiling point of water (212ºF). The interval between these points is divided into 180 equal parts. Although replaced by the Celsius scale, the Fahrenheit scale is still sometimes used for non-scientific measurements. 温标基于水的冰点（32ºF）和水的沸点（212ºF）。这些点之间的间隔被分成180等份。尽管被摄氏刻度所取代，华氏刻度有时仍用于非科学测量。 |
| Neutralization number | 中和值 |
An ASTM number given to quenching oils that reflects the oil’s tendency towards oxidation and sludging. 淬火油的ASTM编号，反映了油的氧化和成泥趋势。 |
| Scale height (Unit m) | 刻度高度（单位：m） |
The altitude H at which the atmospheric pressure has decreased to a certain fraction of its value at sea level B. It depends on the model adopted for the atmosphere: for an isothermal atmosphere, the pressure decreases exponentially with altitude. If H is taken as the altitude at which the pressure has fallen to B/e, then H = RT/g where R is the gas constant for air, T is the absolute temperature T, and g is the acceleration due to gravity. 大气压力降低到其在海平面B处数值的某一部分的高度H。它取决于大气采用的模型：对于等温大气，压力随高度呈指数下降。如果取H作为压力下降到B/e的高度，则H=RT/g，其中R是空气的气体常数，T是绝对温度T，g是重力引起的加速度。 |
| Stress relaxation | 应力松弛 |
The slow decrease in stress level within a part (e.g., a bolt) which is heavily loaded under constant deflection conditions. A ‘‘cousin’’ to creep, which is a slow change in geometry under constant stress conditions. The time-dependent decrease in stress in a solid under constant strain at constant temperature due to creep. The stress-relaxation behavior of a metal is usually shown in a stress-relaxation curve. 在恒定挠曲条件下，零件（如螺栓）内的应力水平缓慢降低，该零件承受重荷载。蠕变的“表亲”，是在恒定应力条件下几何结构的缓慢变化。在恒定温度下，由于蠕变，固体在恒定应变下的应力随时间变化的减小。金属的应力松弛行为通常显示在应力松弛曲线中。 |
| Laser hardening | 激光硬化 |
A surface-hardening process which uses a laser to quickly heat a surface. Heat conduction into the interior of the part will quickly cool the surface, leaving a shallow martensitic layer. Hardening of steel by a moving CO2 or Nd:YAG laser beam focussed down to a few mm in diameter. A point in the surface of an object is rapidly heated into the austenite range and then rapidly cooled to form tempered martensite. 一种使用激光快速加热表面的表面硬化工艺。进入零件内部的热传导将快速冷却表面，留下浅马氏体层。通过移动CO2或Nd:YAG激光束使钢硬化，激光束聚焦至直径几毫米。物体表面的一点迅速加热到奥氏体范围，然后迅速冷却，形成回火马氏体。 |
| Frequency | 频率 |
(temporal frequency, f) (Unit Hz) The number of cycles per second in an oscillation or the repetition rate for a cyclic process. （时间频率，f）（单位Hz）振荡中每秒的周期数或循环过程的重复率。 |
| Tooth lock washers | 带齿锁紧垫圈 |
These washers serve to lock fasteners, such as bolts and nuts, to the component parts of an assembly, or increase the friction between the fasteners and the assembly. They are designated in a manner similar to helical spring lock washers, and are available in carbon steel. 这些垫圈用于将紧固件（如螺栓和螺母）锁定到组件的零部件上，或增加紧固件与组件之间的摩擦力。它们的设计方式类似于螺旋弹簧锁紧垫圈，可采用碳钢。 |
| Full annealing | 全退火 |
An imprecise term that denotes an annealing cycle to produce minimum strength and hardness. For the term to be meaningful, the composition and starting condition of the material and the time-temperature cycle used must be stated. Annealing a ferrous alloy by austenitizing and then cooling slowly through the transformation range. 一个不精确的术语，表示产生最小强度和硬度的退火循环。为了使该术语有意义，必须说明材料的组成和起始条件以及使用的时间-温度循环。通过奥氏体化退火铁合金，然后在转变范围内缓慢冷却。 |
| Accommodation | 适应能力 |
The ability of a robot to respond to changes in the environment. 机器人对环境变化做出反应的能力。 |
| Rolled thread | 滚制螺纹 |
A thread formed by plastically deforming the surface of the blank rather than by cutting operations. Increases fatigue life and thread strength, but is not possible (or perhaps economical) on larger sizes. 通过塑性变形坯料表面而不是通过切割操作形成的螺纹。增加疲劳寿命和螺纹强度，但不太可能（或者说是经济上不太可能）用于较大的尺寸。 |
| Mohr–Coulomb yield criterion | Mohr–Coulomb屈服准则 |
A pressure-dependent yield criterion, according to which yielding occurs when the stress at a point in a material falls on the envelope created by the Mohr’s stress circles at yielding for various tests such as tension, shear, and compression that have different components of hydrostatic stress. 一种与压力相关的屈服准则，根据该准则，当材料中某一点的应力落在屈服时的莫尔应力圆所形成的包络线上时，即发生屈服，用于各种试验，如具有不同静水应力分量的拉伸、剪切和压缩。 |
| Temporal decomposition | 时间分解 |
The splitting of a control problem into parts with relatively short and long time constant so that different controllers may be used for the different parts. 将控制问题分解为具有相对较短和较长时间常数的部分，以便不同的部分可以使用不同的控制器。 |
| Vacuum pump | 真空泵 |
A pump for exhausting air and non-condensable gases from a vessel to be maintained at sub-atmospheric pressure. The pirani and thermal-conductivity gauges are vacuum gauges used to measure the absolute pressure within a vacuum system (vacuum level), usually expressed in torr or Pa. 用于从容器中排出空气和不凝性气体以保持在亚大气压的泵。皮拉尼和热导率计是用于测量真空系统内绝对压力（真空水平）的真空计，通常用托或帕表示。 |
| Shoulder bolt | 轴肩螺栓 |
A bolt for which the unthreaded cylindrical section between the thread and the head is of larger diameter than the threaded section, precisely machined to length and diameter and hardened 一种螺栓，其螺纹和头部之间的无螺纹圆柱段的直径大于螺纹段的直径，精确加工至长度和直径并硬化 |
| External load | 外部负载 |
Forces exerted on fastener and=or joint members by such external factors as weight, wind, inertia, vibration, temperature expansion, pressure, etc. Does not equal the Working load in the fastener. 由重量、风、惯性、振动、温度膨胀、压力等外部因素施加在紧固件和/或接头构件上的力。不等于紧固件中的工作负载。 |
| Mechanical properties of solid materials | 固体材料的力学性能 |
The strength and stiffness properties of solid materials such as fracture toughness, the moduli of elasticity, percent elongation, 固体材料的强度和刚度特性，例如断裂韧性、弹性模量、伸长率、 |
| Melting point (Unit K or °C) | 熔点（单位K或°C） |
The temperature at which a solid material undergoes the phase change to a liquid at a specified pressure, usually 1 atm. Pure metals and eutectics have single-valued melting points, while alloys with other compositions melt over a range of temperature such that there is a well-defined start and end to the melting process, but there are states in between where solid and liquid are both present. 在特定压力下，固体材料发生相变为液体的温度，通常为1大气压。纯金属和共晶具有单值熔点，而具有其他成分的合金在一定温度范围内熔化，熔化过程有一个明确的起点和终点，但其间存在固态和液态并存的状态。 |
| Fillet | 圆角 |
Transition region between bolt head and shank, or between other changes in diameter. 螺栓头和螺栓杆之间的过渡区域，或其他直径变化之间的过渡区域。 |
| Olsen cup test | 奥尔森杯测试 |
A cupping test in which a piece of sheet metal, restrained except at the center, is deformed by a standard steel ball until fracture occurs. The height of the cup at time of fracture is a measure of the ductility. 一种杯突试验，其中一块金属板，除了中心以外，被一个标准钢球变形，直到发生断裂。断裂时杯的高度是延展性的量度。 |
| Cheese head | 圆柱头 |
A cylindrical head on a screw or bolt. For driving, it may be slotted, or hexagonally recessed. 螺钉或螺栓上的圆柱头。为了驱动，它可以是开槽的，也可以是六角形的。 |
| Velocity defect (Unit m/s) | 速度亏损（单位：m/s） |
In a viscous flow, such as a boundary layer or wake, the reduction in velocity, due to friction, compared with that of the free stream. 在粘性流中，如边界层或尾迹，由于摩擦，与自由流相比，速度降低。 |
| Curie temperature | 居里温度 |
The temperature of magnetic transformation below which a metal or alloy is ferromagnetic and above which it is paramagnetic. 磁性转变温度，低于此温度金属或合金为铁磁性，高于此温度则为顺磁性。 |
| Joint | 关节接合处 |
The part of a robot arm permitting either rotational or translational motion. Each joint provides a single degree of freedom, and thus a minimum of six is required if the robot is to be able to position and orientate the end effector anywhere within the workspace. A joint is described by four parameters: the joint angle, joint offset, joint twist, and link length. The joint angle is the angle between an extrapolation of the previous link length and the present link length, measured positive anticlockwise in a plane normal to the joint axis. This is variable in a rotational joint and fixed in a translational joint. The joint offset is the distance between the link length for the previous link and that for the present link, measured along the joint axis. This is variable for a translational joint and fixed for a rotational joint. The joint twist for the nth joint is the angle between the axes of joints Jn and Jn+1, measured positive anticlockwise in a plane normal to the link length and viewed from the position of the Jn+1 joint. The link length is the mutually perpendicular distance between planes passing through the axes of joint Jn and Jn+1. Both the joint twist and link length are fixed in all joints. 机器人手臂上允许旋转或平移运动的部分。每个接合处都有自由度，如果机器人要能够在工作空间内的任何位置定位和定向末端执行器，则至少需要六个接合处具有自由度。关节接合处由四个参数描述：关节角度、关节偏移、关节扭曲和链接长度。关节角度是在垂直于关节轴的平面内逆时针测量的先前连杆长度和当前连杆长度的外推之间的角度。这在旋转关节中是可变的，在平移关节中是固定的。关节偏移是沿关节轴测量的前一个连杆和当前连杆的连杆长度之间的距离。这对于平移关节是可变的，对于旋转关节是固定的。第n个关节的关节扭曲是关节Jn和Jn+1轴之间的角度，在垂直于连杆长度的平面内逆时针测量，从Jn+2关节的位置观察。连杆长度是穿过关节轴Jn和Jn+1的平面之间相互垂直的距离。关节扭曲和连杆长度在所有关节中都是固定的。 |
| Quench aging | 淬火时效 |
Aging induced by rapid cooling after solution heat treatment. 固溶热处理后快速冷却引起的时效。 |
| Structural engineering | 结构工程 |
A branch of civil engineering concerned with the design of buildings, dams, bridges, and other large structures. 土木工程的一个分支，涉及建筑物、水坝、桥梁和其他大型结构的设计。 |
| Nut splitter | 螺母分离器 |
A tool for removing rusted-on and corroded nuts from bolts. It consists of a stiff steel ring that is placed around the nut. A screw thread passing through the ring bears diametrically on a wedged-shape tip that indents and cuts though a face of the nut. 从螺栓上去除锈蚀螺母的工具。它由一个围绕螺母放置的刚性钢环组成。穿过环的螺纹径向支撑在楔形尖端上，该尖端凹陷并穿过螺母的表面。 |
| Ballonet | 气囊 |
An airbag used in a hybrid airship. Helium gas expels air from the ballonet during ascent. Fans draw air in during descent. 混合动力飞艇中使用的安全气囊。氦气在上升过程中将空气从气囊中排出。风扇在下降过程中吸入空气。 |
| Altitude | 高度 |
(Unit m) Vertical height measured relative to a specified datum such as sea level. （单位m）相对于特定基准（例如海平面）测量的垂直高度。 |
| Lead of thread | 螺纹导程 |
On a single threaded screw, the distance the screw or nut advances in one complete revolution. 在单螺纹螺钉上，螺钉或螺母在一整圈中前进的距离。 |
| Water jacket | 水套 |
A casing, typically of sheet metal, surrounding a machine, such as an engine, that requires cooling. Water is circulated through the jacket and a heat exchanger where the heat is removed. 机壳一种机壳，通常由金属板制成，围绕着需要冷却的机器，如发动机。水通过夹套和热交换器循环，在热交换器中热量被去除。 |
| Stress area | 应力面积 |
The effective cross-sectional area of the threaded section of a fastener. Used to compute average stress levels in that section. Based on the mean of pitch and minor diameters. 紧固件螺纹部分的有效横截面积。用于计算该截面中的平均应力水平。基于节距和小直径的平均值。 |
| Dynamic modulus | 动态模量 |
The ratio of stress to strain under cyclic conditions (calculated from data obtained from either free or forced vibration tests, in shear, compression, or tension). 循环条件下的应力与应变之比（根据在剪切、压缩或拉伸中的自由或强制振动测试中获得的数据计算得出）。 |
| Wrist | 腕关节 |
The final three joints on a robot which simulate rotations provided by the human wrist and thus allow orientation of the end effector to which it is attached by the wrist socket. 机器人上的最后三个关节，模拟人类手腕提供的旋转，从而允许其通过手腕插座连接到的末端执行器的方向。 |
| Nominal size | 公称尺寸 |
The intended size of a component. The actual size will depend on manufacturing tolerances. 组件的预期尺寸。实际尺寸取决于制造公差。 |
| Screw conveyor | 螺旋输送机 |
(auger, spiral conveyor, worm conveyor) A machine for bulk handling of semi-solid materials, consisting of a helical screw which rotates in a trough or casing. （螺旋输送机、螺旋输送机、蜗杆输送机）一种用于散装搬运半固态材料的机器，由在槽或外壳中旋转的螺旋螺杆组成。 |
| Tightness, acceptable | 密封性，可接受的 |
Wholly leak-free joints are impossible, at least if the contained fluid is a gas, so it has been proposed that the design of a gasketed joint should start with the selection of an ‘‘acceptable’’ leak rate. The designer would dimension bolts and joint members so that the actual leak rate would never exceed this. Three standard levels of tightness have been proposed as well. 至少在所含流体为气体的情况下，完全无泄漏的接头是不可能的，因此有人建议，垫圈接头的设计应从选择“可接受”的泄漏率开始。设计师将确定螺栓和接头构件的尺寸，以便实际泄漏率永远不会超过此值。还提出了三种标准的密封性等级。 |
| Natural aging | 自然时效 |
Spontaneous aging of a supersaturated solid solution at room temperature. 过饱和固溶体在室温下的自发时效。 |
| Tear strength (Unit N/m) | 撕裂强度（单位：N/m） |
The tensile force divided by the sheet thickness required to tear a pre-split sheet material at a specified rate. Particularly used for plastics, rubber, fabrics, and elastomers. Since the units are not those of stress but equivalent to J/m², the units of toughness, the term ‘strength’ is strictly incorrect. 按规定速率撕裂预裂片材所需的张力除以片材厚度。特别用于塑料、橡胶、织物和弹性体。由于单位不是应力单位，而是相当于J/m²，韧性单位，“强度”一词是完全错误的。 |
| Pneumatic control valve | 气动控制阀 |
(pneumatic valve) A valve in which the position of the valve stem, which varies the open area, is determined by the net force generated by compressed air acting on a diaphragm operating against the force of a compression spring. Depending upon the arrangement of the spring, in the event of air-supply failure, the valve may open or close. （气动阀）一种阀门，其中阀杆的位置随开口面积的变化而变化，由压缩空气作用在隔膜上产生的净力决定，隔膜克服压缩弹簧的力进行操作。根据弹簧的布置，在供气故障的情况下，阀门可以打开或关闭。 |
| Archimedes Wave Swing | 阿基米德波摆动 |
A machine for tidal-power energy generation consisting of two concentric, air-filled submerged cylinders. The inner lower cylinder is tethered to the ocean floor while the upper floater unit, which is closed at the top, moves up and down due to the variations in hydrostatic pressure caused by the wave motion. The relative movement of the two cylinders is used to generate electricity in which linear motion replaces the more common rotary motion of an electromagnetic generator. 一种用于潮汐能发电的机器，由两个同心的充气水下气缸组成。内部下部圆柱体系在海底，而顶部封闭的上部浮子单元由于波浪运动引起的静水压力变化而上下移动。两个气缸的相对运动用于发电，其中直线运动取代了电磁发电机更常见的旋转运动。 |
| Flame hardening | 火焰硬化 |
A process for hardening the surfaces of hardenable ferrous alloys in which an intense flame is used to heat the surface layers above the upper transformation temperature, whereupon the workpiece is immediately quenched. 一种用于硬化可硬化铁合金表面的工艺，其中使用强烈的火焰将表面层加热到转变温度上限以上，然后立即对工件进行淬火。 |
| Sigma-phase embrittlement | σ相脆化 |
Embrittlement of iron-chromium alloys (most notably austenitic stainless steels) caused by precipitation at grain boundaries of the hard, brittle intermetallic sigma phase during long periods of exposure to temperatures between approximately 565 and 980 °C (1050 and 1800 °F). Sigmaphase embrittlement results in severe loss in toughness and ductility and can make the embrittled material structure susceptible to intergranular corrosion. 铁铬合金（最显著的是奥氏体不锈钢）的脆化是由于在长时间暴露于约565至980°C（1050至1800°F）的温度下，硬脆金属间化合物σ相的晶界处沉淀造成的。σ相脆化导致韧性和延展性的严重损失，可使脆化的材料结构易于发生晶间腐蚀。 |
| Screw compressor | 螺杆压缩机 |
A positive-displacement rotary compressor in which gas is progressively compressed by two intermeshing, counter-rotating, helical screws. 一种容积式旋转压缩机，其中气体由两个相互啮合、反向旋转的螺旋螺杆逐渐压缩。 |
| Cone pulley | 锥轮 |
A stepped pulley having several diameters which, when linked by a laterallymoveable transmission belt to a corresponding pulley, gives a series of speed ratios. 具有多种直径的阶梯式皮带轮，当通过可横向移动的传动带连接到相应的皮带轮时，会产生一系列速比。 |
| Waviness | 波纹度 |
Waviness is periodic deviations from geometric surface, often sinusoidal in form and often determined by low-level oscillations of the machine-tool-workpiece system during machining. Typically, wavelengths range from 1 to 10 mm (0.04 to 0.4 in.) and wave heights from a few to several hundred micrometers. 波纹度是与几何表面的周期性偏差，其形式通常是正弦的，通常由机床-工件系统在加工过程中的低水平振荡决定。通常，波长范围为1至10毫米（0.04至0.4英寸），波高范围为几微米至几百微米。 |
| Plowing | 犁 |
In tribology, the formation of grooves by plastic deformation of the softer of two surfaces in relative motion. 在摩擦学中，通过相对运动的两个表面中较软的表面的塑性变形形成凹槽。 |
| Oxidation | 氧化 |
(1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air. （1）因电子损失而导致价态增加的反应。（2）腐蚀反应，其中被腐蚀的金属形成氧化物；通常用于与含有元素氧的气体如空气反应。 |
| Fluid mechanics | 流体力学 |
The study of fluids in motion (fluid dynamics) or fluid statics where there is no relative motion between fluid particles. Fluid statics concerns primarily the variation of pressure with altitude or depth; it includes aerostatics and hydrostatics. Fluid dynamics includes the topics of aerodynamics, gas dynamics, hydraulics, hydrodynamics and many aspects of acoustics, chemical engineering, flight, lubrication, meteorology, non-Newtonian fluid flow, oceanography, power-plant technology, propulsion, and turbomachinery. 研究运动中的流体（流体动力学）或流体静力学，其中流体粒子之间没有相对运动。流体静力学主要关注压力随高度或深度的变化；它包括空气静力学和流体静力学。流体动力学包括空气动力学、气体动力学、水力学、流体动力学以及声学、化学工程、飞行、润滑、气象学、非牛顿流体流动、海洋学、发电厂技术、推进和涡轮机械的许多方面。 |
| Oxygen probe | 定氧测头 |
An atmosphere-monitoring device that electronically measures the difference between the partial pressure of oxygen in a furnace or furnace supply atmosphere and the external air. 一种大气监测装置，以电子方式测量熔炉或熔炉供应大气中的氧分压与外部空气之间的差值。 |
| Final annealing | 最终退火 |
An imprecise term used to denote the last anneal given to a nonferrous alloy prior to shipment. 一个不精确的术语，用于表示有色金属合金在装运前的最后一次退火。 |
| Normal stress (Unit N) | 法向应力（单位：N） |
The stress component perpendicular to a plane on which forces act. Normal stress may be either tensile stress or compressive stress. A stress in a fluid (such as pressure) or a solid, that is perpendicular to the surface on which it acts. The surface may be a real external surface or an imaginary internal one. 垂直于受力平面的应力分量。法向应力可以是拉应力或压应力。流体（如压力）或固体中垂直于其作用表面的应力。该表面可以是真实的外表面或假想的内表面。 |
| Liquid carburizing | 液体渗碳 |
Surface hardening of steel by immersion into a molten bath consisting of cyanides and other salts. 通过浸入由氰化物和其他盐组成的熔池中对钢进行表面硬化。 |
| Dilatometer | 膨胀计 |
An instrument for measuring length or volume changes in a solid during heating and subsequent cooling or isothermal holding. · An instrument for measuring the linear expansion or contraction in a metal resulting from changes in such factors as temperature and allotropy. 一种在加热和随后的冷却或等温保持过程中测量固体长度或体积变化，测量金属因温度和同素异形体等因素的变化而引起的线性膨胀或收缩的仪器。 |
| Caterpillar | 毛虫式履带 |
(crawler vehicle) A vehicle that ‘lays its own road’ by running on endless belts, driven by toothed wheels, on each side. Used on soft ground where spreading of the load reduces contact stress. （履带式车辆）通过在每一侧由齿轮驱动的环形皮带运行来“铺设自己的道路”的车辆。用于负载分散可减少接触应力的松软地面。 |
| Stainless steels | 不锈钢 |
Iron-base alloys that are highly resistant to corrosion in many environments. The predominant alloying element is chromium, which, like iron at room temperature, has BCC crystal structure. Corrosion resistance by passivation is achieved by the formation of chromium oxide on the steel surface. Nickel, which has FCC crystal structure, is another important addition for some steels. Other additions used to enhance properties include manganese, molybdenum, niobium, and titanium. There are several classes of stainless steel. 在许多环境中具有高度耐腐蚀性的铁基合金。主要的合金元素是铬，与室温下的铁一样，铬具有BCC晶体结构。钝化抗腐蚀性是通过在钢表面形成氧化铬来实现的。具有FCC晶体结构的镍是某些钢的另一种重要添加剂。其他用于增强性能的添加剂包括锰、钼、铌和钛。不锈钢的种类有好几种。 |
| Compression ratio | 压缩率 |
The volume of a combustion chamber with the piston at the top of its stroke as a proportion of the total volume of the cylinder with the piston at the bottom of its stroke. For a piston engine, if the swept volume is SW and the clearance volume is CL, the compression ratio is given by ( SW + CL)/CL, i.e. it is a volume ratio rather than a pressure ratio. 活塞位于其冲程顶部的燃烧室的容积与活塞位于其冲程底部的气缸总体积的比例。对于活塞发动机，如果扫气量为SW，间隙容积为CL，则压缩比由(SW+CL)/CL给出，即它是体积比而不是压力比。 |
| Oil quenching | 油淬 |
Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering, or hot quenching. 碳钢在油浴中的硬化。分为常规、快速、马氏体淬火或热淬火。 |
| Preheating | 预热 |
Heating before some further thermal or mechanical treatment. For tool steel, heating to an intermediate temperature immediately before final austenitizing. For some nonferrous alloys, heating to a high temperature for a long time, to homogenize the structure before working. In welding and related processes, heating to an intermediate temperature for a short time immediately before welding, brazing, soldering, cutting, or thermal spraying. 在进一步热处理或机械处理之前加热。对于工具钢，在最终奥氏体化之前立即加热至中间温度。对于一些非铁合金，在工作前长时间加热到高温，以使结构均匀化。在焊接和相关工艺中，在焊接、钎焊、钎焊、切割或热喷涂之前，立即加热到中间温度。 |
| X-ray thickness gauge | X射线厚度计 |
A device comprising an X-ray source and a detector used to determine the thickness of material in sheet or plate form, including metals, paper, plastics, rubber, and ceramics. 一种由X射线源和探测器组成的装置，用于测定片状或平板状材料的厚度，包括金属、纸张、塑料、橡胶和陶瓷。 |
| Standardization | 标准化 |
1. National and international agreements for design, manufacture, materials, performance, practices, requirements, strength, etc. which ensure common results wherever an item is made and wherever used. 2. The manufacture of components so that interchangeability of parts during assembly of new, or repair of old, items is possible without ‘fitting’. 1.关于设计、制造、材料、性能、惯例、要求、强度等的国家和国际协议，确保在任何地方制造和使用物品都能产生共同结果。2.部件的制造，以便在装配新部件或维修旧部件时，无需“装配”即可实现部件的互换性。 |
| Shear strain rate(Unit 1/s) | 剪切应变率（单位1/s） |
In the deformation of solids, the rate at which shear strain is applied in a test or changes with time in a loaded component or structure. 在固体变形中，在试验中施加剪切应变的速率，或在加载部件或结构中随时间变化的速率。 |
| Raised-face flange | 凸面法兰 |
A flange which contacts its mating joint member only in the region in which the gasket is located. The flanges do not contact each other at the bolt circle. 仅在垫圈所在区域接触其配合接头构件的法兰。法兰在螺栓圆处不相互接触。 |
| Screw feeder | 螺旋给料机 |
A mechanism for handling bulk materials in which a rotating helicoidal screw moves the material axially forward. Similar to a screw conveyor, but required to discharge material at a controlled rate very accurately. It operates with the screw completely full. 一种用于处理散装物料的机构，其中旋转的螺旋螺杆使物料轴向向前移动。类似于螺旋输送机，但需要以受控速率非常精确地排出物料。它在螺杆完全充满的情况下运行。 |
| Three-quarters hard | 四分之三硬度 |
A temper of nonferrous alloys and some ferrous alloys characterized by tensile strength and hardness about midway between those of half hard and full hard tempers. 一种非铁合金和一些铁合金的回火，其特征是抗拉强度和硬度介于半硬回火和全硬回火之间。 |
| Fastener | 紧固件 |
A fastener is a mechanical device for holding two or more bodies in definite positions with respect to each other. 紧固件是一种机械装置，用于将两个或多个物体相对于彼此固定在确定的位置。 |
| Semiguided bend | 半导弯曲 |
The bend obtained by applying a force directly to the specimen in the portion that is to be bent. The specimen is either held at one end and forced around a pin or rounded edge, or is supported near the ends and bent by a force applied on the side of the specimen opposite the supports and midway between them. In some instances, the bend is started in this manner and finished in the manner of a free bend. 通过将力直接施加于待弯曲部分中的试样而获得的弯曲。将试样固定在一端，并围绕销或圆边施力，或者在靠近端部的位置支撑试样，并通过施加在试样与支撑件相对的一侧以及两者中间的力进行弯曲。在某些情况下，折弯以此方式开始，然后以自由折弯的方式结束。 |
| constitutive equation | 本构方程 |
(constitutive relation) 1. In solid mechanics or fluid mechanics, an algebraic or numerical relation for the dependency of stress on deformation, strain, strain rate, temperature, etc. in a material. In solid mechanics such a relation is sometimes called an equation of state. Simple linear examples include Hooke’s law and Newton’s viscosity law. 2. In heat transfer, a relation, such as Fourier’s law of heat conduction, connecting heat flux with temperature gradient. （本构关系）1.在固体力学或流体力学中，应力与材料的变形、应变、应变率、温度等之间的代数或数值关系。在固体力学中，这种关系有时称为状态方程。简单的线性例子包括胡克定律和牛顿粘度定律。2.在传热学中，将热流与温度梯度联系起来的一种关系，如傅立叶热传导定律。 |
| Torque control | 扭矩控制 |
A system of optimizing rotor speed for a variable-speed wind turbine by controlling the torque demands of the generator. 通过控制发电机的扭矩需求来优化变速风力涡轮机的转子速度的系统。 |
| Izod test | 悬臂梁试验 |
A type of impact test in which a V-notched specimen, mounted vertically, is subjected to a sudden blow delivered by the weight at the end of a pendulum arm. The energy required to break off the free end is a measure of the impact strength or toughness of the material. 一种冲击试验，其中垂直安装的V形切口试样受到摆臂末端重量的突然冲击。断开自由端所需的能量是材料冲击强度或韧性的量度。 |
| Infinite life diagram | 无限疲劳寿命图 |
A simple plot experimentally derived fatigue-life data, showing the conditions required for infinite life. 一个简单的曲线图，实验得出的疲劳寿命数据，显示了无限寿命所需的条件。 |
| Acoustics | 声学 |
The science and engineering of sound; its production, propagation, control, interaction with materials, etc. 声音科学与工程；它的产生、传播、控制、与材料的相互作用等。 |
| Scoring | 划痕 |
In tribology, a severe form of wear characterized by the formation of extensive grooves and scratches in the direction of sliding. 在摩擦学中，一种严重的磨损形式，其特征是在滑动方向上形成大面积的凹槽和划痕。 |
| Angle of torsion | 扭转角 |
(angle of twist) (Unit ° or rad) The angle relative to a chosen section, normal to the axis of twist, through which another part of a component rotates when subjected to a torque. （扭转角）（单位°或弧度）相对于选定截面的角度，垂直于扭转轴，部件的另一部分在受到扭矩时通过该角度旋转。 |
| Compression member | 压缩构件 |
A structural component, the major loading on which is compressive. 一种结构部件，其上的主要载荷是压缩的。 |
| Outside diameter (Unit m) | 外径（单位：m） |
(external diameter, OD) The diameter of a circular cylindrical tube or a sphere measured between opposite points on the external surface. （外径，OD）在外表面上的相对点之间测量的圆柱管或球体的直径。 |
| Pressure difference (Unit Pa) | 压差（单位Pa） |
(pressure differential, Δp) The difference between two pressures, one of which may be a reference pressure such as barometric pressure. In many flow processes, the pressure difference is more important than the absolute pressure level. （压差，Δp）两个压力之间的差值，其中一个压力可以是参考压力，如大气压力。在许多流动过程中，压差比绝对压力水平更重要。 |
| Bimetallic strip | 双金属片 |
A strip formed by welding, riveting or brazing together two metals having different coefficients of expansion, which causes the strip to curl when its temperature changes. Typical combinations are steel and copper or steel and brass. 将两种膨胀系数不同的金属焊接、铆接或钎焊在一起形成的带材，当温度变化时，带材会卷曲。典型的组合是钢和铜或钢和黄铜。 |
| Grain coarsening | 晶粒粗化 |
A heat treatment that produces excessively large austenitic grains. 产生过大奥氏体晶粒的热处理。 |
| Stress difference (Unit Pa) | 应力差（单位Pa） |
The algebraic difference between the largest and least principal stresses in a loaded body, equal to twice the greatest shear stress in the system. For σ1 > σ2 > σ3, it is given by (σ1 − σ3). 载荷体中最大和最小主应力之间的代数差，等于系统中最大剪应力的两倍。由（σ1− σ3).，可得σ1＞σ2＞σ3。 |
| Oldham coupling | 十字联轴节 |
(double-slider coupling) A device for connecting a pair of misaligned parallel shafts, on the end of each of which are flanges having diametral tenons (tongues) that engage with matching slots spaced at 90° in an intermediate disc. As the coupling rotates, the disc compensates for shaft offset by sliding along each tenon in turn. Low-friction surfaces are requisite and the disc is often made of a polymer. An alternative arrangement has the slots in the flanges and the tenons on the disc. （双滑块联轴器）一种连接一对未对准平行轴的装置，在每个平行轴的端部有法兰，法兰具有直径榫（舌），与中间盘中间隔90°的匹配槽接合。当联轴器旋转时，圆盘通过依次沿每个榫头滑动来补偿轴偏移。低摩擦表面是必需的，阀盘通常由聚合物制成。另一种布置方式是法兰上的槽和阀盘上的榫头。 |
| Verification | 检验 |
Checking or testing an instrument to ensure conformance with a specification. 检查或测试仪器以确保符合规范。 |
| Joule | 焦耳 |
The SI unit of energy. One joule is the work done by a force of one newton acting over a distance of one metre. The symbol is J, where 1 J = 1 N m. 国际单位制能量单位。一焦耳是一牛顿的力在一米的距离上所做的功。符号为J，其中1j=1m。 |
| Screw displacement | 螺杆位移 |
A rotation of a rigid body about an axis accompanied by a translation of the body along the same axis. 刚体绕轴旋转，同时刚体沿同一轴平移。 |
| Toughness (Unit J/m²) | 韧性（单位：J/m²） |
The ability of a metal to absorb energy and deform plastically before fracturing. 1. The ability of a material to resist crack initiation and propagation. 2. The ability of a material to absorb strain energy without fracturing. 金属在破裂前吸收能量和塑性变形的能力。1.材料抵抗裂纹萌生和扩展的能力。2.材料在不发生断裂的情况下吸收应变能的能力。 |
| Surface treatment | 表面处理 |
Any process, including chemical, electrochemical, mechanical, and thermal, designed to protect a surface against corrosion and wear or to alter its mechanical properties. 任何旨在保护表面免受腐蚀和磨损或改变其机械性能的工艺，包括化学、电化学、机械和热处理。 |
| Ablation cooling | 烧蚀冷却 |
The cooling of a surface exposed to very high external gas temperature which causes the surface material to sublime, melt or decompose. The chemical process absorbs heat while the mass flow of material away from the surface blocks the heat flux from the hot gas. 冷却暴露于非常高的外部气体温度的表面，导致表面材料升华、熔化或分解。化学过程吸收热量，而远离表面的物质的质量流阻挡了来自热气体的热通量。 |
| Free machining | 易切削 |
The property that makes machining easy because of the forming of small chips, a characteristic imparted to steel by sulfur, etc. 由于形成小切屑而使加工变得容易的特性，比如硫赋予钢的特性，等等。 |
| Density | 密度 |
The mass per unit volume of a solid material. (mass density, ρ) (Unit kg/m³) The mass per unit volume of a substance that satisfies the continuum assumption. The reciprocal of specific volume. 固体材料每单位体积的质量。（质量密度，ρ）（单位kg/m³）满足连续统假设的物质每单位体积的质量。和比容相关联。 |
| Elastic deformation | 弹性变形 |
A change in dimensions directly proportional to and in phase with an increase or decrease in applied force. 尺寸的变化与施加的力的增加或减少成正比并同相。 |
| Torsional shaft vibration | 扭轴振动 |
The rapid back-and-forth angular twisting along a rotating unbalanced shaft which reaches maxima at critical rotation speeds. Shaft eccentricity, unbalanced mass distribution, oscillatory torque, misalignment, etc. all influence torsional vibration. 沿旋转不平衡轴的快速来回角扭转，在临界转速下达到最大值。轴偏心、质量分布不平衡、振荡扭矩、未对准等都会影响扭转振动。 |
| Vapour-pressure thermometer | 蒸汽压力温度计 |
(vapour-filled thermometer) A type of fluidexpansion thermometer in which the working fluid is a volatile liquid. （蒸汽填充温度计）一种流体膨胀温度计，其中工作流体为挥发性液体。 |
| Critical cooling rate | 临界冷却速度 |
The rate of continuous cooling required to prevent undesirable transformation. For steel, it is the minimum rate at which austenite must be continuously cooled to suppress transformations above the Ms temperature. 防止不期望的转变所需的连续冷却速率。对于钢，它是奥氏体必须持续冷却以抑制Ms温度以上的转变的最小速率。 |
| Absorber | 吸收器 |
1. An auxiliary vibratory system that favourably modifies the vibration characteristics of a main system. 2. Part of an absorption refrigeration system in which the refrigerant is absorbed by a transport medium. 3. The absorber plate is the receiver of a concentrating solar collector where the radiation is absorbed. 1.一种辅助振动系统，可有利地改变主系统的振动特性。2.吸收式制冷系统的一部分，其中制冷剂被传输介质吸收。3.吸收板是吸收辐射的聚光太阳能集热器的接收器。 |
| Mode of failure | 故障模式 |
The various ways in which a material can fail when subjected to loading, surface damage, chemical attack, heating, cooling, or radiation, in either isolation or combination. The failure modes include fracture, fatigue, creep, corrosion, erosion, and embrittlement. 材料在受到载荷、表面损伤、化学侵蚀、加热、冷却或辐射时，可能发生失效的各种方式，无论是单独还是组合。失效模式包括断裂、疲劳、蠕变、腐蚀、侵蚀和脆化。 |
| Bearing area | 承载面积 |
The product of the pin (or hole) diameter and specimen thickness in a bearing test. (bearing surface) (Unit m²) The projected area of a hole, such as a rivet hole, that carries a transverse load. 轴承测试中销（或孔）直径和试样厚度的乘积。（承载面）（单位m²）承载横向载荷的孔（例如铆钉孔）的投影面积。 |
| Critical strain | 临界应变 |
The strain just sufficient to cause recrystallization; because the strain is small, usually only a few percent, recrystallization takes place from only a few nuclei, which produces a recrystallized structure consisting of very large grains. 刚好足以引起再结晶的应变；由于应变很小，通常只有百分之几，再结晶只发生在少数核上，从而产生由非常大的晶粒组成的再结晶结构。 |
| Reproducibility | 再现性 |
A term used to describe test-result variability associated with specifically defined components of variance obtained both from within a single laboratory and between laboratories. 一个术语，用于描述与从单个实验室内和实验室之间获得的具体定义的方差分量相关的测试结果可变性。 |
| Total energy (Unit J) | 总能量（单位J） |
The sum of all forms of energy associated with a system, including kinetic, potential, internal, magnetic, chemical, and electrical energy. 与系统相关的所有形式能量的总和，包括动能、势能、内能、磁能、化学能和电能。 |
| Transformation temperature | 相变温度 |
The temperature at which a change in phase occurs. The term is sometimes used to denote the limiting temperature of a transformation range. The following symbols are used for iron and steels. 发生相位变化的温度。该术语有时用于表示转变范围的极限温度。以下符号用于钢铁。 |
| Hydraulic air compressor | 液压空气压缩机 |
1. A compressor powered by a hydraulic motor. 2. A device in which air is compressed as a result of being entrained in water flowing in a downcomer pipe. The compressed air is released in a chamber at the bottom of the pipe. 1. 由液压马达驱动的压缩机。2.一种装置，其中空气由于夹带在降液管中流动的水中而被压缩。压缩空气在管道底部的腔室中释放。 |
| Tensile strength (Unit Pa) | 抗拉强度（单位Pa） |
In tension testing, the ratio of maximum load to original cross-sectional area. Also known as ultimate strength. The resistance that a material offers to tensile stress. It is defined as the smallest tensile stress required to break the body. (ultimate strength, ultimate tensile strength, UTS, Rm, Rm) The nominal or engineering stress given by the maximum load in a tension test divided by the original cross-sectional area of the specimen. The maximum load could be the fracture load for a brittle material, but for a ductile material it is usually taken as the load at which necking begins, beyond which the load falls. 在拉伸试验中，最大载荷与原始横截面积之比。也称为极限强度。材料对拉伸应力的抵抗力。它被定义为破坏主体所需的最小拉伸应力。（极限强度、极限抗拉强度、UTS、Rm、Rm）拉伸试验中最大载荷除以试样原始横截面积得出的标称或工程应力。对于脆性材料，最大载荷可以是断裂载荷，但对于韧性材料，最大荷载通常被视为颈缩开始时的载荷，超过该载荷时，载荷下降。 |
| Rosette | 玫瑰形的结 |
Strain gages arranged to indicate, at a single position, strain in three different directions. 应变计布置成在单个位置指示三个不同方向的应变。 |
| Two-dimensional flow | 二维流 |
A fluid flow in which the velocity at any time depends upon two spatial coordinates, such as the radial and axial locations in developing pipe flow. 一种流体流动，其中任何时候的速度取决于两个空间坐标，如发展中的管道流中的径向和轴向位置。 |
| Elongation | 伸张率 |
A term used in mechanical testing to describe the amount of extension of a test piece when stressed. 机械测试中使用的术语，用于描述试样在受力时的延伸量。 |
| Distortion | 扭曲 |
Any deviation from an original size, shape, or contour that occurs because of the application of stress or the release of residual stress. 由于施加应力或释放残余应力而发生的与原始尺寸、形状或轮廓的任何偏差。 |
| Concentrated solar power plant (CSP plant) | 聚光太阳能发电厂（CSP发电厂） |
A power plant in which solar radiation is concentrated using mirrors or lenses, typically using parabolic trough mirrors which focus solar radiation on to receiver tubes along the trough’s focal line. In an alternative arrangement molten salt, heated by solar receivers mounted on a tower, is circulated through a steam generator. 使用镜子或透镜集中太阳辐射的发电厂，通常使用抛物面槽镜，将太阳辐射沿着槽的焦线聚焦到接收管上。在另一种布置中，由安装在塔上的太阳能接收器加热的熔盐通过蒸汽发生器循环。 |
| Left hand screw | 左螺旋 |
One that screws into the mating part or advances when turned to the left or counter clockwise. 旋入配合部分或向左或逆时针旋转时前进的螺钉。 |
| Minimum load (Pmin) | 最小负载（Pmin） |
In fatigue, the least algebraic value of applied load in a cycle. 在疲劳中，循环中施加载荷的最小代数值。 |
| Mass flow rate (ṁ) (Unit kg/s) | 质量流量（ṁ）（单位kg/s） |
The mass of a material, usually a fluid or powder, that flows across a surface or through a pipe or other duct per unit time. The corresponding mass flux (ṁ″), with unit kg/s.m², is the mass flow across a real surface or through a duct, divided by the surface or cross-sectional area A, i.e. ṁ″ = ṁ/A or ṁ″ = ρV where ρ is the material density and V is its velocity normal to the surface. 单位时间内流过表面或通过管道或其他管道的材料质量，通常是流体或粉末。相应的质量通量（ṁ″），单位为kg/s.m²，是通过真实表面或通过管道的质量流量除以表面或横截面积A，即ṁ″=ṁ/A或ṁ″=ρV，其中ρ是材料密度，V是其垂直于表面的速度。 |
| Grain size | 晶粒大小 |
A measure of the areas or volumes of grains in a polycrystalline metal, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. For metals, a measure of the areas or volumes of grains in a polycrystalline material, usually expressed as an average when the individual sizes are fairly uniform. In metals containing two or more phases, the grain size refers to that of the matrix unless otherwise specified. Grain sizes are reported in terms of number of grains per unit area or volume, average diameter, or as a grainsize number derived from area measurements. 多晶金属中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。多晶材料中晶粒的面积或体积的量度，通常表示为单个尺寸相当均匀时的平均值。在含有两相或多相的金属中，除非另有说明，晶粒尺寸是指基体的晶粒尺寸。晶粒尺寸以每单位面积或体积的晶粒数、平均直径或从面积测量得出的晶粒尺寸数来报告。 |
| Hypereutectoid alloy | 过共析合金 |
In an alloy system exhibiting a eutectoid, any alloy whose composition has an excess of alloying element compared with the eutectoid composition, and whose equilibrium microstructure contains some eutectoid structure. 在呈现共晶的合金系统中，合金成分比共晶成分多的任何合金，其平衡微观结构包含一些共晶结构。 |
| International Practical Temperature Scale (IPTS) | 国际实用温标（IPTS） |
A close approximation to the thermodynamic temperature scale based upon the triple points of hydrogen (13.8 K), neon (24.6 K), oxygen (54.4 K), argon (83.8 K), mercury (234.3 K), and water (273.2 K); the melting point of gallium (302.9 K); and the freezing points of indium (429.7 K), tin (505.1 K), zinc (692.7 K), aluminium (933.5 K), silver (1 234.9 K), gold (1 337.3 K), and copper (1 基于氢（13.8K）、氖（24.6K）、氧（54.4K）、氩（83.8K），汞（234.3K）和水（273.2K）的三相点的热力学温度标度的近似值；镓的熔点（302.9K）；铟（429.7K）、锡（505.1K）、锌（692.7K），铝（933.5K）、银（1234.9K）、金（1337.3K）和铜等。 |
| Hardness test | 硬度测试 |
1. Any of various tests in which different hard indenters are forced into the surface of a solid under different loads to give permanent impressions, the pressure to cause which being called the hardness. The Brinell test employs a spherical indenter; the Vickers test a square-based pyramid. The relation between indentation hardness H and uniaxial yield stress Y is approximately H = (2.5 ~ 3.0)Y. Originally hardnesses were given in kg/mm² but now are often given in Pa. 2. The tests for scratch and file hardness relate either to one material being able to mark another (Mohs hardness scale for minerals), or to the size of groove produced by a rigid indenter slid under load across a surface. 3. Rebound hardness concerns the height of rebound of a dropped indenter, or an indenter at the end of a pivoted arm, having struck a surface. 1.任何一种试验，其中不同的硬压头在不同载荷下压入固体表面，以产生永久压痕，所产生的压力称为硬度。布氏试验采用球形压头；维氏硬度测试是一个方形金字塔。压痕硬度H与单轴屈服应力Y之间的关系约为H=（2.5~3.0）Y。最初硬度以kg/mm²为单位，但现在通常在Pa.2中给出。划痕和锉刀硬度测试要么与一种材料能够标记另一种材料（矿物的莫氏硬度标度）有关，要么与刚性压头在表面上滑动产生的凹槽大小有关。3.回弹硬度涉及掉落压头或旋转臂端部压头撞击表面后的回弹高度。 |
| Blue annealing | 蓝色退火 |
Heating hot-rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental. 在开放式炉中将热轧铁板加热到转变范围内的温度，然后在空气中冷却，以软化金属。在表面上形成蓝色氧化物是偶然的。 |
| Cohesive strength | 内聚强度 |
(Unit Pa) A theoretical fracture strength for solids based on interatomic forces, approximately equal to E/10 where E is Young’s modulus. （单位Pa）基于原子间力的固体理论断裂强度，大约等于E/10，其中E是杨氏模量。 |
| Coupling | 耦合 |
A detachable mechanism forming a joint. A connector of two components of a joint. 1. Any mechanical fastening connecting two or more shafts, or parts of a mechanism, in order to transmit power. 2. A device for connecting two vehicles. 一种形成关节的可拆卸机构。关节的两个组件的连接器。1.连接两个或多个轴或机构部件的任何机械紧固件，以传递动力。2.连接两辆车的装置。 |
| Induction hardening | 感应淬火 |
A surface-hardening process in which only the surface layer of a suitable ferrous workpiece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched. 一种表面硬化工艺，在该工艺中，只有合适的含铁工件的表面层通过电磁感应加热到高于上临界温度，并立即淬火。 |
| Ratchet marks | 棘轮痕 |
Lines on a fatigue fracture surface that result from the intersection and connection of fatigue fractures propagating from multiple origins. Ratchet marks are parallel to the overall direction of crack propagation and are visible to the unaided eye or at low magnification. 疲劳断裂面上由从多个源头传播的疲劳断裂的交叉和连接产生的线。棘轮标记与裂纹扩展的整个方向平行，肉眼或低倍镜下均可看到。 |
| Annealing carbon | 退火碳 |
Fine, apparently amorphous carbon particles formed in white cast iron and certain steels during prolonged annealing. Also called temper carbon. 白口铸铁和某些钢在长时间退火过程中形成的细小、明显的无定形碳颗粒。也称为回火碳。 |
| Standard fit | 标准匹配 |
The fit of a component machined or otherwise manufactured to standardized clearances and tolerances. 根据标准间隙和公差加工或以其他方式制造的部件的配合。 |
| Box annealing | 箱式退火 |
Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing. 在使氧化最小化的条件下，在密封容器中对金属或合金进行退火。在对铁合金进行箱式退火时，通常将装料缓慢加热至低于转变范围的温度，但有时会高于或低于转变范围，然后缓慢冷却；这个过程也称为紧密退火或罐式退火。 |
| B-basis | B-基础 |
Mechanical property value above which at least 90% of the population of values is expected to fall, with a confidence of 95%. 机械性能值超过该值时，至少90%的值预计会下降，置信度为95%。 |
| Beta annealing | β退火 |
Producing a beta phase by heating certain titanium alloys in the temperature range of which this phase forms followed by cooling at an appropriate rate to prevent its decomposition. 通过在形成β相的温度范围内加热某些钛合金，然后以适当的速率冷却以防止其分解，从而产生β相。 |
| Crack size (a) | 裂纹尺寸（a） |
A lineal measure of a principal planar dimension of a crack. This measure is commonly used in the calculation of quantities descriptive of the stress and displacement fields. In practice, the value of crack size is obtained from procedures for measurement of physical crack size, original crack size, or effective crack size, as appropriate to the situation under consideration. 裂纹主平面尺寸的线性度量。这种测量通常用于计算描述应力场和位移场的量。在实践中，裂纹尺寸的值是通过测量物理裂纹尺寸、原始裂纹尺寸或有效裂纹尺寸的程序获得的，视情况而定。 |
| Tangent modulus | 切线模量 |
The slope of the stress-strain curve at any specified stress or strain. See also modulus of elasticity. 在任何规定的应力或应变下，应力-应变曲线的斜率。另见弹性模量。 |
| Mohr–Coulomb fracture criterion | Mohr–Coulomb断裂准则 |
A fracture criterion, primarily for brittle materials, according to which failure occurs when the stress at a point in a material falls outside the envelope created by the Mohr’s circles for uniaxial tensile strength and uniaxial compressive strength. 一种断裂准则，主要适用于脆性材料，根据该准则，当材料中某一点的应力落在单轴抗拉强度和单轴抗压强度的莫尔圆所形成的包络线之外时，就会发生断裂。 |
| Graphitic carbon | 石墨碳 |
Free carbon in steel or cast iron. 钢或铸铁中的游离碳。 |
| Cyaniding | 氰化 |
A case-hardening process in which a ferrous material is heated above the lower transformation range in a molten salt containing cyanide to cause simultaneous absorption of carbon and nitrogen at the surface and, by diffusion, create a concentration gradient. Quench hardening completes the process. 一种表面硬化工艺，将含铁材料在含氰化物的熔融盐中加热至低于较低转变范围，使其表面同时吸收碳和氮，并通过扩散形成浓度梯度。淬火硬化完成该过程。 |
| Hot shortness | 热脆性 |
The reduction of ductility in steels at high temperatures caused by melting of sulfides that wet grain boundaries and spread along them. 高温下钢的延展性降低，这是由于硫化物的熔化润湿晶界并沿晶界扩散而引起的。 |
| Butterfly valve | 蝶阀 |
A valve in which a disc rotates on a shaft at right angles to the axis of a pipe to regulate flow. When open, the disc is edge-on to the flow and offers limited resistance. When closed, the disc is pressed against a seat in the valve body. 阀瓣在与管道轴线成直角的轴上旋转以调节流量的阀门。当打开时，圆盘与水流边缘并提供有限的阻力。关闭时，阀瓣被压在阀体内的阀座上。 |
| Torque monitor | 扭矩监测器 |
A torque tool control system which monitors the amount of torque being developed by the tool during use, but does not control the tool or the torque produced. 一种扭矩工具控制系统，监控工具在使用过程中产生的扭矩量，但不控制工具或产生的扭矩。 |
| Thermal insulation (insulation) | 隔热（绝缘） |
A material that may be a low-conductivity solid, or a porous solid or fabric in which there are voids containing air or another gas, resulting in overall low thermal conductivity. When applied to the surface of a hot or cold object, surface heat transfer is generally reduced. 一种材料，可以是低导电性固体，或多孔固体或织物，其中存在含有空气或其他气体的空隙，从而导致整体低导热性。当应用于热或冷物体的表面时，表面传热通常减少。 |
| Finished fastener | 精制紧固件 |
Fastener for which all manufacturing steps have been completed, with or without any surface coating and with full or reduced loadability, and which has not been machined into a test piece. 已完成所有制造步骤的紧固件，有或没有任何表面涂层，具有完全或降低的承载能力，并且尚未加工成试件。 |
| Eutectic carbide | 共晶碳化物 |
Carbide formed during freezing as one of the mutually insoluble phases participating in the eutectic reaction of ferrous alloys. 在冷冻过程中形成的碳化物，是参与铁合金共晶反应的互不溶相之一。 |
| Bioenergy | 生物能源 |
1. Energy derived from materials such as purpose-grown energy crops, including sugar cane, maize, wheat, and rice, as well as wood, straw, and animal waste, including sewage, manure, and animal litter. 2. A term sometimes used to cover biomass and biofuels together. 1.来自特定种植的能源作物（包括甘蔗、玉米、小麦和大米）以及木材、稻草和动物粪便（包括污水、粪便和动物垃圾）等材料的能源。2.有时用于同时涵盖生物质和生物燃料的术语。 |
| Safety valve (safety-relief valve) | 安全阀（安全泄压阀） |
A mechanical valve, fitted by law to all pressure vessels (e.g. steam boilers), which opens to prevent the internal pressure exceeding the maximum design value for that vessel. The valve closes again once the pressure reduces to a safe level. 根据法律安装在所有压力容器（如蒸汽锅炉）上的机械阀，其打开以防止内部压力超过该容器的最大设计值。一旦压力降至安全水平，阀门将再次关闭。 |
| Abrasion | 磨损 |
The removal of surface material by the scratching action of hard particles, either deliberately (abrasive papers, abrasive cleaning, abrasive machining) or as a consequence of operation (wear). 通过硬质颗粒的刮擦作用去除表面材料，可以是故意的（砂纸、研磨清洁、研磨加工），也可以是操作的结果（磨损）。 |
| Rotational joint (revolute joint) | 旋转关节 |
In robotics, a single degree-of-freedom joint where the controlled variable is the joint angle. 在机器人技术中，一种单自由度关节，其中受控变量为关节角度。 |
| Counter sink | 台面水槽 |
To cut or shape a depression in an object so that the head of a screw may set flush or below the surface. 在物体上切割或塑造一个凹陷，使螺钉的头部可以齐平或低于表面。 |
| Bearing failure | 轴承故障 |
A failure that occurs in a riveted or bolted joint when the transverse load divided by the bearing area results in a stress that leads to permanent plastic deformation. 当横向载荷除以承载面积产生导致永久塑性变形的应力时，铆接或螺栓连接中发生的失效。 |
| Turbine flow meter | 涡轮流量计 |
(axial flow meter, propeller meter) An in-line flow meter in which the rotation speed N of a propeller or rotor is a measure of the mass flowrate ṁ. Calibration is always necessary but with appropriate design ṁ is closely proportional to N over a wide range. （轴向流量计、螺旋桨流量计）一种串联流量计，其中螺旋桨或转子的转速N是质量流量的测量值ṁ. 校准总是必要的，但需要适当的设计ṁ在很宽的范围内与N成正比。 |
| Fillet radius | 圆角半径 |
Concave junction at two intersecting surfaces of a fastener. Often used to describe the junction between the head and the shank of a threaded fastener (under head fillet). 在紧固件的两个相交表面处的凹形接合处。通常用于描述螺纹紧固件的头部和柄部之间的连接处（头部圆角下方）。 |
| Quench cracking | 淬火开裂 |
Fracture of a metal during quenching from elevated temperature. Most frequently observed in hardened carbon steel, alloy steel, or tool steel parts of high hardness and low toughness. Cracks often emanate from fillets, holes, corners, or other stress raisers and result from high stresses due to the volume changes accompanying transformation to martensite. 高温淬火时金属断裂。在高硬度和低韧性的硬化碳钢、合金钢或工具钢零件中最常见。裂纹通常来自圆角、孔、角部或其他应力集中区，并由伴随马氏体转变的体积变化引起的高应力引起。 |
| Cemented carbides | 硬质合金 |
Sintered mixtures of refractory metal carbides (e.g. tungsten carbide) in a metal matrix binder such as cobalt, nickel, or iron. They have high melting point, toughness, compressive strength, and wear resistance. Applications include use in grinding wheels and papers, cutting tools, drill bits, wire-drawing dies, and ball-point pen tips. Sometimes known as hard metals when the application is to machine tools. 难熔金属碳化物（如碳化钨）在金属基体粘结剂（如钴、镍或铁）中的烧结混合物。它们具有高熔点、韧性、抗压强度和耐磨性。应用包括用于砂轮和纸张、切削工具、钻头、拉丝模和圆珠笔尖。当应用于机床时，有时称为硬金属。 |
| Angularity | 角度 |
The underfaces of the nut and the bolt head should be exactly perpendicular to the thread or shank axes. If the angle between the face and the axis is, for example, 868 or 948, the fastener is said to have an angularity of 48 (sometimes called Perpendicularity). 螺母和螺栓头的底面应与螺纹或柄轴完全垂直。例如，如果面和轴之间的角度为868或948，则称紧固件的角度为48（有时称为垂直度）。 |
| Ultimate strength | 极限应力 |
The maximum tensile strength a bolt or material can support prior to rupture. Always found in the plastic region of the stress–strain or force–elongation curve, and so is not a design strength. Also called Tensile strength and ultimate tensile strength. The maximum stress (tensile, compressive, or shear) a material can sustain without fracture, determined by dividing maximum load by the original cross-sectional area of the specimen. Also known as nominal strength or maximum strength. 螺栓或材料在断裂前可支撑的最大抗拉强度。总是出现在应力-应变或力-伸长率曲线的塑性区域，因此不是设计强度。也称为抗拉强度和极限抗拉强度。材料在不断裂的情况下能够承受的最大应力（拉伸、压缩或剪切），通过将最大载荷除以试样的原始横截面积来确定。也称为标称强度或最大强度。 |
| Vacuum carburizing | 真空渗碳 |
A high-temperature gas carburizing process using furnace pressures between 7 and 55 kPa during the carburizing portion of the cycle. 在循环的渗碳部分期间使用7至55kPa之间的炉压的高温气体渗碳工艺。 |
| Percent error | 误差百分比 |
For testing machines, the ratio, expressed as a percentage, of the error to the correct value of the applied load. 对于试验机，以百分比表示的误差与所施加载荷的正确值之比。 |
| Absolute rating | 绝对标称值 |
A theoretical size designation which is an estimation of the largest particle, by length, that can pass through a filter with a specific 一个理论尺寸名称，它是按长度估算的最大颗粒，它可以通过具有特定过滤器的过滤器 |
| Stress factor | 应力因子 |
A calibration constant used in ultrasonic measurement of bolt stress or strain. It is the ratio between the change in ultrasonic transit time caused by the change in length of the fastener, under load, to the total change in transit time. 用于螺栓应力或应变超声波测量的校准常数。它是由紧固件长度变化引起的超声波传输时间变化与总传输时间变化之间的比率。 |
| Compressor | 压缩机 |
A turbomachine, of either axial or radial type, that increases the pressure of a gas or vapour. 一种增加气体或蒸汽压力的轴向或径向涡轮机。 |
| Inclusions | 夹杂物 |
Small pieces of nonmetallic impurities trapped within the base metal of. 存在于金属基体中的小块非金属杂质。 |
| Water-jet cutting | 水射流切割 |
Cutting of materials such as rock by means of a high-speed jet of water containing abrasive particles. 通过含有磨料颗粒的高速水射流切割岩石等材料。 |
| Strength of bolt | 螺栓强度 |
An ambiguous term which can mean Ultimate strength or Proof load or Endurance limit or Yield strength. 一个模棱两可的术语，可表示极限强度或验证荷载或耐久极限或屈服强度。 |
| Half nut | 半螺母 |
A mechanism attached to the apron of a lathe and operated by a lever. The lever opens and closes a nut that has been split lengthwise so that the two halves of the nut can be closed upon the lead screw when threads are being cut. Also called Split Nut. 固定在车床裙板上并由杠杆操作的机械装置，杠杆打开和关闭纵向分开的螺母，以便在切割螺纹时，螺母的两半可以在丝杠上闭合。也称为剖分螺母。 |
| Total-loss lubrication | 全损耗润滑 |
A system in which the lubricating oil for an internal-combustion engine is burned together with the fuel. 内燃机润滑油与燃料一起燃烧的系统。 |
| Freezing range | 冻融范围 |
That temperature range between liquidus and solidus temperatures in which molten and solid constituents coexist. 熔融和固体成分共存的液相线和固相线温度之间的温度范围。 |
| Hard temper | 硬化回火 |
Same as full hard temper. 和全硬化回火一样。 |
| Alpha iron | 阿尔法铁 |
The body-centered cubic form of pure iron, stable below 910 °C (1670 °F). 纯铁的体心立方形式，在910°C(1670°F)以下稳定。 |
| Bánki turbine | 班基涡轮机 |
A cross-flow, impulse-type water turbine for very low heads in which a jet of water in the form of a flat sheet passes transversely through the turbine, so going through the runner twice. The thin runner blades which run horizontally across the turbine parallel to the axis of rotation are profiled in cross section. 一种用于非常低水头的横流脉冲式水轮机，其中平板形式的水射流横向穿过涡轮机，因此穿过转轮两次。平行于旋转轴水平穿过涡轮机的薄转轮叶片在横截面上具有轮廓。 |
| Viscoelasticity | 粘弹性 |
A property involving a combination of elastic and viscous behavior. A material having this property is considered to combine the features of a perfectly elastic solid and a perfect fluid. A phenomenon of time-dependent, in addition to elastic, deformation (or recovery) in response to load. 结合弹性和粘性的特性。具有这种性质的材料被认为是完美弹性固体和完美流体的结合体。除了弹性变形（或恢复）外，还随时间变化的一种现象。 |
| Newton’s law of gravitation | 牛顿万有引力定律 |
(Newton’s law of universal gravitation) Any two bodies exert a gravitational force of attraction F on each other directed along the line joining their centres of mass, in magnitude proportional to the product of their masses and inversely proportional to the square of the distance r between them. （牛顿万有引力定律）任何两个物体沿其质心连接线相互施加引力F，其大小与其质量乘积成正比，与它们之间距离r的平方成反比。 |
| Slip joint | 滑动接头 |
A mechanical connection which allows limited endwise relative movement of two components such as pipes, rods, and ducts. 一种机械连接，允许两个部件（如管道、杆和管道）进行有限的轴向相对运动。 |
| Elastic recovery | 弹性恢复 |
Amount the dimension of a stressed elastic material returns to its original (unstressed) dimension on release of an applied load. In hardness testing, the shortening of the original dimensions of the indentation upon release of the applied load. 在释放施加的载荷时，受应力弹性材料的尺寸恢复到其原始（无应力）尺寸的量。在硬度测试中，当释放所施加的载荷时，压痕的原始尺寸缩短。 |
| Dew point | 压力露点 |
The temperature and pressure at which a gas begins to condense to a liquid. 气体开始凝结成液体的温度和压力。 |
| Deviation | 偏差 |
The difference between the actual value and the desired value of a controlled variable. 受控变量的实际值与期望值之间的差值。 |
| Fatigue striations | 疲劳条纹 |
Parallel lines frequently observed in electron microscope fractographs or fatigue-fracture surfaces. The lines are transverse to the direction of local crack propagation; the distance between successive lines represents the advance of the crack front during the one cycle of stress variation. 在电子显微镜断口图或疲劳断口表面中经常观察到平行线。这些线横向于局部裂纹扩展方向；连续线之间的距离表示在一个应力变化周期内裂纹前沿的前进。 |
| Workspace (Unit m³) | 工作空间（单位m³） |
(working-space volume) The volume around the base frame of a robot, defined by the reach of the robot. The robot can thus only perform tasks within this volume. （工作空间体积）机器人基架周围的体积，由机器人的可达范围定义。因此，机器人只能执行该体积内的任务。 |
| Pitting | 点蚀 |
In tribology, a type of wear characterized by the presence of small, sharp surface cavities formed by processes such as fatigue, local adhesion, wear, corrosion, or cavitation. 在摩擦学中的一种磨损，其特征是存在由疲劳、局部粘附、磨损、腐蚀或空穴等过程形成的小而尖锐的表面空穴。 |
| Bolt | 螺栓 |
(machine bolt) A fastener in the form of an externally-threaded cylinder with a head on one end that is inserted through holes in assembled parts that are then held together by a nut tightened on to the thread. A bolt has an unthreaded region below the head so that when located in a hole, transverse loads are borne by two plain cylindrical surfaces in contact. In contrast, use of a machine screw, that has threads all along its length, results in threads bearing against the plain surface of a hole. Officially, a threaded fastener designed to be used with a nut. （机械螺栓）外螺纹圆柱状紧固件：一端有头的紧固件，通过装配零件上的孔插入，然后通过拧紧到螺纹上的螺母固定在一起。螺栓头部下方有一个无螺纹区域，因此当位于孔中时，横向载荷由两个接触的平面圆柱面承担。相反，使用沿其长度具有螺纹的机器螺钉，会导致螺纹支撑在孔的平面上。正式情况下，螺纹紧固件设计用于与螺母一起使用。 |
| Gear pump | 齿轮泵 |
A positive-displacement pump in which fluid is pumped by meshing gears, one driven and the other an idler gear, on parallel axes within a closed casing. 一种容积式泵，其中流体由啮合齿轮泵送，在封闭外壳内的平行轴上一个驱动，另一个为空套齿轮。 |
| Surface tension (σ, γ) (Unit N/m) | 表面张力（σ，γ）（单位：N/m） |
At the interface between a liquid and a gas or two immiscible liquids, unbalanced cohesive forces acting on the liquid molecules at the interface lead to the property surface tension which causes tensile forces to develop as if it were a skin or membrane. 液体和气体或两种不混溶液体之间的界面处，作用在界面处的液体分子上的不平衡内聚力导致表面张力的性质，从而导致张力的发展，就像皮肤或薄膜一样。 |
| Design code | 设计规范 |
(design standard) A standard or specification for any aspect of engineering design, issued by national organizations such as ANSI, ASME, BSI, DIN, and ISO. （设计标准）工程设计任何方面的标准或规范，由ANSI、ASME、BSI、DIN和ISO等国家组织发布。 |
| Crank pin | 曲柄销 |
It is a short shaft parallel to the axis of the crankshaft but radially offset from it, to which is attached the big end of a connecting rod in a bearing. Sometimes the crank pin is supported at one end only (a wrist pin) but in built-up or one-piece forged crankshafts, the crank pin is supported by thick plates (crank arms, crank webs) at either end. 它是一个短轴，平行于曲轴的轴线，但径向偏移，轴承中连杆的大端连接到该短轴上。有时曲柄销仅在一端支撑（腕销），在组合式或整体锻造曲轴中，曲柄销在两端由厚板（曲柄臂、曲柄腹板）支撑。 |
| Secant modulus | 割线模量 |
The slope of the secant drawn from the origin to any specified point on a stress-strain curve. Compare with chord modulus. 从原点到应力应变曲线上任何指定点的割线斜率。与弦模量进行比较。 |
| Tension joint | 张力接头 |
A joint which is primarily subjected to loads acting more or less parallel to the axes of the bolts. 主要承受或多或少平行于螺栓轴线的载荷的接头。 |
| Precipitation hardening | 沉淀硬化 |
Hardening caused by the precipitation of a constituent from a supersaturated solid solution. 因成分从过饱和固溶体沉淀而导致的硬化。 |
| Lead angle | 导角 |
The angle of the helix of a screw thread or worm thread. It is the measure of the inclination of a screw thread from a plane perpendicular to the axis of the screw. 螺纹或蜗杆螺纹的螺旋角。它是螺纹从垂直于螺钉轴线的平面的倾斜度的量度。 |
| Barcol hardness test | 巴氏硬度测试 |
An indentation test, similar to the Shore hardness test but using a pointed indentor with a flat tip, used to determine the hardness of such materials as rigid plastics and composites. 一种压痕测试，类似于肖氏硬度测试，但使用带有扁平尖端的尖头压头，用于确定硬质塑料和复合材料等材料的硬度。 |
| Endurance limit | 耐力极限 |
The maximum stress below which a material can presumably endure an infinite number of stress cycles. The value of the maximum stress and the stress ratio also should be stated. That completely reversing stress limit below which a bolt or joint member will have an essentially infinite life under cyclic fatigue loads. Note that the mean stress on the bolts here is zero. 材料可以承受无限次应力循环的最大应力。还应说明最大应力值和应力比。完全逆转的应力极限，低于该极限螺栓或接头构件在循环疲劳载荷下将具有基本上无限的寿命。请注意，此处螺栓上的平均应力为零。 |
| Compression crease | 压缩折痕 |
A crease formed during the compression of composites having a high volume fraction of filaments. These composites fail in compression by forming a crease at an angle to the loading axis. 在压缩具有高体积分数长丝的复合材料期间形成的折痕。这些复合材料通过形成与加载轴成一定角度的折痕而在压缩中失效。 |
| Actual value | 实际价值 |
The output of a plant that is being controlled, i.e. the controlled variable. Not directly accessible by the control system, as it can only be measured by a sensor which may distort the measurement. 受控设备的输出，即受控变量。控制系统不能直接访问，因为它只能由可能会扭曲测量结果的传感器测量。 |
| Compression failure | 压缩失败 |
The reduction or removal of a component’s load-bearing capacity in compression, caused by buckling, fracture, crease formation in fibre composites, etc. 由纤维复合材料中的屈曲、断裂、折痕形成等引起的部件在压缩中的承载能力的降低或消除。 |
| Bainitic hardening | 贝氏体硬化 |
Quench-hardening treatment resulting principally in the formation of bainite. 淬火硬化处理主要导致贝氏体的形成。 |
| Zirconia-toughened alumina composites | 氧化锆增韧氧化铝复合材料 |
(ZTA composites) Ceramic composites based on aluminium oxide to which zirconium oxide is added, resulting in improved fracture toughness. （ZTA复合材料）基于氧化铝的陶瓷复合材料，其中添加了氧化锆，从而提高了断裂韧性。 |
| Intergranular fracture | 沿晶破裂 |
Brittle fracture of a metal in which the fracture is between the grains, or crystals, that form the metal. Also called intercrystalline fracture. 金属的脆性断裂，断裂位于形成金属的晶粒或晶体之间。又称晶间破裂。 |
| Recrystallization temperature | 再结晶温度 |
The approximate minimum temperature at which complete recrystallization of a cold-worked metal occurs within a specified time. 冷加工金属在规定时间内发生完全再结晶的近似最低温度。 |
| Congruent transformation | 全等变换 |
An isothermal or isobaric phase change in which both of the phases concerned have the same composition throughout the process. 等温或等压相变，其中相关的两个相在整个过程中具有相同的成分。 |
| Normality | 常态 |
The principle that the vector sum of plastic strain increments is perpendicular to the yield surface. 塑性应变增量矢量和垂直于屈服面的原理。 |
| Roughness | 粗糙度 |
The deviations from the wavy surface itself, caused by geometry of the cutting tool and its wear, machining conditions, microstructure of the workpiece, vibrations in the system, and so on. Surface roughness changes as a surface goes through the wearing-in process, but may then stabilize. 由刀具的几何形状及其磨损、加工条件、工件的微观结构、系统中的振动等引起的与波状表面本身的偏差。表面粗糙度随着表面经过磨合过程而变化，但随后可能会稳定下来。 |
| Condensing boiler | 冷凝锅炉 |
A relatively small industrial or domestic boiler that burns sulfur-free natural gas so that the products of combustion do not contain sulfuric acid and can be allowed to condense on heat-transfer surfaces without danger of corrosion. 一种相对较小的工业或家用锅炉，燃烧无硫天然气，因此燃烧产物不含硫酸，并且可以在传热表面上冷凝而没有腐蚀的危险。 |
| Chain dimensioning | 链条尺寸标注 |
On an engineering drawing, where the end point of one dimension is the starting point for the next. Parallel dimensioning is preferred as chain dimensioning can lead to the accumulation of tolerances. 在工程图纸上，其中一个尺寸的终点是下一个的起点。平行尺寸标注是首选，因为链尺寸标注可能导致公差累积。 |
| Snap temper | 快速回火 |
A precautionary interim stress-relieving treatment applied to high-hardenability steels immediately after quenching to prevent cracking because of delay in tempering them at the prescribed higher temperature. 在淬火后立即对高淬透性钢进行预防性临时应力消除处理，以防止因在规定的更高温度下回火延迟而开裂。 |
| Crankshaft | 曲轴 |
The main shaft, of which the cranks are a part, of a reciprocating single-or multi-cylinder machine. Crankshafts may be built up in sections or forged as a single component. In an engine, the reciprocating motion of the pistons transmits power to the crankshaft and causes it to rotate, whereas in a pump the crankshaft is driven and its rotation causes the pistons to reciprocate. 曲柄是往复式单缸或多缸机器主轴的一部分。曲轴可以分段组装或作为单个部件锻造。在发动机中，活塞的往复运动将动力传递给曲轴并使其旋转，而在泵中，曲轴被驱动，其旋转使活塞往复运动。 |
| Pressure loss (Unit Pa) | 压力损失（单位Pa） |
The loss in stagnation pressure in internal flow due to wall friction and minor losses in fittings. 壁面摩擦引起的内部流动停滞压力损失和配件的微小损失。 |
| Transfer ratio | 传输比 |
(transfer constant) A complex variable representing the ratio between the output of a transducer and the input causing that output. （传递常数）一个复变量，表示传感器输出与产生该输出的输入之间的比率。 |
| Intergranular cracking | 沿晶断裂 |
Cracking or fracturing that occurs between the grains or crystals in a polycrystalline aggregate. Also called intercrystalline cracking. 多晶聚集体中的晶粒或晶体之间发生的开裂或断裂。也称为晶间断裂。 |
| Rockwell hardness number (HR) | 洛氏硬度值（HR） |
A number derived from the net increase in the depth of impression in a Rockwell hardness test as the load on an indenter is increased from a fixed minor load to a major load and then returned to the minor load. Rockwell hardness numbers are always quoted with a scale symbol representing the penetrator, load, and dial used. 当压头上的载荷从固定的小载荷增加到大载荷，然后返回到小载荷时，洛氏硬度试验中压痕深度的净增加值。洛氏硬度值总是用刻度符号引用，表示所用的穿透器、载荷和刻度盘。 |
| Batch furnace | 间歇式炉 |
A furnace used to heat treat a single load at a time. Batch-type furnaces are necessary for large parts such as heavy forgings and are preferred for complex alloy grades requiring long cycles. 用于一次热处理单个负载的炉子。对于重型锻件等大型零件，间歇式炉是必需的，对于需要长周期的复杂合金牌号来说是首选。 |
| Rated flow (Unit m³/s or kg/s) | 额定流量（单位：m³/s或kg/s） |
In a hydraulic system or machine, the volume or mass flow rate a manufacturer specifies for a component as the maximum desirable for it to function as designed. 在液压系统或机器中，制造商为部件指定的体积或质量流量是其按设计运行所需的最大值。 |
| Zero time | 零时 |
The time when the given loading or constraint conditions are initially obtained in creep or stressrelaxation tests, respectively. 分别在蠕变或应力松弛试验中初始获得给定载荷或约束条件的时间。 |
| Centrifugal pump | 离心泵 |
A pump into which liquid enters axially through the eye of the casing and is then accelerated through an impeller, thereby increasing both its kinetic energy and pressure before being delivered to a ring diffuser (the volute) that further increases the liquid pressure and from which it leaves. 一种泵，液体通过泵壳的眼轴向进入，然后通过叶轮加速，从而在输送到环形扩散器（蜗壳）之前增加其动能和压力，从而进一步增加液体压力并从中流出树叶。 |
| Essential conditions | 必要条件 |
Each type of failure to which bolted joints are subject is set up by three or four conditions. The conditions vary, depending on the mode of failure, but never number more than four. Eliminating any one of the essential conditions for a particular type of failure can prevent that type of failure. 螺栓连接所遭受的每种类型的故障都由三个或四个条件确定。根据故障模式的不同，情况会有所不同，但数量不得超过四个。消除特定类型故障的任何一个基本条件都可以防止该类型故障。 |
| Root diameter (Unit m) | 根部直径（单位：m） |
The diameter of the circle passing through the roots of teeth in gear teeth or screw threads. 穿过齿轮齿或螺纹中齿根的圆的直径。 |
| Nominal diameter | 公称直径 |
The ‘‘catalog diameter’’ of a fastener. Usually roughly equal to the diameter of the body, or the outer diameter of the threads. 紧固件的“目录直径”。通常大致等于主体的直径或螺纹的外径。 |
| Microhardness | 显微硬度 |
The hardness of a material as determined by forcing an indenter such as a Vickers or Knoop indenter into the surface of a material under very light load; usually, the indentations are so small that they must be measured with a microscope. Capable of determining hardnesses of different microconstituents within a structure, or of measuring steep hardness gradients such as those encountered in case hardening. 通过在非常轻的载荷下将压头（如维氏或努氏压头）压入材料表面来确定的材料硬度；通常压痕很小，必须用显微镜测量。能够确定结构内不同微组分的硬度，或测量陡峭的硬度梯度，如表面硬化中遇到的硬度梯度。 |
| Calorizing | 热化 |
Imparting resistance to oxidation to an iron or steel surface by heating in aluminum powder at 800 to 1000 °C (1470 to 1830 °F). 通过在800至1000°C（1470至1830°F）下加热铝粉，赋予铁或钢表面抗氧化性。 |
| Push rod | 推杆 |
A rod which opens and closes a valve via a valve rocker in an overhead-valve piston engine. The rod is actuated by a camshaft located in the crankcase. 在顶置气门活塞发动机中，通过气门摇臂打开和关闭气门的杆。连杆由曲轴箱中的凸轮轴驱动。 |
| Static equilibrium | 静态平衡 |
A solid body, structure, or physical system (or any subdivided part) will be in static equilibrium, either at rest or moving with constant velocity, if the resultants of all external forces and moments acting on it are zero. 如果作用在固体上的所有外力和力矩的合力为零，则固体、结构或物理系统（或任何细分部分）无论是静止还是以恒定速度移动，都是处于静态平衡。 |
| Concentrated load | 集中负荷 |
A load on a component which is distributed over a very small area, idealized as the line load of a wedge or knife edge, and the point load of a cone. 分布在非常小的区域上的部件上的载荷，理想化为楔形或刀刃的线载荷和锥体的点载荷。 |
| Tracking problem | 跟踪问题 |
A control problem where the set point changes with time and thus the plant output must follow the changing set point. The opposite of a regulator problem. 一种控制问题，其中设定值随时间变化，因此设备输出必须遵循变化的设定值。与调节器问题相反。 |
| Terminal velocity (Unit m/s) | 终端速度（单位：m/s） |
The velocity reached by an object in free fall through a fluid when the upward drag and buoyancy forces just balance the object’s weight. For an object with a density lower than that of the fluid, the terminal velocity is vertically upwards. 当向上的阻力和浮力正好平衡物体的重量时，物体自由下落通过流体达到的速度。对于密度低于流体密度的物体，终端速度垂直向上。 |
| Austempered steels | 等温钢 |
Medium to high carbon steels with improved mechanical properties as a result of austempering. After heating to between 800° and 900°C to form the austenite phase, they are quenched to, and held at, just above the martensite transformation range (between 260° and 370°C) to form bainite, before cooling further. Austempering of ductile cast irons results in a microstructure of bainite and spheroidal graphite. Austempered ductile irons have excellent toughness and wear properties. 由于等温淬火，机械性能得到改善的中高碳钢。在加热到800°和900°C之间形成奥氏体相后，将它们淬火并保持在略高于马氏体转变范围（260°和370°C之间）以形成贝氏体，然后进一步冷却。球墨铸铁的等温淬火导致贝氏体和球状石墨的微观结构。等温淬火球墨铸铁具有优异的韧性和耐磨性。 |
| Case | 包盖 |
That portion of a ferrous alloy, extending inward from the surface, whose composition has been altered so that it can be case hardened. Typically considered to be the portion of the alloy (a) whose composition has been measurably altered from the original composition, (b) that appears dark on an etched cross section, or (c) that has a hardness, after hardening, equal to or greater than a specified value. Contrast with core. 铁合金的一部分，从表面向内延伸，其成分已经改变，可以进行表面硬化。通常被认为是合金的一部分，（a）其成分与原始成分发生了可测量的变化，（b）在蚀刻横截面上呈黑色，或（c）硬化后硬度等于或大于规定值。与核心形成对比。 |
| Grain-boundary liquation | 晶界液化 |
An advanced stage of overheating in which material in the region of austenitic grain boundaries melts. 奥氏体晶界区域的材料熔化的过热阶段。 |
| Fin | 翼 |
A thin projecting rib. 一根细长的凸肋。 |
| Scratch hardness | 划痕硬度 |
The resistance of a material, such as a metal, alloy, plastic, or mineral, to scratching by a much harder indenter, such as a diamond stylus, moved slowly across the surface. The scratch hardness number is computed from the loads and the dimensions of the residual scratch. 一种材料（如金属、合金、塑料或矿物）对更硬的压头（如金刚石触针）划伤的抵抗力，在表面上缓慢移动。根据载荷和残余划痕的尺寸计算划痕硬度值。 |
| Dimensional stability | 尺寸稳定性 |
Ability of a plastic part to retain the precise shape in which it was molded, fabricated, or cast. 塑料零件保持其成型、制造或铸造时的精确形状的能力。 |
| Tensometer | 拉力计 |
A bench-top device, used to perform tension and compression tests. 用于进行拉伸和压缩试验的台式装置。 |
| Stress relieving | 应力消除 |
Heating to a suitable temperature, holding long enough to reduce residual stresses, and then cooling slowly enough to minimize the development of new residual stresses. 加热到合适的温度，保持足够长的时间以减少残余应力，然后缓慢冷却以尽量减少新残余应力的产生。 |
| Morse taper | 莫氏锥度 |
A self holding, standard taper largely used on drilling tools, drilling machine spindles, and some lathes. 一种自持式标准锥度，主要用于钻孔工具、钻床主轴和一些车床。 |
| Torricellean barometer | 托里塞莱气压计 |
A vertical glass tube with its upper end sealed and the lower end submerged in a pool of mercury. The space above the mercury is under vacuum. The height to which the mercury rises up the tube is a measure of the barometric pressure. 一种垂直的玻璃管，上端密封，下端浸入汞池中。水银上方的空间处于真空状态。水银在管道中上升的高度是大气压力的量度。 |
| Failure of the bolt | 螺栓失效 |
Term implying that the bolt has broken or the threads have stripped. There can be many reasons for this. 表示螺栓断裂或螺纹脱落的术语。原因可能有很多种。 |
| Connecting rod | 连杆 |
(con rod) A link that transmits power from one system to another, often changing linear to rotary motion, as in the rod connecting the piston to the crankshaft in a reciprocating compressor or pump or to the crankshaft in an internal-combustion engine, as in the diagram. The big end (bottom end) is the larger end that connects to the bearing on one of the crankpins of the crankshaft. The little end (small end) is joined by a gudgeon pin to the piston. （连杆）将动力从一个系统传递到另一个系统的连杆，通常由线性运动变为旋转运动，如图所示，连杆将活塞连接到往复式压缩机或泵的曲轴或内燃机的曲轴上。大端（底端）是连接到曲轴一个曲柄销上轴承的大端。小端（小端）通过活塞销连接到活塞上。 |
| Scatter | 分散 |
Data points or calculations are said to be scattered when they are not all the same. A ‘‘lot of scatter in preload’’ means wide variation in the preloads found in individual bolts. 当数据点或计算不尽相同时，它们被称为分散的。“预载的大量分散”意味着单个螺栓中的预载差异很大。 |
| Turbomolecular pump | 涡轮分子泵 |
A high-vacuum (pressure down to about 10−8 Pa) pump in which momentum is transferred to the gas molecules by a rapidly rotating bladed disc. 高真空（压力降至约10−8Pa）泵，其中动量通过快速旋转的叶片盘传递给气体分子。 |
| Torque reaction (Unit N.m) | 扭矩反作用力（单位：N.m） |
The torque needed to counteract an applied torque. For example, in a helicopter with a single main rotor, the tendency of the fuselage to rotate in the opposite direction to the rotor. 抵消施加扭矩所需的扭矩。例如，在具有单个主旋翼的直升机中，机身沿与旋翼相反的方向旋转的趋势。 |
| Kelvin (K) | 开尔文（K） |
The SI unit of temperature. The Kelvin temperature scale has a zero point at absolute zero and degree intervals (kelvins) the same size as degrees Celsius. The freezing point of water occurs at 273K (0ºC) and the boiling point at 373 K (100ºC). The base unit of thermodynamic temperature in the SI system. It was previously defined to be the fraction 1/273.16 of the thermodynamic temperature of the triple point of water. From 20 May 2019 it has been defined by taking the fixed numerical value of the Boltzmann constant kB to be 1.380 649 × 10−23 when expressed in the unit J/K, which is equal to kg.m²/(s²K). 国际单位制中热力学温度的基本单位。开尔文温度标度在绝对零度和与摄氏度大小相同的度间隔（开尔文）处有一个零点。水的冰点为273K（0ºC），沸点为373K（100ºC）。它先前被定义为水三相点热力学温度的分数1/273.16。从2019年5月20日起，通过将玻尔兹曼常数kB的固定数值取为1.380649×10来定义−当以等于kg·m²/（s²K）的单位J/K表示时。 |
| Catastrophic failure | 灾难性故障 |
A sudden and total failure of a large engineering structure such as an aeroengine, aircraft, space vehicle, bridge, or dam. 大型工程结构（如航空发动机、飞机、航天器、桥梁或水坝）突然完全失效。 |
| Force ratio | 力比 |
The factor by which a simple machine multiplies an applied force. It is the ratio of the load (output force) to the effort (input force). 简单机器乘以所施加的力的因子。它是负载（输出力）与作用力（输入力）的比值。 |
| PSI (pounds per square inch) | PSI（磅/平方英寸） |
Pressure measurement. Psia (pounds per square inch absolute) measures actual pressure with no allowance for atmospheric pressure. Psig (pounds per square inch gauge) measures pressure with the gauge set to zero (0) at atmospheric pressure (14.7 psia). In other words psig = psia – 14.7. 压力测量。Psia（绝对磅/平方英寸）测量实际压力，不考虑大气压力。Psig（磅/平方英寸表压）在大气压（14.7 psia）下，将表压设置为零（0）时测量压力。换句话说，psig=psia–14.7。 |
| Pitch (Unit m) | 间距（单位：m） |
1. In a cascade of identical turbine or compressor blades, the distance between successive blades measured parallel to the leading edges. 2. For a screw thread, the distance between adjacent thread forms measured parallel to the thread axis. 3. For an aircraft, the vertical relationship between the nose and the horizon. The pitch axis is an axis in the plane of the wings of an aircraft, perpendicular to the centreline, about which the aircraft rotates. Pitch motion is the corresponding up or down movement of the aircraft nose. Pitch attitude is the angle between the centreline of an aircraft and the horizontal. The angle is positive when the nose is above its position when the centreline is horizontal. 1.在相同涡轮或压缩机叶片的叶栅中，平行于前缘测量的连续叶片之间的距离。2.对于螺纹，平行于螺纹轴线测量的相邻螺纹形状之间的距离。3.对于飞机，机头和水平线之间的垂直关系。俯仰轴是飞机机翼平面内垂直于中心线的轴，飞机绕中心线旋转。俯仰运动是飞机机头的相应向上或向下运动。俯仰姿态是飞机中心线与水平线之间的角度。当中心线水平时，当机头高于其位置时，角度为正。 |
| Archimedes screw | 阿基米德螺旋泵 |
A machine which comprises a rotating helical blade inside a closefitting tube, which may be used to pump liquids, slurries (such as sewage), granular materials, etc. If water flows into the top of an inclined or vertical Archimedes screw, the screw will rotate and can be used to drive an electrical generator. 一种机器，它在紧密的管子内包含一个旋转的螺旋叶片，可用于泵送液体、泥浆（如污水）、颗粒材料等。如果水流入倾斜或垂直的阿基米德螺杆的顶部，螺杆将旋转，可用于驱动发电机。 |
| Turning angle (θ) | 转向角（θ） |
The change in direction experienced by a gas flow passing through an oblique shock wave or Prandtl–Meyer expansion fan. 气流通过斜激波或Prandtl–Meyer膨胀风机时所经历的方向变化。 |
| Resistance factor | 阻力系数 |
Probabilistic factor representing the uncertainties in the designer’s estimate of the strength of a shear joint. Used in Load and resistance factor design. 概率系数，表示设计人员对剪切接头强度估计的不确定性。用于载荷和阻力系数设计。 |
| Available draught (Unit Pa) | 可用通风量（单位Pa） |
The reduced pressure of combustion gases in a furnace or boiler, either forced or due to the buoyancy of hot gases, which is used to draw in combustion air and remove products of combustion. 炉子或锅炉中燃烧气体的压力降低，无论是强制还是由于热气体的浮力，用于吸入燃烧空气并去除燃烧产物。 |
| Modulus of rupture | 断裂模量 |
Nominal stress at fracture in a bend test or torsion test. In bending, modulus of rupture is the bending moment at fracture divided by the section modulus. In torsion, modulus of rupture is the torque at fracture divided by the polar section modulus. 弯曲试验或扭转试验中的标称断裂应力。在弯曲中，断裂模量是断裂时的弯矩除以截面模量。在扭转中，断裂模量是断裂时的扭矩除以极截面模量。 |
| U-tube | U型管 |
A device consisting of two vertical tubes connected at either the top or bottom by a length of tubing such that a U-shape is formed. 由两个垂直管组成的装置，在顶部或底部通过一段管子连接，形成U形。 |
| Materials selection | 材料选择 |
The process of selecting the most suitable material for a particular application. In the case of solid materials, it involves assessment of candidate materials in terms of their physical properties (density, elastic moduli, fracture toughness, yield strength, hardness, fatigue resistance, coefficient of thermal expansion, thermal conductivity, resistance to thermal shock, creep resistance, corrosion resistance, radiation resistance, etc), and such factors as the function of the final product, its shape, method of manufacture, required tolerances, number to be made, ease of inspection and quality control, cost, and design methodology employed. 为特定应用选择最合适材料的过程。对于固体材料，它涉及根据其物理特性（密度、弹性模量、断裂韧性、屈服强度、硬度、抗疲劳性、热膨胀系数、导热系数、抗热冲击性、抗蠕变性、耐腐蚀性、抗辐射性等）评估候选材料，以及诸如最终产品的功能、其形状、制造方法、所需公差、制造数量、检查和质量控制的容易程度、成本和采用的设计方法等因素。 |
| Nanomanufacturing | 纳米制造 |
1. The manufacture of nanoscale materials. 2. The manufacture of components or devices that have critical dimensions of order 1 nm. 1.纳米材料的制造。2.具有1nm级临界尺寸的部件或装置的制造。 |
| Destructive testing | 破坏性测试 |
Measurement of the mechanical properties of a material, component, or structure, by increased loading until the sample fails by fracture, collapse, or buckling. 通过增加载荷测量材料、部件或结构的机械性能，直到样品因断裂、塌陷或屈曲而失效。 |
| Austenite finish temperature (Af) | 奥氏体完成温度（Af） |
Temperature at which the transformation of martensite into austenite completes upon heating. The same designation is also applied to nonferrous alloys in which martensite transforms into some parent phase. 加热时马氏体转变为奥氏体的温度。相同的名称也适用于马氏体转变为某些母相的有色合金。 |
| Atomizing humidifier | 雾化加湿器 |
A humidifier that functions by spraying fine droplets of water into an airstream. 一种加湿器，通过将细小的水滴喷射到气流中来发挥作用。 |
| Structure | 结构体 |
An assembly, usually load bearing, of connected (pinned, riveted, screwed, bolted, welded, etc.) components, such as bars, tubes, beams, and plates. 由连接（销接、铆接、螺纹连接、螺栓连接、焊接等）部件组成的组件，通常为承重组件，如杆、管、梁和板。 |
| Quench (quenching) | 淬火 |
Rapid cooling. When applicable, the following more specific terms should be used: brine quenching, caustic quenching, cold die quenching, forced-air quenching, intense quenching, oil quenching, press quenching, spray quenching, direct quenching, fog quenching, hot quenching, interrupted quenching, selective quenching, time quenching, and water quenching. 1. The process of rapid-cooling by plunging an object into a bath of water, oil, salt, molten metal, or other media. It is a method of heat treatment used particularly to form martensite preparatory to tempering steels. The bath temperature is the quench temperature. 2. The suppression of combustion. 3. In a piston engine, the cooling of a fraction of the gases during combustion, typically by reducing the clearance between the piston crown and the cylinder head. 快速冷却。适用时，应使用以下更具体的术语：盐水淬火、碱淬火、冷模淬火、强制空气淬火、强淬火、油淬火、压力淬火、喷射淬火、直接淬火、雾淬火、热淬火、间断淬火、选择性淬火、时间淬火和水淬火。1.通过将物体放入水、油、盐、熔融金属或其他介质的浴中快速冷却的过程。这是一种热处理方法，特别用于形成回火钢前的马氏体。浴温度是淬火温度。2.燃烧的抑制。3.在活塞式发动机中，燃烧过程中一部分气体的冷却，通常通过减小活塞顶和气缸盖之间的间隙来实现。 |
| Oxidizing flame | 氧化焰 |
A gas flame produced with excess oxygen in the inner flame. 在内部火焰中过量氧气产生的气体火焰。 |
| Hot isostatic pressing | 热等静压 |
Sintering of powdered materials at high temperature and high hydrostatic pressure in order to minimize porosity. 在高温和高静水压力下烧结粉末材料，以尽量减少孔隙率。 |
| Cavitation | 空蚀空化 |
The formation of vapour- or gas-filled cavities in a liquid due to reduction of the local pressure, often due to acceleration of the fluid, such as in flow through a convergent nozzle. If there is no dissolved gas in the liquid, vaporous cavitation occurs when the pressure falls below the saturated vapour pressure. If the bubbles are formed due to high temperature, the process is termed boiling. If there is dissolved gas, gaseous cavitation occurs due to pressure reduction, temperature increase, or diffusion (degassing). At the tips of marine propellers and in hydraulic machinery, the collapse of cavitation bubbles can cause noise and vibration and lead to surface damage in the form of pitting. 由于局部压力降低而在液体中形成充满蒸汽或气体的空腔，通常原因是流体的加速，例如收敛喷嘴的流动。如果液体中没有溶解气体，当压力降至饱和蒸汽压力以下时，会发生蒸汽空化。如果气泡是由于高温形成的，则该过程称为沸腾。如果存在溶解气体，则由于压力降低、温度升高或扩散（脱气），会发生气穴。在船用螺旋桨尖端和液压机械中，空化气泡的破裂可能会引起噪音和振动，并导致以点蚀形式出现的表面损坏。 |
| Selective heating | 局部加热 |
Intentionally heating only certain portions of a workpiece. 有意仅加热工件的某些部分。 |
| Creep rupture strength (Unit Pa) | 蠕变断裂强度（单位Pa） |
The fracture stress at the end of a creep test in metals and polymers, often plotted against time to give a stress-rupture curve. 金属和聚合物蠕变试验结束时的断裂应力，通常与时间作图以给出应力-断裂曲线。 |
| Hydrogen-induced delayed cracking | 氢致延迟开裂 |
A term sometimes used to identify a form of hydrogen embrittlement in which a metal appears to fracture spontaneously under a steady stress less than the yield stress. There is usually a delay between the application of stress (or exposure of the stressed metal to hydrogen) and the onset of cracking. Also referred to as static fatigue. 有时用于识别一种氢脆形式的术语，其中金属在小于屈服应力的稳定应力下似乎会自发断裂。在施加应力（或将受应力金属暴露于氢）与开裂开始之间通常存在延迟。也称为静态疲劳。 |
| Positive-displacement flow meter | 容积式流量计 |
An instrument of high accuracy that determines volumetric flow rate by dividing the flowing fluid into successive fixed volumes, and measuring their times of passage through the meter. 一种高精度仪器，通过将流动的流体分成连续的固定体积并测量其通过流量计的时间来确定体积流量。 |
| Centrifugal | 离心式 |
Acting or moving in a direction away from the axis of rotation of a rotating body. 沿远离旋转体的旋转轴的方向作用或移动。 |
| Dynamic recovery | 动态恢复 |
A process occurring in hot working of metals in which a fine subgrain structure forms within the elongated grains due to annihilation of dislocations due to easy cross slip and climb. It results in a lowering of the flow stress. Dynamic recovery, as opposed to dynamic recrystallization that occurs in hot working, occurs in metals of high stacking fault energy such as aluminum, αiron, and most bcc metals. 金属热加工中发生的一种过程，由于易于交叉滑动和攀爬，位错湮灭，细长晶粒内形成细亚晶粒结构。这导致流动应力降低。与热加工中发生的动态再结晶相反，动态回复发生在高层错能金属中，如铝、α铁和大多数bcc金属。 |
| Calorie | 卡路里 |
(cal, gram calorie, small calorie) An obsolete (i.e. non-SI) unit of energy equal to 4.186 8 J. It is the amount of energy needed to raise the temperature of 1 gram of pure airfree water from 14.5°C to 15.5°C at standard atmospheric pressure. （卡，克热量，小热量）一种已被淘汰的（即非SI）能量单位，等于4.1868J。它是在标准大气压力下将1克纯无空气水的温度从14.5℃升高到15.5℃所需的能量。 |
| Atomization | 雾化 |
The production of a spray of fine droplets from a liquid, such as diesel oil or petrol, by injection through a nozzle (an atomizer). 通过喷嘴（雾化器）喷射从液体（例如柴油或汽油）中产生细小液滴喷雾。 |
| Coextrusion | 复合挤压 |
The simultaneous extrusion through the same die of two or more materials in combination. 通过同一模具同时挤出两种或多种材料的组合。 |
| Meyer hardness (Unit Pa) | 迈耶硬度（单位Pa） |
A material hardness similar to the Brinell hardness but based upon the projected area of the impression rather than the surface area. 与布氏硬度相似的材料硬度，但基于印模的投影面积而不是表面面积。 |
| Charles law/Charles' law | 查尔斯定律 |
(Gay–Lussac law) The volume of a fixed mass of gas at constant pressure is proportional to its absolute temperature. The volume of a gas at constant pressure is directly proportional to its absolute temperature. （盖-吕萨克定律）在恒定压力下，固定质量气体的体积与其绝对温度成正比。恒压下气体的体积与其绝对温度成正比。 |
| Hot-wire analyzer | 热电阻丝型分析仪 |
An electrical atmosphere analysis device that is based on the fact that the electrical resistivity of steel is a linear function of carbon content over a range from 0.05% C to saturation. The device measures the carbon potential of furnace atmospheres (typically). This term is not to be confused with the hot-wire test which measures heat extraction rates. 一种基于以下事实的电气氛分析设备：钢的电阻率是从0.05%C到饱和范围内的碳含量的线性函数。该设备测量炉内气氛的碳势（通常）。不要将此术语与测量热提取率的热线测试相混淆。 |
| Densimeter | 密度计 |
An instrument used to determine the density or relative density of a solid or liquid. 用于测定固体或液体的密度或相对密度的仪器。 |
| Interrupted quenching | 间断淬火 |
A quenching procedure in which the workpiece is removed from the first quench at a temperature substantially higher than that of the quenchant and is then subjected to a second quenching system having a different cooling rate than the first. 在该淬火过程中，工件在显著高于淬火剂的温度下从第一次淬火中取出，然后经受具有不同于第一次淬火的冷却速率的第二次淬火系统。 |
| Chain | 链 |
A series of connected links, typically of steel. For lifting, pulling, securing, etc., each link is a closed loop, often in the form of a ring. For power transmission, the links are designed to mesh with the teeth of a sprocket wheel. In contrast to belt drives, chain drives tend to be employed in high-torque applications. 一系列连接的链接，通常是钢制的。对于提升、拉动、固定等，每个链节都是一个闭合环，通常呈环形。对于动力传输，链节设计为与链轮的齿啮合。与皮带传动相比，链传动往往用于高扭矩应用。 |
| Ackerman linkage | 阿克曼装置 |
A steering linkage on a motor vehicle that approximately gives rolling without slipping of both wheels about the turning point. This is achieved by having the inner stub axle (on the inside of the turning curve) move through a greater angle than the outer stub axle. 机动车辆上的一种转向联动装置，在转向点附近两个车轮几乎不会打滑。这是通过使内短轴（在转弯曲线的内侧）比外短轴移动更大的角度来实现的。 |
| Acoustic emission | 声发射 |
(stress-wave emission) Sound emitted by some materials when deformed under load. It arises from stress waves emitted by sudden dislocation motion in crystals, slip, crack growth, etc. （应力波发射）某些材料在负载下变形时发出的声音。它是由晶体中突然的位错运动、滑移、裂纹扩展等发出的应力波引起的。 |
| Yielding | 屈服 |
Evidence of plastic deformation in structural materials. Also known as plastic flow or creep. 结构材料塑性变形的证据。也称为塑性流动或蠕变。 |
| Steam gauge | 汽压表 |
A pressure gauge used to measure gauge pressure in a line, boiler, cylinder, or other device operating with steam. 一种压力表，用于测量管道、锅炉、汽缸或其他与蒸汽一起工作的装置中的表压。 |
| Bond strength (Unit Pa) | 结合强度（单位Pa） |
The tensile, compressive or shear stress at which joints fail, e.g. by fracture or excessive deformation. 接头失效的拉伸、压缩或剪切应力，例如断裂或过度变形。 |
| Vane engine (vane motor) | 叶片发动机（叶片马达） |
A rotary engine in which high-pressure hydraulic fluid in the spaces between spring-loaded sliding vanes held in an offset rotor acts on the vanes, causing the rotor to revolve within a cylinder. The design is much like a sliding-vane compressor, as is that of a vane pump, used to pump liquids. 一种旋转式发动机，其中偏置转子中装有弹簧的滑动叶片之间的高压液压流体作用在叶片上，使转子在气缸内旋转。这种设计很像滑动叶片压缩机，就像用于泵送液体的叶片泵一样。 |
| Variance | 方差 |
A measure of the squared dispersion of observed values or measurements expressed as a function of the sum of the squared deviations from the population mean or sample average. 观测值或测量值的平方离散度的度量，表示为总体平均值或样本平均值的平方偏差之和的函数。 |
| Stress distribution | 应力分布 |
The manner in which tensile, compressive, and shear stresses are distributed within a loaded body, indicated by loci of constant stress. 拉应力、压应力和剪应力在受载物体内的分布方式，由恒定应力轨迹表示。 |
| Velocity ratio | 速度比 |
1. The ratio between the input velocity to a machine, train of gears, etc. and the output velocity. 2. The ratio between the displacement of an applied force at one part of a mechanism and the movement of the load at a different part. 1.机器、齿轮系等的输入速度与输出速度之间的比率。2.在机构的一个部分处施加的力的位移与在不同部分处的载荷的移动之间的比率。 |
| 显示更多数据，请使用查询功能！ | ||